KR101219922B1 - Inorganic waterproof coating material for parking place's floor - Google Patents
Inorganic waterproof coating material for parking place's floor Download PDFInfo
- Publication number
- KR101219922B1 KR101219922B1 KR1020110037280A KR20110037280A KR101219922B1 KR 101219922 B1 KR101219922 B1 KR 101219922B1 KR 1020110037280 A KR1020110037280 A KR 1020110037280A KR 20110037280 A KR20110037280 A KR 20110037280A KR 101219922 B1 KR101219922 B1 KR 101219922B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- cement
- weight percent
- floor
- parking lot
- Prior art date
Abstract
본 발명은 콘크리트로 되어 있는 주차장의 노면에 도포되어 물이 침투되는 것을 막는 방수기능은 물론 높은 접착력으로 인해 들뜸현상을 방지할 수 있는 주차장 바닥용 무기질계 도막방수제에 관한 것으로써,
아크릴 에멀젼 22 내지 30 중량%;
알루미나시멘트 15 내지 21 중량%;
마이크로시멘트 6 내지 11 중량%;
백시멘트 6 내지 11 중량%;
흙시멘트 6 내지 11 중량%;
생석회 1 내지 4 중량%;
규사 25 내지 33 중량%;
유동화제 0.1 내지 0.4 중량%;
소포제 0.1 내지 0.4 중량%;; 및
팽창제 0.1 내지 0.4 중량%; 로 이루어지는 것을 특징으로 한다.The present invention relates to an inorganic coating film waterproofing agent for a parking lot floor which can be prevented from being lifted due to a high adhesive force, as well as a waterproof function that prevents water from penetrating the road surface of the parking lot made of concrete,
Acrylic emulsion 22-30% by weight;
15 to 21 weight percent of alumina cement;
6 to 11 weight percent microcement;
6-11% by weight of cement;
Soil cement 6-11 wt%;
Quicklime 1-4 weight percent;
25 to 33 weight percent of silica sand;
0.1 to 0.4% by weight of a glidant;
Antifoaming agent 0.1-0.4 wt%; And
0.1 to 0.4% by weight of expanding agent; .
Description
본 발명은 주차장 바닥용 무기질계 도막방수제에 관한 것으로써, 더욱 상세하게는 통상 콘크리트로 되어 있는 주차장의 노면에 도포되어 물이 침투되는 것을 막는 방수기능은 물론 높은 접착력으로 인해 들뜸현상을 방지할 수 있는 주차장 바닥용 무기질계 도막방수제에 관한 것이다.
The present invention relates to an inorganic coating film waterproofing agent for a parking lot floor, and more particularly, it is applied to a road surface of a parking lot, which is usually made of concrete, to prevent water from penetrating, as well as to prevent lifting due to high adhesion. The present invention relates to an inorganic coating waterproofing agent for floors in parking lots.
현재 주택, 아파트, 병원, 학교 등의 각종 건물 지하 주차장 바닥은 에폭시 또는 우레탄계열의 페인트를 시공하거나 일반 유성페인트를 도포하여 방수층을 형성하도록 시공하고 있다.Currently, the basement floors of various underground parking lots of houses, apartments, hospitals, schools, etc. are constructed with epoxy or urethane-based paints or general oil paint to form a waterproof layer.
이러한 방수층의 도포방법은 복잡하여 일반인이 쉽게 작업할 수가 없고 시공설치 후 양생기간이 장기간 소요되어 공사기간이 길어지고 이에 따른 원자재 및 도포비용이 높아 건축비용이 상당히 소모되고 있다. 또한, 도포 작업시 유해가스가 발생되어 작업자의 작업환경을 저해하고 설치 후 일정양의 가스는 계속 발생되어 주차장 사용자의 불쾌감을 증가시키고 건강까지 침해하고 있다.The coating method of the waterproof layer is complicated, so that the general public can not easily work, and the construction period is long due to the long curing period after the installation and installation, and the cost of the raw materials and the coating is high, resulting in considerable construction cost. In addition, harmful gas is generated during the coating operation to hinder the worker's working environment, and a certain amount of gas continues to be generated after installation, thereby increasing the discomfort of the parking lot user and invading health.
또한, 종래기술의 방수층 형성 방법은 시간이 경과함에 따라 콘크리트와 방수층 사이의 접착력이 약화되어 들뜸현상이 발생되는 문제점이 있다.In addition, the waterproof layer forming method of the prior art has a problem that the lifting force is generated by weakening the adhesive force between the concrete and the waterproof layer over time.
이와 같이 각종 건물의 지하 주차장 바닥은 에폭시 또는 우레탄계열의 페인트를 시공하거나 일반 유성페인트를 도포하는 방식이외 별도 조성물의 도포하는 방법이 사용되지 않고 있어 이에 상기와 같은 바닥 표면의 구조적인 변화와 더불어 도료가 아닌 별도의 조성물을 바닥에 도포하는 방법이 제안될 필요성이 있다.As such, underground parking lot floors of various buildings do not use epoxy or urethane-based paints or apply general oil paint except for the application of a separate composition. There is a need to propose a method of applying a separate composition to the floor.
본 출원인은 유기질계 도막방수제들의 문제점을 해소하기 위하여 "시멘트 혼입 폴리머계 도막방수제 및 그 제조방법"을 출원하여 등록번호 10-0956955호로 특허등록받은 바 있다.In order to solve the problems of organic coating waterproofing agents, the present applicant has filed a patent registration number 10-0956955 by applying "cement-containing polymer coating waterproofing agent and its manufacturing method".
이에 본 출원인은 상기와 같은 종래 기술의 문제점들을 해소할 수 있도록 더욱 기술을 발전시켜, 시멘트의 혼입으로 콘크리트 노면과의 사이에 접착력을 향상시키고, 방수 작업의 편리성을 향상시킨 주차장 바닥용 무기질계 도막방수제를 개발하기에 이르렀다.
In this regard, the present applicant has further developed the technology to solve the problems of the prior art as described above, and improves the adhesive strength between the concrete road surface by the mixing of cement, and the inorganic system for the parking lot floor which improves the convenience of waterproofing work. It has led to the development of a film waterproofing agent.
본 발명은 종래의 문제점을 해결하기 위하여 제안된 것으로, 그 목적은 아크릴 에멀젼과 시멘트 및 기타 재료를 혼합하여 구조물에 도포함으로써 구조물에 물이 침투되는 것을 막는 방수기능은 물론 우수한 내화학성, 내후성, 내균열성, 내충격성 및 친수성과 높은 인장력을 갖는 주차장 바닥용 무기질계 도막방수제를 제공하는데 있다.The present invention has been proposed to solve the conventional problems, the purpose of which is to mix the acrylic emulsion, cement and other materials and apply to the structure to prevent water penetration into the structure as well as excellent chemical resistance, weather resistance, weather resistance The present invention provides an inorganic coating waterproofing agent for a parking lot floor having crack resistance, impact resistance, hydrophilicity and high tensile strength.
또한, 본 발명의 또 다른 목적은, 시멘트를 혼입하되 인장강도 및 신장율을 크게 개선하여 콘크리트 구조물의 시공 면에서 분리되거나 이탈되지 아니하는 우수한 성능을 갖는 주차장 바닥용 무기질계 도막방수제를 제공하는데 있다.In addition, another object of the present invention is to provide an inorganic coating waterproofing agent for a parking lot floor having excellent performance of mixing cement but greatly improving the tensile strength and elongation rate not separated or separated from the construction surface of the concrete structure.
또한, 본 발명의 또 다른 목적은, 시멘트 계열의 무기질 분말을 사용하기 때문에 콘크리트와 함께 수축 및 팽창이 이루어지고, 콘크리트의 수분을 외부로 용이하게 배출함으로써 콘크리트의 부식을 방지할 수 있어서 방수층의 수명을 연장시킬 수 있도록 하며, 독성을 갖는 유해가스의 배출이 없어 도포작업시 작업의 편의성을 향상시킬 수 있는 주차장 바닥용 무기질계 도막방수제를 제공하는데 있다.In addition, another object of the present invention, because the use of cement-based inorganic powder shrinkage and expansion with the concrete, it is possible to easily prevent the corrosion of the concrete by discharging the moisture of the concrete to the outside life of the waterproof layer It is to provide an inorganic coating waterproofing agent for the floor of the parking lot that can be extended, and improve the convenience of the operation during the coating work because there is no emission of toxic harmful gas.
그러나 본 발명의 목적은 상기에 언급된 목적으로 제한되지 않으며, 언급되지 않은 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
However, the object of the present invention is not limited to the above-mentioned objects, and other objects not mentioned can be clearly understood by those skilled in the art from the following description.
상기와 같은 목적을 달성하기 위한 본 발명의 특징에 따르면, According to a feature of the present invention for achieving the above object,
아크릴 에멀젼 22 내지 30 중량%;Acrylic emulsion 22-30% by weight;
알루미나시멘트 15 내지 21 중량%;15 to 21 weight percent of alumina cement;
마이크로시멘트 6 내지 11 중량%;6 to 11 weight percent microcement;
백시멘트 6 내지 11 중량%;6-11% by weight of cement;
흙시멘트 6 내지 11 중량%;Soil cement 6-11 wt%;
생석회 1 내지 4 중량%;Quicklime 1-4 weight percent;
규사 25 내지 33 중량%;25 to 33 weight percent of silica sand;
유동화제 0.1 내지 0.4 중량%;0.1 to 0.4% by weight of a glidant;
소포제 0.1 내지 0.4 중량%;; 및Antifoaming agent 0.1-0.4 wt%; And
팽창제 0.1 내지 0.4 중량%; 로 이루어지는 것을 특징으로 하는 주차장 바닥용 무기질계 도막방수제를 제공한다.0.1 to 0.4% by weight of expanding agent; It provides an inorganic coating film waterproofing agent for the floor of the parking lot, characterized in that consisting of.
이때, 본 발명의 부가적인 특징에 따르면, 상기 아크릴 에멀젼 26.10 중량%; 상기 알루미나시멘트 18.30 중량%; 상기 마이크로시멘트 7.83 중량%; 상기 백시멘트 7.83 중량%; 상기 흙시멘트 7.83 중량%; 상기 생석회 2.61 중량%; 상기 규사 28.72 중량%; 상기 유동화제 0.26 중량%; 상기 소포제 0.26 중량%;; 및 상기 팽창제 0.26 중량%; 로 이루어지는 것이 바람직하다.
At this time, according to an additional feature of the invention, the acrylic emulsion 26.10% by weight; 18.30% by weight of the alumina cement; 7.83 wt% of the microcement; 7.83 wt% of the back cement; 7.83 wt% of the soil cement; 2.61 wt% of the quicklime; 28.72% by weight of silica sand; 0.26% by weight of the glidant; 0.26% by weight of the antifoam; And 0.26% by weight of the expanding agent; It is preferable that it consists of.
상기와 같이 이루어진 본 발명의 주차장 바닥용 무기질계 도막방수제를 적용하면, 독성을 갖는 유해가스의 배출이 없어 도포작업시 작업의 편의성을 향상시킬 수 있는 효과가 있다.Applying the inorganic coating film waterproofing agent for the floor of the parking lot of the present invention made as described above, there is no emission of toxic harmful gases there is an effect that can improve the convenience of the operation during the coating operation.
또한, 아크릴 에멀젼과 시멘트 및 기타 재료를 혼합하여 구조물에 도포함으로써 방수기능은 물론 우수한 내화학성, 내후성, 내균열성, 내충격성 및 친수성과 높은 인장력을 갖는 효과가 있다.In addition, by mixing the acrylic emulsion and cement and other materials to the structure there is an effect of having excellent waterproof resistance, excellent chemical resistance, weather resistance, crack resistance, impact resistance and hydrophilicity and high tensile strength.
또한, 시멘트를 혼입하되 인장강도 및 신장율을 크게 개선하여 콘크리트 구조물의 노면에서 분리되거나 이탈되지 아니하는 우수한 성능을 갖게 되는 효과가 있다.In addition, the cement is mixed, but the tensile strength and elongation rate is greatly improved to have an excellent performance that does not separate or detach from the road surface of the concrete structure.
또한, 시멘트 계열의 무기질 분말을 사용하기 때문에 콘크리트와 함께 수축 및 팽창이 이루어지고, 콘크리트의 수분을 외부로 용이하게 배출함으로써 콘크리트의 부식을 방지할 수 있어서 건물의 수명을 연장시킬 수 있는 효과가 있다.
In addition, the use of cement-based inorganic powder shrinks and expands with the concrete, and can easily prevent the corrosion of the concrete by easily discharging the moisture of the concrete to the outside, thereby extending the life of the building. .
이하, 본 발명의 바람직한 실시예에 의한 주차장 바닥용 무기질계 도막방수제를 상세히 설명하고자 한다.Hereinafter, an inorganic coating film waterproofing agent for a parking lot floor according to a preferred embodiment of the present invention will be described in detail.
그러나, 본 발명의 명세서에서 제시되는 실시예에 의하여 본 발명의 범위가 한정되는 것은 아니며, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의하여 본 발명의 기술사상과 아래에 기재될 특허청구범위의 균등범위 내에서 다양한 수정 및 변형 가능한 것으로 이해되어야 할 것이다.However, the scope of the present invention is not limited by the embodiments presented in the specification of the present invention, and the technical idea of the present invention and claims to be described below by those skilled in the art to which the present invention pertains. It is to be understood that various modifications and variations are possible within the scope of equivalents.
또한 실시예를 설명함에 있어서 본 발명이 속하는 기술 분야에 익히 알려져 있고, 본 발명과 직접적으로 관련이 없는 기술 내용에 대해서는 설명을 생략한다. 이는 불필요한 설명을 생략함으로써 본 발명의 요지를 흐리지 않고 더욱 명확히 전달하기 위함이다.
Further, in describing the embodiments, descriptions of technical contents which are well known in the technical field to which the present invention belongs and which are not directly related to the present invention will be omitted. This is for the sake of clarity of the present invention without omitting the unnecessary explanation.
본 발명의 주차장 바닥용 무기질계 도막방수제는, 아크릴 에멀젼 22 내지 30 중량%; 알루미나시멘트 15 내지 21 중량%; 마이크로시멘트 6 내지 11 중량%; 백시멘트 6 내지 11 중량%; 흙시멘트 6 내지 11 중량%; 생석회 1 내지 4 중량%; 규사 25 내지 33 중량%; 유동화제 0.1 내지 0.4 중량%; 소포제 0.1 내지 0.4 중량%;; 및 팽창제 0.1 내지 0.4 중량%; 로 이루어진다.Inorganic coating film waterproofing agent for a parking lot floor of the present invention, acrylic emulsion 22 to 30% by weight; 15 to 21 weight percent of alumina cement; 6 to 11 weight percent microcement; 6-11% by weight of cement; Soil cement 6-11 wt%; Quicklime 1-4 weight percent; 25 to 33 weight percent of silica sand; 0.1 to 0.4% by weight of a glidant; Antifoaming agent 0.1-0.4 wt%; And 0.1 to 0.4% by weight of expanding agent; .
본 출원인이 다수의 실험을 한 결과, 상기 아크릴 에멀젼 26.10 중량%; 상기 알루미나시멘트 18.30 중량%; 상기 마이크로시멘트 7.83 중량%; 상기 백시멘트 7.83 중량%; 상기 흙시멘트 7.83 중량%; 상기 생석회 2.61 중량%; 상기 규사 28.72 중량%; 상기 유동화제 0.26 중량%; 상기 소포제 0.26 중량%;; 및 상기 팽창제 0.26 중량%; 로 이루어지는 것이 바람직하였다.Applicants have conducted a number of experiments which resulted in 26.10% by weight of the acrylic emulsion; 18.30% by weight of the alumina cement; 7.83 wt% of the microcement; 7.83 wt% of the back cement; 7.83 wt% of the soil cement; 2.61 wt% of the quicklime; 28.72% by weight of silica sand; 0.26% by weight of the glidant; 0.26% by weight of the antifoam; And 0.26% by weight of the expanding agent; It was preferable that it consists of.
상기와 같은 주차장 바닥용 무기질계 도막방수제는 액체상태의 조성물과, 분말상태의 조성물을 별도로 준비하였다가 필요시 혼합하여 즉시 사용하도록 할 수 있다. 이때, 소정 크기의 원형통에 액체상태의 조성물을 넣은 후 분말상태의 조성물을 부어서 전동고속믹서기로 3분 내지 5분 동안 희석시키게 된다.The inorganic coating waterproofing agent for the floor of the parking lot as described above may be prepared separately from the liquid composition and the composition of the powder form, and may be mixed and used immediately if necessary. At this time, the liquid composition is put into a circular cylinder of a predetermined size, and then the powder composition is poured and diluted for 3 to 5 minutes with an electric high speed mixer.
상기 아크릴 에멀젼은 일반적인 통상의 것으로 물과 계면활성제 및 아크릴 수지 공중합체 등을 섞어서 교반 한 것을 사용하며, 이러한 아크릴 에멀젼은 우수한 내마모성, 내후성, 내균열성, 내충격성 및 강도 등이 우수한 것으로 알려져 있다.The acrylic emulsion is commonly used as a mixture of water, a surfactant and an acrylic resin copolymer, and agitated. Such an acrylic emulsion is known to have excellent wear resistance, weather resistance, crack resistance, impact resistance and strength.
또한, 상기 알루미나시멘트는 짧은 시간에 경화가 이루어지도록 하기 위하여 사용하는 것으로서 대단한 조강성을 가지며 내화성이 우수한 데, 본 발명에서는 산화알루미늄이 30 내지 40% 들어 있는 시멘트를 사용한다.In addition, the alumina cement is used to make the hardening in a short time, and has a great roughness and excellent fire resistance, in the present invention uses a cement containing 30 to 40% of aluminum oxide.
또한, 상기 마이크로시멘트는 수밀성과 침투성을 극대화하며 내구성 및 강도를 높이기 위하여 분말도 8000㎠/ｇ 이상의 마이크로시멘트(일명:마이셈 8000)를 사용하는 것이 바람직하다. 물론, 성능이 일부 저하되는 것을 인정하면 분말도 3000㎠/ｇ의 포틀랜트 시멘트 또는 고로 시멘트 등을 사용할 수 있으며, 분말도 6000㎠/ｇ의 마이크로시멘트(일명:마이셈 6000)를 사용할 수 도 있다.In addition, in order to maximize the watertightness and permeability, and to increase the durability and strength, the microcement preferably uses a microcement (aka: Misem 8000) having a powder degree of 8000 cm 2 / g or more. Of course, if it is recognized that the performance is partially reduced, portland cement or blast furnace cement of 3000 cm 2 / g may be used as the powder, and microcement (aka: Misem 6000) of 6000 cm 2 / g may also be used as the powder. .
또한, 상기 백시멘트는 짧은 시간에 경화가 이루어지도록 하기 위하여 사용된다.In addition, the back cement is used for curing in a short time.
또한, 상기 흙시멘트는 시멘트에 흙을 섞어서 만든 것으로 단단하게 된다.In addition, the soil cement is hardened by mixing the soil with cement.
또한, 상기 생석회는 원활한 수화반응을 위하여 사용한다.In addition, the quicklime is used for a smooth hydration reaction.
또한, 상기 규사는 통상적으로 사용되는 모래를 사용할 수 있는데, 많이 포함될수록 강도가 높아지게 되며, 미끄럼을 방지하기 위한 목적으로 사용된다.In addition, the silica sand can be used commonly used sand, the more included is the higher the strength, it is used for the purpose of preventing slipping.
또한, 상기 유동화제(superplasticizer)는 콘크리트를 부드럽게 하기 위한 혼합제로써 시멘트 입자의 분산을 위하여 사용하는데, 입자 사이에 윤활막을 형성하여 각 성분들 사이의 상호 부착력을 저감시켜 배합이나 경화된 콘크리트의 품질을 변경시키는 일 없이 유동성을 대폭적으로 개선시키게 된다.In addition, the superplasticizer is used to disperse the cement particles as a blending agent to soften the concrete. A lubricating film is formed between the particles to reduce the mutual adhesion between the components, thereby improving the quality of the blended or hardened concrete. The liquidity is greatly improved without changing.
본 출원인은 일반적으로 알려진 CMC-PC, Peramin SMF30, Peramin Conpac 149S 등을 포함한 다양한 유동화제가 사용될 수 있음을 실험을 통하여 확인하였다. 상기 제시한 종류의 유동화제 뿐 만 아니라 다른 유동화제의 사용도 가능하다. 이와 같은 유동화제의 사용으로 화학적으로 안정되어 고강도의 콘크리트 제조가 용이하게 되고, 슬럼프 로스(slump loss)가 거의 없게 되는 효과가 있다.Applicant has confirmed through experiments that various fluidizing agents including commonly known CMC-PC, Peramin SMF30, Peramin Conpac 149S and the like can be used. In addition to the fluidizing agents of the kind set forth above, the use of other fluidizing agents is possible. The use of such a fluidizing agent is chemically stable, making it easy to manufacture high-strength concrete, and there is an effect of almost no slump loss.
또한, 상기 소포제는 거품발생을 억제하기 위하여 사용하는데 공기량을 조절하고 기포를 감소시키는 기능을 수행하게 된다. 이로 인해 품질의 안정성을 확보할 수 있게 되며, 강도를 증진시키는 효과가 있다.In addition, the antifoaming agent is used to suppress the foaming to control the amount of air and to reduce the function of bubbles. This makes it possible to ensure the stability of the quality, there is an effect to enhance the strength.
본 출원인은 일반적으로 알려진 Agitan 295, Agitan P803, Agitan P833 등을 포함한 다양한 소포제가 사용될 수 있음을 실험을 통하여 확인하였다. 물론 상기 제시한 종류의 소포제 뿐 만 아니라 다른 소포제의 사용도 가능하다.Applicant has confirmed through experiments that a variety of antifoaming agents including commonly known Agitan 295, Agitan P803, Agitan P833 and the like can be used. It is of course possible to use other antifoaming agents as well as the above-mentioned antifoaming agents.
또한, 상기 팽창제는 거품을 일으켜 부풀게 하는 물질로써 시멘트의 팽창을 위하여 사용한다. 본 발명에서는 일반적으로 알려진 다양한 종류의 팽창제가 사용될 수 있다.In addition, the expanding agent is used to expand the cement as a material to inflate bubbles. In the present invention, various types of expanding agents generally known may be used.
Claims (2)
알루미나시멘트 15 내지 21 중량%;
마이크로시멘트 6 내지 11 중량%;
백시멘트 6 내지 11 중량%;
흙시멘트 6 내지 11 중량%;
생석회 1 내지 4 중량%;
규사 25 내지 33 중량%;
유동화제 0.1 내지 0.4 중량%;
소포제 0.1 내지 0.4 중량%;; 및
팽창제 0.1 내지 0.4 중량%; 로 이루어지는 것을 특징으로 하는 주차장 바닥용 무기질계 도막방수제.
Acrylic emulsion 22-30% by weight;
15 to 21 weight percent of alumina cement;
6 to 11 weight percent microcement;
6-11% by weight of cement;
Soil cement 6-11 wt%;
Quicklime 1-4 weight percent;
25 to 33 weight percent of silica sand;
0.1 to 0.4% by weight of a glidant;
Antifoaming agent 0.1-0.4 wt%; And
0.1 to 0.4% by weight of expanding agent; Inorganic-based coating waterproofing agent for parking lot floor, characterized in that consisting of.
상기 아크릴 에멀젼 26.10 중량%;
상기 알루미나시멘트 18.30 중량%;
상기 마이크로시멘트 7.83 중량%;
상기 백시멘트 7.83 중량%;
상기 흙시멘트 7.83 중량%;
상기 생석회 2.61 중량%;
상기 규사 28.72 중량%;
상기 유동화제 0.26 중량%;
상기 소포제 0.26 중량%;; 및
상기 팽창제 0.26 중량%; 로 이루어지는 것을 특징으로 하는 주차장 바닥용 무기질계 도막방수제.The method of claim 1,
26.10% by weight of the acrylic emulsion;
18.30% by weight of the alumina cement;
7.83 wt% of the microcement;
7.83 wt% of the back cement;
7.83 wt% of the soil cement;
2.61 wt% of the quicklime;
28.72% by weight of silica sand;
0.26% by weight of the glidant;
0.26% by weight of the antifoam; And
0.26% by weight of the expanding agent; Inorganic-based coating waterproofing agent for a parking lot floor, characterized in that consisting of.