JP7415408B2 - 薄膜、及び薄膜転写シート - Google Patents
薄膜、及び薄膜転写シート Download PDFInfo
- Publication number
- JP7415408B2 JP7415408B2 JP2019181970A JP2019181970A JP7415408B2 JP 7415408 B2 JP7415408 B2 JP 7415408B2 JP 2019181970 A JP2019181970 A JP 2019181970A JP 2019181970 A JP2019181970 A JP 2019181970A JP 7415408 B2 JP7415408 B2 JP 7415408B2
- Authority
- JP
- Japan
- Prior art keywords
- thin film
- transfer sheet
- skin
- rate
- support
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
具体的には、支持体上の薄膜の表面を、被転写体における薄膜の貼付箇所に押し付けた後、薄膜から支持体を剥離することによって、薄膜を被転写体に転写する。(特許文献2参照)。
そのため、皮膚の構造及び、機能を保つための保湿が重要である。したがって、薄膜を皮膚に貼付する場合においても、皮膚の構造や機能を保つために、保湿できることが重要となる。
本発明の薄膜による閉塞率調整により、水分蒸散量から示される皮膚バリア性を正常に近づけ、角層水分量を維持もしくは向上させる効果を有する。その結果として本発明の薄膜は、正常皮膚状態を維持し、しかも薄膜であるため、既存化粧品と比較してベタつきや衣服等への布移りが生じない皮膚保湿作用を有する商材となる。
その計算式は、下式(1)
閉塞率=(初期値-サンプル値)/初期値 × 100(%) ・・・式(1)
で表される。
図1に示すように、本発明の実施形態に係る薄膜転写シート1は、薄膜2と、薄膜2を支持する機能を有する支持体3と、を備える。薄膜転写シート1において、薄膜2が有する2つの面のうち一方の面である第1面2aは支持体3の第1面3aに密着している。つまり、薄膜転写シート1は、薄膜2の第1面2aと支持体3の第1面3aとを密着させて積層した積層体として構成されている。
ここで、本実施形態による薄膜転写シート1を構成する各層の詳細な構成について説明する。
薄膜2は、被転写体に対する接着性を発現する程度の薄さを有する。ただし、ここで例えば薄膜2の質量を0.001g/m2未満とするのは技術的に困難であり、加えて、例えば上記用途における膜強度が不十分である。また、薄膜2の質量が5g/m2を超過すると、被転写体との密着性が低下するとともに、被転写体において、蒸れの発生、外観や装着感に違和感を生じる。
薄膜2の質量が上述の範囲内(以下、適正範囲内という)であれば、製造における技術的な課題及び、使用感に問題なく、接着層を用いずとも、薄膜2自体を被転写体の表面に転写して貼り付けることができる。
なお、上述の適正範囲における薄膜2の単位面積当たり質量とは、複数の測定点で測定された重さを算出した薄膜2の膜厚の平均値に膜密度を掛けた値である。
なお、化粧料の含有により薄膜のベトつきや衣服等への布移りが生じないよう、濃度を限定するか、化粧料が含有していない薄膜を積層することが好ましい。
/m2であるとき、薄膜2は1nmの膜厚となる。また、薄膜2の単位面積あたりの質量が5g/m2であるとき、薄膜2は5μmの膜厚となる。当該質量は、薄膜2の第1面2aにて1m2の面積を有する部分あたりの薄膜2の質量である。薄膜2の単位あたりの質量が上述の適正範囲内であれば、粘着層を用いずとも、薄膜2を被転写体の表面に貼り付けることができる。
具体的には、薄膜2の生体適合性材料として、例えば、ポリ乳酸、ポリグリコール酸、ポリカプロラクトンのようなポリエステル及びそれらの共重合体、さらには、化粧品の皮膜形成剤として使用される樹脂、例えば、アクリル樹脂やシリコーン及びそれらの共重合樹脂、酢酸セルロースや酢酸プロピオン酸セルロース、酢酸酪酸セルロースなどのセルロース誘導体、医療機器での使用実績の多い樹脂であるポリカーボネイト、シクロオレフィンコポリマー、スチレン・ブタジエン系エラストマー、ポリイミドが使用可能である。
さらには、タンパク質であるラミニン、フィブロネクチン、インテグリン、テネイシン、アルブミン、ケラチン、コラーゲン、ゼラチン、多糖類であるキチン、キトサン、ヒアルロン酸、グルコマンナン、プルラン、デキストラン、サクランなどが使用できる。
タンパク質や多糖類は水により膨潤、溶解及び、分解を生じるものが多いが、カチオン性ポリマーとアニオン性ポリマーとを混合または積層化することでイオンコンプレックスを形成でき、耐水性の向上が可能である。
支持体3には、特に制限はないが、樹脂基材もしくは、多孔質基材を用いることが好ま
しい。より好ましい多孔質基材は、内部に微小な多数の間隔を有する基材であり、液体を透過させることができる。
支持体3として用いることのできる多孔質基材としては、例えば、不織布、紙、編物、織物等の繊維材料から形成されるシート、メッシュ状のように間隔を含む構造を有する樹脂シート等が挙げられる。
これらの多孔質基材のなかでも、水分を速やかに吸収して拡散できることから、支持体3には不織布が好適に用いられる。不織布を構成する繊維は、例えば、綿、麻、羊毛、パルプ等の天然繊維、ポリエステルやポリプロピレン、ポリビニルアルコール、ポリアクリル酸等の合成繊維、レーヨン等の再生繊維である。上記の繊維のなかでも、天然繊維、特に綿及び、パルプが好適に用いられる。不織布は、1種類の繊維から構成されていてもよいし、2種類以上の繊維から構成されていてもよい。
なお、支持体3は、多孔質基材に限らず、内部に間隔を有さない樹脂シートや金属箔等の基材から構成されていてもよい。
薄膜転写シートにおける保湿効果を有するための、薄膜の閉塞率の好適な範囲について述べる。
薄膜2の傷とは、正常な状態では平坦であるはずの薄膜2表面に生じた微細ななみうち(波打ち)や、それを含む窪み部などの凹凸全般を示す。薄膜の傷は、主に薄膜2の材料、製造時の加工、基材及び、支持体との接触、搬送工程により生じる。また、傷率とはこのような傷の面積比率を表すが、具体的な測定方法については後述する。
傷率の調整は、具体的には、例えば成膜用基材の表面粗さの調整により行うことができる。
本実施形態において、閉塞率は下記の(1)~(5)に示す手順で行う方法によって測定される。この場合の閉塞率とは、薄膜による、水分蒸散量に関する閉塞性を表すものであり、その値は前述の式(1)により算出される。
上述のように、閉塞率は調整することが可能である。本発明における閉塞率は傷率の変動により調整を行っており、薄膜への傷によって、皮膚の水分蒸散量を過剰に妨害することなく、適度な閉塞を保つことが可能である。
また、薄膜への傷率は、調整できる手法が多く、細かく数値差を得られるため、閉塞率変動に有効である。このように、適度な閉塞率を担保する傷率調整薄膜により、皮膚に対して適度な保湿効果を与え、蒸れにくいという機能を有する薄膜を取得できる。
したがって閉塞率は、傷の面積比率と相関を有する。すなわち、傷の面積比率が増加すると、閉塞率は低下する。
傷の面積比率が30%以下であると、5%以上の閉塞率が得られやすく、すなわち、薄膜の貼り付けられた部分にて良好な保湿性が得られる。また、傷の面積比率が20%以下であると、10%以上の閉塞率が得られやすく、すなわち保湿性がより高められる。
閉塞性が極端に高くなることを抑えるため、すなわち、蒸れを抑えるためには、傷の面積比率が0.05%以上であることが好ましい。窪み部の面積比率は上記傷率測定において算出される。
本実施形態において、傷率は下記の(1)~(7)に示す手順で行う方法によって測定される。また、本実施例における傷率とは、薄膜表面の凹凸が観察面積あたりどのくらいの量、存在しているかを示す。
次に、薄膜転写シートの製造方法の一例を説明する。製造は前述の手法で行っている。なお、本実施形態による薄膜転写シートは、上述したように傷率が30%以下であればよく、薄膜転写シートは下記の製造方法とは異なる方法によって製造されてもよい。
次に、薄膜転写シートの使用方法、すなわち、薄膜転写シートを用いた薄膜の被転写体への転写方法の一例を説明する。以下では、支持体として多孔質基材を用い、支持体を湿潤させて薄膜を被転写体に転写する方法について説明する。
<実施例1~4>
ポリ-DL-乳酸(武蔵野化学研究所社製)を、固形分が6%となるように酢酸ブチルに溶解することにより、薄膜2の形成のための塗液としてポリ乳酸溶液を生成した。塗液に用いたポリ-DL-乳酸の平均分子量は、10万を選択した。その後、成膜用基材としてのPETシートに、ワイヤーバーを用いて上記塗液を塗布し、塗膜を形成した。この時、成膜用基材のPETシートの表面粗さRaは0.03μmのものを選択した。塗膜をオーブンで加熱して乾燥・固化させることにより、薄膜2を形成した。薄膜2は、乾燥後の厚さが600nmとなるように形成した。乾燥時の加熱温度は120℃、加熱時間は2分を選択した。
(実施例5~8の転写薄膜転写シートの製造)
成膜基材として用いたPETにおいて、表面粗さRaを0.36μmとして薄膜の傷率を調整した以外は実施例1~4と同様にして、実施例5~8の薄膜転写シートを得た。
成膜基材として用いたPETにおいて、表面粗さRaを0.43μmとして薄膜の傷率を調整した以外は実施例1~4と同様にして、実施例9の薄膜転写シートを得た。
<比較例1>
成膜基材として用いたPETにおいて、表面粗さRaを0.62μmとして薄膜の傷率を調整した以外は実施例1~4と同様にして、比較例1の薄膜転写シートを得た。
本実施形態において、保湿性は下記の (1)~(4)に示す手順で行う方法によって測定された。
各実施例及び、比較例における薄膜転写シートについて、上記の傷率測定方法および閉塞率測定方法に基づく傷率評価と閉塞率評価、さらに、下記の評価方法による肌保湿性能評価を実施した。
上記測定方法を用いて肌保湿性測定を行った。初期角層水分量と比較し、サンプル貼付1時間後の角層水分量が増加した場合を「○」、変化なしの場合を「△」、低下した場合を「×」とした。なお、本例では評価結果が「△」以上であれば合格とした。
表1において、各実施例及び、比較例の薄膜転写シートの傷率に対する評価結果を示した。表1では、傷率に対する評価結果を「傷率」と表記している。なお、表1において、測定値は小数第1位を四捨五入して示している。これは、閉塞率も同様である。
2 薄膜
2a 薄膜の第1面、2b 薄膜の第2面
3 支持体
3a 支持体の第1面、3b 支持体の第2面
Claims (6)
- 生体適合性材料からなり、0.001g/m2以上5g/m2以下の単位面積当たり平均質量を有する薄膜であって、
該薄膜を通過する水分蒸散量に関する閉塞率が、5%以上54%以下であり、
該薄膜の表面に存在する凹凸又はなみうちの面積比率を表す傷率が、2%以上30%以下であることを特徴とする薄膜。 - 生体適合性材料からなり、0.6g/m2以上5g/m2以下の単位面積当たり平均質量を有する薄膜であって、
該薄膜を通過する水分蒸散量に関する閉塞率が、5%以上54%以下であり、
該薄膜の表面に存在する凹凸又はなみうちの面積比率を表す傷率が、2%以上30%以下であることを特徴とする薄膜。 - 前記薄膜が多層膜であることを特徴とする請求項1または2に記載の薄膜。
- 前記薄膜は、機能性物質を含有する層を含むことを特徴とする請求項3に記載の薄膜。
- 前記機能性物質は、エモリエント剤またはヒューメクタント剤、もしくはその両方を含有することを特徴とする請求項4に記載の薄膜。
- 請求項1~5のいずれかに記載の薄膜と、前記薄膜を支持する支持体と、を備えたことを特徴とする薄膜転写シート。