JP6205227B2 - タイヤ用ゴム組成物 - Google Patents
タイヤ用ゴム組成物 Download PDFInfo
- Publication number
- JP6205227B2 JP6205227B2 JP2013204018A JP2013204018A JP6205227B2 JP 6205227 B2 JP6205227 B2 JP 6205227B2 JP 2013204018 A JP2013204018 A JP 2013204018A JP 2013204018 A JP2013204018 A JP 2013204018A JP 6205227 B2 JP6205227 B2 JP 6205227B2
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- thermally expandable
- weight
- rubber composition
- ice
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
熱膨張性マイクロカプセルを以下の工程により調製した。水系成分として、固形分40%のコロイダルシリカ45g、ジエタノールアミン−アジピン酸縮合物1g、塩化ナトリウムを150g及びイオン交換水500gを混合後、pH3.5に調整して水系分散媒体を製造した。次いで、油系成分として、アクリロニトリル70g、メタクリロニトリル70g、メタクリル酸70g、エチレングリコールジメタクリレートを3g及びアゾビス(2,4−ジメチリルバレロニトリル)1gを混合して均一溶液の単量体混合物を調製した。この単量体混合物に、イソペンタン30gまたは2−メチルペンタン30gを加え、オートクレーブに仕込み、水系分散媒体を更に仕込んだ。5分間700rpmで仕込み物を撹拌後、オートクレーブ内を窒素置換し、反応温度60℃で8時間反応させた。なお、反応圧力は0.5MPa、撹拌は350rpmで行った。最終工程では、熱膨張性マイクロカプセルの水分を除去するために、ミキサードライヤーを用いて70℃で乾燥した。
上述した熱膨張性マイクロカプセルの製造方法により熱膨張性マイクロカプセルを調製し、その最終工程において、表1に示す配合になるように、固形ワックスを熱膨張性マイクロカプセルに加え、ミキサードライヤーを用いて70℃で乾燥した。これにより、表1に示す表面処理熱膨張性マイクロカプセル(表面処理マイクロカプセル1及び2)を得た。また固形ワックスの代わりにオイルを分散させた水を添加することにより、表面処理マイクロカプセル3を得た。
表1に示す配合からなる3種類の表面処理熱膨張性マイクロカプセル(表面処理マイクロカプセル1〜3)及び熱膨張性マイクロカプセルを用いて、表5に示す配合剤を共通配合とし、表2,3,4に示す配合からなる15種類のタイヤ用ゴム組成物(実施例1〜6、比較例1〜9)を、硫黄、加硫促進剤、熱膨張性マイクロカプセル及び表面処理熱膨張性マイクロカプセルを除く成分を1.8Lの密閉型ミキサーで5分間混練し放出し、これに硫黄、加硫促進剤、熱膨張性マイクロカプセル及び表面処理熱膨張性マイクロカプセルを加えてオープンロールで混練することにより調製した。なお表5に記載した配合剤の量は、表2,3,4に記載したジエン系ゴム100重量部に対する重量部で示した。
得られた加硫ゴム試験片から、JIS K6251に準拠してJIS3号ダンベル型試験片を切り出した。JIS K6251に準拠し100%変形応力(100%モジュラス)を測定した。得られた100%モジュラスを、表2では比較例1の値を100、表3では比較例4の値を100、表4では比較例7の値を100とする指数にして、それぞれの「M100」の欄に示した。この指数値が大きいほど100%モジュラスが大きいことを意味する。
得られた加硫ゴム試験片の動的粘弾性を、東洋精機製作所社製粘弾性スペクトロメーターを用いて、初期歪み10%、振幅±2%、周波数20Hzの条件で、温度60℃におけるtanδを測定した。得られた結果は、表2では比較例1の値を100、表3では比較例4の値を100、表4では比較例7の値を100とする指数にして、それぞれの「tanδ(60℃)」の欄に示した。この指数値が小さいほど60℃のtanδが小さく、発熱性が小さいことを意味する。
得られた加硫ゴム試験片を偏平円柱状の台ゴムに貼り付け、インサイドドラム型氷上摩擦試験機を用いて、測定温度−1.5℃、荷重5.5kg/cm3、ドラム回転速度25km/hの条件で氷上摩擦係数を測定した。得られた氷上摩擦係数を、表2では比較例1の値を100、表3では比較例4の値を100、表4では比較例7の値を100とする指数にして、それぞれの「氷上摩擦性能」の欄に示した。この指数値が大きいほど氷上摩擦力が大きく氷上性能が優れることを意味する。
・固形ワックス:日本精蝋社製OZOACE0038
・オイル:昭和シェル石油社製エキストラクト4号S
・NR:天然ゴム、RSS#3
・BR:ブタジエンゴム、日本ゼオン社製Nipol BR1220
・固形ワックス:大内新興工業社製パラフィンワックス
・マイクロカプセル:上述した製造方法により得られた熱膨張性マイクロカプセル
・表面処理マイクロカプセル1,2,3:上述した製造方法により得られた表1に記載の表面処理熱膨張性マイクロカプセル
・カーボンブラック:東海カーボン社製シースト6
・シリカ:東ソーシリカ社製Nipsil AQ
・カップリング剤:硫黄含有シランカップリング剤、エボニクデグサ社製Si69
・酸化亜鉛:正同化学工業社製酸化亜鉛3種
・ステアリン酸:日油社製ビーズステアリン酸
・老化防止剤−1:精工化学社社製オゾノン6C
・老化防止剤−2:精工化学社社製ノンフレックスRD
・オイル:昭和シェル石油社製エキストラクト4号S
・硫黄:鶴見化学工業社製金華印油入微粉硫黄
・加硫促進剤:大内新興化学工業社製ノクセラーCZ−G
Claims (3)
- ジエン系ゴム100重量部に、熱膨張性マイクロカプセルの表面に常温で固形のパラフィンワックスを被覆した表面処理熱膨張性マイクロカプセルを0.5〜15重量部配合したタイヤ用ゴム組成物。
- 前記表面処理熱膨張性マイクロカプセルが、常温で固形のパラフィンワックスを熱膨張性マイクロカプセルの重量に対し1〜20重量%被覆したことを特徴とする請求項1に記載のタイヤ用ゴム組成物。
- 請求項1又は2に記載のタイヤ用ゴム組成物でトレッド部を形成した空気入りタイヤ。