Abstract

The present invention relates to a concrete complex manhole and, more specifically, relates to a concrete complex manhole which is provided by coupling high strength concrete and polyethylene (PE) to prevent a leakage in the manhole, block water flowing from the outside, lighten a conventional concrete manhole, and supplement weakness of a load of a conventional polyethylene (PE) manhole and earth pressure. According to the present invention, the complex manhole in which high strength concrete and polyethylene (PE) are coupled to each other is provided to prevent a leakage in the manhole, block water flowing from the outside, lighten a conventional concrete manhole, and supplement weakness of a load of a conventional polyethylene (PE) manhole and earth pressure.

Description

Concrete complex manhole}

본 발명은 콘크리트 복합맨홀에 관한 것으로서, 더욱 상세하게는 고강도 콘크리트와 폴리에틸렌(PE)이 결합된 복합맨홀을 제공함으로써, 맨홀 내부의 누수방지와 외부에서 유입되는 물을 막을 수 있으며, 기존 콘크리트 맨홀을 경량화시킬 수 있으며, 기존 폴리에틸렌(PE) 맨홀 하중과 토압의 단점을 보완시켜줄 수 있는 콘크리트 복합맨홀에 관한 것이다.The present invention relates to a concrete composite manhole, and more particularly, to a composite manhole in which a high strength concrete and polyethylene (PE) are combined to prevent water leakage inside a manhole and to prevent water from entering the manhole. The present invention relates to a concrete composite manhole which can be made lighter and can compensate for the disadvantages of conventional polyethylene (PE) manhole load and earth pressure.

일반적으로 맨홀은 도로상의 우수와 하수 등을 포집하여 특정 위치에 배출하기 위한 것으로, 지중에 매설되는 맨홀 바닥체와, 맨홀바닥체에 결합되어 내부 공간을 형성하는 맨홀 벽체, 지표면에 돌출되도록 맨홀 벽체의 상부에 설치되며, 다수의 통공이 형성된 맨홀뚜껑으로 이루어진다.BACKGROUND ART Generally, a manhole is a manhole bottom body to be buried in the ground, a manhole wall body coupled to the manhole bottom body to form an inner space, a manhole wall body to protrude from the ground surface, And a manhole cover provided with a plurality of through holes.

이중 지중에 설치되는 맨홀 바닥체 및 맨홀 벽체는 토압 등의 하중에 견디도록 압축강도가 우수해야 하며, 지중의 수분 등에 의해 부식되지 않아야 한다.Manhole bottoms and manhole walls installed in the ground should have excellent compressive strength to withstand the loads such as earth pressure, and should not be corroded by moisture in the ground.

이러한 맨홀을 형성하기 위한 재료에 관한 기술로 종래에는 콘크리트를 주로 사용했었다.Conventionally, concrete has been mainly used as a technique relating to a material for forming such a manhole.

그러나, 주유소나 산업폐기물 포집 시설, 원자력 발전소, 광선로 등과 같은 특수 시설의 맨홀의 경우 압축강도 및 내구성, 치밀해야 하며, 설치 공간의 협소함으로 인해 보다 얇은 맨홀 바닥체 및 맨홀 벽체를 설치해야 할 필요성이 있었다.However, the manholes of special facilities such as gas stations, industrial waste collection facilities, nuclear power plants, and light lines must have compressive strength, durability and compactness, and the necessity of installing thinner manhole bottoms and manhole walls due to the narrow space .

이러한 필요에 의해 수경 시멘트에 페놀, 멜라민, 포름알데히드나 포름아미드와 같은 중합체 전구물질을 혼합하여 굴곡강도를 높인 ' 복합재료 함유 시멘트, 시멘트 제품,성형재 콘크리트 부재 및 그의 제조 방법'(한국 등록특허공보 제10-0240737호)이 안출되었다.The present invention relates to a cement, a cement product, a molded material, a concrete member, and a method for manufacturing the same, which have improved flexural strength by mixing polymer precursors such as phenol, melamine, formaldehyde, Bulletin 10-0240737).

그러나, 위와 같은 복합재료 함유 시멘트는 굴곡강도의 개선은 이루어졌으나 치밀하지 못해 누수의 우려가 있는 문제점을 갖고 있었다.However, the cement containing the composite material as described above has been improved in flexural strength, but has a problem of insufficient water leakage due to insufficient durability.

또한, 압축강도가 높지 못해 재료의 두께를 얇게 형성하지 못하는 문제점도 있었으며, 비중이 높아 무게가 무거운 문제점도 있었다.Also, since the compressive strength is not high, the thickness of the material can not be formed thin, and there is a problem that the weight is heavy due to the high specific gravity.

한편, 근래에 들어 이러한 문제점을 감안하여 강화플라스틱과 같은 수지재로써의 맨홀이 많이 개발되었다.Meanwhile, in recent years, in view of such a problem, many manholes have been developed as resin materials such as reinforced plastics.

하지만 이러한 맨홀은 열과 충격에 매우 민감하여 오랜 충격을 받으면 그 변형에 따른 파손이 종종 일어나게 되는 문제점이 있었다.However, such a manhole is very sensitive to heat and impact, so that there is a problem that if a long shock is applied, breakage due to the deformation often occurs.

또한 제조 단가가 비싸 원자재을 수입하는 우리나라에서는 원가 상승을 초래하게 된다.In addition, the manufacturing cost is high and the cost will increase in Korea, which imports raw materials.

종래의 맨홀구조체는 도 1에 도시된 바와 같이, 직육면체의 상부에 맨홀구멍(2)이 형성되고 양측면에 다른 맨홀구조체와 통하는 연결통로(5)가 형성된 구조로서, 종래에는 주로 콘크리이트가 사용되어 왔으나, 최근에는 맨홀구조체의 유지보수를 용이하게하고 내구수명이 향상되며 설치가 용이하도로 합성수지제인 폴리머콘트리트가 사용되고 있다. As shown in FIG. 1, a conventional manhole structure has a structure in which a manhole hole 2 is formed in an upper portion of a rectangular parallelepiped, and a connecting passage 5 communicating with other manhole structures is formed on both sides. Conventionally, Recently, however, polymer concrete, which is a synthetic resin, has been used for facilitating the maintenance of the manhole structure, improving the durability life and facilitating the installation.

그러나, 폴리머콘크리트는 시공이 용이하고 내구수명이 연장된다는 우수한 효과는 있으나 원재료가 고가로서 고가로 제조된다는 문제점이 있다. However, the polymer concrete has an excellent effect of easy construction and prolonged durability life, but has a problem that the raw material is expensive and is manufactured at a high price.

또한 종래의 맨홀구조체는 주로 차도에 설치되므로 어깨부에 차량중량에 의한 동하중이 가해지므로 어깨부의 변형이나 파손이 가게 되어 내구수명이 단축되게 되는 문제점이 있었다.Also, since the conventional manhole structure is installed mainly on the roadway, the dynamic load due to the weight of the vehicle is applied to the shoulder portion, so that deformation or breakage of the shoulder portion is caused and the durability life is shortened.

요약하자면, 하수용 콘크리트맨홀 블록은 중량이므로 시공할 때 어려운 점은 3m 이상의 하수용 콘크리트맨홀 시공시에는 자체 중량의 하중으로 침하현상이 일어나기 때문에 시공을 기피하고 있으며, 좁은 길에서도 장비가 들어갈 수 없어서 시공을 하지 못하는 단점이 있으며, 폴리에틸렌(PE)으로 이루어진 연결관과 연결시에는 각 물질의 탄성계수가 틀려서 상당한 어려움을 겪고 있었다.To summarize, it is difficult to construct a concrete manhole block with a weight of less than 3m because it is a heavy weight concrete manhole block. There is a disadvantage that it can not be applied, and when connecting to a connection pipe made of polyethylene (PE), the modulus of elasticity of each material is different, and it has been difficult.

반면에 하수도용 폴리에틸렌(PE) 맨홀은 경량으로서, 시공상에 편의는 있으나 장기적으로는 하중, 외부 토압으로 인하여 찌그려지는 현상이 일어난다.On the other hand, the polyethylene (PE) manhole for sewerage is lightweight, and there is a convenience in the construction, but in the long term, the phenomenon occurs that it is squeezed because of load and external earth pressure.

따라서, 본 발명에서는 상기한 문제점을 개선하고자 고강도 콘크리트와 폴리에틸렌(PE)이 결합된 복합맨홀을 제공함으로써, 맨홀 내부의 누수방지와 외부에서 유입되는 물을 막을 수 있으며, 기존 콘크리트 맨홀을 경량화시킬 수 있으며, 기존 폴리에틸렌(PE) 맨홀 하중과 토압의 단점을 보완시켜줄 수 있는 콘크리트 복합맨홀을 제안하게 된 것이다.Accordingly, in order to solve the above problems, the present invention provides a composite manhole in which high-strength concrete and polyethylene (PE) are combined to prevent water leakage inside the manhole, to prevent water from entering from the outside, and to reduce the weight of existing concrete manholes , And proposed a composite manhole that can compensate for the disadvantages of conventional polyethylene (PE) manhole load and earth pressure.

한국 등록특허공보 제10-0240737호Korean Patent Registration No. 10-0240737

따라서, 본 발명은 상기 종래의 문제점을 해소하기 위해 안출된 것으로,SUMMARY OF THE INVENTION Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art,

본 발명의 목적은 고강도 콘크리트와 폴리에틸렌(PE)이 결합된 복합맨홀을 제공함으로써, 맨홀 내부의 누수방지와 외부에서 유입되는 물을 막을 수 있으며, 기존 콘크리트 맨홀을 경량화시킬 수 있으며, 기존 폴리에틸렌(PE) 맨홀 하중과 토압의 단점을 보완시켜줄 수 있도록 하는데 있다.It is an object of the present invention to provide a composite manhole in which a high strength concrete and polyethylene (PE) are combined to prevent water leakage inside a manhole, to prevent water from entering from outside, to lighten existing concrete manholes, ) To compensate for the disadvantages of manhole load and earth pressure.

즉, 콘크리트와 폴리에틸렌(PE) 재질의 연결통로관이 결합될 때 탄성계수가 상이해서 일어날 수 있는 부분을 해소하며, 콘크리트맨홀에 직접적으로 폴리에틸렌(PE) 재질의 연결통로관을 연결시 하중 및 토압 등으로 인하여 누수되는 부분을 차단 할 수 있도록 하는데 있다.That is, when the connecting channel of concrete and polyethylene (PE) material is combined, it is possible to eliminate the possibility that the elasticity coefficient is different, and when the connecting pipe of polyethylene material is directly connected to the concrete manhole, So that the leaked portion can be blocked.

본 발명이 해결하고자 하는 과제를 달성하기 위하여, 본 발명의 실시예에 따른 콘크리트 복합맨홀은,In order to accomplish the object of the present invention, there is provided a concrete manhole according to an embodiment of the present invention,

내부가 빈 원기둥 형태의 폴리에틸렌(PE)관(300)을 내부가 빈 원기둥 형태의 거푸집내관(100)의 내면에 형성하거나, 거푸집내관의 외면에 형성한 후, 상기 거푸집내관보다 직경이 큰 내부가 빈 원기둥 형태의 거푸집외관(200)의 내측으로 상기 폴리에틸렌(PE)관(300)이 형성된 거푸집내관(100)을 위치시킨 후, 거푸집내관(100)과 거푸집외관(200) 사이의 공간에 고강도 콘크리트를 투입하여 양생함으로써, 폴리에틸렌(PE)관(300)의 외부를 고강도 콘크리트로 감싸도록 형성되어 본 발명의 과제를 해결하게 된다.(PE) tube 300 having an inner hollow cylindrical shape is formed on the inner surface of the inner mold inner pipe 100 in the shape of an empty cylinder or formed on the outer surface of the inner pipe of the mold, The inner mold 100 having the polyethylene (PE) pipe 300 formed therein is positioned inside the hollow cylindrical outer shape 200 and then the high strength concrete is inserted into the space between the inner pipe 100 and the mold exterior 200. So that the outside of the polyethylene (PE) pipe 300 is surrounded by high-strength concrete, thereby solving the problems of the present invention.

본 발명에 따른 콘크리트 복합맨홀은, 고강도 콘크리트와 폴리에틸렌(PE)이 결합된 복합맨홀을 제공함으로써, 맨홀 내부의 누수방지와 외부에서 유입되는 물을 막을 수 있으며, 기존 콘크리트 맨홀을 경량화시킬 수 있으며, 기존 폴리에틸렌(PE) 맨홀 하중과 토압의 단점을 보완시켜줄 수 있는 효과를 제공하게 된다.The concrete composite manhole according to the present invention can prevent leakage of water from the inside of a manhole and prevent water flowing from the outside by providing a composite manhole combining high strength concrete and polyethylene (PE), can reduce weight of a conventional concrete manhole, It is possible to compensate for the disadvantages of conventional polyethylene (PE) manhole load and earth pressure.

즉, 콘크리트와 폴리에틸렌(PE) 재질의 연결통로관이 결합될 때 탄성계수가 상이해서 일어날 수 있는 부분을 해소하며, 콘크리트맨홀에 직접적으로 폴리에틸렌(PE) 재질의 연결통로관을 연결시 하중 및 토압 등으로 인하여 누수되는 부분을 차단할 수 있는 효과를 제공하게 되는 것이다.That is, when the connecting channel of concrete and polyethylene (PE) material is combined, it is possible to eliminate the possibility that the elasticity coefficient is different, and when the connecting pipe of polyethylene material is directly connected to the concrete manhole, It is possible to block the leakage of the water.

도 1은 종래의 맨홀구조체를 개략적으로 나타낸 종단면도이다.
도 2는 본 발명의 일실시예에 따른 콘크리트 복합맨홀의 사시도이며, 도 3은 측면도이며, 도 4는 상부에서 바라본 사시도이며, 도 5는 내부 사시도이다.
도 6은 본 발명의 일실시예에 따른 콘크리트 복합맨홀을 제조하는 공정을 나타낸 예시도이다.
도 7은 본 발명의 이실시예에 따른 콘크리트 복합맨홀을 제조하는 공정을 나타낸 예시도이다.1 is a longitudinal sectional view schematically showing a conventional manhole structure.
FIG. 2 is a perspective view of a concrete compound manhole according to an embodiment of the present invention, FIG. 3 is a side view, FIG. 4 is a perspective view seen from above, and FIG. 5 is an internal perspective view.
6 is a view illustrating an example of a process for manufacturing a concrete composite manhole according to an embodiment of the present invention.
7 is a view illustrating an example of a process for manufacturing a concrete composite manhole according to an embodiment of the present invention.

이하, 본 발명에 의한 콘크리트 복합맨홀의 실시예를 통해 상세히 설명하도록 한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, concrete manholes according to the present invention will be described in detail.

본 발명의 바람직한 실시예에 따른 콘크리트 복합맨홀은,In the concrete composite manhole according to the preferred embodiment of the present invention,

내부가 빈 원기둥 형태의 폴리에틸렌(PE)관(300)을 내부가 빈 원기둥 형태의 거푸집내관(100)의 내면에 형성하거나, 거푸집내관의 외면에 형성한 후, 상기 거푸집내관보다 직경이 큰 내부가 빈 원기둥 형태의 거푸집외관(200)의 내측으로 상기 폴리에틸렌(PE)관(300)이 형성된 거푸집내관(100)을 위치시킨 후, 거푸집내관(100)과 거푸집외관(200) 사이의 공간에 고강도 콘크리트를 투입하여 양생함으로써, 폴리에틸렌(PE)관(300)의 외부를 고강도 콘크리트(400)로 감싸도록 형성되어 있는 것을 특징으로 한다.(PE) tube 300 having an inner hollow cylindrical shape is formed on the inner surface of the inner mold inner pipe 100 in the shape of an empty cylinder or formed on the outer surface of the inner pipe of the mold, The inner mold 100 having the polyethylene (PE) pipe 300 formed therein is positioned inside the hollow cylindrical outer shape 200 and then the high strength concrete is inserted into the space between the inner pipe 100 and the mold exterior 200. And is formed so as to surround the polyethylene (PE) pipe 300 with the high-strength concrete 400 by curing by curing.

이때, 상기 폴리에틸렌(PE)관(300)의 하측에 연결통로관(350)이 형성되어 있는 것을 특징으로 한다.At this time, a connecting passage pipe 350 is formed on the lower side of the polyethylene (PE) pipe 300.

도 2는 본 발명의 일실시예에 따른 콘크리트 복합맨홀의 사시도이며, 도 3은 측면도이며, 도 4는 상부에서 바라본 사시도이며, 도 5는 내부 사시도이다.FIG. 2 is a perspective view of a concrete compound manhole according to an embodiment of the present invention, FIG. 3 is a side view, FIG. 4 is a perspective view seen from above, and FIG. 5 is an internal perspective view.

도 2 내지 도 5에 도시한 바와 같이, 본 발명인 콘크리트 복합맨홀은, 폴리에틸렌(PE)관(300)의 외부를 고강도 콘크리트(400)가 감싸는 형상을 가지게 된다.As shown in FIGS. 2 to 5, the concrete composite manhole of the present invention has a shape in which the high strength concrete 400 surrounds the outside of the polyethylene (PE) pipe 300.

이때, 하측에는 연결통로관(350)이 형성되게 되는데, 연결통로관은 폴리에틸렌(PE)관(300)의 하측에 결합되어 있는 구조를 가지게 된다.At this time, a connection passage pipe 350 is formed on the lower side, and the connection passage pipe is connected to the lower side of the polyethylene (PE) pipe 300.

상기와 같이, 폴리에틸렌(PE)관(300)의 외부를 고강도 콘크리트(400)가 감싸는 형상을 가지게 되면, 종래 기술에서 언급한 문제점을 해결할 수 있게 되어 맨홀 내부의 누수방지와 외부에서 유입되는 물을 막을 수 있으며, 기존 콘크리트 맨홀을 경량화시킬 수 있으며, 기존 폴리에틸렌(PE) 맨홀 하중과 토압의 단점을 보완시켜줄 수 있는 효과를 제공하게 된다.As described above, if the outer surface of the polyethylene (PE) pipe 300 is shaped so as to surround the high-strength concrete 400, the problems described in the related art can be solved. Thus, it is possible to prevent water leakage inside the manhole, It is possible to reduce the weight of existing concrete manholes and to provide the effect of compensating the disadvantages of conventional polyethylene (PE) manhole load and earth pressure.

도 6은 본 발명의 일실시예에 따른 콘크리트 복합맨홀을 제조하는 공정을 나타낸 예시도이다.6 is a view illustrating an example of a process for manufacturing a concrete composite manhole according to an embodiment of the present invention.

도 6의 경우에는 내부가 빈 원기둥 형태의 거푸집내관(100)과 빈 원기둥 형태의 폴리에틸렌(PE)관(300)을 준비하게 된다.In the case of FIG. 6, the mold inner pipe 100 having an inner hollow shape and the hollow cylindrical polyethylene (PE) pipe 300 are prepared.

이때, 폴리에틸렌(PE)관(300)의 직경은 거푸집내관(100)의 직경보다 작아야 내부에 삽입될 수 있게 된다.At this time, the diameter of the polyethylene (PE) pipe 300 must be smaller than the diameter of the inner pipe 100 to be inserted therein.

이후, 상기 거푸집내관보다 직경이 큰 내부가 빈 원기둥 형태의 거푸집외관(200)을 준비하게 된다.Thereafter, an outer shape 200 of a hollow cylindrical shape having a larger diameter than the inner shape of the formwork is prepared.

상기 거푸집외관(200)은 거푸집내관의 직경보다 충분히 커야 거푸집내관과 거푸집외관 사이의 공간을 충분히 확보할 수가 있을 것이다.The shape of the mold exterior 200 should be sufficiently larger than the diameter of the shape of the mold to ensure a sufficient space between the mold interior and the mold exterior.

이후, 상기 폴리에틸렌(PE)관(300)이 형성된 거푸집내관(100)을 거푸집외관(200)의 내측으로 위치시키게 되면, 거푸집내관(100)과 거푸집외관(200) 사이에 공간이 형성되게 되며, 해당 공간에 고강도 콘크리트(400)를 투입하여 일정시간 양생하게 되는 것이다.A space is formed between the mold inner pipe 100 and the mold outer pipe 200 by locating the inner pipe 100 formed with the polyethylene pipe 300 inside the mold outer pipe 200, The high-strength concrete 400 is put into the space and cured for a certain period of time.

상기와 같은 제조 과정을 거치게 되면, 고강도 콘크리트(400) 내부에 폴리에틸렌(PE)관(300)이 매몰되는 형태를 가지게 되는 것이다.When the above-described manufacturing process is performed, the polyethylene (PE) pipe 300 is buried in the high-strength concrete 400.

이는 탄력성을 향상시키기 위한 제조 과정이며, 탄력성을 제공하기 때문에 외부 충격에도 쉽게 파손되지 않는 장점을 제공하게 된다.This is a manufacturing process for improving the elasticity, and provides elasticity so that it is not easily damaged even by an external impact.

도 7은 본 발명의 이실시예에 따른 콘크리트 복합맨홀을 제조하는 공정을 나타낸 예시도이다.7 is a view illustrating an example of a process for manufacturing a concrete composite manhole according to an embodiment of the present invention.

한편, 도 7의 경우에는 내부가 빈 원기둥 형태의 거푸집내관(100)과 빈 원기둥 형태의 폴리에틸렌(PE)관(300)을 준비하게 된다.In the case of FIG. 7, the mold inner pipe 100 having an inner hollow shape and the hollow cylindrical polyethylene (PE) pipe 300 are prepared.

이때, 폴리에틸렌(PE)관(300)의 직경은 거푸집내관(100)의 직경보다 커야 폴리에틸렌(PE)관(300) 내부에 거푸집내관(100)을 삽입할 수 있게 된다.At this time, the diameter of the polyethylene (PE) tube 300 is larger than the diameter of the inner tube 100 so that the inner tube 100 can be inserted into the polyethylene (PE) tube 300.

이후, 상기 폴리에틸렌(PE)관(300)보다 직경이 큰 내부가 빈 원기둥 형태의 거푸집외관(200)을 준비하게 된다.Thereafter, an outer shape 200 of a hollow cylindrical shape having a diameter larger than that of the polyethylene (PE) pipe 300 is prepared.

상기 거푸집외관(200)은 폴리에틸렌(PE)관(300)의 직경보다 충분히 커야 폴리에틸렌(PE)관(300)과 거푸집외관 사이의 공간을 충분히 확보할 수가 있을 것이다.The mold exterior 200 should be sufficiently larger than the diameter of the polyethylene (PE) tube 300 to provide sufficient space between the polyethylene (PE) tube 300 and the exterior of the mold.

이후, 상기 거푸집내관(100)이 내부에 형성된 폴리에틸렌(PE)관(300)을 거푸집외관(200)의 내측으로 위치시키게 되면, 폴리에틸렌(PE)관(300)과 거푸집외관(200) 사이에 공간이 형성되게 되며, 해당 공간에 고강도 콘크리트(400)를 투입하여 일정시간 양생하게 되는 것이다.Thereafter, a polyethylene (PE) tube 300 having the mold inner pipe 100 inside is placed inside the mold outer pipe 200, a space (not shown) is formed between the polyethylene pipe 300 and the mold outer pipe 200, And the high-strength concrete 400 is put into the space to cure for a certain period of time.

이는 기밀성을 향상시키기 위한 제조 과정이며, 콘크리트(400)에 폴리에틸렌(PE)관(300)이 긴밀하게 붙어있어 고강도를 유지할 수 있게 된다.This is a manufacturing process for improving the airtightness, and the polyethylene (PE) pipe 300 is tightly attached to the concrete 400, so that the high strength can be maintained.

이때, 상기 폴리에틸렌(PE)관(300)의 하측에 연결통로관(350)을 형성하게 되는데, 도 5에 도시한 바와 같이, 내부의 연결통로관을 통해 물을 외부로 유출할 수 있게 된다.At this time, the connection channel pipe 350 is formed below the polyethylene (PE) pipe 300, and as shown in FIG. 5, the water can flow out to the outside through the connection channel pipe inside.

즉, 종래의 콘크리트에 연결통로관을 형성하는 공정이 제거되어, 폴리에틸렌(PE)관에 연결통로관을 형성하거나, 삽입하게 되는 것이다.That is, the process of forming the connecting passage pipe in the conventional concrete is eliminated, and the connecting passage pipe is formed or inserted into the polyethylene (PE) pipe.

이를 통해, 콘크리트와 폴리에틸렌(PE) 재질의 연결통로관이 결합될 때 탄성계수가 상이해서 일어날 수 있는 부분을 해소하며, 콘크리트맨홀에 직접적으로 폴리에틸렌(PE) 재질의 연결통로관을 연결시 하중 및 토압 등으로 인하여 누수되는 부분을 차단할 수 있게 되는 것이다.Through this, it is possible to solve the part that may occur due to the difference of elastic modulus when the concrete channel is connected with the polyethylene pipe (PE), and when the polyethylene pipe pipe is directly connected to the concrete manhole, It is possible to block the leaked portion due to the earth pressure or the like.

즉, 폴리에틸렌(PE)의 탄성계수 380Mpa ~ 980Mpa를 제공하므로 상하, 좌우로의 수축 및 평창이 비교적 많아 장기적으로 수밀에 관해 장담할 수 없게 되지만, 본 발명과 같이 구성하게 되면, 폴리에틸렌(PE)의 표면을 탄성계수가 작은(36Mpa) 콘크리트로 타설하여 수축 및 팽창을 막아 현재 문제시되고 있는 수밀에 관한 문제를 완벽히 해소할 수가 있게 되는 것이다.That is, since the elastic modulus of polyethylene (PE) is in the range of 380 MPa to 980 MPa, shrinkage in the up and down, right and left and shrinkage in the left and right and relatively large pores make it impossible to assure water tightness in the long term. However, (36Mpa) concrete with a small elastic modulus to prevent shrinkage and expansion, thus completely solving the problem of watertightness which is currently in question.

상기와 같은 구성을 통해, 고강도 콘크리트와 폴리에틸렌(PE)이 결합된 복합맨홀을 제공함으로써, 맨홀 내부의 누수방지와 외부에서 유입되는 물을 막을 수 있으며, 기존 콘크리트 맨홀을 경량화시킬 수 있으며, 기존 폴리에틸렌(PE) 맨홀 하중과 토압의 단점을 보완시켜줄 수 있는 효과를 제공하게 된다.By providing the composite manhole combined with the high strength concrete and polyethylene (PE) through the above-described structure, it is possible to prevent the leakage of the inside of the manhole, to block the water flowing from the outside, to lighten the existing concrete manhole, (PE) manhole load and earth pressure.

상기와 같은 내용의 본 발명이 속하는 기술분야의 당업자는 본 발명의 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시 예들은 모든 면에서 예시된 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. It will be understood by those skilled in the art that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is to be understood, therefore, that the embodiments described above are to be considered in all respects as illustrative and not restrictive.

100 : 거푸집내관
200 : 거푸집외관
300 : 폴리에틸렌(PE)관
350 : 연결통로관
400 : 고강도 콘크리트100: die inside
200: Formwork appearance
300: polyethylene (PE) pipe
350: connection passage tube
400: High strength concrete

Claims

In a concrete composite manhole,
(PE) tube 300 having an inner hollow cylindrical shape is formed on the inner surface of the inner mold inner pipe 100 in the shape of an empty cylinder or formed on the outer surface of the inner pipe of the mold, The inner mold 100 having the polyethylene (PE) pipe 300 formed therein is placed inside the hollow cylindrical outer shape 200 and then the high strength concrete is inserted into the space between the inner pipe 100 and the mold exterior 200. (PE) pipe (300) is enclosed in the high strength concrete (400) by curing by injecting and curing the polyethylene pipe (300).

The method according to claim 1,
And a connecting passage pipe (350) is formed below the polyethylene (PE) pipe (300).