JP6542080B2 - Method for improving the amount of dissolved hydrogen in electrolytic hydrogen water - Google Patents
Method for improving the amount of dissolved hydrogen in electrolytic hydrogen water Download PDFInfo
- Publication number
- JP6542080B2 JP6542080B2 JP2015179862A JP2015179862A JP6542080B2 JP 6542080 B2 JP6542080 B2 JP 6542080B2 JP 2015179862 A JP2015179862 A JP 2015179862A JP 2015179862 A JP2015179862 A JP 2015179862A JP 6542080 B2 JP6542080 B2 JP 6542080B2
- Authority
- JP
- Japan
- Prior art keywords
- hydrogen
- water
- electrode
- amount
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、電解水素水の溶存水素量向上方法に関する。
また本発明は、溶存水素量が向上した電解水素水の製造方法、及び溶存水素量向上用電極に関する。
The present invention relates to a method of improving the amount of dissolved hydrogen in electrolytic hydrogen water.
The present invention also relates to a method for producing electrolytic hydrogen water in which the amount of dissolved hydrogen is improved, and an electrode for improving the amount of dissolved hydrogen.
水道水などを直流電気分解することにより陰極に電解水素水を、陽極に電解酸性水を生成する電解水生成装置が知られている（例えば特許文献１参照）。
電解水生成装置は、例えば、イオン交換膜により隔てられた陰極室と陽極室とを備えた電解槽を設けて、この電解槽で水を電気分解することにより、陰極室から電解水素水を、また陽極室から電解酸性水をそれぞれ得るように構成されている。
すなわち、陽極室および陰極室における陽極および陰極では、以下のような電気分解反応が行われる。
陽極： ２Ｈ２Ｏ → Ｏ２ ＋ ４Ｈ＋ ＋ ４ｅ−
陰極： ２Ｈ２Ｏ ＋ ２ｅ− → Ｈ２ ＋ ２ＯＨ−
There is known an electrolyzed water generating apparatus which produces electrolytic hydrogen water at a cathode and electrolyzed acidic water at an anode by direct current electrolysis of tap water or the like (see, for example, Patent Document 1).
The electrolyzed water generator comprises, for example, an electrolyzer comprising a cathode chamber and an anode chamber separated by an ion exchange membrane, and electrolyzed water from the cathode chamber by electrolyzing water in the electrolyzer, Moreover, it is comprised so that an electrolytic acid water may be obtained from an anode chamber, respectively.
That is, the following electrolysis reactions are performed in the anode and the cathode in the anode chamber and the cathode chamber.
Anode: 2H 2 O → O 2 + 4H + + 4e −
Cathode: 2H 2 O + 2e − → H 2 + 2OH −
ここで電解水素水は、薬学的、医学的または生物学的効果があるとされ（例えば特許文献２参照）、注目されている。該効果は、電解水素水中に含まれる溶存水素量を高めればさらに顕著になるものと推測される。
しかし、従来の電解水生成装置では、陰極室の陰極により生じた水素が水素ガスとして空気中に放出され易く、そのため電解水素水中に含まれる溶存水素量を十分に高めることができず、改善が望まれていた。
Here, the electrolytic hydrogen water is regarded as having a pharmacological, medical or biological effect (see, for example, Patent Document 2) and is attracting attention. It is assumed that the effect becomes more remarkable as the amount of dissolved hydrogen contained in the electrolytic hydrogen water is increased.
However, in the conventional electrolyzed water generating apparatus, hydrogen generated by the cathode of the cathode chamber is easily released into the air as hydrogen gas, and therefore the amount of dissolved hydrogen contained in the electrolyzed hydrogen water can not be sufficiently increased. It was desired.
したがって本発明の目的は、電解水素水中に含まれる溶存水素量を十分に向上させる方法を提供することにある。
また本発明の別の目的は、該方法により、溶存水素量が向上した電解水素水の製造方法を提供すること、さらに、電解水素水の溶存水素量を向上させるために用いる電極を提供することにある。
Therefore, an object of the present invention is to provide a method for sufficiently improving the amount of dissolved hydrogen contained in electrolytic hydrogen water.
Another object of the present invention is to provide a method of producing electrolytic hydrogen water having an improved amount of dissolved hydrogen by the method, and to provide an electrode used to improve the amount of dissolved hydrogen of the electrolytic hydrogen water. It is in.
本発明者らは鋭意研究を重ねた結果、Ｔｉを含有する基材の上にＰｔと、ＡｕおよびＷの少なくとも一方を含有する被膜を有する電極を使用して水の電気分解を行うことにより、上記課題を解決できることを見出し、本発明を完成するに至った。
すなわち本発明は以下の通りである。
As a result of intensive studies, the present inventors conducted electrolysis of water using an electrode having a film containing Pt and at least one of Au and W on a substrate containing Ti, It has been found that the above problems can be solved, and the present invention has been completed.
That is, the present invention is as follows.
１．Ｔｉを含有する基材の上に、Ｐｔと、ＡｕおよびＷの少なくとも一方を含有する被膜を有する電極を使用して水の電気分解を行い、電解水素水の溶存水素量を向上させる方法。
２．前記被膜が、Ｐｔ、Ａｕ及びＷを含有する被膜である、前記１に記載の方法。
３．前記被膜の膜厚が０．０５〜１μｍである前記１または２の記載の方法。
４．前記１〜３のいずれか１に記載の方法により、溶存水素量が向上した電解水素水の製造方法。
５．Ｔｉを含有する基材の上に、Ｐｔと、ＡｕおよびＷの少なくとも一方を含有する被膜を有する、溶存水素量向上用電極。
1. A method of electrolysis of water using an electrode having a film containing Pt and at least one of Au and W on a substrate containing Ti to improve the amount of dissolved hydrogen in electrolytic hydrogen water.
2. The method according to 1 above, wherein the film is a film containing Pt, Au and W.
3. The method according to the above 1 or 2, wherein the film thickness of the coating is 0.05 to 1 μm.
4. The manufacturing method of the electrolytic hydrogen water which dissolved hydrogen amount improved by the method any one of said 1-3.
5. An electrode for improving the amount of dissolved hydrogen, comprising a film containing Pt and at least one of Au and W on a substrate containing Ti.
本発明の方法に使用する電極は、Ｔｉを含有する基材の上に、Ｐｔと、ＡｕおよびＷの少なくとも一方を含有する被膜を有する電極であるため、該電極を使用して水の電気分解を行うことにより電解水素水の溶存水素量を向上させることができる。上記電極を用いることによって電解水素水中の溶存水素量を向上させることができる作用機序については明らかではないが、電極で発生した水素は、水素を脱離しやすい性質を有するＡｕによって、その気泡が大きくなる前に電極から脱離するため、水素ガスの電解水素水中での上昇速度を小さくすることができ、電解水素水中に水素が溶解しやすくなるからであると推測される。また、水素を吸着しやすい性質を有するＷによって、より高分散な吸着水素原子を電極表面に生成することができ、高分散な水素分子の生成により、気泡が大きくなりにくく、効率よく溶存水素が生成できるものと推測される。 Since the electrode used in the method of the present invention is an electrode having a film containing Pt and at least one of Au and W on a substrate containing Ti, electrolysis of water using the electrode is carried out The amount of dissolved hydrogen in the electrolyzed hydrogen water can be improved by Although the mechanism of action that can improve the amount of hydrogen dissolved in the electrolytic hydrogen water by using the above electrode is not clear, the hydrogen generated at the electrode has its bubbles formed by Au, which has the property of easily desorbing hydrogen. It is presumed that the rate of rise of hydrogen gas in electrolytic hydrogen water can be reduced because hydrogen is desorbed from the electrode before it becomes large, and hydrogen is easily dissolved in the electrolytic hydrogen water. Further, W having the property of easily adsorbing hydrogen can generate more dispersed adsorbed hydrogen atoms on the electrode surface, and the generation of highly dispersed hydrogen molecules makes it difficult for bubbles to become large, and dissolved hydrogen is efficiently removed. It is presumed that it can be generated.
また、本発明者らは、上記電極が含有する被膜が、Ｐｔ、Ａｕ及びＷを含有する被膜であることにより、さらに電解水素水の溶存水素量を向上させることができることを見出した。これは、電極が水素を脱離する性質を有するＡｕに加え、水素を吸着する性質を有するＷを有することにより、発生した水素の気泡が大きくなる前に電極から脱離させることが可能である一方で、電極で発生した水素が極めて小さいまま気泡として脱離することを抑制でき、電解水素水中に溶解するのに適度なサイズの水素ガスの気泡を発生させることができるため、電解水素水中に含まれる溶存水素量をさらに高めることができるからであると推測される。 Moreover, the present inventors discovered that the film which the said electrode contains is a film containing Pt, Au, and W, and can further improve the dissolved hydrogen amount of electrolytic hydrogen water. This is because, in addition to Au having the property of desorbing hydrogen, the electrode has W having the property of adsorbing hydrogen, so that generated hydrogen can be desorbed from the electrode before the bubbles become large. On the other hand, it is possible to suppress desorption as bubbles while the hydrogen generated at the electrode is extremely small, and to generate bubbles of hydrogen gas of an appropriate size to be dissolved in electrolytic hydrogen water. It is presumed that this is because the amount of dissolved hydrogen contained can be further increased.
本発明の方法に使用する電極は、前記被膜の膜厚が０．０５〜１μｍであることにより、電解水素水中に含まれる溶存水素量をさらに高めることができる。 The electrode used in the method of the present invention can further increase the amount of dissolved hydrogen contained in the electrolytic hydrogen water when the film thickness of the film is 0.05 to 1 μm.
また、本発明の方法により、溶存水素量が向上した電解水素水を製造することができる。 In addition, the method of the present invention can produce electrolytic hydrogen water having an improved amount of dissolved hydrogen.
以下、本発明の実施形態を、図面を参照しながらさらに詳細に説明する。 Hereinafter, embodiments of the present invention will be described in more detail with reference to the drawings.
本発明は、Ｔｉを含有する基材の上に、Ｐｔと、ＡｕおよびＷの少なくとも一方を含有する被膜を有する電極を使用して水の電気分解を行い、電解水素水の溶存水素量を向上させる方法である。
図１は、本発明の方法に使用する電極の一実施形態を説明するための断面図である。
図１において、電極１０は、Ｔｉを含有する基材１０２の上に、Ｐｔと、ＡｕおよびＷの少なくとも一方を含有する被膜１０４が形成されている。
The present invention electrolyzes water using an electrode having a film containing Pt and at least one of Au and W on a substrate containing Ti to improve the amount of dissolved hydrogen in electrolytic hydrogen water It is a way to
FIG. 1 is a cross-sectional view for explaining an embodiment of an electrode used in the method of the present invention.
In FIG. 1, in the electrode 10, a film 104 containing Pt, and at least one of Au and W is formed on a substrate 102 containing Ti.
基材１０２は、Ｔｉを含有する。このような基材１０２は公知のものから適宜選択すればよく、例えば、Ｔｉからなる基材、Ｔｉ合金（例えばＴｉ−Ａｌ、Ｖ、Ｍｏ、Ｐｄ、Ｍｎ、Ｓｎ、Ｆｅ合金からなる基材）等が挙げられる。
なお基材１０２は、被膜１０４を形成する前に、清浄化処理を行うことができる。清浄化処理は、例えば基材１０２表面を有機溶剤とアルカリで脱脂洗浄する方法が挙げられる。また基材１０２は、被膜１０４を形成する前に、化学エッチング処理やブラスト処理等の公知の粗面化処理を行うこともできる。
基材１０２のサイズは、本発明に使用する電極が用いられる電解水生成装置の規模に応じて適宜設定すればよい。
The substrate 102 contains Ti. Such a base 102 may be appropriately selected from known ones, for example, a base made of Ti, a Ti alloy (for example, a base made of Ti-Al, V, Mo, Pd, Mn, Sn, Fe alloy) Etc.
Note that the base material 102 can be subjected to a cleaning treatment before forming the film 104. Examples of the cleaning treatment include a method of degreasing and cleaning the surface of the substrate 102 with an organic solvent and an alkali. The base material 102 can also be subjected to known surface roughening treatment such as chemical etching treatment or blasting treatment before forming the film 104.
The size of the substrate 102 may be appropriately set according to the size of the electrolyzed water generating apparatus in which the electrode used in the present invention is used.
上記のように、基材１０２には被膜１０４が形成される。該被膜はめっきにより形成された被膜であることが好ましい。
該被膜１０４は、Ｐｔと、ＡｕおよびＷの少なくとも一方を含有する。Ｐｔは水の電気分解の際に水素を発生させる性質を担い、Ａｕは前記水素を脱離する性質を担い、Ｗは、前記水素を吸着する性質を担うと推測される。該被膜１０４が、Ｐｔと、ＡｕおよびＷの少なくとも一方を含有する場合、Ｐｔと、ＡｕおよびＷの少なくとも一方の比率は、前者：後者（ａｔ％）として、１：１〜１００：１が好ましく、１０：１〜１００：１がさらに好ましい。この形態の場合、めっき浴に用いられるＰｔ化合物としては、例えば、塩化白金、塩化白金酸、塩化白金酸塩、水酸化白金酸、水酸化白金酸塩、ジニトロジアンミン白金錯塩、ジニトロスルフィド白金錯塩、テトラアンミン白金錯塩、ヘキサアンミン白金錯塩等が挙げられる。Ａｕ化合物としては、例えば、シアン化金カリウム、亜硫酸金ナトリウム等が挙げられる。Ｗ化合物としては、例えば、タングステン酸、タングステン酸ナトリウム、タングステン酸カリウム、タングステン酸アンモニウム等が挙げられる。
As described above, the coating 102 is formed on the substrate 102. The film is preferably a film formed by plating.
The film 104 contains Pt and at least one of Au and W. Pt is responsible for generating hydrogen during electrolysis of water, Au is responsible for releasing the hydrogen, and W is assumed to be responsible for absorbing the hydrogen. When the film 104 contains Pt and at least one of Au and W, the ratio of Pt to at least one of Au and W is preferably 1: 1 to 100: 1 as the former: the latter (at%). 10: 1 to 100: 1 are more preferred. In the case of this form, as a Pt compound used in the plating bath, for example, platinum chloride, chloroplatinic acid, chloroplatinic acid salt, chloroplatinic acid, hydroxyplatinic acid salt, dinitrodiammine platinum complex salt, dinitro sulfide platinum complex salt, Examples thereof include tetraammine platinum complex salts and hexaammine platinum complex salts. Examples of the Au compound include potassium potassium cyanide, sodium gold sulfite and the like. Examples of the W compound include tungstic acid, sodium tungstate, potassium tungstate, ammonium tungstate and the like.
被膜１０４がＰｔと、ＡｕまたはＷを含有する態様としては、被膜１０４が、Ｐｔを含む層とＡｕまたはＷを含む層で別々の層とする合計２層から形成されるものであってもよいし、同一層内で、Ｐｔと、ＡｕまたはＷを含有するものであってもよい。また、被膜１０４がＰｔを含む層と、ＡｕまたはＷを含む層で別々の層として形成されたものである場合、Ｐｔと、ＡｕまたはＷの層の位置関係（上下関係）は特に制限されず、Ｐｔを含む層の上部に、ＡｕまたはＷを含む層が形成されていてもよいし、ＡｕまたはＷを含む層の上部に、Ｐｔを含む層が形成されていてもよい。また、被膜１０４が同一層内でＰｔと、ＡｕまたはＷを含有するものである場合、Ｐｔと、ＡｕまたはＷは、Ｐｔ−Ａｕ合金またはＰｔ−Ｗ合金として含有していてもよいし、それぞれ単独で含有していてもよい。被膜１０４がＰｔと、ＡｕまたはＷを含有する態様として、好ましくは同一層内でＰｔと、ＡｕまたはＷを含有する態様である。電極表面は主としてＰｔに、ＡｕまたはＷが低濃度で含有する状態が好ましく、より高効率での溶存水素の発生が可能であるからである。 In an embodiment in which the coating 104 contains Pt and Au or W, the coating 104 may be formed of a total of two layers of a layer containing Pt and a layer containing Au or W as separate layers. Or may contain Pt and Au or W in the same layer. Also, in the case where the coating 104 is formed as separate layers of a layer containing Pt and a layer containing Au or W, the positional relationship (upper or lower) between the Pt and Au or W layers is not particularly limited. A layer containing Au or W may be formed on the top of the layer containing Pt, or a layer containing Pt may be formed on the top of the layer containing Au or W. When the film 104 contains Pt and Au or W in the same layer, Pt and Au or W may be contained as a Pt-Au alloy or Pt-W alloy, respectively. You may contain independently. In an embodiment in which the coating 104 contains Pt and Au or W, preferably, the coating 104 contains Pt and Au or W in the same layer. It is preferable that the electrode surface mainly contains Pt in a low concentration of Au or W, and it is possible to generate dissolved hydrogen with higher efficiency.
また、前記被膜１０４は、Ｐｔ、Ａｕ及びＷを含有することが好ましい。被膜１０４がＰｔ、Ａｕ及びＷを含有する態様としては、被膜１０４が、Ｐｔ、Ａｕ及びＷをそれぞれ別々の層とする合計３層から形成されるものであってもよいし、同一層内でＰｔ、Ａｕ及びＷを含有するものであってもよいし、あるいはＰｔ、Ａｕ及びＷのうちいずれか２つを１つの同一層内に含み、残りの１つを別の層に含む合計２層から形成されるものであってもよい。前記被膜が上記のような合計２層または３層を形成するものである場合、それぞれの層の位置関係（上下関係）は特に制限されない。また、被膜１０４が同一層内でＰｔ、Ａｕ及びＷのいずれか２つまたは３つを含有するものである場合、Ｐｔ、Ａｕ及びＷは、いずれか２つまたは３つを合金として含有していてもよいし、それぞれ単独で含有していてもよい。 Preferably, the film 104 contains Pt, Au and W. In an embodiment in which the coating 104 contains Pt, Au and W, the coating 104 may be formed of a total of three layers in which Pt, Au and W are separate layers, or in the same layer. It may contain Pt, Au and W, or any two of Pt, Au and W in one and the same layer, and the remaining one in another layer. Or the like. When the coating film forms a total of two or three layers as described above, the positional relationship (upper or lower relationship) of each layer is not particularly limited. Also, when the film 104 contains any two or three of Pt, Au and W in the same layer, Pt, Au and W contain any two or three as an alloy. You may each contain independently.
被膜１０４の形成方法は、例えば、めっき法、スパッタリング法、ＣＶＤ法等が挙げられるが、被膜１０４は、前記のようにめっき法により形成されるのが好ましい。 Examples of the method of forming the film 104 include a plating method, a sputtering method, a CVD method, and the like, but the film 104 is preferably formed by the plating method as described above.
被膜１０４を形成するためのめっき条件は、使用する元素の種類や電極のサイズにより適宜決定すればよいが、電解めっき法を採用する場合、例えば金属濃度は５〜１０ｇ／ｌ、液温は５０〜６０℃、めっき液のｐＨは１〜４、電流密度は０．５〜１Ａ／ｄｍ２が挙げられる。 The plating conditions for forming the film 104 may be appropriately determined according to the type of the element used and the size of the electrode, but in the case of employing the electrolytic plating method, for example, the metal concentration is 5 to 10 g / l and the solution temperature is 50 The plating solution has a pH of 1 to 4 and a current density of 0.5 to 1 A / dm 2 .
このようにして形成された被膜１０４の膜厚は、０．０５〜１μｍが好ましく、０．１〜０．３μｍがさらに好ましい。このような膜厚によれば、コスト面と耐久性という理由から本発明の効果がさらに高まる。なお該膜厚は、例えばめっき時間により調整することができる。 0.05-1 micrometer is preferable and, as for the film thickness of the film | membrane 104 formed in this way, 0.1-0.3 micrometer is more preferable. According to such a film thickness, the effects of the present invention are further enhanced because of cost and durability. The film thickness can be adjusted, for example, by the plating time.
このように、上記の特定の構造を有する電極は、水中の溶存水素量を向上させるための水の電気分解用の電極として使用することができる。すなわち、本発明に使用する電極は、例えば、純水、水道水、井戸水、地下水などを直流電気分解することにより陰極に電解水素水を、陽極に電解酸性水を生成する公知の電解水生成装置における該陰極に用いて、水の電気分解を行うことができる。水の電気分解は、上記電極を陰極として使用するのであれば、任意の方法を適用できる。陰極により電気分解される水の温度は、例えば１０〜２５℃が好ましい。このようにして、電解水素水の溶存水素量を向上させることができる。
また、上記方法によって製造された電解水素水は、溶存水素量が向上した電解水素水となる。溶存水素量が向上した電解水素水は、例えば飲料用や人工透析用等として用いることができる。
Thus, the electrode having the above specific structure can be used as an electrode for water electrolysis to improve the amount of dissolved hydrogen in water. That is, the electrode used in the present invention is, for example, a known electrolyzed water generating device that generates electrolyzed hydrogen water at the cathode and electrolyzed acidic water at the anode by direct current electrolysis of pure water, tap water, well water, ground water, etc. Water electrolysis can be performed on the cathode in For electrolysis of water, any method can be applied as long as the electrode is used as a cathode. The temperature of water electrolyzed by the cathode is preferably, for example, 10 to 25 ° C. Thus, the amount of dissolved hydrogen in the electrolyzed hydrogen water can be improved.
Moreover, the electrolyzed hydrogen water manufactured by the said method turns into electrolyzed hydrogen water in which the amount of dissolved hydrogen improved. The electrolyzed hydrogen water in which the amount of dissolved hydrogen is improved can be used, for example, as a beverage or an artificial dialysis.
電解水素水中の溶存水素量は、任意の方法で測定することができ、例えば、溶存水素計（製品名：ＤＨＤＩ−１、東亜ＤＫＫ製）を用いて測定することができる。 The amount of dissolved hydrogen in the electrolyzed hydrogen water can be measured by any method. For example, it can be measured using a dissolved hydrogen meter (product name: DHDI-1, manufactured by Toa DKK).
以下、本発明を実施例および比較例によりさらに説明するが本発明は下記実施例に制限されない。 Hereinafter, the present invention will be further described by examples and comparative examples, but the present invention is not limited to the following examples.
［実施例１］
図２に示すような電極１０を作成した。
まず、Ｔｉからなる基材１０２を準備した（神戸製鋼所製）。基材１０２に対し、イートレックス（ＥＥＪＡ製）を用いた脱脂処理を行い、基材表面を清浄化処理した。
続いて、Ａｕを１０ｇ／ｌ含有するｐＨ＝１４の第１電解めっき液を調製した。なお、第１電解めっき液には、Ａｕ化合物としてシアン化金カリウムを用い、これを水に溶解させたものを用いた。
次に、清浄化処理した基材１０２に対し、上記第１電解めっき液を用いた電解めっきを行った。電解めっき条件は、めっき温度５０℃、電流密度２Ａ／ｄｍ２、めっき時間１分とした。電解めっき完了後、基材１０２を水洗、乾燥し、基材１０２上に膜厚０．１μｍのＡｕからなる被膜１０４ａを形成した。
続いて、Ｐｔを５ｇ／ｌ、Ｗを５ｇ／ｌ含有するｐＨ＝１の第２電解めっき液を調製した。なお、第２電解めっき液には、Ｐｔ化合物として塩化白金酸、Ｗ化合物としてタングステン酸ナトリウムを用い、これを水に溶解させたものを用いた。
Example 1
An electrode 10 as shown in FIG. 2 was produced.
First, a base material 102 made of Ti was prepared (manufactured by Kobe Steel, Ltd.). The substrate 102 was degreased using Eatrex (manufactured by EEJA) to clean the surface of the substrate.
Subsequently, a first electrolytic plating solution of pH 14 containing 10 g / l of Au was prepared. As the first electrolytic plating solution, gold potassium cyanide was used as the Au compound, and this was dissolved in water.
Next, electrolytic plating using the first electrolytic plating solution was performed on the cleaned base material 102. The electrolytic plating conditions were a plating temperature of 50 ° C., a current density of 2 A / dm 2 , and a plating time of 1 minute. After completion of the electrolytic plating, the base material 102 was washed with water and dried to form a film 104 a of Au having a thickness of 0.1 μm on the base material 102.
Subsequently, a second electrolytic plating solution of pH 1 containing 5 g / l of Pt and 5 g / l of W was prepared. The second electrolytic plating solution was prepared by dissolving chloroplatinic acid as a Pt compound and sodium tungstate as a W compound in water.
次に、被膜１０４ａを形成した基材１０２に対し、上記第２電解めっき液を用いた電解めっきを行った。電解めっき条件は、めっき温度５０℃、電流密度０．５Ａ／ｄｍ２、めっき時間５分とした。電解めっき完了後、基材１０２を水洗、乾燥し、被膜１０４ａ上に膜厚０．１μｍのＰｔ−Ｗ合金からなる被膜１０４ｂを形成し、電極を得た。
図３は、実施例１で得られた電極の断面図および表面の電子顕微鏡写真（１０００倍および１００００倍）である。
続いて、得られた電極を用いて水の電気分解を行い、電解水素水中の溶存水素量（ＤＨ／μｇ／Ｌ）を調べた。水の電気分解は、図８に示すように、プラスチック製のセルに隔膜を隔てて、電極を５枚設置した電解槽に水道水（市水、水温２０℃）を供給し、上記電極に直流電源で電流を流すことによって行った。水の電気分解は以下の条件で行った。
・流量：２．５Ｌ／ｍｉｎ（入口）
・電流密度：１．４Ａ／ｄｍ２
・電極：７０×１００×０．５ｔ
・電極枚数：５枚
・電極触媒膜厚：０．１μｍ
・電極間隔：２ｍｍ
水の電気分解後、陰極側の水の溶存水素量を、溶存水素計（製品名：ＤＨＤＩ−１、東亜ＤＫＫ製）を用いて経時的に測定した（電気分解開始時から１０分間測定）。結果を図９に示す。
Next, electrolytic plating using the second electrolytic plating solution was performed on the base material 102 on which the film 104a was formed. The electrolytic plating conditions were a plating temperature of 50 ° C., a current density of 0.5 A / dm 2 , and a plating time of 5 minutes. After the completion of the electrolytic plating, the base material 102 was washed with water and dried to form a film 104b made of a Pt-W alloy having a film thickness of 0.1 μm on the film 104a, thereby obtaining an electrode.
FIG. 3 is a cross-sectional view of the electrode obtained in Example 1 and an electron micrograph (1000 × and 10000 ×) of the surface.
Subsequently, water was electrolyzed using the obtained electrode, and the amount of dissolved hydrogen (DH / μg / L) in electrolytic hydrogen water was examined. Electrolysis of water, as shown in FIG. 8, separates a diaphragm from a plastic cell and supplies tap water (city water, water temperature 20 ° C.) to an electrolytic cell provided with five electrodes, and direct current to the above electrode It did by flowing current with the power supply. The electrolysis of water was performed under the following conditions.
・ Flow rate: 2.5 L / min (inlet)
・ Current density: 1.4 A / dm 2
-Electrode: 70 x 100 x 0.5 t
・ Number of electrodes: 5 ・ Electrode film thickness: 0.1 μm
・ Electrode distance: 2 mm
After the electrolysis of water, the amount of dissolved hydrogen in the water on the cathode side was measured over time using a dissolved hydrogen meter (product name: DHDI-1, manufactured by Toa DKK) (measured for 10 minutes from the start of electrolysis). The results are shown in FIG.
［実施例２］
実施例１において、第２電解めっき液としてＰｔを５ｇ／ｌ含有するｐＨ＝１の電解めっき液を用いたこと以外は、実施例１を繰り返した。実施例２で得られた電極の断面図および表面の電子顕微鏡写真（１０００倍および１００００倍）を図４に、電解水素水中の溶存水素量（ＤＨ／μｇ／Ｌ）の結果を図９に示す。
Example 2
In Example 1, Example 1 was repeated except that an electrolytic plating solution of pH 1 containing 5 g / l of Pt was used as the second electrolytic plating solution. A cross-sectional view of the electrode obtained in Example 2 and an electron micrograph (1000 × and 10000 ×) of the surface are shown in FIG. 4, and the result of the amount of dissolved hydrogen (DH / μg / L) in electrolytic hydrogen water is shown in FIG. .
［比較例１］
実施例１において、被膜１０４ａの膜厚を０．０５μｍにし、被膜１０４ｂを設けなかったこと以外は、実施例１を繰り返した。比較例１で得られた電極の断面図および表面の電子顕微鏡写真（１０００倍および１００００倍）を図５に、電解水素水中の溶存水素量（ＤＨ／μｇ／Ｌ）の結果を図９に示す。
Comparative Example 1
In Example 1, Example 1 was repeated except that the film thickness of the film 104 a was 0.05 μm and the film 104 b was not provided. The cross-sectional view of the electrode obtained in Comparative Example 1 and the electron micrographs (1000 × and 10000 ×) of the surface are shown in FIG. 5, and the results of the amount of dissolved hydrogen (DH / μg / L) in electrolytic hydrogen water are shown in FIG. .
［比較例２］
実施例１において、電極として厚さ１ｍｍのＷ板を用いたこと以外は、実施例１を繰り返した。比較例２で得られた電極の断面図および表面の電子顕微鏡写真（１０００倍および１００００倍）を図６に、電解水素水中の溶存水素量（ＤＨ／μｇ／Ｌ）の結果を図９に示す。
Comparative Example 2
Example 1 was repeated except that in Example 1, a W plate having a thickness of 1 mm was used as an electrode. FIG. 6 shows a cross-sectional view of the electrode obtained in Comparative Example 2 and electron micrographs (1000 × and 10000 ×) of the surface, and FIG. 9 shows the results of the amount of dissolved hydrogen (DH / μg / L) in electrolytic hydrogen water. .
［比較例３］
実施例２において、被膜１０４ａを設けずに、膜厚を０．１μｍの被膜１０４ｂを設けたこと以外は、実施例１を繰り返した。比較例３で得られた電極の断面図および表面の電子顕微鏡写真（１０００倍および１００００倍）を図７に、電解水素水中の溶存水素量（ＤＨ／μｇ／Ｌ）の結果を図９に示す。
Comparative Example 3
Example 1 was repeated except that the film 104b having a thickness of 0.1 μm was provided without providing the film 104a. A cross-sectional view of the electrode obtained in Comparative Example 3 and an electron micrograph (at 1000 and 10000 times) of the surface are shown in FIG. 7, and the result of the amount of dissolved hydrogen (DH / μg / L) in electrolytic hydrogen water is shown in FIG. .
図９の結果から、実施例１および２で得られた電極は、電解水素水中に含まれる溶存水素量を十分に向上させることが判明した。とくに、実施例１の基材上にＡｕを含有する層（被膜１０４ａ）が形成され、その上にさらにＰｔ−Ｗ合金を含有する層（被膜１０４ｂ）が形成された電極は、該溶存水素量をさらに高めることが分かった。
これに対し、比較例１〜３では、本発明で規定する電極の条件を満たしていないため、実施例に比べ溶存水素量が低下している。
なお、実施例１において被膜１０４ｂのＰｔ−Ｗの代わりにＰｔ−Ｉｒを使用した場合、比較例３と同様の結果を得た。
From the results shown in FIG. 9, it was found that the electrodes obtained in Examples 1 and 2 sufficiently improve the amount of dissolved hydrogen contained in the electrolytic hydrogen water. In particular, an electrode in which a layer containing Au (coating 104a) is formed on the base material of Example 1 and a layer (coating 104b) further containing a Pt-W alloy is formed has the dissolved hydrogen amount. It turned out that the
On the other hand, in Comparative Examples 1 to 3, since the conditions of the electrode specified in the present invention are not satisfied, the amount of dissolved hydrogen is lower than in the examples.
In addition, when using Pt-Ir instead of Pt-W of the film 104b in Example 1, the same result as Comparative Example 3 was obtained.
１０ 電極
１０２ 基材
１０４ 被膜
10 electrode 102 substrate 104 coating
Claims (5)