KR101873488B1 - Eco-Friendly Mortar Composite for Repair Comprising Function of Preventing Neutralization and Saltdamage and Constructing Methods Using Thereof - Google Patents
Eco-Friendly Mortar Composite for Repair Comprising Function of Preventing Neutralization and Saltdamage and Constructing Methods Using Thereof Download PDFInfo
- Publication number
- KR101873488B1 KR101873488B1 KR1020180014350A KR20180014350A KR101873488B1 KR 101873488 B1 KR101873488 B1 KR 101873488B1 KR 1020180014350 A KR1020180014350 A KR 1020180014350A KR 20180014350 A KR20180014350 A KR 20180014350A KR 101873488 B1 KR101873488 B1 KR 101873488B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- cement
- eco
- amount
- Prior art date
Abstract
Description
본 발명은 친환경 보수용 몰탈 조성물 및 이의 시공방법에 관한 것으로서, 보다 상세하게는 염해, 중성화방지 및 방수/방식기능을 갖는 친환경 보수용 몰탈 조성물을 피 구조물의 표면을 보호 시공하기 위한 친환경 보수용 몰탈 조성물 및 이를 이용한 시공방법에 관한 것이다.
The present invention relates to an eco-friendly repair mortar composition and a method for its application, and more particularly, to an eco-friendly repair mortar composition having functions of salting, anti-neutralization, Compositions and methods of construction using the same.
일반적으로 화학 수지를 이용한 조성물에 있어서 코팅특성을 갖도록 하기 위해서는 내마모성과 원가절감을 목적으로 무기물을 충전하지만 그 사용량은 30%이내이며, 이러한 조성물은 다량의 유기용제를 함유하고 있어서 수지 내에 무기물이 침지된 상태를 벗어나면 작업성이 없을 뿐만 아니라, 코팅제로서 제 기능을 발휘하지 못한다.Generally, in order to have a coating property in a composition using a chemical resin, an inorganic material is charged for the purpose of abrasion resistance and cost reduction, but its amount is used within 30%. Such a composition contains a large amount of organic solvent, It is not only not workable but also fails to exhibit its function as a coating agent.
특히, 콘크리트 구조물과 같은 표면이나 바탕면을 코팅하고자 할 때 그 표면이나 바탕면에 프라이머가 도포되지 아니한 상태에서는 시멘트와 같이 비중이 무거운 무기물이 저점도 코팅제에 적용될 경우 1회 도포되는 두께가 0.2mm 내외로 유기용제가 휘발되면서 경화되어 남는 고형분의 두께는 0.07mm정도의 얇은 박막층으로만 형성되게 된다. 그러므로 함침 범위를 벗어난 무기물은 결속력을 갖지 못하고 분리되어 형상을 유지할 수 없기 때문에 보호 보수 성능이 크게 저하되는 것이 심각한 문제로 지적되고 있다.In particular, when a surface such as a concrete structure is to be coated with a primer and a primer is not applied to the surface or base, when a heavy inorganic material such as cement is applied to a low viscosity coating material, The solid content remaining after curing by evaporation of the organic solvent is formed only by a thin film layer having a thickness of about 0.07 mm. Therefore, it is pointed out that it is a serious problem that the performance of the protection and maintenance is greatly deteriorated because the inorganic substance which is out of the impregnation range can not maintain the shape without holding the binding force.
지금까지 국내외에서는 전반적으로 이미 열화가 진행된 콘크리트 표면을 보수하는 재료들로서는 대부분 화학수지나 화합물을 이용한 조성물을 사용하는 경우가 많다. 국내에서 신기술로 개발된 보수제의 이용과 보수공법의 종류를 보면 스틸렌-부타디엔고무(SBR)나 라텍스를 무기물 혼용제와 혼합사용하여 도포하는 방법, 수화 응고형 분말도포제 및 코팅제를 이용한 콘크리트 보호마감 이중코팅처리 기술, 기능성 수지군의 복합과 세라믹 반응을 이용한 콘크리트 구조물의 중성화와 염해 및 화학침식 방지기술, 이소시아네이트 수지(MDI)를 이용한 콘크리트 보수 몰탈제의 제조방법 및 보수공법, 실리게이트 화합물을 이용한 표면보수공법 등이 있다. So far, most of the materials used for repairing concrete surfaces that have already undergone deterioration at home and abroad have used chemical resins or compounds. The use of repair agents and repair methods developed by the new technology in Korea is based on the application of styrene-butadiene rubber (SBR) or latex in combination with an inorganic mineral admixture, a concrete protection finish using a hydration coagulated powder coating agent and a coating agent Coating treatment technology, neutralization of concrete structure by using composite and ceramic reaction of functional resin group, prevention of salt corrosion and chemical erosion, manufacturing method and repair method of concrete repair mortar using isocyanate resin (MDI), surface using silicate compound And repair method.
그리고 최근 들어 에폭시 수용성 타입에 시멘트를 혼합하여 바탕조정제로 사용하고 우레탄 수지에 아크릴 수지를 교합시켜 중도 및 상도 코팅 공정으로 시공하는 공법이 알려져 있다.Recently, it has been known that an epoxy water-soluble type is mixed with cement to be used as a base adjusting agent, and an acrylic resin is mixed with an urethane resin to form an intermediate or top coating process.
그러나 이러한 콘크리트 표면 보호 보수를 위한 공법들은 나름대로 특성을 갖고 있으나, 시공절차가 복잡하고 진정한 보호 보수성능을 발휘하도록 한다기보다는 단순 임시처방에 그치는 보수공법에 한정되어 있으며, 도포된 표면의 수지나 화합물이 노출된 상태로 자외선이나 각종 위해가스, 산성비 등으로 인하여 노화가 급속히 진행되는 단점이 있다.However, the methods for repairing and repairing these concrete surfaces have their own characteristics, but they are limited to the repair method which is simple provisional treatment rather than making the construction procedure complicated and exhibiting true protection and repair performance. There is a disadvantage that the aging proceeds rapidly due to ultraviolet rays, various harmful gases, acid rain, etc. in the exposed state.
또한, 콘크리트 습윤 상태에서의 적응성, 콘크리트 구성물인 알칼리성과의 비결합성에 의한 접착력 저하 등을 해소할만한 뚜렷한 특성이 제안되어 있지 아니하여 개선의 여지가 많았다.In addition, there is no clear characteristic to overcome the adaptability in the wet state of concrete and the deterioration of adhesion due to the nonconformity with the alkaline concrete constituent, so there is much room for improvement.
특히, 열화된 콘크리트 표면을 다공체로 도포하였을 때에는 균일성이 확보되지 않는 문제점 등으로 인해 3회 이상 중첩도포를 필요로 하게 되고, 무엇보다도 표면 보호 보수제로서 기본적으로 요구되는 시공 후 콘크리트 본래 형상 회복이, 필요한 문제가 아직도 해소되지 않고 있다. 이러한 문제점들은 국내뿐만이 아니라 토목 건설산업개발이 활발히 이루어지고 있는 개발도상 국가들이나 선진국들 역시 제대로 해소하지 못하여 매우 고심하고 있는 문제점들이다.Particularly, when the surface of the deteriorated concrete is coated with a porous material, it is necessary to overcoat three or more times due to the problem that the uniformity can not be ensured, and the restoration of the original shape of concrete after the construction, , The necessary problems are still not solved. These problems are problems not only in Korea but also in developed countries and developed countries where civil engineering construction industry is actively developing.
이에, 전술한 문제점을 극복하기 위하여 대한민국특허등록 제10-1060140호에는 에폭시 수지, 반응성 희석제, 응결제, 유화제 및 물을 포함하는 에폭시 베이스 수지성분; 및 폴리옥시프로필렌디아민, 톨루엔, 타이타늄옥사이드, 가라마이트, 안료 및 물을 포함하는 경화성분으로 이루어진 친환경 표면 보호제가 개시되어 있다.
In order to overcome the above-mentioned problems, Korean Patent Registration No. 10-1060140 discloses an epoxy resin composition comprising an epoxy resin, a reactive diluent, a coagulant, an emulsifier and water; And a curing component comprising polyoxypropylene diamine, toluene, titanium oxide, kaolinite, pigment and water.
본 발명은 전술한 문제점을 극복하기 위해 창출된 것으로서, 코팅층을 형성하기 위한 대상표면, 특정적으로 콘크리트 구조물 대상표면에 물리/화학적으로 안정적인 코팅층을 형성하여, 녹방지성, 내식성, 내오염성, 내마모성, 내화학성, 염해방지 및/또는 중성화방지 등을 향상시킬 수 있도록 하는 친환경 보수용 몰탈 조성물을 제공하고자 한다.
The present invention has been made in order to overcome the above-described problems, and it is an object of the present invention to provide a coating layer which is physically / chemically stable on a target surface for forming a coating layer and specifically on a target surface of a concrete structure to provide a rust- , Chemical resistance, prevention of salt corrosion and / or prevention of neutralization, and the like.
본 발명은The present invention
시멘트 100중량부를 기준으로, Based on 100 parts by weight of cement,
칼슘설포알루미네이트 20 내지 40중량부;20 to 40 parts by weight of calcium sulfoaluminate;
실리카 퓸 10 내지 50중량부;10 to 50 parts by weight of silica fume;
메틸메타아크릴레이트 10 내지 50중량부;10 to 50 parts by weight of methyl methacrylate;
옥틸트리에톡시실란 1 내지 10중량부;1 to 10 parts by weight of octyltriethoxysilane;
나노세라믹 입자 5 내지 20중량부;5 to 20 parts by weight of nano-ceramic particles;
파이버 2 내지 20중량부;2 to 20 parts by weight of fibers;
구아검 1 내지 10중량부;1 to 10 parts by weight of guar gum;
박리방리제 5 내지 30중량부;5 to 30 parts by weight of a peeling agent;
부착증진제 1 내지 10중량부;1 to 10 parts by weight of an adhesion promoter;
증점제 3 내지 20중량부;3 to 20 parts by weight of a thickener;
가소제 1 내지 10중량부;1 to 10 parts by weight of a plasticizer;
소포제 0.5 내지 5중량부; 및 0.5 to 5 parts by weight of an antifoaming agent; And
감수제 0.01 내지 10중량부를 포함하는 친환경 보수용 몰탈 조성물을 제공한다.
And 0.01 to 10 parts by weight of a water reducing agent.
또한, 본 발명은 In addition,
콘크리트 구조물 표면의 요철과 레이탄스를 제거하는 단계;Removing the concavities and convexities of the surface of the concrete structure;
상기 콘크리트 구조물 표면의 이물질을 제거하기 위한 고압 세척단계;A high-pressure washing step for removing foreign matters on the surface of the concrete structure;
상기 콘크리트 구조물의 표면상에 퍼티재를 도포하는 바탕 처리단계;A pretreatment step of applying a putty material on the surface of the concrete structure;
상기 콘크리트 구조물의 표면상에, 시멘트 100중량부를 기준으로, 칼슘설포알루미네이트 20 내지 40중량부, 실리카 퓸 10 내지 50중량부, 메틸메타아크릴레이트 10 내지 50중량부, 옥틸트리에톡시실란 1 내지 10중량부, 나노세라믹 입자 5 내지 20중량부, 파이버 2 내지 20중량부, 구아검 1 내지 10중량부, 박리방리제 5 내지 30중량부, 부착증진제 1 내지 10중량부, 증점제 3 내지 20중량부, 가소제 1 내지 10중량부, 소포제 0.5 내지 5중량부, 및 감수제 0.01 내지 10중량부를 포함하는 친환경 보수용 몰탈 조성물을 1차적으로 도포하여 하도층을 형성한 후 1차 양생하는 단계;20 to 40 parts by weight of calcium sulfoaluminate, 10 to 50 parts by weight of silica fume, 10 to 50 parts by weight of methyl methacrylate, 1 to 50 parts by weight of octyltriethoxysilane based on 100 parts by weight of the cement, 5 to 20 parts by weight of nanoceramics, 2 to 20 parts by weight of fibers, 1 to 10 parts by weight of guar gum, 5 to 30 parts by weight of a peeling agent, 1 to 10 parts by weight of an adhesion promoter, 3 to 20 parts by weight of a thickener 1 to 10 parts by weight of a plasticizer, 0.5 to 5 parts by weight of an antifoaming agent, and 0.01 to 10 parts by weight of a water reducing agent is firstly applied to form a primer layer, followed by primary curing;
상기 하도층의 표면상에 상기 하도층과 동일 성분의 친환경 보수용 몰탈 조성물을 2차적으로 도포하여 중도층을 형성한후 2차 양생하는 단계; 및Applying an eco-friendly repair mortar composition having the same composition as that of the undercoating layer to the surface of the undercoating layer to form an intermediate layer and then curing the second coating; And
상기 중도층의 표면상에 상기 중도층과 동일 성분의 친환경 보수용 몰탈 조성물을 3차적으로 도포하여 상도층을 형성한 후 3차 양생하는 단계를 포함하는 친환경 보수용 몰탈 조성물의 시공방법을 제공한다.
A third step of applying an eco-friendly repair mortar composition having the same composition as that of the middle layer to the surface of the intermediate layer to form a top layer and then curing the third layer, thereby providing an eco-friendly repair mortar composition construction method .
본 발명에 따른 친환경 보수용 몰탈 조성물은 유해물질을 배출하지 않아 친환경적이면서도 코팅층을 형성하기 위한 대상표면에 물리적, 화학적으로 안정적인 코팅층을 형성하여, 녹방지성, 내식성, 내오염성, 내마모성, 내화학성, 염해방지 및/또는 중성화방지 등을 향상시킬 수 있도록 하는 효과가 있다.The mortar composition for eco-friendly repair according to the present invention forms a coating layer that is physically and chemically stable on the surface of a target for forming a coating layer while being eco-friendly because it does not emit harmful substances and is excellent in rust resistance, corrosion resistance, stain resistance, abrasion resistance, Prevention of salt damage and / or prevention of neutralization can be improved.
이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.
한 가지 관점에서, 본 발명은 시멘트 100중량부를 기준으로, 칼슘설포알루미네이트 20 내지 40중량부; 실리카 퓸 10 내지 50중량부; 메틸메타아크릴레이트 10 내지 50중량부; 옥틸트리에톡시실란 1 내지 10중량부; 나노세라믹 입자 5 내지 20중량부; 파이버 2 내지 20중량부; 구아검 1 내지 10중량부; 박리방리제 5 내지 30중량부; 부착증진제 1 내지 10중량부; 증점제 3 내지 20중량부; 가소제 1 내지 10중량부; 소포제 0.5 내지 5중량부; 및 감수제 0.01 내지 10중량부를 포함하는 친환경 보수용 몰탈 조성물을 제공한다.In one aspect, the present invention relates to a cement composition comprising, based on 100 parts by weight of cement, 20 to 40 parts by weight of calcium sulfoaluminate; 10 to 50 parts by weight of silica fume; 10 to 50 parts by weight of methyl methacrylate; 1 to 10 parts by weight of octyltriethoxysilane; 5 to 20 parts by weight of nano-ceramic particles; 2 to 20 parts by weight of fibers; 1 to 10 parts by weight of guar gum; 5 to 30 parts by weight of a peeling agent; 1 to 10 parts by weight of an adhesion promoter; 3 to 20 parts by weight of a thickener; 1 to 10 parts by weight of a plasticizer; 0.5 to 5 parts by weight of an antifoaming agent; And 0.01 to 10 parts by weight of a water reducing agent.
다른 관점에서, 본 발명은 콘크리트 구조물 표면의 요철과 레이탄스를 제거하는 단계; 상기 콘크리트 구조물 표면의 이물질을 제거하기 위한 고압 세척단계; 상기 콘크리트 구조물의 표면상에 퍼티재를 도포하는 바탕 처리단계; 상기 콘크리트 구조물의 표면상에, 시멘트 100중량부를 기준으로, 칼슘설포알루미네이트 20 내지 40중량부, 실리카 퓸 10 내지 50중량부, 메틸메타아크릴레이트 10 내지 50중량부, 옥틸트리에톡시실란 1 내지 10중량부, 나노세라믹 입자 5 내지 20중량부, 파이버 2 내지 20중량부, 구아검 1 내지 10중량부, 박리방리제 5 내지 30중량부, 부착증진제 1 내지 10중량부, 증점제 3 내지 20중량부, 가소제 1 내지 10중량부, 소포제 0.5 내지 5중량부, 및 감수제 0.01 내지 10중량부를 포함하는 친환경 보수용 몰탈 조성물을 1차적으로 도포하여 하도층을 형성한 후 1차 양생하는 단계; 상기 하도층의 표면상에 상기 하도층과 동일 성분의 친환경 보수용 몰탈 조성물을 2차적으로 도포하여 중도층을 형성한후 2차 양생하는 단계; 및 상기 중도층의 표면상에 상기 중도층과 동일 성분의 친환경 보수용 몰탈 조성물을 3차적으로 도포하여 상도층을 형성한 후 3차 양생하는 단계를 포함하는 친환경 보수용 몰탈 조성물의 시공방법을 제공한다.
In another aspect, the present invention provides a method of manufacturing a concrete structure, the method comprising: removing concavity and convexity on a surface of a concrete structure; A high-pressure washing step for removing foreign matters on the surface of the concrete structure; A pretreatment step of applying a putty material on the surface of the concrete structure; 20 to 40 parts by weight of calcium sulfoaluminate, 10 to 50 parts by weight of silica fume, 10 to 50 parts by weight of methyl methacrylate, 1 to 50 parts by weight of octyltriethoxysilane based on 100 parts by weight of the cement, 5 to 20 parts by weight of nanoceramics, 2 to 20 parts by weight of fibers, 1 to 10 parts by weight of guar gum, 5 to 30 parts by weight of a peeling agent, 1 to 10 parts by weight of an adhesion promoter, 3 to 20 parts by weight of a thickener 1 to 10 parts by weight of a plasticizer, 0.5 to 5 parts by weight of an antifoaming agent, and 0.01 to 10 parts by weight of a water reducing agent is firstly applied to form a primer layer, followed by primary curing; Applying an eco-friendly repair mortar composition having the same composition as that of the undercoating layer to the surface of the undercoating layer to form an intermediate layer and then curing the second coating; And a third step of applying an eco-friendly repair mortar composition having the same composition as that of the intermediate layer on the surface of the intermediate layer to form an upper layer and then curing the third layer. do.
본 발명에 따른 친환경 보수용 몰탈 조성물은 코팅층을 형성하고자 하는 대상표면, 예를 들면 콘크리트 구조물에 코팅층을 형성시킴으로써 콘크리트의 염해방지와 중성화를 방지하기 제공하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 몰탈 조성물이라면 특별히 한정되지 않는다.The mortar composition for eco-friendly repair according to the present invention is to provide a coating layer on a surface of an object to be formed, for example, a concrete structure to prevent the prevention of salt damage and neutralization of the concrete. Is not particularly limited.
특히, 본 발명에 따른 몰탈 조성물, 특정적으로 친환경 보수용 몰탈 조성물은 콘크리트 중성화 방지, 염해방지 등과 콘크리트 수밀성 증가로 인한 표면강화, 내구성, 부착력, 내오염성 등이 우수한 코팅층을 형성시킬 수 있으므로, 콘크리트 건축물 내외벽 및/또는 옥상 등에 적용될 수 있다.In particular, the mortar composition according to the present invention, particularly the eco-friendly mortar composition for repairing, can form a coating layer having excellent surface durability, durability, adhesion force and stain resistance due to prevention of concrete neutralization, Exterior walls of buildings and / or rooftops, and the like.
본 발명에 따른 시멘트는 당업계에서 통상적으로 사용되는 시멘트라면 특별히 한정되지 않지만, 바람직하게는 일반 포틀랜드 시멘트 또는 고로슬래그시멘트, 초미분말시멘트, 초속경 시멘트 등의 특수 시멘트 등을 사용할 수 있다.The cement according to the present invention is not particularly limited as long as it is a cement conventionally used in the art, but it is preferable to use special Portland cement, blast furnace slag cement, ultrafine powder cement, special cement such as ultra low speed cement and the like.
상기 시멘트의 바람직한 분말도는 3,200 내지 6,500cm2/g인 것이 좋다.The preferred powder of the cement is preferably 3,200 to 6,500 cm 2 / g.
본 발명에 따른 친환경 보수용 몰탈 조성물을 구성하는 시멘트 외 나머지 성분들의 함량은 시멘트 100중량부를 기준으로 한다.The content of the remaining components other than cement constituting the mortar composition for eco-friendly repair according to the present invention is based on 100 parts by weight of cement.
본 발명에 따른 칼슘설포알루미네이트(Calcium Sulfo Aluminate)는 수축보상, 고강도, 예를 들면 높은 압축강도와 휨강도 및 초속경을 부여하기 위한 물질로서, 이러한 목적을 갖는 칼슘설포알루미네이트라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 시멘트 100중량부 기준으로 20 내지 40중량부인 것을 추천한다.The calcium sulfoaluminate according to the present invention is a material for imparting shrinkage compensation, high strength, for example, high compressive strength, bending strength and ultrahigh speed, and any of calcium sulfoaluminate having such a purpose can be used And it is recommended that the amount thereof is 20 to 40 parts by weight based on 100 parts by weight of cement.
여기서, 상기 칼슘설포알루미네이트의 사용량이 20중량부 미만이면 경화속도가 감소하고 40중량부 이상인 경우 체적이 팽창되는 문제점이 발생할 수 있다.If the calcium sulfoaluminate is used in an amount less than 20 parts by weight, the curing rate is decreased. If the amount is more than 40 parts by weight, the volume of the calcium sulfoaluminate may expand.
한편, 상기 칼슘설포알루미네이트는 물과 접촉할 경우 순식간에 반응하여 에트린가이트(Ettringite) 수화물을 생성함으로써, 몰탈 조성물의 압축강도를 수분 내지 수 시간 안에 얻을 수 있도록 한다.On the other hand, when the calcium sulfoaluminate comes into contact with water, the calcium sulfoaluminate reacts instantaneously to generate an ettringite hydrate, so that the compressive strength of the mortar composition can be obtained within several minutes to several hours.
이때, 보다 신속한 수화반응을 위해 초미립 비정질 칼슘설포알루미네이트를 사용할 수도 있다.At this time, ultrafine amorphous calcium sulfoaluminate may be used for a quick hydration reaction.
상기 수화반응성 증대를 위해 사용되는 초미립 비정질 칼슘설포알루미네이트의 블레인 분말도는 5,000 내지 8,000㎠/g 정도인 것이 좋다.The blast powder of the ultrafine amorphous calcium sulfoaluminate used for increasing hydration reactivity is preferably about 5,000 to 8,000 cm 2 / g.
특정 양태로서, 본 발명에 따른 칼슘설포알루미네이트는 칼슘설포알루미네이트 100중량% 기준으로, 28 내지 62중량%인 압연종말슬러지와, 19 내지 52중량%인 백운석슬러지와, 9 내지 20중량%인 부산석고가 포함되도록 구성되고, 상기 혼합물의 입도가 88㎛, 잔분이 5 내지 20중량%로 분쇄되어 이루어질 수 있다.In a particular embodiment, the calcium sulfoaluminate according to the present invention is a calcium sulfoaluminate comprising, based on 100 weight% of calcium sulfoaluminate, 28 to 62 wt% rolled end sludge, 19 to 52 wt% dolomite sludge, 9 to 20 wt% And gypsum gypsum, and the mixture has a particle size of 88 mu m and a balance of 5 to 20 wt%.
이후에, 상기 혼합물을 소성로에서 1,000 내지 1,300℃의 소성온도로 1시간 이상 유지한 후 공냉시켜, 칼슘설포알루미네이트를 제조하게 된다. 이때, 소성온도가 낮거나, 백운석슬러지의 함량이 높은 경우에는 미반응 석회의 양이 많아져 팽창성을 나타내므로 붕괴, 파괴의 염려가 있으며, 소성온도가 높거나 석회석 배합량이 적어도 칼슘설포알루미네이트의 생산이 적어져 소기의 목적을 달성할 수 없다.Thereafter, the mixture is maintained at a firing temperature of 1,000 to 1,300 DEG C for at least one hour in a firing furnace, followed by air cooling to produce calcium sulfoaluminate. At this time, when the calcination temperature is low or the content of dolomite sludge is high, the amount of unreacted lime is increased to cause expansion, so there is a risk of collapse and destruction. When the calcination temperature is high or the amount of limestone is at least calcium sulphoaluminate The production is small and the desired purpose can not be achieved.
본 발명에 따른 실리카 퓸은 친환경 보수용 몰탈 조성물의 압축강도 등을 향상시키기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 실리카 퓸이라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 시멘트 100중량부를 기준으로 10 내지 50중량부를 추천한다.The silica fume according to the present invention is for improving the compressive strength and the like of the mortar composition for eco-friendly repair. Any silica fume commonly used in the art may be used for this purpose. 10 to 50 parts by weight is recommended.
이때, 상기 실리카 퓸은 지르코늄 실리카 퓸을 포함할 수 있다.At this time, the silica fume may include zirconium silica fume.
상기 지르코늄 실리카 퓸은 지르코니아의 제조시 발생하는 부산물로서, 3 내지 5중량%의 산화지르코늄을 포함하고, 200 내지 300kg/m3의 단위용적중량을 가지며, 100,000 내지 150,000cm2/g의 분말도와 0.3 내지 1마이크로미터의 입자크기를 갖는 것이 바람직하다.The zirconium silica fume is a by-product generated in the production of zirconia, which comprises 3 to 5% by weight of zirconium oxide, has a unit volume weight of 200 to 300 kg / m 3 , a powder of 100,000 to 150,000 cm 2 / g, Lt; RTI ID = 0.0 > micrometer. ≪ / RTI >
당업계에서 통상적으로 사용되는 실리카 퓸은 무정형 이산화규소로서, 그 입자크기가 시멘트 입자크기 보다 작아 몰탈 조성물 등에 첨가하면 점성이 증가하고 높은 압축 강도를 얻을 수 있지만, 상기 지르코늄 실리카 퓸은 입자크기가 커서 시멘트 입자사이에 잘 분산되어 점성을 낮추고 유동성을 향상시킬 수 있다.Silica fume, which is commonly used in the art, is amorphous silicon dioxide, and its particle size is smaller than the cement particle size. When added to a mortar composition or the like, the viscosity increases and a high compressive strength can be obtained. However, the zirconium silica fume has a large particle size It can be dispersed well between the cement particles to lower the viscosity and improve the fluidity.
또한, 상기 지르코늄 실리카 퓸은 고온에서 생성되어 포졸란 활성이 우수한 비정질 상태이며 산화규소 함량이 높아 강도 증가에 유리한 점이 있다.The zirconium silica fumarate is an amorphous zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium
이에, 본 발명에 따른 실리카 퓸은 당업계에서 통상적으로 사용되는 실리카 퓸, 예를 들면 무정형 이산화규소 및 지르코늄 실리카 퓸을 혼합하여 사용 가능하며, 이러한 경우 지르코늄 실리카 퓸은 전체 실리카 퓸의 중량 기준으로 20 내지 50중량부를 사용하는 것이 좋다.Thus, the silica fume according to the present invention can be used by mixing silica fumes commonly used in the art, such as amorphous silicon dioxide and zirconium silica fume. In this case, the zirconium silica fume may be used in an amount of 20 To 50 parts by weight.
본 발명에 따른 메틸메타아크릴레이트(MMA: Methyl MethAcrylate)는 우수한 접착력을 갖도록 하는 동시에, 우수한 바인더 물성 및 기계적 물성을 유지하여 시공 후 신속한 경화를 진행하여도 크랙 및 탈락현상을 현저하게 개선될 수 있도록 하기 위한 것이다.Methyl methacrylate (MMA) according to the present invention has excellent adhesive strength and maintains excellent binder physical properties and mechanical properties so that cracks and dropouts can be remarkably improved even after rapid curing after application .
바람직한 메틸메타아크릴레이트의 사용량은 시멘트 100중량부 기준으로 10 내지 50중량부인 것을 추천한다.It is recommended that the preferred amount of methyl methacrylate be 10 to 50 parts by weight based on 100 parts by weight of cement.
여기서, 상기 메틸메타아크릴레이트는 점도가 10 내지 1,000cps인 저점도 메틸메타크릴레이트(MMA) 수지 49 내지 70중량%와, 점도가 2,000 내지 20,000cps인 고점도 메틸메타크릴레이트(MMA) 20 내지 50중량%를 혼합하여 얻어지는 메틸메타크릴레이트 혼합물에 SIS(stylene isoprene stylene), SBR(stylene butadiene rubber), SBS(stylene butadiene stylene) 중에서 선택된 하나 이상의 혼합물 1 내지 10중량%를 혼합한 변성 메틸메타아크릴레이트를 사용할 수도 있다.Wherein the methyl methacrylate comprises 49 to 70% by weight of a low viscosity methyl methacrylate (MMA) resin having a viscosity of 10 to 1,000 cps, 20 to 50% of high viscosity methyl methacrylate (MMA) having a viscosity of 2,000 to 20,000 cps, And 1 to 10% by weight of a mixture of at least one selected from styrene isoprene styrene (SIS), styrene butadiene rubber (SBR), and styrene butadiene styrene (SBS) is mixed with a methyl methacrylate mixture obtained by mixing ethylene / May be used.
이때, 상기 SIS, SBR 및/또는 SBS의 함량이 1중량% 미만인 경우에는 투입시에 내충격성 저하로 인한 크랙이 발생할 수 있고, 10중량%를 초과하는 경우에는 변성 메틸메타크릴레이트 수지의 점도상승으로 인하여 작업성에 문제가 발생될 수 있기 때문에 바람직하지 못하다.When the content of SIS, SBR and / or SBS is less than 1% by weight, cracks may occur due to lowering of impact resistance at the time of charging. When the content exceeds 10% by weight, the viscosity of the modified methyl methacrylate resin Which may cause problems in workability.
본 발명에 따른 옥틸트리에톡시실란은 친환경 보수용 몰탈 조성물의 접착성을 향상시킨다.The octyltriethoxysilane according to the present invention improves the adhesion of the mortar composition for eco-friendly repair.
상기 옥틸트리에톡시실란은 단량체 형태로 사용 가능하며, 상기 단량체의 분자량은 특별히 한정되는 것은 아니지만, 바람직하게는 150 내지 450Da인 것이 좋고, 그 사용량은 시멘트 100중량부를 기준으로 1 내지 10중량부인 것을 추천한다.The octyltriethoxysilane can be used in the form of a monomer. The molecular weight of the monomer is not particularly limited, but is preferably 150 to 450 Da, and the amount of the octyltriethoxysilane used is 1 to 10 parts by weight based on 100 parts by weight of cement I recommend you.
본 발명에 따른 나노세라믹 입자는 몰탈 조성물, 특정적으로 친환경 보수용 몰탈 조성물의 시공시 표면으로 부상하여 치밀하고 경도가 높은 표면을 형성하기 때문에, 수증기와 기타 기체, 액체의 투과를 방지함은 물론, 내습성, 내구성, 내후성, 내충격성, 내약품성이 향상된다.The nanoceramic particles according to the present invention float on the surface during the construction of the mortar composition, specifically the eco-friendly mortar composition for maintenance, thereby forming a dense and hard surface, thereby preventing permeation of water vapor and other gases and liquids , Moisture resistance, durability, weather resistance, impact resistance and chemical resistance are improved.
상기 나노세라믹 입자의 사용량은 시멘트 100중량부 기준으로 5 내지 20중량부인 것이 좋다.The amount of the nanoceramic particles used is preferably 5 to 20 parts by weight based on 100 parts by weight of cement.
바람직한 나노세라믹 입자는 실리콘카바이드, 알루미나, 실리카, 지르코니아-실리카, ZnO, TiO2 및/또는 CaCO3가 포함된다.Preferred nanoceramic particles include silicon carbide, alumina, silica, zirconia-silica, ZnO, TiO 2 and / or CaCO 3 .
이들 세라믹입자는 평균 입경이 나노 범위인 것이 바람직한데, 구체적으로 상기 실리콘카바이드의 평균 입경은 300 내지 500nm, 상기 알루미나의 평균 입경은 500 내지 1000nm, 상기 실리카의 평균 입경은 700 내지 1500nm, 상기 지르코니아-실리카의 평균 입경은 500 내지 1000nm, 상기 ZnO의 평균 입경은 500 내지 1000nm, 상기 TiO2의 평균 입경은 100 내지 300nm, 그리고 CaCO3의 평균 입경은 500 내지 1000nm인 것이 바람직하다.Preferably, the average particle size of the ceramic particles is in the range of 300 to 500 nm, the average particle size of the alumina is 500 to 1000 nm, the average particle size of the silica is 700 to 1500 nm, the zirconia- It is preferable that the average particle size of silica is 500 to 1000 nm, the average particle size of ZnO is 500 to 1000 nm, the average particle size of TiO 2 is 100 to 300 nm, and the average particle size of CaCO 3 is 500 to 1000 nm.
이 중에서도 실리콘카바이드는 천연광물로 존재하지 않으므로 인공적으로 합성하며, 고온에서의 화학적 안정성 및 내식성이 뛰어나고 높은 경도를 갖는다. Among them, silicon carbide does not exist as natural minerals, so it is synthesized artificially, has excellent chemical stability and corrosion resistance at high temperature, and has high hardness.
본 발명에 따른 파이버는 보수용 몰탈 조성물로 형성된 코팅층의 종-횡 방향으로 가해지는 응력에 의한 인장력 및/또는 경량성 등을 제공하기 위한 것으로서, 이러한 목적을 갖는 파이버라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 석면, 암면, 폴리프로필렌, 폴리에스터, 유리섬유, 천연 셀룰로오즈 섬유 및 광물질섬유 중 선택된 어느 하나 이상의 혼합물을 사용하는 것이 좋고, 그 사용량은 시멘트 100중량부 기준으로 2 내지 20중량부인 것이 좋다.The fiber according to the present invention is intended to provide a tensile force and / or light weight due to the stress applied in the longitudinal-transverse direction of the coating layer formed of the repair mortar composition, and any fiber having such a purpose may be used , Preferably a mixture of at least one selected from asbestos, rock wool, polypropylene, polyester, glass fiber, natural cellulose fiber and mineral fiber is preferably used and the amount thereof is 2 to 20 parts by weight based on 100 parts by weight of cement good.
본 발명에 따른 구아검은 보수용 몰탈 조성물의 구성성분을 장시간 동안 안정적으로 보관하기 위한 것으로서, 이러한 목적을 위한 당업계의 통상적인 구아검이라면 어떠한 것을 사용하여도 무방하다.The mortar composition for guar black repair according to the present invention is used to stably store the constituents of the mortar composition for a long period of time. Any guar gum that is conventional in the art for this purpose may be used.
바람직한 구아검의 사용량은 시멘트 100중량부 기준으로 1 내지 10중량부인 것이 좋다.Preferably, the amount of guar gum used is 1 to 10 parts by weight based on 100 parts by weight of cement.
본 발명에 따른 박리방지제는 친환경 보수용 몰탈 조성물이 시공 대상면으로부터 쉽게 박리되는 것을 방지하기 위한 것으로서, 이러한 목적을 갖는 박리방지제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 폴리인산계, 아민계, 또는 인산 에스테르계 박리방지제를 사용하는 것이 좋다.The anti-peeling agent according to the present invention is intended to prevent the eco-friendly repairing mortar composition from being easily peeled off from the surface to be applied. Any anti-peeling agent having such a purpose may be used, , Or a phosphoric ester-based anti-peeling agent.
특정적으로, 상기 박리방지제는 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제; 산가가 10 ㎎KOH/g 이하이고, 총 아민가가 140 내지 400㎎HCl/g인 아민계 박리방지제일 수 있다.Specifically, the anti-peeling agent is a liquid phase anti-peeling agent having a specific gravity of 1.0 or more and a viscosity at 60 DEG C of 110 cPs; The acid value is 10 mgKOH / g or less, and the total amine value is 140 to 400 mg HCl / g.
바람직한 박리방지제의 사용량은 시멘트 100중량부 기준으로 5 내지 30중량부인 것을 추천한다. The amount of the anti-peeling agent is preferably 5 to 30 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 부착증진제는 친환경 보수용 몰탈 조성물이 코팅층을 형성하기 위한 대상표면의 균열부 등에 충진될 경우 보다 용이하게 접착될 수 있도록 하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 부착증진제라면 어떠한 것을 사용하여도 무방하다.The adhesion-promoting agent according to the present invention is intended to make it easier to bond an eco-friendly repair mortar composition to a cracked portion of a target surface for forming a coating layer, and a conventional adhesion promoter Anything may be used.
바람직한 부착증진제로는 아크릴 포스페이트계 부착 증진제, 예를 들면 하이드록시 에틸 아크릴로일 포스페이트, 하이드록시 에틸 메타 아크릴레이트 포스페이트 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 그 사용량은 시멘트 100중량부 기준으로 1 내지 10중량부인 것을 추천한다.As a preferable adhesion promoter, it is preferable to use an acrylate-based adhesion promoter, for example, hydroxyethyl acryloyl phosphate, hydroxyethyl methacrylate phosphate or a mixture of at least one selected from these, It is recommended that the amount is 1 to 10 parts by weight.
본 발명에 따른 증점제는 친환경 보수용 몰탈 조성물의 점도를 조절하여 조성물의 사용을 용이하게 하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 증점제라면 특별히 한정되지 않지만, 바람직하게는 하이드록시 에틸 셀룰로오스(HydroxyEthyl Cellulose), 소수성 우레탄변성계 증점제 또는 이들의 혼합물을 사용하는 것을 추천한다.The thickener according to the present invention is used to adjust the viscosity of the mortar composition for eco-friendly repair to facilitate the use of the composition. For this purpose, the thickener commonly used in the art is not particularly limited, It is recommended to use cellulose (HydroxyEthyl Cellulose), a hydrophobic urethane modifier thickener or a mixture thereof.
상기 증점제의 사용량은 시멘트 100중량부를 기준으로 3 내지 20중량부인 것이 바람직하다.The amount of the thickener is preferably 3 to 20 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 가소제는 친환경 보수용 몰탈 조성물을 구성하는 구성성분들 간의 혼합을 원활하게 수행할 수 있도록 한다.The plasticizer according to the present invention makes it possible to smoothly mix the components constituting the mortar composition for eco-friendly repair.
바람직한 가소제는 테레프탈산 금속염, 스테아린산 금속염, 석유수지, 저분자량 폴리에틸렌 및 저분자량 폴리아미드로 이루어진 군으로부터 선택되는 것이 좋고, 그 사용량은 시멘트 100중량부를 기준으로 1 내지 10중량부인 것이 좋다.The preferred plasticizer is preferably selected from the group consisting of terephthalic acid metal salt, stearic acid metal salt, petroleum resin, low molecular weight polyethylene and low molecular weight polyamide, and the amount thereof is preferably 1 to 10 parts by weight based on 100 parts by weight of cement.
본 발명에 따른 소포제는 연행공기의 발생으로 인한 공기량의 증가를 감소시키기 위한 것이다.The antifoaming agent according to the present invention is intended to reduce an increase in the amount of air due to the generation of entrained air.
바람직한 소포제의 사용량은 시멘트 100중량부를 기준으로 0.5 내지 5중량부를 사용하는 것을 추천한다.It is recommended that 0.5 to 5 parts by weight of a preferred defoaming agent is used based on 100 parts by weight of cement.
바람직한 소포제로는 등유, 파라핀, 미네랄오일, 에탄올합성오일 등과 같은 광유계 소포제, 동식물유, 참기름, 피마자유와 이들의 알킬렌옥사이드 부가물 등과 같은 유지계 소포제, 올레인산, 스테아린산과 이들의 알킬렌옥사이드 부가물 등과 간은 지방산계 소포제, 글리세린모노리시놀레이트, 알케닐호박산 유동체, 솔비톨모노라울에이트, 솔비톨트리올레이트, 천연 왁스 등과 같은 지방산 에스테르계 소포제, 폴리옥시알킬렌류, (폴리)옥시알킬에테르류, 아세틸렌에테르류, (폴리)옥시알킬렌알킬인산에스테르류, (폴리)옥시알킬렌알킬아민류,(폴리)옥시알킬렌아미드 등과 같은 옥시알킬렌계 소포제, 옥틸알콜, 헥사데실알콜, 아세틸렌알콜, 글리콜류 등과 같은 알콜계 소포제, 아크릴레이트폴리아민 등과 같은 아미드계 소포제, 인산트리부틸, 나트륨옥틸포스페이트 등과 같은 인산에스테르계 소포제, 알루미늄스테아레이트, 칼슘올레이트 등과 같은 금속비누계 소포제, 디메틸실리콘유, 실리콘 페이슷, 실리콘 에멀젼, 유기변성 폴리실록산(디메틸폴리실록산 등의 폴리오르가노실록산). 플루오로실리콘유 등과 같은 실리콘계 소포제로 이루어진 군에서 선택되는 어느 하나 이상이 사용될 수 있으나, 이에 제한되는 것은 아니다. Preferred defoaming agents include mineral oil defoaming agents such as kerosene, paraffin, mineral oil and ethanol synthetic oil, retention defoaming agents such as animal and vegetable oils, sesame oil, castor oil and their alkylene oxide adducts, oleic acid, stearic acid and their alkylene oxides Fatty acid ester defoaming agents such as glycerin monolysinolate, alkenyl succinic acid liquid, sorbitol monolaurate, sorbitol trioleate, and natural wax, polyoxyalkylene, (poly) oxyalkyl ether Oxyalkylene antifoaming agents such as (poly) oxyalkylene alkylphosphoric acid esters, (poly) oxyalkylene alkylamines and (poly) oxyalkylene amides, octyl alcohol, hexadecyl alcohol, acetylene alcohol, Alcohol-based defoaming agents such as glycols, amide-based defoaming agents such as acrylate polyamines, tributyl phosphate, Octyl phosphoric acid ester base defoaming agents, such as phosphate, aluminum stearate, calcium oleate (polyorganosiloxanes such as dimethyl polysiloxane), metal soap-based defoaming agent, dimethyl silicone oil, silicone, pay seut, silicone emulsions, organic modified polysiloxanes such as. And silicone-based antifoaming agents such as fluorosilicone oil, etc., but is not limited thereto.
본 발명에 따른 감수제는 보수용 몰탈 조성물의 시공시 몰탈 조성물 속에 있는 작은 공기 거품을 고르게 하기 위하여 사용되는 것으로서, 거품을 일으키는 성질이 좋아, 콘크리트 중에 작은 기포를 고르게 발생시켜 내동결 융해성, 내식성, 내구성 등을 개선한다.The water reducing agent according to the present invention is used to uniformly disperse small air bubbles in the mortar composition during the construction of the repair mortar composition and has good properties of causing bubbles. Therefore, small bubbles are uniformly generated in the concrete to improve the freezing and thawing resistance, Durability and the like are improved.
특히, 상기 감수제는 미리 믹싱된 베이스에 첨가하여 이것을 교반함으로써 더 부드럽게 하며, 품질을 저하시키지 않고 시공성을 개선할 목적으로 이용된다.Particularly, the water reducing agent is added to a previously mixed base to make it smoother by stirring it, and is used for the purpose of improving the workability without deteriorating the quality.
더욱이, 상기 감수제는 몰탈 조성물의 유동성을 좋게 하여 부어 넣기 작업을 용이하게 하고, 굳은 몰탈 조성물의 열전도율을 저하시키며, 수밀성을 향상시키는 등 2차적인 효과도 있다. Furthermore, the water reducing agent has a secondary effect such as facilitating the pouring work by improving the flowability of the mortar composition, lowering the thermal conductivity of the hard mortar composition, and improving the watertightness.
이때, 몰탈 조성물에 사용되는 감수제의 감수율은 일반적으로 10 내지 15%정도이나 그 중 감수율이 20 내지 30%인 것을 본 발명에서는 고성능 감수제라 통칭한다.At this time, the water reducing agent used in the mortar composition generally has a water reducing rate of about 10 to 15%, but a water reducing rate of 20 to 30% is generally referred to as a high-performance water reducing agent in the present invention.
바람직한 고성능 감수제는 나프탈렌형, 멜라민형, 폴리카르복실산형, 아미노 술폰산형 감수제 또는 이들의 혼합물로 이루어진 것이 좋고, 그 함량은 특별히 제한되지 않고 필요에 따라 적절하게 조절할 수 있으며, 예를 들어 시멘트 100중량부를 기준으로 0.01 내지 10중량부를 사용할 수 있다.The preferred high performance water reducing agent is preferably a naphthalene type, a melamine type, a polycarboxylic acid type, an aminosulfonic acid type water reducing agent or a mixture thereof. The content thereof is not particularly limited and can be appropriately adjusted as required. 0.01 to 10 parts by weight may be used.
이때, 상기 나프탈렌형 감수제로서 대표적인 것은 변성리그닌, 알킬아릴술폰산 및 활성지속폴리머, 폴리알킬아일슬폰산염과 반응성고분자, 알킬아릴술폰산염고축합물, 슬폰산기카르복실기 함유 다원폴리머, 알킬나프탈렌슬폰산염, 알킬아릴술폰산염변성리그닌공축합물과 변성리그닌, 리그닌유도체와 알킬아릴술포네이트 또는 이들로부터 선택된 적어도 하나 이상을 들을 수 있다.Typical examples of the naphthalene-type water reducing agent include modified lignin, alkylarylsulfonic acid and active persistent polymer, a polyalkylisocyanate and a reactive polymer, an alkylarylsulfonic acid salt condensate, a sulfonic acid group carboxyl group-containing polyol polymer, an alkylnaphthalene sulfonate, Sulfonic acid salt-modified lignin co-condensates, modified lignin, lignin derivatives and alkylaryl sulfonates, or at least one selected from these.
상기 멜라민형 감수제로서 대표적인 것은 변성메칠멜라민축합물과 수용성특수고분자화합물, 슬폰화멜라민고축합물 또는 이들로부터 선택된 하나 이상의 혼합물을 들을 수 있다.Representative examples of the melamine-type water reducing agent include a modified methylmelamine condensate and a water-soluble special polymer compound, a sulfonated melamine condensate, and a mixture of at least one selected from the foregoing.
상기 폴리카르복실산형 감수제로서 대표적인 것은 불포화 카르복시산 단량체를 단일 성분으로 포함하는 공중합체 또는 그의 염, 예컨대, 폴리(알킬렌 글리콜)모노아크릴레이트, 폴리(알킬렌 글리콜)모노메타크릴레이트, 무수말레인산 및 스티렌의 공중합체, 아크릴레이트나 메타크릴레이트의 공중합체 및 이들 단량체와 공중합가능한 단량체로부터 유도되는 공중합체 등을 포함할 수 있다.Representative examples of the polycarboxylic acid type water reducing agent include a copolymer containing an unsaturated carboxylic acid monomer as a single component or a salt thereof such as poly (alkylene glycol) monoacrylate, poly (alkylene glycol) monomethacrylate, Styrene copolymers, copolymers of acrylates and methacrylates, and copolymers derived from monomers copolymerizable with these monomers.
상기 아미노 술폰산형 감수제로서 대표적인 것은 방향족아미노슬폰산계 고분자화합물, 방향족고분자축합물과 리그닌슬폰산유도체 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 들을 수 있다.Typical examples of the aminosulfonic acid-based water reducing agent include an aromatic aminosulfonic acid-based polymer compound, an aromatic polymer condensate, a lignin sulfonic acid derivative, and a mixture of at least one selected from the foregoing.
또한, 바람직한 감수제, 특정적으로 고성능 감수제는 나프탈렌형 고성능 감수제를 단독으로 사용하거나 나프탈렌계 고성능 감수제가 80 내지 95중량%이고, 폴리카르복실산형 고성능 감수제가 5 내지 20중량%로 이루어진 혼합조성을 사용하는 것이 좋다.In addition, as a preferable water reducing agent, specifically, a high performance water reducing agent, a naphthalene type high performance water reducing agent is used alone, or a mixed composition comprising 80 to 95% by weight of a naphthalene type high performance water reducing agent and 5 to 20% by weight of a polycarboxylic acid type high performance water reducing agent is used It is good.
상기 고성능 감수제의 사용량은 몰탈 조성물 중의 전 공기량이 용적으로 약 4 내지 6%가 되도록 하는 것이 바람직하다. 너무 많이 사용하면 비경제적일 뿐만 아니라, 압축강도의 감소, 철근과의 부착강도의 저하 등 여러 가지 장애가 일어나므로, 적정 사용량을 엄수해야 한다.The amount of the high-performance water reducing agent is preferably such that the total amount of air in the mortar composition is about 4 to 6% by volume. If it is used too much, it will not only be economical but also cause various obstacles such as reduction of compressive strength and deterioration of bond strength with reinforcing steel, so proper usage should be strictly observed.
본 발명에 따른 친환경 보수용 몰탈 조성물은 하기으 특정 양태에 따른 부가물을 1종 또는 1종이상 더 포함할 수 있다.The mortar composition for eco-friendly repair according to the present invention may further include one or more kinds of adducts according to the following specific embodiments.
특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 시공면의 부식을 방지하기 위하여 방청제를 더 포함할 수 있다.In a specific embodiment, the mortar composition for eco-friendly repair according to the present invention may further include an antirust agent to prevent corrosion on the surface to be treated.
이때, 상기 방청제로 사용 가능한 것으로서, 대표적으로 크롬산 스트론튬, 크롬산 칼슘, 크롬산 바륨, 크롬산 아연칼륨, 사염기산 크롬산 아연, 아연말, 인산아연, 유기니트로 화합물 아연염, 규산염 칼슘, 사산화삼납, 아연 칼륨 또는 이들의 혼합물을 사용하는 것이 좋고, 그 사용량은 특별히 한정되는 것은 아니지만, 추천하기로는 시멘트 100중량부 기준으로 0.5 내지 7중량부인 것이 좋다.Typical examples of the rust inhibitor include strontium chromate, calcium chromate, barium chromate, zinc chromate, zinc chromate, zinc phosphate, zinc phosphate, organic nitro compound zinc salt, calcium silicate, Or a mixture thereof, and the amount thereof to be used is not particularly limited, but preferably 0.5 to 7 parts by weight based on 100 parts by weight of cement.
다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 셀프 레벨링(자기충전성능)을 개선하기 위하여 표면평활제를 더 포함할 수 있다.In another specific embodiment, the eco-friendly repair mortar composition according to the present invention may further include a surface smoothing agent to improve self-leveling (self-charging performance).
바람직한 표면평활제로는 스타치에테르, 변성 스타치에테르(Modified Starch ether), 폴리옥사이드계, 우레탄계 및 폴리카본산계 중에서 선택된 어느 하나 이상이 사용될 수 있으나, 이에 제한되는 것은 아니며, 당업계에서 통상적으로 사용되는 종류가 사용될 수 있다.Preferred surface smoothing agents include starch ether, modified starch ether, polyoxide, urethane, and polycarbonate, but are not limited thereto. Can be used.
상기 표면평활제의 사용량은 특별히 한정되는 것은 아니지만, 추천하기로는 시멘트 100중량부를 기준으로 0.5 내지 5중량부인 것이 좋다. The amount of the surface smoothing agent to be used is not particularly limited, but is preferably 0.5 to 5 parts by weight based on 100 parts by weight of the cement.
또 다른 특정 양태로서, 본 발명에 따른 몰탈 조성물, 특정적으로 친환경 보수용 몰탈 조성물은 시멘트 100중량부 기준으로 10 내지 40중량부의 충진재를 더 포함할 수 있다.As another specific embodiment, the mortar composition according to the present invention, particularly the eco-friendly mortar composition, may further comprise 10 to 40 parts by weight of filler based on 100 parts by weight of cement.
여기서, 상기 충진제는 몰탈 조성물의 치수 안정성 및 내모마성을 향상시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 충진재라면 특별히 한정되지 않는다.Here, the filler is for improving the dimensional stability and anti-abrasion property of the mortar composition, and is not particularly limited as long as it is a conventional filler in the art having such a purpose.
바람직한 충진재는 탄산칼슘, 실리카분말, 초미립실리카분말, 수산화칼슘 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용할 수 있다.Preferred fillers are calcium carbonate, silica powder, ultrafine silica powder, calcium hydroxide or a mixture of at least one selected from these.
여기서, 상기 충진제의 사용량이 10중량부 미만이면 치수 안정성 및 내마모성, 칙소성(Thixotropic)의 저하를 가져와 내구성이 좋지 않고, 40중량부를 초과하는 경우에는 칙소 상승에 의한 작업성 저하 및 내충격성 저하 등의 영향을 가져오므로 바람직하지 못하다.If the amount of the filler used is less than 10 parts by weight, the dimensional stability, abrasion resistance, and thixotropic tend to be deteriorated, resulting in poor durability. When the filler is used in an amount exceeding 40 parts by weight, Which is undesirable.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 시멘트 100중량부 기준으로 0.5 내지 5중량부의 방부제를 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention may further contain 0.5 to 5 parts by weight of preservative based on 100 parts by weight of cement.
바람직한 방부제는 이소티아조린(Isothiazoline) 유도체를 포함한다.Preferred preservatives include isothiazoline derivatives.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 강고한 밀착성, 코팅 코팅층의 내수성, 투수성, 산소투과성, 이온투과성, 전기절연성, 내약품성, 기계적 특성(탄성, 유리전이온도, 응력완화) 등을 제공하기 위하여 시멘트 100중량부 기준으로 아크릴 에멀젼 수지 10 내지 40중량부를 더 포함할 수 있다. As another specific embodiment, the mortar composition for eco-friendly repair according to the present invention is characterized in that the mortar composition for repairing the environment has a high adhesion, a water resistance, a water permeability, an oxygen permeability, an ion permeability, an electrical insulation, a chemical resistance, 10 to 40 parts by weight of an acrylic emulsion resin based on 100 parts by weight of the cement may be further provided to provide a cushion,
바람직한 아크릴 에멀젼 수지로는 모노머(2-에틸헥실아크릴레이트), 2- 하이드로에틸메타아크릴레이트, AN(acrylonitrile), 부틸 아크릴레이트(Butyl acrylate), 메타크릴산/메틸메타아크릴레이트(methacrylic acid, methylmethacrylate), SM(styrene monomer), 디아세톤 아크릴아미드(Diacetone acrylamide), 이소부틸메타아크릴레이트, 2-에틸헥실메타아크릴레이트, 2-하이드로에틸아크릴레이트, 2-하이드로프로필아크릴레이트 또는 이들의 혼합물을 사용하는 것이 좋다.Preferred acrylic emulsion resins include monomers such as 2-ethylhexyl acrylate, 2-hydroethylmethacrylate, AN, acrylonitrile, butyl acrylate, methacrylic acid, methylmethacrylate ), SM (styrene monomer), diacetone acrylamide, isobutyl methacrylate, 2-ethylhexyl methacrylate, 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate or a mixture thereof It is good to do.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 조성물 내부에 필름을 형성하여 휨 및 부착강도를 향상시키며, 보수성이 개선되어 중성화, 염화물 이온 침투, 동결융해 등에 대한 내구성을 향상시킬 수 있도록 재유화형 고분자 수지 분말을 시멘트 100중량부 기준으로 0.01 내지 3중량부 더 포함할 수 잇다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention improves warpage and adhesion strength by forming a film inside the composition, and improves water retention, thereby improving durability against neutralization, chloride ion penetration, freezing and thawing , The re-fusing type polymer resin powder may be further added in an amount of 0.01 to 3 parts by weight based on 100 parts by weight of the cement.
바람직한 재유화형 고분자 수지 분말은 초산비닐/비닐바사테이트(Va/VeoVa)로 구성되는데, 겉보기 비중은 475±g/l, 입도는 max,2%>400㎛이고, 물에 재분산 시 0.3 내지 9㎛의 입도분포를 나타낸다.The preferred re-firing polymer resin powder is composed of vinyl acetate / vinyl valerate (Va / VeoVa) with an apparent specific gravity of 475 ± g / l, a particle size of max, 2%> 400 μm, Mu m.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 조성물의 강도를 증가시키고, 조성물간의 결합력, 균열방지 등을 제공하기 위하여 시멘트 100중량부 기준으로 폴리아미드 섬유 5 내지 20중량부를 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention further comprises 5 to 20 parts by weight of polyamide fibers based on 100 parts by weight of cement in order to increase the strength of the composition and to provide bonding strength, can do.
상기 폴리아미드 섬유는 폴리아미드(나일론) 6, 폴리아미드(나일론) 66 또는 이들의 혼합물을 포함한다.The polyamide fibers include polyamide (nylon) 6, polyamide (nylon) 66, or mixtures thereof.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 초기 접착력을 강화하기 위하여 폴리비닐알코올을 더 포함할 수 있는데, 폴리비닐알코올은 몰탈 조성물의 구성성분의 분산성을 좋게 할 뿐만 아니라, 초기의 끈적임 정도(tacky property)도 증가되어 초기접착력을 개선하여 들뜸 현상, 뒤틀림 등의 불량률을 감소시킬 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention may further include polyvinyl alcohol in order to enhance the initial adhesive strength. The polyvinyl alcohol not only improves the dispersibility of the constituents of the mortar composition, The initial tacky property is also increased to improve the initial adhesive force, thereby reducing the defective rate such as floating phenomenon and warping.
상기 폴리비닐알코올의 사용량은 시멘트 100중량부 기준으로 2 내지 10중량부인데, 폴리비닐알코올이 2중량부 이하 일 때는 그 효과가 미미하며, 10중량부 이상일 경우에는 그 양이 과도하여 경제적이지 못할 뿐만 아니라, 몰탈 조성물의 내후성 등에 나쁜 영향을 미칠 수 있어 바람직하지 않다.The amount of polyvinyl alcohol used is 2 to 10 parts by weight based on 100 parts by weight of cement. When the amount of polyvinyl alcohol is less than 2 parts by weight, the effect is insignificant. When the amount is more than 10 parts by weight, But also the weatherability of the mortar composition may be adversely affected.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 테트라에틸렌펜타민(Tetraethylenepentamine; TEPA)을 시멘트 100중량부를 기준으로 2 내지 8중량부로 더 포함할 수 있는데, 테트라에틸렌펜타민은 폴리아민의 일종으로서, 몰탈 조성물의 경화속도 및 점도 조절의 역할을 하며, 그 사용량이 2중량부 이하 일 때는 효과가 미미하며, 8중량부 이상일 경우에는 그 양이 과도하여 경제적이지 못하다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention may further comprise 2 to 8 parts by weight of tetraethylenepentamine (TEPA) based on 100 parts by weight of cement, wherein the tetraethylenepentamine is a polyamine As a kind, it plays a role of controlling the curing speed and viscosity of the mortar composition. When the amount is less than 2 parts by weight, the effect is insignificant. When the amount is more than 8 parts by weight, the amount is excessively excessive.
또 다른 특정 양태로서, 본 발명에 따른 몰탈 조성물은 실온에서 효과적으로 경화하고 내열성, 저온 성능, 내화학성, 내용매성 및 내유성과 같은 개선된 특성을 제공하기 위하여 아미노기 함유 실록산(Aminofunctional siloxan)을 더 포함할 수 있다.In another specific embodiment, the mortar composition according to the present invention further comprises an aminofunctional siloxane to effectively cure at room temperature and to provide improved properties such as heat resistance, low temperature performance, chemical resistance, solvent resistance and oil resistance .
상기 아미노 함유 실록산은 특별히 제한되는 것은 아니며, 일례로서 아미노메틸폴리디메틸실록산을 들 수 있으며, 그 사용량은 시멘트 100중량부를 기준으로 3 내지 10중량부인 것을 추천한다.The amino-containing siloxane is not particularly limited, and examples thereof include aminomethylpolydimethylsiloxane. The amount of the amino-containing siloxane used is preferably 3 to 10 parts by weight based on 100 parts by weight of cement.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 조성물의 수밀성과 투수계수를 개선하기 위하여 시멘트 100중량부 기준으로 0.1 내지 5중량부의 벤토나이트를 더 포함할 수 있는데, 벤토나이트가 0.1중량부 보다 적을 경우 효과가 미미하며, 5중량부를 초과할 경우 과량이 되어 물성을 저하시킬 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention may further contain 0.1 to 5 parts by weight of bentonite based on 100 parts by weight of cement in order to improve the watertightness and permeability of the composition. If the amount is less than 5 parts by weight, the effect is insignificant, and if it is more than 5 parts by weight, the amount is excessive and the physical properties may be deteriorated.
또 다른 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 조성물의 건조 수축을 방지하기 위하여 시멘트 100중량부 기준으로 1 내지 5중량부의 알루민산 칼슘을 더 포함할 수 있는데, 알루민산 칼슘은 조성물에 포함되면 팽창성을 띠게 되어 건초수축을 방지하게 되는데, 사용량이 1중량부 보다 적을 경우에는 효과가 미미하며, 5중량부를 초과할 경우 과다하여 작업성을 저하 시킬수 있다.In another embodiment, the mortar composition for eco-friendly repair according to the present invention may further comprise 1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of cement in order to prevent drying and shrinkage of the composition. If the amount is less than 1 part by weight, the effect is insignificant. If the amount is more than 5 parts by weight, the workability may be deteriorated.
또 다른 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 조성물의 충진성 및 내구성을 향상시키기 위하여 시멘트 100중량부 기준으로 1 내지 5중량부의 플루오린화나트륨을 더 포함할 수 있는데, 플루오린화 나트륨은 1차적으로 충진제로서의 역할도 하지만, 2차적으로는 내구성을 향상시키는 역할을 하는 것으로, 상기와 같은 함량 범위에서 그 효과를 얻을 수 있다.In another embodiment, the mortar composition for eco-friendly repair according to the present invention may further contain 1 to 5 parts by weight of sodium fluoride based on 100 parts by weight of cement in order to improve the filling property and durability of the composition. It plays a role primarily as a filler, but secondarily plays a role of improving durability, and the effect can be obtained in the above content range.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 점도를 조절하고, 부착성을 향상시키기 위하여 부틸글리시딜에테르(Butyl glycidyl ether)를 시멘트 100중량부 기준으로 1 내지 3중량부 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention comprises butyl glycidyl ether in an amount of 1 to 3 parts by weight based on 100 parts by weight of cement to control viscosity and improve adhesion .
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 조성물의 응집력과 재료의 분리를 방지하기 위하여 폴리비닐리덴 플루오라이드 수지를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention may further contain 1 to 3 parts by weight of polyvinylidene fluoride resin based on 100 parts by weight of cement in order to prevent the cohesive force of the composition and the separation of materials .
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 조성물의 혼합시 급격한 반응을 억제하여 반응의 안정성을 향상시키기 위하여 중탄산나트륨을 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention may further contain sodium bicarbonate in an amount of 1 to 3 parts by weight based on 100 parts by weight of cement in order to suppress the abrupt reaction during mixing of the composition to improve the stability of the reaction. have.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 친환경 보수용 몰탈 조성물의 통기성을 확보하기 위하여 시멘트 100중량부를 기준으로 1 내지 3중량부의 소디윰스테아레이트를 더 포함할 수 있는데, 시멘트 100중량부를 기준으로 1중량부 미만이면 목적한 기능을 얻을 수 없고, 3중량부를 초과하면 조성물의 강도 저하현상을 나타내어 좋지 않다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention may further include 1 to 3 parts by weight of sodipyl stearate based on 100 parts by weight of cement in order to ensure the breathability of the mortar composition for eco- If the amount is less than 1 part by weight based on 100 parts by weight, the desired function can not be obtained. If the amount is more than 3 parts by weight, the strength of the composition is lowered.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 조성물의 건조를 촉진하기 위하여 밀도가 낮고 표면적이 큰 규조토를 시멘트 100중량부를 기준으로 1 내지 4중량부로 더 포함할 수 있다.In another specific embodiment, the eco-friendly repair mortar composition according to the present invention may further comprise 1 to 4 parts by weight of diatomaceous earth having a low density and a large surface area based on 100 parts by weight of cement to promote drying of the composition.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 친환경 보수용 몰탈 조성물의 충진성 및 내구성을 향상시키기 위하여 암모늄 노니페놀 에테르설페이트(ammonium nonylphenol ether sulfate)를 시멘트 100중량부 기준으로 1 내지 4중량부로 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention comprises ammonium nonylphenol ether sulfate in an amount of 1 to 100 parts by weight based on 100 parts by weight of cement to improve the filling and durability of the mortar composition for eco- 4 parts by weight.
또 다른 특정 양태로서, 본 발명에 따른 친환경 보수용 몰탈 조성물은 친환경 보수용 몰탈 조성물의 내수성, 내화학성 및/또는 내부착성 등을 향상시키기 위하여 테트라메틸렌 디이소시아네이트를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.
In another specific embodiment, the mortar composition for eco-friendly repair according to the present invention is prepared by adding tetramethylene diisocyanate to 1 to 100 parts by weight of cement based on 100 parts by weight of cement to improve the water resistance, chemical resistance and / 3 parts by weight.
이와 같은 구성을 갖는 본 발명에 따른 몰탈 조성물, 특정적으로 친환경 보수용 몰탈 조성물의 시공방법을 설명하면 다음과 같다.The mortar composition according to the present invention having the above-described structure, and specifically, the method of constructing the mortar composition for environmentally friendly repair will be described as follows.
먼저, 콘크리트 구조물 표면의 요철과 레이탄스를 제거하는 단계;Firstly, the steps of removing the concavity and convexity of the surface of the concrete structure;
상기 콘크리트 구조물 표면의 이물질을 제거하기 위한 고압 세척단계;A high-pressure washing step for removing foreign matters on the surface of the concrete structure;
상기 콘크리트 구조물의 표면상에 퍼티재를 도포하는 바탕 처리단계;A pretreatment step of applying a putty material on the surface of the concrete structure;
상기 콘크리트 구조물의 표면상에, 시멘트 100중량부를 기준으로, 칼슘설포알루미네이트 20 내지 40중량부, 실리카 퓸 10 내지 50중량부, 메틸메타아크릴레이트 10 내지 50중량부, 옥틸트리에톡시실란 1 내지 10중량부, 나노세라믹 입자 5 내지 20중량부, 파이버 2 내지 20중량부, 구아검 1 내지 10중량부, 박리방리제 5 내지 30중량부, 부착증진제 1 내지 10중량부, 증점제 3 내지 20중량부, 가소제 1 내지 10중량부, 소포제 0.5 내지 5중량부, 및 감수제 0.01 내지 10중량부를 포함하는 친환경 보수용 몰탈 조성물을 1차적으로 도포하여 하도층을 형성한 후 1차 양생하는 단계;20 to 40 parts by weight of calcium sulfoaluminate, 10 to 50 parts by weight of silica fume, 10 to 50 parts by weight of methyl methacrylate, 1 to 50 parts by weight of octyltriethoxysilane based on 100 parts by weight of the cement, 5 to 20 parts by weight of nanoceramics, 2 to 20 parts by weight of fibers, 1 to 10 parts by weight of guar gum, 5 to 30 parts by weight of a peeling agent, 1 to 10 parts by weight of an adhesion promoter, 3 to 20 parts by weight of a thickener 1 to 10 parts by weight of a plasticizer, 0.5 to 5 parts by weight of an antifoaming agent, and 0.01 to 10 parts by weight of a water reducing agent is firstly applied to form a primer layer, followed by primary curing;
상기 하도층의 표면상에 상기 하도층과 동일 성분의 친환경 보수용 몰탈 조성물을 2차적으로 도포하여 중도층을 형성한후 2차 양생하는 단계; 및Applying an eco-friendly repair mortar composition having the same composition as that of the undercoating layer to the surface of the undercoating layer to form an intermediate layer and then curing the second coating; And
상기 중도층의 표면상에 상기 중도층과 동일 성분의 친환경 보수용 몰탈 조성물을 3차적으로 도포하여 상도층을 형성한 후 3차 양생하는 단계를 포함한다.
A third step of applying an eco-friendly repairing mortar composition having the same composition as that of the intermediate layer to the surface of the intermediate layer to form an upper layer, followed by a third curing.
이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described in detail by way of examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
[실시예 1][Example 1]
포틀랜트 시멘트 100g, 칼슘설포알루미네이트 30g, 실리카 퓸 30g, 메틸메타아크릴레이트 40g, 약 300Da의 분자량을 갖는 옥틸트리에톡시실란 5g, 평균 입경은 450nm인 실리콘카바이드 12g, 유리섬유 10g, 구아검 5g, 액상형으로 비중이 1.0 이상이고, 60℃ 점도가 110 cPs인 폴리인산계 박리방지제 15g, 하이드록시 에틸 아크릴로일 포스페이트 5g, 하이드록시 에틸 셀룰로오스 12g, 테레프탈산 금속염 5g, 미네랄오일 3g, 및 알킬아릴술폰산 4g을 혼합하여 친환경 보수용 몰탈 조성물을 제조하였다.
5 g of octyltriethoxysilane having a molecular weight of about 300 Da, 12 g of silicon carbide having an average particle size of 450 nm, 10 g of glass fiber, 5 g of guar gum, 5 g of calcium fluoride, 30 g of calcium sulfoaluminate, 30 g of silica fume, 40 g of methyl methacrylate, 15 g of a polyphosphoric acid peeling inhibitor having a specific gravity of 1.0 or more and a specific gravity of 1.0 or more and a viscosity at 60 DEG C of 110 cPs, 5 g of hydroxyethyl acryloyl phosphate, 12 g of hydroxyethyl cellulose, 5 g of terephthalic acid metal salt, 3 g of mineral oil, Were mixed to prepare an eco-friendly repair mortar composition.
[실시예 2][Example 2]
실시예 1과 동일한 방법으로 실시하되, 크롬산 스트론튬 4g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 4 g of strontium chromate was further added.
[실시예 3][Example 3]
실시예 2와 동일한 방법으로 실시하되, 변성 스타치에테르 3g을 더 부가하여 실시하였다.
The same procedure as in Example 2 was carried out except that 3 g of modified starch ether was further added.
[실시예 4][Example 4]
실시예 1과 동일한 방법으로 실시하되, 탄산칼슘 20g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 20 g of calcium carbonate was further added.
[실시예 5][Example 5]
실시예 1과 동일한 방법으로 실시하되, 이소티아조린 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of isothiazolin was added.
[실시예 6][Example 6]
실시예 1과 동일한 방법으로 실시하되, 모노머(2-에틸헥실아크릴레이트) 20g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 20 g of monomer (2-ethylhexyl acrylate) was further added.
[실시예 7][Example 7]
실시예 1과 동일한 방법으로 실시하되, 초산비닐/비닐바사테이트 1.5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 1.5 g of vinyl acetate / vinyl acetate was further added.
[실시예 8][Example 8]
실시예 1과 동일한 방법으로 실시하되, 폴리아미드(나일론) 6 10g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 10 g of polyamide (nylon) 6 was further added.
[실시예 9][Example 9]
실시예 1과 동일한 방법으로 실시하되, 폴리비닐알코올 5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 5 g of polyvinyl alcohol was further added.
[실시예 10][Example 10]
실시예 1과 동일한 방법으로 실시하되, 테트라에틸렌펜타민 4g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 4 g of tetraethylenepentamine was further added.
[실시예 11][Example 11]
실시예 1과 동일한 방법으로 실시하되, 아미노기 함유 실록산 7g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 7 g of amino group-containing siloxane was further added.
[실시예 12][Example 12]
실시예 1과 동일한 방법으로 실시하되, 벤토나이트 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of bentonite was further added.
[실시예 13][Example 13]
실시예 1과 동일한 방법으로 실시하되, 알루민산 칼슘 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of calcium aluminate was further added.
[실시예 14][Example 14]
실시예 1과 동일한 방법으로 실시하되, 플루오린화 나트륨 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of sodium fluoride was further added.
[실시예 15][Example 15]
실시예 1과 동일한 방법으로 실시하되, 부틸글리시딜에테르(Butyl glycidyl ether) 2g을 더 부가하여 실시하였다.
Was carried out in the same manner as in Example 1 except that 2 g of butyl glycidyl ether was further added.
[실시예 16][Example 16]
실시예 1과 동일한 방법으로 실시하되, 폴리비닐리덴 플루오라이드 수지 2g을 더 부가하여 실시하였다.
Was carried out in the same manner as in Example 1 except that 2 g of polyvinylidene fluoride resin was further added.
[실시예 17][Example 17]
실시예 1과 동일한 방법으로 실시하되, 중탄산나트륨 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of sodium bicarbonate was further added.
[실시예 18][Example 18]
실시예 1과 동일한 방법으로 실시하되, 소디윰스테아레이트 1g을 더 부가하여 실시하였다.
Was carried out in the same manner as in Example 1 except that 1 g of sodium dodecyl stearate was further added.
[실시예 19][Example 19]
실시예 1과 동일한 방법으로 실시하되, 규조토 2g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 2 g of diatomaceous earth was further added.
[실시예 20][Example 20]
실시예 1과 동일한 방법으로 실시하되, 암모늄 노니페놀 에테르설페이트(ammonium nonylphenol ether sulfate) 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 3 g of ammonium nonylphenol ether sulfate was further added.
[실시예 21][Example 21]
실시예 1과 동일한 방법으로 실시하되, 테트라메틸렌 디이소시아네이트 2g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 2 g of tetramethylene diisocyanate was further added.
[실시예 22][Example 22]
실시예 1과 동일한 방법으로 실시하되, 실시예 2 내지 실시예 21에 따라 부가된 부가물을 모두 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that the adducts added in Examples 2 to 21 were further added.
[비교예 1][Comparative Example 1]
실시예 1과 동일한 방법으로 실시하되, 칼슘설포알루미네이트를 제외하여 실시하였다.
The procedure of Example 1 was repeated except that calcium sulfoaluminate was excluded.
[비교예 2][Comparative Example 2]
실시예 1과 동일한 방법으로 실시하되, 실리카 퓸 및 메틸메타아크릴레이트를 제외하여 실시하였다.
The procedure of Example 1 was repeated except that silica fume and methyl methacrylate were excluded.
[비교예 3][Comparative Example 3]
실시예 1과 동일한 방법으로 실시하되, 박리방지제 및 부착증진제를 제외하여 실시하였다.
Was carried out in the same manner as in Example 1 except that the peeling inhibitor and the adhesion promoter were excluded.
[실 험][Experiment]
실시예 및 비교예에 따라 제조된 친환경 보수용 몰탈 조성물을 이용하여 0.2평방미터의 콘크리트 표면상에 약 3cm 두께의 코팅층을 형성한 후 표준상태에서의 안정도, 표면경도, 방수성, 소성변화, 부착성 및 박리성 등을 측정하여 표 1로 나타냈다.
A coating layer having a thickness of about 3 cm was formed on a concrete surface of 0.2 square meter using an eco-friendly repair mortar composition prepared according to Examples and Comparative Examples, and then the stability, surface hardness, waterproofness, plasticity, And peelability were measured and shown in Table 1.
표 1에 나타낸 바와 같이, 본 발명에 따른 친환경 보수용 몰탈 조성물을 사용한 실시예 1 내지 실시예 22는 소성변화가 적고, 방수성 및 부착성 등이 좋을 뿐만 아니라, 표면으로부터 쉽게 박리되지 않는 것을 확인할 수 있었다.
As shown in Table 1, in Examples 1 to 22 using the mortar composition for eco-friendly repair according to the present invention, it was confirmed that not only the change in plasticity was small, the waterproof property and the adhesion property were good, there was.
이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As described above, those skilled in the art will understand that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the embodiments described above are all illustrative and not restrictive. The scope of the present invention should be construed as being included in the scope of the present invention without departing from the scope of the present invention.
Claims (5)
칼슘설포알루미네이트 20 내지 40중량부;
실리카 퓸 10 내지 50중량부;
메틸메타아크릴레이트 10 내지 50중량부;
옥틸트리에톡시실란 1 내지 10중량부;
나노세라믹 입자 5 내지 20중량부;
유리섬유 2 내지 20중량부;
구아검 1 내지 10중량부;
박리방지제 5 내지 30중량부;
부착증진제 1 내지 10중량부;
증점제 3 내지 20중량부;
가소제 1 내지 10중량부;
소포제 0.5 내지 5중량부; 및
감수제 0.01 내지 10중량부를 포함하는 친환경 보수용 몰탈 조성물에,
폴리아미드 섬유를 시멘트 100중량부 기준으로 5 내지 20중량부로 더 포함하고,
알루민산 칼슘을 시멘트 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
플루오린화나트륨을 시멘트 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
부틸글리시딜에테르를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하며,
폴리비닐리덴 플루오라이드 수지를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하고,
중탄산나트륨을 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하며,
소디윰스테아레이트를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하고,
규조토를 시멘트 100중량부 기준으로 1 내지 4중량부로 더 포함하며,
암모늄 노니페놀 에테르설페이트를 시멘트 100중량부 기준으로 1 내지 4중량부로 더 포함하고,
테트라메틸렌 디이소시아네이트를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하며,
방청제를 시멘트 100중량부 기준으로 0.5 내지 7중량부로 더 포함하고,
방부제를 시멘트 100중량부 기준으로 0.5 내지 5중량부로 더 포함하는 친환경 보수용 몰탈 조성물.
Based on 100 parts by weight of cement,
20 to 40 parts by weight of calcium sulfoaluminate;
10 to 50 parts by weight of silica fume;
10 to 50 parts by weight of methyl methacrylate;
1 to 10 parts by weight of octyltriethoxysilane;
5 to 20 parts by weight of nano-ceramic particles;
2 to 20 parts by weight of glass fiber;
1 to 10 parts by weight of guar gum;
5 to 30 parts by weight of an anti-peeling agent;
1 to 10 parts by weight of an adhesion promoter;
3 to 20 parts by weight of a thickener;
1 to 10 parts by weight of a plasticizer;
0.5 to 5 parts by weight of an antifoaming agent; And
0.01 to 10 parts by weight of a water reducing agent is added to the mortar composition for eco-
The polyamide fiber further comprises 5 to 20 parts by weight based on 100 parts by weight of the cement,
Further comprising 1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of cement,
Further comprising 1 to 5 parts by weight, based on 100 parts by weight of cement, sodium fluoride,
Butyl glycidyl ether in an amount of 1 to 3 parts by weight based on 100 parts by weight of cement,
Further comprising 1 to 3 parts by weight of polyvinylidene fluoride resin based on 100 parts by weight of cement,
Further comprising sodium bicarbonate in an amount of 1 to 3 parts by weight based on 100 parts by weight of cement,
Further comprising sodium dodecyl stearate in an amount of 1 to 3 parts by weight based on 100 parts by weight of cement,
Further comprising 1 to 4 parts by weight of diatomaceous earth based on 100 parts by weight of cement,
Further comprising 1 to 4 parts by weight of ammonium noniphenol ether sulfate based on 100 parts by weight of cement,
Further comprising 1 to 3 parts by weight of tetramethylene diisocyanate based on 100 parts by weight of cement,
Further comprising an antirust agent in an amount of 0.5 to 7 parts by weight based on 100 parts by weight of cement,
Wherein the preservative further comprises 0.5 to 5 parts by weight based on 100 parts by weight of cement.
상기 콘크리트 구조물 표면의 이물질을 제거하기 위한 고압 세척단계;
상기 콘크리트 구조물의 표면상에 퍼티재를 도포하는 바탕 처리단계;
상기 콘크리트 구조물의 표면상에, 시멘트 100중량부를 기준으로, 칼슘설포알루미네이트 20 내지 40중량부, 실리카 퓸 10 내지 50중량부, 메틸메타아크릴레이트 10 내지 50중량부, 옥틸트리에톡시실란 1 내지 10중량부, 나노세라믹 입자 5 내지 20중량부, 유리섬유 2 내지 20중량부, 구아검 1 내지 10중량부, 박리방지제 5 내지 30중량부, 부착증진제 1 내지 10중량부, 증점제 3 내지 20중량부, 가소제 1 내지 10중량부, 소포제 0.5 내지 5중량부, 및 감수제 0.01 내지 10중량부를 포함하는 친환경 보수용 몰탈 조성물에, 폴리아미드 섬유를 시멘트 100중량부 기준으로 5 내지 20중량부로 더 포함하고, 알루민산 칼슘을 시멘트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 플루오린화나트륨을 시멘트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 부틸글리시딜에테르를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 폴리비닐리덴 플루오라이드 수지를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 중탄산나트륨을 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 소디윰스테아레이트를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 규조토를 시멘트 100중량부 기준으로 1 내지 4중량부로 더 포함하며, 암모늄 노니페놀 에테르설페이트를 시멘트 100중량부 기준으로 1 내지 4중량부로 더 포함하고, 테트라메틸렌 디이소시아네이트를 시멘트 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 방청제를 시멘트 100중량부 기준으로 0.5 내지 7중량부로 더 포함하고, 방부제를 시멘트 100중량부 기준으로 0.5 내지 5중량부로 더 포함하는 친환경 보수용 몰탈 조성물을 1차적으로 도포하여 하도층을 형성한 후 1차 양생하는 단계;
상기 하도층의 표면상에 상기 하도층과 동일 성분의 친환경 보수용 몰탈 조성물을 2차적으로 도포하여 중도층을 형성한후 2차 양생하는 단계; 및
상기 중도층의 표면상에 상기 중도층과 동일 성분의 친환경 보수용 몰탈 조성물을 3차적으로 도포하여 상도층을 형성한 후 3차 양생하는 단계를 포함하는 친환경 보수용 몰탈 조성물의 시공방법.Removing the concavities and convexities of the surface of the concrete structure;
A high-pressure washing step for removing foreign matters on the surface of the concrete structure;
A pretreatment step of applying a putty material on the surface of the concrete structure;
20 to 40 parts by weight of calcium sulfoaluminate, 10 to 50 parts by weight of silica fume, 10 to 50 parts by weight of methyl methacrylate, 1 to 50 parts by weight of octyltriethoxysilane based on 100 parts by weight of the cement, 10 to 10 parts by weight of nano-ceramic particles, 2 to 20 parts by weight of glass fibers, 1 to 10 parts by weight of guar gum, 5 to 30 parts by weight of anti-peeling agent, 1 to 10 parts by weight of adhesion promoter, 1 to 10 parts by weight of a plasticizer, 0.5 to 5 parts by weight of a defoaming agent, and 0.01 to 10 parts by weight of a water reducing agent is further contained in 5 to 20 parts by weight of polyamide fiber based on 100 parts by weight of cement, And 1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of cement, wherein the fluorinated sodium further comprises 1 to 5 parts by weight based on 100 parts by weight of cement, and butyl glycidyl ether Further comprising 1 to 3 parts by weight of cement based on 100 parts by weight of cement, wherein the polyvinylidene fluoride resin is further added in an amount of 1 to 3 parts by weight based on 100 parts by weight of cement and sodium bicarbonate is added in an amount of 1 to 3 parts by weight Further comprising sodium dodecyl stearate in an amount of 1 to 3 parts by weight based on 100 parts by weight of cement, further comprising diatomite in an amount of 1 to 4 parts by weight based on 100 parts by weight of cement, and ammonium noniphenol ether sulfate in cement 100 1 to 4 parts by weight based on 100 parts by weight of cement, further comprising 1 to 3 parts by weight of tetramethylene diisocyanate based on 100 parts by weight of cement, and further containing 0.5 to 7 parts by weight of a rust inhibitor based on 100 parts by weight of cement, An eco-friendly repair mortar composition further containing 0.5 to 5 parts by weight of an antiseptic based on 100 parts by weight of cement is first applied A first curing step after forming a primer layer;
Applying an eco-friendly repair mortar composition having the same composition as that of the undercoating layer to the surface of the undercoating layer to form an intermediate layer and then curing the second coating; And
And applying an eco-friendly repair mortar composition having the same composition as that of the intermediate layer to the surface of the intermediate layer to form an upper layer, followed by a third curing.