KR102436073B1 - Eco-friendly flooring for livestock pen and manufacturing method thereof - Google Patents
Eco-friendly flooring for livestock pen and manufacturing method thereof Download PDFInfo
- Publication number
- KR102436073B1 KR102436073B1 KR1020190059742A KR20190059742A KR102436073B1 KR 102436073 B1 KR102436073 B1 KR 102436073B1 KR 1020190059742 A KR1020190059742 A KR 1020190059742A KR 20190059742 A KR20190059742 A KR 20190059742A KR 102436073 B1 KR102436073 B1 KR 102436073B1
- Authority
- KR
- South Korea
- Prior art keywords
- anhydrite
- quicklime
- weight
- eco
- fly ash
- Prior art date
Abstract
본 발명은 친환경 축사 바닥재에 대한 것으로서, 본 발명에 따른 친환경 축사 바닥재는 생석회(CaO), 상기 생석회의 적어도 일부와 반응시켜 급격한 발열반응을 방지하기 위한 수분 함유 첨가물 및 상기 생석회의 수분 흡수 속도를 조절하기 위한 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 포함한다.The present invention relates to an eco-friendly livestock barn flooring, wherein the eco-friendly barn flooring according to the present invention reacts with quicklime (CaO), at least a portion of the quicklime to prevent a rapid exothermic reaction, and controls the water absorption rate of the quicklime For anhydrite (CaSO 4 ) or a mixture containing the anhydrite.
Description
본 발명은 친환경 축사 바닥재에 관한 것으로, 보다 상세하게는 소독 및 수분 흡수를 위한 친환경 축사 바닥재 및 그 제조 방법에 관한 것이다.The present invention relates to an eco-friendly livestock barn flooring, and more particularly, to an eco-friendly livestock barn flooring for disinfection and moisture absorption, and a manufacturing method thereof.
일반적으로 축사의 바닥은 청소의 미비, 급수기의 누수, 산성 소독약의 과다 사용 등으로 인하여 산성화가 되기 쉽다. 축사의 바닥재의 오염이 심각해질 수록 더 많은 약품을 요구하게 되고, 악순환이 계속되어 질병에 대한 저항력이 약해지기 쉽다.In general, the floor of the barn is prone to acidification due to insufficient cleaning, water leakage, excessive use of acid disinfectant, and the like. The more serious the contamination of the floor material of the barn, the more drugs are required, and the vicious cycle continues, which tends to weaken the resistance to disease.
바닥이 청결하지 못하면 각종질병에 취약하고, 악취, 파리 등의 발생이 많아져 축사 내 환경이 불량해짐으로써 결국 생산성에 악영향을 미치게 된다. 특히, 축사 바닥에 수분이 많은 경우 세균이나 바이러스, 원생동물 등이 번식하기 쉽다. 따라서, 축사의 생산성 측면뿐 아니라, 동물복지 차원에서도 축사의 바닥재의 수분을 효과적으로 탈수하는 것이 중요하다. If the floor is not clean, it is vulnerable to various diseases, and the occurrence of odors and flies increases, resulting in a poor environment in the barn, which will adversely affect productivity. In particular, if there is a lot of moisture on the floor of the barn, bacteria, viruses, and protozoa are easy to propagate. Therefore, it is important to effectively dehydrate the moisture of the floor material of the barn not only in terms of productivity of the barn, but also in terms of animal welfare.
예를 들어, 우사의 경우에는 바닥재로 톱밥이나 등겨 등이 주로 사용되고 있으며, 이러한 바닥재에 생석회를 뿌려 소독 및 수분 저감 효과를 기하고 있다.For example, in the case of a barn, sawdust or rice bran is mainly used as a flooring material, and quicklime is sprinkled on such a flooring material to disinfect and reduce moisture.
오래전부터 생석회(CaO)는 소독용으로 쓰여 왔는데, 생석회는 뛰어난 흡수력을 가져 축사의 습도 조절용으로 이용되어 왔다. 특히, 생석회는 강한 알칼리성을 띠는 물질로 오래전부터 살균소독, 지력 회복, 산성의 중화, 지반 강화제의 기능을 하였다.Since a long time ago, quicklime (CaO) has been used for disinfection, but quicklime has excellent absorption and has been used for humidity control in livestock houses. In particular, quicklime is a substance with strong alkalinity and has long been functioning as a sterilization, disinfection, recovery of intellectual strength, neutralization of acidity, and a ground strengthening agent.
또한, 생석회는 비료, 산성토양 개량제, 수분 포집제로서의 건조제, 석회 플라스터(석회 모르타르), 혼합 시멘트 등 토목건축 재료 등의 다양한 분야에 활용되며, 법규상 축사의 바닥은 콘트리트로 처리해야 하기 때문에, 생석회는 콘크리트 등 축사 바닥재의 재료로서 널리 이용되고 있다.In addition, quicklime is used in various fields such as fertilizer, acid soil conditioner, desiccant as a moisture scavenger, lime plaster (lime mortar), and civil construction materials such as mixed cement. Quicklime is widely used as a material for livestock flooring materials such as concrete.
그러나, 생석회는 피부 및 점막을 상하게 하므로 흡입 시 인체에 손상을 가할 수 있고, 생석회는 파우더 형태로 존재하므로 인체상의 호흡기 질환을 유발할 수 있는 문제도 존재한다. 또한, 생석회는 물과 반응하여 급격한 발열반응을 일으키기 때문에, 화상의 위험, 보관상의 위험이 존재하고, 높은 단가 등으로 인하여 경제점 부담을 높일 수 있다는 문제도 존재한다.However, since quicklime injures the skin and mucous membranes, it may damage the human body when inhaled. Since quicklime exists in powder form, there is also a problem that may cause respiratory diseases in the human body. In addition, since quicklime reacts with water to cause a rapid exothermic reaction, there is a risk of burns and a risk of storage, and there is also a problem that an economic burden may be increased due to a high unit price.
또한, 기존의 경우 축사에서 키우는 동물의 종류, 날씨, 온도, 습도 등 여러 환경 요인에 따라 바닥재의 수분 흡수 기간을 조절하고자 하는 니즈가 충족되지 않았다.In addition, in the existing case, the need to control the moisture absorption period of the flooring material according to various environmental factors such as the type of animal raised in the barn, weather, temperature, and humidity was not satisfied.
본 발명은 상술한 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 단가가 높은 고품위 생석회 대신 상대적으로 단가가 낮은 저품위 생석회를 원료로 한 친환경 축사 바닥재 및 그 바닥재를 제조하는 방법을 제공함에 있다.The present invention is to solve the above problems, and an object of the present invention is to provide an eco-friendly livestock flooring material using low-grade quicklime having a relatively low unit price as a raw material instead of high-grade quicklime having a high unit price and a method for manufacturing the same.
또한, 본 발명의 목적은 바닥재의 원료 비율을 조절함으로써 수분 흡수 기간의 연장 또는 조절이 가능한 친환경 축사 바닥재 및 그 바닥재를 제조하는 방법을 제공함에 있다.In addition, an object of the present invention is to provide an eco-friendly livestock flooring material capable of extending or controlling the moisture absorption period by adjusting the raw material ratio of the flooring material and a method of manufacturing the same.
상기와 같은 본 발명의 목적은 생석회(CaO) 및 상기 생석회의 적어도 일부와 반응시켜 급격한 발열반응을 방지하기 위한 수분 함유 첨가물을 포함하는 것을 특징으로 하는 친환경 축사 바닥재에 의해 달성된다.The object of the present invention as described above is achieved by an eco-friendly livestock barn flooring comprising quicklime (CaO) and a water-containing additive for preventing a rapid exothermic reaction by reacting with at least a portion of the quicklime.
여기서, 상기 생석회는 40 중량% 내지 70 중량%, 상기 수분 함유 첨가물은 30 중량% 내지 60 중량%로 이루어질 수 있다.Here, the quicklime may be comprised of 40 wt% to 70 wt%, and the water-containing additive may be comprised of 30 wt% to 60 wt%.
또한, 상기 생석회의 수분 흡수 속도를 조절하기 위한 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 더 포함할 수 있다.In addition, anhydrite (CaSO 4 ) for controlling the moisture absorption rate of the quicklime or a mixture containing the anhydrite may be further included.
한편, 상기 생석회는 10 중량% 내지 20 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 60 중량% 내지 70 중량%로 이루어질 수 있다.On the other hand, the quicklime is 10 wt% to 20 wt%, the water-containing additive is 10 wt% to 20 wt%, the anhydrite (CaSO 4 ) It may be composed of 60 wt% to 70 wt%.
또한, 상기 생석회는 30 중량% 내지 40 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 40 중량% 내지 50 중량%로 이루어질 수 있다.In addition, the quicklime is 30% to 40% by weight, the water-containing additive is 10% to 20% by weight, and the anhydrite (CaSO 4 ) may be composed of 40% to 50% by weight.
나아가, 상기 무수석고(CaSO4)는 제1형 무수석고, 제2형 무수석고 및 제3형 무수석고 중에 수분흡수기간에 따라 선택된 어느 하나로 이루어질 수 있다.Furthermore, the anhydrite (CaSO 4 ) may be made of any one selected from the type 1 anhydrite, type 2 anhydrite, and type 3 anhydrite, depending on the moisture absorption period.
또한, 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물에 유기염이 더 혼합될 수 있다.In addition, an organic salt may be further mixed with the anhydrite (CaSO 4 ) or a mixture containing the anhydrite.
나아가, 상기 무수석고를 포함하는 혼합물은 건식탈황석고 또는 플라이애시로 이루어질 수 있다.Furthermore, the mixture containing the anhydrite may be made of dry desulfurization gypsum or fly ash.
이 경우, 상기 건식탈황석고는, 코크스를 연료로 하여 생석회 성분 함량이 40 중량% 내지 50 중량%이고 무수석고가 40 중량% 내지 50 중량%인 제1형 건식탈황석고 및 유연탄을 연료로 하여 생석회 성분 함량이 10 중량% 내지 20 중량%이고 무수석고의 성분 함량이 10 중량%인 제2형 건식탈황석고 중 어느 하나를 포함할 수 있다.In this case, the dry desulfurization gypsum is a type 1 dry desulfurization gypsum having a quicklime component content of 40% to 50% by weight and anhydrite of 40% to 50% by weight using coke as a fuel and quicklime using bituminous coal as a fuel It may include any one of type 2 dry desulfurization gypsum having a component content of 10 wt% to 20 wt% and an anhydrite content of 10 wt%.
또한, 상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우, 상기 생석회는 20 중량% 내지 30 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 건식탈황석고 또는 플라이애시는 50 중량% 내지 60 중량%로 이루어질 수 있다.In addition, when the mixture containing the anhydrite is made of dry desulfurized gypsum or fly ash, the quicklime is 20% to 30% by weight, the water-containing additive is 10% to 20% by weight, the dry desulfurized gypsum or fly ash Ash may consist of 50% to 60% by weight.
한편, 상기 건식탈황석고 또는 상기 플라이애시의 입자를 바인딩하기 위한 유기물질을 더 포함하고, 상기 유기물질은, 전분, 녹말, 사탕수수 중 적어도 하나를 포함하고, 상기 생석회에 포함된 생석회량과 상기 건식탈황석고 또는 플라이애시에 포함된 생석회량을 더한 총생석회량의 5 중량% 내지 20 중량%의 범위를 충족할 수 있다.On the other hand, further comprising an organic material for binding particles of the dry desulfurization gypsum or the fly ash, wherein the organic material includes at least one of starch, starch, and sugar cane, and the amount of quicklime contained in the quicklime and the It may satisfy the range of 5 wt% to 20 wt% of the total amount of quicklime plus the amount of quicklime included in dry desulfurization gypsum or fly ash.
나아가, 상기 수분 함유 첨가물은, 수분 함량이 10 중량% 내지 30 중량%인 톱밥, 등겨 및 커피원두찌꺼기 중 적어도 하나를 포함할 수 있다.Furthermore, the water-containing additive may include at least one of sawdust having a water content of 10% to 30% by weight, rice bran, and coffee bean grounds.
한편, 상기와 같은 본 발명의 목적은 생석회와, 상기 생석회의 적어도 일부와 반응시켜 급격한 발열반응을 방지하기 위한 수분 함유 첨가물을 혼합하여 혼합물을 만드는 단계 및 상기 혼합물을 성형하는 단계를 포함하는 것을 특징으로 하는 친환경 축사 바닥재의 제조 방법에 의해 달성된다.On the other hand, an object of the present invention as described above includes the steps of mixing quicklime with at least a portion of the quicklime and a water-containing additive for preventing a rapid exothermic reaction to form a mixture and molding the mixture. It is achieved by a manufacturing method of an eco-friendly livestock barn flooring.
여기서, 상기 생석회는 40 중량% 내지 70 중량%, 상기 수분 함유 첨가물은 30 중량% 내지 60 중량%로 이루어질 수 있다.Here, the quicklime may be comprised of 40 wt% to 70 wt%, and the water-containing additive may be comprised of 30 wt% to 60 wt%.
또한, 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 투입하는 단계를 더 포함할 수 있다.In addition, the step of adding anhydrite (CaSO 4 ) or a mixture containing the anhydrite may be further included.
이 경우, 상기 생석회는 10 중량% 내지 20 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 60 중량% 내지 70 중량%로 이루어질 수 있다.In this case, the quicklime is 10 wt% to 20 wt%, the water-containing additive is 10 wt% to 20 wt%, and the anhydrite (CaSO 4 ) may be composed of 60 wt% to 70 wt%.
또한, 상기 생석회는 30 중량% 내지 40 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 40 중량% 내지 50 중량%로 이루어질 수 있다.In addition, the quicklime is 30% to 40% by weight, the water-containing additive is 10% to 20% by weight, and the anhydrite (CaSO 4 ) may be composed of 40% to 50% by weight.
한편, 상기 무수석고(CaSO4)는 제1형 무수석고, 제2형 무수석고 및 제3형 무수석고 중에 수분흡수기간에 따라 선택된 어느 하나로 이루어질 수 있다.On the other hand, the anhydrite (CaSO 4 ) may be made of any one selected from the type 1 anhydrite, type 2 anhydrite, and type 3 anhydrite according to the moisture absorption period.
이 경우, 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물에 유기염이 혼합되는 단계를 더 포함할 수 있다.In this case, the step of mixing an organic salt in the anhydrite (CaSO 4 ) or a mixture containing the anhydrite may be further included.
나아가, 상기 무수석고를 포함하는 혼합물은 건식탈황석고 또는 플라이애시로 이루어질 수 있다.Furthermore, the mixture containing the anhydrite may be made of dry desulfurization gypsum or fly ash.
이때, 상기 건식탈황석고는, 코크스를 연료로 하여 생석회 성분 함량이 40 중량% 내지 50 중량%이고 무수석고가 40 중량% 내지 50 중량%인 제1형 건식탈황석고 및 유연탄을 연료로 하여 생석회 성분 함량이 10 중량% 내지 20 중량%이고 무수석고의 성분 함량이 10 중량%인 제2형 건식탈황석고 중 어느 하나를 포함할 수 있다.At this time, in the dry desulfurization gypsum, type 1 dry desulfurization gypsum having a quicklime component content of 40% to 50% by weight and anhydrite of 40% to 50% by weight using coke as a fuel and a quicklime component using bituminous coal as a fuel The content may include any one of type 2 dry desulfurization gypsum having a content of 10% by weight to 20% by weight and a component content of anhydrite of 10% by weight.
이 경우, 상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우, 상기 생석회는 20 중량% 내지 30 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 건식탈황석고 또는 플라이애시는 50 중량% 내지 60 중량%로 이루어질 수 있다.In this case, when the mixture containing the anhydrite is made of dry desulfurized gypsum or fly ash, the quicklime is 20% to 30% by weight, the water-containing additive is 10% to 20% by weight, the dry desulfurized gypsum or Fly ash may consist of 50% to 60% by weight.
한편, 상기 건식탈황석고 또는 상기 플라이애시의 입자를 바인딩하기 위한 유기물질을 혼합하는 단계를 더 포함하고, 상기 유기물질은, 전분, 녹말, 사탕수수 중 적어도 하나를 포함하고, 상기 생석회에 포함된 생석회량과 상기 건식탈황석고 또는 플라이애시에 포함된 생석회량을 더한 총생석회량의 5 중량% 내지 20 중량%의 범위를 충족할 수 있다.On the other hand, the method further comprises the step of mixing an organic material for binding particles of the dry desulfurization gypsum or the fly ash, wherein the organic material includes at least one of starch, starch, and sugar cane, and contained in the quicklime It may satisfy the range of 5 wt% to 20 wt% of the total amount of quicklime by adding the amount of quicklime and the amount of quicklime included in the dry desulfurization gypsum or fly ash.
나아가, 상기 수분 함유 첨가물은, 수분 함량이 10 중량% 내지 30 중량%인 톱밥, 등겨 및 커피원두 찌꺼기 중 적어도 하나를 포함할 수 있다.Furthermore, the water-containing additive may include at least one of sawdust having a water content of 10% to 30% by weight, rice bran, and coffee bean dregs.
이상과 같은 본 발명의 친환경 축사 바닥재에 따르면 가축을 사육하는 축사의 바닥의 먼지를 제거할 수 있으며, 특히 가축 등의 소변 등으로 인한 수분을 제거할 수 있다. 또한, 상기 축사 바닥의 수분을 제거하는 경우에 급격한 발열반응을 방지하여 가축 등이 다치는 것을 방지할 수 있다.According to the eco-friendly barn flooring material of the present invention as described above, it is possible to remove dust from the floor of a barn for raising livestock, and in particular, it is possible to remove moisture from urine, etc. of livestock. In addition, it is possible to prevent a sudden exothermic reaction when removing the moisture from the floor of the barn, thereby preventing injuries to livestock and the like.
또한, 본 발명의 친환경 축사 바닥재에 따르면 생석회의 운반, 보관 등에 따른 위험을 줄일 수 있고, 바닥재의 제조원가를 절감하여 경제적 이득을 얻을 수 있다.In addition, according to the eco-friendly livestock flooring material of the present invention, it is possible to reduce risks due to the transportation and storage of quicklime, and it is possible to obtain economic benefits by reducing the manufacturing cost of the flooring material.
또한, 바닥재의 수분 흡수 가능 기간을 조절할 수 있는 효과가 있다.In addition, there is an effect of controlling the water absorption period of the flooring material.
도 1은 본 발명의 일 실시예에 따른 친환경 축사 바닥재의 제조 설비를 간략히 나타낸 도면이다.
도 2는 제조 온도에 따라 구분되는 무수석고의 타입을 설명하기 위한 도면이다.
도 3은 본 발명의 일 실시예에 따른 친환경 축사 바닥재의 제조 방법을 설명하기 위한 흐름도이다.
도 4는 본 발명의 다른 실시예에 따른 친환경 축사 바닥재의 제조 방법을 설명하기 위한 흐름도이다.1 is a view schematically showing a manufacturing facility for an eco-friendly livestock barn flooring according to an embodiment of the present invention.
Figure 2 is a view for explaining the type of anhydrite classified according to the manufacturing temperature.
3 is a flowchart illustrating a method of manufacturing an eco-friendly livestock barn flooring material according to an embodiment of the present invention.
4 is a flowchart illustrating a method of manufacturing an eco-friendly livestock barn flooring material according to another embodiment of the present invention.
먼저, 본 명세서 및 청구범위에서 사용되는 용어는 본 발명의 다양한 실시예들에서의 기능을 고려하여 일반적인 용어들을 선택하였다. 하지만, 이러한 용어들은 당 분야에 종사하는 기술자의 의도나 법률적 또는 기술적 해석 및 새로운 기술의 출현 등에 따라 달라질 수 있다. 또한, 일부 용어는 출원인이 임의로 선정한 용어일 수 있다. 이러한 용어에 대해서는 본 명세서에서 정의된 의미로 해석될 수 있으며, 구체적인 용어 정의가 없으면 본 명세서의 전반적인 내용 및 당해 기술 분야의 통상적인 기술 상식을 토대로 해석될 수도 있다.First, terms used in the present specification and claims have been selected in consideration of functions in various embodiments of the present invention. However, these terms may vary depending on the intention, legal or technical interpretation of a person skilled in the art, and the emergence of new technology. Also, some terms may be arbitrarily selected by the applicant. These terms may be interpreted in the meaning defined in the present specification, and if there is no specific term definition, it may be interpreted based on the general content of the present specification and common technical knowledge in the art.
또한, 본 명세서에 첨부된 각 도면에 기재된 동일한 참조 번호 또는 부호는 실질적으로 동일한 기능을 수행하는 부품 또는 구성요소를 나타낸다. 설명 및 이해의 편의를 위해서 서로 다른 실시예들에서도 동일한 참조번호 또는 부호를 사용하여 설명하도록 한다. 즉, 복수의 도면에서 동일한 참조 번호를 가지는 구성 요소를 모두 도시하고 있다고 하더라도, 복수의 도면들이 하나의 실시예를 의미하는 것은 아니다.Also, the same reference numerals or reference numerals in each drawing appended hereto indicate parts or components that perform substantially the same functions. For the convenience of description and understanding, the same reference numerals or reference numerals are used in different embodiments to be described. That is, even though all components having the same reference numerals are shown in a plurality of drawings, the plurality of drawings do not mean one embodiment.
또한, 본 명세서 및 청구범위에서는 구성요소들 간의 구별을 위하여 '제1', '제2' 등과 같이 서수를 포함하는 용어가 사용될 수 있다. 이러한 서수는 동일 또는 유사한 구성 요소들을 서로 구별하기 위하여 사용하는 것이며, 이러한 서수 사용으로 인하여 용어의 의미가 한정 해석되어서는 안될 것이다. 일 예로, 이러한 서수와 결합된 구성 요소는 그 숫자에 의해 사용 순서나 배치 순서 등이 제한 해석되어서는 안된다. 필요에 따라서는, 각 서수들은 서로 교체되어 사용될 수도 있다.In addition, in this specification and claims, terms including ordinal numbers such as 'first' and 'second' may be used to distinguish between elements. This ordinal number is used to distinguish the same or similar components from each other, and the meaning of the term should not be limitedly interpreted due to the use of the ordinal number. As an example, the components combined with such an ordinal number should not be construed as limiting the order of use or arrangement by the number. If necessary, each ordinal number may be used interchangeably.
본 명세서에서 단수의 표현은 문맥상 명백하게 다름을 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, '포함하다' 또는 '구성하다' 등의 용어는 명세서 상에 기재된 특징, 숫자, 단계, 동작, 구성 요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성 요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.In this specification, the singular expression includes the plural expression unless the context clearly dictates otherwise. In the present application, terms such as 'comprise' or 'comprise' are intended to designate that a feature, number, step, operation, component, part, or a combination thereof described in the specification exists, but one or more other It should be understood that this does not preclude the possibility of addition or presence of features or numbers, steps, operations, components, parts, or combinations thereof.
또한, 본 발명의 실시예에서, 어떤 부분이 다른 부분과 연결되어 있다고 할 때, 이는 직접적인 연결뿐 아니라, 다른 매체를 통한 간접적인 연결의 경우도 포함한다. 또한 어떤 부분이 어떤 구성 요소를 포함한다는 의미는, 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있다는 것을 의미한다.In addition, in the embodiment of the present invention, when a part is connected to another part, this includes not only direct connection but also indirect connection through another medium. In addition, the meaning that a certain part includes a certain component means that other components may be further included, rather than excluding other components, unless specifically stated to the contrary.
이하, 첨부된 도면을 참조하여 본 발명을 더욱 구체적으로 설명하기로 한다.Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.
도 1은 본 발명의 일 실시예에 따른 친환경 축사 바닥재의 제조 설비를 간략히 나타낸 도면이다.1 is a view schematically showing a manufacturing facility for an eco-friendly livestock barn flooring according to an embodiment of the present invention.
본 발명의 일 실시예에 따른 친환경 축사 바닥재는 생석회(CaO)와, 상기 생석회의 적어도 일부와 반응시켜 급격한 발열반응을 방지하기 위한 수분 함유 첨가물을 포함할 수 있다.The eco-friendly barn flooring material according to an embodiment of the present invention may include quicklime (CaO) and a water-containing additive for preventing a rapid exothermic reaction by reacting with at least a portion of the quicklime.
이 경우, 상기 생석회는 40 중량% 내지 70 중량%, 상기 수분 함유 첨가물은 30 중량% 내지 60 중량%로 이루어질 수 있다.In this case, the quicklime may be comprised of 40 wt% to 70 wt%, and the water-containing additive may be comprised of 30 wt% to 60 wt%.
또한, 상기 친환경 축사 바닥재는 상기 생석회의 수분 흡수 속도를 조절하기 위한 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 더 포함할 수 있다.In addition, the eco-friendly barn flooring may further include anhydrite (CaSO 4 ) or a mixture containing the anhydrite for controlling the moisture absorption rate of the quicklime.
이 경우, 상기 생석회의 양을 조절하여 바닥재에 포함되는 칼슘의 양을 조절할 수 있다. 이는 상기 바닥재를 축사에서 제거하여 과수원 또는 수목원 등에서 퇴비로 사용하는 경우에 적절하게 조절하기 위함이다.In this case, the amount of calcium included in the flooring may be adjusted by adjusting the amount of the quicklime. This is to properly control when the flooring material is removed from the barn and used as compost in an orchard or arboretum.
예를 들어, 칼슘의 양이 상대적으로 적은 저칼슘 바닥재의 경우, 상기 생석회는 10 중량% 내지 20 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 60 중량% 내지 70 중량%로 이루어질 수 있다.For example, in the case of a low-calcium flooring material having a relatively small amount of calcium, the quicklime is 10% to 20% by weight, the water-containing additive is 10% to 20% by weight, and the anhydrite (CaSO4) is 60% by weight % to 70% by weight.
반면에 상기 칼슘의 양이 상대적으로 많은 고칼슘 바닥재의 경우 상기 생석회는 30 중량% 내지 40 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 40 중량% 내지 50 중량%로 이루어질 수 있다.On the other hand, in the case of a high-calcium flooring material having a relatively large amount of calcium, the quicklime is 30% to 40% by weight, the water-containing additive is 10% to 20% by weight, and the anhydrite (CaSO4) is 40% to 50% by weight It may consist of weight %.
상기 생석회는 전술한 바와 같이 축사 등에서 소독용으로 많이 사용되었으며, 본 발명에 따른 축사 바닥재를 축사에서 제거하여 과수원, 수목원 등에서 퇴비로 사용하는 경우에 상기 생석회는 토양에 칼슘 성분을 제공하여 토양을 비옥하게 하며, 나아가 산성 토양을 중화시키는 역할을 하게 된다.As described above, the quicklime has been widely used for disinfection in barns, etc., and when the barn flooring material according to the present invention is removed from the barn and used as compost in an orchard, an arboretum, etc., the quicklime provides a calcium component to the soil to fertilize the soil In addition, it plays a role in neutralizing acidic soil.
이하, 본 발명의 친환경 축사 바닥재의 제조 설비와 함께 친환경 바닥재에 대해서 살펴보기로 한다.Hereinafter, the environment-friendly flooring material together with the manufacturing facility of the eco-friendly livestock barn flooring material of the present invention will be looked at.
상기 친환경 축사 바닥재의 제조 설비는 크러셔(crusher)(21), 호퍼(hopper)(22-1 내지 22-3), 스크린(23), 싸일로(silo)(24), 바인딩 유닛(25), 믹서기(26-1, 26-2) 및 성형 장치(briquetting machine)(27)를 포함한다.The manufacturing facility of the eco-friendly barn flooring material includes a
상기 크러셔(21)는 전술한 생석회 자갈을 분쇄하기 위한 구성이다. 상기 크러셔(21)는 지름 30mm 내지 80mm의 굵은 생석회의 자갈을 지름 25mm 이하의 가루로 분쇄할 수 있다. 여기서 생석회는 마그네슘, 실리콘 등의 이물질을 포함하는 저품위생석회가 이용될 수 있다. 저품위 생석회는 생석회 성분의 함량이 60% 내지 90%를 포함하는 것으로서, 일반적으로 석회석을 섭씨 800도 내지 900도 내에서 구워 만들어질 수 있다.The
이 경우, 지름 25mm 이하의 가루로 분쇄된 생석회는 제1 호퍼(22-1)를 통과하게 된다. In this case, the quicklime pulverized into powder with a diameter of 25 mm or less passes through the first hopper 22-1.
상기 스크린(23)은 보내진 생석회 중 일정 크기의 입자만을 거르기 위한 구성이다. 상기 스크린(23)에서 걸러진 지름 25mm 이하의 생석회는 제1 믹서기(26-1)로 보내진다. 이 경우, 지름 25mm 이상의 생석회는 다시 수집하여 후속공정에서 사용할 수 있다.The
상기 생석회가 제1 믹서기(26-1)를 거쳐 제2 믹서기(26-2)로 보내지면, 제2 호퍼(22-2)를 통해 수분이 함유된 첨가물이 제2 믹서기(26-2)로 보내져, 제2 믹서기(26-2) 내에서 생석회와 섞일 수 있다.When the quicklime is sent to the second blender 26-2 through the first blender 26-1, the water-containing additive is transferred to the second blender 26-2 through the second hopper 22-2. It can be sent and mixed with quicklime in the second blender 26-2.
일반적으로 생석회(CaO)와 물(H2O)과 만나게 되면 아래 [화학식 1]과 같은 반응을 일으킨다.In general, when quicklime (CaO) and water (H 2 O) meet, a reaction such as the following [Formula 1] occurs.
[화학식 1] [Formula 1]
CaO + H2O = Ca(OH)2 + 15.6 kcal/molCaO + H 2 O = Ca(OH) 2 + 15.6 kcal/mol
상기 [화학식 1]에 의한 반응은 발열반응에 해당하여 상기 생석회를 물과 반응시키게 되면 급격한 발열반응에 의해 열을 방출하게 된다. 따라서, 이러한 급격한 발열반응을 감소시키기 위하여 전술한 수분이 함유된 첨가물을 투입할 수 있다.The reaction according to [Formula 1] corresponds to an exothermic reaction, and when the quicklime is reacted with water, heat is released by a rapid exothermic reaction. Therefore, in order to reduce such a sudden exothermic reaction, the above-mentioned water-containing additive may be added.
상기 수분이 함유된 첨가물은 10 중량% 내지 30 중량%의 수분을 함유하고 있는 톱밥, 등겨와 같은 천연 첨가물일 수 있다. 이러한 수분 함유 첨가물은 수분을 고화시키는 역할을 하지 못하며, 수분을 흡수하는 역할만을 하게 된다. The moisture-containing additive may be a natural additive such as sawdust or rice bran containing 10% to 30% by weight of moisture. These water-containing additives do not serve to solidify moisture, but only serve to absorb moisture.
따라서, 톱밥, 등겨 등의 천연 첨가물에 이미 포함된 수분은 생석회의 일부와 미리 반응하여 발열반응을 일으키고 생석회의 발열성을 떨어뜨림으로써, 추후 바닥재가 수분과 반응하여 급격하게 발열반응을 일으키는 것을 방지할 수 있다. 즉, 톱밥 등에 포함된 수분이 쿠션 기능을 수행하여, 성형 능률의 향상을 기대할 수 있다.Therefore, moisture already contained in natural additives such as sawdust and rice bran reacts with a part of quicklime in advance to cause an exothermic reaction and lowers the exothermicity of quicklime, thereby preventing the flooring from reacting with moisture and causing a sudden exothermic reaction. can do. That is, moisture contained in sawdust and the like performs a cushioning function, and improvement of molding efficiency can be expected.
또한, 톱밥, 등겨 등의 천연 첨가물은 추후 축사에 바닥재를 공급하는 경우, 수분을 흡수하여 수분을 제거하며, 추후에 퇴비로서 기능하고 특히, 톱밥 등은 질소, 섬유질을 제공할 수 있는 효과가 있다.In addition, natural additives such as sawdust and back husks absorb moisture and remove moisture when supplying flooring to the barn later, and function as compost later. In particular, sawdust has an effect of providing nitrogen and fiber. .
한편, 이러한 천연 첨가물로서 커피 찌꺼기(커피원두 찌꺼기 또는 '그라운즈(Grounds)')를 이용하거나, 톱밥, 등겨 등에 커피원두 찌꺼기를 더 첨가할 수도 있는데 이러한 경우에는 탈취 효과를 기대할 수도 있다.On the other hand, as such a natural additive, coffee grounds (coffee bean grounds or 'Grounds') may be used, or coffee bean grounds may be further added to sawdust, rice bran, etc. In this case, a deodorizing effect may be expected.
이 경우, 상기 생석회는 40 중량% 내지 70 중량%, 상기 수분 함유 첨가물은 30 중량% 내지 60 중량%로 이루어질 수 있다.In this case, the quicklime may be comprised of 40 wt% to 70 wt%, and the water-containing additive may be comprised of 30 wt% to 60 wt%.
제2 믹서기(26-2)에서 혼합된 혼합물은 제3 호퍼(22-3)를 통해 성형장치(27)로 보내지게 되고, 성형장치(27)는 혼합물을 성형하여 최종적으로 바닥재의 완제품(30)을 제조할 수 있다. 상기 성형단계에서는 캐스팅 등의 방법으로 성형을 하여, 축사 등에 공급하는 경우에 먼지 등이 비산하는 것을 방지하게 된다.The mixture mixed in the second mixer 26-2 is sent to the
한편, 본 발명의 다른 실시예에 따르면, 생석회와 수분흡수를 지연시키는 지연제가 함께 혼합될 수 있다. 즉, 상기 생석회와 지연제가 혼합되고, 전술한 수분 함유 첨가물이 첨가될 수 있다.Meanwhile, according to another embodiment of the present invention, quicklime and a retarding agent for delaying water absorption may be mixed together. That is, the quicklime and the retarder may be mixed, and the above-described water-containing additive may be added.
이 경우, 상기 지연제는 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물로 이루어질 수 있다.In this case, the retardant may be made of anhydrite (CaSO 4 ) or a mixture containing the anhydrite.
상기 무수석고는 수분을 고화시키는 효율은 생석회보다 다소 떨어지지만, 수분을 흡수하는 능력은 상기 생석회보다 더 좋은 성질을 가진다. 또한, 상기 무수석고는 수분과 반응하는 경우에 생석회보다 발열량이 현저히 작다. 따라서, 생석회와 비교하면, 생석회와 유사한 또는 더 좋은 수분 제거 효율을 가지면서 급격한 발열반응을 줄일 수 있는 장점이 있다. Although the efficiency of solidifying moisture is somewhat lower than that of quicklime, the anhydrite has better properties than quicklime in its ability to absorb moisture. In addition, when the anhydrite reacts with moisture, the calorific value is significantly lower than that of quicklime. Therefore, compared to quicklime, there is an advantage in that it can reduce a rapid exothermic reaction while having a water removal efficiency similar to or better than that of quicklime.
이 경우, 상기 생석회의 양을 조절하여 바닥재에 포함되는 칼슘의 양을 조절할 수 있다. 이는 상기 바닥재를 축사에서 제거하여 과수원 또는 수목원 등에서 퇴비로 사용하는 경우에 적절하게 조절하기 위함이다.In this case, the amount of calcium included in the flooring may be adjusted by adjusting the amount of the quicklime. This is to properly control when the flooring material is removed from the barn and used as compost in an orchard or arboretum.
예를 들어, 칼슘의 양이 상대적으로 적은 저칼슘 바닥재의 경우, 상기 생석회는 10 중량% 내지 20 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 60 중량% 내지 70 중량%로 이루어질 수 있다.For example, in the case of a low-calcium flooring material having a relatively small amount of calcium, the quicklime is 10% to 20% by weight, the water-containing additive is 10% to 20% by weight, and the anhydrite (CaSO4) is 60% by weight % to 70% by weight.
반면에 상기 칼슘의 양이 상대적으로 많은 고칼슘 바닥재의 경우 상기 생석회는 30 중량% 내지 40 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 40 중량% 내지 50 중량%로 이루어질 수 있다.On the other hand, in the case of a high-calcium flooring material having a relatively large amount of calcium, the quicklime is 30% to 40% by weight, the water-containing additive is 10% to 20% by weight, and the anhydrite (CaSO4) is 40% to 50% by weight It may consist of weight %.
나아가, 본 발명에 따른 축사 바닥재를 축사에서 제거하여 과수원, 수목원 등에서 퇴비로 사용하는 경우에 상기 무수석고는 유황성분을 제공하여 식물 등의 뿌리가 용이하게 토양에 안착시키도록 도와주는 역할을 하게 된다.Furthermore, when the barn flooring material according to the present invention is removed from the barn and used as compost in an orchard, arboretum, etc., the anhydrite provides a sulfur component to help the roots of plants, etc., to easily settle in the soil. .
또한, 상기 무수석고는 바닥재가 수분을 흡수하는 속도를 조절하기 위한 것으로서, 석고를 굽는 온도에 따라 제1형 무수석고, 제2형 무수석고 및 제3형 무수석고로 구분될 수 있다.In addition, the anhydrite is for controlling the rate at which the flooring material absorbs moisture, and may be classified into type 1 anhydrite, type 2 anhydrite, and type 3 anhydrite depending on the baking temperature of the gypsum.
도 2를 참조하면, 제1형 무수석고는 석고가 일반적으로 섭씨 1100도 이상에서 제조되며, 제2형 무수석고는 섭씨 230도 내지 350도 사이에서, 제3형 무수석고는 섭씨 105도 내지 240도 사이에서 제조되는 것을 의미한다.Referring to Figure 2, type 1 anhydrite gypsum is generally produced at 1100 degrees Celsius or more, type 2 anhydrite is between 230 degrees Celsius and 350 degrees Celsius, and type 3 anhydrite is 105 degrees Celsius to 240 degrees Celsius It means that it is manufactured between the figures.
일반적으로, 석고를 굽는 온도가 낮을수록 수분의 흡수 속도가 빨라지게 되며, 굽은 온도가 높을수록 무수석고의 구성이 안정화되어 수분을 천천히 빨아들이게 된다.In general, the lower the temperature at which the gypsum is baked, the faster the absorption rate of water is.
상온에서 이수석고(CaSO4·2H2O)로 존재하는 석고는 클링커(clinker) 온도, 밀(Mill) 회전에 의한 열에너지의 축적 또는 저장 운반중의 온도 상승 등에 의해서 탈수되어 섭씨 80~150도 사이에서 반수석고(β-CaSO4·½H2O)가 되며, 섭씨 105도 내지 240도 사이에서 2차 탈수를 일으켜서 제3형 무수석고가 된다.Gypsum existing as dihydrate gypsum (CaSO 4 ·2H 2 O) at room temperature is dehydrated by the clinker temperature, accumulation of thermal energy due to mill rotation, or temperature increase during storage and transportation, and is between 80 and 150 degrees Celsius. becomes hemihydrate gypsum (β-CaSO 4 ·½H 2 O), and secondary dehydration occurs between 105 and 240 degrees Celsius to form type 3 anhydrite.
이러한 석고의 탈수는 물과의 접촉 시 각형의 용해도 차이에 의하여 초기수화와 응결에 많은 영향을 미치게 된다.The dehydration of such gypsum greatly affects initial hydration and coagulation due to the difference in solubility of prismatic shapes upon contact with water.
제1형 무수석고 및 생석회를 제1 호퍼(22-1)에 통과시켜 만들어진 바닥재(제1 실시예)는 수분을 초장기적으로 흡수하며, 일반적으로 한달 이상 수분을 흡수할 수 있다.The flooring material made by passing type 1 anhydrite and quicklime through the first hopper 22-1 (the first embodiment) absorbs moisture for a very long time, and can generally absorb moisture for more than a month.
제2형 무수석고 및 생석회를 제1 호퍼(22-1)에 통과시켜 만들어진 바닥재(제2 실시예)는 수분을 장기적으로 흡수할 수 있으며, 일반적으로 1달 내외로 수분을 흡수할 수 있다.The flooring material made by passing type 2 anhydrite and quicklime through the first hopper 22-1 (the second embodiment) can absorb moisture for a long time, and generally can absorb moisture within about one month.
제3형 무수석고 및 생석회를 제1 호퍼(22-1)에 통과시켜 만들어진 바닥재(제3 실시예)는 수분을 중기적으로 흡수할 수 있으며, 일반적으로 일주일 이상 한달 내로 수분을 흡수할 수 있다.The flooring material made by passing type 3 anhydrite and quicklime through the first hopper 22-1 (the third embodiment) can absorb moisture in the medium term, and generally can absorb moisture within a week or more .
한편, 무수석고를 투입하지 않고, 생석회만을 제1 호퍼(22-1)에 통과시켜 만들어진 바닥재(제4 실시예)는 수분을 초단기적으로 흡수하게 되며, 일반적으로 1주일동안 수분을 흡수하게 된다.On the other hand, the flooring material (the fourth embodiment) made by passing only quicklime through the first hopper 22-1 without adding anhydrite absorbs moisture in a very short time, and generally absorbs moisture for one week. .
즉, 무수석고의 포함 형태에 따라 바닥재가 초단기, 중기, 장기 또는 초장기적으로 수분을 흡수할 수 있는 기간을 조절하도록 설계가 가능하다.That is, it is possible to design to control the period during which the flooring material can absorb moisture in the very short, medium, long or very long period according to the type of anhydrite included.
한편, 도 1에 나타난 바와 같이, 상기 무수석고와 혼합된 생석회 또는 상기 무수석고가 혼합된 혼합물과 혼합된 생석회는 전술한 스크린(23)으로 보내져서 처리된다.On the other hand, as shown in FIG. 1 , the quicklime mixed with the anhydrite or the quicklime mixed with the mixture mixed with the anhydrite is sent to the
한편, 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물에 유기염이 혼합되어 상기 생석회에 투입될 수 있다.Meanwhile, an organic salt may be mixed with the anhydrite (CaSO 4 ) or a mixture containing the anhydrite and added to the quicklime.
이때, 상기 유기염은 숙신산나트륨(sodium succinate, Na2C4H4O4) 또는 젤라틴(gelatin) 등으로 이루어질 수 있다. In this case, the organic salt may be made of sodium succinate (sodium succinate, Na 2 C 4 H 4 O 4 ) or gelatin.
상기 유기염이 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물에 섞이는 경우, 상기 유기염이 상기 무수석고 입자의 표면의 적어도 일부에 코팅되어 물리적으로 상기 무수석고가 물과 반응하는 것을 지연시킬 수 있다. 또한, 상기 유기염은 화학적으로도 상기 무수석고가 물과 반응하는 것을 지연시키는 역할을 하게 된다. When the organic salt is mixed with the anhydrite (CaSO 4 ) or a mixture containing the anhydrite, the organic salt is coated on at least a portion of the surface of the anhydrite particles so that the anhydrite physically reacts with water can be delayed In addition, the organic salt serves to delay the reaction of the anhydrite with water chemically.
따라서, 본 실시예의 경우 무수석고에 젤라틴 등의 유기염을 추가함으로써 수분 흡수 속도를 조절할 수 있다. 상기 유기염을 투입하는 경우에 물에 희석하여 투입하게 되며, 대략 1% 용액(물 : 유기염 = 100 : 1)으로 희석하여 투입할 수 있다.Therefore, in the present embodiment, the water absorption rate can be controlled by adding an organic salt such as gelatin to the anhydrite. When the organic salt is added, it is diluted with water, and may be diluted with an approximately 1% solution (water: organic salt = 100: 1).
한편, 상기 지연제가 상기 무수석고를 포함하는 혼합물로 이루어진 경우, 상기 혼합물은 건식탈황석고 또는 플라이애시로 이루어질 수 있다.On the other hand, when the retardant is composed of a mixture containing the anhydrite, the mixture may be composed of dry desulfurization gypsum or fly ash.
예를 들어, 상기 제1 믹서기(26-1)로 보내진 생석회는 건식탈황석고 또는 플라이애시와 같이 무수석고를 포함하는 혼합물과 섞일 수 있다. 이 경우, 상기 건식탈황석고 또는 상기 플라이애시의 입자를 바인딩하기 위한 유기물질로 구성된 유기바인더를 함께 혼합할 수 있다.For example, the quicklime sent to the first mixer 26-1 may be mixed with a mixture containing anhydrite such as dry desulfurization gypsum or fly ash. In this case, the dry desulfurization gypsum or an organic binder composed of an organic material for binding the particles of the fly ash may be mixed together.
예를 들어, 싸일로(silo)(24)는 전술한 건식탈황석고 또는 플라이애시를 저장하는 구성에 해당한다. 상기 건식탈황석고는 코크스 또는 유연탄을 보일러 연료로 사용하는 화력발전소의 연소과정에서 발생되는 황산화물(주로 이산화황)을 배연탈황(flue-gas desulfurization) 장치를 이용하여 제거하는 과정에서 산출되는 부산물로서, 산화칼슘과 이산화황이 반응하여 형성된다.For example, the silo (silo) 24 corresponds to the configuration for storing the aforementioned dry desulfurized gypsum or fly ash. The dry desulfurization gypsum is a by-product produced in the process of removing sulfur oxides (mainly sulfur dioxide) generated in the combustion process of a thermal power plant using coke or bituminous coal as boiler fuel using a flue-gas desulfurization device, It is formed by the reaction of calcium oxide and sulfur dioxide.
이때, 상기 건식탈황석고는 코크스를 연료로 하여 생석회 성분 함량이 40 중량% 내지 50 중량%이고 무수석고가 대략 40 중량% 내지 50 중량%인 제1형 건식탈황석고와, 유연탄을 연료로 하여 생석회 성분 함량이 10 중량% 내지 20 중량%이며 무수석고가 성분 함량이 10 중량% 내외인 유동층 보일러를 사용하는 석탄화력발전소의 탈황공정에서 부산물로 발생하는 제2형 건식탈황석고 중 어느 하나를 포함할 수 있다.At this time, the dry desulfurization gypsum is a type 1 dry desulfurization gypsum in which the content of quicklime is 40% to 50% by weight and anhydrite is approximately 40% to 50% by weight using coke as a fuel, and quicklime using bituminous coal as a fuel The component content is 10% by weight to 20% by weight and the anhydrite contains any one of type 2 dry desulfurization gypsum generated as a by-product in the desulfurization process of a coal-fired power plant using a fluidized bed boiler with a component content of about 10% by weight. can
이때, 상기 싸일로는 건식탈황석고 대신 플라이애시(fly ash)를 저장할 수도 있다. 플라이애시는 석탄이나 중유를 보일러 연료로 사용하는 화력발전소에서 유연탄의 연소과정에서 발생되는 회분을 굴뚝에서 전기 집진기로 포집한 연소재로서, 알루미나(Al2O3)와 실리카(SiO2)가 주성분이고 주로 콘크리트의 혼화재로서 사용된다.At this time, the silo may store fly ash instead of dry desulfurization gypsum. Fly ash is a combustion material that collects ash generated during the combustion of bituminous coal in a thermal power plant that uses coal or heavy oil as boiler fuel by an electric dust collector in a chimney. Alumina (Al 2 O 3 ) and silica (SiO 2 ) are the main components. and is mainly used as an admixture for concrete.
플라이애시 또한 생석회에 혼합되면, 가공성(workability)이 개선되고 경화열이 완화됨과 더불어 장기적인 강도 및 수밀성이 향상되어 경제적이다.When fly ash is also mixed with quicklime, workability is improved, heat of hardening is relieved, and long-term strength and watertightness are improved, which is economical.
또한, 상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우 초기에 투입되는 저품위 생석회의 중량비율이 상대적으로 더 낮아질 수 있다.In addition, when the mixture containing the anhydrite is made of dry desulfurized gypsum or fly ash, the weight ratio of low-grade quicklime to be initially added may be relatively lower.
즉, 상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우, 상기 건식탈황석고 또는 플라이애시에 이미 생석회 성분이 포함되어 있으므로, 초기에 투입되는 저품위 생석회의 중량비율을 더 낮출 수 있다.That is, when the mixture containing the anhydrite is made of dry desulfurization gypsum or fly ash, the dry desulfurization gypsum or fly ash already contains a quicklime component, so the weight ratio of low-grade quicklime input at the beginning can be lowered further. .
예를 들어, 상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우, 상기 생석회는 20 중량% 내지 30 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 건식탈황석고 또는 플라이애시는 50 중량% 내지 60 중량%로 이루어질 수 있다.For example, when the mixture containing the anhydrite is made of dry desulfurized gypsum or fly ash, the quicklime is 20% to 30% by weight, the water-containing additive is 10% to 20% by weight, the dry desulfurized gypsum Alternatively, fly ash may be comprised of 50 wt% to 60 wt%.
이하에서는, 건식탈황석고 또는 플라이애시를 건식탈황석고로 통칭하여 설명하도록 한다.Hereinafter, dry desulfurization gypsum or fly ash will be collectively referred to as dry desulfurization gypsum.
상기 싸일로(24)는 저장된 건식탈황석고를 제1 믹서기(26-1)로 보내고, 바인딩 유닛(25)은 제1 믹서기(26-1)로 보내진 건식탈황석고의 입자를 바인딩하기 위한 유기바인더를 공급한다.The
여기서, 상기 유기바인더는 전분, 녹말, 사탕수수 등의 유기물질을 성분으로 하는 천연유기물질일 수 있다. 이때, 전분, 녹말 또는 사탕수수는 물에 희석된 것일 수 있으며 점액질을 만들어 건식탈황석고의 입자를 바인딩하는 역할을 한다.Here, the organic binder may be a natural organic material containing an organic material such as starch, starch, and sugar cane as a component. At this time, starch, starch, or sugar cane may be diluted in water, and serves to bind the particles of dry desulfurization gypsum by making mucilage.
또한, 상기 유기바인더는 건식탈황석고의 입자를 키움과 동시에, 유기바인더에 포함된 수분이 생석회 및 건식탈황석고에 포함된 생석회와 반응하여 발열성을 일정한 수준에서 낮추는 기능을 할 수 있다.In addition, the organic binder increases the particles of the dry desulfurization gypsum and at the same time, the moisture contained in the organic binder reacts with the quicklime and the quicklime contained in the dry desulfurization gypsum, thereby lowering the exothermicity at a certain level.
또한, 상기 유기바인더는 이수화 반응을 지연시킴으로써 바닥재의 수분 흡수 기능이 좀 더 오래 지속되도록 할 수 있다.In addition, the organic binder can delay the dihydration reaction so that the water absorption function of the flooring material lasts a little longer.
다만, 생석회 및 건식탈황석고에 뿌려지는 유기바인더의 양이 너무 많은 경우, 생석회의 발열성 및 수분 고화 능력을 지나치게 상실하게 되어, 바닥재의 제습 효율이 현저히 떨어질 수 있다.However, if the amount of organic binder sprayed on quicklime and dry desulfurization gypsum is too large, heat generation and moisture solidification ability of quicklime are excessively lost, and the dehumidification efficiency of the flooring material may be significantly reduced.
따라서, 유기바인더는 실험적으로 제1 믹서기(26-1)로 보내진 생석회 및 건식탈황석고에 포함된 총생석회량의 5 중량% 내지 20 중량% 이내로 뿌려지는 것이 바람직하다.Therefore, the organic binder is preferably sprayed within 5 wt% to 20 wt% of the total amount of quicklime included in the quicklime and dry desulfurization gypsum experimentally sent to the first mixer 26-1.
또한, 유기바인더는 전체 바닥재의 함유량 중 5 중량% 이내로 투입될 수 있다.In addition, the organic binder may be added within 5% by weight of the total content of the flooring material.
이와 같이, 제1 믹서기(26-1)는 쌍축의 패들을 이용하여 생석회, 무수석고, 건식탈황석고 및 유기바인더를 고루 섞고, 이와 같이 섞인 혼합물을 제2 믹서기(26-2)로 보내게 된다.In this way, the first mixer 26-1 mixes quicklime, anhydrite, dry desulfurization gypsum and an organic binder using a twin-axial paddle, and sends the mixed mixture to the second mixer 26-2. .
상기 제2 믹서기(26-2)에서는 전술한 바와 같이 상기 제2 호퍼(22-2)를 통해 수분이 함유된 첨가물이 제2 믹서기(26-2)로 보내져, 제2 믹서기(26-2) 내에서 혼합물과 섞일 수 있다.In the second mixer 26-2, the water-containing additive is sent to the second mixer 26-2 through the second hopper 22-2 as described above, and the second mixer 26-2 It can be mixed with the mixture in
도 3은 본 발명의 일 실시예에 따른 친환경 축사 바닥재의 제조 방법을 설명하기 위한 흐름도이다.3 is a flowchart illustrating a method of manufacturing an eco-friendly livestock barn flooring material according to an embodiment of the present invention.
먼저, 생석회와, 상기 생석회의 적어도 일부와 반응시켜 급격한 발열반응을 방지하기 위한 수분 함유 첨가물을 혼합(S310)하고, 상기 혼합물을 성형(S330)하게 된다.First, quicklime is mixed with at least a portion of the quicklime to prevent a rapid exothermic reaction by mixing (S310) and molding the mixture (S330).
한편, 상기 수분 함유 첨가물은 생석회의 적어도 일부와 미리 반응시킴으로써 급격한 발열반응을 방지하기 위한 것으로서, 수분 함량이 10 중량% 내지 30 중량%인 톱밥 및 등겨 중 적어도 하나를 포함할 수 있다.On the other hand, the water-containing additive is to prevent a rapid exothermic reaction by reacting in advance with at least a portion of quicklime, and may include at least one of sawdust and rice bran having a water content of 10 wt% to 30 wt%.
이 경우, 상기 생석회는 40 중량% 내지 70 중량%, 상기 수분 함유 첨가물은 30 중량% 내지 60 중량%로 이루어질 수 있다.In this case, the quicklime may be comprised of 40 wt% to 70 wt%, and the water-containing additive may be comprised of 30 wt% to 60 wt%.
한편, 도 4는 본 발명의 다른 실시예에 따른 친환경 축사 바닥재의 제조 방법을 설명하기 위한 흐름도이다.Meanwhile, FIG. 4 is a flowchart illustrating a method of manufacturing an eco-friendly livestock barn flooring material according to another embodiment of the present invention.
본 실시예의 경우, 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 투입하여 혼합하는 단계를 더 포함할 수 있다.In the case of this embodiment, the step of mixing by adding anhydrite (CaSO 4 ) or a mixture containing the anhydrite may be further included.
이 경우, 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 투입하는 단계는 상기 생석회와 수분 함유 첨가물을 혼합하는 단계와 동시에 수행되거나, 또는 상기 생석회와 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 먼저 혼합하고 이어서 수분 함유 첨가물을 혼합하는 것도 가능하다. 이하에서는 도면에 도시된 바와 같이, 상기 생석회와 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 먼저 혼합(S410)하고 이어서 수분 함유 첨가물을 혼합(S430)하고, 혼합물을 성형(S450)하는 것으로 설명한다.In this case, the step of adding the anhydrite (CaSO 4 ) or the mixture containing the anhydrite is performed simultaneously with the step of mixing the quicklime and the water-containing additive, or the quicklime and the anhydrite (CaSO 4 ) or It is also possible to first mix the mixture containing the anhydrite and then mix the water-containing additive. Hereinafter, as shown in the drawings, the quicklime and the anhydrite (CaSO 4 ) or the mixture containing the anhydrite are first mixed (S410) and then the water-containing additive is mixed (S430), and the mixture is molded (S450) ) is explained as
구체적으로, 지름 25mm 이하로 분쇄된 순도 60% 내지 90% 이하의 저품위 생석회를 무수석고(CaSO4) 또는 무수석고를 포함하는 혼합물과 1차 혼합한다.Specifically, low-grade quicklime with a purity of 60% to 90% or less, pulverized to a diameter of 25 mm or less, is first mixed with anhydrite (CaSO 4 ) or a mixture containing anhydrite.
이때, 무수석고는, 섭씨 1100도 이상에서 제조된 제1형 무수석고, 섭씨 230도 내지 350도 사이에서 제조된 제2형 무수석고, 섭씨 105도 내지 240도 사이에서 제조된 제3형 무수석고 중에 수분흡수기간에 따라 선택된 어느 하나를 포함할 수 있다.At this time, the anhydrite is, type 1 anhydrite produced at 1100 degrees Celsius or more, type 2 anhydrite prepared between 230 degrees Celsius and 350 degrees Celsius, and type 3 anhydrite produced between 105 degrees Celsius and 240 degrees Celsius. Among them, any one selected according to the moisture absorption period may be included.
이어서, 상기 1차 혼합에 의한 혼합물에, 상기 생석회의 적어도 일부와 반응시켜 급격한 발열반응을 방지하기 위한 수분 함유 첨가물을 투입하게 된다.Subsequently, a water-containing additive for preventing a rapid exothermic reaction by reacting with at least a portion of the quicklime is added to the mixture by the first mixing.
이때 상기 생석회는 10 중량% 내지 20 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 60 중량% 내지 70 중량%로 이루어질 수 있다.In this case, the quicklime is 10 wt% to 20 wt%, the water-containing additive is 10 wt% to 20 wt%, and the anhydrite (CaSO 4 ) may be composed of 60 wt% to 70 wt%.
또한, 상기 생석회는 30 중량% 내지 40 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 무수석고(CaSO4)는 40 중량% 내지 50 중량%로 이루어질 수 있다.In addition, the quicklime is 30% to 40% by weight, the water-containing additive is 10% to 20% by weight, and the anhydrite (CaSO 4 ) may be composed of 40% to 50% by weight.
한편, 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물에 유기염이 혼합되는 단계를 더 포함할 수 있다.On the other hand, the step of mixing the organic salt in the anhydrite (CaSO 4 ) or a mixture containing the anhydrite may be further included.
이때, 상기 유기염은 숙신산나트륨(sodium succinate, Na2C4H4O4) 또는 젤라틴(gelatin) 등으로 이루어질 수 있다. 상기 유기염이 상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물에 섞이는 경우, 상기 유기염이 상기 무수석고 입자의 표면의 적어도 일부에 코팅되어 물리적으로 상기 무수석고가 물과 반응하는 것을 지연시킬 수 있다. 또한, 상기 유기염은 화학적으로도 상기 무수석고가 물과 반응하는 것을 지연시키는 역할을 하게 된다. 따라서, 본 실시예의 경우 무수석고에 젤라틴 등의 유기염을 추가함으로써 수분 흡수 속도를 조절할 수 있다. 상기 유기염을 투입하는 경우에 물에 희석하여 투입하게 되며, 대략 1% 용액(물 : 유기염 = 100 : 1)으로 희석하여 투입할 수 있다.In this case, the organic salt may be made of sodium succinate (sodium succinate, Na 2 C 4 H 4 O 4 ) or gelatin. When the organic salt is mixed with the anhydrite (CaSO 4 ) or a mixture containing the anhydrite, the organic salt is coated on at least a portion of the surface of the anhydrite particles so that the anhydrite physically reacts with water can be delayed In addition, the organic salt serves to delay the reaction of the anhydrite with water chemically. Therefore, in the present embodiment, the water absorption rate can be controlled by adding an organic salt such as gelatin to the anhydrite. When the organic salt is added, it is diluted with water, and may be diluted with an approximately 1% solution (water: organic salt = 100: 1).
또한, 상기 무수석고를 포함하는 혼합물은 건식탈황석고 또는 플라이애시로 이루어질 수 있다.In addition, the mixture containing the anhydrite may be made of dry desulfurization gypsum or fly ash.
이 경우, 상기 건식탈황석고는 코크스를 연료로 하여 생석회 성분 함량이 40 중량% 내지 50 중량%이고 무수석고가 40 중량% 내지 50 중량%인 제1형 건식탈황석고 및 유연탄을 연료로 하여 생석회 성분 함량이 10 중량% 내지 20 중량%이고 무수석고가 성분 함량이 10 중량% 내외인 제2형 건식탈황석고 중 어느 하나를 포함할 수 있다.In this case, the dry desulfurization gypsum is a type 1 dry desulfurization gypsum having a quicklime component content of 40% to 50% by weight and anhydrite of 40% to 50% by weight using coke as a fuel and a quicklime component using bituminous coal as a fuel The content is 10% to 20% by weight, and the anhydrite may include any one of type 2 dry desulfurization gypsum having a component content of about 10% by weight.
상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우 초기에 투입되는 생석회의 중량비율이 상대적으로 더 낮아질 수 있다.When the mixture containing the anhydrite is made of dry desulfurized gypsum or fly ash, the weight ratio of the quicklime to be initially added may be relatively lower.
예를 들어, 상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우, 생석회를 무수석고를 포함하는 혼합물과 수분 함유 첨가물과 혼합하는 단계에서 상기 생석회는 20 중량% 내지 30 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 건식탈황석고 또는 플라이애시는 50 중량% 내지 60 중량%로 이루어질 수 있다.For example, when the mixture containing the anhydrite is made of dry desulfurized gypsum or fly ash, in the step of mixing the quicklime with the mixture containing anhydrite and a water-containing additive, the quicklime is 20% to 30% by weight, The moisture-containing additive may be comprised of 10 wt% to 20 wt%, and the dry desulfurization gypsum or fly ash may be comprised of 50 wt% to 60 wt%.
한편, 상기 건식탈황석고 또는 상기 플라이애시의 입자를 바인딩하기 위한 유기물질을 혼합하는 단계를 더 포함할 수 있다.On the other hand, the step of mixing the organic material for binding the particles of the dry desulfurization gypsum or the fly ash may be further included.
상기 건식탈황석고를 건식탈황석고의 입자를 바인딩하기 위한 유기물질 및 상기 1차 혼합에 의한 혼합물과 2차 혼합한다. 또한, 여기서, 건식탈황석고는 플라이애시로 대체될 수도 있다.The dry desulfurization gypsum is secondarily mixed with an organic material for binding particles of the dry desulfurization gypsum and the mixture obtained by the first mixing. Also, here, the dry desulfurization gypsum may be replaced with fly ash.
특히, 유기물질은 전분, 녹말, 사탕수수 가루 또는 사탕수수액 등 천연유기물질을 포함할 수 있으며, 이 유기물질은 저품위 생석회 및 건식탈황석고(또는 플라이애시)에 포함된 총생석회량의 5 중량% 내지 20 중량% 이하의 범위에서 혼합되어야 한다.In particular, the organic material may include a natural organic material such as starch, starch, sugar cane powder or sugar cane juice, and this organic material is 5 weight of the total amount of quicklime contained in low-grade quicklime and dry desulfurized gypsum (or fly ash). % to 20% by weight or less.
한편, 이상에서는 본 발명의 바람직한 실시예에 대하여 도시하고 설명하였지만, 본 발명은 상술한 특정의 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변형실시가 가능한 것은 물론이고, 이러한 변형실시들은 본 발명의 기술적 사상이나 전망으로부터 개별적으로 이해되어져서는 안될 것이다.On the other hand, although preferred embodiments of the present invention have been illustrated and described above, the present invention is not limited to the specific embodiments described above, and the technical field to which the present invention belongs without departing from the gist of the present invention as claimed in the claims In addition, various modifications are possible by those of ordinary skill in the art, and these modifications should not be individually understood from the technical spirit or perspective of the present invention.
21: 크러셔 22-1 ~ 22-3: 호퍼
23: 스크린 24: 싸일로
25: 바인딩 유닛 26-1, 26-2: 믹서기
27: 성형장치21: crusher 22-1 to 22-3: hopper
23: screen 24: silo
25: binding units 26-1, 26-2: blender
27: molding device
Claims (24)
생석회(CaO); 및
상기 생석회의 적어도 일부와 반응시켜 급격한 발열반응을 방지하기 위한 수분 함유 첨가물;을 포함하고,
상기 생석회의 수분 흡수 속도를 조절하기 위한 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 더 포함하고, 상기 무수석고를 포함하는 혼합물은 건식탈황석고 또는 플라이애시로 이루어지며,
상기 건식탈황석고는 코크스를 연료로 하여 생석회 성분 함량이 40 중량% 내지 50 중량%이고 무수석고가 40 중량% 내지 50 중량%인 제1형 건식탈황석고 및 유연탄을 연료로 하여 생석회 성분 함량이 10 중량% 내지 20 중량%이고 무수석고의 성분 함량이 10 중량%인 제2형 건식탈황석고 중 어느 하나를 포함하며,
상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우 상기 생석회는 20 중량% 내지 30 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 건식탈황석고 또는 플라이애시는 50 중량% 내지 60 중량%로 이루어진 것을 특징으로 하는 친환경 축사 바닥재.In the eco-friendly livestock flooring,
quicklime (CaO); and
A water-containing additive for preventing a rapid exothermic reaction by reacting with at least a portion of the quicklime;
Anhydrite (CaSO4) or a mixture containing the anhydrite for controlling the water absorption rate of the quicklime is further included, and the mixture containing the anhydrite is made of dry desulfurization gypsum or fly ash,
The dry desulfurization gypsum has a quicklime component content of 40% to 50% by weight using coke as a fuel and a quicklime component content of 10 to 40% by weight to 50% by weight of anhydrite and type 1 dry desulfurization gypsum and bituminous coal as a fuel It contains any one of the type 2 dry desulfurization gypsum having a component content of 10% by weight to 20% by weight and anhydrite,
When the mixture containing the anhydrite consists of dry desulfurized gypsum or fly ash, the quicklime is 20% to 30% by weight, the water-containing additive is 10% to 20% by weight, and the dry desulfurized gypsum or fly ash is 50% by weight Eco-friendly livestock barn flooring, characterized in that it consists of weight% to 60% by weight.
상기 무수석고(CaSO4)는 제1형 무수석고, 제2형 무수석고 및 제3형 무수석고 중에 수분흡수기간에 따라 선택된 어느 하나로 이루어진 것을 특징으로 하는 친환경 축사 바닥재.According to claim 1,
The anhydrite (CaSO 4 ) is an eco-friendly barn flooring, characterized in that it is made of any one selected according to the moisture absorption period among type 1 anhydrite, type 2 anhydrite, and type 3 anhydrite.
상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물에 유기염이 더 혼합되는 것을 특징으로 하는 친환경 축사 바닥재.According to claim 1,
Eco-friendly barn flooring, characterized in that the organic salt is further mixed with the anhydrite (CaSO 4 ) or a mixture containing the anhydrite.
상기 건식탈황석고 또는 상기 플라이애시의 입자를 바인딩하기 위한 유기물질을 더 포함하고,
상기 유기물질은,
전분, 녹말, 사탕수수 중 적어도 하나를 포함하고, 상기 생석회에 포함된 생석회량과 상기 건식탈황석고 또는 플라이애시에 포함된 생석회량을 더한 총생석회량의 5 중량% 내지 20 중량%의 범위를 충족하는 것을 특징으로 하는 친환경 축사 바닥재.According to claim 1,
Further comprising an organic material for binding the particles of the dry desulfurization gypsum or the fly ash,
The organic material is
It contains at least one of starch, starch, and sugar cane, and meets the range of 5% to 20% by weight of the total amount of quicklime by adding the amount of quicklime included in the quicklime and the amount of quicklime included in the dry desulfurization gypsum or fly ash. Eco-friendly barn flooring, characterized in that.
상기 수분 함유 첨가물은,
수분 함량이 10 중량% 내지 30 중량%인 톱밥, 등겨 및 커피원두찌꺼기 중 적어도 하나를 포함하는 것을 특징으로 하는 친환경 축사 바닥재.According to claim 1,
The water-containing additive is
Eco-friendly barn flooring, characterized in that it comprises at least one of sawdust, rice bran, and coffee bean grounds having a moisture content of 10% to 30% by weight.
생석회와, 상기 생석회의 적어도 일부와 반응시켜 급격한 발열반응을 방지하기 위한 수분 함유 첨가물을 혼합하여 혼합물을 만드는 단계; 및
상기 혼합물을 성형하는 단계;를 포함하고,
상기 생석회의 수분 흡수 속도를 조절하기 위한 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물을 더 포함하고, 상기 무수석고를 포함하는 혼합물은 건식탈황석고 또는 플라이애시로 이루어지며,
상기 건식탈황석고는 코크스를 연료로 하여 생석회 성분 함량이 40 중량% 내지 50 중량%이고 무수석고가 40 중량% 내지 50 중량%인 제1형 건식탈황석고 및 유연탄을 연료로 하여 생석회 성분 함량이 10 중량% 내지 20 중량%이고 무수석고의 성분 함량이 10 중량%인 제2형 건식탈황석고 중 어느 하나를 포함하며,
상기 무수석고를 포함하는 혼합물이 건식탈황석고 또는 플라이애시로 이루어지는 경우 상기 생석회는 20 중량% 내지 30 중량%, 상기 수분 함유 첨가물은 10 중량% 내지 20 중량%, 상기 건식탈황석고 또는 플라이애시는 50 중량% 내지 60 중량%로 이루어진 것을 특징으로 하는 친환경 축사 바닥재의 제조 방법.In the method for manufacturing an eco-friendly livestock barn flooring,
preparing a mixture by mixing quicklime and a water-containing additive for preventing a rapid exothermic reaction by reacting with at least a portion of the quicklime; and
Including; molding the mixture;
Anhydrite (CaSO4) or a mixture containing the anhydrite for controlling the water absorption rate of the quicklime is further included, and the mixture containing the anhydrite is made of dry desulfurization gypsum or fly ash,
The dry desulfurization gypsum has a quicklime component content of 40% to 50% by weight using coke as a fuel and a quicklime component content of 10 to 40% by weight to 50% by weight of anhydrite and type 1 dry desulfurization gypsum and bituminous coal as a fuel It contains any one of the type 2 dry desulfurization gypsum having a component content of 10% by weight to 20% by weight and anhydrite,
When the mixture containing the anhydrite consists of dry desulfurized gypsum or fly ash, the quicklime is 20% to 30% by weight, the water-containing additive is 10% to 20% by weight, and the dry desulfurized gypsum or fly ash is 50% by weight Method of manufacturing an eco-friendly livestock barn flooring, characterized in that consisting of weight% to 60% by weight.
상기 무수석고(CaSO4)는 제1형 무수석고, 제2형 무수석고 및 제3형 무수석고 중에 수분흡수기간에 따라 선택된 어느 하나로 이루어진 것을 특징으로 하는 친환경 축사 바닥재의 제조 방법.14. The method of claim 13,
The anhydrite (CaSO 4 ) is a method of manufacturing an eco-friendly livestock barn flooring, characterized in that it is made of any one selected according to the water absorption period among type 1 anhydrite, type 2 anhydrite, and type 3 anhydrite.
상기 무수석고(CaSO4) 또는 상기 무수석고를 포함하는 혼합물에 유기염이 혼합되는 단계를 더 포함하는 것을 특징으로 하는 친환경 축사 바닥재의 제조 방법.14. The method of claim 13,
The method of manufacturing an eco-friendly livestock barn flooring, characterized in that it further comprises the step of mixing an organic salt in the anhydrite (CaSO 4 ) or a mixture containing the anhydrite.
상기 건식탈황석고 또는 상기 플라이애시의 입자를 바인딩하기 위한 유기물질을 혼합하는 단계를 더 포함하고,
상기 유기물질은,
전분, 녹말, 사탕수수 중 적어도 하나를 포함하고, 상기 생석회에 포함된 생석회량과 상기 건식탈황석고 또는 플라이애시에 포함된 생석회량을 더한 총생석회량의 5 중량% 내지 20 중량%의 범위를 충족하는 것을 특징으로 하는 친환경 축사 바닥재의 제조 방법.14. The method of claim 13,
Further comprising the step of mixing an organic material for binding the particles of the dry desulfurization gypsum or the fly ash,
The organic material is
It contains at least one of starch, starch, and sugar cane, and meets the range of 5% to 20% by weight of the total amount of quicklime by adding the amount of quicklime included in the quicklime and the amount of quicklime included in the dry desulfurization gypsum or fly ash. A method of manufacturing an eco-friendly livestock barn flooring, characterized in that
상기 수분 함유 첨가물은,
수분 함량이 10 중량% 내지 30 중량%인 톱밥, 등겨 및 커피원두 찌꺼기 중 적어도 하나를 포함하는 것을 특징으로 하는 친환경 축사 바닥재의 제조 방법.
14. The method of claim 13,
The water-containing additive is
A method of manufacturing an eco-friendly barn flooring material comprising at least one of sawdust having a moisture content of 10% to 30% by weight, rice bran, and coffee bean residues.