KR20110000344A - Manufacturing method for pneumatic tire and the pneumatic tire thereof - Google Patents

Abstract

PURPOSE: A manufacturing method and a pneumatic tire manufactured with pneumatic tire for manufacturing an inner linear film are provided to prevent the damage of the junction in which the rubber of the carcass layer and the inner liner film. CONSTITUTION: A manufacturing method of a pneumatic tire comprises next steps. A carcass layer(300) is laminated in the upper side of an inner liner film(310). A cylinder structure is welded of the cut sheet. A green tire is manufactured by molding a cylinder structure. An inner liner film is one selected from the group consisting of the resin composition of nylon6 and elastomer, and the resin composition of the resin composition of nylon6. The rubber is one selected from the acrylonitrile rubber, butyl rubber, the halobutyl rubber, ethylene propylene rubber, chloroprene rubber, butadiene rubber, styrene butadiene rubber and an isoprene rubber.

Description

Manufacturing Method For Pneumatic Tire And The Pneumatic Tire Thereof}

The present invention relates to a method of manufacturing a pneumatic tire and a pneumatic tire produced by the method.

Typically, the inner surface of a pneumatic tire is provided with an inner liner or other air permeable layer composed of halogenated butyl rubber or other rubber with low air permeability. However, when the halogenated butyl rubber is introduced into the inner liner or air permeation prevention layer, since the hysteresis loss of the halogenated butyl rubber is large, ripples are formed on the inner rubber and the air permeation prevention layer of the carcass layer after vulcanization of the pneumatic tire. The air permeation prevention layer deforms with the deformation of the curse layer. As a result, the problem that the rolling resistance increases.

In general, in order to prevent the above problem, a tie rubber having a low hysteresis loss is inserted into a rubber sheet between the halogenated butyl rubber and the carcass layer to bond the two. As a result, in addition to the thickness of the air permeation prevention layer made of halogenated butyl rubber, the thickness of the tie rubber was added, so that the entire thickness of the layer exceeded 1 mm. This has been a factor in increasing the thickness and weight of the final pneumatic tire.

However, in order to reduce fuel consumption, which is the biggest problem in the automobile industry, it is necessary to reduce the weight of pneumatic tires. In order to reduce the weight of the pneumatic tire, a method of replacing the halogenated butyl rubber with a lighter inner liner film was devised, and a tie gum or an adhesive liquid was applied to the surface to bond the rubber to the manufactured film. Adhesive strength was given to one or both sides depending on the shape of the film and the characteristics of the adhesive liquid.

Initially, an inner liner film manufactured in a tubular shape was developed to remove the film joint, but this was difficult to handle.

As a result, an inner liner film in the form of a sheet has been devised to solve the above problem. However, the inner liner film in the form of a sheet has a problem in that the junction occurs in the forming process, such that a breakage or peeling phenomenon occurs at the junction during the vulcanization process.

An object of the present invention for solving the above problems is to provide a pneumatic tire that does not cause a breakage of the joint even after the vulcanization step.

The present invention for achieving the above object is to form a sheet by laminating a carcass layer on the upper surface of the inner liner film, cutting the sheet, by bonding both ends of the cut sheet to form a cylindrical structure It provides a method of manufacturing a pneumatic tire comprising the step of forming, forming the cylindrical structure to produce a green tire (green tire) and vulcanizing the green tire.

The pneumatic tire manufactured by the manufacturing method of the present invention manufactures a sheet in which the inner liner film and the carcass layer are integrated before the cutting process, so that the rubber of the inner liner film and the carcass layer are bonded even after the vulcanization process. Damage to the joint can be prevented.

In addition, the present invention manufactures a pneumatic tire using one sheet in which a carcass layer is laminated on the upper surface of the inner liner film, so that the inner liner film and the carcass layer can be cut and molded at one time. The process and time for manufacturing a tire can be shortened.

Hereinafter, exemplary embodiments will be described with reference to the accompanying drawings. In adding reference numerals to the components of the following drawings, it is determined that the same components as possible, even if displayed on the other drawings as possible, and unnecessarily obscure the subject matter of the present invention Detailed descriptions of well-known functions and configurations will be omitted.

The innerliner referred to in the present specification refers to a tire having a low-permeability special rubber coated on the inside of the tire in order to prevent air from leaking to the outside from the tire cord, which is the main material of the tire, and various rubbers.

In addition, the innerliner film (innerliner film) referred to herein refers to the thinner in the inner liner film form.

A method of manufacturing a pneumatic tire according to a conventional method will be described with reference to FIGS. 1A to 1D.

First, the carcass layer 100 is formed by a carouseling process of coating a rubber 10 having a predetermined thickness on both sides of the carcass cord 5 of FIG. 1A, and then cutting the carcass layer 100. Usually, the rolling process, namely, a calendering process, referred to in the pneumatic tire manufacturing process, refers to a process of forming a carcass layer by coating rubber of a certain thickness on both sides of the carcass cord 5. The carcass cord 5 mainly consists of a fiber cord and a steel cord.

Next, after the inner liner film 110 of FIG. 1B is cut out, the inner liner film is first molded, as shown in FIG. 1C, so that the edge portions of the inner liner film overlap. Portions of the inner liner film overlap each other to form a bonding portion 120 between the films lacking adhesion. Therefore, in order to improve the adhesive strength of the portion where the inner liner film overlaps, the adhesive liquid may be coated on both sides of the inner liner film or the tie gum treated product may be attached. The adhesive liquid or tie gum may impart adhesive force between the rubber and the film by a crosslinking reaction due to high temperature, but there is a characteristic that the adhesive force is not expressed between the overlapping inner liner films.

When the carcass layer is formed on the outer circumferential surface of the inner liner film, the edge portions of the carcass layer overlap, and the portion indicated by the carcass cord hatched in FIG. 1C is an overlapping portion of the carcass layer.

Next, through the vulcanization process, it becomes a shape as shown in FIG. 1D, and a problem arises in that the inner liner film is broken or peeled off at the junction (that is, the splice portion).

When the pneumatic tire is manufactured by the conventional method of FIGS. 1A to 1D, the carcass layer 100 and the inner liner film 110 must be cut, respectively, so that two cutting processes are required to cut the time and It costs a lot In addition, since the bonding portion 120 of the inner liner film is generated, the bonding portion 120 is damaged or the inner liner film is peeled off during the vulcanization process.

Hereinafter, a method of manufacturing a pneumatic tire by a conventional method different from the above will be described with reference to FIGS. 2A to 2D.

First, the carcass layer 200 is formed by a carouseling process of coating a rubber 10 having a predetermined thickness on both sides of the carcass cord 5 of FIG. 2A, and then cutting the carcass layer 200.

Next, the cylindrical inner liner film 210 of FIG. 2B was prepared. The innerliner film is manufactured to fit the size of the pneumatic tire to be produced, so no cutting process is required.

As shown in Figure 2c, the carcass layer 200 is formed on the outer circumferential surface of the cylindrical inner liner film 210 so that the edge portion of the carcass layer overlaps. The hatched carcass cord indicates the portion where the carcass layer overlaps. Since the cylindrical inner liner film of FIG. 2C is not subjected to the cutting and forming process, the joint portion as shown in FIG. 1C does not occur.

Next, although it becomes a form similar to FIG. 2D through a vulcanization process, since a junction part does not open, the problem that an inner liner film peels off does not arise.

However, when the pneumatic tire is manufactured by the conventional process of FIGS. 2A to 2D, a cylindrical inner liner film that is difficult to handle is required, and a cylindrical inner liner film suitable for the size of the pneumatic tire to be manufactured is manufactured. As a result, the cost of manufacturing and the necessary equipment is high. In addition, there is a problem that a new machine and equipment that can attach the carcass layer and the inner liner film in the molding process.

The present invention relates to a method for producing a pneumatic tire produced by a new method and a pneumatic tire produced by the method.

Method of manufacturing a pneumatic tire of the present invention is to form a sheet by laminating a carcass layer on the upper surface of the inner liner film, cutting the sheet, by joining both ends of the cut sheet cylindrical structure Forming a step, forming the cylindrical structure to produce a green tire (green tire) and comprising the step of vulcanizing the green tire.

The carcass layer preferably comprises a carcass cord and rubber.

The sheet may be formed as one sheet by laminating a carcass layer on the upper surface of the inner liner film and through a rolling process at once.

The innerliner film may be selected from the group consisting of a resin composition of nylon 6 and elastomer, a resin composition of nylon 6 and rubber, and a resin composition of polyethylene terephthalate and elastomer. However, the inner liner film of the present invention is not limited to the above resin composition, and can be used without limitation as long as it can serve as an inner liner. In addition, the resin composition may further include an adhesive composition to improve adhesion to the carcass layer.

The rubber may be selected from the group consisting of acrylonitrile rubber (NBR), butyl rubber, halobutyl rubber, ethylene-propylene rubber, chloroprene rubber, butadiene rubber, styrene-butadiene rubber and isoprene rubber.

Moreover, it is preferable that the pneumatic tire of this invention is manufactured by said method.

3A to 3E schematically show a process of manufacturing a tire including an innerliner film of the present invention and a carcass layer.

First, as shown in FIG. 3A, the carcass layer 300 is formed by coating a rubber 10 having a predetermined thickness on both surfaces of the carcass cord 5.

Next, as shown in FIG. 3B, the inner liner film 310 is prepared, and the carcass layer 300 is laminated on the upper surface of the inner liner film 310 and formed into one sheet by a rolling process. .

The edge of the sheet is cut to obtain a sheet of the form as shown in FIG. 3C. The cut sheet was joined at both ends to form a cylindrical structure 350, which is shown in FIG. 3D. In FIG. 3D, the portion indicated by the hatched carcass code represents a junction where the edge portions of the carcass layer overlap.

In order to improve the adhesive strength of the portion where the inner liner film and the rubber layer of the carcass layer overlap, the adhesive solution may be coated on one side or both sides of the inner liner film, or a tie gum treated product may be attached. The adhesive liquid or tie gum may impart adhesive force between the rubber and the film by a crosslinking reaction due to high temperature, but there is a characteristic that the adhesive force is not expressed between the overlapping inner liner films.

Next, when the cylindrical structure 350 undergoes a vulcanization process, the cylindrical structure 350 is shaped as shown in FIG. 3E. As shown in FIG. 3E, the vulcanized cylindrical structure may be clean because the joint portion to which the inner liner film and the rubber of the carcass layer are bonded is not exposed to the outside.

In addition, compared to the case of manufacturing a pneumatic tire by a conventional method, the pneumatic tire manufacturing method of the present invention by using a single sheet formed by laminating a carcass layer on the upper surface of the inner liner film and rolling them together Since the pneumatic tire is manufactured, even after the vulcanization process, the problem that the inner liner film is peeled off from the joint does not occur.

In addition, since the inner liner film of the sheet form is used instead of the cylindrical inner liner film, it is easy to handle or store the inner liner film, and there is no need to prepare cylindrical inner liner films of various diameters. Can be saved.

The present invention has been described above in connection with specific embodiments of the present invention, but this is only an example and the present invention is not limited thereto. Those skilled in the art can change or modify the described embodiments without departing from the scope of the present invention, and such changes or modifications are within the scope of the present invention. In addition, the materials of each component described herein can be readily selected and substituted for various materials known to those skilled in the art. Those skilled in the art will also appreciate that some of the components described herein can be omitted without degrading performance or adding components to improve performance. In addition, those skilled in the art may change the order of the method steps described herein depending on the process environment or equipment. Therefore, the scope of the present invention should be determined not by the embodiments described, but by the claims and their equivalents.

1 a shows a carcass layer 100 composed of a carcass cord 5 and a rubber 10.

The inner liner film 110 of FIG. 1B is shown.

FIG. 1C shows a part of a cross section of a joint portion in which both ends of the inner liner film 110 and the carcass layer 100 are joined by a molding step during a manufacturing process of a pneumatic tire according to a conventional method.

FIG. 1D shows a part of a cross section of the joint portion in which both ends of the inner liner film and the carcass layer which have completed the vulcanization step are joined in the manufacturing process of the pneumatic tire according to the conventional method.

2A shows a carcass layer 200 composed of a carcass cord 5 and a rubber 10.

The cylindrical inner liner film 210 of FIG. 2B is shown.

FIG. 2C shows a part of the cross section of the joint portion in which both ends of the inner liner film 210 and the carcass layer 200 are joined by a molding step during the manufacturing process of the pneumatic tire according to the conventional method.

FIG. 2D shows a part of a cross section of the joint portion in which both ends of the inner liner film and the carcass layer which have completed the vulcanization step are joined in the manufacturing process of the pneumatic tire according to the conventional method.

3 a shows a carcass layer 300 composed of a carcass cord 5 and a rubber 10.

Figure 3b shows a step of forming a sheet by rolling the carcass layer 300 on the upper surface of the inner liner film 310 of the manufacturing process of the pneumatic tire of the present invention.

Figure 3c shows a sheet finished the rolling and cutting process in the manufacturing process of the pneumatic tire of the present invention.

3D illustrates a portion of a cross section of the cylindrical structure 350 formed by joining both ends of the cut sheet during the manufacturing process of the pneumatic tire of the present invention.

FIG. 3E shows a part of a cross section of the cylindrical structure 350 which has completed the vulcanization process in the manufacturing process of the pneumatic tire of the present invention.

{Description of symbols for main parts of the drawing}

5: carcass cord

10: rubber

100, 200, 300: carcass layer

110, 210, 310: inner liner film

120: junction

350: cylindrical structure

Claims (4)

Stacking a carcass layer on an upper surface of the innerliner film to form one sheet; Cutting the sheet; Joining both ends of the cut sheet to form a cylindrical structure; Forming a green tire by molding the cylindrical structure; And And vulcanizing the green tire. The method of claim 1, The inner liner film is any one selected from the group consisting of a resin composition of nylon 6 and elastomer, a resin composition of nylon 6 and rubber, and a resin composition of polyethylene terephtalate and elastomer. Method of manufacturing pneumatic tires. The method of claim 1, The rubber is air, characterized in that any one or more selected from the group consisting of acrylonitrile rubber (NBR), butyl rubber, halobutyl rubber, ethylene-propylene rubber, chloroprene rubber, butadiene rubber, styrene-butadiene rubber and isoprene rubber Method for manufacturing mouth tires. Pneumatic tire manufactured by the method of any one of Claims 1-3.