KR200420952Y1 - Panel of finishing material - Google Patents

Abstract

The present invention relates to finish panels for construction and furniture.

In the technology of the conventional finish panel, veneer veneer to veneer plywood as a finish panel is thin, and also due to the weak physical properties of the wood, it is difficult to maintain the proper form because it is difficult to maintain the proper form in the finishing process, maintaining a suitable form and stable construction This was difficult, and after construction there was a problem that there is no durability.

The present invention provides a finishing thermoplastic panel for building and furniture, wherein a veneer end plate is provided at a front side and a rear side of the hard thermoplastic synthetic resin plate by a predetermined pressure and heated by a predetermined temperature. It relates to a finish panel made of a fixed contact.

According to the present invention, it is possible to easily manufacture a finish panel made of the hard synthetic resin plate fixed to the veneer end plate in contact with the front portion and the rear portion, respectively,

It is manufactured easily and inexpensively without using expensive adhesives for bonding wood and hard synthetic resin boards, and maintains the shape of natural friendly wood as a finishing surface during construction, and maintains the proper shape by hard synthetic resin boards. Since it is easily possible, stable construction is possible in the finishing process as a natural-friendly wood, and impact resistance after construction has a strong effect of durability.

Finishing panel, resin board

Description

Panel of finishing material

Figure 1a is a longitudinal sectional view showing a finisher panel according to the prior art,

Figure 1b is a perspective view showing a finisher panel according to the prior art,

Figure 1c is a longitudinal sectional view showing one example of the state of use of the finish panel according to the prior art,

Figure 2a is a longitudinal cross-sectional view showing the configuration and action of the finish panel according to the present invention,

FIG. 2B is an enlarged longitudinal sectional view of M in FIG. 2A;

Figure 3 is a perspective view of some cutaway showing the configuration and operation of the finish panel according to the present invention,

Figure 4 is a longitudinal sectional view showing one example of the use state of the finisher panel according to the present invention.

* Description of the symbols for the main parts of the drawings *

10: veneer veneer, 11: veneer veneer, 11s: small gap, 12: veneer veneer, 12s: small gap, 12-2: veneer veneer 12,

20: synthetic resin plate, 20-1: front portion, 20-1a: ridge, 20-2: rear portion, 20-2a: ridge,

100: finish panel,

200: wall surface, 200-1: surface portion, 300: adhesive

The present invention relates to a finishing panel (panel) for construction and furniture, in particular, a rigid thermoplastic synthetic resin plate is bonded to the veneer end plate in contact with the front and rear, respectively, to maintain an appropriate shape in the interior finish construction of natural wood It is possible to easily and stable construction, and also to maintain the best smoothness of the finish surface in the construction, and to a finish panel (panel) is maximized durability even after construction.

In the technique of the conventional finish panel, as shown in Figures 1a and 1b, 1c,

Veneer veneers 10, which are made by slicing solid wood, or thin veneer plywood, in which such veneer veneers are glued together with multiple sheets of adhesive (not shown), for building and furniture interior walls and ceilings. And surface finishing technology in veneer wood,

Veneer veneer 10 to veneer plywood as a finish panel is thin and weak in physical properties as wood, so it is well broken in the process of finishing as a natural wood for building interior walls, ceilings, and furniture. It was difficult to maintain the proper form and stable construction was difficult.

Furthermore, in the prior art, if the surface of the interior wall of the building, the surface of the ceiling, or the surface of the furniture is uneven, the uneven shape of the surface where the thin veneer veneer to thin veneer plywood, which is the finishing material panel, is bonded by the adhesive, the thin veneer Since it appears as a finish surface through the veneer through a thin veneer plywood as it is, there was a problem that aesthetic appearance is poorly finished.

In addition, in the prior art, it is difficult to change the shape of the finish panel made of thin veneer veneers or thin veneer plywood in the case of building interior walls, ceilings, furniture, or corners thereof. There was a difficult issue.

Furthermore, in the prior art, the finish panel of thin veneer veneer or thin veneer plywood is weak in durability due to the weakness of the physical properties as wood, and thus it is not resistant to impact on the finishing surface from the outside and thus has a low durability. Due to the impact on the surface there was a problem that the flaw easily occurs large.

In addition, in the prior art, an expensive adhesive is required to adhere the veneer veneer to the veneer plywood made of wood to the hard synthetic resin plate, and an attempt to adhere the veneer veneer to the veneer plywood made of wood to the hard synthetic resin plate is required. Since it could not be made, the finish panel made of wood has a low impact resistance, durability is weak, there is a problem that a large scratch easily occurs due to the impact on the finish surface from the outside.

The present invention is to solve the above problems in the prior art,

An object of the present invention is to provide a finish panel for building and furniture, wherein a rigid thermoplastic synthetic resin plate is provided, and veneer end plates are respectively applied to the front and rear surfaces of the rigid thermoplastic synthetic resin plate at a predetermined pressure and at a predetermined temperature. Made by contact by the heating by

It is possible to easily manufacture a finish panel made of the hard synthetic resin plate fixed to the veneer end plate in contact with the front portion and the rear portion, respectively,

It is easily manufactured at low cost without using expensive adhesive for bonding wood and hard synthetic resin board,

As the finishing surface, it is possible to maintain the shape of the natural friendly wood firmly and to maintain the proper shape by the hard synthetic resin board, so that the stable surface can be easily applied during the finishing process as the natural wood.

Moreover, if the surface of the interior wall of the building, the surface of the ceiling, and the surface of the furniture are uneven, the hard surface of the synthetic resin board can maintain the smoothness, so that the finishing surface can be properly smoothed and finished evenly. Can be processed and maintained in a state,

In addition, if the interior wall of the building, the ceiling, or furniture is curved, or at the corners of the building, the synthetic resin board, which is thermoplastic, can be solidified after being heated and softened by the appropriate shape change in construction. Easy to do,

In addition, even after construction, the hard synthetic resin plate has impact resistance against impacts from the exterior to the finish surface, and is durable, minimizing the occurrence of flaws due to impact on the finish surface from the outside. The purpose is to provide a finish panel that is capable of minimizing the size of the flaws.

Referring to the configuration of the subject innovation according to a preferred embodiment on the basis of the accompanying drawings as follows.

As the configuration of the present invention is shown in Figures 2a and 2b, and 3, 4,

In the finishing panel which is provided with the veneer veneer which is made by thinly turning solid wood so that surface finishing is possible for building and furniture;

A hard thermoplastic synthetic resin plate 20 is provided,

The veneer end plate 11 (that is, the veneer end plate 11 formed by turning the wood thin) is brought into contact with the front part 20-1 of the synthetic resin plate 20 (that is, Contact with the veneer end plate 11, which is in contact with the front portion 20-1 of the synthetic resin plate 20 is pressed at a predetermined pressure and simultaneously Heated to a temperature to soften and melt the front part 20-1 so as to flow, and the softened and melted front part 20-1 is a plurality of small pieces of the veneer end plate 11. The gap 11s is filled with the corresponding ridges 20-1a, and then solidified in accordance with the interruption of the pressurization and heating, and the front portion 20- of the synthetic resin plate 20. 1) the veneer end plate 11 is brought into contact with and fixed to the veneer end plate 11.

The veneer end plate 11 preferably has a thickness of about 0.1 mm to 1.0 mm.

The hard thermoplastic synthetic resin plate 20 may include an ABS (Acrylonitrile-butadiene-styrene) resin, HIPS (High Impact Polystyrene) resin, PET (Polyethylene terephthalate) resin, PP (Polypropylene) resin, PE (Polyethylene) resin, PVC (PVC) Preferred is a plate made of a polyvinylchloride resin, a polycarbonate resin, or the like.

The synthetic resin plate 20 is preferably about 0.2mm to 3mm in thickness.

The predetermined pressure is preferably about 50kgf / cm 2 to about 200kgf / cm 2, and may be appropriately increased or decreased depending on the material of the synthetic resin plate 20.

The predetermined temperature is preferably about 80 ° C to 300 ° C, and may be appropriately increased or decreased depending on the material of the synthetic resin plate 20.

The predetermined pressure and the predetermined temperature are preferable numerical values with high efficiency.

The veneer end plate 12 (that is, the veneer end plate 12 formed by turning the wood thin) is in contact with the back portion 20-2 of the synthetic resin plate 20 (that is, In contact with the veneer end plate 12 to which the back portion 20-2 of the synthetic resin plate 20 is in contact with the veneer end plate 12, which is in contact with it. The softened and melted surface is heated to allow the rear surface portion 20-2 to flow, and the softened and molten rear surface portion 20-2 is a plurality of small gaps 12s of the veneer end plate 12. After filling with the ridge 20-2a corresponding thereto, it solidifies in accordance with the interruption of the pressurization and heating, and the veneer on the rear portion 20-2 of the synthetic resin plate 20. The end plate 12 abuts and adheres.

The veneer end plate 12 preferably has a thickness of about 0.1 mm to 1.0 mm.

The predetermined pressure is preferably 50kgf / cm 2 to 200kgf / cm 2 as described above, and may be appropriately increased or decreased depending on the material of the synthetic resin plate 20.

As described above, the predetermined temperature is preferably about 80 ° C. to 300 ° C., and may be appropriately increased or decreased depending on the material of the synthetic resin plate 20.

The predetermined pressure and the predetermined temperature are preferable numerical values with high efficiency.

The veneer end plate 11 is fixed to the front portion 20-1 of the synthetic resin plate 20, and the veneer end plate 12 at the rear portion 20-2 of the synthetic resin plate 20. It is preferable that this process of fixation is performed simultaneously.

After the process of fixing the veneer end plate 11 to the front portion 20-1 of the synthetic resin plate 20 is performed, the veneer end plate on the rear portion 20-2 of the synthetic resin plate 20 ( 12) the fixing step is made, and the veneer end plate 12 is fixed to the back portion 20-2 of the synthetic resin plate 20 after the fixing step, the synthetic resin plate 20 of the Any method in which the veneer end plate 11 is fixed to the front portion 20-1 can be performed.

The veneer end plate 11 is fixed to the front portion 20-1 of the synthetic resin plate 20, and the veneer end plate 12 is attached to the rear portion 20-2 of the synthetic resin plate 20. In the fixed synthetic resin plate 20, the front surface of the veneer end plate 11 is more preferably a conventional coating (not shown) is made by a conventional method such as spray (spray).

The action of the present invention of the above configuration is as follows.

The operation of the present invention, as shown in Figures 2a and 2b, and 3, 4,

Since the veneer end plate 11 and the veneer end plate 12 are made of a thin wood, the veneer end plate 11 has a plurality of small gaps 11s and 12s, so that the veneer end plate 11 and the veneer end plate 12 are in contact with the synthetic resin plate 20. The front part 20- of the hard thermoplastic synthetic resin plate 20 which is in contact with each other, that is, in contact with each other, by pressurization by the predetermined pressure and heating by the predetermined temperature to be fixed. 1) and in the veneer end plate 11; In the back portion 20-2 and the veneer end plate 12 of the hard thermoplastic synthetic resin plate 20 which are in contact with each other, that is in contact with each other; The front portion 20-1 and the rear portion 20-2 are softened and melted to enable flow.

The thermoplastic synthetic resin material, which is the front portion 20-1 in the softened and molten state in such a manner as to be flowable, is brought into contact with the veneer end plate 11 by pressing by the predetermined pressure and heating by the predetermined temperature. The plurality of ridges 11s of the plurality of ridges 20-1a correspond to each other, and thus the plurality of ridges of the front portion 20-1 filled in the plurality of gaps 11s ( The synthetic resin material of 20-1a) is reduced in pressure and cooled in accordance with the interruption of the pressurization and heating, and solidifies to become an original hard synthetic resin state. In this case, the plurality of ridges 20-1a are solidified in an irregular shape and an irregular direction and fixed in the plurality of gaps 11s, so that the front portion of the synthetic resin board 20 is fixed. (20-1) and the veneer end plate 11 are not separable from each other, but are in contact with each other and fixed.

Similarly, the thermoplastic synthetic resin material, which is the rear portion 20-2 in the softened and molten state so as to be able to flow, is contacted with the veneer end plate 12 by pressing by the predetermined pressure and heating by the predetermined temperature. The plurality of ridges 20-2a corresponding to the plurality of gaps 12 s of the plurality of ridges 20-2a are filled in the plurality of gaps 12 s of the plurality of ridges 20-2. The synthetic resin material of -2a) is reduced in pressure and cooled in accordance with the interruption of the pressurization and heating, and solidifies to become an original hard synthetic resin state. In this case, since the plurality of ridges 20-2a are solidified in an irregular shape and an irregular direction and fixed in the plurality of gaps 12s, the rear portion of the synthetic resin plate 20 is formed. 20-2) and the veneer end plate 12 are not separable from each other, but are in contact with each other and fixed.

Desirable efficiency is achieved by the desired pressure and the desired temperature.

The veneer end plate 11 is in contact with and fixed to the front portion 20-1 of the synthetic resin plate 20, and the veneer end plate 12 is attached to the rear portion 20-2 of the synthetic resin plate 20. ) Is fixed in contact with the above,

It is possible to easily produce the finish panel without the need for the use of expensive adhesive for bonding the wood and the synthetic resin board 20 to each other.

As an example in which the finish panel according to the present invention is adhered by a general adhesive 300 for surface finishing, as shown in FIG. 4, the wall surface 200 is fixed to the synthetic resin plate 20. The rear portion 12-2 of the veneer end plate 12 is bonded to the surface portion 200-1 of the wall surface 200 by the usual adhesive 300, and the synthetic resin plate 20 is finished panel 100. It forms the main body as a center layer of the wall and is fixed to the wall surface 200 as a component of the finish panel.

In addition, in addition to the wall surface 200, the finish panel according to the present invention can be bonded to the ceiling and furniture by the conventional adhesive 300 for surface finish.

Therefore, the present invention is possible to easily manufacture a finish panel made of the hard synthetic resin plate fixed to the veneer end plate in contact with the front portion and the rear portion, respectively, expensive adhesive for bonding wood and hard synthetic resin plate It is possible to easily manufacture without using.

In addition, the present invention, during the construction process, the finishing surface firmly maintains the shape of the nature-friendly wood, and it is possible to easily maintain the proper shape by a hard synthetic resin board, so that the construction is easily stable during the finishing process as a nature-friendly wood It is possible.

Furthermore, the surface of the wall 200, the surface of the ceiling, the furniture by the hard synthetic resin plate 20 that can maintain the smoothness if the surface of the interior of the building wall 200, the surface of the ceiling, the surface of the furniture is uneven In the uneven portion of the surface of the veneer end plate 12, which is in contact with and fixed to the rear portion 20-2 of the hard synthetic resin plate 20, is not concavely bonded and is kept properly smooth. Since the concave portion can be appropriately smoothed and finished, the finishing surface after the finishing treatment can have an appropriate smoothness and can be finished evenly, thereby maintaining the best appearance after finishing.

In addition, when the surface of the interior wall 200 of the building, the surface of the ceiling, the surface of the furniture forms a curved surface, or the corners thereof, the synthetic resin plate 20, which is thermoplastic, has an appropriate shape after its shape change is properly heated and softened in construction. Since it is possible to solidify after making this, it is possible to make a stable finish construction by utilizing the proper shape necessary.

In addition, even after construction, the hard synthetic resin plate 20 has an impact resistance against impact on the finish surface from the outside, which is strong in durability, and causes scratches due to impact on the finish surface from the outside. It is possible to maximize the durability by minimizing the size and minimizing the size of the defect.

The veneer end plate 11 can be easily maximized the utility of the natural wood material by a suitable selection of the natural wood grain.

Durability may be further improved if a conventional coating is made on the front surface of the veneer end plate 11 fixed to the synthetic resin plate 20 by a conventional method such as spray.

According to the present invention, without the use of expensive adhesive for adhesion between the wood and hard synthetic resin boards, as described above, the veneer end plate is made of a hard synthetic resin board easily adhered to each other It is possible to manufacture the finish panel easily and inexpensively,

In the construction process, the finishing surface is firmly maintained in the form of natural wood, and it is possible to easily maintain the proper shape by hard synthetic resin board, so that it is easy and stable in the finishing process as natural wood.

Moreover, the finishing surface after finishing can be appropriately smoothed and evenly finished, so that the aesthetics can be maintained in the best condition.

In addition, when the surface of the interior wall of the building, the surface of the ceiling, the surface of the furniture forms a curved surface or corners, it is easy to construct a stable finish utilizing the proper shape required.

In addition, even after construction, there is impact resistance (耐 衝擊 性) strong durability, it is possible to minimize the occurrence of scratches due to the impact on the finish surface from the outside and to minimize the size of the scratches.

Claims (1)

In the finishing panel which is provided with a veneer end plate made of thinly turned solid wood to enable the surface finish for building and furniture; A hard thermoplastic synthetic resin plate 20 is provided, The veneer end plate 11 is in contact with the front portion 20-1 of the synthetic resin plate 20 so that the adhesive plate 20 can be fixed to the veneer end plate 11. The front part 20-1 is pressurized to a predetermined pressure together with the veneer end plate 11 which is in contact with it, and simultaneously heated to a predetermined temperature so that the front part 20-1 softens and melts in a flowable manner. The softened and fused front face 20-1 is filled with a plurality of small gaps 11s of the veneer end plate 11 as corresponding ridges 20-1a. After it is solidified, the veneer end plate 11 is brought into contact with and fixed to the front portion 20-1 of the synthetic resin plate 20; The rear portion of the synthetic resin plate 20 is formed such that a veneer end plate 12 is in contact with and fixed to the rear portion 20-2 of the synthetic resin plate 20. 20-2 is pressurized to a predetermined pressure together with the veneer end plate 12 which is in contact with it, and simultaneously heated to a predetermined temperature so that the rear portion 20-2 is softened and melted so as to flow. And the softened and molten back surface 20-2 is filled with a plurality of small gaps 12s of the veneer end plate 12 as corresponding ridges 20-2a and then solidified. ), The veneer end plate (12) is in contact with the back portion (20-2) of the synthetic resin plate (20), characterized in that the panel (panel) is made to be fixed.