JP6177175B2 - Dryer canvas for papermaking - Google Patents
Dryer canvas for papermaking Download PDFInfo
- Publication number
- JP6177175B2 JP6177175B2 JP2014069218A JP2014069218A JP6177175B2 JP 6177175 B2 JP6177175 B2 JP 6177175B2 JP 2014069218 A JP2014069218 A JP 2014069218A JP 2014069218 A JP2014069218 A JP 2014069218A JP 6177175 B2 JP6177175 B2 JP 6177175B2
- Authority
- JP
- Japan
- Prior art keywords
- paper
- warp
- dryer canvas
- papermaking
- wire diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、抄紙機のドライパートで使用される抄紙用ドライヤーカンバスに関する。 The present invention relates to a paper making dryer canvas used in a dry part of a paper machine.
紙との接触面積が多い抄紙用ドライヤーカンバス(以下、カンバスとも記す。)は、ピッチカス等の汚れがカンバス表面に付着しやすい。この汚れがカンバス表面に堆積していくと目詰まりによる通気度の低下を招くだけではなく、接触する紙にマーク欠点の発生や汚れが混入し、問題となっている。そこで、従来は、経糸を丸断面のモノフィラメントで構成し、紙への接触を減らす方法や、2/1綾組織のものを1/2綾組織使いにして紙への接触面積を減らすことなどが行われていた。最近は、緯糸の太さを変えてカンバスを製織することで紙への接触点を減らして汚れの付着を少なくしたものが提案されていた(特許文献1〜2)。 In a papermaking dryer canvas (hereinafter also referred to as a canvas) having a large contact area with paper, dirt such as pitch residue tends to adhere to the canvas surface. If this dirt accumulates on the canvas surface, it not only causes a decrease in air permeability due to clogging, but also causes the occurrence of mark defects and dirt on the contacting paper, which is a problem. Therefore, conventionally, the warp is composed of a monofilament having a round cross section to reduce the contact with paper, or the 2/1 twill structure is used with a 1/2 twill structure to reduce the contact area with paper. It was done. Recently, weaving canvases by changing the thickness of the weft has been proposed to reduce the number of contact points to the paper and reduce the adhesion of dirt (Patent Documents 1 and 2).
しかしながら、経糸を扁平断面から丸断面に変更しても汚れ付着はそれほど減少しない。また、特許文献1や特許文献2の記載の発明では、太い緯糸と細い緯糸を用いて紙との接触点を減少させてカンバス表面への汚れの付着を低減させているものの、ヨコ方向がライン状の凸部分となり、ヨコ密度の少ないカンバスについては、凸部分と凸部分の距離が長くなり、部分的に接圧が大きくなることで、凹部分も結果的に紙と接触してしまうことが考えられ、更なる改善が求められている。 However, even when the warp is changed from a flat cross section to a round cross section, the adhesion of dirt does not decrease so much. In the inventions described in Patent Document 1 and Patent Document 2, thick wefts and thin wefts are used to reduce the contact point with paper to reduce the adhesion of dirt to the canvas surface, but the horizontal direction is a line. For a canvas with a convex shape and a low horizontal density, the distance between the convex portion and the convex portion becomes longer and the contact pressure partially increases, so that the concave portion may also come into contact with the paper. It is considered and further improvement is required.
本発明は、上記問題を解決するため、カンバスの接紙面側表面への汚れの付着を低減した抄紙用ドライヤーカンバスを提供する。 In order to solve the above problems, the present invention provides a papermaking dryer canvas in which the adhesion of dirt to the paper contact surface side surface of the canvas is reduced.
本発明は、経糸と緯糸を織成した抄紙用ドライヤーカンバス本体を含む抄紙用ドライヤーカンバスであって、上記抄紙用ドライヤーカンバス本体の接紙面側には線径が太い経糸と線径が細い経糸が配置され、接紙面側における全ての緯糸上には線径が太い経糸によって形成された突出点が存在すし、上記抄紙用ドライヤーカンバス本体の接紙面側において、経糸3本あたりに上記線径が太い経糸1本が規則的に配置されていることを特徴とする抄紙用ドライヤーカンバスに関する。
The present invention is a papermaking dryer canvas including a papermaking dryer canvas body woven with warps and wefts, and a warp yarn having a large wire diameter and a warp yarn having a thin wire diameter are arranged on the paper contact surface side of the papermaking dryer canvas body. is, to be present projecting point diameter is formed by a thick warp threads on all of the weft in contact paper side, the contact paper side of the papermaking drier canvas body, the wire diameter is thick in three per warp The present invention relates to a paper making dryer canvas characterized in that one warp is regularly arranged .
本発明は、抄紙用ドライヤーカンバス本体の接紙面側に線径が太い経糸と線径が細い経糸を配置し、接紙面側における全ての緯糸に線径が太い経糸によって形成された突出点を存在させることにより、抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減することができる。 In the present invention, a warp with a large wire diameter and a warp with a thin wire diameter are arranged on the paper contact surface side of the dryer canvas body for papermaking, and all the wefts on the paper contact surface side have protruding points formed by the warp having a large wire diameter. By doing so, it is possible to reduce the adhesion of dirt to the surface of the paper making dryer canvas on the paper contact surface side.
本発明において、上記抄紙用ドライヤーカンバス本体は経糸と緯糸を織成した織物である。上記抄紙用ドライヤーカンバス本体の接紙面側には線径が太い経糸と線径が細い経糸が配置され、接紙面側における全ての緯糸上には線径が太い経糸によって形成された突出点が存在する。抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、上記抄紙用ドライヤーカンバス本体の接紙面側において、隣接する緯糸上には互いに斜め方向に線径が太い経糸によって形成された突出点が存在することが好ましい。本発明において、「突出点」は、接紙面側をマイクロスコープなどで観察することにより確認することができる。或いは、後述するように、マークテストにより発色点を測定することにより間接的に確認してもよい。 In the present invention, the papermaking dryer canvas body is a woven fabric in which warps and wefts are woven. On the paper contact side of the paper dryer canvas body, a warp with a large wire diameter and a warp with a thin wire diameter are arranged. On all the wefts on the paper contact surface side, there are protruding points formed by the warp with a large wire diameter. To do. From the viewpoint of reducing the adhesion of dirt to the surface of the paper contact surface of the paper making dryer canvas, on the paper contact surface side of the paper making dryer canvas body, formed on the adjacent wefts by warps having a large wire diameter in an oblique direction. It is preferred that there are projected points. In the present invention, the “protrusion point” can be confirmed by observing the paper contact surface side with a microscope or the like. Or you may confirm indirectly by measuring a coloring point by a mark test so that it may mention later.
本発明において、糸の断面形状が円形断面の場合、糸の線径は直径を意味し、糸の断面形状が楕円断面の場合、糸の線径は短径を意味し、糸の断面形状が扁平断面の場合、糸の線径は短辺を意味する。また、本発明において、糸の断面形状が円形断面の場合、糸の巾は直径を意味し、糸の断面形状が楕円断面の場合、糸の巾は長径を意味し、糸の断面形状が扁平断面の場合、糸の巾は長辺を意味する。なお、本発明において、特に指摘がない場合、扁平断面は、楕円断面以外の扁平断面を意味する。 In the present invention, when the cross-sectional shape of the yarn is a circular cross-section, the wire diameter of the yarn means a diameter, and when the cross-sectional shape of the yarn is an elliptical cross-section, the wire diameter of the yarn means a short diameter, and the cross-sectional shape of the yarn is In the case of a flat cross section, the wire diameter of the yarn means a short side. In the present invention, when the cross-sectional shape of the yarn is a circular cross-section, the width of the yarn means a diameter, and when the cross-sectional shape of the yarn is an elliptical cross-section, the width of the yarn means a long diameter, and the cross-sectional shape of the yarn is flat. In the case of a cross section, the width of the thread means the long side. In the present invention, unless otherwise indicated, the flat cross section means a flat cross section other than an elliptical cross section.
上記抄紙用ドライヤーカンバス本体を織成した経糸又は緯糸の断面形状は、特に限定されないが、円形断面、扁平断面及び楕円断面のいずれであってもよい。円形断面の場合、直径が0.2〜1.2mmであることが好ましく、0.4〜0.9mmであることがより好ましい。扁平断面の場合は、長辺(巾)が0.4〜1.2mmであることが好ましく、より好ましくは0.4〜0.7mmであり、短辺(線径)は0.2〜0.8mmであることが好ましく、より好ましくは0.2〜0.6mmである。楕円断面の場合、長径(巾)が0.4〜1.2mmであることが好ましく、より好ましくは0.4〜0.7mmであり、短径(線径)は0.2〜0.8mmであることが好ましく、より好ましくは0.2〜0.6mmである。これにより抄紙用ドライヤーカンバスの表面の均一性を保持しつつ防汚性を向上させることができる The cross-sectional shape of the warp or weft weaving the paper dryer canvas body is not particularly limited, and may be any of a circular cross section, a flat cross section, and an elliptic cross section. In the case of a circular cross section, the diameter is preferably 0.2 to 1.2 mm, and more preferably 0.4 to 0.9 mm. In the case of a flat cross section, the long side (width) is preferably 0.4 to 1.2 mm, more preferably 0.4 to 0.7 mm, and the short side (wire diameter) is 0.2 to 0. 0.8 mm is preferable, and 0.2 to 0.6 mm is more preferable. In the case of an elliptical cross section, the major axis (width) is preferably 0.4 to 1.2 mm, more preferably 0.4 to 0.7 mm, and the minor axis (wire diameter) is 0.2 to 0.8 mm. It is preferable that the thickness is 0.2 to 0.6 mm. This makes it possible to improve the antifouling property while maintaining the uniformity of the surface of the paper making dryer canvas.
上記抄紙用ドライヤーカンバス本体の接紙面側において、表面への汚れの付着を低減する観点から、上記線径が太い経糸の線径は上記線径が細い経糸の線径の1倍超え2倍以下であることが好ましい。具体的には、上記抄紙用ドライヤーカンバス本体の接紙面側において、表面への汚れの付着を低減する観点から、上記線径が太い経糸が円形断面を有する場合、上記線径が太い経糸の線径は上記線径が細い経糸の線径の1倍超え2倍以下であることが好ましい。また、抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、上記線径が太い経糸が扁平断面を有する場合、上記線径が太い経糸の線径は上記線径が細い経糸の線径の1倍超え2倍以下であることが好ましい。また、抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、上記線径が太い経糸が楕円断面を有する場合、上記線径が太い経糸の線径は上記線径が細い線径の1倍超え2倍以下であることが好ましい。 From the viewpoint of reducing the adhesion of dirt to the surface of the papermaking dryer canvas main body, the diameter of the warp with the larger diameter is more than 1 and less than 2 times the diameter of the warp with the smaller diameter. It is preferable that Specifically, on the paper contact side of the papermaking dryer canvas body, from the viewpoint of reducing the adhesion of dirt to the surface, when the warp having a large wire diameter has a circular cross section, the wire of the warp having a large wire diameter is used. The diameter is preferably more than 1 and less than or equal to 2 times the wire diameter of the warp where the wire diameter is thin. In addition, from the viewpoint of reducing the adhesion of dirt to the surface of the paper contacting dryer canvas, when the warp with a large wire diameter has a flat cross section, the wire diameter of the warp with a large wire diameter is It is preferably more than 1 time and less than 2 times the wire diameter of the thin warp. In addition, from the viewpoint of reducing the adhesion of dirt to the surface of the paper contacting dryer canvas, when the warp having a large wire diameter has an elliptical cross section, the wire diameter of the warp having a large wire diameter is It is preferably more than 1 time and less than 2 times the thin wire diameter.
上記抄紙用ドライヤーカンバス本体の接紙面側において、表面への汚れの付着を低減する観点から、上記線径が太い経糸の巾は上記線径が細い経糸の巾の1倍以上2倍以下であることが好ましい。具体的には、上記抄紙用ドライヤーカンバス本体の接紙面側において、表面への汚れの付着を低減する観点から、上記線径が太い経糸が円形断面を有する場合、上記線径が太い経糸の巾は上記線径が細い経糸の巾の1倍以上2倍以下であることが好ましい。また、上記抄紙用ドライヤーカンバス本体の接紙面側において、表面への汚れの付着を低減する観点から、上記線径が太い経糸が扁平断面を有する場合、上記線径が太い経糸の巾は上記線径が細い経糸の巾の1倍以上2倍以下であることが好ましい。また、上記抄紙用ドライヤーカンバス本体の接紙面側において、表面への汚れの付着を低減する観点から、上記線径が太い経糸が楕円断面を有する場合、上記線径が太い経糸の巾は上記線径が細い経糸の巾の1倍以上3倍以下であることが好ましい。 From the viewpoint of reducing the adhesion of dirt on the surface of the papermaking dryer canvas body, the width of the warp with a large wire diameter is 1 to 2 times the width of the warp with a thin wire diameter. It is preferable. Specifically, from the viewpoint of reducing the adhesion of dirt to the surface of the papermaking dryer canvas body, when the warp having a large wire diameter has a circular cross section, the width of the warp having the large wire diameter is The wire diameter is preferably 1 to 2 times the width of the thin warp. In addition, from the viewpoint of reducing the adhesion of dirt on the surface of the papermaking dryer canvas body, when the warp having a large wire diameter has a flat cross section, the width of the warp having a large wire diameter is The diameter is preferably 1 to 2 times the width of the thin warp. In addition, from the viewpoint of reducing the adhesion of dirt to the surface of the papermaking dryer canvas main body, when the warp having a large wire diameter has an elliptical cross section, the width of the warp having a large wire diameter is The diameter is preferably 1 to 3 times the width of the thin warp.
上記抄紙用ドライヤーカンバス本体の接紙面側において、上記線径が太い経糸の本数及び配置は特に限定されず、例えば、上記線径が太い経糸は経糸32本あたり1〜31本配置することができる。抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、上記抄紙用ドライヤーカンバス本体の接紙面側において、経糸3本あたりに線径が太い経糸1本を規則的に配置することが好ましい。 The number and arrangement of the warp yarns having a large wire diameter are not particularly limited on the paper-contacting surface side of the papermaking dryer canvas body. . From the viewpoint of reducing the adhesion of dirt to the surface of the paper contacting side of the paper making dryer canvas, one warp with a large wire diameter is regularly arranged for every 3 warps on the paper contacting side of the paper making dryer canvas body. It is preferable to do.
上記抄紙用ドライヤーカンバス本体の接紙面側において、抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、経糸3本あたりに線径が太い経糸1本を規則的に配置した場合、隣接する緯糸上には互いに斜め方向に線径が太い経糸によって形成された突出点が存在することが好ましい。また、抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、同じ緯糸上の隣接する突出点(線径の太い経糸によって形成された)間の距離が0.8mm以上7mm以下であることが好ましく、より好ましくは2mm以上6mm以下である。また、抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、同じ経糸上の隣接する突出点(線径の太い経糸によって形成された)間の距離は1.6mm以上6mm以下であることが好ましく、より好ましくは2.2mm以上3.4mm以下である。上記抄紙用ドライヤーカンバス本体の接紙面側において、上記突出点による突出量は、抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、0mmを超え1.0mm以下であることが好ましく、より好ましくは0mmを超え0.5mm以下である。 In order to reduce the adhesion of dirt to the surface of the paper-making dryer canvas on the paper-contacting side of the paper-making dryer canvas body, one warp with a large wire diameter is regularly arranged per three warps. In this case, it is preferable that protruding points formed by warps having a large wire diameter in an oblique direction exist on adjacent wefts. Also, from the viewpoint of reducing the adhesion of dirt to the surface of the paper contacting dryer canvas, the distance between adjacent protruding points on the same weft (formed by thick warps) is 0.8 mm or more It is preferably 7 mm or less, and more preferably 2 mm or more and 6 mm or less. In addition, the distance between adjacent protruding points on the same warp (formed by a thick warp) is 1.6 mm or more from the viewpoint of reducing the adhesion of dirt to the surface of the paper contacting dryer canvas. It is preferably 6 mm or less, more preferably 2.2 mm or more and 3.4 mm or less. On the paper contact surface side of the papermaking dryer canvas body, the protrusion amount due to the protrusion point is more than 0 mm and 1.0 mm or less from the viewpoint of reducing the adhesion of dirt to the surface of the papermaking dryer canvas on the paper contact surface side. More preferably, it is more than 0 mm and 0.5 mm or less.
上記抄紙用ドライヤーカンバス本体を織成した経糸又は緯糸の素材は、特に限定されず、ポリエチレンテレフタレート等のポリエステル、ポリアミド、ポリフェニレンサルファイド、ポリエーテルエーテルケトン等からなる群から選ばれる一種以上の合成樹脂であることが好ましく、耐久性の観点から、ポリエチレンテレフタレート等のポリエステルを含むことがより好ましい。また、経糸又は緯糸とも合成樹脂からなるモノフィラメント糸、合成樹脂からなるマルチフィラメント糸等を用いることができる。また、本発明において、接合用芯線としては、経糸又は緯糸と同様の素材のモノフィラメント糸、マルチフィラメント糸等を用いることができる。 The material of the warp or weft weaving the paper dryer canvas body is not particularly limited, and is one or more synthetic resins selected from the group consisting of polyesters such as polyethylene terephthalate, polyamides, polyphenylene sulfide, polyether ether ketone, and the like. It is preferable to include polyester such as polyethylene terephthalate from the viewpoint of durability. In addition, a monofilament yarn made of a synthetic resin, a multifilament yarn made of a synthetic resin, or the like can be used for both the warp and the weft. In the present invention, as the bonding core wire, a monofilament yarn, a multifilament yarn, or the like made of the same material as the warp or weft can be used.
本発明において、抄紙用ドライヤーカンバス本体の単位長さあたりの糸の本数(密度)は、特に限定されないが、経糸が8〜130本/2.54cmであることが好ましく、より好ましくは40〜130本/2.54cmである。緯糸は、8〜80本/2.54cmであることが好ましく、より好ましくは30〜60本/2.54cmである。これにより抄紙用ドライヤーカンバス本体の表面の均一性を保持しつつ防汚性を向上させることができる。 In the present invention, the number (density) of yarns per unit length of the dryer canvas body for papermaking is not particularly limited, but is preferably 8 to 130 warps / 2.54 cm, more preferably 40 to 130. Book / 2.54 cm. The weft is preferably 8 to 80 pieces / 2.54 cm, more preferably 30 to 60 pieces / 2.54 cm. Thus, the antifouling property can be improved while maintaining the uniformity of the surface of the papermaking dryer canvas body.
上記抄紙用ドライヤーカンバス本体は、一重織であってもよく、二重織以上の多重織であってもよい。また、織組織も特に限定されず、例えば、平織、綾織、朱子織、及び変織等のその他の組織、並びにこれらの組合せのいずれであってもよい。具体的には、図8に列挙した織組織とすることができる。図8Aは平織組織(ヨコ一重織り)の緯糸方向の断面模式図であり、図8Bは1/2綾組織(ヨコ一重織り)の緯糸方向の断面模式図であり、図8Cは1/2綾組織(ヨコ二重織り)の緯糸方向の断面模式図であり、図8Dはヨコ三重織り組織の緯糸方向の断面模式図であり、図8Eは2/1綾組織(ヨコ一重織り)の緯糸方向の断面模式図であり、図8Fは2/1綾組織(ヨコ二重織り)の緯糸方向の断面模式図であり、図8Gは2/2綾組織(ヨコ一重織り)の緯糸方向の断面模式図であり、図8Hは1/3綾組織(ヨコ一重織り)の緯糸方向の断面模式図であり、図8Iはヨコ二重織り組織の緯糸方向の断面模式図であり、図8Jは3/1綾2層組織(ヨコ一重織り)の緯糸方向の断面模式図であり、図8Kは3/1綾組織(ヨコ一重織り)の緯糸方向の断面模式図である。 The papermaking dryer canvas body may be a single weave or a multi-weave of double or more. Further, the woven structure is not particularly limited, and may be any other structure such as plain weave, twill weave, satin weaving, and change in weaving, and combinations thereof. Specifically, the woven structures listed in FIG. 8 can be used. 8A is a schematic cross-sectional view in the weft direction of a plain weave structure (horizontal single weave), FIG. 8B is a schematic cross-sectional view in the weft direction of a 1/2 weave structure (horizontal single weave), and FIG. FIG. 8D is a schematic cross-sectional view in the weft direction of the structure (horizontal double weave), FIG. 8D is a schematic cross-sectional view in the weft direction of the horizontal triple weave structure, and FIG. 8E is the weft direction in the 2/1 twill structure (horizontal single weave). 8F is a schematic cross-sectional view in the weft direction of a 2/1 twill structure (horizontal double weave), and FIG. 8G is a schematic cross-sectional view in the weft direction of a 2/2 twill structure (horizontal single weave). 8H is a schematic cross-sectional view in the weft direction of a 1/3 twill structure (horizontal single weave), FIG. 8I is a schematic cross-sectional view in the weft direction of a horizontal double weave structure, and FIG. FIG. 8K is a schematic cross-sectional view in the weft direction of a 1 twill 2 layer structure (horizontal single weave), and FIG. 8K shows a 3/1 twill structure (horizontal single weave). It is a cross-sectional schematic view of a weft direction Ri).
上記抄紙用ドライヤーカンバスは、特に限定されないが、例えば、経糸と緯糸を織成した抄紙用ドライヤーカンバス本体の端部から緯糸を除去することにより露出した経糸の一部を折り返して、上記抄紙用ドライヤーカンバス本体の両端を連結する継手部を構成するループを形成し、通常の手法でワープループシーム構造やスパイラルシーム構造の継手部を作製することができる。 The paper-making dryer canvas is not particularly limited. For example, a part of the warp yarn exposed by removing the weft from the end of the paper-making dryer canvas main body woven with warp and weft is folded, and the paper-making dryer canvas is used. A loop constituting a joint portion connecting both ends of the main body is formed, and a joint portion having a warp loop seam structure or a spiral seam structure can be produced by a normal method.
以下、図面を参照しながら、本発明の抄紙用ドライヤーカンバスについて詳細に説明する。但し、本発明は、以下の実施形態に限定されるものではない。 Hereinafter, a paper making dryer canvas of the present invention will be described in detail with reference to the drawings. However, the present invention is not limited to the following embodiments.
図1Aは本発明の一実施形態の抄紙用ドライヤーカンバスの接紙面側の表面模式図であり、図1Bは同抄紙用ドライヤーカンバスの緯糸方向の断面模式図である。図1A及び図1Bに示しているように、抄紙用ドライヤーカンバス本体1は、線径が太い経糸11aと線径が細い経糸11b、及び緯糸12を織成したものであり、接紙面側において経糸3本あたりに線径が太い経糸11aが1本規則的に配置されている。図1A及び図1Bに示しているように、抄紙用ドライヤーカンバス本体1の接紙面側の全ての緯糸上において、線径が太い経糸11aは突出点を形成しており、隣接する緯糸上には互いに斜め方向に線径が太い経糸によって形成された突出点が存在する。該実施形態の抄紙用ドライヤーカンバスの接紙面側において、同じ緯糸上の隣接する突出点(線径の太い経糸によって形成された)間の距離が0.8mm以上7mm以下であることが好ましく、より好ましくは2mm以上6mm以下である。また、同じ経糸上の隣接する突出点(線径が線径の太い経糸によって形成された)間の距離は1.6mm以上6mm以下であることが好ましく、より好ましくは2.2mm以上3.4mm以下である。該実施形態の抄紙用ドライヤーカンバス本体の接紙面側において、上記突出点による突出量は、抄紙用ドライヤーカンバスの接紙面側の表面への汚れの付着を低減する観点から、0mmを超え1.0mm以下であることが好ましく、より好ましくは0mmを超え0.5mm以下である。
FIG. 1A is a schematic view of the surface of the paper-making dryer canvas of the embodiment of the present invention on the paper contact surface side, and FIG. 1B is a schematic cross-sectional view in the weft direction of the paper-making dryer canvas. As shown in FIGS. 1A and 1B, the papermaking dryer canvas body 1 is made by weaving a
本発明の抄紙用ドライヤーカンバス本体の接紙面側において、表面への汚れの付着を低減するという観点から、マークテストによって測定した場合、150mm2あたり発色点が7個以上315個以下存在することが好ましく、10個以上120個以下存在することがより好ましく、10個以上62個以下存在することがさらに好ましく、12個以上20個以下存在することが特に好ましい。本発明において、マークテストは、後述するとおりに行う。なお、マークテストによって測定した発色点は、抄紙用ドライヤーカンバス本体の接紙面側の表面と紙との接触点を評価するものである。 From the viewpoint of reducing the adhesion of dirt to the surface of the papermaking dryer canvas body of the present invention, there may be 7 or more and 315 or less coloring points per 150 mm 2 when measured by a mark test. It is preferably 10 or more and 120 or less, more preferably 10 or more and 62 or less, and particularly preferably 12 or more and 20 or less. In the present invention, the mark test is performed as described later. The color development point measured by the mark test evaluates the contact point between the paper-contacting surface of the papermaking dryer canvas body and the paper.
本発明において、180度テープ剥離試験は、JIS K 6854に準じ、後述するとおりに行う。なお、本発明において、テープ剥離強力は、カンバス表面への汚れの付着しにくさ、すなわち防汚性能を評価しており、テープ剥離強力が低いほど、カンバス表面への汚れの付着しにくく、防汚性能が高いことを意味する。 In this invention, a 180 degree | times tape peeling test is performed as it mentions later according to JISK6854. In the present invention, the tape peeling strength is evaluated as being less likely to adhere dirt on the canvas surface, that is, antifouling performance. The lower the tape peeling strength, the less likely dirt adheres to the canvas surface. Means high dirt performance.
以下、実施例に基づいて本発明を詳細に説明する。但し、本発明は、下記の実施例に限定されるものではない。 Hereinafter, the present invention will be described in detail based on examples. However, the present invention is not limited to the following examples.
(実施例1)
経糸11aとしてポリエチレンテレフタレート(PET)モノフィラメント(繊度3370dtex、扁平断面、線径(短辺、以下同様)0.44mm、巾(長辺、以下同様)0.57mm)を、経糸11bとしてポリエチレンテレフタレート(PET)モノフィラメント(繊度2830dtex、扁平断面、線径0.38mm、長辺0.57mm)を、緯糸12としてポリエチレンテレフタレート(PET)モノフィラメント(繊度6950dtex、円形断面、直径0.80mm)を用い、図1A及び図1Bに示すように、接紙面側において、経糸3本あたりに経糸11aが1本になるように経糸11aと経糸11bを規則的に配置し、1/2綾組織(ヨコ二重織り)の抄紙用ドライヤーカンバス本体1を作製した。織物の単位長さあたりの糸の本数(密度)は、経糸は48.3本/2.54cmとし、緯糸は、接紙面側と機械面側のいずれも30.7本/2.54cmとした。実施例1のカンバスの接紙面側において、同じ緯糸上の隣接する突出点間の距離は6.23mmであり、同じ経糸上の隣接する突出点間の距離は5.80mmであった。実施例1のカンバスの接紙面側において、隣接する緯糸上における突出点は互いに斜め方向に存在していた。
Example 1
Polyethylene terephthalate (PET) monofilament (fineness: 3370 dtex, flat cross section, wire diameter (short side, same below) 0.44 mm, width (long side, same below) 0.57 mm) as
(比較例1)
経糸21としてポリエチレンテレフタレート(PET)モノフィラメント(繊度2830dtex、扁平断面、線径0.38mm、巾0.57mm)を、緯糸22としてポリエチレンテレフタレート(PET)モノフィラメント(繊度6950dtex、円形断面、直径0.80mm)を用い、図2A及び図2Bに示す1/2綾組織(ヨコ二重織り)の抄紙用ドライヤーカンバス本体2を作製した。織物の単位長さあたりの糸の本数(密度)は、経糸は48.3本/2.54cmとし、緯糸は、接紙面側と機械面側のいずれも33.4本/2.54cmとした。
(Comparative Example 1)
Polyethylene terephthalate (PET) monofilament (fineness 2830 dtex, flat cross section, wire diameter 0.38 mm, width 0.57 mm) as
(比較例2)
経糸31としてポリエチレンテレフタレート(PET)モノフィラメント(繊度2830dtex、扁平断面、線径0.38mm、巾0.57mm)を、緯糸32aとしてポリエチレンテレフタレート(PET)モノフィラメント(繊度10960dtex、円形断面、直径1.0mm)を、緯糸32bとしてポリエチレンテレフタレート(PET)モノフィラメント(繊度6950dtex、円形断面、直径0.80mm)を用い、図3A及び図3Bに示すように、緯糸22aと緯糸22bを交互に配置し、1/2綾組織(ヨコ二重織り)の抄紙用ドライヤーカンバス本体3を作製した。織物の単位長さあたりの糸の本数(密度)は、経糸は48.1本/2.54cmとし、緯糸は、接紙面側と機械面側のいずれも30.9本/2.54cmとした。
(Comparative Example 2)
Polyethylene terephthalate (PET) monofilament (fineness 2830 dtex, flat cross section, wire diameter 0.38 mm, width 0.57 mm) as
(比較例3)
経糸41aとしてポリエチレンテレフタレート(PET)モノフィラメント(繊度3370dtex、扁平断面、線径0.44mm、巾0.57mm)を、経糸41bとしてポリエチレンテレフタレート(PET)モノフィラメント(繊度2830dtex、扁平断面、線径0.38mm、巾0.57mm)を、緯糸12としてポリエチレンテレフタレート(PET)モノフィラメント(繊度6950dtex、円形断面、直径0.80mm)を用い、図4A及び図4Bに示すように、接紙面側において、経糸4本あたりに経糸41aが2本になるように経糸41aと経糸41bを規則的に配置し、1/2綾組織(ヨコ二重織り)の抄紙用ドライヤーカンバス本体4を作製した。織物の単位長さあたりの糸の本数(密度)は、経糸は48.3本/2.54cmとし、緯糸は、接紙面側と機械面側のいずれも30.6本/2.54cmとした。
(Comparative Example 3)
Polyethylene terephthalate (PET) monofilament (fineness 3370 dtex, flat cross section, wire diameter 0.44 mm, width 0.57 mm) as the
実施例及び比較例の抄紙用ドライヤーカンバス本体の厚み及び接紙面側の突出量を下記のように測定し、その結果を下記表1に示した。また、実施例及び比較例の抄紙用ドライヤーカンバス本体の接紙面側の表面と紙との接触点をマークテストで評価し、その結果を図5A〜5D、及び表1に示した。さらに、実施例及び比較例の抄紙用ドライヤーカンバス本体を用い、180度テープ剥離試験で抄紙用ドライヤーカンバス本体の接紙面側の表面におけるテープ剥離強力を測定し、その結果を表1に示した。テープ剥離強力によりカンバス表面への汚れの付着しにくさ、すなわち防汚性能を評価しており、テープ剥離強力が低いほど、カンバス表面へ汚れが付着しにくく、防汚性能が高いことを意味する。 The thickness of the dryer canvas body for papermaking in Examples and Comparative Examples and the protruding amount on the paper contact surface side were measured as follows, and the results are shown in Table 1 below. Moreover, the contact point of the paper contact surface side of the papermaking dryer canvas main body of the examples and comparative examples and the paper was evaluated by a mark test, and the results are shown in FIGS. 5A to 5D and Table 1. Furthermore, using the papermaking dryer canvas main body of Examples and Comparative Examples, the tape peeling strength on the surface of the papermaking dryer canvas main body on the paper contact surface side was measured by a 180-degree tape peeling test, and the results are shown in Table 1. Evaluates the difficulty of soiling on the canvas surface due to the tape peeling strength, that is, the antifouling performance. The lower the tape peeling strength, the harder it is to adhere to the canvas surface and the higher the antifouling performance. .
(厚み及び接紙面側の突出量)
抄紙用ドライヤーカンバス本体の厚み及び接紙面側の突出量は、マイクロスコープ(株式会社ハイロックス製、品名「ハイスコープアドバンスト」、型番「KH−3000V/VD」)を用いて測定した。接紙面側の突出量は、図1B、図3B及び図4Bにおいて、点線Iと点線II間の距離を測定することで得られた。
(Thickness and protruding amount on the paper contact side)
The thickness of the dryer canvas body for papermaking and the protruding amount on the paper contact surface side were measured using a microscope (manufactured by Hilox, product name “Hiscope Advanced”, model number “KH-3000V / VD”). The amount of protrusion on the paper contact surface side was obtained by measuring the distance between dotted line I and dotted line II in FIGS. 1B, 3B and 4B.
(マークテスト)
抄紙用ドライヤーカンバス本体を幅100mm、長さ500mmに切って、マークテスト用サンプル50として用いた。図6に示しているように、マークテスト用サンプル50の接紙面側の表面上にマークテスト用サンプルと同じ大きさに切った超低圧用プレスケール60(富士フィルム社製、超低圧用ツーシートタイプ「LLW」)を超低圧用プレスケール60の発色側がマークテスト用サンプル50と接触するように配置し、マークテスト用サンプル50とプレスケール60を重ねてローラー70a、70bの間に矢印90で示す方向で通した。ローラー70aには矢印80で示す方向で2kgf/cmの線圧を掛けた。超低圧用プレスケール60の発色側における発色点が抄紙用ドライヤーカンバスの接紙面側の表面と紙との接触点を示すことになる。
(Mark test)
A papermaking dryer canvas body was cut into a width of 100 mm and a length of 500 mm, and used as a
(180度テープ剥離試験)
JIS K 6854に準じて180度テープ剥離試験を行った。抄紙用ドライヤーカンバス本体を裁断し、図7Aに示すように巾(W1)が70mm、長さ(L1)が125mmの剥離試験用サンプル100を得た。剥離試験用サンプル100の接紙面側に、長手方向の端部から長さ(La)80mmにわたり、巾(W2)50mmの透明粘着テープ200(ニチバン株式会社製、ポリエステルテープ、長さ(L2)180mm)をマークテスト用ローラー機(ダイワボウプログレス社製)にて貼り付けた。透明粘着テープ200の貼り付けは、図示はないが、上下二段のローラーで剥離試験用サンプル100と透明粘着テープ200を一定荷重(線圧7.8kg/cm)にて挟み込みながらローラー間を3回通過させ、図7Bに示すように剥離試験用サンプル100と透明粘着テープ200を接着させた。図7B及び図7Cに示すように、透明粘着テープ200の剥離試験用サンプル100と貼り付けた端部とは反対側の端部はチャックの挟みしろとして長さ45mmを残し、つかみ部として巾(W3)60mm、長さ(L3)90mm程度の紙300を張り付け、180°折り返して置いた。透明粘着テープ200を張り付けた剥離試験用サンプル100はテンシロン引張試験機(オリエンテック社製、型番「RTC1310A」)にて、上下が長手方向となるようチャックでつかみ、つかみ間距離は100mm、引張速度200mm/min、テープ引きはがし距離を50mmとしてテープの引きはがし強力を計測した。テープの引きはがし強力を積分平均し、テープ剥離強力とした。
(180 degree tape peeling test)
A 180 degree tape peeling test was conducted according to JIS K 6854. The papermaking dryer canvas body was cut to obtain a
表1の結果から分かるように、接紙面側の経糸の線径が一定である比較例1〜2に比べて、接紙面側に線径が太い経糸と線径が細い経糸を配置し、接紙面側における全ての緯糸上には線径が太い経糸によって形成された突出点が存在する実施例1の方が、テープ剥離強力が小さい。これは、カンバス表面へ汚れが付着しにくく、防汚性能が高かったことを意味する。また、比較例3に比べても、実施例1の方が、テープ剥離強力が小さい。これもカンバス表面へ汚れが付着しにくく、防汚性能が高いことを意味する。これらは、実施例1のカンバスが、比較例1〜3のカンバスより、接紙面側の表面と紙との接触点が少ないことに起因すると思われる。なお、比較例3の場合、接紙面側に線径が太い経糸と線径が細い経糸を配置しているが、接紙面側における一部の緯糸上には線径が太い経糸によって形成された突出点が存在しないため、ヨコ方向に凹部によるラインが生じ、図5Dに示しているように、凹部も接触点の大きさは小さいが紙に接触することになっている。 As can be seen from the results in Table 1, compared to Comparative Examples 1 and 2 in which the warp yarn diameter on the paper contact surface side is constant, a warp yarn having a large wire diameter and a warp yarn having a thin wire diameter are disposed on the paper contact surface side, The tape peeling strength is smaller in Example 1 in which protruding points formed by warps having a large wire diameter exist on all the wefts on the paper surface side. This means that stains hardly adhere to the canvas surface and the antifouling performance was high. Also, compared with Comparative Example 3, Example 1 has a smaller tape peeling strength. This also means that dirt hardly adheres to the canvas surface, and the antifouling performance is high. These are considered to be due to the fact that the canvas of Example 1 has fewer contact points between the paper contact surface and the paper than the canvases of Comparative Examples 1 to 3. In the case of Comparative Example 3, a warp with a large wire diameter and a warp with a thin wire diameter are arranged on the paper contact surface side, but a part of the weft on the paper contact surface side is formed by a warp with a large wire diameter. Since there is no protruding point, a line due to the concave portion is formed in the horizontal direction. As shown in FIG. 5D, the concave portion is also in contact with the paper although the size of the contact point is small.
1、2、3、4 抄紙用ドライヤーカンバス本体
11a、11b、21、31、41a、41b 経糸
12、22、32a、32b、42 緯糸
50 マークテスト用サンプル
60 プレスケール
70a、70b ローラー
100 剥離試験用サンプル
200 透明粘着テープ
300 紙
1, 2, 3, 4 Papermaking
Claims (6)
前記抄紙用ドライヤーカンバス本体の接紙面側には線径が太い経糸と線径が細い経糸が配置され、接紙面側における全ての緯糸上には線径が太い経糸によって形成された突出点が存在し、
前記抄紙用ドライヤーカンバス本体の接紙面側において、経糸3本あたりに前記線径が太い経糸1本が規則的に配置されていることを特徴とする抄紙用ドライヤーカンバス。 A papermaking dryer canvas comprising a papermaking dryer canvas body woven with warps and wefts,
A thick warp and a thin warp are arranged on the paper contact side of the paper dryer canvas main body, and all the wefts on the paper contact surface have protruding points formed by the warp having a large wire diameter. And
1. A papermaking dryer canvas characterized in that, on the paper contacting surface side of the papermaking dryer canvas body, one warp with a large wire diameter is regularly arranged for every three warps .