JP6220469B2 - Method for producing a dyeing agent made from tsuji stone - Google Patents
Method for producing a dyeing agent made from tsuji stone Download PDFInfo
- Publication number
- JP6220469B2 JP6220469B2 JP2017045534A JP2017045534A JP6220469B2 JP 6220469 B2 JP6220469 B2 JP 6220469B2 JP 2017045534 A JP2017045534 A JP 2017045534A JP 2017045534 A JP2017045534 A JP 2017045534A JP 6220469 B2 JP6220469 B2 JP 6220469B2
- Authority
- JP
- Japan
- Prior art keywords
- stone
- stone powder
- solution
- aji
- astringent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、庵治石中の成分の分離方法、庵治石を原料とする染色剤の製造方法、庵治石を原料に含むブルーライトカットガラスに関する。 The present invention relates to a method for separating components in aji stone, a method for producing a stain using aji stone as a raw material, and a blue light cut glass containing aji stone as a raw material.
織物や衣服などでは、繊維を染色剤によって様々な色や模様に染めて見栄えをよくすることが行われている。かかる染色剤には、動物、植物から抽出した天然色素である天然染色剤や、化学的に合成した合成染色剤がある。現在では、コストや所定の色に染めやすい等の理由から、天然染色剤よりも合成染色剤が一般的な染色剤として使用されている。 In textiles and clothes, fibers are dyed into various colors and patterns with a dye to improve their appearance. Such dyes include natural dyes that are natural pigments extracted from animals and plants, and synthetic dyes that are chemically synthesized. At present, synthetic dyes are used as general dyes rather than natural dyes for reasons such as cost and ease of dyeing into predetermined colors.
一方、天然染色剤は、所定の色に染めることが難しいという問題はあるものの、染められたものに独特の風合いを生じさせることができるという点で優れている。現在、天然染色剤として、藍やクチナシ等の植物由来のものが一般的に使用されている。 On the other hand, natural dyes are excellent in that they can give a unique texture to the dyed material, although there is a problem that it is difficult to dye a predetermined color. Currently, plant-derived materials such as indigo and gardenia are generally used as natural dyes.
近年では、両染色剤の利点を生かすために、草木染色剤などの天然染色剤と化学染色剤の組み合わせで繊維材料を染色する技術も開発されている（特許文献１参照）。特許文献１には、この技術を利用すれば、天然染色剤による染色の色調や多彩な色調を呈しつつ、高い堅牢性を有する染色を実現できる旨の記載がある。 In recent years, in order to take advantage of the advantages of both dyes, a technique for dyeing fiber materials with a combination of natural dyes such as plant dyes and chemical dyes has been developed (see Patent Document 1). Patent Document 1 describes that if this technique is used, dyeing with high fastness can be realized while exhibiting a color tone and various color tones with a natural dyeing agent.
ところで、天然染色剤には、動物、植物から抽出した天然色素以外に、鉱物由来の染色剤（鉱物染色剤）もある。かかる鉱物染色剤として、黄土や赤土・赭土・弁柄などから採れるものが知られているが、鉱物染色剤は他の天然材料に比べて種類も少なく、利用される機会も少ない状況にある。 By the way, natural dyes include mineral-derived dyes (mineral dyes) in addition to natural pigments extracted from animals and plants. Such mineral stains are known to be taken from loess, red soil, clay, petal, etc., but there are fewer types of mineral stains than other natural materials, and there are few opportunities for use. .
庵治石や種々の石材を切り出したり石材を加工したりする際には、多量の石粉が発生するが、利用価値が少なく、現状では産業廃棄物として廃棄されている。しかし、かかる石粉中には種々の鉱物や鉱物以外に有効活用できる物質が存在している。 When cutting out stones and various stones or processing stones, a large amount of stone powder is generated, but it has little utility value and is currently discarded as industrial waste. However, there are various minerals and substances that can be used effectively other than minerals in such stone powder.
したがって、庵治石等の石粉から、鉱物や鉱物以外の物質を分離できれば、鉱物は染色剤の材料として利用できる可能性があり、鉱物以外の物質も種々の用途に利用できる可能性がある。 Therefore, if minerals and substances other than minerals can be separated from stone powder such as meiji stones, minerals can be used as dye materials, and substances other than minerals can also be used in various applications.
また、庵治石等の石粉から鉱物や鉱物以外の物質を分離せず、石粉をそのまま利用することができればより活用の範囲が広がる。 In addition, if the stone powder can be used as it is without separating minerals or non-mineral substances from stone powder such as Jiji stone, the range of utilization will be further expanded.
本発明は上記事情に鑑み、庵治石の石粉から有効成分を分離できる庵治石中の成分の分離方法、独特の色合いに染めることができる庵治石を原料とする染色剤の製造方法、庵治石中の成分の分離方法および庵治石を原料に含むブルーライトカットガラスを提供する。 In view of the above circumstances, the present invention provides a method for separating components in a stone that can separate active ingredients from stone powder of a stone, a method for producing a dye using a stone that can be dyed in a unique color, And a blue light cut glass containing jiji stone as a raw material.
第１発明の庵治石を原料とする染色剤の製造方法は、細粒黒雲母花崗岩である庵治石の石粉から染色剤を製造する方法であって、前記庵治石の石粉をタンニンを含有する柿渋溶液に混合し、該混合液が、上から、上澄み液の層と、色がついた液体層と、ケイ素を主成分とする白色層と、残渣層と、が形成されるように保持し、該複数の層が形成された混合液から前記色がついた液体層を分離し、鉄の含有率が最も高く、カルシウムの含有率が二番目に高く、該カルシウムの含有率についでカリウムとケイ素の含有率が高い液体染色剤を得ることを特徴とする。 The method for producing a staining agent using the aji stone of the first invention as a raw material is a method for producing a staining agent from a stone powder of aji stone, which is a fine-grained biotite granite, wherein the stone powder of the aji stone contains tannin. Mixed with the solution, the mixture is held from above, so that a layer of supernatant liquid, a colored liquid layer, a white layer mainly composed of silicon, and a residue layer are formed, The colored liquid layer is separated from the mixed solution in which the plurality of layers are formed, the iron content is the highest, the calcium content is the second highest, and the calcium content is followed by potassium and silicon. A liquid dyeing agent having a high content of is obtained .
第１発明によれば、庵治石の石粉と柿渋溶液を混合することによって、液体層に石粉中の鉱物が柿渋溶液と反応して形成された庵治石由来の色素を含有させることができる。そして、かかる液から庵治石由来の様々な色素を含有する染色剤を製造することができる。すると、かかる染色剤を用いて繊維等を染めれば、非常に優れた色合いの染物を製造することができる。 According to the first invention, by mixing the stone powder of aji stone and amber astringent solution, a pigment derived from aji stone formed by the reaction of the mineral in the stone powder with the astringent solution can be contained in the liquid layer. And the dyeing | staining containing various pigment | dyes derived from a meiji stone can be manufactured from this liquid. Then, if dyeing | staining a fiber etc. using this dyeing agent, the dyeing | staining of the very outstanding color can be manufactured.
庵治石（地域団体商標）は、香川県の庵治町・牟礼町にまたがる八栗五剣山山麓で採れる細粒黒雲母花崗岩であり、石英・長石を主成分とし、少量の黒雲母と角閃石を含むものである。 Oji Stone (Regional Group Trademark) is a fine-grained biotite granite from the foot of Yaguri Gokenzan across Kashiwa-cho and Kakei-cho in Kagawa Prefecture. It is a waste.
本発明の庵治石を原料とする染色剤の製造方法は、上記のような庵治石の石粉を染色剤の原料としたことに特徴を有している。 The method for producing a staining agent using the aji stone of the present invention as a raw material is characterized in that a stone powder of the above aji stone is used as a raw material of the staining agent.
本発明の庵治石を原料とする染色剤の製造方法によって製造された染色剤の用途はとくに限定されない。例えば、織物や糸、紙、革等を染める染色剤として使用できる。また、ペン等のインクや塗装材料などの染色剤として使用することができる。 The use of the dyeing agent produced by the method for producing a dyeing agent made from the mushroom stone of the present invention is not particularly limited. For example, it can be used as a dyeing agent for dyeing fabrics, yarns, paper, leather, and the like. Moreover, it can be used as dyes, such as inks, such as pen, and coating materials.
（本発明の庵治石を原料とする染色剤の製造方法）
本発明の庵治石を原料とする染色剤の製造方法では、本発明の庵治石中の成分の分離方法によって染色剤を製造する。つまり、従来廃棄されていた庵治石の石粉を使用して、この石粉中に含まれる鉱物から染色剤を製造する。
(Manufacturing method of the dyeing agent using the Jinshi stone of the present invention as a raw material)
In the method for producing a staining agent using the aji stone of the present invention as a raw material, the staining agent is produced by the method for separating components in the aji stone of the present invention. In other words, a dyeing agent is produced from minerals contained in this stone powder by using the stone powder of Aji stone that has been conventionally discarded.
（庵治石中の成分の分離方法）
まず、本発明の庵治石を原料とする染色剤の製造方法で採用する、庵治石中の成分の分離方法を説明する。
(Separation method of ingredients in 庵 石)
First, a method for separating components in aji stone, which is employed in the method for producing a stain using ajiji stone of the present invention as a raw material, will be described.
図１に示すように、本発明の庵治石中の成分の分離方法では、まず、庵治石の石粉を混合する柿渋溶液を準備する（図２（Ｂ）参照）。
この柿渋溶液は、天然の柿渋汁や市販の柿渋汁などの柿渋原液を水で薄めたものである。例えば、市販の柿渋汁（例えば、中部サンデー販売 (株)：柿渋）であれば、１０倍程度に薄めれば、タンニンの濃度が染色に適した濃度に調整された柿渋溶液を得ることができる。
As shown in FIG. 1, in the method for separating components in aji stone according to the present invention, first, a persimmon astringent solution in which stone powder of aji stone is mixed is prepared (see FIG. 2B).
This persimmon astringent solution is obtained by diluting a persimmon astringent stock solution such as natural persimmon astringent juice or a commercially available persimmon astringent juice with water. For example, if it is a commercially available persimmon astringent soup (for example, Chubu Sunday Sales Co., Ltd .: persimmon astringent), it is possible to obtain a persimmon astringent solution in which the concentration of tannin is adjusted to a concentration suitable for dyeing when diluted 10 times. .
なお、柿渋原液となる天然の柿渋汁は、渋柿をすりおろしてフィルターで濾して製造することができる。 In addition, the natural persimmon soup that becomes the persimmon astringent stock solution can be produced by grated the persimmon and filtered through a filter.
つぎに、庵治石の石粉（以下、単に石粉という）を準備する（図２（Ａ）参照）。この石粉は、その粒径等はとくに限定されないが、ある程度細かいものが望ましい。例えば、庵治石の切り出しや加工の際に発生した石粉を使用することができる。 Next, a stone powder (hereinafter simply referred to as a stone powder) of Aji stone is prepared (see FIG. 2A). The particle size and the like of the stone powder are not particularly limited, but are desirably somewhat fine. For example, it is possible to use stone powder generated at the time of cutting out or processing aji stone.
石粉と柿渋溶液が準備されると、柿渋溶液に石粉を入れてある程度攪拌して、混合液を形成する（図３（Ａ）参照）。そして、石粉を入れた状態のまま混合液を静置すると、混合液に石粉中の鉱物由来の染色剤が溶け出して、混合液は元の状態から色が変化する。 When the stone powder and the astringent astringent solution are prepared, the stone powder is put into the astringent astringent solution and stirred to some extent to form a mixed solution (see FIG. 3A). And when a liquid mixture is left still in the state which put the stone powder, the coloring agent derived from the mineral in a stone powder will melt | dissolve in a liquid mixture, and the color of a liquid mixture will change from the original state.
混合液をある程度の期間で静置すると、混合液中の固形分が沈殿して、混合液中に複数の層が形成される。具体的には、図４に示すように、上から、液体層と、ケイ素（シリカ）を主成分とする層（白色の固体からなる層）と、その他の物質の層（残渣層）に分離される（図３（Ｂ）、図６〜図８参照）。
なお、白色の個体からなる層が、特許請求の範囲にいう白色層に相当する。
When the mixed solution is allowed to stand for a certain period of time, a solid content in the mixed solution is precipitated, and a plurality of layers are formed in the mixed solution. Specifically, as shown in FIG. 4, the liquid layer, the layer mainly composed of silicon (silica) (layer made of white solid), and the layer of other substances (residue layer) are separated from the top. (See FIG. 3B and FIGS. 6 to 8).
Note that a layer made of a white solid corresponds to a white layer referred to in the claims.
さらに混合液を静置すると、液体層は、上澄み液の層と、色がついた液体層と、に分離されるとともに、液体層から固形分の分離が進行する（図４参照）。そして、液体層から固形分が十分に分離されれば、庵治石中の成分の分離が完了する。この液体層中の色がついた液体層が本発明の染色剤となる。つまり、この色がついた液体層を分離したものが、特許請求の範囲にいう液体染色剤に相当する。 Further mixture is allowed to settle, the liquid layer is a layer of supernatant liquid, and the liquid layer The colored, while being separated, the separation of solids proceeds from the liquid layer (see Figure 4). And if solid content is fully isolate | separated from a liquid layer, isolation | separation of the component in an amber stone will be completed. The colored liquid layer in the liquid layer is the staining agent of the present invention. That is, what separated the colored liquid layer is equivalent to the liquid dyeing agent in the claims.
なお、混合液は、液体層から固形分が十分に分離されるまで静置してもよいが、液体層が所望の色になれば、その状態で液体だけを取り出したり、濾過や沈澱分離等の方法を使用して混合液から固形分を除去したりしてもよい。 The liquid mixture may be allowed to stand until the solid content is sufficiently separated from the liquid layer. However, if the liquid layer has a desired color, only the liquid is taken out in that state, or filtration, precipitation separation, etc. The solid content may be removed from the mixed solution using the above method.
そして、本発明の染色剤に糸などを浸漬すれば、本発明の染色剤中の染色剤が糸などに結合するので、糸などを染色することができる（図５参照）。そして、糸などを染色剤に浸漬する時間を調整すれば、糸などの染色状態を調整することができる。例えば、図５では、右から左に向かって、浸漬時間を長くしたものであるが、浸漬時間を長くすることによって、染色した糸などの色の濃さを変えることができる。 When the yarn or the like is immersed in the staining agent of the present invention, the staining agent in the staining agent of the present invention binds to the yarn or the like, so that the yarn or the like can be dyed (see FIG. 5). If the time for immersing the yarn or the like in the dyeing agent is adjusted, the dyeing state of the yarn or the like can be adjusted. For example, in FIG. 5, the immersion time is increased from the right to the left, but by increasing the immersion time, the color density of the dyed yarn or the like can be changed.
以上のように、本発明の庵治石中の成分の分離方法を使用すれば、柿渋溶液を調整し石粉と混合して静置するだけで、今までにない色合いを有する、庵治石由来の天然の染色剤を製造することができる。しかも、産業廃棄物として廃棄されていた石粉を、染色剤の原料として有効活用できるので、産業廃棄物の量を減らすことができる。 As described above, if the method for separating components in aji stone according to the present invention is used, it is possible to prepare an astringent astringent solution, mix it with stone powder, and leave it alone. The following dyeing agent can be produced. And since the stone powder discarded as industrial waste can be used effectively as a raw material of a dyeing agent, the amount of industrial waste can be reduced.
そして、石粉に含まれる鉱物の量は、石粉を発生した石の性質によって変化する。庵治石は花崗岩であり、黒雲母や錆石等の複数の鉱物が含まれているが、各鉱物の含有量、各鉱物の含有割合によって染色剤の色が変化する。すると、石粉を単体で使用したり、数種類の石粉を混合して使用したりすることによって、特色のある色合いの染色剤を製造することができる。したがって、本発明の庵治石中の成分の分離方法によって製造された染色剤によって糸などを染めれば、独特の風合いを有する染物を製造することができる。 And the quantity of the mineral contained in stone powder changes with the property of the stone which generated stone powder. Oji stone is a granite and contains a plurality of minerals such as biotite and rust stone, but the color of the stain changes depending on the content of each mineral and the content ratio of each mineral. Then, by using the stone powder alone or by mixing and using several kinds of stone powder, it is possible to produce a dye having a characteristic color. Therefore, if a yarn or the like is dyed with the dyeing agent produced by the method for separating components in the stones of the present invention, a dyed product having a unique texture can be produced.
しかも、本発明の庵治石中の成分の分離方法では、染色剤だけでなく、石粉からケイ素の割合が多い白色の粉を回収することができる。この粉は、純度はそれほど高くないものの、ケイ素の割合が多いので、種々の材料の原料として使用できる可能性がある。 Moreover, in the method for separating components in the stones of the present invention, white powder having a high silicon ratio can be recovered from the stone powder as well as the staining agent. Although this powder is not so high in purity, it has a high percentage of silicon, so it may be used as a raw material for various materials.
また、残渣層の物質も、コンクリートの骨材などとして使用できる可能性がある。 There is also a possibility that the material of the residual layer can be used as concrete aggregate.
なお、液体層はそのまま染色剤として使用してもよいが、液体層の水分を除去して染色剤をゲル状や固体状にしてもよい。この場合、染色剤は、水分が除去されているので、取り扱い性を向上することができるし、保存性もよくなる。そして、水分を除去した染色剤に水を加えれば、元の状態の染色剤の状態とできる。 The liquid layer may be used as a staining agent as it is, but the staining agent may be gelled or solid by removing water from the liquid layer. In this case, since the water | moisture content is removed from the dyeing agent, handling property can be improved and preservability is also improved. If water is added to the stain from which moisture has been removed, the original stain can be obtained.
（染色剤ができる理由）
本発明の庵治石中の成分の分離方法によって得られた液体が染色剤となる理由ははっきりとしないが、以下のように考えられる。
(Reason for dyeing)
The reason why the liquid obtained by the method for separating components in the stones of the present invention becomes a staining agent is not clear, but is considered as follows.
柿渋にはタンニンが含まれているので、柿渋溶液にも多量のタンニンが含まれている。このような柿渋溶液に石粉を混合すれば、石粉中の鉱物が柿渋溶液中のタンニンと反応する。すると、石粉から柿渋溶液中に鉱物（金属）が溶けだして、この鉱物とタンニンが強く結合して発色する。したがって、タンニンと結合して発色するようになった鉱物が色素となって染色剤ができると考えられる。例えば、図７に示すように、鉄分が多く含まれているので、この鉄分が発色を生じさせていると考えられる。 Since the persimmon astringent contains tannin, the persimmon astringent solution also contains a large amount of tannin. When stone powder is mixed with such amber astringent solution, minerals in the stone powder react with tannins in the astringent astringent solution. Then, the mineral (metal) starts to dissolve from the stone powder into the persimmon astringent solution, and this mineral and tannin are strongly combined to develop color. Accordingly, it is considered that the mineral that has developed color by combining with tannin becomes a pigment to form a staining agent. For example, as shown in FIG. 7, since a large amount of iron is contained, it is considered that this iron causes color development.
（石粉とタンニン溶液の混合割合について）
本発明の庵治石中の成分の分離方法において、石粉とタンニン溶液の混合する割合はとくに限定されない。しかし、本発明の庵治石中の成分の分離方法によって得られた液を染色剤として使用する場合には、タンニン液と庵治石の石粉を適切な混合割合で混合すれば、繊維等を染めたときに、非常に優れた色合いの染物を製造することができる。
(About mixing ratio of stone powder and tannin solution)
In the method for separating components in the stones of the present invention, the mixing ratio of the stone powder and the tannin solution is not particularly limited. However, when using the liquid obtained by the method for separating components in the stones of the present invention as a dyeing agent, if the tannin liquid and stone powder of the stones are mixed at an appropriate mixing ratio, the fibers are dyed. Sometimes very good shades can be produced.
例えば、市販のタンニン原液を５〜１５％に希釈したタンニン液２００〜１０００ｍｌに対して、庵治石の石粉８０〜４００ｇを混合すれば、本発明の庵治石中の成分の分離方法によって染色剤を製造することができる。また、市販のタンニン原液を８〜１２％に希釈したタンニン液３００〜８００ｍｌに対して、庵治石の石粉１００〜３００ｇを混合しても、染色剤を製造することができる。とくに、市販のタンニン原液を浄水器によって浄化された水によって１０％に希釈したタンニン液５００ｍｌに対して、庵治石の石粉２００ｇを混合した場合には、本発明の庵治石中の成分の分離方法によって綺麗な青色の染色剤を製造することができる。 For example, if 200 to 1000 ml of tannin solution obtained by diluting a commercial tannin stock solution to 5 to 15% is mixed with 80 to 400 g of stone powder of Jiji stone, the staining agent can be obtained by the method for separating components in Jiji stone of the present invention. Can be manufactured. Moreover, a dyeing agent can also be manufactured even if it mixes 100-300g of a stone powder of Jiji stone with respect to 300-800 ml of tannin solutions which diluted the commercially available tannin stock solution to 8-12%. In particular, when 200 g of stone powder of moji stone is mixed with 500 ml of tannin solution obtained by diluting a commercial tannin stock solution to 10% with water purified by a water purifier, the method for separating components in moji stone of the present invention Can produce a beautiful blue dye.
（染色剤の色合いの調整）
そして、タンニンの濃度や種類、石粉の量や石粉の種類、柿渋溶液と石粉を混合している時間等を調整すれば、染色剤の色や色の濃さ等を調整することができる。例えば、保持しておく時間を変化させれば、薄紫〜藍色まで少しずつ違った色の染色剤を製造することができる。また、異なる種類の石粉を混ぜて使用すれば、その混合割合によって、染色剤の色を変化させることができる。
(Adjusting the color of the stain)
Then, by adjusting the concentration and type of tannin, the amount of stone powder, the type of stone powder, the time during which the persimmon astringent solution and the stone powder are mixed, the color of the stain, the intensity of the color, and the like can be adjusted. For example, if the holding time is changed, a dyeing agent having a slightly different color from light purple to indigo can be produced. In addition, if different types of stone powder are mixed and used, the color of the staining agent can be changed depending on the mixing ratio.
（石粉と混合する溶液について）
石粉と混合する溶液は、上述した柿渋溶液以外の溶液を使用することもできる。例えば、本発明の庵治石中の成分の分離方法において、タンニンを所定の量以上含む溶液（タンニン溶液）を使用しても、本発明の庵治石中の成分を分離でき、上記のような染色剤を製造することができる。この場合、タンニン溶液に含まれるタンニンの種類（縮合型（カテコール系）か加水分解型（ピロガロール系））もとくに限定されない。
(About the solution mixed with stone powder)
As the solution to be mixed with the stone powder, a solution other than the amber astringent solution described above can also be used. For example, in the method for separating components in the stones according to the present invention, the components in the stones according to the present invention can be separated even if a solution containing a predetermined amount or more of tannin (tannin solution) is used. Agent can be produced. In this case, the type of tannin contained in the tannin solution (condensation type (catechol type) or hydrolysis type (pyrogallol type)) is not particularly limited.
とくに、染色剤を製造する場合には、添加物を含まない柿渋液を使用すれば、発色状態を良好にできるので、好ましい。また、タンニン溶液に含まれるタンニンの種類が異なれば、鉱物との結合状態などが変化するので、タンニンの種類を変えれば、染色剤の色を変化させることができる可能性がある。 In particular, in the case of producing a dyeing agent, it is preferable to use a persimmon astringent solution that does not contain additives because the color development state can be improved. Further, if the type of tannin contained in the tannin solution is different, the binding state with minerals and the like are changed. Therefore, if the type of tannin is changed, the color of the staining agent may be changed.
（柿渋溶液と石粉の混合について）
庵治石中の成分を分離する場合には、柿渋溶液と石粉を混合した混合液は、混合した状態のまま静置しておく方が望ましい。
(About mixing of persimmon astringent solution and stone powder)
In the case of separating the components in the aji stone, it is desirable to leave the mixed solution of the astringent astringent solution and the stone powder in a mixed state.
一方、染色剤を製造することを目的とする場合であれば、混合液は混合した状態で連続的または間欠的に攪拌してもよい。とくに、柿渋溶液と石粉を混合した際にしっかりと両者が混合するように攪拌し、その後は静置する方が発色性を良くしたり、柿渋溶液に溶けだした金属成分が凝集などして柿渋溶液から分離することを防いだりする上では望ましい。
また、柿渋溶液と石粉は、常温で使用する方が発色性を良くしたり、柿渋溶液に溶けだした金属成分が凝集などして柿渋溶液から分離することを防いだりする上では望ましい。
On the other hand, if the purpose is to produce a staining agent, the mixed solution may be stirred continuously or intermittently in a mixed state. In particular, when the persimmon astringent solution and stone powder are mixed, they are stirred so that they are mixed together, and then left standing to improve color development, or the metal components that have dissolved in the persimmon astringent solution may agglomerate, etc. It is desirable to prevent separation from
In addition, it is preferable that the astringent solution and stone powder be used at room temperature in order to improve the color developability and to prevent the metal component dissolved in the astringent solution from aggregating and separating from the astringent solution.
（ブルーライトカットガラス）
上記例では、庵治石の石粉に含まれる成分を分離して利用する場合を説明したが、庵治石の石粉をそのまま使用する原料として使用することも可能である。
(Blue light cut glass)
In the above example, the case where the components contained in the stone powder of Aji stone are separated and used is described, but the stone powder of Aji stone can be used as a raw material as it is.
庵治石の石粉を混合してガラスを製造することは、香川県出身の芸術家、杉山利恵氏が世界で初めて成功した。杉山利恵氏は、独自の手法で庵治石の石粉をガラスの材料に混合して処理することによって、非常に美しい青色のガラス（さぬき庵治石ガラス）を製造し、現在も数々の作品を創作している（参考ホームページ：さぬき庵治石硝子：http://aji-glass.jp/）。 Toshie Sugiyama, the artist from Kagawa Prefecture, was the first in the world to produce glass by mixing stones from Jiuji Stone. Mr. Toshie Sugiyama produced a very beautiful blue glass (Sanuki Eiji Stone Glass) by mixing and processing the stone powder of Eiji stone into the glass material by a unique method, and has created many works now. (Reference Homepage: Eiji Sanuki Glass: http://aji-glass.jp/)
本発明者は、前述したさぬき庵治石ガラスには、ブルーライトをカットする機能を有すると考えて分析を行った。すると、図９に示すように、さぬき庵治石ガラスは、一般のガラスよりはブルーライトをカットする効果が高くなっている。しかも、さぬき庵治石ガラスは、市販されているブルーライトカットガラスよりはブルーライトをカットする効果は低いものの、濁りの無いクリアな見え方となることが確認された。つまり、市販されているブルーライトカットガラスは、ガラスを通して景色などを見たときに景色が黄色がかり濁ったような見え方になるが、さぬき庵治石ガラスを通して景色を見た場合、景色を濁りが無いクリアな状態で見ることができる。 The present inventor conducted analysis by considering that the above-described Sanuki Kanji stone glass has a function of cutting blue light. Then, as shown in FIG. 9, the Sanuki Eiji stone glass has a higher effect of cutting blue light than general glass. Moreover, it was confirmed that the Sanuki Juji stone glass has a clear appearance with no turbidity, although the effect of cutting blue light is lower than the commercially available blue light cut glass. In other words, the commercially available blue light cut glass looks like a yellowish cloudy landscape when viewed through the glass, but if you view the landscape through Sanuki Eiji stone glass, the landscape becomes cloudy. It can be seen in a clear state.
したがって、従来産廃としていた庵治石の石粉を原料として使用してガラスを製造すれば、ブルーライトをカットする効果があり、しかも、ガラスを通して濁りが無いクリアな景色などを見ることができるガラスを得ることができる。 Therefore, if glass is produced using the traditionally abandoned stone powder of Aji stone, it has the effect of cutting blue light, and it is possible to obtain glass that can be seen through clear scenery without turbidity. be able to.
本発明の庵治石中の成分の分離方法は、庵治石中の成分を分離して回収する方法としててきしている。
また、本発明の庵治石を原料とする染色剤の製造方法は、織物や糸等を染色する染色剤や、ペンなどのインキや塗料の染色剤を製造する方法に適している。
The method for separating components in aji stone according to the present invention has been a method for separating and recovering the components in aji stone.
In addition, the method for producing a dyeing agent using the Juji stone of the present invention as a raw material is suitable for a method of producing a dyeing agent for dyeing fabrics, yarns, etc., or a dye for inks and paints such as pens.
Claims (1)
前記庵治石の石粉をタンニンを含有する柿渋溶液に混合し、
該混合液が、上から、上澄み液の層と、色がついた液体層と、ケイ素を主成分とする白色層と、残渣層と、が形成されるように保持し、
該複数の層が形成された混合液から前記色がついた液体層を分離し、鉄の含有率が最も高く、カルシウムの含有率が二番目に高く、該カルシウムの含有率についでカリウムとケイ素の含有率が高い液体染色剤を得る
ことを特徴とする庵治石を原料とする染色剤の製造方法。 A method for producing a staining agent from fine stone biocite granite stone powder,
Mixing the agate stone powder into an astringent solution containing tannin,
The mixed liquid is retained from above so that a supernatant liquid layer, a colored liquid layer, a white layer mainly composed of silicon, and a residue layer are formed,
The colored liquid layer is separated from the mixed solution in which the plurality of layers are formed, the iron content is the highest, the calcium content is the second highest, and the calcium content is followed by potassium and silicon. Liquid stain with high content of
A method for producing a dyeing material made from aji stone .