JPH07328043A - Dental prosthesis partially having different crystallinity and manufacture thereof - Google Patents
Dental prosthesis partially having different crystallinity and manufacture thereofInfo
- Publication number
- JPH07328043A JPH07328043A JP12136694A JP12136694A JPH07328043A JP H07328043 A JPH07328043 A JP H07328043A JP 12136694 A JP12136694 A JP 12136694A JP 12136694 A JP12136694 A JP 12136694A JP H07328043 A JPH07328043 A JP H07328043A
- Authority
- JP
- Japan
- Prior art keywords
- dental prosthesis
- crystallinity
- transparency
- color
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、部分的に結晶化度の異
なる歯科補綴物およびその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a dental prosthesis having partially different crystallinity and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】従来の歯科補綴物は、例えば、結晶化ガ
ラスを用いてロストワックス法を用いて鋳造し、得られ
た成形体に対して結晶化炉を用いて熱処理を施して結晶
化させることにより製造される。得られた歯科補綴物
は、略均一な結晶化度で結晶化され、略均一な色調また
は透明度を有する。歯科補綴物の部分によって色調また
は透明度を変化させる場合には、歯科補綴物の表面にス
テイン材を塗布するか陶材を築盛している。2. Description of the Related Art A conventional dental prosthesis is, for example, cast by using the lost wax method using crystallized glass, and the obtained molded body is heat-treated in a crystallization furnace to be crystallized. It is manufactured by The dental prosthesis obtained is crystallized with a substantially uniform crystallinity and has a substantially uniform color tone or transparency. When the color tone or the transparency is changed depending on the part of the dental prosthesis, a stain material is applied to the surface of the dental prosthesis or porcelain is built up.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、従来の
結晶化ガラスからなる歯科補綴物は、特に前歯に用いる
場合に、歯冠部の先端部および根幹部の色調に変化を持
たせることが多い。この場合、結晶化炉を用いて熱処理
を施して得られた歯科補綴物に例えばステイン材を塗布
した後、ステイン材を融着させるために、もう一度、結
晶化炉内で熱処理を施さなければならない。このステイ
ン材の色調は、確認するには完全に熱処理が終了してか
らでないと確認できない。また、歯科補綴物の全体にわ
たって色調のグラディエーションを持たせる場合には、
ステイン材の塗布、色調の確認を繰り返し行う必要があ
り、歯科補綴物の作製に多大な時間を要している。陶材
を用いた場合にも同様な問題があり、更に、陶材は機械
的強度が劣り、歯科補綴物が破折する可能性がより高く
なる。本発明は、かかる点に鑑みてなされたものであ
り、天然歯に近似し、より審美性に優れた歯科補綴物お
よびその製造方法を提供する。However, the conventional dental prosthesis made of crystallized glass often changes the color tone of the tip portion and the root portion of the crown portion, especially when used for the anterior teeth. In this case, for example, after applying a stain material to the dental prosthesis obtained by heat treatment using the crystallization furnace, the heat treatment must be performed again in the crystallization furnace in order to fuse the stain material. . The color tone of this stain material can be confirmed only after the heat treatment is completed. Also, if you want to have a color gradation throughout the dental prosthesis,
Since it is necessary to repeatedly apply the stain material and confirm the color tone, it takes a lot of time to manufacture the dental prosthesis. The use of porcelain presents similar problems, and furthermore, porcelain has poor mechanical strength and the dental prosthesis is more likely to break. The present invention has been made in view of the above points, and provides a dental prosthesis which is similar to natural teeth and has more excellent aesthetics, and a method for manufacturing the same.
【０００４】[0004]
【課題を解決するための手段】本発明は、結晶化ガラス
からなる歯科補綴物であって、所定の結晶化度からなる
基本色部と、前記基本色部と異なる結晶化度を有する部
分色部を具備することを特徴とする歯科補綴物を提供す
る。SUMMARY OF THE INVENTION The present invention is a dental prosthesis made of crystallized glass, wherein a basic color portion having a predetermined crystallinity and a partial color having a crystallinity different from the basic color portion are provided. There is provided a dental prosthesis characterized by comprising a part.
【０００５】本発明は、結晶化ガラスからなる所望形状
の成形体の全体に対して第１温度で熱処理を施して結晶
化させる工程と、前記成形体の一部分に対して前記第１
温度よりも高い温度の第２温度で熱処理を施して、所定
の結晶化度からなる基本色部と前記基本色部と異なる結
晶化度を有する部分色部を具備する歯科補綴物を得る工
程とを具備することを特徴とする歯科補綴物の製造方法
を提供する。According to the present invention, a step of heat-treating a whole shaped body of crystallized glass having a desired shape at a first temperature to crystallize the shaped body, and a part of the shaped body are subjected to the first treatment.
Performing a heat treatment at a second temperature higher than the temperature to obtain a dental prosthesis having a basic color part having a predetermined crystallinity and a partial color part having a crystallinity different from the basic color part; The present invention provides a method for manufacturing a dental prosthesis, which comprises:
【０００６】以下、本発明をより詳細に説明する。本発
明の歯科補綴物は、所定の結晶化度からなる基本色部
と、前記基本色部と異なる結晶化度を有する部分色部を
具備し、部分的に結晶化ガラスの結晶化度が異なり、色
調や透明度が異なる。より具体的には、例えば、結晶化
ガラスの結晶化度が比較的低く、あまり白濁せず、透明
度が高い基本色部と、この基本色部よりも結晶度が高
く、透明度が低く白濁した部分色部を有する。The present invention will be described in more detail below. The dental prosthesis of the present invention comprises a basic color part having a predetermined crystallinity and a partial color part having a crystallinity different from the basic color part, and the crystallinity of the crystallized glass is partially different. , The color tone and transparency are different. More specifically, for example, the crystallinity of crystallized glass is relatively low, does not cloud much, and the transparency is high, and the transparency is high, the crystallinity is higher than this basic color, and the transparency is low and cloudy. It has a color part.
【０００７】本発明の歯科補綴物は、複数の連続した領
域に分割された、結晶化ガラスの結晶化度が徐々に異な
る部分色部が形成されたものであっても良く、この場
合、天然歯に近似したグラディエーションを呈する。The dental prosthesis of the present invention may be one in which a partial color portion having a gradually different crystallinity of crystallized glass is formed by being divided into a plurality of continuous regions. It exhibits a gradation similar to teeth.
【０００８】本発明の歯科補綴物に用いられる結晶化ガ
ラスは、例えば、マイカ−β−スポジュウメン系ガラ
ス、マイカ、チタン酸マグネシウム、アパタイトであ
る。本発明の歯科補綴物の製造方法は、まず、結晶化ガ
ラスを通常の成形方法、例えば、ロストワックス法によ
る鋳造で、歯冠のような所望の形状の成形体を作成す
る。次いで、この成形体の全体を、例えば結晶化炉内で
所定の第１温度で加熱して略均一に結晶化させる。これ
により、上述の基本色部が形成される。次いで、成形体
が十分に冷却された後、例えば、ガスバーナーで部分的
に第１温度よりも高い第２温度で加熱し、部分的に結晶
化度を高めて、上述の部分色部を形成する。ガスバーナ
ーで成形体を部分的に加熱すると、加熱された部分の結
晶化ガラスの結晶化度が高くなり、透明度が低下して白
濁化する。この場合、結晶化ガラスの色調の変化は加熱
しながら確認することができる。第２の温度による加熱
は、遠赤外線を利用したスポットヒータも使用できる。The crystallized glass used in the dental prosthesis of the present invention is, for example, mica-β-spodumene glass, mica, magnesium titanate and apatite. In the method for producing a dental prosthesis of the present invention, first, a molded body having a desired shape such as a crown is formed by crystallized glass by a usual molding method, for example, casting by the lost wax method. Next, the entire molded body is heated at, for example, a predetermined first temperature in a crystallization furnace to crystallize substantially uniformly. As a result, the basic color portion described above is formed. Then, after the molded body is sufficiently cooled, for example, it is partially heated with a gas burner at a second temperature higher than the first temperature to partially increase the crystallinity to form the partial color portion described above. To do. When the molded body is partially heated by the gas burner, the crystallized glass in the heated portion has a high crystallinity, which reduces transparency and becomes cloudy. In this case, the change in the color tone of the crystallized glass can be confirmed while heating. For heating by the second temperature, a spot heater using far infrared rays can also be used.
【０００９】本発明の歯科補綴物にグラディエーション
を付ける場合には、上述の部分色部の一部分を、第２温
度よりも高い第３温度で加熱し、さらに結晶化ガラスの
結晶化度が高い部分色部を形成する。このような部分的
な加熱処理を繰り返すことにより歯科補綴物にグラディ
エーションが付けられる。When the dental prosthesis of the present invention is to be provided with a gradient, a part of the above-mentioned partial color part is heated at a third temperature higher than the second temperature, and the crystallinity of the crystallized glass is high. A partial color part is formed. Gradation is applied to the dental prosthesis by repeating such partial heat treatment.
【００１０】例えば、重量比8 〜11％のLi2 CO3 、20〜
28％のMgO 、11〜15％のAl2 O3 、35〜45％の SiO2 、
10〜15％のNa2 Si F6 、0 〜5 ％のZnO 、0 〜5 ％のZr
O2、0 〜0.5 ％の Y2 O3 を主成分とし、着色剤とし
て2 ％以下の CeO2 、 TiO2、Fe2 O3 等の金属酸化物
を含むマイカ−β−スポジュウメン系結晶化ガラス（商
品名：オリンパスキャスタブルセラミックス）を用いた
場合、第１の温度として、13℃／分の昇温速度で室温よ
り750 ℃まで加熱し、750 ℃で２時間係留した後、４℃
／分の昇温速度で750 ℃より880 ℃まで加熱し、880 ℃
に達した後に室温まで冷却する。このとき、オリンパス
キャスタブルセラミックスの色は乳白色でほとんど透明
である。その後、第２の温度として火炎温度1200℃で、
10数秒〜数十秒の範囲で加熱すると透明感がなくなり、
淡黄色となる。時間を長くするほど黄色味が強くあらわ
れる。For example, Li 2 CO 3 in a weight ratio of 8 to 11%, 20 to
28% MgO, 11-15% Al 2 O 3 , 35-45% SiO 2 ,
Of 10~15% Na 2 Si F 6, 0 ~5% of ZnO, 0 to 5% of Zr
O 2, 0 to 0.5% of Y 2 and O 3 as a main component, mica -β- Supojuumen based crystallized glass containing less than 2% of CeO 2, TiO 2, Fe metal oxides such as 2 O 3 as a coloring agent When (commercial name: Olympus Castable Ceramics) is used, the first temperature is raised from room temperature to 750 ° C at a heating rate of 13 ° C / min, and after mooring at 750 ° C for 2 hours, 4 ° C.
880 ℃ by heating from 750 ℃ to 880 ℃ at a heating rate of
After reaching, cool to room temperature. At this time, the color of Olympus castable ceramics is milky white and almost transparent. After that, with a flame temperature of 1200 ° C as the second temperature,
When heated for 10 seconds to tens of seconds, the transparent feeling disappears,
It becomes pale yellow. The longer the time, the stronger the yellow color appears.
【００１１】部分色部の形成は、上述のように基本色部
と異なる温度で加熱する他に、同一温度であっても加熱
時間を増減させることによっても行うことができる。ま
た、本発明の歯科補綴物の製造方法は、初めに、成形体
の一部分を比較的高温の第１温度で加熱して、結晶化を
進行させて白濁化させた後、第１温度よりも低い第２温
度で成形体全体を均一に加熱する。これにより、第１の
温度で加熱した部分だけがより結晶化が進行し、結晶化
度が高くより白濁した部分色部になる。この場合には、
第２の温度で結晶化炉内での熱処理により、第１の温度
で部分的な熱処理による熱歪みを取り除かれ、機械的強
度が高くなる点で優れている。The partial color portion can be formed by heating at a temperature different from that of the basic color portion as described above, or by increasing or decreasing the heating time even at the same temperature. Further, in the method for producing a dental prosthesis of the present invention, first, a part of the molded body is heated at a first temperature of a relatively high temperature to promote crystallization to make it cloudy, The entire compact is uniformly heated at the second low temperature. As a result, only the portion heated at the first temperature is further crystallized, and the crystallized portion becomes a more cloudy partial color portion. In this case,
The heat treatment in the crystallization furnace at the second temperature removes the thermal strain due to the partial heat treatment at the first temperature, and is excellent in that the mechanical strength is increased.
【００１２】また、成形体に熱反射または熱吸収性のペ
ーストを塗布し、部分的に熱の吸収性を低くし、この成
形体に対して結晶化炉内で熱処理を施し、１回の熱処理
により基本色部および部分色部を形成することも可能で
ある。この場合は、１度の熱処理により、部分的な色調
の変化を容易に作ることができる点で優れている。Further, a heat-reflecting or heat-absorbing paste is applied to the molded body to partially reduce the heat absorption, and the molded body is heat-treated in a crystallization furnace to carry out one heat treatment. It is also possible to form the basic color portion and the partial color portion by. In this case, it is excellent in that a partial change in color tone can be easily made by one heat treatment.
【００１３】[0013]
【作用】本発明の歯科補綴物は、これを構成する結晶化
ガラスの結晶化度が部分的に異なっているので、歯科補
綴物の色調および透明度が異なっている。従って、天然
歯に近似した色調および透明度を実現することが可能で
ある。In the dental prosthesis of the present invention, the crystallinity of the crystallized glass constituting the dental prosthesis is partially different, so that the dental prosthesis is different in color tone and transparency. Therefore, it is possible to realize a color tone and transparency similar to those of natural teeth.
【００１４】また、本発明の歯科補綴物の製造方法は、
結晶化ガラスからなる所望形状の成形体の全体に対して
第１温度で熱処理を施すことにより、成形体の全体を均
一に加熱し、成形体の全体を均一の結晶化度に結晶化さ
せる。次いで、成形体の一部分に対して第１温度よりも
高い温度の第２温度で熱処理を施すことにより、加熱部
分の結晶化度を非加熱部分の結晶化度よりも高くする。
これにより、基本色部とこれよりも透明度が低くかつ白
濁した部分色部が形成される。The method for manufacturing a dental prosthesis according to the present invention is
By subjecting the entire molded body of crystallized glass having a desired shape to the heat treatment at the first temperature, the entire molded body is uniformly heated and the entire molded body is crystallized to a uniform crystallinity. Next, the crystallinity of the heated portion is made higher than that of the non-heated portion by heat-treating a part of the molded body at a second temperature higher than the first temperature.
As a result, the basic color portion and the partial color portion having a lower transparency and being cloudy are formed.
【００１５】[0015]
【実施例】以下、図面を参照して本発明の実施例につい
て詳細に説明する。図１は、本発明の歯科補綴物の一実
施例を示す説明図である。図中１０は、前歯部用の歯科
補綴物である。歯科補綴物１０の先端部を含む最外周の
領域は、結晶化度が最も低くく、透明度が高い基本色部
１１である。この基本色部１１の色調および透明度は、
天然歯の先端部に近似するように選択される。基本色部
１１よりも内側には、内側になるほど結晶化度が高くな
る第１〜第５の部分色部１２〜１５が連続して形成され
ている。従って、歯科補綴物１０は、最も内側の根幹部
に近い第５の部分色部が最も透明度が低く白濁してお
り、外側に向かうほど透明度が高くなり、全体として、
天然歯に非常に近似した色調および透明度を有している
ものである。Embodiments of the present invention will now be described in detail with reference to the drawings. FIG. 1 is an explanatory view showing an embodiment of the dental prosthesis of the present invention. In the figure, 10 is a dental prosthesis for the anterior tooth. The outermost peripheral region including the tip portion of the dental prosthesis 10 is the basic color portion 11 having the lowest crystallinity and high transparency. The color tone and transparency of the basic color portion 11 are
Selected to approximate the tip of a natural tooth. Inside the basic color portion 11, first to fifth partial color portions 12 to 15 whose crystallinity increases toward the inside are continuously formed. Therefore, in the dental prosthesis 10, the fifth partial color part closest to the innermost root part has the lowest transparency and becomes cloudy, and the transparency increases toward the outer side, and as a whole,
It has a color tone and transparency very similar to those of natural teeth.
【００１６】かかる構成の歯科補綴物１０は次のように
して製造される。まず、マイカ−スポジウメン系ガラス
（オリンパスキャスタブルセラミックス；商品名：オリ
ンパス光学（株）製）を使用して、ロストワックス法に
よる遠心鋳造により、前歯に対応した形状を有する成形
体を作成する。この成形体を結晶化炉に入れて、必要と
される結晶化温度の一番低い温度（例えば、880 ℃）で
熱処理する。得られた成形体２０は、図２に示すよう
に、図１に示す最も結晶化が進行していない基本色部１
１に相当する結晶化度まで全体的にかつ均一に結晶化さ
れる。The dental prosthesis 10 having such a structure is manufactured as follows. First, a molded body having a shape corresponding to the front tooth is prepared by centrifugal casting by the lost wax method using a mica-spodium-based glass (Olympus castable ceramics; trade name: manufactured by Olympus Optical Co., Ltd.). The compact is placed in a crystallization furnace and heat-treated at the lowest required crystallization temperature (for example, 880 ° C.). As shown in FIG. 2, the obtained molded body 20 has a basic color portion 1 shown in FIG.
It is crystallized entirely and uniformly up to a crystallinity corresponding to 1.
【００１７】次に、第１の熱処理が施された成形体２０
に対して、図３に示すように、ガスバーナー３０（例え
ば1200℃）を用いて熱処理を施し、第１〜第５の部分色
部を形成する。最も結晶化度が高く、天然歯の根幹部に
対応する第５の部分色部は、結晶化を進行させるために
長時間加熱して形成され、外側の部分色部になるほど加
熱時間を短くする。この結果、根幹部の第５の部分色部
１６は、結晶化が最も進行して透明度がなく、先端部に
向かって第４の部分色部１５から第１の部分色部１２に
移行するほど、結晶化が進行せず、透明度が高くなる。Next, the molded body 20 that has been subjected to the first heat treatment.
On the other hand, as shown in FIG. 3, heat treatment is performed using a gas burner 30 (for example, 1200 ° C.) to form first to fifth partial color portions. The fifth partial color portion, which has the highest degree of crystallinity and corresponds to the root portion of the natural tooth, is formed by heating for a long time in order to promote crystallization, and the heating time is shortened toward the outer partial color portion. . As a result, the fifth partial color part 16 of the root part has the highest degree of crystallization and has no transparency, and the fourth partial color part 15 moves to the first partial color part 12 toward the tip. , Crystallization does not proceed and the transparency becomes high.
【００１８】このようにして得られた歯科補綴物１０
は、天然歯に極めて近似したグラディエーションを呈
し、審美性に優れている。また、上述の歯科補綴物１０
の製造方法によれば、ステイン材の塗布や陶材の築盛を
行うことなく、天然歯に近似したグラディエーションを
実現することが可能である。このため、例えば、陶材を
築盛し、炉内で熱処理して、色調を確認するといった操
作を繰り返し行う必要がないので、所要時間が大幅に短
縮でき、しかも、ガスバーナー３０で加熱しながら色調
または透明度を確認しつつ熱処理を行うことができるの
で作業性に優れている。Dental prosthesis 10 thus obtained
Has a gradation very similar to that of natural teeth and has excellent aesthetics. In addition, the dental prosthesis 10 described above
According to the manufacturing method of (1), it is possible to realize a gradation similar to that of natural teeth without applying stain material or building up porcelain. For this reason, for example, it is not necessary to repeat the operations of laying porcelain, heat-treating it in a furnace, and checking the color tone, so the time required can be greatly shortened, and the color tone can be improved while heating with the gas burner 30. Alternatively, since heat treatment can be performed while confirming the transparency, workability is excellent.
【００１９】上記実施例での加熱方法は、変更または変
形が可能であり、第１〜第５の部分色部１２〜１６を形
成する熱処理において、加熱時間を変更して結晶化の進
行の程度をコントロールする代わりに、加熱時間を一定
にし、ガスバーナー３０の出力温度を変更することも可
能である。ガスバーナー３０に代えてスポットヒーター
も使用できる。The heating method in the above embodiment can be changed or modified, and in the heat treatment for forming the first to fifth partial color portions 12 to 16, the heating time is changed to the extent of progress of crystallization. It is also possible to make the heating time constant and change the output temperature of the gas burner 30 instead of controlling A spot heater can be used instead of the gas burner 30.
【００２０】以上実施例に基づいて、本発明を説明し
た。しかし、本発明は上述した実施例に限定されるもの
ではなく、本発明の要旨の範囲内で種々の変形や応用が
可能である。ここで、本発明の要旨をまとめると以下の
ようになる。The present invention has been described above based on the embodiments. However, the present invention is not limited to the embodiments described above, and various modifications and applications are possible within the scope of the gist of the present invention. Here, the summary of the present invention is summarized as follows.
【００２１】（１）結晶化ガラスからなる歯科補綴物で
あって、所定の結晶化度からなる基本色部と、前記基本
色部と異なる結晶化度を有する部分色部を具備すること
を特徴とする歯科補綴物。(1) A dental prosthesis made of crystallized glass, comprising a basic color part having a predetermined crystallinity and a partial color part having a crystallinity different from the basic color part. And dental prosthesis.
【００２２】（２）全体が同一材料からなりかつ一体物
である（１）記載の歯科補綴物。 （３）結晶化ガラスからなる所望形状の成形体の全体に
対して熱処理を施して結晶化させる第１の熱処理工程
と、前記成形体の一部分に対して熱処理を施して結晶化
させる第２の熱処理工程を具備し、所定の結晶化度から
なる基本色部と前記基本色部と異なる結晶化度を有する
部分色部を具備する歯科補綴物を得ることを特徴とする
歯科補綴物の製造方法。(2) The dental prosthesis according to (1), which is entirely made of the same material and is an integral body. (3) A first heat treatment step of heat-treating the entire shaped body of crystallized glass having a desired shape to crystallize it, and a second heat treatment of part of the shaped body to crystallize. A method for producing a dental prosthesis, comprising a heat treatment step, and a dental prosthesis having a basic color part having a predetermined crystallinity and a partial color part having a crystallinity different from the basic color part. .
【００２３】（４）結晶化ガラスからなる所望形状の成
形体の全体に対して第１温度で熱処理を施して結晶化さ
せる工程と、前記成形体の一部分に対して前記第１温度
よりも高い温度の第２温度で熱処理を施して、所定の結
晶化度からなる基本色部と前記基本色部と異なる結晶化
度を有する部分色部を具備する歯科補綴物を得る工程と
を具備することを特徴とする歯科補綴物の製造方法。(4) A step of performing heat treatment at a first temperature to crystallize the entire molded body of crystallized glass having a desired shape, and a part of the molded body having a temperature higher than the first temperature. And a heat treatment at a second temperature of temperature to obtain a dental prosthesis having a basic color part having a predetermined crystallinity and a partial color part having a crystallinity different from the basic color part. And a method for manufacturing a dental prosthesis.
【００２４】（５）結晶化ガラスからなる所望形状の成
形体の一部分に対して所定温度で熱処理を施して結晶化
させる工程と、前記成形体の全体に対して略均一に所定
温度で熱処理を施して、所定の結晶化度からなる基本色
部と前記基本色部と異なる結晶化度を有する部分色部を
具備する歯科補綴物を得る工程とを具備することを特徴
とする歯科補綴物の製造方法。(5) A step of heat-treating a part of a molded body of crystallized glass having a desired shape at a predetermined temperature to crystallize, and a heat treatment at a predetermined temperature substantially uniformly on the entire molded body. A dental prosthesis, characterized by comprising: applying a basic color part having a predetermined crystallinity and a partial color part having a crystallinity different from the basic color part. Production method.
【００２５】（１）記載の歯科補綴物は、結晶化ガラス
の結晶化度が部分的に異なっているので、歯科補綴物の
色調および透明度が異なっている。従って、天然歯に近
似した色調および透明度を実現することが可能である。In the dental prosthesis described in (1), since the crystallinity of the crystallized glass is partially different, the color tone and the transparency of the dental prosthesis are different. Therefore, it is possible to realize a color tone and transparency similar to those of natural teeth.
【００２６】（２）記載の歯科補綴物は、別にステイン
材、陶材を用いることなく、同一材料でかつ一体物であ
るので、製造が容易でかつ機械的強度に優れている。 （３）記載の歯科補綴物の製造方法は、結晶化ガラスの
成形体の全体に対して第１の熱処理を施して基本色部を
形成し、その後、成形体の一部に対して第２の熱処理を
施すことにより、結晶化度が異なる部分色部を形成す
る。天然歯に近似した色調または透明度が変化した歯科
補綴物を容易に製造することができる。The dental prosthesis described in (2) is easy to manufacture and excellent in mechanical strength because it is the same material and is an integral body without using a separate stain material or porcelain. In the method for manufacturing a dental prosthesis according to (3), a first heat treatment is performed on the entire molded body of crystallized glass to form a basic color portion, and then a second molding is performed on a part of the molded body. By performing the heat treatment of, partial color portions having different crystallinity are formed. It is possible to easily manufacture a dental prosthesis having a color tone or transparency that is similar to that of natural teeth.
【００２７】（４）記載の歯科補綴物の製造方法は、結
晶化ガラスの成形体の全体に対して比較的低温で熱処理
を施して透明度が高い基本色部を形成し、その後、成形
体の一部に対してより高い温度で熱処理を施すことによ
り、結晶化度が高く、白濁した透明度が低い部分色部を
形成する。天然歯に近似した色調および透明度が変化し
た歯科補綴物を容易に製造することができる。In the method for manufacturing a dental prosthesis according to (4), the entire molded body of crystallized glass is heat-treated at a relatively low temperature to form a basic color portion having high transparency, and then the molded body is molded. By subjecting a part to heat treatment at a higher temperature, a partial color part having high crystallinity and low transparency is formed. It is possible to easily manufacture a dental prosthesis having a color tone and a transparency that are similar to those of natural teeth.
【００２８】（５）記載の歯科補綴物の製造方法は、結
晶化ガラスからなる成形体の一部分に対して所定温度で
熱処理を施して結晶化させた後、成形体の全体に対して
略均一に所定温度で熱処理を施して、第１の温度で加熱
した部分だけがより結晶化が進行し、結晶化度が高くよ
り白濁した部分色部になる。この場合には、第２の温度
で結晶化炉内での熱処理により、１度目の部分的な熱処
理による熱歪みを取り除かれ、機械的強度が高くなる点
で優れている。In the method for producing a dental prosthesis according to (5), a part of a molded body made of crystallized glass is heat-treated at a predetermined temperature to crystallize, and then the molded body is substantially uniform. Is subjected to heat treatment at a predetermined temperature, and only the portion heated at the first temperature is further crystallized, and becomes a more clouded partial color portion having high crystallinity. In this case, the heat treatment in the crystallization furnace at the second temperature removes the thermal strain due to the first partial heat treatment, which is excellent in that the mechanical strength is increased.
【００２９】[0029]
【発明の効果】以上説明した如く、本発明の歯科補綴物
は、これを構成する結晶化ガラスの結晶化度が部分的に
異なっているので、歯科補綴物の色調および透明度が異
なっている。従って、天然歯に近似した色調および透明
度を実現することが可能である。As described above, in the dental prosthesis of the present invention, the crystallinity of the crystallized glass constituting the dental prosthesis is partially different, and therefore the color tone and transparency of the dental prosthesis are different. Therefore, it is possible to realize a color tone and transparency similar to those of natural teeth.
【００３０】また、本発明の歯科補綴物の製造方法は、
結晶化ガラスからなる所望形状の成形体の全体に対して
第１温度で熱処理を施すことにより、成形体の全体を均
一に加熱し、成形体の全体を均一の結晶化度に結晶化さ
せる。次いで、成形体の一部分に対して第１温度よりも
高い温度の第２温度で熱処理を施すことにより、加熱部
分の結晶化度を非加熱部分の結晶化度よりも高くする。
これにより、基本色部とこれよりも透明度が低くかつ白
濁した部分色部が形成される。この結果、ステイン材の
塗布や陶材の築盛を行うことなく、天然歯に近似した色
調や透明度の変化を有する歯科補綴物を提供できる。ま
た、陶材を築盛し、炉内で熱処理して、色調を確認する
といった操作を繰り返し行う必要がないので、所要時間
が大幅に短縮できる。The method for manufacturing a dental prosthesis according to the present invention is
By subjecting the entire molded body of crystallized glass having a desired shape to the heat treatment at the first temperature, the entire molded body is uniformly heated and the entire molded body is crystallized to a uniform crystallinity. Next, the crystallinity of the heated portion is made higher than that of the non-heated portion by heat-treating a part of the molded body at a second temperature higher than the first temperature.
As a result, the basic color portion and the partial color portion having a lower transparency and being cloudy are formed. As a result, it is possible to provide a dental prosthesis having a change in color tone and transparency similar to that of natural teeth without applying a stain material or building up porcelain. Moreover, since it is not necessary to repeat the operations of laying porcelain, heat-treating it in a furnace, and checking the color tone, the time required can be greatly reduced.
【図１】本発明の歯科補綴物の一実施例を示す説明図。FIG. 1 is an explanatory view showing an embodiment of a dental prosthesis of the present invention.
【図２】本発明の歯科補綴物の製造方法の一実施例にお
いて、第１熱処理後の成形体を示す説明図。FIG. 2 is an explanatory view showing the molded body after the first heat treatment in one embodiment of the method for manufacturing a dental prosthesis of the present invention.
【図３】本発明の歯科補綴物の製造方法の一実施例にお
ける第２熱処理の様子を示す説明図。FIG. 3 is an explanatory view showing a state of second heat treatment in an embodiment of the method for manufacturing a dental prosthesis according to the present invention.
１０…歯科補綴物、１１…基本色部、１２〜１６…部分
色部、２０…成形体、３０…ガスバーナー。10 ... Dental prosthesis, 11 ... Basic color part, 12-16 ... Partial color part, 20 ... Molded body, 30 ... Gas burner.
Claims (2)
て、所定の結晶化度からなる基本色部と、前記基本色部
と異なる結晶化度を有する部分色部を具備することを特
徴とする歯科補綴物。1. A dental prosthesis made of crystallized glass, comprising a basic color part having a predetermined crystallinity and a partial color part having a crystallinity different from the basic color part. Dental prosthesis to do.
の全体に対して第１温度で熱処理を施して結晶化させる
工程と、 前記成形体の一部分に対して前記第１温度よりも高い温
度の第２温度で熱処理を施して、所定の結晶化度からな
る基本色部と前記基本色部と異なる結晶化度を有する部
分色部を具備する歯科補綴物を得る工程とを具備するこ
とを特徴とする歯科補綴物の製造方法。2. A step of performing heat treatment at a first temperature to crystallize the entire shaped body of crystallized glass having a desired shape, and a temperature higher than the first temperature for a part of the shaped body. And a heat treatment at a second temperature to obtain a dental prosthesis having a basic color part having a predetermined crystallinity and a partial color part having a crystallinity different from the basic color part. A method for producing a characteristic dental prosthesis.