WO1984004975A1 - Procede de preparation d'un toner electrophotographique - Google Patents

Procede de preparation d'un toner electrophotographique Download PDF

Info

Publication number
WO1984004975A1
WO1984004975A1 PCT/SE1983/000240 SE8300240W WO8404975A1 WO 1984004975 A1 WO1984004975 A1 WO 1984004975A1 SE 8300240 W SE8300240 W SE 8300240W WO 8404975 A1 WO8404975 A1 WO 8404975A1
Authority
WO
WIPO (PCT)
Prior art keywords
particles
polymer
base particles
shell
colorant
Prior art date
Application number
PCT/SE1983/000240
Other languages
English (en)
Inventor
Anders Axelsson
Lolo Bylander
Sten Porrvik
Olof Tanner
Original Assignee
Kema Nord Ab
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kema Nord Ab filed Critical Kema Nord Ab
Priority to EP19830902456 priority Critical patent/EP0145717A1/fr
Priority to PCT/SE1983/000240 priority patent/WO1984004975A1/fr
Publication of WO1984004975A1 publication Critical patent/WO1984004975A1/fr

Abstract

Procédé de préparation de particules de toner possédant une coquille de matériau polymère où est réparti un colorant. On prépare lesdites particules en traitant les particules de base avec un polymère-coquille et un colorant et on met ces éléments en contact pour obtenir une répartition uniforme des additifs sur les particules de base avant de faire fusionner le polymère-coquille avec les particules de base.
PCT/SE1983/000240 1983-06-10 1983-06-10 Procede de preparation d'un toner electrophotographique WO1984004975A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP19830902456 EP0145717A1 (fr) 1983-06-10 1983-06-10 Procede de preparation d'un toner electrophotographique
PCT/SE1983/000240 WO1984004975A1 (fr) 1983-06-10 1983-06-10 Procede de preparation d'un toner electrophotographique

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/SE1983/000240 WO1984004975A1 (fr) 1983-06-10 1983-06-10 Procede de preparation d'un toner electrophotographique

Publications (1)

Publication Number Publication Date
WO1984004975A1 true WO1984004975A1 (fr) 1984-12-20

Family

ID=20349648

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/SE1983/000240 WO1984004975A1 (fr) 1983-06-10 1983-06-10 Procede de preparation d'un toner electrophotographique

Country Status (2)

Country Link
EP (1) EP0145717A1 (fr)
WO (1) WO1984004975A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1987001828A1 (fr) * 1985-09-20 1987-03-26 Casco Nobel Ab Particules de toner pour la reproduction electrophotographique et procedes pour leur preparation
WO1988007225A1 (fr) * 1987-03-18 1988-09-22 Casco Nobel Ab Particules colorantes pour la copie electrophotographique et procedes de preparation desdites particules

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2890968A (en) * 1955-06-02 1959-06-16 Rca Corp Electrostatic printing process and developer composition therefor
GB1115634A (en) * 1964-07-02 1968-05-29 Rank Xerox Ltd Spray dried xerographic toners
US3788994A (en) * 1971-12-30 1974-01-29 Xerox Corp Pressure fixable electrostatagraphic toner
US3893932A (en) * 1972-07-13 1975-07-08 Xerox Corp Pressure fixable toner
DE2649940A1 (de) * 1975-11-06 1977-05-18 Sublistatic Holding Sa Magnetische toner und ihre herstellung
DE2452530B2 (de) * 1973-11-30 1978-11-02 Sublistatic Holding S.A., Glarus (Schweiz) Elektrophotographischer magnetischer Toner und Verfahren zur Herstellung von Kopien hiermit
DE2908652A1 (de) * 1978-03-06 1979-09-20 Canon Kk Druckfixierbarer toner
DE2929118A1 (de) * 1978-07-18 1980-01-31 Canon Kk Druckfixierbarer, kapselfoermiger toner
DE2945193A1 (de) * 1978-11-09 1980-05-22 Canon Kk Druckfixierbarer kapseltoner

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2890968A (en) * 1955-06-02 1959-06-16 Rca Corp Electrostatic printing process and developer composition therefor
GB1115634A (en) * 1964-07-02 1968-05-29 Rank Xerox Ltd Spray dried xerographic toners
US3788994A (en) * 1971-12-30 1974-01-29 Xerox Corp Pressure fixable electrostatagraphic toner
US3893932A (en) * 1972-07-13 1975-07-08 Xerox Corp Pressure fixable toner
DE2452530B2 (de) * 1973-11-30 1978-11-02 Sublistatic Holding S.A., Glarus (Schweiz) Elektrophotographischer magnetischer Toner und Verfahren zur Herstellung von Kopien hiermit
DE2649940A1 (de) * 1975-11-06 1977-05-18 Sublistatic Holding Sa Magnetische toner und ihre herstellung
DE2908652A1 (de) * 1978-03-06 1979-09-20 Canon Kk Druckfixierbarer toner
DE2929118A1 (de) * 1978-07-18 1980-01-31 Canon Kk Druckfixierbarer, kapselfoermiger toner
DE2945193A1 (de) * 1978-11-09 1980-05-22 Canon Kk Druckfixierbarer kapseltoner

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1987001828A1 (fr) * 1985-09-20 1987-03-26 Casco Nobel Ab Particules de toner pour la reproduction electrophotographique et procedes pour leur preparation
WO1988007225A1 (fr) * 1987-03-18 1988-09-22 Casco Nobel Ab Particules colorantes pour la copie electrophotographique et procedes de preparation desdites particules
US4923776A (en) * 1987-03-18 1990-05-08 Casco Nobel Ab Toner particles for electrophotographic copying and processes for their preparation

Also Published As

Publication number Publication date
EP0145717A1 (fr) 1985-06-26

Similar Documents

Publication Publication Date Title
US4837107A (en) Toner for electrophotographic methods and process for preparing the same
EP0277128B2 (fr) Particules de toner pour la reproduction electrophotographique et procedes pour leur preparation
EP0447045B1 (fr) Procédé de fabrication de microcapsules
US3844811A (en) Agglomeration of pigment particles and compositions utilizing same
JPH026051B2 (fr)
JP2009521723A (ja) 化学的に製造された多孔質トナー
EP0305378B1 (fr) Particules colorantes pour la copie electrophotographique et procedes de preparation desdites particules
US3745118A (en) Toner composition containing preformed carbon black core and process of making same
WO1984004975A1 (fr) Procede de preparation d'un toner electrophotographique
JPH0339309B2 (fr)
KR100429932B1 (ko) 좁은입도분포를갖는수지입자의제조방법
US6399701B1 (en) Surfactant-free semi-continuous emulsion polymerization process for making submicron sized particles for carrier coatings
EP0232275B1 (fr) Procede de production de particules de toner pour applications reprographiques
JPH01184035A (ja) マイクロカプセル化微粒子の製造方法
Tyagi Polyester-Based Chemically Prepared Toner for High-Speed Digital Production Printing
JPH01180241A (ja) マイクロカプセル化微粒子の製造方法
JPH0547825B2 (fr)
JPH02179650A (ja) トナーの製造方法
JPH0774913B2 (ja) 重合トナ−の製造方法
JPH0777831A (ja) 重合粒子の製造方法
Shiozaki et al. Triboelectric charge control of polymer microspheres by surface modification using heterocoagulation
JPH01250964A (ja) 静電潜像現像用トナーの製造方法
JPS58223431A (ja) 球状樹脂複合材の製造法
JPH04123067A (ja) トナーの製造方法
JPH01145663A (ja) 静電荷像用トナーの製造方法

Legal Events

Date Code Title Description
AK Designated states

Designated state(s): JP US

AL Designated countries for regional patents

Designated state(s): AT BE CH DE FR GB LU NL SE