US20200190391A1 - Method Of Creating A Composite Cement With Enhanced Properties For Use In Oil And Gas Wells - Google Patents

Method Of Creating A Composite Cement With Enhanced Properties For Use In Oil And Gas Wells Download PDF

Info

Publication number
US20200190391A1
US20200190391A1 US16/794,211 US202016794211A US2020190391A1 US 20200190391 A1 US20200190391 A1 US 20200190391A1 US 202016794211 A US202016794211 A US 202016794211A US 2020190391 A1 US2020190391 A1 US 2020190391A1
Authority
US
United States
Prior art keywords
cement
composite cement
rotary
fly ash
particle size
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/794,211
Inventor
Greg Garrison
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US15/075,198 external-priority patent/US20170267583A1/en
Application filed by Individual filed Critical Individual
Priority to US16/794,211 priority Critical patent/US20200190391A1/en
Publication of US20200190391A1 publication Critical patent/US20200190391A1/en
Abandoned legal-status Critical Current

Abstract

This invention relates to using a unique blend of components of a composite cement and subjecting them to a rotary mill process using variably sized and shaped media to reduce the blends' particle size. The invention is novel in that it mills the blended materials together to achieve reduced particle size, increased particle surface area, higher compressive strength and lower permeability. In one embodiment, the invention combines fly ash or other pozzolan material with a cement of any type at varying rations between 1% and 99%. In a further embodiment the invention combines fly ash or other pozzolan material at 60% with a cement of any type at 40%.

Description

    CROSS REFERENCE TO PRIORITY
  • This application claims priority to U.S. patent application Ser. No. 15/075,198, filed on Mar. 31, 2016. The disclosures of the prior application are incorporated by reference herein in its entirety.
  • FIELD OF THE INVENTION
  • The present invention relates to a method of preparing a rotary milled composite cement with increased reactivity and stability in order to improve suitability for certain applications, such as for use in oil and gas wells. The new rotary milled composite cement illustrates broader range of mixing densities, improved inherent fluid loss control and low free fluid control. Set cement properties are improved as well with regard to higher strengths, lower permeability and greater durability as compared to conventional cement or blends currently used to achieve zonal isolation.
  • BACKGROUND OF THE INVENTION
  • Pozzolan cement is a type of hydraulic cement, meaning it reacts with calcium hydroxide and water to form a water resistant cementitious compound. The use of pozzolanic cements dates back to 500-400 BC, when the ancient Greeks used volcanic ashes.
  • The benefits of pozzolan cements and concretes are numerous. First, pozzolan materials are generally cheaper than their alternative, Portland cement. Second, the production of pozzolan cements is generally more environmentally friendly than Portland cements. For example, the production of Portland cement requires large amounts of energy, and as a result, enormous amounts of carbon dioxide are produced, along with numerous other pollutants. Third, the addition of pozzolan tends to increase durability of the end product. For example, Pozzolan concretes have been shown to outperform Portland concretes with regard to sulfate attacks and alkaline silicon reactivity attacks. Finally, many of the artificial pozzolans are industrial byproducts, such as blast furnace slag, the usage of which creates value and environmental savings where otherwise none would be.
  • Despite these advantages, many of the industrial byproduct pozzolans, such as blast furnace slag, are too costly or not always available. Other cheaper and more readily available pozzolans, such as fly ash, are not immediately suitable for use, but must be processed in order to be suitable for use as high quality cement. For instance, it has been shown that milling Class F fly ash to under 45 microns in diameter, results in the production of slag grade 100 or above concrete, as per ASTM C989.
  • With respect to the oil and gas industry, part of the process of preparing a well for further drilling, production or abandonment is cementing the well. Cementing protects and seals the wellbore. Part of the completion process of a prospective production well, cementing is used to seal the annulus after a casing string has been run in a wellbore. Additionally, cementing is used to seal a lost circulation zone, or an area where there is a reduction or absence of flow within the well. Also, cementing is used to plug a well prior to abandoning it.
  • Cementing is performed when a cement slurry is deployed into the well via pumps, displacing the drilling fluids still located within the well, and replacing them with cement. The cement slurry flows to the bottom of the wellbore through the casing, which will eventually be the pipe through which the hydrocarbons flow to the surface. From there it fills in the space between the casing and the actual wellbore, and hardens. This creates a seal so that outside materials cannot enter the well flow, as well as permanently positions the casing in place.
  • Determining the required physical properties of the cement is essential before commencing cementing operations. Special mixers, including hydraulic jet mixers, re-circulating mixers or batch mixers, are typically used to combine dry cement with water to create the wet cement, also known as slurry. Cement used in the well cementing processes can be one of the 5 different API types or even construction grade cement can be utilized.
  • Additives to the cement can include accelerators, which shorten the setting time required for the cement, as well as retarders, which do the opposite and make the cement setting time longer. In order to decrease or increase the density of the cement, lightweight and heavyweight additives are added. Nitrogen can be utilized as a means to reduce the density of the cement. Extenders, such as fly ash and sodium silicates, can be used to replace portions of the cement in an effort to reduce the cost of cementing.
  • The final size of the cement particles has a direct relationship with how much water is required to make a slurry without producing an excess of water at the top of the cement or in pockets as the cement hardens. In other words, the rate at which a cement particle hydrates when exposed to water greatly depends on its size. A small particle reacts much more quickly than a large particle and a very large particle, larger than about 50 μm, probably will never become fully hydrated, even if exposed to enough water. The particle size diameter is therefore critical in controlling the rate at which cements gain strength. The surface area increases inversely as the square of the mean particle diameter, therefore reducing the surface area by a factor of, for example, five increases the area by 25, and because the new surface area is chemically fresh, it is more reactive.
  • Pozzolans consist generally of aspherical particles and spherical particles in the form of aluminio ferro silicate glass beads. Traditional milling techniques simply crush pozzolans, which fails to polish or grind the material. This results in non-active pozzolan particles as compared to rotary milled pozzolan. Using a combination of a rotatory mill with variably sized and shaped media, not only can fly ash be reduced to below 40 microns, but its surface area can be increased from the typical 0.695 m2/g to 1.263 m2/g, thus increasing the reactivity and stability of the resulting fly ash. Furthermore, the treatment described above both reduces the size of the non-spherical particles while at the same time roughing up the spherical particles, thereby increasing the surface area without reducing the flow ability of the pozzolan and results in a concomitant rise in reactivity.
  • One skilled in the art will recognize that despite increased reactivity and stability, fly ash with a particulate size of 40 microns or below is unsuitable in and of itself for use in oil and gas wells. It would be greatly beneficial to reduce the overall size of a composite cement to reduce the particle size of the entire blend.
  • Currently such fly ash is combined with other materials to form a composite cement. Often such added materials are of larger particle sizes than 40 microns, thus reducing the reactivity and slurry properties of the blended concrete. Even if the added particles are separately milled to a mean particle size of less than, for example, 25 microns, it is still possible to further improve the reactivity, stability, and slurry properties. Using the method described below, one can achieve mean particles sizes of 7 microns or below with surface areas of 153 m2/g.
  • SUMMARY OF THE INVENTION
  • This invention relates to using a unique blend of components of a composite cement and subjecting them to a rotary mill process using variably sized and shaped media to reduce the blends' particle size. The invention is novel in that it mills the blended materials together to achieve a particle topsize of 40 microns or less.
  • The invention provides a compelling solution to increasing reactivity, stability, and slurry properties of composite cement. To date, such composite cements are either separately milled to achieve smaller particle sizes, or are of differing particle sizes. One unmet need is for cheaper composite cements, suitable for use in oil and gas wells. One object of the invention is to achieve a particle with a topsize of less than 40 microns in blended cement, thus increasing the reactivity and stability and further improving the slurry properties, without destroying the spherical particles found within the fly ash component.
  • One advantage of the disclosed invention is creating composite cement material that can achieve zonal isolation in an oil and gas well. The disclosed invention utilizes the process of mixing fly ash with lime sources in a rotary mill to make a solid material that when added with water to create a slurry which can be pumped into an oil and gas well to achieve zonal isolation. A rotary milling process suitable for use in this invention is described in U.S. patent application Ser. No. 13/647,838, entitled Process for Treating Fly Ash and a Rotary Mill Therefor, of which the process or processes described in pages 5-24 and FIG. 1-4 are incorporated by reference as if fully set forth herein. This process along with the inventive technique solves a very compelling problem of creating a broad range of slurry densities that can be achieved without changing the solid blend, creating an exceptional set of cement properties across a wide range of densities. The inventive process can utilize the exact formula described or the process can replace the lime substitute with cement of any type or class with concentration ranges of between 1% to 99% The varying ratios will produce different cement properties, all of which will form a slurry when added to water, which can achieve zonal isolation in an oil and gas well.
  • In one embodiment, the invention combines fly ash or other pozzolan material with a cement of any type at varying rations between 1% and 99%. The rotary mill process is implemented to reduce the particle sizes of cement and fly ash components to achieve an average mean size of less than 15 microns. The rotary milled composite cement that results has an exceptional set of cement properties across a wide range of densities, suitable for offshore and land cementing operations.
  • In a further embodiment, the invention combines fly ash or other pozzolan material with a cement of any type a ratio of 60% fly ash or other pozzolan material with a ratio of 40% cement of any type. The rotary mill process is implemented to reduce the particle sizes of cement and fly ash or other pozzolan material components to achieve a rotary milled composite cement mixture with an average mean size of less than 15 microns. The rotary milled composite cement that results has an exceptional set of cement properties across a wide range of densities, suitable for offshore and land cementing operations.
  • In practicing the disclosed invention via the preferred embodiment, to increase the surface area of untreated pozzolan a rotary mill employs different sizes and shapes of ceramic media and treats the pozzolan in a batch process for 30 minutes or longer. In some embodiments the treatment may occur in a batch process for less than 30 minutes. In summary, the surface area of both non-spherical and spherical particles can be increased by grinding the non-spherical particles and by roughing up the surface of the spheres. Both types of particles are treated in the rotary mill using a tailored mix of ceramic media. The mill essentially impacts the particles utilizing the tailored media so as to increase the surface area of the small spherical panicles to activate them while at the same time grinding non-spherical particles to a smaller and smaller diameter to provide a more reactive surface area without destroying the spherical particles of the pozzolan components. Then conventional fluid loss additives, dispersants and viscosity reducers may be added to the cement blends. Furthermore, type III, class III or any other microfine cement may be incorporated in the invention with or without subjecting the cement to the rotary milling process.
  • Table 1 below reflects advantages of an embodiment of the rotary milled composite cement of the invention.
  • TABLE 1
    Composite 12.0 ppg 12.0 ppg 13.8 ppg 13.8 ppg 16.0 ppg 16.0 ppg
    Cement Weight Inventive Conv. Inventive Conv. Inventive Conv.
    and Type Composite Blend Composite Blend Composite Blend
    Thickening Time 6:45 4:55 5:36 7:00 6:33 4:46
    (HR:MIN)
    Temp. (° F.) 180 180 180 180 180 180
    Compressive 1085 675 2317 982 4526 1980
    Strength (psi)
    Permeability .01 .2 .01 .2 .01 .13
    (mD)
  • As can be seen from Table 1 the compressive strength of the inventive rotary milled composite cement is greatly increased in comparison to a similarly weighted conventional cement. Additionally, the permeability of the inventive rotary milled composite cement is greatly reduced in comparison to a similarly weighted conventional cement. The physical properties of the slurry and set rotary milled composite cement are superior to conventional type extended or composite blends using fly ash. This includes all other inert fillers with cement blends that have not been subjected to the patented milling process. The compressive strength, permeability and resistance to chemical attack is drastically improved. The rotary milled composite cement shows a wide range of mixing densities, improved fluid loss control and stability.
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • Embodiments of the invention will now be described, by way of example, with reference to the accompanying drawings, wherein:
  • FIG. 1 is a chart showing a comparison of the mean particle size of a composite cement of the prior art with the mean particle size of a rotary milled composite cement of the invention.
  • FIG. 2 is a chart showing a comparison of the average particle surface area of a composite cement of the prior art with a rotary milled composite cement of the invention.
  • DETAILED DESCRIPTION
  • The following description provides details with reference to the accompanying drawings. It should be understood that the invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein.
  • Referring to FIG. 1, mean particle size results were obtained using a Beckman Coulter LS Particle Size Analyzer. The procedure used in obtaining the data was a standard procedure well known to those of skill in the art. With respect to rotary milled composite cements incorporating the invention the mean particle sizes shown were 9.444, 7.880, 3.088, and 2.657 μm, respectively, and median particle sizes were 7.618, 5.895, 2.396, and 2.122 μm, respectively. On the other hand, an exemplary cement incorporated in the prior art showed a mean particle size of 48.78 μm and a median particle size of 26.37 μm.
  • Referring to FIG. 2, average particle surface area measurements were made using Coulter LS Particle Size Analyzer. The procedure used in obtaining the data was a standard procedure well known to those of skill in the art. With respect to rotary milled cements incorporating the invention, the specific surface area was 18,971 cm2/g, 21,669 cm2/g, 15,316 cm2/g, and 16,032 cm2/g. On the other hand, an exemplary cement incorporated in the prior art exhibited a specific surface area of 8,957 cm2/g.

Claims (4)

1. A method for creating a rotary milled composite cement mixture suitable for use in oil in gas wells comprising:
rotary milling a composite cement mixture comprised of,
40% of cement;
60% of fly ash;
wherein the rotary milled composite cement mixture has:
a maximum particle size of 25 microns;
a mean particle size of less than 12 microns; and
an average particle surface area of at least 14,500 cm2/g.
2. The method of claim 1, further comprising hydrating the rotary milled composite cement mixture to a density of 12 pounds per gallon and having a compressive strength of more than 1,000 pounds per square inch.
3. The method of claim 1 further comprising hydrating the rotary milled composite cement mixture to a density of 13.8 pounds per gallon and having a compressive strength of more than 2,000 pounds per square inch.
4. The method of claim 1, further comprising hydrating the rotary milled composite cement mixture to a density of 16 pounds per gallon and having a compressive strength of more than 4,000 pounds per square inch.
US16/794,211 2016-03-21 2020-02-18 Method Of Creating A Composite Cement With Enhanced Properties For Use In Oil And Gas Wells Abandoned US20200190391A1 (en)