KR20160053417A - High performance laminar color steel sheet and method of the same - Google Patents
High performance laminar color steel sheet and method of the same Download PDFInfo
- Publication number
- KR20160053417A KR20160053417A KR1020140152149A KR20140152149A KR20160053417A KR 20160053417 A KR20160053417 A KR 20160053417A KR 1020140152149 A KR1020140152149 A KR 1020140152149A KR 20140152149 A KR20140152149 A KR 20140152149A KR 20160053417 A KR20160053417 A KR 20160053417A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- meth
- parts
- light
- acrylate
- Prior art date
Abstract
본 발명은 고기능성 라미나 칼라강판의 및 제조 방법에 관한 것으로, 소지 강판; 전처리층; 하도 도막층; 우레탄(메타)아크릴레이트 프리폴리머 45~65중량부, (메타)아크릴레이트 모노머 25~40중량부, 카르복실레이티드(메타)아크릴레이트 모너머 20~30중량부, 중량부, 광개시제 3~5중량부, 및 부착증진제 2~5중량부를 포함하는 자외선 경화성 접착층; 및 광 투과성 필름을 순차적으로 포함하는 것인 고기능성 칼라강판 및 그 제조방법을 제공한다. The present invention relates to a high-performance laminated steel sheet and a method of manufacturing the same. Pretreatment layer; Undercoating layer; 45 to 65 parts by weight of urethane (meth) acrylate prepolymer, 25 to 40 parts by weight of (meth) acrylate monomer, 20 to 30 parts by weight of carboxylate (meth) acrylate monomer, 3 to 5 parts by weight of photoinitiator And 2 to 5 parts by weight of an adhesion promoter; And a light-transmitting film sequentially, and a method of manufacturing the same.
Description
본 발명은 고기능성 라미나 칼라강판의 및 제조 방법에 관한 것으로, 더욱 상세하게는 칼라 강판에 액상의 자외선 경화형 접착 조성물을 도포하고, 광 투과성이 우수한 PET 필름 또는 PVC 시트를 합지 후 자외선을 조사하여 경화시킴으로써, 우수한 표면 외관을 보유하고 작업성 및 기능성이 향상된 고기능성 라미나 칼라강판 및 그 제조방법에 관한 것이다.
More particularly, the present invention relates to a method for manufacturing a high-performance laminated steel sheet and a method for manufacturing the same, and more particularly, to a method for producing a laminated steel sheet by applying a liquid ultraviolet curable adhesive composition to a colored steel sheet, And more particularly, to a high-performance laminar-colored steel sheet having excellent surface appearance and improved workability and functionality, and a method for producing the same.
라미나 칼라강판은 냉장고, 세탁기, TV 등 가전제품의 케이스 또는 각종 건축물의 내외장재로 이용되는 등 다양한 용도로 활용되고 있으며, 이와 같은 라미나 칼라강판은 용도상 가공성, 내구성뿐만 아니라, 생산성 및 우수한 심미성이 요구되는바 관련 기술에 대한 연구 개발이 활발하게 이루어지고 있다. Lamina color steel plates are used for a variety of purposes such as being used as cases of household appliances such as refrigerators, washing machines, televisions, and various interior and exterior materials of buildings. Such Lamina color steel plates are excellent in workability and durability, And research and development of related technologies are being actively carried out.
종래에는 라미나 강판 제조에 있어서, 열경화성 접착제(폴리에스테르계, 우레탄계, 아크릴계, 에폭시계) 또는 열가소성 접착제(핫멜트계, PE계)를 도금강판 상에 적용하여 도금강판과 광 투과성 필름을 합지시켰으나, 이 경우 휘발성 유기 용제의 사용으로 인하여 인체에 유해한 유기화합물(VOCs)이 발생하고, 이로 인한 수질 및 대기 오염이 가속화되었다. Conventionally, a plated steel sheet and a light-transmitting film are laminated by applying a thermosetting adhesive (polyester type, urethane type, acrylic type, epoxy type) or a thermoplastic adhesive (hot melt type, PE type) on a plated steel sheet in the production of a laminated steel sheet, In this case, harmful organic compounds (VOCs) are generated due to the use of volatile organic solvents, thereby accelerating water quality and air pollution.
또한, 접착제를 경화시키는 과정에서 필연적으로 가해지는 열에 의해 필름이 수축 및 팽창할 수 있으므로, 사용 가능한 필름 소재의 종류가 한정되거나 생산 효율이 저하 될수 밖에 없었으며, 경화 과정에서 불순물이 침투하거나 열이 고르게 전달되지 않아 기포가 발생하기도 하였으므로, 상대적으로 제품의 불량률이 높고 생산성이 낮은 문제점이 있었다. In addition, since the film can be shrunk and expanded due to heat inevitably applied in the process of curing the adhesive, the kind of usable film material is limited or the production efficiency is lowered. In the curing process, impurities penetrate or heat The bubbles are generated because they are not uniformly conveyed. Therefore, there is a problem that the defective rate of the product is relatively high and the productivity is low.
따라서, 상기 환경적인 문제점뿐만 아니라 생산성 및 제품의 품질을 향상시키기 위한 연구가 활발히 진행되었으며, 본 발명자들은 상기 문제점을 해결하기 위하여 기존의 제품과 차별화되는 제품을 개발하고자 하였다.
Therefore, research has been actively carried out to improve not only the environmental problems but also the productivity and the product quality. The inventors of the present invention have sought to develop a product differentiated from existing products in order to solve the above problems.
본 발명은 전술한 문제점을 해결하기 위해 안출된 것으로, 칼라강판의 제조과정에서 필름층 합지 후 열에 의한 변형을 최소화하기 위하여 자외선 경화성 접착 조성물을 적용하고자 하였으며, 이를 통해 친환경적이고, 내구성이 우수하며 접착층의 기포 발생이 최소화되어 우수한 표면 외관이 구현된 칼라강판 및 그 제조 방법을 제공하고자 한다.
DISCLOSURE OF THE INVENTION The present invention was conceived to solve the problems described above, and an object of the present invention is to provide an ultraviolet ray curable adhesive composition for minimizing deformation due to heat after laminating a film layer in a manufacturing process of a color steel sheet. And to provide a color steel sheet having excellent surface appearance and a method of manufacturing the same.
본 발명의 일 측면에 따르면, 소지 강판(110); 전처리층(120); 하도 도막층(130); 우레탄(메타)아크릴레이트 프리폴리머 45~65중량부, (메타)아크릴레이트 모노머 25~40중량부, 카르복실레이티드(메타)아크릴레이트 모너머 20~30중량부, 중량부, 광개시제 3~5중량부, 및 부착증진제 2~5중량부를 포함하는 자외선 경화성 접착층(140); 및 광 투과성 필름(150)을 순차적으로 포함하는 것인 고기능성 칼라강판이 제공된다. According to an aspect of the present invention, A
일 실시예에 따르면, 상기 광 투과성 필름(150)은 폴리메틸메타크릴레이트(PMMA), 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 폴리프로필렌(PP), 또는 폴리스티렌(PS) 필름일 수 있다. According to one embodiment, the light
일 실시예에 따르면, 상기 광 투과성 필름(150)은 표면에 패턴 또는 요철이 형성되어 있을 수 있다. According to one embodiment, the light-
일 실시예에 따르면, 상기 광 투과성 필름(150)의 두께는 10㎛ 내지 125㎛ 이고, 자외선 광 투과율이 70% 이상일 수 있다. According to one embodiment, the thickness of the light-
일 실시예에 따르면, 상기 자외선 경화성 접착층(140)의 두께는 3㎛ 내지 50㎛일 수 있다. According to one embodiment, the thickness of the ultraviolet curable
본 발명의 다른 측면에 따르면, 소지 강판(110) 상에 전처리층(120)을 형성하는 단계; 상기 전처리층(120) 상에 하도 도막층(130)을 형성하는 단계; 상기 하도 도막층(130) 상에 우레탄(메타)아크릴레이트 프리폴리머 45~65중량부, (메타)아크릴레이트 모노머 25~40중량부, 카르복실레이티드(메타)아크릴레이트 모너머 20~30중량부, 광개시제 3~5중량부, 및 부착증진제 2~5중량부를 포함하는 자외선 경화성 접착 조성물을 도포하는 단계; 상기 자외선 경화성 접착 조성물 상에 광 투과성 필름(150)을 합지하는 단계; 및 상기 합지된 광 투과성 필름(150) 상에 자외선을 조사하여 상기 자외선 경화성 접착 조성물을 경화시키는 단계;를 포함하는 것인 고기능성 칼라강판의 제조방법이 제공된다. According to another aspect of the present invention, there is provided a method of manufacturing a semiconductor device, comprising: forming a pretreatment layer (120) on a base steel sheet (110); Forming a
일 실시예에 따르면, 상기 합지된 광 투과성 필름(150) 상에 조사되는 자외선은 500mJ/cm2 내지 3,000mJ/cm2의 에너지 밀도로 조사되는 것 일 수 있다. According to one embodiment, ultraviolet light is irradiated on the laminated a light transmitting
일 실시예에 따르면, 상기 광 투과성 필름(150)의 두께는 10㎛ 내지 125㎛ 이고, 자외선 광 투과율이 70% 이상일 수 있다.
According to one embodiment, the thickness of the light-
상기 고기능성 칼라강판은 제조 공정에서 열에 의한 필름층의 변형이 최소화 되므로, 우수한 표면 외관이 구현될 수 있으며, 유기 용제에 의해 발생할 수 있는 환경오염이나 인체에 대한 유해성을 차단할 수 있다. The high-performance color steel sheet minimizes the deformation of the film layer due to heat in the manufacturing process, so that it can realize excellent surface appearance and can prevent environmental pollution or harmfulness to the human body caused by the organic solvent.
또한, 상기 고기능성 칼라강판은 열에 의한 경화 공정에서 발생할 수 있는 기포가 발생하지 않으며, 접착층의 경화속도가 빠르므로 생산성이 향상될 수 있다.In addition, the high-performance color steel sheet does not generate bubbles that can be generated in the heat curing process, and the curing speed of the adhesive layer is high, so that the productivity can be improved.
다만, 본 발명의 효과는 상기한 효과로 한정되는 것은 아니며, 본 발명의 상세한 설명 또는 특허청구범위에 기재된 발명의 구성으로부터 추론 가능한 모든 효과를 포함하는 것으로 이해되어야 한다.
It should be understood, however, that the effects of the present invention are not limited to the above-described effects, but include all effects that can be deduced from the detailed description of the present invention or the configuration of the invention described in the claims.
도 1은 본 발명의 일 실시예에 따른 고기능성 라미나 칼라 강판의 단면도를 나타낸 것이다.
도 2는 본 발명의 일 실시예에 따른 고기능성 라미나 칼라 강판의 제조방법을 흐름도로 나타낸 것이다.
도 3은 일 실시예에 따른 필름 합지 공정을 개략적으로 도식화한 것이다.1 is a sectional view of a high-performance laminated steel sheet according to an embodiment of the present invention.
2 is a flowchart illustrating a method of manufacturing a high-performance laminated steel sheet according to an exemplary embodiment of the present invention.
Figure 3 is a schematic representation of a film laminating process in accordance with one embodiment.
이하에서는 첨부한 도면을 참조하여 본 발명을 설명하기로 한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며, 따라서 여기에서 설명하는 실시예로 한정되는 것은 아니다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 유사한 부분에 대해서는 유사한 도면 부호를 붙였다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described with reference to the accompanying drawings. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. In order to clearly illustrate the present invention, parts not related to the description are omitted, and similar parts are denoted by like reference characters throughout the specification.
명세서 전체에서, 어떤 부분이 다른 부분과 "연결"되어 있다고 할 때, 이는 "직접적으로 연결"되어 있는 경우뿐 아니라, 그 중간에 다른 부재를 사이에 두고 "간접적으로 연결"되어 있는 경우도 포함한다. 또한 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 구비할 수 있다는 것을 의미한다.Throughout the specification, when a part is referred to as being "connected" to another part, it includes not only "directly connected" but also "indirectly connected" . Also, when an element is referred to as "comprising ", it means that it can include other elements, not excluding other elements unless specifically stated otherwise.
본 명세서에서 사용되는 용어는 본 발명에서의 기능을 고려하면서 가능한 현재 널리 사용되는 일반적인 용어들을 선택하였으나, 이는 당 분야에 종사하는 기술자의 의도 또는 판례, 새로운 기술의 출현 등에 따라 달라질 수 있다. 또한, 특정한 경우는 출원인이 임의로 선정한 용어도 있으며, 이 경우 해당되는 발명의 설명 부분에서 상세히 그 의미를 기재할 것이다. 따라서 본 발명에서 사용되는 용어는 단순한 용어의 명칭이 아닌, 그 용어가 가지는 의미와 본 발명의 전반에 걸친 내용을 토대로 정의되어야 한다.
As used herein, the terminology used herein is intended to encompass all commonly used generic terms that may be considered while considering the functionality of the present invention, but this may vary depending upon the intent or circumstance of the skilled artisan, the emergence of new technology, and the like. Also, in certain cases, there may be a term selected arbitrarily by the applicant, in which case the meaning thereof will be described in detail in the description of the corresponding invention. Therefore, the term used in the present invention should be defined based on the meaning of the term, not on the name of a simple term, but on the entire contents of the present invention.
이하 첨부된 도면을 참조하여 본 발명의 실시예를 상세히 설명하기로 한다.
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.
고기능성 High functionality
라미나Lamina
칼라강판Color steel plate
도 1은 본 발명의 일 실시예에 따른 고기능성 라미나 칼라 강판의 단면도를 나타낸 것이다. 1 is a sectional view of a high-performance laminated steel sheet according to an embodiment of the present invention.
본 발명의 일 측면에 따르면, 소지 강판(110); 전처리층(120); 하도 도막층(130); 우레탄(메타)아크릴레이트 프리폴리머 45~65중량부, (메타)아크릴레이트 모노머 25~40중량부, 카르복실레이티드(메타)아크릴레이트 모너머 20~30중량부, 중량부, 광개시제 3~5중량부, 및 부착증진제 2~5중량부를 포함하는 자외선 경화성 접착층(140); 및 광 투과성 필름(150)을 순차적으로 포함하는 것인 고기능성 칼라강판이 제공된다. According to an aspect of the present invention, A
상기 칼라 강판은 소지 강판(110); 전처리층(120); 하도 도막층(130); 상도 도막층; 자외선 경화성 접착층(140) 및 광 투과성 필름(150)을 순차적으로 포함할 수 있다. The color steel plate includes a
상기 소지 강판(110)은 통상의 연속도장공정에 사용되는 용융 아연도금강판으로써, 아연 50~55%에 알루미늄 도금강판(수퍼갈륨강판) 또는 용융도금강판(GI), 크롬(CR), 알루미늄(Al), 스테인리스(Stainless)등 다양한 소지를 사용할 수 있다. The
상기 소지층은 아연도금강판으로 입체 무늬 또는 다양한 문양이 형성된 것을 사용할 수 있으며, 필요에 따라 가전 제품의 케이스 또는 건축물 내, 외부 마감재에 사용되는 다양한 강판류가 적용될 수 있다. The base layer may be a galvanized steel sheet having a three-dimensional pattern or a variety of patterns. If necessary, a variety of steel sheets used in cases, buildings, and exterior finishes of household appliances may be applied.
일 실시예에 따르면, 상기 소지 강판(110) 상에 전처리층(120)이 형성될 수 있다. According to one embodiment, the
상기 전처리층(120)은 전술한 소지 강판(110)의 표면에 부착된 이물질을 제거함으로써, 상기 소지 강판(110)과 하도 도막층(130)간의 부착성을 높이기 위해 형성할 수 있다. The
상기 전처리층(120)은 알칼리 탈지제로 세정하고 그 위에 크로메이트를 피막 처리하여 형성할 수 있으나, 이에 한정되지 않으며 가전용으로 제조시 논크롬(Non-Cr) 처리도 가능하다. The
상기 크로메이트 처리를 위하여 크롬산 또는 중크롬산염을 주성분으로 하는 용액 속에 강판을 넣어 방청 피막을 형성할 수 있으며, 크로메이트와 인산염의 대체물질로서 알콕시실란(Alkoxysilane)을 사용할 수도 있다. For the chromate treatment, a steel sheet may be put in a solution containing chromic acid or dichromate as a main component to form a rust preventive film. Alternatively, an alkoxysilane may be used as a substitute for chromate and phosphate.
일 실시예에 따르면, 상기 소지 강판(110)의 전처리층(120) 상에 하도 도막층(130)이 형성될 수 있다. According to one embodiment, the undercoating
상기 하도 도막층(130)은 강판의 내구성을 높이고, 하단의 전처리된 소지 강판(110)과 상단의 상도 도막층의 계면의 결합력을 증가시켜 도장이 원활하게 이루어질 수 있도록 한다. The
상업적으로 구득가능한 폴리에스테르계 하도로서는 고려화학의 YP500 시리즈, 건설화학의 8600시리즈, 삼화페인트의 화인코트 P-331, 시그마 삼성 코팅의 K004 시리즈 등이 있으며, 이에 한정되지 않는다. Commercially available polyester grades include, but are not limited to YP500 series of Koryo Chemical, 8600 series of construction chemicals, Fine coat P-331 of Samhwa paint, and K004 series of Sigma Samsung coating.
상기 하도 도막층(130)은 일반적인 내식성, 상도 도막층과의 부착성을 제공할 뿐만 아니라, 소재 강판과 상도 간 계면에서 완충 역할을 하므로 가공시 발생되는 소재의 균열이 상도층까지 전달되지 않고 하도층에서 흡수되도록 할 수 있다. Since the
상기 하도에 사용되는 안료는 내식성을 위하여 방청안료를 일부 사용하고, 상도와 마찬가지로 PCM 도료에 사용하는 유기, 무기 안료를 용도에 맞게 선택적으로 사용할 수 있다.The pigment used for the undercoat may be selected from a group of anticorrosive pigments for corrosion resistance, and organic and inorganic pigments used for PCM paints, as in the case of the top coat.
일 실시예에 따르면, 도면에 나타나 있지 않으나, 상기 하도 도막층(130) 상에 상도 도막층(미도시)이 형성될 수 있다. According to one embodiment, although not shown in the drawings, a top coat layer (not shown) may be formed on the
상기 상도 도막층(미도시)은 칼라강판의 마감 표면을 정리하고 원하는 색감이나 광을 부여하기 위해 형성될 수 있다. The upper coating layer (not shown) may be formed to arrange the finished surface of the color steel sheet and to impart a desired color or light.
다만, 상기 하도 도막층(130) 및 상도 도막층은 반드시 별개의 도막층으로 형성될 필요는 없으며, 필요에 따라 심미성과 기능성을 보유한 하나의 도막층으로 형성할 수도 있다. However, the
일 실시예에 따르면, 상기 하도 도막층(130) 또는 상도 도막층(미도시) 상에는 자외선 경화성 접착층(140)이 형성될 수 있다. According to one embodiment, an ultraviolet curable
상기 자외선 경화성 접착층(140)은 상기 하도 도막층(130) 상에 자외성 경화성 접착 조성물이 도포된 후, 자외선에 의해 경화되어 형성될 수 있다. The ultraviolet curable
상기 자외선 경화성 접착 조성물은 기존의 열경화성 접착 조성물과 비교하여 부착성, 선영도, 경도 및 가공성이 뛰어나고, 도장 후 열경화 공정이 불필요하므로, 열에 의한 변형이 최소화되며, 경화 속도가 빠르므로 생산성 및 작업성이 우수하다. The ultraviolet ray curable adhesive composition is excellent in adhesion, linearity, hardness and workability as compared with conventional thermosetting adhesive compositions, and since heat curing is not required after coating, the ultraviolet ray curable adhesive composition minimizes heat deformation, It is excellent.
상기 자외선 경화성 접착 조성물은 우레탄(메타)아크릴레이트 프리폴리머 45~65중량부, (메타)아크릴레이트 모노머 25~40중량부, 카르복실레이티드(메타)아크릴레이트 모너머 20~30중량부, 광개시제 3~5중량부, 및 부착증진제 2~5중량부를 포함할 수 있다. The ultraviolet curable adhesive composition comprises 45 to 65 parts by weight of a urethane (meth) acrylate prepolymer, 25 to 40 parts by weight of a (meth) acrylate monomer, 20 to 30 parts by weight of a carboxylate (meth) acrylate monomer, To 5 parts by weight of the adhesion promoter, and 2 to 5 parts by weight of the adhesion promoter.
상기 자외선 경화성 접착 조성물은 적어도 하나 이상의 디이소시아네이트 화합물, 적어도 하나 이상의 디올 화합물, 폴리올 및 수산기를 갖는 (메타)아크릴레이트의 공중합물인 우레탄(메타)아크릴레이트 프리폴리머, (메타)아크릴레이트 모너머, 및 카르복실레이티드(메타)아크릴레이트 모너머를 포함할 수 있다.The ultraviolet curable adhesive composition comprises a urethane (meth) acrylate prepolymer, a (meth) acrylate monomer, and a urethane acrylate monomer, which are a copolymer of at least one diisocyanate compound, at least one diol compound, (Meth) acrylate monomers.
상기 우레탄(메타)아크릴레이트 프리폴리머는 디이소시아네이트 화합물, 디올 화합물, 폴리올, 수산기 함유 (메타)아크릴레이트의 공중합물일 수 있다.The urethane (meth) acrylate prepolymer may be a copolymer of a diisocyanate compound, a diol compound, a polyol, and a hydroxyl group-containing (meth) acrylate.
이 때, 상기 우레탄(메타)아크릴레이트 프리폴리머는 중량평균분자량이 3000 내지 20000이고 분자당 평균우레탄 결합이 6내지 25개 존재하는 것을 특징으로 한다. 또한, 상기 디올 화합물은 200미만의 분자량을 갖는 단분자 화합물이며, 상기 폴리올은 중량평균분자량이 200내지 3000일 수 있다. In this case, the urethane (meth) acrylate prepolymer has a weight average molecular weight of 3,000 to 20,000 and 6 to 25 average urethane bonds per molecule. In addition, the diol compound is a monomolecular compound having a molecular weight of less than 200, and the polyol may have a weight average molecular weight of 200 to 3000.
상기 우레탄(메타)아크릴레이트 프리폴리머는 접착 조성물의 총 중량을 기준으로, 35~70중량부, 바람직하게는 45~65중량부가 포함될 수 있다.The urethane (meth) acrylate prepolymer may contain 35 to 70 parts by weight, preferably 45 to 65 parts by weight, based on the total weight of the adhesive composition.
상기 우레탄(메타)아크릴레이트 프리폴리머가 35중량부 미만이며, 가공성 내지 부착력이 저하될 수 있으며, 70중량부를 초과하면 도막이 과도하게 유연해져 오히려 부착력이 저하될 수 있다.The urethane (meth) acrylate prepolymer may be less than 35 parts by weight, and the workability or adhesion may be deteriorated. When the amount of the urethane (meth) acrylate prepolymer is more than 70 parts by weight, the coating may become excessively soft and adherence may be deteriorated.
또한, 상기 우레탄(메타)아크릴레이트 프리폴리머가 중량 평균 분자량이 3000 미만이면 경화된 도장의 인장강도 및 경도가 과도하게 높아져, 신율이 낮아지고 부착성 및 가공성이 저하되며, 20000 초과이면 그 반대의 결과가 발생할 수 있으므로 적절한 범위 내에서 유지하는 것이 바람직하다. If the weight average molecular weight of the urethane (meth) acrylate prepolymer is less than 3,000, the tensile strength and hardness of the cured coating excessively increase, and the elongation is lowered and the adhesiveness and workability are lowered. On the other hand, So it is desirable to keep it within an appropriate range.
또한, 디이소시아네이트 화합물, 중량 평균 분자량 200 미만의 디올 화합물, 중량 평균 분자량 200 내지 3000인 폴리올의 혼합물에 수산기 함유 (메타)아크릴레이트를 공중합시켜 합성된 우레탄(메타)아크릴레이트 프리폴리머를 자외선 경화성 도료 조성물에 사용함으로써, 가공성, 부착력, 및 경도가 향상될 수 있다.Further, a urethane (meth) acrylate prepolymer synthesized by copolymerizing a hydroxyl group-containing (meth) acrylate with a mixture of a diisocyanate compound, a diol compound having a weight average molecular weight of less than 200 and a polyol having a weight average molecular weight of 200 to 3000, , The workability, the adhesion, and the hardness can be improved.
상기 디이소시아네이트 화합물로는 지방족, 지환족 및 방향족 디이소시아네이트 화합물이 모두 사용될 수 있으며, 이 중 이소포론디이소시아네이트, 2,4-톨루엔디이소시아네이트 및 그 이성질체, 1,6-헥사메틸렌디이소시아네이트, 라이신디이소시아네이트, 트리메틸헥사메틸렌디이소시아네이트, 2,2-비스-4′-프로판이소시아네이트, 6-이소프로필-1,3-페닐디이소시아네이트, 비스(2-이소시아네이트에틸)-퓨마레이트, 1,6-헥산디이소시아네이트, 4,4′-바이페닐렌디이소시아네이트, 3,3′-디메틸페닐렌디이소시아네이트, 3,3′-디메틸-4,4′-디페닐메탄디이소시아네이트, p-페닐렌디이소시아네이트, m-페닐렌디이소시아네이트, 1,5-나프탈렌디이소시아네이트, 1,4-자일렌디이소시아네이트, 1,3-자일렌디이소시아네이트에서 하나를 선택하거나 또는 이들의 혼합물을 사용할 수 있다. As the diisocyanate compound, aliphatic, alicyclic, and aromatic diisocyanate compounds may be used. Of these, isophorone diisocyanate, 2,4-toluene diisocyanate and its isomers, 1,6-hexamethylene diisocyanate, Isocyanate, isocyanate, trimethylhexamethylene diisocyanate, 2,2-bis-4'-propane isocyanate, 6-isopropyl-1,3-phenyldiisocyanate, bis (2- Isocyanate, 4,4'-biphenylene diisocyanate, 3,3'-dimethylphenylene diisocyanate, 3,3'-dimethyl-4,4'-diphenylmethane diisocyanate, p-phenylene diisocyanate, m- Isocyanate, 1,5-naphthalene diisocyanate, 1,4-xylene diisocyanate, 1,3-xylene diisocyanate, or a mixture thereof Can be used.
일 실시예에 따르면, 상기 디이소시아네이트 화합물로는 2,4-톨루엔디이소시아네이트 및 그 이성질체, 1,6-헥사메틸렌디이소시아네이트, 이소포론디이소시아네이트에서 하나를 선택하거나 또는 이들의 혼합물을 사용할 수 있으나, 이에 한정되는 것은 아니다. According to one embodiment, the diisocyanate compound may be selected from among 2,4-toluene diisocyanate and its isomers, 1,6-hexamethylene diisocyanate, and isophorone diisocyanate, or a mixture thereof. However, But is not limited thereto.
상기 디올 화합물은 분자량 200 미만의 단분자를 사용하는 것이 바람직하며, 예컨대, 에틸렌 글리콜, 프로필렌 글리콜, 1.3-부탄디올, 1.4-부탄디올, 1.5-펜탄디올, 1.6-헥산디올, 네오펜틸글리콜, 비스페놀A, 비스페놀F, 디사이크로 펜탄디올, 또는 이들의 혼합물을 사용할 수 있다. The diol compound is preferably a monomer having a molecular weight of less than 200, and examples thereof include ethylene glycol, propylene glycol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6- hexanediol, neopentyl glycol, bisphenol A, Bisphenol F, dicyclopentanediol, or a mixture thereof.
상기 폴리올은 중량 평균 분자량이 200 내지 3000 일 수 있으며, 중량 평균 분자량이 200 미만이면 도막의 경도가 높아져 부착성이 저하될 수 있고, 3,000을 초과하면 도막이 과도하게 유연해질 수 있으므로, 적절한 범위 내에서 유지하는 것이 바람직하다. The polyol may have a weight average molecular weight of 200 to 3000. If the weight average molecular weight is less than 200, the hardness of the coating film may increase and the adhesion may be deteriorated. If the weight average molecular weight is more than 3,000, the coating film may become excessively flexible, .
상기 폴리올로는 폴리에테르 폴리올, 폴리에스테르 폴리올, 폴리카보네이트 폴리올 또는 폴리카프로락톤 폴리올을 사용할 수 있으나, 이에 한정되는 것은 아니다.The polyol may be a polyether polyol, a polyester polyol, a polycarbonate polyol or a polycaprolactone polyol, but is not limited thereto.
상기 디이소시아네이트로 치환된 우레탄 프리폴리머(prepolymer)의 양 말단에 이중결합을 도입하는 방법은 특별히 한정되지 않으나, 우레탄 프리폴리머 1몰에 대해 2몰의 수산기 함유 (메타)아크릴레이트를 반응시키는 프리폴리머법을 사용하는 것이 바람직하다.A method of introducing a double bond at both ends of a urethane prepolymer substituted with the diisocyanate is not particularly limited, but a prepolymer method in which 2 mol of a hydroxyl group-containing (meth) acrylate is reacted with 1 mol of a urethane prepolymer is used .
상기 수산기 함유 (메타)아크릴레이트는 알킬기에 2~6개의 탄소를 갖는 것으로, 2-하이드록시에틸(메타)아크릴레이트, 2-하이드록시프로필(메타)아크릴레이트, 2-하이드록시부틸(메타)아크릴레이트 중에서 하나를 선택하거나 또는 이들의 혼합물을 사용할 수 있다.The hydroxyl group-containing (meth) acrylate has 2 to 6 carbons in the alkyl group, and examples thereof include 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2- Acrylate, or a mixture thereof may be used.
상기 우레탄(메타)아크릴레이트 프리폴리머에 희석하는 (메타)아크릴레이트 모노머는 단관능성 모노머와 다관능성 모노머를 사용할 수 있다.The (meth) acrylate monomer to be diluted with the urethane (meth) acrylate prepolymer may be a monofunctional monomer and a multi-functional monomer.
상기 단관능성 모노머로는 디에틸아미노에틸(메타)아크릴레이트, 디메틸아미노에틸(메타)아크릴레이트, t-옥틸(메타)아크릴레이트, N,N-디메틸(메타)아크릴레이트, N-비닐카프로락탐, N-비닐피롤리돈, 이소부톡시(메타)아크릴아마이드, 디아세톤(메타)아크릴아마이드, 보닐(메타)아크릴레이트, 이소보닐(메타)아크릴레이트, 트리사이클로데카닐(메타)아크릴레이트, 디사이클로펜타닐(메타)아크릴레이트, 디사이클로펜타디엔(메타)아크릴레이트, 메톡시폴리프로필렌글리콜(메타)아크릴레이트, 메톡시폴리에틸렌글리콜(메타)아크릴레이트, 에톡시에톡시에틸(메타)아크릴레이트, 메톡시에틸렌글리콜(메타)아크릴레이트, 폴리프로필렌글리콜모노(메타)아크릴레이트, 폴리에틸렌글리콜모노(메타)아크릴레이트, 페녹시에틸(메타)아크릴레이트, 사이크로헥실(메타)아크릴레이트, 벤질(메타)아크릴레이트, 에폭시디에틸렌글리콜(메타)아크릴레이트, 부톡시에틸(메타)아크릴레이트, 테트라하이드로퍼퓨릴(메타)아크릴레이트, 스티어릴(메타)아크릴레이트, 옥타데실(메타)아크릴레이트, 라우릴(메타)아크릴레이트, 도데실(메타)아크릴레이트, 이소데실(메타)아크릴레이트, 노닐(메타)아크릴레이트, 2-에틸헥실(메타)아크릴레이트, 이소아밀(메타)아크릴레이트, t-부틸(메타)아크릴레이트, 이소부틸(메타)아크릴레이트, 부틸(메타)아크릴레이트, 이소프로필(메타)아크릴레이트, 프로필(메타)아크릴레이트, 에틸(메타)아크릴레이트, 메틸(메타)아크릴레이트 중에서 하나를 선택하거나 또는 이들의 혼합물을 사용할 수 있다.Examples of the monofunctional monomer include diethylaminoethyl (meth) acrylate, dimethylaminoethyl (meth) acrylate, t-octyl (meth) acrylate, N, N- (Meth) acrylate, N-vinylpyrrolidone, isobutoxy (meth) acrylamide, diacetone (meth) acrylamide, (Meth) acrylate, methoxypolypropylene glycol (meth) acrylate, methoxypolyethylene glycol (meth) acrylate, ethoxyethoxyethyl (meth) acrylate, (Meth) acrylates such as methoxyethylene glycol (meth) acrylate, polypropylene glycol mono (meth) acrylate, polyethylene glycol mono (meth) acrylate, phenoxyethyl (Meth) acrylate, benzyl (meth) acrylate, epoxy diethylene glycol (meth) acrylate, butoxyethyl (meth) acrylate, tetrahydroperfuryl (Meth) acrylate, isooctyl (meth) acrylate, isooctyl (meth) acrylate, lauryl (meth) acrylate, dodecyl (Meth) acrylate, isopropyl (meth) acrylate, ethyl (meth) acrylate, isopropyl (meth) acrylate, Acrylate, and methyl (meth) acrylate, or a mixture thereof may be used.
또한, 상기 다관능성 모노머로는 트리메틸올프로판트리(메타)아크릴레이트, 펜타에리트리톨트리(메타)아크릴레이트, 에틸렌글리콜디(메타)아크릴레이트, 디프로필렌글리콜디(메타)아크릴레이트, 1,6-헥산디올디(메타)아크릴레이트, 트리프로필렌글리콜디(메타)아크릴레이트, 트리메틸올프로판트리옥시에틸(메타)아크릴레이트, 트리사이크로데칸디메탄올디(메타)아크릴레이트 중에서 하나를 선택하거나 또는 이들의 혼합물을 사용할 수 있으나 이에 한정되는 것은 아니다.Examples of the polyfunctional monomer include trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, ethylene glycol di (meth) acrylate, dipropylene glycol di (meth) (Meth) acrylate, trimethylolpropane trioxyethyl (meth) acrylate, tricyclodecane dimethanol di (meth) acrylate, or a mixture of Mixtures of these may be used, but are not limited thereto.
상기 (메타)아크릴레이트 모노머는 20~45중량부 포함될 수 있으며, 바람직하게는 25~40중량부 포함될 수 있다. 25중량부 미만인 경우 도막이 과도하게 유연해져 경도 및 내스크레치성이 저하될 수 있고, 40중량부 초과인 경우 도막의 과도하게 경화되어 가공성 내지 부착력이 저하될 수 있다.The (meth) acrylate monomer may be contained in an amount of 20 to 45 parts by weight, and preferably 25 to 40 parts by weight. When the amount is less than 25 parts by weight, the coating film may become excessively soft and the hardness and scratch resistance may be deteriorated. If the amount is more than 40 parts by weight, the coating film may be excessively cured and workability or adhesion may be deteriorated.
또한, 상기 카르복실레이티드(메타)아크릴레이트 모노머는 2-(메타)아크릴로일옥시에틸석시네이트, 2-(메타)아크릴로일옥시헥사하이드로프탈레이트, 2-(메타)아크릴로일옥시에틸프탈레이트, 2-(메타)아크릴로일옥시에틸-2-하이드록시에틸프탈레이트, 및 β-카르복실에틸(메타)아크릴레이트 중 하나 이상을 사용할 수 있으나 이에 한정되지 아니하며, 바람직하게는 β-카르복실에틸(메타)아크릴레이트를 사용할 수 있다. The carboxylated (meth) acrylate monomer may be at least one selected from the group consisting of 2- (meth) acryloyloxyethyl succinate, 2- (meth) acryloyloxyhexahydrophthalate, 2- (Meth) acrylate, ethyl phthalate, 2- (meth) acryloyloxyethyl-2-hydroxyethyl phthalate, and beta -carboxyl ethyl (meth) acrylate. Ethyl (meth) acrylate can be used.
상기 카르복실레이티드(메타)아크릴레이트 모노머는 15~35 중량부 포함될 수 있으며, 바람직하게는 20~30중량부 포함될 수 있다. 20중량부 미만인 경우 내구성이 저하될 수 있으며, 30중량부 초과인 경우 도막의 경도가 과도하게 증가하여 가공성이 저하되고 외력에 의해 갈라짐이 발생할 수 있다. The carboxylated (meth) acrylate monomer may be contained in an amount of 15 to 35 parts by weight, and preferably 20 to 30 parts by weight. If it is less than 20 parts by weight, durability may be deteriorated. If it is more than 30 parts by weight, the hardness of the coating film may excessively increase, resulting in deterioration of workability and cracking due to external force.
한편, 상기 광개시제는 1-하이드록시사이클로헥실페닐케톤, 2,2-디메톡시-2-페닐-아세토페논, 벤즈알데히드, 안트라퀴논, 3-메틸아세토페논, 4-클로로벤조페논, 4,4′-디메톡시벤조페논, 벤조인프로필에테르, 벤조인에틸에테르, 1-(4-이소프로필-페놀)-2-하이드록시-2-메틸프로판-1-온, 티오잔톤, 벤조페논, 2,4,6-트리메틸벤조일-디페닐포스핀 중에서 적어도 하나 이상을 혼합하여 사용할 수 있다. On the other hand, the photoinitiator may be 1-hydroxycyclohexyl phenyl ketone, 2,2-dimethoxy-2-phenyl-acetophenone, benzaldehyde, anthraquinone, 3-methylacetophenone, 4-chlorobenzophenone, Benzoin ethyl ether, 1- (4-isopropyl-phenol) -2-hydroxy-2-methylpropan-1-one, thioxanthone, benzophenone, 2,4- 6-trimethylbenzoyl-diphenylphosphine may be mixed and used.
상업적으로 공급되는 광개시제 제품으로는 Irgacure184, 651,500,819,907,1800(시바가이기사) 등과 Darocure 1116,1173(머크사), Lucirine LR8728(바스프사), Micure HP-8, TPO, CP-4, BK-6(미원상사) 등이 사용 될 수 있으나, 이에 한정되는 것은 아니다.Commercially available photoinitiator products include Irgacure 184, 651, 500, 819, 907, 1800 (Shiba Kagi), Darocure 1116, 1173 (Merck), Lucirine LR8728 (BASF), Micure HP-8, TPO, CP- And the like may be used, but the present invention is not limited thereto.
상기 광개시제는 상기 자외성 경화성 접착 조성물의 총 중량을 기준으로 1~6중량%, 바람직하게는 3~5중량%로 포함될 수 있으며, 1중량% 미만으로 포함되면 경화성이 떨어지고, 6중량%를 초과하여 포함되면 도막의 황변, 가경화로 인한 부착성 내지 가공성이 저하될 수 있으므로 적절한 범위 내에서 조절하는 것이 바람직하다. The photoinitiator may be contained in an amount of 1 to 6% by weight, preferably 3 to 5% by weight based on the total weight of the ultraviolet curable adhesive composition. When the content is less than 1% by weight, the curing property is deteriorated. , It is preferable to control the coating film within a suitable range, because the yellowing of the coating film and adherability and workability due to hardening of the coating film may be deteriorated.
상기 부착증진제로는 인산 에스테르계를 사용할 수 있는데, 상업용으로 공급되는 인산 에스테르계 부착증진제 제품으로는 Lubrizol 2063 (Lubrizol 사), PAM-200 (Rhodia 사) 등을 사용 할 수 있으며, 이에 한정되는 것은 아니다.As the adhesion promoting agent, phosphoric acid ester-based agents can be used. Lubrizol 2063 (Lubrizol company), PAM-200 (Rhodia corporation) or the like can be used as a phosphoric acid ester adhesion promoter product supplied for commercial use. no.
또한, 자외선 경화성 접착 조성물은 필요에 따라 산화방지제, 광흡수제, 광안정제, 실란커플링제, 열중합금지제, 유기안료, 무기안료, 평활제, 분산제, 및 소포제 중 하나 이상의 첨가제를 더 포함할 수도 있다.The ultraviolet curable adhesive composition may further include at least one additive agent selected from an antioxidant, a light absorber, a light stabilizer, a silane coupling agent, a thermosetting agent, an organic pigment, an inorganic pigment, a smoothing agent, .
일 실시예에 따르면, 상기 광 투과성 필름(150)은 폴리메틸메타크릴레이트(PMMA), 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 폴리프로필렌(PP), 또는 폴리스티렌(PS) 필름일 수 있다. According to one embodiment, the
일 실시예에 따르면, 상기 광 투과성 필름(150)은 표면에 패턴 또는 요철이 형성되어 있을 수 있다. According to one embodiment, the light-
상기 패턴(pattern)은 특정한 형태를 가지는 유형, 모형 등을 의미하며, 예컨대 생활속에서 쉽게 접할 수 있는 문자, 도형, 숫자, 동물, 꽃, 스트라이프 문양 등일 수도 있으나, 이에 한정되는 것은 아니다. The pattern may be a type, a model, or the like having a specific shape. For example, the pattern may be a letter, a figure, a number, an animal, a flower, a stripe pattern, and the like that are easily accessible in daily life.
상기 요철은 일정한 무늬를 이루는 필름 외면에 형성된 미세한 양각 또는 음각의 구조를 지칭하는 것으로, 스크래치, 엠보스(emboss) 또는 헤어라인(hair line)과 같은 입체무늬를 형성할 수 있으며, 상기 요철이 형성된 광 투과성 필름(150)을 통해 외관이 더욱 화려한 칼라무늬 강판을 구현할 수 있다. The irregularities refer to a fine embossed or intaglio structure formed on the outer surface of the film which forms a uniform pattern, and it is possible to form a three-dimensional pattern such as a scratch, an emboss or a hair line, A color patterned steel sheet having a brighter appearance can be realized through the
일 실시예에 따르면, 상기 광 투과성 필름(150)의 두께는 10㎛ 내지 125㎛ 이고, 자외선 광 투과율이 70% 이상일 수 있다. According to one embodiment, the thickness of the light-
상기 광 투과성 필름(150)의 두께가 10㎛ 미만인 경우 압착시 필름의 구김 자국이 하부 도막층에 전이될 수 있고, 상도 도막층 표면의 평활도가 저하되어 고선영성을 구현하기 어려우며, 125㎛ 초과인 경우 상도 도막층의 미경화가 발생할 수 있고, 필름의 가격 상승으로 생산 원가가 상승할 수 있다.When the thickness of the light-
또한, 자외선 광 투과율이 70% 미만인 경우 상도 도막층(20)의 경화 불량으로 표면 외관의 불량이 야기될 수 있으며, 하부 도막층의 문양이나 외관이 명확하게 드러나지 않아 칼라 강판의 미려함이 저하될 수 있다. If the ultraviolet light transmittance is less than 70%, defective surface appearance may occur due to poor curing of the top coat layer 20, and the pattern or appearance of the bottom coat layer may not be clearly revealed, which may degrade the quality of the colored steel sheet have.
일 실시예에 따르면, 상기 자외선 경화성 접착층(140)의 두께는 3㎛ 내지 50㎛일 수 있다. According to one embodiment, the thickness of the ultraviolet curable
상기 자외선 경화성 접착층(140)의 두께가 3㎛ 미만인 경우 접착층의 내구성이 저하되어 외력에 의해 상부의 광 투과성 필름(150)이 쉽게 탈리될 수 있으며, 두께가 50㎛ 초과인 경우 접착층의 유연성 및 가공성이 저하되고, 외력에 의해 접착층에 갈라짐이 발생할 수 있어 강판 표면의 불량률이 증가할 수 있다.
When the thickness of the ultraviolet-curing
고기능성 High functionality
라미나Lamina
칼라강판Color steel plate
제조 방법 Manufacturing method
본 발명의 다른 측면에 따르면, 소지 강판(110) 상에 전처리층(120)을 형성하는 단계(S1); 상기 전처리층(120) 상에 하도 도막층(130)을 형성하는 단계(S2); 상기 하도 도막층(130) 상에 우레탄(메타)아크릴레이트 프리폴리머 45~65중량부, (메타)아크릴레이트 모노머 25~40중량부, 카르복실레이티드(메타)아크릴레이트 모너머 20~30중량부, 광개시제 3~5중량부, 및 부착증진제 2~5중량부를 포함하는 자외선 경화성 접착 조성물을 도포하는 단계(S3); 상기 자외선 경화성 접착 조성물 상에 광 투과성 필름(150)을 합지하는 단계(S4); 및 상기 합지된 광 투과성 필름(150) 상에 자외선을 조사하여 상기 자외선 경화성 접착 조성물을 경화시키는 단계(S5);를 포함하는 것인 고기능성 칼라강판의 제조방법이 제공된다. According to another aspect of the present invention, there is provided a method of manufacturing a semiconductor device, comprising: forming a pretreatment layer (120) on a base steel sheet (110); (S2) forming a lower coating layer (130) on the pretreatment layer (120); (Meth) acrylate prepolymer, 45 to 65 parts by weight of a urethane (meth) acrylate prepolymer, 25 to 40 parts by weight of a (meth) acrylate monomer, 20 to 30 parts by weight of a carboxylate 3 to 5 parts by weight of a photoinitiator, and 2 to 5 parts by weight of an adhesion promoting agent (S3); (S4) bonding the light-
도 2는 본 발명의 일 실시예에 따른 고기능성 라미나 칼라 강판의 제조방법을 흐름도로 나타낸 것이다. 2 is a flowchart illustrating a method of manufacturing a high-performance laminated steel sheet according to an exemplary embodiment of the present invention.
상기 고기능성 칼라강판의 제조 방법은 소지 강판(110) 상에 전처리층(120)을 형성하는 단계; 하도 도막층(130)을 형성하는 단계; 자외선 경화성 접착 조성물을 도포하는 단계; 광 투과성 필름(150)을 합지하는 단계; 및 자외선을 조사하여 상기 자외선 경화성 접착 조성물을 경화시키는 단계를 포함할 수 있다. The method for manufacturing a high-performance color steel sheet includes the steps of: forming a
즉, 상기 칼라 강판은 상기 소지 강판(110) 상에 도막층을 순차적으로 형성한 후, 상기 도막층 상에 광 투과성 필름(150)을 합지하여 제조할 수 있다. That is, the colored steel sheet may be manufactured by sequentially forming a coating layer on the
이 때, 상기 도막층 상에 자외선 경화성 접착 조성물을 도포한 후 광 투과성 필름(150)을 합지할 수 있으며, 광 투과성 필름(150)을 합지한 후 자외선을 조사하여 상기 도포된 자외선 접착 조성물을 경화시킬 수 있다.In this case, the ultraviolet ray-curable adhesive composition may be coated on the coating layer, followed by laminating the light-
상기 자외선 접착 조성물을 도포하는 방법을 특별히 한정되지 않으며, 예컨대, 롤 코터(Coater), 바(Bar) 코터, 스프레이 코터를 이용하여 도포할 수 있다. The method of applying the ultraviolet ray-curable composition is not particularly limited, and it can be applied using, for example, a roll coater, a bar coater or a spray coater.
도 3은 일 실시예에 따른 필름 합지 공정을 개략적으로 도식화 한 것이다. Figure 3 is a schematic representation of a film laminating process in accordance with one embodiment.
통상적으로 칼라 강판은 띠 형태의 소지 강판(110)이 이송 롤러(210)에 의해 이송되며, 연속적으로 도막층이 형성되어 제조된다.Typically, a colored steel sheet is manufactured by conveying a strip-shaped
일 실시예에 따르면, 상기 고기능성 칼라강판은 연속 공정을 통해 효과적으로 제조될 수 있으며, 도 3에 나타난 것과 같이 상기 칼라 강판은 하도 도막층(130) 상에 자외선 경화성 접착 조성물이 도포된 후, 광 투과성 필름(150) 합지 공정을 위하여 이송 롤러(210)에 의해 이송될 수 있다. According to one embodiment, the high-performance color steel sheet can be effectively manufactured through a continuous process. As shown in FIG. 3, after the color steel sheet is coated with the ultraviolet-curable adhesive composition on the
광 투과성 필름(150)은 필름 공급 롤러(230)에 의해서 연속적으로 공급될 수 있으며, 상기 필름 공급 롤러(230)에 권취된 광 투과성 필름(150)은 합지 롤러(220)에 의하여 칼라강판 상에 위치할 수 있다. The
상기 합지 롤러(220)는 광 투과성 필름(150)의 상면과 접촉하여 회전하면서 상기 광 투과성 필름(150) 상면을 아래 방향으로 가압할 수 있고, 하부의 이송 롤러(210)는 강판의 하면과 접촉하여 상기 합지 롤러(220)에 대하여 역방향으로 회전하면서 칼라 강판의 하면을 윗 방향으로 가압할 수 있다.The
상기 합지 롤러(220)는 고무 롤 또는 금속 롤일 수 있으나, 상기 합지 롤러(220)가 금속롤인 경우, 가압(압착)시 국부적인 압력 편차에 의하여 도막의 완전 파괴가 일어날 수 있으므로, 고무 롤을 사용하는 것이 바람직하다. The
즉, 고무의 탄성에 의하여 가압(압착)시 좌우의 압력편차를 완화할 수 있으므로 표면의 평활도를 균일하게 할 수 있으며, 도막이 파괴되는 것을 방지할 수 있다.That is, since the elasticity of the rubber can relieve pressure deviations in the left and right pressures (press-fitting), the smoothness of the surface can be made uniform, and the coating film can be prevented from being broken.
이 때 상기의 합지 롤러(220)는 롤러 형태뿐만 아니라 막대나 판자 등 다양한 형태로 구성할 수 있다.At this time, the above-mentioned
상기 광 투과성 필름(150)은 칼라강판 상에 위치하여 합지될 수 있으며, 상기 칼라 강판은 이송 롤러(210)에 의해 연속적으로 이송되어 상기 광 투과성 필름(150) 하단의 자외선 경화성 접착 조성물은 자외선에 의해 경화될 수 있다. The
일 실시예에 따르면, 상기 합지된 광 투과성 필름(150) 상에 조사되는 자외선은 500mJ/cm2 내지 3,000mJ/cm2의 에너지 밀도로 조사되는 것 일 수 있다. According to one embodiment, ultraviolet light is irradiated on the laminated a
상기 자외선의 에너지 밀도가 500mJ/cm2 미만인 경우 도막 표면 외관의 불량이 야기될 수 있고, 3,000mJ/cm2초과인 경우 상도 도막층이 과도하게 경화되어 부착력이 저하되거나 도막이 파괴될 수 있다.If the energy density of the ultraviolet ray is less than 500 mJ / cm 2, the appearance of the surface of the coating film may be defective. If the energy density exceeds 3,000 mJ / cm 2 , the top coat layer may be excessively cured, resulting in deterioration of adhesion or destruction of the coating film.
상기 자외선의 에너지 밀도가 500mJ/cm2 미만인 경우 도막 표면 외관이 미경화가 발생하여 불량이 야기될 수 있고, 3,000mJ/cm2를 초과하는 경우 도막층이 과도하게 경화되어 하부와의 부착불량 또는 도막 표면상의 갈라짐 현상을 초래할 수 있다.If the energy density of the ultraviolet rays is less than 500 mJ / cm 2, the surface appearance of the coating film may be unfavorably formed and defective. If the energy density exceeds 3,000 mJ / cm 2 , the coating layer is excessively cured, It may cause cracking on the surface.
상기 자외선은 복수의 행과 열로 배열되는 다수의 자외선 램프(수은, 메탈, 갈륨)를 통해 조사할 수 있으며, 상기 자외선 램프는 강판의 면적, 강판의 이동속도, 자외선 조사량 등의 작업 환경을 고려하여 적절하게 배치할 수 있다. The ultraviolet lamp can be irradiated through a plurality of ultraviolet lamps (mercury, metal, gallium) arranged in a plurality of rows and columns, and the ultraviolet lamps can be irradiated with ultraviolet rays in consideration of the working environment such as the area of the steel sheet, the moving speed of the steel sheet, It can be arranged properly.
일 실시예에 따르면, 상기 광 투과성 필름(150)의 두께는 10㎛ 내지 125㎛ 이고, 자외선 광 투과율이 70% 이상일 수 있다. According to one embodiment, the thickness of the light-
상기 광 투과성 필름(150)의 두께가 10㎛ 미만인 경우 압착시 필름의 구김 자국이 하부 도막층에 전이될 수 있고, 상도 도막층 표면의 평활도가 저하되어 고선영성을 구현하기 어려우며, 125㎛ 초과인 경우 상도 도막층의 미경화가 발생할 수 있고, 필름의 가격 상승으로 생산 원가가 상승할 수 있다.When the thickness of the light-
또한, 자외선 광 투과율이 70% 미만인 경우 상도 도막층의 경화 불량으로 표면 외관의 불량이 야기될 수 있으며, 하부 도막층의 문양이나 외관이 명확하게 드러나지 않아 칼라 강판 외면의 미려함이 저하될 수 있다. In addition, when the ultraviolet light transmittance is less than 70%, defects in surface appearance may occur due to poor curing of the top coat layer, and the pattern or appearance of the bottom coat layer may not be clearly revealed, which may degrade the appearance of the outer surface of the color plate.
상기 자외선 경화성 도료 조성물은 전술한 바와 같이 코팅부에서의 스프레딩 공정을 거쳐 강판 상에 고르게 분산되어 있으므로, 적은 양의 자외선 조사에도 불구하고 균일하고 신속한 경화가 이루어지며, 이에 따라 생산 공정의 비용 절감 및 수율 향상을 도모할 수 있다.Since the ultraviolet ray-curable coating composition is uniformly dispersed on the steel sheet through the spreading process in the coating portion as described above, uniform and rapid curing can be achieved in spite of a small amount of ultraviolet ray irradiation, And the yield can be improved.
또한, 상기 자외선 조사부는 500mJ/cm² 내지 3,000mJ/cm²의 에너지로 자외선을 조사할 수 있다. 자외선의 에너지 밀도가 500mJ/cm2 미만인 경우 도막 표면 외관이 미경화가 발생하여 불량이 야기될 수 있고, 3,000mJ/cm2를 초과하는 경우 도막층이 과도하게 경화되어 하부와의 부착불량 또는 도막 표면상의 갈라짐 현상을 초래할 수 있다.The ultraviolet ray irradiating unit may irradiate ultraviolet rays at an energy of 500 mJ / cm2 to 3,000 mJ / cm2. If the energy density of the ultraviolet rays is less than 500 mJ / cm 2, the surface appearance of the coating film may be unfavorably formed and defective. If it exceeds 3,000 mJ / cm 2 , the coating layer is excessively cured, Resulting in a cracking phenomenon.
이하 실시예를 통해서 본 발명을 더욱 상세히 설명하나, 하기 실시예에 의해 본 발명이 제한되지 않음은 자명하다.
Hereinafter, the present invention will be described in more detail with reference to Examples. However, it is apparent that the present invention is not limited by the following Examples.
아크릴레이트urethane
Acrylate
아크릴레이트Meta
Acrylate
레이티드
아크릴레이트Carboxyl
Rated
Acrylate
실시예 1Example 1
상기 실시예 1에 따른 자외선 경화성 접착 조성물을 롤 코팅을 통해 강판에 5~10㎛ 두께로 코팅한 후 100㎛ 두께의 PET 필름을 강판상에 합지하였다. 이후 자외선을 조사하여 자외성 경화성 접착 조성물을 경화시켰다.
The ultraviolet curable adhesive composition according to Example 1 was coated on a steel sheet through a roll coating to a thickness of 5 to 10 mu m, and then a PET film having a thickness of 100 mu m was laminated on the steel sheet. Then, ultraviolet rays were irradiated to cure the ultraviolet-curable adhesive composition.
실시예 2Example 2
상기 실시예 2에 따른 자외선 경화성 접착 조성물을 롤 코팅을 통해 강판에 5~10㎛ 두께로 코팅한 후 100㎛ 두께의 PET 필름을 강판상에 합지하였다. 이후 자외선을 조사하여 자외성 경화성 접착 조성물을 경화시켰다.
The UV-curable adhesive composition according to Example 2 was coated on the steel sheet through a roll coating to a thickness of 5 to 10 탆, and then a PET film having a thickness of 100 탆 was laminated on the steel sheet. Then, ultraviolet rays were irradiated to cure the ultraviolet-curable adhesive composition.
비교예 1 내지 3Comparative Examples 1 to 3
상기 비교예 1 내지 3에 따른 자외선 경화성 접착 조성물을 롤 코팅을 통해 강판에 5~10㎛ 두께로 코팅한 후 100㎛ 두께의 PET 필름을 강판상에 합지하였다. 이후 자외선을 조사하여 자외성 경화성 접착 조성물을 경화시켰다.
The ultraviolet-curable adhesive compositions according to Comparative Examples 1 to 3 were coated on a steel sheet through a roll coating to a thickness of 5 to 10 탆, and then a PET film having a thickness of 100 탆 was laminated on the steel sheet. Then, ultraviolet rays were irradiated to cure the ultraviolet-curable adhesive composition.
비교예 4Comparative Example 4
상기 제조예 1과 동일한 방법으로 칼라 강판을 제조하였으나, 상기 자외선 경화성 접착 조성물 대신 기존의 우레탄계 용제형 접착 조성물을 5~10㎛ 두께로 도포한 후 열풍 건조를 통해 용제를 증발시켜 경화시킨 후 표면이 완전히 냉각되기 전에 투명 PET 필름을 합지하였다.
A colored steel sheet was prepared in the same manner as in Preparation Example 1. However, instead of the ultraviolet ray-curable adhesive composition, a conventional urethane-based adhesive composition was applied in a thickness of 5 to 10 탆, and then the solvent was evaporated through hot air drying to cure the surface, A transparent PET film was laminated before being completely cooled.
비교예 5Comparative Example 5
상기 제조예 1과 동일한 방법으로 칼라 강판을 제조하였으나, 상기 자외선 경화성 접착 조성물 대신 기존의 우레탄/멜라민계 용제형 접착 조성물을 5~10㎛ 두께로 도포한 후 열풍 건조를 통해 용제를 증발시켜 경화시킨 후 표면이 완전히 냉각되기 전에 투명 PET 필름을 합지하였다.
A color steel sheet was prepared in the same manner as in Preparation Example 1 except that a conventional urethane / melamine solvent type adhesive composition was applied in a thickness of 5 to 10 탆 instead of the ultraviolet curable adhesive composition, and then the solvent was evaporated through hot air drying to cure The transparent PET film was laminated before the rear surface was completely cooled.
(◎: 우수, ○: 양호, △: 보통, X: 불량)(?: Excellent,?: Good,?: Fair, X: poor)
물성평가 시험조건Physical property evaluation test conditions
1) 외관: 기포의 발생, 도막층 내 티끌 등의 이물질 침투여부 확인(육안판정)1) Appearance: Confirmation of occurrence of air bubbles, penetration of foreign matter such as dust in the coating layer (visual determination)
2) 부착성: 1mm 간격 가로 x 세로로 10칸을 칼로 그은 후 스카치 테이프로 완전 밀착 후 순간 박리하여 도막의 박리 유무 확인2) Adhesiveness: After scraping with a knife 10 mm wide x 1 mm wide, tightly with scotch tape, peel off instantly and check whether the film is peeled off
3) 내열탕성: CCET(CUT CROSS ERICHEN TEST) 한후 98도 1시간 침지후 박리 유무 확인 3) Resistance of hot water bath: CCET (CUT CROSS ERICHEN TEST)
4) 가공성: 상온(20℃)에서 T bending하여 가공부위에 크랙 발생여부 평가
4) Processability: T bending at room temperature (20 ℃)
상기 표 2와 같이, 실시예 1 및 실시예 2의 자외선 경화성 접착 조성물을 사용하는 경우에는 표면 외관, 부착성, 내열탕성 및 가공성 등 기본 물성이 양호하게 나타났다. As shown in Table 2, when the ultraviolet curable adhesive compositions of Examples 1 and 2 were used, basic physical properties such as surface appearance, adhesion, resistance to hot water resistance and workability were good.
반면, 동일한 자외선 경화성 접착 조성물을 사용함에도 불구하고, 메타아크릴레이트 또는 카르복실레이티드아크릴레이트 모너머의 함량을 달리한 비교예 1 내지 3의 경우, 메타아크릴레이트 또는 카르복실레이티드아크릴레이트의 함량이 과소하거나 과다하여 기본 물성이 다소 저하되었다.On the other hand, in the case of Comparative Examples 1 to 3 in which the content of methacrylate or carboxylated acrylate monomer was different, the content of methacrylate or carboxylated acrylate The basic physical properties were somewhat lowered.
한편, 종래와 같이 자외선 경화성 접착 조성물 대신 열경화성 접착 조성물을 사용한 비교예 4 및 5의 경우 열풍오븐에서 발생하는 타르와 티끌의 발생과 함께 열에 의해 필름이 변형되어 강판 외관의 불량률이 상대적으로 증가하였다. On the other hand, in Comparative Examples 4 and 5 in which a thermosetting adhesive composition was used instead of the ultraviolet ray-curable adhesive composition as in the prior art, the occurrence of tar and dust generated in the hot air oven was accompanied by a deformation of the film due to heat.
또한, 실시예에 명확히 나타나지 않았으나, 공정속도를 증가시킨 경우에는 완전한 경화가 이루어지지 않고, 기포가 다량 발생하여 외관의 불량률이 더욱 증가하였으며, 특히 끓인물에 침지하여 부착 강도를 평가하는 내비등성 테스트에서 모두 불량으로 나타났다.In addition, although not clearly shown in the examples, when the process speed is increased, complete curing is not performed, and a large amount of bubbles are generated, thereby further increasing the defective rate of appearance. Particularly, In all cases.
전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명되어 있는 각 구성 요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성 요소들도 결합된 형태로 실시될 수 있다.It will be understood by those skilled in the art that the foregoing description of the present invention is for illustrative purposes only and that those of ordinary skill in the art can readily understand that various changes and modifications may be made without departing from the spirit or essential characteristics of the present invention. will be. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive. For example, each component described as a single entity may be distributed and implemented, and components described as being distributed may also be implemented in a combined form.
본 발명의 범위는 후술하는 특허청구범위에 의해 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
The scope of the present invention is defined by the appended claims, and all changes or modifications derived from the meaning and scope of the claims and their equivalents should be construed as being included within the scope of the present invention.
100: 칼라 강판
110: 소지 강판
120: 전처리층
130: 하도 도막층
140: 자외선 경화성 접착층
150: 광 투과성 필름
210: 이송 롤러
220: 합지 롤러
230: 필름 공급 롤러100: Color steel plate
110:
120: Pre-treatment layer
130: Lower coating layer
140: UV curable adhesive layer
150: light transmissive film
210: Feed roller
220: Lapping roller
230: Film feed roller
Claims (8)
전처리층;
하도 도막층;
우레탄(메타)아크릴레이트 프리폴리머 45~65중량부, (메타)아크릴레이트 모노머 25~40중량부, 카르복실레이티드(메타)아크릴레이트 모너머 20~30중량부, 중량부, 광개시제 3~5중량부, 및 부착증진제 2~5중량부를 포함하는 자외선 경화성 접착층; 및
광 투과성 필름을 순차적으로 포함하는 것인 고기능성 칼라강판.
Base steel sheet;
Pretreatment layer;
Undercoating layer;
45 to 65 parts by weight of urethane (meth) acrylate prepolymer, 25 to 40 parts by weight of (meth) acrylate monomer, 20 to 30 parts by weight of carboxylate (meth) acrylate monomer, 3 to 5 parts by weight of photoinitiator And 2 to 5 parts by weight of an adhesion promoter; And
And a light-transmissive film in this order.
상기 광 투과성 필름은 폴리메틸메타크릴레이트(PMMA), 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 폴리프로필렌(PP), 또는 폴리스티렌(PS) 필름인 것인 고기능성 칼라강판.
The method according to claim 1,
Wherein the light transmissive film is a polymethyl methacrylate (PMMA), a polyethylene terephthalate (PET), a polyethylene (PE), a polypropylene (PP), or a polystyrene (PS) film.
상기 광 투과성 필름은 표면에 패턴 또는 요철이 형성되어 있는 것인 고기능성 칼라강판.
The method according to claim 1,
Wherein the light-transmitting film has a pattern or unevenness formed on the surface thereof.
상기 광 투과성 필름의 두께는 10㎛ 내지 125㎛ 이고, 자외선 광 투과율이 70% 이상인 것인 고기능성 칼라강판.
The method according to claim 1,
Wherein the light-transmitting film has a thickness of 10 to 125 탆 and an ultraviolet light transmittance of 70% or more.
상기 자외선 경화성 접착층의 두께는 3㎛ 내지 50㎛인 것인 고기능성 칼라강판.
The method according to claim 1,
Wherein the ultraviolet-curing adhesive layer has a thickness of 3 to 50 占 퐉.
상기 전처리층 상에 하도 도막층을 형성하는 단계;
상기 하도 도막층 상에 우레탄(메타)아크릴레이트 프리폴리머 45~65중량부, (메타)아크릴레이트 모노머 25~40중량부, 카르복실레이티드(메타)아크릴레이트 모너머 20~30중량부, 광개시제 3~5중량부, 및 부착증진제 2~5중량부를 포함하는 자외선 경화성 접착 조성물을 도포하는 단계;
상기 자외선 경화성 접착 조성물 상에 광 투과성 필름을 합지하는 단계; 및
상기 합지된 광 투과성 필름 상에 자외선을 조사하여 상기 자외선 경화성 접착 조성물을 경화시키는 단계;를 포함하는 것인 고기능성 칼라강판의 제조방법.
Forming a pretreatment layer on the base steel sheet;
Forming a primer coating layer on the pretreatment layer;
(Meth) acrylate prepolymer, 45 to 65 parts by weight of a urethane (meth) acrylate prepolymer, 25 to 40 parts by weight of a (meth) acrylate monomer, 20 to 30 parts by weight of a carboxylated To 5 parts by weight of an adhesion promoting agent, and 2 to 5 parts by weight of an adhesion promoting agent;
Laminating a light-transmissive film on the ultraviolet-curable adhesive composition; And
And curing the ultraviolet-curable adhesive composition by irradiating ultraviolet light onto the laminated light-transmitting film.
상기 합지된 광 투과성 필름 상에 조사되는 자외선은 500mJ/cm2 내지 3,000mJ/cm2의 에너지 밀도로 조사되는 것인 고기능성 칼라강판의 제조방법.
The method according to claim 6,
Wherein the laminated light-transmitting ultraviolet rays irradiated on the film is 500mJ / cm 2 to a high production method of the functional color steel plate it will be irradiated with an energy density of 3,000mJ / cm 2.
상기 광 투과성 필름의 두께는 10㎛ 내지 125㎛ 이고, 자외선 광 투과율이 70% 이상인 것인 고기능성 칼라강판의 제조방법.The method according to claim 6,
Wherein the thickness of the light-transmissive film is 10 占 퐉 to 125 占 퐉 and the ultraviolet light transmittance is 70% or more.