JP5801941B1 - Cleaning composition, dishwashing method, liquid cleaning composition kit and cartridge cleaning - Google Patents
Cleaning composition, dishwashing method, liquid cleaning composition kit and cartridge cleaning Download PDFInfo
- Publication number
- JP5801941B1 JP5801941B1 JP2014236890A JP2014236890A JP5801941B1 JP 5801941 B1 JP5801941 B1 JP 5801941B1 JP 2014236890 A JP2014236890 A JP 2014236890A JP 2014236890 A JP2014236890 A JP 2014236890A JP 5801941 B1 JP5801941 B1 JP 5801941B1
- Authority
- JP
- Japan
- Prior art keywords
- agent
- cleaning
- cleaning composition
- composition
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】優れた洗浄力及び防食能（特に、アルミ、アルミ合金、銅、銅合金等の金属の腐食抑制効果）を兼ね備える洗浄剤組成物及び食器洗浄方法を提供すること。【解決手段】本発明の洗浄剤組成物は、アルカリ剤を１０〜６０重量％、防食剤を０．０５〜５重量％及びキレート剤を８〜６０重量％含むことを特徴とする。【選択図】なしDisclosed is a cleaning composition and a dishwashing method that have both excellent cleaning power and anticorrosion performance (particularly, the effect of inhibiting the corrosion of metals such as aluminum, aluminum alloys, copper, and copper alloys). The cleaning composition of the present invention is characterized by containing 10 to 60% by weight of an alkali agent, 0.05 to 5% by weight of an anticorrosive agent, and 8 to 60% by weight of a chelating agent. [Selection figure] None
Description
本発明は、洗浄剤組成物、食器洗浄方法、液体洗浄剤組成物用キット及びカートリッジ洗浄剤に関する。 The present invention relates to a cleaning composition, a dishwashing method, a kit for a liquid cleaning composition, and a cartridge cleaning agent.
自動食器洗浄機用の洗浄剤組成物等の洗浄剤組成物として、アルカリ剤を含有する組成物が用いられることが多い。しかしながらこのような洗浄剤組成物を自動食器洗浄機に用いると、被洗物や食器洗浄機に使用されているアルミ又はアルミ合金、銅又は銅合金等の金属が腐食するという問題があった。このため自動食器洗浄機用等の洗浄剤組成物には、洗浄力に優れると共に、金属に対して低腐食性であることが求められている。 As a detergent composition such as a detergent composition for an automatic dishwasher, a composition containing an alkaline agent is often used. However, when such a detergent composition is used in an automatic dishwasher, there has been a problem that metal such as aluminum or aluminum alloy, copper or copper alloy used in an object to be washed or dishwasher corrodes. For this reason, a cleaning composition for an automatic dishwasher or the like is required to have excellent detergency and low corrosiveness to metals.
特許文献１には、洗浄力に優れ、銅板等の腐食防止効果にも優れた金属用アルカリ洗浄剤組成物として、アルカリ剤と防錆剤とキレート剤とを特定の比率で含有し、且つキレート剤の含有量が０．０１〜０．５重量％である洗浄剤組成物が開示されている。 Patent Document 1 contains an alkali agent, a rust inhibitor, and a chelating agent in a specific ratio as an alkali detergent composition for metal having excellent detergency and excellent corrosion prevention effect for copper plates and the like. A detergent composition in which the content of the agent is 0.01 to 0.5% by weight is disclosed.
特許文献２には、（Ａ）ケイ酸塩、（Ｂ）オレフィン単量体と不飽和カルボン酸単量体とのコポリマー及び／又はその塩並びに（Ｃ）不飽和カルボン酸単量体を主体とするポリマー及び／又はその塩を特定の比率で含有する自動食器洗浄機用洗浄剤組成物が開示されている。 Patent Document 2 mainly comprises (A) a silicate, (B) a copolymer of an olefin monomer and an unsaturated carboxylic acid monomer and / or a salt thereof, and (C) an unsaturated carboxylic acid monomer. A detergent composition for an automatic dishwashing machine containing a specific ratio of the polymer and / or salt thereof is disclosed.
しかしながら上記のような洗浄剤組成物についても、洗浄力及び防食能（アルミ、アルミ合金、銅、銅合金等の金属の腐食抑制効果）をより向上させるための改善の余地があった。
本発明は、上記のような課題を解決するためになされたものであり、優れた洗浄力及び防食能（特に、アルミ、アルミ合金、銅、銅合金等の金属の腐食抑制効果）を兼ね備える洗浄剤組成物及び食器洗浄方法を提供することを主な目的とする。
However, the cleaning composition as described above has room for improvement in order to further improve the cleaning power and anticorrosive ability (corrosion inhibiting effect of metals such as aluminum, aluminum alloy, copper, and copper alloy).
The present invention has been made in order to solve the above-described problems, and has excellent cleaning power and corrosion resistance (particularly, corrosion inhibition effect of metals such as aluminum, aluminum alloy, copper and copper alloy). The main object is to provide an agent composition and a dishwashing method.
本発明者は、上記課題を解決するために鋭意研究した結果、洗浄剤組成物にアルカリ剤、防食剤及びキレート剤を配合し、且つこれらの成分の配合量を所定の割合とすることにより、洗浄剤組成物が優れた洗浄力及び防食能を兼ね備えるものとなることを見出した。 As a result of diligent research to solve the above problems, the present inventor blended an alkaline agent, an anticorrosive agent, and a chelating agent with the cleaning composition, and the blending amount of these components is set to a predetermined ratio. It has been found that the detergent composition has excellent detergency and anticorrosive ability.
即ち、本発明の洗浄剤組成物は、
アルカリ剤を１０〜６０重量％、防食剤を０．０５〜５重量％及びキレート剤を８〜６０重量％含むことを特徴とする。
本発明の洗浄剤組成物は、アルカリ剤、防食剤及びキレート剤の配合量が上記割合であることにより、優れた洗浄力及び防食能を兼ね備えるものである。このような洗浄剤組成物は、例えば自動食器洗浄機用洗浄剤組成物として特に好適に用いられる。
That is, the cleaning composition of the present invention is
It contains 10 to 60% by weight of an alkali agent, 0.05 to 5% by weight of an anticorrosive agent, and 8 to 60% by weight of a chelating agent.
The cleaning composition of the present invention has excellent cleaning power and anticorrosive ability when the blending amounts of the alkaline agent, the anticorrosive and the chelating agent are in the above ratio. Such a cleaning composition is particularly preferably used as a cleaning composition for an automatic dishwasher, for example.
本発明の洗浄剤組成物は、さらに、塩素剤を１〜１０重量％含むことが好ましい。
本発明の洗浄剤組成物が塩素剤をこのような量含むと、塩素剤によるさらに優れた洗浄力と高い除菌効果、高い脱臭効果又は漂白効果とを併せ持つことができるため好ましい。
塩素剤はキレート剤と併用すると、銅、銅合金等の金属の腐食を著しく促進するが、本発明においては、アルカリ剤、防食剤及びキレート剤の配合量を上記割合とすることにより、洗浄剤組成物が上記量の塩素剤を含有する場合であっても優れた防食能を発揮することができる。このため本発明の洗浄剤組成物が塩素剤を含有する場合には、塩素剤による優れた洗浄力等を発揮することができ、しかも優れた防食能を発揮することができるという従来の洗浄剤では実現できなかった有利な効果を奏する。
It is preferable that the cleaning composition of the present invention further contains 1 to 10% by weight of a chlorine agent.
It is preferable that the cleaning composition of the present invention contains such a chlorine agent in such an amount because it can have a further excellent detergency with the chlorine agent and a high sterilizing effect, a high deodorizing effect or a bleaching effect.
When the chlorinating agent is used in combination with a chelating agent, the corrosion of metals such as copper and copper alloys is remarkably accelerated. Even when the composition contains the above amount of chlorine agent, excellent anticorrosive ability can be exhibited. For this reason, when the cleaning composition of the present invention contains a chlorine agent, the conventional cleaning agent can exhibit excellent detergency, etc. due to the chlorine agent, and can also exhibit excellent anticorrosive ability. With this, there are advantageous effects that could not be realized.
本発明の洗浄剤組成物においては、上記防食剤がベンゾトリアゾール又はその誘導体、ベンゾイミダゾール又はその誘導体及びベンゾチアゾール又はその誘導体からなる群より選択される少なくとも１種であることが好ましい。
これらの防食剤を使用すると、洗浄剤組成物の防食能がより向上し、銅又は銅合金等の金属の腐食をより充分に抑制することができるため好ましい。
In the cleaning composition of the present invention, the anticorrosive agent is preferably at least one selected from the group consisting of benzotriazole or a derivative thereof, benzimidazole or a derivative thereof, and benzothiazole or a derivative thereof.
Use of these anticorrosive agents is preferable because the anticorrosive ability of the cleaning composition is further improved and corrosion of metals such as copper or copper alloys can be more sufficiently suppressed.
本発明の洗浄剤組成物においては、上記アルカリ剤がアルカリ金属の水酸化物、アルカリ金属のリン酸塩、アルカリ金属の炭酸塩及びケイ酸のアルカリ金属塩からなる群より選択される少なくとも１種の化合物であることが好ましい。アルカリ剤がこのような化合物であると、洗浄剤組成物の防食能がより向上し、アルミ、アルミ合金、銅、銅合金等の金属の腐食をより充分に抑制することができる。 In the cleaning composition of the present invention, the alkali agent is at least one selected from the group consisting of alkali metal hydroxides, alkali metal phosphates, alkali metal carbonates and alkali metal salts of silicic acid. It is preferable that it is a compound of these. When the alkaline agent is such a compound, the anticorrosive ability of the cleaning composition is further improved, and corrosion of metals such as aluminum, aluminum alloy, copper and copper alloy can be more sufficiently suppressed.
本発明におけるケイ酸のアルカリ金属塩としては、ケイ酸ナトリウムが好ましい。
上記アルカリ剤としてケイ酸ナトリウムを使用すると、防食能がさらに向上し、金属の腐食をより充分に抑制することができる。
中でも、優れた防食能を発揮できることから、上記ケイ酸ナトリウムを構成するＮａ２ＯとＳｉＯ２とのモル比が、Ｎａ２Ｏ：ＳｉＯ２＝１：０．５〜１：４であることが好ましい。
As the alkali metal salt of silicic acid in the present invention, sodium silicate is preferred.
When sodium silicate is used as the alkali agent, the anticorrosion ability is further improved, and the corrosion of the metal can be more sufficiently suppressed.
Among them, since the excellent anticorrosive ability can be exhibited, the molar ratio of Na 2 O and SiO 2 constituting the sodium silicate is Na 2 O: SiO 2 = 1: 0.5 to 1: 4. preferable.
本発明の洗浄剤組成物においては、上記アルカリ剤が、ケイ酸のアルカリ金属塩を含み、上記アルカリ剤に含まれるＳｉＯ２と、Ｎａ２Ｏとして換算した上記アルカリ剤とのモル比が、アルカリ剤（Ｎａ２Ｏ換算）：ＳｉＯ２＝１：０．６〜１：４であることが好ましい。
上記アルカリ剤（Ｎａ２Ｏ換算）とアルカリ剤に含まれるＳｉＯ２とのモル比が上記範囲であると、洗浄剤組成物がより防食能に優れるものとなるため好ましい。
In the cleaning composition of the present invention, the alkali agent contains an alkali metal salt of silicic acid, and the molar ratio between SiO 2 contained in the alkali agent and the alkali agent converted as Na 2 O is an alkali. Agent (Na 2 O equivalent): SiO 2 = 1: 0.6 to 1: 4 is preferable.
It is preferable for the molar ratio of the alkali agent (in terms of Na 2 O) and SiO 2 contained in the alkali agent to be in the above range since the cleaning composition will be more excellent in corrosion resistance.
本発明の洗浄剤組成物は、さらに、界面活性剤を０．０１〜１０重量％含むことが好ましい。
また、本発明の洗浄剤組成物は、さらに、平均分子量３,０００〜３００,０００の高分子分散剤を０．１〜２０重量％含むことが好ましい。
界面活性剤及び／又は平均分子量３,０００〜３００,０００の高分子分散剤を上記量含むことにより、洗浄剤組成物の汚れ成分に対する分散力がより向上する。
なお、本明細書中、平均分子量は重量平均分子量（Ｍｗ）である。
The detergent composition of the present invention preferably further contains 0.01 to 10% by weight of a surfactant.
Moreover, it is preferable that the cleaning composition of the present invention further contains 0.1 to 20% by weight of a polymer dispersant having an average molecular weight of 3,000 to 300,000.
By including the surfactant and / or the polymer dispersant having an average molecular weight of 3,000 to 300,000 in the above amount, the dispersibility of the cleaning composition with respect to the soil component is further improved.
In addition, in this specification, an average molecular weight is a weight average molecular weight (Mw).
本発明の洗浄剤組成物は、例えば自動食器洗浄機用洗浄剤組成物として特に好適に用いられる。 The cleaning composition of the present invention is particularly preferably used as a cleaning composition for an automatic dishwasher, for example.
本発明の食器洗浄方法は、本発明の洗浄剤組成物を使用する食器洗浄方法であって、自動食器洗浄機中で、本発明の洗浄剤組成物を水で希釈した液体洗浄剤組成物と食器とを接触させる洗浄工程を含み、上記液体洗浄剤組成物中の上記洗浄剤組成物の濃度は０．０３〜０．５重量％であることを特徴とする。 The dishwashing method of the present invention is a dishwashing method using the cleaning composition of the present invention, and is a liquid cleaning composition obtained by diluting the cleaning composition of the present invention with water in an automatic dishwashing machine. A cleaning step of contacting the tableware, wherein the concentration of the cleaning composition in the liquid cleaning composition is 0.03 to 0.5% by weight.
本発明の食器洗浄方法においては、洗浄工程で使用する液体洗浄剤組成物中の上記洗浄剤組成物の濃度が０．０３〜０．５重量％であると、優れた洗浄効果及び防食効果を得ることができる。 In the dishwashing method of the present invention, when the concentration of the cleaning composition in the liquid cleaning composition used in the cleaning step is 0.03 to 0.5% by weight, an excellent cleaning effect and anticorrosion effect are obtained. Can be obtained.
本発明の食器洗浄方法においては、上記液体洗浄剤組成物が、さらに塩素剤を３〜５０ｐｐｍ含むことが好ましい。上記液体洗浄剤組成物が塩素剤を３〜５０ｐｐｍ含むと、上記効果に加えて、塩素剤によるさらに優れた洗浄力と高い除菌効果、高い脱臭効果又は漂白効果とを発揮することができるため好ましい。 In the dishwashing method of this invention, it is preferable that the said liquid cleaning composition contains 3-50 ppm of chlorine agents further. When the liquid detergent composition contains 3 to 50 ppm of chlorinating agent, in addition to the above-described effects, the chlorinating agent can exhibit further excellent detergency and high sterilizing effect, high deodorizing effect or bleaching effect. preferable.
本発明の液体洗浄剤組成物用キットは、本発明の洗浄剤組成物と塩素剤とを含んで構成され、上記洗浄剤組成物と上記塩素剤とを混合して液体洗浄剤組成物を調製するためのキットであって、上記洗浄剤組成物は、上記塩素剤と分離された状態であることを特徴とする。 The liquid detergent composition kit of the present invention comprises the detergent composition of the present invention and a chlorine agent, and the liquid detergent composition is prepared by mixing the detergent composition and the chlorine agent. The cleaning composition is in a state separated from the chlorinating agent.
本発明の液体洗浄剤組成物用キットは、本発明の洗浄剤組成物と塩素剤とを含む液体洗浄剤組成物を調製するためのものである。このような液体洗浄剤組成物は、上記洗浄剤組成物を含むため、優れた洗浄力及び防食能を兼ね備える洗浄液として使用することができるものである。また、塩素剤を含むことにより、高い除菌効果、高い脱臭効果及び漂白効果を発揮できるものである。さらに、本発明の液体洗浄剤組成物用キットにおいては、洗浄剤組成物と塩素剤とが混合されるまで分離された状態であることにより、保管時等における洗浄剤組成物の成分や塩素剤の分解を防止することができるという効果も奏する。 The kit for liquid cleaning composition of this invention is for preparing the liquid cleaning composition containing the cleaning composition of this invention, and a chlorine agent. Since such a liquid cleaning composition contains the said cleaning composition, it can be used as a cleaning liquid which has the outstanding cleaning power and anticorrosion ability. Moreover, by including a chlorine agent, a high sterilizing effect, a high deodorizing effect and a bleaching effect can be exhibited. Furthermore, in the kit for the liquid cleaning composition of the present invention, the cleaning composition component and the chlorinating agent at the time of storage or the like can be obtained by being separated until the cleaning composition and the chlorinating agent are mixed. The effect that decomposition | disassembly of can be prevented is also show | played.
本発明のカートリッジ洗浄剤は、内容物の供給口部を有する水不溶性の容器を、上記供給口部を下向きに設置し、上記供給口部へ水が噴射されて内容物を溶かしながら供給する方式の自動食器洗浄機用のカートリッジ洗浄剤であって、上記容器は、容器本体と中蓋体と外蓋体とからなり、上記内容物は、本発明の洗浄剤組成物と、塩素剤とを含み、上記洗浄剤組成物は、所定形状に成形された固形体、粒状体又は粉状体からなり、上記塩素剤は、所定形状に成形された固形体、粒状体又は粉状体からなり、上記容器本体には、上記洗浄剤組成物が収容されており、上記中蓋体には、上記塩素剤が収容されており、上記容器本体と上記中蓋体との間には、上記塩素剤又は上記洗浄剤組成物の移動を防止する仕切りが設けられていることを特徴とする。 The cartridge cleaning agent of the present invention is a system in which a water-insoluble container having a content supply port is installed with the supply port facing downward, and water is injected into the supply port while melting the content. A cartridge cleaner for an automatic dishwashing machine, wherein the container comprises a container body, an inner lid body, and an outer lid body, and the contents include the detergent composition of the present invention and a chlorine agent. The cleaning composition is composed of a solid body, a granular body or a powdery body molded into a predetermined shape, and the chlorinating agent is composed of a solid body, a granular body or a powdered body molded into a predetermined shape, The container body contains the cleaning composition, the inner lid contains the chlorine agent, and the chlorine agent is placed between the container body and the inner lid. Or a partition for preventing movement of the cleaning composition is provided. That.
本発明のカートリッジ洗浄剤を食器等の洗浄に用いると、本発明の洗浄剤組成物と塩素剤とを含む洗浄液により食器等を洗浄することができる。このような洗浄液は、上記洗浄剤組成物を含むため、優れた洗浄力及び防食能を兼ね備えるものである。また、塩素剤を含むことにより、高い除菌効果、高い脱臭効果及び漂白効果を発揮できるものである。 When the cartridge cleaning agent of the present invention is used for cleaning tableware and the like, the tableware and the like can be cleaned with a cleaning liquid containing the cleaning composition of the present invention and a chlorine agent. Since such a cleaning liquid contains the said cleaning composition, it has the outstanding cleaning power and anti-corrosion ability. Moreover, by including a chlorine agent, a high sterilizing effect, a high deodorizing effect and a bleaching effect can be exhibited.
また、本発明のカートリッジ洗浄剤では、塩素剤は、容器本体の内部には配設されておらず、中蓋体に収容されており、洗浄剤組成物は、容器本体の内部に収容されており、容器本体と中蓋体との間には、塩素剤又は洗浄剤組成物の移動を防止する仕切りが設けられているので、カートリッジ洗浄剤の製造時には洗浄剤組成物と塩素剤とが全く接触しない状態で製造することができ、塩素剤や洗浄剤組成物の一部の分解を防止することができる。
さらに、塩素剤と洗浄剤組成物とは仕切りにより分離された状態で配置されているので、簡易に製造することができ、安価かつ安全に製造が可能である。
Further, in the cartridge cleaning agent of the present invention, the chlorine agent is not disposed inside the container body, but is stored in the inner lid body, and the cleaning composition is stored in the container body. In addition, since a partition for preventing the movement of the chlorine agent or the cleaning composition is provided between the container main body and the inner lid body, the cleaning composition and the chlorine agent are completely removed when the cartridge cleaning agent is manufactured. It can manufacture in the state which does not contact, and can prevent partial decomposition | disassembly of a chlorine agent or a cleaning composition.
Furthermore, since the chlorine agent and the cleaning composition are arranged in a state separated by a partition, they can be easily manufactured, and can be manufactured inexpensively and safely.
さらに、本発明のカートリッジ洗浄剤では、本体容器の内部に収容する洗浄剤組成物や中蓋体に収容する塩素剤の量を調節することにより、噴射水の温度が低くても、容易に塩素剤の供給量を適量の範囲に制御することができる。従って、洗浄中に塩素剤を充分に自動食器洗浄機内に供給することができるとともに、過剰に塩素剤が供給されるのを防止することができる。 Furthermore, in the cartridge cleaning agent of the present invention, by adjusting the amount of the cleaning agent composition contained in the main body container and the amount of the chlorine agent contained in the inner lid, chlorine can be easily obtained even when the temperature of the jet water is low. The supply amount of the agent can be controlled within an appropriate range. Therefore, it is possible to sufficiently supply the chlorine agent into the automatic dishwashing machine during cleaning, and to prevent excessive supply of the chlorine agent.
本発明の洗浄剤組成物は、洗浄力に優れ、かつ防食能に優れるものである。
本発明の洗浄剤組成物は、例えば自動食器洗浄機用の洗浄剤として好適である。
The cleaning composition of the present invention has excellent detergency and anticorrosive ability.
The cleaning composition of the present invention is suitable as a cleaning agent for an automatic dishwasher, for example.
以下、本発明の実施形態について具体的に説明する。しかしながら、本発明は、以下の実施形態に限定されるものではなく、本発明の要旨を変更しない範囲において適宜変更して適用することができる。 Hereinafter, embodiments of the present invention will be specifically described. However, the present invention is not limited to the following embodiments, and can be applied with appropriate modifications without departing from the scope of the present invention.
本発明の洗浄剤組成物は、アルカリ剤を１０〜６０重量％、防食剤を０．０５〜５重量％及びキレート剤を８〜６０重量％含む。
本明細書中、洗浄剤組成物の各成分の配合量は、特に断らない場合には洗浄剤組成物に対する重量％である。
上記アルカリ剤、防食剤及びキレート剤は、それぞれ１種のみ用いてもよく、２種以上を併用してもよい。
The cleaning composition of the present invention contains 10 to 60% by weight of an alkaline agent, 0.05 to 5% by weight of an anticorrosive agent and 8 to 60% by weight of a chelating agent.
In the present specification, the blending amount of each component of the cleaning composition is wt% with respect to the cleaning composition unless otherwise specified.
Each of the alkali agent, anticorrosive agent and chelating agent may be used alone or in combination of two or more.
上記アルカリ剤としては、水溶性のアルカリ剤であればよく、例えば、アルカリ金属塩又はアルカリ土類金属塩を用いることができる。アルカリ金属塩としては、アルカリ金属の水酸化物、アルカリ金属のリン酸塩、アルカリ金属の炭酸塩及びケイ酸のアルカリ金属塩からなる群より選択される少なくとも１種の化合物が好ましく、例えば、水酸化ナトリウム、水酸化カリウム等のアルカリ金属の水酸化物；リン酸三ナトリウム等のアルカリ金属のリン酸塩；炭酸ナトリウム、炭酸カリウム、炭酸水素ナトリウム、炭酸水素カリウム等のアルカリ金属の炭酸塩；ケイ酸ナトリウム（メタケイ酸ナトリウム、セスキケイ酸ナトリウム、オルソケイ酸ナトリウム、ケイ酸ソーダ１号、ケイ酸ソーダ２号、ケイ酸ソーダ３号、ケイ酸ソーダ４号）、ケイ酸カリウム（メタケイ酸カリウム、セスキケイ酸カリウム、オルソケイ酸カリウム）等のケイ酸のアルカリ金属塩が好ましい。これらのアルカリ剤は、水和物となっていてもよい。中でも、ケイ酸のアルカリ金属塩がより好ましく、ケイ酸ナトリウムがさらに好ましい。なお、後記するキレート剤として例示される化合物は、本発明におけるアルカリ剤には含まれない。 The alkaline agent may be a water-soluble alkaline agent. For example, an alkali metal salt or an alkaline earth metal salt can be used. The alkali metal salt is preferably at least one compound selected from the group consisting of alkali metal hydroxides, alkali metal phosphates, alkali metal carbonates, and alkali metal salts of silicic acid. Alkali metal hydroxides such as sodium oxide and potassium hydroxide; Alkali metal phosphates such as trisodium phosphate; Alkali metal carbonates such as sodium carbonate, potassium carbonate, sodium bicarbonate and potassium bicarbonate; Sodium silicate (sodium metasilicate, sodium sesquisilicate, sodium orthosilicate, sodium silicate 1, sodium silicate 2, sodium silicate 3, sodium silicate 4), potassium silicate (potassium metasilicate, sesquisilicate) An alkali metal salt of silicic acid such as potassium or potassium orthosilicate) is preferred. These alkaline agents may be hydrated. Among these, an alkali metal salt of silicic acid is more preferable, and sodium silicate is more preferable. In addition, the compound illustrated as a chelating agent mentioned later is not contained in the alkaline agent in this invention.
上記ケイ酸ナトリウムを構成するＮａ２ＯとＳｉＯ２とのモル比は、Ｎａ２Ｏ：ＳｉＯ２＝１：０．５〜１：４であることが好ましく、１：０．６〜１：４がより好ましい。Ｎａ２ＯとＳｉＯ２とのモル比がこのようなケイ酸ナトリウムを用いると、洗浄剤組成物の防食能がさらに向上する。Ｎａ２ＯとＳｉＯ２とのモル比は、さらに好ましくはＮａ２Ｏ：ＳｉＯ２＝１：０．７〜１：３．５である。 The molar ratio of Na 2 O and SiO 2 constituting the sodium silicate is preferably Na 2 O: SiO 2 = 1: 0.5 to 1: 4, and 1: 0.6 to 1: 4. Is more preferable. When such a sodium silicate has a molar ratio of Na 2 O to SiO 2 , the anticorrosive ability of the cleaning composition is further improved. The molar ratio of Na 2 O and SiO 2 is more preferably Na 2 O: SiO 2 = 1: 0.7 to 1: 3.5.
本発明の洗浄剤組成物においては、上記アルカリ剤が、ケイ酸のアルカリ金属塩を含むことが好ましい。この場合に、上記アルカリ剤に含まれるＳｉＯ２と、Ｎａ２Ｏとして換算した上記アルカリ剤とのモル比が、アルカリ剤（Ｎａ２Ｏ換算）：ＳｉＯ２＝１：０．６〜１：４であることが好ましい。上記アルカリ剤に含まれるＳｉＯ２と、アルカリ剤（Ｎａ２Ｏ換算）とのモル比が上記範囲であると、洗浄剤組成物がより防食能に優れるものとなる。上記アルカリ剤に含まれるＳｉＯ２と、アルカリ剤（Ｎａ２Ｏ換算）とのモル比（アルカリ剤（Ｎａ２Ｏ換算）：ＳｉＯ２）は、より好ましくは１：０．７〜１：４であり、更に好ましくは１：０．８〜１：４である。 In the cleaning composition of the present invention, the alkali agent preferably contains an alkali metal salt of silicic acid. In this case, the molar ratio of SiO 2 contained in the alkali agent to the alkali agent converted as Na 2 O is alkali agent (Na 2 O conversion): SiO 2 = 1: 0.6 to 1: 4. It is preferable that When the molar ratio between the SiO 2 contained in the alkali agent and the alkali agent (Na 2 O conversion) is in the above range, the cleaning composition has a more excellent anticorrosive ability. The molar ratio (alkali agent (Na 2 O equivalent): SiO 2 ) between SiO 2 contained in the alkali agent and the alkali agent (Na 2 O equivalent) is more preferably 1: 0.7 to 1: 4. Yes, more preferably 1: 0.8 to 1: 4.
上記アルカリ剤の含有量は、洗浄剤組成物に対して１０〜６０重量％である。アルカリ剤が１０重量％未満であると、洗浄剤組成物の洗浄力が不充分となる。アルカリ剤が６０重量％を超えると、洗浄剤組成物の防食能が不充分となる。上記アルカリ剤の含有量は、好ましくは２０〜５０重量％である。 Content of the said alkali agent is 10 to 60 weight% with respect to a cleaning composition. When the alkaline agent is less than 10% by weight, the cleaning power of the cleaning composition is insufficient. If the alkali agent exceeds 60% by weight, the anticorrosive ability of the cleaning composition will be insufficient. The content of the alkali agent is preferably 20 to 50% by weight.
上記防食剤としては、銅又は銅合金に対する防食剤を用いることが好ましい。このような防食剤として、例えば、ベンゾトリアゾール又はその誘導体（例えば、ベンゾトリアゾール、トリルトリアゾール、５−ドデシルベンゾトリアゾール、５−オクチルベンゾトリアゾール、５−ヘキシルベンゾトリアゾール、５−ブチルベンゾトリアゾール、５−メチルベンゾトリアゾール、４−カルボキシベンゾトリアゾール、５−カルボキシベンゾトリアゾール、カルボキシベンゾトリアゾールメチルエステル、カルボキシベンゾトリアゾールブチルエステル、カルボキシベンゾトリアゾールヘキシルエステル、ベンゾトリアゾールオクチルエステル、ジカルボキシプロピルベンゾトリアゾール等）、ベンゾイミダゾール又はその誘導体（例えば、ベンゾイミダゾール、２−メルカプトベンゾイミダゾール、チアゾリルベンゾイミダゾール、チアベンダゾール等）、ベンゾチアゾール又はその誘導体（例えば、ベンゾチアゾール、２−メチルベンゾチアゾール、２−アミノベンゾチアゾール、２−メルカプトベンゾチアゾール等）を好適に使用することができる。中でも、ベンゾイミダゾール、ベンゾトリアゾール、トリルトリアゾールが好ましく、ベンゾイミダゾールがより好ましい。 As said anticorrosive, it is preferable to use the anticorrosive with respect to copper or a copper alloy. Examples of such anticorrosives include benzotriazole or its derivatives (for example, benzotriazole, tolyltriazole, 5-dodecylbenzotriazole, 5-octylbenzotriazole, 5-hexylbenzotriazole, 5-butylbenzotriazole, 5-methyl Benzotriazole, 4-carboxybenzotriazole, 5-carboxybenzotriazole, carboxybenzotriazole methyl ester, carboxybenzotriazole butyl ester, carboxybenzotriazole hexyl ester, benzotriazole octyl ester, dicarboxypropylbenzotriazole, etc.), benzimidazole or its Derivatives (eg, benzimidazole, 2-mercaptobenzimidazole, thiazolylbenzoy Imidazole, thiabendazole, etc.), benzothiazole or derivatives thereof (e.g., benzothiazole, 2-methyl-benzothiazole, 2-aminobenzothiazole, 2-mercaptobenzothiazole, etc.) can be suitably used. Among these, benzimidazole, benzotriazole, and tolyltriazole are preferable, and benzimidazole is more preferable.
上記防食剤の含有量は、洗浄剤組成物に対して０．０５〜５重量％である。防食剤が０．０５重量％未満であると、洗浄剤組成物の防食能が不充分となる。防食剤が５重量％を超えると、防食剤特有の臭いの影響が強くなる。上記防食剤の含有量は、好ましくは０．１〜２重量％である。 The content of the anticorrosive is 0.05 to 5% by weight with respect to the cleaning composition. If the anticorrosive agent is less than 0.05% by weight, the anticorrosive ability of the cleaning composition will be insufficient. When the anticorrosive agent exceeds 5% by weight, the influence of the odor peculiar to the anticorrosive agent becomes strong. The content of the anticorrosive is preferably 0.1 to 2% by weight.
上記キレート剤としては、アミノカルボン酸系、ヒドロキシカルボン酸系、リン酸系、エーテルカルボン酸塩、ホスホン酸系等のキレート剤が挙げられる。なお、後記する平均分子量３,０００〜３００,０００の高分子分散剤として例示されるポリアクリル酸ナトリウム等の化合物は、本発明におけるキレート剤には含まれない。 Examples of the chelating agent include aminocarboxylic acid-based, hydroxycarboxylic acid-based, phosphoric acid-based, ether carboxylate, and phosphonic acid-based chelating agents. A compound such as sodium polyacrylate exemplified as a polymer dispersant having an average molecular weight of 3,000 to 300,000 described later is not included in the chelating agent in the present invention.
上記アミノカルボン酸系のキレート剤としては、エチレンジアミン四酢酸（ＥＤＴＡ）、ニトリロ三酢酸（ＮＴＡ）、メチルグリシン二酢酸（ＭＧＤＡ）、ジエチレントリアミン五酢酸（ＤＴＰＡ）、ヒドロキシエチルエチレンジアミン三酢酸（ＨＥＤＴＡ）、トリエチレンテトラミン六酢酸（ＴＴＨＡ）、グルタミン酸二酢酸（ＧＬＤＡ）、ヒドロキシエチルイミノ二酢酸（ＨＩＤＡ）、ジヒドロキシエチルグリシン（ＤＨＥＧ）、１，３−プロパンジアミン四酢酸（ＰＤＴＡ）、１，３−ジアミノ−２−ヒドロキシプロパン六酢酸（ＤＰＴＡ−ＯＨ）、アスパラギン酸二酢酸（ＡＳＤＡ）、エチレンジアミンコハク酸（ＥＤＤＳ）又はこれらの塩等が挙げられる。 Examples of the aminocarboxylic acid-based chelating agents include ethylenediaminetetraacetic acid (EDTA), nitrilotriacetic acid (NTA), methylglycine diacetic acid (MGDA), diethylenetriaminepentaacetic acid (DTPA), hydroxyethylethylenediaminetriacetic acid (HEDTA), Ethylenetetramine hexaacetic acid (TTHA), glutamic acid diacetic acid (GLDA), hydroxyethyliminodiacetic acid (HIDA), dihydroxyethylglycine (DHEG), 1,3-propanediaminetetraacetic acid (PDTA), 1,3-diamino-2 -Hydroxypropane hexaacetic acid (DPTA-OH), aspartic acid diacetic acid (ASDA), ethylenediaminesuccinic acid (EDDS), or a salt thereof.
上記ヒドロキシカルボン酸系のキレート剤としては、例えば、リンゴ酸、コハク酸、クエン酸、乳酸、酒石酸、グルコン酸又はこれらの塩（例えば、ナトリウム塩、カリウム塩、マグネシウム塩、カルシウム塩等）が挙げられる。具体的には、クエン酸ナトリウム、クエン酸カルシウム等のクエン酸塩；リンゴ酸ナトリウム、リンゴ酸カルシウム等のリンゴ酸塩；グルコン酸ナトリウム、グルコン酸カルシウム等のグルコン酸塩等が挙げられる。 Examples of the hydroxycarboxylic acid-based chelating agent include malic acid, succinic acid, citric acid, lactic acid, tartaric acid, gluconic acid, and salts thereof (for example, sodium salt, potassium salt, magnesium salt, calcium salt, etc.). It is done. Specific examples include citrates such as sodium citrate and calcium citrate; malates such as sodium malate and calcium malate; and gluconates such as sodium gluconate and calcium gluconate.
上記リン酸系のキレート剤としては、トリポリリン酸、ヘキサメタリン酸塩等が挙げられる。
上記ホスホン酸系のキレート剤としては、ヒドロキシエチリデンジホスホン酸（ＨＥＤＰ）、ニトリロトリスメチレンホスホン酸（ＮＴＭＰ）、ホスホノブタントリカルボン酸（ＰＢＴＣ）、エチレンジアミンテトラメチレンホスホン酸（ＥＤＴＭＰ）又はこれらの塩等が挙げられる。
Examples of the phosphoric acid-based chelating agent include tripolyphosphoric acid and hexametaphosphate.
Examples of the phosphonic acid-based chelating agent include hydroxyethylidene diphosphonic acid (HEDP), nitrilotrismethylenephosphonic acid (NTMP), phosphonobutanetricarboxylic acid (PBTC), ethylenediaminetetramethylenephosphonic acid (EDTMP), and salts thereof. Is mentioned.
本発明におけるキレート剤としては、アミノカルボン酸系、ホスホン酸系等のキレート剤が好ましく、ニトリロ三酢酸、エチレンジアミン四酢酸、メチルグリシン二酢酸、エチレンジアミンテトラメチレンホスホン酸、ホスホノブタントリカルボン酸又はこれらの塩等がより好ましく、ニトリロ三酢酸、エチレンジアミン四酢酸又はこれらの塩がさらに好ましい。 As the chelating agent in the present invention, aminocarboxylic acid-based and phosphonic acid-based chelating agents are preferable, such as nitrilotriacetic acid, ethylenediaminetetraacetic acid, methylglycinediacetic acid, ethylenediaminetetramethylenephosphonic acid, phosphonobutanetricarboxylic acid, or these. A salt or the like is more preferable, and nitrilotriacetic acid, ethylenediaminetetraacetic acid or a salt thereof is more preferable.
上記キレート剤の含有量は、洗浄剤組成物に対して８〜６０重量％である。キレート剤が８重量％未満であると、洗浄剤組成物の洗浄力が不充分となる。キレート剤が６０重量％を超えると、洗浄剤組成物の防食能が不充分となる。上記キレート剤の含有量は、好ましくは３０〜５０重量％である。 The content of the chelating agent is 8 to 60% by weight with respect to the cleaning composition. When the chelating agent is less than 8% by weight, the cleaning power of the cleaning composition becomes insufficient. When the chelating agent exceeds 60% by weight, the anticorrosive ability of the cleaning composition becomes insufficient. The content of the chelating agent is preferably 30 to 50% by weight.
本発明の洗浄剤組成物は、塩素剤を含むことが好ましい。
上記塩素剤としては、例えば、塩素化イソシアヌル酸塩（塩素化イソシアヌル酸ナトリウム（ジクロロイソシアヌル酸ナトリウム）、塩素化イソシアヌル酸カリウム（ジクロロイソシアヌル酸カリウム）等）、トリクロロイソシアヌル酸、次亜塩素酸塩（次亜塩素酸ナトリウム、次亜塩素酸カリウム、次亜塩素酸カルシウム等）等が挙げられる。これらの塩素剤は１種を用いてもよく、２種以上を併用してもよい。また、これらの塩素剤は、水和物であってもよい。中でも、塩素剤として、塩素化イソシアヌル酸塩、トリクロロイソシアヌル酸が好ましく、塩素化イソシアヌル酸ナトリウムがより好ましい。
The cleaning composition of the present invention preferably contains a chlorine agent.
Examples of the chlorinating agent include chlorinated isocyanurate (chlorinated isocyanurate (sodium dichloroisocyanurate), chlorinated isocyanurate (potassium dichloroisocyanurate), etc.), trichloroisocyanurate, hypochlorite ( Sodium hypochlorite, potassium hypochlorite, calcium hypochlorite, etc.). These chlorine agents may be used alone or in combination of two or more. These chlorine agents may be hydrates. Among these, as the chlorinating agent, chlorinated isocyanurate and trichloroisocyanuric acid are preferable, and chlorinated sodium isocyanurate is more preferable.
本発明の洗浄剤組成物が塩素剤を含む場合、塩素剤の含有量は、洗浄剤組成物に対して１〜１０重量％が好ましい。上記塩素剤の含有量は、水又は結晶水を除いた純分の重量％である。塩素剤が１重量％未満であると、洗浄力と除菌効果、脱臭作用又は漂白作用とにおいて充分な効果が得られない場合がある。塩素剤が１０重量％を超えると、洗浄剤組成物の防食能が低下する場合がある。塩素剤の含有量は、好ましくは２〜５重量％である。 When the cleaning composition of the present invention contains a chlorine agent, the content of the chlorine agent is preferably 1 to 10% by weight with respect to the cleaning composition. Content of the said chlorine agent is weight% of the pure part except water or crystal water. If the chlorinating agent is less than 1% by weight, sufficient effects may not be obtained in detergency, disinfection effect, deodorizing action or bleaching action. When a chlorine agent exceeds 10 weight%, the anti-corrosion ability of a cleaning composition may fall. The content of the chlorine agent is preferably 2 to 5% by weight.
本発明の洗浄剤組成物は、界面活性剤及び／又は平均分子量３,０００〜３００,０００の高分子分散剤を含有することが好ましく、界面活性剤及び平均分子量３,０００〜３００,０００の高分子分散剤を含有することがより好ましい。これらはそれぞれ１種のみ用いてもよく、２種以上を併用してもよい。 The detergent composition of the present invention preferably contains a surfactant and / or a polymer dispersant having an average molecular weight of 3,000 to 300,000, and has a surfactant and an average molecular weight of 3,000 to 300,000. It is more preferable to contain a polymer dispersant. These may be used alone or in combination of two or more.
本発明の洗浄剤組成物に使用される界面活性剤としては、公知の陰イオン界面活性剤、公知の陽イオン界面活性剤、公知の両性界面活性剤、公知の非イオン界面活性剤等を使用することができ、好ましくは非イオン界面活性剤である。非イオン界面活性剤として、例えば、ポリオキシアルキレンモノアルキルエーテル、ポリオキシアルキレンジアルキルエーテル、プルロニック型ブロックポリマー、リバースプルロニック型ブロックポリマー、テトロニック型ブロックポリマー、リバーステトロニック型ブロックポリマー、ポリオキシアルキレンアルキルフェニルエーテル、脂肪酸アルカノールアミド、ポリオキシアルキレン脂肪酸アルカノールアミド、ポリオキシアルキレン脂肪酸エステル、ポリオキシアルキレンソルビタン脂肪酸エステル、ポリグリセリン脂肪酸エステル、ソルビタン脂肪酸エステル、ショ糖脂肪酸エステル、アルキルポリグリコシド、ポリオキシエチレンメチルエーテル脂肪酸エステル、ポリオキシアルキレンアルキルアミン等が挙げられる。中でも、ポリオキシアルキレンモノアルキルエーテルが好ましい。 As the surfactant used in the cleaning composition of the present invention, a known anionic surfactant, a known cationic surfactant, a known amphoteric surfactant, a known nonionic surfactant, etc. are used. Preferably, it is a nonionic surfactant. Nonionic surfactants include, for example, polyoxyalkylene monoalkyl ether, polyoxyalkylene dialkyl ether, pluronic block polymer, reverse pluronic block polymer, tetronic block polymer, reverse tetronic block polymer, polyoxyalkylene alkyl Phenyl ether, fatty acid alkanolamide, polyoxyalkylene fatty acid alkanolamide, polyoxyalkylene fatty acid ester, polyoxyalkylene sorbitan fatty acid ester, polyglycerin fatty acid ester, sorbitan fatty acid ester, sucrose fatty acid ester, alkyl polyglycoside, polyoxyethylene methyl ether Examples include fatty acid esters and polyoxyalkylene alkylamines. Among these, polyoxyalkylene monoalkyl ether is preferable.
上記界面活性剤の含有量は、洗浄剤組成物に対して０．０１〜１０重量％であることが好ましい。界面活性剤の含有量が上記範囲であると、洗浄剤組成物の洗浄力がより向上するため好ましい。界面活性剤の含有量は、２〜８重量％がより好ましい。 The content of the surfactant is preferably 0.01 to 10% by weight with respect to the cleaning composition. It is preferable for the content of the surfactant to be in the above range since the cleaning power of the cleaning composition is further improved. The content of the surfactant is more preferably 2 to 8% by weight.
上記平均分子量３,０００〜３００,０００の高分子分散剤としては、例えば、ポリアクリル酸、ポリアコニット酸、ポリイタコン酸、ポリシトラコン酸、ポリフマル酸、ポリマレイン酸、ポリメタコン酸、ポリ−α−ヒドロキシアクリル酸、ポリビニルホスホン酸、スルホン化ポリマレイン酸、オレフィン−マレイン酸共重合体、無水マレイン酸ジイソブチレン共重合体、無水マレイン酸スチレン共重合体、無水マレイン酸メチルビニルエーテル共重合体、無水マレイン酸エチレン共重合体、無水マレイン酸エチレンクロスリンク共重合体、無水マレイン酸アクリル酸共重合体、無水マレイン酸酢酸ビニル共重合体、無水マレイン酸アクリロニトリル共重合体、無水マレイン酸アクリル酸エステル共重合体、無水マレイン酸ブタジエン共重合体、無水マレイン酸イソプレン共重合体、無水マレイン酸と一酸化炭素から誘導されるポリ−β−ケトカルボン酸、イタコン酸、エチレン共重合体、イタコン酸アコニット酸共重合体、イタコン酸マレイン酸共重合体、イタコン酸アクリル酸共重合体、マロン酸メチレン共重合体、イタコン酸フマール酸共重合体、エチレングリコールエチレンテレフタレート共重合体、ビニルピロリドン酢酸ビニル共重合体、これらの金属塩等が挙げられる。
金属塩としては、例えば、カリウム、ナトリウム等のアルカリ金属の塩；マグネシウム、カルシウム等のアルカリ土類金属の塩を挙げることができる。中でも、アルカリ金属の塩が好ましく、ナトリウム塩又はカリウム塩がより好ましい。
本発明における３,０００〜３００,０００の高分子分散剤としては、ポリアクリル酸塩が好ましく、ポリアクリル酸ナトリウムがより好ましい。
Examples of the polymer dispersant having an average molecular weight of 3,000 to 300,000 include, for example, polyacrylic acid, polyaconitic acid, polyitaconic acid, polycitraconic acid, polyfumaric acid, polymaleic acid, polymethaconic acid, and poly-α-hydroxyacrylic. Acid, polyvinylphosphonic acid, sulfonated polymaleic acid, olefin-maleic acid copolymer, maleic anhydride diisobutylene copolymer, maleic anhydride styrene copolymer, maleic anhydride methyl vinyl ether copolymer, maleic anhydride ethylene copolymer Polymer, maleic anhydride ethylene cross-linked copolymer, maleic anhydride acrylic copolymer, maleic anhydride vinyl acetate copolymer, maleic anhydride acrylonitrile copolymer, maleic anhydride acrylic ester copolymer, anhydrous Maleic acid butadiene copolymer , Maleic anhydride isoprene copolymer, poly-β-ketocarboxylic acid derived from maleic anhydride and carbon monoxide, itaconic acid, ethylene copolymer, itaconic acid aconitic acid copolymer, itaconic acid maleic acid copolymer Itaconic acid acrylic acid copolymer, malonic acid methylene copolymer, itaconic acid fumaric acid copolymer, ethylene glycol ethylene terephthalate copolymer, vinylpyrrolidone vinyl acetate copolymer, and metal salts thereof.
Examples of the metal salt include salts of alkali metals such as potassium and sodium; alkaline earth metal salts such as magnesium and calcium. Among them, alkali metal salts are preferable, and sodium salts or potassium salts are more preferable.
The polymer dispersant of 3,000 to 300,000 in the present invention is preferably a polyacrylate, and more preferably sodium polyacrylate.
上記平均分子量３,０００〜３００,０００の高分子分散剤の含有量は、洗浄剤組成物に対して０．１〜２０重量％であることが好ましい。高分子分散剤の含有量が上記範囲であると、洗浄剤組成物の洗浄力がより向上するため好ましい。上記高分子分散剤の含有量は、１〜１８重量％がより好ましく、３〜１５重量％がさらに好ましい。 The content of the polymer dispersant having an average molecular weight of 3,000 to 300,000 is preferably 0.1 to 20% by weight with respect to the cleaning composition. It is preferable for the content of the polymer dispersant to be in the above range because the cleaning power of the cleaning composition is further improved. The content of the polymer dispersant is more preferably 1 to 18% by weight, and further preferably 3 to 15% by weight.
本発明の洗浄剤組成物は、必要に応じて溶媒、増量剤、酵素、消泡剤等の洗浄剤組成物に配合される他の成分を含有してもよい。これらは１種のみ用いてもよく、２種以上を併用してもよい。 The cleaning composition of the present invention may contain other components blended in the cleaning composition, such as a solvent, an extender, an enzyme, and an antifoaming agent, as necessary. These may be used alone or in combination of two or more.
上記溶媒としては、水等が挙げられる。
上記増量剤としては、硫酸ナトリウム（芒硝）、粉末シリカ等が挙げられる。
上記酵素としては、プロテアーゼ、エステラーゼ、リパーゼ、ヌクレアーゼ、セルラーゼ、アミラーゼ及びペクチナーゼ等が挙げられる。これらの酵素が含まれていると、酵素の機能により洗浄力が向上する。
上記消泡剤としては、エマルジョン型、オイル型、オイルコンパウンド型、溶液型、自己乳化型等の消泡剤が挙げられる。
Examples of the solvent include water.
Examples of the extender include sodium sulfate (sodium salt) and powdered silica.
Examples of the enzyme include protease, esterase, lipase, nuclease, cellulase, amylase, and pectinase. When these enzymes are contained, the cleaning power is improved by the function of the enzymes.
Examples of the antifoaming agent include emulsion type, oil type, oil compound type, solution type, and self-emulsifying type.
本発明の洗浄剤組成物の剤形は、液体、固体（粉末、顆粒（粒状）、錠剤、タブレット、フレーク又はブロック等）のいずれでもよい。好ましくは、固体であり、粉末、顆粒、ブロック等である。また、本発明の洗浄剤組成物は、カートリッジ洗浄剤等にも好適に使用される。 The dosage form of the cleaning composition of the present invention may be liquid or solid (powder, granules (granular), tablets, tablets, flakes, blocks, etc.). Preferably, it is solid, such as powder, granule, block and the like. The cleaning composition of the present invention is also suitably used for cartridge cleaning agents and the like.
本発明の洗浄剤組成物の製造方法は特に限定されず、剤形に応じて適宜選択すればよい。例えば、上述したアルカリ剤、防食剤及びキレート剤並びに所望により配合される塩素剤、非イオン界面活性剤及び高分子分散剤等を混合又は撹拌等することにより製造することができる。各成分を混合する順番、混合又は撹拌の方法等は特に限定されない。 The manufacturing method of the cleaning composition of the present invention is not particularly limited, and may be appropriately selected depending on the dosage form. For example, it can be produced by mixing or stirring the above-mentioned alkali agent, anticorrosive agent, chelating agent, and optionally added chlorine agent, nonionic surfactant, polymer dispersant and the like. The order of mixing each component, the method of mixing or stirring, etc. are not particularly limited.
例えば、ブロックなどの固形体の洗浄剤組成物を製造する際には、例えば、まず、水及び水以外の洗浄剤組成物の原料を撹拌混合し、スラリー液を調製した後、上記スラリー液を所望の型又は容器等に投入し、冷却して固化させることが好ましい。 For example, when producing a solid detergent composition such as a block, for example, first, water and raw materials of the detergent composition other than water are mixed by stirring to prepare a slurry liquid, and then the slurry liquid is prepared. It is preferable to put into a desired mold or container and cool and solidify.
具体的には、まず、水に水以外の洗浄剤組成物の原料を加えた後、３０〜９０℃に維持し、攪拌することにより、水及び洗浄剤組成物を含むスラリー液を調製する。
水以外の洗浄剤組成物の原料の投入量は、上記スラリー液の全量に対して３５〜１００重量％が好ましい。
次に、上記スラリー液を所望の型又は容器に投入し、その後、上記スラリー液を常温で１〜２４時間放置して固化させ、型又は容器の形状に固化された固形体からなる洗浄剤組成物を製造する。
Specifically, first, after adding the raw material of the cleaning composition other than water to water, the slurry liquid containing water and the cleaning composition is prepared by maintaining at 30 to 90 ° C. and stirring.
The amount of the raw material for the cleaning composition other than water is preferably 35 to 100% by weight based on the total amount of the slurry.
Next, the slurry liquid is charged into a desired mold or container, and then the slurry liquid is left to solidify at room temperature for 1 to 24 hours to be solidified into a mold or container shape. Manufacturing things.
顆粒状（粒状）の洗浄剤組成物を製造する際には、洗浄剤組成物の原料となるアルカリ剤、防食剤及びキレート剤並びに所望により添加される塩素剤、界面活性剤及び高分子分散剤等の粒状原料を混合すればよい。混合にはリボンミキサー、ナウターミキサー、ドラムミキサーが好適に用いられる。
また、粉末状の洗浄剤組成物を製造する際には、洗浄剤組成物の原料となるアルカリ剤、防食剤及びキレート剤並びに所望により添加される塩素剤、界面活性剤及び高分子分散剤等の粉状原料を混合すればよい。混合にはリボンミキサー、ナウターミキサー、ドラムミキサーが好適に用いられる。
When producing a granular (granular) detergent composition, an alkali agent, anticorrosive agent and chelating agent as raw materials for the detergent composition, and optionally added chlorine agent, surfactant and polymer dispersant What is necessary is just to mix granular raw materials, such as. For mixing, a ribbon mixer, a nauter mixer, and a drum mixer are preferably used.
In addition, when producing a powdery cleaning composition, alkaline agents, anticorrosives and chelating agents as raw materials for the cleaning composition, and optionally added chlorine agents, surfactants, polymer dispersing agents, etc. The powdery raw material may be mixed. For mixing, a ribbon mixer, a nauter mixer, and a drum mixer are preferably used.
本発明の洗浄剤組成物は、洗浄力に優れるものであり、かつアルミ、アルミ合金、銅、銅合金等の金属に対する防食能が高いため、例えば、自動食器洗浄機用洗浄剤組成物として好適に用いられる。 The cleaning composition of the present invention is excellent in detergency and has a high anticorrosive ability against metals such as aluminum, aluminum alloy, copper and copper alloy, and is therefore suitable as a cleaning composition for automatic dishwashers, for example. Used for.
本発明の洗浄剤組成物の使用方法としては、例えば食器等を洗浄する場合であれば、洗浄剤組成物を水で希釈した液体洗浄剤組成物を洗浄液として、食器等に接触させて洗浄すればよい。液体洗浄剤組成物における洗浄剤組成物の濃度は、例えば、０．０３〜０．５重量％とすることが好ましい。このような濃度で使用することにより、洗浄液が優れた洗浄力及び防食能を発揮できるため好ましい。また、洗浄に用いる液体洗浄剤組成物（洗浄液）の温度は特に限定されないが、例えば、４０〜７０℃とすることが好ましい。 As a method of using the cleaning composition of the present invention, for example, when cleaning dishes, etc., the cleaning composition is diluted with water, and the cleaning composition is used as a cleaning liquid to be brought into contact with the dishes etc. That's fine. The concentration of the cleaning composition in the liquid cleaning composition is preferably 0.03 to 0.5% by weight, for example. Use at such a concentration is preferable because the cleaning liquid can exhibit excellent cleaning power and corrosion resistance. Moreover, the temperature of the liquid detergent composition (cleaning liquid) used for cleaning is not particularly limited, but is preferably 40 to 70 ° C, for example.
本発明の洗浄剤組成物が塩素剤を含まない場合には、該洗浄剤組成物と塩素剤とを洗浄の際に併用することによっても、本発明の洗浄剤組成物が奏する優れた洗浄力及び防食能に加えて、塩素剤によるさらに優れた洗浄力と高い除菌効果、高い脱臭効果又は漂白効果とを得ることができる。 When the cleaning composition of the present invention does not contain a chlorinating agent, excellent cleaning power exhibited by the cleaning composition of the present invention can be obtained by using the cleaning composition and the chlorinating agent in combination. Further, in addition to the anticorrosive ability, it is possible to obtain a further excellent detergency and high sterilizing effect, high deodorizing effect or bleaching effect by the chlorine agent.
本発明の食器洗浄方法は、本発明の洗浄剤組成物を使用する食器洗浄方法であって、自動食器洗浄機中で、上記洗浄剤組成物を水で希釈した液体洗浄剤組成物と食器とを接触させる洗浄工程を含み、上記液体洗浄剤組成物中の上記洗浄剤組成物の濃度は０．０３〜０．５重量％であることを特徴とする。本発明の食器洗浄方法に用いられる自動食器洗浄機は特に限定されないが、好ましくは業務用自動食器洗浄機である。 The dishwashing method of the present invention is a dishwashing method using the cleaning composition of the present invention, wherein the cleaning composition is diluted with water in an automatic dishwashing machine, and the dishwashing method. And the concentration of the cleaning composition in the liquid cleaning composition is 0.03 to 0.5% by weight. Although the automatic dishwasher used for the dishwashing method of this invention is not specifically limited, Preferably it is a commercial automatic dishwasher.
上記液体洗浄剤組成物中の上記洗浄剤組成物の濃度が０．０３〜０．５重量％であると、液体洗浄剤組成物が優れた洗浄力及び防食能を発揮することができる。上記液体洗浄剤組成物中の上記洗浄剤組成物の濃度は、好ましくは０．０４〜０．３重量％である。 When the concentration of the cleaning composition in the liquid cleaning composition is 0.03 to 0.5% by weight, the liquid cleaning composition can exhibit excellent cleaning power and corrosion resistance. The concentration of the cleaning composition in the liquid cleaning composition is preferably 0.04 to 0.3% by weight.
本発明の食器洗浄方法においては、上記液体洗浄剤組成物が、さらに塩素剤を３〜５０ｐｐｍ含むことが好ましい。本明細書中、液体洗浄剤組成物中の塩素剤の濃度は、以下の方法で測定される有効塩素濃度を意味する。洗浄槽の洗浄剤組成物（洗浄液）を１００ｇサンプリングし、ヨウ化カリウム５ｇと反応させ、０．０１Ｎチオ硫酸ナトリウム水溶液で滴定する。その滴定量Ａ（ｍＬ）、求める有効塩素濃度をＡｖＣＬ（ｐｐｍ）とすると、ＡｖＣＬ（ｐｐｍ）＝Ａ（ｍＬ）×３．５４６で求めることができる。
上記液体洗浄剤組成物が塩素剤を３〜５０ｐｐｍ含むと、塩素剤によるさらに優れた洗浄力と高い除菌効果、高い脱臭効果又は漂白効果とを発揮することができるため好ましい。上記液体洗浄剤組成物中の塩素剤の濃度は、好ましくは５〜４５ｐｐｍである。
In the dishwashing method of this invention, it is preferable that the said liquid cleaning composition contains 3-50 ppm of chlorine agents further. In this specification, the density | concentration of the chlorine agent in a liquid cleaning composition means the effective chlorine concentration measured with the following method. 100 g of the cleaning composition (cleaning liquid) in the cleaning tank is sampled, reacted with 5 g of potassium iodide, and titrated with a 0.01N sodium thiosulfate aqueous solution. When the titration amount A (mL) and the effective chlorine concentration to be obtained are AvCL (ppm), AvCL (ppm) = A (mL) × 3.546 can be obtained.
It is preferable that the liquid detergent composition contains 3 to 50 ppm of a chlorine agent because it can exhibit further excellent detergency and high sterilizing effect, high deodorizing effect or bleaching effect. The concentration of the chlorine agent in the liquid detergent composition is preferably 5 to 45 ppm.
上記塩素剤は、洗浄剤組成物に含まれていたものであってもよく、洗浄剤組成物とは別に添加されたものであってもよい。本発明の食器洗浄方法においては、洗浄剤組成物として、上述した塩素剤を含む洗浄剤組成物を使用してもよく、塩素剤を含まない洗浄剤組成物を使用してもよい。 The chlorine agent may be included in the cleaning composition, or may be added separately from the cleaning composition. In the dishwashing method of the present invention, the cleaning composition containing the above-described chlorine agent may be used as the cleaning composition, or a cleaning composition containing no chlorine agent may be used.
上記洗浄工程において塩素剤を含む洗浄剤組成物を用いる場合には、該洗浄剤組成物の濃度が０．０３〜０．５重量％である液体洗浄剤組成物を調製した場合に、該液体洗浄剤組成物中の塩素剤の濃度が３〜５０ｐｐｍとなるように、塩素剤の配合量を適宜設定することが好ましい。塩素剤及びその好ましい態様は上述したとおりであり、１種又は２種以上を使用することができる。 In the case where a cleaning composition containing a chlorine agent is used in the cleaning step, when the liquid cleaning composition having a concentration of the cleaning composition of 0.03 to 0.5% by weight is prepared, the liquid It is preferable to appropriately set the blending amount of the chlorine agent so that the concentration of the chlorine agent in the cleaning composition is 3 to 50 ppm. A chlorine agent and its preferable aspect are as above-mentioned, 1 type (s) or 2 or more types can be used.
上記洗浄工程に用いられる洗浄剤組成物が塩素剤を含まない場合には、液体洗浄剤組成物に塩素剤を別途添加することができる。塩素剤の添加方法は、液体洗浄剤組成物中に塩素剤が上記量含まれることになればよく、特に限定されない。例えば、洗浄剤組成物を水で希釈した水溶液に塩素剤を添加して液体洗浄剤組成物を調製してもよく、洗浄剤組成物に使用時に塩素剤を添加してもよく、水で塩素剤を希釈した塩素剤水溶液で洗浄剤組成物を希釈してもよい。
このような、塩素剤を含まない本発明の洗浄剤組成物と塩素剤とを使用する食器洗浄方法であって、自動食器洗浄機中で、上記洗浄剤組成物と塩素剤とを水で希釈した液体洗浄剤組成物と食器とを接触させる洗浄工程を含み、上記液体洗浄剤組成物中の上記洗浄剤組成物の濃度は０．０３〜０．５重量％であり、上記塩素剤の濃度は３〜５０ｐｐｍである食器洗浄方法は、本発明の実施態様の１つである。
When the cleaning composition used in the cleaning step does not contain a chlorine agent, a chlorine agent can be added separately to the liquid cleaning composition. The method for adding the chlorine agent is not particularly limited as long as the amount of the chlorine agent is contained in the liquid detergent composition. For example, a liquid detergent composition may be prepared by adding a chlorine agent to an aqueous solution obtained by diluting the detergent composition with water, or a chlorine agent may be added to the detergent composition at the time of use. The cleaning composition may be diluted with an aqueous chlorine agent solution in which the agent is diluted.
Such a dishwashing method using the cleaning composition of the present invention not containing a chlorine agent and a chlorine agent, wherein the cleaning composition and the chlorine agent are diluted with water in an automatic dishwashing machine. A cleaning step of bringing the liquid cleaning composition into contact with tableware, wherein the concentration of the cleaning composition in the liquid cleaning composition is 0.03 to 0.5% by weight, and the concentration of the chlorine agent A dishwashing method in which is 3 to 50 ppm is one embodiment of the present invention.
また、洗浄工程では、塩素剤を含む洗浄剤組成物を使用し、さらに別途塩素剤を添加して液体洗浄剤組成物中の塩素濃度を調整することもできる。
上記洗浄工程において、洗浄剤組成物とは別に塩素剤を添加する場合、塩素剤としては上述した化合物が挙げられ、１種又は２種以上を使用することができる。中でも、塩素化イソシアヌル酸塩、トリクロロイソシアヌル酸、次亜塩素酸塩が好ましく、塩素化イソシアヌル酸ナトリウム、トリクロロイソシアヌル酸、次亜塩素酸ナトリウムがより好ましく、塩素化イソシアヌル酸ナトリウム、次亜塩素酸ナトリウムがさらに好ましい。
In the cleaning step, a cleaning agent composition containing a chlorine agent can be used, and a chlorine agent can be added separately to adjust the chlorine concentration in the liquid cleaning composition.
In the above-described cleaning step, when a chlorine agent is added separately from the cleaning composition, examples of the chlorine agent include the compounds described above, and one or more types can be used. Among them, chlorinated isocyanurate, trichloroisocyanuric acid and hypochlorite are preferable, sodium chlorinated isocyanurate, trichloroisocyanuric acid and sodium hypochlorite are more preferable, sodium chlorinated isocyanurate and sodium hypochlorite. Is more preferable.
上記洗浄工程における液体洗浄剤組成物の温度は特に限定されないが、例えば、４０〜７０℃とすることが好ましく、５０〜６５℃がより好ましい。洗浄時間は特に限定されないが、通常１サイクル０．５〜２分であり、１サイクル１〜１．５分が好ましい。 Although the temperature of the liquid detergent composition in the said washing | cleaning process is not specifically limited, For example, it is preferable to set it as 40-70 degreeC, and 50-65 degreeC is more preferable. The washing time is not particularly limited, but is usually 0.5 to 2 minutes per cycle, and preferably 1 to 1.5 minutes per cycle.
本発明の食器洗浄方法に用いられる洗浄剤組成物及びその好ましい態様等は、上述したとおりである。好ましくは、固体の洗浄剤組成物を用いる。
また、洗浄工程において塩素剤を洗浄剤組成物とは別に添加する場合、塩素剤は、固体であることが好ましい。上記塩素剤は、有効成分である塩素剤単独でもよく、塩素剤に結合補助剤等を加え、造粒、固形化等したものであってもよい。
The detergent composition used in the dishwashing method of the present invention and preferred embodiments thereof are as described above. Preferably, a solid detergent composition is used.
Moreover, when adding a chlorine agent separately from a cleaning composition in a washing | cleaning process, it is preferable that a chlorine agent is solid. The chlorinating agent may be a chlorinating agent alone as an active ingredient, or may be granulated or solidified by adding a binding aid or the like to the chlorinating agent.
上記洗浄剤組成物及び所望により使用される塩素剤の供給方法等は特に限定されず、例えば、自動供給装置を利用してもよく、手動により投入してもよい。また、本発明の洗浄方法に使用される洗浄剤組成物及び塩素剤として、後述する液体洗浄剤組成物用キット又はカートリッジ洗浄剤等を用いることもできる。 The method of supplying the cleaning composition and the chlorine agent used as desired is not particularly limited. For example, an automatic supply device may be used, or the supply may be performed manually. In addition, as a cleaning composition and a chlorinating agent used in the cleaning method of the present invention, a liquid cleaning composition kit or cartridge cleaning agent described later can be used.
本発明の液体洗浄剤組成物用キットは、上記洗浄剤組成物と塩素剤とを含んで構成され、上記洗浄剤組成物と上記塩素剤とを混合して液体洗浄剤組成物を調製するためのキットであって、上記洗浄剤組成物は、上記塩素剤と分離された状態であることを特徴とする。
本発明の液体洗浄剤組成物用キットに含まれる洗浄剤組成物及びその好ましい態様等は上述したとおりであるが、塩素剤を含まないことが好ましい。
The kit for a liquid cleaning composition of the present invention comprises the cleaning composition and a chlorinating agent, and the liquid cleaning composition is prepared by mixing the cleaning composition and the chlorinating agent. The cleaning composition is in a state separated from the chlorinating agent.
Although the cleaning composition contained in the kit for the liquid cleaning composition of the present invention and preferred embodiments thereof are as described above, it is preferable that no chlorine agent is contained.
上記塩素剤としては上述した化合物が挙げられ、１種又は２種以上を使用することができる。中でも、塩素化イソシアヌル酸塩、トリクロロイソシアヌル酸、次亜塩素酸塩が好ましく、塩素化イソシアヌル酸ナトリウム、トリクロロイソシアヌル酸、次亜塩素酸ナトリウムがより好ましく、塩素化イソシアヌル酸ナトリウム、トリクロロイソシアヌル酸がさらに好ましい。上記塩素剤は、有効成分である塩素剤単独でもよく、塩素剤に結合補助剤等を加え、造粒、固形化等したものであってもよい。
本発明のキットにおける上記洗浄剤組成物と上記塩素剤との合計量に対する上記塩素剤の割合は、１〜１０重量％が好ましく、より好ましくは２〜５重量％である。また、例えば本発明の液体洗浄剤組成物用キットを上記食器洗浄方法に用いる場合には、洗浄剤組成物の濃度が０．０３〜０．５重量％である液体洗浄剤組成物を調製した場合に、該液体洗浄剤組成物中の塩素剤の濃度が３〜５０ｐｐｍとなるように、塩素剤の配合量を適宜設定することが好ましい。
Examples of the chlorine agent include the compounds described above, and one or more can be used. Among them, chlorinated isocyanurate, trichloroisocyanuric acid and hypochlorite are preferable, sodium chlorinated isocyanurate, trichloroisocyanuric acid and sodium hypochlorite are more preferable, sodium chlorinated isocyanurate and trichloroisocyanuric acid are further included. preferable. The chlorinating agent may be a chlorinating agent alone as an active ingredient, or may be granulated or solidified by adding a binding aid or the like to the chlorinating agent.
The ratio of the chlorine agent to the total amount of the cleaning composition and the chlorine agent in the kit of the present invention is preferably 1 to 10% by weight, more preferably 2 to 5% by weight. For example, when the kit for a liquid detergent composition of the present invention is used in the above-described dishwashing method, a liquid detergent composition having a concentration of the detergent composition of 0.03 to 0.5% by weight was prepared. In this case, it is preferable to appropriately set the blending amount of the chlorinating agent so that the concentration of the chlorinating agent in the liquid cleaning composition is 3 to 50 ppm.
本発明の液体洗浄剤組成物用キットは、上記洗浄剤組成物と上記塩素剤とを分離された状態で含むものであればよく、その形態等は特に限定されない。例えば、後述するカートリッジ洗浄剤等も本発明のキットの好ましい実施態様の一つである。 The liquid detergent composition kit of the present invention is not particularly limited as long as it contains the detergent composition and the chlorine agent in a separated state. For example, a cartridge cleaning agent described below is one of the preferred embodiments of the kit of the present invention.
本発明のカートリッジ洗浄剤は、内容物の供給口部を有する水不溶性の容器を、上記供給口部を下向きに設置し、上記供給口部へ水が噴射されて内容物を溶かしながら供給する方式の自動食器洗浄機用のカートリッジ洗浄剤であって、
上記容器は、容器本体と中蓋体と外蓋体とからなり、
上記内容物は、本発明の洗浄剤組成物と、塩素剤とを含み、
上記洗浄剤組成物は、所定形状に成形された固形体、粒状体又は粉状体からなり、上記塩素剤は、所定形状に成形された固形体、粒状体又は粉状体からなり、
上記容器本体には、上記洗浄剤組成物が収容されており、
上記中蓋体には、上記塩素剤が収容されており、上記容器本体と上記中蓋体との間には、上記塩素剤又は上記洗浄剤組成物の移動を防止する仕切りが設けられていることを特徴とする。
The cartridge cleaning agent of the present invention is a system in which a water-insoluble container having a content supply port is installed with the supply port facing downward, and water is injected into the supply port while melting the content. A cartridge cleaner for an automatic dishwasher
The container comprises a container body, an inner lid body, and an outer lid body,
The content includes the cleaning composition of the present invention and a chlorine agent,
The cleaning composition is composed of a solid body, a granular body or a powdery body molded into a predetermined shape, and the chlorine agent is composed of a solid body, a granular body or a powdered body molded into a predetermined shape,
The container body contains the cleaning composition,
The inner lid contains the chlorine agent, and a partition is provided between the container body and the inner lid to prevent the chlorine agent or the cleaning composition from moving. It is characterized by that.
なお、本発明における固形体とは、洗浄剤組成物においては、直径５ｃｍ以上（好ましくは直径５〜３０ｃｍ）の球状、直径５ｃｍ以上（好ましくは直径５〜２５ｃｍ）で高さが５ｃｍ以上（好ましくは高さが５〜２５ｃｍ）の円柱状又はそれと同等の体積のものを８０重量％以上含むものをいい、塩素剤においては直径５ｍｍ以上（好ましくは直径５〜５０ｍｍ）の球状又はそれと同等の体積のものを８０重量％以上含むものをいう。また、粒状体とは、上記した固形体の条件に該当せず、直径０．１ｍｍ以上（好ましくは直径０．１〜１０ｍｍ）の球状又はそれと同等の体積のものを８０重量％以上含むものをいい、粉状体とは、直径０．１ｍｍ以上の球状又はそれと同等の体積のものが８０重量％未満であるものをいう。 In the present invention, the solid body in the present invention is a sphere having a diameter of 5 cm or more (preferably 5 to 30 cm), a diameter of 5 cm or more (preferably 5 to 25 cm) and a height of 5 cm or more (preferably Means a columnar shape having a height of 5 to 25 cm) or containing 80% by weight or more of the same volume, and in the case of a chlorine agent, a spherical shape having a diameter of 5 mm or more (preferably a diameter of 5 to 50 mm) or a volume equivalent thereto. The thing containing 80 weight% or more of the thing. In addition, the granular material does not correspond to the above-mentioned conditions of the solid body and includes 80% by weight or more of a spherical shape having a diameter of 0.1 mm or more (preferably a diameter of 0.1 to 10 mm) or a volume equivalent thereto. A fine powder means a material having a spherical shape with a diameter of 0.1 mm or more or an equivalent volume of less than 80% by weight.
本発明のカートリッジ洗浄剤では、上記中蓋体は、噴射水を通過させるための貫通孔が形成されるとともに、上記塩素剤を載置するための載置部を備え、上記戴置部には、洗浄液を容器外へ排水する開口部が形成されるとともに、上記塩素剤を上記中蓋体の内部に保持するための上記載置部を覆うカバー部を備えており、上記外蓋体は、使用時まで容器内外の空間を遮断し、使用時に取り外すように構成され、フィルム状部材又は硬質部材からなることが望ましい。 In the cartridge cleaning agent of the present invention, the inner lid body has a through hole for allowing the jet water to pass therethrough, and further includes a mounting portion for mounting the chlorine agent. An opening for draining the cleaning liquid to the outside of the container is formed, and a cover for covering the placement portion for holding the chlorinating agent inside the inner lid is provided, and the outer lid is It is desirable to block the space inside and outside the container until use, and to remove it during use, and it is desirable to be made of a film-like member or a hard member.
本発明のカートリッジ洗浄剤では、内容物を空間的に遮断する部材が必要であるとともに、噴射水を通過させ、洗浄剤組成物及び塩素剤と接触した洗浄液を容器外に排出するための部材も必要となる。そのため、本発明のカートリッジ洗浄剤では、噴射水を通過させるための貫通孔及び洗浄液を容器外へ排水する開口部が形成された中蓋体と使用時まで容器内外の空間を遮断する外蓋体とが設けられている。
上記中蓋体は、容器本体に固定されていても良いし、脱着可能でも良い。また、上記貫通孔は、大きい１つの貫通孔であってもよく、小さい複数の貫通孔が形成されていてもよい。必要であれば内容物がこぼれないよう、取り付けの際に水溶性のフィルムを貼りつけてもよい。
The cartridge cleaning agent of the present invention requires a member for spatially blocking the contents, and also includes a member for allowing the jet water to pass through and discharging the cleaning liquid that has come into contact with the cleaning composition and the chlorine agent out of the container. Necessary. Therefore, in the cartridge cleaning agent of the present invention, the inner lid formed with the through hole for allowing the jet water to pass through and the opening for draining the cleaning liquid to the outside of the container, and the outer lid for blocking the space inside and outside the container until use And are provided.
The inner lid may be fixed to the container body or may be removable. Further, the through hole may be one large through hole, or a plurality of small through holes may be formed. If necessary, a water-soluble film may be attached at the time of attachment so that the contents do not spill.
上記構成のカートリッジ洗浄剤では、洗浄剤組成物と塩素剤とを分離して収容するために、塩素剤を収容する中蓋体が設けられているが、この戴置部には、塩素剤を保持するカバー部を備えており、これにより、塩素剤を洗浄剤組成物と好適な条件で分離することができる。これにより、上述した効果を得ることができる。 In the cartridge cleaning agent having the above-described configuration, an inner lid for storing the chlorine agent is provided in order to separate and store the cleaning agent composition and the chlorine agent. The holding | maintenance cover part is provided and, thereby, a chlorine agent can be isolate | separated on a suitable condition from a cleaning composition. Thereby, the effect mentioned above can be acquired.
本発明のカートリッジ洗浄剤において、上記中蓋体には、上記塩素剤の移動を規制するための区画部材が設けられていることが望ましい。
区画部材により塩素剤の移動を規制することにより、各塩素剤を均一に溶解させることができる。
In the cartridge cleaning agent of the present invention, it is desirable that the inner lid body is provided with a partition member for restricting movement of the chlorine agent.
By restricting the movement of the chlorine agent by the partition member, each chlorine agent can be uniformly dissolved.
本発明のカートリッジ洗浄剤に使用される洗浄剤組成物に含まれる成分等やその好ましい態様等は上述したとおりであるが、塩素剤を含まないことが好ましい。 The components included in the cleaning composition used in the cartridge cleaning agent of the present invention and preferred embodiments thereof are as described above, but it is preferable that no chlorine agent is included.
本発明のカートリッジ洗浄剤に用いられる塩素剤としては上述した本発明の洗浄剤組成物に使用できる化合物が挙げられ、１種又は２種以上を使用することができる。中でも、塩素化イソシアヌル酸塩、トリクロロイソシアヌル酸、次亜塩素酸塩が好ましく、塩素化イソシアヌル酸ナトリウム、トリクロロイソシアヌル酸、次亜塩素酸ナトリウムがより好ましく、塩素化イソシアヌル酸ナトリウム、トリクロロイソシアヌル酸がさらに好ましい。上記塩素剤は、有効成分である塩素剤単独でもよく、塩素剤に結合補助剤等を加え、造粒、固形化したものであってもよい。 Examples of the chlorine agent used in the cartridge cleaning agent of the present invention include compounds that can be used in the above-described cleaning composition of the present invention, and one or more of them can be used. Among them, chlorinated isocyanurate, trichloroisocyanuric acid and hypochlorite are preferable, sodium chlorinated isocyanurate, trichloroisocyanuric acid and sodium hypochlorite are more preferable, sodium chlorinated isocyanurate and trichloroisocyanuric acid are further included. preferable. The chlorinating agent may be a chlorinating agent alone as an active ingredient, or may be granulated and solidified by adding a binding aid to the chlorinating agent.
本発明のカートリッジ洗浄剤では、上記洗浄剤組成物は、所定形状に成形された固形体からなり、上記塩素剤は、所定形状に成形された固形体又は粒状体からなることが望ましい。
本発明のカートリッジ洗浄剤では、上記塩素剤や洗浄剤組成物の形状は、単一でもよいし、請求項に記載された組み合わせの範囲内で、粒状体と固形体等、又は、大きさや結合剤が異なる複数の固形体といった複数の形状の剤を併用してもよい。
In the cartridge cleaning agent of the present invention, the cleaning composition is preferably composed of a solid body molded into a predetermined shape, and the chlorine agent is preferably composed of a solid body or granular material molded into a predetermined shape.
In the cartridge cleaning agent of the present invention, the shape of the chlorine agent or the cleaning composition may be a single shape, or within the range of the combination described in the claims, the granular material and the solid material, or the size or combination A plurality of shapes of agents such as a plurality of solid bodies having different agents may be used in combination.
上記態様は、本発明のカートリッジ洗浄剤の一態様であり、上記洗浄剤組成物は固形体からなり、上記塩素剤は固形体又は粒状体からなり、両者は表面積が小さく、接触しにくい形状であるので、上記構成のカートリッジ洗浄剤は、塩素剤や洗浄剤組成物の一部の分解を防止することができるとともに、洗浄中に適量の塩素剤を自動食器洗浄機内に供給することができ、簡易に製造することができ、かつ、安全に製造が可能なカートリッジ洗浄剤を提供することができる。 The above aspect is an aspect of the cartridge cleaning agent of the present invention, wherein the cleaning composition is made of a solid body, the chlorinating agent is made of a solid body or a granular body, and both have a small surface area and are difficult to contact. Therefore, the cartridge cleaning agent having the above-described configuration can prevent the chlorine agent and a part of the cleaning agent composition from being decomposed, and can supply an appropriate amount of the chlorine agent into the automatic dishwasher during the cleaning. It is possible to provide a cartridge cleaning agent that can be easily manufactured and can be manufactured safely.
上記構成のカートリッジ洗浄剤では、上記塩素剤は、所定形状に成形された固形体であることが望ましい。
水を噴射して使用するカートリッジ洗浄剤においては、逐次使用する部分以上の部分にまで、噴射水により洗浄剤組成物が濡らされ、その水分を仲立ちとしてキレート剤等の洗浄剤組成物と塩素剤が反応し、それらの一部が分解する場合があるが、上記構成のカートリッジ洗浄剤では、洗浄剤組成物と塩素剤との接触機会が少ないので、上記問題は発生しにくく、特に上記のような洗浄剤組成物の形状が固形であり、塩素剤の形状も固形の場合には、最も洗浄剤組成物と塩素剤の保管時及び使用時の接触確率が少なくなるため、反応等に起因して分解する危険性が小さく、自動食器洗浄機用の洗浄剤として最も適している。
In the cartridge cleaning agent having the above-described configuration, the chlorine agent is preferably a solid body formed into a predetermined shape.
In the cartridge cleaning agent used by jetting water, the cleaning composition is wetted by the jet water to more than the part to be used sequentially, and the cleaning composition such as a chelating agent and the chlorine agent with the water as an intermediate. However, in the cartridge cleaning agent having the above structure, since the opportunity for contact between the cleaning agent composition and the chlorine agent is small, the above problem is unlikely to occur. If the shape of the cleansing composition is solid and the shape of the chlorinating agent is also solid, the contact probability at the time of storage and use of the cleaning agent composition and the chlorinating agent is the least, resulting in reaction, etc. It is most suitable as a cleaning agent for automatic dishwashers.
上記のように、上記構成のカートリッジ洗浄剤では、塩素剤が特に、所定形状に成形された固形体であると、塩素剤と洗浄剤組成物の分離を完全に行うことができるので、上述した本発明の効果がより高くなる。 As described above, in the cartridge cleaning agent having the above-described configuration, when the chlorine agent is a solid body formed into a predetermined shape, the chlorine agent and the cleaning agent composition can be completely separated. The effect of the present invention becomes higher.
本発明のカートリッジ洗浄剤では、上記洗浄剤組成物と上記塩素剤との合計量に対する上記塩素剤の割合は、１〜１０重量％であることが好ましい。なお上記塩素剤の量は、水又は結晶水を除いた純分の重量％である。
上記塩素剤の割合が１〜１０重量％であると、優れた防食能及び優れた洗浄力と高い除菌効果、高い脱臭効果又は漂白効果を得ることができる。上記塩素剤の割合が１重量％未満であると、塩素剤の量が少なすぎて、自動食器洗浄機内を充分に除菌できない場合や、脱臭効果又は漂白効果が不充分となる場合がある。上記塩素剤の割合が１０重量％を超えると、防食能が不充分となる場合がある。また、塩素剤の量が多すぎて、コストが高くなる場合や、噴射水の温度が高い場合に塩素剤の供給量が多すぎて使用環境中に刺激臭を生じることがある。
上記洗浄剤組成物と上記塩素剤との合計量に対する上記塩素剤の割合は、好ましくは２〜５重量％である。
In the cartridge cleaning agent of the present invention, the ratio of the chlorine agent to the total amount of the cleaning composition and the chlorine agent is preferably 1 to 10% by weight. Note that the amount of the chlorinating agent is a weight% of pure component excluding water or crystal water.
When the proportion of the chlorinating agent is 1 to 10% by weight, excellent anticorrosive ability, excellent detergency and high sterilizing effect, high deodorizing effect or bleaching effect can be obtained. If the proportion of the chlorinating agent is less than 1% by weight, the amount of the chlorinating agent may be too small to disinfect the interior of the automatic dishwasher sufficiently, or the deodorizing effect or the bleaching effect may be insufficient. If the proportion of the chlorinating agent exceeds 10% by weight, the anticorrosive ability may be insufficient. In addition, when the amount of the chlorinating agent is too high, the cost becomes high, or when the temperature of the jet water is high, the supply amount of the chlorinating agent is too large and an irritating odor may be generated in the use environment.
The ratio of the chlorine agent to the total amount of the cleaning composition and the chlorine agent is preferably 2 to 5% by weight.
本発明のカートリッジ洗浄剤は、自動食器洗浄機用のカートリッジ洗浄剤として使用することができるものである。
本発明のカートリッジ洗浄剤では、洗浄剤組成物は容器本体に収容されており、塩素剤は中蓋体に収容されており、上記容器本体と上記中蓋体との間には、上記塩素剤又は洗浄剤組成物の移動を防止する仕切りが設けられているが、その実施形態として次のものが考えられる。
The cartridge cleaner of the present invention can be used as a cartridge cleaner for an automatic dishwasher.
In the cartridge cleaning agent of the present invention, the cleaning composition is stored in the container body, the chlorine agent is stored in the inner lid body, and the chlorine agent is interposed between the container body and the inner lid body. Or although the partition which prevents a movement of a cleaning composition is provided, the following can be considered as the embodiment.
以下、本発明のカートリッジ洗浄剤の実施形態について説明する。
本発明のカートリッジ洗浄剤では、塩素剤は、所定形状に成形された固形体、粒状体又は粉体からなり、洗浄剤組成物は、所定形状に成形された固形体又は粒状体からなり、上記中蓋体に上記塩素剤が収容されるとともに、上記容器本体に上記洗浄剤組成物が収容されている。
Hereinafter, embodiments of the cartridge cleaning agent of the present invention will be described.
In the cartridge cleaning agent of the present invention, the chlorine agent comprises a solid body, granule or powder molded into a predetermined shape, and the cleaning composition comprises a solid body or granule molded into a predetermined shape, The chlorine agent is accommodated in the inner lid, and the cleaning composition is accommodated in the container body.
図１は、本発明の実施形態に係るカートリッジ洗浄剤を構成する容器の一例を模式的に示す説明図である。図２は、図１に示すカートリッジ洗浄剤を構成する中蓋体の一例を模式的に示す概念図である。 FIG. 1 is an explanatory view schematically showing an example of a container constituting a cartridge cleaning agent according to an embodiment of the present invention. FIG. 2 is a conceptual diagram schematically showing an example of an inner lid body constituting the cartridge cleaning agent shown in FIG.
図１に示したように、本実施形態に係るカートリッジ洗浄剤１０を構成する容器は、容器本体１１と中蓋体１２と外蓋体１３とからなる。
容器本体１１は、円筒容器の下部が次第に縮径していく、所謂、ロート形状となっており、最下部の径の小さい筒部材１１ａには、中蓋体１２をねじ込むためのねじ１１０ａが形成されている。図示はしていないが、本発明では、筒部材１１ａは、ねじ込みでなく爪構造によるはめ込み式で中蓋体を固定するようになっていてもよい。
As shown in FIG. 1, the container constituting the
The
中蓋体１２は、有底円筒形状であり、底部１２ｂには、噴射水を通過させるための円筒部材１２ｄと、洗浄剤組成物２０及び塩素剤２１(図３参照）が溶解した洗浄液を通過させるための開口部１２ａが２個設けられており、中蓋体１２の円筒部分１２ｃの内壁には、容器本体１１の筒部材１１ａにねじ込むためのねじ１２０ａが設けられている。
開口部１２ａ及び底部１２ｂを含む、塩素剤を載置するための部分が中蓋体１２における載置部である。
なお、図２には開口部１２ａは２個示しているが、開口部１２ａの数は１個ないし２個以上であってもよい。
中蓋体１２は、筒部材１１ａに嵌め込むことにより固定されればよいので、容器本体１１の筒部材１１ａや中蓋体１２にねじ１２０ａが設けられていなくてもよい。その場合には、中蓋体１２に爪部を形成し、筒部材１１ａの方に爪の受け構造が形成されていれば中蓋体１２を嵌め込んだ後、固定することができる。
The
A portion for placing the chlorine agent, including the
Although two
Since the
また、この中蓋体１２は、さらに内筒１２ｅが設けられており、内筒１２ｅの内部に塩素剤２１を収容できるように構成されており、塩素剤２１を内筒１２ｅの内部に収容した状態で保持するために円環形状のカバー部１４が設けられている。
中蓋体１２を構成するカバー部１４は、円筒部材１２ｄと重なる部分を除いて、水が通過することができるように網状又は板状で開口部を有する部材１４ａにより構成されており、縁部には、網状又は板状で開口部を有する部材１４ａを支持、固定するための支持部材１４ｂが配設されている。そして、図示はしていないが、中蓋体１２の内部に塩素剤２１が収容された状態で、支持部材１４ｂが内筒１２ｅの上面周囲に接着剤を介して貼り付けられるか、爪状の構造などで固定され、中蓋体１２の内部（内筒１２ｅの内部）に塩素剤２１が保持され、上部に存在する洗浄剤組成物２０と分離状態とすることができる。
Further, the
The
なお、中蓋体は塩素剤が保持され、噴射水が通過する構造となっていれば、上記構造に限定されない。従って、カバー部１４に円筒部材１２ｄや内筒１２ｅが結合していてもよく、円筒部材１２ｄや内筒１２ｅが他の部材から独立した部材であってもよく、内筒１２ｅが無い構造でもよい。
また、塩素剤が粒状体、固形体である場合には、カバー部１４は、それに対応した塩素剤が漏れない程度の粗さの網状体であればよく、塩素剤が漏れなければ、円筒部材１２ｄや内筒１２ｅに、スリットが形成されていてもよく、メッシュ状であってもよく、適度の間隔でフレームが形成されたものであってもよい。また、内筒１２ｅの代わりに棒状のものが設けられていてもよい。
また、容器本体と中蓋体と外蓋体は、２つ以上の部材が一体成形されたものであってもよい。具体的には、例えば、中蓋とカバー部、中蓋と外蓋部をヒンジで結合した構造であってもよい。
The inner lid body is not limited to the above structure as long as it has a structure in which the chlorine agent is held and the jet water passes. Accordingly, the
Further, when the chlorine agent is a granular or solid body, the
Further, the container body, the inner lid body, and the outer lid body may be formed by integrally molding two or more members. Specifically, for example, a structure in which an inner lid and a cover portion and an inner lid and an outer lid portion are coupled by a hinge may be used.
外蓋体１３は、使用時まで容器内外の空間を遮断する役割を果たすものであり、使用時には、取り外すように構成されている。
図１では、外蓋体１３にも、ねじ１３０ａが設けられ、中蓋体１２にねじ込むように構成されているが、中蓋体と同様に、ねじ１３０ａは設けず、中蓋体１２に爪受け構造を形成し、外蓋体１３に浅い爪を形成し嵌め込むようにしてもよい。
The
In FIG. 1, the
容器本体１１と中蓋体１２と外蓋体１３とは、ポリエチレン、ポリプロピレン、ＰＥＴ等のプラスチックからなるが、特に、外蓋体１３は、嵌め込む形式のものが好ましく、そのためには、硬質部材が好ましい。
なお、外蓋体１３は、フィルム状部材により構成され、使用時にはがすことが可能な接着剤により中蓋体１２に接着されていてもよい。
The
In addition, the
図３は、本発明のカートリッジ洗浄剤の一例を模式的に示す概念図である。
この例では、洗浄剤組成物２０は、容器本体１１の形状で固化した固形体であり、一方、塩素剤２１は、粉状体からなり、粉状体からなる塩素剤２１は、中蓋体１２の内部に載置されており、カバー部１４により中蓋体１２の外に飛散しない構成となっている。なお、塩素剤２１は、粉状体であるので、底部１２ｂに設けられた開口部１２ａから飛散しないよう、開口部１２ａにも目の細かい網状部材が設けられている。
図３に示すカートリッジ洗浄剤１０では、洗浄剤組成物２０と塩素剤２１とは、カバー部１４で分離されており、直接接触することはないため、塩素剤２１と洗浄剤組成物２０とが反応することはなく、水に溶解した塩素剤２１と洗浄剤組成物２０とを良好に洗浄液中に供給することができる。なお、図３では、わかりにくいが、洗浄剤組成物２０は、当然、円筒部材１２ｄの内部には、収容されていない。図４〜図６のカートリッジ洗浄剤でも同様である。
FIG. 3 is a conceptual diagram schematically showing an example of the cartridge cleaning agent of the present invention.
In this example, the cleaning
In the
図４は、本発明のカートリッジ洗浄剤の別の例を模式的に示す概念図である。
この例では、洗浄剤組成物２２は、粒状体であり、一方、塩素剤２３は、所定形状に成形された固形体からなり、固形体からなる塩素剤２３は、中蓋体１２の内部に載置されており、カバー部１４によりその内部に保持されている。
図４に示すカートリッジ洗浄剤１５でも、洗浄剤組成物２２と塩素剤２３とは、カバー部１４で分離されており、直接接触することはない。
FIG. 4 is a conceptual diagram schematically showing another example of the cartridge cleaning agent of the present invention.
In this example, the
Also in the
図５は、本発明のカートリッジ洗浄剤のさらに別の例を模式的に示す概念図である。
この例では、洗浄剤組成物２２及び塩素剤２４は、ともに粒状体であるが、粒状体からなる塩素剤２４は、中蓋体１２の内部に載置されており、カバー部１４によりその内部に保持されている。図５に示すカートリッジ洗浄剤１６でも、洗浄剤組成物２２と塩素剤２４とはカバー部１４により分離されており、直接接触することはない。
FIG. 5 is a conceptual diagram schematically showing still another example of the cartridge cleaning agent of the present invention.
In this example, the cleaning
図６は、本発明のカートリッジ洗浄剤のさらに別の例を模式的に示す概念図である。
この例では、洗浄剤組成物２２は、粒状体であり、一方、塩素剤２１は、粉状体であり、粉状体からなる塩素剤２１は、中蓋体１２の内部に載置されており、カバー部１４によりその内部に保持されている。図６に示すカートリッジ洗浄剤１７でも、洗浄剤組成物２２と塩素剤２１とはカバー部１４により分離されており、直接接触することはない。
このように、塩素剤と洗浄剤組成物とは、中蓋体を構成するカバー部により分離されており、塩素剤と洗浄剤組成物とが直接接触することはなく、塩素剤や洗浄剤組成物の一部の分解を防止することができる。
FIG. 6 is a conceptual diagram schematically showing still another example of the cartridge cleaning agent of the present invention.
In this example, the
Thus, the chlorine agent and the cleaning composition are separated by the cover part constituting the inner lid, and the chlorine agent and the cleaning composition are not in direct contact with each other. The decomposition of a part of the object can be prevented.
図７（ａ）は、本発明のカートリッジ洗浄剤を構成する中蓋体の別の例を模式的に示す概念図であり、図７（ｂ）は、図７（ａ）に示す中蓋体に固形体の塩素剤を収容した状態を模式的に示す概念図であり、図７（ｃ）は、図７（ａ）に示す中蓋体の裏面に外蓋体としてのフィルム部材を接着した状態を模式的に示す概念図である。 FIG. 7 (a) is a conceptual diagram schematically showing another example of the inner lid constituting the cartridge cleaning agent of the present invention, and FIG. 7 (b) is an inner lid shown in FIG. 7 (a). FIG. 7C is a conceptual diagram schematically showing a state in which a solid chlorine agent is accommodated in FIG. 7C, in which a film member as an outer lid is bonded to the back surface of the inner lid shown in FIG. It is a conceptual diagram which shows a state typically.
図７（ａ）に示す中蓋体３２は、有底円筒形状であり、底部３２ｂには、噴射水を通過させるための円筒部材３２ｄと、洗浄剤組成物２０（図８参照）及び塩素剤２３（図７（ｂ）参照）が溶解した洗浄液を通過させるための開口部３２ａが設けられており、中蓋体３２の円筒部分３２ｃの内壁には、容器本体１１の筒部材１１ａにねじ込むためのねじ３２０ａが設けられている。
開口部３２ａ及び底部３２ｂを含む、塩素剤を載置するための部分が中蓋体３２における載置部である。
底部３２ｂは網目形状となっており、多数の開口部３２ａが形成されている。底部３２ｂが網目形状であり多数の開口部３２ａが形成されていると、洗浄液が中蓋体の底部を通過しやすく、均一に排出されるという利点がある。
The
A portion for placing the chlorine agent, including the
The bottom 32b has a mesh shape, and a large number of
また、この中蓋体３２には、さらに内筒３２ｅが設けられており、内筒３２ｅの内部に塩素剤２３を収容できるように構成されている（図７（ｂ）参照）。
この中蓋体３２に収容する塩素剤としては、底部３２ｂの網目形状の開口部３２ａから落下することのない大きさの固形体の塩素剤２３であることが望ましい。
また、中蓋体３２の内筒３２ｅ内には、固形体の塩素剤２３の移動を規制するための区画部材３２ｆが複数箇所に設けられていて、内筒３２ｅ内の空間が区画されている。区画部材３２ｆの間隔は、区画部材３２ｆの間に固形体の塩素剤が入るように定めることが望ましい。このように固形体の塩素剤２３の移動を規制することにより、各塩素剤を均一に溶解させることができる。
Further, the
The chlorine agent contained in the
Further, in the
また、区画部材３２ｆによる区画は、内筒３２ｅ内の空間を完全に区画するのではなく、緩く区画することが望ましい。「緩く」というのは、区画部材３２ｆにより固形体の塩素剤２３の移動が規制される程度に内筒３２ｅ内の空間が区画されている一方、区画部材３２ｆと内筒３２ｅの内壁の間、及び／又は、区画部材３２ｆと円筒部材３２ｄの外壁の間に空間を設けて、水や洗浄液等の液体が内筒３２ｅの間で自由に移動できる状態のことを意味する。このような状態であると、水、洗浄液等の液体が特定の部位に噴射されたとしても、液体が内筒３２ｅの中で偏ることがないので、特定の塩素剤２３のみが溶解することが防止される。
In addition, it is desirable that the partitioning by the partitioning
また、図７（ｂ）に示すように、塩素剤２３を内筒３２ｅの内部に収容した状態で保持するために円環形状のカバー部３４が設けられている。
カバー部３４の役割は図２に示すカバー部１４と同様であるが、図７（ｂ）にはカバー部の形態として開口部の形状が異なる部材３４ａを示している。また、カバー部３４には図２に示すカバー部１４の支持部材に相当する部位は存在していない。
また、図示していないが、円筒部材３２ｄの上面に段付きを設け、段付きとカバー部３４の開口部３４ｃがかみ合うようにしてカバー部３４の位置ずれを防止するようにしてもよい。
また、中蓋体３２に設けていた区画部材３２ｆに代えてカバー部３４の中蓋体側になる面に区画部材を設けて、カバー部３４を被せた際に内筒３２ｅ内の空間を区画できるようにしてもよい。
Moreover, as shown in FIG.7 (b), in order to hold | maintain the
Although the role of the
Further, although not shown, a step may be provided on the upper surface of the
Further, instead of the
図７（ｃ）には図７（ａ）に示す中蓋体３２の裏面に外蓋体としてのフィルム部材３３を接着した状態を示している。
フィルム部材３３は、カートリッジ洗浄剤の使用時に剥がすことが可能な接着剤により中蓋体３２に接着されていてもよい。フィルム部材３３は、接着剤が塗布されていない突出部３３ａを手で掴んで剥がすことができる。また、フィルム部材を水溶性フィルムとしておき、水が触れることによってフィルム部材が溶解してなくなるようにしておいてもよい。
FIG. 7C shows a state in which a
The
図８は、本発明のカートリッジ洗浄剤のさらに別の例を模式的に示す概念図である。
図８には、図３に示すカートリッジ洗浄剤において中蓋体及びカバー部として図７（ｂ）に示す中蓋体３２及びカバー部３４を使用し、固形体の塩素剤２３を中蓋体３２の内部に載置している。また、中蓋体３２の裏面には外蓋体としてのフィルム部材３３を接着している。
この実施形態でも塩素剤と洗浄剤組成物とは、中蓋体を構成するカバー部により分離されており、塩素剤と洗浄剤組成物とが直接接触することはなく、塩素剤や洗浄剤組成物の一部の分解を防止することができる。また、外蓋体としてのフィルム部材により、使用時まで容器内外の空間が遮断されている。
FIG. 8 is a conceptual diagram schematically showing still another example of the cartridge cleaning agent of the present invention.
8 uses the
Also in this embodiment, the chlorine agent and the cleaning agent composition are separated by the cover part constituting the inner lid body, and the chlorine agent and the cleaning agent composition are not in direct contact, and the chlorine agent and the cleaning agent composition The decomposition of a part of the object can be prevented. Further, the space inside and outside the container is blocked by the film member as the outer lid until use.
本発明のカートリッジ洗浄剤に用いる洗浄剤組成物を製造する際には、まず、水及び水以外の洗浄剤組成物の原料を撹拌混合し、スラリー液を調製した後、上記スラリー液をカートリッジ洗浄剤を構成する容器本体に投入し、冷却して固化させることが好ましい。 When manufacturing the cleaning composition used for the cartridge cleaning agent of the present invention, first, water and raw materials of the cleaning composition other than water are mixed by stirring to prepare a slurry liquid, and then the slurry liquid is cleaned with a cartridge. It is preferable to put in the container body constituting the agent and to cool and solidify.
具体的には、例えば、まず、水に水以外の洗浄剤組成物の原料を加えた後、３０〜９０℃に維持し、攪拌することにより、水及び洗浄剤組成物を含むスラリー液を調製する。
水以外の洗浄剤組成物の原料の投入量は、上記スラリー液の全量に対して５０〜１００重量％が望ましい。これにより、カートリッジ洗浄剤に使用した場合に洗浄力が充分に高い洗浄剤組成物が得られる。
Specifically, for example, first, after adding the raw material of the cleaning composition other than water to water, the slurry liquid containing water and the cleaning composition is prepared by maintaining at 30 to 90 ° C. and stirring. To do.
The amount of the raw material for the cleaning composition other than water is preferably 50 to 100% by weight based on the total amount of the slurry. As a result, a cleaning composition having a sufficiently high cleaning power when used as a cartridge cleaning agent can be obtained.
次に、上記スラリー液を容器本体に投入し、その後、上記スラリー液を常温で１〜２４時間放置して固化させ、容器本体の形状に固化された固形体の洗浄剤組成物を製造する。上記スラリーを別の所定形状の容器に投入して固化させれば、その容器の形状の固形体となる。
粒状体の洗浄剤組成物を作製する際には、洗浄剤組成物の原料となるアルカリ剤、防食剤及びキレート剤並びに所望により添加される界面活性剤及び高分子分散剤等の粒状原料を混合すればよい。混合にはリボンミキサー、ナウターミキサー、ドラムミキサーが好適に用いられる。
また、粉状体の洗浄剤組成物を作製する際には、洗浄剤組成物の原料となるアルカリ剤、防食剤及びキレート剤並びに所望により添加される界面活性剤及び高分子分散剤等の粉状原料を混合すればよい。混合にはリボンミキサー、ナウターミキサー、ドラムミキサーが好適に用いられる。
上記のようにして作製した所定形状に成形された固形体、粒状体又は粉状体の洗浄剤組成物を容器本体に収容し、その後、所定形状に成形された固形体、粒状体又は粉状体の塩素剤を中蓋体の内部に収容し、カバー部を設けた後、容器本体と中蓋体と外蓋体とを組み合わせることにより本発明のカートリッジ洗浄剤を製造することができる。
Next, the slurry liquid is charged into the container body, and then the slurry liquid is left to solidify at room temperature for 1 to 24 hours to produce a solid detergent composition solidified in the shape of the container body. When the slurry is put into another container having a predetermined shape and solidified, a solid body having the shape of the container is obtained.
When preparing a granular cleaning composition, mixing granular raw materials such as alkali agents, anticorrosives and chelating agents, and surfactants and polymer dispersants added as desired. do it. For mixing, a ribbon mixer, a nauter mixer, and a drum mixer are preferably used.
Further, when preparing a powdery detergent composition, powders such as alkali agents, anticorrosives and chelating agents, and surfactants and polymer dispersants that are added as desired are used as raw materials for the detergent composition. What is necessary is just to mix a raw material. For mixing, a ribbon mixer, a nauter mixer, and a drum mixer are preferably used.
The solid, granular or powdery cleaning composition formed into a predetermined shape prepared as described above is accommodated in the container body, and then the solid, granular or powdery shape formed into a predetermined shape. The cartridge cleaning agent of the present invention can be manufactured by combining the container main body, the inner lid body, and the outer lid body after housing the body chlorine agent inside the inner lid body and providing the cover portion.
本発明に係るカートリッジ洗浄剤を用いて、食器等を洗浄する際には、供給口部を下向きにして自動食器洗浄機の洗浄剤固定部に固定する。洗浄剤固定部には、噴射器が中蓋体の直ぐ下に配置されており、噴射器より噴射された水が中蓋体の円筒部材内の貫通孔を通過して、容器本体に収容された洗浄剤組成物に到達し、洗浄剤組成物を少しずつ、溶かしていくように構成されている。 When cleaning tableware or the like using the cartridge cleaning agent according to the present invention, the supply port portion is faced downward and fixed to the cleaning agent fixing portion of the automatic dishwashing machine. In the cleaning agent fixing portion, an injector is disposed immediately below the inner lid body, and water ejected from the injector passes through a through hole in the cylindrical member of the inner lid body and is accommodated in the container body. The detergent composition is reached, and the detergent composition is dissolved little by little.
洗浄剤組成物と接触し、洗浄剤組成物を溶解させた水溶液は、塩素剤と接触し、塩素剤も溶かしていく。これにより、塩素剤と洗浄剤組成物とを含む洗浄液は、中蓋体底部の開口部から下に落ちて自動食器洗浄機の洗浄タンク内へ流れ、この洗浄液により食器等を洗浄することができる。 The aqueous solution in contact with the cleaning composition to dissolve the cleaning composition comes into contact with the chlorinating agent and dissolves the chlorinating agent. As a result, the cleaning liquid containing the chlorine agent and the cleaning composition falls down from the opening at the bottom of the inner lid body and flows into the cleaning tank of the automatic dishwasher, and the dishes and the like can be cleaned with this cleaning liquid. .
上記のような、上記カートリッジ洗浄剤に水を供給して洗浄剤組成物と接触させる工程、得られる洗浄剤組成物を溶解させた水溶液を、塩素剤と接触させて塩素剤を溶解させる工程、及び、得られる塩素剤と洗浄剤組成物とを含む液体洗浄剤組成物（洗浄液）を自動食器洗浄機の洗浄タンクに供給し、該液体洗浄剤組成物と食器類とを接触させる洗浄工程を含む食器洗浄方法も、本発明に包含される。液体洗浄剤組成物における洗浄剤組成物の濃度は、０．０３〜０．５重量％であることが好ましく、０．０４〜０．３重量％がより好ましい。上記液体洗浄剤組成物における塩素剤の濃度は、３〜５０ｐｐｍであることが好ましく、５〜４５ｐｐｍがより好ましい。洗浄工程における液体洗浄剤組成物の温度は特に限定されないが、例えば、５０〜７０℃とすることが好ましい。 A step of supplying water to the cartridge cleaning agent as described above and bringing it into contact with the cleaning composition, a step of bringing an aqueous solution in which the resulting cleaning composition is dissolved into contact with the chlorine agent and dissolving the chlorine agent, And a cleaning step of supplying the liquid cleaning composition (cleaning liquid) containing the obtained chlorine agent and the cleaning composition to a cleaning tank of an automatic dishwashing machine and bringing the liquid cleaning composition and the dishes into contact with each other. A dishwashing method is also encompassed by the present invention. The concentration of the cleaning composition in the liquid cleaning composition is preferably 0.03 to 0.5% by weight, and more preferably 0.04 to 0.3% by weight. The concentration of the chlorine agent in the liquid detergent composition is preferably 3 to 50 ppm, more preferably 5 to 45 ppm. Although the temperature of the liquid detergent composition in a washing | cleaning process is not specifically limited, For example, it is preferable to set it as 50-70 degreeC.
本発明のカートリッジ洗浄剤を、上記食器洗浄方法に用いる場合には、液体洗浄剤組成中の洗浄剤組成物及び塩素剤の濃度が上記範囲となるように、カートリッジ洗浄剤に収容する洗浄剤組成物及び塩素剤の量、溶解度、供給水量、供給水温度等を適宜設定すればよい。 When the cartridge cleaning agent of the present invention is used in the above-described dishwashing method, the cleaning agent composition contained in the cartridge cleaning agent so that the concentration of the cleaning agent composition and the chlorine agent in the liquid cleaning agent composition is in the above range. What is necessary is just to set suitably the quantity, solubility, supply water quantity, supply water temperature, etc. of a thing and a chlorine agent.
以下、本発明をより具体的に説明する実施例を示す。なお、本発明はこれらの実施例のみに限定されるものではない。 Examples that more specifically describe the present invention are shown below. In addition, this invention is not limited only to these Examples.
＜実施例１〜１６＞
アルカリ剤、防食剤、キレート剤、塩素剤、界面活性剤及び高分子分散剤、並びに、無水ボウショウ又は水を、表１〜２に示す割合となるように配合し、混合又は加温溶解することにより実施例１〜１６の各洗浄剤組成物を製造した。表１〜２中の数値は、洗浄剤組成物に対する各成分の重量％である。
<Examples 1 to 16>
Alkali agent, anticorrosive agent, chelating agent, chlorinating agent, surfactant and polymer dispersing agent, and anhydrous bouche or water are blended so as to have the ratios shown in Tables 1-2, and mixed or heated to dissolve. Thus, each cleaning composition of Examples 1 to 16 was produced. The numerical value in Tables 1-2 is weight% of each component with respect to cleaning composition.
＜比較例１〜８＞
アルカリ剤、キレート剤、塩素剤、界面活性剤及び高分子分散剤、並びに、無水ボウショウ又は水を、表３に示す割合となるように配合し、混合又は加温溶解することにより比較例１〜８の各洗浄剤組成物を製造した。表３中の数値は、洗浄剤組成物に対する各成分の重量％である。
<Comparative Examples 1-8>
Comparative Examples 1 to 1 were prepared by blending an alkali agent, a chelating agent, a chlorine agent, a surfactant and a polymer dispersant, and anhydrous bow or water so as to have the ratio shown in Table 3, and mixing or heating and dissolving. 8 cleaning compositions were prepared. The numerical values in Table 3 are weight percentages of the respective components with respect to the cleaning composition.
＜評価方法＞
実施例１〜１６及び比較例１〜８で製造した洗浄剤組成物について、以下の方法で防食能及び洗浄力の評価を行った。
<Evaluation method>
About the detergent composition manufactured in Examples 1-16 and Comparative Examples 1-8, anticorrosive ability and cleaning power were evaluated with the following method.
（１）防食能評価（銅合金）
（ｉ）評価方法
試験金属ピースとして、酸洗浄した円柱型銅合金（ＣＡＣ４０６、直径１６ｍｍ×高さ５ｍｍ ムク３．５ｍｍ穴）を自動食器洗浄機槽内に設置した攪拌機の羽に固定し、４７０ｒｐｍで回転させた。自動食器洗浄機として、三洋電機株式会社製ドアタイプの洗浄機（型番ＤＷ−ＤＲ６２型）を使用し、洗浄工程では洗浄剤組成物濃度０．１５重量％とした洗浄液（液体洗浄剤組成物）を使用し、洗浄温度６０℃とした。すすぎ工程ではすすぎ温度８０℃とし、洗浄１サイクルを洗浄時間４５秒、すすぎ８秒とした。洗浄水には、水道水を用いた。３時間稼働後、試験金属ピースの重量変化を測定し、以下の基準で防食能を評価した。
(1) Corrosion protection evaluation (copper alloy)
(I) Evaluation method As a test metal piece, acid-washed cylindrical copper alloy (CAC406,
（ｉｉ）評価基準
洗浄剤組成物の防食能を次のように評価した。
◎：溶解量０．２ｍｇ／ｃｍ２未満
○：溶解量０．２ｍｇ／ｃｍ２以上、０．４ｍｇ／ｃｍ２未満
△：溶解量０．４ｍｇ／ｃｍ２以上、０．６ｍｇ／ｃｍ２未満
×：溶解量０．６ｍｇ／ｃｍ２以上
(Ii) Evaluation criteria The anticorrosive ability of the detergent composition was evaluated as follows.
◎: less dissolved amount 0.2mg / cm 2 ○: soluble amount 0.2 mg / cm 2 or more and less than 0.4mg / cm 2 △: dissolved amount 0.4 mg / cm 2 or more, 0.6 mg / cm 2 less × : Dissolved amount 0.6 mg / cm 2 or more
（２）防食能評価（アルミ）
（ｉ）評価方法
試験金属ピースとして、アルミシート（ＡＡ１０５０、縦１５０ｍｍ×横１５０ｍｍ×高さ０．５ｍｍ）を自動食器洗浄機槽内に設置した攪拌機の羽に固定し、４７０ｒｐｍで回転させた。自動食器洗浄機として、ホシザキ製ドアタイプの洗浄機（型番ＪＷ−６５０ＵＦ）を使用し、洗浄工程では洗浄剤組成物濃度０．１５重量％とした洗浄液を使用し、洗浄温度６０℃とした。すすぎ工程ではすすぎ温度８０℃とし、洗浄１サイクルを洗浄時間４５秒、すすぎ８秒とした。洗浄水には、水道水を用いた。３時間稼働後、試験金属ピースの重量変化を測定し、以下の基準で防食能を評価した。
(2) Corrosion protection evaluation (aluminum)
(I) Evaluation Method As a test metal piece, an aluminum sheet (AA1050, length 150 mm × width 150 mm × height 0.5 mm) was fixed to a blade of a stirrer installed in an automatic dishwasher tank and rotated at 470 rpm. As an automatic dishwasher, a door type washing machine (model number JW-650UF) made by Hoshizaki was used, and a washing liquid having a detergent composition concentration of 0.15 wt% was used in the washing step, and the washing temperature was set to 60 ° C. In the rinsing step, the rinsing temperature was 80 ° C., and one cycle of cleaning was performed with a cleaning time of 45 seconds and a rinsing time of 8 seconds. Tap water was used as the washing water. After operating for 3 hours, the weight change of the test metal piece was measured, and the anticorrosion ability was evaluated according to the following criteria.
（ｉｉ）評価基準
洗浄剤組成物の防食能を次のように評価した。
◎：腐食痕跡なし、光沢あり
○：腐食痕跡なし、光沢弱い
△：腐食痕跡あり、光沢弱い
×：腐食痕跡あり、光沢なし
(Ii) Evaluation criteria The anticorrosive ability of the detergent composition was evaluated as follows.
◎: No corrosion trace, glossy ○: No corrosion trace, weak gloss △: Corrosion trace, weak gloss ×: Corrosion trace, no gloss
（３）洗浄力評価
（ｉ）評価方法
（被洗物の調製）
９０ｇの精製水に小麦粉を１０ｇ、卵黄を７０ｇ、ラードを３５ｇ及び牛脂を３５ｇ、加えてよく撹拌して溶解させた。得られた混合物を汚れに供した。この複合汚れ１ｇを、グラスの内側に塗り広げ、室温で乾燥させたものを洗浄試験用試料とした。
(3) Detergency evaluation (i) Evaluation method (preparation of objects to be washed)
In 90 g of purified water, 10 g of flour, 70 g of egg yolk, 35 g of lard and 35 g of beef tallow were added and dissolved by stirring well. The resulting mixture was subjected to soiling. 1 g of this composite soil was spread on the inside of the glass and dried at room temperature to make a sample for a cleaning test.
（洗浄条件）
洗浄力試験は、洗浄工程において、自動食器洗浄機内の水量に対して洗浄剤組成物の濃度が０．１重量％になるように洗浄剤組成物を投入して洗浄液とし、自動食器洗浄機を用いて洗浄試験用試料の汚れを洗浄してその外観を目視で評価することにより行った。
自動食器洗浄機として、ホシザキ製ドアタイプの洗浄機（型番ＪＷ−６５０ＵＦ）を用い、洗浄条件は洗浄時間４０秒、洗浄温度６０℃、すすぎ時間８秒、すすぎ温度８０℃とした。洗浄水には、水道水を用いた。
(Cleaning conditions)
In the cleaning process, in the cleaning process, the cleaning composition is added so that the concentration of the cleaning composition is 0.1% by weight with respect to the amount of water in the automatic dishwashing machine. It was performed by cleaning the dirt of the sample for cleaning test and visually evaluating its appearance.
As an automatic dishwasher, a door type washing machine (model number JW-650UF) manufactured by Hoshizaki was used, and washing conditions were a washing time of 40 seconds, a washing temperature of 60 ° C., a rinsing time of 8 seconds, and a rinsing temperature of 80 ° C. Tap water was used as the washing water.
（ｉｉ）評価基準
洗浄剤組成物の洗浄力を次のように評価した。
◎：汚れの付着は見られない。
○：汚れの付着はほとんど見られない。
△：薄い曇り状の汚れが見られる。
×：明らかな汚れの残留が見られる。
(Ii) Evaluation criteria The detergency of the cleaning composition was evaluated as follows.
(Double-circle): The adhesion of dirt is not seen.
○: Almost no dirt is observed.
Δ: A light cloudy stain is observed.
X: Obvious residue of dirt is observed.
実施例及び比較例で製造した各洗浄剤組成物について、以下の方法で漂白力の評価を行った。
（４）漂白力評価
（ｉ）評価方法
（被洗物の調製）
１）ポリプロピレン製コップの内側を紙やすりで全面削り、その後中性洗剤でよく洗った。
２）上記コップに、標準濃度の４倍で調整した緑茶粉末水溶液８０℃を注ぎ、すぐに捨て、５分間静置した。
About each detergent composition manufactured by the Example and the comparative example, the bleaching power was evaluated with the following method.
(4) Bleaching power evaluation (i) Evaluation method (preparation of washing object)
1) The entire inside of the polypropylene cup was shaved with a sandpaper, and then washed thoroughly with a neutral detergent.
2) A green tea powder aqueous solution 80 ° C. adjusted to 4 times the standard concentration was poured into the above cup, immediately discarded, and allowed to stand for 5 minutes.
（洗浄条件）
洗浄液の濃度は、自動食器洗浄機内の水量に対して洗浄剤組成物の濃度が０．１重量％とした。この洗浄剤組成物の濃度を初期値とした。洗浄方法は、自動食器洗浄機を用いて、上記洗浄液による洗浄工程及び水によるすすぎ工程により洗浄試験用試料の茶渋汚れを１サイクル洗浄し、その洗浄済のコップに対して上記被洗物の調整２）の通り再度汚れを付着させた。そのコップをさらに１サイクル洗浄することを繰り返し、目視で茶渋汚れの蓄積を評価し、蓄積が認められた際の洗浄回数を評価基準とした。なお、洗浄サイクルが５回終わった後、自動食器洗浄機の水を張り替え、洗浄剤組成物の濃度を初期値に戻した。自動食器洗浄機として、ホシザキ製ドアタイプの洗浄機（型番ＪＷ−６５０ＵＦ）を使用し、洗浄温度６０℃、すすぎ温度８０℃とし、洗浄１サイクルを洗浄時間４５秒、すすぎ８秒とした。
(Cleaning conditions)
The concentration of the cleaning liquid was 0.1% by weight with respect to the amount of water in the automatic dishwasher. The concentration of this cleaning composition was taken as the initial value. The washing method uses an automatic dishwasher to wash one cycle of tea stains of the washing test sample by the washing step with the washing solution and the rinsing step with water, and the washing object is adjusted with respect to the washed cup. As shown in 2), the dirt was adhered again. The cup was further washed for one cycle, the accumulation of tea astringent stains was visually evaluated, and the number of washings when accumulation was observed was used as an evaluation criterion. In addition, after the washing | cleaning cycle was completed 5 times, the water of the automatic dishwasher was replaced and the density | concentration of the cleaning composition was returned to the initial value. As an automatic dishwasher, a Hoshizaki door type washer (model number JW-650UF) was used. The washing temperature was 60 ° C., the rinsing temperature was 80 ° C., and the washing cycle was 45 seconds and the rinsing time was 8 seconds.
（ｉｉ）評価基準
洗浄剤組成物の漂白力を次のように評価した。
◎：洗浄サイクル３０回以上
○：洗浄サイクル２０回以上２９回以下
△：洗浄サイクル１０回以上１９回以下
×：洗浄サイクル１回以上９回以下
なお実施例１〜２及び９〜１０並びに比較例２の洗浄剤組成物については、漂白力の評価を行わなかった。
(Ii) Evaluation Criteria The bleaching power of the detergent composition was evaluated as follows.
◎: Cleaning cycle 30 times or more ○:
実施例及び比較例で製造した各洗浄剤組成物の組成並びに防食能及び洗浄力の評価結果を表１〜３に示した。 Tables 1 to 3 show the compositions of the cleaning compositions prepared in Examples and Comparative Examples, and the evaluation results of anticorrosive ability and cleaning power.
表１〜３及び後掲の表４中の記載は、以下の通りである。
ＥＤＴＡ：エチレンジアミン四酢酸二ナトリウム
ＮＴＡ：ニトリロ三酢酸ナトリウム
非イオン界面活性剤：ポリオキシアルキレンモノアルキルエーテル（Ｃ＝１２、エチレンオキサイド付加モル数の平均値３、プロピレンオキサイド付加モル数の平均値５）
ポリアクリル酸Ｎａ：重量平均分子量（Ｍｗ）が４,５００のポリアクリル酸ナトリウム
The descriptions in Tables 1 to 3 and Table 4 below are as follows.
EDTA: ethylenediaminetetraacetic acid disodium NTA: nitrilotriacetic acid sodium nonionic surfactant: polyoxyalkylene monoalkyl ether (C = 12, average value of ethylene oxide addition moles 3, average value of propylene oxide addition moles 5)
Polyacrylic acid Na: sodium polyacrylate having a weight average molecular weight (Mw) of 4,500
表１〜４中の「残」は、洗浄剤組成物１００重量％から水及びは無水ボウショウ以外の成分の重量％を引いた残りが水又は無水ボウショウであることを意味する。
表１〜４中の「ケイ酸ナトリウム中のＳｉＯ２／Ｎａ２Ｏ（モル比）」は、アルカリ剤として使用したケイ酸ナトリウムを構成するＮａ２ＯとＳｉＯ２とのモル比である。
また、「洗浄剤組成物中のＳｉＯ２／Ｎａ２Ｏ（モル比）」は、アルカリ剤に含まれるＳｉＯ２と、Ｎａ２Ｏとして換算したアルカリ剤とのモル比（アルカリ剤中のＳｉＯ２／アルカリ剤（Ｎａ２Ｏ換算））である。
The “residue” in Tables 1 to 4 means that the balance obtained by subtracting the weight percent of ingredients other than water and anhydrous bowel from 100% by weight of the cleaning composition is water or anhydrous bowel.
“SiO 2 / Na 2 O (molar ratio) in sodium silicate” in Tables 1 to 4 is a molar ratio of Na 2 O and SiO 2 constituting sodium silicate used as an alkali agent.
In addition, “SiO 2 / Na 2 O (molar ratio) in the detergent composition” is a molar ratio of SiO 2 contained in the alkali agent and the alkali agent converted as Na 2 O (SiO 2 in the alkali agent). / Alkaline agent (Na 2 O conversion).
表１〜３から、実施例１〜１６の洗浄剤組成物は、洗浄力に優れ、かつ防食能に優れるものであった。また、塩素剤を配合した実施例３〜８及び１１〜１６の洗浄剤組成物は、漂白力にも優れていた。一方比較例１〜８の洗浄剤組成物は、洗浄力又は防食能が不充分であった。 From Tables 1 to 3, the cleaning compositions of Examples 1 to 16 were excellent in detergency and excellent in anticorrosive ability. Moreover, the cleaning composition of Examples 3-8 and 11-16 which mix | blended the chlorine agent was excellent also in the bleaching power. On the other hand, the cleaning compositions of Comparative Examples 1-8 were insufficient in detergency or anticorrosive ability.
実施例１７〜１８
アルカリ剤、防食剤、キレート剤、界面活性剤及び高分子分散剤、並びに、水を、表４に示す割合となるように配合して混合した後、８０℃に加熱して維持し、攪拌することにより、水と水以外の洗浄剤組成物の原料とを含むスラリー液を調製した。表４中の数値は、洗浄剤組成物に対する各成分の重量％である。
Examples 17-18
Alkali agent, anticorrosive agent, chelating agent, surfactant and polymer dispersant, and water were mixed and mixed so as to have the ratio shown in Table 4, then heated to 80 ° C., maintained, and stirred. Thus, a slurry liquid containing water and a raw material of the cleaning composition other than water was prepared. The numerical values in Table 4 are weight percentages of the respective components with respect to the cleaning composition.
次に、上記で調製したスラリー液を、ポリプロピレン製容器に充填し、上記スラリー液の温度が３０℃以下に下がるまで常温で放置してスラリー液を固化させ、円柱の形状（直径１５ｃｍ×高さ１５ｃｍ）に固化された固形体からなる洗浄剤組成物を調製した。
Next, the slurry liquid prepared above is filled into a polypropylene container, and left at room temperature until the temperature of the slurry liquid falls to 30 ° C. or lower to solidify the slurry liquid, and the shape of the cylinder (
実施例１９〜２４
アルカリ剤、防食剤、キレート剤、界面活性剤及び高分子分散剤、並びに、水を、表４に示す割合となるように配合して混合した後、８０℃に加熱して維持し、攪拌することにより、水と水以外の洗浄剤組成物の原料とを含むスラリー液を調製した。表４中の数値は、洗浄剤組成物に対する各成分の重量％である。
Examples 19-24
Alkali agent, anticorrosive agent, chelating agent, surfactant and polymer dispersant, and water were mixed and mixed so as to have the ratio shown in Table 4, then heated to 80 ° C., maintained, and stirred. Thus, a slurry liquid containing water and a raw material of the cleaning composition other than water was prepared. The numerical values in Table 4 are weight percentages of the respective components with respect to the cleaning composition.
次に、上記で調製したスラリー液を、図１に示す形状の容器本体（円筒部分の直径１５ｃｍ、高さ１５ｃｍ）に充填し、上記スラリー液の温度が３０℃以下に下がるまで常温で放置してスラリー液を固化させ、容器本体の形状に固化された固形体からなる洗浄剤組成物を調製した。 Next, the slurry liquid prepared above is filled in a container main body having a shape shown in FIG. 1 (the diameter of the cylindrical portion is 15 cm and the height is 15 cm), and is left at room temperature until the temperature of the slurry liquid falls below 30 ° C. The slurry liquid was solidified to prepare a cleaning composition comprising a solid body solidified in the shape of the container body.
別途、粉状体である塩素剤（トリクロロイソシアヌル酸又はジクロロイソシアヌル酸ナトリウム、有効塩素濃度５０％以上、平均粒径：２５０μｍ以上）を、洗浄剤組成物と塩素剤との合計重量に対して１〜１０重量％となる量計量して、図７（ａ）に示す中蓋体３２の内部に、図７（ｂ）に示すような状態で収容し、カバー部を接着した後、容器本体と中蓋体を組み合わせて図８に示すカートリッジ洗浄剤１８を製造した。
Separately, a chlorinating agent (trichloroisocyanuric acid or sodium dichloroisocyanurate, effective chlorine concentration of 50% or more, average particle size: 250 μm or more), which is a powder, is 1 for the total weight of the cleaning composition and the chlorinating agent. 10% by weight and stored in the state shown in FIG. 7 (b) in the
＜評価方法＞
実施例１７〜２４で製造した洗浄剤組成物又はカートリッジ洗浄剤を用いて、以下の方法で防食能及び洗浄力の評価を行った。実施例１７及び１８の洗浄剤組成物については、洗浄工程において液体用供給装置による滴下により塩素剤６重量％の次亜塩素酸ナトリウム水溶液を添加した。
<Evaluation method>
Using the cleaning composition or cartridge cleaning agent manufactured in Examples 17 to 24, the anticorrosion ability and cleaning power were evaluated by the following methods. About the cleaning composition of Example 17 and 18, the sodium hypochlorite aqueous solution of 6 weight% of chlorine agents was added by the dripping with the supply apparatus for liquids in the washing | cleaning process.
（１）防食能評価（銅合金）
洗浄工程において、洗浄液中の洗浄剤組成物の濃度（重量％）及び塩素剤の濃度（ｐｐｍ）が表４に示す濃度であったこと以外は、実施例１〜１６と同様の方法で評価を行った。なお、塩素剤の濃度は、後記する方法で測定した有効塩素濃度である。
(1) Corrosion protection evaluation (copper alloy)
In the washing step, the evaluation was performed in the same manner as in Examples 1 to 16, except that the concentration (% by weight) of the cleaning composition in the cleaning liquid and the concentration (ppm) of the chlorine agent were the concentrations shown in Table 4. went. In addition, the density | concentration of a chlorine agent is an effective chlorine density | concentration measured by the method mentioned later.
（２）防食能評価（アルミ）
洗浄工程において、洗浄液中の洗浄剤組成物の濃度（重量％）及び塩素剤の濃度（ｐｐｍ）が表４に示す濃度であったこと以外は、実施例１〜１６と同様の方法で評価を行った。
(2) Corrosion protection evaluation (aluminum)
In the washing step, the evaluation was performed in the same manner as in Examples 1 to 16, except that the concentration (% by weight) of the cleaning composition in the cleaning liquid and the concentration (ppm) of the chlorine agent were the concentrations shown in Table 4. went.
（３）洗浄力評価
洗浄工程において、洗浄液中の洗浄剤組成物の濃度（重量％）及び塩素剤の濃度（ｐｐｍ）が表４に示す濃度であったこと以外は、実施例１〜１６と同様の方法で評価を行った。
(3) Detergency Evaluation In the cleaning step, Examples 1 to 16 except that the concentration (wt%) of the cleaning composition in the cleaning liquid and the concentration (ppm) of the chlorine agent were the concentrations shown in Table 4. Evaluation was performed in the same manner.
（４）漂白力評価
洗浄条件を以下のようにした以外は、実施例１〜１６と同様の方法で評価を行った。
洗浄液の濃度は、自動食器洗浄機内の水量に対して洗浄剤組成物の濃度が表４に示す濃度（重量％）となるようにした。洗浄液中の塩素剤は、有効塩素濃度が表４に示す有効塩素濃度（ｐｐｍ）になるように調整した。この洗浄剤組成物の濃度及び塩素剤の濃度（有効塩素濃度）を初期値とした。洗浄方法は、自動食器洗浄機を用いて、上記洗浄液による洗浄工程及び水によるすすぎ工程により洗浄試験用試料の茶渋汚れを１サイクル洗浄し、その洗浄済のコップに対して上記被洗物の調整２）の通り再度汚れを付着させた。そのコップをさらに１サイクル洗浄することを繰り返し、目視で茶渋汚れの蓄積を評価し、蓄積が認められた際の洗浄回数を評価基準とした。なお、洗浄サイクルが５回終わった後、自動食器洗浄機の水を張り替え、洗浄剤組成物の濃度及び有効塩素濃度を初期値に戻した。自動食器洗浄機として、ホシザキ製ドアタイプの洗浄機（型番ＪＷ−６５０ＵＦ）を使用し、洗浄温度６０℃、すすぎ温度８０℃とし、洗浄１サイクルを洗浄時間４５秒、すすぎ８秒とした。
(4) Bleaching power evaluation Evaluation was performed in the same manner as in Examples 1 to 16, except that the washing conditions were as follows.
The concentration of the cleaning liquid was set such that the concentration of the cleaning composition was the concentration (% by weight) shown in Table 4 with respect to the amount of water in the automatic dishwasher. The chlorine agent in the cleaning liquid was adjusted so that the effective chlorine concentration was the effective chlorine concentration (ppm) shown in Table 4. The concentration of this cleaning composition and the concentration of chlorinating agent (effective chlorine concentration) were used as initial values. The washing method uses an automatic dishwasher to wash one cycle of tea stains of the washing test sample by the washing step with the washing solution and the rinsing step with water, and the washing object is adjusted with respect to the washed cup. As shown in 2), the dirt was adhered again. The cup was further washed for one cycle, the accumulation of tea astringent stains was visually evaluated, and the number of washings when accumulation was observed was used as an evaluation criterion. In addition, after the washing cycle was completed five times, the water in the automatic dishwasher was replaced, and the concentration of the cleaning composition and the effective chlorine concentration were returned to the initial values. As an automatic dishwasher, a Hoshizaki door type washer (model number JW-650UF) was used. The washing temperature was 60 ° C., the rinsing temperature was 80 ° C., and the washing cycle was 45 seconds and the rinsing time was 8 seconds.
（５）洗浄工程の有効塩素濃度
自動食器用洗浄機の洗浄液１００ｇを２００ｍＬ三角フラスコに取り、ヨウ化カリウム溶液５ｇ、氷酢酸１０ｍＬを添加し、次に０．０１Ｎチオ硫酸ナトリウム規定液でヨウ素の黄色が消失するまで滴定し、次式から算出した。滴定量Ａ（ｍＬ）、求める有効塩素濃度をＡｖＣＬ（ｐｐｍ）とすると、ＡｖＣＬ（ｐｐｍ）＝Ａ（ｍＬ）×３．５４６で求めた。
(5) Effective Chlorine Concentration of Washing Process Take 100 g of washing liquid of an automatic dishwasher in a 200 mL Erlenmeyer flask, add 5 g of potassium iodide solution and 10 mL of glacial acetic acid, and then add iodine with 0.01 N sodium thiosulfate normal solution. Titration was carried out until the yellow color disappeared, and calculation was performed from the following formula. When the titration amount A (mL) and the effective chlorine concentration to be obtained are AvCL (ppm), AvCL (ppm) = A (mL) × 3.546.
上記評価結果を、表４に示す。 The evaluation results are shown in Table 4.
表４から、実施例１７〜１８で製造した洗浄剤組成物と塩素剤とを使用した洗浄液により食器を洗浄すると、優れた洗浄効果、防食効果及び漂白効果が得られることが分かる。実施例１９〜２４で製造したカートリッジ洗浄剤についても、食器の洗浄において優れた洗浄効果、防食効果及び漂白効果が得られることが分かる。 From Table 4, it turns out that the outstanding cleaning effect, anticorrosion effect, and a bleaching effect are acquired when tableware is wash | cleaned with the washing | cleaning liquid which uses the cleaning composition and the chlorine agent which were manufactured in Examples 17-18. It can be seen that the cartridge cleaning agents produced in Examples 19 to 24 also have excellent cleaning effects, anticorrosion effects, and bleaching effects in cleaning dishes.
１０、１５、１６、１７、１８ カートリッジ洗浄剤
１１ 容器本体
１１ａ 筒部材
１２、３２ 中蓋体
１２ａ、３２ａ 開口部
１２ｂ、３２ｂ 底部
１２ｃ、３２ｃ 円筒部分
１２ｄ、３２ｄ 円筒部材
１２ｅ、３２ｅ 内筒
１３ 外蓋体
１４、３４ カバー部
１４ａ、３４ａ 網状または板状で開口部を有する部材
１４ｂ 支持部材
２０、２２ 洗浄剤組成物
２１、２３、２４ 活性塩素剤
３２ｆ 区画部材
３３ フィルム部材
３３ａ フィルム部材の突出部
３４ｃ カバー部の開口部
１１０ａ、１２０ａ、１３０ａ、３２０ａ ねじ
10, 15, 16, 17, 18
Claims (9)
The dishwashing | cleaning method of Claim 8 whose density | concentration of the chlorine agent in the said liquid cleaning composition is 3-50 ppm.