KR101351479B1 - Insulation film using psa mixed with aerogel and method for manufacturing the same - Google Patents

Insulation film using psa mixed with aerogel and method for manufacturing the same Download PDF

Info

Publication number
KR101351479B1
KR101351479B1 KR1020110143543A KR20110143543A KR101351479B1 KR 101351479 B1 KR101351479 B1 KR 101351479B1 KR 1020110143543 A KR1020110143543 A KR 1020110143543A KR 20110143543 A KR20110143543 A KR 20110143543A KR 101351479 B1 KR101351479 B1 KR 101351479B1
Authority
KR
South Korea
Prior art keywords
sensitive adhesive
airgel
pressure
psa
mixed
Prior art date
Application number
KR1020110143543A
Other languages
Korean (ko)
Other versions
KR20130075241A (en
Inventor
임현창
정진안
김수민
조재훈
Original Assignee
재단법인 포항산업과학연구원
주식회사 포스코
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 재단법인 포항산업과학연구원, 주식회사 포스코 filed Critical 재단법인 포항산업과학연구원
Priority to KR1020110143543A priority Critical patent/KR101351479B1/en
Publication of KR20130075241A publication Critical patent/KR20130075241A/en
Application granted granted Critical
Publication of KR101351479B1 publication Critical patent/KR101351479B1/en

Abstract

본 발명은 에어로겔이 혼합된 압력 감지 점착제(PSA)를 이용하여 열관류율을 낮춘 단열 필름 및 그 제조 방법에 관한 것이다. 본 발명에 따른 단열 필름은, 에어로겔이 혼합된 압력 감지 점착제(PSA), 및 에어로겔이 혼합된 압력 감지 점착제(PSA)가 상부에 도포되는 필름을 포함하여 이루어진다. 본 발명에 따른 단열 필름 제조 방법은, 압력 감지 점착제의 고형분 비율을 조절하는 단계; 고형분 대비 에어로겔의 비율을 조절하는 단계; 압력 감지 점착제에 상기 에어로겔을 교반하여 혼합하는 단계; 에어로겔이 혼합된 압력 감지 점착제를 필름에 도포하는 단계를 포함하여 이루어진다. The present invention relates to a heat insulating film having a low heat permeability using a pressure-sensitive adhesive (PSA) mixed with an airgel and a method of manufacturing the same. The heat insulation film according to the present invention comprises a pressure sensitive adhesive (PSA) in which an airgel is mixed, and a film in which the pressure sensitive adhesive (PSA) in which the airgel is mixed is applied. Method for producing a heat insulation film according to the invention, the step of adjusting the solid content ratio of the pressure-sensitive adhesive; Adjusting the ratio of airgel to solids; Stirring and mixing the airgel with a pressure sensitive adhesive; Applying a pressure-sensitive adhesive mixed with an airgel on the film is made.

Description

에어로겔이 혼합된 압력 감지 점착제를 이용한 단열 필름 및 그 제조 방법{INSULATION FILM USING PSA MIXED WITH AEROGEL AND METHOD FOR MANUFACTURING THE SAME}INSULATION FILM USING PSA MIXED WITH AEROGEL AND METHOD FOR MANUFACTURING THE SAME}

본 발명은 단열 필름에 관한 것으로서, 특히, 에어로겔이 혼합된 압력 감지 점착제(PSA)를 이용하여 열관류율을 낮춘 단열 필름 및 그 제조 방법에 관한 것이다.The present invention relates to a heat insulating film, and more particularly, to a heat insulating film having a low heat permeability using a pressure-sensitive adhesive (PSA) mixed with an airgel and a method of manufacturing the same.

현재 일반적으로 사용되고 있는 에너지의 대부분은 화석연료에서 얻어지는데, 그 소비가 매년 증가하여 근시일 내에 지구상의 모든 화석연료가 고갈될 것으로 예측되고 있다. 또한 화석연료는 온실가스를 대기 중으로 배출하여 지구 온난화의 주범이 되고 있으며, 해수면 상승 등 기후 변화를 유발시키는 주요 원인으로 알려지면서 국제사회에서 각종 협약에 의하여 개별 국가에 사용을 제한하고 있다.Most of the energy currently in use today comes from fossil fuels, which are expected to increase every year and deplete all fossil fuels on Earth in the near future. In addition, fossil fuels emit greenhouse gases into the atmosphere, becoming a major culprit of global warming, and are known to be a major cause of climate change, such as sea level rise.

이러한 상황은 에너지의 효율적 이용을 위한 절약 설비에 대한 투자로 이어져서, 구 건축물을 에너지 저소비형 구조로 전환하고 신규 건축물에서는 에너지 소비 규정에 대한 규제가 강화되고 있다.This situation has led to investments in saving facilities for efficient use of energy, which has led to the conversion of old buildings to low energy consumption structures, and the tightening of energy consumption regulations in new buildings.

이러한 점에서 창호(window)는 건물 내외부를 관통하는 중요한 매개체이나 이 창호는 벽체에 비하여 열전도율이 10배 이상으로 취약하다. 통상적으로 건물의 에너지 소모분의 약 40%가 창을 통하여 이루어지고 있는데, 에너지 수입이 98%인 한국의 실정에서는 창호를 통한 건축물의 단열율을 높이는 것이 에너지 절약의 지름길이며 나아가 국가경제의 경쟁력 강화에 직결된다고 할 수 있다. In this regard, windows are important mediators that penetrate the interior and exterior of buildings, but these windows are ten times more fragile than thermal walls. Normally, 40% of the energy consumption of buildings is made through windows. In Korea, where energy import is 98%, increasing the insulation rate of buildings through windows is a shortcut to energy saving and further strengthening the competitiveness of the national economy. It can be said that directly.

실질적으로, 국내 에너지 수요는 매년 대략 100만 내지 200만 톤(석유환산기준)인데, 이중 국내 건물 부분에서 이뤄지는 국가 에너지 총소비는 전체 에너지 소비의 약 24%로 알려 있으며, 이 중에서도 건물의 전체 열손실의 40%가 창을 통해 이루어진다고 알려져 있다.In fact, domestic energy demand is approximately 1 million to 2 million tonnes (oil equivalent) annually, of which the total national energy consumption in the domestic building sector is known to be about 24% of the total energy consumption, among which the total heat of buildings It is known that 40% of the loss is through the window.

참고로, 에너지 관리공단이 3년된 국내건물의 에너지 성능 분석결과 최대 냉방 부하 중 침기로 인한 냉방 부하가 35%로 가장 높고 창을 통한(전도. 일사) 냉방 부하는 31%로 냉방 에너지 소비의 66%가 창과 문을 통해 발생되는 것으로 나타났다. 또한, 난방 부하 역시 창과 문의 침기로 인한 요인이 63%. 그리고 창의 전도를 통해 발생한 난방 부하가 29%에 이르렀다. 이는 벽체에 의한 손실률이 5%인데 비하여 유리 창호를 통한 에너지의 낭비 및 손실이 크다고 하는 것을 단적으로 보여주고 있다.For reference, the Korea Energy Management Corporation's energy performance analysis of a three-year-old domestic building showed that the cooling load due to infiltration was the highest among the maximum cooling loads at 35%, and the cooling load through windows (conduction, solar radiation) was 31%. % Was generated through windows and doors. In addition, heating load is also 63% due to window and door aeration. And the heating load generated by the conduction of the window reached 29%. This shows that the loss rate due to the wall is 5%, but the waste and loss of energy through the glass window is large.

이 때문에 국내는 물론이고 국제적으로도 건물에서 에너지 절약의 절대적 요소인 창호를 통한 에너지 절약을 위해 창호의 단열율을 엄격하게 규정하고 있으며 창호의 열효율성을 높이기 위한 다양한 제품이 개발되어 사용되고 있다. 특히, 독일을 포함한 유럽 및 미국 등 선진국의 대부분이 건축물의 에너지 절감을 위해 건축법에 열관류율을 규정함으로서 단열성 및 기밀성이 기존 창호에 비하여 월등한 시스템 창호를 의무화하고 있다. 일본의 건축 단열법에 따른 유리 열관류율은 2.0kcal/㎡hr℃, 그리고 영국의 경우는 2.60kcal/㎡hr℃로 규정하여, 고효율인 단열 창호의 사용율을 높이고자 하고 있다. 한국의 경우 현재 창호의 열관류율은 2.9kcal/㎡hr℃로 규정하고 있으나, 점차 규제의 강화로 복층 유리로도 단열 규정을 쉽게 만족시킬 수 없는 것이 현 실정이다.For this reason, in Korea as well as internationally, the building strictly regulates the insulation rate of windows to save energy through windows, which are the absolute elements of energy saving, and various products have been developed and used to increase the thermal efficiency of windows. In particular, most industrialized countries such as Germany and Europe and the United States stipulate heat-transfer rates in the Building Act to save energy in buildings, requiring system windows with better insulation and airtightness than existing windows. The glass heat transmission rate according to the Japanese building insulation method is 2.0kcal / ㎡hr ℃ and 2.60kcal / ㎡hr ℃ in the UK. In Korea, the heat transmission rate of windows and doors is currently set at 2.9kcal / ㎡hr ℃. However, due to the stricter regulations, it is not easy to satisfy the insulation regulations even with double-layer glass.

최근에는 창호 내부의 공기층을 늘리거나, 창호의 두께 및 갯수를 늘리고 로우 이(Low-E) 코팅을 한 유리를 이용하여 열손실을 낮추려는 시도가 있었지만 현재의 창호 시스템에서는 열관류율을 낮추는 데는 한계가 있다. In recent years, attempts have been made to reduce heat loss by increasing the air layer inside windows, increasing the thickness and number of windows, and using glass with low-E coating, but current window systems have limitations in reducing the heat transmission rate. have.

본 발명의 목적은 에어로겔이 혼합된 압력 감지 점착제(PSA)를 이용하여 높은 단열 성능을 갖는 단열 필름을 제공하는 것이다. An object of the present invention is to provide a heat insulating film having a high heat insulating performance using a pressure-sensitive adhesive (PSA) mixed with an airgel.

본 발명의 일양상에 따라서 단열 필름은, 에어로겔이 혼합된 압력 감지 점착제(PSA), 및 상기 에어로겔이 혼합된 압력 감지 점착제(PSA)가 상부에 도포되는 필름을 포함하여 이루어진다. According to an aspect of the present invention, the thermal insulation film comprises a pressure sensitive adhesive (PSA) in which an airgel is mixed, and a film in which the pressure sensitive adhesive (PSA) in which the airgel is mixed is applied.

바람직하게는, 상기 압력 감지 점착제(PSA)의 고형분(solid) 비율은 20∼40%로 유지할 수 있다. Preferably, the solid ratio of the pressure sensitive adhesive (PSA) may be maintained at 20 to 40%.

바람직하게는, 상기 고형분(solid) 대비 에어로겔의 비율은 30∼50%가 될 수 있다. Preferably, the ratio of airgel to solid may be 30 to 50%.

바람직하게는, 상기 에어로겔을 상기 압력 감지 점착제(PSA)에 혼합할 때 교반기의 rpm은 약 1,000이며 교반 시간은 약 10분이 될 수 있다. Preferably, when the airgel is mixed with the pressure sensitive adhesive (PSA), the rpm of the stirrer may be about 1,000 and the stirring time may be about 10 minutes.

바람직하게는, 상기 압력 감지 점착제(PSA)에는 솔벤트를 이용하여 점도가 조절될 수 있다.Preferably, the pressure-sensitive adhesive (PSA) may be adjusted in viscosity using a solvent.

바람직하게는, 상기 에어로겔이 혼합된 압력 감지 점착제(PSA)는 코팅기를 이용하여 일정 두께로 필름상에 도포될 수 있다. Preferably, the pressure-sensitive adhesive (PSA) in which the airgel is mixed may be applied on the film to a predetermined thickness by using a coating machine.

본 발명의 또다른 양상에 따라서, 단열 필름 제조 방법은, 압력 감지 점착제의 고형분 비율을 조절하는 단계; 고형분 대비 에어로겔의 비율을 조절하는 단계; 상기 압력 감지 점착제에 상기 에어로겔을 교반하여 혼합하는 단계; 및 상기 에어로겔이 혼합된 압력 감지 점착제를 필름에 도포하는 단계를 포함한다. According to another aspect of the invention, the method for producing a heat insulation film, the step of adjusting the solid content ratio of the pressure sensitive adhesive; Adjusting the ratio of airgel to solids; Stirring and mixing the airgel with the pressure sensitive adhesive; And applying the pressure sensitive adhesive mixed with the airgel to the film.

바람직하게는, 상기 압력 감지 점착제의 고형분 비율은 30%가 될 수 있다. Preferably, the solid content ratio of the pressure sensitive adhesive may be 30%.

바람직하게는, 상기 고형분 대비 에어로겔의 비율은 40%가 될 수 있다. Preferably, the ratio of airgel to solids may be 40%.

바람직하게는, 상기 압력 감지 점착제의 점도는 솔벤트를 이용하여 조절될 수 있다. Preferably, the viscosity of the pressure-sensitive adhesive can be adjusted using a solvent.

바람직하게는, 상기 에어로겔과 상기 압력 감지 점착제의 혼합은, 교반기를 이용하여 1000rpm으로 10분동안 교반하여 이루어질 수 있다.Preferably, the airgel and the pressure-sensitive adhesive may be mixed by stirring for 10 minutes at 1000 rpm using a stirrer.

본 발명을 실시함으로써, 에어로겔이 혼합된 압력 감지 점착제(PSA)를 이용하여 단열 필름의 단열 성능을 높일 수 있게 된다. By implementing the present invention, it is possible to increase the heat insulating performance of the heat insulating film by using a pressure-sensitive adhesive (PSA) mixed with an airgel.

도1은 본 발명에 따른 에어로겔이 혼합된 압력 감지 점착제(PSA)를 도시한 도면이다.
도2는 본 발명에 따른 단열 필름으로서, 에어로겔이 혼합된 압력 감지 점착제(PSA)가 필름에 도포되어 있는 형상을 도시한 도면이다.
도3은 본 발명에 따른 단열 필름 제조 방법을 설명하는 제조 공정도이다.1 is a view showing a pressure-sensitive adhesive (PSA) mixed with an airgel according to the present invention.
Figure 2 is a heat insulation film according to the present invention, a view showing a shape in which a pressure-sensitive adhesive (PSA) mixed with an airgel is applied to the film.
3 is a manufacturing process chart illustrating a method for manufacturing a heat insulation film according to the present invention.

이하, 본 발명의 바람직한 실시예를 첨부된 도면을 참조하여 상세히 설명한다. 도면에 기재된 사항은 발명의 사상을 설명하는데 편리를 위한 것이지, 발명이 도면에 기재된 것에 한정되는 것은 아니다. 또한, 설명의 편의를 위해서 다소 과장되어 있음을 알 수 있다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. The matters described in the drawings are for convenience in describing the idea of the invention, but the invention is not limited to those described in the drawings. In addition, it can be seen that slightly exaggerated for convenience of description.

도1은 본 발명에 따른 에어로겔이 혼합된 압력 감지 점착제(PSA)를 도시한 도면이다.1 is a view showing a pressure-sensitive adhesive (PSA) mixed with an airgel according to the present invention.

본 발명에서 사용되는 에어로겔(10)은, 실리콘 산화물(SiO2)로 구성되는 물질로서, 기공율이 90% 이상이며 비표면적이 700 내지 800m2/g 인 밀도가 매우 낮은 특성의 물질이다. 또한, 열전도율은 현존하는 고체 중에서 가장 낮아서 0,02 W/mK의 값을 갖는다. The airgel 10 used in the present invention is a material composed of silicon oxide (SiO 2 ), having a porosity of 90% or more, and a material having a very low density having a specific surface area of 700 to 800 m 2 / g. In addition, the thermal conductivity is the lowest among existing solids and has a value of 0,02 W / mK.

원래 에어로겔은 머리카락 굵기의 10만분의 1인 실리콘 산화물로 된 실이 성글게 얽혀 이루어지며, 이 실과 실 사이에는 공기 분자들이 들어 있는데, 전체 부피의 98%를 공기가 차지하는 형태였다. 제조에 시간이 많이 걸리고, 손가락으로 가볍게 누르기만 해도 깨질 정도로 약해 실용화가 어려웠으나, 특수 섬유를 첨가해 헝겊처럼 부드러워서 쉽게 깨지지 않고, 짧은 시간에 대량생산이 가능한 새로운 에어로젤 기술이 개발되었다. 이처럼 개량된 에어로젤은 섭씨 1,100℃에서도 전혀 타지 않고, 충격방지 시트를 놓고 화약을 터뜨려도 전혀 흔적이 남지 않아 유리섬유 등 기존의 건축물 단열재를 대체할 소재로 주목을 받고 있다. Originally, aerogels consisted of a coarse entangled yarn made of silicon oxide, one hundredth of the thickness of the hair, which contained air molecules, with 98% of the total volume of air. It took a lot of time to manufacture, and it was so weak that it could be broken by just pressing lightly with fingers. The improved aerogels are attracting attention as a material to replace existing building insulation materials, such as fiberglass, because they do not burn at all at 1,100 degrees Celsius, and do not leave any traces even when the powder is blown over the impact resistant sheet.

도1에 도시된 에어로겔(10)은 이처럼 개량된 에어로겔로서 그 지름의 크기(d)는 1 내지 10㎛ 정도이다.The airgel 10 shown in FIG. 1 is an improved airgel as described above, and the diameter d of the diameter is about 1 to 10 μm.

에어로겔이 혼합된 압력 감지 점착제(PSA)를 제조하기 위해서, 먼저 에어로겔이 쉽게 혼합될 수 있는 적당한 점도의 압력 감지 점착제(PSA)를 선정한다. 만일 압력 감지 점착제(PSA)의 점도가 너무 높으면 에어로겔(10)이 쉽게 교반되지 않아서 에어로겔이 압력 감지 점착제에 균일하게 확산 및 분포되는 것이 어려워질 수 있다. 또한 압력 감지 점착제는 높은 투명도를 갖는 것이 바람직한데, 에어로겔이 혼합된 후에 창호에 적용하였을 때 가능한 많은 량의 빛을 실내로 확산시킬 수 있도록 하기 위한 것이다.In order to prepare a pressure-sensitive adhesive (PSA) in which an airgel is mixed, first, a pressure-sensitive adhesive (PSA) having a suitable viscosity to which the airgel can be easily mixed is selected. If the viscosity of the pressure sensitive adhesive (PSA) is too high, the aerogel 10 may not be easily stirred, and it may be difficult for the airgel to be uniformly dispersed and distributed in the pressure sensitive adhesive. It is also desirable to have a high transparency of the pressure-sensitive adhesive, to allow as much light as possible to diffuse into the room when applied to the windows after the airgel is mixed.

압력 감지 점착제(PSA)가 선정되면, 여기에 에어로겔을 첨가한다. 비교적 점도가 낮은, 예를들면, 고형분(solid) 비율이 20∼40%인 점착제에, 고형분(solid) 비율이 30∼50%인 에어로겔을 혼합한다. Once the pressure sensitive adhesive (PSA) is selected, an airgel is added thereto. An airgel having a solid content of 30 to 50% is mixed with a pressure-sensitive adhesive having a relatively low viscosity, for example, a solid content of 20 to 40%.

압력 감지 점착제(PSA) 내부에 에어로겔을 균일하게 분산시키기 위해서 교반기를 이용할 수 있다. 이때, 교반기는 1000rpm으로 약 10분간 교반시킬 수 있다. 압력 감지 점착제(PSA)를 일정한 점도로 유지하기 위해서는 용제(solvent)를 이용하여 점도를 조정할 수 있다. In order to uniformly disperse the airgel inside the pressure sensitive adhesive (PSA), an agitator may be used. At this time, the stirrer may be stirred at 1000 rpm for about 10 minutes. In order to maintain the pressure-sensitive adhesive (PSA) at a constant viscosity, the viscosity may be adjusted using a solvent.

도2는 본 발명에 따른 단열 필름으로서, 에어로겔이 혼합된 압력 감지 점착제(PSA)가 필름에 도포되어 있는 형상을 도시한 도면이다. Figure 2 is a heat insulation film according to the present invention, a view showing a shape in which a pressure-sensitive adhesive (PSA) mixed with an airgel is applied to the film.

전술된 바와 같이 교반기를 통해서 에어로겔(10)이 균일하게 분산된 압력 감지 점착제(20)(PSA)를 필름(30)에 코팅하여 단열 필름(100)을 완성하게 된다. 이 때, 코팅기(미도시)를 사용하여 필름 상에 에어로겔(10)이 혼합된 압력 감지 점착제(20)(PSA)를 일정 두께로 균일하게 코팅할 수 있다. 에어로겔(10)이 혼합된 압력 감지 점착제(20)(PSA)의 두께를 두껍게 할수록 단열 효과는 상승하나 투명도가 저하될 수 있다. 즉, 에어로겔(10)이 혼합된 압력 감지 센서(20)(PSA)의 두께에 따른 단열 효과와 단열 필름의 투명도는 반비례하게 되어, 실내로 확산되어 들어오는 빛의 량이 줄어들게 될 수 있다. As described above, the pressure-sensitive adhesive 20 (PSA) in which the airgel 10 is uniformly dispersed through the stirrer is coated on the film 30 to complete the thermal insulation film 100. At this time, the pressure-sensitive adhesive 20 (PSA) in which the airgel 10 is mixed on the film may be uniformly coated to a predetermined thickness using a coater (not shown). The thicker the thickness of the pressure-sensitive adhesive 20 (PSA) in which the airgel 10 is mixed, the higher the thermal insulation effect, the lower the transparency. That is, the insulation effect according to the thickness of the pressure sensor 20 (PSA) in which the airgel 10 is mixed and the transparency of the insulation film are inversely proportional, and the amount of light diffused into the room may be reduced.

이 필름(30)의 재료로는 일반적으로 사용하는 비닐 필름을 사용할 수도 있고 다른 기능들을 첨가한, 예를들면 UV 차단 필름 등을 사용할 수 있다. As the material of the film 30, a vinyl film generally used may be used, or a UV blocking film or the like having other functions added thereto may be used.

도3은 본 발명에 따른 단열 필름 제조 방법을 설명하는 제조 공정도이다.3 is a manufacturing process chart illustrating a method for manufacturing a heat insulation film according to the present invention.

먼저 적당한 압력 감지 점착제(PSA)를 선정한 후에, 압력 감지 점착제 내의 고형분(solid) 비율을 조절한다 (S310). 이때, 고형분 비율은 바람직하게는, 20∼40% 정도로 유지할 수 있다. First select a suitable pressure-sensitive adhesive (PSA), and then adjust the solid ratio (solid) in the pressure-sensitive adhesive (S310). At this time, the solid content ratio is preferably maintained at about 20 to 40%.

이어서, 고형분 대비 에어로겔의 비율을 조절한다 (S320). 고형분 대비 에어로겔의 비율은 바람직하게는, 30∼50% 정도로 유지할 수 있다. Next, the ratio of the airgel to the solid content is adjusted (S320). The ratio of the airgel to the solid content is preferably maintained at about 30 to 50%.

계속해서, 압력 감지 점착제(PSA)에 상기 에어로겔을 교반하여 혼합한다 (S330). 이때, 교반기는 1000rpm으로 약 10분간 교반시켜서 압력 감지 점착제 내부에 에어로겔이 균일하게 분포되도록 한다. Subsequently, the airgel is mixed with a pressure-sensitive adhesive (PSA) by mixing (S330). At this time, the stirrer was stirred at 1000 rpm for about 10 minutes to uniformly distribute the airgel inside the pressure-sensitive adhesive.

압력 감지 점착제(PSA)를 일정한 점도로 유지하기 위해서는 용제(solvent)를 이용하여 점도를 조정할 수 있다. In order to maintain the pressure-sensitive adhesive (PSA) at a constant viscosity, the viscosity may be adjusted using a solvent.

이어서, 에어로겔이 혼합된 압력 감지 점착제(PSA)를 필름에 도포하여 단열 필름을 완성하게 된다 (S340). Subsequently, the pressure-sensitive adhesive (PSA) mixed with the airgel is applied to the film to complete the thermal insulation film (S340).

이와 같이 완성된 단열 필름은 창호 즉, 가정이나 사무실 등의 유리창이나 건물의 실내외를 분리시켜주는 곳에 부착하여 사용하게 된다. The completed thermal insulation film is attached to a window, that is, a glass window of a home or office, or a place that separates the interior and exterior of a building.

이상 본 발명이 하나의 실시예에 따라서 설명되었지만, 본 설명은 청구범위에 기재된 넓은 개념에 대한 단순한 실시예에 불과함을 알 수 있다. 청구범위에 기재된 용어들은 통상적인 의미로 해석되어야 하며, 특정하지 않는 한 이들 용어들은 특정한 또는 특별하게 한정된 의미로 제한되어서는 않됨을 알 수 있다.While the invention has been described above in accordance with one embodiment, it can be seen that this description is merely an example of a broad concept described in the claims. It is to be understood that the terms set forth in the claims are to be interpreted in a conventional sense, and unless otherwise specified, these terms should not be limited to any particular or specially defined meaning.

10: 에어로겔
20: 압력 감지 점착제(PSA)
30: 필름
100: 단열 필름10: airgel
20: pressure sensitive adhesive (PSA)
30: Film
100: heat insulation film

Claims (11)

단열 필름에 있어서,
에어로겔이 혼합된 압력 감지 점착제(PSA), 및
상기 에어로겔이 혼합된 압력 감지 점착제(PSA)가 상부에 도포되는 필름을 포함하며,
상기 압력 감지 점착제(PSA)의 고형분(solid) 비율은 20∼40%이고, 상기 고형분(solid) 대비 에어로겔의 비율은 30~50%이며, 에어로겔의 지름은 1∼10㎛인 단열 필름.In the thermal insulation film,
Air-sensitive pressure sensitive adhesive (PSA), and
It includes a film is applied on the pressure-sensitive adhesive (PSA) mixed with the airgel,
The ratio of solids (solid) of the pressure-sensitive adhesive (PSA) is 20 to 40%, the ratio of the airgel to the solid (solid) is 30 to 50%, the diameter of the airgel is 1 to 10㎛. 삭제delete 삭제delete 제1항에 있어서,
상기 에어로겔을 상기 압력 감지 점착제(PSA)에 혼합할 때 교반기의 rpm은 1,000이며 교반 시간은 10분인 것을 특징으로 하는 단열 필름.The method of claim 1,
When the airgel is mixed with the pressure sensitive adhesive (PSA), the rpm of the stirrer is 1,000, and the stirring time is 10 minutes, characterized in that the stirring time. 제1항에 있어서,
상기 압력 감지 점착제(PSA)에는 솔벤트를 이용하여 점도가 조절되는 것을 특징으로 하는 단열 필름.The method of claim 1,
The pressure-sensitive adhesive (PSA) heat insulating film, characterized in that the viscosity is controlled by using a solvent. 제1항에 있어서,
상기 에어로겔이 혼합된 압력 감지 점착제(PSA)는 코팅기를 이용하여 일정 두께로 필름상에 도포되는 것을 특징으로 하는 단열 필름. The method of claim 1,
Pressure-sensitive adhesive (PSA) is a mixture of the airgel is a heat insulating film, characterized in that the coating on the film to a predetermined thickness using a coating machine. 단열 필름 제조 방법에 있어서,
압력 감지 점착제의 고형분 비율을 20∼40%로 조절하는 단계;
상기 고형분 대비 1∼10㎛의 지름을 갖는 에어로겔의 비율을 30∼50%로 조절하는 단계;
상기 압력 감지 점착제에 상기 에어로겔을 교반하여 혼합하는 단계;
상기 에어로겔이 혼합된 압력 감지 점착제를 필름에 도포하는 단계를 포함하는 단열 필름 제조 방법.In the heat insulation film manufacturing method,
Adjusting the solid content ratio of the pressure sensitive adhesive to 20 to 40%;
Adjusting the ratio of the airgel having a diameter of 1 to 10 μm to the solids to 30 to 50%;
Stirring and mixing the airgel with the pressure sensitive adhesive;
Method of manufacturing a heat insulation film comprising the step of applying a pressure-sensitive adhesive mixed with the airgel on the film. 삭제delete 삭제delete 제7항에 있어서,
상기 압력 감지 점착제의 점도는 솔벤트를 이용하여 조절하는 것을 특징으로하는 단열 필름 제조 방법.The method of claim 7, wherein
The viscosity of the pressure-sensitive adhesive is a heat insulating film manufacturing method, characterized in that by using a solvent to adjust. 제7항에 있어서,
상기 에어로겔과 상기 압력 감지 점착제의 혼합은, 교반기를 이용하여 1000rpm으로 10분동안 교반하여 이루어지는 것을 특징으로 하는 단열 필름 제조 방법.The method of claim 7, wherein
Mixing of the airgel and the pressure-sensitive adhesive, a method for producing a heat insulating film, characterized in that the stirring for 10 minutes at 1000rpm using a stirrer.
KR1020110143543A 2011-12-27 2011-12-27 Insulation film using psa mixed with aerogel and method for manufacturing the same KR101351479B1 (en)