KR101752214B1 - Hybrid water proofing structure using infiltrative liquid waterproofing agent, asphalt and reinforce grid laminate and the method of its construction - Google Patents
Hybrid water proofing structure using infiltrative liquid waterproofing agent, asphalt and reinforce grid laminate and the method of its construction Download PDFInfo
- Publication number
- KR101752214B1 KR101752214B1 KR1020160026099A KR20160026099A KR101752214B1 KR 101752214 B1 KR101752214 B1 KR 101752214B1 KR 1020160026099 A KR1020160026099 A KR 1020160026099A KR 20160026099 A KR20160026099 A KR 20160026099A KR 101752214 B1 KR101752214 B1 KR 101752214B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- asphalt
- waterproofing
- waterproofing material
- delete delete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
본 발명은 침투식 액체 방수제, 아스팔트 및 보강그리드 적층 복합 방수구조 및 그 시공공법에 관한 것으로, 침투식 액체 방수제를 도포한 후 그 위에 아스팔트 및 보강그리드를 차례로 적층하고 상층부에 방수재를 도포하여 다중 적층된 적층 복합 방수구조로서, 방수성능 및 방수구조물의 내구성을 향상시키고, 시공기간을 단축시키며, 친환경적 작업환경을 제공하기 위한 침투식 액체 방수제, 아스팔트 및 보강그리드 적층 복합 방수구조 및 그 시공공법에 관한 것이다.The present invention relates to an infiltrating liquid waterproofing agent, an asphalt and a reinforcing grid laminated composite waterproofing structure and a construction method thereof, wherein an infiltrating liquid waterproofing agent is applied, an asphalt and a reinforcing grid are sequentially laminated on the infiltrating liquid waterproofing agent, The present invention relates to a laminated composite waterproofing structure, a composite waterproofing structure of an asphaltic waterproofing agent, an asphalt and a reinforced grid, and a construction method thereof for improving the waterproof performance and durability of a waterproof structure, shortening a construction period and providing an environment- will be.
Description
본 발명은 침투식 액체 방수제, 아스팔트 및 보강그리드 적층 복합 방수구조 및 그 시공공법에 관한 것으로, 더욱 상세하게는 침투식 액체 방수제를 도포한 후 그 위에 아스팔트 및 보강그리드를 차례로 적층하고 상층부에 방수재를 도포하여 다중 적층된 적층 복합 방수구조로서, 방수성능 및 방수구조물의 내구성을 향상시키고, 시공기간을 단축시키며, 친환경적 작업환경을 제공하기 위한 침투식 액체 방수제, 아스팔트 및 보강그리드 적층 복합 방수구조 및 그 시공공법에 관한 것이다.
The present invention relates to an infiltrating liquid waterproofing agent, an asphalt and reinforcing grid laminated composite waterproofing structure and a construction method thereof, and more particularly, to an infiltrating liquid waterproofing agent, an asphalt and a reinforcing grid waterproofing agent, Layered composite waterproofing structure, which is a multi-layered laminated composite waterproofing structure, has improved waterproof performance and durability of a waterproof structure, shortens a construction period, and provides an environment- It relates to construction method.
일반적으로, 옥상, 지붕, 지하실 등 각종 구조물 바닥, 각종 유체 저장탱크 등의 콘크리트 구조물에는 빗물 등이 스며들었을 경우, 일부가 내부로 침투하여 구조물의 내구성에 악영향을 주게 되므로 각종 방수재료를 사용하여 지붕, 외벽, 바닥, 저장탱크 등을 방수 시공하고 있다.
Generally, when rainwater or the like penetrates into concrete structures such as rooftops, roofs, basements, and various kinds of fluid storage tanks, a part thereof penetrates into the inside and adversely affects the durability of the structure. , Exterior walls, floors, storage tanks, etc.
상기한 방수 시공공법으로는 아스팔트, 콜타르피치, 우레탄, 에폭시 등 도막방수재를 도포하여 방수코팅층을 형성하는 방법, 아스팔트나 콜타르피치를 함침한 종이, 펠트, 천 등 방수시트로 시공면을 덮고, 그 위에 모르타르, 레미콘 등을 타설하는 방법 등이 있다.
Examples of the waterproof construction method include a method of forming a waterproof coating layer by applying a coating material such as asphalt, a coal tar pitch, a urethane, and an epoxy, a method of covering a construction surface with a waterproof sheet such as paper impregnated with asphalt or coal tar pitch, A mortar, a concrete mixer or the like is laid on the concrete.
상기와 같은 종래 방수공법으로서, 한국등록특허 10-0977160에는 바탕기재에 프라이머를 도포하는 단계와, 상기 바탕기재의 코너부에 부틸합성고무 밴드를 시공하는 단계와, 상기 프라이머에 무용제형 폴리우레탄 매스틱 방수재를 도포하는 단계와, 상기 방수재의 상부에 보호층을 시공하는 단계를 포함하여 이루어지며, 상기 무용제형 폴리우레탄 매스틱 방수재는 제1액과 제2액으로 이루어지며, 상기 제1액은 우레탄 경화제 15∼40중량%, 연화제 10∼40중량%, 무기질 필러 20∼70중량%, 점착부여제 2∼20중량%, 반응 촉매 0.1∼5중량%, 안료 1∼10중량% 및 기타 첨가제 0.1∼5중량%를 포함하여 이루어지고, 상기 제2액은 분자쇄에 2개 이상의 이소시아네이트 반응기를 가지는 우레탄 프리폴리머 또는 단량체로 이루어지며, 상기 부틸합성고무 밴드는 부틸합성고무 매스틱 조성물을 단면이 이등변 삼각형으로 되는 바형상의 부틸합성고무 밴드로 성형하되, 상기 이등변 삼각형은 등변의 길이가 2∼7cm이고, 꼭지각의 크기가 80∼150°이며, 상기 부틸합성고무 밴드의 하나 이상의 측면에는 이형층이 구비되고, 상기 부틸합성고무 매스틱 조성물은 부틸고무 10∼30중량%, 연화제 3∼20중량%, 무기질 필러 20∼70중량%, 점착부여제 8∼25중량%, 개질재 4∼15중량% 및 점도 조정제 4.8∼25중량%로 이루어지는 것을 특징으로 하는 무용제형 폴리우레탄 매스틱 방수재를 이용한 방수공법이 공지되어 있다.
Korean Patent Registration No. 10-0977160 discloses a conventional waterproofing method as described above, which comprises a step of applying a primer to a base substrate, a step of applying a butyl synthetic rubber band to the corner of the base substrate, and a step of applying a non- Applying a stick waterproofing material and a protective layer on top of the waterproofing material, wherein the solventless polyurethane mastic waterproofing material comprises a first liquid and a second liquid, 10 to 40 wt% of a urethane curing agent, 10 to 40 wt% of a softening agent, 20 to 70 wt% of an inorganic filler, 2 to 20 wt% of a tackifier, 0.1 to 5 wt% of a reaction catalyst, To 5% by weight, said second liquid being comprised of a urethane prepolymer or monomer having at least two isocyanate reactors in its molecular chain, said butyl synthetic rubber band being a butyl synthetic rubber sheet Wherein the isosceles triangle has an equilateral length of 2 to 7 cm and a vertex angle of 80 to 150 °, and the one of the butyl synthetic rubber bands Wherein the butyl rubber mastic composition comprises 10 to 30% by weight of butyl rubber, 3 to 20% by weight of a softener, 20 to 70% by weight of an inorganic filler, 8 to 25% by weight of a tackifier, 4 to 15% by weight of a water-repellent agent, 4.8 to 25% by weight of a viscosity adjusting agent, and a waterproofing method using a water-soluble polyurethane mastic waterproofing agent.
또한, 한국등록특허 10-1573298에는 기초부재 표면에 프라이머를 도포하는 단계; 상기 프라이머 상부에 바탕조정제로서 폴리우레아를 도포하는 단계; 및 상기 바탕조정제 상부에 방수용으로서 폴리우레아를 코팅하는 단계;를 포함하고, 상기 바탕조정제는 폴리이소시아네이트를 함유하는 A액 및 폴리올, 폴리아민 및 폴리아스파틱 에스터를 함유하는 B액으로 이루어지며, 상기 A액은 NCO%가 8 내지 20중량%이고, 상기 B액은 폴리올이 5 내지 20중량%이고, 폴리아민이 20 내지 40중량%이고, 폴리아스파틱에스터(polyaspartic ester)가 20 내지 40 중량% 이며, 상기 A액과 B액의 부피비는 1:1이고, 상기 B액에는 실리콘계 소포제, 1.3-BG, 1.4-BD, 프로필렌 카보네이트(Propylene carbonate)가 첨가물로서 포함되는 것을 특징으로 하는 바탕조정제로 폴리우레아를 이용하는 방수공법이 개발된 바 있다.
Korean Patent Registration No. 10-1573298 discloses a method of manufacturing a base member, comprising the steps of: applying a primer to a surface of a base member; Applying polyurea as an undercoating agent to the top of the primer; And coating a polyurea coating on the top of the primer for waterproofing, wherein the primer comprises a solution A comprising polyisocyanate and a solution B containing polyol, polyamine and polyaspartic ester, wherein A Wherein the liquid B has a NCO content of 8 to 20% by weight and the liquid B has a polyol content of 5 to 20% by weight, a polyamine content of 20 to 40% by weight, a polyaspartic ester content of 20 to 40% Wherein the volume ratio of the liquid A to the liquid B is 1: 1, and the liquid B contains a silicone-based defoaming agent, 1.3-BG, 1.4-BD and propylene carbonate as an additive. A waterproofing method has been developed.
또한, 한국등록특허 10-1469840에는 MMA수지를 포함하는 프라이머를 교면 바닥면에 도포하여 프라이머층을 형성하는 단계(S10); 상기 프라이머층 상부에 MMA수지를 포함하는 방수재를 도포하여 방수층을 형성하는 단계(S20); 상기 방수층의 상부로 택코팅을 실시하는 단계(S30);를 포함하는 교면 포장 방수공법에 있어서, 상기 S20 단계에서, 상기 방수재는 MMA수지와 골재를 포함하되, 상기 MMA수지는 MMA, PMMA, 우레탄(UR), 불포화 폴리에스테르(UP), 에폭시 아크릴레이트를 배합하여 고분자 물질화 된 수지이며, 상기 골재는 규사, 탄산칼슘, 자연사를 포함하는 것을 특징으로 하고, 상기 방수재는, MMA수지 100중량부에 대해 골재 100 내지 400중량부, 상기 골재보다 입경이 작은 충진분말 100 내지 300중량부, 경화제 2 내지 5중량부를 포함하면서, 증점제로는 메틸셀롤로오즈(MC)에 수용성 고분자를 도입한 것으로 타 조성들과 혼합 시 즉각적인 증점효과가 나타나지 않고 수용성 고분자가 용해된 이후에 메틸셀롤로오즈(MC)가 증점효과를 나타내도록 하는 히드록실프로필메틸셀룰로오즈계 점성분말 1 내지 3중량부와, 표면장력을 저하시킴으로써 미세균열로의 충진을 확보할 수 있도록 소디움 라우릴 설페이트 0.5 내지 1중량부가 더 배합되는 것을 특징으로 하는 교면 포장 방수공법이 공지된 바 있다.
Korean Patent No. 10-1469840 discloses a method of forming a primer layer by applying a primer including an MMA resin to a bottom surface of a bridge (S10); Forming a waterproof layer by applying a waterproof material including MMA resin on the primer layer (S20); (S30), wherein the waterproofing material comprises MMA resin and aggregate, wherein the MMA resin is selected from the group consisting of MMA, PMMA, urethane (UR), an unsaturated polyester (UP), and an epoxy acrylate, wherein the aggregate includes silica, calcium carbonate, and natural fibers. The waterproofing material is a mixture of 100 parts by weight of MMA resin 100 to 400 parts by weight of an aggregate, 100 to 300 parts by weight of a filler powder having a particle diameter smaller than that of the aggregate, and 2 to 5 parts by weight of a curing agent. The water-soluble polymer is introduced into methylcellulose (MC) (MC) in which the water-soluble polymer is dissolved after the water-soluble polymer is mixed with the aqueous solution of the hydroxypropylmethylcellulose-based
이 외에도 방수시트를 이용한 공법으로서 한국공개특허 10-2010-0046369에는 골조바닥(10)에 소정의 폭(W)과 길이(L)를 가지는 아스팔트 방수시트(S)를 1개의 단위로 하여 독립적으로 시공하는 공법으로서, 상기 골조바닥(10) 전면에 아스팔트 프라이머을 도포하여 아스팔트 프라이머층(11)을 형성하는 프라이머층 형성단계(S1); 상기 아스팔트 프라이머층(11)의 상부에 고온으로 녹인 아스팔트를 길게 도포하여 제1아스팔트층(12)을 형성하는 제1아스팔트층 형성단계(S2); 상기 제1아스팔트층(12) 상에 아스팔트 방수시트(S)와 다른 아스팔트 방수시트(S')를 이격된 상태로 배치하여 압착시키는 아스팔트 방수시트 배치단계(S3); 상기 아스팔트 방수시트(S)와 다른 아스팔트 방수시트(S')의 가장자리 상부 및 이격된 부분으로 돌출되는 제1아스팔트층(12)의 상부를 덮도록 고온으로 녹인 아스팔트를 도포하여 제2아스팔트층(13)을 형성하는 제2아스팔트층 형성단계(S4); 및 상기 제2아스팔트층(13)의 상부면에 비닐(14)을 부착하는 비닐 부착단계(S5);를 포함하는 것 아스팔트 방수시트를 이용한 방수공법이 공지되어 있다.
As a method using a waterproof sheet, Korean Patent Laid-Open No. 10-2010-0046369 discloses a method of separately forming an asphalt waterproof sheet S having a predetermined width (W) and a length (L) (S1) for forming an asphalt primer layer (11) by applying an asphalt primer to the entire surface of the frame bottom (10); A first asphalt layer forming step (S2) of forming a first asphalt layer (12) by applying long asphalt melted at a high temperature on the asphalt primer layer (11); Placing asphalt waterproof sheet (S) and another asphalt waterproof sheet (S ') apart from each other on the first asphalt layer (12) and compressing the asphalt waterproof sheet (S); Asphalt melted at a high temperature is applied to cover the upper portion of the first asphalt layer 12 protruding from the upper portion of the edge of the asphalt waterproof sheet S and another portion of the asphalt waterproof sheet S ' A second asphalt layer forming step (S4) of forming a second asphalt layer (13); And a vinyl attaching step (S5) of attaching vinyl (14) to the upper surface of the second asphalt layer (13). A waterproofing method using an asphalt waterproofing sheet is known.
또한, 아스팔트를 이용한 공법으로서 한국등록특허10-0377431에는 양생이 완료된 신설 콘크리트 교량상판(10) 또는 폴리머 콘크리트 및 리넥스(Linax)로 처리된 노후 콘크리트 교량상판(10)을 도막 방수처리함에 있어서, 교량상판(10)에 먼지와 불순물을 제거한 후 0.3kg/m 2 의 프라이머(20)를 시공함과 동시에 6×9mm의 유리섬유 매쉬(21)를 0.08kg의 중량으로 시공하고 그 상단에 가소제,충진제 및 폴리머가 첨가되고 32-38%의 아스팔트로 구성된 도막 방수제 구스(22)를 200-220℃의 온도로 가열하여 5-7kg/m 2 의 양으로 포설 시공하여 3-5mm의 규사(23)를 2kg/m2 살포하고 아스팔트(30)를 포설시켜서 교면을 방수처리 할 수 있게한 것을 특징으로 하는 구스계 재료 및 유리섬유 매쉬를 이용한 콘크리트 교량표면 상부 방수공법이 공지되어 있다.
Also, Korean Patent Registration No. 10-0377431 discloses a waterproofing treatment of a weathered concrete bridge top plate 10 treated with a new concrete bridge top plate 10 or a polymer concrete and Linax which has been cured in a coating method using asphalt, After removing dust and impurities from the bridge top plate 10, a primer 20 of 0.3 kg /
그러나, 상기와 같이 도막방수재를 사용하여 방수코팅층을 시공하는 경우에는 시공도 쉽고 가격도 저렴하지만, 구조물에 균열이 발생하면 방수코팅층이 파괴되어 균열이 발생한 부분은 방수효과를 상실한다는 문제점이 있다.
However, when the waterproof coating layer is applied using the waterproof coating material as described above, the waterproof coating layer is easily broken and the waterproof coating is damaged when the structure is cracked.
또한, 방수시트를 사용하여 방수시공하는 경우에는 물이 샐 경우 결함 부분의 발견과 보수가 어려워 세심한 시공이 필요하다는 문제점이 있다.
Further, when the waterproofing sheet is used for waterproofing, it is difficult to find and repair the defective portion when the water leaks, which requires a careful construction.
한편, 콘크리트는 다공성의 건설 재료로서 그 내부에는 직경 0.1 내지 50㎜의 큰 기포에서부터 10㎚ 내지 10㎛ 크기의 작은 모세관 공극들이 존재하며, 외부 환경하에서 건조·수축에 의해 생성된 폭 0.3㎜ 이하의 미세한 균열이 무수히 존재한다.
On the other hand, concrete is a porous construction material in which small capillary voids having a size of 10 nm to 10 탆 are present from large bubbles having a diameter of 0.1 to 50 mm and having a width of 0.3 mm or less There are numerous fine cracks.
이러한 공극과 균열은 외부의 수분과 열화 물질 등이 침투하는 통로가 되어 콘크리트 구조물의 내구성을 저하시킬 수 있기 때문에, 장기적인 내구성을 확보하기 위해서는 콘크리트의 표면에 방수 및 열화 억제성 물질을 도포하여 콘크리트 내부로의 열화 물질 등의 침투를 방지하는 것이 요구된다.
Since such pores and cracks may become a pathway for penetrating external moisture and deterioration materials, the durability of the concrete structure may be deteriorated. Therefore, in order to secure long-term durability, a waterproof and deterioration inhibiting material is applied to the surface of the concrete, It is required to prevent penetration of deteriorated substances and the like into the furnace.
이러한 목적으로 콘크리트의 표면에 도포하는 방수 및 열화 억제성 물질로서 종래에는 에폭시계 또는 폴리우레탄계와 같은 유기질계 방수제가 많이 이용되었고, 최근에는 한국등록특허 10-1400065에 변성 아크릴 에멀젼 55∼75 중량부; 에틸렌글리콜수지 20∼35 중량부; 에폭시수지 5∼10 중량부; 비이온성 계면활성제 5∼10 중량부; 실리콘수지 1∼3 중량부;로 이루어진 침투식 액체 방수제를 사용하는 방수공법이 공지된 바 있으나, 이러한 유기질계 방수제는 자외선 등의 외부 환경 조건에 취약하기 때문에 장기적으로 내구 성능을 발휘하지 못하고, 탄성 계수 및 수축 팽창율이 콘크리트와 달라 시간이 경과함에 따라 박리되거나 들뜨는 현상이 발생하는 문제점이 있다.
For this purpose, organic water-repellent agents such as epoxy-based or polyurethane-based agents have been widely used as waterproofing and deterioration inhibiting materials to be applied to the surface of concrete. In recent years, Korean Patent No. 10-1400065 discloses a modified acrylic emulsion containing 55 to 75 parts by weight ; 20 to 35 parts by weight of an ethylene glycol resin; 5 to 10 parts by weight of an epoxy resin; 5 to 10 parts by weight of a nonionic surfactant; And 1 to 3 parts by weight of a silicone resin. However, such an organic waterproofing agent is vulnerable to external environmental conditions such as ultraviolet rays and, therefore, does not exhibit durability for a long period of time, There is a problem in that the coefficient and the shrinkage expansion rate are different from concrete and peel off or float as time elapses.
이에 본 발명자들은 상기와 같은 도막방수재를 사용한 방수코팅층, 방수시트를 사용한 방수시공 및 유기질계 침투식 액체 방수제를 사용하는 방수공법의 문제점을 해결하기 위하여 침투식 액체 방수제, 아스팔트 및 보강그리드 적층 복합 방수구조 및 그 시공공법을 안출하여 본 발명을 완성하게 되었다.
Accordingly, the present inventors have conducted extensive studies to solve the problems of the waterproof coating method using the waterproof coating material, the waterproofing method using the waterproof sheet and the waterproofing method using the organic waterproofing agent, Structure and its construction method, thereby completing the present invention.
본 발명은 침투식 액체 방수제를 도포한 후 그 위에 아스팔트 및 보강그리드를 차례로 적층하고 상층부에 방수재를 도포하여 다중 적층된 적층 복합 방수구조 및 그 시공공법을 제공하는 것을 해결하고자 하는 과제로 한다.
An object of the present invention is to provide a multi-layer laminated composite waterproof structure by applying an infiltrating liquid waterproofing agent, then laminating the asphalt and the reinforcing grid in order, and applying a waterproofing material to the upper layer, and a construction method thereof.
본 발명은 방수구조체의 방수구조에 있어서, 상기 방수구조체 상에 도포되는 침투식 액체 방수제층과; 상기 침투식 액체 방수제층 상에 도포 적층되는 제1아스팔트층과; 상기 제1아스팔트층 상에 도포 적층되는 노출방수재층;을 포함하여 구성되는 복합 방수구조를 과제의 해결수단으로 한다.
The present invention provides a waterproof structure of a waterproof structure, comprising: a layer of a liquid water repellent agent applied on the waterproof structure; A first asphalt layer deposited and laminated on the permeable liquid water repellent layer; And a layer of an exposed waterproofing material layered on the first asphalt layer to form a composite waterproofing structure.
상기 제1아스팔트층 상부 및 상기 노출방수재층 사이에는 보강그리드층을 더 포함하여 적층 구성되는 복합 방수구조를 과제의 해결수단으로 한다.
And a reinforcing grid layer is further provided between the upper portion of the first asphalt layer and the exposed waterproofing material layer.
상기 보강그리드층 상부 및 상기 노출방수재층 사이에는 제2아스팔트층을 더 포함하여 적층 구성되는 복합 방수구조를 과제의 해결수단으로 한다.
And a second asphalt layer is further disposed between the upper part of the reinforcing grid layer and the exposed waterproofing material layer.
상기 침투식 액체 방수제는 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 것을 과제의 해결수단으로 한다.
And the penetration type liquid waterproofing agent is composed of an acrylic emulsion and EVA (ethylene vinyl acetate).
상기 보강그리드는 탄소섬유그리드, 유리섬유그리드, 합성수지그리드 또는 부직포를 사용하는 것을 과제의 해결수단으로 한다.
The reinforcing grid uses a carbon fiber grid, a glass fiber grid, a synthetic resin grid or a nonwoven fabric as a solution to the problem.
상기 노출방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 폐연마재분말, 순환골재분말, 시멘트분말을 포함하는 무기질계 분체를 혼합 포함하여 구성되는 복합 하이브리드 방수재인 것을 과제의 해결수단으로 한다.
The impregnated waterproofing material comprises an acrylic copolymer liquid resin prepared by copolymerizing a composition comprising acrylate, methacrylate and butadiene rubber latex, and an inorganic powder including a waste abrasive powder, a recycled aggregate powder and a cement powder Which is a hybrid hybrid waterproofing material.
상기 노출방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 급결 시멘트를 혼합 포함하여 구성되는 복합 하이브리드 방수재인 것을 과제의 해결수단으로 한다.
Wherein the exposed waterproofing material is a composite hybrid waterproofing material comprising an acrylic copolymer liquid resin prepared by copolymerizing a composition containing an acrylate, a methacrylate and a butadiene rubber latex, and a cement mixed therein.
상기 노출방수재는 MMA수지(Methyl Metacrylate)에 칼라규사를 혼합 포함하여 구성되는 복합 하이브리드 방수재인 것을 과제의 해결수단으로 한다.
The exposed waterproofing material is a composite hybrid waterproofing material comprising MMA resin (Methyl methacrylate) mixed with silica sand.
상기 노출방수재는 1액형 또는 2액형 우레탄 바인더에 슬래그 볼(PS Ball) 및 칼라규사를 혼합 포함하여 구성되는 복합 하이브리드 방수재인 것을 과제의 해결수단으로 한다.
Wherein the impregnated waterproofing material is a composite hybrid waterproofing material comprising a one-pack or two-pack type urethane binder mixed with a slag ball (PS ball) and colored silica.
또한, 본 발명은 방수구조체 상에 침투식 액체 방수제를 도포하는 단계; 상기 침투식 액체 방수제층 상에 제1아스팔트를 도포하는 단계; 상기 아스팔트층 상에 노출방수재를 도포하는 단계;를 포함하는 복합 방수구조 시공공법을 과제의 해결수단으로 한다.
The present invention also provides a method for manufacturing a waterproofing structure, comprising: applying an imbibing liquid waterproofing agent on a waterproofing structure; Applying a first asphalt on the permeable liquid water repellent layer; And applying an exposed waterproofing material on the asphalt layer. The present invention provides a composite waterproofing construction method.
상기 제1아스팔트 상부 및 상기 노출방수재 사이에는 보강그리드를 배열 적층하는 단계를 더 포함하는 복합 방수구조 시공공법을 과제의 해결수단으로 한다.
And a reinforcing grid is stacked between the upper portion of the first asphalt and the exposed waterproofing material.
상기 보강그리드 상부 및 상기 노출방수재 사이에는 제2아스팔트를 도포 적층하는 단계를 더 포함하는 복합 방수구조 시공공법을 과제의 해결수단으로 한다.
And a second asphalt is applied and laminated between the upper portion of the reinforcing grid and the exposed waterproofing material.
본 발명에 따른 복합 방수구조는 건축물의 옥상, 지하주차장, 토목구조물, 철도 및 도로 교량, 터널 등 사용범위에 제한받지 않으며, 상온에서 시공함으로서 화재의 위험이 없고, 무용제형 제품으로 작업자의 안전이 고려되며, 도막식으로 시공함으로써 이음매 없는 방수층의 시공이 가능하고 우수한 접착력으로 수밀성이 우수한 효과가 있다.
The composite waterproof structure according to the present invention is not limited to the use range of rooftops, underground parking lots, civil structures, railroad, road bridges and tunnels of buildings, and is free from the risk of fire due to construction at room temperature. And it is possible to construct a seamless waterproof layer by coating with a coating film type, and there is an effect of excellent water tightness with excellent adhesive force.
또한, 수성 침투식 액체 방수제를 프라이어로 사용하므로 구조체의 방수성능 및 방수구조물의 내구성을 향상시키고, 유기용제를 포함하지 않아 친환경적 작업환경을 제공하는 우수한 효과가 있다.
Further, since the water repellent liquid water repellent agent is used as a fryer, the water repellent performance of the structure and the durability of the waterproof structure are improved, and an organic solvent-free environment is provided to provide an environmentally friendly working environment.
도 1은 본 발명의 일실시예에 따른 침투식 액체 방수제, 아스팔트 및 보강그리드 적층 복합 방수구조를 나타내는 도면
도 2는 본 발명의 또 다른 실시예에 따른 침투식 액체 방수제, 아스팔트 및 보강그리드 적층 복합 방수구조를 나타내는 도면BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a view showing an infiltrating liquid waterproofing agent, an asphalt and a reinforcing grid laminated composite waterproof structure according to an embodiment of the present invention; FIG.
2 is a view showing an infiltrating liquid waterproofing agent, an asphalt and a reinforcing grid laminated composite waterproof structure according to another embodiment of the present invention
본 발명은 방수구조체의 방수구조에 있어서, 상기 방수구조체 상에 도포되는 침투식 액체 방수제층과; 상기 침투식 액체 방수제층 상에 도포 적층되는 제1아스팔트층과; 상기 제1아스팔트층 상에 도포 적층되는 노출방수재층;을 포함하여 구성되는 복합 방수구조를 기술구성의 특징으로 한다.
The present invention provides a waterproof structure of a waterproof structure, comprising: a layer of a liquid water repellent agent applied on the waterproof structure; A first asphalt layer deposited and laminated on the permeable liquid water repellent layer; And an exposed waterproofing material layer laminated on the first asphalt layer to form a composite waterproof structure.
상기 제1아스팔트층 상부 및 상기 노출방수재층 사이에는 보강그리드층을 더 포함하여 적층 구성되는 복합 방수구조를 기술구성의 특징으로 한다.
And a reinforcing grid layer is disposed between the upper portion of the first asphalt layer and the exposed waterproofing material layer to form a composite waterproof structure.
상기 보강그리드층 상부 및 상기 노출방수재층 사이에는 제2아스팔트층을 더 포함하여 적층 구성되는 복합 방수구조를 기술구성의 특징으로 한다.
And a second asphalt layer is disposed between the upper surface of the reinforcing grid layer and the exposed waterproofing material layer to form a composite waterproof structure.
상기 침투식 액체 방수제는 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 것을 기술구성의 특징으로 한다.
And the infiltrating liquid waterproofing agent is composed of an acrylic emulsion and EVA (ethylene vinyl acetate).
상기 보강그리드는 탄소섬유그리드, 유리섬유그리드, 합성수지그리드 또는 부직포를 사용하는 것을 기술구성의 특징으로 한다.
The reinforcing grid is characterized by using a carbon fiber grid, a glass fiber grid, a synthetic resin grid or a nonwoven fabric.
상기 노출방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 폐연마재분말, 순환골재분말, 시멘트분말을 포함하는 무기질계 분체를 혼합 포함하여 구성되는 복합 하이브리드 방수재인 것을 기술구성의 특징으로 한다.
The impregnated waterproofing material comprises an acrylic copolymer liquid resin prepared by copolymerizing a composition comprising acrylate, methacrylate and butadiene rubber latex, and an inorganic powder including a waste abrasive powder, a recycled aggregate powder and a cement powder Which is a hybrid hybrid waterproofing material.
상기 노출방수재는 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 급결 시멘트를 혼합 포함하여 구성되는 복합 하이브리드 방수재인 것을 기술구성의 특징으로 한다.
And the exposed waterproofing material is a hybrid hybrid waterproofing material comprising an acrylic copolymer liquid resin prepared by copolymerizing a composition containing acrylate, methacrylate, and butadiene rubber latex, and curing cement mixed therein.
상기 노출방수재는 MMA수지(Methyl Metacrylate)에 칼라규사를 혼합 포함하여 구성되는 복합 하이브리드 방수재인 것을 기술구성의 특징으로 한다.
The exposed waterproofing material is a hybrid hybrid waterproofing material comprising MMA resin (Methyl methacrylate) mixed with color silica.
상기 노출방수재는 1액형 또는 2액형 우레탄 바인더에 슬래그 볼(PS Ball) 및 칼라규사를 혼합 포함하여 구성되는 복합 하이브리드 방수재인 것을 기술구성의 특징으로 한다.
The impregnated waterproofing material is a composite hybrid waterproofing material comprising a one-pack or two-pack type urethane binder mixed with a slag ball (PS ball) and color silica.
또한, 본 발명은 방수구조체 상에 침투식 액체 방수제를 도포하는 단계; 상기 침투식 액체 방수제층 상에 제1아스팔트를 도포하는 단계; 상기 아스팔트층 상에 노출방수재를 도포하는 단계;를 포함하는 복합 방수구조 시공공법을 기술구성의 특징으로 한다.
The present invention also provides a method for manufacturing a waterproofing structure, comprising: applying an imbibing liquid waterproofing agent on a waterproofing structure; Applying a first asphalt on the permeable liquid water repellent layer; And applying an exposed waterproofing material on the asphalt layer. The present invention also provides a composite waterproofing construction method.
상기 제1아스팔트 상부 및 상기 노출방수재 사이에는 보강그리드를 배열 적층하는 단계를 더 포함하는 복합 방수구조 시공공법을 기술구성의 특징으로 한다.
And a reinforcing grid arranged between the first asphalt upper portion and the exposed waterproofing material.
상기 보강그리드 상부 및 상기 노출방수재 사이에는 제2아스팔트를 도포 적층하는 단계를 더 포함하는 복합 방수구조 시공공법을 기술구성의 특징으로 한다.
And a second asphalt is applied and laminated between the upper part of the reinforcing grid and the exposed waterproofing material.
이하에서는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 도면을 통하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며, 여기에서 설명하는 도면에 한정되지 않는다.
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. The present invention may, however, be embodied in many different forms and should not be construed as limited to the illustrative embodiments set forth herein.
[도 1]을 참조하면, 본 발명의 적층 복합 방수구조는 방수구조체(1) 상에 도포되는 침투식 액체 방수제층(2)과; 상기 침투식 액체 방수제층 상에 도포되는 제1아스팔트층(3)과; 상기 제1아스팔트층 상에 도포되는 노출방수재층(6);을 포함하여 적층 구성되며, 상기 제1아스팔트층 상에는 보강그리드층(4)이 적층 배열될 수 있다.
Referring to FIG. 1, the laminated composite waterproof structure of the present invention comprises a
본 발명의 방수구조체(1)는 콘크리트로 구조물, 발포수지, 목재, 유류 저장탱크, 집수탱크, 하수처리시설, 수영장, 주차장바닥, 정화조, 정수장 및 각종 수처리 구조물, 교량 상판이나 교각 등과 같은 다양한 재질 및 용도의 것일 수 있다.
The waterproofing structure (1) of the present invention can be applied to various materials such as concrete structure, foamed resin, wood, oil storage tank, collecting tank, sewage treatment facility, swimming pool, parking lot floor, purification tank, water treatment plant and various water treatment structures, bridge top plate, And may be of a purpose.
상기 방수구조체의 세척작업 등이 완료되면 방수구조체 상에 프라이머로서 침투식 액체 방수제를 도포한다. 상기 침투식 액체 방수제 프라이머는 콘크리트 등의 방수구조체 표면에 침투되어 표면을 강화시키고, 이후 도포되는 아스팔트층과 결합하여 접착력을 향상시킬 수 있다.
When the washing operation of the waterproof structure is completed, the water repellent liquid waterproofing agent is applied as a primer on the waterproof structure. The penetrating liquid waterproofing primer may penetrate the surface of the waterproofing structure such as concrete to strengthen the surface, and then may bond with the applied asphalt layer to improve the adhesive strength.
본 발명의 침투식 액체 방수제 프라이머는 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 것을 사용한다.
The penetration liquid waterproofing primer of the present invention is composed of an acrylic emulsion and EVA (ethylene vinyl acetate).
상기 아크릴에멀젼은 내수성, 내알카리성, 작업성 등이 우수하고 콘크리트, 몰탈미장 등의 바탕면에 깊숙이 침투, 흡수되어 기공, 먼지 등을 바인딩 처리하며 표면을 단단하게 해주며, 상부도포층과의 접착력을 증진시켜주는 역할을 하지만, 방수층의 강도와 조막성능 및 방수성능은 만족스럽지 못한 단점이 있다.
The acrylic emulsion is excellent in water resistance, alkali resistance, workability, and penetrates and absorbs deeply into the base surface of concrete, mortar, etc. to bind and treat pores and dust, and hardens the surface. But the strength of the waterproof layer, the film forming performance and the waterproof performance are unsatisfactory.
또한, EVA(에틸렌비닐아세테이트)는 방수층의 강도와 부착성 및 방수성을 향상시키기 위한 것으로, 상기 아크릴에멀젼과 함께 사용하게 되면 방수층의 강도와 조막성능, 탄성 및 방수성능을 향상시킬 수 있으므로 본 발명에서는 상기 아크릴 에멀젼 및 EVA(에틸렌비닐아세테이트)를 포함하여 조성되는 프라이머를 침투식 액체 방수제로 사용한다.
EVA (ethylene vinyl acetate) is used for improving the strength, adhesion and waterproofness of the waterproof layer. When used together with the acrylic emulsion, the strength, film forming performance, elasticity and waterproof performance of the waterproof layer can be improved. A primer composed of the acrylic emulsion and EVA (ethylene vinyl acetate) is used as the penetrating liquid waterproofing agent.
[도 2]를 참조하면, 상기 보강그리드층(4) 상에는 제2아스팔트층(5)이 더 도포될 수 있는데, 상기 제2아스팔트층은 일반적으로 방수시공되는 것으로 상세한 설명은 생략한다.
Referring to FIG. 2, a
상기 제1아스팔트층 상에 배열되는 보강그리드층(4)은 수축,팽창으로 인한 장력을 흡수하고 제1아스팔트층(3) 및 노출방수재층(6)에 작용하는 전단강도를 흡수할 수 있으며 제1아스팔트층(3)으로부터 발생되는 수증기의 압력을 제거하여 제1아스팔트층의 균열을 예방할 수 있는 효과가 있다.
The reinforcing
상기 보강그리드는 탄소섬유그리드, 유리섬유그리드, 합성수지그리드 또는 부직포를 사용하는 것이 바람직하다.
The reinforcing grid preferably comprises a carbon fiber grid, a glass fiber grid, a synthetic resin grid or a nonwoven fabric.
상기 제1아스팔트층(3) 또는 상기 보강그리드층(4) 또는 상기 제2아스팔트층(5)상에 도포되는 노출방수재층(6)은 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 폐연마재분말, 순환골재분말, 시멘트분말을 포함하여 구성되는 무기질계 분체가 혼합된 복합 하이브리드 방수재를 도포하여 형성한다.
The exposed
상기 복합 하이브리드 방수재를 사용하여 노출방수재층(6)을 형성하게 되면, 아크릴계 공중합 액상수지에 혼합된 무기질계 분체는 콘크리트 미세 셀(cell) 사이로 침투되어 콘크리트와 결합되어 복합 하이브리드 방수재와 콘크리트와의 부착강도를 증강시키게 되는데, 이때, 무기질계 분체는 폐연마재분말, 순환골재분말, 시멘트분말을 포함하여 구성되는 것이 바람직하다.
When the impregnated
상기와 같이, 부착강도 및 인장강도가 우수하게 발현되는 이유는 아크릴레이트 및 메타아크릴레이트의 -COOH기가 고분자 말단에 존재하여 분체의 무기질 재료에 존재하는 양이온(나트륨이온, 칼슘이온, 마그네슘이온 등)과 매우 강력한 이온결합을 형성하므로 강한 부착강도와 인장강도를 발현시키게 되고, 상기 무기질 분체로 인하여 에어포켓이 발생되지 않으며, 표면조도가 우수하게 되기 때문이다.
As described above, the adhesion strength and the tensile strength are excellently expressed because the -COOH groups of acrylate and methacrylate are present at the end of the polymer and the cations (sodium ion, calcium ion, magnesium ion, etc.) present in the inorganic material of the powder, And thus exhibits strong bonding strength and tensile strength, and air pockets are not generated due to the inorganic powder, and the surface roughness is excellent.
또한, 상기 아크릴계 공중합 액상수지는 내균열성이 우수한 유기계 액상수지로서 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되며, 이때, 아크릴레이트 및 메타아크릴레이트과 부타디엔고무 라텍스를 공중합시키므로써 내균열성 뿐만 아니라 부타디엔고무 라텍스의 접착성 및 탄성을 부가하여 우수한 방수내구성을 발현할 수 있다.
The acrylic copolymer liquid resin is prepared by copolymerizing a composition containing an acrylate, a methacrylate and a butadiene rubber latex as an organic liquid resin excellent in crack resistance, wherein the acrylate, methacrylate and butadiene rubber latex are copolymerized , So that not only crack resistance but also adhesion and elasticity of butadiene rubber latex can be added to exhibit excellent waterproof durability.
또한, 상기 노출방수재층(6)은 아크릴레이트, 메타아크릴레이트 및 부타디엔고무 라텍스를 포함하는 조성물을 공중합시켜 제조되는 아크릴계 공중합 액상수지에 급결시멘트를 혼합한 복합 하이브리드 방수재를 도포하여 형성할 수 있는데, 상기 급결시멘트를 사용하는 경우에는 고속도로 등과 같은 급결이 필요한 부분에 사용할 수 있다.
The exposed
또한, 상기 노출방수재층(6)은 MMA수지(Methyl Metacrylate)에 칼라규사를 혼합 포함하여 구성되는 복합 하이브리드 방수재를 도포하여 형성할 수 있으며, 친환경적이며 자연경화할 수 있는 인보도 또는 자전거도로 방수에 사용할 수 있다.
The exposed
또한, 상기 노출방수재층(6)은 1액형 또는 2액형 우레탄 바인더에 슬래그 볼(PS Ball) 및 칼라규사를 혼합 포함하여 구성되는 복합 하이브리드 방수재를 도포하여 형성할 수 있으며, 이 때, 칼라규사혼합으로 인해 PS Ball만 섞여있는 그것에 비하여 높은 강도를 나타내고, 검은색의 PS Ball과 칼라규사가 일정비율로 섞여 색상이 발현될 수 있다.
The exposed
아울러, [도 2]에 도시한 바와 같이, 상기 보강그리드층(4) 상부 및 상기 노출방수재층(6) 사이에는 제2아스팔트층(5)이 더 도포될 수 있는데, 이는 상기 보강그리드층(4)을 보강하면서 상기 노출방수재층(6)과의 부착력을 더욱 향상시키고 방수성능을 높이기 위한 것이다.
2, a
한편, 본 발명의 복합 방수구조는 방수구조체 상에 침투식 액체 방수제를 도포하는 단계; 상기 침투식 액체 방수제층 상에 제1아스팔트를 도포하는 단계; 상기 아스팔트층 상에 노출방수재를 도포하는 단계;를 포함하는 복합 방수구조 시공공법으로 시공될 수 있으며, 이 때, 상기 제1아스팔트 상부 및 상기 노출방수재 사이에는 보강그리드를 배열 적층하는 단계를 더 포함하거나, 상기 보강그리드 상부 및 상기 노출방수재 사이에는 제2아스팔트를 도포 적층하는 단계를 더 포함하여 시공될 수 있다.
On the other hand, the composite waterproofing structure of the present invention includes the steps of applying a water permeable liquid waterproofing agent on a waterproofing structure; Applying a first asphalt on the permeable liquid water repellent layer; And a step of applying an exposed waterproofing material on the asphalt layer. The step of stacking the reinforcing grid on the first asphalt upper part and the exposed waterproofing material may further include the step of laminating the reinforcing grid Or coating the second asphalt layer between the upper part of the reinforcing grid and the exposed waterproofing material.
이상의 설명은 본 발명의 기술사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 도면들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 도면에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.
The foregoing description is merely illustrative of the technical idea of the present invention, and various changes and modifications may be made by those skilled in the art without departing from the essential characteristics of the present invention. Therefore, the drawings disclosed in the present invention are not intended to limit the scope of the present invention and are not intended to limit the scope of the present invention. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.
1 : 방수구조체 2 : 침투식 액체 방수제층
3 : 제1아스팔트층 4 : 보강그리드층
5 : 제2아스팔트층 6 : 노출방수재층1: waterproof structure 2: penetrating liquid waterproofing layer
3: first asphalt layer 4: reinforcing grid layer
5: Second asphalt layer 6: Exposed waterproofing layer
Claims (12)
A waterproof structure of a waterproof structure, comprising: a layer of an infiltrating liquid waterproofing agent applied on the waterproof structure; A first asphalt layer deposited and laminated on the permeable liquid water repellent layer; And an impregnated waterproofing material layer formed on the first asphalt layer, wherein the impregnated liquid waterproofing agent comprises an acrylic emulsion and EVA (ethylene vinyl acetate), and the exposed waterproofing material is selected from the group consisting of acrylate, A composite hybrid waterproofing material comprising an acrylic copolymer liquid resin prepared by copolymerizing a composition comprising a latex and a butadiene rubber latex, and an inorganic powder including a waste abrasive powder, a recycled aggregate powder and a cement powder; Or an acrylic copolymer liquid resin prepared by copolymerizing a composition comprising an acrylate, a methacrylate and a butadiene rubber latex, wherein the acrylic hybrid copolymer is prepared by mixing an acrylic copolymer liquid resin of the hybrid hybrid waterproofing material The -COOH group of the acrylate and methacrylate contained in the cement composition forms an ionic bond with the cations including sodium ions, calcium ions and magnesium ions present in the inorganic powder or the cement so as to develop the adhesion strength and the tensile strength, The inorganic powder mixed in the acrylic copolymer liquid resin or the cement cement penetrates into the concrete fine cells and is bonded with the concrete to develop the bond strength with the concrete. The butadiene rubber latex of the acrylic copolymer liquid resin is an acrylate And methacrylate to add the adhesion and elasticity of the butadiene rubber latex.
상기 제1아스팔트층 상부 및 상기 노출방수재층 사이에는 탄소섬유그리드, 유리섬유그리드, 합성수지그리드 또는 부직포로부터 선택된 보강그리드층을 더 포함하여 적층 구성되는 것을 특징으로 하는 복합 방수구조
The method according to claim 1,
And a reinforcing grid layer selected from a carbon fiber grid, a glass fiber grid, a synthetic resin grid, or a nonwoven fabric is laminated between the upper portion of the first asphalt layer and the exposed waterproofing material layer.
상기 보강그리드층 상부 및 상기 노출방수재층 사이에는 제2아스팔트층을 더 포함하여 적층 구성되는 것을 특징으로 하는 복합 방수구조
3. The method of claim 2,
And a second asphalt layer is disposed between the upper surface of the reinforcing grid layer and the exposed waterproofing material layer.