KR100192843B1 - Method for coating sheet with polyester for welding - Google Patents
Method for coating sheet with polyester for welding Download PDFInfo
- Publication number
- KR100192843B1 KR100192843B1 KR1019960056464A KR19960056464A KR100192843B1 KR 100192843 B1 KR100192843 B1 KR 100192843B1 KR 1019960056464 A KR1019960056464 A KR 1019960056464A KR 19960056464 A KR19960056464 A KR 19960056464A KR 100192843 B1 KR100192843 B1 KR 100192843B1
- Authority
- KR
- South Korea
- Prior art keywords
- resin film
- polyester resin
- metal plate
- nickel
- tin
- Prior art date
Abstract
본 발명은 금속판의 양면에 폴리에스테르 수지 필름을 라미네이트시키는 데 있어서 제관시의 용접부를 남겨 두고 띠 모양으로 접착시킨 후, 주석 도금이나 니켈 도금, 또는 니켈 도금 및 주석 도금을 실시함으로써 이루어지는 캔(Can) 제작시 사용되는 용접관용 폴리에스테르 수지 필름 피복 금속판 및 그 제조 방법에 대한 것으로, 본 발명의 제조 방법은, 탈지, 산세, 건조 등의 공정을 거친 금속판을 150∼260℃로 가열한 후, 일면에 접착제가 도포된 폴리에스테르 수지필름을, 제관시 용접부를 잘라내고 접착제가 도포된 면을 금속판과 마주보게 하여 띠 모양으로 접착시키며, 재차 180∼250℃로 가열한 다음 급냉하여 제관시 용접부만 남겨두고 폴리에스테르 수지필름을 띠 모양으로 접착하고, 얻이진 폴리에스테르 수지필름 피복 금속판의 제관시 용접부로 되는 부분에 용접성을 향상시키기 위해 니켈 또는 주석 도금 또는 니켈 및 주석 도금을 실시하여 도금층을 형성하는 구성이며, 본 발명의 금속판은, 금속판(1)의 양면에, 제관시 용접부를 잘라낸 일면에 접착제가 도포된 띠 모양의 폴리에스테르 수지필림을 접착하여 수지필름층(3)을 형성하고 제관시 용접부에는 니켈 또는 주석 또는 니켈 및 주석을 도금하여 이루어진 도금층(2)을 형성하여 이루어진 구성이다.The present invention relates to a method for laminating a polyester resin film on both sides of a metal sheet, comprising the steps of: sticking the metal sheet in a strip shape while leaving the welded portion at the time of steel stripping and then tin plating, nickel plating, or nickel plating and tin plating; The present invention relates to a method for producing a coated metal plate for a polyester resin film for use in a welding process and a method for producing the same. The method comprises the steps of heating a metal plate subjected to processes such as degreasing, pickling and drying at 150 to 260 캜, The polyester resin film coated with the adhesive is cut out of the welded portion at the time of pipe cutting, and the surface coated with the adhesive is adhered to the metal plate so as to have a strip shape. After heating to 180 to 250 ° C again, A polyester resin film is adhered in a strip shape, and the obtained polyester resin film is covered with a metal sheet Nickel or tin plating or nickel and tin plating is performed to improve the weldability of the metal plate 1. The metal plate of the present invention has a structure in which an adhesive is applied to both surfaces of the metal plate 1, And a coating layer 2 made of nickel or tin or nickel and tin is formed on the welded portion when the resin film layer 3 is formed by adhering the applied band-shaped polyester resin film.
Description
본 발명은 캔(Can) 제작시 사용되는 용접관용 라미네이트 금속판 및 그 제조방법에 대한 것으로, 보다 상세하게는 금속판의 양면에 폴리에스테르 수지 필름을 라미네이트시키는 데 있어서 제관시의 용접부를 남겨 두고 띠 모양으로 접착시킨 후, 주석 도금이나 니켈 도금 또는 니켈 도금 및 주석 도금을 실시함으로써 이루어지는 용접관용 폴리에스테르 수지 필름 피복 금속판 및 그 제조방법에 대한 것이다.More particularly, the present invention relates to a laminate metal plate for use in manufacturing a can and a method of manufacturing the same, and more particularly to a laminate metal plate for welding a can, And then performing tin plating, nickel plating or nickel plating and tin plating for the welded pipe, and a method of manufacturing the same.
종래의 용접관용 폴리에스테르 수지 필름 피복 금속판을 제조하는데 있어서 제1도 도시와 같이, 금속판(1)의 양면에 먼저 주석 또는 니켈 및 주석을 도금한 후 도장 및 인쇄하거나 또는 금속판의 양면에 주석 또는 니켈 및 주석을 도금하여 도금층(2)을 형성한 후 제관시의 용접부만 남겨두고 띠 모양의 폴리에스테르 수지필름을 접착시켜 수지필름층(3)을 형성시키는 방법등이 사용되어져 왔다.As shown in FIG. 1, a conventional method for producing a polyester resin film-coated metal plate for a welder includes coating and printing with tin or nickel and tin on both surfaces of a metal plate 1, And a method of forming a resin film layer 3 by bonding a strip-shaped polyester resin film while leaving only a welded portion at the time of tube manufacturing after forming the plating layer 2 by plating the tin.
그러나, 이러한 방법으로 용접관용 금속판을 제조시용접성을 부여하기 위하여 금속판 전체에 주석 등의 도금을 실시하여야 하므로 용접부를 제외한 나머지 부분 즉, 도장 및 인쇄 부분 또는 폴리에스테르 수지 필름 피복 부분의 불필요한 도금으로 인해 막대한 양의 주소 또는 니켈이 낭비되며, 제조 원가가 상승되는 문제가 있었다.However, in order to provide the weldability in the production of the metal plate for welding pipe by such a method, the entire metal plate must be plated with tin or the like, so that the remainder except the welded portion, that is, unnecessary plating of the coating and printing portion or the polyester resin film- An enormous amount of the address or nickel is wasted, and the manufacturing cost is increased.
또한, 2-피스 캔(Two-Piece Can)용 폴리에스테르 수지 필름 피복 금속판의 경우 기존 제관 설비와 다른 별도의 제관 설비가 필요하며, 제관후 별도의 인쇄 공정이 필요하다. 뿐만 아니라 열접착성 및 가공성의 확보를 위해 고가의 첨가제를 사용해야 하므로 폴리에스테르 수지 필름의 가격이 높아 제조 비용이 상승되는 등의 문제가 있었다.In addition, in the case of a metal plate coated with a polyester resin film for a two-piece can, a separate plumbing facility other than the existing plumbing facility is required, and a separate printing process is required after the plumbing. In addition, expensive additives have to be used for securing the heat adhesion and processability, so that there is a problem that the production cost is increased due to a high price of the polyester resin film.
본 발명은 상기 설명한 종래 기술의 문제를 해결하기 위하여 이루어진 것으로, 용접부만 주석 등의 도금층을 형성하는 것에 의해 주석이나 니켈의 낭비를 방지하여 제조 비용을 저하시키고, 도장, 인쇄 공정이 생략되어 열에너지의 손실을 감소시키며 환경 오염 물질의 배출을 억제하여 작업 환경을 개선할 수 있는 용접관용 폴리에스테르 수지 필름 피복 금속판 및 그 제조 방법을 제공하는 것을 목적으로 한다.The present invention has been made in order to solve the above-described problems of the prior art, and it is an object of the present invention to provide a method of manufacturing a semiconductor device, Which is capable of reducing loss and suppressing the discharge of environmental pollutants to improve the working environment, and a method for manufacturing the same.
상기 목적을 달성하기 위하여 본 발명에서는, 탈지, 산세, 건조 등의 공정을 거친 금속판을 150∼260℃로 가열한 후, 일면에 접착제가 도포된 폴리에스테르 수지필름을, 제관시 용접부를 잘라낸 뒤, 접착제가 도포된 면이 금속판과 마주보게 하며 띠 모양으로 접착시키고, 다시 180∼250℃로 가열한 다음 급냉 또는 서냉하여 제관시 용접부만 남겨두고 폴리에스테르 수지필름을 띠 모양으로 접착하고, 얻어진 폴리에스테르 수지필름 피복 금속판의 제관시 용접부로 되는 부분에 용접성을 향상시키기 위해 니켈 또는 주석 도금 또는 니켈 및 주석 도금을 실시하여 도금층을 형성하는 용접관용 폴리에스테르 수지필름 피복 금속판의 제조 방법을 제공한다.In order to attain the above object, the present invention provides a method for producing a polyester resin film, which comprises heating a metal sheet subjected to processes such as degreasing, pickling, and drying to 150 to 260 캜, The surface to which the adhesive is applied faces the metal plate and is adhered in a strip shape. The adhesive tape is heated again to 180 to 250 DEG C and then quenched or gradually cooled to leave a welded portion in the tubing to adhere the polyester resin film in strip form. There is provided a method for manufacturing a polyester resin film clad metal sheet for a welder in which nickel or tin plating or nickel and tin plating is performed to improve the weldability of the resin film-clad metal sheet as a welded portion at the time of steel making.
또한, 본 발명에서는 금속판의 양면에, 제관시 용접부를 잘라낸 일면에 접착제가 도포된 띠 모양의 폴리에스테르 수지필름을 접착하여 수지필름층을 형성하고 제관시 용접부에는 니켈 또는 주석 또는 니켈 및 주석을 도금하여 이루어진 도금층을 형성하여 이루어진 용접관용 폴리에스테르 수지필름 피복 금속판을 제공한다.In addition, in the present invention, a resin film layer is formed by adhering a strip-shaped polyester resin film coated with an adhesive on one side of a metal plate, both sides of which are cut out of the welded portion, and nickel or tin or nickel and tin are plated And a plated layer formed on the surface of the metal foil.
제1도는 종래 기술에 의해 제조된 용접관용 폴리에스테르 수지필름 피복 금속판의 구조를 보이는 단면도.1 is a cross-sectional view showing the structure of a polyester resin film coated metal plate for a welder manufactured by a conventional technique;
제2도는 본 발명에 따라 제조된 용접관용 폴리에스테르 수지필름 피복 금속판의 구조를 보이는 단면도이다.FIG. 2 is a cross-sectional view showing the structure of a polyester resin film coated metal plate for a welder manufactured according to the present invention.
* 도면의 주요부분에 대한 부호의 설명DESCRIPTION OF THE REFERENCE NUMERALS
1 : 금속판 2 : 도금층1: metal plate 2: plated layer
3 : 수지필름층3: resin film layer
이하에서는 양호한 실시예와 관련하여 본 발명을 상세하게 설명한다.Hereinafter, the present invention will be described in detail with reference to the preferred embodiments.
본 발명의 일 측면에 따른 용접관용 폴리에스테르 수지필름 피복 금속판의 제조방법에서는 제2도 도시와 같이, 탈지, 산세, 건조 등의 공정을 거친 금속판(1)을 150∼260℃로 가열한 다음, 한면에 접착제가 도포된 면을 금속판(1)과 마주보게 하여 띠 모양으로 금속판의 양면에 접착시켜 수지필름층(3)을 형성한 뒤, 다시 180∼250℃로 가열한 다음 급냉 또는 서냉함으로써, 제관시 용접할 부분만 남겨 두고 금속판(1)의 양면에 폴리에스테르 수지필름을 띠 모양으로 접착한 폴리에스테르 수지필름 피복 금속판을 얻고, 상기 공정에서 얻어진 폴리에스테르 수지필름 피복 금속판의 폴리에스테르 수지필름이 접착되지 않은 부분, 즉 제관시 용접부로 되는 부분에는 용접성을 부여하기 위해 부착량 400∼500mg/㎡의 니켈을 도금한 후, 부착량 0.6∼2.5mg/㎡의 주석을 도금하거나, 부착량 0.2∼2.0g/㎡의 니켈을 도금하여 도금층(2)을 형성하였다.In the method for producing a polyester resin film coated metal sheet for a welder according to an aspect of the present invention, as shown in FIG. 2, a metal plate 1 having been subjected to processes such as degreasing, pickling and drying is heated to 150 to 260 캜, The surface to which the adhesive is applied on one side facing the metal plate 1 is adhered to both sides of the metal plate in a strip shape to form the resin film layer 3 and then heated again to 180 to 250 캜 and then quenched or gradually cooled, A polyester resin film covered metal plate in which a polyester resin film is adhered to both sides of the metal plate 1 in a belt shape is obtained while leaving only the part to be welded at the time of pipe making, and the polyester resin film of the polyester resin film- In order to impart weldability to the unbonded portion, that is, the portion to be welded at the time of pipe-making, nickel having an adhesion amount of 400 to 500 mg / m 2 is plated, and then a tin of 0.6 to 2.5 mg / Or amount of deposition of plated nickel 0.2~2.0g / ㎡ to form a coating layer (2).
또한, 본 발명의 다른 측면에 의하면, 금속판(1)위에 도금층이 없이 띠 모양으로 폴리에스테르 수지필름만이 접착되어 수지필름층(3)이 형성된 부분과, 제관시 용접하기 위해 폴리에스테르 수지필름이 접착되지 아니하고 띠 모양으로 형성된 용접성을 향상시키기 위한 도금층(2)을 가지는 용접부를 구비하는 폴리에스테르 수지필름 피복 금속판이 얻어진다.According to another aspect of the present invention, there is provided a method of manufacturing a metal film, comprising the steps of: forming a metal film on a surface of a metal plate, wherein only a polyester resin film is adhered without a plating layer in a strip shape to form a resin film layer; A polyester resin film coated metal plate having a welded portion having a plating layer 2 for improving the weldability without being bonded and formed in a strip shape is obtained.
이 금속판의 폴리에스테르 수지필름이 접착된 부분에서 제관시 관의 내면으로 되는 금속판쪽(내면)에 접착되는 폴리에스테르 수지필름은 금속판과 접착되는 면에 우레탄계 접착층이 0.5∼3.5㎛ 도포되고, 제관시 관의 외면으로 되는 금속판쪽(외면)에 접착되는 폴리에스테르 수지필름은 금속판과 접착되는 면에 그라비아 인쇄층, 그 위에 두께 0.5∼3.5㎛의 우레탄계 또는 에폭시계 접착제층이 도포되어 있으며, 금속판과 접착되는 면의 반대면에는 윤활성을 확보하기 위한 크리어 코팅 또는 실리콘 입자를 포함하는 2∼5㎛의 윤활층을 구비하도록 구성된다.In the polyester resin film adhered to the metal plate side (inner side) which is the inner surface of the tube at the time of adhering the polyester resin film of the metal plate, the urethane adhesive layer is applied to the surface to be adhered to the metal plate at 0.5 to 3.5 탆, A polyester resin film adhered to the metal plate side (outer surface) serving as the outer surface of the tube has a gravure printing layer on its surface to be bonded to the metal plate, a urethane or epoxy adhesive layer having a thickness of 0.5 to 3.5 m thereon, And a lubricating layer of 2 to 5 mu m containing silicone particles or a creel coating for ensuring lubricity.
또한, 폴리에스테르 수지필름 피복 금속판의 폴리에스테르 수지필름이 접착되지 않은 부분, 즉 제관시 용접부로 되는 부분에는 용접성을 부여하기 위해 부착량 40∼500mg/㎡의 니켈을 도금한 후 부착량 0.6∼2.5g/㎡의 주석을 도금하거나, 또는 부착량 0.8∼2.5g/㎡의 주석을 도금하거나, 부착량 0.2∼2.0g/㎡의 니켈을 도금하여 도금층(2)을 형성한다.Further, in order to provide weldability to the portion where the polyester resin film of the polyester resin film-covered metal sheet is not adhered, that is, the portion to be welded at the time of pipe-making, nickel is plated at an adhesion amount of 40 to 500 mg / M 2 of tin or a coating amount of tin of 0.8 to 2.5 g / m 2 or plating nickel of an adhesion amount of 0.2 to 2.0 g / m 2 to form a plating layer 2.
이와 같이 하여 용접성이 우수하며 식품에 대한 보존성이 뛰어난 용접관용 폴리에스테르 수지필름 피복 금속판을 얻을 수 있다.In this manner, a polyester resin film coated metal plate for a welded pipe excellent in weldability and excellent in preservability against food can be obtained.
또한, 본 발명에서는 폴리에스테르 수지 필름 피복 금속판을 제조함에 있어 금속판에 폴리에스테르 수지 필름을 피복시킨 후, 도금을 실시하기 전에 도금이 용이하도록 산세, 수세, 탈지 등의 공정을 거칠 수 있다.In addition, in the present invention, in the production of the polyester resin film coated metal sheet, the metal plate may be coated with a polyester resin film and then subjected to a process such as pickling, washing and degreasing to facilitate plating before plating.
이하에서는 실시예와 관련하여 본 발명을 설명한다.Hereinafter, the present invention will be described with reference to examples.
[실시예 1][Example 1]
탈지, 산세, 건조 등의 공정을 거친 금속판을 150∼200℃로 가열한 후, 제관시의 용접부 만큼 절단해낸 띠 모양의 폴리에스테르 수지필름을 금속판의 양면에 라미네이트롤을 이용하여 접착시켰다. 금속판의 내면(제관시 관의 내면에 접착되는 필름은 금속판과 접착되는 면에 우레탄계 접착제가 0.5∼2㎛의 두께로 도포되어 있으며, 금속판의 외면(제관시 관의 외면)에 접착되는 필름은 금속판과 접착되는 면에 그라비아 인쇄층, 그 위에 흰색 경화제가 포함된 두께 0.5∼3.0㎛의 우레탄계 접착층을 가지며, 그 반대면에 실리콘 입자를 포함하는 두께 2∼5㎛의 윤활층을 가짐으로써 구성된다.The metal plate subjected to the processes such as degreasing, pickling, and drying was heated to 150 to 200 ° C, and then a strip-shaped polyester resin film cut by a welded portion at the time of steel making was adhered to both sides of the metal plate using a laminate roll. The inner surface of the metal plate (the film to be adhered to the inner surface of the metal tube is coated with a urethane adhesive in a thickness of 0.5 to 2 占 퐉 on the surface to be adhered to the metal plate and the film to be adhered to the outer surface A urethane adhesive layer having a thickness of 0.5 to 3.0 占 퐉 and containing a white hardening agent on the gravure printing layer, and a lubricating layer having a thickness of 2 to 5 占 퐉 including silicon particles on the opposite surface.
폴리에스테르 수지필름을 양면에 띠 모양으로 접착시킨 후, 다시 금속판을 180∼220℃로 가열한 다음 급냉하여 폴리에스테르 수지필름 피복 금속판을 얻었다. 위 금속판에 제관시의 용접성을 부여하기 위하여 0.2∼0.5g/㎡의 니켈과 1.0∼g/㎡의 주석을 도금하여 도금층을 형성하였다.After the polyester resin film was stuck to both sides in a strip shape, the metal plate was heated again to 180 to 220 캜 and then quenched to obtain a polyester resin film coated metal plate. In order to impart weldability to the upper metal plate, 0.2 to 0.5 g / m 2 of nickel and 1.0 to g / m 2 of tin were plated to form a plated layer.
[실시예 2][Example 2]
탈지, 산세, 건조 등의 공정을 거친 금속판을 240∼260℃로 가열한 뒤, 금속판의 내 외면에 열접착성이 있는 이축 연신 폴리에스테르 필름을 실시예 1과 같이 용접부 만큼 잘라낸 뒤 라미네이트롤을 이용하여 띠 모양으로 열접착시켰다. 내면에 사용된 폴리에스테르 수지필름은 융점이 210∼230℃이며 두께는 15∼25㎛이다. 외면에 사용된 폴리에스테르 수지필름은 흰색을 내기 위한 산화 티타늄 색소를 포함하며, 금속판과 접착되는 반대면에 우레탄계 접착제가 도포되어 있으며, 그 위에 그라비아 인쇄층을 보호하기 위해 외면에 윤활층을 가지는 폴리에스테르 수지필름으로 되어 있다. 금속판의 내외면에 폴리에스테르 수지필름을 열접착 시킨 다음 수초 이내에 80℃이하의 물에 급냉함으로써 폴리에스테르 수지필름 피복 금속판을 얻었다. 다시 위 금속판에 제관시의 용접성을 부여하기 위하여 0.8∼1.2g/㎡의 주석을 도금하여 도금층을 형성하였다.The biaxially stretched polyester film having thermal adhesiveness to the inner and outer surfaces of the metal sheet was cut out by a welded portion as in Example 1, followed by the use of a laminate roll And thermally adhered in a strip shape. The polyester resin film used for the inner surface has a melting point of 210 to 230 캜 and a thickness of 15 to 25 탆. The polyester resin film used for the outer surface includes a titanium oxide dye for imparting white color, and a urethane adhesive is applied to the opposite surface to be adhered to the metal plate. On the upper surface, a poly It is made of an ester resin film. A polyester resin film was thermally adhered to the inner and outer surfaces of the metal sheet and then quenched in water at 80 DEG C or lower within a few seconds to obtain a polyester resin film coated metal sheet. And then plated with 0.8 to 1.2 g / m < 2 > of tin in order to impart weldability to the upper metal plate.
[실시예 3][Example 3]
탈지, 산세, 건조 등의 공정을 거친 금속판을 220∼260℃로 가열한 다음, 금속판의 내 외면에 이층 구조의 이축 연신 폴리에스테르 필름을 제관시의 용접부만큼 잘라낸 뒤 라미네이트를 이용하며 띠 모양으로 열접착시킨 다음, 수초 이내에 80℃ 이하의 물에 급냉함으로써, 폴리에스테르 수지필름 피복 금속판을 얻었다. 금속판의 내면(제관시 관의 내면)에 사용되는 폴리에스테르 수지필름은 2층 구조로 되어 있으며, 금속판과 접착되는 면의 필름의 융점은 180∼200℃이고 그 위의 필름층은 융점이 230∼250℃이며, 흰색을 내기 위한 산화 티타늄 색소를 포함하며, 그 위에 우레탄계 접착제층, 그라비아 인쇄층, 크리어 코팅을 외면에 가지는 폴리에스테르 수지필름 등으로 구성되어 있다. 이렇게 얻어진 폴리에스테르 수지필름 피복 금속판에 제관시 용접성을 부여하기 위하여 부착량 40∼80mg/㎡의 니켈을 도금하고, 그 위에 부착량은 0.6∼2.5g/㎡의 주석을 도금하여 도금층을 형성한 뒤 화학 처리를 행하였다.A metal plate subjected to processes such as degreasing, pickling, and drying is heated to 220 to 260 ° C., and a biaxially stretched polyester film having a two-layer structure is cut out to the inner and outer surfaces of the metal plate by a weld portion at the time of steel making. And then rapidly cooled in water at 80 DEG C or less within a few seconds to obtain a polyester resin film coated metal plate. The polyester resin film used for the inner surface of the metal sheet (the inner surface of the pipe for the tube making) has a two-layer structure, the melting point of the film on the surface bonded to the metal sheet is 180 to 200 ° C, 250 ° C, and contains a titanium oxide pigment for white coloring, a urethane-based adhesive layer, a gravure printing layer, and a polyester resin film having a clear coating on the outer surface thereof. Nickel of 40 to 80 mg / m < 2 > was plated on the thus obtained polyester resin film-clad metal sheet to give weldability at the time of plating, and a coating layer was formed thereon by plating the tin of 0.6 to 2.5 g / .
[실시예 4][Example 4]
탈지 및 수세, 건조 등의 공정을 거친 금속판에 실시예 1 에서와 같은 방법으로 폴리에스테르 수지필름을 피복시킨 다음, 산세 및 수세를 거쳐 실시예 1 에서와 같이 니켈 및 주석도금을 실시하였다.A metal plate subjected to processes such as degreasing, washing, and drying was coated with a polyester resin film in the same manner as in Example 1, and nickel and tin plating were performed as in Example 1 after pickling and washing with water.
[실시예 5][Example 5]
탈지 및 산세, 건조 등의 공정을 거친 금속판에 실시예 2와 같은 방법으로 폴리에스테르 수지 필름을 피복시킨 다음, 산세 및 수세를 거쳐 실시예 2와 같이 주석 도금을 실시하였다.A metal plate subjected to processes such as degreasing, pickling, and drying was coated with a polyester resin film in the same manner as in Example 2, and then tin-plated as in Example 2 through pickling and water washing.
[실시예 6][Example 6]
탈지 및 산세, 건조 등의 공정을 거친 금속판에 실시예 3과 같은 방법으로 폴리에스테르 수지 필름을 피복시킨 다음, 탈지 및 산세를 거쳐 실시예 3과 같이 니켈 및 주석 도금을 실시하였다.A metal plate subjected to processes such as degreasing, pickling, and drying was coated with a polyester resin film in the same manner as in Example 3, followed by degreasing and pickling, and nickel and tin plating were carried out as in Example 3.
따라서, 본 발명에 의해 얻어진 폴리에스테르 수지 필름 피복 금속판에 의하면, 용접부 외의 폴리에스테르 수지필름이 접착되는 부위에는 주석 도금 또는 니켈 및 주석을 도금하지 아니하여도 우수한 용접성이 확보되므로 상당한 량의 주석 및 니켈을 절약할 수 있어서 제조 비용의 절감을 가져오며, 도장, 인쇄 공정이 생략되므로 과다한 열에너지의 손실을 줄이고 작업 환경을 개선하는 등 환경 오염 물질의 배출을 억제할 수 있으며, 기존의 제관 설비를 그대로 이용하여 3-피스 캔을 제조하는 것이 가능하나, 또한 종래의 경우 금속판의 전체에 도금을 실시함으로 인해 도금층을 두껍게 하는 것이 경제적인 이유로 곤란하여 도금층을 가능한한 얇게 형성함으로써 유통 기간이 길어지거나 녹이 용이하게 형성될 수 있는 지역에 사용할 때, 녹이 발생할 수 있었으나, 본 발명에서는 용접부만 도금하므로 두껍게 도금층을 형성하여도 제조비용 상승에 미치는 영향이 적어 도금층을 두껍게 형성할 수 있어서 내식성이 향상되는 등 유용한 발명인 것이다.Therefore, according to the polyester resin film-covered metal sheet obtained by the present invention, excellent weldability can be ensured even if tin plating or nickel and tin are not plated on the portion where the polyester resin film other than the welded portion is adhered, so that a considerable amount of tin and nickel It is possible to save manufacturing cost, omitting painting and printing process, and thus it is possible to suppress the discharge of environmental pollutants such as reduction of loss of excessive heat energy and improvement of working environment, It is possible to manufacture a three-piece can, but in the conventional case, it is difficult to increase the thickness of the plating layer by plating the entire metal plate, which is difficult because of economical reasons, so that the plating layer is made as thin as possible, When used in areas that can form, rust can occur But, to useful inventions such as the present invention, because the welding portion is thicker by plating only even impact on the production cost rises in less can form a thick plating layer improves the corrosion resistance, forming a plating layer.
Claims (2)