KR101436942B1 - Additive composition for starch-based adhesive and use of the same - Google Patents

Additive composition for starch-based adhesive and use of the same Download PDF

Info

Publication number
KR101436942B1
KR101436942B1 KR1020120156014A KR20120156014A KR101436942B1 KR 101436942 B1 KR101436942 B1 KR 101436942B1 KR 1020120156014 A KR1020120156014 A KR 1020120156014A KR 20120156014 A KR20120156014 A KR 20120156014A KR 101436942 B1 KR101436942 B1 KR 101436942B1
Authority
KR
South Korea
Prior art keywords
starch
based adhesive
weight
additive composition
parts
Prior art date
Application number
KR1020120156014A
Other languages
Korean (ko)
Other versions
KR20140086023A (en
Inventor
권오윤
양다혜
조영모
전영승
Original Assignee
대상 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 대상 주식회사 filed Critical 대상 주식회사
Priority to KR1020120156014A priority Critical patent/KR101436942B1/en
Publication of KR20140086023A publication Critical patent/KR20140086023A/en
Application granted granted Critical
Publication of KR101436942B1 publication Critical patent/KR101436942B1/en

Abstract

본 발명의 일 예는 저점도화 과정을 거치지 않은 일반전분 또는 변성전분, 저점도화 전분, 수용성 무기물 및 점착성 개선제를 포함하는 전분계 접착제용 첨가제 조성물을 제공한다. 본 발명에 따른 전분계 접착제용 첨가제 조성물을 이용하여 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조시 필요한 캐리어부 또는 메인부를 형성할 수 있다. 본 발명에 따른 전분계 접착제용 첨가물 조성물로부터 제조된 전분계 접착제는 점도 안정성 및 도포성이 양호하고, 향상된 접착력을 나타낸다. 또한, 본 발명에 따른 전분계 접착제용 첨가물 조성물을 사용하는 경우 전분계 접착제의 물성을 일정 수준으로 유지시키면서 동시에 일반 전분의 사용량을 절감할 수 있다.One example of the present invention provides an additive composition for starch-based adhesives comprising general starch or modified starch, low-viscosity starch, a water-soluble inorganic substance and a tackiness-improving agent which have not undergone a low-viscosity process. The additive composition for a starch-based adhesive according to the present invention can be used to form a carrier part or a main part necessary for manufacturing a starch-based adhesive by a one-tank method or a two-tank method. The starch-based adhesive prepared from the additive composition for a starch-based adhesive according to the present invention exhibits good viscosity stability and coatability and exhibits improved adhesion. In addition, when the additive composition for a starch-based adhesive according to the present invention is used, the physical properties of the starch-based adhesive can be maintained at a certain level and the amount of the starch used can be reduced.

Description

전분계 접착제용 첨가제 조성물 및 이의 용도{Additive composition for starch-based adhesive and use of the same}Additive compositions for starch-based adhesives and uses thereof -

본 발명은 전분계 접착제용 첨가제 조성물 및 이의 용도에 관한 것으로서, 더 상세하게는 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 캐리어부 또는 메인부에 첨가되어 캐리어부나 메인부를 형성할 수 있는 첨가제 조성물 및 이의 용도에 관한 것이다.The present invention relates to an additive composition for a starch-based adhesive and a use thereof, and more particularly to an additive composition for a starch-based adhesive which is used in a starch-based adhesive manufacturing process by a one-tank or two- To an additive composition which can be added to a main portion to form a carrier portion or a main portion, and a use thereof.

골판지(corrugated board)는 도 1에서 보이는 바와 같이 원판지(liner; 라이너지라고도 함)에 파형의 골심지(corrugating medium; 중심지라고도 함)를 접착제로 붙여서 만든 판지로서 도 2에서 보이는 바와 같이 원판지와 골심지로 이루어진 기본 판지의 수에 따라 편면골판지(single faced corrugated board), 양면골판지(double faced, single wall), 이중양면골판지(double wall), 삼중양면골판지(triple wall) 등으로 나누어진다. 골판지는 비교적 적은 무게의 재료를 사용하면서도 높은 압축강도를 나타내고 동시에 완충도가 높기 때문에 주로 포장용 상자 제조에 사용된다. 판지초지기(板紙抄紙機)에 의하여 생산된 평량(坪量) 180∼400g/㎡의 라이너지와 평량 120∼150g/㎡의 골심지 두루마리를 코루게이터(corrugating machine)에 걸어 기계를 작동시키면, 골심지에 물결 모양의 일정한 골이 만들어짐과 동시에 라이너지와 접착되어 골판지가 만들어지는데, 이때 라이너지와 골심지의 접착을 위해 일반적으로 전분계 접착제가 사용된다.A corrugated board is a cardboard made by adhering a corrugating medium (also referred to as a center) to a liner (also referred to as a liner) as shown in FIG. 1, Depending on the number of corrugated baseboards, it is divided into a single faced corrugated board, a double faced, single wall, a double wall, and a triple wall. Corrugated cardboard is mainly used in the manufacture of packaging boxes because of its high compressive strength and high buffering capacity, while using relatively small weight materials. When liner paper with basis weight of 180-400 g / m 2 produced by cardboard paper machine and paper roll of 120-150 g / m 2 basis weight is put on a corrugating machine and the machine is operated, The corrugated board is made by attaching to the liner paper at the same time as the corrugated paper is formed. In this case, a starch-based adhesive is generally used for bonding the liner paper to the corrugated paper.

골판지의 제조에 사용되는 전분계 접착제는 스테인 홀(Stein Hall) 방식이나 노 캐리어(no carrier) 방식이라 불리는 제호 방법으로 제조된다. 스테인 홀 제호방식은 캐리어(carrier)부라고 불리는 알칼리 호화한 전분계와 메인(main)부라고 불리는 미호화 전분의 슬러리와 혼합물로 이루어지며, 하나의 반응기에서 캐리어부와 메인부를 연속적으로 형성시켜 접착제를 제조하는 원 탱크(one tank) 제호 방식과 별도의 반응기에서 캐리어부와 메인부를 형성하고, 캐리어부와 메인부를 혼합하여 접착제를 제조하는 투 탱크(two tank) 제호 방식으로 구분할 수 있다. 또한, 노 캐리어 제호 방식은 하나의 반응기에 물과 전분을 넣고 전분 슬러리를 만든 후, 수산화칼슘을 첨가하여 적정한 점도에 이르렀을 때 붕산(또는 붕사)을 가하여 반응을 정지하여 접착제를 만드는 방식을 말한다.The starch-based adhesives used for the production of corrugated board are manufactured by a method called a stein hole method or a no carrier method. The stain hole finishing system is composed of a mixture of a slurry of an alkali-enriched starch system called a carrier unit and a slurry of a finely divided starch called a main part, and the carrier part and the main part are continuously formed in one reactor, A two tank system in which a carrier unit and a main unit are formed in a reactor separate from the one tank manufacturing system in which the carrier unit and the main unit are combined to produce an adhesive. In addition, in the no carrier method, water and starch are added to one reactor to prepare a slurry of starch, and calcium hydroxide is added to the reactor to form an adhesive by adding boric acid (or borax) to stop the reaction when a suitable viscosity is reached.

최근 들어 국내 골판지 시장에서는 크기가 작은 상자의 수요가 증가하고 있으며, 물류비의 감소를 위하여 압축강도가 강한 강화 골심지를 이용하여 이중양면 골판지를 양면 골판지로 생산하는 기술의 수요 또한 증가하고 있는 추세이며, 실제로 물품 수요에 있어서 양면 골판지의 비중이 증가하고 있는 상황이다. 그러나 현재 상용되는 골판지의 강도를 개선하기 위하여 생산된 강화 골심지는 밀도가 높거나 표면에 전분이 코팅되어 있어, 일반전분을 사용하는 골판지 접착제의 접착 성능이 저하되어 골판지의 품질 불량이 증가하고 있다. 또한, 골판지 제조에 사용되는 원단의 종류가 다양하고 품질변화가 심하며, 최근에 코루게이터(corrugator)의 속도가 빨라짐에 따라 접착력이 저하되는 문제가 있어 이를 개선할 수 있는 골판지 접착제의 개발이 요구되고 있는 실정이다.In recent years, the demand for small size boxes has increased in the domestic corrugated cardboard market. In order to reduce the distribution cost, the demand for the technology of producing the double-sided corrugated cardboard with double-sided corrugated cardboard using the reinforced corrugated cardboard having a high compressive strength is also increasing. In fact, the proportion of double-sided corrugated cardboard is increasing in terms of demand for goods. However, in order to improve the strength of the corrugated board, corrugated cardboards produced by using the common starch have poor quality due to high density or coated with starch on the surface. In addition, there are various types of fabrics used for manufacturing corrugated cardboard, quality changes are severe, and adhesion of corrugator is lowered as speed of corrugator is recently increased. Therefore, it is required to develop a corrugated cardboard adhesive which can improve the corrugated cardboard In fact.

골판지용 전분계 접착제 제조 기술로 대한민국등록특허공보 제10-0818579호에는 저점도화 과정을 거치지 아니한 일반전분 또는 변성전분, 저점도화 전분, 및 콜로이드성 무기물을 포함하는 접착제 조성물이 개시되어 있으나, 상기 접착제 조성물은 전분계 접착제를 장기간 보관시 콜로이드성 무기물의 침전으로 인해 보관 안정성이 떨어지는 문제가 있고, 이로 인해 품질의 신뢰성이 저하될 수 있다. 또한, 콜도이드성 무기물의 침전을 억제하기 위해 전분계 접착제의 점도를 높게 유지하는 경우 일반 전분의 사용량이 늘어나고 원지로의 도포성 및 침투성이 떨어지는 문제가 있다. 또한, 대한민국등록특허공보 제10-1186071호에는 일반전분 또는 변성전분, 저점도화 전분, 콜로이드성 무기물 및 잉크 함유 폐수를 포함하는 접착제 조성물이 개시되어 있으나, 상기 접착제 조성물은 장기간 보관시 콜로이드성 무기물의 침전으로 인해 보관 안정성이 떨어지는 문제뿐만 아니라 노 캐리어 제호 방식에만 적용되는 한계를 가진다.Korean Patent Publication No. 10-0818579 discloses an adhesive composition comprising common starch or modified starch, low-viscosity starch, and colloidal inorganic material not subjected to a low-viscosity process as a technique for producing a starch-based adhesive for corrugated cardboard, The composition has a problem that storage stability of the starch-based adhesive is deteriorated due to precipitation of colloidal inorganic material when stored for a long period of time, which may deteriorate the reliability of the quality. In addition, when the viscosity of the starch-based adhesive is kept high in order to suppress the precipitation of the colloidal inorganic material, there is a problem that the amount of the common starch used is increased and the applicability to the raw paper is poor. In addition, Korean Patent Publication No. 10-1186071 discloses an adhesive composition comprising common starch or modified starch, low-viscosity starch, colloidal inorganic substance, and ink containing wastewater. However, There is a problem that not only storage stability is lowered due to sedimentation, but also there is a limit to be applied only to the no carrier method.

한편, 골판지용 전분계 접착제 제조시 사용되는 상업적인 첨가제로 타피오카 저점도 변성전분인 AMYLOK A(공급자 : National Starch and Chemical Co., 미국)와 일반 전분과 용해성 고분자가 혼합된 프리믹스 형태의 제품인 "강력분말"(공급자 : 화진 케미칼, 대한민국)이 있다. 이 중 AMYLOK A를 사용한 골판지용 전분계 접착제는 접착력이 상대적으로 떨어지고, 소정의 접착력을 유지하기 위해서는 일반 전분을 일정량 이상으로 사용하면서 동시에 수산화나트륨 및 붕사의 첨가량을 상향조절해야 하는 문제가 있다. 또한, "강력분말"은 골판지용 전분계 접착제 제조시 고분자에 의해 풀의 엉김 현상이 발생하고 이를 해결하기 위해 교반 속도를 높이거나 및 교반 시간을 늘려야 하는 문제가 있으며, 엉김 현상의 발생으로 인해 전분계 접착제의 도포성이 떨어지는 문제가 있다.On the other hand, as a commercial additive used in the production of a starch-based adhesive for corrugated cardboard, AMYLOK A (supplier: National Starch and Chemical Co., USA), which is a tapioca low viscosity modified starch and a premixed product of a general starch and a soluble polymer "(Supplier: Hwajin Chemical, Korea). Among them, the starch-based adhesive for corrugated cardboard using AMYLOK A is relatively low in adhesive strength, and in order to maintain a predetermined adhesive strength, there is a problem that the addition amount of sodium hydroxide and borax must be adjusted upwards while using a common starch over a certain amount. In addition, "strong powder" is a problem in that when the starch-based adhesive for corrugated cardboard is produced, aggregation of the paste occurs due to the polymer, and in order to solve this problem, there is a problem of increasing the stirring speed and increasing the stirring time. There is a problem that the applicability of the adhesive is deteriorated.

본 발명은 종래 문제점을 해결하기 위해 도출된 것으로서, 본 발명의 일 목적은 전분계 접착제의 점도 안정성, 도포성 또는 접착력을 향상시키면서 동시에 전분계 접착제 제조시 일반 전분의 사용량을 절감할 수 있는 전분계 접착제용 첨가제 조성물을 제공하는데에 있다.It is an object of the present invention to provide a starch-based adhesive which can improve the viscosity stability, coatability or adhesive strength of a starch-based adhesive while reducing the amount of common starch used in the production of starch- And to provide an additive composition for an adhesive.

또한, 본 발명의 다른 목적은 전분계 접착제용 첨가제 조성물의 용도를 제공하는데에 있다.Another object of the present invention is to provide a use of an additive composition for a starch based adhesive.

또한, 본 발명의 또 다른 목적은 전분계 접착제 및 이의 제조방법을 제공하는데에 있다.Still another object of the present invention is to provide a starch-based adhesive and a method for producing the same.

본 발명의 발명자는 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되어 캐리어부 또는 메인부를 형성할 수 있는 첨가제 조성물을 연구하던 중 첨가제 조성물의 일 성분으로 수용성 무기물 및 특정 점착성 개선제를 포함하고, 이를 저점도화 과정을 거치지 않은 전분과 저점도화 전분과 일정 함량으로 조화시키는 경우 전분계 접착제의 점도 안정성, 도포성 또는 접착력을 향상시키면서 동시에 전분계 접착제 제조시 일반 전분의 사용량을 절감할 수 있다는 점을 발견하고 본 발명을 완성하였다.The inventors of the present invention have been studying an additive composition capable of forming a carrier portion or a main portion by being used in a starch-based adhesive manufacturing process by a one-tank or two- The present invention relates to a starch-based adhesive composition which contains a water-soluble inorganic substance and a specific tackiness-improving agent as one component, and when the starch-based adhesive is harmonized with a low-viscosity starch and a low- It is possible to reduce the amount of common starch used in the preparation, and thus the present invention has been completed.

본 발명의 일 목적을 해결하기 위하여, 본 발명의 일 예는 전체 중량을 기준으로 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 55~85 중량%, 저점도화 전분 6~18 중량%, 수용성 무기물 3~14 중량% 및 점착성 개선제 3~14 중량%를 포함하고, 상기 점착성 개선제는 로진(rosin), 열가소성 비닐계 수지, 열가소성 변성 셀룰로오스 및 카제인으로 이루어진 군에서 선택된 1종 이상인 것을 특징으로 하는 전분계 접착제용 첨가제 조성물을 제공한다. 또한, 본 발명의 다른 예는 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정 중 캐리어부 제조시 사용되는 조성물로서, 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 저점도화 전분 3~10 중량부, 수용성 무기물 2~8 중량부 및 점착성 개선제 2~8 중량부를 포함하고, 상기 점착성 개선제는 로진(rosin), 열가소성 비닐계 수지, 열가소성 변성 셀룰로오스 및 카제인으로 이루어진 군에서 선택된 1종 이상인 것을 특징으로 하는 전분계 접착제용 첨가제 조성물을 제공한다. 또한, 본 발명의 또 다른 예는 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정 중 메인부 제조시 사용되는 조성물로서, 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 저점도화 전분 0.5~1.5 중량부, 수용성 무기물 0.3~1.2 중량부 및 점착성 개선제 0.3~1.2 중량부를 포함하고, 상기 점착성 개선제는 로진(rosin), 열가소성 비닐계 수지, 열가소성 변성 셀룰로오스 및 카제인으로 이루어진 군에서 선택된 1종 이상인 것을 특징으로 하는 전분계 접착제용 첨가제 조성물을 제공한다.
In order to solve one object of the present invention, an example of the present invention is a starch composition comprising 55 to 85% by weight of general starch or modified starch, 6 to 18% by weight of low viscosity starch, To 14% by weight of a starch-based adhesive and 3 to 14% by weight of a tackiness-improving agent, wherein the tackiness-improving agent is at least one selected from the group consisting of rosin, thermoplastic vinyl resins, thermoplastic modified cellulose and casein Soluble additive composition. Another example of the present invention is a composition for use in the production of a carrier part in a starch-based adhesive manufacturing process by a one-tank or two-tank tableting method, wherein the starch- 3 to 10 parts by weight of a low viscosity starch per 100 parts by weight of modified starch, 2 to 8 parts by weight of a water soluble inorganic substance and 2 to 8 parts by weight of a tackiness improving agent, wherein the tackiness improving agent is rosin, a thermoplastic vinyl resin, Wherein the additive composition is at least one selected from the group consisting of starch, cellulose, and casein. Another example of the present invention is a composition for use in manufacturing a main part of a starch-based adhesive manufacturing process by a one-tank or two-tank tableting method, 0.5 to 1.5 parts by weight of a low viscosity starch, 0.3 to 1.2 parts by weight of a water-soluble inorganic substance, and 0.3 to 1.2 parts by weight of a tackiness improving agent per 100 parts by weight of starch or modified starch, wherein the tackiness improving agent is rosin, a thermoplastic vinyl resin, Wherein the additive composition is at least one selected from the group consisting of modified cellulose and casein.

본 발명의 다른 목적을 해결하기 위하여, 본 발명은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 캐리어부로서, 물, 상기 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분, 및 알칼리 물질을 포함하는 혼합물 형태이고, 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 및 저점도화 전분은 모두 호화된 상태로 존재하는 것을 특징으로 하는 캐리어부를 제공한다. 또한, 본 발명은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 캐리어부로서, 물, 상기 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물 및 알칼리 물질을 포함하는 혼합물 형태이고, 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 및 저점도화 전분은 모두 호화된 상태로 존재하는 것을 특징으로 하는 캐리어부를 제공한다. 또한, 본 발명은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 메인부로서, 물, 상기 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분, 및 붕소 함유 화합물을 포함하는 혼합물 형태인 것을 특징으로 하는 메인부를 제공한다. 또한, 본 발명은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 메인부로서, 물, 상기 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물 및 붕소 함유 화합물을 포함하는 혼합물 형태인 것을 특징으로 하는 메인부를 제공한다.In order to solve the other object of the present invention, the present invention provides a carrier part used in a starch-based adhesive manufacturing process by a one-tank method or a two-tank method, A starch-based adhesive additive composition according to an example, a starch-based adhesive additive composition according to an example, a starch-modified starch and a starch-free starch, which are not subjected to a low- Or both of the modified starch and the low-viscosity starch exist in an enriched state. In addition, the present invention is a carrier part used in a starch-based adhesive manufacturing process by a one-tank or two-tank tableting method, comprising water, a starch-based adhesive for another example of the present invention An additive composition and an alkaline substance, and the ordinary starch or the modified starch and the low-viscosity starch which are not subjected to the low-viscosity treatment are present in a state of being enriched. In addition, the present invention is a main part used in a starch-based adhesive manufacturing process based on a one-tank or two-tank tableting method, comprising water, a starch-based adhesive for one example of the present invention The present invention provides a main part characterized by an additive composition, an additive composition for a starch-based adhesive, and a mixture containing common starch or modified starch and a boron-containing compound which have not undergone a separate low-viscosity process. In addition, the present invention is a main part used in a starch-based adhesive manufacturing process by a one-tank or two-tank tableting method, comprising water, a starch-based adhesive according to still another embodiment of the present invention Wherein the main component is in the form of a mixture containing a boron-containing additive composition and a boron-containing compound.

본 발명의 또 다른 목적을 해결하기 위하여, 본 발명은 상기 메인부 또는 캐리어부를 포함하는 전분계 접착제를 제공한다.In order to solve still another object of the present invention, the present invention provides a starch-based adhesive comprising the main part or the carrier part.

본 발명에 따른 전분계 접착제용 첨가제 조성물을 이용하여 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조시 필요한 캐리어부 또는 메인부를 형성할 수 있다. 본 발명에 따른 전분계 접착제용 첨가물 조성물로부터 제조된 전분계 접착제는 점도 안정성 및 도포성이 양호하고, 향상된 접착력을 나타낸다. 또한, 본 발명에 따른 전분계 접착제용 첨가물 조성물을 사용하는 경우 전분계 접착제의 물성을 일정 수준으로 유지시키면서 동시에 일반 전분의 사용량을 절감할 수 있다.The additive composition for a starch-based adhesive according to the present invention can be used to form a carrier part or a main part necessary for manufacturing a starch-based adhesive by a one-tank method or a two-tank method. The starch-based adhesive prepared from the additive composition for a starch-based adhesive according to the present invention exhibits good viscosity stability and coatability and exhibits improved adhesion. In addition, when the additive composition for a starch-based adhesive according to the present invention is used, the physical properties of the starch-based adhesive can be maintained at a certain level and the amount of the starch used can be reduced.

도 1은 골판지(corrugated board)의 기본 구조를 나타낸 것이다.
도 2는 골판지의 종류를 나타낸 것이다.1 shows the basic structure of a corrugated board.
Fig. 2 shows the kind of corrugated cardboard.

이하, 본 발명을 구체적으로 설명한다.
Hereinafter, the present invention will be described in detail.

본 발명의 일 측면은 전분계 접착제, 특히 골판지용 전분계 접착제 제조시 사용되는 첨가제 조성물 및 이의 용도에 관한 것이다. 본 발명의 첨가제 조성물로부터 제조된 골판지용 전분계 접착제는 골판지 원지인 라이너(liner)와 골심지의 접착에 사용되는 접착제로서, 골판지 제조시 접착제는 골심지로 전이되고 코루게이터(corrugator)에서 열 및 압력을 받아 접착제 중 전분성분이 완전호화되고, 점도가 급격히 상승함으로써, 초기접착력을 발휘하게 되며 후속공정인 건조공정에서 접착제의 건조와 함께 접착이 완료되게 된다.One aspect of the invention relates to starch based adhesives, in particular additive compositions used in the production of starch based adhesives for corrugated cardboards and their uses. The starch-based adhesive for corrugated cardboard manufactured from the additive composition of the present invention is an adhesive used for bonding corrugated paper with a liner as a corrugated cardboard substrate. In the production of corrugated cardboard, the adhesive is transferred to a corrugated paper sheet and heat and pressure are applied in a corrugator The starch component in the adhesive is completely supergraded and the viscosity is increased so that the initial adhesive force is exerted and the adhesive is completed together with the drying of the adhesive in the subsequent drying process.

본 발명의 전분계 접착제용 첨가제 조성물은 저점도화 과정을 거치지 않은 일반전분 또는 변성전분, 수용성 무기물 및 점착성 개선제를 포함한다. 이하, 본 발명에 따른 전분계 접착제용 첨가제 조성물의 구성성분에 대해 설명한다.
The additive composition for a starch-based adhesive of the present invention includes common starch or modified starch, a water-soluble inorganic substance and a tackiness-improving agent which are not subjected to a low-viscosity process. Hereinafter, constituent components of the additive composition for a starch-based adhesive according to the present invention will be described.

저점도화Low viscosity 과정을 거치지 않은 일반전분 또는 변성전분 Unprocessed ordinary starch or modified starch

본 발명의 전분계 접착제용 첨가제 조성물의 일 성분인 저점도화 과정을 거치지 않은 일반전분 또는 변성전분은 후술하는 산화처리, 산처리 또는 효소처리와 같은 저점도화 과정을 거치지 않은 전분을 의미한다. 상기 저점도화 과정을 거치지 않은 일반전분은 비변성전분과 동일한 의미로 사용되며, 옥수수 전분, 찰옥수수 전분, 타피오카 전분, 감자 전분, 고구마 전분 및 밀 전분으로 이루어지는 군으로부터 선택된 1종 이상으로 구성될 수 있다. 또한, 상기 저점도화 과정을 거치지 않은 변성전분은 옥수수 전분, 찰옥수수 전분, 타피오카 전분, 감자 전분, 고구마 전분 및 밀 전분으로 이루어진 군으로부터 선택된 1종 이상의 일반전분에 에스테르화, 에테르 또는 그라프트 반응을 실시한 전분일 수 있다. 본 발명에서 저점도화 과정을 거치지 않은 일반전분 또는 변성전분은 전분계 접착재 내에서 호화되거나 팽윤된 상태로 존재하며, 골판지 제조시 건조 과정을 거쳐 완전 호화되고 후기 접착력을 발휘한다.
As a component of the additive composition for a starch-based adhesive of the present invention, general starch or modified starch not subjected to a low-viscosity process means starch which has not undergone a low-viscosity process such as oxidation treatment, acid treatment or enzyme treatment described later. The ordinary starch not subjected to the low-viscosity treatment is used in the same sense as the non-modified starch and may be composed of at least one selected from the group consisting of corn starch, waxy corn starch, tapioca starch, potato starch, sweet potato starch and wheat starch have. In addition, the modified starch not subjected to the low-viscosity treatment may be subjected to esterification, ether or graft reaction to at least one general starch selected from the group consisting of corn starch, corn starch, tapioca starch, potato starch, sweet potato starch and wheat starch Lt; / RTI > In the present invention, ordinary starch or modified starch which is not subjected to a low-viscosity process is present in a starch-based adhesive in a state of being swollen or swollen, and undergoes a drying process in the production of a corrugated cardboard,

저점도화Low viscosity 전분 Starch

본 발명의 전분계 접착제용 첨가제 조성물의 일 성분인 저점도화 전분은 옥수수 전분, 찰옥수수 전분, 타피오카 전분, 감자 전분, 고구마 전분 및 밀 전분으로 이루어진 군으로부터 선택된 1종 이상의 일반전분을 이용하여 얻은 산화전분(oxidized starch), 산처리전분(thin boiling starch), 덱스트린 또는 효소처리 전분일 수 있다. 본 발명에서 저점도화 전분은 호화 개시 온도가 낮고 저점도 특성을 가지며, 골판지 제조시 초기 접착력을 발휘하고, 전분계 접착제의 점도 안정성을 향상시킨다. 본 발명에서 저점도화 전분은 50℃에서 20 중량% 호화액의 점도가 바람직하게는 50~400 센티포이즈(centipoise, cPs)의 범위를 갖고, 더 바람직하게 100~350 센티포이즈(centipoise, cPs)는 갖는다.
The low-viscosity starch, which is one component of the additive composition for a starch-based adhesive of the present invention, is an oxidized starch obtained by using at least one general starch selected from the group consisting of corn starch, corn starch, tapioca starch, potato starch, sweet potato starch, An oxidized starch, a thin boiling starch, a dextrin or an enzyme-treated starch. In the present invention, the low-viscosity starch has a low onset temperature and low viscosity, exhibits an initial adhesive strength in the production of corrugated cardboard, and improves the viscosity stability of the starch-based adhesive. In the present invention, the viscosity of the low-viscosity starch at 20 ° C is preferably 50 to 400 centipoise (cPs) at 50 ° C, more preferably 100 to 350 centipoise (cPs) .

수용성 무기물Water-soluble inorganic matter

본 발명의 전분계 접착제용 첨가제 조성물의 일 성분인 수용성 무기물은 전분계 접착제 내에서 용해된 상태로 존재하여 전분계 접착제의 보관 안정성을 향상시키고, 골판지 제조시 저점도화 전분의 초기 접착력을 강화시킨다. 본 발명에서 수용성 물기물은 상기의 조건을 만족하는 것이라면 그 종류가 크게 제한되지 않으며, 예를 들어 규산계 화합물인 것이 바람직하고, 규산나트륨(sodium silicate) 또는 규산칼륨(potassium silicate)과 같은 규산염(silicate salt)인 것이 더 바람직하다. 본 발명에서 규산나트륨은 Na2OㆍnSiO2로 표시되는 규산나트륨염의 총칭이며, 메타규산나트륨(Na2SiO3), 오쏘규산나트륨(Na4SiO4), 이규산나트륨(Na2Si2O5), 사규산나트륨(Na2Si4O9)에서 선택될 수 있으며, 이 중 물에 대한 용해성을 고려할 때 메타규산나트륨(Na2SiO3)인 것이 바람직하다.
The water-soluble inorganic material as one component of the additive composition for a starch-based adhesive of the present invention is present in a dissolved state in the starch-based adhesive to improve the storage stability of the starch-based adhesive and enhance the initial adhesive strength of the low viscosity starch in the production of corrugated board. The water-soluble water in the present invention is not particularly limited as long as it satisfies the above conditions. For example, it is preferably a silicate-based compound, and a silicate such as sodium silicate or potassium silicate silicate salt). And sodium silicate in the present invention are collectively Sodium salt expressed by Na 2 O and nSiO 2, meta-sodium silicate (Na 2 SiO 3), an ortho sodium silicate (Na 4 SiO 4), sodium (Na 2 Si2O 5) yigyu acid , And sodium saccharinate (Na 2 Si 4 O 9 ). Of these, sodium metasilicate (Na 2 SiO 3 ) is preferable in view of solubility in water.

점착성 개선제Adhesion improver

본 발명의 전분계 접착제용 첨가제 조성물의 일 성분인 점착성 개선제는 골판지 제조시 건조 과정을 거치는 동안 열에 의해 가소화되고 저점도화 과정을 거치지 않은 일반전분 또는 변성전분의 후기 접착력을 강화시킨다. 본 발명에서 점착성 개선제는 로진(rosin), 열가소성 비닐계 수지, 열가소성 변성 셀룰로오스 및 카제인으로 이루어진 군에서 선택된 1종 이상 선택될 수 있다. 이 중, 로진은 검 로진(gum rosin, 고무 로진이라고도 함)인 것이 바람직하다. 또한, 열가소성 비닐계 수지는 비닐기(vinyl group)를 함유하는 단량체를 부가중합하여 얻은 폴리머 중 열가소성을 가진 것을 말하여, 예를 들어 폴리비닐아세테이트(Polyvinyl acetate), 폴리비닐알코올(Polyvinyl alcohol), 에틸렌-비닐아세테이트 공중합체(Ehtylene-Vinyl Acetate Copolymer, EVA) 및 에틸렌-비닐알코올 공중합체(Ehtylene-Vinyl Alcohol Copolymer, EVOH)로 이루어진 군에서 1종 이상 선택될 수 있다. 또한, 열가소성 변성 셀룰로오스는 에스테르화 또는 에테르화에 의해 변성된 셀룰로오스 중 열가소성을 보이는 것을 의미하며, 이 중 셀룰로오스 에스테르 유도체인 것이 바람직하다. 상기 셀룰로오스 에스테르 유도체는 메틸 셀룰로오스, 에틸 셀룰로오스, 에틸메틸 셀룰로오스, 하이드록시에틸 셀룰로오스, 하이드록시프로필 셀룰로오스, 하이드록시에틸메틸 셀룰로오스, 하이드록시프로필메틸 셀룰로오스, 에틸하이드록시에틸 셀룰로오스 및 카르복시메틸 세룰로오스로 이루어진 군에서 1종 이상 선택될 수 있다.
The tackiness improving agent, which is one component of the additive composition for a starch-based adhesive of the present invention, strengthens the late adhesion of ordinary starch or modified starch which is plasticized by heat and not subjected to a low viscosity during the drying process in the production of corrugated board. In the present invention, the tackiness-improving agent may be selected from the group consisting of rosin, thermoplastic vinyl resin, thermoplastic modified cellulose and casein. Among them, rosin is preferably gum rosin (also referred to as rubber rosin). The thermoplastic vinyl resin is a polymer obtained by additionally adding a monomer containing a vinyl group and has thermoplasticity. Examples of the thermoplastic resin include polyvinyl acetate, polyvinyl alcohol, One or more selected from the group consisting of an ethylene-vinyl acetate copolymer (Ehtylene-Vinyl Acetate Copolymer (EVA)) and an ethylene-vinyl alcohol copolymer (Ehtylene-Vinyl Alcohol Copolymer (EVOH) In addition, the thermoplastic modified cellulose means that it exhibits thermoplasticity among the cellulose modified by esterification or etherification, and among these, a cellulose ester derivative is preferable. The cellulose ester derivative may be selected from the group consisting of methylcellulose, ethylcellulose, ethylmethylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, hydroxyethylmethylcellulose, hydroxypropylmethylcellulose, ethylhydroxyethylcellulose and carboxymethylcellulose One or more of them may be selected.

본 발명의 일 예에 따른 According to one embodiment of the present invention 전분계Starch-based 접착제용 첨가제 조성물 및 이의 용도 Additive compositions for adhesives and uses thereof

본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물은 전체 중량을 기준으로 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 55~85 중량%, 저점도화 전분 6~18 중량%, 수용성 무기물 3~14 중량% 및 점착성 개선제 3~14 중량%를 포함한다. 이때, 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물은 전분계 접착제의 적정한 점도 범위 및 양호한 접착력을 고려할 때, 바람직하게는 전체 중량을 기준으로 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 60~85 중량%, 저점도화 전분 7~18 중량%, 수용성 무기물 3~12 중량% 및 점착성 개선제 3~12 중량%를 포함하고, 더 바람직하게는 일반전분 또는 변성전분 70~80 중량%, 저점도화 전분 10~15 중량%, 수용성 무기물 5~7.5 중량% 및 점착성 개선제 5~7.5 중량%를 포함한다.The additive composition for a starch-based adhesive according to one embodiment of the present invention comprises 55 to 85% by weight of general starch or modified starch not subjected to a low-viscosity treatment on the basis of the total weight, 6 to 18% by weight of a low viscosity starch, By weight and 3 to 14% by weight of a tackifier. At this time, the additive composition for a starch-based adhesive according to an embodiment of the present invention is preferably a starch-modified starch or modified starch 60 that is not subjected to a low-viscosity treatment based on the total weight, To 70% by weight of starch or modified starch, more preferably from 70% to 80% by weight of starch or modified starch, from 7% to 18% by weight of low viscosity starch, from 3% to 12% 10 to 15% by weight of starch, 5 to 7.5% by weight of a water-soluble inorganic substance, and 5 to 7.5% by weight of a tackiness improving agent.

본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에서 캐리어부를 제조하는데 사용될 수 있다. 특히, 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 장치 중 전분계 접착제용 첨가제 조성물을 공급하는 공급부와 별도로 저점도화 과정을 거치지 않은 일반전분 또는 변성전분을 공급하는 공급부를 구비하는 경우 효과적으로 사용될 수 있다. 예를 들어, 본 발명은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 캐리어부로서, 물, 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분, 및 알칼리 물질을 포함하는 혼합물 형태이고, 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 및 저점도화 전분은 모두 호화된 상태로 존재하는 것을 특징으로 하는 캐리어부를 제공한다. 상기 캐리어부는 바람직하게는 물 100 중량부 당 전분계 접착제용 첨가제 조성물 3~7 중량부, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 3.5~7.5 중량부 및 알칼리 물질 1~2.5 중량부를 포함한다. 또한, 상기 캐리어부는 더 바람직하게는 물 100 중량부 당 전분계 접착제용 첨가제 조성물 4~6 중량부, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 4~7 중량부 및 알칼리 물질 1~2 중량부를 포함한다. 이때, 상기 알칼리 물질은 물에 용해될 수 있고 전분을 호화시킬 수 있는 것이라면 그 종류가 크게 제한되지 않으며, 바람직하게는 수산화나트륨, 수산화칼슘 및 수산화칼륨으로 이루어진 군에서 선택되는 1종 이상일 수 있다. 또한, 상기 알칼리 물질은 캐리어부를 제조하는 과정에서 바람직하게는 물에 용해된 수용액 형태로 공급될 수 있다.The additive composition for a starch-based adhesive according to an embodiment of the present invention can be used for manufacturing a carrier part in a starch-based adhesive manufacturing process by a one-tank or two-tank adhesive process. In particular, the additive composition for a starch-based adhesive according to an embodiment of the present invention may be prepared by supplying a starch-based adhesive additive composition in a starch-based adhesive manufacturing apparatus by a one-tank or two- It may be effectively used when it is provided with a general starch which has not undergone a low-viscosity process, or a supply part which supplies modified starch separately from the supply part. For example, the present invention is a carrier part used in a starch-based adhesive manufacturing process by a one-tank or two-tank tableting method, wherein water, a starch-based adhesive according to an example of the present invention A starch-modified starch, a starch-based starch, a starch-based starch, a starch-based starch, an additive composition for starch-based adhesives, and a starch or modified starch which are not subjected to a low- Are all present in a gorgeous state. The carrier portion preferably comprises 3 to 7 parts by weight of the additive composition for a starch-based adhesive per 100 parts by weight of water, 3.5 to 7.5 parts by weight of ordinary starch or modified starch which is not subjected to a low- 1 to 2.5 parts by weight of the material. The carrier part preferably further comprises 4 to 6 parts by weight of the additive composition for a starch-based adhesive per 100 parts by weight of water, 4 to 7 parts by weight of a common starch or modified starch which is not subjected to a low- And 1 to 2 parts by weight of an alkali substance. At this time, the alkali substance may be at least one selected from the group consisting of sodium hydroxide, calcium hydroxide, and potassium hydroxide, as long as the alkali substance is soluble in water and can starch the starch. In addition, the alkali material may be supplied in the form of an aqueous solution, preferably dissolved in water, during the production of the carrier part.

또한, 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에서 메인부를 제조하는데 사용될 수 있다. 특히, 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 장치 중 전분계 접착제용 첨가제 조성물을 공급하는 공급부와 별도로 저점도화 과정을 거치지 않은 일반전분 또는 변성전분을 공급하는 공급부를 구비하는 경우 효과적으로 사용될 수 있다. 예를 들어, 본 발명은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 메인부로서, 물, 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분, 및 붕소 함유 화합물을 포함하는 혼합물 형태인 것을 특징으로 하는 메인부를 제공한다. 상기 메인부는 바람직하게는 물 100 중량부 당 전분계 접착제용 첨가제 조성물 1.5~4.5 중량부, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 25~35 중량부 및 붕소 함유 화합물 0.5~1.0 중량부를 포함한다. 또한, 상기 메인부는 바람직하게는 물 100 중량부 당 전분계 접착제용 첨가제 조성물 2~4 중량부, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 27~33 중량부 및 붕소 함유 화합물 0.5~1.0 중량부를 포함한다. 이때, 상기 붕소 함유 화합물은 붕소를 함유하고 전분계 접착제의 초기 접착력을 개선시킬 수 있는 것이라면 그 종류가 크게 제한되지 않으며, 예를 들어 붕산 또는 붕산염에서 선택될 수 있다. 상기 붕산염의 예로는 붕사(borax)가 있다.
Also, the additive composition for a starch-based adhesive according to an embodiment of the present invention can be used to manufacture a main part in a starch-based adhesive manufacturing process by a one-tank method or a two-tank method. In particular, the additive composition for a starch-based adhesive according to an embodiment of the present invention may be prepared by supplying a starch-based adhesive additive composition in a starch-based adhesive manufacturing apparatus by a one-tank or two- It may be effectively used when it is provided with a general starch which has not undergone a low-viscosity process, or a supply part which supplies modified starch separately from the supply part. For example, the present invention is a main part used in a starch-based adhesive manufacturing process by a one-tank method or a two-tank method, wherein water, a starch-based adhesive according to an example of the present invention Wherein the additive composition for a starch-based adhesive is in the form of a mixture containing common starch or modified starch and a boron-containing compound which are not separately subjected to a low-viscosity process. The main part preferably contains 1.5 to 4.5 parts by weight of an additive composition for a starch-based adhesive per 100 parts by weight of water, 25 to 35 parts by weight of a general starch or modified starch which is not subjected to a low- Containing compound in an amount of 0.5 to 1.0 part by weight. The main part preferably comprises 2 to 4 parts by weight of the additive composition for a starch-based adhesive per 100 parts by weight of water, 27 to 33 parts by weight of a common starch or modified starch not subjected to a low- And 0.5 to 1.0 parts by weight of a boron-containing compound. The boron-containing compound may be selected from, for example, boric acid or boric acid salts, as long as it contains boron and can improve the initial adhesion of the starch-based adhesive. An example of such a borate is borax.

본 발명의 다른 예에 따른 According to another embodiment of the present invention 전분계Starch-based 접착제용 첨가제 조성물 및 이의 용도 Additive compositions for adhesives and uses thereof

본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정 중 캐리어부 제조시 사용되는 조성물로서, 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 저점도화 전분 3~10 중량부, 수용성 무기물 2~8 중량부 및 점착성 개선제 2~8 중량부를 포함한다. 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물은 전분계 접착제의 적정한 점도 범위 및 양호한 접착력을 고려할 때, 바람직하게는 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 저점도화 전분 4~9 중량부, 수용성 무기물 2~6 중량부 및 점착성 개선제 2~6 중량부를 포함한다. 본 발명의 다른 예에 따른 전분계 접착제용 조성물은 전술한 본 발명의 일 예에 따른 전분계 접착제용 조성물에 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 적당량을 첨가하여 제조될 수 있다. 또한, 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물은 바람직하게는 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 알칼리 물질 10~20 중량부, 바람직하게는 12~18 중량부를 더 포함할 수 있다. 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물이 알칼리 물질을 포함하는 경우 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정 중 캐리어부 제조시 알칼리 물질을 별도로 첨가하지 않아도 된다. 이때, 상기 알칼리 물질은 물에 용해될 수 있고 전분을 호화시킬 수 있는 것이라면 그 종류가 크게 제한되지 않으며, 바람직하게는 수산화나트륨, 수산화칼슘 및 수산화칼륨으로 이루어진 군에서 선택되는 1종 이상일 수 있다.The additive composition for a starch-based adhesive according to another embodiment of the present invention is a composition used in the production of a carrier part in a starch-based adhesive manufacturing process by a one-tank or two- 3 to 10 parts by weight of low viscosity starch, 2 to 8 parts by weight of a water-soluble inorganic substance and 2 to 8 parts by weight of a tackiness improving agent per 100 parts by weight of ordinary starch or modified starch not subjected to the process. The additive composition for a starch-based adhesive according to another embodiment of the present invention is preferably a starch-modified starch or a starch-modified starch having a low viscosity, To 9 parts by weight, 2 to 6 parts by weight of a water-soluble inorganic substance, and 2 to 6 parts by weight of a tackiness improving agent. The composition for a starch-based adhesive according to another embodiment of the present invention may be prepared by adding an ordinary starch or a modified starch which is not subjected to a low-viscosity treatment to the composition for a starch-based adhesive according to the example of the present invention described above. Further, the additive composition for a starch-based adhesive according to another embodiment of the present invention preferably comprises 10 to 20 parts by weight, preferably 12 to 18 parts by weight, of an alkali substance per 100 parts by weight of ordinary starch or modified starch not subjected to a low- . When the additive composition for a starch-based adhesive according to another embodiment of the present invention comprises an alkali substance, during the production of the carrier part during the production of the starch-based adhesive by a one-tank or two- The material need not be added separately. At this time, the alkali substance may be at least one selected from the group consisting of sodium hydroxide, calcium hydroxide, and potassium hydroxide, as long as the alkali substance is soluble in water and can starch the starch.

본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에서 캐리어부를 제조하는데 사용될 수 있다. 특히, 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 장치 중 전분계 접착제용 첨가제 조성물을 공급하는 공급부만을 구비하고 일반전분 또는 변성전분을 공급하는 공급부를 구비하지 않는 경우 효과적으로 사용될 수 있다. 예를 들어, 본 발명은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 캐리어부로서, 물, 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물 및 알칼리 물질을 포함하는 혼합물 형태이고, 상기 전분계 접착제용 첨가제 조성물에 포함된 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 및 저점도화 전분은 모두 호화된 상태로 존재하는 것을 특징으로 하는 캐리어부를 제공한다. 이때, 상기 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물은 알칼리 물질을 별도로 포함하지 않는 형태이다. 상기 캐리어부는 바람직하게는 물 100 중량부 당 전분계 접착제용 첨가제 조성물 7~14 중량부 및 알칼리 물질 1~2.5 중량부를 포함한다. 또한, 상기 캐리어부는 더 바람직하게는 물 100 중량부 당 전분계 접착제용 첨가제 조성물 8~12 중량부 및 알칼리 물질 1~2 중량부를 포함한다. 이때, 상기 알칼리 물질은 물에 용해될 수 있고 전분을 호화시킬 수 있는 것이라면 그 종류가 크게 제한되지 않으며, 바람직하게는 수산화나트륨, 수산화칼슘 및 수산화칼륨으로 이루어진 군에서 선택되는 1종 이상일 수 있다. 또한, 상기 알칼리 물질은 캐리어부를 제조하는 과정에서 바람직하게는 물에 용해된 수용액 형태로 공급될 수 있다.
The additive composition for a starch-based adhesive according to another example of the present invention can be used for manufacturing a carrier part in a starch-based adhesive manufacturing process by a one-tank method or a two-tank method. Particularly, the additive composition for a starch-based adhesive according to another embodiment of the present invention is characterized in that an additive composition for a starch-based adhesive is supplied in a starch-based adhesive manufacturing apparatus by a one-tank or two- It can be effectively used when it is provided with only a supply part and does not have a supply part for supplying common starch or modified starch. For example, the present invention is a carrier part used in a starch-based adhesive manufacturing process by a one-tank method or a two-tank tableting method, which comprises water, a starch-based adhesive according to another example of the present invention Wherein the starch or modified starch and the starch-modified starch which are not mixed with the starch-based adhesive additive composition and have not undergone the low-viscosity treatment are all present in a gelled state Thereby providing a carrier portion. At this time, the additive composition for a starch based adhesive according to another example of the present invention does not contain an alkali substance separately. The carrier portion preferably comprises 7 to 14 parts by weight of the additive composition for a starch-based adhesive per 100 parts by weight of water and 1 to 2.5 parts by weight of an alkali substance. The carrier part preferably further comprises 8 to 12 parts by weight of an additive composition for a starch-based adhesive and 1 to 2 parts by weight of an alkali substance per 100 parts by weight of water. At this time, the alkali substance may be at least one selected from the group consisting of sodium hydroxide, calcium hydroxide, and potassium hydroxide, as long as the alkali substance is soluble in water and can starch the starch. In addition, the alkali material may be supplied in the form of an aqueous solution, preferably dissolved in water, during the production of the carrier part.

본 발명의 또 다른 예에 따른 According to another embodiment of the present invention 전분계Starch-based 접착제용 첨가제 조성물 및 이의 용도 Additive compositions for adhesives and uses thereof

본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정 중 메인부 제조시 사용되는 조성물로서, 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 저점도화 전분 0.5~1.5 중량부, 수용성 무기물 0.3~1.2 중량부 및 점착성 개선제 0.3~1.2 중량부를 포함한다. 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물은 전분계 접착제의 적정한 점도 범위 및 양호한 접착력을 고려할 때, 바람직하게는 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 저점도화 전분 0.8~1.4 중량부, 수용성 무기물 0.4~1.0 중량부 및 점착성 개선제 0.4~1.0 중량부를 포함하고, 더 바람직하게는 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 저점도화 전분 0.8~1.4 중량부, 수용성 무기물 0.4~0.8 중량부 및 점착성 개선제 0.4~0.8 중량부를 포함한다. 본 발명의 또 다른 예에 따른 전분계 접착제용 조성물은 전술한 본 발명의 일 예에 따른 전분계 접착제용 조성물에 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 적당량을 첨가하여 제조될 수 있다. 또한, 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물은 바람직하게는 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 100 중량부 당 붕소 함유 화합물 1~10 중량부, 바람직하게는 2~5 중량부를 더 포함할 수 있다. 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물이 붕소 함유 물질을 포함하는 경우 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정 중 메인부 제조시 붕소 함유 물질을 별도로 첨가하지 않아도 된다. 이때, 상기 붕소 함유 화합물은 붕소를 함유하고 전분계 접착제의 초기 접착력을 개선시킬 수 있는 것이라면 그 종류가 크게 제한되지 않으며, 예를 들어 붕산 또는 붕산염에서 선택될 수 있다. 상기 붕산염의 예로는 붕사(borax)가 있다.The additive composition for a starch-based adhesive according to another embodiment of the present invention is a composition used in the production of a main part in a starch-based adhesive manufacturing process by a one-tank or two-tank tableting method, 0.5 to 1.5 parts by weight of low viscosity starch, 0.3 to 1.2 parts by weight of a water soluble inorganic substance and 0.3 to 1.2 parts by weight of a tackiness improving agent per 100 parts by weight of ordinary starch or modified starch not subjected to a dipping process. In the additive composition for a starch-based adhesive according to another embodiment of the present invention, in consideration of a suitable viscosity range of the starch-based adhesive and a good adhesive strength, it is preferable to use a low starch starch or a low starch starch per 100 parts by weight of the modified starch 0.4 to 1.0 part by weight of a water-soluble inorganic substance and 0.4 to 1.0 part by weight of a tackiness-improving agent, more preferably 0.8 to 1.4 parts by weight of low-viscosity starch per 100 parts by weight of modified starch or modified starch not subjected to a low- 0.4 to 0.8 parts by weight of a water-soluble inorganic substance, and 0.4 to 0.8 parts by weight of a tackiness improving agent. The composition for a starch-based adhesive according to another embodiment of the present invention may be prepared by adding an appropriate amount of a general starch or a modified starch to the composition for a starch-based adhesive according to an example of the present invention. Further, the additive composition for a starch-based adhesive according to still another embodiment of the present invention preferably contains 1 to 10 parts by weight of a boron-containing compound per 100 parts by weight of a general starch or modified starch not subjected to a low-viscosity treatment, preferably 2 to 5 parts by weight Weight parts. When the additive composition for a starch-based adhesive according to another embodiment of the present invention contains a boron-containing substance, the main part manufacturing process of the starch-based adhesive manufacturing process by a one-tank or two- The boron-containing material may not be separately added. The boron-containing compound may be selected from, for example, boric acid or boric acid salts, as long as it contains boron and can improve the initial adhesion of the starch-based adhesive. An example of such a borate is borax.

본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에서 메인부를 제조하는데 사용될 수 있다. 특히, 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 장치 중 전분계 접착제용 첨가제 조성물을 공급하는 공급부만을 구비하고 일반전분 또는 변성전분을 공급하는 공급부를 구비하지 않는 경우 효과적으로 사용될 수 있다. 예를 들어, 본 발명은 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 메인부로서, 물, 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물 및 붕소 함유 화합물을 포함하는 혼합물 형태인 것을 특징으로 하는 메인부를 제공한다. 이때, 상기 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물은 붕소 함유 화합물을 별도로 포함하지 않는 형태이다. 상기 메인부는 바람직하게는 물 100 중량부 당 전분계 접착제용 첨가제 조성물 30~40 중량부 및 붕소 함유 화합물 0.5~1.0 중량부를 포함한다. 또한, 상기 메인부는 더 바람직하게는 물 100 중량부 당 전분계 접착제용 첨가제 조성물 30~36 중량부 및 붕소 함유 화합물 0.6~0.9 중량부를 포함한다. 이때, 상기 붕소 함유 화합물은 붕소를 함유하고 전분계 접착제의 초기 접착력을 개선시킬 수 있는 것이라면 그 종류가 크게 제한되지 않으며, 예를 들어 붕산 또는 붕산염에서 선택될 수 있다. 상기 붕산염의 예로는 붕사(borax)가 있다.
The additive composition for a starch-based adhesive according to still another embodiment of the present invention can be used for manufacturing a main part in a starch-based adhesive manufacturing process by a one-tank method or a two-tank method. In particular, the additive composition for a starch-based adhesive according to still another embodiment of the present invention may be prepared by supplying an additive composition for a starch-based adhesive in a starch-based adhesive manufacturing apparatus by a one-tank or two- And does not have a supply part for supplying general starch or modified starch, can be effectively used. For example, the present invention is a main part used in a starch-based adhesive manufacturing process by a one-tank or two-tank tableting method, which comprises water, a starch based on another example of the present invention Wherein the main part is in the form of a mixture containing an additive composition for an adhesive and a boron-containing compound. At this time, the additive composition for a starch-based adhesive according to another embodiment of the present invention does not contain a boron-containing compound separately. The main portion preferably comprises 30 to 40 parts by weight of the additive composition for a starch-based adhesive and 0.5 to 1.0 part by weight of a boron-containing compound per 100 parts by weight of water. More preferably, the main portion includes 30 to 36 parts by weight of the additive composition for a starch-based adhesive and 0.6 to 0.9 parts by weight of a boron-containing compound per 100 parts by weight of water. The boron-containing compound may be selected from, for example, boric acid or boric acid salts, as long as it contains boron and can improve the initial adhesion of the starch-based adhesive. An example of such a borate is borax.

본 발명의 다른 측면은 전분계 접착제에 관한 것으로서, 본 발명에 따른 전분계 접착제는 전술한 메인부 또는 캐리어부 중 하나 또는 양쪽을 모두 포함한다. 이때, 상기 캐리어부는 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물 또는 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물로부터 제조될 수 있다. 또한, 상기 메인부는 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물 또는 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물로부터 제조될 수 있다. 본 발명에 따른 전분계 접착제는 보관 안정성이 우수하고, 적정 수준의 점도 범위를 가져 도포성이 양호하며, 전분계 접착제용 첨가제 조성물에 포함된 구성성분의 조화에 의해 접착력이 매우 우수하다. 따라서, 본 발명에 따른 전분계 접착제는 골판지 제조뿐만 아니라 , 벽지 제조, 종이층 결합, 또는 펄프 몰드 제조시에 접착제로 사용될 수 있다.Another aspect of the present invention relates to a starch-based adhesive, wherein the starch-based adhesive according to the present invention comprises one or both of the aforementioned main portion or carrier portion. At this time, the carrier part may be prepared from the additive composition for a starch-based adhesive according to an example of the present invention or the additive composition for a starch-based adhesive according to another example of the present invention. The main part may be prepared from the additive composition for a starch-based adhesive according to an example of the present invention or the additive composition for a starch-based adhesive according to another example of the present invention. The starch-based adhesive according to the present invention is excellent in storage stability, has an appropriate range of viscosity, has good applicability, and has excellent adhesion strength due to the harmonization of the constituents contained in the additive composition for a starch-based adhesive. Therefore, the starch-based adhesive according to the present invention can be used not only as a corrugated paperboard but also as an adhesive in the production of wallpaper, bonding of paper layers, or pulp mold production.

본 발명에 따른 전분계 접착제는 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의해 제조될 수 있다. 이때, 캐리어부는 일반 전분, 물 및 알칼리 물질의 수용액을 반응기에 첨가하고 교반하여 전분을 호화시킴으로써 제조할 수 있다. 또한, 캐리어부는 바람직하게는 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물, 일반 전분, 물 및 알칼리 물질의 수용액을 반응기에 첨가하고 교반하여 전분을 호화시킴으로써 제조할 수 있다. 또한, 캐리어부는 더 바람직하게는 본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물, 물 및 알칼리 물질의 수용액(본 발명의 다른 예에 따른 전분계 접착제용 첨가제 조성물이 알칼리 물질을 포함하는 경우 생략이 가능함)을 반응기에 첨가하고 교반하여 전분을 호화시킴으로써 제조될 수 있다. 또한, 메인부는 일반 전분, 물 및 붕소 함유 화합물을 첨가하고 교반하여 제조할 수 있다. 또한, 메인부는 바람직하게는 본 발명의 일 예에 따른 전분계 접착제용 첨가제 조성물, 일반 전분, 물 및 붕소 함유 화합물을 첨가하고 교반하여 제조할 수 있다. 또한, 메인부는 더 바람직하게는 본 발명의 또 다른 예에 따른 전분계 접착제용 첨가제 조성물, 물 및 붕소 함유 화합물(본 발명의 도 다른 예에 따른 전분계 접착제용 첨가제 조성물이 붕소 함유 화합물을 포함하는 경우 생략이 가능함)을 첨가하고 교반하여 제조할 수 있다. 상기 캐리어부 및 메인부가 하나의 반응기에서 순차적으로 제조되어 전분계 접착제를 형성하는 경우 원 탱크(one tank) 제호 방식에 해당한다. 또한, 상기 캐리어부 및 메인부가 서로 별도의 반응기에서 제조되고, 이후 혼합되어 전분계 접착제를 형성하는 경우 투 탱크(two tank) 제호 방식에 해당한다.
The starch-based adhesive according to the present invention can be manufactured by a one-tank or two-tank method. At this time, the carrier part can be prepared by adding an aqueous solution of common starch, water and an alkali substance to a reactor and stirring to gelatinize the starch. In addition, the carrier part can be preferably prepared by adding an additive composition for a starch-based adhesive according to an example of the present invention, an aqueous solution of common starch, water and an alkali substance to a reactor and stirring to starch the starch. Further, the carrier part preferably further comprises an additive composition for a starch-based adhesive according to another example of the present invention, an aqueous solution of water and an alkali substance (in the case where the additive composition for a starch-based adhesive according to another example of the present invention contains an alkali substance, Can be added to the reactor and agitated to gelatinize the starch. In addition, the main part can be prepared by adding and stirring general starch, water and boron-containing compounds. The main part may be prepared by adding and stirring an additive composition for a starch-based adhesive, a general starch, water and a boron-containing compound, according to an example of the present invention. Further, the main part preferably further comprises an additive composition for a starch-based adhesive according to still another embodiment of the present invention, water and a boron-containing compound (the additive composition for a starch-based adhesive according to another embodiment of the present invention includes a boron-containing compound May be omitted) may be added and stirred. When the carrier portion and the main portion are sequentially manufactured in one reactor to form a starch-based adhesive, this corresponds to a one tank method. In addition, the carrier part and the main part are manufactured in separate reactors and then mixed to form a starch-based adhesive, which corresponds to a two tank system.

이하, 본 발명을 실시예를 통하여 보다 구체적으로 설명하고자 한다. 다만, 하기 실시예들은 본 발명의 내용을 명확하게 예시하기 위한 것일 뿐 본 발명의 보호범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described more specifically by way of examples. However, the following examples are intended to clearly illustrate the present invention and do not limit the scope of protection of the present invention.

1. One. 전분계Starch-based 접착제용 첨가제 조성물의 제조 Preparation of additive composition for adhesive

첨가제 제조예 1.Additive Preparation Example 1

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 800g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 100g, 수용성 무기물인 규산나트륨(sodium silicate) 50g 및 점착성 개선제인 검로진(gum rosin) 50g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 조성물을 제조하였다.
800 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity starch having a viscosity of 300 centipoise (centipoise) (cPs) at 50 ° C (product name: oxidized starch # 150; 50 g of sodium silicate as a water-soluble inorganic substance and 50 g of gum rosin as a tackiness improving agent were sequentially introduced into a mixer (product name: Lodige Mixer; supplier: Lodige Process Technology, Germany) To prepare an additive composition for a starch-based adhesive.

첨가제 제조예 2.Additive Preparation Example 2

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 700g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 150g, 수용성 무기물인 규산나트륨(sodium silicate) 75g 및 점착성 개선제인 검로진(gum rosin) 75g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 첨가제 조성물을 제조하였다.
700 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity oxidized starch having a viscosity of 300 centipoise (centipoise) (cPs) of 20 wt% 75 g of sodium silicate as a water-soluble inorganic substance and 75 g of gum rosin as a tackiness improving agent were sequentially introduced into a mixer (product name: Lodige Mixer; supplier: Lodige Process Technology, Germany) To prepare an additive additive composition for a starch-based adhesive.

첨가제 제조예 3.Additive Preparation Example 3

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 750g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 150g, 수용성 무기물인 규산나트륨(sodium silicate) 50g 및 점착성 개선제인 검로진(gum rosin) 50g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 조성물을 제조하였다.
750 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity starch having a viscosity of 300 centipoise (centipoise) (cPs) at 50 ° C (product name: oxidized starch # 150; 50 g of sodium silicate as a water-soluble inorganic substance and 50 g of gum rosin as a tackiness improving agent were sequentially introduced into a mixer (product name: Lodige Mixer; supplier: Lodige Process Technology, Germany) To prepare an additive composition for a starch-based adhesive.

첨가제 제조예 4.Additive Preparation Example 4

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 800g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 100g, 수용성 무기물인 규산나트륨(sodium silicate) 50g 및 점착성 개선제인 폴리비닐아세테이트(polyvinyl acetate) 50g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 조성물을 제조하였다.
800 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity starch having a viscosity of 300 centipoise (centipoise) (cPs) at 50 ° C (product name: oxidized starch # 150; 50 g of sodium silicate as a water-soluble inorganic substance and 50 g of polyvinyl acetate as a tackiness improving agent were sequentially introduced into a mixer (product name: Lodige Mixer; supplier: Lodige Process Technology, Germany) To prepare an additive composition for a starch-based adhesive.

첨가제 제조예 5.Additive Preparation Example 5

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 700g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 150g, 수용성 무기물인 규산나트륨(sodium silicate) 75g 및 점착성 개선제인 폴리비닐아세테이트(polyvinyl acetate) 75g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 조성물을 제조하였다.
700 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity oxidized starch having a viscosity of 300 centipoise (centipoise) (cPs) of 20 wt% 75 g of sodium silicate as a water-soluble inorganic substance and 75 g of polyvinyl acetate as a tackiness improving agent were sequentially introduced into a mixer (product name: Lodige Mixer; supplier: Lodige Process Technology, Germany) To prepare an additive composition for a starch-based adhesive.

첨가제 비교제조예 1.Comparative Example 1

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 800g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 100g, 콜로이드성 무기물인 탄산칼슘 50g 및 점착성 개선제인 검로진(gum rosin) 50g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 조성물을 제조하였다.
800 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity starch having a viscosity of 300 centipoise (centipoise) (cPs) at 50 ° C (product name: oxidized starch # 150; 50 g of colloidal inorganic calcium carbonate and 50 g of gum rosin as a tackiness improving agent were sequentially introduced into a mixer (Lodige Mixer, supplier: Lodige Process Technology, Germany), and stirred at a speed of 100 rpm To prepare an additive composition for a starch-based adhesive.

첨가제 비교제조예 2.Comparative Example 2

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 800g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 100g, 양이온성 고분자 30g 및 점착성 개선제인 검로진(gum rosin) 70g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 조성물을 제조하였다.
800 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity starch having a viscosity of 300 centipoise (centipoise) (cPs) at 50 ° C (product name: oxidized starch # 150; (Product name: Lodige Mixer; supplier: Lodige Process Technology, Germany), and the mixture was stirred at a speed of 100 rpm to prepare a starch-based polymer An additive composition for an adhesive was prepared.

첨가제 비교제조예 3.EXAMPLES COMPARATIVE EXAMPLES 3.

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 500g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 200g, 수용성 무기물인 규산나트륨(sodium silicate) 150g 및 점착성 개선제인 검로진(gum rosin) 150g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 조성물을 제조하였다.
500 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity starch having a viscosity of 300 centipoise (centipoise) (cPs) at 50 ° C (product name: oxidized starch # 150; 150 g of sodium silicate as a water-soluble inorganic substance and 150 g of gum rosin as a tackiness improving agent were sequentially introduced into a mixer (product name: Lodige Mixer; supplier: Lodige Process Technology, Germany) To prepare an additive composition for a starch-based adhesive.

첨가제 비교제조예 4.EXAMPLES COMPARATIVE EXAMPLES 4.

일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 900g, 50℃에서 20 중량% 호화액의 점도가 300 센티포이즈(centipoise, cPs)인 저점도 산화전분(제품명 : 산화전분 #150; 공급사 : 대상 주식회사, 대한민국) 50g, 수용성 무기물인 규산나트륨(sodium silicate) 25g 및 점착성 개선제인 검로진(gum rosin) 25g을 혼합기(제품명 : Lodige Mixer; 공급자 : Lodige Process Technology, 독일)에 순차적으로 투입하고, 100 rpm의 속도로 교반하여 전분계 접착제용 첨가제 조성물을 제조하였다.
900 g of common corn starch (supplier: Target Co., Ltd., Korea), low viscosity oxidized starch having a viscosity of 300 centipoise (centipoise) (cPs) at 20 ° C at 50 ° C (trade name: oxidized starch # 150; 25 g of sodium silicate as a water-soluble inorganic substance and 25 g of gum rosin as a tackiness improving agent were sequentially introduced into a mixer (product name: Lodige Mixer; supplier: Lodige Process Technology, Germany) To prepare an additive composition for a starch-based adhesive.

2. 골판지용 2. For corrugated board 전분계Starch-based 접착제의 제조 Manufacture of adhesives

(1) 원 탱크(one tank) 제호 방식에 의한 골판지용 전분계 접착제의 제조
(1) Production of starch-based adhesives for corrugated cardboard by one-tank method

접착제 제조예 1-1.Adhesive Production Example 1-1.

유리 재질의 반응기에 약 52℃의 물 750g을 넣고, 여기에 첨가제 제조예 1에서 제조한 전분계 접착제용 첨가제 조성물 37.5g, 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 42.5g을 순차적으로 첨가하고 교반한 후, 다시 33 중량% 농도의 수산화나트륨 수용액 33g을 첨가하고 약 2000 rpm의 속도로 약 5분 동안 교반하여 호화액 형태의 캐리어부를 제조하였다. 이후, 반응기에 수용된 캐리어부를 계속 교반하면서, 여기에 약 32℃의 물 1000g 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 400g을 순차적으로 첨가하고 5분 동안 교반하였다. 이후, 반응기에 붕사(borax) 6g을 첨가하고 5분 동안 교반하여 골판지용 전분계 접착제를 제조하였다.
750 g of water at about 52 캜 was placed in a glass reactor, 37.5 g of the additive composition for a starch-based adhesive prepared in Additive Preparation Example 1, and 42.5 g of common corn starch (supplier: KK) were sequentially added 33 g of an aqueous sodium hydroxide solution having a concentration of 33% by weight was further added thereto, followed by stirring at a speed of about 2000 rpm for about 5 minutes to prepare a carrier portion in the form of a liquor. Thereafter, 1000 g of water at about 32 캜 and 400 g of common corn starch (supplier: Kobunshi Kagaku Co., Ltd., Korea) were sequentially added thereto while stirring the carrier portion accommodated in the reactor, and the mixture was stirred for 5 minutes. Thereafter, 6 g of borax was added to the reactor and stirred for 5 minutes to prepare a starch-based adhesive for corrugated board.

접착제 제조예 1-2.Adhesive Production Example 1-2.

유리 재질의 반응기에 약 52℃의 물 750g을 넣고, 여기에 첨가제 제조예 1에서 제조한 전분계 접착제용 첨가제 조성물 37.5g, 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 42.5g을 순차적으로 첨가하고 교반한 후, 다시 33 중량% 농도의 수산화나트륨 수용액 35g을 첨가하고 약 2000 rpm의 속도로 약 5분 동안 교반하여 호화액 형태의 캐리어부를 제조하였다. 이후, 반응기에 수용된 캐리어부를 계속 교반하면서, 여기에 약 32℃의 물 1000g 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 380g을 순차적으로 첨가하고 5분 동안 교반하였다. 이후, 반응기에 붕사(borax) 6g을 첨가하고 5분 동안 교반하여 골판지용 전분계 접착제를 제조하였다.
750 g of water at about 52 캜 was placed in a glass reactor, 37.5 g of the additive composition for a starch-based adhesive prepared in Additive Preparation Example 1, and 42.5 g of common corn starch (supplier: KK) were sequentially added Then, 35 g of aqueous sodium hydroxide solution having a concentration of 33% by weight was further added thereto, and the mixture was stirred at a speed of about 2000 rpm for about 5 minutes to prepare a carrier portion in the form of a liquid. Thereafter, 1000 g of water at about 32 캜 and 380 g of common corn starch (supplier: Kobunshi Kagaku Co., Ltd.) were sequentially added thereto while stirring the carrier portion kept in the reactor, and the mixture was stirred for 5 minutes. Thereafter, 6 g of borax was added to the reactor and stirred for 5 minutes to prepare a starch-based adhesive for corrugated board.

접착제 제조예 1-3.Adhesive Production Example 1-3.

유리 재질의 반응기에 약 52℃의 물 750g을 넣고, 여기에 첨가제 제조예 1에서 제조한 전분계 첨가제 조성물 37.5g, 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 42.5g을 순차적으로 첨가하고 교반한 후, 다시 33 중량% 농도의 수산화나트륨 수용액 33g을 첨가하고 약 2000 rpm의 속도로 약 5분 동안 교반하여 호화액 형태의 캐리어부를 제조하였다. 이후, 반응기에 수용된 캐리어부를 계속 교반하면서, 여기에 약 32℃의 물 1000g 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 360g을 순차적으로 첨가하고 5분 동안 교반하였다. 이후, 반응기에 붕사(borax) 7g을 첨가하고 5분 동안 교반하여 골판지용 전분계 접착제를 제조하였다.
750 g of water at about 52 캜 was placed in a glass reactor, and 37.5 g of the starch-based additive composition prepared in Additive Preparation Example 1 and 42.5 g of common corn starch (supplier: KK) were sequentially added thereto, Thereafter, 33 g of an aqueous sodium hydroxide solution having a concentration of 33% by weight was further added thereto, and the mixture was stirred at a speed of about 2000 rpm for about 5 minutes to prepare a carrier portion in the form of a liquid. Thereafter, 1000 g of water at about 32 캜 and 360 g of common corn starch (supplier: Kobunshi Kagaku Co., Ltd., Korea) were sequentially added thereto while stirring the carrier portion kept in the reactor, and the mixture was stirred for 5 minutes. Thereafter, 7 g of borax was added to the reactor and stirred for 5 minutes to prepare a starch-based adhesive for corrugated board.

접착제 제조예 1-4.Adhesive Production Examples 1-4.

유리 재질의 반응기에 약 52℃의 물 750g을 넣고, 여기에 첨가제 제조예 1에서 제조한 전분계 접착제용 첨가제 조성물 37.5g, 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 42.5g을 순차적으로 첨가하고 교반한 후, 다시 33 중량% 농도의 수산화나트륨륨 수용액 33g을 첨가하고 약 2000 rpm의 속도로 약 5분 동안 교반하여 호화액 형태의 캐리어부를 제조하였다. 이후, 반응기에 수용된 캐리어부를 계속 교반하면서, 여기에 약 32℃의 물 1000g 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 340g을 순차적으로 첨가하고 5분 동안 교반하였다. 이후, 반응기에 붕사(borax) 8g을 첨가하고 5분 동안 교반하여 골판지용 전분계 접착제를 제조하였다.
750 g of water at about 52 캜 was placed in a glass reactor, 37.5 g of the additive composition for a starch-based adhesive prepared in Additive Preparation Example 1, and 42.5 g of common corn starch (supplier: KK) were sequentially added And 33 g of a 33% by weight aqueous sodium hydroxide solution was further added thereto and stirred at a speed of about 2000 rpm for about 5 minutes to prepare a carrier portion in the form of a liquid. Thereafter, 1000 g of water at about 32 캜 and 340 g of common corn starch (supplier: Kanto Kagaku Co., Ltd.) were sequentially added thereto while stirring the carrier portion kept in the reactor, and the mixture was stirred for 5 minutes. Then, borax (8 g) was added to the reactor and stirred for 5 minutes to prepare a starch-based adhesive for corrugated board.

접착제 제조예 1-5.Adhesive Production Example 1-5.

유리 재질의 반응기에 약 52℃의 물 750g을 넣고, 여기에 첨가제 제조예 1에서 제조한 전분계 접착제용 첨가제 조성물 37.5g, 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 42.5g을 순차적으로 첨가하고 교반한 후, 다시 33 중량% 농도의 수산화나트륨 수용액 33g을 첨가하고 약 2000 rpm의 속도로 약 5분 동안 교반하여 호화액 형태의 캐리어부를 제조하였다. 이후, 반응기에 수용된 캐리어부를 계속 교반하면서, 여기에 약 32℃의 물 1000g 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 320g을 순차적으로 첨가하고 5분 동안 교반하였다. 이후, 반응기에 붕사(borax) 10g을 첨가하고 5분 동안 교반하여 골판지용 전분계 접착제를 제조하였다.
750 g of water at about 52 캜 was placed in a glass reactor, 37.5 g of the additive composition for a starch-based adhesive prepared in Additive Preparation Example 1, and 42.5 g of common corn starch (supplier: KK) were sequentially added 33 g of an aqueous sodium hydroxide solution having a concentration of 33% by weight was further added thereto, followed by stirring at a speed of about 2000 rpm for about 5 minutes to prepare a carrier portion in the form of a liquor. Thereafter, 1000 g of water at about 32 캜 and 320 g of common corn starch (supplier: Kobunshi Kagaku Co., Ltd., Korea) were sequentially added thereto while stirring the carrier portion kept in the reactor, and the mixture was stirred for 5 minutes. Thereafter, 10 g of borax was added to the reactor and stirred for 5 minutes to prepare a starch-based adhesive for corrugated cardboard.

접착제 제조예 2.Adhesive Production Example 2

전분계 접착제용 첨가제 조성물로 첨가제 제조예 2에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
A starch-based adhesive for corrugated cardboard was produced under the same conditions and in the same manner as in Preparation Example 1 of the adhesive, except that the additive composition for additive for starch-based adhesives was used.

접착제 제조예 3.Adhesive Production Example 3

전분계 접착제용 첨가제 조성물로 첨가제 제조예 3에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
A starch-based adhesive for corrugated cardboard was prepared in the same manner as in Preparation Example 1 of the adhesive, except that the additive composition for a starch-based adhesive was prepared in the same manner as in Preparation Example 3 of the additive.

접착제 제조예 4.Adhesive Production Example 4.

전분계 첨가제 조성물로 첨가제 제조예 4에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 접착제를 제조하였다.
An adhesive for corrugated cardboard was produced under the same conditions and in the same manner as in Preparation Example 1 of the adhesive, except that the starch-based additive composition used in the additive preparation example 4 was used.

접착제 제조예 5.Adhesive Production Example 5.

전분계 접착제용 첨가제 조성물로 첨가제 제조예 5에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
A starch-based adhesive for corrugated cardboard was prepared in the same manner as in Preparation Example 1 of the adhesive preparation, except that the additive composition for additive for starch-based adhesives was used.

접착제 비교제조예 1.Adhesive Comparative Production Example 1

전분계 접착제용 첨가제 조성물로 첨가제 비교제조예 1에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
A starch-based adhesive for corrugated cardboard was prepared in the same manner as in Preparation Example 1 of the adhesive, except that the additive composition for starch-based adhesive was prepared in Comparative Preparation Example 1.

접착제 비교제조예 2.Adhesive Comparative Production Example 2

전분계 접착제용 첨가제 조성물로 첨가제 비교제조예 2에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
A starch-based adhesive for corrugated cardboard was prepared in the same manner as in Preparation Example 1 of the adhesive preparation, except that the additive composition for starch-based adhesives used in Comparative Preparation Example 2 was used.

접착제 비교제조예 3.Adhesive Comparative Production Example 3

전분계 접착제용 첨가제 조성물로 첨가제 비교제조예 3에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
A starch-based adhesive for corrugated cardboard was prepared in the same manner as in Preparation Example 1 of the adhesive, except that the additive composition for the starch-based adhesive was prepared in Comparative Preparation Example 3.

접착제 비교제조예 4.Adhesive Comparative Production Example 4.

전분계 첨가제 조성물로 첨가제 비교제조예 5에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
A starch-based adhesive for corrugated cardboard was prepared in the same manner as in Preparation Example 1 of the adhesive, except that the additive composition prepared in Comparative Preparation Example 5 was used as the starch-based additive composition.

접착제 비교제조예 5.Adhesive Comparative Production Example 5

전분계 접착제용 첨가제 조성물로 골판지 접착제용 타피오카 저점도 변성전분(제품명 : AMYLOK A; 공급자 : National Starch and Chemical Co., 미국)를 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
Except that tapioca low viscosity modified starch (trade name: AMYLOK A; supplied by National Starch and Chemical Co., USA) for corrugated cardboard adhesive was used as the additive composition for a starch based adhesive, A starch-based adhesive was prepared.

접착제 비교제조예 6.Adhesive Comparative Production Example 6

전분계 접착제용 첨가제 조성물로 일반 전분과 용해성 고분자가 혼합된 프리믹스 형태의 제품(제품명 : 강력분말; 공급자 : 화진 케미칼, 대한민국)을 사용한 점을 제외하고는 접착제 제조예 1과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
Except that a premix type product (trade name: Powder Powder; supplier: Hwajin Chemical Co., Ltd.) in which general starch and soluble polymer were mixed as an additive composition for a starch-based adhesive was used, A starch-based adhesive was prepared.

접착제 비교제조예 7.Adhesive Comparative Production Example 7

유리 재질의 반응기에 약 52℃의 물 750g을 넣고, 여기에 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 80g을 첨가하고 교반한 후, 다시 33 중량% 농도의 수산화나트륨 수용액 33g을 첨가하고 약 2000 rpm의 속도로 약 5분 동안 교반하여 호화액 형태의 캐리어부를 제조하였다. 이후, 반응기에 수용된 캐리어부를 계속 교반하면서, 여기에 약 32℃의 물 1000g 및 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 400g을 순차적으로 첨가하고 5분 동안 교반하였다. 이후, 반응기에 붕사(borax) 6g을 첨가하고 5분 동안 교반하여 골판지용 전분계 접착제를 제조하였다.
To the glass reactor, 750 g of water at about 52 캜 was added, and 80 g of common corn starch (supplier: Kobunshi Co., Ltd., Korea) was added and stirred. Then, 33 g of a 33 wt% aqueous solution of sodium hydroxide rpm for about 5 minutes to prepare a carrier portion in the form of a liquefied liquid. Thereafter, 1000 g of water at about 32 캜 and 400 g of common corn starch (supplier: Kobunshi Kagaku Co., Ltd., Korea) were sequentially added thereto while stirring the carrier portion accommodated in the reactor, and the mixture was stirred for 5 minutes. Thereafter, 6 g of borax was added to the reactor and stirred for 5 minutes to prepare a starch-based adhesive for corrugated board.

(2) 투 탱크(two tank) 제호 방식에 의한 골판지용 전분계 접착제의 제조
(2) Production of starch-based adhesives for corrugated cardboard by two-tank method

접착제 제조예 6.Adhesive Production Example 6

유리 재질의 반응기에 약 50℃의 물 500g을 넣고, 여기에 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 55g을 첨가하고 교반한 후, 다시 33 중량% 농도의 수산화나트륨 수용액 27.6g을 첨가하고 약 1500 rpm의 속도로 약 10분 동안 교반하여 호화액 형태의 캐리어부를 제조하였다. 유리 재질의 다른 반응기에 약 32℃의 물 790g을 넣고, 여기에 첨가제 제조예 1에서 제조한 전분계 접착제용 첨가제 조성물 22g, 일반 옥수수 전분(공급자 : 대상 주식회사, 대한민국) 242g 및 붕사 5.8g을 순차적으로 첨가하고 5분 동안 교반하여 메인부를 제조하였다. 이후, 캐리어부를 메인부가 수용된 반응기에 약 10분 동안 서서히 투입하고 약 15분 동안 교반하여 골판지용 전분계 접착제를 제조하였다.
To the glass reactor, 500 g of water at about 50 캜 was added, and 55 g of common corn starch (supplier: Kobunshi Kabushiki Kaisha, Korea) was added and stirred. Then, 27.6 g of a sodium hydroxide aqueous solution having a concentration of 33% The mixture was stirred at a speed of 1500 rpm for about 10 minutes to prepare a carrier portion in the form of a liquor. 790 g of water at about 32 캜 was placed in another reactor made of glass and 22 g of the additive composition for a starch-based adhesive prepared in Additive Preparation Example 1, 242 g of common corn starch (supplier: KK), and 5.8 g of borax were added sequentially And the mixture was stirred for 5 minutes to prepare a main portion. Thereafter, the carrier portion was slowly added to the reactor containing the main portion for about 10 minutes and stirred for about 15 minutes to prepare a starch-based adhesive for corrugated cardboard.

접착제 제조예 7.Adhesive Production Example 7.

전분계 접착제용 첨가제 조성물로 첨가제 제조예 4에서 제조한 것을 사용한 점을 제외하고는 접착제 제조예 6과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
A starch-based adhesive for corrugated cardboard was produced under the same conditions and in the same manner as in Preparation Example 6 of the adhesive, except that the additive composition for a starch-based adhesive was prepared in the same manner as in Preparation Example 4 of the additive.

접착제 비교제조예 8.Adhesive Comparative Production Example 8

전분계 접착제용 첨가제 조성물로 골판지 접착제용 타피오카 저점도 변성전분(제품명 : AMYLOK A; 공급자 : National Starch and Chemical Co., 미국)를 사용한 점을 제외하고는 접착제 제조예 6과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
Except that tapioca low viscosity modified starch (trade name: AMYLOK A; supplied by National Starch and Chemical Co., USA) for corrugated cardboard adhesive was used as the additive composition for a starch-based adhesive. A starch-based adhesive was prepared.

접착제 비교제조예 9.Adhesive Comparative Production Example 9

전분계 접착제용 첨가제 조성물로 일반 전분과 용해성 고분자가 혼합된 프리믹스 형태의 제품(제품명 : 강력분말; 공급자 : 화진 케미칼, 대한민국)을 사용한 점을 제외하고는 접착제 제조예 6과 동일한 조건 및 방법으로 골판지용 전분계 접착제를 제조하였다.
Except that a premix type product (trade name: strong powder: Supplier: Hwajin Chemical Co., Ltd.) in which general starch and soluble polymer were mixed as an additive composition for a starch-based adhesive was used, A starch-based adhesive was prepared.

3. 골판지용 3. For corrugated board 전분계Starch-based 접착제의 물성 평가 Evaluation of properties of adhesives

접착제 제조예 1-1 내지 7 및 접착제 비교제조예 1 내지 9에서 제조한 골판지용 전분계 접착제의 주요 물성으로 포드 컵 점도 및 접착력을 측정하였다.
Adhesive Production Examples 1-1 to 7 and Adhesives Comparative Examples 1 to 9 were evaluated for the main properties of the starch-based adhesive for corrugated cardboard and the cup cup viscosity and adhesion.

(1) 포드 컵(Ford cup) 점도의 측정 방법(1) Method of measuring viscosity of Ford cup

골판지용 전분계 접착제를 포드용 컵 점도계(제품명 : Fordcup visco tester #3; 공급자 ; Soltec)의 포드 컵 용기에 넣고 포드 컵 용기 바닥의 구멍을 통해 일정량의 골판지용 접착제가 유출되는데 소요되는 시간을 측정하였다.
The starch-based adhesive for corrugated board was placed in a Ford cup container of a Ford cup viscometer (product name: Fordcup visco tester # 3; supplied by Soltec), and the time required for a certain amount of corrugated board adhesive to flow out through the hole in the bottom of the cup cup was measured Respectively.

(2) 접착력의 측정방법(2) Method of measuring adhesive force

실험실용 코터(제품명 : K-Coater; 공급자 : RK Coat Instruments LTd)의 #3 로드바를 이용하여 KLB180 원지의 35㎜×*40㎜ 면적에 골판지용 전분계 접착제를 도포하였다. 이후, 도포된 부위에 다른 KLB180 원지를 붙이고, 약 150℃로 가온된 다리미로 문지르고 골판지용 접착제를 건조시켜 시료를 제조하였다. 이후, 인장강도 측정기(제품명 : TA-XT Plus; 공급자 : Stable Micro Systems)로 시료의 접착 강도를 측정하였다.
A starch-based adhesive for corrugated cardboard was applied to a 35 mm x 40 mm area of KLB 180 raw paper using a # 3 rod bar of a laboratory coater (product name: K-Coater; supplier: RK Coat Instruments LTd). Then, a different KLB 180 raw paper was attached to the applied area, rubbed with a warmed iron at about 150 ° C, and the adhesive for corrugated cardboard was dried to prepare a sample. Thereafter, the adhesive strength of the sample was measured with a tensile strength meter (product name: TA-XT Plus; supplier: Stable Micro Systems).

(3) 골판지용 전분계 접착제의 물성 측정 결과(3) Results of measurement of physical properties of starch-based adhesive for corrugated cardboard

하기 표 1은 제조예 1-1 내지 7 및 접착제 비교제조예 1 내지 9에서 제조한 골판지용 전분계 접착제의 포드 컵 점도 및 접착력을 측정한 결과를 나타낸 것이다.Table 1 below shows the results of measurement of the cup cup viscosity and adhesion of the starch-based adhesive for corrugated cardboard prepared in Production Examples 1-1 to 7 and Comparative Production Examples 1 to 9.

골판지용 전분계 접착제 구분Starch-based adhesive for corrugated board 제호 방식Method of addressing 포드 컵 점도(초)Ford cup viscosity (sec) 접착 강도(gf)Adhesive strength (g f ) 접착제 제조예 1-1Adhesive Production Example 1-1 원 탱크(one tank) 방식One tank system 3232 889889 접착제 제조예 1-2Adhesive Production Example 1-2 3535 862862 접착제 제조예 1-3Adhesive Production Example 1-3 3232 846846 접착제 제조예 1-4Adhesive Production Example 1-4 3232 805805 접착제 제조예 1-5Adhesive Production Example 1-5 3535 762762 접착제 제조예 2Adhesive Production Example 2 2929 875875 접착제 제조예 3Adhesive Production Example 3 3131 880880 접착제 제조예 4Adhesive Production Example 4 3232 878878 접착제 제조예 5Adhesive Production Example 5 3030 894894 접착제 비교제조예 1Comparative Example 1 3131 695695 접착제 비교제조예 2Comparative Example 2 7272 732732 접착제 비교제조예 3Adhesive Comparative Production Example 3 2424 613613 접착제 비교제조예 4Adhesive Comparative Production Example 4 4949 689689 접착제 비교제조예 5Adhesive Comparative Production Example 5 2525 701701 접착제 비교제조예 6Comparative Example 6 2020 750750 접착제 비교제조예 7Adhesive Comparative Production Example 7 5555 678678 접착제 제조예 6Adhesive Production Example 6 투 탱그(two tank) 방식Two-tank system 3030 751751 접착제 제조예 7Adhesive Production Example 7 3030 762762 접착제 비교제조예 8Adhesive Comparative Production Example 8 2525 694694 접착제 비교제조예 9Adhesive Comparative Production Example 9 3030 679679

상기 표 1에 의할 때, 첨가제 제조예 1 내지 5에서 제조한 첨가제 조성물로부터 골판지용 전분계 접착제를 제조하는 경우 전분계 접착제의 물성을 변화시키지 않으면서 동시에 메인부에 사용되는 일반 옥수수 전분의 사용량을 줄일 수 있다. 또한, 첨가제 제조예 1 내지 5에서 제조한 첨가제 조성물을 이용하여 제조한 골판지용 전분계 접착제 및 제조예 1 내지 5에서 제조한 첨가제 조성물을 이용하여 제조한 캐리어부 또는 메인부를 포함하는 골판지용 전분계 접착제는 적정 수준의 점도를 유지하여 원지로의 도포성 및 침투성이 양호하다. 또한, 첨가제 제조예 1 내지 5에서 제조한 첨가제 조성물을 이용하여 제조한 골판지용 전분계 접착제 및 제조예 1 내지 5에서 제조한 첨가제 조성물을 이용하여 제조한 캐리어부 또는 메인부를 포함하는 골판지용 전분계 접착제는 우수한 접착력을 나타낸다.When the starch-based adhesive for corrugated cardboard was prepared from the additive composition prepared in Additive Preparation Examples 1 to 5, the physical properties of the starch-based adhesive were not changed, and the amount of common corn starch used in the main part . Further, it is also possible to use the starch-based adhesive for corrugated cardboard manufactured using the additive composition prepared in Additive Preparation Examples 1 to 5 and the carrier portion or the starch-based starch-based corrugated cardboard material containing the main portion prepared using the additive composition prepared in Production Examples 1 to 5 The adhesive maintains an appropriate level of viscosity and is excellent in coating property and permeability to raw paper. Further, it is also possible to use the starch-based adhesive for corrugated cardboard manufactured using the additive composition prepared in Additive Preparation Examples 1 to 5 and the carrier portion or the starch-based starch-based corrugated cardboard material containing the main portion prepared using the additive composition prepared in Production Examples 1 to 5 The adhesive exhibits excellent adhesion.

한편, 일반 옥수수 전분만을 사용한 접착제 비교제조예 7, 일반 옥수수 전분의 첨가량이 상대적으로 높은 접착제 비교제조예 4 및 규산나트륨을 사용하지 않은 접착제 비교제조예 2에서 제조한 골판지용 전분계 접착제는 점도가 상대적으로 높아 도포성 및 침투성이 불량하고, 접착력이 상대적으로 낮게 나타났으며, 다른 접착제 비교제조예에서 제조한 골판지용 전분계 접착제도 접착력이 상대적으로 낮게 나타났다.
On the other hand, the adhesive using only common corn starch Comparative Preparation Example 7, the adhesive having relatively high addition amount of common corn starch, the comparative preparation example 4, and the adhesive without using sodium silicate The starch-based adhesive for corrugated cardboard prepared in Comparative Preparation Example 2 had a viscosity The adhesive strength was relatively low, and the adhesive strength was relatively low. Also, the adhesive strength of the starch-based adhesive for corrugated cardboard manufactured in the comparative example of other adhesives was relatively low.

이상에서와 같이 본 발명을 상기의 실시예를 통해 설명하였지만 본 발명이 반드시 여기에만 한정되는 것은 아니며 본 발명의 범주와 사상을 벗어나지 않는 범위 내에서 다양한 변형실시가 가능함은 물론이다. 따라서, 본 발명의 보호범위는 본 발명에 첨부된 특허청구의 범위에 속하는 모든 실시 태양을 포함하는 것으로 해석되어야 한다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. Accordingly, the scope of protection of the present invention should be construed as including all embodiments falling within the scope of the appended claims.

Claims (22)

전체 중량을 기준으로 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 55~85 중량%, 저점도화 전분 6~18 중량%, 수용성 무기물 3~14 중량% 및 점착성 개선제 3~14 중량%를 포함하고,
상기 저점도화 과정을 거치지 않은 일반전분은 옥수수 전분, 찰옥수수 전분, 타피오카 전분, 감자 전분, 고구마 전분 및 밀 전분으로 이루어진 군에서 선택된 1종 이상이고,
상기 저점도화 과정을 거치지 않은 변성전분은 옥수수 전분, 찰옥수수 전분, 타피오카 전분, 감자 전분, 고구마 전분 및 밀 전분으로 이루어진 군에서 선택된 1종 이상의 전분이 에스테르화, 에테르화 또는 그라프트화된 것이고,
상기 저점도화 전분은 산화전분(oxidized starch), 산처리전분(thin boiling starch), 덱스트린 및 효소처리 전분으로 이루어진 군에서 선택된 1종 이상으로 구성되고, 50℃에서 20 중량% 호화액의 점도가 50~400 센티포이즈(centipoise, cPs) 이며,
상기 점착성 개선제는 로진(rosin), 열가소성 비닐계 수지, 열가소성 변성 셀룰로오스 및 카제인으로 이루어진 군에서 선택된 1종 이상인 것을 특징으로 하는 전분계 접착제용 첨가제 조성물.
55 to 85% by weight of general starch or modified starch, 6 to 18% by weight of a low viscosity starch, 3 to 14% by weight of a water-soluble inorganic substance and 3 to 14% by weight of a stickiness improver,
The ordinary starches not subjected to the low-viscosity treatment may be at least one selected from the group consisting of corn starch, waxy corn starch, tapioca starch, potato starch, sweet potato starch and wheat starch,
The modified starches which have not undergone the lowering step are those obtained by esterification, etherification or grafting of at least one starch selected from the group consisting of corn starch, waxy corn starch, tapioca starch, potato starch, sweet potato starch and wheat starch,
Wherein the low viscosity starch is composed of at least one selected from the group consisting of oxidized starch, thin boiling starch, dextrin and enzyme-treated starch, wherein the viscosity of the 20 wt% ~ 400 centipoise (cPs)
Wherein the tackiness-improving agent is at least one selected from the group consisting of rosin, thermoplastic vinyl resin, thermoplastic modified cellulose and casein.
제 1항에 있어서, 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 전분 70~80 중량%, 저점도화 전분 10~15 중량%, 수용성 무기물 5~7.5 중량% 및 점착성 개선제 5~7.5 중량%를 포함하는 것을 특징으로 하는 전분계 접착제용 첨가제 조성물.
The method according to claim 1, comprising 70 to 80% by weight of general starch or modified starch starch which has not undergone a low viscosity, 10 to 15% by weight of a low viscosity starch, 5 to 7.5% by weight of a water soluble inorganic substance and 5 to 7.5% By weight based on the total weight of the composition.
제 1항에 있어서, 상기 저점도화 전분은 50℃에서 20 중량% 호화액의 점도가 100~350 센티포이즈(centipoise, cPs) 인 것을 특징으로 하는 전분계 접착제용 첨가제 조성물.
The additive composition for a starch-based adhesive according to claim 1, wherein the low viscosity starch has a viscosity of 100 to 350 centipoise (cPs) at 20 ° C at 50 ° C.
삭제delete 제 1항 내지 제 3항 중 어느 한 항에 있어서, 상기 수용성 무기물은 규산계 화합물인 것을 특징으로 하는 전분계 접착제용 첨가제 조성물.
The additive composition for a starch-based adhesive according to any one of claims 1 to 3, wherein the water-soluble inorganic material is a silicic acid-based compound.
제 5항에 있어서, 상기 규산계 화합물은 규산나트륨(sodium silicate) 또는 규산칼륨(potassium silicate)인 것을 특징으로 하는 전분계 접착제용 첨가제 조성물.
The additive composition for a starch-based adhesive according to claim 5, wherein the silicate-based compound is sodium silicate or potassium silicate.
제 1항 내지 제 3항 중 어느 한 항에 있어서, 상기 열가소성 비닐계 수지는 폴리비닐아세테이트(Polyvinyl acetate), 폴리비닐알코올(Polyvinyl alcohol), 에틸렌-비닐아세테이트 공중합체(Ehtylene-Vinyl Acetate Copolymer, EVA) 및 에틸렌-비닐알코올 공중합체(Ehtylene-Vinyl Alcohol Copolymer, EVOH)로 이루어진 군에서 1종 이상 선택되는 것을 특징으로 하는 전분계 접착제용 첨가제 조성물.
4. The thermoplastic resin composition according to any one of claims 1 to 3, wherein the thermoplastic vinyl resin is at least one selected from the group consisting of polyvinyl acetate, polyvinyl alcohol, ethylene-vinyl acetate copolymer (EVA-Vinyl Acetate Copolymer) ) And an ethylene-vinyl alcohol copolymer (EVOH). The additive composition for a starch-based adhesive according to claim 1, wherein the at least one additive is selected from the group consisting of ethylene-vinyl alcohol copolymer (EVOH)
제 1항 내지 제 3항 중 어느 한 항에 있어서, 상기 열가소성 변성 셀룰로오스는 셀룰로오스 에스테르 유도체인 것을 특징으로 하는 전분계 접착제용 첨가제 조성물.
The additive composition for a starch-based adhesive according to any one of claims 1 to 3, wherein the thermoplastic modified cellulose is a cellulose ester derivative.
제 8항에 있어서, 상기 셀룰로오스 에스테르 유도체는 메틸 셀룰로오스, 에틸 셀룰로오스, 에틸메틸 셀룰로오스, 하이드록시에틸 셀룰로오스, 하이드록시프로필 셀룰로오스, 하이드록시에틸메틸 셀룰로오스, 하이드록시프로필메틸 셀룰로오스, 에틸하이드록시에틸 셀룰로오스 및 카르복시메틸 세룰로오스로 이루어진 군에서 1종 이상 선택되는 것을 특징으로 하는 전분계 접착제용 첨가제 조성물.
The cellulose ester derivative according to claim 8, wherein the cellulose ester derivative is selected from the group consisting of methylcellulose, ethylcellulose, ethylmethylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, hydroxyethylmethylcellulose, hydroxypropylmethylcellulose, ethylhydroxyethylcellulose, Methylcellulose, and methylcellulose. The additive composition for a starch-based adhesive according to claim 1,
삭제delete 삭제delete 삭제delete 원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 캐리어부로서,
물, 제 1항의 전분계 접착제용 첨가제 조성물, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분, 및 알칼리 물질을 포함하는 혼합물 형태이고,
저점도화 과정을 거치지 않은 일반전분 또는 변성전분 및 저점도화 전분은 모두 호화된 상태로 존재하는 것을 특징으로 하는 캐리어부.
A carrier part used in a starch-based adhesive manufacturing process by a one-tank or two-tank sealing method,
Water, an additive composition for a starch-based adhesive according to any one of claims 1 to 3, and a starch-modified starch which is not subjected to a low-viscosity treatment separately from an additive composition for a starch-based adhesive,
Characterized in that the ordinary starch or the modified starch and the low-viscosity starch which have not undergone the low-viscosity treatment are present in a state of being enriched.
제 13항에 있어서, 물 100 중량부 당 전분계 접착제용 첨가제 조성물 3~7 중량부, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 3.5~7.5 중량부 및 알칼리 물질 1~2.5 중량부를 포함하는 것을 특징으로 하는 캐리어부.
14. The composition of claim 13, wherein 3-7 parts by weight of the additive composition for a starch based adhesive is added to 100 parts by weight of water, 3.5-7.5 parts by weight of ordinary starch or modified starch which is not subjected to a low- 1 to 2.5 parts by weight of a material.
제 14항에 있어서, 물 100 중량부 당 전분계 접착제용 첨가제 조성물 4~6 중량부, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 4~7 중량부 및 알칼리 물질 1~2 중량부를 포함하는 것을 특징으로 하는 캐리어부.
The composition according to claim 14, which comprises 4 to 6 parts by weight of an additive composition for a starch-based adhesive per 100 parts by weight of water, 4 to 7 parts by weight of a general starch or modified starch which is not subjected to a low- 1 to 2 parts by weight of a substance.
제 13항에 있어서, 상기 알칼리 물질은 수산화나트륨, 수산화칼슘 및 수산화칼륨으로 이루어진 군에서 선택된 1종 이상인 것을 특징으로 하는 캐리어부.
14. The carrier part of claim 13, wherein the alkali material is at least one selected from the group consisting of sodium hydroxide, calcium hydroxide, and potassium hydroxide.
원 탱크(one tank) 제호 방식 또는 투 탱크(two tank) 제호 방식에 의한 전분계 접착제 제조 공정에 사용되는 메인부로서,
물, 제 1항의 전분계 접착제용 첨가제 조성물, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분, 및 붕소 함유 화합물을 포함하는 혼합물 형태인 것을 특징으로 하는 메인부.
A main part used in a starch-based adhesive manufacturing process by a one-tank or two-tank sealing method,
Wherein the additive composition for a starch-based adhesive according to claim 1, the additive composition for a starch-based adhesive according to claim 1, and the starch-modified starch or the modified starch.
제 17항에 있어서, 물 100 중량부 당 전분계 접착제용 첨가제 조성물 1.5~4.5 중량부, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 25~35 중량부 및 붕소 함유 화합물 0.5~1.0 중량부를 포함하는 것을 특징으로 하는 메인부.
18. The composition according to claim 17, wherein 1.5 to 4.5 parts by weight of an additive composition for a starch-based adhesive is added to 100 parts by weight of water, 25 to 35 parts by weight of a general starch or modified starch not subjected to a low- Containing compound in an amount of 0.5 to 1.0 part by weight.
제 18항에 있어서, 물 100 중량부 당 전분계 접착제용 첨가제 조성물 2~4 중량부, 전분계 접착제용 첨가제 조성물과 별개의 저점도화 과정을 거치지 않은 일반전분 또는 변성전분 27~33 중량부 및 붕소 함유 화합물 0.5~1.0 중량부를 포함하는 것을 특징으로 하는 메인부.
The composition according to claim 18, which comprises 2 to 4 parts by weight of an additive composition for a starch based adhesive, 100 parts by weight of water, 27 to 33 parts by weight of a modified starch or modified starch which is not subjected to a low- Containing compound in an amount of 0.5 to 1.0 part by weight.
제 17항에 있어서, 상기 붕소 함유 화합물은 붕사인 것을 특징으로 하는 메인부.
18. The main part according to claim 17, wherein the boron-containing compound is borax.
제 13항 내지 제 16항 중 어느 한 항의 캐리어부 또는 제 17항 내지 제 20항 중 어느 한 항의 메인부를 포함하는 전분계 접착제.
A starch-based adhesive comprising the carrier part of any one of claims 13 to 16 or the main part of any one of claims 17 to 20.
제 21항에 있어서, 골판지 제조, 벽지 제조, 종이층 결합, 또는 펄프 몰드 제조시 접착제로 사용되는 것을 특징으로 하는 전분계 접착제.22. The starch-based adhesive of claim 21, used as an adhesive in corrugated paper manufacturing, wallpaper making, paper layer bonding, or pulp mold making.
KR1020120156014A 2012-12-28 2012-12-28 Additive composition for starch-based adhesive and use of the same KR101436942B1 (en)