JP5884423B2 - Polymer compound and organic photoelectric conversion device using the same - Google Patents

Description

  The present invention relates to a polymer compound, and an organic photoelectric conversion element and an organic thin film transistor using the same.

  An organic semiconductor material is used for organic photoelectric conversion elements, such as an organic solar cell and an optical sensor, for example. In particular, when a high molecular compound is used among organic semiconductor materials, a thin film can be produced by an inexpensive coating method, and the manufacturing cost of the element can be reduced.

繰り返し単位（Ａ） 繰り返し単位（Ｂ） In order to improve various characteristics of the organic photoelectric conversion element, various polymer compounds have been studied for organic semiconductor materials constituting the element. For example, Patent Document 1 describes an organic thin film solar cell having an organic layer containing a polymer compound composed of a repeating unit (A) and a repeating unit (B).

Repeating unit (A) Repeating unit (B)

Special table 2009-506519

  However, the organic thin film solar cell using the polymer compound has a problem that the ionization potential is shallow and the open-circuit voltage (Voc) is not sufficient.

  Therefore, an object of the present invention is to provide a polymer compound having a deep ionization potential and a large open circuit voltage (Voc).

（１）
〔式（１）中Ａｒ^１、Ａｒ^２は、置換基を有してもよい炭素数６〜６０のアリール基をあらわす。Ａｒ^１、Ａｒ^２は、同一であっても、相異なっていてもよい。Xは炭素原子、珪素原子、またはゲルマニウム原子を表す。〕
That is, the present invention first provides a polymer compound containing a repeating unit represented by the formula (1).

(1)
[In the formula (1), Ar ¹ and Ar ² represent an aryl group having 6 to 60 carbon atoms which may have a substituent. Ar ¹ and Ar ² may be the same or different. X represents a carbon atom, a silicon atom, or a germanium atom. ]

（２）
〔式（２）中、Ｒは水素原子またはフッ素原子を表す。複数個あるＲは、同一であっても、相異なっていてもよい。Qは酸素原子、硫黄原子、またはセレン原子を表す。〕 Secondly, the present invention provides a polymer compound containing a repeating unit represented by the formula (2) in addition to the repeating unit represented by the formula (1).

(2)
[In formula (2), R represents a hydrogen atom or a fluorine atom. A plurality of R may be the same or different. Q represents an oxygen atom, a sulfur atom, or a selenium atom. ]

  Thirdly, the present invention provides an organic photoelectric conversion element having a pair of electrodes and a functional layer provided between the electrodes, wherein the functional layer includes an electron accepting compound and the polymer compound.

  Fourthly, the present invention provides an organic thin film transistor comprising a source electrode, a drain electrode, an organic semiconductor layer, and a gate electrode, wherein the organic semiconductor layer includes the polymer compound.

  The polymer compound of the present invention is extremely useful because it has a large open-circuit voltage (Voc).

  Hereinafter, the present invention will be described in detail.

（１）
〔式（１）中Ａｒ^１、Ａｒ^２は、置換基を有してもよい炭素数６〜６０のアリール基をあらわす。Ａｒ^１、Ａｒ^２は、同一であっても、相異なっていてもよい。Xは炭素原子、珪素原子、またはゲルマニウム原子を表す。〕 <Polymer compound>
The polymer compound of the present invention provides a polymer compound containing a repeating unit represented by the formula (1).

(1)
[In the formula (1), Ar ¹ and Ar ² represent an aryl group having 6 to 60 carbon atoms which may have a substituent. Ar ¹ and Ar ² may be the same or different. X represents a carbon atom, a silicon atom, or a germanium atom. ]

In formula (1), Ar < ¹ >, Ar < ² > shows the C6-C60 aryl group which may have a substituent.

In Ar ¹ and Ar ² , Ar ¹ and Ar ² are an optionally substituted aryl group having 6 to 60 carbon atoms and an aromatic group having 6 to 60 carbon atoms that may have a substituent. The group remove | excluding one hydrogen atom on the aromatic ring in a hydrocarbon compound is shown. The aromatic hydrocarbon compound may be a single ring or a condensed ring. Among these, since excellent solubility is obtained and production is easy, a condensed ring or a single ring in which five or less rings are condensed is preferable, and a condensed ring or a single ring in which two rings are condensed is preferable. A ring is more preferable, and a single ring is more preferable.

  Examples of the aromatic hydrocarbon compound include benzene, naphthalene, anthracene, fluorene, pyrene, and perylene. Of these, benzene or naphthalene is preferable, and benzene is more preferable.

  The aromatic hydrocarbon group may further have a substituent, and in this case, the whole including the substituent is an aromatic hydrocarbon group. However, in this case, the carbon number of the above-described preferred aromatic hydrocarbon group does not include the carbon number of the substituent.

Examples of the substituent for Ar ¹ and Ar ² include a halogen atom, an alkyl group, an alkoxy group, an aryl group, and a heteroaryl group.

  Examples of the halogen atom include bromine, chlorine, and fluorine. Among these, fluorine is preferable.

  Examples of the alkyl group include a methyl group, ethyl group, n-propyl group, iso-propyl group, n-butyl group, iso-butyl group, sec-butyl group, tert-butyl group, n-pentyl group, n- Examples include a hexyl group, n-octyl group, iso-octyl group, n-decyl group, n-dodecyl group, n-pentadecyl group, and n-octadecyl group. A hydrogen atom in the alkyl group may be substituted with a fluorine atom. Examples of the alkyl group in which a hydrogen atom is substituted with a fluorine atom include a trifluoromethyl group, a pentafluoroethyl group, a perfluorobutyl group, a perfluorohexyl group, and a perfluorooctyl group.

  Examples of the alkoxy group include a methoxy group, an ethoxy group, a propoxy group, an iso-propoxy group, a butoxy group, an iso-butoxy group, a sec-butoxy group, a tert-butoxy group, a pentyloxy group, a hexyloxy group, and a cyclohexyloxy group. , Heptyloxy group, octyloxy group, 2-ethylhexyloxy group, nonyloxy group, decyloxy group, 3,7-dimethyloctyloxy group. A hydrogen atom in the alkoxy group may be substituted with a fluorine atom. Examples of the alkoxy group in which a hydrogen atom is substituted with a fluorine atom include a trifluoromethoxy group, a pentafluoroethoxy group, a perfluorobutoxy group, a perfluorohexyloxy group, and a perfluorooctyloxy group.

The aryl group is an atomic group obtained by removing one hydrogen atom from an aromatic hydrocarbon which may have a substituent. The aryl group includes a group containing a benzene ring, a group containing a condensed ring having aromaticity, a group having a structure in which two or more benzene rings or a condensed ring having aromaticity are directly bonded, and two or more benzenes Examples include a group in which a ring or an aromatic condensed ring is bonded via a group such as vinylene. The aryl group preferably has 6 to 60 carbon atoms, more preferably 6 to 30 carbon atoms. A hydrogen atom in the aryl group may be substituted with a fluorine atom. Examples of the aryl group include a phenyl group, a 1-naphthyl group, and a 2-naphthyl group. Examples of the substituent that the aromatic hydrocarbon may have include a chlorine atom, a bromine atom, an iodine atom, an alkyl group, and an alkoxy group. Specific examples of the alkyl group and alkoxy group are the same as the specific examples of the alkyl group and alkoxy group mentioned as the substituents for Ar ¹ and Ar ² .

A heteroaryl group is an atomic group obtained by removing one hydrogen atom from an aromatic heterocyclic compound which may have a substituent. Examples of the heteroaryl group include a thienyl group, a pyrrolyl group, a furyl group, a pyridyl group, a quinolyl group, and an isoquinolyl group. The hydrogen atom in the heteroaryl group may be substituted with a fluorine atom. Examples of the substituent that the aromatic heterocyclic compound may have include a chlorine atom, a bromine atom, an iodine atom, an alkyl group, and an alkoxy group. Specific examples of the alkyl group and alkoxy group are the same as the specific examples of the alkyl group and alkoxy group as substituents for Ar ¹ and Ar ² .

When the substituents of Ar ¹ and Ar ² are an alkyl group or an alkoxy group, the alkyl group or the alkoxy group preferably has 1 to 20 carbon atoms from the viewpoint of solubility of the polymer compound in a solvent. 2 to 18 is more preferable.

Hydrogen in the substituents of Ar ¹ and Ar ² may be substituted with fluorine.

  X represents a carbon atom, a silicon atom, or a germanium atom, and among these, a carbon atom is preferable.

Examples of the repeating unit represented by the formula (1) include the following repeating units.

  The amount of the repeating unit represented by the formula (1) contained in the polymer compound of the present invention is selected from the viewpoint of increasing the photoelectric conversion efficiency of an organic photoelectric conversion device having a functional layer containing the polymer compound. It is preferable that it is 10-90 mol% with respect to the total amount of the repeating unit which a compound contains, and it is more preferable that it is 30-70 mol%.

（２）
式（２）中、Ｒは水素原子またはフッ素原子を表す。複数個あるＲは、同一であっても、相異なっていてもよい。Qは酸素原子、硫黄原子、またはセレン原子を表す。 The polymer compound of the present invention preferably contains a repeating unit represented by the formula (2) in addition to the repeating unit represented by the formula (1).

(2)
In formula (2), R represents a hydrogen atom or a fluorine atom. A plurality of R may be the same or different. Q represents an oxygen atom, a sulfur atom, or a selenium atom.

As a repeating unit represented by Formula (2), the following repeating unit is mentioned, for example.

  From the viewpoint of photoelectric conversion efficiency, it is preferable to include a repeating unit in which the repeating unit represented by the formula (1) and the repeating unit represented by the formula (2) are directly bonded.

  When the polymer compound of the present invention contains a repeating unit represented by formula (2) in addition to the repeating unit represented by formula (1), it is represented by formula (1) contained in the polymer compound. From the viewpoint of increasing the photoelectric conversion efficiency of the organic photoelectric conversion element having the functional layer containing the polymer compound, the total amount of the repeating unit and the repeating unit represented by the formula (2) is a repeating amount contained in the polymer compound. It is preferably 20 to 100 mol%, more preferably 30 to 100 mol%, based on the total amount of units.

  The ratio of the number of repeating units represented by formula (1) contained in the polymer compound of the present invention to the number of repeating units represented by formula (2) is, for example, 1: 9 to 9: 1. Yes, 3: 7-7: 3 is preferred.

The weight average molecular weight in terms of polystyrene of the polymer compound of the present invention is preferably 10 ³ to 10 ⁸ , more preferably 10 ³ to 10 ⁷ , and still more preferably 10 ³ to 10 ⁶ .

  The polymer compound of the present invention is preferably a conjugated polymer compound. Here, the conjugated polymer compound means a compound in which atoms constituting the main chain of the polymer compound are substantially conjugated.

  The polymer compound of the present invention may have a repeating unit other than the repeating unit represented by the formula (1) and the repeating unit represented by the formula (2). Examples of the repeating unit include an arylene group and a heteroarylene group. Examples of the arylene group include a phenylene group, a naphthalenediyl group, an anthracenediyl group, a pyrenediyl group, and a fluorenediyl group. Examples of the heteroarylene group include a flangyl group, a pyrrole diyl group, a pyridinediyl group, and the like.

<Method for producing polymer compound>
The polymer compound of the present invention may be produced by any method. For example, after synthesizing a monomer having a functional group suitable for the polymerization reaction to be used, the monomer is dissolved in an organic solvent, if necessary, , And can be synthesized by polymerization using a known aryl coupling reaction using a catalyst, a ligand and the like. The synthesis of the monomer can be performed, for example, with reference to the methods disclosed in JP-A Nos. 2006-182920 and 2006-335933.

  Examples of the polymerization by the aryl coupling reaction include polymerization by Stille coupling reaction, polymerization by Suzuki coupling reaction, polymerization by Yamamoto coupling reaction, and polymerization by Kumada-Tamao coupling reaction.

  Polymerization by Stille coupling reaction is necessary using palladium complexes such as palladium [tetrakis (triphenylphosphine)], [tris (dibenzylideneacetone)] dipalladium, palladium acetate, bis (triphenylphosphine) palladium dichloride as catalysts. Depending on the ligand, ligands such as triphenylphosphine, tri (2-methylphenyl) phosphine, tri (2-methoxyphenyl) phosphine, diphenylphosphinopropane, tri (cyclohexyl) phosphine, tri (tert-butyl) phosphine A monomer having an organotin residue and a monomer having a halogen atom such as a bromine atom, an iodine atom or a chlorine atom, or a sulfonate group such as a trifluoromethanesulfonate group or a p-toluenesulfonate group. This is a polymerization in which the monomer is reacted. The details of the polymerization by the Stille coupling reaction are described in, for example, Angewante Chemie International Edition, 2005, Vol. 44, p. 4442-4489.

  Polymerization by Suzuki coupling reaction uses a palladium complex or nickel complex as a catalyst in the presence of an inorganic base or an organic base, and a ligand is added as necessary to have a boronic acid residue or a boric acid ester residue. This is a polymerization in which a monomer is reacted with a monomer having a halogen atom such as a bromine atom, an iodine atom or a chlorine atom, or a monomer having a sulfonate group such as a trifluoromethanesulfonate group or a p-toluenesulfonate group.

  Examples of the inorganic base include sodium carbonate, potassium carbonate, cesium carbonate, tripotassium phosphate, and potassium fluoride. Examples of the organic base include tetrabutylammonium fluoride, tetrabutylammonium chloride, tetrabutylammonium bromide, and tetraethylammonium hydroxide. Examples of the palladium complex include palladium [tetrakis (triphenylphosphine)], [tris (dibenzylideneacetone)] dipalladium, palladium acetate, and bis (triphenylphosphine) palladium dichloride. Examples of the nickel complex include bis (cyclooctadiene) nickel. Examples of the ligand include triphenylphosphine, tri (2-methylphenyl) phosphine, tri (2-methoxyphenyl) phosphine, diphenylphosphinopropane, tri (cyclohexyl) phosphine, and tri (tert-butyl) phosphine. It is done.

  Details of the polymerization by the Suzuki coupling reaction are described in, for example, Journal of Polymer Science: Part A: Polymer Chemistry (Part A: Polymer Chemistry), 2001, Vol. 39, p. 1533-1556.

  Polymerization by Yamamoto coupling reaction uses a catalyst and a reducing agent to react monomers having halogen atoms, monomers having sulfonate groups such as trifluoromethanesulfonate groups, or monomers having halogen atoms and monomers having sulfonate groups. Polymerization.

  Catalysts include nickel zero-valent complexes such as bis (cyclooctadiene) nickel and ligands such as bipyridyl, [bis (diphenylphosphino) ethane] nickel dichloride, [bis (diphenylphosphino) propane] nickel. A catalyst comprising a nickel complex other than a nickel zero-valent complex such as dichloride and a ligand such as triphenylphosphine, diphenylphosphinopropane, tri (cyclohexyl) phosphine, tri (tert-butyl) phosphine, if necessary. . Examples of the reducing agent include zinc and magnesium. Polymerization by the Yamamoto coupling reaction may be performed using a dehydrated solvent in the reaction, may be performed in an inert atmosphere, or may be performed by adding a dehydrating agent to the reaction system.

  Details of the polymerization by Yamamoto coupling are described in, for example, Macromolecules, 1992, Vol. 25, p. 1214-1223.

  Polymerization by Kumada-Tamao coupling reaction uses a nickel catalyst such as [bis (diphenylphosphino) ethane] nickel dichloride, [bis (diphenylphosphino) propane] nickel dichloride, and a compound having a magnesium halide group and a halogen atom. Polymerization to react with the compound having For the reaction, a dehydrated solvent may be used for the reaction, the reaction may be performed in an inert atmosphere, or a dehydrating agent may be added to the reaction system.

  In the polymerization by the aryl coupling reaction, a solvent is usually used. The solvent may be selected in consideration of the polymerization reaction used, the solubility of the monomer and polymer, and the like. Specifically, tetrahydrofuran, toluene, 1,4-dioxane, dimethoxyethane, N, N-dimethylacetamide, N, N-dimethylformamide, an organic solvent such as a mixed solvent obtained by mixing two or more of these solvents, an organic solvent Examples thereof include a solvent having two phases of a phase and an aqueous phase. The solvent used in the Stille coupling reaction is preferably an organic solvent such as tetrahydrofuran, toluene, N, N-dimethylformamide, a mixed solvent obtained by mixing two or more of these solvents, or a solvent having two phases of an organic solvent phase and an aqueous phase. The solvent used for the Stille coupling reaction is preferably deoxygenated before the reaction in order to suppress side reactions. Solvents used in the Suzuki coupling reaction are organic solvents such as tetrahydrofuran, toluene, 1,4-dioxane, dimethoxyethane, N, N-dimethylacetamide, N, N-dimethylformamide, and mixed solvents in which two or more of these solvents are mixed. A solvent and a solvent having two phases of an organic solvent phase and an aqueous phase are preferred. The solvent used for the Suzuki coupling reaction is preferably deoxygenated before the reaction in order to suppress side reactions. The solvent used for the Yamamoto coupling reaction is an organic solvent such as tetrahydrofuran, toluene, 1,4-dioxane, dimethoxyethane, N, N-dimethylacetamide, N, N-dimethylformamide, or a mixed solvent in which two or more of these solvents are mixed. A solvent is preferred. The solvent used for the Yamamoto coupling reaction is preferably deoxygenated before the reaction in order to suppress side reactions.

  Among the polymerizations by the aryl coupling reaction, from the viewpoint of reactivity, a method of polymerizing by a Stille coupling reaction, a method of polymerizing by a Suzuki coupling reaction, a method of polymerizing by a Yamamoto coupling reaction are preferable, and a Stille coupling reaction More preferred are a method of polymerizing, a method of polymerizing by a Suzuki coupling reaction, and a method of polymerizing by a Yamamoto coupling reaction using a nickel zero-valent complex.

  The lower limit of the reaction temperature of the aryl coupling reaction is preferably −100 ° C., more preferably −20 ° C., and particularly preferably 0 ° C. from the viewpoint of reactivity. The upper limit of the reaction temperature is preferably 200 ° C., more preferably 150 ° C., and particularly preferably 120 ° C. from the viewpoint of the stability of the monomer and the polymer compound.

  In the polymerization by the aryl coupling reaction, a known method can be used as a method for removing the polymer compound of the present invention from the reaction solution after completion of the reaction. For example, the polymer compound of the present invention can be obtained by adding a reaction solution to a lower alcohol such as methanol, filtering the deposited precipitate, and drying the filtrate. When the purity of the obtained polymer compound is low, it can be purified by recrystallization, continuous extraction with a Soxhlet extractor, column chromatography, or the like.

  When the polymer compound of the present invention is used for the production of an organic photoelectric conversion element, if a polymerization active group remains at the terminal of the polymer compound, characteristics such as durability of the organic photoelectric conversion element may be deteriorated. It is preferable to protect the terminal of the polymer compound with a stable group.

Examples of the stable group for protecting the terminal include an alkyl group, an alkoxy group, a fluoroalkyl group, a fluoroalkoxy group, an aryl group, an arylamino group, and a monovalent heterocyclic group. Examples of the arylamino group include a phenylamino group and a diphenylamino group.
Examples of the monovalent heterocyclic group include thienyl group, pyrrolyl group, furyl group, pyridyl group, quinolyl group, and isoquinolyl group. Further, the polymerization active group remaining at the terminal of the polymer compound may be replaced with a hydrogen atom instead of a stable group. From the viewpoint of enhancing hole transportability, it is preferable that the stable group for protecting the terminal is a group imparting electron donating properties such as an arylamino group. When the polymer compound is a conjugated polymer compound, the end of a group having a conjugated bond in which the conjugated structure of the main chain of the polymer compound and the conjugated structure of a stable group protecting the end are continuous is also protected. It can preferably be used as a stable group. Examples of the group include an aryl group and a monovalent heterocyclic group having aromaticity.

（３）
（式（３）中、Ｒ、Qは、それぞれ前述と同じ意味を表す。Ｚは、ホウ酸、ホウ酸エステル残基を表す。２個あるＺは、同一でも相異なっていてもよい。）

（４）
（式（４）中、X、Ａｒ^１、Ａｒ^２はそれぞれ前述と同じ意味を表す。） When the polymer compound of the present invention is produced using Suzuki coupling, for example, the polymer compound is produced by polymerizing the compound represented by the formula (3) and the compound represented by the formula (4). be able to.

(3)
(In formula (3), R and Q each represent the same meaning as described above. Z represents boric acid or a boric acid ester residue. The two Zs may be the same or different.)

(4)
(In the formula (4), X, Ar ¹ and Ar ² each have the same meaning as described above.)

（式中、Ｍｅはメチル基を表し、Ｅｔはエチル基を表す。） In formula (3), the boric acid ester residue represented by Z represents a group in which one hydrogen atom has been removed from the boric acid ester, and specific examples thereof include groups represented by the following formula.

(In the formula, Me represents a methyl group, and Et represents an ethyl group.)

  As a compound represented by Formula (3), the following compound is mentioned, for example.

  The compound represented by the formula (4) of the present invention may be produced by any method. For example, the method shown in Scheme 7 of Tetrahedron, 2008, Vol. 64, page 9033, WO2008109701 (0082) The method shown in the paragraph can be used as a reference.

As a compound represented by Formula (4), the following compound is mentioned, for example.

<Organic photoelectric conversion element>
Moreover, the high molecular compound of this invention can obtain a big open end voltage.

The organic photoelectric conversion device of the present invention has a pair of electrodes and a functional layer between the electrodes, and the functional layer contains the electron-accepting compound and the polymer compound of the present invention. As an electron-accepting compound, fullerene or a fullerene derivative is preferable. As a specific example of the organic photoelectric conversion element,
1. An organic photoelectric conversion element having a pair of electrodes and a functional layer between the electrodes, the functional layer containing an electron-accepting compound and the polymer compound of the present invention;
2. An organic photoelectric conversion element comprising a pair of electrodes and a functional layer between the electrodes, the functional layer containing an electron-accepting compound and the polymer compound of the present invention, wherein the electron-accepting compound is a fullerene An organic photoelectric conversion element which is a derivative;
Is mentioned. In general, at least one of the pair of electrodes is transparent or translucent. Hereinafter, this case will be described as an example.

  1 above. In the organic photoelectric conversion element, the amount of the electron-accepting compound in the functional layer containing the electron-accepting compound and the polymer compound is 10 to 1000 parts by weight with respect to 100 parts by weight of the polymer compound. Is preferable, and it is more preferable that it is 20-500 weight part. In addition, 2. In the organic photoelectric conversion element, the amount of the fullerene derivative in the functional layer containing the fullerene derivative and the polymer compound is preferably 10 to 1000 parts by weight with respect to 100 parts by weight of the polymer compound, More preferably, it is -500 weight part. From the viewpoint of increasing the photoelectric conversion efficiency, the amount of the fullerene derivative in the functional layer is preferably 20 to 400 parts by weight, and preferably 40 to 250 parts by weight with respect to 100 parts by weight of the polymer compound. More preferably, it is 80 to 120 parts by weight. From the viewpoint of increasing the short-circuit current density, the amount of the fullerene derivative in the functional layer is preferably 20 to 250 parts by weight, and preferably 40 to 120 parts by weight with respect to 100 parts by weight of the polymer compound. More preferred.

  In order for the organic photoelectric conversion element to have high photoelectric conversion efficiency, the electron-accepting compound and the polymer compound of the present invention have an absorption region that can efficiently absorb the spectrum of desired incident light. It is important that the heterojunction interface includes many heterojunction interfaces in order to efficiently separate excitons, and that the heterojunction interface has a charge transporting property for quickly transporting charges generated by the heterojunction interface to the electrode.

  From such a viewpoint, as the organic photoelectric conversion element, the above 1. , 2. From the standpoint of including a large number of heterojunction interfaces, the organic photoelectric conversion element is preferable. The organic photoelectric conversion element is more preferable. Further, in the organic photoelectric conversion element of the present invention, an additional layer may be provided between at least one electrode and the functional layer in the element. Examples of the additional layer include a charge transport layer that transports holes or electrons, and a buffer layer.

  The organic photoelectric conversion element of the present invention is usually formed on a substrate. The substrate may be any substrate that does not chemically change when an electrode is formed and an organic layer is formed. Examples of the material for the substrate include glass, plastic, polymer film, and silicon. In the case of an opaque substrate, the opposite electrode (that is, the electrode far from the substrate) is preferably transparent or translucent.

  As a material for the pair of electrodes, a metal, a conductive polymer, or the like can be used. The material of one of the pair of electrodes is preferably a material having a low work function. For example, metals such as lithium, sodium, potassium, rubidium, cesium, magnesium, calcium, strontium, barium, aluminum, scandium, vanadium, zinc, yttrium, indium, cerium, samarium, europium, terbium, ytterbium, and those metals An alloy of two or more of these metals, or one or more of those metals and one or more of gold, silver, platinum, copper, manganese, titanium, cobalt, nickel, tungsten, tin An alloy with metal, graphite, a graphite intercalation compound, or the like is used. Examples of the alloy include magnesium-silver alloy, magnesium-indium alloy, magnesium-aluminum alloy, indium-silver alloy, lithium-aluminum alloy, lithium-magnesium alloy, lithium-indium alloy, and calcium-aluminum alloy.

  Examples of the material of the transparent or translucent electrode include a conductive metal oxide film and a translucent metal thin film. Specifically, a film formed using a conductive material made of indium oxide, zinc oxide, tin oxide, and indium tin oxide (ITO), indium zinc oxide, etc., which is a composite thereof, NESA Gold, platinum, silver, and copper are used, and ITO, indium / zinc / oxide, and tin oxide are preferable. Examples of the method for producing the electrode include a vacuum deposition method, a sputtering method, an ion plating method, a plating method, and the like. Moreover, you may use organic transparent conductive films, such as polyaniline and its derivative (s), polythiophene, and its derivative (s) as an electrode material.

  As a material used for the charge transport layer as the additional layer, that is, the hole transport layer or the electron transport layer, an electron donating compound and an electron accepting compound described later can be used, respectively.

  As a material used for the buffer layer as an additional layer, halides or oxides of alkali metals or alkaline earth metals such as lithium fluoride can be used. In addition, fine particles of an inorganic semiconductor such as titanium oxide can be used.

<Organic thin film>
As the functional layer in the organic photoelectric conversion element of the present invention, for example, an organic thin film containing the polymer compound of the present invention and an electron-accepting compound can be used.

  The organic thin film has a thickness of usually 1 nm to 100 μm, preferably 2 nm to 1000 nm, more preferably 5 nm to 500 nm, and further preferably 20 nm to 200 nm.

  The organic thin film may contain the polymer compound alone or in combination of two or more. Moreover, in order to improve the hole transport property of the organic thin film, a low molecular compound and / or a high molecular compound other than the high molecular compound can be mixed and used as the electron donating compound in the organic thin film.

  Examples of the electron-donating compound that the organic thin film may contain in addition to the polymer compound of the present invention include, for example, pyrazoline derivatives, arylamine derivatives, stilbene derivatives, triphenyldiamine derivatives, oligothiophene and its derivatives, polyvinylcarbazole and its Derivatives, polysilanes and derivatives thereof, polysiloxane derivatives having aromatic amines in the side chain or main chain, polyaniline and derivatives thereof, polythiophene and derivatives thereof, polypyrrole and derivatives thereof, polyphenylene vinylene and derivatives thereof, polythienylene vinylene and derivatives thereof Is mentioned.

Examples of the electron-accepting compound include oxadiazole derivatives, anthraquinodimethane and derivatives thereof, benzoquinone and derivatives thereof, naphthoquinone and derivatives thereof, anthraquinones and derivatives thereof, tetracyanoanthraquinodimethane and derivatives thereof, and fluorenone derivatives. , diphenyldicyanoethylene and derivatives thereof, diphenoquinone derivatives, 8-hydroxyquinoline and metal complexes of derivatives thereof, polyquinoline and derivatives thereof, polyquinoxaline and its derivatives, polyfluorene and its derivatives, fullerene and derivatives thereof such as C _60, carbon nanotube And phenanthroline derivatives such as 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline, and fullerene and derivatives thereof are particularly preferable.

  The electron-donating compound and the electron-accepting compound are relatively determined from the energy levels of these compounds.

Fullerenes and derivatives thereof include C ₆₀ , C ₇₀ , C ₈₄ and derivatives thereof.
A fullerene derivative represents a compound in which at least a part of fullerene is modified.

（Ｉ） （ＩＩ） （ＩＩＩ） （ＩＶ）
（式（Ｉ）〜（ＩＶ）中、Ｒ^ａは、アルキル基、アリール基、ヘテロアリール基又はエステル構造を有する基である。複数個あるＲ^ａは、同一であっても相異なってもよい。Ｒ^ｂはアルキル基又はアリール基を表す。複数個あるＲ^ｂは、同一であっても相異なってもよい。） Examples of the fullerene derivative include a compound represented by the formula (I), a compound represented by the formula (II), a compound represented by the formula (III), and a compound represented by the formula (IV).

(I) (II) (III) (IV)
(In formulas (I) to (IV), R ^a is an alkyl group, aryl group, heteroaryl group or group having an ester structure. A plurality of R ^a may be the same or different. R ^b represents an alkyl group or an aryl group, and a plurality of R ^b may be the same or different.)

Definitions and specific examples of the alkyl group, aryl group and heteroaryl group represented by R ^a and R ^b are the definitions and specific examples of the alkyl group, aryl group and heteroaryl group described above as substituents for Ar ¹ and Ar ^2. Same as example.

Examples of the group having an ester structure represented by ^Ra include a group represented by the formula (V).

(V)
(In formula (V), u1 represents an integer of 1 to 6, u2 represents an integer of 0 to 6, and R ^c represents an alkyl group, an aryl group, or a heteroaryl group.)

The definitions and specific examples of the alkyl group, aryl group and heteroaryl group represented by R ^c are the same as the definitions and specific examples of the alkyl group, aryl group and heteroaryl group mentioned as the substituents for Ar ¹ and Ar ^2. It is.

Specific examples of the C ₆₀ derivative include the following.

Specific examples of the C ₇₀ derivative include the following.

<Method for producing organic thin film>
The organic thin film may be produced by any method. For example, the organic thin film may be produced by a film formation method from a solution containing the polymer compound of the present invention, or an organic thin film may be formed by a vacuum deposition method. Good. Examples of the method for producing an organic thin film by film formation from a solution include a method of producing an organic thin film by applying the solution on one electrode and then evaporating the solvent.

  The solvent used for film formation from a solution is not particularly limited as long as it dissolves the polymer compound of the present invention. Examples of the solvent include unsaturated hydrocarbon solvents such as toluene, xylene, mesitylene, tetralin, decalin, bicyclohexyl, n-butylbenzene, sec-butylbenzene, tert-butylbenzene, carbon tetrachloride, chloroform, dichloromethane. Halogenated saturated hydrocarbon solvents such as dichloroethane, chlorobutane, bromobutane, chloropentane, bromopentane, chlorohexane, bromohexane, chlorocyclohexane and bromocyclohexane, and halogenated unsaturated hydrocarbons such as chlorobenzene, dichlorobenzene and trichlorobenzene Examples of the solvent include ether solvents such as tetrahydrofuran and tetrahydropyran. The polymer compound of the present invention can usually be dissolved in the solvent in an amount of 0.1% by weight or more.

  For film formation from solution, spin coating method, casting method, micro gravure coating method, gravure coating method, bar coating method, roll coating method, wire bar coating method, dip coating method, spray coating method, screen printing method, flexographic method Coating methods such as a printing method, an offset printing method, an ink jet printing method, a dispenser printing method, a nozzle coating method, a capillary coating method can be used, and a spin coating method, a flexographic printing method, an ink jet printing method, and a dispenser printing method are preferable.

<Application of device>
By irradiating light such as sunlight from a transparent or translucent electrode, the organic photoelectric conversion element generates a photovoltaic force between the electrodes and can be operated as an organic thin film solar cell. It can also be used as an organic thin film solar cell module by integrating a plurality of organic thin film solar cells.

  In addition, by applying light from a transparent or translucent electrode in a state where a voltage is applied between the electrodes, a photocurrent flows and it can be operated as an organic photosensor. It can also be used as an organic image sensor by integrating a plurality of organic photosensors.

<Organic transistor>
The organic thin film transistor of the present invention includes a source electrode, a drain electrode, an organic semiconductor layer, and a gate electrode. The organic semiconductor layer is represented by the repeating unit represented by the formula (A) and the formula (B). A polymer compound containing a repeating unit or a polymer compound containing a repeating unit represented by formula (1).

  Since the polymer compound of the present invention has high charge mobility, the organic thin film transistor having the organic semiconductor layer containing the polymer compound of the present invention has high field effect mobility.

  Examples will be shown below for illustrating the present invention in more detail, but the present invention is not limited to these examples.

  The polystyrene equivalent weight average molecular weight of the polymer compound was determined by size exclusion chromatography (SEC).

  Column: TOSOH TSKgel SuperHM-H (2) + TSKgel SuperH2000 (4.6 mm I.d. x 15 cm); Detector: RI (SHIMADZU RID-10A); Mobile phase: Tetrahydrofuran (THF)

Reference example 1
(Synthesis of 4,4′-dihexadecylbenzophenone)
Into the flask, 19.6 g (87.4 mmol) of 1-hexene and a tetrahydrofuran solution (0.5 mol / L, 175 mL) of 9-borabicyclo [3.3.1] nonane were added and stirred for 16 hours. To this solution, 9.90 g (29.1 mmol) of 4,4′-dibromobenzophenone and 0.480 g (0.582 mmol) of dichloro [1,1′-bis (diphenylphosphino) ferrocene] palladium were added. Furthermore, 47 mL of 5 mol / L sodium hydroxide aqueous solution was dripped at this solution, and it was made to recirculate | reflux for 5 hours. The reaction solution was concentrated with an evaporator, toluene and water were added, and the mixture was extracted with toluene. The toluene solution was evaporated with an evaporator. The obtained solid was purified with a silica gel column using hexane as a developing solvent, and a hexane solution was recovered. Thereafter, the hexane solution was evaporated by an evaporator to obtain 4,4′-dihexadecylbenzophenone. The yield was 11.2 g, and the yield was 61%.

Reference example 2
(Synthesis of 3-bromo-2,2′-bithiophene)
Add 19.3 g (79.7 mmol) of 2,3-dibromothiophene, 0.501 g (0.613 mmol) of dichloro [1,1′-bis (diphenylphosphino) ferrocene] palladium and 100 mL of diethyl ether to the flask. It was. To this solution, a diethyl ether solution of 2-thienylmagnesium bromide (1.2 mol / L, 50 mL) was added dropwise and refluxed for 6 hours. The reaction mixture was poured into water and extracted with diethyl ether. The diethyl ether solution was evaporated with an evaporator. The obtained solid was purified with a silica gel column using hexane as a developing solvent, and a hexane solution was recovered. Thereafter, the hexane solution was evaporated by an evaporator to obtain 3-bromo-2,2′-bithiophene. The yield was 11.9 g, and the yield was 79%.
¹ H-NMR (300 MHz, CDCl ₃ ) δ 7.42 (m, 1H), 7.34 (m, 1H), 7.19 (m, 1H), 7.08 (m, 1H), 7.01 ( m, 1H)

Reference example 3
(Synthesis of Compound 1)
The flask was charged with 11.0 g (44.9 mmol) of 3-bromo-2,2′-bithiophene and 100 mL of diethyl ether, and cooled to −78 ° C. To this solution, a hexane solution of n-butyllithium (2.6 mol / L, 17.3 mL) was added dropwise and stirred for 1 hour. To this solution, 28.3 g (44.9 mmol) of 4,4′-dihexadecylbenzophenone was added. The reaction was gradually warmed to room temperature and stirred at room temperature for 3 hours. The reaction mixture was poured into water and extracted with diethyl ether. The diethyl ether solution was evaporated with an evaporator. The obtained solid was purified with a silica gel column using a mixed solution of hexane and chloroform (volume ratio 4/1) as a developing solvent, and a mixed solution of hexane and chloroform was recovered. Thereafter, a mixed solution of hexane and chloroform was evaporated with an evaporator to obtain Compound 1. The yield was 29.1 g, and the yield was 81%. In addition, the structure of the compound 1, the below-mentioned compound 2, and the below-mentioned compound 3 is shown in the reaction formula in the synthesis | combining section of the below-mentioned high molecular compound 1, respectively.
¹ H-NMR (300 MHz, CDCl ₃ ) δ 7.09-7.23 (m, 10H), 6.84 (m, 1H), 6.63 (m, 1H), 6.40 (m, 1H), 2.60 (t, 4H), 1.00-1.70 (m, 56H), 0.88 (t, 6H)

Reference example 4
(Synthesis of Compound 2)
A flask was charged with 29.1 g (36.5 mmol) of Compound 1, 3 mL of boron trifluoride diethyl etherate, and 400 mL of chloroform, and refluxed for 5 hours. The reaction solution was poured into water and extracted with chloroform. The chloroform solution was evaporated with an evaporator. The obtained solid was purified with a silica gel column using hexane as a developing solvent, and a hexane solution was recovered. Thereafter, hexane was evaporated with an evaporator to obtain Compound 2. The yield was 2.88g, and the yield was 10%.
¹ H-NMR (300 MHz, CDCl ₃ ) δ 7.00-7.21 (m, 12H), 2.53 (t, 4H), 1.55 (t, 4H), 1.10-1.40 (m , 52H), 0.88 (t, 6H)

Reference Example 5
(Synthesis of Compound 3)
To the flask, 2.88 g (3.70 mmol) of compound 2, 1.38 g (7.76 mmol) of N-bromosuccinimide and 100 mL of chloroform were added and stirred for 2 hours. The reaction solution was poured into water and extracted with chloroform. The chloroform solution was evaporated with an evaporator. The obtained solid was purified with a silica gel column using a mixed solution of hexane and chloroform (volume ratio 9/1) as a developing solvent, and a mixed solution of hexane and chloroform was recovered. Thereafter, a mixed solution of hexane and chloroform was evaporated by an evaporator to obtain Compound 3. The yield was 2.00 g, and the yield was 58%.
¹ H-NMR (300 MHz, CDCl ₃ ) δ 6.90-7.10 (m, 10H), 2.54 (t, 4H), 1.57 (t, 4H), 1.10-1.40 (m , 52H), 0.88 (t, 6H)

Example 1
Synthesis of Polymer Compound 1 0.300 g (0.320 mmol) of compound 3 and 4,7-bis (4,4,5,5-tetramethyl-1,3) were placed in a flask in which the gas in the flask was replaced with nitrogen. , 2-dioxaborolan-2-yl) benzo-2,1,3-thiadiazole 0.124 g (0.320 mmol), toluene 50 mL, tris (dibenzylideneacetone) dipalladium 5.9 mg, tri-tert-butyl 7.4 mg of phosphonium tetrafluoroborate was added and stirred. To this solution, 1.6 mL of a 2 mol / L potassium carbonate aqueous solution was dropped and refluxed for 5 hours. To the reaction solution, 7.8 mg of phenylboronic acid was added and refluxed for 1 hour. Next, 0.1 g of sodium N, N-diethyldithiocarbamate trihydrate was added to the reaction solution, and the mixture was refluxed for 3 hours. Thereafter, the reaction solution was poured into water, toluene was added, and the toluene layer was extracted. After the toluene solution was washed with an acetic acid aqueous solution and water, the toluene solution was added dropwise to acetone to obtain a precipitate. The precipitate was dissolved in chlorobenzene and purified with a silica gel column using chlorobenzene as a developing solvent. The purified chlorobenzene solution was added dropwise to methanol, and the precipitate was filtered to obtain a polymer compound 1 represented by 4 in the following reaction formula. The yield was 250 mg, the polystyrene-equivalent number average molecular weight was 1.5 × 10 ⁴ , and the weight average molecular weight was 2.9 × 10 ⁴ .

フラスコ内の気体を窒素で置換したフラスコに、２，６−ジブロモ−４，４−ジヘキサデシルシクロペンタ［２，１−ｂ：３，４−ｂ’］ジチオフェンを３．８ｇ（４．９ｍｍｏｌ）、４，７−ビス（４，４，５，５−テトラメチル−１，３，２−ジオキサボロラン−２−イル）−２，１，３−ベンゾチアジアゾールを１．９ｇ（４．９ｍｍｏｌ）、テトラヒドロフランを１７０ｍＬ、トリス（ジベンジリデンアセトン）ジパラジウムを８９ｍｇ、トリ−ｔｅｒｔ−ブチルホスホニウムテトラフルオロボレートを０．１１ｇ入れて撹拌した。この溶液に、２ｍｏｌ／Ｌの炭酸カリウム水溶液を２４ｍＬ滴下し、３時間還流させた。反応液に、フェニルボロン酸を０．１１ｇ加えて、１時間還流させた。次に、反応液にＮ，Ｎ−ジエチルジチオカルバミド酸ナトリウム三水和物を０．１ｇ加えて、３時間還流させた。その後、反応液を水に注ぎ、トルエンを加え、トルエン層を抽出した。トルエン溶液を酢酸水溶液及び水で洗浄した後、トルエン溶液をアセトンに滴下し、析出物を得た。析出物をクロロホルムに溶解させ、クロロホルムを展開溶媒として用いたシリカゲルカラムで精製を行った。精製後のクロロホルム溶液をメタノールに滴下し、析出物をろ過し、高分子化合物２を得た。得量は３．４ｇであり、ポリスチレン換算の数平均分子量は６．４×１０^４であり、重量平均分子量は２．９×１０^５であった。 Reference Example 6
Synthesis of polymer compound 2

3.8 g (4.9 mmol) of 2,6-dibromo-4,4-dihexadecylcyclopenta [2,1-b: 3,4-b ′] dithiophene was added to the flask where the gas in the flask was replaced with nitrogen. ), 4,7-bis (4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl) -2,1,3-benzothiadiazole 1.9 g (4.9 mmol), 170 mL of tetrahydrofuran, 89 mg of tris (dibenzylideneacetone) dipalladium, and 0.11 g of tri-tert-butylphosphonium tetrafluoroborate were added and stirred. To this solution, 24 mL of a 2 mol / L potassium carbonate aqueous solution was dropped and refluxed for 3 hours. To the reaction solution, 0.11 g of phenylboronic acid was added and refluxed for 1 hour. Next, 0.1 g of sodium N, N-diethyldithiocarbamate trihydrate was added to the reaction solution, and the mixture was refluxed for 3 hours. Thereafter, the reaction solution was poured into water, toluene was added, and the toluene layer was extracted. After the toluene solution was washed with an acetic acid aqueous solution and water, the toluene solution was added dropwise to acetone to obtain a precipitate. The precipitate was dissolved in chloroform and purified with a silica gel column using chloroform as a developing solvent. The purified chloroform solution was added dropwise to methanol, and the precipitate was filtered to obtain polymer compound 2. The obtained amount was 3.4 g, the number average molecular weight in terms of polystyrene was 6.4 × 10 ⁴ , and the weight average molecular weight was 2.9 × 10 ⁵ .

Example 2
(Production and evaluation of organic thin-film solar cells)
A fullerene derivative C70PCBM (Phenyl C71-butyric acid methyl ester, manufactured by American Dye Source Co., Ltd., trade name: ADS71BFA (Lot No. 11A004E), which is an electron-accepting compound, and a polymer compound 1 which is an electron-donating compound are The mixture was dissolved in o-dichlorobenzene so that the concentration of the mixture was 2.25% by weight, and the resulting solution was filtered through a Teflon filter having a pore size of 0.5 μm. A coating solution 1 was prepared.

A glass substrate provided with an ITO film with a thickness of 150 nm by a sputtering method was subjected to surface treatment by ozone UV treatment. Next, a PEDOT: PSS solution (CleviosP VP AI4083 manufactured by HC Starck Co., Ltd.) is applied onto the ITO film by spin coating, and heated at 120 ° C. for 10 minutes in the atmosphere to thereby form a hole injection layer having a thickness of 50 nm. It was created. Next, the coating solution 1 was applied onto the ITO film by spin coating to obtain a functional layer of an organic thin film solar cell. The film thickness of the functional layer was 100 nm. Then, the organic thin film solar cell was produced by vapor-depositing calcium with a film thickness of 4 nm with a vacuum evaporation machine, and vapor-depositing aluminum with a film thickness of 100 nm. The degree of vacuum at the time of vapor deposition was 1 to 9 × 10 ⁻³ Pa in all cases. The shape of the organic thin film solar cell thus obtained was a square of 2 mm × 2 mm. The obtained organic thin film solar cell is irradiated with a certain amount of light using a solar simulator (trade name: OTENTO-SUNII: AM1.5G filter, irradiance: 100 mW / cm ² ), and the generated current and voltage are measured. did. Voc (open end voltage) was 0.56V.

Comparative Example 1
(Production and evaluation of organic thin-film solar cells)
An organic thin film solar cell was prepared and evaluated in the same manner as in Example 2 except that the polymer compound 2 was used instead of the polymer compound 1. Voc (open end voltage) was 0.53V.

Example 3
(Measurement of ionization potential of organic thin film)
The polymer compound 1 was dissolved in o-dichlorobenzene at 0.75% by weight. The obtained solution was filtered through a Teflon (registered trademark) filter having a pore size of 0.5 μm and applied by spin coating. The coating operation was performed at 23 ° C. Then, it baked for 5 minutes on 120 degreeC conditions in air | atmosphere, and obtained the organic thin film with a film thickness of about 100 nm. The ionization potential was measured using an atmospheric photoelectron spectrometer (AC-2, manufactured by Riken Keiki Co., Ltd.) using the obtained thin film. The obtained ionization potential was 4.90 eV.

Comparative Example 2
(Measurement of ionization potential of organic thin film)
The ionization potential of the organic thin film was measured in the same manner as in Example 3 except that the polymer compound 2 was used instead of the polymer compound 1. The obtained ionization potential was 4.78 eV.

  Thus, the polymer compound 1 using the repeating unit represented by the formula (1) has a deeper ionization potential of the thin film than the polymer compound 2 not using the repeating unit represented by the formula (1). , Showed a high open circuit voltage.

Claims (5)

A polymer compound having a repeating unit represented by the formula (1) and a repeating unit represented by the formula (2), the repeating unit and the formula represented by the formula (1) contained in the polymer compound (2) The high molecular compound whose total amount of the repeating unit represented by this polymer compound is 30-100 mol% with respect to the total amount of the repeating unit which this high molecular compound contains .

(1)
[In the formula (1), Ar ¹ and Ar ² represent an aryl group having 6 to 60 carbon atoms which may have a substituent. Ar ¹ and Ar ² may be the same or different. X represents a carbon atom, a silicon atom, or a germanium atom. ]

(2)
[In formula (2), R represents a hydrogen atom or a fluorine atom. A plurality of R may be the same or different. Q represents an oxygen atom, a sulfur atom, or a selenium atom. ] An organic photoelectric conversion element comprising a pair of electrodes and a functional layer provided between the electrodes, wherein the functional layer includes an electron-accepting compound and the polymer compound according to claim 1 . The organic photoelectric conversion element according to claim 2 , wherein the amount of the electron-accepting compound contained in the functional layer is 10 to 1000 parts by weight with respect to 100 parts by weight of the polymer compound. The organic photoelectric conversion device according to claim 2 or 3 , wherein the electron-accepting compound is a fullerene derivative. An organic thin film transistor comprising a source electrode, a drain electrode, an organic semiconductor layer, and a gate electrode, wherein the organic semiconductor layer includes the polymer compound according to claim 1 .