US20150096887A1 - Electrodes containing iridium nanoparticles for the electrolytic production of oxygen from water - Google Patents
Electrodes containing iridium nanoparticles for the electrolytic production of oxygen from water Download PDFInfo
- Publication number
- US20150096887A1 US20150096887A1 US14/328,635 US201414328635A US2015096887A1 US 20150096887 A1 US20150096887 A1 US 20150096887A1 US 201414328635 A US201414328635 A US 201414328635A US 2015096887 A1 US2015096887 A1 US 2015096887A1
- Authority
- US
- United States
- Prior art keywords
- iridium
- electrode
- nanoparticles
- iridium nanoparticles
- hydride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Electrodes employing as active material iridium nanoparticles synthesized by a novel route are provided. The nanoparticle synthesis is facile and reproducible, and provides iridium nanoparticles of very small dimension and high purity for a wide range of metals. The electrodes utilizing these nanoparticles have excellent efficiency catalyzing the electrolytic production of oxygen from water.
Description
- This application is a continuation-in-part of application Ser. Nos. 14/046,081 and 14/046,120, filed 4 Oct. 2013, and a continuation-in-part of application Ser. No. 14/219,836, filed 19 Mar. 2014, the specifications of which is incorporated herein by reference.
- The present invention relates in general to iridium nanoparticles synthesized by a novel route and their use as catalysts of electrochemical water splitting.
- Electrochemical oxidation/reduction of water, or “water splitting”—conversion of H2O to H2 and O2 by application of electrical potential across electrodes of a cell—can in theory be a useful approach to produce hydrogen and oxygen fuels. As a practical matter, such an approach is severely limited by the fact that energy input generally exceeds the energy obtainable from the produced fuels. Electrode materials which increase the quantity of product at a given voltage can potentially overcome this challenge.
- Iridium metal and/or oxide have been used as an electrode active material for the electrolytic production of oxygen gas from water. The efficiency of such an electrode can be improved through the use of nanoparticulate iridium. Nanoparticulate iridium of high quality is difficult and expensive to obtain in production scale quantity.
- Electrodes and iridium nanoparticles synthesized by a novel route are provided.
- In an embodiment, an electrode comprising iridium nanoparticles is disclosed, wherein the iridium nanoparticles are synthesized by a method comprising adding surfactant to a reagent complex according to Formula I:
-
Ir0·Xy I, - wherein Ir0 is zero-valent iridium, X is a hydride, and y is an integral or fractional value greater than zero. The electrode which contains iridium nanoparticles synthesized by this method has excellent ability to electrolytically produce oxygen from water.
- Various aspects and advantages of the invention will become apparent and more readily appreciated from the following description of the embodiments taken in conjunction with the accompanying drawings, of which:
-
FIG. 1 is first cycle voltammograms of electrochemical cells having iridium-containing electrodes where the iridium is either directly from a commercial source or is nanoparticulate iridium synthesized by a disclosed method; -
FIG. 2 is second cycle voltammograms of the electrochemical cells ofFIG. 1 ; and -
FIG. 3 is tenth cycle voltammograms of the electrochemical cells ofFIG. 1 . - The present disclosure describes iridium nanoparticles suitable for use as active material in an electrode of an electrochemical cell. The disclosure also describes the electrodes which include such nanoparticles. The iridium nanoparticles are synthesized by a mechanochemical method which is facile, easily scalable to industrial needs, and produces pure iridium nanoparticles free of contaminants to the low nanometer(nm) scale.
- The iridium nanoparticles and electrodes of the present disclosure can be useful in the electrochemical production of oxygen gas from water.
- A reagent complex for the synthesis of metallic iridium nanoparticles is described by Formula I:
-
Ir0·Xy I, - wherein Ir0 is zero-valent iridium metal and X is a hydride. The subscript y can be any positive fractional or integral value. In some cases, y can be a value from 1 to 4, inclusive. In some cases, y can be a value from 1 to 2, inclusive. In some cases, y will be approximately 2.
- The hydride employed in Formula I can be a solid metal hydride (e.g. NaH, or IrH2), metalloid hydride (e.g. BH3), complex metal hydride (e.g. LiAlH4), or salt metalloid hydride also referred to as a salt hydride (e.g. LiBH4). In some examples the hydride will be LiBH4, yielding a reagent complex having the formula Ir·LiBH4. In some specific examples, the reagent complex will have the formula Ir·(LiBH4)2. It is to be appreciated that the term hydride as used herein can also encompass a corresponding deuteride or tritide.
- The reagent complex can be a complex of individual molecular entities, such as a single metal atom in oxidation state zero in complex with one or more hydride molecules. Alternatively the complex described by Formula I can exist as a molecular cluster, such as a cluster of metal atoms in oxidation state zero interspersed with hydride molecules, or a cluster of metal atoms in oxidation state zero, the cluster surface-coated with hydride molecules or the salt hydride interspersed throughout the cluster.
- One process by which a reagent complex according to Formula I can be obtained includes a step of ball-milling a mixture which includes both a hydride and a preparation composed of iridium. The preparation composed of iridium can be derived from any source of metallic iridium, but will typically be a source of metallic iridium that contains zero-valent iridium at greater than 50% purity and at a high surface-area-to-mass ratio. For example, a suitable preparation composed of iridium would be an iridium powder comparable to commercial grade iridium powder.
- The ball-milling step can be performed with any type of ball mill, such as a planetary ball mill, and with any type of ball-milling media, such as stainless steel beads. It will typically be preferable to perform the ball-milling step in an inert environment, such as in a glove box under vacuum or under argon.
- The reagent complex described above and by Formula I can be used in a method for synthesizing iridium nanoparticles. The method for synthesizing iridium nanoparticles includes the step of adding surfactant to a reagent complex according to Formula I, the reagent complex being in all particulars as described above. In some examples of the method for synthesizing iridium nanoparticles, the reagent complex can be in suspended contact with a solvent or solvent system. Suitable solvents in which the reagent complex can be suspended during addition of surfactant will typically be solvents in which the suspended reagent complex is stable for at least an hour. In some examples, such suitable solvents can include ethereal solvents or aprotic solvents. In some particular examples, such a suitable solvent will be THF. In some instances, it may be preferred to perform the method for synthesizing iridium nanoparticles in an inert environment, such as in a glove-box under vacuum or argon.
- In some variations of the method for synthesizing iridium nanoparticles, the surfactant can be in suspended or solvated contact with a solvent or solvent system. In different variations wherein the reagent complex is in suspended contact with a solvent or solvent system and the surfactant is suspended or dissolved in a solvent or solvent system, the reagent complex can be in suspended contact with a solvent or solvent system of the same or different composition as compared to the solvent or solvent system in which the surfactant is dissolved or suspended.
- In some variations of the method for synthesizing iridium nanoparticles, the reagent complex can be combined with surfactant in the absence of solvent. In some such cases a solvent or solvent system can be added subsequent to such combination. In other aspects, surfactant which is not suspended or dissolved in a solvent or solvent system can be added to a reagent complex which itself is in suspended contact with a solvent or solvent system. In yet other aspects, surfactant which is suspended or dissolved in a solvent or solvent system can be added to a reagent complex which is not in suspended contact with a solvent or solvent system.
- The surfactant utilized in the method for synthesizing iridium nanoparticles can be any known in the art. Usable surfactants can include nonionic, cationic, anionic, amphoteric, zwitterionic, and polymeric surfactants and combinations thereof. Such surfactants typically have a lipophilic moiety that is hydrocarbon based, organosilane based, or fluorocarbon based. Without implying limitation, examples of types of surfactants which can be suitable include alkyl sulfates and sulfonates, petroleum and lignin sulfonates, phosphate esters, sulfosuccinate esters, carboxylates, alcohols, ethoxylated alcohols and alkylphenols, fatty acid esters, ethoxylated acids, alkanolamides, ethoxylated amines, amine oxides, alkyl amines, nitriles, quaternary ammonium salts, carboxybetaines, sulfobetaines, or polymeric surfactants.
- In some instances the surfactant employed in the method for synthesizing iridium nanoparticles will be one capable of oxidizing, protonating, or otherwise covalently modifying the hydride incorporated in the reagent complex. In some variations the surfactant can be a carboxylate, nitrile, or amine. In some examples the surfactant can be octylamine.
- Also disclosed is an electrode suitable for use in an electrochemical cell. The electrode includes as active material iridium nanoparticles. The iridium nanoparticles included in the electrode have an average maximum dimension less than 100 nm. In some instances, the iridium nanoparticles included in the electrode have an average maximum dimension of 10 nm or less. In some instances, the iridium nanoparticles included in the electrode have an average maximum dimension of 5 nm or less. The iridium nanoparticles included in the electrode are, in some variations, generally of uniform size. The iridium nanoparticles included in the electrode can be obtained by the process for synthesizing iridium nanoparticles, as disclosed above.
- In some instances, an electrode of the present disclosure can, when deployed in an appropriately configured electrochemical cell, catalyze the half-cell reaction:
- In some such instances, as illustrated below, the disclosed electrode will catalyze the half-cell reaction with greater efficiency than does an otherwise identical electrode having iridium from a different source
- It will be appreciated that the disclosed electrode can, include additional structural substrates, binding agents, and/or other active materials. In a non-limiting example, a co-suspension in THF of iridium nanoparticles synthesized by the disclosed method, acid-treated carbon black, and fluorinated sulfonic acid polymer were sonicated and cast on a glassy carbon electrode. For comparison purposes, an otherwise identical electrode was prepared in which iridium nanoparticles synthesized by the disclosed method were replaced with commercially obtained iridium powder.
- Each of the two electrode types, disclosed and comparative, was deployed in an electrochemical cell opposite a platinum electrode and with oxygenated sulfuric acid electrolyte. Each of the cell types was subjected to voltammetric analysis, as shown in
FIGS. 1-3 .FIGS. 1 , 2, and 3 show first cycle, second cycle, and tenth cycle voltammetric curves, respectively. In each case, the solid line represents data for the electrochemical cell having the disclosed electrode with iridium nanoparticles synthesized by the disclosed method. The dotted line represents data for the electrochemical cell having the comparative electrode with commercially obtained iridium powder. - Comparison of
FIGS. 1-3 indicates that the disclosed electrode is highly consistent over multiple cycles, generating similar current density across all voltages in cycle ten as compared to cycle one. Of significance, each ofFIGS. 1-3 shows that the disclosed electrode has superior electrochemical performance relative to the comparative electrode. At operative potentials, the electrode having iridium nanoparticles synthesized by the disclosed method generates greater current density, and hence greater quantity of oxygen, than does the electrode having commercially obtained iridium. - Various aspects of the present disclosure are further illustrated with respect to the following Examples. It is to be understood that these Examples are provided to illustrate specific embodiments of the present disclosure and should not be construed as limiting the scope of the present disclosure in or to any particular aspect.
- To a stainless steel ball mill jar is added 2.0 g of iridium powder (−325 mesh) and 0.453 g lithium borohydride powder. Stainless steel balls are added to the jar as well. The mixture is subjected to 250 rpm for 4 hours, under argon, in a planetary ball mill. 0.750 g of the resulting Ir(LiBH4)2 powder is then added to 10 mL THF, along with 4.110 g octylamine. This mixture is stirred, under argon, for 4 hours. The nanoparticle product is then collected and the reaction solution decanted away. The isolated nanoparticle powder is washed with ethanol, then ethanol/water, and finally acetone before being dried.
- Iridium electrodes were prepared by drop casting a catalyst ink onto a glassy carbon electrode. The catalyst ink was first prepared by sonicating a mixture of catalyst, acid-treated carbon black (CB, Alfa Aesar), Na+-exchanged Nafion® solution (5 wt %, Ion Power) with tetrahydofuran (THF, Sigma-Aldrich). After drop casting, the catalyst film was allowed to dry at room temperature overnight and the final composition of the film was expected to be 100, 20, and 20 μg/cm2 for Iridium nanoparticles, CB, and Nafion®, respectively.
- Electrochemistry was used to determine the catalytic ability of the catalyst. Cyclic voltammetry experiments were performed in 1M H2SO4 electrolyte that was saturated with O2. Scans were cycles between 1V vs. RHE (reversible hydrogen electrode) and 1.6 V vs. RHE a total of 10 times at 10 mV/s. The catalysts-containing working electrode was rotated at 1600 rpm. Counter electrode used in the cell was a platinum wire separated from the cell using a glass frit. All potentials were measured versus a Ag/AgCl electrode but the potentials were converted to RHE for ease of understanding.
- The foregoing description relates to what are presently considered to be the most practical embodiments. It is to be understood, however, that the disclosure is not to be limited to these embodiments but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims, which scope is to be accorded the broadest interpretation so as to encompass all such modifications and equivalent structures as is permitted under the law.
Claims (7)
1. An electrode comprising iridium nanoparticles, the iridium nanoparticles synthesized by a method comprising:
adding surfactant to a reagent complex according to Formula I,
Ir0·Xy I,
Ir0·Xy I,
wherein Ir0 is zero-valent iridium, X is a hydride, and y is an integral or fractional value greater than zero.
2. The electrode of claim 1 wherein the reagent complex is obtained by a process that includes a step of:
ball milling a mixture that includes a hydride and a preparation composed of iridium.
3. The electrode of claim 1 wherein the hydride is lithium borohydride.
4. The electrode of claim 1 wherein the iridium nanoparticles have an average maximum dimension less than 100 nm.
5. The electrode of claim 1 wherein the iridium nanoparticles have an average maximum dimension less than 10 nm.
6. The electrode of claim 1 wherein the iridium nanoparticles have an average maximum dimension less than 5 nm.