JP6749294B2 - Method for manufacturing laminated optical film - Google Patents

Method for manufacturing laminated optical film Download PDF

Info

Publication number
JP6749294B2
JP6749294B2 JP2017157172A JP2017157172A JP6749294B2 JP 6749294 B2 JP6749294 B2 JP 6749294B2 JP 2017157172 A JP2017157172 A JP 2017157172A JP 2017157172 A JP2017157172 A JP 2017157172A JP 6749294 B2 JP6749294 B2 JP 6749294B2
Authority
JP
Japan
Prior art keywords
width
optical film
adhesive layer
film
protective film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2017157172A
Other languages
Japanese (ja)
Other versions
JP2018010307A (en
Inventor
俊之 仲
俊之 仲
武志 川上
武志 川上
卓也 安藤
卓也 安藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Chemical Co Ltd
Original Assignee
Sumitomo Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Chemical Co Ltd filed Critical Sumitomo Chemical Co Ltd
Publication of JP2018010307A publication Critical patent/JP2018010307A/en
Application granted granted Critical
Publication of JP6749294B2 publication Critical patent/JP6749294B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、積層光学フィルムの製造方法に関する。 The present invention relates to a method for manufacturing a laminated optical film.

従来、複数枚の光学フィルムを、接着剤層又は粘着剤層を介して一対の貼合ロール間を通過させることによって圧着する積層光学フィルムの製造方法が知られている(例えば、特許文献1参照)。接着剤層又は粘着剤層は通常、積層される光学フィルムのいずれか一方に接着剤又は粘着剤が塗布されることによって供給される。 BACKGROUND ART Conventionally, there is known a method for producing a laminated optical film in which a plurality of optical films are pressure-bonded by passing between a pair of bonding rolls via an adhesive layer or a pressure-sensitive adhesive layer (see, for example, Patent Document 1). ). The adhesive layer or the pressure-sensitive adhesive layer is usually supplied by applying the adhesive agent or the pressure-sensitive adhesive to one of the laminated optical films.

特開2014−172290号公報JP, 2014-172290, A

貼合に際し、接着剤又は粘着剤が光学フィルムの幅方向の端部からはみ出した場合、貼合ロールに接着剤又は粘着剤が付着して汚れてしまう。そして、貼合ロールに付着した接着剤又は粘着剤は後続の光学フィルムに転着し、積層光学フィルムをロール状に巻き取った場合にブロッキングの原因になり得る。 If the adhesive or the pressure-sensitive adhesive sticks out from the end portion of the optical film in the width direction during bonding, the adhesive or the pressure-sensitive adhesive adheres to the bonding roll and becomes dirty. Then, the adhesive or pressure-sensitive adhesive attached to the laminating roll is transferred to the subsequent optical film and may cause blocking when the laminated optical film is wound into a roll.

本発明は、光学フィルム同士の貼合に用いる接着剤又は粘着剤による貼合ロールの汚れを防止することができる、積層光学フィルムの製造方法を提供することを目的とする。 An object of the present invention is to provide a method for producing a laminated optical film, which can prevent a bonding roll from being soiled with an adhesive or a pressure-sensitive adhesive used for bonding optical films to each other.

本発明は、回転する一対の貼合ロールの間に、第1の光学フィルムと、接着剤層又は粘着剤層と、第2の光学フィルムとを、一対の貼合ロール間を結ぶ方向にこの順に配列した状態で導入して第1の光学フィルムと第2の光学フィルムとを貼合する、積層光学フィルムの製造方法であって、貼合時において、接着剤層又は粘着剤層の幅は、第1の光学フィルムの幅以上であり、第1の光学フィルムは、幅方向の位置が接着剤層又は粘着剤層の存在幅以内にあり、第2の光学フィルムの幅は、接着剤層又は粘着剤層の幅よりも大きく、第2の光学フィルムは、接着剤層又は粘着剤層の存在幅を内包するように位置しており、第1の光学フィルム側の貼合ロールと第1の光学フィルムとの間に、接着剤層又は粘着剤層の幅よりも大きい幅を有する第3の光学フィルムを、接着剤層又は粘着剤層の幅を内包するようにして介在させる、積層光学フィルムの製造方法を提供する。 The present invention provides the first optical film, the adhesive layer or the pressure-sensitive adhesive layer, and the second optical film between the pair of rotating bonding rolls in the direction connecting the pair of bonding rolls. A method for producing a laminated optical film, which comprises introducing the first optical film and the second optical film in a state of being arranged in order, wherein the width of the adhesive layer or the pressure-sensitive adhesive layer is at the time of attaching. , The width of the first optical film is greater than or equal to the width of the first optical film, the width of the first optical film is within the width of the adhesive layer or the pressure-sensitive adhesive layer, and the width of the second optical film is the width of the adhesive layer. Alternatively, the second optical film is larger than the width of the pressure-sensitive adhesive layer, and the second optical film is positioned so as to include the existing width of the adhesive layer or the pressure-sensitive adhesive layer. A third optical film having a width larger than the width of the adhesive layer or the pressure-sensitive adhesive layer is interposed between the third optical film and the optical film of 1. so as to include the width of the adhesive layer or the pressure-sensitive adhesive layer. A method for manufacturing a film is provided.

この製造方法によれば、第1の光学フィルムと第2の光学フィルムとの貼合時において、接着剤層又は粘着剤層と貼合ロールとの間に、接着剤層又は粘着剤層よりも幅広の第2の光学フィルム又は第3の光学フィルムが介在しているので、接着剤又は粘着剤による貼合ロールの汚れを防止することができる。 According to this manufacturing method, when the first optical film and the second optical film are bonded together, the adhesive layer or the pressure-sensitive adhesive layer and the bonding roll are more than the adhesive layer or the pressure-sensitive adhesive layer between the bonding layer and the bonding roll. Since the wide second optical film or the third optical film is interposed, it is possible to prevent the bonding roll from being soiled by the adhesive or the pressure-sensitive adhesive.

この製造方法において、第1の光学フィルム側の貼合ロールの幅は、第3の光学フィルムの幅よりも小さく、且つ、第1の光学フィルム側の貼合ロールは、幅方向の位置が第3の光学フィルムの存在幅内にある態様としてもよい。この場合、貼合ロールが接着剤又は粘着剤によって汚れることが一層防止される。 In this manufacturing method, the width of the bonding roll on the first optical film side is smaller than the width of the third optical film, and the bonding roll on the first optical film side has a widthwise position It is also possible to adopt a mode in which the optical film of No. 3 is within the existing width. In this case, the bonding roll is further prevented from being soiled with the adhesive or the pressure-sensitive adhesive.

本発明は、別の態様において、回転する一対の貼合ロールの間に、第1の光学フィルムと、接着剤層又は粘着剤層と、第2の光学フィルムとを、一対の貼合ロール間を結ぶ方向にこの順に配列した状態で導入して第1の光学フィルムと第2の光学フィルムとを貼合する、積層光学フィルムの製造方法であって、貼合時において、接着剤層又は粘着剤層の幅は、第1の光学フィルムの幅以上であり、第1の光学フィルムは、幅方向の位置が接着剤層又は粘着剤層の存在幅以内にあり、第2の光学フィルムの幅は、接着剤層又は粘着剤層の幅よりも大きく、第2の光学フィルムは、接着剤層又は粘着剤層の存在幅を内包するように位置しており、第1の光学フィルム側の貼合ロールの幅は、第1の光学フィルムの幅よりも小さく、第1の光学フィルム側の貼合ロールは、幅方向の位置が第1の光学フィルムの存在幅内にある、積層光学フィルムの製造方法を提供する。 In another aspect, the present invention provides, between a pair of rotating bonding rolls, a first optical film, an adhesive layer or a pressure-sensitive adhesive layer, and a second optical film between a pair of bonding rolls. A method for producing a laminated optical film, which comprises introducing the first optical film and the second optical film in the state of being arranged in this order in the direction connecting the two, and bonding the adhesive layer or the adhesive layer at the time of bonding. The width of the agent layer is equal to or more than the width of the first optical film, the first optical film has a position in the width direction within the existing width of the adhesive layer or the pressure-sensitive adhesive layer, and the width of the second optical film. Is larger than the width of the adhesive layer or the pressure-sensitive adhesive layer, the second optical film is positioned so as to include the existing width of the adhesive layer or the pressure-sensitive adhesive layer, and the second optical film is attached to the first optical film side. The width of the laminating roll is smaller than the width of the first optical film, and the laminating roll on the first optical film side has a position in the width direction within the existing width of the first optical film. A manufacturing method is provided.

この製造方法によれば、接着剤層又は粘着剤層が第1の光学フィルムの存在幅からはみ出しているが、第1の光学フィルム側の貼合ロールの幅が、第1の光学フィルムの幅よりも小さく、且つ、第1の光学フィルム側の貼合ロールが、幅方向の位置が第1の光学フィルムの存在幅内にあるので、当該貼合ロールが接着剤又は粘着剤によって汚れることが防止される。 According to this manufacturing method, the adhesive layer or the pressure-sensitive adhesive layer extends beyond the existing width of the first optical film, but the width of the bonding roll on the first optical film side is the width of the first optical film. Smaller than that, and since the bonding roll on the side of the first optical film has the position in the width direction within the existing width of the first optical film, the bonding roll may be contaminated with the adhesive or the adhesive. To be prevented.

また、本発明は、別の態様において、回転する一対の貼合ロールの間に、第1の光学フィルムと、接着剤層又は粘着剤層と、第2の光学フィルムとを、一対の貼合ロール間を結ぶ方向にこの順に配列した状態で導入して第1の光学フィルムと第2の光学フィルムとを貼合する、積層光学フィルムの製造方法であって、貼合時において、接着剤層又は粘着剤層の幅は、第1の光学フィルムの幅未満であり、接着剤層又は粘着剤層は、幅方向の位置が第1の光学フィルムの存在幅内にあり、第2の光学フィルムの幅は、接着剤層又は粘着剤層の幅よりも大きく、第2の光学フィルムは、接着剤層又は粘着剤層の存在幅を内包するように位置している、積層光学フィルムの製造方法を提供する。 In addition, the present invention, in another aspect, a pair of laminating a first optical film, an adhesive layer or a pressure-sensitive adhesive layer, and a second optical film between a pair of rotating laminating rolls. A method for producing a laminated optical film, which comprises introducing the first optical film and the second optical film in a state in which they are arranged in this order in a direction connecting the rolls, and is an adhesive layer at the time of bonding. Alternatively, the width of the pressure-sensitive adhesive layer is less than the width of the first optical film, and the position of the adhesive layer or the pressure-sensitive adhesive layer in the width direction is within the existing width of the first optical film, and the second optical film. Is larger than the width of the adhesive layer or the pressure-sensitive adhesive layer, and the second optical film is positioned so as to include the existing width of the adhesive layer or the pressure-sensitive adhesive layer. I will provide a.

この製造方法によれば、接着剤層又は粘着剤層が第1の光学フィルム及び第2の光学フィルムの存在幅をはみ出す可能性が極めて小さいので、接着剤又は粘着剤による貼合ロールの汚れを防止することができる。 According to this manufacturing method, since the adhesive layer or the pressure-sensitive adhesive layer has a very small possibility of protruding the existing width of the first optical film and the second optical film, it is possible to prevent the bonding roll from being soiled by the adhesive or the pressure-sensitive adhesive. Can be prevented.

この製造方法において、第1の光学フィルム側の貼合ロールの幅は、第1の光学フィルムの幅よりも小さく、且つ、第1の光学フィルム側の貼合ロールは、幅方向の位置が第1の光学フィルムの存在幅内にある態様としてもよい。この場合、貼合ロールが接着剤又は粘着剤によって汚れることが一層防止される。 In this manufacturing method, the width of the bonding roll on the side of the first optical film is smaller than the width of the first optical film, and the bonding roll on the side of the first optical film is located at the position in the width direction. A mode in which the width of the optical film 1 is within the existing width may be adopted. In this case, the bonding roll is further prevented from being soiled with the adhesive or the pressure-sensitive adhesive.

また、この製造方法において、接着剤層又は粘着剤層の幅は、第1の光学フィルムの幅よりも0.1〜50mm小さい態様としてもよい。この場合、第1の光学フィルムと第2の光学フィルムとを幅方向の端部まで十分に接着又は粘着させることができる。 Moreover, in this manufacturing method, the width of the adhesive layer or the pressure-sensitive adhesive layer may be smaller than the width of the first optical film by 0.1 to 50 mm. In this case, the first optical film and the second optical film can be sufficiently adhered or adhered to the ends in the width direction.

以上に述べた各製造方法においては、第1の光学フィルムは、樹脂基材と樹脂基材の片面又は両面に設けられた光学機能層とを有し、樹脂基材及び光学機能層は、互いに幅が等しく両端が揃っており、第1の光学フィルムは、光学機能層側が接着剤層又は粘着剤層側を向くように配置されており、第2の光学フィルムは、保護フィルムである態様としてもよい。この態様では、第1の光学フィルムが樹脂基材と光学機能層とを有していながらも、幅方向の端部の膜厚が安定している。 In each of the manufacturing methods described above, the first optical film has a resin base material and an optical functional layer provided on one or both sides of the resin base material, and the resin base material and the optical functional layer are mutually The widths are equal and both ends are aligned, the first optical film is arranged so that the optical functional layer side faces the adhesive layer or the pressure-sensitive adhesive layer side, and the second optical film is a protective film. Good. In this aspect, although the first optical film has the resin base material and the optical functional layer, the film thickness at the end portion in the width direction is stable.

上記光学機能層は、偏光子であってもよく、このとき、偏光子は樹脂基材に塗工されて設けられたものである態様であってもよい。 The optical functional layer may be a polarizer, and at this time, the polarizer may be applied by coating on a resin base material.

本発明は、別の態様において、回転する一対の貼合ロールの間に、樹脂基材と、樹脂基材の片面又は両面に設けられた光学機能層と、接着剤層又は粘着剤層と、保護フィルムとを、一対の貼合ロール間を結ぶ方向にこの順に配列した状態で導入して光学機能層と保護フィルムとを貼合する、積層光学フィルムの製造方法であって、貼合時において、光学機能層の幅は、樹脂基材の幅よりも小さく、接着剤層又は粘着剤層の幅は、光学機能層の幅以上であり、且つ、樹脂基材の幅よりも小さく、樹脂基材は、光学機能層及び接着剤層又は粘着剤層の存在幅を内包するように位置しており、保護フィルムの幅は、接着剤層又は粘着剤層の幅よりも大きく、保護フィルムは、接着剤層又は粘着剤層の存在幅を内包するように位置している、積層光学フィルムの製造方法を提供する。 The present invention, in another aspect, between a pair of rotating laminating rolls, a resin substrate, an optical functional layer provided on one side or both sides of the resin substrate, an adhesive layer or a pressure-sensitive adhesive layer, A protective film and a method for producing a laminated optical film, which comprises introducing an optical functional layer and a protective film by introducing the protective film in a state of being arranged in this order in a direction connecting a pair of laminating rolls, at the time of laminating. The width of the optical functional layer is smaller than the width of the resin base material, the width of the adhesive layer or the pressure-sensitive adhesive layer is equal to or larger than the width of the optical functional layer, and smaller than the width of the resin base material. The material is positioned so as to include the existing width of the optical functional layer and the adhesive layer or the pressure-sensitive adhesive layer, the width of the protective film is larger than the width of the adhesive layer or the pressure-sensitive adhesive layer, the protective film, Provided is a method for producing a laminated optical film, which is positioned so as to include the existing width of an adhesive layer or a pressure-sensitive adhesive layer.

この製造方法によれば、光学機能層と保護フィルムとの貼合時において、接着剤層又は粘着剤層と貼合ロールとの間に、接着剤層又は粘着剤層よりも幅広の樹脂基材又は保護フィルムが介在しているので、接着剤又は粘着剤による貼合ロールの汚れを防止することができる。 According to this manufacturing method, at the time of bonding the optical functional layer and the protective film, between the adhesive layer or the pressure-sensitive adhesive layer and the bonding roll, a resin base material wider than the adhesive layer or the pressure-sensitive adhesive layer. Alternatively, since the protective film is interposed, it is possible to prevent the bonding roll from being soiled with the adhesive or the adhesive.

この製造方法において、樹脂基材側の貼合ロールの幅は、樹脂基材の幅よりも小さく、且つ、樹脂基材側の貼合ロールは、幅方向の位置が樹脂基材の存在幅内にある態様としてもよい。この場合、貼合ロールが接着剤又は粘着剤によって汚れることが一層防止される。 In this manufacturing method, the width of the bonding roll on the resin base material side is smaller than the width of the resin base material, and the bonding roll on the resin base material side has a position in the width direction within the existing width of the resin base material. It is also possible to adopt the mode described in 1. In this case, the bonding roll is further prevented from being soiled with the adhesive or the pressure-sensitive adhesive.

また、この製造方法において、上記光学機能層は偏光子であってもよく、このとき、偏光子は樹脂基材に塗工されて設けられたものである態様であってもよい。 Further, in this manufacturing method, the optical function layer may be a polarizer, and at this time, the polarizer may be applied by coating on a resin base material.

本発明によれば、光学フィルム同士の貼合に用いる接着剤又は粘着剤による貼合ロールの汚れを防止することができる、積層光学フィルムの製造方法を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the manufacturing method of a laminated optical film which can prevent a bonding roll from being soiled with the adhesive agent or adhesive agent used for bonding optical films can be provided.

第1の実施形態の製造方法で製造される積層光学フィルムの断面図である。It is sectional drawing of the laminated optical film manufactured by the manufacturing method of 1st Embodiment. 第1の実施形態の製造方法を示す図である。It is a figure which shows the manufacturing method of 1st Embodiment. 図2のIII-III断面図であって、第1の実施形態の貼合時の積層状態を示す図である。FIG. 3 is a cross-sectional view taken along the line III-III in FIG. 2, showing a laminated state at the time of bonding in the first embodiment. 第2の実施形態の製造方法で製造される積層光学フィルムの断面図である。It is sectional drawing of the laminated optical film manufactured by the manufacturing method of 2nd Embodiment. 第2の実施形態の製造方法を示す図である。It is a figure which shows the manufacturing method of 2nd Embodiment. 図5のVI-VI断面図であって、第2の実施形態の貼合時の積層状態を示す図である。It is a VI-VI sectional view of FIG. 5, and is a figure which shows the laminated state at the time of sticking of 2nd Embodiment. 第3の実施形態の製造方法で製造される積層光学フィルムの断面図である。It is sectional drawing of the laminated optical film manufactured by the manufacturing method of 3rd Embodiment. 第3の実施形態の貼合時の積層状態を示す図である。It is a figure which shows the laminated state at the time of sticking of 3rd Embodiment. 第4の実施形態の製造方法で製造される積層光学フィルムの断面図である。It is sectional drawing of the laminated optical film manufactured by the manufacturing method of 4th Embodiment. 第4の実施形態の貼合時の積層状態を示す図である。It is a figure which shows the laminated state at the time of sticking of 4th Embodiment.

以下、本発明の好適な実施形態について、図面を参照しながら詳細に説明する。なお、各図において同一部分又は相当部分には同一符号を付し、重複する説明は省略する。また、各図面の寸法比率は必ずしも実際のものとは一致せず、特に、フィルムの厚さや幅に関しては誇張して描いてある。 Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the drawings. In the drawings, the same or corresponding parts are designated by the same reference numerals, and overlapping description will be omitted. Further, the dimensional ratios in the drawings do not always match the actual ones, and in particular, the thickness and width of the film are exaggerated.

<第1の実施形態>
(積層光学フィルム)
図1に示されているとおり、第1の実施形態の積層光学フィルムの製造方法により製造される積層光学フィルム1Aは、第1の光学フィルム2の一方の面に第2の光学フィルム3が接着剤層5を介して積層されており、且つ、第1の光学フィルム2の他方の面に第3の光学フィルム6が積層されている。第1の光学フィルム2は、二つの層、すなわち樹脂基材21と、その片面に設けられた偏光子22とを有しており、これらは互いに剥離可能である。
<First Embodiment>
(Laminated optical film)
As shown in FIG. 1, in the laminated optical film 1A manufactured by the method for manufacturing a laminated optical film of the first embodiment, the second optical film 3 is bonded to one surface of the first optical film 2. The third optical film 6 is laminated via the agent layer 5, and the third optical film 6 is laminated on the other surface of the first optical film 2. The first optical film 2 has two layers, that is, a resin base material 21 and a polarizer 22 provided on one surface thereof, and these are separable from each other.

第1の光学フィルム2において、樹脂基材21及び偏光子22は、互いに幅が等しく両端が揃っており、第1の光学フィルム2は、偏光子22側が接着剤層5側を向くように配置されている。なお、本明細書において各光学フィルムの「幅」とは、積層光学フィルム1Aの製造時における各光学フィルムの搬送方向に垂直な方向であって、貼合ロールの延在方向の幅をいう。また、各フィルムの幅の相対的な大小関係(広狭関係)については「大きい」及び「小さい」の表現を用いている。 In the first optical film 2, the resin base material 21 and the polarizer 22 have the same width and both ends are aligned, and the first optical film 2 is arranged such that the polarizer 22 side faces the adhesive layer 5 side. Has been done. In addition, in this specification, the "width" of each optical film is a direction perpendicular to the transport direction of each optical film at the time of manufacturing the laminated optical film 1A, and refers to the width in the extending direction of the bonding roll. Further, the expressions "large" and "small" are used for the relative size relation (width relation) of the width of each film.

積層光学フィルム1Aは、第3の光学フィルム6及び樹脂基材21が取り除かれ、偏光子22と第2の光学フィルム(=後述する保護フィルム)3とを備える偏光板10として利用されるものである。偏光板10は、必要に応じて剥離された樹脂基材21側や第2の光学フィルム3側に、保護フィルムその他の光学フィルムを接着剤層や粘着剤層を介して新たに設けてもよい。 The laminated optical film 1A is used as a polarizing plate 10 in which the third optical film 6 and the resin base material 21 are removed and the polarizer 22 and the second optical film (=protective film described later) 3 are provided. is there. In the polarizing plate 10, a protective film or other optical film may be newly provided on the resin substrate 21 side or the second optical film 3 side, which is peeled off, if necessary, via an adhesive layer or a pressure-sensitive adhesive layer. ..

第1の光学フィルム2、第2の光学フィルム3、第3の光学フィルム6及び接着剤層5の互いの幅の大小関係や位置関係については後述するとおりであり、これらの層は、各幅方向の中心軸が略揃っている。すなわち、図1に示されている断面図において積層態様が略左右対称をなしている。 The magnitude relationship and the positional relationship of the widths of the first optical film 2, the second optical film 3, the third optical film 6, and the adhesive layer 5 are as described later, and these layers have the respective widths. The central axes of directions are almost aligned. That is, in the cross-sectional view shown in FIG. 1, the stacking manner is substantially symmetrical.

ここで、各フィルム及び接着剤層5の構成について説明する。偏光子22の材料としては、従来から偏光板の製造に使用されている公知の材料を用いることができ、例えば、ポリビニルアルコール系樹脂、ポリ酢酸ビニル樹脂、エチレン/酢酸ビニル(EVA)樹脂、ポリアミド樹脂、ポリエステル系樹脂等が挙げられる。なかでもポリビニルアルコール系樹脂が好ましい。これらの材料を延伸処理、ヨウ素又は二色性染料による染色及びホウ酸処理を施すことによりフィルム状の偏光子22を得ることができる。このフィルム状の偏光子22を任意の大きさに切り出したものを第1の光学フィルム2としてもよいし、更に樹脂基材21の片面又は両面に粘着剤を介して貼り合わせた積層体を第1の光学フィルム2としてもよい。 Here, the configuration of each film and the adhesive layer 5 will be described. As the material of the polarizer 22, a known material which has been conventionally used for manufacturing a polarizing plate can be used. For example, polyvinyl alcohol resin, polyvinyl acetate resin, ethylene/vinyl acetate (EVA) resin, polyamide Examples thereof include resins and polyester resins. Among them, polyvinyl alcohol resin is preferable. The film-shaped polarizer 22 can be obtained by subjecting these materials to stretching treatment, dyeing with iodine or a dichroic dye, and boric acid treatment. The film-shaped polarizer 22 cut into an arbitrary size may be used as the first optical film 2, or a laminated body obtained by laminating one side or both sides of the resin base material 21 with an adhesive may be used. The optical film 2 of 1 may be used.

また、偏光子22の形成方法としては、樹脂基材21の片面又は両面に偏光子22の材料を溶解した塗液を薄膜状(フィルム状)に塗工、乾燥した後、樹脂基材21ごと延伸処理し、ヨウ素又は二色性染料による染色及びホウ酸処理してもよい。その後、樹脂基材21ごと任意の大きさに切り出して第1の光学フィルム2とすることができる。 In addition, as a method of forming the polarizer 22, one or both surfaces of the resin base material 21 are coated with a coating solution in which the material of the polarizer 22 is dissolved in a thin film (film form), dried, and then the whole resin base material 21. It may be stretched, dyed with iodine or a dichroic dye, and treated with boric acid. After that, the first optical film 2 can be obtained by cutting out the resin substrate 21 into an arbitrary size.

延伸処理方法には、フィルム長手方向(フィルム搬送方向)に延伸する縦延伸やフィルム幅方向に延伸する横延伸又は斜め延伸など挙げられる。縦延伸方式としては、ロール間延伸、圧縮延伸等が挙げられ、横延伸方式としては、テンター法などが挙げられる。延伸処理は、湿潤延伸方法、乾式延伸方法のいずれも採用できるが、乾式延伸方法を用いるほうが、延伸温度を広い範囲から選択することができる点で好ましい。 Examples of the stretching treatment method include longitudinal stretching for stretching in the longitudinal direction of the film (film transport direction), transverse stretching for stretching in the film width direction, and diagonal stretching. Examples of the longitudinal stretching method include inter-roll stretching and compression stretching, and examples of the lateral stretching method include a tenter method. As the stretching treatment, either a wet stretching method or a dry stretching method can be adopted, but it is preferable to use the dry stretching method because the stretching temperature can be selected from a wide range.

偏光子22の厚さは、2〜75μmであることが好ましく、2〜50μmであることがより好ましく、2〜30μmであることが更に好ましい。 The thickness of the polarizer 22 is preferably 2 to 75 μm, more preferably 2 to 50 μm, and further preferably 2 to 30 μm.

樹脂基材21は、偏光子22を薄膜状(フィルム状)に塗工するための支持体としての役割、及び偏光子22の表面を保護する役割をもつものであり、各種の樹脂材料を用いることができる。樹脂基材21の材料としては、例えばポリエチレンテレフタレート(PET)系樹脂、ポリプロピレン系樹脂、ポリカーボネート系樹脂が挙げられる。 The resin base material 21 has a role as a support for coating the polarizer 22 in a thin film shape (film shape) and a role for protecting the surface of the polarizer 22, and various resin materials are used. be able to. Examples of the material of the resin base material 21 include polyethylene terephthalate (PET) resin, polypropylene resin, and polycarbonate resin.

樹脂基材21の厚さは、20〜500μmであることが好ましく、30〜300μmであることがより好ましく、50〜200μmであることが更に好ましい。 The thickness of the resin base material 21 is preferably 20 to 500 μm, more preferably 30 to 300 μm, and further preferably 50 to 200 μm.

第2の光学フィルム3は、ここでは保護フィルム3であり、第3の光学フィルム6は仮保護フィルム6である。 The second optical film 3 is here a protective film 3 and the third optical film 6 is a temporary protective film 6.

保護フィルム3は、偏光子22の主面や端部の割れや傷つきを防止するフィルムである。ここで「保護フィルム」とは、偏光子22に種々積層され得るフィルムのなかでも、接着剤を介して直接積層されたフィルムを指している。 The protective film 3 is a film that prevents the main surface and end portions of the polarizer 22 from being cracked or scratched. Here, the “protective film” refers to a film that is directly laminated via an adhesive, among various films that can be laminated on the polarizer 22.

保護フィルム3は、偏光板の分野で知られている各種の透明樹脂フィルムで構成することができる。例えば、トリアセチルセルロースを代表例とするセルロース系樹脂、ポリプロピレン系樹脂を代表例とするポリオレフィン系樹脂、ノルボルネン系樹脂を代表例とする環状オレフィン系樹脂、ポリメチルメタクリレート系樹脂を代表例とするアクリル系樹脂、ポリエチレンテレフタレート系樹脂を代表例とするポリエステル系樹脂等が挙げられる。なかでも、セルロース系樹脂が代表的である。 The protective film 3 can be composed of various transparent resin films known in the field of polarizing plates. For example, a cellulose resin typified by triacetyl cellulose, a polyolefin resin typified by a polypropylene resin, a cyclic olefin resin typified by a norbornene resin, and an acrylic resin typified by a polymethylmethacrylate resin. Examples thereof include polyester resins and polyester resins represented by polyethylene terephthalate resins. Of these, a cellulosic resin is typical.

保護フィルム3としては、光学機能を有しないフィルムであってもよいし、位相差フィルムや輝度向上フィルムといった光学機能を併せもつフィルムであってもよい。 The protective film 3 may be a film having no optical function or a film having an optical function such as a retardation film or a brightness enhancement film.

保護フィルム3の厚さは、5〜90μmであることが好ましく、5〜80μmであることがより好ましく、5〜50μmであることが更に好ましい。 The thickness of the protective film 3 is preferably 5 to 90 μm, more preferably 5 to 80 μm, and further preferably 5 to 50 μm.

接着剤層5をなす接着剤としては、従来から偏光板の製造に使用されている各種の接着剤を使用することができる。例えば、耐候性や屈折率、カチオン重合性等の観点から、分子内に芳香環を含まないエポキシ樹脂が好ましい。また、活性エネルギー線(紫外線又は熱線)の照射によって硬化するものが好ましい。 As the adhesive forming the adhesive layer 5, various kinds of adhesives conventionally used for manufacturing a polarizing plate can be used. For example, from the viewpoint of weather resistance, refractive index, cationic polymerizability, etc., an epoxy resin having no aromatic ring in the molecule is preferable. Further, those which are cured by irradiation with active energy rays (ultraviolet rays or heat rays) are preferable.

エポキシ樹脂としては、例えば水素化エポキシ樹脂、脂環式エポキシ樹脂、脂肪族エポキシ樹脂等が好ましい。エポキシ樹脂に対して、重合開始剤(例えば紫外線照射で重合させるための光カチオン重合開始剤、熱線照射によって重合させるための熱カチオン重合開始剤)や、更に他の添加剤(増感剤等)を添加して、塗布用のエポキシ樹脂組成物を調製して使用することができる。 As the epoxy resin, for example, hydrogenated epoxy resin, alicyclic epoxy resin, aliphatic epoxy resin and the like are preferable. For epoxy resins, polymerization initiators (eg, photocationic polymerization initiators for polymerization by UV irradiation, thermal cationic polymerization initiators for polymerization by heat ray irradiation), and other additives (sensitizers, etc.) Can be added to prepare and use an epoxy resin composition for coating.

また、接着剤としては、アクリルアミド、アクリレート、ウレタンアクリレート、エポキシアクリレート等のアクリル系樹脂や、ポリビニルアルコール系の水系接着剤を使用することもできる。 As the adhesive, an acrylic resin such as acrylamide, acrylate, urethane acrylate, or epoxy acrylate, or a polyvinyl alcohol-based water-based adhesive can be used.

偏光板10は、液晶セル等の表示用セル(画像表示素子)の片面又は両面に貼着されるものである。偏光板は、保護フィルム上に積層される他の光学層を更に含むことができる。他の光学層としては、ある種の偏光を透過し、それと逆の性質を示す偏光を反射する反射型偏光フィルム;表面に凹凸形状を有する防眩機能付フィルム;表面反射防止機能付フィルム;表面に反射機能を有する反射フィルム;反射機能と透過機能とを併せ持つ半透過反射フィルム;視野角補償フィルム等が挙げられる。 The polarizing plate 10 is attached to one side or both sides of a display cell (image display element) such as a liquid crystal cell. The polarizing plate may further include another optical layer laminated on the protective film. As the other optical layer, a reflective polarizing film that transmits a certain polarized light and reflects a polarized light having the opposite property; a film having an uneven surface with an antiglare function; a film with a surface antireflection function; a surface A reflective film having a reflective function; a semi-transmissive reflective film having both a reflective function and a transmissive function; and a viewing angle compensation film.

偏光子22と保護フィルム3の二層からなる偏光板10の厚さは、10〜500μmであることが好ましく、10〜300μmであることがより好ましく、10〜200μmであることが更に好ましい。 The thickness of the polarizing plate 10 having two layers of the polarizer 22 and the protective film 3 is preferably 10 to 500 μm, more preferably 10 to 300 μm, and further preferably 10 to 200 μm.

仮保護フィルム6は、接着剤が貼合ロールに付着することを防止するためのフィルムであり、また、仮保護フィルム6を積層した部材(ここでは第1の光学フィルム2)の表面を損傷、摩損等から保護するためのフィルムである。仮保護フィルム6の材料としては、上記保護フィルムと同様のものを用いることができ、なかでもポリエチレンテレフタレート、ポリエチレンナフタレート、ポリエチレンイソフタレート、ポリブチレンテレフタレート等のポリエステル系樹脂が好ましい。 The temporary protective film 6 is a film for preventing the adhesive from adhering to the bonding roll, and also damages the surface of the member (here, the first optical film 2) in which the temporary protective film 6 is laminated, It is a film to protect from abrasion and the like. As the material of the temporary protective film 6, the same materials as those of the above-mentioned protective film can be used, and among them, polyester resins such as polyethylene terephthalate, polyethylene naphthalate, polyethylene isophthalate and polybutylene terephthalate are preferable.

仮保護フィルム6は、基材となるフィルムの他に、このフィルムの表面に積層された弱い接着性を有する粘着剤層を有していてもよい。 The temporary protective film 6 may have a pressure-sensitive adhesive layer having a weak adhesive property, which is laminated on the surface of the film, in addition to the film serving as the base material.

仮保護フィルム6の厚さは、5〜200μmであることが好ましく、5〜100μmであることがより好ましく、5〜50μmであることが更に好ましい。 The thickness of the temporary protective film 6 is preferably 5 to 200 μm, more preferably 5 to 100 μm, and further preferably 5 to 50 μm.

(積層光学フィルムの製造方法)
積層光学フィルム1Aの製造方法としては、図2及び図3に示されているとおり、回転する一対の貼合ロール7a,7bの間に、第1の光学フィルム2と、接着剤層5と、保護フィルム3とを、一対の貼合ロール7a,7b間を結ぶ方向にこの順に配列した状態で導入して、第1の光学フィルム2と保護フィルム3とを貼合する。このとき、第1の光学フィルム2側の貼合ロール7aと第1の光学フィルム2との間に仮保護フィルム6を介在させる。
(Method for manufacturing laminated optical film)
As a manufacturing method of the laminated optical film 1A, as shown in FIGS. 2 and 3, between the pair of rotating bonding rolls 7a and 7b, the first optical film 2, the adhesive layer 5, and The protective film 3 is introduced in the state of being arranged in this order in the direction connecting the pair of bonding rolls 7a and 7b, and the first optical film 2 and the protective film 3 are bonded together. At this time, the temporary protective film 6 is interposed between the bonding roll 7a on the first optical film 2 side and the first optical film 2.

ここで、第1の光学フィルム2における偏光子22は、樹脂基材21に塗工、乾燥した後、樹脂基材21ごと延伸処理し、ヨウ素又は二色性染料による染色及びホウ酸処理を施し、水洗、乾燥の後、幅方向端部を切り出して樹脂基材21と偏光子22の互いの幅が等しく、両端を揃えることで供給し、接着剤層5は保護フィルム3に塗工することで供給する。なお図2では、接着剤層5の図示を省略している。 Here, the polarizer 22 in the first optical film 2 is applied to the resin base material 21, dried, and then stretched together with the resin base material 21, dyed with iodine or a dichroic dye, and subjected to boric acid treatment. After rinsing with water and drying, the widthwise ends are cut out so that the resin base material 21 and the polarizer 22 have the same width and are supplied by aligning both ends, and the adhesive layer 5 is applied to the protective film 3. Supplied by. The adhesive layer 5 is not shown in FIG.

第1の光学フィルム2、保護フィルム3、及び仮保護フィルム6は積層されて積層体4Aとなり、積層体4Aはその後、接着剤層5が硬化することで、図1に示された積層光学フィルム1Aとして完成する。 The first optical film 2, the protective film 3, and the temporary protective film 6 are laminated to form a laminated body 4A, and the laminated body 4A is then cured by the adhesive layer 5, whereby the laminated optical film shown in FIG. Completed as 1A.

貼合時の各部材の存在態様について説明する。図3に示されているとおり、一対の貼合ロール7a,7b間における各フィルムや接着剤層5の幅は、以下の関係を満たしている。なお、図3では図面を見やすくするために貼合ロール7a,7bを積層体4Aから離して描いている。
・接着剤層5の幅Wは、第1の光学フィルム2の幅W以上である。(W≧W
・第1の光学フィルム2は、幅方向の位置が接着剤層5の存在幅W以内にある。
・保護フィルム3の幅Wは、接着剤層5の幅Wよりも大きい。(W>W
・保護フィルム3は、接着剤層5の存在幅Wを内包するように位置している。
・仮保護フィルム6の幅Wは、接着剤層5の幅Wよりも大きい。(W>W
・仮保護フィルム6は、接着剤層5の存在幅Wを内包するように介在している。
The mode of existence of each member at the time of bonding will be described. As shown in FIG. 3, the width of each film or the adhesive layer 5 between the pair of bonding rolls 7a and 7b satisfies the following relationship. In addition, in FIG. 3, the bonding rolls 7a and 7b are drawn away from the laminated body 4A in order to make the drawing easy to see.
The width W A of the adhesive layer 5 is greater than or equal to the width W 1 of the first optical film 2. (W A ≧W 1 )
- first optical film 2, the position in the width direction is within the existence range W A of the adhesive layer 5.
- the width W 2 of the protective film 3 is greater than the width W A of the adhesive layer 5. (W 2 >W A )
· Protective film 3 is positioned so as to include the presence width W A of the adhesive layer 5.
- the width W 3 of the temporary protective film 6 is larger than the width W A of the adhesive layer 5. (W 3> W A)
- temporary protective film 6 is interposed so as to include the presence width W A of the adhesive layer 5.

ここで「内包」とは、幅が広い側の部材の両端部が、幅が狭い側の部材の両端部よりも、幅方向において外側に位置していることをいう。 Here, the term “inner package” means that both ends of the member on the wide side are located outside in the width direction with respect to both ends of the member on the narrow side.

なお、保護フィルム3の幅と仮保護フィルム6の幅との大小関係は任意である。 The size relationship between the width of the protective film 3 and the width of the temporary protective film 6 is arbitrary.

また、第1の実施形態の製造方法は、必須の要件ではないが、以下の関係も満たしている。
・第1の光学フィルム2側の貼合ロール7aの幅WR1は、仮保護フィルム6の幅Wよりも小さい。(W>WR1
・第1の光学フィルム2側の貼合ロール7aは、幅方向の位置が仮保護フィルム6の存在幅W内にある。
・保護フィルム3側の貼合ロール7bの幅WR2は、接着剤層5の幅Wよりも大きい。(WR2>W
・保護フィルム3側の貼合ロール7bは、幅方向の位置が接着剤層5の存在幅Wを内包するように位置している。
・保護フィルム3側の貼合ロール7bの幅WR2は、保護フィルム3の幅Wよりも大きい。(WR2>W
・保護フィルム3側の貼合ロール7bは、幅方向の位置が保護フィルム3の存在幅Wを内包するように位置している。
The manufacturing method of the first embodiment also satisfies the following relationship, although it is not an essential requirement.
The width W R1 of the bonding roll 7 a on the first optical film 2 side is smaller than the width W 3 of the temporary protective film 6. (W 3 >W R1 )
- first optical film 2 side of the lamination rolls 7a, the position in the width direction is within the existence range W 3 of the temporary protective film 6.
The width W R2 of the bonding roll 7 b on the protective film 3 side is larger than the width W A of the adhesive layer 5. (W R2> W A)
- lamination rolls 7b of the protective film 3 side, the position in the width direction are positioned so as to include the presence width W A of the adhesive layer 5.
The width W R2 of the bonding roll 7b on the protective film 3 side is larger than the width W 2 of the protective film 3. (W R2> W 2)
- lamination rolls 7b of the protective film 3 side is positioned such that the positions in the width direction containing the present width W 2 of the protective film 3.

ここで「貼合ロールの幅」とは、貼合に寄与する有効接触面となる部分と同径を維持しながら延びている部分の全幅を意味する。例えば、貼合ロール7a,7bの端部側において幅方向の一部が縮径し第1の光学フィルム2又は保護フィルム3と接触しない部分がある場合は、縮径した部分を除いた部分の幅を貼合ロール7a,7bの全幅とする。 Here, the "width of the bonding roll" means the entire width of the portion extending while maintaining the same diameter as the portion that becomes the effective contact surface that contributes to the bonding. For example, when a part in the width direction on the end side of the bonding rolls 7a and 7b has a reduced diameter and does not come into contact with the first optical film 2 or the protective film 3, a portion excluding the reduced diameter is used. The width is the entire width of the bonding rolls 7a and 7b.

第1の光学フィルム2側の貼合ロール7aの幅WR1は、接着剤層5の幅Wよりも小さいことが好ましく、第1の光学フィルム2の幅Wよりも小さいことがより好ましい。また、貼合ロール7aの幅WR1は、第3の光学フィルム6の幅Wよりも1〜100mm小さいことが好ましく、1〜50mm小さいことがより好ましい。 The width W R1 of the bonding roll 7a on the first optical film 2 side is preferably smaller than the width W A of the adhesive layer 5, and more preferably smaller than the width W 1 of the first optical film 2. .. The width W R1 of the laminating roll 7a is preferably smaller than the width W 3 of the third optical film 6 by 1 to 100 mm, more preferably 1 to 50 mm.

この製造方法によれば、第1の光学フィルム2と保護フィルム3との貼合時において、接着剤層5と貼合ロール7a,7bとの間に、接着剤層5よりも幅広の保護フィルム3又は仮保護フィルム6が介在しているので、接着剤による貼合ロール7a,7bの汚れを防止することができる。 According to this manufacturing method, at the time of bonding the first optical film 2 and the protective film 3, a protective film wider than the adhesive layer 5 between the adhesive layer 5 and the bonding rolls 7a and 7b. 3 or the provisional protective film 6 is interposed, it is possible to prevent the bonding rolls 7a and 7b from being soiled by the adhesive.

また、この製造方法において、第1の光学フィルム2側の貼合ロール7aの幅WR1は、仮保護フィルム6の幅Wよりも小さく、且つ、第1の光学フィルム2側の貼合ロール7aは、幅方向の位置が仮保護フィルム6の存在幅W内にあるので、貼合ロール7aが接着剤によって汚れることが一層防止される。 Moreover, in this manufacturing method, the width W R1 of the bonding roll 7a on the first optical film 2 side is smaller than the width W 3 of the temporary protective film 6, and the bonding roll on the first optical film 2 side. 7a, the position in the width direction because in the present width W 3 of the temporary protective film 6, the lamination rolls 7a is be contaminated by the adhesive is further prevented.

また、第1の光学フィルム2を構成している樹脂基材21と偏光子22とは、互いに幅が等しく両端が揃っているので、第1の光学フィルム2として幅方向の端部の膜厚が安定している。 Further, since the resin base material 21 and the polarizer 22 forming the first optical film 2 have the same width and both ends are aligned, the film thickness of the end portion in the width direction as the first optical film 2 is obtained. Is stable.

また、接着剤層5の幅Wが第1の光学フィルム2の幅W以上である(W≧W)ので、樹脂基材21を偏光子22から剥離する際に、偏光子22が裂けることが防止される。 Further, since the width W A of the adhesive layer 5 is equal to or larger than the width W 1 of the first optical film 2 (W A ≧W 1 ), when the resin base material 21 is peeled from the polarizer 22, the polarizer 22 Is prevented from tearing.

なお、この第1の実施形態では保護フィルム3側の貼合ロール7bの幅WR2が保護フィルム3の幅Wよりも大きい態様を示したが、貼合ロール7bの幅は、保護フィルム3の幅Wより小さくてもよい。この場合、貼合ロール7bは、保護フィルム3の存在幅W内に位置するようにする。これによれば、貼合ロール7bが接着剤によって汚れることが一層防止される。 Although the width W R2 of the bonding roll 7b on the side of the protective film 3 is larger than the width W 2 of the protective film 3 in the first embodiment, the width of the bonding roll 7b is equal to the width of the protective film 3b. May be smaller than the width W 2 . In this case, the lamination rolls 7b is to be positioned in the presence width W 2 of the protective film 3. According to this, the bonding roll 7b is further prevented from being soiled by the adhesive.

<第2の実施形態>
以下、本発明の第2の実施形態について説明する。第1の実施形態との相違点について主に説明する。
<Second Embodiment>
Hereinafter, the second embodiment of the present invention will be described. Differences from the first embodiment will be mainly described.

(積層光学フィルム)
図4に示されているとおり、第2の実施形態の積層光学フィルムの製造方法により製造される積層光学フィルム1Bは、第3の光学フィルム6を備えていない。
(Laminated optical film)
As shown in FIG. 4, the laminated optical film 1B manufactured by the method for manufacturing a laminated optical film of the second embodiment does not include the third optical film 6.

(積層光学フィルムの製造方法)
積層光学フィルム1Bの製造方法としては、図5及び図6に示されているとおり、回転する一対の貼合ロール7a,7bの間に、第1の光学フィルム2と、接着剤層5と、保護フィルム3とを、一対の貼合ロール7a,7b間を結ぶ方向にこの順に配列した状態で導入して、第1の光学フィルム2と保護フィルム3とを貼合する。
(Method for manufacturing laminated optical film)
As a method for manufacturing the laminated optical film 1B, as shown in FIGS. 5 and 6, the first optical film 2 and the adhesive layer 5 are provided between the pair of rotating bonding rolls 7a and 7b. The protective film 3 is introduced in the state of being arranged in this order in the direction connecting the pair of bonding rolls 7a and 7b, and the first optical film 2 and the protective film 3 are bonded together.

第1の光学フィルム2及び保護フィルム3は積層されて積層体4Bとなり、積層体4Bはその後、接着剤層5が硬化することで、図4に示された積層光学フィルム1Bとして完成する。 The 1st optical film 2 and the protective film 3 are laminated|stacked, and it becomes the laminated body 4B, and the adhesive body layer 5 cures the laminated body 4B after that, and it is completed as the laminated optical film 1B shown in FIG.

貼合時の各部材の存在態様について説明する。図6に示されているとおり、一対の貼合ロール7a,7b間における各フィルム、接着剤層5、及び貼合ロール7aの幅は、以下の関係を満たしている。なお、図6では図面を見やすくするために貼合ロール7a,7bを積層体4Bから離して描いている。
・接着剤層5の幅Wは、第1の光学フィルム2の幅W以上である。(W≧W
・第1の光学フィルム2は、幅方向の位置が接着剤層5の存在幅W以内にある。
・保護フィルム3の幅Wは、接着剤層5の幅Wよりも大きい。(W>W
・保護フィルム3は、接着剤層5の存在幅Wを内包するように位置している。
・第1の光学フィルム2側の貼合ロール7aの幅WR1は、第1の光学フィルム2の幅Wよりも小さい。(W>WR1
・第1の光学フィルム2側の貼合ロール7aは、幅方向の位置が第1の光学フィルム2の存在幅W内にある。
The mode of existence of each member at the time of bonding will be described. As shown in FIG. 6, the widths of the films, the adhesive layer 5, and the bonding roll 7a between the pair of bonding rolls 7a and 7b satisfy the following relationship. In addition, in FIG. 6, the bonding rolls 7a and 7b are drawn away from the laminated body 4B in order to make the drawing easy to see.
The width W A of the adhesive layer 5 is greater than or equal to the width W 1 of the first optical film 2. (W A ≧W 1 )
- first optical film 2, the position in the width direction is within the existence range W A of the adhesive layer 5.
- the width W 2 of the protective film 3 is greater than the width W A of the adhesive layer 5. (W 2 >W A )
· Protective film 3 is positioned so as to include the presence width W A of the adhesive layer 5.
The width W R1 of the bonding roll 7 a on the first optical film 2 side is smaller than the width W 1 of the first optical film 2. (W 1 >W R1 )
The position in the width direction of the bonding roll 7 a on the first optical film 2 side is within the existing width W 1 of the first optical film 2.

ここで、第1の光学フィルム2側の貼合ロール7aの幅WR1は、第1の光学フィルム2の幅Wよりも1〜200mm小さいことが好ましく、1〜100mm小さいことがより好ましい。 Here, the width W R1 of the bonding roll 7 a on the first optical film 2 side is preferably 1 to 200 mm smaller than the width W 1 of the first optical film 2, and more preferably 1 to 100 mm smaller.

また、第2の実施形態の製造方法は、必須の要件ではないが、以下の関係も満たしている。
・保護フィルム3側の貼合ロール7bの幅WR2は、接着剤層5の幅Wよりも大きい。(WR2>W
・保護フィルム3側の貼合ロール7bは、幅方向の位置が接着剤層5の存在幅Wを内包するように位置している。
・保護フィルム3側の貼合ロール7bの幅WR2は、保護フィルム3の幅Wよりも大きい。(WR2>W
・保護フィルム3側の貼合ロール7bは、幅方向の位置が保護フィルム3の存在幅Wを内包するように位置している。
The manufacturing method of the second embodiment also satisfies the following relationship, although it is not an essential requirement.
The width W R2 of the bonding roll 7 b on the protective film 3 side is larger than the width W A of the adhesive layer 5. (W R2> W A)
- lamination rolls 7b of the protective film 3 side, the position in the width direction are positioned so as to include the presence width W A of the adhesive layer 5.
The width W R2 of the bonding roll 7b on the protective film 3 side is larger than the width W 2 of the protective film 3. (W R2> W 2)
- lamination rolls 7b of the protective film 3 side is positioned such that the positions in the width direction containing the present width W 2 of the protective film 3.

この製造方法によれば、接着剤層5が第1の光学フィルム2の存在幅からはみ出しているが、第1の光学フィルム2側の貼合ロール7aの幅WR1が、第1の光学フィルム2の幅Wよりも小さく、且つ、第1の光学フィルム2側の貼合ロール7aが、幅方向の位置が第1の光学フィルム2の存在幅W内にあるので、当該貼合ロール7aが接着剤によって汚れることが防止される。 According to this manufacturing method, the adhesive layer 5 protrudes from the existing width of the first optical film 2, but the width W R1 of the bonding roll 7a on the first optical film 2 side is the first optical film. The width of the bonding roll 7a on the side of the first optical film 2 is smaller than the width W 1 of the second optical film 2, and the position in the width direction is within the existing width W 1 of the first optical film 2. 7a is prevented from being soiled by the adhesive.

なお、この第2の実施形態では保護フィルム3側の貼合ロール7bの幅WR2が保護フィルム3の幅Wよりも大きい態様を示したが、貼合ロール7bの幅WR2を保護フィルム3の幅Wより小さくしてもよいことは、第1の実施形態の場合と同様である。 Incidentally, the width W R2 of the second in the embodiment the protective film 3 side of the lamination rolls 7b showed greater aspect than the width W 2 of the protective film 3 protects the width W R2 of lamination rolls 7b Film It may be smaller than the width W 2 of 3 as in the case of the first embodiment.

<第3の実施形態>
以下、本発明の第3の実施形態について説明する。第2の実施形態との相違点について主に説明する。
<Third Embodiment>
The third embodiment of the present invention will be described below. Differences from the second embodiment will be mainly described.

(積層光学フィルム)
図7に示されているとおり、第3の実施形態の積層光学フィルムの製造方法により製造される積層光学フィルム1Cは、第1の光学フィルム2の幅が接着剤層5の幅よりも大きい。
(Laminated optical film)
As shown in FIG. 7, in the laminated optical film 1C manufactured by the method for manufacturing a laminated optical film of the third embodiment, the width of the first optical film 2 is larger than the width of the adhesive layer 5.

この他、第1の光学フィルム2、保護フィルム3及び接着剤層5の互いの幅の大小関係や位置関係については後述するとおりであり、これらの層は、各幅方向の中心軸が略揃っている。すなわち、図7に示されている断面図において積層態様が略左右対称をなしている。 In addition, the size relationship and the positional relationship of the widths of the first optical film 2, the protective film 3, and the adhesive layer 5 are as described later, and these layers have substantially the same central axis in each width direction. ing. That is, in the cross-sectional view shown in FIG. 7, the stacking manner is substantially symmetrical.

(積層光学フィルムの製造方法)
積層光学フィルム1Cの製造方法としては、図5及び図8に示されているとおり、回転する一対の貼合ロール7a,7bの間に、第1の光学フィルム2と、接着剤層5と、保護フィルム3とを、一対の貼合ロール7a,7b間を結ぶ方向にこの順に配列した状態で導入して、第1の光学フィルム2と保護フィルム3とを貼合する。
(Method for manufacturing laminated optical film)
As a manufacturing method of the laminated optical film 1C, as shown in FIGS. 5 and 8, the first optical film 2 and the adhesive layer 5 are provided between the pair of rotating bonding rolls 7a and 7b. The protective film 3 is introduced in the state of being arranged in this order in the direction connecting the pair of bonding rolls 7a and 7b, and the first optical film 2 and the protective film 3 are bonded together.

第1の光学フィルム2及び保護フィルム3は積層されて積層体4Cとなり、積層体4Cはその後、接着剤層5が硬化することで、図7に示された積層光学フィルム1Cとして完成する。 The 1st optical film 2 and the protective film 3 are laminated|stacked, and it becomes the laminated body 4C, and the laminated body 4C is completed after that as the adhesive layer 5 hardens|cures.

貼合時の各部材の存在態様について説明する。図8に示されているとおり、一対の貼合ロール7a,7b間における各フィルムや接着剤層5の幅は、以下の関係を満たしている。なお、図8では図面を見やすくするために貼合ロール7a,7bを積層体4Cから離して描いている。
・接着剤層5の幅Wは、第1の光学フィルム2の幅W未満である。(W>W
・接着剤層5は、幅方向の位置が第1の光学フィルム2の存在幅W内にある。
・保護フィルム3の幅Wは、接着剤層5の幅Wよりも大きい。(W>W
・保護フィルム3は、接着剤層5の存在幅Wを内包するように位置している。
The mode of existence of each member at the time of bonding will be described. As shown in FIG. 8, the widths of the films and the adhesive layer 5 between the pair of bonding rolls 7a and 7b satisfy the following relationship. In addition, in FIG. 8, the bonding rolls 7a and 7b are drawn away from the laminated body 4C in order to make the drawing easy to see.
The width W A of the adhesive layer 5 is less than the width W 1 of the first optical film 2. (W 1> W A)
The position of the adhesive layer 5 in the width direction is within the existing width W 1 of the first optical film 2.
- the width W 2 of the protective film 3 is greater than the width W A of the adhesive layer 5. (W 2 >W A )
· Protective film 3 is positioned so as to include the presence width W A of the adhesive layer 5.

ここで、接着剤層5の幅Wは、第1の光学フィルム2の幅Wよりも0.1〜50mm小さいことが好ましく、0.1〜20mm小さいことがより好ましく、0.1〜5mm小さいことが更に好ましい。この場合、第1の光学フィルム2と保護フィルム3とを幅方向の端部まで十分に接着させることができる。 Here, the width W A of the adhesive layer 5 is preferably 0.1 to 50 mm smaller than the width W 1 of the first optical film 2, more preferably 0.1 to 20 mm smaller, and 0.1 to 10 mm smaller. More preferably, it is 5 mm smaller. In this case, the first optical film 2 and the protective film 3 can be sufficiently adhered to the ends in the width direction.

なお、第1の光学フィルム2の幅Wと保護フィルム3の幅Wとの大小関係は任意であるが、ここでは同一としている。(W=WAlthough the magnitude relation between the width W 2 of the first width W 1 of the optical film 2 and the protective film 3 is arbitrary, it is taken here to be the same. (W 1 =W 2 )

また、第3の実施形態の製造方法は、必須の要件ではないが、以下の関係も満たしている。
・両貼合ロール7a,7bの幅WR1,WR2は、それぞれ第1の光学フィルム2の幅W及び保護フィルム3の幅Wよりも大きい。(WR1>W、且つ、WR2>W
・両貼合ロール7a,7bは、幅方向の位置が、それぞれ第1の光学フィルム2の存在幅W及び第2の光学フィルム3の存在幅Wを内包するように位置している。
The manufacturing method of the third embodiment also satisfies the following relationship, although it is not an essential requirement.
- Both the lamination rolls 7a, the width W of 7b R1, W R2 is greater than the width W 2 of the first width W 1 and the protective film 3 of the optical film 2, respectively. (W R1 >W 1 and W R2 >W 2 )
- Both the lamination rolls 7a, 7b, the position in the width direction is positioned so as to include the presence width W 2 of the first present width W 1 and the second optical film 3 of the optical film 2, respectively.

両貼合ロール7a,7bの幅の大小関係は任意であるが、ここでは同一としている。(WR1=WR2The size relationship between the widths of the two bonding rolls 7a and 7b is arbitrary, but they are the same here. (W R1 =W R2 )

この製造方法によれば、接着剤層5が第1の光学フィルム2及び保護フィルム3の存在幅をはみ出す可能性が極めて小さいので、接着剤による貼合ロール7a,7bの汚れを防止することができる。 According to this manufacturing method, since the adhesive layer 5 is extremely unlikely to extend beyond the existing width of the first optical film 2 and the protective film 3, it is possible to prevent the bonding rolls 7a and 7b from being soiled by the adhesive. it can.

なお、この第3の実施形態では貼合ロール7a,7bの幅WR1,WR2がそれぞれ第1の光学フィルム2の幅W及び保護フィルム3の幅Wよりも大きい態様を示したが、貼合ロール7a,7bの幅は、第1の光学フィルム2の幅W及び保護フィルム3の幅Wより小さくてもよく、接着剤層5の幅Wよりも小さくてもよい。この場合、貼合ロール7a,7bは、それぞれ第1の光学フィルム2の存在幅W内、保護フィルム3の存在幅W内に位置するようにする。これによれば、貼合ロール7a,7bが接着剤によって汚れることが一層防止される。 Incidentally, the third lamination rolls 7a in the embodiment, although 7b width W R1, W R2 of showed greater aspect than the width W 2 of the first width W 1 and the protective film 3 of the optical film 2, respectively , lamination rolls 7a, the width of 7b may be smaller than the width W 2 of the first width W 1 and the protective film 3 of the optical film 2 may be smaller than the width W a of the adhesive layer 5. In this case, the lamination rolls 7a, 7b, the first inner presence width W 1 of the optical film 2, respectively, to be located within the existing width W 2 of the protective film 3. According to this, the bonding rolls 7a and 7b are further prevented from being soiled by the adhesive.

また、この第3の実施形態では、第1の実施形態と同様に接着剤層5を保護フィルム3に塗工することで設けているが、接着剤層5は、偏光子22側に塗工して設けてもよい。 In addition, in the third embodiment, the adhesive layer 5 is provided by coating the protective film 3 as in the first embodiment. However, the adhesive layer 5 is coated on the polarizer 22 side. You may provide it.

(第1〜第3の実施形態の変形例)
上記第1〜第3の実施形態は、以下の態様として実施することもできる。すなわち、第1の光学フィルム2が偏光板(例えば、図1に示された偏光板10の構成を備える偏光板。)であり、第2の光学フィルム3がセパレータであり、これらを接着剤に代えて粘着剤で貼合する態様としてもよい。この場合、積層光学フィルムとして、セパレータ付き偏光板が製造される。以下、この態様について説明する。
(Modifications of the first to third embodiments)
The above first to third embodiments can also be implemented as the following aspects. That is, the first optical film 2 is a polarizing plate (for example, a polarizing plate having the configuration of the polarizing plate 10 shown in FIG. 1), the second optical film 3 is a separator, and these are used as an adhesive. Instead, an adhesive may be used for bonding. In this case, a polarizing plate with a separator is manufactured as a laminated optical film. Hereinafter, this aspect will be described.

粘着剤層は、偏光板を他の物品(例えば液晶セル)に貼着させるときに機能する層である。粘着剤層は、アクリル系樹脂や、シリコーン系樹脂、ポリエステル、ポリウレタン、ポリエーテル等で構成することができる。 The adhesive layer is a layer that functions when the polarizing plate is attached to another article (for example, a liquid crystal cell). The pressure-sensitive adhesive layer can be made of acrylic resin, silicone resin, polyester, polyurethane, polyether or the like.

粘着剤層の厚さは、2〜500μmであることが好ましく、2〜200μmであることがより好ましく、2〜50μmであることが更に好ましい。 The thickness of the pressure-sensitive adhesive layer is preferably 2 to 500 μm, more preferably 2 to 200 μm, and further preferably 2 to 50 μm.

粘着剤層を偏光板に積層する方法としては、例えば、偏光板に上記樹脂や任意の添加成分を含む溶液を塗布する方法でもよく、セパレータ上に当該溶液で粘着剤層を形成した後に偏光板に積層する方法でもよい。 As a method of laminating the pressure-sensitive adhesive layer on the polarizing plate, for example, a method of applying a solution containing the above-mentioned resin or any additional component to the polarizing plate may be used, and the polarizing plate may be formed after the pressure-sensitive adhesive layer is formed on the separator with the solution. It may be a method of laminating on.

セパレータは、粘着剤層の保護や異物の付着防止等を目的として貼着される剥離可能なフィルムであって、偏光板の使用時に剥がされて粘着剤層が露出される。セパレータは、例えばポリエチレンのようなポリエチレン系樹脂、ポリプロピレンのようなポリプロピレン系樹脂、ポリエチレンテレフタレートのようなポリエステル系樹脂等で構成することができる。中でも、ポリエチレンテレフタレートの延伸フィルムが好ましい。 The separator is a peelable film that is attached for the purpose of protecting the pressure-sensitive adhesive layer, preventing adhesion of foreign matter, and the like, and is peeled off when the polarizing plate is used to expose the pressure-sensitive adhesive layer. The separator can be made of, for example, a polyethylene resin such as polyethylene, a polypropylene resin such as polypropylene, a polyester resin such as polyethylene terephthalate, or the like. Among them, a stretched film of polyethylene terephthalate is preferable.

セパレータは、偏光板の使用時に容易に剥がすことができるように、粘着剤層に接する面にシリコーン樹脂等による離型処理を施してもよい。 The separator may be subjected to a release treatment with a silicone resin or the like on the surface in contact with the pressure-sensitive adhesive layer so that it can be easily peeled off when the polarizing plate is used.

セパレータの厚さは、10〜500μmであることが好ましく、10〜300μmであることがより好ましく、10〜200μmであることが更に好ましい。 The thickness of the separator is preferably 10 to 500 μm, more preferably 10 to 300 μm, and further preferably 10 to 200 μm.

上記態様であっても、上記実施形態と同様の作用によって、粘着剤による貼合ロール7a,7bの汚れを防止することができる。 Even in the above-described aspect, it is possible to prevent the bonding rolls 7a and 7b from being soiled with the adhesive by the same operation as that in the above-described embodiment.

第1の光学フィルム2として偏光板を用いる場合は、偏光子の片面又は両面に接着剤を介して保護フィルムを積層させたものが通常用いられる。偏光子の片面にのみ保護フィルムを積層させた偏光板の場合、保護フィルムを積層させた側とは反対側の面を接着剤層側となるように積層させればよい。偏光板は、保護フィルム上に積層される他の光学層や保護フィルム表面を保護する保護層を更に含んでいてもよい。他の光学層としては、ある種の偏光を透過し、それと逆の性質を示す偏光を反射する反射型偏光フィルム;表面に凹凸形状を有する防眩機能付フィルム;表面反射防止機能付フィルム;表面に反射機能を有する反射フィルム;反射機能と透過機能とを併せ持つ半透過反射フィルム;視野角補償フィルム等が挙げられる。保護フィルム表面を保護する保護層としては、一般的な透明樹脂フィルム用いることができる。例えば、トリアセチルセルロースを代表例とするセルロース系樹脂、ポリプロピレン系樹脂を代表例とするポリオレフィン系樹脂、ノルボルネン系樹脂を代表例とする環状オレフィン系樹脂、ポリメチルメタクリレート系樹脂を代表例とするアクリル系樹脂、ポリエチレンテレフタレート系樹脂を代表例とするポリエステル系樹脂等が挙げられる。保護フィルム表面を保護する保護層は、光学機能を有しないフィルムであってもよいし、位相差フィルムや輝度向上フィルムといった光学機能を併せもつフィルムであってもよい。 When a polarizing plate is used as the first optical film 2, a polarizing plate having a protective film laminated on one side or both sides of the polarizer via an adhesive is usually used. In the case of a polarizing plate in which a protective film is laminated only on one surface of a polarizer, it may be laminated so that the surface on the side opposite to the side on which the protective film is laminated is the adhesive layer side. The polarizing plate may further include another optical layer laminated on the protective film or a protective layer for protecting the surface of the protective film. As the other optical layer, a reflective polarizing film that transmits a certain polarized light and reflects a polarized light having the opposite property; a film having an uneven surface with an antiglare function; a film with a surface antireflection function; a surface A reflective film having a reflective function; a semi-transmissive reflective film having both a reflective function and a transmissive function; and a viewing angle compensation film. A general transparent resin film can be used as the protective layer for protecting the surface of the protective film. For example, a cellulose resin typified by triacetyl cellulose, a polyolefin resin typified by a polypropylene resin, a cyclic olefin resin typified by a norbornene resin, and an acrylic resin typified by a polymethylmethacrylate resin. Examples thereof include polyester resins and polyester resins represented by polyethylene terephthalate resins. The protective layer that protects the surface of the protective film may be a film having no optical function, or may be a film having an optical function such as a retardation film or a brightness enhancement film.

<第4の実施形態>
以下、本発明の第4の実施形態について説明する。第2の実施形態との相違点について主に説明する。
<Fourth Embodiment>
The fourth embodiment of the present invention will be described below. Differences from the second embodiment will be mainly described.

(積層光学フィルム)
図9に示されているとおり、第4の実施形態の積層光学フィルムの製造方法により製造される積層光学フィルム1Dは、第1の光学フィルム2において樹脂基材21と偏光子22との幅が揃っておらず、樹脂基材21の幅が偏光子22の幅よりも大きい。
(Laminated optical film)
As shown in FIG. 9, in the laminated optical film 1D manufactured by the method for manufacturing a laminated optical film of the fourth embodiment, in the first optical film 2, the width of the resin base material 21 and the polarizer 22 is They are not aligned, and the width of the resin base material 21 is larger than the width of the polarizer 22.

この他、樹脂基材21、偏光子22、保護フィルム3及び接着剤層5の互いの幅の大小関係や位置関係については後述するとおりであり、これらの層は、各幅方向の中心軸が略揃っている。すなわち、図9に示されている断面図において積層態様が略左右対称をなしている。 In addition, the magnitude relationship and the positional relationship of the widths of the resin base material 21, the polarizer 22, the protective film 3, and the adhesive layer 5 are as described later, and these layers have a central axis in each width direction. It is almost complete. That is, in the cross-sectional view shown in FIG. 9, the stacking manner is substantially symmetrical.

(積層光学フィルムの製造方法)
積層光学フィルム1Dの製造方法としては、図5及び図10に示されているとおり、回転する一対の貼合ロール7a,7bの間に、樹脂基材21と、偏光子22と、接着剤層5と、保護フィルム3とを、一対の貼合ロール7a,7b間を結ぶ方向にこの順に配列した状態で導入して、偏光子22と保護フィルム3とを貼合する。
(Method for manufacturing laminated optical film)
As a method for manufacturing the laminated optical film 1D, as shown in FIGS. 5 and 10, the resin base material 21, the polarizer 22, and the adhesive layer are provided between the pair of rotating bonding rolls 7a and 7b. 5 and the protective film 3 are introduced in a state of being arranged in this order in the direction connecting the pair of bonding rolls 7a and 7b, and the polarizer 22 and the protective film 3 are bonded together.

ここで、第1の光学フィルム2における偏光子22は、樹脂基材21の幅方向中央部のみ塗工し、両端部は未塗工とした上で乾燥し、樹脂基材21ごと延伸処理後、ヨウ素又は二色性染料による染色及びホウ酸処理を施し、水洗、乾燥することで供給する。 Here, the polarizer 22 in the first optical film 2 is coated only on the central portion in the width direction of the resin base material 21, is uncoated on both end portions, and is dried, and is stretched together with the resin base material 21. , Dyed with iodine or dichroic dye, treated with boric acid, washed with water and dried.

樹脂基材21、偏光子22及び保護フィルム3は積層されて積層体4Dとなり、積層体4Dはその後、接着剤層5が硬化することで、図9に示された積層光学フィルム1Dとして完成する。 The resin substrate 21, the polarizer 22, and the protective film 3 are laminated to form a laminated body 4D, and the laminated body 4D is then cured by curing the adhesive layer 5 to complete the laminated optical film 1D shown in FIG. ..

貼合時の各部材の存在態様について説明する。図10に示されているとおり、一対の貼合ロール7a,7b間における各フィルムや接着剤層5の幅は、以下の関係を満たしている。なお、図10では図面を見やすくするために貼合ロール7a,7bを積層体4Dから離して描いている。
・偏光子22の幅W12は、樹脂基材21の幅W11よりも小さい。(W11>W12
・接着剤層5の幅Wは、偏光子22の幅W12以上であり、且つ、樹脂基材21の幅W11よりも小さい。(W11>W≧W12
・樹脂基材21は、偏光子22の存在幅W12及び接着剤層5の存在幅Wを内包するように位置している。
・保護フィルム3の幅Wは、接着剤層5の幅Wよりも大きい。(W>W
・保護フィルム3は、接着剤層5の存在幅Wを内包するように位置している。
The mode of existence of each member at the time of bonding will be described. As shown in FIG. 10, the width of each film and the adhesive layer 5 between the pair of bonding rolls 7a and 7b satisfy the following relationship. In addition, in FIG. 10, the bonding rolls 7a and 7b are drawn away from the laminated body 4D in order to make the drawing easy to see.
The width W 12 of the polarizer 22 is smaller than the width W 11 of the resin base material 21. (W 11 >W 12 )
The width W A of the adhesive layer 5 is equal to or larger than the width W 12 of the polarizer 22 and smaller than the width W 11 of the resin base material 21. (W 11 >W A ≧W 12 )
Resin substrate 21 is positioned so as to include the presence width W A of the present width W 12 and the adhesive layer 5 of the polarizer 22.
- the width W 2 of the protective film 3 is greater than the width W A of the adhesive layer 5. (W 2 >W A )
· Protective film 3 is positioned so as to include the presence width W A of the adhesive layer 5.

なお、樹脂基材21の幅W12と保護フィルム3の幅Wとの大小関係は任意である。 The size relationship between the width W 12 of the resin base material 21 and the width W 2 of the protective film 3 is arbitrary.

また、第4の実施形態の製造方法は、必須の要件ではないが、以下の関係も満たしている。
・樹脂基材21側の貼合ロール7aの幅WR1は、樹脂基材21の幅W11よりも小さい。(W11>WR1
・樹脂基材21側の貼合ロール7aは、幅方向の位置が樹脂基材21の存在幅内にある。
・保護フィルム3側の貼合ロール7bの幅WR2は、保護フィルム3の幅Wよりも大きい。(WR2>W
・保護フィルム3側の貼合ロール7bは、幅方向の位置が保護フィルム3の存在幅Wを内包するように位置している。
The manufacturing method of the fourth embodiment also satisfies the following relationship, although it is not an essential requirement.
The width W R1 of the bonding roll 7 a on the resin base material 21 side is smaller than the width W 11 of the resin base material 21. (W 11 >W R1 )
The position in the width direction of the bonding roll 7a on the resin base material 21 side is within the existing width of the resin base material 21.
The width W R2 of the bonding roll 7b on the protective film 3 side is larger than the width W 2 of the protective film 3. (W R2> W 2)
- lamination rolls 7b of the protective film 3 side is positioned such that the positions in the width direction containing the present width W 2 of the protective film 3.

ここで、樹脂基材21側の貼合ロール7aの幅WR1は、接着剤層5の幅Wよりも小さいことが好ましく、偏光子22の幅W12よりも小さいことがより好ましい。また、貼合ロール7aの幅WR1は、樹脂基材21の幅W11よりも1〜100mm小さいことが好ましく、1〜50mm小さいことがより好ましい。 Here, the width W R1 of the bonding roll 7 a on the resin base material 21 side is preferably smaller than the width W A of the adhesive layer 5, and more preferably smaller than the width W 12 of the polarizer 22. The width W R1 of the bonding roll 7a is preferably 1 to 100 mm smaller than the width W 11 of the resin base material 21, and more preferably 1 to 50 mm smaller.

この製造方法によれば、偏光子22と保護フィルム3との貼合時において、接着剤層5と貼合ロール7a,7bとの間に、接着剤層5よりも幅広の樹脂基材21又は保護フィルム3が介在しているので、接着剤による貼合ロール7a,7bの汚れを防止することができる。 According to this manufacturing method, at the time of bonding the polarizer 22 and the protective film 3, the resin base material 21 wider than the adhesive layer 5 or between the adhesive layer 5 and the bonding rolls 7a and 7b. Since the protective film 3 is interposed, it is possible to prevent the bonding rolls 7a and 7b from being soiled by the adhesive.

また、この製造方法において、樹脂基材21側の貼合ロール7aの幅WR1は、樹脂基材21の幅よりも小さく、且つ、樹脂基材21側の貼合ロール7aは、幅方向の位置が樹脂基材21の存在幅W11内にあるので、貼合ロール7aが接着剤によって汚れることが一層防止される。 Further, in this manufacturing method, the width W R1 of the bonding roll 7a on the resin base material 21 side is smaller than the width of the resin base material 21, and the bonding roll 7a on the resin base material 21 side extends in the width direction. Since the position is within the existing width W 11 of the resin base material 21, the bonding roll 7a is further prevented from being soiled by the adhesive.

上記第4の実施形態においては、第1の光学フィルム2が、偏光板であってもよい。偏光板としては、偏光子の片面又は両面に接着剤を介して保護フィルムを積層させたものであってもよい。そして、偏光子は、保護フィルムの幅よりも小さく、且つ保護フィルムの存在幅内に存在していればよい。偏光子の片面にのみ保護フィルムを積層させた偏光板の場合、保護フィルムを積層させた側とは反対側の面を接着剤層側となるように積層させればよい。偏光板は、保護フィルム上に積層される他の光学層や保護フィルム表面を保護する保護層を更に含んでいてもよい。他の光学層としては、ある種の偏光を透過し、それと逆の性質を示す偏光を反射する反射型偏光フィルム;表面に凹凸形状を有する防眩機能付フィルム;表面反射防止機能付フィルム;表面に反射機能を有する反射フィルム;反射機能と透過機能とを併せ持つ半透過反射フィルム;視野角補償フィルム等が挙げられる。保護フィルム表面を保護する保護層としては、一般的な透明樹脂フィルム用いることができる。例えば、トリアセチルセルロースを代表例とするセルロース系樹脂、ポリプロピレン系樹脂を代表例とするポリオレフィン系樹脂、ノルボルネン系樹脂を代表例とする環状オレフィン系樹脂、ポリメチルメタクリレート系樹脂を代表例とするアクリル系樹脂、ポリエチレンテレフタレート系樹脂を代表例とするポリエステル系樹脂等が挙げられる。保護フィルム表面を保護する保護層は、光学機能を有しないフィルムであってもよいし、位相差フィルムや輝度向上フィルムといった光学機能を併せもつフィルムであってもよい。 In the fourth embodiment, the first optical film 2 may be a polarizing plate. The polarizing plate may be one in which a protective film is laminated on one side or both sides of a polarizer via an adhesive. Then, the polarizer may be smaller than the width of the protective film and may exist within the existing width of the protective film. In the case of a polarizing plate in which a protective film is laminated only on one surface of a polarizer, it may be laminated so that the surface on the side opposite to the side on which the protective film is laminated is the adhesive layer side. The polarizing plate may further include another optical layer laminated on the protective film or a protective layer for protecting the surface of the protective film. As the other optical layer, a reflective polarizing film that transmits a certain polarized light and reflects a polarized light having the opposite property; a film having an uneven surface with an antiglare function; a film with a surface antireflection function; a surface A reflective film having a reflective function; a semi-transmissive reflective film having both a reflective function and a transmissive function; and a viewing angle compensation film. A general transparent resin film can be used as the protective layer for protecting the surface of the protective film. For example, a cellulose resin typified by triacetyl cellulose, a polyolefin resin typified by a polypropylene resin, a cyclic olefin resin typified by a norbornene resin, and an acrylic resin typified by a polymethylmethacrylate resin. Examples thereof include polyester resins and polyester resins represented by polyethylene terephthalate resins. The protective layer that protects the surface of the protective film may be a film having no optical function, or may be a film having an optical function such as a retardation film or a brightness enhancement film.

以上、本発明の好適な実施形態について説明したが、本発明は上記実施形態に何ら限定されるものではない。 The preferred embodiment of the present invention has been described above, but the present invention is not limited to the above embodiment.

例えば、上記各実施形態では偏光子22が樹脂基材21の片面に塗工された態様を示したが、偏光子22は樹脂基材21の両面に塗工されていてもよい。この場合、積層光学フィルム1A〜1Dを製造した後、接着剤層5に面している偏光子22と樹脂基材21との間を剥がすことによって、樹脂基材21側に残っている偏光子を別の偏光板の製造のために利用することができる。 For example, in each of the above-described embodiments, the mode in which the polarizer 22 is applied to one surface of the resin base material 21 is shown, but the polarizer 22 may be applied to both surfaces of the resin base material 21. In this case, after manufacturing the laminated optical films 1A to 1D, the polarizer 22 facing the adhesive layer 5 and the resin base material 21 are peeled off from each other, whereby the polarizer remaining on the resin base material 21 side. Can be used for manufacturing another polarizing plate.

また、上記各実施形態では、樹脂基材21の片面に偏光子22が設けられた第1の光学フィルムの例を用いて説明したが、樹脂基材21の片面又は両面に偏光子22とは別の光学機能層を設けてもよい。偏光子22以外の光学機能層としては、位相差層、視野角補償層等が挙げられ、樹脂基材21上に、目的の光学機能を有する材料を溶解又は分散させた液を塗付、乾燥することにより当該層を設けることができる。 Moreover, in each of the above-described embodiments, the example of the first optical film in which the polarizer 22 is provided on one surface of the resin base material 21 is described, but the polarizer 22 is provided on one surface or both surfaces of the resin base material 21. Another optical functional layer may be provided. Examples of the optical functional layer other than the polarizer 22 include a retardation layer, a viewing angle compensation layer, and the like, and a liquid in which a material having an intended optical function is dissolved or dispersed is applied onto the resin base material 21 and dried. By doing so, the layer can be provided.

1A〜1D…積層光学フィルム、2…第1の光学フィルム、3…保護フィルム(第2の光学フィルム)、4A〜4D…積層体、5…接着剤層、6…仮保護フィルム(第3の光学フィルム)、7a…第1の光学フィルム側の貼合ロール、7b…保護フィルム側の貼合ロール、10…偏光板、21…樹脂基材、22…偏光子、W…第1の光学フィルムの幅、W11…樹脂基材の幅、W12…偏光子の幅、W…保護フィルムの幅、W…仮保護フィルムの幅、W…接着剤層の幅、WR1…第1の光学フィルム側の貼合ロールの幅、WR2…保護フィルム側の貼合ロールの幅。 1A to 1D... laminated optical film, 2... first optical film, 3... protective film (second optical film), 4A-4D... laminated body, 5... adhesive layer, 6... temporary protective film (third protective film) Optical film), 7a... Bonding roll on the first optical film side, 7b... Bonding roll on the protective film side, 10... Polarizing plate, 21... Resin base material, 22... Polarizer, W 1 ... First optics Width of film, W 11 ... Width of resin substrate, W 12 ... Width of polarizer, W 2 ... Width of protective film, W 3 ... Width of temporary protective film, W A ... Width of adhesive layer, W R1 ... Width of the bonding roll on the side of the first optical film, W R2 ... Width of the bonding roll on the side of the protective film.

Claims (4)

回転する一対の貼合ロールの間に、樹脂基材と、前記樹脂基材の片面又は両面に設けられた光学機能層と、接着剤層又は粘着剤層と、光学フィルムとを、前記一対の貼合ロール間を結ぶ方向にこの順に配列した状態で導入して前記光学機能層と前記光学フィルムとを貼合する、積層光学フィルムの製造方法であって、
貼合時において、
前記光学機能層の幅は、前記樹脂基材の幅よりも小さく、
前記接着剤層又は前記粘着剤層の幅は、前記光学機能層の幅以上であり、且つ、前記樹脂基材の幅よりも小さく、
前記樹脂基材は、前記光学機能層及び前記接着剤層又は前記粘着剤層の存在幅を内包するように位置しており、
前記光学フィルムの幅は、前記接着剤層又は前記粘着剤層の幅よりも大きく、
前記光学フィルムは、前記接着剤層又は前記粘着剤層の存在幅を内包するように位置しており、
前記樹脂基材側の前記貼合ロールの幅は、前記樹脂基材の幅よりも小さく、且つ、前記光学機能層の幅よりも大きく、
前記樹脂基材側の前記貼合ロールは、幅方向の位置が前記樹脂基材の存在幅内にある、積層光学フィルムの製造方法。
Between the pair of rotating bonding rolls, a resin substrate, an optical functional layer provided on one or both sides of the resin substrate, an adhesive layer or a pressure-sensitive adhesive layer, and an optical film, the pair of A method for producing a laminated optical film, which comprises introducing the optical functional layer and the optical film introduced in a state of being arranged in this order in a direction connecting the bonding rolls,
When pasting,
The width of the optical functional layer is smaller than the width of the resin substrate,
The width of the adhesive layer or the pressure-sensitive adhesive layer is not less than the width of the optical functional layer, and smaller than the width of the resin substrate,
The resin substrate is positioned so as to include the existing width of the optical functional layer and the adhesive layer or the pressure-sensitive adhesive layer,
The width of the optical film is larger than the width of the adhesive layer or the pressure-sensitive adhesive layer,
The optical film is positioned so as to include the existing width of the adhesive layer or the pressure-sensitive adhesive layer,
The width of the bonding roll on the resin substrate side is smaller than the width of the resin substrate, and larger than the width of the optical functional layer,
The method for producing a laminated optical film, wherein the laminating roll on the resin substrate side has a position in the width direction within the existing width of the resin substrate.
前記光学フィルムは、保護フィルムである、請求項1記載の積層光学フィルムの製造方法。 The method for producing a laminated optical film according to claim 1, wherein the optical film is a protective film. 前記光学機能層は、偏光子である、請求項1又は2記載の積層光学フィルムの製造方法。 The method for producing a laminated optical film according to claim 1, wherein the optical functional layer is a polarizer. 前記偏光子は、前記樹脂基材に塗工されて設けられたものである、請求項3記載の積層光学フィルムの製造方法。 The method for producing a laminated optical film according to claim 3, wherein the polarizer is provided by being applied to the resin base material.
JP2017157172A 2016-02-25 2017-08-16 Method for manufacturing laminated optical film Active JP6749294B2 (en)