KR20040006446A - Method for manufacture of articial stone plate - Google Patents
Method for manufacture of articial stone plate Download PDFInfo
- Publication number
- KR20040006446A KR20040006446A KR1020020040734A KR20020040734A KR20040006446A KR 20040006446 A KR20040006446 A KR 20040006446A KR 1020020040734 A KR1020020040734 A KR 1020020040734A KR 20020040734 A KR20020040734 A KR 20020040734A KR 20040006446 A KR20040006446 A KR 20040006446A
- Authority
- KR
- South Korea
- Prior art keywords
- stone plate
- artificial stone
- molding
- building
- concave
- Prior art date
Abstract
본 발명은 앵커와 같은 별도의 고정부재 없이 건축물의 외벽에 보다 신속·편리하게 시공할 수 있도록 하고, 또 시공 후에 외벽으로부터의 탈영이 방지되면서 장식효과가 극대화되는 인조석 판재에 관한 것이다.The present invention relates to an artificial stone plate that can be installed on the outer wall of the building more quickly and conveniently without a separate fixing member such as an anchor, and also maximizes the decorative effect while preventing desertion from the outer wall after construction.
개시한 본 발명은 시멘트, 황사, 화산석 등의 무기재료의 골재와 물을 혼합한 반죽재료를 소정형상의 몰드에 충진·경화시켜 제조하는 단위면적의 인조석 판재에 있어서: 반죽재료를 경화하기 전에 그 반죽재료의 일측 표면을, 시공 때 시멘트 몰탈이 충진될 수 있도록 요철형태로 형성하여 경화시키며 상기 요철형태는 단위면적에 대해 폭방향으로 배열·형성되는 톱니형 또는 구형파 중에서 선택된 것을 특징으로 한다.Disclosed is a unit area artificial stone plate manufactured by filling and curing a dough material mixed with an aggregate of inorganic material such as cement, yellow sand, volcanic stone and water in a mold of a predetermined shape: before hardening the dough material. The surface of one side of the kneading material is formed into a concave-convex shape so that cement mortar can be filled during construction, and the concave-convex shape is selected from sawtooth or square waves arranged and formed in a width direction with respect to the unit area.
이에 따라 인조석 판재의 시공 시에 별도의 앵커와 같은 고정부재를 설치하지 않음으로써 작업공수가 줄어들면서 건축물에 신속·편리하게 시공할 수 있고, 또한 톱니형 또는 구형파의 요철부가 건축물의 외벽에 도포된 몰탈에 견고하게 고정되어 있음으로 탈영이 방지됨은 물론 건축물 외장재에 대해 천연석과 같은 외적심미감을 얻을 수 있는 이점이 있다.Accordingly, by installing a fixing member such as a separate anchor when constructing an artificial stone plate, the construction labor can be reduced quickly and conveniently, and the jagged or square wave irregularities are applied to the exterior wall of the building. Since it is firmly fixed to mortar, it is possible to prevent desertion and to obtain an external aesthetic feeling such as natural stone for building exterior materials.
Description
본 발명은 건축물의 외벽 보호와 장식을 목적으로 설치되는 건축물 내, 외장용 인조석 판재에 관한 것으로, 더욱 상세하게는 건축물 내,외장재로서, 자연석 형태의 성형몰드에 충진되어 그 이면에는 여러 다양한 형태의 자연무늬가 표출되고 배면에는 요철부가 형성된 인조석 판재를 성형하여 시공 시에 작업공수를 줄이면서 별도의 고정부재 없이 건축물의 내, 외벽에 보다 신속·편리하게 시공할 수 있도록 하고, 또 시공 후에 외벽으로부터의 탈영을 방지하면서 장식효과의 극대화를 양립하도록 하는 인조석 판재 및 그 제조방법에 관한 것이다.The present invention relates to an artificial stone plate for building and exterior, which is installed for the purpose of protecting and decorating the outer wall of a building, and more specifically, as a building material, as an exterior material, filled in a molding mold in the form of natural stone, The pattern is exposed and the back side is formed of artificial stone plate with irregularities to reduce the labor during construction, so that it can be installed on the inner and outer walls of the building more quickly and conveniently without additional fixing members. The present invention relates to an artificial stone plate and a method of manufacturing the same to prevent desertion while maximizing decorative effects.
일반적으로 패널형태의 건축물 내, 외장재는 일정한 면적을 갖는 목재 판재와 석재 판재로 대별되며, 상기 석재 판재는 다시 자연석 판재와 인조석 판재로 구분된다.In general, in the panel-type building, the exterior material is roughly divided into a wood plate and a stone plate having a predetermined area, and the stone plate is further divided into natural stone plate and artificial stone plate.
상기의 목재 판재 또는 석재 판재는 통상적으로 일정한 규격의 정사각형 또는 직사각형의 단위판재로 성형되어진 후 이들을 건물의 내벽 또는 외벽에 대해 가로 및 세로로 조립하여 시공하고 있다.The wood plate or stone plate is typically molded into a square or rectangular unit plate of a certain standard, and then assembled by horizontally and vertically with respect to the inner wall or outer wall of the building.
상기한 바와 같은 건축물 내, 외장재의 판재를 건축물의 내, 외벽에 대해 가로 및 세로로 시공할 때 목재 판재의 경우에는 하나의 판재 측면에 상호 대향하게 돌기와 홈을 각각 형성하여 돌기부분을 건물 외벽에 고정되는 못과 같은 고정부재 등으로 고정한 후 판재의 홈에 다른 판재의 돌기를 끼워 조립하여 그 결합상태가 수평이 되도록 한 것이다.When the boards of the building materials and exterior materials are constructed horizontally and vertically with respect to the interior and exterior walls of the building, in the case of wood boards, the projections are formed on the outer wall of the building by forming projections and grooves on the side of a single plate. After fixing with a fixing member such as a nail to be fixed, and then assembling the projections of the other plate into the groove of the plate to assemble the horizontal state.
그리고 석재 판재를 건축물의 외벽에 시설할 때의 한 예로서, 상기한 목재 판재와 같이 결합용 돌기와 홈을 형성하지 않고 건축물 외벽과 석재 판재의 배면에 각각 시멘트 몰탈을 발라 부착함과 아울러 석재 판재들과의 사이에 일정간격의 메지를 형성한 후 상기 메지에 접착제 또는 시멘트 몰탈 등을 충진하여 마감처리하고 있는 실정이다.And as an example of installing the stone plate on the outer wall of the building, as in the above-mentioned wood plate, without forming the joining protrusions and grooves, cement mortar is applied to the outer wall of the building and the back of the stone plate, respectively, and the stone plates After forming a message with a certain interval between the and is filled with an adhesive or cement mortar and the like to finish the treatment.
또한, 다른 한 예로서, 건축물의 외벽과 석재 판재의 배면에 각각 시멘트 몰탈을 고르게 도포한 후 상기 석재 판재의 부착면에 복수개의 앵커와 같은 고정부재를 결합한 상태로 석재 판재를 시멘트 몰탈의 표면에 부착하는 것이다.In another example, the cement mortar is evenly applied to the outer wall of the building and the rear surface of the stone plate, and then the stone plate is bonded to the surface of the cement mortar in a state in which fixing members such as a plurality of anchors are coupled to the attachment surface of the stone plate. To attach.
이와 같이하면, 석재 판재의 부착면에 별도의 앵커를 부착한 상태로서 석재 판재를 시멘트 몰탈의 표면에 부착하면 부착면에 결합된 고정부재로서의 앵커가 양 시멘트 몰탈에 매입된 상태로 그 시멘트 몰탈이 굳어지게 되므로 건축물에 부착되는 석재판재의 결합력이 향상되는 것이다.In this way, when the stone plate is attached to the surface of the cement mortar by attaching a separate anchor to the attachment surface of the stone plate, the cement mortar is buried in both cement mortars while the anchor as a fixing member coupled to the attachment surface is embedded in both cement mortars. As it is hardened, the bonding strength of the stone board attached to the building is improved.
그러나, 전자의 석재 판재의 경우에 있어서는 단위 판재의 비중이 무거울 뿐만 아니라 배면이 평탄하여 그 자중 또는 경미한 외력에 의해서 석재 판재가 탈영되거나 또는 작업자의 부주의 또는 동절기에 얼었던 시멘트 몰탈이 하절기에 해빙되면서 건물 외벽과 시멘트 몰탈 사이가 벌어져 결국, 석재 판재가 건축물 외벽에 대해 탈영되어 안전사고를 유발하는 문제점이 있다.However, in the case of the former stone plate, not only the specific gravity of the unit plate is heavy, but also the back surface is flat, so that the stone plate is deserted by its own weight or slight external force or the cement mortar frozen in the carelessness or winter of the worker is thawed in the summer. There is a problem that the gap between the building exterior wall and the cement mortar, the stone plate is deserted on the exterior wall of the building causing a safety accident.
그리고 후자의 석재 판재의 경우에 있어서는 석재 판재의 부착면에 별도의 앵커와 같은 고정부재를 결합한 상태로 건물의 외벽에 석재 판재를 부착해야 하기 때문에, 별도의 앵커를 사용함에 따라 재료비가 상승함은 물론 여러 번의 작업을 순차적으로 수행해야만 하는 등 작업율이 저하되는 문제점 등으로 지적되고 있다.And in the case of the latter stone plate, since the stone plate should be attached to the exterior wall of the building with the fixing member such as a separate anchor attached to the attachment surface of the stone plate, the material cost increases according to the use of a separate anchor. Of course, it is pointed out that the work rate is lowered, such as having to perform several tasks sequentially.
한편, 상기 석재 판재의 경우에도 목재 판재의 경우와 같이 판재의 측면에 결합용 돌기와 홈을 형성하여 상호 조립하는 것을 고려할 수도 있으나, 자연석 판재의 경우에는 원석을 절단 및 연마할 때 절단 등의 방법으로 결합용 돌기와 홈을 형성하여야 하고, 인조석 판재의 경우에는 시멘트에 장식용 골재 등을 혼합하여 성형틀에서 성형하고 양생한 후 그 측면에 결합용 돌기와 홈을 절단기 또는 연마기 등을 사용하여 형성해야 함으로서 그 가격이 비싸지고 결합용 돌기와 홈을 형성할 때 판재가 파손됨으로서 생산성이 낮게 되며 결합 후 내충격성이 취약한 문제점이 있다.Meanwhile, in the case of the stone plate, as in the case of the wood plate, it may be considered to form a coupling protrusion and a groove on the side of the plate to mutually assemble, but in the case of natural stone plate by cutting or grinding the raw stone The joining protrusions and grooves should be formed.In the case of artificial stone plate, the aggregate should be mixed with cement for molding in molding mold and cured, and then the joining protrusions and grooves should be formed on the side by using cutter or grinder. This is expensive and the productivity is low because the plate is broken when forming the coupling protrusion and the groove, there is a problem that the impact resistance after bonding is weak.
따라서, 최근에는 인조석 판재의 시공 시에 별도의 고정부재를 이용하지 않고 건축물 외벽에 간단히 부착시킬 수 있는 인조석 판재가 안출되어 제품화되고 있으며, 예를 들어 본인이 선출하여 등록된 실용신안등록 제246499호(명칭: 앵커를 갖는 인조석판)에 의하면, 백시멘트, 황사, 화산석 등을 물과 혼합하여 형성한 반죽재를 얻고, 상기 반죽재료를 소정규격의 몰드에 충진·경화시켜 소정형태로 성형하는 인조석판에 있어서, 상기 반죽재료의 경화전에 여러 형태로 제작된 앵커를 몰딩 고정시켜 단일체로 구성한 인조석판을 제공하고 있다.Therefore, recently, artificial stone plate that can be easily attached to the exterior wall of a building without using a separate fixing member at the time of construction of artificial stone plate has been devised and commercialized. For example, Utility Model Registration No. 246499 registered and selected by the person himself. According to (name: artificial stone plate having an anchor), a synthetic material obtained by mixing back cement, yellow sand, volcanic stone and the like with water is obtained, and the dough material is filled into a mold of a predetermined standard and cured to form a predetermined shape. In the slab, an artificial stone plate composed of a single piece is provided by molding and fixing anchors manufactured in various forms before curing of the dough material.
그러나, 상기의 앵커를 갖는 인조석판을 건축물 외벽에 시공 시에 수작업 공수를 줄이면서 시공 시간을 단축할 수는 있으나, 상기 인조석판의 제조 때 여러 형태로 제작된 다수의 앵커를 반죽재료에 일정 간격 및 깊이로 매입시켜야 하는 불편함이 있고, 이로 인하여 생산성이 저하되는 문제점이 있다.However, the construction time can be shortened while reducing the man-hours during the construction of the artificial stone plate having the anchor on the outer wall of the building, a number of anchors made in various forms when the artificial stone plate is manufactured at a predetermined interval And there is a inconvenience to be buried in depth, thereby there is a problem that the productivity is lowered.
따라서, 상기와 같은 문제점을 치유하면서도 비용 면에서는 보다 저가의 건축물 내, 외장용 인조석 판재를, 그리고 신뢰성 면에서는 시공 시에 작업공수를 줄이면서 외벽으로부터의 탈영이 방지되는 건축물 내,외장용 인조석 판재를 제공하는 것이 바람직하다.Therefore, while recovering from the above problems, inexpensive interior and exterior artificial stone plate in terms of cost, and reliability in terms of construction, while reducing the man-hours during construction, it provides an interior and exterior artificial stone plate that prevents desertion from the outer wall. It is desirable to.
따라서, 본 발명의 목적은 인조석 판재의 시공 시에 작업공수를 줄이면서 건축물의 외벽에 보다 신속·편리하게 시공할 수 있는 인조석 판재를 제공하는 하는 것이며, 이 인조석 판재는 시멘트 몰탈이 충진되도록 요철부를 폭방향으로 배열·형성한 것으로 완성하여, 시공 시에 상기 요철부에 충진된 시멘트 몰탈과 건축물 외벽의 시멘트 몰탈이 상호 결합된 상태로 고형되어짐으로써, 달성된다.Accordingly, an object of the present invention is to provide an artificial stone plate that can be installed on the outer wall of the building more quickly and conveniently while reducing the number of work during construction of the artificial stone plate, the artificial stone plate is a concave-convex portion so that the cement mortar is filled Completed by arranging and forming in the width direction, it is achieved by solidifying the cement mortar filled in the concave-convex portion during construction and the cement mortar of the outer wall of the building.
본 발명의 다른 목적은 해빙 및 화재에 관계없이 건축물의 외벽에 대해 탈영이 방지되는 인조석 판재를 제공하는 것이며, 이 인조석 판재는 외부의 충격이나 진동 및 해빙 시에 인조석 판재의 배면에 형성된 요철부가 건축물의 외벽에 대해 인조석 판재와의 결합 강도를 견고하게 유지해 줌으로써, 달성된다.It is another object of the present invention to provide an artificial stone plate which is prevented from deserting the outer wall of a building regardless of sea ice and fire, and the artificial stone plate has an uneven portion formed on the back of the artificial stone plate during external impact, vibration and thawing. This is achieved by maintaining a firm bond strength with the artificial stone plate against the outer wall of the.
본 발명의 또다른 목적은 건축물 외장재에 대해 천연석과 같은 외적 심미감이 표출되는 인조석 판재의 제조방법을 제공하는 것이며, 이 인조석 판재의 제조방법은 자연석형태의 몰드 성형면에 무기재료의 골재와 물을 혼합한 반죽재료를 충진한 다음 그 충진된 반죽재료 위에 요철부가 형성된 성형부재를 가압과 진동을 통해 매입·이탈시켜 성형함으로써 달성된다.It is still another object of the present invention to provide a method of manufacturing artificial stone plates in which external aesthetics such as natural stones are expressed with respect to building exterior materials, and the method of manufacturing artificial stone plates includes aggregate and water of inorganic material on a molded molding surface in the form of natural stone. It is achieved by filling the dough material mixed with and then molding and forming a molded member formed with irregularities on the filled dough material through pressure and vibration.
본 발명의 또다른 목적들은 다음의 상세한 설명과 첨부된 도면으로부터 보다 명확해질 것이다.Other objects of the present invention will become more apparent from the following detailed description and the accompanying drawings.
도 1 내지 도 6은 본 발명에 따른 인조석 판재의 설명에 제공되는 실시 예를 나타내는 구성도로서,1 to 6 is a configuration diagram showing an embodiment provided for the description of the artificial stone plate according to the present invention,
도 1은 상기 인조석 판재를 성형하기 위한 판상의 성형부재를 나타내어 보인 사시도이고,1 is a perspective view showing a plate-shaped forming member for molding the artificial stone plate,
도 2는 상기 인조석 판재를 제조하기 위해 도 1의 성형부재와 반죽재료가 충진된 성형몰드를 나타내어 보인 분해 단면도이고,Figure 2 is an exploded cross-sectional view showing a molding mold filled with the molding member and the dough material of Figure 1 to manufacture the artificial stone plate,
도 3은 도 2의 성형몰드의 반죽재료에 상기 성형부재를 올려놓은 상태에서 가압·진동으로 상기 성형부재의 일부를 매입시키는 과정을 보인 단면도이고,3 is a cross-sectional view showing a process of embedding a part of the molding member by pressing and vibration in a state where the molding member is placed on the dough material of the molding mold of FIG.
도 4는 도 3의 성형부재가 매입된 성형몰드를 열풍건조실에서 경화시킨 후에 성형부재를 성형몰드로부터 탈영시킨 상태를 나타내어 보인 단면도이고,4 is a cross-sectional view illustrating a state in which the molding member is deserted from the molding mold after the molding mold in which the molding member of FIG. 3 is embedded is cured in a hot air drying chamber.
도 5는 도 4의 성형몰드로부터 탈영되어 제조·완성된 인조석 판재를 나타내어 보인 단면도이고,FIG. 5 is a cross-sectional view illustrating an artificial stone plate manufactured and completed by desertifying from the molding mold of FIG. 4. FIG.
도 6는 도 5의 배면에 톱니형의 걸림부가 형성된 인조석 판재를 건축물의 외벽에 시공한 상태를 나타내어 보인 단면도이다.FIG. 6 is a cross-sectional view illustrating a state in which an artificial stone plate having a sawtooth engaging portion formed on a rear surface of FIG. 5 is constructed on an outer wall of a building; FIG.
<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>
100 : 성형부재 102 : 요철부100: forming member 102: uneven portion
110 : 인조석 판재 112 : 반죽재료110: artificial stone plate 112: dough material
114 : 톱니형의 요철부 120 : 성형 몰드114: serrated uneven portion 120: molding mold
130 : 가압·진동수단 140 : 시멘트 몰탈130 pressurization and vibration means 140 cement mortar
상기와 같은 목적들을 달성하기 위한 본 발명에 의한 인조석 판재의 제조방법에 의하면, 자연석 형태로 된 성형 몰드의 성형면에 무기재료의 골재와 물을 혼합한 반죽재료를 충진한 후에 열풍건조실에서 경화시켜 성형하는 인조석 판재의 제조방법에 있어서: 상기 반죽재료의 경화 전에, 단위면적을 가지며 일측 면에는 요철부가 폭방향으로 배열·형성되어진 성형부재를 상기 성형몰드의 성형면에 충진된 반죽재료의 표면에 매입하여 경화시키며 상기 경화된 반죽재료로부터 상기 성형부재와 상기 성형몰드를 탈영시켜 상기 반죽재료의 표면에 상기 성형부재의 요철부와 대칭되는 요철부가 형성되어져 성형되는 것을 특징으로 한다.According to the manufacturing method of the artificial stone plate according to the present invention for achieving the above objects, the filling surface of the molding mold of the natural stone form filled with the dough material mixed with the aggregate of the inorganic material and water and then cured in a hot air drying room In the manufacturing method of the artificial stone plate to be molded: Before the hardening of the dough material, a molding member having a unit area and one side surface is formed and arranged in the width direction on the surface of the dough material filled in the molding surface of the molding mold It is embedded and cured, and the molding member and the molding mold is deserted from the cured dough material, characterized in that the surface of the dough material is formed by forming an uneven portion symmetrical with the uneven portion of the molding member.
바람직하기로, 상기 매입과정에서 상기 반죽재료와 성형부재의 요철부와의 충진밀도를 높이기 위해 상기 성형부재를 가압·진동으로 매입시키는 것을 특징으로 한다.Preferably, in order to increase the filling density of the kneading material and the concave-convex portion of the molding member in the embedding process, the molding member is characterized in that it is embedded by pressing and vibration.
본 발명에 의한 인조석 판재에 의하면, 무기재료의 골재와 물을 혼합한 반죽재료를 소정규격의 성형 몰드에 충진·경화시켜 소정형태로 성형하는 단위면적의인조석 판재에 있어서:According to the artificial stone plate according to the present invention, in the artificial stone plate of the unit area in which the kneading material mixed with the aggregate of the inorganic material and water is filled into a mold of a predetermined standard and cured to be molded into a predetermined shape:
상기 반죽재료를 경화하기 전에 그 반죽재료의 일측 표면을, 시공 때 시멘트 몰탈이 충진될 수 있도록 요철형태로 형성하여 경화시키며 상기 요철형태는 단위면적에 대해 폭방향으로 배열·형성된 것을 특징으로 한다.Before hardening the dough material, the surface of one side of the dough material is formed into a concave-convex shape so that cement mortar can be filled during construction, and the concave-convex shape is arranged and formed in the width direction with respect to the unit area.
선택적으로, 상기 요철형태가 상기 인조석 판재의 길이방향에 대해 양 단부로부터 일정 거리를 남겨두고 형성되어진 것을 특징으로 한다.Optionally, the uneven shape is formed leaving a certain distance from both ends with respect to the longitudinal direction of the artificial stone plate.
선택적으로, 상기 요철형태는 일측 방향으로 기울어진 톱니형태로 형성된 것을 특징으로 한다.Optionally, the concave-convex shape is formed in a sawtooth shape inclined in one direction.
선택적으로, 상기 요철형태는 구형파 형태로 형성된 것을 특징으로 한다.Optionally, the irregular shape is characterized in that formed in the form of a square wave.
이와 같이, 인조석 판재의 배면에 요철부를, 그리고 이면에는 다양한 형태의 자연무늬를 표출시켜 성형함으로써, 인조석 판재의 시공 시에 요철부에 시멘트 몰탈을 충진한 후 건축물 외벽에 도포된 시멘트 몰탈 위에 인조석 판재를 밀착하는 것에 의해 두 시멘트 몰탈이 상호 결합된 상태로 고형되어지게 됨을 알 수 있다.In this way, by forming the uneven portion on the back surface of the artificial stone plate, and by forming a variety of natural patterns on the back surface, after filling the cement mortar in the uneven portion during the construction of the artificial stone plate, the artificial stone plate on the cement mortar coated on the building exterior wall It can be seen that by contacting the two cement mortar is solidified in a mutually bonded state.
그 결과, 인조석 판재의 시공 시에 별도의 앵커와 같은 고정부재를 설치하지 않음으로써 작업공수가 줄어들면서 건축물의 외벽에 보다 신속·편리하게 시공할 수 있고, 또한 외부의 충격, 진동 및 해빙 시에 요철부가 건축물의 외벽에 도포된 시멘트 몰탈에 대해 강도를 보다 견고하게 유지하고 있음으로써, 탈영의 방지는 물론 건축물 외장재에 대해 천연석과 같은 외적 심미감을 얻을 수 있는 이점이 있는 것이다.As a result, it is possible to install more quickly and conveniently on the outer wall of the building by reducing the labor time by not installing a fixing member such as a separate anchor when constructing the artificial stone plate, and also during external impact, vibration and thawing. As the uneven portion maintains the strength more firmly against the cement mortar applied to the outer wall of the building, there is an advantage that can prevent the desertion and obtain an external aesthetic like natural stone for the building exterior material.
그리고, 본 발명의 실시 예로는 다수개가 존재할 수 있으며, 이하에서는 가장 바람직한 실시 예에 대하여 상세히 설명하고자 한다.And, there may be a plurality of embodiments of the present invention, the following will be described in detail for the most preferred embodiment.
이 바람직한 실시 예를 통해 본 발명의 목적, 기타의 목적, 특징 및 이점은 예시할 목적으로 도시한 첨부 도면과 관련해서 본 발명에 의한 실시 예를 가지고 이하의 설명으로부터 보다 명백해질 것이다.Through this preferred embodiment, the objects, other objects, features and advantages of the present invention will become more apparent from the following description with an embodiment according to the present invention in connection with the accompanying drawings shown for illustrative purposes.
이하, 첨부한 도면을 참조하여 본 발명에 따른 인조석 판재의 바람직한 실시 예를 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the artificial stone plate according to the present invention with reference to the accompanying drawings will be described in detail.
도 1은 본 발명에 따른 인조석 판재를 성형하기 위한 판상의 성형부재를 나타내어 보인 사시도이고, 도 2는 상기 인조석 판재를 제조하기 위해 도 1의 성형부재와 반죽재료가 충진된 성형몰드를 나타내어 보인 분해 단면도이며, 도 3은 도 2의 성형몰드의 반죽재료에 상기 성형부재를 올려놓은 상태에서 가압·진동으로 상기 성형부재의 일부를 매입시키는 과정을 보인 단면도이고, 도 4는 도 3의 성형부재가 매입된 성형몰드를 열풍건조실에서 경화시킨 후에 성형부재를 성형몰드로부터 탈영시킨 상태를 나타내어 보인 단면도이다.1 is a perspective view showing a plate-shaped molding member for molding the artificial stone plate according to the present invention, Figure 2 is a decomposition showing the molding mold filled with the molding member and the dough material of Figure 1 to manufacture the artificial stone plate 3 is a cross-sectional view illustrating a process of embedding a part of the molding member by pressing and vibration in a state where the molding member is placed on the dough material of the molding mold of FIG. 2, and FIG. A cross-sectional view showing a state in which the molded member is deserted from the molding mold after the embedded molding mold is cured in a hot air drying chamber.
본 실시 예에 따른 인조석 판재(110)를 성형하기 위해 도 1은 같은 단위면적의 성형부재(100)를 필요로 한다. 그리고 단위면적의 성형부재(100)는 경화된 인조석 판재(100)로부터 이탈이 보다 쉽게 이루어지도록, 예컨대 고무 또는 실리콘 재질로 이루어진 것으로서, 그 일측 면에는 도 1 및 도 2에 나타내는 바와 같이, 톱니형상의 요철부(102)가 단위면적에 대해 폭방향으로 배열·형성되어 있다. 그리고 톱니형의 요철부(102)는 이후에 설명될 시멘트 몰탈이 충진되어 건축물의 벽에 대해 탈영이 없도록 일측 방향으로 일정한 각을 가지고 기울어져 형성되어 있다. 다른 실시 예로서, 전술한 요철부(102)를 톱니형인 아닌 구형파 형태 또는 그외의 사인파(sine wave) 형태로 형성해주는 방안도 실시 가능하다. 상기 구형파 또는 톱니형의 요철부(102)는 도 1과 같이, 인조석 판재(110)의 길이방향에 대해 양 단부로부터 일정 거리를 남겨두고 형성되어져 있으며, 인조석 판재(110)의 제조 시에 그 인조석 판재를 형성하는 반죽재료(112)의 배면에 매입되어 그와 같은 대칭형상을 갖는 구형파 또는 톱니형의 요철부를 형성하는 역할을 한다.In order to mold the artificial stone plate 110 according to the present embodiment, Figure 1 requires a molding member 100 of the same unit area. In addition, the molding member 100 of the unit area is made of, for example, a rubber or silicone material so as to be more easily separated from the hardened artificial stone plate 100, and one side thereof has a sawtooth shape as shown in FIGS. 1 and 2. Irregularities 102 are arranged and formed in the width direction with respect to the unit area. And the serrated uneven portion 102 is filled with cement mortar to be described later is formed to be inclined at a certain angle in one direction so that there is no desertion with respect to the wall of the building. As another example, the above-described concave-convex portion 102 may be embodied in the form of a square wave or other sine wave instead of sawtooth. The square wave or serrated uneven portion 102 is formed with a certain distance from both ends with respect to the longitudinal direction of the artificial stone plate 110, as shown in Figure 1, the artificial stone during the production of the artificial plate 110 It is embedded in the back surface of the dough material 112 forming the plate material and serves to form a square wave or sawtooth uneven portion having such a symmetrical shape.
이와 같이 톱니형 또는 구형파의 요철부(102)가 형성된 성형부재(100)를 반죽재료(112)의 배면에 매입하여 경화시키 위해서는 먼저 무기재료의 골재인 시멘트 28 내지 32%, 황사 35 내지 39%, 화산석 입자 26 내지 30%에 유기재료인 염화칼슘, 경화제, 안료등을 혼합한 후에 그 혼합된 재료에 물을 투입하고 교반하여 반죽상태의 재료를 준비한다.Thus, in order to cure the molded member 100 having the sawtooth or square wave uneven portion 102 formed on the back surface of the kneading material 112, first, the aggregate of inorganic material is 28 to 32% and 35 to 39% of yellow sand. After mixing 26-30% of the volcanic stone particles with organic materials such as calcium chloride, hardener and pigment, water is added to the mixed material and stirred to prepare a dough material.
이후 바닥면이 자연석 형태로 형성된 도 2 내지 도 4와 같은 성형 몰드(120)를 준비하고, 또한 수용성의 접착액 규산소다와 물을 중량비로서 1:8 내지 15 정도로 혼합하여 접착수용액을 제조한 후 이를 성형 몰드(120)의 성형면에 적당량을 분사하여 도포한다.Thereafter, a molding mold 120 as shown in FIGS. 2 to 4 having a bottom surface formed in a natural stone form is prepared, and a water-soluble adhesive liquid silicate and water are mixed at a weight ratio of about 1: 8 to 15 to prepare an adhesive aqueous solution. This is applied by spraying a suitable amount on the molding surface of the molding mold (120).
그리고 상기 접착수용액이 도포된 상태에서 투명질의 운모조각을 상기 접착수용액의 표면에 골고루 뿌려 부착되도록 한다. 여기서 운모조각은 아주 가벼운 비늘 같은 것이므로 접착수용액을 도포하지 않으면 반죽재료(112)로 침투하거나 바람에 날려 자체가 없어질 염려가 있으므로 접착수용액을 도포한 후에 운모조각을 뿌려 부착하는 것이다. 운모조각을 뿌려 부착한 다음 중량비로써 흑색안료 25%와 물75%를 희석하거나 또는 흑색안료 30%와 물 70%를 희석하여 된 표면처리액을 상기 운모조각이 뿌려진 접착수용액 위로 분사하여 적층 도포함으로써, 0.5mm 내지 3mm의 반점이 성형 몰드(120)의 성형면에 골고루 분포하게 된다.In addition, the mica flakes of the transparent material are evenly sprayed onto the surface of the adhesive solution in the state where the adhesive solution is applied. Here, the mica pieces are very light scales, so if the adhesive solution is not applied, the mica pieces may penetrate into the dough material 112 or be blown in the wind and disappear. After spraying mica flakes, the surface treatment solution diluted by 25% black pigment and 75% water by weight ratio or diluted 30% black pigment and 70% water is sprayed onto the mica-sprayed adhesive solution and laminated. , 0.5mm to 3mm spot is evenly distributed on the molding surface of the molding mold 120.
상기 도포과정에서, 운모조각 및 흑색안료가 뿌려지는 양은 자연상태의 화강암 표면에 부착된 운모 및 반점의 양을 감안하여 조절한다.In the application process, the amount of mica fragments and black pigments to be sprayed is adjusted in consideration of the amount of mica and spots attached to the natural granite surface.
계속해서, 상기 표면처리액을 적층 도포 후에 일정시간, 예컨대 3분 안에 상기 준비된 반죽재료(112)를 성형 몰드(120)에 충진하면서 진동수단으로 성형 몰드(120)를 진동시키면 반죽재료(112)의 충진밀도가 향상됨과 아울러 상기 흑색안료의 반점이 반죽재료와 희석되면서 0.5mm 내지 3mm의 반점이 자연 화강석 모양으로 확장 번지면서 일치를 이루게 된다.Subsequently, when the molding mold 120 is vibrated by the vibrating means while filling the molding mold 120 with the prepared dough material 112 within a predetermined time, for example, 3 minutes after laminating the surface treatment solution, the dough material 112 is applied. As the filling density of the black pigment is improved and the spots of the black pigment are diluted with the dough material, the spots of 0.5 mm to 3 mm are expanded and spread into the shape of natural granite, thereby achieving agreement.
이때, 성형 몰드(120)를 진동시키는 과정에서 도 2에 나타내는 바와 같이, 단위면적을 갖는 성형부재(100)의 톱니형 또는 구형파 형태의 요철부(102)가 밑으로 향하도록 그 성형부재(110)를 반죽재료(10)의 위에 올려놓은 다음 도 3과 같이 가압 및 진동수단(130)을 통해 가압과 진동을 동시 수행해 줌으로써, 그 성형부재(100)의 요철부(102)가 반죽재료(112)에 매입되어지고, 또한 진동에 의해서 반죽재료(112)가 성형부재(100)의 요철부(102)로 고루 스며들어 성형부재(100)의 요철부(102)와 반죽재료(112)와의 충진밀도가 견고해지게 된다.At this time, as shown in FIG. 2 in the process of vibrating the molding mold 120, the molding member 110 so that the serrated or square wave-shaped uneven portion 102 of the molding member 100 having a unit area is directed downward. ) Is placed on top of the dough material 10 and then simultaneously pressurized and vibrated through the pressurizing and vibrating means 130 as shown in FIG. 3, so that the uneven part 102 of the molding member 100 is kneaded material 112. ), And the kneading material 112 is evenly soaked into the uneven portion 102 of the forming member 100 by vibrating to fill the uneven portion 102 of the forming member 100 with the kneading material 112. Density will be firm.
이후 성형부재(100)의 요철부(102)가 반죽재료(112)에 매입 완료되었을 경우 그 반죽재료가 충진된 성형 몰드(120)를 열풍건조실에서 충분하게 건조한 후에 도 4와 같이, 성형부재(100)를 경화된 반죽재료(112)로부터 탈영시키면 그 경화된 반죽재료(112)의 배면에는 성형부재(100)의 요철부(102)와 동일한 형상을 갖는 톱니형 또는 구형파 또는 사인파의 요철부(114)가 대향하게 형성. 즉 톱니형 또는 구형파 또는 사인파의 요철부(114)가 인조석 판재(110)의 길이방향에 대해 양 단부로부터 일정 거리를 남겨두고 형성되어진다.After the concave-convex portion 102 of the molding member 100 is completed to be filled in the dough material 112, the molding mold filled with the dough material 120 is sufficiently dried in a hot air drying chamber, as shown in FIG. When the 100 is removed from the hardened dough material 112, the back surface of the hardened dough material 112 has a sawtooth or square wave or sinusoidal uneven portion having the same shape as the uneven portion 102 of the molding member 100 ( 114) formed oppositely. That is, the uneven portion 114 of the sawtooth or square wave or sinusoidal wave is formed leaving a certain distance from both ends with respect to the longitudinal direction of the artificial stone plate 110.
이어서 성형 몰드(120)를 탈영함으로써, 반죽재료(112)의 이면에는 검정색이 표출되거나 시간이 경과에 의해 20% 내지 30%의 검정색이 탈색되면서 도 5와 같은 톱니형의 요철부(114)를 갖는 천연 화강석과 같은 인조석 판재(110)가 완성되는 것이다.Subsequently, by desertifying the molding mold 120, black is expressed on the back surface of the dough material 112 or 20% to 30% of the black color is decolored with time, so that the tooth-shaped uneven portion 114 as shown in FIG. Artificial stone plate 110, such as having a natural granite is completed.
상기의 과정을 거쳐 완성된 인조석 판재(110)를 건축물의 외벽에 시공하고자 할 때에는 도 6에 나타내는 바와 같이, 시멘트 몰탈(140)을 시공할 벽면에 고르게 바르고, 또한 인조석 판재(110)의 요철부(114)에 시멘트 몰탈을 고르게 충진한 후에 인조석 판재(110)를 벽면에 압착하여 부착시킨다.When the artificial stone plate 110 completed through the above process is to be installed on the outer wall of the building, as shown in FIG. 6, the cement mortar 140 is evenly applied to the wall surface to be constructed, and the uneven portion of the artificial stone plate 110 is also applied. After the cement mortar is evenly filled in the 114, the artificial plate 110 is pressed onto the wall and adhered thereto.
전술한 바와 같이, 인조석 판재(110)를 건축물 벽면에 도포된 시멘트 몰탈(140) 위로 압착시키면, 건축물의 벽에 도포된 시멘트 몰탈(140)과 인조석 판재(110)의 톱니형 또는 구형파의 요철부(114)에 충진되어 있는 시멘트 몰탈이 상호 결합되고, 이와 같이 두 시멘트 몰탈이 상호 결합된 상태로 고형되어짐으로 진동, 외력에 의해 탈영이 되지 않을 뿐만 아니라 도 6과 같이, 건축물의 벽면에 대해 톱니형의 요철부(114)가 지면쪽으로 기울어져 매입·고형됨으로써 인조석 판재(110)의 자중에 의해 하향으로 흘러내려 이탈되는 일이 없고, 결국에는 인조석 판재(110)가 건축물의 벽면에 보다 강하게 부착되는 것이다.As described above, when the artificial stone plate 110 is pressed onto the cement mortar 140 applied to the wall of the building, the jagged or square wave uneven portion of the cement mortar 140 and the artificial stone plate 110 applied to the wall of the building. Cement mortar filled in the 114 is bonded to each other, and thus the two cement mortar is solidified in a mutually bonded state, so as not to be deserted by vibration and external force, as shown in FIG. As the uneven portion 114 of the die is inclined toward the ground and is embedded and solid, the artificial stone plate 110 does not flow downward due to the weight of the artificial stone plate 110 and is detached, and eventually, the artificial stone plate 110 is more strongly attached to the wall of the building. Will be.
한편, 비교 예로서, 종래의 기술, 즉 다시 말해서 인조석 판재의 배면에 앵커와 같은 여러 형태의 고정부재를 일정간격 및 깊이로 매입함으로써, 생산성의 저하와 더불어 제조공정의 불편함 및 재료비가 상승하는 것과는 달리, 본 발명은 인조석 판재의 배면에 시멘트 몰탈이 충진되도록 요철부가, 그리고 배면에는 다양한 형태의 자연무늬가 표출되어 경화되는 것으로 인조석 판재가 완성되어짐을 알 수 있다.On the other hand, as a comparative example, the conventional technology, that is, by embedding a fixed member of various types such as an anchor on the back surface of the artificial stone plate at a predetermined interval and depth, the productivity and the inconvenience of the manufacturing process and material cost increases Unlike the present invention, it can be seen that the artificial stone plate is completed by hardening by expressing the uneven portion, and various types of natural patterns on the rear surface of the artificial stone plate so that cement mortar is filled.
이 결과에서 본 발명에 의하면, 인조석 판재의 시공 시에 별도의 앵커와 같은 고정부재를 설치하지 않음으로써 작업공수가 줄어들면서 건축물에 신속·편리하게 시공할 수 있고, 또한 톱니형 또는 구형파 형태의 요철부가 건축물의 외벽에 도포된 몰탈에 견고하게 고정되어 있음으로 탈영이 방지됨은 물론 건축물 외장재에 대해 천연석과 같은 외적 심미감을 얻을 수 있는 이점이 있는 것이다.In this result, according to the present invention, by installing a fixing member such as a separate anchor at the time of the construction of artificial stone plate can be quickly and conveniently installed in the building while reducing the number of work, and also sawtooth or square wave shape irregularities Since it is firmly fixed to the mortar applied to the exterior wall of the additional building, it is possible to prevent desertion and to obtain an external aesthetic like natural stone for the building exterior material.
그리고, 상기에서 본 발명의 특정한 실시 예가 설명 및 도시되었지만 본 발명이 당업자에 의해 다양하게 변형되어 실시될 가능성이 있는 것은 자명한 일이다.In addition, although specific embodiments of the present invention have been described and illustrated above, it is obvious that the present invention may be variously modified and implemented by those skilled in the art.
이와 같은 변형된 실시 예들은 본 발명의 기술적 사상이나 전망으로부터 개별적으로 이해되어져서는 안되며, 이와 같은 변형된 실시 예들은 본 발명의 첨부된 특허청구범위 안에 속한다 해야 할 것이다.Such modified embodiments should not be individually understood from the technical spirit or the prospect of the present invention, and such modified embodiments should fall within the appended claims of the present invention.
상술한 설명으로부터 분명한 본 발명의 인조석 판재에 의하면, 인조석 판재의 시공 시에 인조석 판재의 요철부에 충진된 시멘트 몰탈과 건축물의 외벽에 도포된 시멘트 몰탈이 상호 결합되어 고형됨으로써, 별도의 앵커와 같은 고정부재를 필요치 않으며, 이것에 의해 작업공수가 줄어들면서 신속·편리하게 시공할 수 있다.According to the artificial stone plate of the present invention evident from the above description, the cement mortar filled in the uneven portion of the artificial stone plate and the cement mortar applied to the outer wall of the building at the time of construction of the artificial stone plate is solidly bonded to each other, such as a separate anchor There is no need for a fixing member, and as a result, the man-hours can be reduced quickly and conveniently.
또한, 외부의 충격, 진동 및 해빙 시에 요철부가 건축물의 외벽에 도포된 시멘트 몰탈에 대해 강도를 보다 견고하게 유지하고 있음으로써, 탈영의 방지는 물론 건축물 외장재에 대해 천연석과 같은 외적 심미감을 얻을 수가 있는 뛰어난 인조석 판재를 얻을 수 있다.In addition, by maintaining the strength of the cement mortar applied to the exterior wall of the building during the impact, vibration, and thawing of the outside more firmly, it is possible not only to prevent desertion but also to obtain an external aesthetic like natural stone for the building exterior material. You can get an excellent artificial stone plate.
Claims (7)