KR101347304B1 - Diffusion sheet having excellent light shielding property - Google Patents
Diffusion sheet having excellent light shielding property Download PDFInfo
- Publication number
- KR101347304B1 KR101347304B1 KR1020130037370A KR20130037370A KR101347304B1 KR 101347304 B1 KR101347304 B1 KR 101347304B1 KR 1020130037370 A KR1020130037370 A KR 1020130037370A KR 20130037370 A KR20130037370 A KR 20130037370A KR 101347304 B1 KR101347304 B1 KR 101347304B1
- Authority
- KR
- South Korea
- Prior art keywords
- diffusion sheet
- light
- titanium oxide
- diffusion
- amorphous titanium
- Prior art date
Abstract
본 발명은, 비정형(非定型) 산화티타늄 입자와 플라스틱 수지를 포함하는 확산층을 포함하는 확산시트로서, 상기 확산층이 상기 플라스틱 수지 100 중량부에 대해 상기 비정형 산화티타늄 입자를 5 내지 25 중량부 포함하는 확산시트에 관한 것으로, 본 발명에 따른 확산시트는 빛을 다양한 각도 및 방향으로 굴절 및 산란시켜 세분화하고, 불규칙적인 난반사를 유도하며, 또한 일부 시트로 입광된 빛을 흡수하여 빛에 대한 확산 및 분산작용을 더욱 크게 발휘 및 증진시킬 수 있으므로, 액정표시장치의 백라이트 유닛의 확산시트로 유용하게 사용될 수 있다. The present invention provides a diffusion sheet including a diffusion layer containing amorphous titanium oxide particles and a plastic resin, wherein the diffusion layer contains 5 to 25 parts by weight of the amorphous titanium oxide particles with respect to 100 parts by weight of the plastic resin. Diffusing sheet according to the present invention, the diffusing sheet according to the present invention refracts and scatters the light at various angles and directions to subdivide, induce irregular diffuse reflection, and also absorbs the light incident on some sheets to diffuse and disperse light Since the action can be further exhibited and enhanced, it can be usefully used as a diffusion sheet of the backlight unit of the liquid crystal display device.
Description
본 발명은 광 차폐성이 우수한 확산시트에 관한 것으로서, 특히 빛을 다양한 각도 및 방향으로 굴절 및 산란시켜 세분화하고, 불규칙적인 난반사를 유도하며, 또한 시트로 입광된 빛을 일부 흡수하여 빛에 대한 확산 및 분산작용을 더욱 크게 발휘 및 증진시킬 수 있는 확산시트에 대한 것이다. The present invention relates to a diffusion sheet having excellent light shielding properties, in particular, refracting and scattering light at various angles and directions to subdivide, induce irregular diffuse reflection, and also partially absorb light incident on the sheet to diffuse and diffuse light. The present invention relates to a diffusion sheet capable of exhibiting and enhancing a dispersing effect even more.
본 발명은 액정표시장치(liquid crystal display, LCD)의 백라이트 유닛(back light unit, BLU)의 부품 중 하나인 확산시트에 관한 것으로, 보다 상세하게는 빛에 대한 확산, 굴절, 분산효과를 크게 높여 광 차폐 기능을 발휘할 수 있도록 한, 차폐 기능이 우수한 확산시트에 관한 것이다. BACKGROUND OF THE
일반적으로, 평판 디스플레이(flat display)는 크게 발광형과 수광형으로 분류한다. 수광형 평판 디스플레이의 예로서 액정표시장치를 들 수 있는데, 이러한 액정표시장치는 그 자체가 발광하여 액정 화상을 형성하지 못하고, 외부로부터 빛이 입사되어야 액정 화상을 형성할 수 있다. In general, flat displays are classified into light emitting and light receiving types. An example of a light-receiving flat panel display is a liquid crystal display device. The liquid crystal display device itself does not emit light to form a liquid crystal image, and light may be incident from outside to form a liquid crystal image.
따라서, 자체적으로 빛을 내지 못하는 액정표시장치는 백라이트 유닛이 액정표시장치(LCD)의 뒷면에서 디스플레이 영상이 눈에 보일 수 있도록 고르게 빛을 비춰주는 역할을 하게 된다. 백라이트 유닛은 광원으로서 대부분 LED(light emitting diode)를 포함하고 있으며, 또한 광원으로부터 발산되는 빛을 액정 화면 전체 영역에 걸쳐 균일하게 분산시켜주기 위한 도광판(light guide plate)을 포함한다. 또한, 도광판을 통과한 백라이트 광원의 빛을 여러 방향으로 고르게 굴절, 분산, 난반사시키기 위하여 확산시트를 포함하며, 확산시트는 도광판 패턴의 비춰짐 현상을 개선시켜 액정 화면 전체가 균일한 밝기를 유지하도록 하는 역할을 담당하게 된다. Therefore, the liquid crystal display which does not emit light by itself serves to evenly illuminate the backlight unit so that the display image is visible from the back of the LCD. The backlight unit mostly includes a light emitting diode (LED) as a light source, and also includes a light guide plate for uniformly dispersing light emitted from the light source over the entire area of the liquid crystal display. In addition, the diffusion sheet includes a diffuser sheet for evenly refracting, dispersing, and diffusely reflecting the light of the backlight light source passing through the light guide plate in various directions. It will play a role.
도 1을 참조하면, 백라이트 유닛(1)은 도광판(10)의 상면에 확산시트(20), 집광시트(30) 및 보호시트(40)가 적층되어 있고, 도광판(10)의 하면에 반사시트(50)가 적층된 형태로 이루어져 있다.Referring to FIG. 1, in the
그런데, 종래기술에 의한 확산시트는 백라이트 광원의 빛을 단순히 확산 및 분산시킬 뿐이므로, 빛을 여러 방향으로 난반사시키는 기능이 떨어져 도광판 패턴이 비춰지는 문제점이 있었다. 또한, 최근에는 박막형 디스플레이를 구현하기 위해 박막형태의 광학필름이 사용되고 있으며, 보다 적은 양의 광학필름이 사용됨에 따라 도광판에 형성되어 있는 패턴들이 액정 화상에 비춰지는 현상들이 나타나고 있다. However, since the diffusion sheet according to the related art merely diffuses and diffuses the light of the backlight light source, there is a problem in that the light guide plate pattern is reflected due to the poor function of diffusely reflecting the light in various directions. In addition, recently, a thin film type optical film has been used to realize a thin film type display, and as a smaller amount of optical film is used, a phenomenon in which patterns formed on the light guide plate are reflected on a liquid crystal image has been shown.
따라서, 빛을 다양한 각도 및 방향으로 굴절 및 산란시켜 세분화하고, 불규칙적인 난반사를 유도하며, 또한 일부 시트로 입광된 빛을 흡수하여 빛에 대한 확산 및 분산작용을 더욱 크게 발휘 및 증진시켜 우수한 광 차폐 기능을 발휘할 수 있는 확산시트의 개발이 요구되는 실정이다. Therefore, the light is refracted and scattered at various angles and directions to subdivide, induce irregular diffuse reflections, and also absorb and absorb light incident on some sheets, thereby exhibiting and enhancing diffusion and dispersion of light, thereby providing excellent light shielding. The development of a diffusion sheet capable of exhibiting a function is required.
따라서, 본 발명의 목적은 빛을 다양한 각도 및 방향으로 확산, 굴절 및 산란시켜 세분화하고, 불규칙적인 난반사를 유도하며, 또한 일부 시트로 입광된 빛을 흡수하여 빛에 대한 확산 및 분산작용을 더욱 크게 발휘 및 증진시킬 수 있는 확산시트를 제공하는 것이다. Accordingly, an object of the present invention is to diffuse, refract, and scatter light at various angles and directions to subdivide it, to induce irregular diffuse reflection, and to absorb light incident on some sheets to further increase diffusion and dispersion of light. It is to provide a diffusion sheet that can be exhibited and promoted.
상기 목적을 달성하기 위하여 본 발명은 비정형(非定型) 산화티타늄 입자와 플라스틱 수지를 포함하는 확산층을 포함하는 확산시트로서, 상기 확산층이 상기 플라스틱 수지 100 중량부에 대해 상기 비정형 산화티타늄 입자를 5 내지 25 중량부 포함하는 확산시트를 제공한다. In order to achieve the above object, the present invention provides a diffusion sheet comprising a diffusion layer containing amorphous titanium oxide particles and a plastic resin, the diffusion layer is 5 to 5 parts by weight of the amorphous titanium oxide particles to 100 parts by weight of the plastic resin It provides a diffusion sheet comprising 25 parts by weight.
본 발명의 확산시트는 빛을 다양한 각도 및 방향으로 굴절 및 산란시켜 세분화하고, 불규칙적인 난반사를 유도하며, 또한 일부 시트로 입광된 빛을 흡수하여 빛에 대한 확산 및 분산작용을 더욱 크게 발휘 및 증진시킬 수 있으므로, 액정표시장치의 백라이트 유닛의 확산시트로 유용하게 사용될 수 있다. Diffusion sheet of the present invention is to refraction and scatter the light at various angles and directions to subdivide, induce irregular diffuse reflection, and also absorb and absorb the light incident on some sheets to further exhibit and enhance the diffusion and dispersion of light It can be used as a diffusion sheet of the backlight unit of the liquid crystal display device.
도 1은 통상적인 백라이트 유닛을 구성하는 구성 물품들의 단면을 모식적으로 나타낸 도면이다.
도 2는 본 발명의 일례에 따른 확산시트의 모식적인 단면도이다.
도 3은 본 발명의 일례에 따른 확산시트에서 입사광이 굴절 및 산란되는 형태를 나타낸 도면이다. 1 is a diagram schematically showing a cross section of constituent articles constituting a conventional backlight unit.
2 is a schematic cross-sectional view of a diffusion sheet according to an example of the present invention.
3 is a view illustrating a form in which incident light is refracted and scattered in a diffusion sheet according to an example of the present invention.
이하 본 발명을 더욱 상세히 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명의 확산시트는 비정형(非定型) 산화티타늄 입자와 플라스틱 수지를 포함하는 확산층을 포함한다. The diffusion sheet of the present invention includes a diffusion layer containing amorphous titanium oxide particles and a plastic resin.
상기 비정형 산화티타늄 입자는 확산시트에 포함되는 확산층 내에 포함되어, 확산시트에 입사되는 빛을 다양한 각도 및 방향으로 확산, 굴절 및 산란시켜 세분화하고, 불규칙적인 난반사를 유도하게 하는 효과를 발휘할 수 있으며, 시트에 광택성을 부여할 수 있다. The amorphous titanium oxide particles may be included in the diffusion layer included in the diffusion sheet, thereby diffusing, refracting, and scattering the light incident on the diffusion sheet at various angles and directions, and may have an effect of inducing irregular diffuse reflection. Glossiness can be provided to a sheet.
상기 비정형 산화티타늄 입자는 입자의 최대 크기를 기준으로 하였을 때, 그 크기가 0.01 내지 10 ㎛, 0.05 내지 5 ㎛, 0.1 내지 1 ㎛, 0.3 내지 0.5 ㎛일 수 있다. The amorphous titanium oxide particles may have a size of 0.01 to 10 μm, 0.05 to 5 μm, 0.1 to 1 μm, and 0.3 to 0.5 μm based on the maximum size of the particles.
상기 비정형 산화티타늄 입자의 크기가 0.01 ㎛ 미만인 경우 분산성이 낮아질 수 있기 때문에 바람직하지 못하고, 입자의 크기가 10 ㎛를 초과하는 경우 원하는 굴절 및 산란 효과가 얻어지지 않고, 너무 큰 입자 크기로 인해 균일한 분산성에 문제를 나타낼 수 있어서 바람직하지 못하다.If the size of the amorphous titanium oxide particles is less than 0.01 ㎛ is not preferable because the dispersibility may be lowered, if the size of the particles exceeds 10 ㎛ the desired refractive and scattering effect is not obtained, uniform due to too large particle size This is undesirable because it may present a problem in dispersibility.
상기 비정형 산화티타늄 입자는 전체적인 형태가 특정한 형상을 지니지 않는 비정형(非定型)으로 이루어져 있으며, 산화티타늄 자체는 아나타제(anatase) 또는 루타일(rutile)의 결정형으로 이루어질 수 있고, 어느 것도 사용될 수 있지만, 바람직하게는 루타일 형일 수 있다. 상기 루타일 형은 상기 아나타제 형에 비하여 상대적으로 빛에 대한 고 흡수성(high absorbance property)을 가지므로, 자외선에 대한 흡수 능력이 좋아 자외선 차단 효과가 뛰어나고, 자외선에 대한 높은 안정성(UV 신뢰성)을 나타내므로 황변되지 않으며, 또한 굴절율(2.7:2.5) 및 유전율(114:31)이 높으므로 보다 바람직하게 사용될 수 있다. The amorphous titanium oxide particles are in an amorphous form in which the overall form does not have a specific shape, and the titanium oxide itself may be formed in an anatase or rutile crystalline form, but any may be used. Preferably it may be rutile type. Since the rutile type has a high absorbance property for light relative to the anatase type, the rutile type has a high UV absorption effect due to good absorption of ultraviolet rays and exhibits high stability against UV rays (UV reliability). Therefore, it is not yellowed, and since the refractive index (2.7: 2.5) and the dielectric constant (114: 31) are high, it can be used more preferably.
상기 비정형 산화티타늄 입자는 플라스틱 수지 100 중량부에 대하여 5 내지 25 중량부, 바람직하게는 10 내지 23 중량부, 더욱 바람직하게는 15 내지 20 중량부 포함될 수 있다. The amorphous titanium oxide particles may be included 5 to 25 parts by weight, preferably 10 to 23 parts by weight, more preferably 15 to 20 parts by weight based on 100 parts by weight of the plastic resin.
상기 플라스틱 수지는 열경화형 수지, UV 경화형 수지, 수분경화성 수지 또는 이들의 혼합물일 수 있으며, 상기 열경화성 수지, UV 경화성 수지 또는 수분경화성 수지는, 예컨대 에폭시계, 페놀계, 우레탄계, 폴리에스테르계, 아미노계 등의 열경화형 수지, 아크릴계, 비닐계 등의 UV 경화형 수지, 일액형 실리콘 등의 실리콘기를 함유한 수분경화수지일 수 있고, 이의 구체적인 예로는 (메트)아크릴레이트계 수지, 불포화 폴리에스테르 수지, 폴리에스테르 (메트)아크릴레이트 수지, 실리콘 우레탄 (메트)아크릴레이트 수지, 실리콘 폴리에스테르 (메트)아크릴레이트 수지, 불소 우레탄 (메트)아크릴레이트 수지, 페놀 수지, 에폭시 수지, 우레아 포름알데히드 수지, 멜라민 포름알데히드 수지 및 이들의 혼합물을 들 수 있다. 바람직하게는 일반적인 광 차폐성 확산시트에 사용되는 수지인, 고온, 고습, 내 UV 신뢰성 면에서 뛰어난 열경화형 수지가 사용될 수 있다. The plastic resin may be a thermosetting resin, a UV curable resin, a moisture curable resin, or a mixture thereof, and the thermosetting resin, the UV curable resin, or the water curable resin may be, for example, epoxy, phenol, urethane, polyester, or amino. It may be a thermosetting resin such as a system, UV-curable resin such as acrylic, vinyl-based, moisture-curable resin containing a silicone group, such as one-component silicone, specific examples thereof include (meth) acrylate-based resin, unsaturated polyester resin, Polyester (meth) acrylate resin, silicone urethane (meth) acrylate resin, silicone polyester (meth) acrylate resin, fluorine urethane (meth) acrylate resin, phenol resin, epoxy resin, urea formaldehyde resin, melamine form Aldehyde resins and mixtures thereof. Preferably, a thermosetting resin having excellent high temperature, high humidity, and UV resistance in terms of resin used in a general light shielding diffusion sheet may be used.
또한, 본 발명의 확산시트는 필요에 따라 확산 기능을 위하여 상기 비정형(非定型) 산화티타늄 입자 외에 필러를 포함할 수 있다. In addition, the diffusion sheet of the present invention may include a filler in addition to the amorphous titanium oxide particles for the diffusion function if necessary.
상기 필러는 경질 아크릴레이트, 폴리스티렌, 나일론, 연질 아크릴레이트 및 실리콘 중에서 선택된 재질을 포함하는 유기 고분자 필러일 수 있으며, 이들 중 내용제성이 좋고 분산이 용이한 경질 아크릴레이트가 바람직하다. 상기 필러는 구형이 바람직하며, 0.5 내지 5 ㎛, 바람직하게는 0.8 내지 3 ㎛의 평균 입경을 가질 수 있다. 상기 필러는 그 굴절율이 상기 플라스틱 수지의 굴절율과의 차이가 0.02 이상인 것이 바람직하다. The filler may be an organic polymer filler including a material selected from hard acrylate, polystyrene, nylon, soft acrylate and silicone, and among these, hard acrylate having good solvent resistance and easy dispersion is preferable. The filler is preferably spherical, and may have an average particle diameter of 0.5 to 5 μm, preferably 0.8 to 3 μm. The filler preferably has a refractive index of 0.02 or more that is different from the refractive index of the plastic resin.
상기 필러는 확산층을 이루는 플라스틱 수지 100 중량부에 대하여 40 내지 80 중량부, 바람직하게는 50 내지 60 중량부의 양으로 사용될 수 있다.The filler may be used in an amount of 40 to 80 parts by weight, preferably 50 to 60 parts by weight based on 100 parts by weight of the plastic resin forming the diffusion layer.
본 발명의 확산시트는 사출, 압출, 웨트 코팅, 캐스팅 등의 통상적인 시트 또는 필름의 제조방법에 의해 제조될 수 있으며, 또한 도광판의 상면에 코팅함으로써 시트 형태인 코팅층을 이루도록 제조될 수 있다. The diffusion sheet of the present invention may be prepared by a conventional sheet or film manufacturing method such as injection, extrusion, wet coating, casting, etc., and may also be prepared to form a coating layer in the form of a sheet by coating on the upper surface of the light guide plate.
본 발명의 확산시트는 그 두께가 38 내지 270 ㎛, 100 내지 270 ㎛, 150 내지 270 ㎛일 수 있다. Diffusion sheet of the present invention may have a thickness of 38 to 270 ㎛, 100 to 270 ㎛, 150 to 270 ㎛.
상기 플라스틱 수지는, 필요에 따라, 추가의 열경화제, UV 경화제, 경화촉진제, 커플링제, 광산발생제, 산화방지제, 계면활성제, 라디칼 개시제 및 이들의 혼합물을 포함할 수 있으며, 이들을 용매와 혼합시켜 얻어지는 플라스틱 조성물의 형태로 본 발명의 확산시트를 제조에 사용될 수 있다. 예컨대, 상기 플라스틱 수지가 열경화형 수지인 경우, 상기 조성물은, 열경화형 수지, 열경화제, 경화촉진제, 커플링제, 산화방지제 및 용매를 포함할 수 있다. The plastic resin may include additional thermosetting agents, UV curing agents, curing accelerators, coupling agents, photoacid generators, antioxidants, surfactants, radical initiators, and mixtures thereof, if necessary, by mixing them with a solvent. In the form of the resulting plastic composition, the diffusion sheet of the present invention can be used for production. For example, when the plastic resin is a thermosetting resin, the composition may include a thermosetting resin, a thermosetting agent, a curing accelerator, a coupling agent, an antioxidant, and a solvent.
상기 열경화제는 통상적으로 열경화형 수지를 열경화하기 위해서 사용할 수 있는 것이면 특별히 한정되지 않으며, 예컨대 아민계 경화제, 산무수물계 경화제, 이미다졸계 경화제, 카르복실산계 경화제, 유기산히드라지드계 경화제, 페놀계 경화제, 폴리올계 경화제, 옥사졸린계 경화제, 멜라민계 경화제 또는 이들의 혼합물 등을 들 수 있다.The thermosetting agent is not particularly limited as long as it can be generally used for thermosetting the thermosetting resin, and examples thereof include amine curing agents, acid anhydride curing agents, imidazole curing agents, carboxylic acid curing agents, organic acid hydrazide curing agents, and phenols. And a curing agent, a polyol curing agent, an oxazoline curing agent, a melamine curing agent, or a mixture thereof.
상기 경화촉진제로서는, 열경화형 수지와 열경화제의 반응을 촉진하는 기능을 수행할 수 있는 것이면 어떤 것도 사용 가능하고, 예컨대 이미다졸계 경화촉진제, 포스핀계 경화촉진제, 암모늄계 경화촉진제, 루이스산계 경화촉진제 또는 이들의 혼합물 등을 들 수 있다.As the curing accelerator, any one can be used as long as it can perform a function of promoting the reaction between the thermosetting resin and the thermosetting agent. For example, an imidazole curing accelerator, a phosphine curing accelerator, an ammonium curing accelerator, a Lewis acid curing accelerator. Or mixtures thereof.
상기 커플링제로서는 실란 커플링제, 티타네이트계 커플링제, 알루미네이트계 커플링제, 실리콘 화합물 등을 들 수 있으며, 이들 커플링제는 단독으로 또는 혼합하여 사용할 수 있다.As said coupling agent, a silane coupling agent, a titanate coupling agent, an aluminate coupling agent, a silicone compound, etc. are mentioned, These coupling agents can be used individually or in mixture.
상기 산화방지제로서는 페놀계, 유황계 또는 인계 산화방지제를 들 수 있고, 상기 산화방지제는 열경화성 수지 조성물의 열경화시의 산화 열화를 방지함으로써 경화물의 내열 안정성을 향상시키기 위하여 사용될 수 있다. Examples of the antioxidant include phenol-based, sulfur-based or phosphorus-based antioxidants, and the antioxidants may be used to improve the heat resistance stability of the cured product by preventing oxidative degradation during thermosetting of the thermosetting resin composition.
상기 용매로는 전술한 플라스틱 수지 조성물 성분들과 상용성을 가지되 이들과 반응하지 않는 것으로서, 수지 조성물에 사용되는 공지의 용매이면 어느 것이나 사용 가능하다. 이러한 용매의 예로는 메틸에틸케톤, 메틸이소부틸케톤, 톨루엔, 자일렌, 부틸아세테이트 또는 사이클로헥사논 등을 들 수 있다. 상기 용매는 단독 또는 2종 이상을 배합하여 사용할 수 있다.
The solvent may be compatible with the above-described plastic resin composition components, but does not react with any of them, as long as it is a known solvent used in the resin composition. Examples of such a solvent include methyl ethyl ketone, methyl isobutyl ketone, toluene, xylene, butyl acetate or cyclohexanone. The said solvent can be used individually or in mixture of 2 or more types.
이하, 본 발명의 확산시트를 도면을 참조하여 더욱 상세히 설명하지만, 해당 도면은 본 발명을 예시하기 위한 것일 뿐 본 발명의 범주가 그것에 의해 한정되는 것은 아니다.
Hereinafter, the diffusion sheet of the present invention will be described in more detail with reference to the drawings, but the drawings are intended to illustrate the present invention, but the scope of the present invention is not limited thereto.
도 2에는 본 발명의 일 실시예에 따른 확산시트의 단면이 모식적으로 도시되어 있다. 2 is a cross-sectional view schematically showing a diffusion sheet according to an embodiment of the present invention.
도 2를 참조하면, 본 발명의 일 실시예에 따른 확산시트(100)는, 비정형 산화티타늄(110)과 확산시트(100)의 전체 형태를 이루고 있는 플라스틱 수지(120)를 포함하며, 확산시트(100) 내에 산화티타늄(110)이 입자형태로 내부에 존재하고 있다. 2, the
도 3에는 본 발명의 확산시트가 빛을 확산 및 분산시키는 원리를 보여주는 도면이 도시되어 있다. 3 is a view showing a principle that the diffusion sheet of the present invention diffuses and diffuses light.
도 3을 참조하면, 도광판을 통과하여 본 발명의 확산시트(100) 내로 입사된 빛은 비정형 산화티타늄(110) 입자에 부딪혀 다양한 방향으로 굴절 및 산란되며, 특히 비정형 산화티타늄(110)은 표면의 형상이 제각기 다르므로 더욱 효과적으로 빛을 확산 및 분산시킬 수 있다.Referring to FIG. 3, light incident through the light guide plate into the
따라서, 본 발명의 확산시트는 빛을 다양한 각도 및 방향으로 확산, 굴절 및 산란시켜 세분화하고, 불규칙적인 난반사를 유도하며, 또한 일부 시트로 입광된 빛을 흡수하여 빛에 대한 확산 및 분산작용을 더욱 크게 발휘 및 증진시킬 수 있다.Therefore, the diffusion sheet of the present invention diffuses, refracts, and scatters light at various angles and directions, thereby subdividing it, inducing irregular diffuse reflection, and also absorbing light incident on some sheets to further diffuse and disperse light. Can be greatly exerted and promoted.
또한, 본 발명의 확산시트는 우수한 차폐성능을 가져, 도광판에 형성되어 있는 패턴들이 액정 화상에 비춰지는 현상을 억제하여, 액정 표시 장치의 화면 시인성 또한 향상시키는 효과를 발휘할 수 있다.
In addition, the diffusion sheet of the present invention has an excellent shielding performance, it is possible to suppress the phenomenon that the patterns formed on the light guide plate is reflected on the liquid crystal image, it can exhibit the effect of improving the screen visibility of the liquid crystal display device.
이하, 본 발명을 실시예에 의해 상세히 설명한다. 단, 하기 실시예는 본 발명을 예시하는 것일 뿐, 본 발명의 내용이 하기 실시예에 의해 한정되는 것은 아니다.
Hereinafter, the present invention will be described in detail by way of examples. However, the following examples are illustrative of the present invention, and the contents of the present invention are not limited by the following examples.
실시예 1Example 1
메타크릴에스터를 주성분으로 하는 비닐계 공중합체 수지(애경화학㈜, 아크릴 공중합체 A-811) 100 중량부에 입자의 최소입경이 0.01 ㎛이고, 최대입경이 10 ㎛인 비정형 산화티타늄 입자(플라스틱용 Ti-pure R-104, 듀퐁사제) 15 중량부, PMMA 아크릴 유기 필러 50 중량부와 톨루엔 및 사이클로헥사논으로 이루어진 혼합 용매 300 중량부를 혼합하여 수지 조성물을 제조하였다. 제조한 수지 조성물을 기재층인 두께 188 ㎛의 투명 폴리에틸렌테레프탈레이트 필름(V7200, SKC㈜)에 웨트 코팅 방식을 이용하여 도포하여 두께 15 ㎛의 확산층을 형성한 후, 드라이어를 이용하여 90초 동안, 온도 100℃로 열 조사하여 경화함으로써 확산시트를 제조하였다.
Amorphous titanium oxide particles having a minimum particle size of 0.01 μm and a maximum particle size of 10 μm in 100 parts by weight of a vinyl copolymer resin (Aekyung Chemical Co., Ltd., acrylic copolymer A-811) mainly composed of methacrylate esters (for plastics) 15 parts by weight of Ti-pure R-104, manufactured by DuPont, 50 parts by weight of PMMA acrylic organic filler, and 300 parts by weight of a mixed solvent consisting of toluene and cyclohexanone were mixed to prepare a resin composition. The resin composition thus prepared was applied to a transparent polyethylene terephthalate film (V7200, SKC, Inc.) having a thickness of 188 μm using a wet coating method to form a diffusion layer having a thickness of 15 μm, and then dried for 90 seconds using a dryer. The diffusion sheet was manufactured by heat-irradiating and hardening at the temperature of 100 degreeC.
실시예 2Example 2
비정형 산화티타늄 입자(플라스틱용 Ti-pure R-104, 듀퐁사제)를 5 중량부 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 확산시트를 제조하였다.
A diffusion sheet was prepared in the same manner as in Example 1, except that 5 parts by weight of amorphous titanium oxide particles (Ti-pure R-104 for plastic, manufactured by DuPont) was used.
실시예 3Example 3
비정형 산화티타늄 입자(플라스틱용 Ti-pure R-104, 듀퐁사제)를 25 중량부 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 확산시트를 제조하였다.
A diffusion sheet was prepared in the same manner as in Example 1, except that 25 parts by weight of amorphous titanium oxide particles (Ti-pure R-104 for plastics, manufactured by DuPont) were used.
비교예 1Comparative Example 1
메타크릴에스터를 주성분으로 하는 비닐계 공중합체 수지(애경화학㈜, 아크릴 공중합체 A-811) 100 중량부에 PMMA 아크릴 유기 필러 80 중량부와 톨루엔 및 사이클로헥사논으로 이루어진 혼합용매 200 중량부를 혼합하여 수지 조성물을 제조하였다. 제조한 수지 조성물을 기재층인 두께 188 ㎛의 투명 폴리에틸렌테레프탈레이트 필름(V7200, SKC㈜)에 웨트 코팅 방식을 이용하여 도포하여 두께 20 ㎛의 확산층을 형성한 후, 드라이어를 이용하여 90초 동안, 온도 100℃로 열 조사하여 경화함으로써 확산시트를 제조하였다.
80 parts by weight of a PMMA acrylic organic filler and 200 parts by weight of a mixed solvent composed of toluene and cyclohexanone are mixed with 100 parts by weight of a vinyl copolymer resin (Aekyung Chemical Co., Ltd., acrylic copolymer A-811) mainly composed of methacrylate ester. A resin composition was prepared. After applying the prepared resin composition to the transparent polyethylene terephthalate film (V7200, SKC Co., Ltd.) having a thickness of 188 ㎛ using a wet coating method to form a diffusion layer having a thickness of 20 ㎛, using a dryer for 90 seconds, The diffusion sheet was manufactured by heat-irradiating and hardening at the temperature of 100 degreeC.
실험예Experimental Example
상기 실시예 1 내지 3 및 비교예 1에서 제조된 각각의 확산 시트들을 구동 중인 CCFL BLU 램프 위에 1장씩 올려 놓고 램프 마스킹(lamp masking) 비교를 하면서 차폐력을 측정하였다. 비교예 1에 따른 확산시트의 램프 마스킹 차폐력의 수준을 기준으로, 실시예 1 내지 3의 확산시트의 상대적인 차폐력의 정도를 정성적으로 나타내었으며, 구체적으로 CCFL BLU 램프의 차폐 정도가 100% 일 때를 매우 우수로, CCFL BLU 램프의 차폐 정도가 80% 일 때를 우수로, CCFL BLU 램프의 차폐 정도가 60% 일 때를 양호로, CCFL BLU 램프의 차폐 정도가 40% 일 때를 불량으로 나타내었다. 또한, 실시예 1 내지 3, 및 비교예 1에서 제조된 각각의 확산 시트들의 휘도를 ㈜에스피텍사의 코노미터(conometer)를 사용하여 측정하여, 실시예 1에 따른 확산시트의 휘도를 기준(100%)으로 하여, 실시예 2 및 3, 및 비교예 1의 확산시트의 상대적인 휘도 값으로 구하였다. 측정 결과를 표 1에 나타내었다. Each of the diffusion sheets manufactured in Examples 1 to 3 and Comparative Example 1 was placed on a driving CCFL BLU lamp one by one, and the shielding force was measured while comparing lamp masking. Based on the level of the mask masking shielding power of the diffusion sheet according to Comparative Example 1, the relative shielding power of the diffusion sheet of Examples 1 to 3 qualitatively exhibited, specifically, the shielding degree of the CCFL BLU lamp is 100% Is excellent when the CCFL BLU lamp is 80% shielded, when the CCFL BLU lamp is 60% good, and when the CCFL BLU lamp is 40% poor. As shown. In addition, the luminance of each of the diffusion sheets manufactured in Examples 1 to 3 and Comparative Example 1 was measured by using a conometer manufactured by Spitek Co., Ltd., based on the luminance of the diffusion sheet according to Example 1 (100). %), And the relative luminance values of the diffusion sheets of Examples 2 and 3 and Comparative Example 1 were obtained. The measurement results are shown in Table 1.
상기 표 1을 통하여 알 수 있듯이, 비정형 산화티타늄 입자를 플라스틱 수지 100 중량부에 대하여 15 중량부 포함하는 실시예 1의 확산시트는 차폐력이 우수함을 알 수 있었다. 반면, 비정형 산화티타늄 입자를 포함하지 않은 비교예 1의 확산시트는 실시예 1의 확산시트에 비해 휘도는 향상되었지만 차폐력이 불량함을 알 수 있었다. As can be seen from Table 1, the diffusion sheet of Example 1 containing 15 parts by weight of amorphous titanium oxide particles with respect to 100 parts by weight of the plastic resin was found to have excellent shielding force. On the other hand, the diffusion sheet of Comparative Example 1, which does not contain amorphous titanium oxide particles, it was found that the brightness is improved compared to the diffusion sheet of Example 1, but the shielding power is poor.
한편, 실시예 1의 확산시트에 비하여 비정형 산화티타늄 입자를 상대적으로 소량 포함하는 실시예 2는 휘도의 증가와 함께 차폐력이 감소함을 알 수 있었고, 비정형 산화티타늄 입자를 상대적으로 다량 포함하는 실시예 3은 휘도의 감소와 함께 차폐력이 증가함을 알 수 있었다. 이와 같이, 상기 비정형 산화티타늄 입자를 플라스틱 수지 100 중량부에 대하여 5 내지 25 중량부 범위로 포함하면, 확산시트의 차폐력을 양호하게 하면서도 휘도를 우수하게 유지할 수 있으므로, 상기 범위 내에서 비정형 산화티타늄 입자의 함량을 조절하여, 원하는 조건에 따라 적절히 확산시트의 휘도와 차폐력을 조절할 수 있음을 확인할 수 있었다. On the other hand, Example 2 containing a relatively small amount of amorphous titanium oxide particles compared to the diffusion sheet of Example 1 was found that the shielding power decreases with the increase in brightness, the implementation containing a relatively large amount of amorphous titanium oxide particles In Example 3, it was found that shielding force increased with decreasing luminance. As such, when the amorphous titanium oxide particles are included in the range of 5 to 25 parts by weight with respect to 100 parts by weight of the plastic resin, the shielding strength of the diffusion sheet can be maintained while maintaining excellent brightness, and thus, the amorphous titanium oxide is in the above range. By adjusting the content of the particles, it was confirmed that the brightness and shielding power of the diffusion sheet can be properly adjusted according to the desired conditions.
1: 백라이트 유닛 10: 도광판
20: 확산시트 30: 집광시트
40: 보호시트 50: 반사시트
100: 확산시트 110: 비정형 산화티타늄
120: 플라스틱 수지1: backlight unit 10: light guide plate
20: diffusion sheet 30: light collecting sheet
40: protective sheet 50: reflective sheet
100: diffusion sheet 110: amorphous titanium oxide
120: plastic resin
Claims (6)
상기 확산층이 상기 메타크릴에스터를 포함하는 비닐계 수지 100 중량부에 대해 상기 비정형 산화티타늄 입자를 5 내지 25 중량부 포함하는 확산시트.
A diffusion sheet comprising a diffusion layer comprising an amorphous titanium oxide particle and a vinyl resin containing methacrylate ester,
The diffusion sheet includes 5 to 25 parts by weight of the amorphous titanium oxide particles with respect to 100 parts by weight of the vinyl resin containing the methacryl ester.
상기 비정형 산화티타늄 입자의 크기가 0.01 내지 10 ㎛인 확산시트.
The method of claim 1,
A diffusion sheet having a size of the amorphous titanium oxide particles of 0.01 to 10 ㎛.
상기 비정형 산화티타늄 입자가 루타일 형인 확산시트.
The method of claim 1,
A diffusion sheet of the amorphous titanium oxide particles is rutile type.
상기 확산시트의 두께가 38 내지 270 ㎛인 확산시트.
The method of claim 1,
Diffusion sheet of 38 to 270 ㎛ thickness of the diffusion sheet.