KR100777064B1 - Method of Producting of the facial cream preparing Biovital-water using material Radiating Far 0Infared and Mineral - Google Patents

Abstract

The present invention relates to a method for producing a cosmetic massage pack comprising a natural mineral consisting of a far-infrared radiation active solution containing a mineral and a clay mineral.

The present invention powders a mixed mineral of zeolite, ganbanite, bentonite and sepiolite, and attapulgite, which is a far-infrared mineral containing a large amount of minerals beneficial to animals and plants as well as the human body, and powdered mineral minerals by adding water thereto. After dissolving the mineral from the mineral water was added to the ceramic powder made by baking ocher to prepare the mineral water, after preparing a far-infrared radioactive solution containing a large amount of minerals, and mixed with the clay mineral bentonite and montmorillonite powder, sterilization and aging It relates to a method for producing a beauty massage pack.

Minerals are trace elements obtained from minerals and are trace elements necessary for the growth and growth of animals and plants. Therefore, when the mineral is deficient, the flora and fauna will see a decrease in growth and a decrease in harvest.

Far-infrared rays are known to have a variety of functions, such as the function of activating animals and plants, promoting metabolism, odor removal, pollutant adsorption and decomposition removal and nutrition absorption, cell activation.

The present invention powders mineral minerals containing a large amount of the minerals and dissolves them in water to make mineral water rich in minerals and mix ceramic powders that emit far infrared rays to the far-infrared radiation active solution containing minerals. The present invention relates to a method for producing a beauty massage pack containing natural minerals, which are rich in minerals and are prepared by mixing bentonite and montmorillonite powder, which are clay minerals having adsorptive power.

Far Infrared Radiation Material, Ceramic Powder, Mineral Minerals, Beauty Massage Pack

Description

Method of Producting of the facial cream preparing Biovital-water using material Radiating Far 0Infared and Mineral}

Figure 1. Manufacturing process diagram of the present invention

The present invention relates to a method for manufacturing a cosmetic massage pack, and more particularly, to a method for manufacturing a cosmetic massage pack using a mineral active solution containing far-infrared radiation minerals.

As the human skin ages, it is damaged by various contaminants and stresses. As a result, the skin cells are damaged and cell proliferation is not properly performed, resulting in loss of elasticity and wrinkles.

Normal healthy skin has a protective ability to protect the skin from external damage factors, but the protective ability decreases due to continuous external stimuli, which lowers the skin's protective ability, resulting in decreased skin elasticity, wrinkles, and skin aging. do.

Aging of the skin may be attributed to a decrease in the moisturizing power of the skin and a decrease in the regenerative function.

In addition, the skin is damaged by ultraviolet rays and skin aging, the skin loses its elasticity, it can be seen that wrinkles occur.

As a method of preventing aging of the skin and maintaining healthy skin, it may not be exposed to ultraviolet rays or various pollutants, may not be stressed, and may provide a method of maintaining skin health by administering nutrients to the skin.

The present invention relates to a method for manufacturing a beauty massage pack using far-infrared radiation substances to keep skin healthy and to absorb cosmetics or nourishing creams well into the skin to prevent aging of the skin and maintain healthy skin. The present invention relates to a method for producing a beauty pack for massage comprising a large amount of minerals dissolved from the ceramic powder and clay minerals, which are far-infrared radiation materials.

Far Infared Ray is a kind of electromagnetic wave and belongs to the category of infrared rays. Infrared is an electromagnetic wave that has a longer wavelength and thermal effect than the red region of visible light, and infrared rays in a long wavelength region are called far infrared rays within the infrared wavelength range, and it is difficult to accurately distinguish wavelength bands of far infrared rays, but it is generally in the range of 3 μm to 1000 μm. Infrared rays are defined as far infrared rays.

In particular, it can be seen that the wavelength region of far-infrared rays used as a heat source in the industrial field uses a large range of the wavelength range of 2.5 μm to 25 μm.

Far-infrared rays, unlike other rays, have the characteristics of radiation, penetration, resonance, and absorption, so that metabolic and growth-promoting actions and resonances are caused by the vitalization of animals and plants. It has been found to have water activation, deodorization by absorption (adsorption), energy saving, etc., and many products and technologies utilizing the functions and actions of far-infrared rays are found throughout living and industry. You can see it is being developed.

Specific actions and effects on far-infrared rays include the treatment of various diseases and the hangover removal effect due to the growth and development of living organisms (animals and animals), the activation of cells and the promotion of metabolism, and the ability to activate water. Water purification effect, odor removal effect and decontamination effect of pollutants and growth promotion effect to help nutrient absorption and growth in plants, especially for humans, metabolism promotion, blood circulation promoting cell It can be seen that the disease treatment effect and fatigue recovery effect, cosmetic effects due to the activation of.

As such, although far infrared rays are partially included in visible light, they are emitted from ceramics such as ceramics and porcelain made by baking ocher at high temperatures, and minerals such as ganbanite and zeolite are emitted in a large amount of far infrared rays that are beneficial to the human body. have.

Elvan and zeolite are not only minerals that emit far-infrared rays, but are also known as minerals having a large amount of minerals that are beneficial to the human body.

Minerals are trace elements contained in ores, which are essential for life and flora and fauna such as vitamins.

Minerals are dissolved in the water by melting trace elements in the ground, rock, rock, etc., which is absorbed by water or absorbed by plants.

The best way for humans to absorb minerals is to consume it from plants that have absorbed abundant minerals.

Minerals are essential for the growth and growth of plants, as well as animals, including humans, and soils that lack minerals are able to absorb nutrients no matter how rich the fertilizer is. can see.

There are about 70 kinds of minerals in the natural world, and not only minerals that are beneficial to the human body but also minerals that harm the human body are present. In other words, the harmful minerals (harmful elements) are arsenic (As), palladium (Pb), mercury (Hg), uranium (U), antimony (Sb), barium (Ba), beryllium (Be), bismuth (Bi), silver ( Ag) etc. can be mentioned, for example.
In addition, the minerals required for animals and plants are extremely small amounts of human intake of minerals can be harmful. Therefore, it is desirable that minerals be absorbed in food (animals and animals).

delete

Soils lacking in minerals do not grow well even with high fertilizers and poor growth.

Therefore, it is no exaggeration to say that healthy and fresh plants contain many nutrients and many minerals.

The present invention contains a large amount of minerals that greatly help the growth and growth of animals and plants, and using a ceramic powder that emits far infrared rays, the far-infrared radiation active solution rich in minerals is mixed with clay minerals. It relates to a method of manufacturing a beauty massage pack containing natural minerals prepared by sterilization and aging.

The present invention has been developed for the purpose of providing a beauty pack that keeps the skin healthy, prevents aging of the skin, and activates the cells of the skin, thereby maintaining a smooth and glossy skin.

The present invention is to extract the beneficial natural minerals of plants and animals from mineral minerals and to dissolve them in water to mix ceramic powders that emit far-infrared rays in the mineral water prepared by mixing the far-infrared radiation active solution and then mix the mineral powder-rich clay minerals It relates to a method of manufacturing a beauty pack for a massage that is rich in minerals and emits far infrared rays. Looking at the manufacturing process for this is as follows.

The present invention is prepared by a first step process of preparing a far infrared radiation active solution and a second step process of preparing a massage pack using the far infrared radiation active solution prepared in the first step process.

First, the first step of preparing a far-infrared radioactive solution will be described.

Raw material for pulverizing mixed minerals composed of 25 to 35% by weight zeolite, 25 to 35% by weight of bentonite, 25 to 35% by weight of bentonite, 5 to 10% by weight of sepiolite, and 5 to 10% by weight of attapleite to 400 to 600 mesh. And a mineral dissolving step of dissolving minerals from the mixed minerals by mixing and stirring 10 to 20% by weight of the powdered mixed mineral and 80 to 90% by weight of water prepared in the process. It has a mineral water separation process to separate the mixed minerals and the water (mineral water) by mixing the water mixed with stirring for a certain period of time through the filtration membrane (screen), and put the separated mineral water into the precipitation tank to be included in the mineral water It has a mineral water extraction step of precipitating fine mixed minerals and separating only the supernatant water, 80 to 90% by weight of the mineral water obtained in the mineral water extraction process and 1300 ~ 1500 ℃ A process of mixing the mineral water and ceramic powder mixed with 10 to 20% by weight of the ceramic powder obtained by pulverizing the ceramic obtained by the sintering process to about 400 to 600 mesh, and the ceramic powder mixed with the mineral water through a homogenizer It has a nano (NANO) grinding process that makes the particles of the powder extremely fine, about 5000-10,000 mesh, and boils the ceramic mixed solution mixed with the mineral water and fine ceramic powder produced through the nano grinding process for 1 to 3 hours. It has a sterilization process to sterilize the ceramic mixed solution by heating, and gradually cools it to 15 ~ 25 ℃, and forms a far-infrared radiation active solution containing minerals through the cooling and aging process of aging at 15 ~ 25 ℃ for 5 ~ 24 hours. And using this to perform a massage pack manufacturing process of the second step.

Referring to the massage pack manufacturing process of the second step is as follows.

There is a clay mineral mixing process of mixing 5-10% by weight of 400-600 mesh montmorillonite and 5-10% by weight of bentonite to 80-90% by weight of the far-infrared radiation active solution containing minerals obtained in the first step. It is charged to the stirrer and has a fine grinding process of finely crushing the particle size of the clay mineral to about 5000 to 10,000 mash, and then heating it for 1 to 5 hours to have a viscosity adjustment and sterilization process, and the heated thing is 15 to 25 ° C. It is to be prepared by the aging process to slowly cool the furnace and mature it for 5 to 24 hours.

In the present invention, the mineral minerals extracted from the zeolite, bentorite and elvan are described as follows.

Zeolite is a generic term for aluminum silicate hydrate minerals of alkali and alkaline earth metals, and has a molecular structure that has a porous structure due to loose atomic bonds in crystal structure, and has the property of adsorbing other particulate matter.

It is a mineral that is used as an adsorbent by using this property and as a molecular sieve to separate other particulates. In particular, zeolite has a property of adsorbing metal ions and converting the strong water into a single water, which can be used as a filter material of a softener.

Zeolite emits a large amount of minerals, and by using this property, it can be seen that it is used as an additive for soil improvement, fertilizer and pesticide supplement, and animal feed.

Bentonite is a mineral of aluminum silicate and has physicochemical properties such as ion exchange, suspension, adsorption, and swelling. Bentonite is used in civil engineering works because of its physical and chemical properties. It is known as a mineral that absorbs and neutralizes environmental pollutants and easily elutes large amounts of minerals in water.

Elvan is a mineral-rich rock that has been nicknamed a mysterious stone or weak stone.

Elvanite is composed of silicic anhydride (SiO ₂ ) and aluminum oxide (Al ₂ O ₃ ), and it contains ferric oxide (Fe ₂ O ₃ ) which is essential for human body and living cells. It contains 40 kinds of minerals. At the same time, it is known as a bio-mineral that emits far-infrared rays, and it is known as a mineral that has a function of adsorption, mineral elution ion exchange, harmful metal adsorption and decomposition, removal of sources of rot, and freshness retention.

By this function and action, it can be seen that elvan is used for water activator, water purifier, soil improver, deodorant, far-infrared radiant, environmental improver and the like.

Attaplugite used in the present invention is a creamy to gray clay mineral of magnesium aluminum silicate series belonging to monoclinic system, and has an elongated chain crystal structure.

When powdered attapleite is dispersed in water, it is connected to an irregular lattice and has thickening, suspension, and thixotropic or gilling.

Particularly, it is mixed with Sepiolite to form needle lump, and it can be seen to form an irregular network form by entangled in solvent such as water.When it is dispersed in water, it increases the viscosity of the solution. Used as an oil remover, animal floor covering, tank cleaning agent, potting compound and fertilizer, insecticide, neutralizing agent, and buffer.

Sepiolite is a light mineral (specific gravity 2.0 or less) with various colors such as white, gray, yellow, red, and blue green.

Like Attapluguite, it has adsorption, decolorizing, binding, and thickening ability, and is mixed with attapleite to be used in an adsorbent, neutralizing agent, buffer, and water to increase viscosity.

Montmorillonite is a mineral belonging to monoclinic system. It is a kind of white, gray, pink, sometimes blue and green clay mineral. It has a specific gravity of 2 to 2.5, and absorbs moisture to swell 7 to 10 times its original volume. It can be seen that it is used as a composition of toothpaste, soap and bath as a mineral having adhesive strength and ion exchangeability.

In addition, it is rich in minerals and has the ability to adsorb sebum and skin wastes.

The present invention manufactured using such a raw material will be described in more detail as follows.

It consists of 25 to 35% by weight of zeolite, elvanite and bentonite, respectively, and finely grinds the mixed minerals in which 5% to 10% by weight of sepiolite and attaplezite are mixed to about 400 to 600 meshes, and then mixes the raw materials. And a mixed mineral raw material in powder form through a mixing process.

10-20% by weight of the powdered mixed mineral prepared in the above step and 80-90% by weight of purified water are mixed and stirred to carry out the mineral dissolution step of dissolving the mineral from the powdered mixed mineral.

Performing a mineral water separation process of separating the minerals and minerals dissolved water (mineral water) by passing the mixture of the mixed minerals and water for a predetermined time (5 ~ 10 hours) through a filtration membrane (screen), Precipitate mineral water to extract only supernatant and pure mineral water.

Ceramic powder is added to the mineral water by mixing 80 to 90% by weight of the pure mineral water obtained above and 10 to 20% by weight of the ceramic powder obtained by pulverizing the clay at 1300 to 1500 ° C and pulverizing it to 400 to 600 mesh. Dissolves and performs a nano (NANO) grinding step of processing the microparticles extremely finely so that the particles of the ceramic powder to 5000 ~ 10,000 mesh using a homogenizer.

As such, the finely ground ceramic powder in mineral water is sterilized by heating for 1 to 3 hours, and the concentration is controlled by adjusting the heating time.

After heating, it is gradually cooled and aged for 5 to 24 hours to form a far-infrared radioactive solution containing minerals, and 400-600 mesh montmorillonite in 80-90% by weight of the far-infrared radiation-active solution containing the minerals thus prepared. 5-10% by weight of bentonite 5-10% by weight of clay minerals are mixed, and then charged into a stirrer, and the particle size of the clay minerals is finely pulverized and stirred to about 5000-10,000 mash, and then 1-5 hours. After heating to adjust viscosity and sterilization, the heated slowly cooled to 15 ~ 25 ℃ and aged for 5 to 24 hours to prepare a beauty massage pack.

The cosmetic massage pack manufactured through such a process includes a large amount of minerals, and the ceramic powder has fine particles through a nano-crushing process to emit a large amount of far infrared rays in comparison with a lumped far infrared emitter.

In addition, the present invention by mixing montmorillonite and bentonite powder, which are clay minerals containing a large amount of minerals in the far-infrared radiation active solution including minerals, finely homogenizing them and sterilizing and aging them, supplies minerals to the skin and radiates the far infrared rays to the skin. It will keep you healthy.

The present invention has a large amount of minerals dissolved from zeolites, macbanite, mentorite and sepiolite, attapleite, emits a large amount of far-infrared rays from the ceramic powder, and the main component is a mineral rich in minerals such as bentonite and montmorillonite It is manufactured by.

Usually minerals are taken by mouth through food, but are also absorbed into the body through the skin.

The present invention includes a large amount of minerals by directly dissolving mineral minerals in water to produce mineral water and far-infrared rays radiated by far-infrared radiation ceramic powder penetrates deep into the skin to expand blood vessels in the skin to promote blood circulation. It promotes the activation of skin cells and metabolism to remove the waste accumulated in the skin to keep the skin healthy.

In addition, bentonite and montmorillonite, the clay minerals added to the active solution in which minerals and far infrared rays are radiated, have strong adsorptive power to adsorb and remove sebum and wastewater, thus maintaining a smooth and clean skin, preventing skin aging, and removing wrinkles. It is a very useful invention to provide a beauty pack for massage.

Claims (1)

Raw material for pulverizing a mixed mineral composed of 25 to 35% by weight of zeolite, 25 to 35% by weight of bentonite, 25 to 35% by weight of bentonite, 5 to 10% by weight of sepiolite, and 5 to 10% by weight of attapleite to 400 to 600 mesh. Grinding and mixing process A mineral dissolving step of dissolving the mineral from the mixed mineral by mixing and stirring 10 to 20% by weight of the powdered mixed mineral prepared in the above step and 80 to 90% by weight of water; A mineral water separation process of separating the mixed minerals and water by stirring for a predetermined time and separating the mixed minerals and water (mineral water) in which the mixed minerals and minerals are dissolved by passing through a filtration membrane (screen); A mineral water extraction process of adding the separated mineral water to a precipitation tank to precipitate fine mixed minerals contained in the mineral water and separating only the supernatant water;  Mineral water and ceramics mixed with 80 to 90% by weight of mineral water obtained in the mineral water extraction step and 10 to 20% by weight of ceramic powder obtained by pulverizing the ceramic obtained by calcining the clay at 1300 to 1500 ° C to about 400 to 600 mesh. Mixing process of powder,  A nano (NANO) grinding process of extremely finely grinding the particles of the ceramic powder to 5000 to 10,000 mash through a homogenizer of the ceramic powder mixed in the mineral water; A sterilization step of sterilizing the ceramic mixed solution by heating the ceramic mixed solution mixed with the mineral water and the fine ceramic powder prepared by the nano-crushing process for 1 to 3 hours to boil;  It is gradually cooled to 15-25 ° C., and a far-infrared radiation active solution containing minerals is formed through a cooling and maturing process of aging at 15-25 ° C. for 5 to 24 hours at room temperature.  Clay mineral mixing process of mixing 5-10% by weight of 400-600 mesh montmorillonite and 5-10% by weight of bentonite with 80-90% by weight of the far-infrared radiation active solution containing the minerals, It is charged to a stirrer, and the fine grinding step of finely crushing the particle size of the clay mineral to about 5000 ~ 10,000 mash, By heating it to adjust viscosity and sterilization, The method for producing a beauty massage pack containing natural minerals, characterized in that it is slowly cooled to 15 ~ 25 ℃ and aged through a aging process for 5 to 24 hours.