US20140357422A1

US20140357422A1 - Thermoplastic multi-layer golf ball

Info

Publication number: US20140357422A1
Application number: US13/906,393
Authority: US
Inventors: Jun Ichinose
Original assignee: Nike International Ltd
Current assignee: Nike International Ltd
Priority date: 2013-05-31
Filing date: 2013-05-31
Publication date: 2014-12-04
Also published as: WO2014193778A1

Abstract

A thermoplastic multi-layer golf ball has a thermoplastic core center, a thermoplastic core layer, and an inner cover layer and outer cover layer each including a thermoplastic polyurethane. The core center has a diameter of about 5-20 mm and a first flexural modulus of ≦about 8,000 psi. The core layer has a diameter of about 28-40 mm, a thickness of about 4-10 mm, a second flexural modulus of ≦about 15,000 psi and greater than the first flexural modulus, a 10-130 kg compression deformation of about 2.6-4.0 mm, and a surface hardness greater than the core center's surface hardness. The outer cover layer has a 10-130 kg compression deformation of about 2.3-3.2 mm and a surface hardness that is less than that of the inner cover layer. The difference between the core center's specific gravity and the core layer's specific gravity is ≦about 0.1 g/cm³.

Description

FIELD OF THE INVENTION

The invention concerns multi-layer golf balls with small core centers.

BACKGROUND

This section provides information helpful in understanding the invention but that is not necessarily prior art.
Golf ball core and cover layers are typically constructed with polymer compositions including, for example, polybutadiene rubber, polyurethanes, polyamides, ionomers, and blends of such polymers. Ionomers, particularly ethylene-based ionomers, are a preferred group of polymers for golf ball layers because of their toughness, durability, and wide range of hardness values.
Golf ball compositions comprising highly neutralized acid polymers are known. For example, U.S. Pat. No. 7,375,151, the entire disclosure of which is incorporated herein by reference, discloses a highly-resilient thermoplastic ionomer resin composition comprising (a) melt-processible, ethylene acid copolymer; (b) aliphatic, mono-functional organic acid or its salt; (c) a thermoplastic resin; (d) a cation source; and (e) optionally, a filler. The ionomer resin may be neutralized to greater than 90% of all the acid groups present and remain melt-processible. The patent discloses using the highly-resilient thermoplastic composition in one-piece, two-piece, three-piece, and multi-layered golf balls.
Construction of a thermoplastic ball, in which all layers are thermoplastic, must provide performance characteristics. While various uses for highly neutralized acid polymers in golf balls have been discovered, there is a need to improve golf ball materials using highly neutralized acid polymers or other thermoplastic polymers to particular golf ball constructions having desirable spin, feel, and COR properties.

SUMMARY OF THE DISCLOSURE

This section provides a general summary of the disclosure and is not comprehensive of its full scope or all of the disclosed features.
Disclosed is a thermoplastic multi-layer golf ball with a core center including a first thermoplastic material, a core layer outward from the core center including a second thermoplastic material, an inner cover layer outward from the core layer including a thermoplastic polyurethane, and an outer cover layer on the surface of the ball including a thermoplastic polyurethane that may be the same as or different from the thermoplastic polyurethane of the inner cover layer. The core center has a diameter of from about 5 mm to about 20 mm, a first flexural modulus of up to about 8,000 psi and a surface hardness. The core layer has a diameter of from about 28 mm to about 40 mm, a thickness of from about 4 mm to about 10 mm, a second flexural modulus of up to about 15,000 psi that is greater than the first flexural modulus, a 10-130 kg compression deformation of from about 2.6 mm to about 4.0 mm, and a surface hardness greater than the surface hardness of the core center. The outer cover layer has a 10-130 kg compression deformation of from about 2.3 mm to about 3.2 mm, and a surface hardness that is less than the surface hardness of the inner cover layer. The difference between the specific gravity of the core center and the specific gravity of the core layer is not more than about 0.1 g/cm³. The resulting golf ball has a desirable soft feel when hit, and the golf ball has long distance.
In various embodiments, the first thermoplastic material of the core center, the second thermoplastic material of the core layer, or each of these includes an ionomer resin, which may be the same or different from one another when both contain an ionomer resin and which may be made using, or each independently may be made using a monomeric organic acid or salt of such an acid and may be neutralized from at least about 40% to about 100%, preferably from at least about 90% to about 100%. The polymeric portion of the thermoplastic material or materials may essentially be the ionomer resin.
The golf ball has a multi-layer core including a core center as an innermost core part and one or more “core layers” outward from and enclosing the center. A “core layer” for this invention is a golf ball layer lying between the center and the two outermost layers of the golf ball. The two outermost golf ball layers for purposes of describing this invention will be referred to as the “inner cover layer” and the “outer cover layer,” with the outer cover layer being the outmost structural layer of the golf ball and the inner cover layer being located immediately inward of the outer cover layer. Coating layers (whether paint layers or clear coating layers) are not considered to be structural layers.
Hardness is measured according to ASTM D2240, but measured on a curved surface of the core center and core layer or on a land area of a curved surface of the cover. It is understood in this technical field of art that the hardness measured in this way often varies from the hardness of a flat slab or button of material in a non-linear way that cannot be correlated, for example because of effects of underlying layers. Because of the curved surface, care must be taken to center the golf ball or golf ball subassembly under the durometer indentor before a surface hardness reading is obtained and to measure an even area, e.g. on the dimpled surface cover measurements are taken on a land (fret) area between dimples. Specific gravity is measured according to ASTM D792. Flexural modulus is measured according to ASTM D790. Specific gravity is measured according to ASTM D792. “Compression deformation” in the deformation amount in millimeters under a compressive load of 130 kg minus the deformation amount in millimeters under a compressive load of 10 kg. The amount of deformation of the ball under a force of 10 kg is measured, then the force is increased to 130 kg and the amount of deformation under the new force of 130 kg is measured. The deformation amount at 10 kg is subtracted from the deformation amount at 130 kg to give the 10-130 kg compression deformation, which is reported in millimeters. “Coefficient of restitution” or COR in the present invention is measured generally according to the following procedure: a golf ball is fired by an air cannon at an initial velocity of 40 msec, and a speed monitoring device is located over a distance of 0.6 to 0.9 meters from the cannon. After striking a steel plate positioned about 1.2 meters away from the air cannon, the test object rebounds through the speed-monitoring device. The return velocity divided by the initial velocity is the COR.
“A,” “an,” “the,” “at least one,” and “one or more” are used interchangeably to indicate that at least one of the item is present; a plurality of such items may be present unless the context clearly indicates otherwise. All numerical values of parameters (e.g., of quantities or conditions) in this specification, including the appended claims, are to be understood as being modified in all instances by the term “about” whether or not “about” actually appears before the numerical value. “About” indicates that the stated numerical value allows some slight imprecision (with some approach to exactness in the value; approximately or reasonably close to the value; nearly). If the imprecision provided by “about” is not otherwise understood in the art with this ordinary meaning, then “about” as used herein indicates at least variations that may arise from ordinary methods of measuring and using such parameters. In addition, disclosure of ranges includes disclosure of all values and further divided ranges within the entire range. Each value within a range and the endpoints of a range are hereby all disclosed as separate embodiment. In this description of the invention, for convenience, “polymer” and “resin” are used interchangeably to encompass resins, oligomers, and polymers. The terms “comprises,” “comprising,” “including,” and “having,” are inclusive and therefore specify the presence of stated items, but do not preclude the presence of other items. As used in this specification, the term “or” includes any and all combinations of one or more of the listed items. When the terms first, second, third, etc. are used to differentiate various items from each other, these designations are merely for convenience and do not limit the items.

BRIEF DESCRIPTION OF THE DRAWINGS

The FIGURE is a partial cross-sectional view of an embodiment of a multi-layer golf ball that illustrates some aspects of the disclosed technology. The parts of the FIGURE are not necessarily to scale.

DETAILED DESCRIPTION

A detailed description of exemplary, nonlimiting embodiments follows.
As shown in the FIGURE, a multi-layer golf ball 100 has a core center 110 with a surface 115, a core layer 120 that is radially outward from the core center 110 and has a surface 125, an inner cover layer 130 that has a surface 135 and an outer cover layer 140 that forms the outermost layer of the golf ball 100 and has a surface 145. Each of the core center, the core layer, the inner cover layer, and the outer cover layer includes a thermoplastic material.
The golf ball has a multi-layer core including at least a core center made of a first thermoplastic material and a core layer disposed radially outward from and enclosing the core center made of a second thermoplastic material and a multi-layer cover including at least an inner cover layer and an outer cover layer, both of which independently include a thermoplastic polyurethane, preferably a thermoplastic polyurethane elastomer. Each of the first and second thermoplastic materials has at least one thermoplastic polymer, and in preferred embodiments each includes at least one thermoplastic elastomer. Each of the first and second thermoplastic materials as well as the cover layers may also include one or more non-elastomeric polymers, plasticizers, fillers, and customary additives.
The surface hardnesses, compression deformation and flexural modulus properties, and specific gravities of the golf ball layers are determined by a combination of factors, including the nature and amount of thermoplastic elastomers in the thermoplastic materials, the presence, nature, and amount of other polymeric materials or plasticizers, and the presence, nature, and amount of fillers.
Each of the first and second thermoplastic materials generally includes at least one thermoplastic elastomer. Nonlimiting examples of suitable thermoplastic elastomers that can be used include metal cation ionomers of addition copolymers of ethylenically unsaturated acids, (“ionomer resins”), metallocene-catalyzed block copolymers of ethylene and α-olefins having 4 to about 8 carbon atoms, thermoplastic polyamide elastomers (such as polyether block polyamides), thermoplastic polyester elastomers, thermoplastic styrene block copolymer elastomers such as poly(styrene-butadiene-styrene), poly(styrene-ethylene-co-butylene-styrene), and poly(styrene-isoprene-styrene), thermoplastic polyurethane elastomers, thermoplastic polyurea elastomers, and dynamic vulcanizates of rubbers in these thermoplastic elastomers and in other thermoplastic matrix polymers. The inner cover layer and the outer cover layer each include a thermoplastic polyurethane, which is preferably an elastomer, and each may include other polymers or elastomers.
Ionomer resins, which are metal cation ionomers of addition copolymers of ethylenically unsaturated acids, are preferably alpha olefin, particularly ethylene, copolymers with C_3-8α,β-ethylenically unsaturated carboxylic acids, particularly acrylic or methacrylic acid. The copolymers may also contain a softening monomer such as an alkyl acrylate or methacrylate, for example a C₁to C₈alkyl acrylate or methacrylate ester. The α,β-ethylenically unsaturated carboxylic acid monomer may be from about 4 weight percent or about 6 weight percent or about 8 weight percent up to about 20 weight percent or up to about 35 weight percent of the copolymer, and the softening monomer, when present, is preferably present in a finite amount, preferably at least about 5 weight percent or at least about 11 weight percent, up to about 23 weight percent or up to about 25 weight percent or up to about 50 weight percent of the copolymer.
Nonlimiting specific examples of acid-containing ethylene copolymers include copolymers of ethylene/acrylic acid/n-butyl acrylate, ethylene/methacrylic acid/n-butyl acrylate, ethylene/methacrylic acid/isobutyl acrylate, ethylene/acrylic acid/isobutyl acrylate, ethylene/methacrylic acid/n-butyl methacrylate, ethylene/acrylic acid/methyl methacrylate, ethylene/acrylic acid/methyl acrylate, ethylene/methacrylic acid/methyl acrylate, ethylene/methacrylic acid/methyl methacrylate, and ethylene/acrylic acid/n-butyl methacrylate. Preferred acid-containing ethylene copolymers include copolymers of ethylene/methacrylic acid/n-butyl acrylate, ethylene/acrylic acid/n-butyl acrylate, ethylene/methacrylic acid/methyl acrylate, ethylene/acrylic acid/ethyl acrylate, ethylene/methacrylic acid/ethyl acrylate, and ethylene/acrylic acid/methyl acrylate. In various embodiments the most preferred acid-containing ethylene copolymers include ethylene/(meth)acrylic acid/n-butyl acrylate, ethylene/(meth)acrylic acid/ethyl acrylate, and ethylene/(meth)acrylic acid/methyl acrylate copolymers.
The ionomer resin may be a high acid ionomer resin. In general, ionomers prepared by neutralizing acid copolymers including at least about 16 weight % of copolymerized acid residues based on the total weight of the unneutralized ethylene acid copolymer are considered “high acid” ionomers. In these high modulus ionomers, the acid monomer, particularly acrylic or methacrylic acid, is present in about 16 to about 35 weight %. In various embodiments, the copolymerized carboxylic acid may be from about 16 weight %, or about 17 weight % or about 18.5 weight % or about 20 weight % up to about 21.5 weight % or up to about 25 weight % or up to about 30 weight % or up to about 35 weight % of the unneutralized copolymer. A high acid monomer may be combined with a “low acid” monomer in which the copolymerized carboxylic acid is less than 16 weight % of the unneutralized copolymer.
The acid moiety in the ethylene acid copolymer is neutralized by any metal cation. Suitable preferred cations include lithium, sodium, potassium, magnesium, calcium, barium, lead, tin, zinc, aluminum, or a combination of these cations; in various embodiments alkali metal, alkaline earth metal, or zinc cations are particularly preferred. In various embodiments, the acid groups of the ionomer may be neutralized from about 10% or from about 20% or from about 30% or from about 40% to about 60% or to about 70% or to about 75% or to about 80% or to about 90%.
A sufficiently high molecular weight, monomeric organic acid or salt of such an organic acid may be added to the acid copolymer or ionomer so that the acid copolymer or ionomer can be neutralized, without losing processability, to a level above the level that would cause the ionomer alone to become non-melt-processable. The high-molecular weight, monomeric organic acid its salt may be added to the ethylene-unsaturated acid copolymers before they are neutralized or after they are optionally partially neutralized to a level between about 1 and about 100%, provided that the level of neutralization is such that the resulting ionomer remains melt-processable. In generally, when the high-molecular weight, monomeric organic acid is included the acid groups of the copolymer may be neutralized from at least about 40 to about 100%, preferably from at least about 90% to about 100%, and most preferably 100% without losing processability. Such high neutralization, particularly to levels greater than 80%, greater than 90% or greater than 95% or most preferably 100%, without loss of processability can be done by (a) melt-blending the ethylene α,β-ethylenically unsaturated carboxylic acid copolymer or a melt-processable salt of the copolymer with an organic acid or a salt of organic acid, and (b) adding a sufficient amount of a cation source up to 110% of the amount needed to neutralize the total acid in the copolymer or ionomer and organic acid or salt to the desired level to increase the level of neutralization of all the acid moieties in the mixture preferably to greater than 90%, preferably greater than 95%, or preferably to 100%. To obtain 100% neutralization, it is preferred to add a slight excess of up to 110% of cation source over the amount stoichiometrically required to obtain the 100% neutralization.
The high-molecular weight, monomeric saturated or unsaturated acid may have from 8 or 12 or 18 carbon atoms to less than 36 carbon atoms. Nonlimiting suitable examples of the high-molecular weight, monomeric saturated or unsaturated organic acids include stearic, behenic, erucic, oleic, and linoleic acids and their salts, particularly the barium, lithium, sodium, zinc, bismuth, chromium, cobalt, copper, potassium, strontium, titanium, tungsten, magnesium, or calcium salts of these fatty acids. These may be used in combinations.
In various preferred embodiments, one of the first thermoplastic material of the core center and the second thermoplastic material of the core layer includes an ionomer resin, and each of the first and second thermoplastic materials may independently include an ionomer resin, which may be the same as or different from one another. The ionomer resins used in the first thermoplastic material or second thermoplastic materials may be prepared using a monomeric organic acid or salt of such as acid as has been described, and may be neutralized from at least about 40% to about 100% or one of the other neutralization ranges mentioned above, especially at least about neutralized from at least about 90% to about 100%, more preferably neutralized from at least about 95% to about 100%, and particularly preferably 100% neutralized.
Thermoplastic polyolefin elastomers may also be used in the thermoplastic materials of the golf ball. These are metallocene-catalyzed block copolymers of ethylene and α-olefins having 4 to about 8 carbon atoms that are prepared by single-site metallocene catalysis, for example in a high pressure process in the presence of a catalyst system comprising a cyclopentadienyl-transition metal compound and an alumoxane. Nonlimiting examples of the α-olefin softening comonomer include hexane-1 or octene-1; octene-1 is a preferred comonomer to use. These materials are commercially available, for example, from ExxonMobil under the tradename Exact™ and from the Dow Chemical Company under the tradename Engage™.
In various preferred embodiments, one of the first thermoplastic material of the core center and the second thermoplastic material of the core layer includes both an ionomer resin and a thermoplastic polyolefin elastomer. The ionomer resin may be made using a monomeric organic acid or salt thereof with the ionomer resin is neutralized from at least about 40% to about 100% or preferably from at least about 90% or 95% to about 100%, and particularly preferably 100%. In various embodiment, the thermoplastic material includes a combination of a metal ionomer of a copolymer of ethylene and at least one of acrylic acid and methacrylic acid, a metallocene-catalyzed copolymer of ethylene and an α-olefin having 4 to about 8 carbon atoms, and a metal salt of an unsaturated fatty acid. This material may be prepared as described in Statz et al., U.S. Pat. No. 7,375,151 or as described in Kennedy, “Process for Making Thermoplastic Golf Ball Material and Golf Ball with Thermoplastic Material, U.S. patent application Ser. No. 13/825,112, filed 15 Mar. 2013, the entire contents of both being incorporated herein by reference.
Suitable thermoplastic styrene block copolymer elastomers that may be used in the thermoplastic materials of the golf ball include poly(styrene-butadiene-styrene), poly(styrene-ethylene-co-butylene-styrene), poly(styrene-isoprene-styrene), and poly(styrene-ethylene-co-propylene) copolymers. These styrenic block copolymers may be prepared by living anionic polymerization with sequential addition of styrene and the diene forming the soft block, for example using butyl lithium as initiator. Thermoplastic styrene block copolymer elastomers are commercially available, for example, under the trademark Kraton™ sold by Kraton Polymers U.S. LLC, Houston, Tex. Other such elastomers may be made as block copolymers by using other polymerizable, hard, non-rubber monomers in place of the styrene, including meth(acrylate) esters such as methyl methacrylate and cyclohexyl methacrylate, and other vinyl arylenes, such as alkyl styrenes.
The inner cover layer and the outer cover layer each include a thermoplastic polyurethane, especially a thermoplastic polyurethane elastomer. Thermoplastic polyurethane elastomers such as thermoplastic polyester-polyurethanes, polyether-polyurethanes, and polycarbonate-polyurethanes may be used including, without limitation, polyurethanes polymerized using as polymeric diol reactants polyethers and polyesters including polycaprolactone polyesters. These polymeric diol-based polyurethanes are prepared by reaction of the polymeric diol (polyester diol, polyether diol, polycaprolactone diol, polytetrahydrofuran diol, or polycarbonate diol), one or more polyisocyanates, and, optionally, one or more chain extension compounds. Chain extension compounds, as the term is being used, are compounds having two or more functional groups reactive with isocyanate groups, such as the diols, amino alcohols, and diamines. Preferably the polymeric diol-based polyurethane is substantially linear (i.e., substantially all of the reactants are difunctional).
Diisocyanates used in making the polyurethane elastomers may be aromatic or aliphatic. Useful diisocyanate compounds used to prepare thermoplastic polyurethanes include, without limitation, isophorone diisocyanate (IPDI), methylene bis-4-cyclohexyl isocyanate (H₁₂MDI), cyclohexyl diisocyanate (CHDI), m-tetramethyl xylene diisocyanate (m-TMXDI), p-tetramethyl xylene diisocyanate (p-TMXDI), 4,4′-methylene diphenyl diisocyanate (MDI, also known as 4,4′-diphenylmethane diisocyanate), 2,4- or 2,6-toluene diisocyanate (TDI), ethylene diisocyanate, 1,2-diisocyanatopropane, 1,3-diisocyanatopropane, 1,6-diisocyanatohexane (hexamethylene diisocyanate or HDI), 1,4-butylene diisocyanate, lysine diisocyanate, meta-xylylenediioscyanate and para-xylylenediisocyanate, 4-chloro-1,3-phenylene diisocyanate, 1,5-tetrahydro-naphthalene diisocyanate, 4,4′-dibenzyl diisocyanate, and xylylene diisocyanate (XDI), and combinations of these. Nonlimiting examples of higher-functionality polyisocyanates that may be used in limited amounts to produce branched thermoplastic polyurethanes (optionally along with monofunctional alcohols or monofunctional isocyanates) include 1,2,4-benzene triisocyanate, 1,3,6-hexamethylene triisocyanate, 1,6,11-undecane triisocyanate, bicycloheptane triisocyanate, triphenylmethane-4,4′,4″-triisocyanate, isocyanurates of diisocyanates, biurets of diisocyanates, allophanates of diisocyanates, and the like.
Nonlimiting examples of suitable diols that may be used as extenders include ethylene glycol and lower oligomers of ethylene glycol including diethylene glycol, triethylene glycol and tetraethylene glycol; propylene glycol and lower oligomers of propylene glycol including dipropylene glycol, tripropylene glycol and tetrapropylene glycol; cyclohexanedimethanol, 1,6-hexanediol, 2-ethyl-1,6-hexanediol, 1,4-butanediol, 2,3-butanediol, 1,5-pentanediol, 1,3-propanediol, butylene glycol, neopentyl glycol, dihydroxyalkylated aromatic compounds such as the bis(2-hydroxyethyl)ethers of hydroquinone and resorcinol; p-xylene-α,α′-diol; the bis(2-hydroxyethyl)ether of p-xylene-α,α′-diol; m-xylene-α,α′-diol, and combinations of these. Other active hydrogen-containing chain extenders that contain at least two active hydrogen groups may be used, for example, dithiols, diamines, or compounds having a mixture of hydroxyl, thiol, and amine groups, such as alkanolamines, aminoalkyl mercaptans, and hydroxyalkyl mercaptans, among others. Suitable diamine extenders include, without limitation, ethylene diamine, diethylene triamine, triethylene tetraamine, and combinations of these. Other typical chain extenders are amino alcohols such as ethanolamine, propanolamine, butanolamine, and combinations of these. The molecular weight of the chain extenders preferably range from about 60 to about 400. Alcohols and amines are preferred.
In addition to difunctional extenders, a small amount of a trifunctional extender such as trimethylolpropane, 1,2,6-hexanetriol and glycerol, or monofunctional active hydrogen compounds such as butanol or dimethyl amine, may also be present. The amount of trifunctional extender or monofunctional compound employed may be, for example, 5.0 equivalent percent or less based on the total weight of the reaction product and active hydrogen containing groups used.
The polyester diols used in forming a thermoplastic polyurethane elastomer are in general prepared by the condensation polymerization of one or more polyacid compounds and one or more polyol compounds. Preferably, the polyacid compounds and polyol compounds are di-functional, i.e., diacid compounds and diols are used to prepare substantially linear polyester diols, although minor amounts of mono-functional, tri-functional, and higher functionality materials can be included to provide a slightly branched, but uncrosslinked polyester polyol component. Suitable dicarboxylic acids include, without limitation, glutaric acid, succinic acid, malonic acid, oxalic acid, phthalic acid, hexahydrophthalic acid, adipic acid, maleic acid, suberic acid, azelaic acid, dodecanedioic acid, their anhydrides and polymerizable esters (e.g., methyl esters) and acid halides (e.g., acid chlorides), and mixtures of these. Suitable polyols include those already mentioned, especially the diols. Typical catalysts for the esterification polymerization are protonic acids, Lewis acids, titanium alkoxides, and dialkyltin oxides.
A polymeric polyether or polycaprolactone diol reactant for preparing thermoplastic polyurethane elastomers may be obtained by reacting a diol initiator, e.g., 1,3-propanediol or ethylene or propylene glycol, with a lactone or alkylene oxide chain-extension reagent. Lactones that can be ring opened by an active hydrogen are well-known in the art. Examples of suitable lactones include, without limitation, E-caprolactone, γ-caprolactone, β-butyrolactone, β-propriolactone, γ-butyrolactone, α-methyl-γ-butyrolactone, β-methyl-γ-butyrolactone, γ-valerolactone, ε-valerolactone, γ-decanolactone, ε-decanolactone, γ-nonanoic lactone, γ-octanoic lactone, and combinations of these. In one preferred embodiment, the lactone is ε-caprolactone. Useful catalysts include those mentioned above for polyester synthesis. Alternatively, the reaction can be initiated by forming a sodium salt of the hydroxyl group on the molecules that will react with the lactone ring. In other embodiments, a diol initiator may be reacted with an oxirane-containing compound to produce a polyether diol to be used in the polyurethane elastomer polymerization. Alkylene oxide polymer segments include, without limitation, the polymerization products of ethylene oxide, propylene oxide, 1,2-cyclohexene oxide, 1-butene oxide, 2-butene oxide, 1-hexene oxide, tert-butylethylene oxide, phenyl glycidyl ether, 1-decene oxide, isobutylene oxide, cyclopentene oxide, 1-pentene oxide, and combinations of these. The oxirane-containing compound is preferably selected from ethylene oxide, propylene oxide, butylene oxide, tetrahydrofuran, and combinations of these. The alkylene oxide polymerization is typically base-catalyzed. The polymerization may be carried out, for example, by charging the hydroxyl-functional initiator compound and a catalytic amount of caustic, such as potassium hydroxide, sodium methoxide, or potassium tert-butoxide, and adding the alkylene oxide at a sufficient rate to keep the monomer available for reaction. Two or more different alkylene oxide monomers may be randomly copolymerized by coincidental addition or polymerized in blocks by sequential addition. Homopolymers or copolymers of ethylene oxide or propylene oxide are preferred. Tetrahydrofuran may be polymerized by a cationic ring-opening reaction using such counterions as SbF₆ ⁻, AsF₆ ⁻, PF₆ ⁻, SbCl₆ ⁻, BF₄ ⁻, CF₃SO₃ ⁻, FSO₃ ⁻, and ClO₄ ⁻. Initiation is by formation of a tertiary oxonium ion. The polytetrahydrofuran segment can be prepared as a “living polymer” and terminated by reaction with the hydroxyl group of a diol such as any of those mentioned above. Polytetrahydrofuran is also known as polytetramethylene ether glycol (PTMEG).
Aliphatic polycarbonate diols that may be used in making a thermoplastic polyurethane elastomer may be prepared by the reaction of diols with dialkyl carbonates (such as diethyl carbonate), diphenyl carbonate, or dioxolanones (such as cyclic carbonates having five- and six-member rings) in the presence of catalysts like alkali metal, tin catalysts, or titanium compounds. Useful diols include, without limitation, any of those already mentioned. Aromatic polycarbonates are usually prepared from reaction of bisphenols, e.g., bisphenol A, with phosgene or diphenyl carbonate.
In various embodiments, the polymeric diol preferably has a weight average molecular weight of at least about 500, more preferably at least about 1000, and even more preferably at least about 1800 and a weight average molecular weight of up to about 10,000, but polymeric diols having weight average molecular weights of up to about 5000, especially up to about 4000, may also be preferred. The polymeric diol advantageously has a weight average molecular weight in the range from about 500 to about 10,000, preferably from about 1000 to about 5000, and more preferably from about 1500 to about 4000. The weight average molecular weights may be determined by ASTM D4274.
The reaction of the polyisocyanate, polymeric diol, and diol or other chain extension agent is typically carried out at an elevated temperature in the presence of a catalyst. Typical catalysts for this reaction include organotin catalysts such as stannous octoate, dibutyl tin dilaurate, dibutyl tin diacetate, dibutyl tin oxide, tertiary amines, zinc salts, and manganese salts. Generally, for elastomeric polyurethanes, the ratio of polymeric diol, such as polyester diol, to extender can be varied within a relatively wide range depending largely on the desired hardness of the final polyurethane elastomer. For example, the equivalent proportion of polyester diol to extender may be within the range of 1:0 to 1:12 and, more preferably, from 1:1 to 1:8. Preferably, the diisocyanate(s) employed are proportioned such that the overall ratio of equivalents of isocyanate to equivalents of active hydrogen containing materials is within the range of 1:1 to 1:1.05, and more preferably, 1:1 to 1:1.02. The polymeric diol segments typically are from about 35% to about 65% by weight of the polyurethane polymer, and preferably from about 35% to about 50% by weight of the polyurethane polymer.
The selection of diisocyanate, extenders, polymeric diols, and the weight percent of the polymeric diols used takes into account the desired hardness and other properties of the polyurethane elastomer and the thermoplastic material containing it.
Suitable thermoplastic polyurea elastomers that may be included in one of the golf ball layers may be prepared by reaction of one or more polymeric diamines or polyols with one or more of the polyisocyanates already mentioned and one or more diamine extenders. Nonlimiting examples of suitable diamine extenders include ethylene diamine, 1,3-propylene diamine, 2-methyl-pentamethylene diamine, hexamethylene diamine, 2,2,4- and 2,4,4-trimethyl-1,6-hexane diamine, imino-bis(propylamine), imido-bis(propylamine), N-(3-aminopropyl)-N-methyl-1,3-propanediamine), 1,4-bis(3-aminopropoxy)butane, diethyleneglycol-di(aminopropyl)ether), 1-methyl-2,6-diamino-cyclohexane, 1,4-diamino-cyclohexane, 1,3- or 1,4-bis(methylamino)-cyclohexane, isophorone diamine, 1,2- or 1,4-bis(sec-butylamino)-cyclohexane, N,N′-diisopropyl-isophorone diamine, 4,4′-diamino-dicyclohexylmethane, 3,3′-dimethyl-4,4′-diamino-dicyclohexylmethane, N,N′-dialkylamino-dicyclohexylmethane, and 3,3′-diethyl-5,5′-dimethyl-4,4′-diamino-dicyclohexylmethane. Polymeric diamines include polyoxyethylene diamines, polyoxypropylene diamines, poly(oxyethylene-oxypropylene) diamines, and poly(tetramethylene ether) diamines. The amine- and hydroxyl-functional extenders already mentioned may be used as well. Generally, as before, trifunctional reactants are limited and may be used in conjunction with monofunctional reactants to prevent crosslinking.
Suitable thermoplastic polyamide elastomers that may be included in one of the golf ball layers may be obtained by: (1) polycondensation of (a) a dicarboxylic acid, such as oxalic acid, adipic acid, sebacic acid, terephthalic acid, isophthalic acid, 1,4-cyclohexanedicarboxylic acid, or any of the other dicarboxylic acids already mentioned with (b) a diamine, such as ethylenediamine, tetramethylenediamine, pentamethylenediamine, hexamethylenediamine, or decamethylenediamine, 1,4-cyclohexanediamine, m-xylylenediamine, or any of the other diamines already mentioned; (2) a ring-opening polymerization of a cyclic lactam, such as ε-caprolactam or ω-laurolactam; (3) polycondensation of an aminocarboxylic acid, such as 6-aminocaproic acid, 9-aminononanoic acid, 11-aminoundecanoic acid, or 12-aminododecanoic acid; or (4) copolymerization of a cyclic lactam with a dicarboxylic acid and a diamine to prepare a carboxylic acid-functional polyamide block, followed by reaction with a polymeric ether diol (polyoxyalkylene glycol) such as any of those already mentioned. Polymerization may be carried out, for example, at temperatures of from about 180° C. to about 300° C. Specific examples of suitable polyamide blocks include NYLON 6, NYLON 66, NYLON 610, NYLON 11, NYLON 12, copolymerized NYLON, NYLON MXD6, and NYLON 46 elastomers.
The effects of the type and molecular weights of the soft segment polymeric polyols used in making thermoplastic polyurea elastomers and polyamide elastomers are analogous to the same effects in making thermoplastic polyurethane elastomers.
Thermoplastic polyester elastomers that may be included in one of the golf ball layers have blocks of monomer units with low chain length that form the crystalline regions and blocks of softening segments with monomer units having relatively higher chain lengths. Thermoplastic polyester elastomers are commercially available under the trademark Hytrel® from DuPont and under the trademark Pebax® from Arkema. Grades with a hardness of about 25 Shore D to about 70 Shore D are available.
The golf ball layers may include other polymers. In one example, the first or second thermoplastic material may include dispersed domains of cured rubbers, which may be incorporated in a thermoplastic elastomer matrix via dynamic vulcanization of rubbers in any of these thermoplastic elastomers or in other thermoplastic polymers. One such composition is described in Voorheis et al, U.S. Pat. No. 7,148,279, which is incorporated herein by reference. In various embodiments, the first thermoplastic material may include a thermoplastic dynamic vulanizate of a rubber in a non-elastomeric matrix resin such as polypropylene. Thermoplastic vulcanizates commercially available from ExxonMobil under the tradename Santoprene™ are believed to be vulcanized domains of EPDM in polypropylene.
One or more plasticizers may be incorporated into the layers to adjust hardness, flexural modulus, or compression deformation properties. One example of such a plasticizer is the high molecular weight, monomeric organic acid or its salt that may be incorporated, for example, with an ionomer polymer as already described, including metal stearates such as zinc stearate, calcium stearate, barium stearate, lithium stearate and magnesium stearate.
In preferred embodiments, the golf ball is free from any thermoset rubber layer or other thermoset layer.
Various fillers may be added to the thermoplastic compositions, particularly the first and second thermoplastic compositions, generally to adjust the specific gravity, hardness, flexural modulus, compression deformation, other properties of the golf ball layers. Nonlimiting examples of suitable fillers include clay, talc, asbestos, graphite, glass, mica, calcium metasilicate, barium sulfate, zinc sulfide, aluminum hydroxide, silicates, diatomaceous earth, carbonates (such as calcium carbonate, magnesium carbonate and the like), metals (such as titanium, tungsten, aluminum, bismuth, nickel, molybdenum, iron, copper, brass, boron, bronze, cobalt, beryllium and alloys of these), metal oxides (such as zinc oxide, iron oxide, aluminum oxide, titanium oxide, magnesium oxide, zirconium oxide and the like), particulate synthetic plastics (such as high molecular weight polyethylene, polystyrene, polyethylene ionomeric resins and the like), particulate carbonaceous materials (such as carbon black, natural bitumen and the like), as well as cotton flock, cellulose flock and/or leather fiber.
The difference between the specific gravity of the core center and the specific gravity of the core layer is not more than about 0.1 g/cm³. Nonlimiting examples of heavy-weight fillers that may be used to increase specific gravity include titanium, tungsten, aluminum, bismuth, nickel, molybdenum, iron, steel, lead, copper, brass, boron, boron carbide whiskers, bronze, cobalt, beryllium, zinc, tin, and metal oxides (such as zinc oxide, iron oxide, aluminum oxide, titanium oxide, magnesium oxide, zirconium oxide). Nonlimiting examples of light-weight fillers that may be used to decrease specific gravity include particulate plastics, glass, ceramics, and hollow spheres, regrinds, or foams of these. Fillers that may be used in the core center and core layers of a golf ball are typically in a finely divided form.
The outer cover layer may be formulated with a pigment, such as a yellow or white pigment, and in particular a white pigment such as titanium dioxide or zinc oxide. Generally titanium dioxide is used as a white pigment, for example in amounts of from about 0.5 parts by weight or 1 part by weight to about 8 parts by weight or 10 parts by weight passed on 100 parts by weight of polymer. In various embodiments, a white-colored outer cover layer may be tinted with a small amount of blue pigment or brightener.
Customary additives can also be included in the thermoplastic materials, for example dispersants, antioxidants such as phenols, phosphites, and hydrazides, processing aids, surfactants, stabilizers, and so on. The outer cover layer may also contain additives such as hindered amine light stabilizers such as piperidines and oxanalides, ultraviolet light absorbers such as benzotriazoles, triazines, and hindered phenols, fluorescent materials and fluorescent brighteners, dyes such as blue dye, and antistatic agents.
The specific gravity of each of the core center and the core layer may be at least about 1.01 g/cm³. In various embodiments, the core center specific gravity may be from about 1.02 g/cm³or from about 1.05 g/cm³or from about 1.06 g/cm³to about 1.07 g/cm³or to about 1.10 g/cm³or to about 1.15 g/cm³. The difference between the specific gravity of the core center and the specific gravity of the core layer is not more than about 0.1 g/cm³.
The core center has a first flexural modulus of up to about 8,000 psi, preferably from about 2800 psi to about 7400 psi, and more preferably from about 3000 psi to about 7200 psi. The core layer has a second flexural modulus of up to about 15,000 psi, preferably from about 7000 psi to about 13,000 psi, and more preferably from about 7200 psi to about 12,000 psi. In various embodiments, the second flexural modulus may be from about 3000 psi to about 6000 psi, preferably from about 4000 psi to about 5000 psi greater than the first flexural modulus.
The core layer has a 10-130 kg compression deformation of from about 2.6 mm to about 4.0 mm, preferably from about 3.3 mm to about 3.8 mm, and more preferably from about 3.4 mm to about 3.7 mm. The surface hardness of the core layer is greater than the surface hardness of the core center. In various embodiments, the surface hardness of the core layer is from about 4 to about 15, preferably from about 6 to about 12 Shore D hardness units greater than the surface hardness of the core center.
The first and second thermoplastic materials may be made by conventional methods, such as melt mixing in a single- or twin-screw extruder, a Banbury mixer, an internal mixer, two-roll mill, or a ribbon mixer. The first thermoplastic material may be formed into a core center and the second thermoplastic material may be formed into a core layer around the core center by usual methods, for example by injection molding with a mold temperature in the range of 150° C. to 230° C. The molded core center and core layer may be ground to a desired diameter after cooling. Grinding can also be used to remove flash, pin marks, and gate marks due to the molding process.
The core center has a diameter of about 5 mm to about 20 mm. In various embodiments, the core center has a diameter of from about 8 mm to about 19 mm, more preferably from about 10 mm to about 18 mm.
The core layer has a diameter of from about 28 mm to about 40 mm and a thickness of from about 4 mm to about 10 mm. In various embodiments, the core layer may have a diameter of from about 30 mm to about 38 mm, more preferably from about 32 mm to about 36 mm or a thickness of from about 5 mm to about 8 mm, more preferably from about 6 mm to about 7 mm.
The core may have one or more further core layers arranged such that the surface hardness of an innermost core layer is greater than the surface hardness of the core center, the surface hardness of the next adjacent core layer outward from the innermost core layer has a surface hardness greater than the surface hardness of the innermost core layer, and so on with the surface hardness of each succeeding outward core layer being greater than that of its inwardly adjacent core layer.
The inner cover layer and the outer cover layer are molded over the core. Each of the layers cover may be formed on the multi-layer core by injection molding, compression molding, casting, and so on. For example, when the cover layers are formed by injection molding, a core fabricated beforehand may be set inside a mold, and the third thermoplastic materials may be injected into the mold, then the fourth thermoplastic materials may be formed into the outer cover layer a second mold in the same way. The cover layers are typically molded on the core by injection molding or compression molding. Alternatively, another method that may be used involves pre-molding a pair of half-covers from the cover layer materials by die casting or another molding method, enclosing the core in the half-covers, and compression-molding at, for example, between 120° C. and 170° C. for a period of 1 to 5 minutes to attach the cover layer halves around the core. The core may be surface-treated before the cover layers are formed over it to increase the adhesion between the core and the inner cover layer. Nonlimiting examples of suitable surface preparations include mechanically or chemically abrasion, corona discharge, plasma treatment, or application of an adhesion promoter such as a silane or of an adhesive. The outer cover layer is typically formed with a dimple pattern and profile to provide desirable aerodynamic characteristics to the golf ball.
Typically, the cover layers may each independently have a thickness of from about 0.6 mm to about 2.0 mm, preferably from about 0.8 mm to about 1.6 mm. In various preferred embodiments, the inner cover layer has a thickness of from about 0.6 mm to about 1.4 mm and the outer cover layer has a thickness of from about 0.6 mm to about 1.4 mm.
The outer cover layer has a 10-130 kg compression deformation of from about 2.3 mm to about 3.2 mm, preferably from about 2.4 mm to about 3.0 mm, and more preferably from about 2.5 mm to about 2.9 mm. The outer cover layer has surface hardness that is less than the surface hardness of the inner cover layer. In various embodiments, the surface hardness of the outer cover layer is from about 8 to about 20, preferably from about 10 to about 16 Shore D hardness units less than the surface hardness of the inner cover layer. In certain preferred embodiments, the inner cover layer may have a surface hardness of from about 60 to about 72 Shore D, preferably from about 63 to about 70 Shore D and the outer cover layer may have a surface hardness of from about 48 to about 60 Shore D, preferably from about 50 to about 58 Shore D.
The golf balls can be of any size, although the USGA requires that golf balls used in competition have a diameter of at least 1.68 inches (42.672 mm) and a weight of no greater than 1.62 ounces (45.926 g). For play outside of USGA competition, the golf balls can have smaller diameters and be heavier.
After a golf ball has been molded, it may undergo various further processing steps such as buffing, painting and marking as disclosed in U.S. Pat. No. 4,911,451. In a particularly preferred embodiment of the invention, the golf ball has a dimple pattern that coverage of 65% or more of the surface. The golf ball typically is coated with a durable, abrasion-resistant and relatively non-yellowing finish coat.
The description is merely exemplary in nature and, thus, variations that do not depart from the gist of the disclosure are a part of the invention. Variations are not to be regarded as a departure from the spirit and scope of the disclosure

Claims

What is claimed is:

1. A golf ball, comprising:

a core center comprising a first thermoplastic material, wherein the core center has a diameter of from about 5 mm to about 20 mm, a first flexural modulus of up to about 8,000 psi, and a surface hardness;

a core layer comprising a second thermoplastic material disposed radially outward from the core center, wherein the core layer has a diameter of from about 28 mm to about 40 mm, a thickness of from about 4 mm to about 10 mm, a second flexural modulus of up to about 15,000 psi that is greater than the first flexural modulus, a 10-130 kg compression deformation of from about 2.6 mm to about 4.0 mm, and a surface hardness that is greater than the surface hardness of the core center;

an inner cover layer disposed radially outward from the core layer, wherein the inner cover layer comprises a thermoplastic polyurethane and has a surface hardness; and

an outer cover layer on the surface of the golf ball having a 10-130 kg compression deformation of from about 2.3 mm to about 3.2 mm, comprising a thermoplastic polyurethane that may be the same as or different from the thermoplastic polyurethane of the inner cover layer, and having a surface hardness that is less than the surface hardness of the inner cover layer, wherein the difference between the specific gravity of the core center and the specific gravity of the core layer is not more than about 0.1 g/cm³.

2. A golf ball according to claim 1, wherein one of the first thermoplastic material and the second thermoplastic material comprises an ionomer resin.

3. A golf ball according to claim 2, wherein the ionomer resin comprises a monomeric organic acid or salt thereof and wherein the ionomer resin is neutralized from at least about 40% to about 100%.

4. A golf ball according to claim 3, wherein the ionomer resin is neutralized from at least about 90% to about 100%.

5. A golf ball according to claim 1, wherein each of the first thermoplastic material and the second thermoplastic material independently comprises an ionomer resin.

6. A golf ball according to claim 5, wherein each ionomer resin comprises a monomeric organic acid or salt thereof and wherein each ionomer resin is independently neutralized from at least about 40% to 100%.

7. A golf ball according to claim 6, wherein each ionomer resin is independently neutralized from at least about 90% to 100%.

8. A golf ball according to claim 1, wherein the core center has a diameter of from about 8 mm to about 19 mm.

9. A golf ball according to claim 1, wherein the first flexural modulus is from about 2800 psi to about 7400 psi.

10. A golf ball according to claim 1, wherein the second flexural modulus is from about 7000 psi to about 13,000 psi.

11. A golf ball according to claim 1, wherein the second flexural modulus is from about 3000 psi to about 6000 psi greater than the first flexural modulus.

12. A golf ball according to claim 1, wherein the core layer has a diameter of from about 30 mm to about 38 mm or has a thickness of from about 5 mm to about 8 mm.

13. A golf ball according to claim 1, wherein the core layer has a 10-130 kg compression deformation of from about 3.3 mm to about 3.8 mm.

14. A golf ball according to claim 1, wherein the surface hardness of the core layer is from about 4 to about 15 Shore D hardness units greater than the surface hardness of the core center.

15. A golf ball according to claim 1, wherein the inner cover layer has a thickness of from about 0.6 mm to about 2.0 mm and the outer cover layer has a thickness of from about 0.6 mm to about 2.0 mm.

16. A golf ball according to claim 1, wherein the outer cover layer has a 10-130 kg compression deformation of from about 2.4 mm to about 3.0 mm.

17. A golf ball according to claim 1, wherein the surface hardness of the inner cover layer is from about 8 to about 20 Shore D hardness units greater than the surface hardness of the outer cover layer.

18. A golf ball according to claim 1, wherein the specific gravity of each of the core center and the core layer is at least about 1.01 g/cm³.

19. A golf ball according to claim 1, wherein the first flexural modulus is from about 3000 to about 7200 psi and the second flexural modulus is from about 7200 to about 12,000 psi.

20. A golf ball according to claim 1, wherein each of the inner cover layer and the outer cover layer independently has a thickness of from about 0.6 mm to about 2.0 mm.