KR101732416B1 - Opet sheet containing metal layer for furniture and building material, and method for manufacturing the same - Google Patents
Opet sheet containing metal layer for furniture and building material, and method for manufacturing the same Download PDFInfo
- Publication number
- KR101732416B1 KR101732416B1 KR1020150133305A KR20150133305A KR101732416B1 KR 101732416 B1 KR101732416 B1 KR 101732416B1 KR 1020150133305 A KR1020150133305 A KR 1020150133305A KR 20150133305 A KR20150133305 A KR 20150133305A KR 101732416 B1 KR101732416 B1 KR 101732416B1
- Authority
- KR
- South Korea
- Prior art keywords
- metal layer
- opet
- sheet
- furniture
- film
- Prior art date
Abstract
본 발명은 가구 및 건축자재용 메탈층을 포함하는 OPET 시트 및 이의 제조방법에 관한 것으로서, 보다 상세하게는 플라스틱, 발포판넬, 스틸(steel) 또는 목질재료인 폼 판넬, 우드, PB, MDF 또는 PW로 이루어진 가구나 건축자재 등에 접착하여 사용가능한 OPET 필름을 포함하는 가구 및 건축자재용 메탈층을 포함하는 OPET 시트 및 이의 제조방법을 제공한다.
본 발명에 따르면 고후도의 OPET 필름을 이용하여 평활도와 내열도가 우수하고, 메탈층을 포함하여 고내후성과 메탈 질감을 나타내는 가구 및 건축자재용 OPET 시트를 제공하는 효과가 있다. 또한 하드코팅을 하여 표면을 보호하고 스크래치를 방지하며 경도를 향상시키는 효과를 제공할 수 있다. The present invention relates to an OPET sheet including a metal layer for furniture and building materials and a method of manufacturing the same. More particularly, the present invention relates to a plastic sheet, a foam panel, a steel panel, a wood panel, And an OPET sheet including a metal layer for furniture and building materials including an OPET film which can be used by being adhered to a building material or the like.
According to the present invention, it is possible to provide an OPET sheet for furniture and building materials which is excellent in smoothness and heat resistance and has a high weather resistance and a metal texture including a metal layer by using an OPET film of Kofudo. In addition, a hard coating can be provided to protect the surface, prevent scratches, and improve hardness.
Description
본 발명은 가구 및 건축자재용 메탈층을 포함하는 OPET 시트 및 이의 제조방법에 관한 것으로서, 보다 상세하게는 목질재료, 플라스틱, 발포판넬 및 스틸(steel) 등에 접착하여 사용 가능한 OPET 필름을 포함하는 가구 및 건축자재용 메탈층을 포함하는 OPET 시트 및 이의 제조방법에 관한 것이다. The present invention relates to an OPET sheet comprising a metal layer for furniture and building materials and a method of manufacturing the same. More particularly, the present invention relates to an OPET sheet comprising an OPET sheet which can be used to adhere to wood materials, plastics, foam panels, And a metal layer for building materials, and a method of manufacturing the OPET sheet.
일반적으로, 시트지는 건물 내부의 인테리어용으로 사용되거나 가구의 표면에 부착하여 장식 또는 가구의 표면을 보호하기 위해 사용된다. 이러한 시트지는 펄프 또는 합성수지를 포함하는데 주로 PVC 필름을 많이 사용하고 있다. In general, a sheet of paper is used for the interior of a building or for attaching to the surface of the furniture to protect the surface of the ornament or furniture. Such sheet includes pulp or synthetic resin, and mainly uses PVC film.
그런데, 종래의 PVC 필름은 내수성과 내유성이 우수하나 내열성과 내용제성이 떨어지고 환경호르몬이 검출되는 약점이 있으며, 화재발생 시에 인체에 치명적인 유독가스를 발생시킨다는 문제가 있었다.However, the conventional PVC film is excellent in water resistance and oil resistance, but has poor heat resistance and solvent resistance, has a weak point of detecting environmental hormones, and has a problem of generating toxic gas which is fatal to the human body in the event of fire.
종래의 PVC 필름의 문제를 해결하기 위해 PVC 필름 대신 GPET 필름을 이용하고 있으나, GPET 필름은 주로 얇은 두께로 생산되기 때문에 경도가 낮아 사용범위가 한정되는 문제점 등이 있었다.In order to solve the problem of the conventional PVC film, the GPET film is used instead of the PVC film. However, since the GPET film is produced mainly in a thin thickness, the hardness is low and the use range is limited.
본 발명은 가구나 건축자재의 표면을 보호하고 장식이 가능하며 유해하지 않은 가구 및 건축자재용 메탈층을 포함하는 OPET 시트 및 이의 제조방법을 제공하는데 목적이 있다.It is an object of the present invention to provide an OPET sheet comprising a metal layer for furniture and building materials which is capable of protecting the surfaces of furniture and building materials and which is decoratable and not harmful, and a method of manufacturing the same.
본 발명은 두께 100㎛ 이상의 OPET(oriented polyethlene terephthalate; OPET) 필름의 일면에 UV 프라이머 처리를 하는 단계; 상기 UV 프라이머 처리된 상부에 메탈층을 형성하는 단계; 상기 메탈층의 상부에 PU(poly urethan; PU) 프라이머 처리를 하는 단계; 및 상기 PU 프라이머 처리된 상부에 하드코팅하는 단계를 포함하는 가구 및 건축자재용 메탈층을 포함하는 PET 시트 제조방법을 제공한다. The present invention relates to a process for producing a polyimide film, which comprises UV primer treatment on one side of OPET (oriented polyethlene terephthalate) film having a thickness of 100 m or more; Forming a metal layer on the UV primed top; Performing a polyurethane (PU) primer treatment on the metal layer; And hard coating the upper part of the PU primer treated with a metal layer for furniture and building materials.
상기 OPET 필름의 두께는 100㎛ ~ 350 ㎛일 수 있다.The thickness of the OPET film may be 100 mu m to 350 mu m.
상기 OPET 필름은 이축 연신 PET 필름일 수 있다.The OPET film may be a biaxially stretched PET film.
데코필름의 표면 마감이 종래에는 무광이나 단순 엠보 가공이 주류였으나 최근에는 표면 마감이 고광택(high gloss, 광택도 85% 이상)으로 바뀜에 따라 데코필름 후가공(보드에 접착)시 원단의 평활도가 아주 중요한 변수로 떠오르고 있다. 또한 가구용 고광택(high gloss) 시트의 경우 시트의 평활도, 스티프니스(stiffness) 등이 고광택 시트 품질을 확보하는데 매우 중요한 요소이다. 현재 건축자재 및 가구용 데코 필름의 소재로 고광택 시트용 원단은 PVC, GPET가 대부분인데 이 두 원단은 스티프니스(stiffness)가 낮고 내열도가 80 ℃ 이하이기 때문에 평활도, 스티프니스 확보에 한계가 있다. 그러나 본 발명에서 적용하는 OPET는 GPET, PVC 보다 스티프니스와 내열도가 월등히 우수하기 때문에 GPET, PVC의 단점을 극복할 수 있다. 즉 고광택(high gloss) 작업시 펄(pearl) 인쇄, 하드 코팅 등이 용이하고 완성된 제품을 목질 판상재(PB, MDF 등)나 플라스틱 발포폼재, 스틸 플레이트 등에 접착이 쉬워 우수한 고광택 판넬을 제조하기 쉽다. 또한 이축연신 투명 PET(OPET)는 무연신 GPET나 PVC보다 내열도가 아주 우수하고 표면 강도가 강하여 완제품 물성 평가시 확연히 성능 차이를 나타내는바, 고광택 시트의 경우 베이스(base) 원단의 품질에 따라 완제품의 성능이 좌우된다고 할 수 있다. 본원발명은 베이스 원단으로 OPET를 적용함으로써 고평활도와 고내후성을 구현할 수 있는 장점이 있다. The surface finish of the decolor film is conventionally matte or simple embossing. However, recently, as the surface finish is changed to high gloss (more than 85% gloss), the smoothness of the fabric It is emerging as an important variable. Also, in the case of a high gloss sheet for furniture, the smoothness and stiffness of the sheet are very important factors for securing the high gloss sheet quality. Currently, PVC and GPET are used for high-gloss sheet as a material for decorative materials for furniture and furniture. Both of these fabrics have low stiffness and heat resistance of 80 ℃ or less, which limits the smoothness and stiffness. However, since OPET applied in the present invention is much superior in stiffness and heat resistance than GPET and PVC, the drawbacks of GPET and PVC can be overcome. It is easy to make pearl printing, hard coating and so on during high gloss work. It is easy to adhere finished wood products (PB, MDF, etc.), plastic foams and steel plates, easy. In addition, biaxially stretched transparent PET (OPET) exhibits significantly higher heat resistance than non-oriented GPET or PVC and has a strong surface strength, which shows a distinct performance difference in the evaluation of finished product properties. In the case of a high gloss sheet, The performance of the system is influenced. The present invention has an advantage that high smoothness and high weather resistance can be realized by applying OPET as a base fabric.
상기 UV 프라이머는 우레탄, 아크릴레이트 수지 및 광개시제를 1 : 1 : 0.1 의 중량비로 포함하는 것일 수 있으나 이에 제한되는 것은 아니다. 상기 UV 프라이머 처리는 OPET 필름의 일면에 프라이머를 도포하고 UV 경화하는 방법으로 처리할 수 있다. 종래에는 메탈층을 포함할 경우 메탈층이 쉽게 박리되는 문제가 있었으나 본 발명에 따른 UV 프라이머 처리를 수행하는 경우 OPET 필름층에서 메탈층이 쉽게 박리되는 문제를 해결할 수 있다. The UV primer may include but is not limited to urethane, acrylate resin, and photoinitiator in a weight ratio of 1: 1: 0.1. The UV primer treatment can be performed by applying a primer to one side of the OPET film and UV-curing the primer. Conventionally, when a metal layer is included, there is a problem that the metal layer easily peels off. However, when the UV primer treatment according to the present invention is performed, the problem that the metal layer easily peels off the OPET film layer can be solved.
상기 메탈층을 형성하는 단계에서 메탈은 알루미늄, 마그네슘, 구리 및 텅스텐으로 이루어진 군에서 선택될 수 있고, 증착, 스퍼터링 및 메탈잉크인쇄 방법으로 이루어진 군에서 선택되는 방법으로 메탈층을 형성할 수 있다. 이때 메탈층의 두께는 150 내지 700 Å(angstrom)일 수 있고, 바람직하게는 300 내지 450Å이고, 더욱 바람직하게는 400Å일 수 있다.In the step of forming the metal layer, the metal may be selected from the group consisting of aluminum, magnesium, copper and tungsten, and the metal layer may be formed by a method selected from the group consisting of vapor deposition, sputtering and metal ink printing. In this case, the thickness of the metal layer may be 150 to 700 angstroms, preferably 300 to 450 angstroms, and more preferably 400 angstroms.
PU 프라이머는 폴리우레탄과 이소시아네이트를 혼합하여 0.5 내지 1.5㎛ 두께로 메탈층의 상부에 도포하고 35 내지 60℃에서 60 내지 80시간 동안 숙성시켜 열가소성 수지를 열경화성 수지로 변화시킬 수 있다. 상기 시간은 바람직하게는 70 내지 80시간일 수 있고, 더욱 바람직하게는 72시간일 수 있다. The PU primer can be applied to the top of the metal layer by mixing polyurethane and isocyanate to a thickness of 0.5 to 1.5 占 퐉 and aged at 35 to 60 占 폚 for 60 to 80 hours to change the thermoplastic resin to a thermosetting resin. The time may preferably be 70 to 80 hours, and more preferably 72 hours.
상기 하드코팅은 UV 경화형 수지 도포 후 경화하는 방법으로 수행할 수 있다. 하드 코팅에 의해 표면 보호, 스크래치 방지, 경도 향상의 효과를 구현할 수 있다.The hard coating may be performed by applying a UV curable resin and then curing. The effect of surface protection, scratch prevention, and hardness improvement can be realized by hard coating.
본 발명은 메탈층을 증착하고 메탈층에 PU 프라이머를 도포한 후 UV 하드코팅을 수행함으로써 유리거울에 가까운 반사도 (약 98~99%의 반사도)를 얻을 수 있으며, 상기 수치 범위에서 가장 우수한 효과를 나타낼 수 있다. 또한 고후도의 투명 OPET를 베이스 원단으로 적용함으로써 우수한 표면 강도나 스티프니스(stiffness), 평활도를 구현할 수 있어 데코용 뿐 아니라 대형 전면 유리 거울을 대체 있는 효과가 있다. 이에 따라 무겁고 깨짐에 대한 위험도가 높은 유리의 단점을 제거할 수 있다. In the present invention, it is possible to obtain a reflectance close to a glass mirror (about 98 to 99% reflectivity) by depositing a metal layer and applying a PU primer to the metal layer and then performing a UV hard coating, . In addition, by applying Kofudo's transparent OPET as a base fabric, it is possible to realize excellent surface strength, stiffness, and smoothness, and it is effective not only for decoration but also for replacing a large front glass mirror. This eliminates the disadvantages of glass, which is heavy and highly dangerous to breakage.
상기 제조된 메탈층을 포함하는 OPET 시트는 UV 프라이머 처리하지 않은 PET의 일면을 코어재에 부착할 수 있다. 이때 UV 프라이머 처리하지 않은 OPET의 일면에 접착제, 프라이머 또는 이형지를 더 포함할 수 있으나 이에 한정되는 것은 아니다. 상기 코어재는 목질재료, 플라스틱, 발포판넬 또는 스틸(steel)일 수 있고, 바람직하게는 폼 판넬, 우드, PB, MDF 또는 PW일 수 있으나 이에 한정되는 것은 아니다. The OPET sheet containing the metal layer thus prepared can adhere one surface of the non-UV primer-treated PET to the core material. At this time, an OPET not treated with UV primer may further include an adhesive, a primer, or a release paper on one side, but is not limited thereto. The core material may be a wood material, plastic, foam panel or steel, preferably a foam panel, wood, PB, MDF or PW but is not limited thereto.
본 발명을 일면이 UV 프라이머 처리된 두께 100㎛ 이상의 OPET 필름; 상기 OPET 필름의 UV 프라이머 처리된 일면에 형성되는 메탈층; 상기 메탈층의 상부에 처리되는 PU 프라이머; 및 상기 PU 프라이머 처리된 상부에 형성되는 하드코팅층을 포함하는 메탈층을 포함하는 OPET 시트를 제공한다. The present invention relates to an OPET film having a thickness of 100 mu m or more, which is UV-primed on one side; A metal layer formed on the UV primer-treated surface of the OPET film; A PU primer treated on top of the metal layer; And a metal layer comprising a hard coating layer formed on the PU primed top.
상기 메탈층에서 메탈은 알루미늄, 마그네슘, 구리 및 텅스텐으로 이루어진 군에서 선택될 수 있다. 상기 메탈층은, 상기 OPET 필름의 UV 프라이머 처리된 면에 증착, 스퍼터링, 및 메탈잉크 인쇄 방법으로 이루어진 군에서 선택되는 방법으로 형성될 수 있다. In the metal layer, the metal may be selected from the group consisting of aluminum, magnesium, copper, and tungsten. The metal layer may be formed by a method selected from the group consisting of vapor deposition, sputtering, and metal ink printing on the UV primer-treated surface of the OPET film.
상기 OPET 필름, UV 프라이머, 메탈층, PU 프라이머 및 하드코팅층은 상기에서 설명한 내용과 동일하므로 여기서는 생략한다. The OPET film, the UV primer, the metal layer, the PU primer and the hard coat layer are the same as those described above, and thus will not be described here.
본 발명에 따르면 고후도의 OPET 필름을 이용하여 평활도와 내열도가 우수하고, 메탈층을 포함하여 고내후성과 메탈 질감을 나타내는 가구 및 건축자재용 PET 시트를 제공하는 효과가 있다. According to the present invention, it is possible to provide a PET sheet for furniture and building materials, which is excellent in smoothness and heat resistance, and exhibits high weatherability and metal texture including a metal layer, using OPFET film of Kofudo.
또한 하드코팅을 하여 표면을 보호하고 스크래치를 방지하며 경도를 향상시키는 효과를 제공한다.It also provides a hard coating that protects the surface, prevents scratches and improves hardness.
아울러 본원발명은 메탈층을 증착하고 메탈층에 PU 프라이머를 도포한 후, UV 하드코팅을 함으로써 유리 거울에 가까운 반사도를 얻을 수 있다. 또한 고후도의 투명 OPET를 사용함으로써 우수한 표면강도나 스티프니스(stiffness), 평활도를 구현할 수 있어 데코용 뿐 아니라 대형 전면 유리 거울을 대체할 수 있다. 이에 따라 무겁고, 깨짐에 대한 위험도가 높은 유리의 단점을 제거할 수 있다.Further, in the present invention, a reflectivity close to the glass mirror can be obtained by depositing a metal layer, applying a PU primer to the metal layer, and then performing UV hard coating. In addition, by using Kofudo's transparent OPET, excellent surface strength, stiffness, and smoothness can be realized, which can replace large glass front mirrors as well as decor. Accordingly, it is possible to eliminate the disadvantage of the glass which is heavy and has a high risk of breakage.
도 1은 본 발명의 일실시예에 따른 PET 시트를 코어재에 부착한 단면이다.1 is a cross-sectional view of a PET sheet according to an embodiment of the present invention attached to a core material.
이하, 실시예를 통하여 본 발명을 상세하게 설명한다. 본 발명의 목적, 특징, 장점은 이하의 도면 및 실시예를 통하여 쉽게 이해될 것이다. 본 발명은 여기서 설명되는 도면 및 실시예에 한정되지 않고, 다른 형태로 구체화될 수 있다. 여기서 소개되는 도면 및 실시예는 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위하여 제공되는 것이다. 따라서. 이하의 도면 및 실시예에 의하여 본 발명의 권리범위가 제한되어서는 안 된다.Hereinafter, the present invention will be described in detail by way of examples. The objects, features and advantages of the present invention will be readily understood through the following drawings and examples. The present invention is not limited to the drawings and embodiments described herein, but may be embodied in other forms. The drawings and embodiments are provided so that those skilled in the art can fully understand the spirit of the present invention. therefore. The scope of the present invention should not be limited by the following drawings and examples.
<실시예> 가구 및 건축자재용 메탈층 포함 OPET 시트의 제조<Examples> Production of OPET Sheet Containing Metal Layer for Furniture and Building Materials
투명 OPET 필름에 양면을 코로나 처리하고 상기 코로나 처리된 OPET 필름에 UV 프라이머 처리를 수행하였다. 이때 상기 프라이머는 1㎛의 두께로 코팅한 후 365 nm의 UV를 10초간 조사하는 방법으로 수행하였다. 그 후 알루미늄을 이용하여 스퍼터링 증착하여 약 400 Å 두께의 메탈층을 형성하였다. 그 다음 메탈층 위에 PU 프라이머 처리하였다. PU 프라이머는 1㎛의 두께로 코팅한 후 42℃에서 72시간 동안 숙성시키는 방법으로 수행하였다. 그 후 PU 프라이머 처리된 상부에 UV 경화형 수지를 도포한 후 경화시켜 하드코팅층을 형성함으로써 메탈층을 포함하는 OPET 시트를 제조하였다. 제조된 OPET 시트의 단면을 도 1에 나타내었다. Both sides of the transparent OPET film were corona treated and the corona treated OPET film was subjected to UV primer treatment. At this time, the primer was coated with a thickness of 1 탆 and irradiated with 365 nm UV for 10 seconds. Thereafter, aluminum was sputter deposited to form a metal layer having a thickness of about 400 Å. The metal layer was then primed with PU. The PU primer was coated at a thickness of 1 mu m and then aged at 42 DEG C for 72 hours. Then, an OPET sheet containing a metal layer was prepared by applying a UV curable resin on the PU primed top and curing it to form a hard coat layer. The cross section of the prepared OPET sheet is shown in Fig.
<비교예> <Comparative Example>
투명 PET에 알루미늄을 증착한 후 증착면에 접착제를 도포하여 증착면에 PVC를 접착한 다음 증착 반대면에 하드코팅을 수행하여 PET 메탈 시트를 제조하였다.Aluminum was deposited on transparent PET, then adhesive was applied on the deposition surface, PVC was adhered to the deposition surface, and hard coating was performed on the opposite side of the deposition to produce a PET metal sheet.
일반적으로 가구 및 가전용 데코필름으로 사용하는 종래의 메탈 시트(비교예 )는 투명 PET의 두께를 고후도로 올리는데 한계가 있었다. 또한 투명 PET 층의 헤이즈(haze)가 높기 때문에 미러(mirror)용으로 사용할 수가 없었다. 본 발명은 이를 보완하기 위한 것으로 증착된 메탈층에 PU 프라이머를 도포한 후 UV 하드코팅을 수행함으로써 유리 거울에 가까운 반사도를 얻을 수 있으며 또한 종래 방법과 다르게 PVC나 다른 원단을 합지할 필요가 없다. 또한 고후도 투명 OPET를 사용함으로써 우수한 표면강도나 스티프니스(stiffness), 평활도 등을 구현할 수 있어 데코용 뿐만 아니라 대형 전면 유리 거울을 대체할 수 있는 효과가 있다. 이에 따라 무겁고 깨짐에 대한 위험도가 높은 유리의 단점을 제거할 수 있다. In general, a conventional metal sheet (comparative example) used as a decorative film for furniture and home appliances has a limitation in raising the thickness of transparent PET to a high degree. Further, since the transparent PET layer has a high haze, it can not be used for a mirror. In order to compensate for this, the present invention can provide a reflectivity close to the glass mirror by applying the PU primer to the deposited metal layer and then performing UV hard coating, and it is not necessary to laminate PVC or other fabric unlike the conventional method. In addition, by using Kokudo transparent OPET, excellent surface strength, stiffness and smoothness can be realized, which can replace a large front glass mirror as well as a decoration. This eliminates the disadvantages of glass, which is heavy and highly dangerous to breakage.
110: OPET 필름 111: UV 프라이머
112: 메탈층 113: PU 프라이머
114: 하드코팅층 115: 접착제
116: 코어재110: OPET film 111: UV primer
112: metal layer 113: PU primer
114: hard coating layer 115: adhesive
116: core material
Claims (6)
두께 100㎛ 이상의 OPET(oriented polyethlene terephthalate) 필름의 일면에 UV 프라이머 처리를 하는 단계;
상기 UV 프라이머 처리된 상부에 메탈층을 형성하는 단계;
상기 메탈층의 상부에 PU(polyurethane) 프라이머 처리를 하는 단계; 및
상기 PU 프라이머 처리된 상부에 하드코팅하는 단계를 포함하는
메탈층을 포함하는 OPET 시트 제조방법.
1. A method for producing an OPET sheet comprising a metal layer for furniture and building materials to be adhered to a core material composed of woody material, plastic, foam panel or steel,
A UV primer treatment on one side of an oriented polyethlene terephthalate (OPET) film having a thickness of 100 占 퐉 or more;
Forming a metal layer on the UV primed top;
Performing a PU (polyurethane) primer treatment on the metal layer; And
And hard coating the PU primed tops
A method for producing an OPET sheet comprising a metal layer.
상기 메탈층을 형성하는 단계에서 메탈은
알루미늄, 마그네슘, 구리 및 텅스텐으로 이루어진 군에서 선택되는 것을 특징으로 하는
메탈층을 포함하는 OPET 시트 제조방법.
The method according to claim 1,
In the step of forming the metal layer,
Aluminum, magnesium, copper, and tungsten.
A method for producing an OPET sheet comprising a metal layer.
상기 메탈층을 형성하는 단계는
스퍼터링, 증착 및 메탈잉크인쇄 방법으로 이루어진 군에서 선택되는 방법으로 메탈층을 형성하는 것을 특징으로 하는
메탈층을 포함하는 OPET 시트 제조방법.
The method according to claim 1,
The step of forming the metal layer
Wherein the metal layer is formed by a method selected from the group consisting of sputtering, vapor deposition, and metal ink printing method
A method for producing an OPET sheet comprising a metal layer.
일면이 UV 프라이머 처리된 두께 100㎛ 이상의 OPET 필름;
상기 OPET 필름의 UV 프라이머 처리된 일면에 형성되는 메탈층;
상기 메탈층의 상부에 처리되는 PU 프라이머; 및
상기 PU 프라이머 처리된 상부에 형성되는 하드코팅층을 포함하는
메탈층을 포함하는 OPET 시트.
An OPET sheet comprising a metal layer for furniture and building materials used by adhering to a core composed of woody material, plastic, foam panel or steel,
An OPET film having a thickness of 100 mu m or more on one side of which is UV primed;
A metal layer formed on the UV primer-treated surface of the OPET film;
A PU primer treated on top of the metal layer; And
And a hard coat layer formed on the PU primed upper portion
An OPET sheet comprising a metal layer.
상기 메탈층에서 메탈은
알루미늄, 마그네슘, 구리 및 텅스텐으로 이루어진 군에서 선택되는 것을 특징으로 하는
메탈층을 포함하는 OPET 시트.
The method of claim 4,
In the metal layer,
Aluminum, magnesium, copper, and tungsten.
An OPET sheet comprising a metal layer.
상기 메탈층은
상기 OPET 필름의 UV 프라이머 처리된 면에,
스퍼터링, 증착 및 메탈잉크인쇄 방법으로 이루어진 군에서 선택되는 방법으로 형성되는 것을 특징으로 하는
메탈층을 포함하는 OPET 시트.The method of claim 4,
The metal layer
On the UV primer treated side of the OPET film,
Sputtering, vapor deposition, and metal ink printing method.
An OPET sheet comprising a metal layer.