JP5988591B2 - Overpressure release valve - Google Patents

Description

  The present invention safely removes excess pressure from a sealed fuel cell, an electrolytic cell of a secondary battery, a container of a capacitor, a closed vessel such as a reaction vessel or a storage vessel, or a closed vessel such as a pipe. The present invention relates to an overpressure release valve that opens to the outside, and a dome-type elastic body used therefor.

  Rechargeable batteries such as fuel cells, nickel cadmium batteries, nickel metal hydride batteries, lithium ion batteries, lead storage batteries, capacitors, portable electronic devices such as mobile phones and laptop personal computers, home appliances, and automobile power supplies Used.

  For these batteries and capacitors, when the internal pressure becomes excessive, the pressure is automatically released to the outside, and moisture and moisture that degrade the storage capacity can be used repeatedly without entering the outside. A check valve is installed.

  For example, the battery exterior is formed by an aluminum laminate film obtained by laminating an aluminum foil and a plastic film layer in Patent Document 1, and the aluminum laminate film is provided with a gas vent, and the gas vent has a plurality of through holes on the bottom surface. An electric double layer capacitor is disclosed in which a main body is thermally fused to a laminate film, an upper surface of the main body is closed with a film material, and the film material is fixed with a pressing member.

  Further, Patent Document 2 discloses a laminated body having a plurality of thin plate-like electrode plates and a thin plate-like insulating member that is inserted between the electrode plates and insulates between the electrode plates, and a container that contains the sheet-like member and accommodates the laminated body And an electric double layer capacitor having an electrolyte filled in the container, provided with a lid that is on the side of the laminated body in the container and straddles two opposite sides of the rectangular cross section inside the container, At least a part of the flat part is provided with a pressure adjusting valve, and the pressure adjusting valve is provided in the through hole formed in the lid, the hole formed in the sheet-like member, and the hole. An electric double layer capacitor having a vent valve having a slit or a small hole in the center is disclosed.

  Patent Document 3 discloses a resin-made housing having a pressure relief valve attached to an opening provided in a laminate film and having an annular groove that opens to the inside, and a communication hole that communicates the groove and the outside. The rubber part has a main body part that is held on the inner peripheral surface side of the groove part and a valve part that extends from the main body part toward the outside and is in elastic contact with the outer peripheral surface of the groove part. A pressure release valve is disclosed that includes a valve body that releases the internal pressure to the outside by releasing the contact between the valve portion and the outer peripheral surface when the internal pressure becomes higher than a certain pressure.

  The conventional pressure release valve has a function in the opposite direction of the release of excess pressure from the inside to the outside and the prevention of moisture / moisture ingress from the outside to the inside. And the slit valve cannot be completely sealed, preventing the ingress of moisture from the outside, or improving the function of one of them, making the other function too lenient, releasing excess pressure and preventing moisture and moisture from entering. The balance of the performance is lacking, or the pressure release valve is not suitable for downsizing in combination with the weight reduction of the battery and capacitor.

Japanese Patent No. 4672956 International Publication No. 2007-4467 Pamphlet JP 2010-114127 A

  The present invention has been made to solve the above-described problems, and can sufficiently exhibit both the effects of releasing excessive pressure from the inside to the outside and preventing moisture and moisture from entering from the outside to the inside. Combined with the lighter weight and longer life of batteries and capacitors, even small and simple shapes can be released many times as many as tens of thousands of times while stably and reliably releasing excess internal pressure over a long period of time. It is an object of the present invention to provide an overpressure relief valve having a simple shape that is easy to manufacture and a dome-shaped elastic body for the overpressure relief valve used therein.

The overpressure release valve according to claim 1, which has been made to achieve the above object, covers an inner lid in which an airtight hole to the inside of a sealed container is conducted, and covers the inner lid. an outer lid housing is open open holes to the outside world, while enclosing the dome elastic material, integrally, wherein attached to the closed vessel, an excess pressure release valve for releasing the excessive pressure the inside to the outside The dome-shaped elastic body is urged by compression of the inner lid and the outer lid that is in contact with the inner lid while having a ridge at the dome opening to open the airtight hole with the excess pressure. Preferably, the dome has a notch for hermetically closing from the outside at the top of the dome and guiding the excessive pressure to the open hole at the dome opening.

  The overpressure release valve according to claim 2 is the one described in claim 1, wherein the dome top portion of the dome-shaped elastic body is thick at least at a portion closing the airtight hole. It is characterized by that.

Excess pressure release valve according to claim 3 has been described in any one of claims 1-2, wherein the domed elastic body, an ethylene - propylene - diene rubber, silicone rubber, butyl rubber, halogenated butyl rubber, nitrile Rubber, hydrogenated nitrile rubber, fluorine rubber, acrylic rubber, urethane rubber, ethylene-propylene rubber, chloroprene rubber, chlorosulfonated polyethylene rubber, epichlorohydrin rubber, styrene butadiene rubber, butadiene rubber, polysulfide rubber, norbornene rubber, isoprene rubber, It is characterized by being molded from natural rubber and / or thermoplastic elastomer.

Excess pressure release valve according to claim 4, those described in any one of claims 1-3, wherein the lid, the outer lid is attached by being incorporated threaded and / or welded parts It is characterized by that.

Excess pressure release valve according to claim 5 has been described in any one of claims 1-4, wherein the closed vessel is thermoplastic resins, metals, or formed by laminating thermoplastic resin It is hermetically sealed by being attached to the inner lid and / or the outer lid at the welding site .

An overpressure release valve according to a sixth aspect is the one according to any one of the first to fifth aspects, wherein the outer lid is reduced in diameter on the outer side, and is a stepped portion due to the reduced diameter. And it is attached to the said airtight container, It is characterized by the above-mentioned.

The overpressure relief valve of claim 7, those described in any one of claims 1-6, wherein the outer lid is in the inner side, has a circumferential projection along the outer periphery, the sealed container It is characterized by being attached at the welding site .

Excess pressure release valve according to claim 8, those described in any one of claims 1-7, tangent at the dome opening of the domed resilient member is inclined to the dome top side It is characterized by that.

The overpressure release valve according to a ninth aspect is the one according to any one of the first to eighth aspects, wherein the sealed container is a capacitor or a battery.

The dome-shaped elastic body for an overpressure release valve according to claim 10 , which has been made to achieve the above object, includes an inner lid in which an airtight hole to the inside of a sealed container is conducted, and covers the inner lid. an outer lid housing is open open hole to cage outside world, integrally, wherein attached to the sealed container is used in a overpressure relief valve for releasing the excessive pressure the inside to the outside, the outer A dome-type elastic body included in the lid, which is formed of an elastic material that is biased by compression by pressing the inner lid and the outer lid that is in contact with the inner lid while having a flange at the dome opening, A dome top portion that airtightly closes the airtight hole by the overpressure so that the airtight hole can be opened by the excessive pressure, and a notch that guides the excessive pressure to the open hole in the dome opening, To do.

  The excessive pressure relief valve of the present invention is an excessive pressure to be opened even if it has a simple structure in which a dome-shaped elastic body having a simple shape that is easy to mold precisely is sandwiched between an inner lid and an outer lid and enclosed in the outer lid. When pressure is applied, the excess pressure is released safely and reliably from the inside of the container to the outside. On the other hand, until the excess pressure is applied, the airtight hole in the inner lid is completely sealed to allow moisture and moisture to enter from the outside. Can be reliably prevented, and both conflicting effects can be fully expressed.

  This overpressure release valve has a dome-shaped elastic body, so it can be compactly enclosed between the inner lid and outer lid, and the airtight hole in the inner lid can be opened only with excess pressure, maintaining a sealed state Therefore, even a small and simple shape can be used stably over a long period of time, contributing to weight reduction and long life of batteries and capacitor containers and piping.

  This overpressure relief valve can be opened many times as many as tens of thousands of times by repeatedly applying excessive pressure inside various sealed containers and pipes such as batteries and capacitors at any desired pressure from low pressure to high pressure. And high reliability. This overpressure release valve operates reliably even in a wide range of excessive pressures from a relatively low pressure of several kPa to 10 kPa to a high pressure of 200 kPa to 1 MPa, and can release the pressure safely and reliably to the outside. belongs to.

  This excessive pressure release valve has a small and simple structure, and can produce a uniform product in large quantities at low cost, and has high productivity. This overpressure release valve can be easily and manufactured in large quantities by molding a dome-shaped elastic body, outer lid / inner lid, and welding of the outer lid and inner lid, so that electronic devices such as various containers and pipes such as batteries and capacitors It is useful as a safety valve for general-purpose products and daily necessities.

  This dome-shaped elastic body is a member that can be easily and mass-produced by molding with a simple structure in which the excess pressure inside the container is released by the excess pressure release valve and the inside of the container is sealed.

It is a schematic cross section of an excessive pressure release valve to which the present invention is applied. It is a schematic cross section which shows the middle of manufacture of another overpressure release valve to which this invention is applied. It is the perspective view which shows the one aspect | mode of the dome shape elastic body for overpressure relief valves to which this invention is applied, and the schematic cross section of another aspect. It is a figure which shows the correlation of the hardness or thickness at the time of the uncompressed of the dome shape elastic body in the overpressure release valve to which this invention is applied, and an operating pressure. It is a figure which shows the correlation with the hardness at the time of the uncompressed of the dome shape elastic body in the overpressure relief valve to which this invention is applied, and an operating pressure for every thickness at the time of the uncompressed of the dome shape elastic body. It is a figure which shows the correlation of the hardness or thickness at the time of the uncompressed of the dome shape elastic body in another overpressure release valve to which this invention is applied, and an operating pressure. It is a figure which shows the correlation between the frequency | count of a measurement when the operating pressure is repeatedly measured in the excessive pressure release valve to which this invention is applied, and an operating pressure. It is a figure which shows the correlation with the hardness at the time of uncompressed of the dome shape elastic body in another overpressure release valve to which this invention is applied, and an operating pressure for every thickness at the time of uncompressed of a dome shape elastic body. It is a perspective view which shows the battery or capacitor which attached the overpressure release valve to which this invention is applied.

  Hereinafter, although the form for implementing this invention is demonstrated in detail, the scope of the present invention is not limited to these forms.

  An embodiment of the overpressure release valve 1 to which the present invention is applied will be described with reference to FIG. 1. A disk-shaped inner lid 10 and a cylindrical hook 35 that covers and fits the inner lid 10. And the dome-shaped elastic body 20 having a small diameter of substantially the same diameter or a small amount of play enclosed in a cavity 36 in which the outer lid 30 is recessed and partitioned by the inner lid 10.

  An outer lid of the excess pressure relief valve 1 is formed in the through hole 44 for the excess pressure relief valve formed in the airtight container 40 formed of a laminate layer composed of the aluminum layer 42 and the thermoplastic resin layers 41 and 43 laminated on both sides thereof. 30 is inserted, and is welded and attached to the thermoplastic resin 41 of the sealed container 40 on the flange 35 of the outer lid 30 to be in a sealed state. The inner lid 10 has a protrusion 11 that circulates along the outer periphery on the inner side of the sealed container 40, and the outer lid 30 has a protrusion that circulates along the inner periphery forming the cavity 36 on the inner side of the sealed container 40. 31. The inner lid 10 and the outer lid 30 are integrated with each other by welding the projection 11 around the inner lid 10 and the projection 31 having a square cross section around the outer lid 30. Both protrusions 11 and 31 are blunted by welding.

  In the center of the inner lid 10, an airtight hole 12 that conducts to the inside of the sealed container 40 is opened in a cylindrical shape. An open hole 33 that leads to the outside world is opened in a recess that forms a cavity 36 of the outer lid 30.

  The dome-shaped elastic body 20 is substantially bowl-shaped on the outside and has an inner space 26. The dome-shaped elastic body 20 closes the airtight hole 12 of the inner lid 10 with the dome top portion 21, and is in contact with the outer lid 30 together with the dome opening 24 and the flange 25 protruding to the outer periphery thereof. The dome opening 24 faces the open hole 33. The dome-shaped elastic body 20 is pressed by the inner lid 10 and the outer lid 30 and is urged by compression so that the hermetic hole 12 can be opened with excessive pressure at the dome top portion 21 so as to be hermetically closed. The inside of the sealed container 40 is isolated from the inside.

  Since the elastic body 20 is a dome shape, the spring coefficient is smaller than that of the plate rubber elastic body or the columnar rubber elastic body, and the operating pressure at which the excessive pressure release valve 1 can release the desired excessive pressure is appropriately adjusted. It is easy to do. If the dome-shaped elastic body 20 has a curved surface that is gently curved at the dome top portion 21, the airtight hole 12 can always be reliably closed even if the position is somewhat shifted or restored by repeated operation, Even if the airtight hole 12 or the dome-shaped elastic body 20 varies from lot to lot, the airtight hole 12 can be evenly closed. If the dome-shaped elastic body 20 is flat or stepped at the top, the airtight hole 12 cannot be closed, a gap is likely to be formed, airtightness is lacking, and the expected excessive pressure is not reached. However, the excessive pressure release valve 1 will operate.

  In the dome-shaped elastic body 20, a notch 23 that cuts an excessive pressure inside the sealed container 40 and guides it to an open hole is cut into a flange 25 protruding from the outer periphery of the dome opening 24. The notch 23 forms a gap that allows the inside and outside of the dome-shaped elastic body 20 to be ventilated even when the dome-shaped elastic body 20 is compressed. By appropriately controlling the size of the gap formed by the notch 23 and the airtight hole 12 and the open hole 33, the flow rate when the excessive pressure is released inside the sealed container 40 can be adjusted.

  As shown in FIG. 2, the excessive pressure release valve 1 of another aspect to which the present invention is applied is a protrusion that circulates along the inner periphery forming the cavity 36 on the inner side of the sealed container 40 on the flange 35 of the outer lid 30. 31 and / or a protrusion 32 having a triangular cross section that circulates slightly closer to the center than the outer periphery of the flange 35. The flange 32 inside the sealed container 40 together with the protrusion 32 of the outer lid 30 may be welded to the sealed container 40 made of thermoplastic resin. Since the looped protrusion 32 is welded to the hermetic container 40 made of a thermoplastic resin, the sharp melting of the sharp protrusion 32 proceeds more quickly than the surrounding area and is surely welded. Therefore, the welding strength is higher than that between flat surfaces. Strengthens and improves adhesion and sealing. These weldings with the outer lid 30 may be thermal welding or ultrasonic welding.

  The overpressure release valve 1 is composed of the material, hardness, thickness, and compressibility of the dome-shaped elastic body 20, the shape of the thick portion of the dome top 21, the end area of the dome opening 24, Depending on the shape and the like, in particular, the hardness and thickness of the dome-shaped elastic body 20 can be arbitrarily adjusted to a desired operating pressure. By using the dome-shaped elastic body 20, the airtight hole 12 of the inner lid 10 can be airtightly closed in a normal state, and can be denatured so that it can be released to the outside when excessive pressure is generated.

  The material of the dome-shaped elastic body 20 is not particularly limited as long as it exhibits elasticity, but ethylene-propylene-diene rubber (EPDM), which is a copolymer of ethylene, propylene, and non-conjugated diene monomer; methyl silicone rubber (MQ) ), Vinyl methyl silicone rubber (VMQ), phenyl methyl silicone rubber (PMQ), phenyl vinyl methyl silicone rubber (PVMQ), and fluorinated silicone rubber (FVMQ) in which a fluoroalkyl group is introduced into the side chain of vinyl silicone rubber. Butyl rubber (IIR) which is a copolymer of isobutene and isoprene; halogenated butyl rubber (X-IIR) such as chlorinated butyl rubber (CIIR) and brominated butyl rubber (BIIR); copolymer of butadiene and acrylonitrile Nitrilego, a polymer Hydrogenated nitrile rubber (HNBR) which is a hydrogenated nitrile rubber; Fluoro rubber (FKM) such as polyvinylidene fluoride, tetrafluoroethylene-polypropylene copolymer, tetrafluoroethylene-perfluorovinyl ether copolymer; Acrylic rubber (ACM); Urethane rubber such as polyester urethane rubber and polyether urethane rubber; ethylene-propylene rubber (EPM); chloroprene rubber (CR); chlorosulfonated polyethylene rubber (CSM); epichlorohydrin homopolymer (CO), Epichlorohydrin rubber such as epichlorohydrin copolymer (COE); styrene butadiene rubber (SBR); butadiene rubber (BR); polysulfide rubber (T); norbornene rubber (NOR); isoprene rubber (IR) Natural rubber (NR); styrene elastomer, olefin elastomer, vinyl chloride elastomer, urethane elastomer, ester elastomer, amide elastomer, silicone elastomer, nitrile elastomer, 1,2-polybutadiene (1,2-PB) It is preferable that it is formed of one or more resins selected from thermoplastic elastomers (TPE) such as

  The hardness of the dome-shaped elastic body 20 is, for example, A5 to A90, preferably A10 to A80 in Shore A hardness when not compressed.

The thickness t ₁ of the dome-shaped elastic body 20 is, for example, 0.2 to 1.0 mm, preferably 0.3 to 0.6 mm in trunk thickness when uncompressed.

  The dome-shaped elastic body 20 may have a uniform thickness as a whole when uncompressed, but the dome top portion 21 may be a thick portion 22 at a portion where at least the airtight hole 12 is closed. preferable. If the dome top portion 21 is thick, the air permeability is remarkably reduced, so that volatile gas unexpectedly leaks from the inside of the sealed container 40 or moisture or moisture enters the inside of the sealed container 40 from the outside. Can be almost completely prevented. For example, when the dome-shaped elastic body 20 is formed of X-IIR such as IIR, CIIR, or BIIR having high gas permeability, the thick portion 22 is not provided as shown in FIG. Although it is good, especially when it is formed of EPDM or ACM having a slightly low gas permeability, or when it is formed of silicone rubber such as MQ, VMQ, PVMQ, or FVMQ having a low gas permeability, the thick portion 22 Is preferably provided.

  The surface of the dome-shaped elastic body 20, particularly the surface on the inner lid 10 side, may have a coating film deposited with a metal such as aluminum, and the coating film sputtered or deposited with aluminum, silica, or the like. You may have (not shown). These coating films preferably have a thickness of 20 to 500 nm.

  As shown in FIGS. 1 and 2, the dome top portion 21 of the dome-shaped elastic body 20 is thicker in a wider range than the airtight hole 12, and the thick-walled portion 22 is flat on the inner space 26 side of the dome-shaped elastic body 20. In other words, it may be a so-called plano-convex lens shape, and has a uniform thickness over a wider range than the airtight hole 12 as shown in FIG. It may be recessed in the shape of a so-called meniscus lens, and as shown in FIG. 3 (d), it becomes thicker closer to the dome top portion 21 than the airtight hole 12, and the thick portion 22 becomes a so-called convex meniscus lens. It may be in the shape. However, if the dome top portion 21 of the dome-shaped elastic body 20 has a so-called biconvex lens shape, the fluctuation of the operating pressure of the excessive pressure release valve 1 may increase, which is not preferable.

  The dome opening 24 of the dome-shaped elastic body 20 may have a collar 25 as shown in FIGS. 1 and 2 and FIGS. 3A to 3D, and has a collar as shown in FIG. You don't have to.

When uncompressed, the dome-shaped elastic body 20 has a height H of, for example, 2.75 to 3.25 mm, preferably about 3 mm (specifically 3.1 mm), and has an outer diameter D ₂ that does not include the flange 25. For example, it is 4.6 to 8.2 mm, preferably about 6 mm (specifically 6.2 mm), and the outer diameter D ₁ including the heel provided as necessary is, for example, 5.4 to 9.2 mm, preferably 7.3 mm.

The dome-shaped elastic body 20, when having a thick portion 22, a thickness _{t 2,} for example 1.0 to 3.0 mm, preferably in 1.5 mm.

Diameter _{D 4} of the hermetic holes 12 of the inner lid 10 is for example 1.0 to 3.0 mm, preferably 2.0 mm. The dome-shaped elastic body 20, when having a thick portion 22, 1.0 to 2.0 times the diameter _{D 4} of the hermetic holes 12 diameter _{D 3} of the thick portion 22 when not compressed, preferably 1.5 While doubling, the thickness is adjusted to 1.0 to 6.0 mm, preferably 1.5 to 4.5 mm, more preferably 3.0 mm.

  If the dome-shaped elastic body 20 is larger than the above range, it is too soft and the dome-shaped elastic body 20 is swollen before reaching the desired overpressure, and the overpressure release valve 1 is activated or sealed from the outside. The outside air containing moisture or moisture may enter the container 40.

  In the dome-shaped elastic body 20, a tangent line at the dome opening 24 is preferably inclined toward the dome top 21 side on the inner lid 10 side, and an angle θ formed by the tangent line and the central axis direction is an acute angle. And more preferable.

  The dome-shaped elastic body 20 has a rough surface when the surface on the inner lid 10 side is a smooth polished surface by mold surface polishing when molding the mold such as compression molding or injection molding. For this reason, a gap with the airtight hole 12 is not generated, and it is preferable to completely close the hole to prevent an unexpected leakage from the sealed container 40. It is preferable that the surface on the inner lid 10 side of the dome-shaped elastic body 20 is a part of a curved sphere of about R2 to R5.

  The dome-shaped elastic body 20 is pressed between the inner lid 10 and the outer lid 30 so as to be compressed, and is compressed by about 10 to 30%, preferably about 20% from the uncompressed height H. It is biased according to the natural elasticity.

  The dome-shaped elastic body 20 may have rounded corners.

  The material of the inner lid 10 and the outer lid 30 is not particularly limited as long as it can be welded, but may be a thermoplastic resin capable of ultrasonic welding, laser welding, or heat welding, and can be welded metal. It may be.

  The sealed container 40 may be a box or bag formed of a thermoplastic resin or metal, and is a bag formed of a laminate layer in which both surfaces of a metal foil such as an aluminum foil are coated with these resins. Also good. In order to weld the outer lid 30 and the airtight container, it is more preferable that the welded portions of both are the same resin or metal.

  The thermoplastic resin used for the inner lid 10, the outer lid 30, and the sealed container 40 is a polyolefin such as polyethylene (PE), polypropylene (PP), polyvinyl chloride (PVC), or polyvinylidene chloride (PVDC), polystyrene (PS ), Acrylonitrile-styrene-butadiene copolymer (ABS), acrylonitrile-styrene copolymer (AS), acrylic resin (PMMA), polyphenylene ether (PPE), polyacetal (POM), cellulose acetate (CA), polyethylene terephthalate ( PET), polybutylene terephthalate (PBT), polyamide (PA), polycarbonate (PC), polyacetal (POM), polyphenylene sulfide (PPS), polyether ether ketone (PEEK), fluororesin, urea Alone or a mixture of down resins.

  As shown in FIG. 9, the overpressure release valve 1 includes a sealed container 40, for example, a container such as an electrolytic cell for a fuel cell or a secondary battery, a closed container such as a capacitor container, a reaction container, a storage container, or a pipe, Particularly preferably, it is attached to a battery or capacitor container.

  A gas-liquid separation membrane may be attached to the sealed container (not shown) for the purpose of preventing the liquid such as the electrolytic solution inside the sealed container 40 from flowing out. It is preferable that a gas-liquid separation membrane is attached to the inside of the projection 11 inside the sealed container 40 of the inner lid 10 by welding. The gas-liquid separation membrane is preferably circular, and its diameter is larger than the airtight hole 12 and smaller than the inside of the protrusion 11. Materials for the gas-liquid separation membrane include polyethylene (PE), polypropylene (PP), polystyrene (PS), polyamide (PA), polyvinyl chloride (PVC), cellulose acetate (CA), polyethylene terephthalate (PET), polyether Nonwoven fabric made of thermoplastic resin materials such as sulfone (PES) and polytetrafluoroethylene (PTFE), continuous porous membrane by stretching (Gore-Tex (trademark) manufactured by Japan Gore-Tex, Temish (trademark) manufactured by Nitto Denko Corporation, Tokuyama NF sheet, porum, ramiporum, etc.)), continuous porous membrane by extraction method: Saporus (registered trademark of Asahi Rubber Co., Ltd.) is preferably used.

  The excessive pressure release valve 1 is manufactured as shown in FIG. 2, for example. First, the dome-shaped elastic body 20 is inserted into the cavity 36 of the molded outer lid 30 with the dome opening 24 side facing the open hole of the outer lid 30, and the dome opening 24 is fitted in the cavity 36. The outer lid 30 is brought into contact. Next, the inner lid 10 is fitted and screwed into the opening step portion 37 of the outer lid 30 and urged while compressing the dome-shaped elastic body 20, and then the projection 11 of the inner lid 10 and the projection 31 of the outer lid 30 are Then, the lids 10 and 30 are welded together. Then, in the cavity 36, the thickness of the dome-shaped elastic body 20 is increased by the amount that the height of the dome-shaped elastic body 20 is reduced by the compression, and the airtight hole 12 of the inner lid 10 is energized by the bias. Are closed hermetically at the dome top 21, but the inner space 26 of the dome-shaped elastic body 20 and the cavity 36 space sandwiched between the dome-shaped elastic body 20 and the inner lid 10, even if the notch 23 is somewhat crushed, Keep it conductive. When the protrusion 32 of the outer lid 30 is aligned around the through hole 44 for the overpressure release valve of the sealed container 40 and the sealed container 40 and the outer cover 30 are welded, the sealed container 40 to which the overpressure release valve 1 is attached is obtained. can get. Although the overpressure release valve 1 of the embodiment of FIG. 2 has been described, the overpressure release valve 1 of the embodiment of FIG.

  Explaining with reference to FIG. 1, the overpressure release valve 1 operates as follows. The overpressure release valve 1 completely opens the airtight hole 12 of the inner lid 10 at the dome top portion 21 of the dome-shaped elastic body 20 when the pressure inside the sealed container 40 is normal pressure or less than the desired excess pressure to be opened. Because it is closed, it is kept airtight. When the inside of the hermetic container 40 reaches or exceeds the desired excess pressure, the dome-shaped elastic body 20 is slightly deformed at the contact portion with the airtight hole 12 of the inner lid 10 to form a gap for releasing the excess pressure. Then, the excess pressure reaches the cavity 36 of the outer lid 30 as shown by the arrow, passes through the notch 23 of the dome-shaped elastic body 20, and the open hole 33 of the outer lid 30 from the inner space 26 of the dome-shaped elastic body 20. And then released to the outside world. When the excessive pressure is released, the dome top portion 21 of the dome-shaped elastic body 20 again completely closes the airtight hole 12 of the inner lid 10 and returns to the airtight state.

  The example which produced the excess pressure relief valve to which this invention is applied is shown in a following example.

(Preparation Examples 1 to 7)
First, various EPDM-containing raw material compositions were prepared in order to produce the dome-shaped elastic body 20 of the overpressure release valve 1 as shown in FIG.
[Preparation] The ingredients shown in Table 1 below were kneaded with a kneader to prepare EPDM-containing raw material compositions of Preparation Examples 1 to 7, respectively.
[Evaluation of physical properties] Next, each of the EPDM-containing raw material compositions was subjected to press vulcanization at 170 ° C for 10 minutes, followed by secondary vulcanization at 170 ° C for 30 minutes to obtain a rubber test plate for evaluating physical properties having a thickness of 2 mm. Produced. The physical properties of the rubber test plate were evaluated as follows. The hardness is measured as the Shore A hardness by the durometer A method in accordance with JIS K6253 by superposing three 2 mm thick rubber test plates. Tensile strength and elongation are measured in a dumbbell shape No. 3 at a tensile speed of 500 mm / min according to JIS K6251. The tear strength is measured in accordance with JIS K6252 in the form of a not-cut angle with a tensile speed of 500 mm / min. The results are summarized in Table 1.

(Preparation Examples 8 to 15)
In order to produce the dome-shaped elastic body 20 of the excessive pressure release valve 1 with various hardnesses, various silicone rubber-containing raw material compositions were prepared and cured to evaluate physical properties.
[Preparation] The composition components shown in Table 2 below were kneaded with an open roll to prepare silicone rubber-containing raw material compositions of Preparation Examples 8 to 15, respectively.
[Evaluation of physical properties] Next, the rubber rubber test plate for physical property evaluation having a thickness of 2 mm was obtained by press vulcanizing the raw material composition containing silicone rubber at 170 ° C. for 10 minutes, followed by secondary vulcanization at 200 ° C. for 4 hours. Was made. The physical properties of this rubber test plate were evaluated in the same manner as in Preparation Examples 1 to 7. The results are summarized in Table 2.

(Example 1 (1) to (4))
[Production] The EPDM-containing raw material composition obtained in Preparation Example 5 or 6 was poured into a mold having a cavity having a shape for forming the dome-shaped elastic body 20 having the shape shown in FIG. After press vulcanizing for a minute, secondary vulcanization was performed at 170 ° C. for 30 minutes to produce a dome-shaped elastic body 20. When the dome-shaped elastic body 20 is uncompressed, the height H is 3.1 mm, the outer diameter D ₁ including the flange 25 is 5.4 mm, the outer diameter D ₂ not including the flange 25 is 4.6 mm, and is thick. The diameter D _{3 of the} part 22 is 1.2 mm, the body thickness t ₁ is 0.5 mm or 0.6 mm, the maximum thickness of the thick part 22 is 1.5 mm, and the width / height of the notch 23 is 0.4 mm. The height of the collar 25 is 0.8 mm, and the dome R is 2.3 mm. The dome-shaped elastic body 1 is made of polypropylene having the shape shown in FIG. 2 and is enclosed in a holder composed of an inner lid 10 and an outer lid 30 in which the diameter of the airtight hole 12 is 2 mm. An open valve 1 was produced.
[Functional Evaluation] Excess pressure value (relief pressure) that can be opened for four types of overpressure release valves 1 using the EPDM-containing raw material composition of Preparation Example 5 or 6 and having a body thickness of 0.5 mm or 0.6 mm The following working pressure measurement test was conducted on the next day after the dome-shaped elastic body was manufactured. The measurement conditions were as follows. The measuring device was a leak test machine for rubber valve (manufactured by Takachiho Seiki Co., Ltd.), and the fixture for the excess pressure release valve 1 to the leak test machine for rubber valve (manufactured by Takachiho Seiki Co., Ltd.) was used. Tool C-3825-01 (manufactured by Asahi Rubber Co., Ltd.), pressurization gas is nitrogen gas, pressurization condition is 2 kPa / sec, leak detection pressure is 3 kPa, the number of repeated measurements is 5, and the interval time for each time (residual pressure released state) For 1 minute and the measurement temperature is room temperature (25 ° C.). The measuring method uses a leak tester for rubber valves (manufactured by Takachiho Seiki Co., Ltd.), and it is connected airtightly to a leak test jig C-3825-01 from a nitrogen gas cylinder through a regulator, and the pressure increase rate becomes constant. By pressurizing with such a program, the primary side pressure when the leak detection pressure becomes 3 kPa is printed and recorded as the operating pressure. The measurement results of the operating pressure measurement test of the excess pressure release valve 1 are shown in Table 3 below, and are shown in FIG. 4 as average values.

As apparent from Table 3 and FIG. 4A, the harder the dome-shaped elastic body 20 is, the higher the operating pressure of the excess pressure release valve 1 is. As is apparent from Table 3 and FIG. It was found that the operating pressure of the excess pressure release valve 1 was higher as the body thickness t ₁ of the mold elastic body 20 was larger. In order to set the operating pressure to 100 kPa or less, which is a lower pressure, if the body thickness t ₁ of the dome-shaped elastic body 20 is kept at 0.5 to 0.6 mm, its hardness is set to A30 / S or less, type elastic body thickness _{t 1} if it is left hardness A49 / S~A60 / S of 20 it is necessary to 0.4mm or less.

(Example 2 (1) to (8))
[Fabrication] The use of the eight types of silicone rubber-containing raw material compositions obtained in Preparation Examples 8 to 15 and press vulcanization at 170 ° C for 10 minutes, followed by secondary vulcanization at 200 ° C for 4 hours Then, an excess pressure release valve 1 was produced in the same manner as in Example 1 except that a total of 8 types of dome-shaped elastic bodies 20 having a body thickness of 0.5 mm were produced.
[Functional Evaluation] In order to measure the overpressure value (relief pressure) that can be opened once for each of the overpressure release valves 1, the same operating pressure measurement test as in Example 1 was performed. The measurement results of the operating pressure measurement test of the excess pressure release valve 1 are shown in Table 4 and FIG.
(Example 3 (1) to (8))
[Fabrication] The use of the eight types of silicone rubber-containing raw material compositions obtained in Preparation Examples 8 to 15 and press vulcanization at 170 ° C for 10 minutes, followed by secondary vulcanization at 200 ° C for 4 hours Excess pressure relief valve 1 was produced in the same manner as in Example 1 except that a total of 8 types of dome-shaped elastic bodies 20 having a body thickness of 0.6 mm were produced.
[Functional Evaluation] In order to measure the overpressure value (relief pressure) that can be opened once for each of the overpressure release valves 1, the same operating pressure measurement test as in Example 1 was performed. The measurement results of the operating pressure measurement test of the excess pressure release valve 1 are shown in Table 4 and FIG.

As is apparent from Table 4 and FIG. 5, the harder the dome-shaped elastic body, the higher the operating pressure of the overpressure release valve 1 and the thicker the body thickness t ₁ of the dome-type elastic body, the overpressure release valve. The working pressure of 1 was found to be high.

(Example 4 (1) to (2))
[Fabrication] The two types of silicone rubber-containing raw material compositions obtained in Preparation Examples 8 and 10 were used, and they were press vulcanized at 170 ° C for 10 minutes, followed by secondary vulcanization at 200 ° C for 4 hours. Then, an excess pressure relief valve 1 was produced in the same manner as in Example 1 except that two kinds of dome-shaped elastic bodies 20 having a body thickness of 0.6 mm were produced. It was attached to a 300 mL transparent sealed container 40 made of acrylic resin as shown in FIG.
[Functional evaluation] In order to measure the operating pressure (relief pressure) and the open flow (relief flow) of the overpressure when each of the overpressure release valves 1 is opened, the following working pressure / open flow measurement test is performed. went.
In the test, from a nitrogen gas cylinder having a compressed nitrogen gas capacity of 1.5 m ³ , a regulator (manufactured by YUTAKA; trade name CF-2510-RN-V) and a flow meter with a needle valve (flow meter) Product name: RK1250-15-SS-1 / 4-H2-1L / min-0.2 MPa-0-D, measurement range: 0.5 L / min to 1 L / min, supply pressure (inlet side): A small digital pressure gauge (manufactured by Nagano Keiki Co., Ltd., product number: GC61-374-17N380) that is connected to the sealed container 40 in an airtight manner up to 0.2 MPa and that measures the internal pressure of the container. XXXXXX, measurable range: -0.1 to 1 MPa), and overpressure release valve 1 is made of stainless steel SUS303 leak test jig C-3825-01 (morning Nylon gas released from the open valve as excess pressure is guided to the water-filled Erlenmeyer flask by a water replacement method, and the operating pressure when the overpressure release valve 1 is activated The pressure was measured with a pressure gauge, and the nitrogen gas amount was measured for a predetermined time immediately after the operation.
The measurement method is as follows: (i) the nitrogen cylinder valve is opened and the regulator is adjusted to 0.2 MPa; (ii) the flow meter valve is adjusted to 0.5 L / min and flows into the sealed container 40; (iii) Measure the working pressure when the overpressure release valve is activated by overpressure with a pressure gauge. (iv) Immediately after confirming the generation of bubbles, capture nitrogen gas for 1 minute by the underwater displacement method. The amount of nitrogen gas trapped in 1 minute was measured to obtain an open flow rate (mL / min) and converted per unit time.
The measurement results of the operating pressure / opening flow rate measurement test of the excess pressure release valve 1 are shown in Table 5 below.

表５から明らかな通り、ドーム型弾性体の硬さが硬い程、過剰圧力開放弁１の作動圧が高く、単位時間当たりの開放流量が大きいことが分かった。

As apparent from Table 5, it was found that the harder the dome-shaped elastic body, the higher the operating pressure of the excess pressure release valve 1 and the larger the release flow rate per unit time.

(Example 5 (1) to (6))
[Fabrication] The three types of EPDM-containing raw material compositions obtained in Preparation Examples 2, 5, and 7 were used, and after press vulcanization at 170 ° C for 10 minutes, secondary vulcanization was performed at 170 ° C for 30 minutes. Excess pressure relief valve 1 was produced in the same manner as in Example 1, except that a total of six types of dome-shaped elastic bodies 20 having a body thickness of 0.3 mm or 0.4 mm were produced.
[Functional Evaluation] In order to measure the overpressure value (relief pressure) that can be opened for each of the overpressure release valves 1, the same operating pressure measurement test as in Example 1 was performed. In Examples 5 (4) and (5), the desired working pressure was 90 to 110 kPa, and the variation of the working pressure was examined for three lots. The measurement results of the operating pressure measurement test of the excess pressure release valve 1 are shown in Table 6 below.

  As is apparent from Table 6, the harder the dome-shaped elastic body is, the higher the operating pressure of the overpressure release valve 1 is. The thicker the dome-type elastic body is, the higher the operating pressure of the overpressure release valve 1 is. I found it expensive. Moreover, the variation for each lot was extremely small, and the fluctuation range was about ± 3 kPa on average.

(Example 6 (1) to (10))
[Fabrication] The four types of EPDM-containing raw material compositions obtained in Preparation Examples 2, 5, 6 and 7 were used, and press vulcanization was performed at 170 ° C. for 10 minutes, and then at 170 ° C. for 30 minutes. Except for producing 10 types of dome-shaped elastic bodies 20 having a body thickness of 0.3 mm, 0.4 mm, 0.5 mm, or 0.6 mm by subsequent vulcanization, the same as in Example 1, An overpressure release valve 1 was produced.
[Functional Evaluation] In order to measure the overpressure value (relief pressure) that can be opened for each of the overpressure release valves 1, the same operating pressure measurement test as in Example 1 was performed. The measurement results of the operating pressure measurement test of the excess pressure release valve 1 are shown in the following Table 7 and FIG. 6 as five average values.

  As is clear from Table 7 and FIG. 6A, if the body thickness of the dome-shaped elastic body when uncompressed is the same, the harder the dome-shaped elastic body is, the harder the operating pressure of the overpressure release valve 1 is. Is high and shows a positive correlation. On the other hand, as is clear from Table 7 and FIG. 6B, if the dome-shaped elastic body has the same uncompressed hardness, the dome-shaped elastic body is uncompressed. The thicker the body thickness, the higher the operating pressure of the overpressure release valve 1, indicating a positive correlation.

(Example 7 (1) to (2))
[Preparation] The two EPDM-containing raw material compositions obtained in Preparation Examples 5 and 7 were used, and press vulcanization was performed at 170 ° C for 10 minutes, followed by secondary vulcanization at 170 ° C for 30 minutes. Excess pressure relief valve 1 was produced in the same manner as in Example 1, except that a plurality of lots of two types of dome-shaped elastic bodies 20 having a body thickness of 0.3 mm or 0.4 mm were produced.
[Functional Evaluation] In order to measure the overpressure value (relief pressure) that can be opened for each of the overpressure release valves 1, after 2 weeks from the production of the dome-shaped elastic body, the same operating pressure measurement test as in Example 1 Went. The measurement results of the operating pressure measurement test of the excess pressure release valve 1 are shown in Table 8 below.

  As is apparent from Tables 6 and 8, the dome-shaped elastic body was vulcanized rather than the case where the operating pressure of the overpressure release valve 1 was measured on the next day after the dome-shaped elastic body was vulcanized. When the operating pressure of the overpressure release valve 1 is measured after two weeks have elapsed, the operating pressure is increased by several kPa. This is considered to be because the intermolecular structure is unstable and flexible immediately after the production of the dome-shaped elastic body, but the intermolecular structure is stabilized and the cured state is settled after two weeks or more. In general, the thicker the uncompressed body thickness of the dome-shaped elastic body, the smaller the variation in operating pressure.

(Example 8)
[Preparation] Using the EPDM-containing raw material composition obtained in Preparation Example 7 and press vulcanizing at 170 ° C. for 10 minutes, followed by secondary vulcanization at 170 ° C. for 30 minutes, resulting in 0.3 mm Excess pressure relief valve 1 was produced in the same manner as in Example 1 except that the dome-shaped elastic body 20 having a body thickness of 10 mm was produced.
[Functional evaluation] In order to measure the overpressure value (relief pressure) that can be opened for each of the overpressure release valves 1, after 7 days from the production of the dome-shaped elastic body, the number of repeated measurements is 400 times or more. The operating pressure measurement test was performed in the same manner as in Example 1 except that was set at room temperature (22 ° C.). The measurement result of the operating pressure measurement test of the excess pressure release valve 1 is shown in FIG.

  As apparent from FIG. 7, the operating pressure continued to decrease slightly until the number of repetitions was about 200, but remained almost unchanged up to 400 times thereafter. In addition, it could be used without changing up to about 50,000 times.

(Example 9 (1) to (14))
[Preparation] The seven types of EPDM-containing raw material compositions obtained in Preparation Examples 1 to 7 were used, and they were press vulcanized at 170 ° C for 10 minutes, and then secondary vulcanized at 170 ° C for 30 minutes. When the dome-shaped elastic body 20 is not compressed, the height H is 3.1 mm, the outer diameter D ₁ including the flange 25 is 7.3 mm, the outer diameter D ₂ not including the flange 25 is 6.2 mm, The diameter D ₃ of the thick portion 22 is 3 mm, the body thickness t ₁ is 0.3 mm or 0.5 mm, the maximum thickness of the thick portion 22 is 1.5 mm, the notch 23 has a width of 1 mm and a height of 0. Excess pressure relief valve 1 was prepared in the same manner as in Example 1, except that a total of 14 types of dome-shaped elastic bodies 20 with a height of 4 mm, a collar 25 of 0.8 mm, and a dome radius of 3.25 mm were produced. Was made.
[Functional Evaluation] In order to measure the overpressure value (relief pressure) that can be opened once for each of the overpressure release valves 1, the measurement temperature is set to room temperature (23 ° C.) on the seventh day from the production of the dome-shaped elastic body 20. ), The same operating pressure measurement test as in Example 1 was performed. The measurement results of the operating pressure measurement test of the excess pressure release valve 1 are shown in Tables 9 to 10 below and FIG.

  As is clear from Tables 9 to 10 and FIG. 8, the working pressure is positively correlated with the Shore A hardness of the dome-shaped elastic body 20 when the dome-shaped elastic body 20 is uncompressed for each body thickness when the dome-shaped elastic body 20 is not compressed. Was showing.

  When a battery or a capacitor in which such an overpressure release valve 1 is attached to the sealed container 40 is manufactured as shown in FIG. 9, the excess pressure inside the sealed container 40 can be released as a check valve, and the sealed container 40 can be released from the outside. We were able to prevent moisture and moisture from entering inside.

  Even if the excessive pressure release valve of the present invention is small, it can safely release excessive pressure from low pressure to high pressure, so various batteries such as fuel cells, secondary batteries and lithium ion batteries, electric double layer capacitors, It is used as a safety valve or a check valve for opening excess pressure of various capacitors such as lithium ion capacitors, hydrogen fuel produced or supplied, and the like. It can also be used as a safety valve that releases excess gas from containers for sparkling beverages such as beer and carbonated beverages, storage containers for gas generating reagents such as hydrogen peroxide, air piping and gas piping. . It is particularly useful as a safety valve or check valve for batteries used in small mobile phones, laptop personal computers, portable radios, portable TVs, and portable lights. Among them, portable electronic devices such as small mobile phones and laptop personal computers It is useful as an overpressure release valve for batteries and capacitors incorporated in equipment.

1 is an overpressure release valve, 10 is an inner lid, 11 is a protrusion, 12 is an airtight hole, 20 is a dome-shaped elastic body, 21 is a dome top, 22 is a thick part, 23 is a notch, 24 is a dome opening, 25 is a bag, 26 is an inner space, 30 is an outer lid, 31 is a protrusion, 32 is a protrusion, 33 is an open hole, 35 is a bag, 36 is a cavity, 37 is an opening step portion, 40 is a sealed container, 41 is a thermoplastic resin layer, 42 is an aluminum layer, 43 is a thermoplastic resin layer, the through holes 44, 50 is a battery or a capacitor, D ₁ is the outside diameter of the dome-shaped elastic member including a flange, D ₂ is domed not include a flange The outer diameter of the elastic body, D ₃ is the diameter of the thick portion of the dome-shaped elastic body, D ₄ is the diameter of the airtight hole in the inner lid, H is the height of the dome-shaped elastic body, and t ₁ is the height of the dome-shaped elastic body. fuselage thickness, t ₂ is the thickness of the thick portion of the dome-shaped elastic body, theta is the dome opening 24 of the dome-shaped elastic body 20 It is an angle formed by the line and the central axis direction.

Claims (10)

The inner lid in which the airtight hole to the inside of the hermetic container is conducted, and the outer lid that covers the inner lid and encloses the dome-shaped elastic body and has an open hole to the outside, are integrated with the hermetic seal. is attached to the container, a overpressure relief valve to open the internal overpressure in the external world, the domed resilient member is in contact while having a flange in the inner lid and the dome opening Energized by compression with the outer lid, the airtight hole can be opened with the excess pressure so as to be airtightly closed from the outside at the top of the dome, and the excess pressure is guided to the open hole at the dome opening. An over-pressure release valve characterized by having a notch.   2. The overpressure release valve according to claim 1, wherein the dome top portion of the dome-shaped elastic body is thick at least at a portion blocking the airtight hole. The dome-shaped elastic body is ethylene-propylene-diene rubber, silicone rubber, butyl rubber, halogenated butyl rubber, nitrile rubber, hydrogenated nitrile rubber, fluorine rubber, acrylic rubber, urethane rubber, ethylene-propylene rubber, chloroprene rubber, chlorosulfonated. polyethylene rubber, epichlorohydrin rubber, styrene-butadiene rubber, butadiene rubber, polysulfide rubber, polynorbornene rubber, isoprene rubber, natural rubber, and / or a thermoplastic elastomer, any claim 1-2, characterized in that it has been formed An overpressure relief valve according to claim 1. It said inner lid, said outer lid, the excess pressure release valve according to any one of claims 1 to 3, characterized in that mounted in being incorporated threaded and / or welded sites. The sealed container, thermoplastic resins, metals, or formed by laminating thermoplastic resins and, by being attached by welding site within said lid and / or said outer lid is sealed The overpressure release valve according to any one of claims 1 to 4 , wherein the overpressure release valve is provided. Said outer lid, a reduced diameter at the external side, in the welding site is step portion due to the diameter reduction, the excess of any one of claims 1-5, characterized in that attached to the sealed container Pressure relief valve. The overpressure release according to any one of claims 1 to 6 , wherein the outer lid has a circumferential protrusion along the outer periphery on the inner side, and is attached to the sealed container at a welding site. valve. The overpressure release valve according to any one of claims 1 to 7 , wherein a tangent line at the dome opening of the dome-shaped elastic body is inclined toward the top of the dome. Excess pressure release valve according to any one of claims 1-8 wherein said closed container, characterized in that a capacitor or a battery. A lid inner airtight hole to the interior of the sealed container is conductive, the outer lid are opened open holes to the outside world covers the inner lid is integrally mounted to the closed container, wherein It is used for an overpressure release valve that releases internal excess pressure to the outside world, and is a dome-type elastic body contained in the outer lid, and is in contact with the inner lid and its dome opening while having a ridge. A dome top portion that is formed of an elastic material that is biased by compression by pressing with the outer lid, and that seals the airtight hole from the outside so that the airtight hole can be opened by the excessive pressure by the biasing; A dome-type elastic body for an overpressure release valve, characterized in that the opening has a notch for guiding the overpressure to the open hole.

Images