RU2201338C2

RU2201338C2 - Rubber mold lubricant

Info

Publication number: RU2201338C2
Application number: RU2001106930A
Authority: RU
Inventors: В.Ф. Илькова; В.И. Зобнин; Л.А. Федореева; Н.П. Никонова; Е.Г. Илькова; А.А. Курамина
Original assignee: Иркутская государственная сельскохозяйственная академия
Priority date: 2001-03-14
Filing date: 2001-03-14
Publication date: 2003-03-27

Abstract

FIELD: manufacture of building materials. SUBSTANCE: lubricant for rubber molds used for manufacturing concrete products includes, wt %: oxalic acid 0.7-2.1, spent motor fuel 20-30, saponified tallow pitch 2.0- 3.0, and water - the balance. EFFECT: improved quality of product surfaces, increased stability of lubricant, and reduced its cost.

Description

Изобретение относится к промышленности строительных материалов, а именно к смазкам для резиновых форм при производстве бетонных изделий и мелкозернистого бетона. The invention relates to the building materials industry, namely, lubricants for rubber molds in the production of concrete products and fine-grained concrete.

Смазка для форм - обязательная технологическая операция при изготовлении бетонных изделий. Lubricant for molds is a mandatory technological operation in the manufacture of concrete products.

Известна смазка для резиновых форм, включающая мыло, воду, оксалат натрия и мочевину /а.с. СССР 990530, В 28 В 7/38, 1983/. Known lubricant for rubber forms, including soap, water, sodium oxalate and urea / a.s. USSR 990530, B 28 V 7/38, 1983 /.

Недостатком смазки данного состава является невысокая стабильность, смазка не исключает образования жирных пятен на поверхности бетонных изделий, что требует дополнительной отделки поверхности бетонных изделий. The lack of lubrication of this composition is low stability, the lubrication does not exclude the formation of greasy stains on the surface of concrete products, which requires additional surface treatment of concrete products.

Задача изобретения - повышение качества поверхности бетонных изделии, повышение стабильности смазки, снижение стоимости смазки. The objective of the invention is to improve the surface quality of concrete products, increasing the stability of the lubricant, reducing the cost of lubrication.

Указанная задача достигается тем, что смазка для резиновых форм при изготовлении бетонных изделии и мелкозернистого бетона, включающая отработанное моторное масло, эмульгатор, добавку и воду, содержит в качестве эмульгатора омыленный талловый пек, в качестве добавки щавелевую кислоту при следующем соотношении компонентов, мас.%:
Отработанное моторное масло - 20-30
Омыленный талловыи пек - 2,0-3,0
Щавелевая кислота - 0,7-2,1
Вода - Остальное
Смазка на основе отработанных моторных масел по консистенции представляет собой пасту светло-коричненго цвета, легко наносимую на поверхность формы растиранием или разбрызгиванием под давлением. Паста обладает высокой адгезией к поверхности резиновых форм и обеспечивает нанесение смазки тонким слоем равномерной толщины.This problem is achieved in that the lubricant for rubber forms in the manufacture of concrete products and fine-grained concrete, including waste motor oil, emulsifier, additive and water, contains saponified tall tar as an emulsifier, as oxalic acid in the following ratio of components, wt.% :
Used engine oil - 20-30
Saponified Tall Pitch - 2.0-3.0
Oxalic acid - 0.7-2.1
Water - Else
Consistency-based grease based on used motor oils is a light brown paste that is easily applied to the mold surface by rubbing or spraying under pressure. The paste has high adhesion to the surface of rubber molds and provides lubrication with a thin layer of uniform thickness.

Для приготовления смазки использовали отработанное моторное масло, щавелевую кислоту, воду и омыленный талловый пек Селенгинского ЦКК, являющийся поверхностно-активным веществом. Введение омыленного таллового пека в состав смазки обеспечивает получение стабильной смазки за счет наличия в составе пека смоляных и жирных кислот. В результате реакции компонентов омыленного таллового пека с отработанным моторным маслом и щавелевый кислотой образуются натриевые мыла, которые являются гидрофильными эмульгаторами и дают эмульсию типа "масло в воде", являясь пластификатором цементных систем, омыленный талловый пек уменьшает адгезию резиновых форм к поверхности бетонных изделий, этим обеспечивается хорошее качество поверхности бетонных изделий. To prepare the lubricant, used engine oil, oxalic acid, water and saponified tall oil pitch of the Selenginsky Central Control Commission, which is a surface-active substance, were used. The introduction of saponified tall pitch in the composition of the lubricant provides a stable lubricant due to the presence of tar and fatty acids in the composition of the pitch. As a result of the reaction of saponified tall oil pitch components with used motor oil and oxalic acid, sodium soaps are formed, which are hydrophilic emulsifiers and give an oil-in-water emulsion, being a plasticizer of cement systems, saponified tall pitch reduces the adhesion of rubber forms to the surface of concrete products, this good surface quality of concrete products is provided.

Примеры состава смазки, позволяющие исключить образование жирных пятен на поверхности бетонных изделий, исключить образование воздушных пузырей-раковин на поверхности бетонных изделий, повысить стабильность смазки, при следующем соотношении компонентов, мас.%:
Отработанное моторное масло - 20; 25; 30
Омыленный талловый пек - 2,0; 2,5; 3,0
Щавелевая кислота - 0,7; 1,4; 2,1
Вода - 77,3; 71,1; 64,9
Все компоненты, кроме масла, используются в виде водных растров, щавелевая кислота вводится с расчетным количеством воды. Приготовление смазки производится в лопастном смесителе и поэтому смазку можно готовить в условиях любого завода или полигона ЖБИ. Общая продолжительность получения однородной пасты ориентировочно составляет 20-30 мин. Для улучшения качества смазки после длительного хранения желательно кратковременное перемешивание в течение 1 мин.Examples of the composition of the lubricant to eliminate the formation of greasy spots on the surface of concrete products, to eliminate the formation of air bubbles-shells on the surface of concrete products, to increase the stability of the lubricant, in the following ratio of components, wt.%:
Spent engine oil - 20; 25; thirty
Saponified tall pitch - 2.0; 2.5; 3.0
Oxalic acid - 0.7; 1.4; 2.1
Water - 77.3; 71.1; 64.9
All components, except oil, are used in the form of water rasters, oxalic acid is introduced with the estimated amount of water. Lubricant preparation is carried out in a paddle mixer and therefore lubrication can be prepared in any plant or precast test site. The total duration of obtaining a homogeneous paste is approximately 20-30 minutes To improve the quality of the lubricant after long-term storage, short-term mixing for 1 minute is desirable.

Использование данного состава смазки позволит обеспечить хорошую распалубливаемость, ровную и гладкую поверхность бетонных изделий без жирных пятен, раковин, ухудшающих внешний вид и требующих дополнительных затрат для их удаления, исключение наростов на резиновых формах после распалубки. Использование отработанных моторных масел позволит отказаться от применения для смазок дорогостоящих масляных соединений, это приведет к снижению стоимости смазки. Повышение стабильности смазки. Смазка данного состава прошла апробацию в КТИ "Востоксиборгстрой" при производстве бетонных изделий: тротуартной плитки, камней бортовых, при производстве гидротехнического бетона и др. The use of this composition of the lubricant will ensure good raspalublivaemost, smooth and smooth surface of concrete products without grease stains, sinks, worsening the appearance and requiring additional costs for their removal, the exclusion of growths on rubber molds after stripping. The use of used motor oils will make it possible to abandon the use of expensive oil compounds for lubricants, this will lead to a decrease in the cost of lubrication. Improving lubricant stability. The lubricant of this composition was tested at KTI Vostoksiborgstroy in the production of concrete products: paving slabs, on-board stones, in the production of hydraulic concrete, etc.

Claims

A lubricant for rubber forms, including oxalic acid and water, characterized in that it additionally contains used motor oil and saponified tall oil pitch in the following ratio, wt. %:
Oxalic acid - 0.7-2.1
Used engine oil - 20-30
Saponified Tall Pitch - 2.0-3.0
Water - Else