KR20140109022A - Functionality special mortar composition use Method of water proofing - Google Patents
Functionality special mortar composition use Method of water proofing Download PDFInfo
- Publication number
- KR20140109022A KR20140109022A KR1020130023116A KR20130023116A KR20140109022A KR 20140109022 A KR20140109022 A KR 20140109022A KR 1020130023116 A KR1020130023116 A KR 1020130023116A KR 20130023116 A KR20130023116 A KR 20130023116A KR 20140109022 A KR20140109022 A KR 20140109022A
- Authority
- KR
- South Korea
- Prior art keywords
- waterproofing
- mortar
- weight
- functional
- construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
본 발명은 기능성 특수몰탈을 이용한 방수공법에 관한 것이다
본 발명의 목적은 급 변화하고 있는 기후 환경과 현재 사용 중인 각종 건축물의 하자와 부실로 재건축 시기가 점점 앞당겨 지고 있는 실정이다
특히 건축물은 시공시 방수 공사를 해야 하므로 현재 널리 사용중인 것은 우레탄도막.아스팔트.액체.씨트 등 방수공법 으로 시공하고 있다
현재 사용중인 공법으로 시공시 몇 년 못가 방수층에 하자가 발생하여 각종 건축물 옥상 지하주차장 베란다 물탱크 저수조 등 누수가 발생되고 있어 생활에 불편을 주고있다
앞으로 각종 주거 형태의 변화에 따른 방수공법 역시 중요 하다고 사료 된다 그러므로 이제 방수공사 공법도 기능성이 있는 공법을 사용해서 내용 연수가 오래 가는 자재와 시공 방법이 전문화 되어야 하고 각종 현장에서 누구나 손쉽게 사용 할수 있어야 한다
본 발명에서 1차 방수층 및 바닥 보강재로 사용한 기능성특수몰탈 제품은 신축,보수공사 현장에서 제품에 물만부어 기존 콘크리트 및 몰탈 바닥에 부으면 자력으로 표면이 평활하게 형성이 되고 타설 두게도 4mm-5mm만 도포 해도 기능성 특수 몰탈이 들뜨지 않아 건축물 방수 하자 발생을 해결 하는 것이다
본 발명 제품을 이용한 방수공법은 이러한 문제점을 해결하기 위해서 방수공사에 있어 기능 전문성을 가지고 있는 제품으로 2차 방수층 으로 널리 사용중인 우레탄 도막 방수재를 보호하고 긴 기간 동안 하자 없이 소비자가 사용 할수 있는 방수공법이다The present invention relates to a waterproofing method using a functional special mortar
It is an object of the present invention to provide a system and method for improving the quality of a building,
Particularly, since buildings are required to be waterproofed when they are constructed, they are currently being used by waterproofing methods such as urethane coatings, asphalt, liquids and seats
The construction method that is currently in use is that the waterproof layer is defective for a few years at the time of construction, causing leakage of water such as the roof water tank,
Waterproofing method is also important due to changes in various types of residential buildings. Therefore, waterproofing construction method should be specialized in materials and construction methods with long service life by using functional construction method.
In the present invention, the functional special mortar product used as the primary waterproof layer and the bottom stiffener is formed by pouring only the water into the product at the site of the new construction and repair and pouring it on the existing concrete and mortar floor, the surface is smoothly formed by the magnetic force, It is solving the occurrence of defects of building waterproofing because special functional mortar is not excited
In order to solve these problems, the waterproofing method using the product of the present invention has a function specialty in waterproofing work. It protects the urethane coating waterproofing material which is widely used as the second waterproofing layer, to be
Description
..
발명이 속하는 기술 및 그 분야의 종래기술The technology to which the invention belongs and the prior art in the field
본 발명은 기능성 특수몰탈을 이용한 방수시공 공법에 관한 것이다The present invention relates to a waterproofing method using a functional special mortar
현재 건축물의 신축 및 보수 공사를 할 경우 아파트.주택옥상 지하 주차장 상가 물탱크에 방수공사 공법으로 사용되고 있는 것은 씨트방수.아스팔트도포공법 액체방수 우레탄도막 방수 공법을 주로 사용 중에 있다If the building is newly constructed and repaired, it is used as a waterproofing construction method on the roof of an apartment, an underground parking lot, an underground parking lot, and a liquid waterproofing urethane coating waterproofing method for asphalt application method is mainly used
많은 건축물이 기후 변화와 외부 환경 요인으로 화학적 물리적 현상으로 구조물 바닥의 표면 강도 부실로 기존 콘크리트 및 몰탈 바닥이 들뜨고 균열이 발생 하고 있다Many buildings are exposed to chemical and physical phenomena due to climate change and external environmental factors, and the existing concrete and mortar floors are cracked due to the lack of surface strength of the structure floor
현재 사용중인 방수공법은 기존 바닥에 이물질 제거 및 청소 작업후 방수공사를 위해 1차로 바닥 보강 작업에 쓰이는 자재는 일반적으로 시중에 있는 시멘트에 모래를 혼합한 몰탈을 사용하고 있다Currently, the waterproofing method currently used is the mortar which is used in the floor reinforcement work for the waterproofing work after removing and cleaning the foreign body on the existing floor.
이 일반 몰탈 제품은 유동성이 없고 접착력이 약해 두게를 얇게 도포시 들뜨는 하자가 있으며 압축 강도 와 표면 강도가 약해 기존 바닥균열 부분에 침투 시킬수 없는 문제점 이 있다This general mortar product has no fluidity and weak adhesive force, and has a defect that it spreads when it is applied thinly, and has a problem that the compressive strength and surface strength are weak and it can not penetrate the existing floor crack part
현재 방수공사에 많이 사용중인 우레탄 도막 방수 시공 방법은 1차로 바닥 전처리 및 청소가 중요 하지만 현재 건축물 대부분 콘크리트 및 몰탈 바닥 표면이 들뜨고 부실해 특히 바닥에 강도가 시간이 갈수록 약해저 습기 차단이 안되 우레탄 도막 방수재로 공사후 2-3년이 지나면 부실한 바닥 부분에서부터 우레탄 방수층이 들뜸 현상이 많이 일어나 아파트 및 주택 각종 건축물 옥상 슬라브에서 눈비가 올때면 바닥표면의 부실과 균열을 발생시키고 빗물이 침투하여 방수층 들뜸 현상을 촉진시켜 누수로 인한 건축 구조물의 수명을 단축 시키는 원인이 된다Currently, urethane coating waterproofing method, which is widely used for waterproofing construction, is important in the first floor pre-treatment and cleaning. However, most of the buildings in the present construction are flooded with concrete and mortar bottom surface. Especially, After 2-3 years after construction, the urethane waterproofing layer has been lifted from the poor bottom part. When the snow is coming from the roof slab of apartment buildings and various buildings, the bottom surface is cracked and cracked, rain water penetrates, Thereby shortening the life of the building structure due to leakage
기초 바닥 공사의 시공 방법 개선과 사용 자재를 기능성 있는 제품으로 전환 사용하여 시공 원가 절감과 각종 현장에서 누구나 손쉽게 빠르게 사용 할 수 있고 신축 및 보수공사에서 방수공사 하자를 줄이기 위해 연구를 하게 되었다We improved the construction method of foundation floor construction and converted the used materials into functional products, so that it is possible to use it quickly and easily at various sites and reduce the cost of construction.
..
본 발명은 이런 문제점을 해결 하기 위해서 신축 및 보수 공사현장에서 현재 많이 사용중인 우레탄 도막 방수재를 기존 바닥에 도포 하기전 기능성 특수 몰탈을 먼저 전체 바닥면에 도포 해서 기존 바닥의 표면을 강화와 1차 방수층을 형성 시킨다In order to solve this problem, in order to solve this problem, before applying the urethane coating waterproofing material which is currently in use in the new construction and repair work, the functional special mortar is first applied to the entire floor surface to strengthen the surface of the existing floor, to form the
기능성 특수 몰탈의 특성은 고강도와 고접착력으로 들뜸 현황 방지 균열 방생 방지 각 현장에 따라 시공 두게 조정이 가능한 제품으로 2차 방수층인 우레탄 도막 방수재가 하자와 들뜸 현상이 없도록 기능성 특수 몰탈 조성물을 이용한 방수시공 공법을 제공하는데 목적이 있다Functional special mortar is characterized by high strength and high adhesive strength. Prevention of cracking Debris prevention It is possible to adjust the construction according to each site. Waterproofing using functional special mortar composition so that the urethane coating waterproofing material, which is the second waterproofing layer, There is a purpose in providing the method.
이상에서 진술 한바 와 같이 본 발명은As described above, according to the present invention,
1) 기능성 특수 몰탈을 이용하여 아파트 및 주택 각종 건축물에 방수공사를 할 경우 누구나 현장에서 본 제품에 물만 부어 믹셔기로 혼합 후 사용 할수 있도록 하였으며 제품에 기능성을 주기위해 내구성강화 접착 및 표면 강도을 높여 기존 바닥을 보강하고 타설 두게도 4-5mm 로 1차 방수층을 형성 하고있어 2차 방수층 우레탄 도막 방수재를 현재 사용하고 있는 3mm 두게로 하고 있으나 기능성 특수 몰탈이 바닥에 4-5mm 타설되어 있어 특수 몰탈 위에 우레탄 도막재를 2mm 두게로 도포해도 아무 이상이 없었으며 인건비 및 자재비 절감으로 공사비 절감 효과를 가져온다1) When waterproofing the apartment buildings and various buildings by using the special functional mortar, it is possible to mix them with the mixer after pouring only the water to the products in the field. The durability is strengthened to give the product functionality. And the first waterproof layer is formed with 4-5mm for the installation. The second waterproof layer urethane coating waterproofing material is 3mm thick, but the functional special mortar is laid 4-5mm on the bottom, so that the urethane coating layer There was nothing wrong with applying 2 mm of ash, and it saved the cost of labor by reducing labor and material cost.
2) 우레탄 도막 방수층 밑에 본 제품 기능성 특수 몰탈로 기존 바닥에 높고 깊은곳을 현장 바닥 여건에 따라 스스로 채워져 그 동안 시공 바닥면의 요철 부위와 표면이 고르지 못해 불규칙적으로 된 부위를 불곡이 없이 전체을 평탄 하게 해결 함으로써 방수공사 품질이 향상되는 효과를 가진다2) Urethane film This special functional mortar under the waterproofing layer of the product is filled with the original floor according to the conditions of the field floor, so that the irregularities and irregularities on the bottom surface of the construction floor are irregular. It has the effect of improving waterproofing quality
3) 공정 개선의 효과는 바닥 정리 와 청소 작업 마친후 기능성 특수 몰탈에 현장에서 물만부어 타설하면 바닥의 기초 보강작업과 1차 방수층 형성이 끝나므로 누구나 손쉽게 사용할수 있어 공정개선의 효과를 가져 왔다3) The effect of the process improvement is that when the water is poured into the functional special mortar only after the completion of the floor cleaning and cleaning work, the foundation reinforcement work of the floor and the formation of the first waterproof layer are completed.
4) 본 발명에 따른 기능성 특수 몰탈을 먼저 시공 바닥면에 타설함으로써 2차 도포 우레탄 도막 방수재의 가장 취약점인 기존 바닥의 들뜸현상과 표면강도가 약한점을 해결 기포발생 현상과 우레탄 방수재 훼손을 방지하고 방수층 수명이 길어 자재비및 관리비 공사비 절감으로 소비자에게 편익를 주는 효과가 있다4) The functional special mortar according to the present invention is first laid on the floor of the construction to solve the weakness of the existing floor, which is the weakest point of the secondary coating urethane coating waterproofing material, and weak surface strength. Waterproof layer has a long lifetime and it has the effect of giving convenience to consumers by reducing the material cost and management cost.
도1은 발명의 방수공법을 설명하가 위한 단면도이다
도면의 주요 부분에 대한 부호 설명
1. 기존 콘크리트 바닥 및 몰탈 바닥
2. 수용성 접착제
3. 기능성 특수 몰탈
4. 우레탄용 접착제
5. 우레탄 중도제
6. 우레탄 중도 보호 탑코팅1 is a cross-sectional view for illustrating a waterproofing method of the present invention
DESCRIPTION OF THE DRAWINGS FIG.
1. Existing concrete floor and mortar floor
2. Water-soluble adhesive
3. Functional special mortar
4. Adhesive for urethane
5. Urethane intermediates
6. Urethane mid-protection top coating
상기 목적을 달성하기 위해 본 발명의 구성은 기능성 특수몰탈에 쓰이는 재료는 전체 중량에 대한 백분율로 한 것이며In order to achieve the above object, the present invention is characterized in that the material used for the functional special mortar is a percentage of the total weight
포틀랜트시멘트 40-45중량％ 조강시멘트 0.9-1.2 중량％ 멜멘트 1-1.5 중량％ 소포재 0.05-0.5 중량％ M.C 0.1-0.4중량％ 분말수지 2-4 중량％ 칼슘카보나이트 2.5-3 중량％ 규사(Sio2) 35-44 중량％ 으로 이루어진 것이 특징으로 한다Portland cement 40-45% by weight Crude steel cement 0.9-1.2% by weight Melamine 1-1.5% by weight Pellets 0.05-0.5% by weight MC 0.1-0.4% by weight Powder resin 2-4% by weight Calcium carbonate 2.5-3% by weight Silica (Sio2) in an amount of 35 to 44% by weight
상기 재료로 많이 쓰이는 시멘트는 국내 시중에서 손쉽게 구할수 있는 일반 포틀랜트 시멘트를 사용 하였고 골재로 사용한 규사도 국내에서 생산한 규사로 사용 하여 가격 면에서도 경쟁력을 잦주었다Cement which is widely used for the above materials is made of ordinary portland cement which can be easily obtained in the market in the country.
또한 골재를 일반 모래를 사용 하지 않고 규사를 이용한것는 일반 모래에는 토분이 있어 하자가 발생할수 있어 규사는 깨끗한 물로 세척하여 토분기를 제거 후 건조기에서 수분을 완전히 제거시켜 혼합 사용 하였다Also, it is possible to cause defects due to the presence of soil in the general sand that does not use the ordinary sand, and the silica sand is washed with clean water to remove the soil from the soil, and then the water is completely removed from the dryer
기존 콘크리트 및 몰탈 바닥면 보수와 표면강도 보강를 위해 기능성 특수몰탈을 4-5mm 두게로 타설 도포 해도 들뜸 현상이 없으며 압축 강도를 높여 주고 기존 바닥면에 균열간 틈새로 스스로 흘러 들어 갈수 있도록 유동화재를 사용 하였고 규사 역시 타설후 표면의 평활성과 균열 속으로 흘러 침투 할수 있도록 사용한 규사 규격을 6-7호사 (60-80mesh 0.6-0.25mm) 고운 입자를 사용 하였다Existing concrete and mortar It has no floating phenomenon even if the special mortar is cast by 4-5mm in order to repair the floor surface and reinforce the surface strength. It increases the compressive strength and uses the floating fire so that it can flow into the gap between the existing cracks. (60-80mesh 0.6-0.25mm) fine particles were used for the silica sand specimens used to penetrate into the smoothness and cracks of the surface after casting.
접착력을 좋게 하기위해 분말 접착재를 사용 하였으며 굳은 시간을 일반시멘트 보다 빠르게 하기위해 조강 시멘트를 혼합 하였다Powder adhesive was used to improve adhesion and crude steel cement was mixed to make the hardening time faster than general cement
본 제품에 각종 현장에서 물만 부어 믹셔기로 혼합해 기존 콘크리트 및 몰탈 바닥에 부으면 스스로 바닥에 퍼져 양생후 표면이 평활 하고 높은 강도를 유지한다This product is poured only in water at various sites, mixed with mixer, spread on floor of existing concrete and mortar itself, and after curing, surface is smooth and high strength is maintained
초기 강도와 굳은 시간을 빠르게 하기 위해 조강 시멘트를 사용하여 내화학성과 분말도가 높아 우수한 수밀성을 가지고 있으며 일반 시멘트와 서로간에 친화성이 좋아 혼합 사용을 해 봐도 아무 문제가 없었고 분말 수지는 비닐아세데이트를 사용 하였다In order to accelerate the initial strength and hardening time, it has good watertightness due to high chemical resistance and high degree of powdering by using crude steel cement. It has no problem even when mixed with good general cement and good compatibility with each other. Was used
본 기능성 특수 몰탈에 사용한 물의량은 중량비에 21-22 ％이다The amount of water used in this functional special mortar is 21-22% by weight
바닥 보강 작업과 1차 방수층 형성을 위해 특수 몰탈을 사용 하기 위해서는In order to use special mortar to reinforce the floor and to form the first waterproof layer
1) 시공 하고자 하는 바닥에 불순 물이 없게 깨끗하게 제거하고 고압 청소기 및 진공 청소기로 청소를 한다1) Clean the floor that you want to install without any impurities and clean it with high pressure cleaner and vacuum cleaner
2) 청소 작업이 끝나면 수용성 프라이머를 시공 부위 전체 바닥에 로라를 이용 도포 한다2) When the cleaning work is finished, apply the water-soluble primer to the bottom of the construction site using the roller
3) 수용성 프라이머가 건조된 후 기능성 특수 몰탈에 중량비 21-22％ 넣고 믹셔기로 2분 정도 혼합 후 시공 바닥에 타설양생 시킨후 2차 방수층인 우레탄 도막 방수재를 2mm 두게로 도포한다3) After the water-soluble primer is dried, it is put into a functional special mortar with a weight ratio of 21-22%. After mixing for 2 minutes with a mixer, it is cured on the floor and applied with urethane coating waterproofing material of 2mm thickness
본 발명의 기능성 특수 몰탈 공법 의 원리 와 특성은The principles and characteristics of the functional special mortar process of the present invention
1. 시공면이 평활하다 2. 들뜸 현상이 없다1. The construction surface is smooth 2. No lift
3. 내마모성이 우수하다 4. 시공이 간편하다3. Excellent abrasion resistance. 4. Easy to install.
5. 보수가 간편하고 유지 관리가 좋다5. Easy maintenance and good maintenance
6. 높은 강도와 우수한 접착력 으로 균열 박리 현상이 발생 하지 않는다6. High strength and good adhesive force do not cause cracking
본 제품에는 이러한 기능과 특성이 있어 2차 방수층인 우레탄 도막 방수재를 특수 몰탈 위에 도포 해도 오래 동안 하자 없이 사용 할수있다This product has such features and characteristics that it can be used for a long time even if it is coated on the special mortar with the urethane coating waterproofing material of the second waterproof layer
현재 사용 중인 우레탄 도막 방수 시공은 기존 콘크리트 및 몰탈 미장 바닥 위에 방수층인 우레탄 도막 방수재를 도포 하는 것으로 방수 공사가 마감되며 기존 바닥이 강도가 약하거나 수분이 있을시 우레탄 도막 방수층이 들뜸 현상이 많이 발생하여 누수가 되고있다The currently used urethane coating waterproofing works by applying urethane coating waterproofing material which is a waterproofing layer on the existing concrete and mortar plastering floor, and the waterproofing work is finished. When the existing floor is weak in strength or when there is moisture, the urethane coating waterproofing layer is floating It is becoming a leak.
본 발명에서 1차 방수층 및 바닥 보강재로 사용 되고 있는 기능성 특수 몰탈은 높은 강도 와 우수한 접착력과 바닥면이 평활 하고 표면이 좋아 우레탄 도막 방수층 훼손을 방지하고 내구력을 증가 시켜주고 있어 현재 사용중인 방수 시공 공법에 비해 한층 개선이 되고 우수한 점을 보여 주고 있다In the present invention, the functional special mortar used as the first waterproof layer and the bottom stiffener has high strength and excellent adhesive force, and the bottom surface is smooth and the surface is good, thereby preventing the urethane film waterproof layer from being damaged and increasing the durability. Compared to the previous year.
(실시예)(Example)
실험을 위해 구성비 내용에 따라 제품을 만들어 사용 하였다For the experiment, the product was made and used according to the composition ratio.
포틀랜트 시멘트 40-45 중량％ 조강 시멘트 0.9-1.2중량％Portland cement 40-45 wt% Crude steel cement 0.9-1.2 wt%
멜멘트 1-1.5 중량％ 소포재 0.05-0.5중량％Melamine 1-1.5% by weight Vesicle 0.05-0.5%
M.C 0.1-0.4 중량％ 분말수지 2- 4 중량％M. C 0.1-0.4 wt% Powder resin 2-4 wt%
칼슘카보나이트 2.5-3 중량％ 규사(Sio2) 35 -44 중량％Calcium Carbonate 2.5-3% Sio2 35-44%
상기 배합비에 따라 믹셔기에 넣고 10분간 회전 혼합하여 제품을 만들어 실험 하였다The mixture was put into a mixer according to the mixing ratio and rotated and mixed for 10 minutes to prepare a product
만든 제품의 압축강도 및응결시간 등을 실험 하고 그결과를 다음 표 1과 같다The compressive strength and the settling time of the product were tested and the results are shown in Table 1
Claims (1)
2) 고압 및 진공 청소 작업후 수용성 접착재(프라이마)를도포한다
3) 도포한 수용성 접착재(프라이머)가 건조후 기능성 특수 몰탈을 4-5mm 정도 타설 시공 전체 바닥에 도포 한다
기능성 특수 몰탈 제품에 대한 조성물은
포틀랜트 시멘트 40-45 중량％ 조강시멘트 0.9-1.2 중량％ 멜멘트 1-1.5 중량％ 소포재 0.05-0.5 중량％ M.C 0.1-0.4 중량％ 분말수지 2-4 중량％ 칼슘카보나이트 2.5-3 중량％ 규사(Sio2) 35-44 중량％ 로 혼합 해서 이루어진 조성물 이다
4) 위 조성물을 가진 기능성 특수 몰탈 타설 도포후 완전히 건조(양생)된 후 우레탄 도막 방수재를 기능성 특수 몰탈 위에 타설 도포한다1) Removal and pretreatment of the floor surface of waterproofing construction site
2) Apply water-soluble adhesive (primer) after high-pressure and vacuum cleaning
3) After the applied water-soluble adhesive (primer) is dried, the functional special mortar is applied to the bottom of the pouring work about 4-5mm
The composition for the functional specialty mortar product
Portland cement 40-45% by weight Crude steel cement 0.9-1.2% by weight Melamine 1-1.5% by weight Pellets 0.05-0.5% by weight MC 0.1-0.4% by weight Powder resin 2-4% by weight Calcium carbonate 2.5-3% by weight Silica (Sio2) in an amount of 35 to 44% by weight
4) After applying functional special mortar casting with the above composition, after fully drying (curing), urethane coating waterproofing material is put on the functional special mortar