JP6019942B2 - 樹脂組成物、繊維集束剤及び成形品 - Google Patents
樹脂組成物、繊維集束剤及び成形品 Download PDFInfo
- Publication number
- JP6019942B2 JP6019942B2 JP2012191518A JP2012191518A JP6019942B2 JP 6019942 B2 JP6019942 B2 JP 6019942B2 JP 2012191518 A JP2012191518 A JP 2012191518A JP 2012191518 A JP2012191518 A JP 2012191518A JP 6019942 B2 JP6019942 B2 JP 6019942B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- mass
- sizing agent
- parts
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記繊維強化プラスチックに使用する炭素繊維やガラス繊維としては、通常、高強度を付与する観点から、繊維集束剤によって概ね数千〜数万程度に集束された繊維材料を使用することが多い。
また、本発明は、引張強度をはじめとする強度に優れた成形品を提供することである。
また、前記繊維集束剤を用いて集束した繊維とマトリックス樹脂とを含む成形品は、引張した場合や屈曲した場合、強い衝撃を受けた場合であっても、割れ等を引きこさないレベルの機械的強度を備えた繊維強化プラスチックをはじめとする成形品を製造できる。かかる成形品は、例えば自動車や航空機の部材、家電製品の部品や風力発電部材をはじめとする様々な用途で使用することができる。
前記アクリル樹脂(A)としては、ポリオキシアルキレン構造とグリシジル基とを組み合わせ有するものを使用する。
ここで、前記アクリル樹脂(A)の代わりに、ポリオキシアルキレン構造を有さないアクリル樹脂を使用した場合、前記樹脂組成物の保存安定性が低下や、ガラス繊維や炭素繊維の集束性の低下や、最終的に得られる成形品の強度の低下等を引き起こす場合がある。
また前記アクリル樹脂(A)の代わりに、グリシジル基を有さないアクリル樹脂を使用した場合、最終的に得られる成形品の強度の低下等を引き起こす場合がある。
前記ポリオキシアルキレン構造としては、アクリル樹脂(A)の良好な水分散安定性と、優れた集束性や成形品の高強度化との両立を図るうえで、オキシエチレン構造を有するものであることが好ましい。
前記ポリオキシアルキレン構造としては、例えばポリオキシエチレン構造や、ポリオキシエチレンとポリオキシプロピレンとから構成される共重合体からなるポリオキシエチレン−ポリオキシプロピレン構造、ポリオキシエチレンとポリオキシブチレンとから構成される共重合体からなるポリオキシエチレン−ポリオキシブチレン構造、ポリオキシエチレンとポリオキシテトラメチレンとから構成される共重合体からなるポリオキシエチレン−ポリオキシテトラメチレン構造や、それらの末端に存在し得る水酸基がアルキル基等によって封止された構造等が挙げられる。
また、前記ポリオキシアルキレン構造は、オキシエチレン単位と、その他のオキシアルキレン単位とからなるランダム構造であってもよいが、アクリル樹脂(A)の良好な水分散安定性と、優れた集束性や成形品の高強度化との両立を図るうえで、ポリオキシエチレンと、その他のポリオキシアルキレンとから構成されるブロック構造であることが好ましい。
前記ポリオキシアルキレン構造は、前記アクリル樹脂(A)の全量に対して5質量%〜40質量%の範囲で存在することが好ましい。また、前記ポリオキシアルキレン構造は、前記アクリル樹脂(A)の良好な水分散安定性と、優れた集束性や成形品の高強度化との両立を図るうえで、前記ポリオキシアルキレン構造の全体に対して、75質量%〜100質量%の範囲のポリオキシエチレン構造を有するものであることが好ましい。
また、前記アクリル樹脂(A)が有するグリシジル基は、炭素繊維等の優れた集束性と成形品の高強度化との両立を図るうえで、前記アクリル樹脂(A)全体に対して200g/当量〜1500g/当量の範囲で存在することが好ましい。
前記アクリル樹脂(A)としては、より一層優れた強度を備えた成形品を得るうえで、5,000〜150,000の範囲の重量平均分子量を有するものを使用することが好ましい。なお、前記重量平均分子量はゲル浸透クロマトグラフィー(GPC)を用いて測定された値を指す。
前記アクリル樹脂(A)は、例えばポリオキシアルキレン構造を有する(メタ)アクリル単量体とグリシジル基を有する(メタ)アクリル単量体とを含有する重合性不飽和二重結合を有する単量体混合物(a)を、ラジカル重合することによって製造することができる。なお、本発明において「(メタ)アクリル」の表記は、「アクリル」及び「メタクリル」のいずれか一方または両方を表すものである。
前記ポリオキシアルキレン構造を有する(メタ)アクリル単量体としては、例えば(メタ)アクリル酸または(メタ)アクリル酸エステルと、ポリオキシアルキレングリコールとをエステル化反応して得られるものや、(メタ)アクリル酸または(メタ)アクリル酸エステルと、ポリオキシアルキレンモノアルキルエーテルとをエステル化反応して得られるもの等を使用することができる。
具体的には、前記ポリオキシアルキレン構造を有する(メタ)アクリル単量体としては、メトキシポリオキシエチレングリコール(メタ)アクリレート、メトキシ(ポリオキシエチレン−ポリオキシプロピレン)グリコール(メタ)アクリレート、メトキシ(ポリオキシエチレン−ポリオキシテトラメチレン)グリコール(メタ)アクリレート等を使用することができる。なかでもメトキシポリオキシエチレングリコール(メタ)アクリレートを使用することが、アクリル樹脂(A)の良好な水分散安定性と、優れた集束性や成形品の高強度化との両立を図ることが可能な樹脂組成物を得るうえで好ましい。
前記ポリオキシアルキレン構造を有する(メタ)アクリル単量体は、前記単量体混合物(a)の全量に対して10〜40質量%の範囲で使用することが、前記した所定量のポリオキシアルキレン構造をアクリル樹脂(A)に導入し、その結果、アクリル樹脂(A)の良好な水分散安定性と、優れた集束性や成形品の高強度化との両立を図ることが可能な樹脂組成物を得るうえで好ましい。
また、前記グリシジル基を有する(メタ)アクリル単量体としては、例えば(メタ)アクリル酸グリシジル等を使用することができる。
前記グリシジル基を有する(メタ)アクリル単量体は、前記単量体混合物(a)の全量に対して10〜70質量%の範囲で使用することが、前記した所定量のグリシジル基をアクリル樹脂(A)に導入し、その結果、優れた集束性や成形品の高強度化とを付与可能な樹脂組成物を得るうえで好ましい。
前記ポリオキシアルキレン構造を有する(メタ)アクリル単量体と前記グリシジル基を有する(メタ)アクリル単量体とは、その質量割合[前記ポリオキシアルキレン構造を有する(メタ)アクリル単量体/前記グリシジル基を有する(メタ)アクリル単量体]が0.1〜4となる範囲で使用することが、前記アクリル樹脂(A)の良好な水分散安定性と、優れた集束性や成形品の高強度化との両立を図るうえで好ましい。
前記アクリル樹脂(A)の製造に使用可能な単量体混合物(a)は、前記したポリオキシアルキレン構造を有する(メタ)アクリル単量体及びグリシジル基を有する(メタ)アクリル単量体の他に、必要に応じてその他の重合性不飽和二重結合を有する単量体を使用することができる。
前記その他の重合性不飽和二重結合を有する単量体としては、例えば(メタ)アクリル酸アルキルエステルを使用することができる。
前記(メタ)アクリル酸アルキルエステルとしては、例えば(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸プロピル、(メタ)アクリル酸n−ブチル、(メタ)アクリル酸シクロヘキシル、(メタ)アクリル酸2−エチルヘキシル、(メタ)アクリル酸ラウリル、(メタ)アクリル酸ステアリル等を使用することができる。なかでも、より一層優れた集束性と強度を備えた成形品を得る観点から、炭素原子数1〜8のアルキル基を有する(メタ)アクリル酸アルキルエステルを使用することが好ましい。
前記(メタ)アクリル酸エステルは、前記単量体混合物(a)の全量に対して、0質量%〜80質量%の範囲で使用することが好ましく、2質量%〜40質量%の範囲で使用することがより好ましい。
また、前記その他の単量体としては、例えばスチレン、α−メチルスチレン、パラメチルスチレン、クロロメチルスチレン、酢酸ビニル等のビニル単量体を使用することができる。
また、前記その他の単量体としては、例えば(メタ)アクリル酸2−ヒドロキシプロピル、(メタ)アクリル酸4−ヒドロキブチル、(メタ)アクリル酸テトラヒドロフルフリル、(メタ)アクリル酸イソボルニル、(メタ)アクリル酸ベンジル、(メタ)アクリル酸2−ヒドロキシブチル、(メタ)アクリル酸グリシジル、(メタ)アクリル酸、ジ(メタ)アクリル酸ジエチレングリコール、ジ(メタ)アクリル酸−1,4−ブタンジオール、ジ(メタ)アクリル酸−1,6−ヘキサンジオール、トリ(メタ)アクリル酸トリメチロールプロパン、ジ(メタ)アクリル酸グリセリン、等を使用することができる。
本発明の樹脂組成物は、良好な塗工作業性等を付与する観点から、前記樹脂組成物の全量に対して前記アクリル樹脂(A)を2質量%〜80質量%の範囲で含有するものを使用することが好ましく、5質量%〜70質量%の範囲で含有するものを使用することがより好ましい。
また、前記樹脂組成物は、良好な塗工作業性等を付与する観点から、前記樹脂組成物の全量に対して前記水性媒体(B)を15質量%〜95質量%の範囲で含有するものを使用することが好ましく、25質量%〜90質量%の範囲で含有するものを使用することがより好ましい。
また、前記ガラス繊維としては、含アルカリガラス、低アルカリガラス、無アルカリガラス等を用いて形成されるガラス繊維を使用することができる。
攪拌機、還流冷却管、温度計および窒素吹き込み管を備えた4つ口フラスコにメチルエチルケトン45質量部、NKエステルM−230G(新中村化学工業株式会社製、メトキシポリエチレングリコールメタクリレート)30質量部を仕込み80℃に昇温した。
次いで、メタクリル酸グリシジル50質量部、スチレン10質量部、メタクリル酸n−ブチル10質量部、メチルエチルケトン15質量部、V−59(和光純薬工業株式会社製の触媒、2,2’−アゾビス(2-メチルブチロニトリル)1.6質量部の溶解混合物を2時間かけて滴下し、80℃〜85℃の範囲で反応を行った。
メタクリル酸グリシジルの使用量を50質量部から8質量部に変更し、スチレンの使用量を10質量部から20質量部に変更し、かつ、メタクリル酸n−ブチル10質量部の代わりにアクリル酸2−エチルヘキシルを42質量部使用すること以外は、実施例1と同様の方法で、重量平均分子量4.5万のビニル重合体を含む樹脂組成物からなる炭素繊維集束剤(II)〔不揮発分23重量%〕を得た。
メタクリル酸グリシジルの使用量を50質量部から75質量部に変更し、スチレンの使用量を10質量部から0質量部に変更し、かつ、メタクリル酸n−ブチルの使用量を10質量部から5質量部に変更し、かつ、NKエステルM−230G(新中村化学工業株式会社製、メトキシポリエチレングリコールメタクリレート)の使用量を30質量部から20質量部に変更したこと以外は、実施例1と同様の方法で、重量平均分子量2.5万のビニル重合体を含む樹脂組成物からなる炭素繊維集束剤(III)〔不揮発分23重量%〕を得た。
メタクリル酸グリシジルの使用量を50質量部から40質量部に変更し、スチレンの使用量を10質量部から5質量部に変更し、かつ、NKエステルM−230G(新中村化学工業株式会社製、メトキシポリエチレングリコールメタクリレート)の使用量を30質量部から45質量部に変更したこと以外は、実施例1と同様の方法で、重量平均分子量3.5万のビニル重合体を含む樹脂組成物からなる炭素繊維集束剤(IV)〔不揮発分23重量%〕を得た。
スチレンの使用量を10質量部から12質量部に変更し、メタクリル酸n−ブチルの使用量を10質量部から30質量部に変更し、かつ、NKエステルM−230G(新中村化学工業株式会社製、メトキシポリエチレングリコールメタクリレート)の使用量を30質量部から8質量部に変更したこと以外は、実施例1と同様の方法で、重量平均分子量6.6万のビニル重合体を含む樹脂組成物からなる炭素繊維集束剤(V)〔不揮発分23重量%〕を得た。
メタクリル酸グリシジルの使用量を50質量部から60質量部に変更し、スチレンの使用量を10質量部から5質量部に変更し、メタクリル酸n−ブチルの使用量を10質量部から0質量部に変更し、NKエステルM−230G(新中村化学工業株式会社製、メトキシポリエチレングリコールメタクリレート)の使用量を30質量部から20質量部に変更し、メタクリル酸n−ブチルを15質量部使用し、かつ、V−59(和光純薬工業株式会社製の触媒、2,2’−アゾビス(2-メチルブチロニトリル)の使用量を1.6質量部から3.2質量部に変更すること以外は、実施例1と同様の方法で、重量平均分子量2万のビニル重合体を含む樹脂組成物からなる炭素繊維集束剤(VI)〔不揮発分23重量%〕を得た。
メタクリル酸グリシジルの使用量を50質量部から0質量部に変更し、スチレンの使用量を10質量部から20質量部に変更し、かつ、メタクリル酸n−ブチルの使用量を10質量部から50質量部に変更すること以外は、実施例1と同様の方法で、重量平均分子量6万のビニル重合体を含む樹脂組成物からなる炭素繊維集束剤(I’)〔不揮発分23重量%〕を得た。
攪拌機、還流冷却管、温度計および窒素吹き込み管を備えた4つ口フラスコにメチルエチルケトン45質量部を仕込み80℃に昇温した。
次いで、メタクリル酸グリシジル40質量部、スチレン20質量部、メタクリル酸n−ブチル40質量部、メチルエチルケトン15質量部、V−59(和光純薬工業株式会社製の触媒、2,2’−アゾビス(2-メチルブチロニトリル)1.6質量部の溶解混合物を2時間かけて滴下し、80℃〜85℃の範囲で反応を行った。
ビニル重合体の重量平均分子量は、ゲル・パーミエーション・クロマトグラフィー(GPC)法により、下記の条件で測定した。
カラム:東ソー株式会社製の下記のカラムを直列に接続して使用した。
「TSKgel G4000」(7.8mmI.D.×30cm)×1本
「TSKgel G3000」(7.8mmI.D.×30cm)×1本
「TSKgel G2000」(7.8mmI.D.×30cm)×1本
検出器:RI(示差屈折計)
カラム温度:40℃
溶離液:テトラヒドロフラン(THF)
流速:1.0mL/分
注入量:100μL(試料濃度0.4質量%のテトラヒドロフラン溶液)
標準試料:下記の単分散ポリスチレンを用いて検量線を作成した。
東ソー株式会社製「TSKgel 標準ポリスチレン A−500」
東ソー株式会社製「TSKgel 標準ポリスチレン A−1000」
東ソー株式会社製「TSKgel 標準ポリスチレン A−2500」
東ソー株式会社製「TSKgel 標準ポリスチレン A−5000」
東ソー株式会社製「TSKgel 標準ポリスチレン F−1」
東ソー株式会社製「TSKgel 標準ポリスチレン F−2」
東ソー株式会社製「TSKgel 標準ポリスチレン F−4」
東ソー株式会社製「TSKgel 標準ポリスチレン F−10」
東ソー株式会社製「TSKgel 標準ポリスチレン F−20」
東ソー株式会社製「TSKgel 標準ポリスチレン F−40」
東ソー株式会社製「TSKgel 標準ポリスチレン F−80」
東ソー株式会社製「TSKgel 標準ポリスチレン F−128」
東ソー株式会社製「TSKgel 標準ポリスチレン F−288」
東ソー株式会社製「TSKgel 標準ポリスチレン F−550」
前記樹脂組成物からなる炭素繊維集束剤の保存安定性を沈殿等の有無に基づいて評価した。
前記炭素繊維集束剤を、容量140mlのガラス瓶に100ml入れ、密栓した状態で23℃の環境下に3ヶ月間放置した。
前記放置後、容器内の炭素繊維集束剤を目視で観察し、沈殿や凝集物が確認されたものを「×」、沈殿は確認されるが攪拌により容易に分散できたものを「△」、沈殿や凝集物が確認されなかったものを「○」と評価した。
ポリアクリロニトリル系炭素繊維(直径7μm/6000本)のノーサイズ糸を束ね、前記で得た炭素繊維集束剤を浸漬法で含浸し、ローラーで絞ることで有効成分の付着量を1質量%に調整し、ついで、150℃で30分間熱処理することによって、前記炭素繊維集束剤によって表面処理の施された(集束された)炭素繊維束(炭素繊維ストランド)を得た。
TM式摩擦抱合力試験機TM−200(大栄科学精機社製)を用い、ジグザグに配置した鏡面クロムメッキステンレス針3本を介して50gの張力で、炭素繊維ストランドを1000回擦過させ(往復運動速度300回/分)、炭素繊維ストランドの毛羽たちの状態を下記の基準で目視判定した。
○:数本の毛羽は見られたものの、実用上問題ないレベルであった。
△:毛羽立ちが確認でき、糸切れも若干見られた。
×:毛羽立ち及び単糸の糸切れが非常に多く確認できた。
前記炭素繊維ストランドを、約5mmの長さに裁断することによって炭素繊維チョップドストランドを作製した。
前記で得た炭素繊維ストランドを、6−ナイロン樹脂ペレット(汎用射出成型グレード)とを、炭素繊維質量含有率が30質量%となるように二軸押し出し混錬機にてコンパウンドし、3mmΦ×3mm長のコンパウンドペレットに加工した。
ビスフェノールA型液状エポキシ樹脂〔エピクロン850S、DIC(株)製〕100質量部にジシアンジアミド4質量部とN−(3,4−ジクロロフェニル)−N’,N’−ジメチルウレア4質量部を調合し離型紙上に塗布する。塗布した樹脂フィルム上に前記で得た炭素繊維ストランドを等間隔で一方向に引き揃え並べた後、加熱してエポキシ樹脂を含浸し、炭素繊維含有率が60質量%のプリプレグを作製した。作製したプリプレグを積層しながら金型に充填した後、150℃加圧下で1時間、続いて140℃で4時間処理することによって炭素繊維強化プラスチックを作製した。
「重量平均分子量」は、アクリル樹脂の重量平均分子量を表す。
Claims (5)
- ポリオキシアルキレン構造とグリシジル基とを有するアクリル樹脂(A)及び水性媒体(B)を含有することを特徴とする繊維集束剤であって、前記アクリル樹脂(A)が、ポリオキシアルキレン構造を有する(メタ)アクリル単量体とグリシジル基を有する(メタ)アクリル単量体とを含有する重合性不飽和二重結合を有する単量体混合物(a)を重合して得られるものであって、前記ポリオキシアルキレン構造を有する(メタ)アクリル単量体が、前記重合性不飽和二重結合を有する単量体混合物(a)の全量に対して10質量%〜40質量%の範囲で含まれるものであることを特徴とする繊維集束剤。
- 前記アクリル樹脂(A)が、ポリオキシアルキレン構造を有する(メタ)アクリル単量体とグリシジル基を有する(メタ)アクリル単量体とを含有する重合性不飽和二重結合を有する単量体混合物(a)を重合して得られるものであって、前記グリシジル基を有する(メタ)アクリル単量体が、前記重合性不飽和二重結合を有する単量体混合物(a)の全量に対して10質量%〜70質量%の範囲で含まれるものである請求項1に記載の繊維集束剤。
- 前記ポリオキシアルキレン構造が、ポリオキシエチレン構造、ポリオキシエチレン−ポリオキシプロピレン構造、ポリオキシエチレン−ポリオキシブチレン構造、及び、それらの末端の水酸基がアルキル基によって封止された構造からなる群より選ばれる1種以上である請求項1に記載の繊維集束剤。
- 請求項1〜3のいずれか1項に記載の繊維集束剤によって集束された炭素繊維またはガラス繊維。
- 請求項4に記載の炭素繊維またはガラス繊維と、マトリックス樹脂(C)とを含有することを特徴とする成形品。