[go: up one dir, main page]
More Web Proxy on the site http://driver.im/

SU1592293A1 - Enamel for cast iron - Google Patents

Enamel for cast iron Download PDF

Info

Publication number
SU1592293A1
SU1592293A1 SU884471668A SU4471668A SU1592293A1 SU 1592293 A1 SU1592293 A1 SU 1592293A1 SU 884471668 A SU884471668 A SU 884471668A SU 4471668 A SU4471668 A SU 4471668A SU 1592293 A1 SU1592293 A1 SU 1592293A1
Authority
SU
USSR - Soviet Union
Prior art keywords
enamel
cast iron
cao
components
sag
Prior art date
Application number
SU884471668A
Other languages
Russian (ru)
Inventor
Vladimir D Afonin
Aleksandr K Zhuravlev
Oleg V Kucherov
Valerij M Sobolev
Serafima N Marochkina
Valentina D Novikova
Vera V Malakhova
Lyubov A Makarova
Mariya I Zajchenko
Original Assignee
Nii Sanitarnoj Tekhniki Oboru
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nii Sanitarnoj Tekhniki Oboru filed Critical Nii Sanitarnoj Tekhniki Oboru
Priority to SU884471668A priority Critical patent/SU1592293A1/en
Application granted granted Critical
Publication of SU1592293A1 publication Critical patent/SU1592293A1/en

Description

Изобретение относится к составам для зашиты санитарно-технического оборудования. С целью повьте- ния растекаемости эмаль для чугуна содержит следующие компоненты, мае.2: 8ί02 38-50; В20э9-14,· ΝβίΟ 19-23;

Με0 2-3; СаРг 3-5; Р20уЗ-5; ΑΙ.*^

3-5,5; ΤΐΟί 0,6-1,0, К/) 0,3^1,0;

Ре20э 0,1-0,5; СаО 3-5 и 2-4. КТР эмали Зо(= (315-330)..· 10'71/град, температура обжига 800-810*С, ударная прочность 0,7-0,8 Дж, растекаемость 70-80 мм. 2 табл. *

'8

Изобретение относится к силикатным эмалям, предназначенным для эмалирования чугунных санитарно-технических изделий.

Целью изобретения является повышение растекаемости.

Конкретные составы эмали приведены в табл.1.

Для уменьшения стоимости часть компонентов в эмаль вводят через ваграночный шлак (до 7 мае.2) и отходы титановой эмали Т - 5 к (до 9 мае.2). Фтор вводится в виде криолита и отходов титановой эмали, находится в связанном состоянии и при варке эмали не улетучивается в окружающую среду.

Получение эмали осуществляют по известной технологиисмешение компонентов шихты, варка эмалевого стекла с последующей грануляцией в воду, сушка гранулята, сухой помол фритты в мельнице.

Эмаль наносят перед покровной эмалью на грунтовую эмаль согласно технологии порошкового эмалирования чугунных изделий. Эмаль может быть нанесена как вручную, так и с помощью робота-манипулятора.

Свойства эмали приведены в табл.2,

Предлагаемая эмаль может, быть использована в качестве промежуточного слоя для защитного покрытия . чугунных санитарно-технических приборов.

00

The invention relates to compositions for the protection of sanitary equipment. In order to improve the flowability, enamel for cast iron contains the following components, May.2: 8ί0 2 38-50; B 2 0 e 9-14, · ΝβίΟ 19-23;

Μ ε 0 2-3; Ca g 3-5; Р 2 0 at З-5; ΑΙ. * ^

3-5,5; ΤΐΟί 0.6-1.0, K /) 0.3 ^ 1.0;

Re 2 0 e 0.1-0.5; CaO 3-5 and 2-4. KTP enamel Zo (= (315-330) .. · 10 ' 7 1 / hail, firing temperature 800-810 * C, impact strength 0.7-0.8 J, flowability 70-80 mm. Table 2 *

'eight

The invention relates to silicate enamels, intended for enameling cast-iron sanitary ware.

The aim of the invention is to increase the spreadability.

Specific enamel compositions are given in table 1.

To reduce the cost of the components in the enamel is injected through cupola slag (up to May 7.2) and waste of titanium enamel T - 5 K (up to 9 May.2). Fluorine is introduced in the form of cryolite and waste titanium enamel, is in a bound state and when boiling enamel does not evaporate into the environment.

Enamel production is carried out using a known technology, mixing the components of the mixture, boiling the enamel glass, followed by granulation into water, drying the granulate, and dry grinding of frit in a mill.

The enamel is applied before the surface enamel on the ground enamel according to the technology of powder enameling of cast iron products. Enamel can be applied both manually and with the help of a robotic arm.

The properties of the enamel are shown in table 2,

The proposed enamel can be used as an intermediate layer for a protective coating. cast iron sanitary appliances.

00

Claims (1)

Формула изобретенияClaim Эмаль для чугуна, включающаяEnamel for cast iron, including 8ίΟ2, В±03, Με0, Ρ20ΤΐΟχ8ίΟ 2 , В ± 0 3 , Μ ε 0, Ρ 2 0ΤΐΟχ А1103, СаР1, Ре20э, СаО, отличающаяся тем, что, с цельюA1 1 0 3 , CaP 1 , Fe 2 0 e , CaO, characterized in that, with the aim повышения растекаемости, она допол-enhancement of spreadability, it adds 3 3 1592293' 1592293 ' л l нительно содержит К^О contains K ^ O к Г- при еле- to G- with barely ΤίΟι ΤίΟι 0,6-1,0 0.6-1.0 дующем соотношении компонентов,мае.%: following ratio of components, May.%: АЦО з ACO s 3,0-5,5 3.0-5.5 3ίο2 3ίο 2 38-50 38-50 СаГ* SaG * 3-5 3-5 Β«θ3 Β "θ 3 9-14 · 9-14 · Ре20э Re 2 0 e 0,1-0,5 0.1-0.5 Ыа2ОNa 2 Oh 19—23 5 19–23 5 СаО Cao 3-5 3-5 ΜβΟ ΜβΟ 2-3 2-3 к,о ч to about h 0,3-1,0 0.3-1.0 3-5 . · · I 3-5 . · · I 2-4 2-4
Та блица 1Table 1 Компоненты, мае, X Components, May, X Содержание в эмали, мае. % Enamel content, May. % 1 one I 2 II 2 I 3 3 | 4 (прототип) | 4 (prototype) 810± 810 ± 38 38 44 44 50 50 37 37 вгоэ in g of e 9 9 12 12 14 14 9 9 N3^0 N3 ^ 0 23 23 21 21 19 nineteen 22 22 М£0 M £ 0 3 3 2,5 2.5 2 2 9 9 СаГг Sag g 5 five 4 four 3 3 6 6 ΡΐΟί ΡΐΟί 5 five 4 four 3 3 7 7 А1*0Э A1 * 0 E 5,5 5.5 4 four 3 3 4 ' four ' ΤίΟ1 ΤίΟ 1 1 , one , 0,8 0.8 0,6 0.6 2 2 к2оto 2 o 1 one 0,5 0.5 о,з oh w - - 'Ре403 'Re 4 0 3 0,5 0.5 0,2 0.2 0,1 0.1 - - СаО Cao 5 five 4 four 3 3 4 four Ъ B 4 four 3 3 2 2 — -
Т а T a блица 2 blitz 2 Показатели Indicators Эмаль Enamel 1 . 1 . 1 one I 2 I 3 I 2 I 3 4 (прототип) 4 (prototype) Температура варки,°С Cooking temperature, ° С 1200 1200 1200 1200 1200 1200 1200 1200 Продолжительность варки, ч Duration of cooking, h 1,5 1.5 1,5 1,5 1.5 1.5 1,5' 1.5 '
Коэффициент объемного термического расширения в диапазонеThe coefficient of volumetric thermal expansion in the range 20-400* С Зе/х 1020-400 * С Зе / х 10 град ’ hail 330 330 320 320 315 315 332 332 Температура обжига,*С Firing temperature, * С 800 800 805 805 810 810 800 800 Ударная прочность, Дж Impact strength, j 0,7 0.7 0,75 0.75 0,8 0.8 0,8 0.8 Растекаемость, мм Flowability, mm 80 80 75 75 70 70 60 60
SU884471668A 1988-08-10 1988-08-10 Enamel for cast iron SU1592293A1 (en)