KR20050079917A - Colored asphalt - Google Patents
Colored asphalt Download PDFInfo
- Publication number
- KR20050079917A KR20050079917A KR1020050040500A KR20050040500A KR20050079917A KR 20050079917 A KR20050079917 A KR 20050079917A KR 1020050040500 A KR1020050040500 A KR 1020050040500A KR 20050040500 A KR20050040500 A KR 20050040500A KR 20050079917 A KR20050079917 A KR 20050079917A
- Authority
- KR
- South Korea
- Prior art keywords
- color
- asphalt
- colored
- aggregate
- binder
- Prior art date
Abstract
본 발명은 차도, 보도, 자전거 전용도로, 경기장트랙, 어린이 보호구역, 미끄럼 방지구역, 주차장, 공원, 산책로 등에 시공되어 운전자와 보행자의 안전을 도모하고,The present invention is installed in the driveway, sidewalk, bicycle path, stadium track, child protection area, non-slip area, parking lot, park, trails, etc. to promote the safety of drivers and pedestrians,
보다 아름다운 도시미관을 제공하기 위하여 설치되는 칼라아스팔트에 관한 것으로서,Regarding the color asphalt installed to provide a more beautiful city view,
보다 상세하게는,More specifically,
기존의 검정아스팔트핏치를 포함하는 각종 유색의 바인더를 칼라아스콘의 제조용 바인더로 사용하면서도,While using a variety of colored binders including the existing black asphalt pitch as a binder for the production of color asphalt,
투명아스팔트핏치를 이용한 칼라아스팔트에 발현되는 색상의 품질과 동일한 품질의 색상을 구현할 수 있도록 한 발명이다.It is an invention to realize a color of the same quality as the color of the color asphalt expressed using the transparent asphalt pitch.
Description
본 발명은 차도, 보도, 자전거 전용도로, 공원, 경기장트랙, 어린이 보호구역, 미끄럼 방지구역, 주차장 등에 시공되어 운전자와 보행자의 안전을 도모하고,The present invention is installed in a driveway, sidewalk, bicycle path, park, stadium track, child protection area, anti-slip area, parking lot, etc. to promote the safety of drivers and pedestrians,
보다 아름다운 도시미관을 제공하기 위하여 설치되는 칼라아스팔트용 골재 및 그 제조방법에 관한 것으로서 It relates to aggregates for color asphalt installed to provide a more beautiful city view and a manufacturing method thereof.
기존의 검정아스팔트핏치를 칼라아스콘의 제조용 바인더로 사용하면서도,While using the old black asphalt pitch as a binder for the production of color asphalt,
투명아스팔트핏치를 이용한 칼라아스팔트에 발현되는 색상의 품질과 동일한 품질의 색상을 구현할 수 있도록 한 발명이다.It is an invention to realize a color of the same quality as the color of the color asphalt expressed using the transparent asphalt pitch.
칼라아스팔트의 도입의 초기단계에서는In the early stages of the introduction of color asphalt
일반 차도용 검정아스팔트의 시공에 사용되었던 바인더인 검정아스팔트핏치에 안료를 투입하여 칼라아스콘을 제조하였으며, Color asphalt was prepared by adding a pigment to the black asphalt pitch, which is a binder used in the construction of black asphalt for general driveway.
이를 칼라아스팔트의 재료로 사용하였다.This was used as the material of the color asphalt.
즉,In other words,
아스콘 제조용 골재에 In aggregate for ascon production
검정아스팔트핏치(=아스팔트시멘트)에 제한된 몇 몇 색상의 안료를 첨가 및 혼합하므로써By adding and mixing several colors of pigments limited to black asphalt pitch (= asphalt cement)
안료가 검정아스팔트핏치에 균일하게 혼합되어 전체적으로 단일한 색상을 이루는 칼라아스콘을 제조하였으며, 이를 칼라아스팔트의 시공의 재료로 사용하였다.The pigment was uniformly mixed with the black asphalt pitch to produce a color ascone having a single color as a whole, which was used as a material for the construction of the color asphalt.
그러나 상기에서와 같이 검정아스팔트핏치를 바인더로 사용하여 제조된 칼라아스콘은 However, the color ascone prepared using the black asphalt pitch as a binder as described above
검정에 가까운 아스팔트핏치의 짙은 색상으로 인하여 Due to the dark color of the asphalt pitches
발현시키고자 첨가되었던 안료 원래의 색상이 발현시키는 것이 현실적으로 불가능하였으므로,Since it was practically impossible to express the original color of the pigment that was added to express,
색상 표현의 한계에 봉착하게 되었으며 이는 보다 다양한 소재의 개발을 요구해 오고 있다.We have faced the limitations of color expression, which has required the development of more diverse materials.
한편, 상술된 바와 같은 검정아스팔트핏치를 바인더로 사용하던 칼라아스팔트에 있어서의 단점인 색상표현의 한계를 극복하고자 On the other hand, to overcome the limitation of the color expression which is a disadvantage in the color asphalt used as the binder black asphalt pitch as described above
현재에는 검정아스팔트핏치를 대체하여 투명(반투명)아스팔트핏치를 아스콘 제조용 바인더로 사용하고 있다.Currently, transparent asphalt pitches are used to replace black asphalt pitches as binders for ascon.
그러나 투명아스팔트핏치는 높은 제조단가로 아스콘 제조단가 및 칼라아스팔트의 시공단가의 급격한 상승을 수반하여 소비자의 부담이 가중되는 현실적인 단점으로 귀결되게 되었다. However, the transparent asphalt pitch has resulted in the actual disadvantage that the burden on the consumer is accompanied by a sharp increase in the construction cost of ascon and the construction cost of the color asphalt due to the high manufacturing cost.
이에, 본 발명에서는,Therefore, in the present invention,
기존의 검정아스팔트핏치를 칼라아스콘의 제조용 바인더로 사용하면서도,While using the old black asphalt pitch as a binder for the production of color asphalt,
투명아스팔트핏치를 이용한 칼라아스팔트에 발현되는 색상의 품질과 동일한 품질의 색상이 구현될 수 있도록 하기 위하여,In order to achieve a color of the same quality as that of the color expressed on the color asphalt using the transparent asphalt pitch,
골재의 표면에 코팅될 바인더인 검정아스팔트핏치의 색을 희석(퇴색)시켜 바인더로 사용하거나, The color of black asphalt pitch, which is a binder to be coated on the surface of the aggregate, is diluted (faded) to be used as a binder,
골재표면에 1차 코팅된 검정아스팔트핏치층의 표면에 2차 코팅층을 형성시켜 검정색의 외부로의 노출을 차단하며,The secondary coating layer is formed on the surface of the black asphalt pitch layer coated on the aggregate surface to block black exposure to the outside,
상기 희석 또는 차단된 코팅층의 표면에 표현하고자 하는 색상의 안료의 색이 발현된 코팅재를 이용한 재코팅층이 형성되도록 하는 방법으로 제조된 칼라아스콘용 칼라골재 및 칼라상기 골재를 사용하여 시공된 칼라아스팔트를 제공하고자 한다.The color asphalt prepared by using the color aggregate and the color aggregate for the color ascone manufactured by the method for forming a recoating layer using the coating material expressing the color of the pigment of the color to be expressed on the surface of the diluted or blocked coating layer To provide.
칼라아스콘은Colorascon
아스팔트콘크리트(Asphalt Concrete)를 줄인 명칭이며, It is short for Asphalt Concrete.
아스팔트, 아스팔트혼합물, 아스팔트콘크리트, 가열혼합·가열포설 역청포장용혼합물(KSF2349 규격), HMA(hot mix asphalt)등 여러 가지로 호칭되고 있다.Asphalt, asphalt mixture, asphalt concrete, heat-mixed and heated laying bitumen paving mixture (KSF2349 standard), HMA (hot mix asphalt), etc. are called various.
아스팔트를 시공하기 위하여 제조되는 혼합물인 아스팔트 콘크리트 혼합물(이하"아스콘"이라 한다.)은 Asphalt concrete mixture (hereinafter referred to as "ascon"), which is a mixture prepared for the construction of asphalt,
그리고 상기의 구성은 아스팔트(asphalt)와 굵은골재(자갈:Aggregate), 잔골재(모래:Sand) 또는 포장용 채움재(필러,석분:mineral filler) 등으로 이루어져 있으며, And the configuration is composed of asphalt (asphalt) and coarse aggregate (gravel: Aggregate), fine aggregate (sand: Sand) or packing filler (filler, mineral powder),
상기를 가열 혼합 또는 상온 혼합한 것으로 사용목적 이나 용도, 기능, 공법에 따라 여러 가지로 구분하고 있다. The above is mixed by heating or room temperature and classified into various types according to the purpose of use, use, function, and construction method.
일반적인 시방서에 따르는 아스팔트의 적층 구조는 다음과 같다.Asphalt laminate according to the general specification is as follows.
*표층 (Surface Course) * Surface Course
*중간층 (Binder Course) * Binder Course
*기층 (Base Course) * Base Course
*보조기층 (Subbase Course) * Subbase Course
*동상방지층 (Antifrost Layer) * Antifrost Layer
*차단층 (filter Layer) * Filter layer
*노상 (Subgrade)으로 구성되어짐이 일반적이며,* Generally composed of subgrade
다음은 본 발명의 이해를 돕기 위하여 아스콘의 종류 및 재료 등에 대해서 알아본다.Next, to help understand the present invention, it looks at the types and materials of ascon.
*아스콘(아스팔트콘크리트혼합물)포장의 종류에 따른 분류로는 * The classification according to the type of ascon (asphalt concrete mixture) packaging
1. 공법에 의한 구분: 일반 아스콘 포장, 개질 아스콘 포장, 재생 아스콘 포장 1. Classification by construction method: normal ascon packaging, modified ascon packaging, recycled ascon packaging
2. 기능에 의한 구분: 일반 포장, 칼라 포장, 미끄럼 방지 포장, 내유성 포장, 배수성 포장, 투수성 포장 (보도, 자전차도로 등) 2. Classification by function: general pavement, color pavement, anti-slip pavement, oil proof pavement, drainage pavement, water permeable pavement (press, bicycle road, etc.)
3. 장소에 의한 구분: 차도 포장, 보도 포장, 공항 활주로 포장, 주차장 포장, 터널 포장, 교면 포장, 공원 포장, 운동장 포장 3. Classification by place: driveway pavement, sidewalk pavement, airport runway pavement, parking lot pavement, tunnel pavement, bridge pavement, park pavement, playground pavement
등으로 나눌 수 있다.And so on.
*아스콘의 종류 및 품질규격은 * Ascon type and quality standard
KSF2349에 따라 기층용(3개), 표층(중간층)용(11개)으로 구분되어 있다.According to KSF2349, it is divided into base layer (3 pieces) and surface layer (middle layer) pieces (11 pieces).
*아스콘의 규격은, 혼합골재 최대입도의 골재번호에 따라 * The specification of ascon, according to the aggregate number of the maximum particle size of mixed aggregate
#78(78호), #67(67호), #57(57 호), #467(467호),#357(357호)로 호칭되고 있다. It is called # 78 (78), # 67 (67), # 57 (57), # 467 (467), and # 357 (357).
#78규격의 골재 최대크기는 13㎜이며, Maximum aggregate size of # 78 standard is 13㎜,
#67규격은 20㎜, # 67 is 20mm
#57규격은 25㎜, # 57 is 25mm
#467규격은 40 ㎜, # 467 size is 40 mm,
#367규격은 50㎜로 구분된다.The # 367 standard is divided into 50mm.
한편, 아스팔트의 혼합재인 아스콘의 제조에 사용되는 재료로는, In addition, as a material used for manufacture of the asphalt concrete which is a mixed material of asphalt,
1. 아스팔트(Asphalt) Asphalt
유기혼합물과 미량의 무기화합물등이 포함된 수 천 종 이상의 고분자 탄화수소(CH)가 매우 복잡하게 구성된 흑색 또는 흑갈색 고체 또는 반고체의 열가소성 물질을 뜻하며 미국은 아스팔트시멘트(Asphalt Cement), 유럽은 비트멘(Bitumen:역청)으로 통용된다. It is a black or dark brown solid or semi-solid thermoplastic composed of thousands of high molecular hydrocarbons (CH) containing organic mixtures and trace inorganic compounds. Commonly used as Bitumen.
ㄱ) 천연아스팔트A) natural asphalt
레이크(Lake) 아스팔트, 록(Lock)아스팔트, 샌드아스팔트, 길소나이트 아스팔트, 그라하마이트아스팔트, 글랜스피치아스팔트 Lake Asphalt, Lock Asphalt, Sand Asphalt, Gilsonite Asphalt, Grahamite Asphalt, Gland Peach Asphalt
ㄴ) 석유아스팔트B) petroleum asphalt
스트레이트 아스팔트(KSM2201), 아스팔트시멘트(도로 포장용 아스팔트로 사용) 커트백아스팔트 (KSM2202), 유화아스팔트 (KSM2203), 블로운아스팔트, 개질아스팔트 Straight Asphalt (KSM2201), Asphalt Cement (Used for Road Paving Asphalt) Cut Back Asphalt (KSM2202), Emulsified Asphalt (KSM2203), Blown Asphalt, Modified Asphalt
등이 있다.Etc.
a. 아스팔트시멘트a. Asphalt cement
도로포장용으로 사용되는 아스팔트를 말하며 감압증류공정(VDU)에서 운전조건을 조정하여 침입도 및 기타물성을 조절하여 생산한다. Asphalt used for road pavement, produced by adjusting operating conditions in VDU.
현재 국내에서는 침입도 80-100인 AP-3와 침입도 60-80인 AP-5가 사용되고 있는데, Currently in Korea, AP-3 with 80-100 intrusion and AP-5 with 60-80 intrusion are used.
종래 AP-3가 시장의 주종을 이루고 있었던데 비해 최근에는 혹서기 도로파손 피해(소성변형)를 예방하기 위하여 고온에서의 포장성능이 상대적으로 우수하다고 평가되는 AP-5의 수요가 점증하고 있다.Conventional AP-3 has been the dominant market, but in recent years, the demand for AP-5, which is considered to have a relatively good pavement performance at high temperature in order to prevent road damage damage (plastic deformation), is increasing.
b. 컷백아스팔트b. Cut back asphalt
도로포장용 아스팔트인 아스팔트시멘트는 상온에서 반고체 상태이므로 골재와 혼합하거나 살포시는 가열하여 사용해야 하는 불편이 따르는데, Asphalt cement, a road paving asphalt, is semisolid at room temperature, so it is inconvenient to use it when it is mixed with aggregate or heated.
이를 개선한 것이 컷백아스팔트이다. The improvement is the cutback asphalt.
상온에서 액체상태로 만들기 위해 사용된 용제의 종류에 따라 급속경화형(Rapid Curing : RC), 중속경화형(Medium Curing : MC), 완속경화형(Slow Curing : SC) 등이 있으며, Rapid Curing (RC), Medium Curing (MC), and Slow Curing (SC) are available depending on the type of solvent used to make the liquid at room temperature.
현재 국내시장은 중속경화형이 대부분 사용된다.Currently, the medium-speed hardening type is mostly used in the domestic market.
c. 개질아스팔트c. Modified asphalt
특정용도의 도로포장에 사용하기 위하여 아스팔트시멘트에 합성수지나 고무 등을 첨가하여 포장성능을 개선시킨 아스팔트로서, 교량, 고가도로 및 중차량도로 등의 포장에 사용되고 있으며 도심도로의 경우 빛의 반사 또는 우천시 빗물고임 등의 문제를 해결하기 위하여 배수 아스팔트(Drainage)가 사용되기도 한다. Asphalt which improves pavement performance by adding synthetic resin or rubber to asphalt cement for use in paving road for specific use. It is used for pavement of bridges, overpasses and heavy vehicle roads. Drainage asphalt is also used to solve problems such as pooling.
ㄷ) 타르(Tar)Tar
타르는 주로 석탄의 건류 과정에서 얻어지며 매우 특이한 냄새가 나는 것이 특징으로 흑색의 액체이며, 한국산업규격 KS M 2206 포장타르로 정하여져 있다. Tar is mainly obtained from coal drying process and has a very peculiar smell. It is a black liquid, and it is determined by Korean Industrial Standard KS M 2206 Pavement Tar.
2. 골재 2. Aggregate
ㄱ) 굵은 골재 아스콘용 굵은 골재는 단단하고, 강하고, 내구적이며, A) coarse aggregate coarse aggregate for ascon is hard, strong, durable,
부착물이 없어야 하고 점토나 실트 그 밖의 해로운 물질이 함유되어 있지 않은 것으로 KSF2357 규격에 적합한 것이어야 한다. It shall be free of deposits and contain no clay, silt or other harmful substances and shall comply with the KSF2357 standard.
ㄴ) 잔골재 아스콘용 잔골재는 자연모래와 암석, 자갈 등을 깨어 얻어진 부순 모래 또는 이들의 혼합물을 말하며, KSF2357 규격에 적합한 것이어야 한다. B) Fine aggregate As aggregate fine aggregate for ascon refers to crushed sand or mixture thereof obtained by breaking natural sand, rock and gravel, etc., and shall comply with KSF2357 standard.
3. 채움재 3. Filler
채움재는 석회석분, 포틀랜드 시멘트, 소석회, 플라이애쉬, 회수더스트, 전기로 제강더스트, 주물더스트, 각종 소각회 및 기타 적당한 광물성 물질의 분말이어야 한다. Filler shall be powder of limestone powder, portland cement, slaked lime, fly ash, recovered dust, furnace steelmaking dust, foundry dust, various incineration ashes and other suitable mineral substances.
사용할 때에는 먼지, 진흙, 유기물, 덩어리진 미립자 등의 해로운 물질이 함유되어 있지 않아야 하며, 품질이 KSF3501 규격에 적합한 것이어야 한다.When used, it should be free of harmful substances such as dust, mud, organic matter, agglomerated fine particles, etc., and its quality should be in accordance with KSF3501 standard.
일반적인 기존의 칼라아스팔트에 있어서는,In general existing color asphalt,
상술된 각 군의 재료로부터 선택된 아스팔트, 골재, 채움재 등과 발현시키고자 하는 색상의 안료를 믹싱기 내에 동시에 투입하고, Asphalt, aggregate, filler and the like selected from the above-described materials of each group are simultaneously introduced into the mixer into the pigment of the color to be expressed,
아스팔트재의 특성에 따라 상기를 상온믹싱 또는 가열믹싱(150~200도씨)하므로써 전체적으로 단일한 색상을 띠는 칼라아스콘을 제조하고 이를 칼라아스팔트의 시공에 사용하여 왔다.Depending on the characteristics of the asphalt material, the above-mentioned mixing at room temperature or heating (150-200 degrees C) has produced a color ascone having a single color as a whole and has been used in the construction of color asphalt.
그러나 현재 칼라아스콘의 제조용 바인더로 주로 사용되고 있는However, currently used mainly as a binder for the production of color ascon
투명아스팔트핏치는 그 제조단가가 고가이므로,As the transparent asphalt fittings are expensive to manufacture,
전체 칼라아스팔트의 시공단가를 상승시키는 원인으로 작용하고 있다.It is acting as a cause to raise the construction cost of the entire color asphalt.
이에 본 발명에서는 전술된 [발명이 속하는 기술분야 및 그 분야의 종래기술]의 단점을 해소된 칼라아스팔트를 제공하기 위하여, 검정아스팔트핏치를 포함하는 유색의 바인더재를 아스팔트재로 사용하여 이하의 공정을 통해 칼라아스콘을 제조하고자 한다.Therefore, in the present invention, in order to provide a color asphalt solved the above-mentioned disadvantages of the technical field of the present invention and the prior art in the field, using a colored binder material including black asphalt pitch as an asphalt material in the following process To prepare a color ascon through.
(다양한 종류의 유색바인더재를 대표하여 검정아스팔트핏치를 아스팔트재로 사용한 실시예에 의해 본 발명의 제조공정을 포괄하여 설명한다.) (The manufacturing process of the present invention will be comprehensively described by examples in which black asphalt pitches are used as asphalt materials on behalf of various types of colored binder materials.)
공정 1): Process 1):
골재의 표면에 코팅될 바인더재인 검정아스팔트핏치의 색을 희석시키므로 써 골재의 표면에 상기 희석된 색상의 1차 희석코팅층을 형성시키거나(a),By diluting the color of the black asphalt pitch, which is a binder material to be coated on the surface of the aggregate, to form a first dilution coating layer of the diluted color on the surface of the aggregate (a),
또는 골재의 표면에 검정아스팔트핏치로 1차 코팅층을 형성시키고,Or to form a primary coating layer with black asphalt pitch on the surface of the aggregate,
상기 코팅층의 표면에 2차로 차단코팅층을 형성시켜 바인더재의 원색상인 검정색이 By forming a second barrier coating layer on the surface of the coating layer is black as the primary color of the binder material
외부로의 노출되는 것을 차단하는 단계(b);(B) blocking exposure to the outside;
공정 2): Process 2):
상기 희석코팅층 또는 차단코팅층의 표면에 On the surface of the dilution coating layer or barrier coating layer
발현시키고자 하는 색상의 안료 또는 상기 색상이 발현된 코팅재를 이용하여 By using the pigment of the color to be expressed or the coating material expressing the color
재코팅하므로써 원하는 색상의 코팅층이 형성되도록 하는 단계; Recoating to form a coating layer of a desired color;
의 두 단계공정으로 요약될 수 있다.It can be summarized in two steps.
그러면 상기 본 발명의 구성을 단계별로 보다 상세히 설명한다.This will be described in more detail step by step the configuration of the present invention.
상기 공정1)의 a)를 실현하고자,In order to realize a) of step 1),
회전하는 믹싱기의 내부에 검정색(또는 진회색)아스팔트핏치와 백색의 안료 또는 백색석분을 동시에 투입하고, A black (or dark gray) asphalt pitch and a white pigment or white stone powder are simultaneously introduced into the rotating mixer.
상기를 균일하게 혼합하므로써 검정색상의 아스팔트핏치가 회백색을 띄도록 색상을 희석시킨다.By uniformly mixing the above, dilute the color so that the asphalt pitch of black color becomes grayish white.
상기 b)를 실현하고자,To realize b) above,
ㄱ)회전하는 믹싱기의 내부에 검정아스팔트핏치와 골재를 투입하고, A) put black asphalt pitch and aggregate into the inside of the rotating mixer,
상기를 믹싱하므로써 골재의 표면에 검정아스팔트핏치의 코팅층이 형성되도록 하며,By mixing the above to form a coating layer of black asphalt pitch on the surface of the aggregate,
ㄴ)상기 이후에 백색의 안료 또는 백색석분을 투입하므로써 검정의 코팅층의 표면에 백색의 2차 코팅층이 형성되도록 한다.B) After the addition of a white pigment or white stone powder to form a white secondary coating layer on the surface of the black coating layer.
그러나 상기 백색안료 및 백색석분을 투입하는 대신에 백색을 띠는 유, 무기원료의 액상수지 중 1종을 투입하므로써 차단코팅층을 형성할 수도 있다.However, instead of adding the white pigment and the white stone powder, it is also possible to form a barrier coating layer by adding one of the liquid resin of the white oil, inorganic material.
상기 ㄴ)의 액상수지의 투입량을 미리 계측하여 상기 ㄱ)에서 투입되는 검정아스팔트핏치의 투입량을 감하도록 한다.The input amount of the liquid resin of b) is measured in advance so as to reduce the input amount of the black asphalt pitch input from the a).
상기 공정 1)의 a) 및 b)의 단계의 이후에 이루어지는 공정 2)의 단계를 실현하고자,In order to realize the step of step 2) after the step a) and b) of the step 1),
상기 공정1)의 a) 또는 b) 중 하나의 단계의 이후에 After step a) or b) of step 1).
믹싱기의 내부에 발현시키고자 하는 색상의 안료를 투입하거나,Inject the pigment of the color to be expressed inside the mixer,
유기 또는 무기원료로 제조된 동일한 색상의 액상수지를 믹싱기의 내부에 투입하므로써 상기 희석코팅층 또는 차단코팅층의 표면에 발현시키고자 하는 색상의 코팅층이 형성되도록 한다.By adding the liquid resin of the same color made of organic or inorganic raw materials into the mixing machine to form a coating layer of the color to be expressed on the surface of the dilution coating layer or the barrier coating layer.
한편, Meanwhile,
상기 믹싱의 단계에 투입되는 전체 바인더인 검정아스팔트피치 및 액상수지의 양에 따라 According to the amount of the black asphalt pitch and the liquid resin, which are all binders added to the mixing step
칼라골재 또는 칼라아스콘의 두 형태로 제조가 가능하다.It can be produced in two forms: colored aggregate or colored ascon.
상기를 칼라골재로서 제조하기 위한 검정아스팔트피치를 포함하는 전체 바인더의 투입양은The input amount of the total binder including the black asphalt pitch for preparing the above as a color aggregate is
투입골재의 표면적과 비례하여 골재 표면에 적절한 두께의 코팅층을 형성할 수 있는 양으로 감소시켜 투입하여야하며, 이는 이하 기술될 실시예인 D에 예시한다.In proportion to the surface area of the input aggregate, the input should be reduced to an amount capable of forming a coating layer of an appropriate thickness on the aggregate surface, which is illustrated in Example D, which will be described below.
상기 제조된 칼라골재는 The manufactured aggregate is
믹싱기의 외부로 투출시켜 상온 또는 저온에서 건조하므로써 칼라골재로 제조보관하여 추후 아스콘용 골재로 사용한다.It is thrown to the outside of the mixer and dried at room temperature or low temperature, so it is manufactured and stored as color aggregate and used as aggregate for later use.
또한, 이와 같은 방법으로 제조한 다양한 색상의 칼라골재를 2 종 이상 혼합하고, 상기에 아스팔트재를 혼합, 칼라아스팔트의 시공면에 포설 및 전압하므로써 여러 색상이 혼합된 골재로 이루어진 칼라아스팔트를 제공할 수 있게 된다.In addition, by mixing two or more kinds of color aggregates of various colors prepared by the above method, by mixing the asphalt material on the construction surface of the color asphalt, and providing a color asphalt consisting of aggregates mixed in a number of colors. It becomes possible.
또 칼라아스콘의 제조에 사용되는 검정아스팔트핏치를 포함하는 전체 바인더의 투입양은 In addition, the input amount of the total binder including the black asphalt pitch used for the production of color asphalt
투입골재의 표면적과 비례하여 골재 표면에 적절한 두께의 코팅층을 형성할 수 있는 양The amount capable of forming a coating layer of suitable thickness on the aggregate surface in proportion to the surface area of the input aggregate.
에 칼라아스팔트의 시공에 적합한 접착력이 발현되는 바인더의 양이 추가로 증가 투입되어 제조되어야 한다. 이는 이하 기술될 실시예인 A,B,C,E에 예시한다.The amount of the binder expressing the adhesive force suitable for the construction of the colored asphalt should be added to increase the production. This is illustrated in the examples A, B, C, and E which will be described below.
상기 제조된 칼라아스콘은 칼라아스팔트시공면에 타설 및 전압 후, After the prepared colored asphalt is placed on the color asphalt construction surface and voltage,
건조 및 경화의 단계를 거쳐 칼라아스팔트로 완성되게 된다.It is dried and cured to complete the colored asphalt.
이하 실시예를 들어 본 발명을 보다 상세히 설명한다.The present invention will be described in more detail with reference to the following Examples.
A. A.
(골재의 품질 및 규격은 KSF2357 규격에 적합한 것을 사용한다.)(The quality and specification of the aggregate should be suitable for KSF2357 standard.)
굵은골재(자갈:Aggregate), 잔골재(모래:Sand) 또는 채움재(필러,석분:mineral filler)를 적정비율로 혼합한 혼합골재 1000KG,Coarse aggregate (gravel: Aggregate), fine aggregate (sand :) or filler (mineral filler) mixed aggregate 1000KG,
검정아스팔트핏치 60KGBlack Asphalt Pitch 60KG
백색석분(탄산칼슘) 30KG, White stone powder (calcium carbonate) 30KG,
적색안료10KG을 원료로 한다.10kg red pigment is used as raw material.
1)골재와 검정아스팔트피치 및 백색석분을 믹싱기에 투입 약 20~30초간 혼합한다(아스팔트피치의 검정색상이 희석된 회백색의 아스팔트피치 및 골재표면에 회백색의 코팅층 형성)1) Aggregate, black asphalt pitch and white stone powder are mixed in the mixer for about 20 ~ 30 seconds.
2)상기에 적색의 안료를 투입하고 15~20초간 혼합하므로써 칼라아스콘을 제조한다.(적색의 코팅층 및 전체적으로 적색인 칼라아스콘 형성).2) A color pigment is prepared by adding a red pigment to the mixture and mixing for 15 to 20 seconds. (Formation of a red coating layer and overall color ascon).
3)상기를 아스팔트 시공면에 포설 및 전압하므로써 적색의 아스팔트를 시공한다. 3) Red asphalt is constructed by laying and voltage on the asphalt construction surface.
B.B.
골재 1000KGAggregate 1000KG
검정아스팔트피치 30KGBlack Asphalt Pitch 30KG
*투명아스팔트피치 30KG* Transparent asphalt pitch 30KG
백색석분 30KGWhite Stone Powder 30KG
증백제(산화티타늄) 4KGBrightener (Titanium Oxide) 4KG
청색안료 10KGBlue Pigment 10KG
을 원료로 한다.Is used as a raw material.
1)골재와 검정아스팔트피치30KG 및 투명아스팔트피치10KG을 믹싱기에 투입 약 20~30초간 혼합하여 골재표면에 아스팔트피치의 코팅층을 형성한다.1) Aggregate, black asphalt pitch 30KG and transparent asphalt pitch 10KG are added to the mixer for about 20-30 seconds to form a coating layer of asphalt pitch on the aggregate surface.
2)상기에 백색석분을 투입하여 15~20초간 혼합한다(상기 1)의 코팅층의 상단에 백색의 코팅층을 형성).2) The white stone powder is added to the mixture for 15 to 20 seconds (to form a white coating layer on the top of the coating layer of 1).
3)상기에 청색안료와 투명아스팔트피치20KG을 투입하여 15~20초간 혼합하므로써 칼라아스콘을 제조한다(청색의 코팅층이 형성됨과 동시에 전체적으로 청색인 칼라아스콘 제조).3) The blue pigment and transparent asphalt pitch 20KG was added to the mixture for 15 to 20 seconds to prepare a color ascon (blue coating layer is formed and at the same time as a whole blue color ascon production).
4)상기를 아스팔트 시공면에 포설 및 전압하므로써 청색의 아스팔트를 시공한다. 4) Blue asphalt is constructed by laying and voltage on the asphalt construction surface.
(검정아스팔트피치의 투여량이 감소되었으므로 안료의 투입량을 감소시킬 수 있다.)(The dosage of the black asphalt pitch is reduced, thus reducing the dosage of the pigment.)
C.C.
골재 1000KGAggregate 1000KG
검정아스팔트핏치 50KGBlack Asphalt Pitch 50KG
백색의 무기 또는 유기원료의 액상수지 10KG10KG liquid resin of inorganic or organic raw material
백색석분 30KGWhite Stone Powder 30KG
증백제(산화티타늄) 4KGBrightener (Titanium Oxide) 4KG
황색안료 10KGYellow Pigment 10KG
을 원료로 한다.Is used as a raw material.
1)골재와 검정아스팔트핏치를 믹싱기에 투입 약 20~30초간 혼합한다.1) Put aggregate and black asphalt pitcher into the mixer and mix for about 20-30 seconds.
2)상기에 백색석분과 백색의 무기 또는 유기원료의 액상수지 10KG을 투입하여 15~20초간 혼합한다.2) Put 10KG of liquid resin of white stone powder and white inorganic or organic raw material and mix for 15 ~ 20 seconds.
3)상기에 황색안료를 투입하여 15~20초간 혼합하므로써 칼라아스콘을 제조한다.3) The color pigment is prepared by adding yellow pigment to the mixture for 15 to 20 seconds.
4)상기를 아스팔트 시공면에 포설 및 전압하므로써 황색의 아스팔트를 시공한다. 4) Yellow asphalt is constructed by laying and voltage on the asphalt construction surface.
D.D.
골재 1000KGAggregate 1000KG
검정아스팔트핏치 20KGBlack Asphalt Pitch 20KG
*백색의 무기 또는 유기원료의 액상수지 10KG* 10KG of liquid resin of white inorganic or organic raw material
화이트카본20KGWhite Carbon 20KG
증백제 2KGBrightener 2KG
안료 6KGPigment 6KG
을 원료로 한다.Is used as a raw material.
1)골재와 검정아스팔트핏치를 믹싱기에 투입 약 20~30초간 혼합한다.1) Put aggregate and black asphalt pitcher into the mixer and mix for about 20-30 seconds.
2)상기에 화이트카본을 투입하여 15~20초간 혼합한다(백색의 코팅층 형성).2) Put white carbon in the above and mix for 15 to 20 seconds (white coating layer formation).
3)상기에 안료 및 증백제를 투입하여 15~20초간 혼합하므로써 칼라골재를 제조한다.3) Put the pigment and brightener into the above to prepare a color aggregate by mixing for 15 to 20 seconds.
4)상기 골재를 믹싱기 외부로 투출시키고, 상온 또는 저온으로 경화 및 건조하여 건식의 칼라골재로 제조한다.4) The aggregate is discharged to the outside of the mixer, and cured and dried at room temperature or low temperature to produce a dry colored aggregate.
상기 건식의 칼라골재를 칼라아스콘의 제조공정에 골재로 믹싱기에 투입하고,The dry color aggregate is put into the mixing machine as an aggregate in the manufacturing process of color ascon,
상기에 투명 또는 반투명의 유기 또는 무기원료의 액상수지 Transparent or translucent liquid resin of organic or inorganic raw material
또는 골재의 색상과 동일한 유기 또는 무기원료의 액상수지30KG을 상온 또는 가열혼합기에 투입하여 20~30초간 혼합한 후, Alternatively, 30 kg of liquid resin of organic or inorganic raw material of the same color as the aggregate is added to a room temperature or a heating mixer, and then mixed for 20 to 30 seconds.
아스팔트 시공면에 포설 및 전압하므로써 원하는 색상의 칼라아스팔트를 시공한다. Color asphalt of desired color is constructed by laying and voltage on asphalt construction surface.
E.E.
골재 1000KGAggregate 1000KG
검정아스팔트핏치 30KGBlack Asphalt Pitch 30KG
백색의 액상합성수지 15KG White Liquid Synthetic Resin 15KG
증백제 (산화티타늄)2KGBrightener (Titanium Oxide) 2KG
안료15KG이 혼합된 액상합성수지 15KG(원하는 색상의 안료 혼합)Liquid synthetic resin 15KG mixed with pigment 15KG (Pigment of desired color)
을 원료로 한다.Is used as a raw material.
1)골재와 검정아스팔트핏치를 믹싱기에 투입 약 20~30초간 혼합한다(검정색의 코팅층 형성).1) Put the aggregate and black asphalt pitch into the mixer and mix for about 20-30 seconds (formation of black coating layer).
2)상기에 백색의 액상수지를 투입하여 15~20초간 혼합한다(백색의 코팅층 형성).2) Put the white liquid resin into the mixture for 15 to 20 seconds (white coating layer formation).
3)상기에 안료가 혼합된 액상합성수지와 화이트카본을 투입하여 15~20초간 혼합하므로써 칼라아스콘을 제조한다.(원하는 색상의 코팅층 형성).3) Put the liquid synthetic resin and the white carbon mixed with the above pigment for 15 to 20 seconds to prepare a color ascone (to form a coating layer of the desired color).
4)상기를 아스팔트 시공면에 포설 및 전압하므로써 칼라아스팔트를 시공한다. 4) Color asphalt is constructed by laying and voltage on the asphalt construction surface.
한편, 상기 실시예를 통해 희석된 바인더재를 사용하여 제조되는 골재 및 칼라아스콘에 있어서는, 투입안료를 실제 발현시키고자 하는 색상보다 짙은 색상으로 선택하므로써 희석바인더재와 혼합된 상태에서 실제 원하는 색상에 가장 가까운 색상을 발현하도록 제조하는 것이 바람직하다.On the other hand, in the aggregate and color ascone manufactured using the binder material diluted through the above embodiment, by selecting a color darker than the color to actually express the input pigment to the actual desired color in the mixed state with the dilution binder material It is desirable to make it to produce the closest color.
또한, 칼라아스팔트에 실제 발현시키고자 하는 실제 색상에 따라 검정아스팔트핏치의 희석비율을 가감한다.In addition, the dilution ratio of the black asphalt pitch is added or subtracted according to the actual color to be actually expressed in the colored asphalt.
아울러, 상기 모든 실시예에 있어서 각 원료간의 혼합비는 혼합원료의 특성을 감안하여 적정비율로 가감이 가능하다.In addition, in all the above embodiments, the mixing ratio between the respective raw materials may be added or decreased at an appropriate ratio in consideration of the characteristics of the mixed raw materials.
또한 보다 선명한 색상을 발현시키기 위하여 산화티타늄을 포함하는 각종 증백제 중 1종을 첨가혼합하여 제조하거나,In addition, to produce a more vivid color by adding and mixing one of the various brighteners including titanium oxide,
또는 각종 물리적혼화재 및 화학적혼화제를 필요에 따라 투여하여 제조하므로써Or by administering various physical admixtures and chemical admixtures as necessary
작업성 및 물성이 강화된 칼라골재 및 칼라아스콘을 제조할 수 있다.Color aggregates and colored ascones can be produced with enhanced workability and physical properties.
또 본 발명에 따라 칼라골재 및 칼라아스콘의 제조에 사용되는 바인더의 원색상에 관계없이 원하는 색상의 칼라골재 및 칼라아스콘이 제조가능하게 되므로서, In addition, according to the present invention, regardless of the primary color of the binder used for the production of color aggregates and color ascones, color aggregates and color ascones of a desired color can be manufactured,
그에 따라 사용가능한 바인더재는 상술된 예에서 언급한 검정아스팔트핏치를 포함하는 것은 물론이거니와 그 외에도 칼라아스팔트의 시공에 적합하도록 제조된 유색의 바인더 및 유색의 합성수지폐기물을 원료로 하여 제조된 재활용바인더 등도 사용가능하게 되었으며,Accordingly, the binder material usable may include not only the black asphalt pitch mentioned in the above-mentioned examples, but also used colored binders and recycled binders made of colored synthetic resin wastes, which are suitable for the construction of colored asphalt. Is possible,
상기 유색의 바인더재는 본 발명에 따라 희석코팅 및 차단코팅되므로써 원하는 색상을 적절하게 표현할 수 있는 칼라아스팔트제조용 바인더로서 사용될 수 있게 된다.The colored binder material can be used as a binder for producing color asphalt which can appropriately express a desired color by dilution coating and blocking coating according to the present invention.
또 상기 다양한 실시예에 따른 칼라아스콘의 혼합공정에 각종 반사분말(반짝이가루 등), 인광안료, 야광안료 등을 첨가제조하거나,In addition, various reflective powders (shiny powder, etc.), phosphorescent pigments, luminous pigments, etc. may be added to the mixing process of the color ascon according to the various embodiments;
칼라골재를 특정 규격의 판상의 성형물의 표면에 접착하여 블럭형으로 제조하고, 이를 원하는 시공면에 모자이크식 배열로 시공하므로써By adhering the color aggregate to the surface of the plate-shaped molding of a specific standard, it is manufactured in the form of a block, and it is constructed in a mosaic arrangement on the desired construction surface.
더욱 다양한 미감을 제공할 수 있는 칼라아스팔트를 제공할 수 있다. Color asphalt can be provided that can provide a variety of aesthetics.
본 발명에 따라 제조된 칼라아스콘을 차도, 보도, 자전거 전용도로, 어린이 보호구역, 미끄럼 방지구역, 주차장 등에 다양한 색상으로 시공하여The construction of Calas Ascon according to the present invention in a variety of colors, such as roads, sidewalks, bicycle paths, child protection zones, anti-slip zones, parking lots, etc.
명시성을 높이므로써 운전자와 보행자의 경각심 유발시키고,By increasing the clarity, it raises awareness of drivers and pedestrians,
강한 마찰저항을 갖는 노면을 제공하므로써 감속의 보조수단의 역할을 하므로써 교통사고를 줄이며,By providing a road surface with strong frictional resistance, it reduces traffic accidents by acting as an auxiliary means of deceleration
경기장트랙, 공원, 산책로, 인도 등에 시공하므로써 보다 아름다운 도시미관을 제공하는 등의 유익한 기능을 저단가로 제공할 수 있으며,By providing construction tracks, parks, trails, sidewalks, etc., it is possible to provide useful functions such as providing a more beautiful city aesthetic at a lower price.
미리 제조된 칼라골재를 사용하여 칼라아스팔트를 시공하게 되므로써 공정을 축소시키는 장점을 제공할 수 있게 되는 효과,By using pre-manufactured color aggregates, color asphalt is used to provide the benefits of reducing the process.
또 칼라골재 및 칼라아스콘의 제조에 사용되는 바인더재의 원색상에 관계없이 원하는 색상의 칼라골재 및 칼라아스콘이 본 발명에 따라 제조가능하게 되므로서, In addition, the color aggregate and the color ascon of the desired color can be manufactured according to the present invention irrespective of the primary color of the binder material used for the production of the color aggregate and the color ascon,
칼라아스팔트에 사용가능한 바인더재는 검정아스팔트핏치를 포함하는 것은 물론이거니와 그 외에도 칼라아스팔트의 시공에 적합하도록 제조된 유색의 바인더 및 유색의 합성수지폐기물을 원료로 하여 제조된 재활용바인더 등도 사용가능하게 되었으며,The binder material that can be used for the colored asphalt includes not only black asphalt pitch, but also colored binders and recycled binders made of colored synthetic resin wastes that are suitable for the construction of colored asphalt.
상기 유색의 바인더재는 본 발명에 따라 희석코팅 및 차단코팅되므로써 원하는 색상을 적절하게 표현할 수 있는 칼라아스팔트제조용 바인더로서 사용될 수 있게 된다.The colored binder material can be used as a binder for producing color asphalt which can appropriately express a desired color by dilution coating and blocking coating according to the present invention.
또한, 다양한 색상의 칼라골재를 제조하고, 상기 칼라골재 2종 이상과 아스팔트재를 혼합하여 칼라아스콘을 제조하므로써 다색의 칼라아스팔트를 제공할 수 있게 된다.In addition, it is possible to provide a multi-color asphalt by producing a color aggregate of a variety of colors, by producing a color ascon by mixing two or more kinds of the color aggregate and asphalt material.
또한 본 발명에 따른 칼라골재를 사용하여 칼라블럭을 제조하고, 이를 원하는 모자이크식배열로 시공하므로써 전체적으로 다양한 문양을 이루는 칼라아스팔트를 제공할 수 있다.In addition, by using the color aggregate according to the present invention to produce a color block, by constructing the desired mosaic arrangement can provide a color asphalt forming a variety of patterns as a whole.
Claims (7)