US20070106092A1

US20070106092A1 - Hydrofluoroethers having at least one hydrogenated -OCFX'CH3 end group wherein X'=F, CF3 and their preparation process

Info

Publication number: US20070106092A1
Application number: US11/588,325
Authority: US
Inventors: Rosaldo Picozzi; Antonella Di Meo; Claudio Tonelli
Original assignee: Solvay Solexis SpA
Current assignee: Solvay Specialty Polymers Italy SpA
Priority date: 2002-08-01
Filing date: 2006-10-27
Publication date: 2007-05-10
Also published as: US20040024249A1; US7161030B2; EP1388554A3; CA2435920A1; EP1388554A2; DE60316514D1; DE60316514T2; EP1388554B1; JP2004067684A; ITMI20021731A1

Abstract

Hydrofluoroethers of formula:
T-CFX′—O—R_f—CFX-T′ (II) wherein:

T=CH₃;
X, X′, equal to or different from each other, are selected between F, CF₃;
T′=F, Cl, H, C₁—C₃perfluoroalkyl, CH₃, CH₂0H, COC₁, CHO, CO₂H;
R_fis a perfluoroalkylene or a perfluoropolyoxyalkylene and respective preparation process by reduction with hydrogen in the presence of a platinum catalyst supported on metal fluorides of the corresponding compounds with at least one —COCl end group.

Description

CROSS-REFERENCE TO RELATED APPLICATION

This is a Divisional Application, which claims the benefit of pending U.S. patent application Ser. No. 10/630,697, filed Jul. 3, 2003. The disclosure of the prior application is hereby incorporated herein in its entirety by reference.

BACKGROUND OF THE INVENTION

The present invention relates to hydrofluoroethers characterized in having at least one hydrogenated —OCFX′CH₃end group wherein X′=F, CF₃and their preparation process.
More specifically, the preparation process relates to the reduction with H₂, in the presence of platinum catalysts (Pt), of the corresponding fluorinated acylchloride precursors.
Hydrofluoroethers prepared by direct fluorination with F₂or electrochemical fluorination of an ether compound or by alkylation of fluorinated alcohols are known.
In patent application WO 99/47,480 it is shown that hydrofluoroethers can be obtained by alkylation of fluorinated carbonyl compounds. The above methods employ starting compounds having a low molecular weight with a number of carbon atoms equal to or lower than 12, besides they give low yields and selectivity, and do not give hydrofluoroethers having at least one OCFX′CH₃end group with X′=F, CF₃.
More specifically patent application WO 99/47,480 describes an alkylation process of perfluorinated carbonyl compounds in the presence of a Lewis acid, for example SbF₅. Although in the general formula:
R_f—(O—R)_x (I)
wherein:
R_fis a fluorinated C₁—C₁₅alkyl, optionally substituted and optionally containing heteroatoms in the chain as N, O, S;
R is a C₁—C₁₀alkyl, optionally substituted,
x ranges from 1 to 3,
a great number of potential hydrofluoroethers is contained, really by the process only hydrofluoroethers having end groups different from —OCFX′CH₃are obtainable. See the Examples of patent application WO 99/47,480. Therefore the compounds having —OCFX′CH₃termination have not been prepared and no indication about how to prepare them is given. Accordingly the skilled man in the art on the basis of the aforesaid patent and of the common general knowledge is unable to prepare the compounds of the present invention.
Generally the reaction described in patent application WO 99/47,480 proceeds with very low conversions when R_fis branched. The reaction shows the limitation that to obtain acceptable conversions it is necessary to use CH₃F as alkylating agent, has the drawback to require the use of Lewis acids which are aggressive and need the use of pressure resistant equipments built in special substances. Furthermore HF forms, producing further problems in the equipment choice. Since the alkylation reaction is an equilibrium reaction, it does not allow the obtainment of hydrofluoroethers with a high yield.
The Applicant has furthermore found that by using a Lewis acid as SbF₅, in the ratios suggested by patent application WO 99/47,480 and by following the same modalities suggested by the same, no hydrofluoroethers are obtained starting from precursors having a perfluoropolyether structure, in particular containing —OCF₂O— sequences; besides the use of SbF₅amounts higher than those suggested causes the almost total degradation of the initial perfluoropolyether structure without obtaining however hydrofluoroethers (see the comparative Examples).
The need was therefore felt to obtain hydrofluoroethers by a process avoiding the prior art inconveniences and limitations.
It has been found a hydrogenation process of fluorinated precursors containing acylchloride groups carried out in the presence of platinum catalysts which allows to obtain hydrofluoroethers characterized in having at least one —OCFX′CH₃end group and quantitative conversions with selectivity even of the order of 70%.
An object of the present invention are therefore hydrofluoroethers of formula:
T-CFX′—O—R_f—CFX-T′ (II)
wherein:

T=CH₃;
X, X′, equal to or different from each other, are selected from F, CF₃;
T′=F, Cl, H, C₁—C₃perfluoroalkyl, CH₃, CH₂OH, COCl, CHO, CO₂H;
R_fis selected from:

C₂—C₁₅perfluoroalkylene;
—(C₂F₄O)_m(CF₂CF(CF₃)O)_n(CF₂O)_p(CF(CF₃)O)_q—
wherein:
the sum n+m+p+q ranges from 2 to 200, the (p+q)/(m+n+p+q) ratio is lower than or
equal to 10:100, preferably comprised between 0.5:100 and 4:100, the n/m ratio ranges
from 0.2 to 6, preferably from 0.5 to 3; m, n, p, q are equal to or different from each other
and when m, n range from 1 to 100, preferably from 1 to 80, then p, q range from 0 to 80,
preferably from 0 to 50; the units with n, m, p, q indexes being statistically distributed
along the chain;

- —(CF₂CF₂CF₂O) _r— wherein r ranges from 2 to 200,
- —(CF (CF₃) CF₂O) _s— wherein s ranges from 2 to 200,

The preferred structures of the perfluorooxyalkylene chain R_fare selected from the following:

—(CF₂CF₂O)_m— (CF₂O) _p—,
—(CF₂CF (CF₃) O)_n— (CF₂O) _p—(CF (CF₃) O) _q
wherein the indexes have the above meanings.

A further object of the present invention is the preparation process of the formula (II) compounds comprising the reduction of the formula (III) corresponding precursors:
T″-CFX′—O—R_f—CFX-T″′ (III)
wherein:

T″ is —COCl,
T″′=F, C₁—C₃perfluoroalkyl, COCl, H, Cl,
X, X′, R_fare as defined in formula (II),
carried out with gaseous hydrogen in the presence of a catalyst formed by supported platinum, preferably on metal fluorides, preferably in the presence of inert solvents, at a temperature in the range 20° C.-150° C., preferably 80° C.-120° C., at a pressure between 1 and 50 atm, preferably between 1 and 10 atm.

The formula (III) compounds having at least one —COCl end group are known, preparable for example by reaction of the corresponding PFPEs having —COF or —COOH end groups with inorganic chlorides or chlorinating agents such as thionyl chloride; preferably they are prepared according to what described in Italian patent applications MI2002A 001733 and MI2002A 001734 filed at the same time as the present application, and herein incorporated by reference, by a solid-liquid reaction between a large excess of inorganic chloride, CaCl₂and a PFPE acylfluoride, at a temperature higher than 100° C., under strong stirring or alternatively a PFPE acylfluoride can be hydrolyzed obtaining the corresponding carboxylic acid which is subsequently treated with SOCl₂, in the presence of a tertiary amine, at a temperature in the range 50-100° C., obtaining the corresponding acylchloride.
The formula (II) hydrofluoroethers can alternatively be obtained from the corresponding PFPEs having at least one —CHO or —CH(OH)O(CH₂)_tR end group wherein t=0 or 1 and R is a C₁—C₁₀alkyl group, H, or R_f.
The process can be carried out in a continuous or discontinuous way.
The metal fluorides are preferably selected from the group formed by CaF₂, BaF₂, MgF₂, AlF₃; more preferably CaF₂. The Pt concentration on the support is comprised between 0.1% and 10% with respect to the total weight of the catalyst, preferably between 1% and 2% by weight. The used catalyst amount is in the range 1%-100% by weight with respect to the weight of the formula (III) compound, preferably 10%-100% by weight.
The inert solvents can for example be linear or cyclic perfluorinated ethers such for example perfluorotetrahydrofuran, perfluorotetrahydropyran, or their mixtures.
The invention hydrofluoroethers having at least one —OCFX′CH₃end group with X′=F, CF₃can be used as refrigerants, solvents in cleaning processes of printed circuits, and degreasing in vapour phase of metal components as substituents of CFCs, HCFCs and PFCs, resulted harmful for the ozone layer or show a high GWP (greenhouse potential).
Besides they found application for the wide range of utilization temperatures as substituents of HFCs which in some cases have a limited application as refrigerants due to their very low boiling temperature or their very high freezing point.
The following Examples are given for illustrative and not limitative purposes of the present invention.

EXAMPLES

Example 1

In a 1,000 ml flask, equipped with mechanical stirrer, bubbling pipe to introduce hydrogen/nitrogen, condenser with a bubble-counter
36.7 g of Pt supported on CaF₂(Pt=1.5% by weight), 400 ml of mixture 1:1 of perfluorobutyltetrahydrofuran and perfluoropropyltetrahydropyran (D100), are introduced.
By external heating with thermostated oil bath, the solvent is brought to the boiling temperature (100° C.), then hydrogen is fed at atmospheric pressure at a flow-rate of 20 1/h, and 36.7 g of perfluoropolyether (PFPE) acylchloride of formula (IV)
CF₃O(CF₂CF (CF₃) O) _n(CF₂O) _pCF₂COCl (IV)
wherein n/p=25 and n, p are integers such that the number average molecular weight is 400, are fed by dropping funnel in 30 minutes.
When the PFPE-COCl feeding is over, the reduction is let complete for 15 minutes in hydrogen flow. It is then cooled to room temperature in nitrogen flow. The raw reaction compound is filtered to recover the catalyst.
The NMR (¹⁹F and ¹H) analysis of the compound shows a 100% conversion of the starting PFPE-acylchloride and a yield in formula (V) hydrofluoroether of 60% by moles:
CF₃O(CF₂CF (CF₃) O)_n(CF₂O) _pCF₂CH₃ (V)
The NMR analysis shows furthermore the presence of the alcoholic compound of structure (VI) in an amount equal to 40% by moles:
CF₃O(CF₂CF (CF3) O)_n(CF₂O) _pCF₂CH₂OH (VI)
To separate the hydrofluoroether (V) from the alcohol (VI), the raw reaction compound is chromatographed on silica gel using D 100 as eluent. From the extract, after solvent distillation, 18 g of a compound are obtained which by the NMR (¹⁹F and ¹H) analysis shows to be the hydrofluoroether of formula (V).

Example 2

In the same equipment of the Example 1
32.5 g of Pt supported on CaF₂(Pt=1.5%), 150 ml of D100, are introduced.
One operates as described in the Example 1, by feeding 38.9 g of PFPE acylchloride of formula (VII):
Cl (CF₂CF (CF₃) O) _nCF₂COCl (VII)
wherein n=3 and the number average molecular weight equal to 647.
The NMR (¹⁹F and ¹H) analysis of the compound shows a 100% conversion of the starting PFPE-acylchloride, and a yield of 70% by moles in hydrofluoroether of formula (VIII):
Cl (CF₂CF (CF₃) O) _nCF₂CH₃ (VIII)
The NMR analysis shows furthermore the presence of the alcohol compound in an amount equal to 30% by moles, having structure (IX):
Cl (CF₂CF (CF₃) O) _nCF₂CH₂OH (IX)
To separate the hydrofluoroether from the alcohol, the raw reaction compound is chromatographed on silica gel using D 100 as eluent. From the extract, after solvent distillation, 23 g of a compound are obtained which by the NMR. (¹⁹F and ¹H) analysis shows to be the hydroflucroether of formula (VIII).
The experimentation is repeated with the same modalities feeding each time 38 g of the acylchloride of the Example 2 by using the same catalyst of the preceding test. After a cycle of 10 consecutive tests no variation of the reaction conversion and selectivity has been obtained and therefore no catalyst deactivation was evident.

Example 3

In a 100 ml flask equipped with mechanical stirrer, bubbling pipe to introduce hydrogen/nitrogen, condenser with bubble-counter,
1 g of Pt supported on C (Pt=5%),
40 ml of D100, are introduced.
One operates as described in the Example 1, by feeding 3.54 g of PFPE-acylchloride of the Example 2.
The NMR (¹⁹F and ¹H) analysis of the compound shows a partial conversion of the starting PFPE-acylchloride (53% by moles) and the converted compound shows to be a mixture of compounds of which the formula (VIII) hydrofluoroether forms the 64% by moles.
The difference to 100 is constituted by the acid of formula (X):
Cl (CF₂CF (CF₃) O) _nCF₂CO₂H (X)

Example 4

In the same equipment of the Example 1
30.4 g of Pt on CaF₂(Pt=1.5%),
150 ml of D100, are introduced.
One operates as described in the Example 1, by feeding 35.2 g of PFPE-acylchloride of formula (XI):
ClOCCF₂O (CF₂CF₂O) _m(CF₂O) _pCF₂COCl (XI)
wherein m/p=1 and m, p are such that the number average molecular weight is 2,030.
The NMR (¹⁹F and ¹H) analysis of the compound shows a 100% conversion of the starting PFPE-acylchloride obtaining a reaction mixture which on an average has 60% by moles of —CF₂CH₃end groups, 32% of —CF₂CH₂OH end groups, 8% of CF₂CO₂H end groups.
From the mixture, after chromatography on silica and solvent distillation, 5.8 g of hydrofluoroether of formula:
CH₃CF₂O(CF₂CF₂O) _n(CF₂O) _mCF₂CH₃ (XII),
12 g of PFPE of formula:
CH₃CF₂O (CF₂CF₂O) _m(CF₂O) _mCF₂CH₂OH (XIII),
9.7 g of PFPE-alcohol of formula:
HOCH₂CF₂O(CF₂CF₂O) _m(CF₂O) _pCF₂CH₂OH (XIV),
and 2.4 g of PFPE-acid of formula (XV):
HO (O) CCF₂O(CF₂CF₂O) _m(CF₂O) _pCF₂C (O) OH (XV),
are obtained.

Example 5

In the same equipment of the Example 3
3.26 g of Pt on CaF₂(Pt=1.5%),
40 ml of D100, are introduced.
One operates as described in the Example 1, by feeding 3.21 g of PFPE-aldehyde of formula (XVI):
H (O) CCF₂O (CF₂CF₂O) _m(CF₂O) _pCF₂C (O) H (XVI)
wherein m/p=1 and m, p are such that the number average molecular weight is 2,000.
The NMR (¹⁹F and ¹H) analysis of the compound shows a 100% conversion of the starting PFPE-aldehyde with the obtainment of a reaction mixture which on an average has 30% by moles of —CF₂CH₃end groups and 70% of —CF₂CH₂OH groups.

Example 6

In the same equipment of the Example 3
2.9 g of Pt on CaF₂(Pt=1.5%),
40 ml of D100, are introduced.
One operates as described in the Example 1, by feeding 2.48 g of hydrated PFPE-aldehyde of formula:
(HO) ₂HCCF₂O (CF₂CF₂O) _m(CF₂O) _pCF₂CH (OH) ₂ (XVII)
wherein m/p=1 and m, p are such that the number average molecular weight is 2,000.
The NMR (¹⁹F and ¹H) analysis of the compound shows a 100% conversion of the starting hydrated PFPE-aldehyde with the obtainment of a reaction mixture which on an average has 14% by moles of —CF₂CH₃end groups and 86% of —CF₂CH₂OH groups.

Example 7 (Comparative)

In the same equipment of the Example 3
4 g of Pt on CaF₂(Pt=1.5%),
40 ml of D100, are introduced.
By operating as described in the Example 1, 4 g of PFPE-alcohol of formula:
Cl (CF₂CF (CF₃) O) _nCF₂CH₂OH (IX)
are fed, wherein n=3 and number average molecular weight equal to 604.
The compound NMR (¹⁹F and ¹H) shows that no reaction has taken place, only the PFPE alcohol of formula (IX) being present.

Example 8 (Comparative)

In the same equipment of the Example 3
4 g of Pt on CaF₂(Pt=1.5%),
40 ml of D100, are introduced.
By operating as described in the Example 1, 4 g of PFPE-alcohol of formula:
HOCH₂CF₂O (CF₂CF₂O) _m(CF₂O) _pCF₂CH₂OH (XIV)
are introduced, wherein m/p=1 and m, p are such that the number average molecular weight is 2,000.
The NMR (¹⁹F and ¹H) of the compound shows that no reaction has taken place; only the PFPE-alcohol of formula (XIV) being present.

Example 9 (Comparative)

In the same equipment of Example 3
60 mg of Pt black,
40 ml of D100, are introduced.
By operating as described in the Example 1, 4 g of PFPE-acylchloride of formula (VII) of the Example 2, are introduced.
The NMR (¹⁹F and ¹H) of the compound shows that no reaction has taken place, only the PFPE-acylchloride of formula (VII) being present.

Example 10 (Comparative)

A 250 ml AISI 316 reactor equipped with magnetic stirring, bubbling pipe, thermocouple for the temperature reading and manometer, is dried at 70° C. under vacuum for 7 hours. It is then transferred in dry-box and fed with:
47 mg of SbF₅,
10 g of PFPE-acylfluoride of formula:
FC (O) CF₂O (CF₂CF₂O) _m(CF₂O) _pCF₂C (O) F (XVIII)
wherein m/p=2.13 and m, p such that the number average molecular weight is 1,529.
The reactor is reassembled in the dry-box and cooled to −8° C. After the reactor has been put under vacuum, 1.82 g of gaseous CH₃CF₃are fed. Then one operates by letting the reaction mixture reach the room temperature, then heating it to 30° C. and leaving it for 45 minutes at said temperature. The reactor is then cooled again to −30° C. and after 20 minutes the reaction mixture is quenched by the addition of 8 g of anhydrous methanol. It is brought to room temperature, then the reaction raw compound is discharged from the reactor. The methanol excess is removed by distillation at reduced pressure. 8.9 g of a compound are obtained, which at the ¹⁹F and ¹H NMR analysis shows to be only a PFPE-ester of formula:
CH₃C (O) CF₂O (CF₂CF₂O)_m(CF₂O) _pCF₂C (O) OCH₃ (XIX)
i.e. the reaction compound between the starting PFPE-acylfluoride and the methyl alcohol.
Therefore no formation of hydrofluoroether has been noticed.

Example 11 (Comparative)

In the same equipment of the Example 10 and proceeding as described in the Example 10, the acid catalyst amount is increased by feeding:
2.2 g of SbF₅,
10.5 g of PFPE-acylfluoride of the Example 10.
It is cooled to −80° C. noticing a residual pressure of 1.5 bar. One proceeds however as described in the Example 10 by feeding 1.82 g of CH₃CF₃. A further pressure increase is observed. After quenching with methanol at low temperature, it is let reach again the room temperature. The gas is sampled and is analyzed by gas-mass. It shows to be constituted by a mixture of decomposition compounds of the PFPE-acylfluoride chain, having low number average molecular weight (MW≦500).
None of these shows hydrofluoroether structure with —OCF₂CH₃end groups.
The liquid reaction mass gives only 2.5 g of PFPE-ester of formula:
CH₃C (O) CF₂O (CF₂CF₂O) _m(CF₂O) _pCF₂C (O) OCH₃ (XIX)
wherein m/p=5 and m, p are such that the number average molecular weight is 1,371.

Claims

1. Hydrofluoroethers of formula:

T-CFX′—O—R_f—CFX-T′ (II)

wherein:

T=CH₃;

X, X′, equal to or different from each other, are selected between F, CF₃;

T′=F, Cl, H, C₁—C₃perfluoroalkyl, CH₃, CH₂OH, COCl, CHO, CO₂H;

R_fis selected from:

C₂—C₁₅perfluoroalkylene;

—(C₂F₄O)_m(CF₂CF(CF₃)O)_n(CF₂O)_p(CF(CF₃)O)_q—

wherein

the sum n+m+p+q ranges from 2 to 200,

the (p+q)/(m+n+p+q) ratio is lower than or equal to 10:100, the n/m ratio ranges from 0.2 to 6; m, n, p, q are equal to or different from each other and when m, n range from 1 to 100, then p, q range from 0 to 80; the units with n, m, p, q indexes being statistically distributed along the chain;

—(CF₂CF₂CF₂O)_r— wherein r ranges from 2 to 200,

—(CF(CF₃)CF₂O)_s— wherein s ranges from 2 to 200

2. Hydrofluoroethers according to claim 1, wherein R_fis selected from the following structures:

—(CF₂CF₂O)_m—(CF₂O)_p—,

—(CF₂CF(CF₃)O)_n—(CF₂O)_p—(CF(CF₃)O)_q.

3-7. (canceled)

8. Hydrofluoroethers of claim 1, wherein the (p+q)/(m+n+p+q) ratio is between 0.5:100 and 4:100.

9. Hydrofluoroethers of claim 1, wherein the n/m ratio ranges from 0.5 to 3.

10. Hydrofluoroethers of claim 1, wherein when m, n range from 1 to 80, then p, q range from 0 to 80.

11. Hydrofluoroethers of claim 10, wherein when m, n range from 1 to 80, then p, q range from 0 to 50.