JPH0823940B2 - Optical information recording medium - Google Patents

Optical information recording medium

Info

Publication number
JPH0823940B2
JPH0823940B2 JP63239165A JP23916588A JPH0823940B2 JP H0823940 B2 JPH0823940 B2 JP H0823940B2 JP 63239165 A JP63239165 A JP 63239165A JP 23916588 A JP23916588 A JP 23916588A JP H0823940 B2 JPH0823940 B2 JP H0823940B2
Authority
JP
Japan
Prior art keywords
layer
intermediate layer
recording medium
information recording
light
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP63239165A
Other languages
Japanese (ja)
Other versions
JPH0287341A (en
Inventor
雄治 新井
恵美子 浜田
有明 辛
隆 石黒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taiyo Yuden Co Ltd
Original Assignee
Taiyo Yuden Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taiyo Yuden Co Ltd filed Critical Taiyo Yuden Co Ltd
Priority to JP63239165A priority Critical patent/JPH0823940B2/en
Priority to US07/340,082 priority patent/US4990388A/en
Priority to US07/340,544 priority patent/US5155723A/en
Priority to AT89106810T priority patent/ATE112649T1/en
Priority to ES89106810T priority patent/ES2064377T3/en
Priority to DE68918652T priority patent/DE68918652T2/en
Priority to DE68924016T priority patent/DE68924016T3/en
Priority to EP89106873A priority patent/EP0353394B2/en
Priority to EP19890106810 priority patent/EP0353392B1/en
Priority to AT89106873T priority patent/ATE127265T1/en
Priority to ES89106873T priority patent/ES2078901T5/en
Priority to CA 599417 priority patent/CA1332466C/en
Priority to CA000599416A priority patent/CA1331807C/en
Priority to MYPI89000677A priority patent/MY106947A/en
Priority to MYPI89000675A priority patent/MY104122A/en
Priority to AU35108/89A priority patent/AU626072B2/en
Priority to AU35105/89A priority patent/AU626071B2/en
Priority to DK198902543A priority patent/DK174110B1/en
Priority to DK198902544A priority patent/DK175044B1/en
Priority to PH38708A priority patent/PH26093A/en
Priority to PH38708D priority patent/PH26092A/en
Priority to KR1019890010425A priority patent/KR950005034B1/en
Priority to KR1019890010424A priority patent/KR950006839B1/en
Priority to FI893561A priority patent/FI893561A/en
Priority to FI893562A priority patent/FI893562A/en
Priority to PT91310A priority patent/PT91310B/en
Priority to PT91311A priority patent/PT91311B/en
Publication of JPH0287341A publication Critical patent/JPH0287341A/en
Priority to HK114195A priority patent/HK114195A/en
Publication of JPH0823940B2 publication Critical patent/JPH0823940B2/en
Priority to HK105796A priority patent/HK105796A/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 [産業上の利用分野] 本発明は、レーザ光を照射し、その反射光により記録
データを再生する光情報記録媒体に関する。
TECHNICAL FIELD The present invention relates to an optical information recording medium that irradiates a laser beam and reproduces recorded data by the reflected light.

[従来の技術] レーザ光の照射により、データを記録することができ
る光情報記録媒体は、Te、Bi、Mn等の金属層や、シアニ
ン、メロシアニン、フタロシアニン等の色素層等からな
る記録層を有し、レーザ光の照射により、上記記録層を
変形、昇華、蒸発或は変性させる等の手段で、ピットを
形成し、データを記録する。このような記録層を有する
光情報記録媒体では、ピットを形成する際の記録層の変
形、昇華、蒸発或は変性等を容易にするため、記録層の
背後に空隙を設けることが一般に行なわれている。具体
的には例えば、空間部を挟んで2枚の基板を積層する、
いわゆるエアサンドイッチ構造と呼ばれる積層構造がと
られる。
[Prior Art] An optical information recording medium capable of recording data by irradiating a laser beam has a recording layer including a metal layer such as Te, Bi and Mn and a dye layer such as cyanine, merocyanine and phthalocyanine. The pits are formed and the data is recorded by means of deforming, sublimating, evaporating or modifying the recording layer by irradiating the laser beam. In an optical information recording medium having such a recording layer, a void is generally provided behind the recording layer in order to facilitate deformation, sublimation, evaporation or modification of the recording layer when forming pits. ing. Specifically, for example, two substrates are stacked with a space in between,
A laminated structure called a so-called air sandwich structure is adopted.

この光情報記録媒体では、上記透光性を有する基板1
側からレーザ光を照射し、ピットを形成する。そして、
記録されたデータを再生するときは、上記基板1側から
記録時よりパワーの弱いレーザ光を照射し、上記ピット
とそれ以外の部分との反射光の違いにより、信号を読み
とる。
In this optical information recording medium, the translucent substrate 1 is used.
Laser light is irradiated from the side to form pits. And
When the recorded data is reproduced, a laser beam whose power is weaker than that at the time of recording is emitted from the side of the substrate 1, and a signal is read due to the difference in reflected light between the pit and other portions.

一方、予めデータが記録され、その後のデータの書き
込みや消去ができない、いわゆるROM型光情報記録媒体
が情報処理や音響部門で既に広く実用化されている。こ
の種の光情報記録媒体は、上記のような記録層を持た
ず、記録データを再生するためのピットを予めプレス等
の手段でポリカーボネート製の基板の上に形成し、この
上にAu、Ag、Cu、Al等の金属膜からなる反射層を形成
し、さらにこの上を保護層で覆ったものである。
On the other hand, a so-called ROM type optical information recording medium in which data is recorded in advance and the data cannot be written or erased thereafter has already been widely put to practical use in the information processing and audio departments. This kind of optical information recording medium does not have a recording layer as described above, and pits for reproducing recorded data are formed beforehand on a polycarbonate substrate by means of a press or the like, and Au, Ag A reflective layer made of a metal film such as Cu, Al or the like is formed and further covered with a protective layer.

このROM型光情報記録媒体で最も代表的なものが音響
部門や情報処理部門等で広く実用化されているコンパク
トディスク、いわゆるCDであり、このCDの記録、再生信
号の仕様は、いわゆるCDフォーマットとして規格化さ
れ、これに準拠する再生装置は、コンパクトディスクプ
レーヤ(CDプレーヤ)として極めて広く普及している。
The most typical of these ROM type optical information recording media is a compact disc, a so-called CD, which has been widely put into practical use in the audio sector and the information processing sector. The specifications of the recording and reproducing signals of this CD are the so-called CD format. A playback device that has been standardized as, and is compliant with this, is extremely widespread as a compact disc player (CD player).

[発明が解決しようとする課題] 上記光情報記録媒体は、CDと同じレーザ光を用いる記
録、再生手段であるため、既に再生装置が広く普及して
いるCDプレーヤで再生できること、すなわち、CDフォー
マットに準拠することが強く望まれる。
[Problems to be Solved by the Invention] Since the above optical information recording medium is a recording / reproducing means that uses the same laser light as that of a CD, it can be reproduced by a CD player whose reproducing device is already widespread, that is, a CD format. It is strongly desired to comply with.

しかしながら、上記の光情報記録媒体は、CDには無い
記録層を有し、基板にではなく、この記録層にピットを
形成して記録する手段がとられる。さらに、この記録層
にピットを形成するのを容易にするための空隙等を有す
ることから、再生信号が自ずとCDと異なってくる。この
ため、いわゆるCDについての規格を定めた上記CDフォー
マットを満足することが困難であった。特に、再生信号
の変調度が低いことにより、CDフォーマットに準拠した
再生信号が得られないのが現状である。
However, the above-mentioned optical information recording medium has a recording layer not found in CD, and means for forming pits on this recording layer, not on the substrate, is used for recording. Further, since the recording layer has voids or the like for facilitating the formation of pits, the reproduced signal naturally differs from that of the CD. For this reason, it is difficult to satisfy the above-mentioned CD format that defines the standard for so-called CD. In particular, under the present circumstances, a reproduction signal conforming to the CD format cannot be obtained due to the low degree of modulation of the reproduction signal.

本発明は、上記従来の問題点を解消するためなされた
もので、その目的は、CDフォーマットに準拠した変調度
の高い再生信号が得られる書き込みが可能な光情報記録
媒体を提供することにある。
The present invention has been made to solve the above-mentioned conventional problems, and an object thereof is to provide a writable optical information recording medium capable of obtaining a reproduction signal having a high degree of modulation conforming to the CD format. .

[課題を解決するための手段] すなわち、上記目的を達成するため、本発明において
採用した第一の手段の要旨は、透光性基板1の上に他の
層を介してレーザ光を吸収する光吸収層2と、光吸収層
2の上に直接または他の層を介して設けられたレーザ光
を反射する光反射層3とを有する光情報記録媒体におい
て、光吸収層2がレーザ光の照射により、発熱と圧力増
大を伴う材料を含有し、この光吸収層2と、透光性基板
1との間に中間層6を介在させ、この中間層6のロック
ウェル硬度がASTM D785でM100〜50であることを特徴と
する光情報記録媒体である。
[Means for Solving the Problem] That is, in order to achieve the above-mentioned object, the gist of the first means adopted in the present invention is to absorb laser light through another layer on the transparent substrate 1. In an optical information recording medium having a light absorbing layer 2 and a light reflecting layer 3 provided on the light absorbing layer 2 directly or via another layer, which reflects the laser light, A material containing heat and pressure increase by irradiation is contained, and an intermediate layer 6 is interposed between the light absorption layer 2 and the transparent substrate 1. The intermediate layer 6 has a Rockwell hardness of ASTM D785 of M100. The optical information recording medium is characterized in that

第二の手段の要旨は、前記光情報記録媒体において、
中間層6の熱変形温度がASTM D648 4.6Kg/cm2で50〜150
℃である光情報記録媒体である。
The gist of the second means is, in the optical information recording medium,
The heat distortion temperature of the mid layer 6 is 50 to 150 at ASTM D648 4.6 Kg / cm 2 .
The optical information recording medium has a temperature of ° C.

[作用] 上記光情報記録媒体では、光吸収層2にレーザ光を照
射したとき、同光吸収層2がレーザ光を吸収して発熱
し、溶融、蒸発、昇華、反応、分解或は変性する等し
て、熱や圧力増大として局部的なエネルギーの変換がな
されるが、このとき、透光性基板1と光吸収層2との間
に介在された中間層6の熱変形温度がASTM D648 4.6Kg/
cm2で50〜150℃の範囲であり、あるいはロックウェル硬
度がASTM D785でM100〜50の範囲であることから、上記
光吸収層2で発生したエネルギーが中間層6の表面の局
部的な変形によって吸収される。このため、同層6に上
記変形によるピット5が形成される。
[Operation] In the above optical information recording medium, when the light absorption layer 2 is irradiated with laser light, the light absorption layer 2 absorbs the laser light and generates heat, and is melted, evaporated, sublimated, reacted, decomposed or modified. As a result, local energy conversion is performed as heat and pressure increase. At this time, the heat distortion temperature of the intermediate layer 6 interposed between the transparent substrate 1 and the light absorbing layer 2 is ASTM D648. 4.6Kg /
The energy generated in the light absorbing layer 2 is locally deformed on the surface of the intermediate layer 6 because the Rockwell hardness is in the range of 50 to 150 ° C. in cm 2 or the Rockwell hardness is in the range of M100 to 50 in ASTM D785. Absorbed by Therefore, the pits 5 are formed in the same layer 6 by the above deformation.

こうして、中間層6に形成されるピット5は、予めプ
レス等の手段によって透光性基板の表層に形成されるピ
ットに近似するものである。また、光吸収層2の背後に
密着して他の層、例えば金属層による光反射層3を設け
ることができる。従って、形態的にもCDに近似した光情
報記録媒体が得られ、CDフォーマットに準拠した記録可
能な光情報記録媒体が容易に得られる。
Thus, the pits 5 formed in the intermediate layer 6 are similar to the pits previously formed in the surface layer of the translucent substrate by means such as pressing. Further, another layer, for example, the light reflection layer 3 made of a metal layer can be provided in close contact with the back of the light absorption layer 2. Therefore, an optical information recording medium similar in form to a CD can be obtained, and a recordable optical information recording medium conforming to the CD format can be easily obtained.

ここで、中間層6の熱変形温度、或は硬度を前記の範
囲に限定したのは、次の理由による。すなわち、中間層
の熱変形温度が上記範囲に満たないときは、一旦形成し
たピット5がその後受ける熱によって容易に変形してし
まうため、記録されたデータの安定性が悪い。また、中
間層6の熱変形温度が上記範囲を越えるときは、光吸収
層2で発生したエネルギーを、中間層6の変形という形
で吸収しにくいため、明瞭なピット5が形成できず、変
調度の大きな再生信号が得られない。硬度についても同
様で、中間層6の硬度が上記範囲に満たないときは、一
旦形成したピット5が小さな外力によって容易に変形さ
れてしまうため、記録されたデータの安定性が悪い。ま
た、中間層6の硬度が上記範囲を越えるときは、光吸収
層2で発生したエネルギーを、中間層6の変形という形
で吸収しにくいため、明瞭なピット5が形成できず、変
調度の大きな再生信号が得られない。
Here, the reason why the heat distortion temperature or hardness of the mid layer 6 is limited to the above range is as follows. That is, when the thermal deformation temperature of the intermediate layer is less than the above range, the pits 5 once formed are easily deformed by the heat received thereafter, and the stability of the recorded data is poor. Further, when the thermal deformation temperature of the intermediate layer 6 exceeds the above range, it is difficult to absorb the energy generated in the light absorption layer 2 in the form of the deformation of the intermediate layer 6, so that the clear pit 5 cannot be formed and the modulation occurs. A reproduced signal with a high frequency cannot be obtained. The same applies to the hardness. When the hardness of the intermediate layer 6 is less than the above range, the pits 5 once formed are easily deformed by a small external force, and the stability of the recorded data is poor. Further, when the hardness of the intermediate layer 6 exceeds the above range, the energy generated in the light absorption layer 2 is difficult to be absorbed in the form of deformation of the intermediate layer 6, so that clear pits 5 cannot be formed and the modulation degree is reduced. No large playback signal can be obtained.

[実施例] 次に、図面を参照しながら、本発明の実施例について
詳細に説明する。
[Embodiment] Next, an embodiment of the present invention will be described in detail with reference to the drawings.

本発明による光情報記録媒体の模式的な構造の例を、
第1図〜第3図に示す。同図において、1は、透光性を
有する基板、6は、その上に形成された樹脂等からなる
中間層、2は、さらにその上に形成された光吸収層で、
照射されたレーザ光を吸収して発熱し、溶融、蒸発、昇
華、変形または変性し、上記中間層6を局部的に変形さ
せ、光学的に変性したピットを形成する作用を有する層
である。
An example of a schematic structure of the optical information recording medium according to the present invention,
It is shown in FIGS. In the figure, 1 is a translucent substrate, 6 is an intermediate layer made of a resin or the like formed thereon, 2 is a light absorbing layer further formed thereon,
It is a layer having a function of absorbing the irradiated laser beam to generate heat, melt, evaporate, sublimate, deform or modify, locally deform the intermediate layer 6 to form an optically modified pit.

既に述べた通り、本発明においては、上記中間層6の
熱変形温度がASTM D648 4.6Kg/cm2で50〜150℃、或はロ
ックウェル硬度がASTM D785でM100〜50の範囲であるこ
とが必要である。他方、光吸収層2の背後側、例えば、
保護層4は、この中間層6より熱変形温度が高く、かつ
硬度が高いものがよい。3は、光吸収層2の上に形成さ
れたレーザ光を反射する光反射層、4は、その外側に設
けられた保護層を示す。
As described above, in the present invention, the heat distortion temperature of the intermediate layer 6 is in the range of 50 to 150 ° C. at ASTM D648 4.6 Kg / cm 2 , or the Rockwell hardness is in the range of M100 to 50 at ASTM D785. is necessary. On the other hand, behind the light absorption layer 2, for example,
The protective layer 4 preferably has a higher heat distortion temperature and a higher hardness than the intermediate layer 6. Reference numeral 3 denotes a light reflection layer which is formed on the light absorption layer 2 and reflects the laser light, and 4 denotes a protective layer which is provided outside thereof.

なお、第2図と第4図は、レーザ光による記録前の状
態を、第3図と第5図は、記録後の状態、すなわち、レ
ーザ光の照射時の光吸収層2の局部的な熱変形により、
中間層6が一部変形され、ピット5が形成された状態を
模式的に示す。第3図は、レーザ光の照射に伴う光吸収
層2の発熱、圧力増大による変形が、実質的に中間層6
にのみ及び、透光性基板1には、殆ど及んでいない状態
を示している。これに対し、第5図は、変形が中間層6
のみならず、透光性基板1へも及び、中間層6から透光
性基板1にわたってピット5が形成されている場合を示
している。一般には、中間層の膜厚が30nm以下というよ
うに、薄い場合で、かつ透光性基板1の熱変形温度がAS
TM D648 4.6Kg/cm2で85〜200℃で、ロックウェル硬度が
ASTM D785でM200〜75程度である場合、後者のようなピ
ット5が形成される。
2 and 4 show a state before recording with laser light, and FIGS. 3 and 5 show a state after recording, that is, a local state of the light absorption layer 2 at the time of laser light irradiation. Due to thermal deformation,
The state in which the intermediate layer 6 is partially deformed and the pits 5 are formed is schematically shown. FIG. 3 shows that the heat absorption of the light absorption layer 2 due to the irradiation of the laser light and the deformation due to the increase in pressure are substantially caused by the intermediate layer 6.
1 and the transparent substrate 1 is barely reached. On the other hand, in FIG.
Not only that, the case where the pits 5 are formed over the transparent substrate 1 and from the intermediate layer 6 to the transparent substrate 1 is shown. Generally, when the thickness of the intermediate layer is as thin as 30 nm or less, and the heat distortion temperature of the transparent substrate 1 is AS.
TM D648 4.6 Kg / cm 2 85 ~ 200 ℃, Rockwell hardness
If it is about M200 to 75 according to ASTM D785, the pit 5 like the latter is formed.

本発明では、第3図と第5図の何れの形態のピット5
が形成されても、差し支えない。
In the present invention, the pit 5 of any of the forms shown in FIGS.
It does not matter even if the formation is made.

この光情報記録媒体の具体例について、以下に説明す
る。
A specific example of this optical information recording medium will be described below.

(実施例1) 透光性基板1として、射出成型法により形成された直
径46〜117mmφの範囲に、幅0.8μm、深さ0.08μm、ピ
ッチ1.6μmのスパイラル状のプレグルーブ8を有する
厚さ1.2mm、外径120mmφ、内径15mmφのポリカーボネー
ト製円板(帝人化成(株)製、商品名:パンライト)を
用いた。このポリカーボネート基板1のロックウェル硬
度ASTMは、D785でM75であり、熱変形温度ASTMは、D64
8、4.6kg/cm2で130℃である。
(Example 1) As a light-transmissive substrate 1, a thickness having a spiral pre-groove 8 having a width of 0.8 µm, a depth of 0.08 µm, and a pitch of 1.6 µm in a diameter range of 46 to 117 mmφ formed by an injection molding method. A polycarbonate disc having a diameter of 1.2 mm, an outer diameter of 120 mmφ and an inner diameter of 15 mmφ (manufactured by Teijin Chemicals Ltd., trade name: Panlite) was used. The polycarbonate substrate 1 has a Rockwell hardness ASTM of D785 of M75 and a heat distortion temperature ASTM of D64.
8, 4.6kg / cm 2 and 130 ℃.

この透光性基板1の上に中間層6としてアクリル樹脂
(サンノプコ製のSN-EX7042)を厚さ70nmにスピンコー
トで形成し、さらにこの上に、光吸収層2を形成するた
めの有機色素として、0.65gの1,1′ジプロピル3,3,3′,
3′テトラメチル5,5′ジメトキシインドジカーボシアニ
ンアイオダイドを、ジアセトンアルコール溶剤10ccに溶
解し、これを上記の基板1の表面に、スピンコート法に
より塗布し、膜厚90nmの光吸収層2を形成した。上記中
間層6の熱変形温度ASTMは、D648、4.6kg/cm2で100℃、
ロックウェル硬度ASTMは、D785でM85である。
An acrylic resin (SN-EX7042 made by San Nopco) is spin-coated on the transparent substrate 1 as the intermediate layer 6 to a thickness of 70 nm, and an organic dye for forming the light absorbing layer 2 on the spin coating. As 0.65 g of 1,1 ′ dipropyl 3,3,3 ′,
3'Tetramethyl 5,5 'dimethoxyindodicarbocyanine iodide was dissolved in 10 cc of diacetone alcohol solvent, and this was coated on the surface of the substrate 1 by spin coating to form a light absorption layer having a thickness of 90 nm. Formed 2. The heat distortion temperature ASTM of the intermediate layer 6 is D648, 4.6 kg / cm 2 , 100 ° C,
Rockwell hardness ASTM is D85 and M85.

次に、上記光吸収層2の上に、シリコンアクリル樹脂
を厚さ50nmスピンコートで形成した後、ディスクの直径
45〜118nmφの領域の全面にスパッタリング法により、
膜厚50nmのAu膜を成膜し、光反射層3を形成した。さら
に、この光反射層3の上に紫外線硬化性樹脂をスピンコ
ートし、これに紫外線を照射して硬化させ、膜厚10μm
の保護層4を形成した。
Next, a silicon acrylic resin is formed on the light absorption layer 2 by spin coating with a thickness of 50 nm, and then the diameter of the disc is increased.
By the sputtering method over the entire area of 45 ~ 118 nmφ,
An Au film having a film thickness of 50 nm was formed to form the light reflecting layer 3. Further, an ultraviolet curable resin is spin-coated on the light reflecting layer 3 and is irradiated with ultraviolet rays to cure the resin so that the film thickness is 10 μm.
Was formed on the protective layer 4.

こうして得られた光ディスクに波長780nmの半導体レ
ーザを線速1.2m/sec、記録パワー6.0mWで照射し、EFM信
号を記録した。そして、この光ディスクを、市販のCDプ
レーヤ(Aurex XR-V73、再生光の波長λ=780nm)で再
生したところ、再生信号のアイパターンから得られるI
11/Itopが0.63、I3/Itopが0.32であった。
The optical disk thus obtained was irradiated with a semiconductor laser having a wavelength of 780 nm at a linear velocity of 1.2 m / sec and a recording power of 6.0 mW to record an EFM signal. Then, when this optical disk was reproduced with a commercially available CD player (Aurex XR-V73, reproduction light wavelength λ = 780 nm), I obtained from the eye pattern of the reproduction signal
11 / Itop was 0.63 and I 3 / Itop was 0.32.

CD規格では、I11/Itopが0.6以上、I3/Itopが0.3〜0.7
と定められており、この実施例による光ディスクは、こ
の規格を満足している。
According to the CD standard, I 11 / Itop is 0.6 or more, I 3 / Itop is 0.3 to 0.7
The optical disc according to this embodiment satisfies this standard.

さらにこの記録後の光ディスクの上記保護層4、光反
射層3及び光吸収層2を剥離し、中間層6の表面を観察
したところ、そこに光学的に変性した凸状のピット5が
形成されているのが確認された。
Further, when the protective layer 4, the light reflecting layer 3 and the light absorbing layer 2 of the optical disc after the recording were peeled off and the surface of the intermediate layer 6 was observed, optically modified convex pits 5 were formed there. Was confirmed.

(実施例2) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で80℃、ロックウェル硬度ASTMが
D785でM95の塩化ビニル共重合体(積水化学製のエスレ
ックA)により、60nmの厚さに形成したこと以外は、上
記実施例1と同様にして光ディスクを製作した。
(Example 2) In Example 1 above, the intermediate layer 6 has a heat distortion temperature.
ASTM D648 is 4.6 kg / cm 2 at 80 ° C, Rockwell hardness ASTM is
An optical disk was produced in the same manner as in Example 1 except that the D785 was formed from a vinyl chloride copolymer of M95 (Eslec A manufactured by Sekisui Chemical Co., Ltd.) to a thickness of 60 nm.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.66、I3/Itopが0.35で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.66, and I 3 / Itop was 0.35.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例3) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で90℃、ロックウェル硬度ASTMが
D785でM100のアクリル樹脂(サンノプコ製のSN-EX559
5)により形成したこと、光吸収層2の膜厚を130nmとし
たこと、光吸収層2と光反射層3との間にシリコンアク
リル樹脂層を形成しなかったこと、及び反射層3をAuと
Irとの9:1の合金膜により形成したこと以外は、上記実
施例1と同様にして光ディスクを製作した。
(Example 3) In Example 1, the intermediate layer 6 has a heat distortion temperature.
ASTM D648 is 4.6 kg / cm 2 at 90 ° C, Rockwell hardness ASTM is
D785 M100 acrylic resin (San Nopco SN-EX559
5), the thickness of the light absorption layer 2 was set to 130 nm, the silicon acrylic resin layer was not formed between the light absorption layer 2 and the light reflection layer 3, and the reflection layer 3 was made of Au. When
An optical disk was manufactured in the same manner as in Example 1 except that it was formed of a 9: 1 alloy film with Ir.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.63、I3/Itopが0.32で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.63, and I 3 / Itop was 0.32.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例4) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で85℃、ロックウェル硬度ASTMが
D785でM70のポリスチレン(三洋化成製のST-95)により
形成したこと以外は、上記実施例1と同様にして光ディ
スクを製作した。
(Example 4) In Example 1 above, as the intermediate layer 6, a heat distortion temperature was used.
ASTM D648 is 4.6 kg / cm 2 at 85 ℃, Rockwell hardness ASTM is
An optical disk was produced in the same manner as in Example 1 except that the D785 was formed of M70 polystyrene (ST-95 manufactured by Sanyo Kasei).

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.65、I3/Itopが0.34で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.65, and I 3 / Itop was 0.34.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例5) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で55℃、ロックウェル硬度ASTMが
D785でM70のポリ酢酸ビニル(三井ポリケミカル製のエ
バフレックス)により厚さ60nmに形成したこと、及びシ
リコンアクリル樹脂の上に、さらにイソシアネートを10
nmスピンコートしたこと以外は、上記実施例1と同様に
して光ディスクを製作した。
Example 5 In Example 1 above, the intermediate layer 6 has a heat distortion temperature.
ASTM D648 is 4.6 kg / cm 2 at 55 ° C, Rockwell hardness ASTM is
D785 was used to form M60 polyvinyl acetate (Evaflex made by Mitsui Polychemicals) to a thickness of 60 nm.
An optical disk was manufactured in the same manner as in Example 1 except that the spin coating was performed in nm.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.66、I3/Itopが0.32で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.66, and I 3 / Itop was 0.32.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例6) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で50℃、ロックウェル硬度ASTMが
D785でM60のポリウレタン樹脂(日本ポリウレタン工業
製のニッポラン133と同社製のコロネートLとを1:1に配
合)により厚さ50nmに形成したこと、この中間層6の上
にシリコン樹脂を厚さ15nmスピンコートで形成して耐溶
剤処理した後、1、1′ジブチル3、3、3′、3′テ
トラメチル4、5、4′5′ジベンゾインドジカーボシ
アニンパークロレートを用いて厚さ130nmの光吸収層2
を形成したこと、光吸収層2と光反射層3との間にシリ
コンアクリル樹脂をコーティングしなかったこと、及び
反射層3をAuとIrとの9:1の合金膜により形成したこと
以外は、上記実施例1と同様にして光ディスクを製作し
た。
(Example 6) In Example 1 above, the intermediate layer 6 has a heat distortion temperature.
ASTM D648 is 4.6 kg / cm 2 at 50 ° C, Rockwell hardness ASTM is
D60 was used to form M60 polyurethane resin (Nipporan 133 manufactured by Nippon Polyurethane Industry Co., Ltd. and Coronate L manufactured by the same company in a ratio of 1: 1) to a thickness of 50 nm. After spin-coating and solvent-resistant treatment, 1,1'dibutyl 3,3,3 ', 3'tetramethyl 4,5,4'5'dibenzoindodicarbocyanine perchlorate having a thickness of 130 nm was used. Light absorption layer 2
Except that a silicon acrylic resin was not coated between the light absorption layer 2 and the light reflection layer 3 and that the reflection layer 3 was formed of a 9: 1 alloy film of Au and Ir. An optical disk was manufactured in the same manner as in Example 1 above.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.66、I3/Itopが0.33で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.66, and I 3 / Itop was 0.33.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例7) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で50℃、ロックウェル硬度ASTMが
D785でM60のポリウレタン樹脂(日本ポリウレタン工業
製のニッポラン133と同社製のコロネートLとを1:1に配
合)により厚50nmに形成したこと、この中間層6の上に
シリコン系コート剤を厚さ15nmスピンコートで形成して
耐溶剤処理した後、1、1′ジブチル3、3、3′、
3′テトラメチル4、5、4′5′ジベンゾインドジカ
ーボシアニンパークロレートを用いて光吸収層2を形成
したこと、この光吸収層2の上にシリコンアクリル樹脂
に代えてシリコン樹脂を形成したこと、及び光反射層3
の上にポリサルファイド添加エポキシ樹脂を20nmコーデ
ィングで形成した上に保護層4を設けたこと以外は、上
記実施例1と同様にして光ディスクを製作した。
(Embodiment 7) In the above-mentioned Embodiment 1, the intermediate layer 6 has a heat distortion temperature.
ASTM D648 is 4.6 kg / cm 2 at 50 ° C, Rockwell hardness ASTM is
D60 was used to form M60 polyurethane resin (Nipporan 133 manufactured by Nippon Polyurethane Industry Co., Ltd. and Coronate L manufactured by the same company in a ratio of 1: 1) to a thickness of 50 nm. After 15 nm spin coating and solvent-resistant treatment, 1,1'dibutyl 3,3,3 ',
The light absorbing layer 2 was formed using 3'tetramethyl 4,5,4'5 'dibenzoindodicarbocyanine perchlorate, and a silicon resin was formed on the light absorbing layer 2 instead of the silicon acrylic resin. And the light reflection layer 3
An optical disk was manufactured in the same manner as in Example 1 except that the protective layer 4 was provided on the polysulfide-added epoxy resin formed by 20 nm coding on the above.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.66、I3/Itopが0.33で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.66, and I 3 / Itop was 0.33.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例8) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で60℃、ロックウェル硬度ASTMが
D785でM100のヒドロキシプロピルセルロースにより形成
したこと、光吸収層2を形成する有機色素として、1、
1′ジブチル3、3、3′、3′テトラメチル4、5、
4′5′ジベンゾインドジカーボシアニンパークロレー
トを用いたこと、及び光吸収層2の上に、シリコンアク
リル樹脂に代えて、シリコン樹脂をコーディングした以
外は、上記実施例1と同様にして光ディスクを製作し
た。
(Embodiment 8) In the above Embodiment 1, the intermediate layer 6 has a heat distortion temperature.
ASTM D648 is 4.6 kg / cm 2 at 60 ° C, Rockwell hardness ASTM is
D785 was formed from hydroxypropyl cellulose of M100, and as an organic dye forming the light absorption layer 2, 1.
1'dibutyl 3,3,3 ', 3' tetramethyl 4,5,
An optical disc was prepared in the same manner as in Example 1 except that 4′5 ′ dibenzoindodicarbocyanine perchlorate was used and that a silicone resin was coated on the light absorption layer 2 instead of the silicone acrylic resin. I made it.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.65、I3/Itopが0.32で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.65 and I 3 / Itop was 0.32.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例9) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で50℃、ロックウェル硬度ASTMが
D785でM30のウレタン系熱可塑性樹脂(日本ポリウレタ
ン工業製のニッポラン133と同社製のコロネートLとを
5:1に配合)により厚50nmに形成したこと、及びこの中
間層6の上にシリコン系コート剤を厚さ15nmスピンコー
トで形成して耐溶剤処理した後、1、1′ジブチル3、
3、3′、3′テトラメチル4、5、4′5′ジベンゾ
インドジカーボシアニンパークロレートを用いて光吸収
層2を形成したこと、及びシリコンアクリル樹脂に代え
て、シリコン樹脂をコーティングで形成したこと以外
は、上記実施例1と同様にして光ディスクを製作した。
(Example 9) In Example 1 above, the intermediate layer 6 has a heat distortion temperature.
ASTM D648 is 4.6 kg / cm 2 at 50 ° C, Rockwell hardness ASTM is
D785 used M30 urethane thermoplastic resin (Nipporan 133 made by Nippon Polyurethane Industry Co., Ltd. and Coronate L made by the same company)
5: 1) to have a thickness of 50 nm, and a silicon-based coating agent was formed on the intermediate layer 6 by spin coating with a thickness of 15 nm and treated with a solvent to give 1,1′dibutyl 3,
Forming the light absorption layer 2 using 3,3 ', 3' tetramethyl 4,5,4'5'dibenzoindodicarbocyanine perchlorate, and forming a silicon resin by coating instead of the silicon acrylic resin An optical disk was manufactured in the same manner as in Example 1 except for the above.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.67、I3/Itopが0.34で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.67, and I 3 / Itop was 0.34.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例10) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で70℃、ロックウェル硬度ASTMが
D785でM90のアクリル樹脂(サンノプコ製のSN-EX7052)
により形成したこと、有機色素として、1、1′ジプロ
ピル5、7、5′、7′ジメトキシインドジカーボシア
ニンフルオロボレートを用いて膜厚130nmの光吸収層2
を形成したこと、光反射層3をCu膜により形成したこ
と、及び保護層4をシリコン系ハードコート剤により、
厚さ5μmに形成したこと以外は、上記実施例1と同様
にして光ディスクを製作した。
(Example 10) In Example 1 above, as the intermediate layer 6, a heat distortion temperature was used.
ASTM D648 is 4.6 kg / cm 2 at 70 ° C, Rockwell hardness ASTM is
D785 M90 acrylic resin (San Nopco SN-EX7052)
The light absorbing layer 2 having a thickness of 130 nm is formed by using 1,1′dipropyl 5,7,5 ′, 7′dimethoxyindodicarbocyanine fluoroborate as an organic dye.
Was formed, the light reflecting layer 3 was formed of a Cu film, and the protective layer 4 was formed of a silicon-based hard coat agent.
An optical disk was manufactured in the same manner as in Example 1 except that the thickness was 5 μm.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.63、I3/Itopが0.32で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.63, and I 3 / Itop was 0.32.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例11) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で50℃、ロックウェル硬度ASTMが
D785でM60のポリウレタン系樹脂(日本ポリウレタン工
業製のニッポラン133と同社製のコロネートLとを1:1に
配合)により形成したこと、光吸収層2を形成する有機
色素として、1、1′ジプロピル5、7、5′、7′ジ
メトキシインドジカーボシアニンフルオロボレートを用
いたこと、光吸収層2の上に厚さ30nmのSiO2膜をスパッ
タリング法により設けたこと、光反射層3をCu膜により
形成したこと、光反射層3の上に厚さ20nmのエポキシ樹
脂をスピンコートした上に保護層4を形成したこと、保
護層4をシリコン系ハードコート剤により、厚さ5μm
に形成したこと以外は、上記実施例1と同様にして光デ
ィスクを製作した。
(Embodiment 11) In the above Embodiment 1, the intermediate layer 6 has a heat distortion temperature.
ASTM D648 is 4.6 kg / cm 2 at 50 ° C, Rockwell hardness ASTM is
It was formed from M60 polyurethane resin with D785 (Nipporan 133 manufactured by Nippon Polyurethane Industry Co., Ltd. and Coronate L manufactured by the same company were mixed in a ratio of 1: 1). 5, 7, 5 ', 7'dimethoxyindodicarbocyanine fluoroborate was used, a SiO 2 film having a thickness of 30 nm was provided on the light absorption layer 2 by a sputtering method, and the light reflection layer 3 was a Cu film. The protective layer 4 is formed on the light-reflecting layer 3 by spin-coating an epoxy resin with a thickness of 20 nm on the light-reflecting layer 3, and the protective layer 4 is made to have a thickness of 5 μm by a silicon-based hard coating agent.
An optical disk was manufactured in the same manner as in Example 1 except that the optical disk was formed.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.66、I3/Itopが0.33で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.66, and I 3 / Itop was 0.33.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(実施例12) 上記実施例1において、透光性基板1としてガラス円
板を用いたこと、中間層6として、熱変形温度ASTM D64
8が4.6kg/cm2で70℃、ロックウェル硬度ASTMがD785でM9
0の表面に2p法(photo polymarization method)により
プレグルーブを形成したアクリル樹脂(サンノプコ製の
SN-EX7052)により形成したこと、光吸収層2を形成す
る有機色素として、1、1′ジプロピル5、7、5′、
7′ジメトキシインドジカーボシアニンフルオロボレー
トを用いて膜厚130nmを光吸収層2を形成したこと、光
反射層3をCu膜により形成したこと、保護層4をシリコ
ン系ハードコート剤により、厚さ5μmに形成したこと
以外は、上記実施例1と同様にして光ディスクを製作し
た。
Example 12 In Example 1, a glass disk was used as the translucent substrate 1, and the intermediate layer 6 had a heat distortion temperature ASTM D64.
8 is 4.6 kg / cm 2 at 70 ° C, Rockwell hardness ASTM is D785 and M9
An acrylic resin with pregrooves formed on the surface of 0 by the 2p method (photo polymarization method) (made by San Nopco
SN-EX7052), as the organic dye forming the light absorption layer 2, 1, 1'dipropyl 5, 7, 5 ',
The light absorbing layer 2 was formed to a thickness of 130 nm using 7'dimethoxyindodicarbocyanine fluoroborate, the light reflecting layer 3 was formed of a Cu film, and the protective layer 4 was formed to a thickness of a silicon hard coat agent. An optical disc was manufactured in the same manner as in Example 1 except that the thickness was 5 μm.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.63、I3/Itopが0.32で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.63, and I 3 / Itop was 0.32.

さらに、上記実施例1と同様にして、記録後の中間層
6の表面を観察したところ、そこに光学的に変性した凸
状のピット5が形成されているのが確認された。
Furthermore, when the surface of the intermediate layer 6 after recording was observed in the same manner as in Example 1, it was confirmed that the optically modified convex pits 5 were formed therein.

(比較例) 上記実施例1において、中間層6として、熱変形温度
ASTM D648が4.6kg/cm2で180℃、ロックウェル硬度ASTM
がD785でM100のアルコキシシラン系シリコン樹脂により
形成したこと以外は、上記実施例1と同様にして光ディ
スクを製作した。
(Comparative Example) In the above-mentioned Example 1, the intermediate layer 6 has a heat distortion temperature.
180 ° C at ASTM D648 of 4.6 kg / cm 2 , Rockwell hardness ASTM
An optical disk was manufactured in the same manner as in Example 1 except that the material was D785 and was formed of an alkoxysilane-based silicon resin of M100.

こうして得られた光ディスクに、上記実施例1と同様
にしてEFM信号を記録し、その後、この光ディスクを、
市販のCDプレーヤで再生したところ、再生信号のアイパ
ターンから得られるI11/Itopが0.28、I3/Itopが0.05で
あった。
An EFM signal was recorded on the optical disc thus obtained in the same manner as in Example 1 above, and then this optical disc was recorded.
When reproduced with a commercially available CD player, I 11 / Itop obtained from the eye pattern of the reproduced signal was 0.28 and I 3 / Itop was 0.05.

この光ディスクは、上記CDフォーマットを満足するこ
とができない。
This optical disc cannot satisfy the above CD format.

[発明の効果] 以上説明した通り、本発明の光情報記録媒体とその記
録方法によれば、レーザ光の照射により、透光性基板1
の上に形成された中間層6にピットを形成できると共
に、光吸収層2の背後に反射層3を密着して形成するこ
とができることから、CDと光学的に近似するピット形態
と層構造をとることができる。
[Effects of the Invention] As described above, according to the optical information recording medium and the recording method thereof of the present invention, the transparent substrate 1 is irradiated with the laser light.
Since the pits can be formed in the intermediate layer 6 formed on the above and the reflection layer 3 can be formed in close contact with the back of the light absorption layer 2, a pit form and a layer structure optically similar to CD can be formed. Can be taken.

特に、透光性基板1の上に比較的熱変形温度が低い
か、或は硬度の低い中間層6を形成していることから、
レーザ光の照射により光吸収層2に発生するエネルギー
により、この中間層6に明瞭なピットを形成することが
でき、これによって変調度の高い再生信号が得られる。
In particular, since the intermediate layer 6 having a relatively low heat distortion temperature or a low hardness is formed on the transparent substrate 1,
Due to the energy generated in the light absorption layer 2 by the irradiation of the laser beam, a clear pit can be formed in the intermediate layer 6, and a reproduction signal having a high degree of modulation can be obtained.

【図面の簡単な説明】[Brief description of drawings]

第1図は、光情報記録媒体の構造の一例を示す模式半断
面斜視図、第2図は、第1図の光記録前のA部拡大図、
第3図は、第1図の光記録後のA部拡大図、第4図は、
他の例を示す光記録前の光ディスクの要部拡大断面図、
第5図は、同光ディスクにおける光記録後の要部拡大断
面図である。 1……基板、2……光吸収層、3……反射層、4……保
護層
FIG. 1 is a schematic half cross-sectional perspective view showing an example of the structure of an optical information recording medium, FIG. 2 is an enlarged view of part A before optical recording of FIG. 1,
FIG. 3 is an enlarged view of part A after optical recording in FIG. 1, and FIG.
An enlarged sectional view of an essential part of an optical disc before optical recording showing another example,
FIG. 5 is an enlarged cross-sectional view of a main part of the optical disc after optical recording. 1 ... Substrate, 2 ... Light absorbing layer, 3 ... Reflective layer, 4 ... Protective layer

フロントページの続き (72)発明者 石黒 隆 東京都台東区上野6丁目16番20号 太陽誘 電株式会社内 (56)参考文献 特開 昭58−189851(JP,A)Front page continuation (72) Inventor Takashi Ishiguro 6-16-20 Ueno Taito-ku, Tokyo Within Taiyo Denki Co., Ltd. (56) Reference JP-A-58-189851 (JP, A)

Claims (2)

【特許請求の範囲】[Claims] 【請求項1】透光性基板1の上に他の層を介してレーザ
光を吸収する光吸収層2と、光吸収層2の上に直接また
は他の層を介して設けられたレーザ光を反射する光反射
層3とを有する光情報記録媒体において、光吸収層2が
レーザ光の照射により、発熱と圧力増大を伴う材料を含
有し、この光吸収層2と、透光性基板1との間に中間層
6を介在させ、この中間層6のロックウェル硬度がASTM
D785でM100〜50であることを特徴とする光情報記録媒
体。
1. A light absorbing layer 2 which absorbs a laser beam through another layer on a transparent substrate 1, and a laser beam which is provided on the light absorbing layer 2 directly or through another layer. In the optical information recording medium having a light reflection layer 3 that reflects light, the light absorption layer 2 contains a material that generates heat and increases pressure when irradiated with a laser beam, and the light absorption layer 2 and the transparent substrate 1 The intermediate layer 6 is interposed between the intermediate layer 6 and
An optical information recording medium characterized by having a D785 of M100 to 50.
【請求項2】中間層6の熱変形温度がASTM D648 4.6Kg/
cm2で50〜150℃であることを特徴とする特許請求の範囲
第1項に記載の光情報記録媒体。
2. The heat distortion temperature of the intermediate layer 6 is ASTM D648 4.6 Kg /
The optical information recording medium according to claim 1, wherein the optical information recording medium has a temperature of 50 to 150 ° C. in cm 2 .
JP63239165A 1988-07-30 1988-09-24 Optical information recording medium Expired - Lifetime JPH0823940B2 (en)