KR101011754B1 - Texture expression according to using sand of steel support and stone table with the steel support - Google Patents

Abstract

PURPOSE: A texture expression method of steel supports for an upper plate and a stone table with steel supports are provided, which can enhance natural beauty and stereoscopic perception of steel supports for an upper plate. CONSTITUTION: A texture expression method of steel supports for an upper plate comprises: a first painting step(S1) of painting the surface of steel supports for an upper plate with paint; a second painting step(S2) of painting the surface of steel supports for an upper plate with paint mixed with hardener and sand; a first drying and curing step(S3) of drying and hardening the surface of steel supports for an upper plate; a third painting step(S4) of painting the surface of steel supports for an upper plate with paint; a second drying and curing step(S5) of drying and hardening the surface of steel supports for an upper plate; and a coating step(S6) of coating the surface of steel supports for an upper plate.

Description

Texture expression according to using sand of steel support and stone table with the steel support}

The present invention relates to a method for expressing a steel leg texture using sand and a stone table provided with a steel leg textured by the method. More specifically, the surface of the steel leg for supporting a plate is mixed with sand. It can be painted to increase the natural beauty and three-dimensional appearance of the steel legs for supporting the top plate. Even if the top plate made of stone is placed, it is stably supported by high strength steel and at the same time, it realizes the aesthetic effect with the top plate made of stone. It relates to a steel leg texture expression method for supporting the upper plate using the sand can be raised and the stone table is provided with a steel leg textured by this method.

In general, a variety of materials are used for the interior and exterior materials of the furniture to suit the function and aesthetics of the furniture, wood, synthetic resin, steel and stone are used as the material.

As the interior and exterior materials of the furniture used in the prior art, the stone is used in a variety of durable and environmentally friendly materials, in particular, it is used in expensive furniture with a luxurious feel.

However, stone has a disadvantage in that it is difficult, heavy, and expensive to make various types of furniture parts because of limitations in processing methods.

In recent years, furniture made of steel has been increasing. In particular, steel has less volatile organic compounds such as formaldehyde and carbon monoxide than wood, and the recycling process is not difficult. I am getting it.

As the Ministry of Environment approved steel furniture as an eco-friendly product in 2005, the domestic market of steel furniture grew rapidly, and steel furniture, which was mainly used for office furniture, is also used as home furniture.

Steel has the advantage of being able to produce furniture at low cost and simplified process compared to wood or stone, and it is durable and non-combustible material that can reduce damage in case of fire.

In addition, there is an advantage that it is possible to manufacture a furniture having a complicated shape because of its excellent ductility and malleability and easy processing.

However, despite the advantages of the steel as described above, the steel is not applied to a variety of furniture due to the texture feels sharp and cold.

In recent years, furniture made of various materials, such as steel and wood, stone and steel, has been manufactured, taking advantage of the properties of each material.

For example, the seat is made of wood, the dining table is made so that the marble top plate is placed on the upper side of the seat, the frame is made of steel, a part of the bookshelf and chairs are made of wood, and the like.

As described above, the seat 30 'is made of wood and the dining table 100' is made so that the marble top plate 20 'is placed on the top of the seat. The disadvantage is that the life can be shortened.

When steel is used instead of wood in the pedestal 30 ', the durability is high, but the aesthetic effect is inferior due to the texture apart from the top plate 20' made of marble.

Accordingly, it is necessary to develop a method of manufacturing steel furniture that can provide both the luxury of the stone and the practicality and durability of the steel, and can enhance the aesthetic effect as a whole.

Accordingly, the present invention has been made to solve the above problems, the object of the present invention is to paint with a mixture of sand, to increase the aesthetic effect of the furniture produced using iron, furniture made of various materials and The stone table is provided with a method of expressing the top of the steel bridge texture using sand and the steel legs textured by this method, which can achieve the harmony of the materials, and take advantage of the inexpensive and durable steel materials. In providing.

The method for expressing the upper steel support leg legs using sand of the present invention includes a primary painting step (S1) in which the surface of the upper steel support leg 10 is first painted with paint; A secondary painting step (S2) in which a surface of the upper plate supporting steel leg 10, which is primarily painted, is secondly painted with a paint mixed with a hardener and sand; A primary drying and curing step (S3) in which the surface of the upper plate supporting steel legs 10 which are secondary painted are dried and cured at room temperature (deleted); A tertiary painting step (S4) in which the surface of the steel plate for supporting the upper plate (1), which is primarily dried, is tertiaryly painted with paint; A secondary drying and curing step (S5) in which the surface of the upper plate supporting steel leg 10, which is tertiary painted, is dried and cured at room temperature (deleted); A coating step (S6) of which the surface of the dried upper plate supporting steel legs 10 is matte or glossy coated; And is formed to include a plurality of protrusions.

In addition, in the secondary painting step (S2), the curing agent is mixed with the paint at 15 to 25% by weight of the paint weight, the paint mixed with the curing agent is mixed with sand at 95 to 105% by weight of the sand weight, The paint is mixed with the sand, characterized in that the surface of the upper support steel legs 10 is secondary painted.

In addition, the paint is characterized in that the acrylic urethane is used.

In addition, the primary drying and curing step (S3) is characterized in that it is carried out for at least 24 hours or more.

In addition, the secondary painting step (S2) is a painting operation is made by a knife, it characterized in that the surface smoothing operation of the upper plate supporting steel leg 10 by a knife or a wire.

In addition, between the first drying and curing step (S3) and the third phase painting step (S4), the surface 10 of the first dried steel plate supporting steel legs are refined and partially corrected and supplemented. (S3-1) is further characterized.

In addition, in the coating step (S6), the coating agent is mixed with the curing agent at a weight of 195 to 205% of the weight of the curing agent, and the surface of the upper leg support steel leg 10 is coated with the curing agent with a matt or gloss coating. It is characterized by.

The stone table of the present invention includes a plurality of steel plate supporting steel legs 10 textured by the method as described above; And a top plate 20 which is supported by the top plate supporting steel legs 10 and is placed on the top plate supporting steel legs 10 and made of stone. Characterized in that it is formed to include.

Accordingly, the stone table for expressing the steel legs texture using the sand of the present invention and the stone table provided with the steel legs textured by this method is painted with a mixture of sand, the aesthetic effect of the furniture made of steel There is an advantage that can be increased.

In addition, a stone table for expressing the steel bridge texture using the sand of the present invention, and the stone table is provided with the steel legs textured by this method is a combination of furniture made of expensive material stone and steel, a relatively inexpensive material By making it possible to achieve, it is possible to reduce the cost compared to the table made of stone as a whole, there is an advantage that can be used simultaneously with the durability and practicality of the steel.

Particularly, the stone table for expressing the steel bridge texture using the sand of the present invention and the stone table provided with the steel legs textured by the method are made of stone and steel, which are environmentally friendly materials, and thus formaldehyde and carbon monoxide, etc., compared to wood. It has the advantage of reducing the occurrence of various volatile organic compounds, cancer, emotional anxiety, respiratory disease.

Figure 1 is a step showing a method for expressing the upper steel plate legs texture using the sand of the present invention.
Figure 2 is a perspective view showing a state before the texture is expressed on the upper leg support steel legs of the stone table.
Figure 3 is a perspective view showing a stone table provided with a steel leg textured by the method for expressing the steel bridge texture using the sand of the present invention.

Hereinafter, a method of expressing a steel leg texture using the sand of the present invention having the characteristics as described above, and a stone table provided with the steel leg textured by the method will be described in detail with reference to the accompanying drawings.

1 is a step diagram showing a method for expressing the upper steel support leg legs texture using sand of the present invention, Figure 2 is a perspective view showing a state before the texture is expressed on the upper steel support legs of the stone table, Figure 3 is a present invention Is a perspective view showing a stone table is provided with a steel leg textured by the method of expressing the steel bridge texture using the sand of the sand.

1 is a step diagram showing a method for expressing the top of the steel bridge texture using the sand of the present invention, the method for expressing the top of the steel bridge texture using the sand of the present invention is a primary painting step (S1); Secondary painting step S2; Primary drying and curing step (S3); Third painting step (S4); Secondary drying and curing step (S5); And coating step (S6); It is formed to include.

The first painting step S1 is a step in which the surface of the upper plate supporting steel leg 10 is first painted with paint.

The steel is oxidized and rusted by reacting with oxygen in the air. In the first painting step S1, the surface of the upper plate supporting steel leg 10 is painted by a flat brush or a round brush to prevent rust.

The secondary painting step (S2) is a step in which the surface of the upper support steel legs 10, which is primarily painted, is secondaryly painted with a paint mixed with a hardener and sand.

In the second painting step (S2), the curing agent is mixed with the paint at 15 to 25% by weight of the paint weight, the paint mixed with the curing agent is mixed with sand at 95 to 105% by weight of the sand weight, the sand It is characterized in that the surface of the upper support steel legs 10 are painted with a paint mixed with the secondary.

The curing agent helps to harden the paint. If too much is added, the paint color becomes weak and at the same time, the tensile strength and the compressive strength due to external impact are weakened. If the amount is too small, the surface strength and hardness are weakened and the elasticity is increased.

Therefore, the curing agent and the paint should be mixed in an appropriate ratio, and in the present invention, when the curing agent and the paint were mixed in a ratio of about 1: 5 through several experiments, the result was the most suitable for texturing.

The second painting step (S2) is a painting operation by the knife, the first drying and curing step (S3) through the surface smoothing operation of the steel plate 10 for supporting the upper plate by a knife or a metal wire can be made. have.

In this case, the tools used may be replaced by other tools as well as brushes and knives, and the tools are not limited to brushes and knives.

The first drying and curing step (S3) is a step of drying and curing the surface of the steel plate 10 for supporting the upper plate is secondary paint.

The first drying and curing step (S3) is characterized in that it is carried out for at least 24 hours or more.

The tertiary painting step (S4) is a step of tertiary painting with paint to harmonize the surface of the steel plate 10 for supporting the upper plate which is primarily dried with the upper plate.

In the third painting step S4, the texture expressed by the paint mixed with sand is emphasized in the second painting step S2, and may be expressed by a flat brush for color matching with the top plate.

In this case, the tool used may be replaced with a brush or other tool of another type, not a flat brush, and the tool is not limited to the flat brush.

The secondary drying and curing step (S5) is a step of drying and curing the surface of the steel legs for supporting the upper plate painted in the third.

The coating step (S6) is a step in which the surface of the dried upper plate supporting steel leg 10 is matte or glossy coated.

In the coating step S6, the coating agent is mixed with the curing agent at a weight of 195 to 205% of the weight of the curing agent, and the surface of the upper leg support steel leg 10 is coated with a coating agent mixed with the curing agent to have a matt or gloss coating. It features.

As the paint used in the method for expressing the steel leg texture using sand according to the present invention, it is preferable that the acryl urethane, which is a two-component paint, is used.

The acryl urethane has the advantage of being resistant to moisture and direct sunlight and having a low elasticity to increase durability and life of furniture.

Between the primary drying and curing step (S3) and the tertiary painting step (S4), the surface of the first dried and hardened top plate supporting steel leg 10 is refined and partially corrected and supplemented (S3-1) may be further added.

On the other hand, the stone table 100 of the present invention is supported by a plurality of top plate support steel legs 10 and the top plate support steel legs 10 represented by the texture as described above, the top plate support It is formed to include an upper plate 20 made of stone and placed on the steel leg 10.

In the stone table 100 of the present invention, the steel used for the upper plate supporting steel leg 10 is too large if the thickness of the steel is 4.5T or more, and the strength is low if the thickness of the steel is 4.5T or less. Since it is difficult to stably support 20), it is preferable to use steel having a thickness of 4.5T.

The upper plate supporting steel legs 10 supporting the upper plate 20 are laser cut, bent, welded, or assembled so that a plurality of the upper plates are connected to each other to form a pedestal in a structure and a shape in which a large weight plate can be stably supported. The top plate 20 may be placed for the base 30 composed of the steel plate 10 for supporting the top plate.

The upper plate 20 is preferably placed on the upper side of the upper plate supporting steel legs 10 after the upper plate supporting steel legs 10 after the coating step (S6) is dried for 3 to 4 hours.

Accordingly, the method of expressing the top plate steel leg texture using the sand of the present invention is to paint the surface of the top plate steel leg with a mixture of sand, thereby increasing the durability and overall harmony of the furniture made of steel It has the advantage of increasing the aesthetic effect.

In addition, the stone table of the present invention is manufactured to be in harmony with the furniture made of stone, which is an expensive material and a relatively inexpensive material, it is possible to reduce the cost compared to the table is made of stone as a whole, It has the advantage of being able to utilize durability and practicality at the same time.

In particular, since the stone table of the present invention is made of stone and steel, which are environmentally friendly materials, there is less generation of various volatile organic compounds such as formaldehyde and carbon monoxide than wood, thereby reducing the possibility of developing cancer, emotional anxiety, and respiratory diseases.

The present invention is not limited to the above-described embodiment, and the scope of application is of course various modifications can be made without departing from the gist of the present invention claimed in the claims.

S1 ~ S6: Each step of the method of expressing the steel bridge texture for supporting the upper plate using sand
100: stone table
10: steel legs for supporting the top plate
20: top plate
30: base

Claims (8)

A primary painting step (S1) in which the surface of the upper plate supporting steel leg 10 is primarily painted with paint;
A secondary painting step (S2) in which a surface of the upper plate supporting steel leg 10, which is primarily painted, is secondly painted with a paint mixed with a hardener and sand;
A first drying and curing step (S3) of drying and curing the surface of the steel plate for supporting the upper plate (10), which is secondary painted;
A tertiary painting step (S4) in which the surface of the upper leg supporting steel leg (10), which is primarily dried and cured, is tertiaryly painted with paint;
A secondary drying and curing step (S5) of drying and curing the surface of the steel plate supporting steel legs (10), which are tertiary painted;
A coating step (S6) of which the surface of the upper leg supporting steel leg (10), which is dried and cured second, is matte or glossy coated; Steel leg texture representation method for supporting the upper plate using the sand, characterized in that formed.
The method of claim 1,
In the second painting step (S2)
The curing agent is mixed with the paint at a weight of 15-25% by weight of the paint,
The paint mixed with the curing agent is mixed with sand at 95 to 105% by weight of the sand,
The method for expressing the upper leg support steel leg texture using sand, characterized in that the surface of the upper support steel leg (10) is secondary paint by the paint mixed with the sand.
The method of claim 2,
The paint is a method of expressing the iron bridge texture using the sand, characterized in that the acryl urethane is used.
The method of claim 1,
The primary drying and curing step (S3)
The method of expressing the steel bridge texture for the upper plate support using sand, characterized in that performed for at least 24 hours or more.
The method of claim 1,
The second painting step (S2) is
The painting work is performed by a knife, and the surface of the steel support for leg support using sand, characterized in that the surface smoothing operation of the steel support for the upper plate (10) is performed by a knife or wire.
The method of claim 1,
Between the first drying and curing step (S3) and the third painting step (S4)
Steel legs for supporting the upper plate with sand, characterized in that the surface of the primary dried and hardened steel support plate 10 is further refined and partially corrected and supplemented (S3-1). How to express the texture.
The method of claim 1,
In the coating step S6, the coating agent is mixed with the curing agent at a weight of 195 to 205% of the weight of the curing agent, and the surface of the upper leg support steel leg 10 is coated with a coating agent mixed with the curing agent to have a matt or gloss coating. A method of expressing the texture of the steel legs for supporting the upper plate using sand.
A plurality of top plate supporting steel legs textured by the method according to any one of claims 1 to 7; And
A top plate 20 supported by the top plate supporting steel legs 10 and positioned above the top plate supporting steel legs 10 and formed of stone; Stone table, characterized in that is formed, including.