KR870006117A - 고분자량 프리폴리머로부터 제조된 폴리우레탄 및 탄성중합체 및 이의 제조방법 - Google Patents

고분자량 프리폴리머로부터 제조된 폴리우레탄 및 탄성중합체 및 이의 제조방법 Download PDF

Info

Publication number
KR870006117A
KR870006117A KR860011342A KR860011342A KR870006117A KR 870006117 A KR870006117 A KR 870006117A KR 860011342 A KR860011342 A KR 860011342A KR 860011342 A KR860011342 A KR 860011342A KR 870006117 A KR870006117 A KR 870006117A
Authority
KR
South Korea
Prior art keywords
isocyanate
prepolymer
reactive material
equivalent
polyisocyanate
Prior art date
Application number
KR860011342A
Other languages
English (en)
Other versions
KR900008460B1 (ko
Inventor
쥬니어 도날드 조셉 부르쉘
디. 페플레이 리차드
Original Assignee
리차드 지. 워터맨
더 다우 케미칼 캄파니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 리차드 지. 워터맨, 더 다우 케미칼 캄파니 filed Critical 리차드 지. 워터맨
Publication of KR870006117A publication Critical patent/KR870006117A/ko
Application granted granted Critical
Publication of KR900008460B1 publication Critical patent/KR900008460B1/ko

Abstract

내용 없음

Description

고분자량 프리폴리머로부터 제조된 폴리우레탄 탄성중합체 및 이의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (10)

  1. 이소시아네이트-말단-준-프리폴리머(quasi-prepolymer)를 활성 수소-함유 조성물과 반응시켜 폴리우레탄 및 폴리우레아 폴리머를 제조하는 방법에 있어서, 준-프리폴리머로서 모노머 폴리이소시아네이트중의 이소시아네이트-말단 프리폴리머의 용액을 사용하며, 이소시아네이트-말단 프리폴리머는 폴리이소시아네이트와 비교적 고당량의 이소시아네이트-반응성 물질과의 반응생성물이며 비교적 고당량의 이소시아네이트-반응성 물질의 평균 분자량의 적어도 2배의 평균 분자량을 가짐을 특징으로 하는 방법.
  2. 제1항에 있어서, 프리폴리머가 1 내지 8중량%의 이소시아네이트 함량을 가지며, 준-프리폴리머는 200 내지 525의 당량을 갖는 방법.
  3. 제1항 또는 2항에 있어서, 프리폴리머가 700 내지 2000의 당량을 갖는 이소시아네이트-반응성 물질과, 방향족 폴리이소시아네이트 또는 지방족 폴리이소시아네이트와의 반응생성물로 이루어지는 방법.
  4. 제1항 내지 3항 중의 어느 한 항에 있어서, 이소시아네이트-반응성 물질이 폴리에테르 폴리올 또는 아민-말단 폴리에테르이고, 방향족 폴리이소시아네이트가 2,4'-및/또는 4,4'-디페닐메탄디이소시아네이트 또는 이의 유도체이며, 폴리우레탄 및/또는 폴리우레아폴리머가 적어도 0.95g/cc (950kg/l)의 밀도를 갖는 방법.
  5. 제1항 내지 4항 중의 어느 한 항에 있어서, 활성수소-함유 조성물이 또한 비교적 저당량의 활성수소-함유 물질 및 비교적 고당량의 활성수소-함유 물질로 이루어지는 방법.
  6. 제1항 내지 5항중의어느 한항에 있어서, 활성수소-함유 잔기당 0.95 내지 1.3의 이소시아네이트 그룹이 존재하는 방법.
  7. 모노머 폴리이소시아네이트 중의 이소시아네이트-말단 프리폴리머의 용액으로 이루어지며, 여기에서 이소시아네이트-말단 프리폴리머는 폴리이소시아네이트와 비교적 고당량의 이소시아네이트-반응성 물질과의 반응 생성물이고, 비교적 고당량의 이소시아네이트-반응성 물질의 평균 분자량의 적어도 2배의 평균 분자량을 갖는, 준-프리폴리머.
  8. 제7항에 있어서, 프리폴리머가 1 내지 8중량%의 이소시아네이트 함량을 가지고, 준-프리폴리머가 200 내지 525의 당량을 갖는 준-프리폴리머.
  9. 제7항 또는 8항에 있어서, 프리폴리머가 700 내지 2000의 당량을 갖는 이소시아네이트-반응성 물질과, 방향족 폴리이소시아네이트 또는 지방족 폴리이소시아네이트와의 반응 생성물로 이루어지는 준-프리폴리머.
  10. 제7항에 내지 9항중 어느 한 항에 있어서, 이소시아네이트-반응성 물질이 폴리에테르 폴리올 또는 아민-말단 폴리에테르이고, 방향족 폴리이소시아네이트가 2,4'- 및/또는 4,4'-디페닐메탄디이소시아네이트 또는 이의 유도체로 이루어지는 준-프리폴리머.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019860011342A 1985-12-27 1986-12-27 폴리우레탄 및 폴리우레아 폴리머의 제조방법 및 이에 사용되는 준-프리폴리머 KR900008460B1 (ko)