JPH0915609A - Spacer for liquid crystal display - Google Patents
Spacer for liquid crystal displayInfo
- Publication number
- JPH0915609A JPH0915609A JP16238795A JP16238795A JPH0915609A JP H0915609 A JPH0915609 A JP H0915609A JP 16238795 A JP16238795 A JP 16238795A JP 16238795 A JP16238795 A JP 16238795A JP H0915609 A JPH0915609 A JP H0915609A
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- spacer
- spacers
- adhesive
- hydrophobic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、液晶ディスプレーの電
極基板の間隔を制御する液晶ディスプレー用スペーサに
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a liquid crystal display spacer for controlling the distance between electrode substrates of a liquid crystal display.
【0002】[0002]
【従来の技術】一般に、液晶ディスプレーでは、配向膜
が形成された1対の電極基板間に、液晶が介在されると
共に、これら電極基板の間隔を制御する複数のスペーサ
が介装されている。このスペーサの材料としては、樹脂
やガラスなどがあるが、一般には、環境の温度変化によ
る液晶の膨張に追従することを目的として、樹脂製スペ
ーサが多く使用されている。2. Description of the Related Art Generally, in a liquid crystal display, a liquid crystal is interposed between a pair of electrode substrates on which an alignment film is formed, and a plurality of spacers for controlling the intervals between these electrode substrates are interposed. Resins, glass, and the like are used as the material for the spacers. Generally, resin spacers are often used for the purpose of following the expansion of the liquid crystal due to the temperature change of the environment.
【0003】ところが、このような液晶ディスプレーで
は、スペーサが、液晶と共に電極基板間に配置されてい
るため、配向膜によって規制された液晶分子の配向が、
スペーサによって乱されることがあり、スペーサ周辺の
液晶分子が電圧のON/OFFで配向制御ができなくな
る。特に、スペーサの表面方向に規則正しく束縛された
液晶分子の配向制御が困難となり、暗視野状態におい
て、スペーサ周囲より光抜けが生じ、コントラストが低
下するという欠点を有する。However, in such a liquid crystal display, since the spacer is arranged between the electrode substrates together with the liquid crystal, the alignment of the liquid crystal molecules regulated by the alignment film is
The liquid crystal molecules around the spacer may be disturbed by the spacer, and the orientation cannot be controlled by turning the voltage ON / OFF. In particular, it is difficult to control the alignment of liquid crystal molecules that are regularly bound in the spacer surface direction, and in the dark field state, light leakage occurs from the periphery of the spacer, and the contrast decreases.
【0004】また、スペーサが、液晶注入時、電圧印加
時および衝撃付加時に液晶セル内で移動することによ
り、スペーサが基板上に不均一に分散してしまい、セル
ギャップ精度が悪化して、表示むらが発生するという欠
点を有する。かかる欠点は、通常のねじれネマチック
(TN型)液晶セルでも発生するが、超ねじれネマチッ
ク(STN型)液晶セルにおいて特に顕著である。これ
は、STN型セルにおいては、セルギャップ精度の不均
一や液晶分子の配向乱れが表示品質に及ぼす影響が大き
いことによる。Further, the spacers move in the liquid crystal cell when the liquid crystal is injected, when a voltage is applied, and when a shock is applied, so that the spacers are non-uniformly dispersed on the substrate and the cell gap accuracy is deteriorated. It has a drawback that unevenness occurs. Such a defect occurs even in a normal twisted nematic (TN type) liquid crystal cell, but is particularly remarkable in a super twisted nematic (STN type) liquid crystal cell. This is because in the STN type cell, the nonuniformity of the cell gap accuracy and the alignment disorder of the liquid crystal molecules have a great influence on the display quality.
【0005】そこで、このような欠点を解消するため、
低表面張力のスペーサの表面の一部分に付着性物質が付
着され、液晶分子の配向不良が表面張力の小さい表面に
より抑制され、スペーサを部分的に覆っている付着性物
質により接着力が得られ、スペーサの液晶セル内での移
動を防止する液晶ディスプレーが、たとえば特開平3−
293327号公報に開示されている。Therefore, in order to eliminate such drawbacks,
An adhesive substance is attached to a part of the surface of the spacer having a low surface tension, the misalignment of liquid crystal molecules is suppressed by the surface having a small surface tension, and the adhesive substance partially covering the spacer provides an adhesive force, A liquid crystal display that prevents the spacers from moving in the liquid crystal cell is disclosed in, for example, Japanese Patent Laid-Open No.
It is disclosed in Japanese Patent No. 293327.
【0006】[0006]
【発明が解決しようとする課題】ところが、前述した液
晶ディスプレー用スペーサにおいては、次のような問題
点があることが本発明者により見い出された。すなわ
ち、低表面張力のスペーサの製造工程が煩雑である上、
付着性物質がスペーサの一部分にしか付着していないの
で、スペーサが液晶セル内で充分に固定されない。その
ため、スペーサが移動して、液晶セル内で不均一にな
り、表示むらが発生する。However, the present inventor has found that the above-mentioned spacer for liquid crystal display has the following problems. That is, the manufacturing process of the low surface tension spacer is complicated, and
Since the adhesive substance adheres only to a part of the spacer, the spacer is not sufficiently fixed in the liquid crystal cell. Therefore, the spacers move and become non-uniform in the liquid crystal cell, resulting in display unevenness.
【0007】本発明の目的は、前述した問題点に鑑み、
スペーサ周囲の光抜けを防止することができると共に、
液晶セル内での固着性を向上することができ、製造工程
が簡便な液晶ディスプレー用スペーサを提供することに
ある。本発明の前記ならびにその他の目的と新規な特徴
は、本明細書の記述および添付図面から明らかになるで
あろう。The object of the present invention is to solve the above-mentioned problems.
It is possible to prevent light leakage around the spacer,
An object of the present invention is to provide a spacer for a liquid crystal display, which can improve the sticking property in a liquid crystal cell and has a simple manufacturing process. The above and other objects and novel features of the present invention will become apparent from the description of the present specification and the accompanying drawings.
【0008】[0008]
【課題を解決するための手段】本願において開示される
発明の概要を簡単に説明すれば、以下のとおりである。 (1)本発明の液晶ディスプレー用スペーサは、液晶デ
ィスプレーの対向する電極基板間に液晶組成物と共に介
在されて、電極基板の間隔を制御するもので、表面上
に、疎水性接着剤と親水性接着剤とを付着したものであ
る。The outline of the invention disclosed in the present application will be briefly described as follows. (1) The liquid crystal display spacer of the present invention is interposed between the electrode substrates facing each other of the liquid crystal display together with the liquid crystal composition to control the distance between the electrode substrates. An adhesive is attached.
【0009】(2)本発明の液晶ディスプレー用スペー
サは、液晶ディスプレーの対向する電極基板間に液晶組
成物と共に介在されて、電極基板の間隔を制御するもの
で、表面上に、疎水性接着剤および親水性接着剤が付着
された領域を、不規則に有するものである。本発明の液
晶ディスプレー用スペーサの形状や材質は特に規定しな
いが、一般には、次のようなものが好適に用いられる。
すなわち、形状としては、ファイバー状、真球(ビー
ズ)状などがあるが、真球が好適である。材料として
は、ガラス、樹脂があるが、樹脂が好適であり、スチレ
ン・ジビニルベンゼン共重合体、ベンゾグアナミン・メ
ラミン・ホルムアルデヒド縮合体などがある。(2) The spacer for a liquid crystal display according to the present invention is interposed between the opposing electrode substrates of the liquid crystal display together with the liquid crystal composition to control the distance between the electrode substrates. And irregularly having a region to which the hydrophilic adhesive is attached. The shape and material of the spacer for a liquid crystal display of the present invention are not particularly specified, but generally the following ones are preferably used.
That is, the shape may be a fiber shape, a true sphere (bead) shape, or the like, but a true sphere is preferable. Examples of the material include glass and resin, and resin is preferable, and examples thereof include styrene / divinylbenzene copolymer and benzoguanamine / melamine / formaldehyde condensate.
【0010】また、スペーサ径は、一般に3〜15μm
のものが用いられる。本発明における親水性接着剤と
は、たとえばアクリルモノマーもしくはメタクリルモノ
マーに親水基として、カルボキシル基や水酸基およびア
ミノ基などが少なくとも10モル%以上含まれているも
ので、その表面張力は概ね50dyne/cm以上のものをい
う。The spacer diameter is generally 3 to 15 μm.
Is used. The hydrophilic adhesive in the present invention is, for example, an acrylic monomer or a methacrylic monomer containing at least 10 mol% or more of a carboxyl group, a hydroxyl group and an amino group as a hydrophilic group, and the surface tension thereof is about 50 dyne / cm. The above is said.
【0011】また、疎水性接着剤としては、たとえばア
クリルモノマーまたはメタクリルモノマーの側鎖がアル
キル鎖を含有するもので、そのアルキル鎖の炭素数が5
以上のもの、またはパーフロロアルキル基を有するもの
で、その表面張力は概ね30dyne/cm以下のものをい
う。スペーサ表面に接着剤を付着する方法としては、各
種方法が用いられるが、スペーサ分散後に、親水性接着
剤のエマルジョン、疎水性接着剤のエマルジョンを滴下
する方法でも付着し得る。また、たとえばメカノフュー
ジョン法を用いればよい。ここで、メカノフュージョン
法とは、圧縮剪断摩擦原理に基づいて、微粒子表面に強
力な機械エネルギーを加えて、スペーサ表面に、親水性
接着剤と疎水性接着剤とを順次付着させ、スペーサの表
面改質を行なう方法である。As the hydrophobic adhesive, for example, a side chain of an acrylic monomer or a methacrylic monomer contains an alkyl chain, and the alkyl chain has 5 carbon atoms.
The above or those having a perfluoroalkyl group and having a surface tension of about 30 dyne / cm or less. Although various methods are used to attach the adhesive to the spacer surface, a method of dropping the emulsion of the hydrophilic adhesive or the emulsion of the hydrophobic adhesive after dispersing the spacer may also be used. Further, for example, the mechanofusion method may be used. Here, the mechanofusion method is based on the compression shear friction principle, applying strong mechanical energy to the surface of the fine particles to sequentially attach hydrophilic and hydrophobic adhesives to the spacer surface, and the surface of the spacer This is a method of reforming.
【0012】親水性接着剤と疎水性接着剤とを混在させ
る方法としては、たとえば、水/イソプロピルアルコー
ル=85/15の混合液に分散したスペーサに、親水性
および疎水性接着剤からなるエマルジョン接着剤を、そ
れぞれ別々に、またはそれらを混合した後に滴下する方
法が利用できる。また、メカノフュージョン法で、親水
性接着剤と疎水性接着剤とを逐次または混合して付着さ
せる方法も利用できる。As a method of mixing the hydrophilic adhesive and the hydrophobic adhesive, for example, an emulsion adhesive consisting of a hydrophilic adhesive and a hydrophobic adhesive is attached to a spacer dispersed in a mixed solution of water / isopropyl alcohol = 85/15. A method of adding the agents separately or after mixing them can be used. Further, a method in which a hydrophilic adhesive and a hydrophobic adhesive are sequentially or mixed and attached by a mechanofusion method can also be used.
【0013】また、疎水性接着剤および親水性接着剤の
材料としては、熱可塑性または熱硬化性の液晶組成物を
汚染しない樹脂なら何を用いてもよい。As the material of the hydrophobic adhesive and the hydrophilic adhesive, any resin may be used as long as it does not contaminate the thermoplastic or thermosetting liquid crystal composition.
【0014】[0014]
【作 用】前述した手段によれば、スペーサの表面に疎
水性接着剤と親水性接着剤とが不規則に付着されたの
で、液晶分子はスペーサの表面方向に不規則な方向に束
縛されると共に、スペーサが液晶セル内で固定され、ス
ペーサの移動が防止される。また、スペーサは、その表
面に疎水性接着剤および親水性接着剤を不規則に付着す
るだけで得られるので、製造工程が簡便化される。[Operation] According to the above-mentioned means, since the hydrophobic adhesive and the hydrophilic adhesive are irregularly adhered to the surface of the spacer, the liquid crystal molecules are bound to the surface of the spacer in an irregular direction. At the same time, the spacer is fixed in the liquid crystal cell, and the movement of the spacer is prevented. In addition, the spacer can be obtained by merely randomly attaching the hydrophobic adhesive and the hydrophilic adhesive to the surface thereof, so that the manufacturing process is simplified.
【0015】[0015]
【実施例】以下、本発明の実施例を図面に基づいて詳細
に説明する。図1は本発明の実施例に係る液晶ディスプ
レーの要部断面図を示す。 〔実施例1〕図1において、液晶ディスプレーの液晶セ
ル(240°ツイストSTNセル)は、1対の対向する
ガラス基板(50mm角×1.1t,面研磨ソーダライ
ム)10が配設され、1対のガラス基板10間にITO
(20Ω/□)からなる1対の透明電極20が対向して
配設されている。Embodiments of the present invention will be described below in detail with reference to the drawings. FIG. 1 is a sectional view of a main part of a liquid crystal display according to an embodiment of the present invention. [Embodiment 1] In FIG. 1, a liquid crystal cell (240 ° twist STN cell) of a liquid crystal display is provided with a pair of opposing glass substrates (50 mm square × 1.1 t, surface-polished soda lime) 10. ITO between the pair of glass substrates 10
A pair of transparent electrodes 20 made of (20Ω / □) are arranged so as to face each other.
【0016】1対の透明電極20間には、ラビングされ
たポリイミドからなる1対の配向膜(膜厚0.1μm)
30が対向するように配設されている。これら1対の配
向膜30間には、正の誘電異方性を有する液晶組成物4
0が注入されると共に、複数の粒子状のスペーサ51が
固定されている。さらに、液晶組成物40の周辺はエポ
キシ接着剤(図示略す)により封止されている。Between the pair of transparent electrodes 20, a pair of alignment films made of rubbed polyimide (film thickness 0.1 μm)
30 are arranged so as to face each other. A liquid crystal composition 4 having a positive dielectric anisotropy is provided between the pair of alignment films 30.
0 is injected, and a plurality of particulate spacers 51 are fixed. Further, the periphery of the liquid crystal composition 40 is sealed with an epoxy adhesive (not shown).
【0017】また、水/イソプロピルアルコール=85
/15からなる分散媒100gに、スペーサ(スチレン
・ジビニルベンゼン共重合体製微球体スペーサ、粒径6
μm)51を分散させたものに、疎水性接着剤61とし
て、n−ブチルアクリレート/ラウリルアクリレート=
75モル%/25モル%からなるエマルジョン10g
(樹脂分1g)および親水性接着剤71として、n−ブ
チルアクリレート/メタクリル酸=85モル%/15モ
ル%からなる平均粒径0.5μmのエマルジョン10g
(樹脂分1g)をそれぞれ滴下して、スペーサ51の表
面に疎水性および親水性接着剤61,71からなる接着
層が不規則に形成されている。Water / isopropyl alcohol = 85
Spacer (styrene / divinylbenzene copolymer microsphere spacer, particle size 6
(μm) 51 dispersed therein, and as a hydrophobic adhesive 61, n-butyl acrylate / lauryl acrylate =
10 g of emulsion consisting of 75 mol% / 25 mol%
(Resin content: 1 g) and hydrophilic adhesive 71: 10 g of an emulsion of n-butyl acrylate / methacrylic acid = 85 mol% / 15 mol% with an average particle size of 0.5 μm
(Resin content 1 g) is dropped, and adhesive layers made of hydrophobic and hydrophilic adhesives 61 and 71 are irregularly formed on the surface of the spacer 51.
【0018】かかる液晶セルは、接着剤つきスペーサ5
1を、透明電極20,ラビング処理された配向膜30が
順次形成されたガラス基板10に160℃で固着させた
後、シール剤を印刷した対向ガラス基板10と貼り合わ
せ、液晶組成物40を注入して作製される。次に、この
ようにして、作製された液晶セルに対し、100Hz−
3.0Vの交流電圧を印加し、スペーサ周囲の光抜けを
偏光顕微鏡で観察した。光抜け(%)は、((周囲に光
抜けのあるスペーサの個数)/(スペーサの総数))×
100より、算出した。この場合、光抜け30%以下を
合格とする。さらに、ITOガラス基板10上に、乾式
法でスペーサ51を散布し、これに30cmの距離から
圧力が4kg/cm2 のエアーガンを用いて、ガラス基
板10に垂直に吹き付け、スペーサ51の固着性を観察
した。固着性(%)は、((エアガン吹き付け後、基板
に残留したスペーサ個数)/(吹き付け前のスペーサ個
数))×100より、算出した。この場合、固着性70
%以上を合格とする。結果を表1に示す。The liquid crystal cell has a spacer 5 with an adhesive.
1 is fixed to a glass substrate 10 on which a transparent electrode 20 and an alignment film 30 subjected to a rubbing treatment are sequentially formed at 160 ° C., and then the glass substrate 10 is attached to a counter glass substrate 10 printed with a sealant, and a liquid crystal composition 40 is injected. Is produced. Next, with respect to the liquid crystal cell thus manufactured, 100 Hz-
An AC voltage of 3.0 V was applied, and light leakage around the spacer was observed with a polarizing microscope. Light leakage (%) is ((number of spacers with light leakage around) / (total number of spacers)) x
Calculated from 100. In this case, the light leakage of 30% or less is determined to be acceptable. Further, the spacers 51 are sprayed on the ITO glass substrate 10 by a dry method, and the spacers 51 are sprayed vertically from the distance of 30 cm with an air gun whose pressure is 4 kg / cm 2 to fix the spacers 51. I observed. The adhesion (%) was calculated from ((number of spacers remaining on the substrate after spraying with an air gun) / (number of spacers before spraying)) × 100. In this case, the stickiness 70
Pass more than%. Table 1 shows the results.
【0019】〔実施例2〕水/イソプロピルアルコール
=85wt%/15wt%からなる分散媒100gに、
スペーサ(スチレン・ジビニルベンゼン共重合体の微球
体スペーサ、粒径6μm)52を分散させたものに、親
水性接着剤72として、n−ブチルアクリレート/ヒド
ロキシエチルアクリレート=70モル%/30モル%か
らなる平均粒径0.7μmのエマルジョン10g(樹脂
分1g)および疎水性接着剤62として、n−ブチルア
クリレート/パーフロロブチルアクリレート=80モル
%/20モル%からなる平均粒径0.4μmのエマルジ
ョン10g(樹脂分1g)をそれぞれ滴下して、スペー
サ表面に疎水性および親水性接着剤62,72からなる
接着層を不規則に形成した。Example 2 100 g of a dispersion medium composed of water / isopropyl alcohol = 85 wt% / 15 wt%,
N-butyl acrylate / hydroxyethyl acrylate = 70 mol% / 30 mol% as a hydrophilic adhesive 72 in which spacers (microsphere spacer of styrene / divinylbenzene copolymer, particle size 6 μm) 52 are dispersed. 10 g of emulsion having an average particle size of 0.7 μm (resin content 1 g) and the hydrophobic adhesive 62 are n-butyl acrylate / perfluorobutyl acrylate = 80 mol% / 20 mol% emulsion having an average particle size of 0.4 μm 10 g (resin content: 1 g) was dropped, and an adhesive layer made of hydrophobic and hydrophilic adhesives 62 and 72 was irregularly formed on the spacer surface.
【0020】この接着剤つきスペーサ52を用いて、実
施例1と同様に液晶セルを作製し、スペーサ周囲の光抜
けを観察した。また、実施例1と同様にスペーサ52の
固着性も観察した。結果を表1に示す。 〔実施例3〕水/イソプロピルアルコール=85wt%
/15wt%からなる分散媒100gに、スペーサ(ス
チレン・ジビニルベンゼン共重合体の微球体スペーサ、
粒径6μm)53を分散させたものに、親水性接着剤7
3として、n−ブチルアクリレート/アクリル酸=80
モル%/20モル%からなる平均粒径0.7μmのエマ
ルジョン15g(樹脂分1g)および疎水性接着剤63
として、n−ブチルアクリレート/ドデシルアクリレー
ト=75モル%/25モル%からなる平均粒径0.4μ
mのエマルジョン5g(樹脂分1g)をそれぞれ滴下し
て、スペーサ表面に疎水性および親水性接着剤63,7
3からなる接着層を不規則に形成した。Using this spacer 52 with an adhesive, a liquid crystal cell was produced in the same manner as in Example 1, and the light leakage around the spacer was observed. Further, similarly to Example 1, the adhesiveness of the spacer 52 was also observed. Table 1 shows the results. [Example 3] Water / isopropyl alcohol = 85 wt%
Spacer (styrene / divinylbenzene copolymer microsphere spacer,
A hydrophilic adhesive 7 is added to a dispersion of 53 (particle size 6 μm) 53.
3, n-butyl acrylate / acrylic acid = 80
Emulsion 15 g (resin content 1 g) having an average particle size of 0.7 μm consisting of mol% / 20 mol% and hydrophobic adhesive 63
As an average particle size of 0.4 μm consisting of n-butyl acrylate / dodecyl acrylate = 75 mol% / 25 mol%
5 g of the emulsion of m (resin content 1 g) was dropped, and the hydrophobic and hydrophilic adhesives 63, 7 were applied to the spacer surface.
An adhesive layer consisting of 3 was irregularly formed.
【0021】この接着剤つきスペーサ53を用いて、実
施例1と同様に液晶セルを作製し、スペーサ周囲の光抜
けを観察した。さらに、実施例1と同様にスペーサ53
の固着性も観察した。結果を表1に示す。 〔実施例4〕水/イソプロピルアルコール=85wt%
/15wt%からなる分散媒100gに、スペーサ(ス
チレン・ジビニルベンゼン共重合体の微球体スペーサ、
粒径6μm)54を分散させたものに、親水性接着剤7
4として、n−ブチルアクリレート/2−エチルヒドロ
キシアクリレート=60モル%/40モル%からなる平
均粒径0.7μmのエマルジョン15g(樹脂分1g)
および疎水性接着剤64として、n−ブチルアクリレー
ト/パーフロロヘキシルアクリレート=80モル%/2
0モル%からなる平均粒径0.4μmのエマルジョン5
g(樹脂分1g)をそれぞれ滴下して、スペーサ表面に
疎水性および親水性接着剤64,74からなる接着層を
不規則に形成した。Using this adhesive-attached spacer 53, a liquid crystal cell was prepared in the same manner as in Example 1, and the light leakage around the spacer was observed. Further, as in the first embodiment, the spacer 53
Was also observed. Table 1 shows the results. Example 4 Water / isopropyl alcohol = 85 wt%
Spacer (styrene / divinylbenzene copolymer microsphere spacer,
The hydrophilic adhesive 7 is added to a dispersion of 54 (particle size 6 μm).
4, 15 g of emulsion having an average particle size of 0.7 μm (n-butyl acrylate / 2-ethyl hydroxyacrylate = 60 mol% / 40 mol%, resin content 1 g)
And as the hydrophobic adhesive 64, n-butyl acrylate / perfluorohexyl acrylate = 80 mol% / 2
Emulsion 5 consisting of 0 mol% and having an average particle size of 0.4 μm 5
Then, g (resin content: 1 g) was dropped, and an adhesive layer composed of hydrophobic and hydrophilic adhesives 64 and 74 was irregularly formed on the spacer surface.
【0022】この接着剤つきスペーサ54を用いて、実
施例1と同様に液晶セルを作製し、スペーサ周囲の光抜
けを観察した。また、実施例1と同様にスペーサ54の
固着性も観察した。結果を表1に示す。 〔比較例1〕実施例1における親水性接着剤を全く用い
ず、疎水性接着剤n−ブチルアクリレート/ラウリルア
クリレート=75モル%/25モル%からなるエマルジ
ョン20g(樹脂分2g)のみを用いて、スペーサ表面
に疎水性接着剤層を形成した。Using this adhesive-attached spacer 54, a liquid crystal cell was prepared in the same manner as in Example 1, and the light leakage around the spacer was observed. In addition, similarly to Example 1, the adhesiveness of the spacer 54 was also observed. Table 1 shows the results. Comparative Example 1 The hydrophilic adhesive in Example 1 was not used at all, and only 20 g of emulsion (resin content 2 g) composed of the hydrophobic adhesive n-butyl acrylate / lauryl acrylate = 75 mol% / 25 mol% was used. A hydrophobic adhesive layer was formed on the spacer surface.
【0023】この接着剤つきスペーサを用いて、実施例
1と同様に液晶セルを作製し、スペーサ周囲の光抜けを
観察した。また、実施例1と同様にスペーサの固着性を
観察した。結果を表1に示す。 〔比較例2〕実施例1における疎水性接着剤を全く用い
ず、親水性接着剤n−ブチルアクリレート/メタクリル
酸=75モル%/25モル%からなるエマルジョン20
g(樹脂分2g)のみを用いて、スペーサ表面に親水性
接着剤層を形成した。Using this adhesive-attached spacer, a liquid crystal cell was prepared in the same manner as in Example 1, and light leakage around the spacer was observed. Further, similarly to Example 1, the adhesiveness of the spacer was observed. Table 1 shows the results. [Comparative Example 2] Emulsion 20 composed of hydrophilic adhesive n-butyl acrylate / methacrylic acid = 75 mol% / 25 mol% without using the hydrophobic adhesive in Example 1 at all.
A hydrophilic adhesive layer was formed on the spacer surface using only g (resin content 2 g).
【0024】この接着剤つきスペーサを用いて、実施例
1と同様に液晶セルを作製し、スペーサ周囲の光抜けを
観察した。さらに、実施例1と同様にスペーサの固着性
も観察した。結果を表1に示す。Using this spacer with an adhesive, a liquid crystal cell was prepared in the same manner as in Example 1, and light leakage around the spacer was observed. Further, similarly to Example 1, the adhesiveness of the spacer was also observed. Table 1 shows the results.
【0025】[0025]
【表1】 [Table 1]
【0026】このように、本実施例では、表1より明ら
かなように、スペーサ周囲の光抜けが防止でき、スペー
サの固着性を向上できることが分かる。よって、液晶デ
ィスプレーのコントラストを向上することができ、表示
むらを防止することができる。以上、本発明者によって
なされた発明を、実施例に基づき具体的に説明したが、
本発明は、前記実施例に限定されるものではなく、その
要旨を逸脱しない範囲で、種々変更可能であることは、
言うまでもない。Thus, in this embodiment, as is clear from Table 1, light leakage around the spacer can be prevented, and the fixing property of the spacer can be improved. Therefore, the contrast of the liquid crystal display can be improved, and display unevenness can be prevented. As described above, the invention made by the present inventor has been specifically described based on Examples.
The present invention is not limited to the above-mentioned embodiment, and various modifications can be made without departing from the scope of the invention.
Needless to say.
【0027】[0027]
【発明の効果】本願によって開示される発明によって得
られる効果を簡単に説明すれば、以下のとおりである。
本発明によれば、スペーサの表面に親水性接着剤および
疎水性接着剤が不規則に付着されたので、液晶分子はス
ペーサの表面方向に不規則な方向に束縛されると共に、
液晶セル内のスペーサの移動が防止される。The effects obtained by the invention disclosed in the present application will be briefly described as follows.
According to the present invention, since the hydrophilic adhesive and the hydrophobic adhesive are irregularly adhered to the surface of the spacer, the liquid crystal molecules are bound in the surface direction of the spacer in an irregular direction, and
The movement of the spacer in the liquid crystal cell is prevented.
【0028】従って、表示むらを防止することができる
と共に、スペーサ周囲の光抜けが防止でき、液晶ディス
プレーのコントラストを向上することができる。また、
スペーサは、その表面に疎水性接着剤および親水性接着
剤を不規則に付着するだけの簡便な製造工程によって容
易に作製することができる。Therefore, display unevenness can be prevented, light leakage around the spacers can be prevented, and the contrast of the liquid crystal display can be improved. Also,
The spacer can be easily manufactured by a simple manufacturing process in which a hydrophobic adhesive and a hydrophilic adhesive are irregularly attached to the surface of the spacer.
【図1】本発明の実施例である液晶ディスプレーの要部
断面図である。FIG. 1 is a cross-sectional view of essential parts of a liquid crystal display that is an embodiment of the present invention.
【符号の説明】 10 ガラス基板 20 透明電極 30 配向膜 40 液晶組成物 51,52,53,54 スペーサ 61,62,63,64 疎水性接着剤 71,72,73,74 親水性接着剤[Explanation of Codes] 10 Glass Substrate 20 Transparent Electrode 30 Alignment Film 40 Liquid Crystal Composition 51, 52, 53, 54 Spacers 61, 62, 63, 64 Hydrophobic Adhesive 71, 72, 73, 74 Hydrophilic Adhesive
Claims (2)
に液晶組成物と共に介在され、前記電極基板の間隔を制
御する液晶ディスプレー用スペーサにおいて、表面上
に、疎水性接着剤と親水性接着剤とが付着されたことを
特徴とする液晶ディスプレー用スペーサ。1. In a spacer for a liquid crystal display, which is interposed between electrode substrates facing each other of a liquid crystal display together with a liquid crystal composition to control a distance between the electrode substrates, a hydrophobic adhesive and a hydrophilic adhesive are provided on a surface of the spacer. Spacer for liquid crystal display characterized by being attached.
に液晶組成物と共に介在され、前記電極基板の間隔を制
御する液晶ディスプレー用スペーサにおいて、表面上
に、疎水性接着剤および親水性接着剤が付着された領域
を、不規則に有することを特徴とする液晶ディスプレー
用スペーサ。2. In a spacer for a liquid crystal display, which is interposed between electrode substrates facing each other of a liquid crystal display together with a liquid crystal composition to control a gap between the electrode substrates, a hydrophobic adhesive and a hydrophilic adhesive are attached on the surface. A spacer for a liquid crystal display, characterized by having irregular areas.