KR100655152B1 - Composition for sterilizing and product using the same - Google Patents
Composition for sterilizing and product using the same Download PDFInfo
- Publication number
- KR100655152B1 KR100655152B1 KR1020040084920A KR20040084920A KR100655152B1 KR 100655152 B1 KR100655152 B1 KR 100655152B1 KR 1020040084920 A KR1020040084920 A KR 1020040084920A KR 20040084920 A KR20040084920 A KR 20040084920A KR 100655152 B1 KR100655152 B1 KR 100655152B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- composition
- oxide
- sterilizing
- Prior art date
Abstract
본 발명은 산화규소 45 내지 55 중량부, 산화알루미늄 8 내지 12 중량부, 수산화칼륨 3 내지 5 중량부, 산화마그네슘 3 내지 5 중량부, 붕산 25 내지 30 중량부, 산화망간 3 내지 5 중량부, 산화제일철 2 내지 3 중량부 및 사산화삼철 2 내지 3 중량부를 포함하는 살균 조성물을 제공한다. The present invention is 45 to 55 parts by weight of silicon oxide, 8 to 12 parts by weight of aluminum oxide, 3 to 5 parts by weight of potassium hydroxide, 3 to 5 parts by weight of magnesium oxide, 25 to 30 parts by weight of boric acid, 3 to 5 parts by weight of manganese oxide, It provides a sterilizing composition comprising 2-3 parts by weight of ferrous oxide and 2-3 parts by weight of ferric tetraoxide.
Description
도 1은 본 발명의 실시예 1의 살균 조성물의 모습을 보여주는 것이다.Figure 1 shows the appearance of the sterilizing composition of Example 1 of the present invention.
도 2는 본 발명의 실시예 2의 살균 조성물의 모습을 보여주는 것이다.Figure 2 shows the appearance of the sterilizing composition of Example 2 of the present invention.
도 3a 내지 3c는 본 발명의 실시예 1의 살균 조성물의 1 % 에서의 대장균 (E. coli)에 대한 살균 효과를 보여주는 것으로, 3a는 초기의 모습, 3b는 처리 10 분 후의 모습, 3c는 처리 30 분 후의 모습을 각각 보여준다.Figures 3a to 3c shows the bactericidal effect against E. coli in 1% of the bactericidal composition of Example 1 of the present invention, 3a the initial appearance, 3b 10 minutes after the treatment, 3c treatment Show 30 minutes after each one.
도 4a 내지 4c는 본 발명의 실시예 1의 살균 조성물의 1 % 에서의 포도상구균 (S. aureus)에 대한 살균 효과를 보여주는 것으로, 4a는 초기의 모습, 4b는 처리 10 분 후의 모습, 4c는 처리 30 분 후의 모습을 각각 보여준다.Figures 4a to 4c shows the bactericidal effect against S. aureus in 1% of the bactericidal composition of Example 1 of the present invention, 4a is the initial appearance, 4b is 10 minutes after treatment, 4c is Shown after 30 minutes of treatment, respectively.
도 5a 내지 5c는 본 발명의 실시예 2의 살균 조성물의 1 % 에서의 대장균 (E. coli)에 대한 살균 효과를 보여주는 것으로, 5a는 초기의 모습, 5b는 처리 10 분 후의 모습, 5c는 처리 30 분 후의 모습을 각각 보여준다.Figures 5a to 5c shows the bactericidal effect against E. coli in 1% of the bactericidal composition of Example 2 of the present invention, 5a is the initial appearance, 5b is 10 minutes after the treatment, 5c is the treatment Show 30 minutes after each one.
도 6a 내지 6c는 본 발명의 실시예 2의 살균 조성물의 1 % 에서의 포도상구균 (S. aureus)에 대한 살균 효과를 보여주는 것으로, 6a는 초기의 모습, 6b는 처리 10 분 후의 모습, 6c는 처리 30 분 후의 모습을 각각 보여준다.Figure 6a to 6c shows the bactericidal effect against S. aureus in 1% of the bactericidal composition of Example 2 of the present invention, 6a is the initial appearance, 6b is 10 minutes after treatment, 6c is Shown after 30 minutes of treatment, respectively.
도 7a 내지 7c는 본 발명의 실시예 2의 살균 조성물의 2 % 에서의 대장균 (E. coli)에 대한 살균 효과를 보여주는 것으로, 7a는 초기의 모습, 7b는 처리 10 분 후의 모습, 7c는 처리 30 분 후의 모습을 각각 보여준다.Figures 7a to 7c shows the bactericidal effect against E. coli in 2% of the bactericidal composition of Example 2 of the present invention, 7a is the initial appearance, 7b is 10 minutes after the treatment, 7c is treated Show 30 minutes after each one.
도 8a 내지 8c는 본 발명의 실시예 2의 살균 조성물의 2 % 에서의 포도상구균 (S. aureus)에 대한 살균 효과를 보여주는 것으로, 8a는 초기의 모습, 8b는 처리 10 분 후의 모습, 8c는 처리 30 분 후의 모습을 각각 보여준다. 8a to 8c shows the bactericidal effect against S. aureus in 2% of the bactericidal composition of Example 2 of the present invention, 8a is the initial state, 8b is 10 minutes after the treatment, 8c is Shown after 30 minutes of treatment, respectively.
도 9a 내지 9d는 본 발명의 실시예 2의 살균 조성물로 제조된 적용예 13의 스폰지에 대한 살균력 시험 결과를 보여주는 사진이다. 도 9a 및 9b는 S. aureus에 대한 살균력을 보여주는 것으로, 9a는 대조편에 접종 즉시 회수한 생균수를 보여주는 것이고, 9b는 시혐편에서 18시간 동안 배양 후의 생균수를 보여주고, 도 9c 및 9d는 K. Pneumoniae에 대한 살균력을 보여주는 것으로, 9c는 대조편에 접종 즉시 회수한 생균수를 보여주는 것이고, 9d는 시험편에서 18 시간 동안 배양 후의 생균수를 보여준다.9a to 9d are photographs showing the sterilization test results for the sponge of Application Example 13 prepared with the sterilizing composition of Example 2 of the present invention. 9a and 9b show the bactericidal activity against S. aureus , 9a shows the viable count recovered immediately after inoculation on the control, 9b shows the viable count after incubation for 18 hours on the test specimen, Figures 9c and 9d Shows the bactericidal activity against K. Pneumoniae , 9c shows the viable count recovered immediately after inoculation to the control, 9d shows the viable count after incubation for 18 hours in the specimen.
본 발명은 살균용 조성물 및 이를 이용한 제품에 관한 것이다.The present invention relates to a sterilizing composition and a product using the same.
우리가 살고 있는 주위 환경에는 무수히 많은 균들이 분포하고 있으며, 이러한 균들은 번식력이 매우 강하기 때문에 적절한 온도와 습도가 주어지면 그 수가 기하급수적으로 증가하여 악취를 유발하고 쾌적한 생활환경을 저해할 뿐 아니라, 인간에게 각종 질병을 유발한다. 따라서 건강하고 쾌적한 생활을 위하여 주방용품, 욕실용품, 섬유류 등을 비롯하여 인간의 위생에 직, 간접적으로 영향을 미치는 각종 용품에서 세균을 제거하는 것이 매우 중요하다. 통상의 경우 균을 제거하는 방법은 다음과 같다.In the environment where we live, a myriad of bacteria are distributed, and because they are very fertile, their numbers increase exponentially when given the proper temperature and humidity, causing odors and impairing the pleasant living environment. It causes various diseases in humans. Therefore, it is very important to remove germs from various utensils that directly or indirectly affect human hygiene, including kitchen utensils, bathroom utensils, and textiles, for a healthy and pleasant life. In general, the method of removing bacteria is as follows.
첫 번째는 가장 일반적인 방법으로 고압 증기 멸균이 있다. 일반적으로 대부분의 세균이 열에 약하다는 점을 이용하여 약 121°C에서 15분 정도를 처리하여 세균을 사멸시키는 방법으로 주로 실험실 등에서 행해진다.The first is the most common method of autoclaving. In general, most bacteria are heat-sensitive, and are treated at about 121 ° C. for about 15 minutes to kill bacteria.
두 번째는 에틸렌 옥사이드 가스에 의한 방법으로, 주로 열에 약한 플라스틱 용기를 멸균하는데 많이 사용된다.The second method is by ethylene oxide gas, which is mainly used to sterilize plastic containers which are weak to heat.
세 번째는 자외선을 이용한 살균방법으로, 자외선은 일반적으로 260 내지 280 nm 부근의 파장에서 가장 살균력이 강하며 무균실이나 무균 작업대와 같이 주로 표면을 살균하기 위하여 많이 이용된다. The third is a sterilization method using ultraviolet rays, which are generally the most sterilizing at wavelengths of around 260 to 280 nm, and are widely used for sterilizing surfaces, such as clean rooms or aseptic working tables.
네 번째는 필터를 이용한 방법이다. 이 방법은 세균뿐만 아니라 액체 속에서 입자기 큰 물질을 제거하는데 이용되기도 한다. 세균의 일반적인 크기는 0.2 내지 2.0 ㎛로 세균의 크기보다 더 작은 구멍을 가진 매체를 통과하게 되면 구멍보다 크기가 큰 것들은 전부 걸리고 구멍 크기보다 작은 것들만 통과하게 되는 원리를 이용한 방법이다. Fourth is the method using a filter. This method is also used to remove particulate matter from liquids as well as bacteria. The general size of the bacteria is 0.2 to 2.0 μm, and if a medium having a hole smaller than the size of the bacteria is passed, all of the larger sized holes are caught and only smaller than the sized holes are used.
이 외에도, 염소, CaOCl2, H2O2, O3 및 석탄산 유도체인 페놀과 크레졸 등의 화학물질을 이용하기도 한다. 이 중에서 염소 화합물이 많이 이용되며, 오존은 기술 개발을 통하여 많이 활용되고 있다. In addition, chemicals such as chlorine, CaOCl 2 , H 2 O 2 , O 3 and phenol derivatives such as phenol and cresol are used. Among them, chlorine compounds are used a lot, and ozone is used a lot through technology development.
그러나 상기의 방법들 중 열에 의한 살균은 열에 약한 물질에는 적용할 수 없으며, 화학물질에 의한 살균은 인체에 대한 유해성 문제가 있다. 그러나 근본적으로 상기 방법들은 모두 일시적인 살균 효과만을 기대할 수 있을 뿐이며, 일상생활 중에서 지속적으로 번식하는 세균들을 계속적으로 제거할 수는 없다.However, heat sterilization of the above methods can not be applied to heat-sensitive materials, chemical sterilization is harmful to the human body. In essence, however, all of these methods can only expect a temporary bactericidal effect and cannot continuously remove bacteria that continually reproduce in daily life.
다른 측면에서, 세균의 부착을 방지하는 효과를 갖는 항균 제품들은 많이 출시되어 있지만, 제품의 지속적인 사용 중에 제품 자체에 번식하게 된 세균들을 살균하는 효과를 갖는 살균 제품은 선보여진 바가 없다. 특히, 주방이나 욕실과 같이 세균 번식에 유리한 온도와 습도를 갖는 환경에서 사용되는 제품들은 인간의 건강 및 위생에 밀접한 관련이 있으면서도 세균이 번식하기 쉬운 환경에 노출되어 있어 세균의 번식이 용이하며, 이러한 세균의 번식은 인간의 위생적이고 건강한 생활에 위해를 가하기 때문에, 항균의 효과를 넘어서 살균 효과를 갖는 제품이 절실히 요구되고 있다. 따라서 일시적인 살균이나 항균이 아니라 지속적으로 살균효과를 지속할 수 있다면 바람직하다 할 것이다. On the other hand, many antibacterial products having the effect of preventing the adhesion of bacteria are on the market, but no sterilizing products having the effect of disinfecting bacteria that have propagated in the product itself during the continuous use of the product have not been shown. In particular, products used in environments with favorable temperature and humidity, such as kitchens and bathrooms, are closely related to human health and hygiene, and are easily exposed to the environment where bacteria are easily reproduced. Since the propagation of bacteria causes harm to human's hygienic and healthy life, there is an urgent need for a product having a bactericidal effect beyond the antibacterial effect. Therefore, it would be desirable to be able to sustain the sterilization effect continuously rather than temporary sterilization or antibacterial.
특별히 섬유제품과 관련되어 액상형태로 제조되어 스프레이 등의 형태로 분무되어 섬유에 부착되어 살균력을 지속할 수 있다면 바람직하다 할 것이다.It is particularly desirable if it is made in the form of liquid in connection with the textile product and sprayed in the form of a spray or the like to adhere to the fibers to maintain sterilizing power.
본 발명은, 그러므로, 지속적인 살균 효과를 발휘하는 살균 조성물을 제공하는 것을 목적으로 한다. 또한 본 발명은 상기 살균 조성물을 각종 용기, 주방용품, 목욕용품, 정수기용 플라스틱 제품, 의류, 침구류, 문구 및 건축자재를 비롯한 각종 생활용품의 생산에 적용하여 자체 살균력을 갖는 제품을 생산하는 것을 목적으 로 한다. 나아가서, 본 발명은 섬유에 용이하게 적용할 수 있는 액상 살균 조성물을 제공하는 것을 목적으로 한다.It is therefore an object of the present invention to provide a bactericidal composition that exhibits a sustained bactericidal effect. In addition, the present invention is to apply the sterilizing composition to the production of various household goods, including various containers, kitchen utensils, bath products, plastic products for water purifiers, clothing, bedding, stationery and building materials to produce a product having its own sterilization power The purpose. Furthermore, an object of this invention is to provide the liquid sterilization composition which can be easily applied to a fiber.
본 발명에 따른 살균 조성물은 산화규소 (silicon dioxide, SiO2) 45 내지 55 중량부, 산화알루미늄 (aluminum oxide, Al2O3) 8 내지 12 중량부, 수산화칼륨 (potassium hydroxide, KOH) 3 내지 5 중량부, 산화마그네슘 (magnesium oxide, MgO) 3 내지 5 중량부, 붕산 (boric acid, H3BO3) 25 내지 30 중량부, 산화망간 (Manganese oxide, MnO) 3 내지 5 중량부, 산화제일철 (Ferrous oxide, FeO) 2 내지 3 중량부 및 사산화삼철 (Red oxide, Fe3O4) 2 내지 3 중량부를 포함한다. The bactericidal composition according to the present invention is 45 to 55 parts by weight of silicon dioxide (SiO 2 ), 8 to 12 parts by weight of aluminum oxide (aluminum oxide, Al 2 O 3 ), potassium hydroxide (KOH) 3 to 5 Parts by weight, magnesium oxide (MgO) 3 to 5 parts by weight, boric acid (H 3 BO 3 ) 25 to 30 parts by weight, manganese oxide (MnO) 3 to 5 parts by weight, ferrous oxide ( 2 to 3 parts by weight of ferrous oxide (FeO) and 2 to 3 parts by weight of trioxide (red oxide, Fe 3 O 4 ).
본 발명자들은 상기와 같은 성분들을 상기의 조성으로 교반, 혼합한 후, 1350 내지 1550°C의 유리 용해로에 투입하여 19 내지 21 시간 동안 용융시키고, 얻어진 용융 혼합물을 냉각수에 투입하여 분해된 유리상의 입자를 나노 크기로 미세하게 분쇄하여 분말화하여, 뛰어난 살균 효과를 갖는 분말 조성물을 제조하였으며, 이를 '바이오타이트'라 명명하였다.The present inventors stirred and mixed the above components in the above composition, and then added to a glass melting furnace at 1350 to 1550 ° C. to melt for 19 to 21 hours, and the obtained molten mixture was added to cooling water to decompose glassy particles. Was finely pulverized to a nano size and powdered to prepare a powder composition having an excellent bactericidal effect, which was named 'biotite'.
본 발명의 살균 조성물 바이오타이트는 한국화학시험연구원의 검사결과, 1 % 농도로서, 대장균에 대하여 10 분 후 60.0 %, 30분 후 87.8 %, 포도상 구균에 대하여 10 분 후 51.7 %, 30 분 후 90.5%의 살균효과를 나타내는 것으로 확인되었다. 이러한 살균 효과는 상기 바이오타이트가 방출하는 원적외선에 의한 것으로 추측되며, 본 발명의 바이오타이트는 일반적인 산화규소가 열에 의하여 방출하는 원적외선과 달리 상온에서도 지속적으로 원적외선을 방출시킬 수 있다. The bactericidal composition biotite of the present invention has a concentration of 1% as a test result of the Korea Testing Institute, 60.0% after 10 minutes for E. coli, 87.8% after 30 minutes, 51.7% after 10 minutes for Staphylococcus, 90.5 after 30 minutes It was confirmed to exhibit a bactericidal effect of%. The bactericidal effect is assumed to be due to the far infrared rays emitted by the biotite, and the biotite of the present invention can continuously emit far infrared rays at room temperature, unlike the far infrared rays which are normally emitted by silicon oxide by heat.
또한, 상기 살균 조성물은 평균 입경 1 내지 100 nm의 미세입자 형태이므로, 합성수지에 혼합시 균일하게 분산되어 적용된 제품에서 균일한 살균효과를 나타낼 수 있다. 이러한 원적외선 방출 효과 및 살균 효과로 인하여 상기 바이오타이트는 화장용 조성물 및 외용 항생제, 무좀약 등의 의약 조성물로서도 사용 가능하다. 상기 살균용 조성물은 각종 박테리아 및 효모, 곰팡이, 조류 등의 각종 진균류에 대해서 살균효과를 갖는다. In addition, since the sterilizing composition is in the form of microparticles having an average particle diameter of 1 to 100 nm, it may be uniformly dispersed when mixed in a synthetic resin to exhibit a uniform sterilizing effect in the applied product. Due to the far-infrared emission effect and bactericidal effect, the biotite can be used as a pharmaceutical composition such as cosmetic compositions, antibiotics for external use, and athlete's foot medicine. The bactericidal composition has a bactericidal effect against various fungi such as bacteria and yeast, mold, algae and the like.
또한, 본 발명의 살균 조성물은 상기 바이오타이트에 은 이온 (Ag+), 아연 이온 (Zn2+) 및 백금족 원소로 구성된 군 중에서 선택된 한 가지 이상의 물질을 추가적으로 포함할 수 있다. In addition, the bactericidal composition of the present invention may further include at least one material selected from the group consisting of silver ions (Ag + ), zinc ions (Zn 2+ ), and platinum group elements.
이 때, 바이오타이트, 은 이온, 아연 이온 및 백금족 원소의 함량비는 중량비로 1 : 0.01 - 4 : 0.01 - 4 : 0.001 - 0.5 (바이오타이트 중량:은 이온 중량:아연 이온 중량: 백금족 원소 중량)인 것이 바람직하다. At this time, the content ratio of biotite, silver ions, zinc ions, and platinum group elements is 1: 0.01 to 4: 0.01 to 4: 0.001 to 0.5 (biotite weight: silver ion weight: zinc ion weight: platinum group element weight). Is preferably.
상기 백금족 원소는 루테늄(Ru), 로듐(Rh), 팔라듐(Pd), 오스뮴(Os), 이리듐(Ir) 및 백금(Pt)으로 구성되는 군 중에서 선택될 수 있으며, 특히, 팔라듐 또는 백금이 바람직하다. 상기 조성범위는 반복 실험 결과 최상의 살균 효과를 얻을 수 있는 범위를 정한 것이다. 이 때, 상기 백금족 원소들은 이온화 되어 있는 액체 상태로 사용한다.The platinum group element may be selected from the group consisting of ruthenium (Ru), rhodium (Rh), palladium (Pd), osmium (Os), iridium (Ir) and platinum (Pt), in particular palladium or platinum Do. The composition range is defined to obtain the best sterilization effect as a result of repeated experiments. At this time, the platinum group elements are used in an ionized liquid state.
일반적으로, 지구상에 존재하는 모든 금속은 살균력이 있으며, 그 중에서도 가장 뛰어난 살균력을 지닌 것으로 알려진 원소는 백금족 원소들이다. 백금 원소는 대표적인 전이원소로 모두 화유원소에 속하며 산출량은 적으나 장식용 귀금속으로 아름다운 은백색이며 (분말은 흑색) 녹는점이 높고 비중도 크다. 또한, 화학적 형질은 비활성이며, 산, 알칼리에 잘 침식되지 않는다. 루테늄과 오스뮴, 로듐과 이리듐, 팔라듐과 백금의 성질이 특히 비슷하며, 각종 유기화합물의 반응에 촉매 작용을 하는 화합물로서 알려져 있다. 한편, 은(Ag+) 또는 아연 (Zn2+) 등과 같은 금속이온들 역시 살균성 (항균성) 또는 살조성을 가지고 있다는 것이 알려져 있고, 담수성 조류에 대한 은의 살균, 방조작용에 대하여 일본 등 선진국에서 많은 연구가 진행되고 있다. 이들 은 이온 또는 아연 이온은 인체에 대한 독성이 거의 없기 때문에 염소 또는 기타 독성이 있는 살미생물제 대용으로 사용 가치가 높을 것으로 기대되고 있다.In general, all metals present on Earth are bactericidal, and the most known of them are the platinum group elements. Platinum element is a representative transition element, all belong to petroleum element, and its output is small, but it is a beautiful silver white (powder is black) as decorative precious metal, and its melting point is high and its specific gravity is high. In addition, chemical traits are inert and do not erode well to acids and alkalis. Ruthenium and osmium, rhodium and iridium, palladium and platinum are particularly similar in nature and are known as compounds that catalyze the reaction of various organic compounds. On the other hand, metal ions such as silver (Ag + ) or zinc (Zn 2+ ) are also known to have bactericidal (antimicrobial) or algae. Research is ongoing. These silver ions or zinc ions are expected to be of high value as a substitute for chlorine or other toxic microbicides because they have little toxicity to humans.
따라서 우수한 살균력을 갖는 바이오타이트에 은 이온(Ag+), 아연 이온 (Zn2+) 및 백금족 원소로 구성된 군 중에서 선택된 한 가지 이상의 물질을 추가적으로 포함하는 살균 조성물은 보다 증진된 살균 효과를 갖는다 (표 2 참조). Therefore, the sterilizing composition further comprising one or more substances selected from the group consisting of silver ions (Ag + ), zinc ions (Zn 2+ ) and platinum group elements in the biotite having good bactericidal power has a more enhanced bactericidal effect (Table 2).
또한, 본 발명의 살균 조성물은 상기 바이오타이트에 폴리헥사메틸렌구아니딘 포스페이트를 추가적으로 포함할 수 있다. 이 때, 바이오타이트와 폴리헥사메틸렌구아니딘 포스페이트의 함량비는 중량비로 1 : 0.01 - 2 (바이오타이트 중량 : 폴리헥사메틸렌구아니딘 포스페이트 중량)인 것이 바람직하다. In addition, the bactericidal composition of the present invention may further include polyhexamethyleneguanidine phosphate in the biotite. At this time, it is preferable that the content ratio of biotite and polyhexamethyleneguanidine phosphate is 1: 0.01-2 (biotite weight: weight of polyhexamethyleneguanidine phosphate) by weight ratio.
폴리헥사메틸렌구아니딘 포스페이트는 박테리아, 효모, 곰팡이 등의 세균에 대하여 살균효과를 가지며 인체에 거의 독성이 없는 물질로서, 바이오타이트에 폴 리헥사메틸렌구아니딘 포스페이트를 추가적으로 포함하는 살균 조성물은 보다 증진된 살균효과를 나타낸다. Polyhexamethyleneguanidine phosphate has a bactericidal effect against bacteria, yeasts, molds, etc., and is almost nontoxic to humans. Indicates.
또한, 본 발명의 살균 조성물은 상기 바이오타이트에 은 이온(Ag+), 아연 이온 (Zn2+) 및 백금족 원소로 구성된 군 중에서 선택된 한 가지 이상의 물질 및 폴리헥사메틸렌구아니딘 포스페이트를 추가적으로 포함할 수 있다. 이 때, 각 성분의 함량비는 중량비로 1 : 0.01 - 4 : 0.01 - 4 : 0.001 - 0.5 : 0.01 - 2 (바이오타이트 중량:은 이온 중량:아연 이온 중량:백금족 원소 중량:폴리헥사메틸렌구아니딘 포스페이트 중량)인 것이 바람직하다.In addition, the bactericidal composition of the present invention may further include polyhexamethyleneguanidine phosphate and at least one material selected from the group consisting of silver ions (Ag + ), zinc ions (Zn 2+ ) and platinum group elements in the biotite. . At this time, the content ratio of each component is 1: 0.01-4: 0.01-4: 0.001-0.5: 0.01-2 (Biotite weight: Silver ion weight: Zinc ion weight: Platinum group element weight: Polyhexamethyleneguanidine phosphate Weight).
또한, 본 발명은 상기 살균 조성물을 합성수지에 혼합하여 얻어지는 혼합물을 용융 및 압출성형 하거나, 상기 합성수지와의 혼합물로 처리하여 얻어진 살균 제품을 제공한다. The present invention also provides a sterilized product obtained by melting and extruding a mixture obtained by mixing the sterilizing composition with a synthetic resin or by treating with a mixture with the synthetic resin.
이 때, 본 발명의 살균 조성물의 함량은 합성수지와 혼합물 전체 중량에 대하여 0.01 내지 1 중량%로 하는 것이 바람직하다. At this time, the content of the sterilizing composition of the present invention is preferably 0.01 to 1% by weight based on the total weight of the synthetic resin and the mixture.
본 발명의 살균 조성물의 함량이 0.01 중량% 이하인 경우 원하는 살균 효과를 얻기 어렵고, 1 중량% 이상인 경우 제조되는 합성수지 제품의 물성에 영향을 미칠 수 있기 때문에 바람직하지 않다. If the content of the bactericidal composition of the present invention is less than 0.01% by weight, it is difficult to obtain the desired sterilization effect, and if it is 1% by weight or more, it is not preferable because it may affect the physical properties of the synthetic resin product to be produced.
상기 합성수지는, 예컨대, 폴리에틸렌 (polyethylene, PE) 수지, 폴리염화비닐 (polyvinyl chloride, PVC) 수지, 폴리프로필렌 (polypropylene, PP) 수지, 폴리우레탄 수지 (polyurethane, PU), 아크릴 수지 (acrylic resin), ABS (acrylonitrile butadiene styrene) 수지, 아세트산비닐 수지, 테프론 수지, 폴리카보네이트 및 프탈산 수지를 포함한다. The synthetic resin is, for example, polyethylene (PE) resin, polyvinyl chloride (PVC) resin, polypropylene (PP) resin, polyurethane resin (polyurethane, PU), acrylic resin (acrylic resin), ABS (acrylonitrile butadiene styrene) resins, vinyl acetate resins, Teflon resins, polycarbonates and phthalic acid resins.
예컨대, 본 발명의 살균 조성물이 0.01 내지 1 중량% 포함되어 있는 합성수지와 살균조성물의 혼합물을 용융시키고 성형하여 우수한 살균력을 갖는 합성수지 소재의 제품을 얻을 수 있다. For example, a product of a synthetic resin material having excellent sterilizing power may be obtained by melting and molding a mixture of a synthetic resin and a sterilizing composition containing 0.01 to 1% by weight of the sterilizing composition of the present invention.
또한, 본 발명의 살균 조성물이 상기 중량% 범위 내에서 에멀젼 상태의 합성수지 (예컨대, 아크릴 수지 및 아세트산비닐 수지)에 혼합되어 있는 혼합물을 적절한 용매, 예컨대, 아세톤 및 크실렌과 같은 케톤류 또는 부틸알코올과 같은 알코올류로 희석하여 제조된 제품을 함침시키거나 표면처리하여 우수한 살균력이 있는 각종 제품을 얻을 수 있다. In addition, the mixture in which the bactericidal composition of the present invention is mixed with the synthetic resin (eg, acrylic resin and vinyl acetate resin) in an emulsion state within the above weight% range may be mixed with a suitable solvent such as ketones such as acetone and xylene or butyl alcohol. Impregnated or surface treated products prepared by diluting with alcohols can be obtained a variety of products having excellent sterilization power.
본 발명의 살균 조성물은 각종 주방용품, 욕실용품, 건축자재, 가전제품, 위생용품, 섬유류, 포장재, 화장품, 문구류, 완구류, 농원예용 포장재, 정수기용 각종 플라스틱 제품 등과 같은 다양한 용품에 적용될 수 있다. 더욱 상세하게, 상기 제품들은 도마, 치약용기, 칫솔갑, 화장품 용기, 쓰레기통, 대야, 플라스틱제 컵 및 병, 쌀통, 김치통, 각종 식품 저장용기, 바가지, 양념통, 물통, 음료용기, 부직포, 섬유, 행주, 걸레, 수세미, 이불 커버, 침대 커버, 식탁 매트, 변기 시트 커버, 불고기판, 기저귀, 생리대, 마스크, 과일 포장지, 꽃 포장지, 벽지, 장판, 정수기 자동 멈춤장치를 포함하는 일체의 정수기용 프라스틱 제품 등일 수 있다. 그러나, 본 발명의 살균 조성물은, 상기 예시된 제품들 외에도, 합성수지에 의하여 제작될 수 있거나, 이에 의하여 코팅될 수 있는 모든 제품에 적용 가능하다. The sterilizing composition of the present invention can be applied to various articles such as various kitchen utensils, bathroom articles, building materials, home appliances, sanitary articles, fibers, packaging materials, cosmetics, stationery, toys, agricultural horticultural packaging materials, various plastic products for water purifiers, and the like. More specifically, the products include cutting boards, toothpaste containers, toothbrush packs, cosmetic containers, waste bins, basins, plastic cups and bottles, rice containers, kimchi containers, various food storage containers, gourds, seasoning containers, water bottles, beverage containers, non-woven fabrics, Fiber, cloth, rag, loofah, duvet cover, bed cover, dining table mat, toilet seat cover, barbecue plate, diaper, sanitary napkin, mask, fruit wrapper, flower wrapper, wallpaper, blanket, water purifier All water purifiers including automatic stop Plastic products, and the like. However, the bactericidal composition of the present invention, in addition to the products exemplified above, is applicable to all products that can be made or coated by a synthetic resin.
또한 본 발명은 반영구적이고 우수한 살균 효과를 갖는 액상 살균 조성물을 제공한다. 이러한 본 발명에 따른 액상 살균 조성물은 수용성 (oil-in-water type) 폴리머 에멀젼 내에 산화규소 (silicon dioxide, SiO2) 45 내지 55 중량부, 산화알루미늄 (aluminum oxide, Al2O3) 8 내지 12 중량부, 수산화칼륨 (potassium hydroxide, KOH) 3 내지 5 중량부, 산화마그네슘 (magnesium oxide, MgO) 3 내지 5 중량부, 붕산 (boric acid, H3BO3) 25 내지 30 중량부, 산화망간 (manganese oxide, MnO) 3 내지 5 중량부, 산화제일철 (ferrous oxide, FeO) 2 내지 3 중량부 및 사산화삼철 (Red oxide, Fe3O4) 2 내지 3 중량부로 이루어진 살균 분말을 상기 수용성 폴리머 에멀젼 중량을 기준으로 0.1 내지 5 중량%의 양으로 포함한다. The present invention also provides a liquid sterilization composition having a semi-permanent and excellent sterilization effect. The liquid sterilizing composition according to the present invention is 45 to 55 parts by weight of silicon dioxide (SiO 2 ), aluminum oxide (aluminum oxide, Al 2 O 3 ) in an oil-in-water type polymer emulsion. Parts by weight, potassium hydroxide (KOH) 3-5 parts by weight, magnesium oxide (MgO) 3-5 parts by weight, boric acid (H 3 BO 3 ) 25-30 parts by weight, manganese oxide ( Manganese oxide (MnO) 3 to 5 parts by weight, ferrous oxide (FeO) 2 to 3 parts by weight and ferric tetraoxide (Red oxide, Fe 3 O 4 ) 2 to 3 parts by weight of the sterilized powder weight of the water-soluble polymer emulsion It is included in the amount of 0.1 to 5% by weight based on.
상기 액상 살균 조성물은 물에 희석하여 분사될 수 있는 액상 형태로 사용가능하기 때문에, 섬유에 분사하여 적용함으로써 손쉽게 섬유의 살균을 수행할 수 있다. Since the liquid sterilization composition can be used in a liquid form that can be diluted and sprayed in water, the sterilization of the fiber can be easily performed by spraying and applying the fiber.
상기 수용성 폴리머 에멀젼은 고형분 함량이 약 35 내지 45 중량%인 것으로, 폴리우레탄, 에폭시, 아클릴, 아세트산비닐 및 불포화 폴리에스테르로 이루어진 군 중에서 선택된 폴리머를 사용하여 얻을 수 있다. The water-soluble polymer emulsion has a solid content of about 35 to 45% by weight, and can be obtained using a polymer selected from the group consisting of polyurethane, epoxy, acyl, vinyl acetate and unsaturated polyester.
또한, 상기 수용성 폴리머 에멀젼은, 에멀젼 제조를 용이하게 하기 위하여, 유화제 및/또는 계면활성제 및/또는 유기용매를 추가적으로 포함할 수 있으며, 폴리머와 살균 분말의 결합 및 섬유에의 흡착을 보다 강력하게 하기 위하여 결합제 및/또는 증점제를 추가적으로 포함할 수 있다. In addition, the water-soluble polymer emulsion may further include an emulsifier and / or a surfactant and / or an organic solvent in order to facilitate the preparation of the emulsion, to make the binding of the polymer and the sterilizing powder and adsorption to the fiber more powerful. And may further include a binder and / or a thickener.
이 때, 상기 유화제로서 피마자유 계열을 3 내지 15 중량%의 양으로, 상기 계면활성제로서 통상적으로 사용되는 계면 활성제를 3 내지 15 중량%의 양으로, 상기 유기용매로서, 예컨대, MEK (Methyl ethyl ketone) 등과 같은 유기용매를 10 내지 15 중량%의 양으로, 상기 증점제로서, 예컨대, 메틸셀룰로오스 등을 3 내지 5 중량%의 양으로, 상기 결합제로서 통상적으로 사용되는 유화제로 이루어진 군 중에서 선택된 것을 1 내지 3 중량%의 양으로 포함할 수 있다.At this time, castor oil based on the amount of castor oil in the amount of 3 to 15% by weight, and surfactants commonly used as the surfactant in an amount of 3 to 15% by weight, as the organic solvent, for example, MEK (Methyl ethyl ketone) in an amount of 10 to 15% by weight of the organic solvent, the thickener, such as methylcellulose in an amount of 3 to 5% by weight, selected from the group consisting of emulsifiers commonly used as the
본 발명에 따른 액상 살균 조성물은 물로 희석하여 섬유에 분사하여 적용할 수 있다. 보다 상세하게, 본 발명의 조성물을 물로 약 5 배 내지 10 배 희석한 희석액을 섬유에 분사하고 건조시키면, 살균 조성물 내의 폴리머와 살균 분말이 결합된 고형성분만 남아 대부분의 균에 대하여 99.9 %의 높은 살균력을 나타낸다. (표 6 참조). 또한, 용매가 증발되면서 남게 되는 고형성분은 불용성이고 섬유 조직에 강하게 결합하여 흡착하므로, 세탁 중에 용해되거나 세탁 후에 제거되지 않고, 반영구적으로, 99.5% 이상의 우수한 살균 효과를 나타낸다. (표 7 참조).Liquid sterilization composition according to the present invention can be applied by diluting with water and spraying on the fiber. More specifically, when a diluent diluted about 5 to 10 times with water of the composition of the present invention is sprayed onto a fiber and dried, only a solid component combined with the polymer and the sterilizing powder in the sterilizing composition remains 99.9% higher for most bacteria. It shows bactericidal power. (See Table 6). In addition, since the solid component remaining as the solvent evaporates is insoluble and strongly binds to and adsorbs the fibrous tissue, it is not dissolved during washing or removed after washing, and semipermanently shows excellent sterilizing effect of 99.5% or more. (See Table 7).
또한, 본 발명에 따른 액상 살균 조성물은 상기와 같이 희석물 형태로 분사되어 사용될 수 있으므로, 번거로운 과정이나 별도의 기구를 사용하지 아니하고도, 단지 분무기에 넣어 섬유에 분사하는 매우 간단하고 용이한 과정에 의하여 섬유를 살균할 수 있다는 장점이 있다. In addition, since the liquid sterilization composition according to the present invention can be used in the form of a dilution as described above, it can be used in a very simple and easy process of spraying the fiber into a sprayer, without using a cumbersome process or a separate device. There is an advantage that can sterilize the fiber.
본 발명의 액상 살균 조성물은 면, 생사, 양모 등을 포함하는 모든 동물성 또는 식물성 천연 섬유, 나일론, 폴리에스테르, 아크릴로니트릴, 폴리비닐알코올, 폴리염화비닐, 폴리염화비닐리덴, 폴리프로필렌, 폴리우레탄과 같은 합성섬유 또는 천연섬유와 합성섬유의 혼방을 포함하는 모든 섬유에 적용가능하며, 평직, 능직, 수자직 등 본 발명의 살균 조성물의 고형성분이 흡착할 수 있는 구조를 갖는 모든 섬유에 사용 가능하다. Liquid sterilizing compositions of the present invention are all animal or vegetable natural fibers including cotton, raw silk, wool, etc., nylon, polyester, acrylonitrile, polyvinyl alcohol, polyvinyl chloride, polyvinylidene chloride, polypropylene, polyurethane Applicable to all fibers, including synthetic fibers or blends of natural fibers and synthetic fibers such as, and can be used for all fibers having a structure that can be adsorbed solid components of the bactericidal composition of the present invention, such as plain weave, twill weave, satin weave. .
또한, 본 발명의 액상 살균 조성물은 상기와 같이 섬유에 직접 분사하는 것 외에도, 세균이 번식하거나 또는 불괘한 냄새가 나는 모든 부위에 분사하여 살균 효과와 악취 제거효과를 얻을 수 있다. 본 발명의 조성물이 적용될 수 있는 구체적인 예는 다음과 같다:In addition, the liquid sterilizing composition of the present invention, in addition to spraying directly on the fiber as described above, it can be sprayed to all the areas where the bacteria propagate or unpleasant smell can be obtained sterilization effect and odor removal effect. Specific examples to which the composition of the present invention may be applied are as follows:
에어컨 (공기 흡입 내부 필터); 행주, 수세미, 수저통 등과 같은 주방용품 및 주방의 각종 냄새 발생 부분; 손수건; 신발 또는 신발 깔창; 내의류; 생리 용품; 쇼파, 침대 매트리스, 방석; 실내 냄새 발생 부분; 담요, 이불 등의 침구류; 마스크; 양말; 베개; 카페트; 신발장; 곰팡이가 서식할 수 있는 모든 장소; 냉장고, 냉각판; 이불장; 이불장 뒤; 욕실; 걸레; 습기찬 곳; 장난감; 기저귀; 자동차 시트 및 바닥; 컴퓨터 자판기; 전화 수화기; 식탁보; 씽크대 내부 및 외부; 유리창틀 (결로 현상 있는 곳); 수건; 반지하실 또는 지하실; 쓰레기통; 공기청정기 필터; 진공 청소기 내부 필터; 고무장갑 내부 등. Air conditioner (air intake internal filter); Kitchen utensils such as dish towels, scrubbers, cutlery and the like, and various odor generating parts of the kitchen; handkerchief; Shoes or shoe insoles; underclothing; Menstrual supplies; Sofa, bed mattress, cushion; Indoor odor generating part; Bedding such as blankets and duvets; Mask; Amount - say; Pillow; carpet; shoe closet; All places where fungi may live; Refrigerator, cold plate; Quilt; Behind the sheet; bathroom; Mop; Damp place; toy; diaper; Car seats and floors; Computer vending machines; Telephone handset; tablecloth; Inside and outside the sink; Glass window frames (with condensation); Towel; Ring cellar or cellar; trash can; Air purifier filters; Vacuum cleaner internal filter; Rubber gloves inside etc.
이제, 본 발명을 실시예, 실험예 및 적용예에 의하여 더욱 상세히 설명할 것이다. 그러나, 이들은 단지 본 발명을 예시하기 위한 것이며, 본 발명의 범위가 이들 실시예, 실험예 및 적용예들에 의하여 한정되는 것은 아니다.Now, the present invention will be described in more detail by Examples, Experimental Examples and Application Examples. However, these are merely for illustrating the present invention, and the scope of the present invention is not limited by these examples, experimental examples, and applications.
실시예 1: 살균 조성물의 제조 (1) - 바이오타이트Example 1 Preparation of Bactericidal Compositions (1) -Biotite
산화규소 45 g, 산화알루미늄 8 g, 수산화칼륨 3 g, 산화마그네슘 3 g, 붕산 25 g, 산화망간 3 g, 산화제일철 2 g 및 사산화삼철 2 g을 배합용기에 넣고 33 rpm의 교반기에 의하여 0.5 내지 1 시간 동안 교반하여 혼합한 후, 1350 내지 1550 ??의 유리용해로에 투입하여 19 내지 21 시간 동안 용융시키고, 이 용융혼합물을 냉각수에 투입하여 분해된 유리상의 입자를 볼밀링하여 나노크기로 미세분쇄하여 분말상의 바이오타이트를 얻었다. 도 1은 이러한 바이오타이트를 보인다.45 g of silicon oxide, 8 g of aluminum oxide, 3 g of potassium hydroxide, 3 g of magnesium oxide, 25 g of boric acid, 3 g of manganese oxide, 2 g of ferric oxide, and 2 g of ferric tetraoxide were placed in a mixing vessel and 0.5 rpm with a stirrer at 33 rpm. After mixing for 1 to 1 hour, the mixture is added to a glass melting furnace of 1350 to 1550 ° C. and melted for 19 to 21 hours. The molten mixture is added to cooling water to ball mill the decomposed glassy particles to a nano size. Grinding gave a powdered biotite. 1 shows this biotite.
시험예 1: 살균 조성물 (1) (바이오타이트)의 살균 시험Test Example 1: Sterilization Test of Bactericidal Composition (1) (Biotite)
실험기기Experiment apparatus
클린 벤취 (Clean Bench, 수공양행, 한국)Clean Bench (Shandan, Korea)
콜로니 카운터 (Colony Counter, 덕우과학, 한국)Colony Counter (Deokwoo Science, Korea)
인큐베이터 (Memmert, 독일)Incubators (Memmert, Germany)
시험균주Test strain
대장균 (Escherichia coli, ATCC 25922) Escherichia coli (ATCC 25922)
황색 포도상구균 (Staphylococcus aureus, ATCC 25923)Staphylococcus aureus (Staphylococcus aureus, ATCC 25923)
위 시험균주를 액체배지 (Brain Heart Infusion Broth)에 진탕 배양시킨 후, 세균을 희석하여 초기 접종균수가 1 ~ 9 x 105 cfu/ml가 되도록 조정하여 시험에 사용하였다. 상기 배양한 세균을 멸균된 생리식염수 100 ml에 각각 접종한 후, 초기 세균수를 측정하였다. 상기 세균을 포함하는 생리식염수 100 ml에 실시예 1에서 얻어진 살균 조성물 바이오타이트를 1 % 농도가 되도록 넣고 10 분 및 30 분 후 세균수를 측정하였다. 세균수는 배지상의 균수에 희석배수를 곱하여 산출하였다.The test strain was shaken and cultured in a liquid heart (Brain Heart Infusion Broth), and the bacteria were diluted to adjust the initial inoculated bacteria to 1 to 9 x 10 5 cfu / ml and used for the test. The cultured bacteria were inoculated in 100 ml of sterile physiological saline, and the initial bacterial counts were measured. The bactericidal composition biotite obtained in Example 1 was added to 100 ml of physiological saline containing the bacteria so as to have a concentration of 1%, and the number of bacteria was measured after 10 minutes and 30 minutes. The number of bacteria was calculated by multiplying the number of bacteria on the medium by the dilution factor.
상기의 시험 결과를 도 3a 내지 3c, 도4a 내지 4c 및 아래의 표 1에 나타내었다. 본 시험은 한국화학시험연구원에 의하여 수행되었으며, 하기의 표 1은 한국화학시험연구원에서 평가한 결과이다.The test results are shown in FIGS. 3A to 3C, 4A to 4C, and Table 1 below. This test was performed by the Korea Testing Institute, Table 1 below is the result of the evaluation by the Korea Testing Institute.
단위 : CFU/mlUnit: CFU / ml
* : 감소율 (%) = {(초기 세균수-일정시간 후 세균수)/초기 세균수} x 100*: Reduction rate (%) = {(initial number of bacteria-number of bacteria after a certain time) / initial number of bacteria} x 100
상기 결과로부터 알 수 있는 바와 같이, 본 발명의 살균 조성물 바이오타이트는 1 %의 농도로도 대장균에 대하여 10 분 후 60.0 %, 30 분후, 87.8%, 포도상구균에 대하여 10 분 후 51.7 %, 30 분 후 90.5 %의 우수한 살균효과를 나타내었다. 이러한 결과로 미루어 보아 바이오타이트의 사용 농도를 증가시키거나 살균 시간을 늘린다면 100 %에 가까운 살균 효과를 얻을 수 있을 것으로 기대된다.As can be seen from the above results, the bactericidal composition biotite of the present invention is 60.0% after 10 minutes for E. coli, 30 minutes, 87.8% after 10 minutes for E. coli and 51.7% for 30 minutes even at a concentration of 1%. After 90.5% showed an excellent bactericidal effect. These results suggest that increasing the concentration of biotite or increasing the sterilization time can achieve a sterilization effect of nearly 100%.
실시예 2: 살균 조성물의 제조 (2)Example 2: Preparation of Bactericidal Compositions (2)
상기 실시예 1에서 제조한 바이오타이트 10 g에 은 이온 15 g, 아연 이온 15 g, 팔라듐 3 g 및 폴리헥사메틸렌구아니딘 포스페이트 (SKYBIO 1100, SK Chemicals Co., Ltd., 한국) 15 g을 첨가하고, 혼합하여 도 2에 나타낸 바와 같은 본 발명의 살균 조성물을 제조하였다.15 g of silver ions, 15 g of zinc ions, 3 g of palladium and 15 g of polyhexamethyleneguanidine phosphate (SKYBIO 1100, SK Chemicals Co., Ltd., Korea) were added to 10 g of the biotite prepared in Example 1, And mixed to prepare a bactericidal composition of the present invention as shown in FIG. 2.
시험예 2: 살균 조성물 (2)의 살균 시험Test Example 2: Sterilization Test of Sterilization Composition (2)
실험기기Experiment apparatus
클린 벤취 (Clean Bench, 수공양행, 한국)Clean Bench (Shandan, Korea)
콜로니 카운터 (Colony Counter, 덕우과학, 한국)Colony Counter (Deokwoo Science, Korea)
인큐베이터 (Memmert, 독일)Incubators (Memmert, Germany)
시험균주Test strain
대장균 (Escherichia coli, ATCC 25922) Escherichia coli (ATCC 25922)
황색 포도상구균 (Staphylococcus aureus, ATCC 25923)Staphylococcus aureus (Staphylococcus aureus, ATCC 25923)
위 시험균주를 액체배지 (Brain Heart Infusion Broth)에 진탕 배양시킨 후, 세균을 희석하여 초기 접종균수가 1 ~ 9 x 105 cfu/ml가 되도록 조정하여 시험에 사용하였다. 상기 배양한 세균을 멸균된 생리식염수 100 ml에 각각 접종한 후, 초기 세균수를 측정하였다. 상기 세균을 포함하는 생리식염수 100 ml에 실시예 2에서 얻어진 살균 조성물을 1 % 및 2 % 농도가 되도록 각각 넣고 10 분 및 30 분 후 각각의 경우에서의 세균수를 측정하였다. 세균수는 배지상의 균수에 희석배수를 곱하여 산출하였다.The test strain was shaken and cultured in a liquid heart (Brain Heart Infusion Broth), and the bacteria were diluted to adjust the initial inoculated bacteria to 1 to 9 x 10 5 cfu / ml and used for the test. The cultured bacteria were inoculated in 100 ml of sterile physiological saline, and the initial bacterial counts were measured. The germicidal composition obtained in Example 2 was added to 100 ml of physiological saline containing the bacteria so as to have a concentration of 1% and 2%, respectively, and the number of bacteria in each case was measured after 10 minutes and 30 minutes. The number of bacteria was calculated by multiplying the number of bacteria on the medium by the dilution factor.
상기의 시험 결과를 도 5a 내지 5c, 도 6a 내지 6c, 도 7a 내지 7c, 도 8a 내지 8c 및 아래의 표 2에 나타내었다. 본 시험은 한국화학시험연구원에 의하여 수행되었으며, 하기의 표 2는 한국화학시험연구원에서 평가한 결과이다.The test results are shown in FIGS. 5A to 5C, 6A to 6C, 7A to 7C, 8A to 8C, and Table 2 below. This test was carried out by the Korea Testing Institute, Table 2 below is the result of the evaluation by the Korea Testing Institute.
단위 : CFU/mlUnit: CFU / ml
* : 감소율 (%) = {(초기 세균수-일정시간 후 세균수)/초기 세균수} x 100*: Reduction rate (%) = {(initial number of bacteria-number of bacteria after a certain time) / initial number of bacteria} x 100
상기 결과로부터 알 수 있는 바와 같이, 본 발명의 살균 조성물 (2)는 대장균에 대하여 1 %에서 10 분 후 49.0 %의 살균 효과를 보였으나, 30분 후 100%의 살균효과를 나타냈고, 2 %에서는 10 분 후 이미 100 %의 살균효과를 나타내었으며, 포도상구균에 대해서는 1 % 및 2 %에서 모두 10 분 후에 100 %의 살균효과를 나타내었다.As can be seen from the above results, the bactericidal composition (2) of the present invention exhibited a bactericidal effect of 19.0 to 49.0% after 10 minutes against E. coli, but showed a bactericidal effect of 100% after 30 minutes, and 2% In 10 minutes, the bactericidal effect was already 100%, and for Staphylococcus aureus, 1% and 2% showed 100% bactericidal effect after 10 minutes.
적용예 1: 본 발명의 살균 조성물을 이용한 도마의 제조Application Example 1 Preparation of Cutting Board Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 폴리에틸렌 수지 99.5 중량부와 혼합하여 용융 및 성형작업하여 도마를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of polyethylene resin to prepare a cutting board by melting and molding.
안전성 시험Safety test
상기와 같이 본 발명의 살균 조성물을 사용하여 도마와 같은 식품 조리용 기구를 제작하는 경우 안전성 확인을 위하여, 상기와 같이 제작된 도마를 국가공인시험기관인 한국생활환경시험연구원에 의뢰하여 식품공전 제6의 기구 및 용기·포장의 기준 및 규격 중 합성수지제 1-2 PE/PP에 의한 시험을 실시한 결과 하기 표 3에 나타낸 바와 같이 식품 조리용으로 사용하기에 적합함을 확인하였다.When manufacturing a food cooking utensil such as a cutting board using the bactericidal composition of the present invention as described above, the cutting board manufactured as described above was commissioned by the Korea Living Environment Testing Institute, a national accredited testing institution, for food safety. As a result of the test by synthetic resin 1-2 PE / PP among the standards and specifications of utensils, containers, and packaging, it was confirmed that it is suitable for use for food cooking as shown in Table 3 below.
살균력 시험Bactericidal test
상기와 같이 제작된 도마는 자체의 살균력 이외에 상기 도마에 접촉하여 놓여있는 물건에 대해서도 우수한 살균력을 가지는 것을 확인하기 위하여, 상기와 같이 제작된 도마 표면 (50 mm x 60 mm)에 전배양한 균액을 일정량 접종한 후, 멸균 면봉을 이용하여 접종 즉시 회수하여 초기 균수를 측정하였고, 30 분 접촉 후 동일한 방법으로 회수하여 잔존 균수를 측정하였다.In order to confirm that the cutting board manufactured as described above has excellent sterilizing power for the object placed in contact with the cutting board in addition to its own sterilizing power, the culture solution pre-cultured on the cutting board surface (50 mm x 60 mm) prepared as described above was used. After inoculating a certain amount, using a sterile cotton swab was immediately recovered after inoculation to measure the initial bacterial count, after 30 minutes contact was recovered by the same method to measure the remaining bacteria.
시험균주로는 대장균 (Escherichia coli, ATCC 25922)과 황색 포도상구균 (Staphylococcus aureus, ATCC 25923)을 사용하였으며, 시험조건은 다음과 같다:A test strain were used Escherichia coli (Escherichia coli, ATCC 25922) and Staphylococcus aureus (Staphylococcus aureus, ATCC 25923), the test conditions were as follows:
사용배지 (Test medium): 표준한천배지 (Plate Count Agar)Test medium: Plate Count Agar
배양온도 (Incubation Temp.): 35 ± 1 ℃Incubation Temp .: 35 ± 1 ℃
배양기간 (Incubation Period): 24 시간Incubation Period: 24 hours
시험 결과를 다음의 표 4에 나타내었다.The test results are shown in Table 4 below.
살균력(%)={(초기 잔존생균수 - 접촉후 잔존생균수)/초기 잔존생균수} x 100Bactericidal power (%) = {(initial number of remaining bacteria-number of remaining bacteria after contact) / initial number of remaining bacteria} x 100
상기 결과로부터 알 수 있는 바와 같이, 본 실시예의 살균 도마는 자체에 대한 살균력 이외에 표면에 위치하는 물건에 대해서도 30 분 접촉 후 94 %가 넘는 우수한 살균력을 나타내었다. 따라서 상기와 같은 도마 표면에 행주, 칼 등의 주방용품을 접촉시켜 놓음으로써 이들에 대한 살균효과까지 얻을 수 있다. As can be seen from the above results, the sterilizing cutting board of the present embodiment exhibited excellent sterilizing power of more than 94% after 30 minutes of contact with objects placed on the surface in addition to the sterilizing power on itself. Therefore, by bringing kitchen utensils such as dishcloths and knives into contact with the cutting board surface as described above, a sterilization effect thereof can be obtained.
적용예 2: 본 발명의 살균 조성물을 이용한 치약 용기의 제조Application Example 2: Preparation of Toothpaste Container Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 폴리에틸렌 수지 99.5 중량부와 혼합하여 용융 및 성형작업함으로써 살균 치약 용기를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of polyethylene resin to prepare a sterile toothpaste container by melting and molding.
적용예 3: 본 발명의 살균 조성물을 이용한 칫솔갑의 제조Application Example 3: Preparation of Toothbrush Pack Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 PVC 수지 99.5 중량부와 혼합하여 용융 및 성형작업함으로써 살균 칫솔갑을 제작하였다. 0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of PVC resin to prepare a sterilized toothbrush pack.
적용예 4: 본 발명의 살균 조성물을 이용한 화장품 용기의 제조Application Example 4: Preparation of Cosmetic Container Using Sterilizing Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 아크릴 수지 99.5 중량부와 혼합하여 용융 및 성형작업함으로써 살균 화장품 용기를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of the acrylic resin to prepare a sterilizing cosmetic container by melting and molding.
적용예 5: 본 발명의 살균 조성물을 이용한 쓰레기통 및 대야의 제조Application Example 5: Preparation of Garbage Can and Basin Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 폴리프로필렌 수지 99.5 중량부와 혼합하여 용융 및 성형작업함으로써 살균 쓰레기통 및 대야를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of polypropylene resin to prepare a sterilization bin and a basin by melting and molding.
적용예 6: 본 발명의 살균 조성물을 이용한 플라스틱제 컵 및 물병의 제조Application Example 6 Preparation of Plastic Cup and Water Bottle Using Sterilizing Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 폴리프로필렌 수지 99.5 중량부와 혼합하여 용융 및 성형작업함으로써 살균 컵 및 물병을 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of polypropylene resin to prepare a sterilization cup and a water bottle by melting and molding.
적용예 7: 본 발명의 살균 조성물을 이용한 쌀통의 제조Application Example 7 Preparation of Rice Bucket Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 ABS 수지 99.5 중량부와 혼합하여 용융 및 성형작업함으로써 살균 쌀통을 제작하였다.0.5 parts by weight of the sterilization composition prepared in Example 2 was mixed with 99.5 parts by weight of ABS resin to prepare a sterilization rice container by melting and molding.
적용예 8: 본 발명의 살균 조성물을 이용한 바가지, 식품저장용기 양념통 및 물통의 제조Application Example 8: Preparation of gourd, food storage seasoning container and bucket using the sterilizing composition of the present invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 폴리프로필렌 수지 99.5 중량부와 혼합하여 용융 및 성형작업함으로써 살균 바가지, 식품저장용기 양념통 및 물통을 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of polypropylene resin to prepare a sterilization gourd, food storage container seasoning container and bucket.
적용예 9: 본 발명의 살균 조성물을 이용한 음료병의 제조Application Example 9 Preparation of Beverage Bottle Using Sterilizing Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 폴리에틸렌 수지 99.5 중량부와 혼합하여 용융 및 성형작업함으로써 살균 음료병을 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of polyethylene resin to prepare a sterile beverage bottle by melting and molding.
적용예 10: 본 발명의 살균 조성물을 이용한 부직포의 제조Application Example 10 Preparation of Nonwoven Fabric Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 아세트산비닐 수지 99.5 중량부와 혼합하여 섬유를 얇은 솜모양으로 만든 것에 내뿜고 열을 가하여 건조시킴으로써 살균 부직포를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of a vinyl acetate resin, and the fibers were blown into a thin cotton fabric, and heat and dried to prepare a sterilized nonwoven fabric.
적용예 11: 본 발명의 살균 조성물을 이용한 섬유의 제조Application Example 11: Preparation of Fiber Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 에멀젼 상태의 아크릴 수지 99.5 중량부와 혼합한 후 크실렌을 넣어 10 배 희석시킨 용액에 리버스코다를 이용하여 면 섬유를 처리하고 열풍 건조시킴으로써 살균 섬유를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of an acrylic resin in an emulsion state, and then treated with cotton fibers in a solution diluted 10-fold with xylene using reverscoda and hot air dried to prepare sterilized fibers. It was.
적용예 12: 본 발명의 살균 조성물을 이용한 행주 및 걸레의 제조Application Example 12 Preparation of Dish and Mop Using Bactericidal Composition of the Present Invention
상상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 에멀젼 상태의 아크릴 수지 99.5 중량부와 혼합한 후 크실렌을 넣어 10 배 희석시킨 용액을 그라비아 인쇄법을 이용하여 면 섬유에 코팅함으로써 살균 행주 및 걸레를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of an acrylic resin in an emulsion state, and the solution diluted 10-fold with xylene was coated on cotton fibers using gravure printing to remove sterilization cloths and rags. Produced.
적용예 13: 본 발명의 살균 조성물을 이용한 수세미의 제조Application Example 13: Preparation of a Scrubber Using the Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 에멀젼 상태의 아크릴 수지 99.5 중량부와 혼합한 후 크실렌을 넣어 10 배 희석시킨 용액에 제작된 수세미 스폰지를 함침시킨 후 바로 꺼내어 열풍 건조시켜 살균 스폰지를 제조하였다. 0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of an acrylic resin in an emulsion state, impregnated with a scrubber sponge prepared in a solution diluted 10-fold with xylene, and then immediately taken out and dried by hot air to prepare a sterilized sponge. It was.
상기와 같은 스폰지의 살균력을 확인하기 위하여 한국화학시험연구원에 의뢰하여 살균력을 시험하였다, 상기 살균력 시험에 사용된 시험 기기, 시험 균주 및 시험방법은 다음과 같다:In order to confirm the sterilization power of the sponge, the sterilization power was tested by the Korea Testing Institute. The test equipment, test strain and test method used for the sterilization test are as follows:
시험기기 - Clean Bench (수공양행, 한국), Test Equipment-Clean Bench (Sooyang, Korea),
Colony Counter(덕우과학, 한국), Colony Counter (Deokwoo Science, Korea),
Incubator(덕우과학, 한국) Incubator (Dukwoo Science, Korea)
시험균주 - Staphylococcus aureus ATCC 6538 Test strain- Staphylococcus aureus ATCC 6538
Klebsiella pneumonia ATCC 4352 Klebsiella pneumonia ATCC 4352
시험방법 - 상기 균을 액체배지에 진탕 배양시킨 후 배양된 세군을 희석하여 시험에 사용하였다. 상기와 같이 제조된 살균 스폰지 (시험편)와 살균처리되지 아니한 스폰지 (대조편)을 각각 2 cm2의 크기로 자른 후, 상기에서 얻은 시험 균액을 접종한 다음, 37 ± 1°C에서 18 ±시간 동안 배양하였다. 중화 용액 (20ml)을 이용하여 시험편 및 대조편에서 균액을 추출한 후, 세균수를 측정하여 시험편과 대조편의 살균률을 비교하였다. 배지에서 세균이 증식한 경우에는 배지상의 균수에 희석배수를 곱하여 산출하였고, 배지에서 세균이 증식하지 않은 경우에는 추출단계에서 이루어진 희석배수를 곱하여 '20 미만 (<20)'으로 표시하였다. Test Method-The bacteria were shaken and cultured in a liquid medium, and three cultured groups were diluted and used for the test. The sterilized sponge (test piece) and the non-sterile sponge (control piece) prepared as described above were cut to a size of 2 cm 2 , respectively, and then inoculated with the test cell solution obtained above, and then 18 ± hour at 37 ± 1 ° C. Incubated for After the bacterial solution was extracted from the test piece and the control piece using a neutralizing solution (20ml), the bacterial count was measured to compare the sterilization rates of the test piece and the control piece. When bacteria were grown in the medium, the bacterial count on the medium was multiplied by the dilution factor, and when the bacteria did not grow in the medium, the dilution factor was multiplied by the extraction step and expressed as 'less than 20 (<20)'.
상기의 시험결과를 다음의 표 5 및 도 9a 내지 9d에 나타내었다. The test results are shown in Table 5 and FIGS. 9A to 9D.
단위: CFU/mlUnit: CFU / ml
*: 감소율 (%) = {(A-B)/A} x 100*:% Reduction = {(A-B) / A} x 100
여기서, A: 접종 직후의 생균수 (3 검체 평균값), Where A is the number of live bacteria immediately after inoculation (3 sample average values),
B: 접종 후 18시간 배양 후의 생균수 (3 검체의 평균값). B: Number of viable cells after incubation for 18 hours (average value of 3 samples).
또한, 도 9a 및 9b는 S. aureus에 대한 살균력을 보여주는 것으로, 9a는 대조편에 접종 즉시 회수한 생균수를 보여주는 것이고, 9b는 시혐편에서 18시간 동안 배양 후의 생균수를 보여주는 것이다. 또한, 도 9c 및 9d는 K. Pneumoniae에 대한 살균력을 보여주는 것으로, 9c는 대조편에 접종 즉시 회수한 생균수를 보여주는 것이고, 9d는 시험편에서 18 시간 동안 배양 후의 생균수를 보여주는 것이다. 도 9a 및 9d로부터 알 수 있는 바와 같이, 상기와 같이 살균 조성물 처리된 스폰지에서 생균수가 매우 현저하게 감소하는 것을 확인할 수 있다. 따라서 이와 같은 살균 스폰지를 사용하여 제조된 수세미도 역시 우수한 살균력을 갖는다고 결론 내릴 수 있다.9A and 9B show bactericidal activity against S. aureus , 9a shows the viable count recovered immediately after inoculation to the control, and 9b shows the viable count after 18 hours in the specimen. 9C and 9D show bactericidal activity against K. Pneumoniae , 9c shows the viable count recovered immediately after inoculation to the control, and 9d shows the viable count after culture for 18 hours in the test piece. As can be seen from Figures 9a and 9d, it can be seen that the number of viable bacteria in the sponges treated with the sterilizing composition as described above significantly reduced. Thus, it can be concluded that scrubbers prepared using such sterilizing sponges also have excellent sterilizing power.
적용예 14: 본 발명의 살균 조성물을 이용한 이불 커버, 침대 커버 및 식탁매트의 제조Application Example 14 Preparation of Duvet Cover, Bed Cover and Placemat Using Sterilizing Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 에멀젼 상태의 아크릴 수지 99.5 중량부와 혼합한 후 크실렌을 넣어 10 배 희석시킨 용액을 리버스코다 또는 그라비아 인쇄법을 이용하여 이불 커버, 침대 커버 및 식탁매트의 제조시 각 섬유에 처리함으로써 살균 이불 커버, 침대 커버 및 식탁매트를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of an acrylic resin in an emulsion state, and the solution diluted 10-fold by adding xylene was quilt cover, bed cover and table mat using a reverskoda or gravure printing method. By treating each fiber in the manufacture of the sterile quilt cover, bed cover and placemats were produced.
적용예 15: 본 발명의 살균 조성물을 이용한 변기 시트 커버의 제조Application Example 15 Preparation of Toilet Seat Cover Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 에멀젼 상태의 아크릴 수지 99.5 중량부와 혼합한 후 크실렌을 넣어 10 배 희석시킨 용액을 리버스코다 또는 그라비아 인쇄법을 이용하여 변기 시트 커버 제조시 표면에 코팅함으로써 살균 변기 시트 커버를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of an acrylic resin in an emulsion state, and the solution diluted 10-fold by adding xylene was coated on the surface of the toilet seat cover by using a reverskoda or gravure printing method. The sterilized toilet seat cover was produced by doing so.
적용예 16: 본 발명의 살균 조성물을 이용한 불고기판의 제조Application Example 16 Preparation of Bulgogi Plate Using Bactericidal Composition of the Present Invention
상기 실시예 1에서 제조한 살균 조성물 0.5 중량부를 테프론 수지 99.5 중량부와 혼합하여 용융 및 성형작업하여 살균 불고기판을 제작하였다. 이와 같이 제작된 불고기판에 불고기 양념이 되어 있는 돼지고기를 익혀본 결과 기름이 튀지 않고 속부터 골고루 익으며 눌러 붙지 않음을 확인하였다.0.5 parts by weight of the sterilizing composition prepared in Example 1 was mixed with 99.5 parts by weight of Teflon resin to prepare a sterilized barbecue plate by melting and molding. As a result of cooking pork with bulgogi seasoning on the bulgogi plate, the oil was not fried and evenly cooked from the inside and did not stick.
적용예 17: 본 발명의 살균 조성물을 이용한 기저귀의 제조Application Example 17 Preparation of Diaper Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 에멀젼 상태의 프탈산 수지 99.5 중량부와 혼합한 후 크실렌을 넣어 10 배 희석시킨 용액을 기저귀 소재에 그라비아 인쇄법으로 코팅함으로써 살균 기저기 소재를 제작한 뒤 이를 이용하여 살균 지저귀를 제작하였다. 여기서 기저귀 소재는 펄프 또는 면 등을 이용하여 제작된 기저귀감을 의미한다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of the phthalic acid resin in an emulsion state, and a 10-fold diluted solution of xylene was coated on the diaper material by gravure printing to prepare a sterilizing base material. Using this, a sterile twitter was produced. Here, the diaper material means a diaper feeling manufactured using pulp or cotton.
상기와 같이 제작된 기저귀를 사용하여 본 결과 살균 효과가 뛰어날 뿐 아니라 기저귀 표면 밖으로 살균 조성물이 빠져나오지 않아 피부에 이물감이나 손상을 주지 않음을 확인하였다.As a result of using the diaper manufactured as described above, it was confirmed that not only the sterilizing effect was excellent, but also the disinfectant composition did not come out of the diaper surface and did not cause foreign matter or damage to the skin.
적용예 18: 본 발명의 살균 조성물을 이용한 생리대의 제조Application Example 18 Preparation of Sanitary Napkin Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 에멀젼 상태의 프탈산 수지 99.5 중량부와 혼합한 후 크실렌을 넣어 10 배 희석시킨 용액을 생리대 소재에 리버스코다를 이용하여 코팅함으로써 살균 생리대 소재를 제작한 뒤 이를 이용하여 살균 생리대를 제작하였다. 여기서 기저귀 소재는 펄프 또는 면 등을 이용하여 제작된 생리대감을 의미한다.After mixing 0.5 parts by weight of the sterilizing composition prepared in Example 2 with 99.5 parts by weight of the phthalic acid resin in an emulsion state, a solution of 10 times diluted with xylene was coated on the sanitary napkin to produce a sterilizing sanitary napkin material. Using this, a sterile sanitary napkin was produced. Here, the diaper material means a feeling of sanitary napkin manufactured using pulp or cotton.
상기와 같이 제작된 생리대를 사용하여 본 결과 살균 효과가 뛰어날 뿐 아니라 생리대 표면 밖으로 살균 조성물이 빠져나오지 않아 피부에 이물감이나 손상을 주지 않음을 확인하였다.As a result of using the sanitary napkin manufactured as described above, the bactericidal effect was not only excellent but it was confirmed that the sanitizing composition did not come out of the surface of the sanitary napkin so as not to cause foreign matter or damage to the skin.
적용예 19: 본 발명의 살균 조성물을 이용한 마스크의 제조Application Example 19 Preparation of Mask Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부를 에멀젼 상태의 프탈산 수지 99.5 중량부와 혼합한 후 크실렌을 넣어 10 배 희석시킨 용액을 마스크 안감 에 리버스코다를 이용하여 코팅함으로써 살균 마스크 안감을 제작한 뒤 이를 이용하여 살균 마스크를 제작하였다. 여기서 마스크 안감은 마스크 착용시 신체에 닿는 면으로 펄프 또는 면 등을 이용하여 제작된 것을 의미한다.0.5 parts by weight of the sterilizing composition prepared in Example 2 was mixed with 99.5 parts by weight of the phthalic acid resin in an emulsion state, and then a solution 10 times diluted with xylene was coated on the mask lining using reverscoda to prepare a sterilization mask lining. Using this, a sterile mask was produced. Here, the mask lining means a face made of pulp or cotton, which is in contact with the body when the mask is worn.
상기와 같이 제작된 마스크를 사용하여 본 결과 외부로부터 해로운 균을 걸러주어 뛰어난 살균 효과를 보일 뿐 아니라 마스크 표면 밖으로 살균 조성물이 빠져나오지 않아 피부에 이물감이나 손상을 주지 않음을 확인하였다.As a result of using the mask manufactured as described above, it was confirmed that the sterilizing composition was not removed from the outside of the mask surface as well as showing excellent sterilizing effect by filtering harmful bacteria from the outside, and did not cause foreign matter or damage to the skin.
적용예 20: 본 발명의 살균 조성물을 이용한 과일 포장지의 제조Application Example 20 Preparation of Fruit Wrap Using Sterilizing Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부와 PE 필름 99.5 중량부를 혼합한 후 연속 압출하여 살균 과일 포장지를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 and 99.5 parts by weight of the PE film were mixed, followed by continuous extrusion to prepare sterilized fruit wrappers.
적용예 21: 본 발명의 살균 조성물을 이용한 꽃 포장지의 제조Application Example 21 Preparation of Floral Wrapping Paper Using Sterilizing Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부와 PE 필름 99.5 중량부를 혼합한 후 연속 압출하여 살균 꽃 포장지를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 and 99.5 parts by weight of the PE film were mixed and then continuously extruded to produce a sterilized flower wrapping paper.
적용예 22: 본 발명의 살균 조성물을 이용한 벽지의 제조Application Example 22 Preparation of Wallpaper Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부와 PVC 99.5 중량부를 혼합한 후 벽지에 그라비아 인쇄법으로 코팅함으로써 살균 벽지를 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 and 99.5 parts by weight of PVC were mixed and then coated on the wallpaper by a gravure printing method to prepare a sterilized wallpaper.
적용예 23: 본 발명의 살균 조성물을 이용한 장판의 제조Application Example 23 Preparation of Encapsulation Using Bactericidal Composition of the Present Invention
상기 실시예 2에서 제조한 살균 조성물 0.5 중량부와 PVC 99.5 중량부를 혼합한 후 장판에 그라비아 인쇄법으로 코팅함으로써 살균 장판을 제작하였다.0.5 parts by weight of the sterilizing composition prepared in Example 2 and 99.5 parts by weight of PVC were mixed and then coated on the sheet by gravure printing to prepare a sterilized sheet.
실시예 3: 액상 살균 조성물의 제조Example 3: Preparation of Liquid Sterilization Composition
고형분 함량 40 %의 수용성 (oil-in-water) 폴리우레탄 에멀젼과 상기 실시 예 2에서 제조한 살균 분말 3 중량%를 혼합하여 액상 살균 조성물을 제조하였다. Liquid sterilization composition was prepared by mixing 3% by weight of the sterilized powder prepared in Example 2 with an oil-in-water polyurethane emulsion having a solid content of 40%.
액상 살균조성물의 살균력 시험 1Test sterilization of
상기 액상 살균 조성물을 사용하여 한국화학시험연구원에서 다음과 같이 살균력 시험을 수행하였다.Using the liquid sterilization composition was carried out as follows sterilization test in the Korea Testing Institute.
접종물: KS K 0905에서 규정하는 표준포 (면), 5 x 5 cm, Inoculum: Standard cloth (cotton), 5 x 5 cm, as defined in KS K 0905
시험균주: 대장균 (Escherichia coli, ATCC 25922),Test strain: Escherichia coli (ATCC 25922),
황색 포도상구균 (Staphylococcus aureus, ATCC 25923).Staphylococcus aureus (Staphylococcus aureus, ATCC 25923).
대장균 및 황색포도상구균이 각각 접종된 접종물(면 5x5cm)의 초기 세균수를 측정하고, 상기의 살균 조성물을 5 배 희석한 희석물을 각각 1 ml/(접종물)의 양으로 처리하고, 30 분 후의 세균수를 측정하여 다음의 표 6에 나타내었다.Measure the initial bacterial count of the inoculum (5x5 cm cotton) inoculated with E. coli and Staphylococcus aureus, and treat the dilution diluted 5 times with the bactericidal composition in an amount of 1 ml / (inoculation), 30 The number of bacteria after minutes was measured and shown in Table 6 below.
* 감소율(%) = {(초기세균수 - 일정시간후 세균수)/(초기세균수)} x 100 *% Reduction = {(initial number of bacteria-number of bacteria after a certain time) / (initial number of bacteria)} x 100
상기의 시험 결과에서 알 수 있는 바와 같이, 본 발명의 살균 조성물은 면직물에 적용시 99.9 %의 높은 살균력을 나타내었다.As can be seen from the above test results, the bactericidal composition of the present invention exhibited a high bactericidal power of 99.9% when applied to cotton fabrics.
액상 살균조성물의 살균력 시험 2Test of sterilization of
상기 액상 살균 조성물을 사용하여 한국화학시험연구원에서 다음과 같이 살균력 시험을 수행하였다.Using the liquid sterilization composition was carried out as follows sterilization test in the Korea Testing Institute.
접종물: KS K 0905에서 규정하는 표준포 (면), 5 x 5 cm, Inoculum: Standard cloth (cotton), 5 x 5 cm, as defined in KS K 0905
시험균주: 대장균 (Escherichia coli, ATCC 25922),Test strain: Escherichia coli (ATCC 25922),
황색 포도상구균 (Staphylococcus aureus, ATCC 25923).Staphylococcus aureus (Staphylococcus aureus, ATCC 25923).
대장균 및 황색포도상구균이 각각 접종된 접종물(면 5x5cm)의 초기 세균수를 측정하고, 상기의 살균 조성물을 5 배 희석한 희석물을 각각 1 ml/(접종물)의 양으로 처리하고, 40°C에서 12 시간 건조시킨 후, 표준 세탁코스에서 무세제 상태로 10 회 세탁한 후의 세균수를 측정하여 다음의 표 7에 나타내었다.Measure the initial bacterial count of the inoculum (5x5 cm cotton) inoculated with E. coli and Staphylococcus aureus, and treat the dilution diluted 5 times with the bactericidal composition in an amount of 1 ml / (inoculation), 40 After drying for 12 hours at ° C, the number of bacteria after washing 10 times in a detergent-free state in a standard washing course was measured and shown in Table 7.
* 감소율(%) = {(초기세균수 - 일정시간후 세균수)/(초기세균수)} x 100 *% Reduction = {(initial number of bacteria-number of bacteria after a certain time) / (initial number of bacteria)} x 100
세제에 의한 살균효과를 배제하고 순수하게 본 발명의 액상 살균 조성물에 의한 살균효과만을 측정하기 위하여 무세제 상태로 세탁하였다. In order to eliminate the bactericidal effect by the detergent and to measure only the bactericidal effect by the liquid sterilizing composition of the present invention, it was washed in a detergent-free state.
상기의 시험 결과에서 알 수 있는 바와 같이, 본 발명에 따른 액상 살균 조성물은 면직물에 적용 시, 10 회 세탁한 후에도 95 % 이상의 높은 살균력 지속적으로 유지하는 것으로 나타났다.As can be seen from the above test results, the liquid sterilizing composition according to the present invention, when applied to a cotton fabric, was found to maintain a high sterilizing power of more than 95% even after 10 washes.
이상에서 살펴본 바와 같이, 본 발명의 살균 조성물은 뛰어난 살균 효과로 인하여, 각종 주방용품, 욕실용품, 건축자재, 가전제품, 위생용품, 섬유류, 포장재, 화장품, 문구, 완구류, 농원예용 포장재, 정수기용 각종 플라스틱 제품의 제작에 적용될 수 있으며, 외용 항생제, 무좀약 등과 같은 의약분야에도 적용 가능하 다.As described above, the sterilizing composition of the present invention, due to the excellent sterilizing effect, various kitchen utensils, bathroom products, building materials, home appliances, hygiene products, textiles, packaging materials, cosmetics, stationery, toys, agricultural gardening packaging materials, water purifiers It can be applied to the production of various plastic products, and also applicable to the pharmaceutical field such as external antibiotics, athlete's foot medicine.
또한, 본 발명에 따른 액상 살균조성물은 섬유에 적용 시 폴리머와 살균 분말이 섬유에 강력하게 흡착하여 세탁 후에도 제거되지 아니하여 반영구적인 살균효과 제공한다. 이러한 액상 살균 조성물을 적당히 희석하여 분사 가능한 형태로 제조함으로써, 손쉽게 섬유의 살균에 적용될 수 있는 스프레이 제품 등으로 제작에 사용할 수 있다. 특별히 본 발명에 따른 액상 살균조성물을 적당히 희석하여 섬유에 분사할 경우 80회 이상의 세탁에도 살균력이 지속되는 효과가 있다.In addition, the liquid sterilization composition according to the present invention provides a semi-permanent sterilization effect when the polymer and sterilization powder are strongly adsorbed on the fiber and are not removed even after washing. By appropriately diluting such a liquid sterilization composition to produce a sprayable form, it can be used for production as a spray product that can be easily applied to sterilization of fibers. Particularly, when the liquid sterilization composition according to the present invention is properly diluted and sprayed onto the fiber, the sterilizing power is maintained even after 80 times of washing.
Claims (13)