US20170106477A1

US20170106477A1 - Additive manufacturing systems and methods

Info

Publication number: US20170106477A1
Application number: US14/886,535
Authority: US
Inventors: Sergey Mironets; Alexander Staroselsky; Thomas J. Martin
Original assignee: Delavan Inc
Current assignee: Collins Engine Nozzles Inc
Priority date: 2015-10-19
Filing date: 2015-10-19
Publication date: 2017-04-20
Also published as: EP3159083A1; EP3159083B1

Abstract

A method for additively manufacturing an article includes applying energy to a powder to produce a weld pool of molten powder and applying an electromagnetic field to the weld pool to control one or more characteristics of the weld pool. Applying the electromagnetic field can include applying an electric field and/or a magnetic field to the weld pool.

Description

BACKGROUND

1. Field
The present disclosure relates to additive manufacturing, more specifically to techniques and systems for additive manufacturing processes (e.g., powder bed fusion and direct energy deposition for building or repairing metal parts).
2. Description of Related Art
Traditionally, some main criteria for selection of powdered alloys for additive manufacturing are weldability, propensity to form a stable weld pool without keyhole porosity, and absence of defects during the solidification process. In addition to these criteria, other very important technological aspects of the fusion process also need to be considered because they can affect the material microstructure evolution.
There are many challenges in the Powder Bed Fusion and Direct Energy Deposition technologies that prevent additively built components from being implemented for demanding applications. For example the desired grain size and morphology is not controllable with traditional techniques. Grain directionality is typically considered as one of the weakest points of additively build material.
Another challenge is that optimal melting/solidification rates are difficult to achieve. Depending on alloy composition and part cross section the solidification rate difference may produce undesirable phases, microstructure defects, and excessive thermal stresses.
In certain cases, precursor material is difficult to segregate from alloying elements. Material chemical composition uniformity may be altered during the fusion process as a result. Additionally, weld pool melt velocities create strong molten metal turbulence that leads to spattering and melt ejections.
Further, molten metal surface tension affects weld pool geometry. For thin walled structures, controlling the width of weld pool is critical. Weld pool consists of several areas such as molten metal, liquid phase, and solid phase sintering. The total width of the additively built walls varies depending on the size of partially melted and satellite particles that are bonded to the solid state sintered area of the weld pool.
Such conventional methods and systems have generally been considered satisfactory for their intended purpose. However, there is still a need in the art for improved additive manufacturing procedures. The present disclosure provides a solution for this need.

SUMMARY

A method for additively manufacturing an article includes applying energy to a powder to produce a weld pool of molten powder and applying an electromagnetic field to the weld pool to control one or more characteristics of the weld pool. Applying the electromagnetic field can include applying an electric field and/or a magnetic field to the weld pool.
Applying energy to a powder can include applying a laser beam. The laser beam can be moved along a melt direction to melt the powder in a powder bed or along with the deposition of powder injected into the focused laser beam.
In certain embodiments, applying the magnetic field to the weld pool can include applying the magnetic field such that a magnetic induction vector of the magnetic field is oriented at a certain angle (e.g., perpendicular) to the melt direction at the weld pool. Applying the electromagnetic field to control one or more characteristics of the weld pool can include controlling at least one of molten flow and/or convection, grain growth rate, grain morphology, and/or weld pool geometry.
Controlling weld pool geometry can include reducing a cross-sectional area of the weld pool to reduce wall thickness of an additively manufactured article. In certain embodiments, controlling molten flow can include controlling molten flow rate of the molten flow within the weld pool.
In accordance with at least one aspect of this disclosure, a system for additive manufacturing includes a build platform for additively constructing an article thereon, energy applicator configured to heat and melt a powder on the build platform to create a weld pool of molten powder, and an electromagnetic field system configured to selectively apply an electromagnetic field to the weld pool. The electromagnetic field system can be operatively connected to the energy applicator to activate with activation of the energy applicator.
In certain embodiments, the energy applicator can include a laser. The laser can be configured to move relative to a build platform (e.g., mechanically or via a scanning reflector to move the laser beam). In certain embodiments, the electromagnetic field system can be configured to move with the laser (e.g. mechanically or via computer control of electric power, current and voltage to an arrangement of electromagnets).
In certain embodiments, the electromagnetic field system can include a plurality of magnets disposed in a linear pattern (e.g., parallel) relative to the laser beam motion. In certain embodiments, the electromagnetic field system can include a plurality of electromagnets disposed in a circular manner surrounding the laser beam. The plurality of electromagnets can be configured to be activated to create a magnetic field having an induction vector at a controlled angle relative (e.g. perpendicular) to the direction of motion of the laser.
The system can further include a control system operatively connected to activate/deactivate each electromagnet of the plurality of electromagnets as desired to create a predetermined magnetic field strength and orientation. The control system can be configured to activate two diametrically opposed electromagnets at a time.
In accordance with at least one aspect of this disclosure, a laser sintered article includes at least a portion thereof that was exposed to an electromagnetic field when exposed to a laser during manufacture.
These and other features of the systems and methods of the subject disclosure will become more readily apparent to those skilled in the art from the following detailed description taken in conjunction with the drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

So that those skilled in the art to which the subject disclosure appertains will readily understand how to make and use the devices and methods of the subject disclosure without undue experimentation, embodiments thereof will be described in detail herein below with reference to certain figures, wherein:

FIG. 1 is a flow chart of an embodiment of a method in accordance with this disclosure;

FIG. 2 is a schematic diagram of an embodiment of a system in accordance with this disclosure;

FIG. 3 is a cross-sectional view of a weld pool during an additive manufacturing procedure in accordance with this disclosure, showing an induction vector perpendicular to a direction of laser movement.

FIG. 4A is a plan view of an embodiment of an electromagnetic field system in accordance with this disclosure, showing two diametrically opposed electromagnets activated to produce a predetermined field relative to a first laser scan direction;

FIG. 4B is a plan view of an embodiment of an electromagnetic field system in accordance with this disclosure, showing two diametrically opposed electromagnets activated to produce a predetermined field relative to a second laser scan direction; and

FIG. 4C is a plan view of an embodiment of an electromagnetic field system in accordance with this disclosure, showing two diametrically opposed electromagnets activated to produce a predetermined field relative to a third laser scan direction.

FIG. 5 is a perspective schematic view of an embodiment of a system in accordance with this disclosure; showing an electromagnetic field system having two permanent magnets disposed adjacent to a powder bed.

DETAILED DESCRIPTION

Reference will now be made to the drawings wherein like reference numerals identify similar structural features or aspects of the subject disclosure. For purposes of explanation and illustration, and not limitation, an illustrative view of an embodiment of a method in accordance with the disclosure is shown in FIG. 1 and is designated generally by reference character 100. Other embodiments and/or aspects of this disclosure are shown in FIGS. 2-5. The systems and methods described herein can be used to improve manufacturing characteristics and the quality of additively manufactured articles.
Referring to FIGS. 1-3, a method 100 for additively manufacturing an article includes applying 101 energy to a powder 209 to produce a weld pool 313 of molten powder and applying 103 an electromagnetic field to the weld pool 313 to control one or more characteristics of the weld pool 313. Applying the electromagnetic field 103 can include applying an electric field and/or a magnetic field to the weld pool 313. The powder 209 can be any suitable powder (e.g., metal powder) that can be used in additive manufacture. In certain embodiments, the powder 209 can be conductive, but this is not necessary.
Applying energy 101 to a powder can include applying a laser beam 203 a. The laser beam 203 a can be moved in a melt direction 315 along a powder bed (e.g., on build platform 201). It is also contemplated that the laser beam 203 a can be moved along with the deposition of powder 209 injected into the laser beam 203 a instead of using a powder bed.
Referring to FIG. 3, in certain embodiments, applying the magnetic field to the weld pool 313 can include applying the magnetic field such that a magnetic induction vector B of the magnetic field is perpendicular to the melt direction 315 at the weld pool 313. Applying the electromagnetic field to control one or more characteristics of the weld pool 313 can include controlling at least one of molten flow and/or convection, grain growth rate, grain morphology, and/or weld pool geometry. Controlling weld pool 313 geometry can include reducing a cross-sectional area (e.g., as shown by the broken lines in FIG. 3) of the weld pool 313 to reduce wall thickness of an additively manufactured article. Minimizing the width of weld pool is a way to produce thin walls such as those used in the fin plate heat exchangers.
In certain embodiments, controlling molten flow can include controlling molten flow rate of the molten flow within the weld pool 313. Electric current coupled with the magnetic field can create Lorentz force opposing the direction of the weld melt flow direction 315. The applied magnetic field is able to influence the natural convection motion within an electrically neutral molten metal fluid using the phenomenon is known as Hartmann effect, which helps control the melt flow to form more uniform weld pool geometry. The electromagnetic fields can control the flow of the electrically conducting (e.g., metal or metal alloy) weld pool 313 to resist the thermal buoyancy and surface tension driven convection motion and to reduce flow instabilities.
Referring specifically to FIGS. 2-4C, a system 200 for additive manufacturing includes a build platform 201 for additively constructing an article thereon and energy applicator 203 configured to heat and melt a powder 209 on the build platform 201 to create a weld pool 313 of molten powder. In certain embodiments, the energy applicator 203 can include a laser. The laser can be configured to move relative to a build platform 201 (e.g., mechanically and/or via a scanning reflector 207 to move the laser beam 203 a as shown).
The system 200 can also include an electromagnetic field system 205 configured to selectively apply an electromagnetic field to the weld pool 313. In certain embodiments, the electromagnetic field system 205 can be operatively connected to the energy applicator 203 to activate with activation of the energy applicator 203. It is contemplated that the electromagnetic field system 205 can be configured to move with the laser beam 203 a or energy applicator 203, or otherwise modify the electromagnetic field to follow the laser beam 203 a while still applying a desired electromagnetic field to the weld pool 313.
As shown in FIGS. 4A-4C, the electromagnetic field system 205 can include a plurality of electromagnets 205 a, 205 b disposed in a circular manner. It is contemplated that the electromagnets 205 a, 205 b can be disposed in any other suitable arrangement to create a predetermined magnetic field. The plurality of electromagnets 205 a, 205 b can be configured to be activated to create a magnetic field having an induction vector B perpendicular to a direction of motion of the laser (e.g., melt direction 315).
The system 200 can further include a control system 211 operatively connected to activate/deactivate each electromagnet 205 a, 205 b of the plurality of electromagnets as desired to create a predetermined magnetic field. As shown, the control system 211 can be configured to activate two diametrically opposed electromagnets 205 a at a time. Which electromagnets that are active electromagnets 205 a and/or the polarity thereof can be controlled to create a predetermined magnetic field relative to the melt direction 315.
For example, as shown in FIGS. 4A-4C, the active electromagnets 205 a are the ones that are perpendicular to the melt direction. For opposite direction, the polarity can change. Other electromagnets 205 b can remain inactive. Any other suitable scheme and/or timing for activation and/or deactivation of electromagnets 205 a, 205 b is contemplated herein. The produced magnetic fields can be steady and/or oscillatory as desired.
The directions and/or intensities of the applied fields (e.g., electric and/or magnetic) can be optimized to minimize secondary motion and provide the most uniform temperature gradient possible in the weld pool 313. If the melt direction 315 changes, a different pair of electromagnets can activate simultaneously with the change of the melt direction 315 as shown. The scheme of selective activation of magnetic field can depend on any other suitable manufacturing process parameters (e.g., laser scan direction, speed and power to optimally compensate melt convection).
Referring to FIG. 5, another embodiment of an electromagnetic field system 500 is shown disposed aligned with the powder 209 being acted on by laser 203 to produce weld pool 313 The electromagnetic field system 500 can include one or more magnets 550 a, 550 b. As shown, the system 500 can have two or more magnets 550 a, 550 b disposed in an aligned relationship to create a predetermined (e.g., perpendicular) magnetic field at the weld pool 313 relative to the direction of motion of the laser 203. While magnets 550 a, 550 b are shown as permanent magnets, it is contemplated that magnets 550 a, 550 b and include electromagnets.
In certain embodiments, it is contemplated that any suitable permanent magnet or electromagnet can be utilized. Also, it is contemplated that each one or more of the electromagnets and/or permanent magnets can be enhanced with the use of magnetic shells as known in the art. For example, a general property of magnetic fields is that they decay with the distance from their magnetic source. However, as is appreciated by those having ordinary skill in the art, surrounding a magnetic source with a magnetic shell can enhance the field as it moves away from the source. Further, a second magnetic shell can concentrate the captured magnetic energy into a small region, allowing magnetic energy to be transferred and concentrated to the melt pool.
Using the above methods and systems, a laser sintered article (or any other additively manufactured article) can include at least a portion thereof that was exposed to an electromagnetic field when exposed to a laser during manufacture, which can impart advantageous properties to such an article. New properties can be created by manipulation of the phase stability through the application of a strong magnetic field combined with thermal treatment. A strong magnetic field can provide a body force that resists motion in the melt, for example. In addition, an oscillating magnetic field can produce induction heating that which can be used control the melt temperature by localized heating. In the case of the formation of superalloys, the magnetic field can be used to control annealing in order to affect solute formation which can result in in improved creep strength.
Melting and re-solidification of metals and metal alloys can be controlled in direct metal laser melting (DMLM) processes. However, the technique is not limited to metals as it can be applied to any similar process involving conducting melts. Other applications could involve controlled solidification of aluminum melts, molten steel, electropolymers, and electronics materials. Magnetic controlled solidification techniques may also be used to control the physical properties of fiber reinforced composites by controlled the pattern, spacing and orientation of microfibers during curing of the slurry.
An advantage to the herein disclosed methods and systems include thinner/controllable weld pool widths and more uniform weld pool geometry, which can be important for producing thin walled structures and components with high resolution features. Some other advantages include reduced thermal stresses, improved surface finish due to a lowered influence of the Marangoni stresses at the upper surface which minimizes the irregular melt pool cross-section shape; improved grain morphology by formation of the grain structures similar to an equiaxed grain structure; and reduced micro segregation by lowering the melt velocities to prevent strong spattering and melt ejections driven by the dynamics in the weld pool.
The methods and systems of the present disclosure, as described above and shown in the drawings, provide for additive manufacturing techniques and systems which can provide articles with superior material properties and higher resolution. While the apparatus and methods of the subject disclosure have been shown and described with reference to embodiments, those skilled in the art will readily appreciate that changes and/or modifications may be made thereto without departing from the spirit and scope of the subject disclosure.

Claims

What is claimed is:

1. A method for additively manufacturing an article, comprising:

applying energy to a powder to produce a weld pool of molten powder; and

applying an electromagnetic field to the weld pool to control one or more characteristics of the weld pool.

2. The method of claim 1, wherein applying the electromagnetic field includes applying an electric field to the weld pool.

3. The method of claim 1, wherein applying the electromagnetic field includes applying a magnetic field to the weld pool.

4. The method of claim 1, wherein applying energy to a powder includes applying a laser beam.

5. The method of claim 3, wherein applying energy to a powder includes moving the laser beam along a melt direction to melt the powder in a powder bed or along with the deposition of powder injected into the laser beam.

6. The method of claim 5, wherein applying the magnetic field to the weld pool includes applying the magnetic field such that a magnetic induction vector of the magnetic field is perpendicular to the melt direction at the weld pool.

7. The method of claim 1, wherein applying the electromagnetic field to control one or more characteristics of the weld pool includes controlling at least one of molten flow and/or convection, grain growth rate, grain morphology, and/or weld pool geometry.

8. The method of claim 7, wherein controlling weld pool geometry includes reducing a cross-sectional area of the weld pool to reduce wall thickness of an additively manufactured article.

9. The method of claim 7, wherein controlling molten flow includes controlling molten flow rate of the molten flow within the weld pool.

10. A system for additive manufacturing, comprising;

a build platform for additively constructing an article thereon;

energy applicator configured to heat and melt a powder on the build platform to create a weld pool of molten powder; and

an electromagnetic field system configured to selectively apply an electromagnetic field to the weld pool.

11. The system of claim 10, wherein the electromagnetic field system is operatively connected to the energy applicator to activate with activation of the energy applicator.

12. The system of claim 10, wherein the energy applicator includes a laser.

13. The system of claim 12, wherein the laser is configured to move relative to a build platform.

14. The system of claim 13, wherein the electromagnetic field system is configured to move with the laser.

15. The system of claim 13, wherein the electromagnetic field system includes a plurality of electromagnets disposed in a circular manner.

16. The system of claim 15, wherein the plurality of electromagnets are configured to be activated to create a magnetic field having an induction vector perpendicular to a direction of motion of the laser.

17. The system of claim 15, further comprising a control system operatively connected to activate/deactivate each electromagnet of the plurality of electromagnets as desired to create a predetermined magnetic field strength and/or orientation.

18. The system of claim 17, wherein the control system is configured to activate two diametrically opposed electromagnets at a time.

19. A laser sintered article having at least a portion thereof that was exposed to an electromagnetic field when exposed to a laser during manufacture.