JP5764772B1 - Water battery - Google Patents

Abstract

To provide a water battery capable of obtaining a larger electromotive force with a quick rise and maintaining a stable discharge for a longer time. A water battery including a housing and a battery cell provided in the housing and operating by pouring water into the housing during use, the battery cell being a metal material having a smaller ionization tendency than magnesium. A positive electrode composed of a positive electrode connected electrically to the positive electrode, a negative electrode composed of a magnesium alloy material, a negative electrode electrically connected to the negative electrode, a surface of the positive electrode, or a positive electrode A sheet material having water absorption and water retention provided between the negative electrode and a water-soluble solid electrolyte filled in the housing, the solid electrolyte being composed of one or more citrates Yes. [Selection] Figure 1

Description

  The present invention relates to a water battery that generates electricity by causing an electrochemical reaction by using different types of electrodes having different ionization tendencies for a positive electrode and a negative electrode and injecting water or an electrolytic solution.

  Water batteries and seawater batteries that obtain electromotive force by immersing dissimilar electrodes with different ionization tendencies in water or seawater have been well known in the past, and in order to obtain higher performance in this type of water battery or seawater battery. Many proposals have also been made.

  For example, a small water battery that can generate a predetermined electromotive force by supplying a small amount of moisture has been proposed (Patent Document 1).

  The water battery disclosed in Patent Document 1 includes a positive electrode active material layer that is in contact with the inner surface of the positive electrode plate between the positive electrode plate and the negative electrode plate, and between the positive electrode plate and the inner surface of the negative electrode plate. An electric insulator layer is interposed between the positive electrode plate and the negative electrode plate.

  Further, the present applicant has proposed a water battery that has a plurality of battery cells, can be stored for a long period of time, and can be used as an emergency power source (Patent Document 2).

  Each battery cell of the water battery disclosed in Patent Document 2 includes a carbonized cloth constituting a positive electrode, a positive electrode lead electrode electrically connected to the carbonized cloth, and a salt provided in close contact with the carbonized cloth. And a paper sheet having water absorption provided in close contact with the salt-containing cloth, and formed in a material that is provided in close contact with the paper sheet and constitutes the negative electrode, and has a higher ionization tendency than the positive electrode. A metal plate, a negative electrode lead electrode electrically connected to the metal plate, and a shrinkable cover member that crimps the carbonized cloth, the positive electrode lead electrode, the salt-containing cloth, the paper sheet, the metal plate, and the negative electrode lead electrode to each other. The salt-containing cloth is made of a cloth obtained by impregnating a multi-layer woven cotton cloth with salt.

JP 2011-222236 A Japanese Patent No. 4759659

  However, in a conventional water battery, for example, in the case of a water battery in which magnesium metal is used as a negative electrode, magnesium hydroxide generated by an electrochemical reaction is deposited on the surface of the negative electrode. The electrochemical reaction between the positive and negative electrodes becomes very slow and the electromotive force decreases.On the other hand, when the concentration of the electrolyzed water is high, the electrochemical reaction between the positive and negative electrodes occurs rapidly and occurs on the surface of the negative electrode. There was a problem that a new electrochemical reaction was inhibited by the precipitated magnesium hydroxide.

  Moreover, although the water battery of patent document 1 can produce a required electromotive force rapidly, there existed a problem that it was not able to be maintained over a long time.

  In recent years, a water battery that can be stored for a long period of time as an emergency battery for an emergency such as a disaster, and that can generate electricity simply by injecting a liquid such as water in an emergency such as a disaster, is expected. From the viewpoint of convenience of use, a water battery having the same shape as a commercially available dry battery is also expected.

  Accordingly, an object of the present invention is to provide a water battery that can obtain a larger electromotive force with a quick rise and can maintain a stable discharge for a longer time.

  Still another object of the present invention is to provide a water battery that can be easily manufactured at low cost, is simple to use, and is convenient to carry.

  According to the present invention, a water battery including a housing and a battery cell provided in the housing and operating by pouring water into the housing at the time of use, the battery cell having a smaller ionization tendency than magnesium. A positive electrode composed of a metal material, a positive electrode extraction electrode electrically connected to the positive electrode, a negative electrode composed of a magnesium alloy material, a negative electrode extraction electrode electrically connected to the negative electrode, and a positive electrode and a negative electrode A sheet material having water absorption and water retention provided therebetween and a water-soluble solid electrolyte filled in the housing are provided, and the solid electrolyte is composed of one or more citrates.

  As described above, according to the water battery of the present invention, by using one or more kinds of citrate as the solid electrolyte, a larger electromotive force can be obtained at a quick rise and a stable discharge can be maintained for a long time. it can.

  The magnesium alloy material of the negative electrode preferably contains 0.01% or less of an aluminum component and 0.5 to 1.3% of a manganese component in magnesium. Thereby, the stable discharge can be maintained over a long time.

  The housing is composed of a lid and a bottomed cylindrical portion provided with at least one water inlet on the side surface, the positive electrode is formed in a cylindrical shape that can be inserted into the housing from a metal plate, and the negative electrode is a negative electrode at one end It has a hole for inserting an extraction electrode, is formed in a column shape that can be inserted into the positive electrode, the sheet material is disposed between the positive electrode and the negative electrode, and the solid electrolyte is filled at the bottom of the housing Is preferred. This makes it possible to obtain a water battery that can be easily manufactured at low cost, is easy to use, and is convenient to carry.

  The housing is composed of a lid body provided with at least one water inlet and a box body, and the positive electrode is a flat metal plate, a conductive nonwoven fabric provided in close contact with one side of the metal plate, and a metal Insulating sheets disposed on both sides of the laminate of the plate and the conductive nonwoven fabric, the negative electrode is composed of a magnesium alloy plate, the sheet material is a porous resin sheet, and between the positive electrode and the negative electrode It is preferable that they are stacked on each other. Thereby, the capacity | capacitance of an electrolyte cell can be enlarged.

  The housing is composed of a lid body provided with at least one water inlet and a box body, the positive electrode is composed of a flat metal plate, the negative electrode is composed of a magnesium alloy plate, and the sheet material is It is a porous resin sheet, and is preferably laminated on both sides of the positive electrode, and the positive electrode and the negative electrode preferably constitute a battery cell integrated at the top by resin molding. Thereby, replacement | exchange of a battery cell can be performed easily.

  A water battery comprising a housing and a battery cell unit comprising a plurality of battery cells provided in the housing and operating by pouring water into the housing during use, wherein the plurality of battery cells are electrically It is preferable that they are connected in series or in parallel. Thereby, the electromotive force of a water battery can be improved and the stable discharge can be maintained over a long time.

  It is preferable that a common positive electrode or negative electrode is provided between two adjacent battery cells among the plurality of battery cells. Thereby, a battery cell unit becomes compact and it can aim at reduction of cost.

  The water battery of the present invention can obtain a larger electromotive force with a quick rise by using one or more citrates as the solid electrolyte, and can maintain a stable discharge for a long time. In addition, by placing a sheet material having water absorption and water retention between the positive electrode and the negative electrode, it is possible to improve the standing characteristics of the water battery. As an emergency battery for emergency use, water can be used in an emergency such as a disaster. Power can be generated simply by injecting a liquid such as

  Moreover, by forming the same cylindrical shape as a commercially available dry battery, it is possible to easily manufacture at a low cost, and to provide a water battery that can be used for various lighting fixtures, electronic devices, etc. and is convenient to carry. it can.

It is sectional drawing which shows roughly the structure of the water battery in the 1st Embodiment of this invention. It is a disassembled perspective view which shows the structure of the water battery in embodiment of FIG. It is a figure which shows the manufacturing process of the water battery in embodiment of FIG. It is a perspective view which shows roughly the structure of the water battery in the 2nd Embodiment of this invention. It is a disassembled perspective view which shows the structure of the battery cell of the water battery in embodiment of FIG. It is a perspective view which shows the other structure of the battery cell of the water battery which concerns on 2nd Embodiment. It is a figure which shows schematically the structure of the water battery in the 3rd Embodiment of this invention. It is a figure which shows the manufacturing process of the battery cell of the water battery in embodiment of FIG. It is sectional drawing which shows roughly the other structural example of the water battery which concerns on 3rd Embodiment. It is a figure which shows the difference of the electromotive current in the structure of various battery cells. It is a figure which shows the difference of the estimated electromotive current in the density | concentration of the base of electrolyte. It is a figure which shows the relationship between the density | concentration of the base of electrolyte, and an electromotive voltage. It is a figure which shows the difference of the estimated electromotive current in the pH value of electrolyte. It is a figure which shows the relationship between the pH value of electrolyte, and an electromotive voltage. It is a figure which shows transition of the electromotive current of the unit area of the water battery of this invention, and the conventional water battery. It is a figure which shows the difference of the electromotive voltage in various electrolytes. It is a figure which shows the difference of the electromotive current of the unit area in various electrolytes. It is a figure which shows schematically the other structural example of a battery cell unit.

  Hereinafter, embodiments of a water battery according to the present invention will be described with reference to the drawings.

  FIG. 1 shows the configuration of the water battery 100 according to the first embodiment of the present invention, and FIG. 2 shows the specific structure of the water battery 100 in detail. FIG. 3 shows a manufacturing process of the water battery 100.

  As shown in FIGS. 1 and 2, a water battery 100 according to this embodiment includes a housing 10, a positive electrode 20 made of a metal material having a smaller ionization tendency than magnesium, and a positive electrode drawer electrically connected to the positive electrode. Electrode 30, negative electrode 40 made of a magnesium alloy material, negative electrode extraction electrode 50 electrically connected to the negative electrode, and a sheet having water absorption and water retention provided in close contact between the positive electrode and the negative electrode A material 60 and a water-soluble solid electrolyte 70 filled in the housing are provided. Here, the positive electrode 20, the positive electrode extraction electrode 30, the negative electrode 40, the negative electrode extraction electrode 50, and the sheet material 60 constitute one battery cell.

  The housing 10 includes, for example, a cylindrical portion 10a formed in a bottomed cylindrical shape whose upper surface is opened from a plastic material, and a lid 10b that closes the upper surface. The cylindrical portion 10a is provided with at least one water inlet 11 on the side surface. Moreover, the protrusion part is formed in the bottom face of the cylinder part 10a. The outer surface of the cylindrical portion 10a is covered with a conductive layer 12 made of a conductive material.

  The positive electrode 20 is formed in a cylindrical shape that can be inserted into the cylindrical portion 10 a of the housing 10 from a metal plate. The positive electrode 20 is made of a material having a relatively high conductivity and a smaller ionization tendency than magnesium, for example, high-purity aluminum or high-purity copper. In this embodiment, a flat plate made of high purity copper is used.

  The positive electrode lead electrode 30 is formed of a conductive metal material such as copper and is electrically connected to the positive electrode 20. In the present embodiment, a thin metal piece is used, adhered to the positive electrode 20 with a conductive adhesive, and the upper part is formed to be bent outward so as to be electrically connected to the outer surface of the cylindrical portion 10 a of the housing 10. The protruding portion on the bottom surface of the cylindrical portion 10 a of the housing 10 serves as the positive electrode terminal 31. In addition, a waterproof treatment is applied to the bonding portion between the positive electrode lead electrode 30 and the positive electrode 20.

  The negative electrode 40 is formed of a material having a higher ionization tendency than the positive electrode 20, for example, a high purity magnesium alloy material. For example, the magnesium alloy material does not contain a zinc (Zn) component in high-purity magnesium, an aluminum (Al) component is 0.01% or less, and a manganese (Mn) component is 0.5 to 1.3%. Contained. The negative electrode 40 is formed in a cylindrical shape that can be inserted into the positive electrode 20. In addition, a hole 41 for inserting the negative electrode lead electrode 50 is provided at one end of the negative electrode 40.

  The negative electrode extraction electrode 50 is formed of a conductive metal material such as copper. In the present embodiment, the disk portion 51 as a negative electrode terminal and the columnar portion arranged perpendicular to the disk portion 51 are used. 52. The disc portion 51 can be fitted into a recess formed on the outer surface of the lid 10b. The cylindrical portion 52 is configured to be inserted into the hole 41 of the negative electrode 40 and electrically connected to the negative electrode 40. A negative electrode conductive layer 53 is formed on the surface of the cylindrical portion 52.

  The sheet material 60 is composed of a nonwoven fabric having water absorption and water retention. The sheet material 60 is provided between the positive electrode 20 and the negative electrode 40.

  The solid electrolyte 70 is a powder of a citrate substance and is filled in the bottom of the housing 10. As the solid electrolyte 70, for example, sodium citrate, potassium citrate, ammonium citrate, iron (III) ammonium citrate, or the like can be used. In addition, you may mix and use 2 types in the said ratio among the said citrate. For example, a mixture of sodium citrate and iron (III) ammonium citrate, or a mixture of potassium citrate and iron (III) ammonium citrate may be used.

  In the manufacturing process of the water battery 100, as shown in FIG. 3, on the positive electrode side, after forming a metal plate for the positive electrode 20, the positive electrode lead electrode 30 is bonded to the positive electrode 20 with a conductive adhesive. Next, the bonded portion of the positive electrode lead electrode 30 is waterproofed. Next, the positive electrode 20 is processed into a cylindrical shape, and the upper portion of the positive electrode lead electrode 30 is bent outward. On the housing side, a water injection port 11 is formed on the side surface of the resin cylindrical portion 10a, and the conductive layer 12 made of a conductive material is coated on the outer surface of the cylindrical portion 10a by a method such as painting (or vapor deposition). Next, the insulating paper P is disposed on the bottom surface inside the cylinder portion 10a. Then, the positive electrode 20 processed into a cylindrical shape is inserted into the cylindrical portion 10 a of the housing 10. Next, the solid electrolyte 70 is filled in the cylindrical portion 10 a of the housing 10. On the other hand, on the negative electrode side, a hole 41 is formed at one end of the negative electrode 40 formed in a columnar shape. Further, the negative electrode conductive layer 53 is formed on the surface of the cylindrical portion 52 of the negative electrode 50. Next, the disc part 51 of the negative electrode lead-out electrode 50 is fitted into the recess of the lid body 10b and attached. Subsequently, the cylindrical part 52 is inserted into the hole 41 of the negative electrode 40 to constitute a negative electrode assembly. Next, the sheet material 60 is wound around the surface of the negative electrode 40. Next, the negative electrode assembly around which the sheet material 60 is wound is inserted into the positive electrode 20 to seal the housing 10. Finally, the outer surface of the housing 10 is covered with an insulating outer covering layer F made of a resin film or the like, and the water battery 100 is completed.

  As described above, the water battery 100 of this embodiment includes the housing 10, the positive electrode 20, the positive electrode extraction electrode 30, the negative electrode 40, the negative electrode extraction electrode 50, the sheet material 60, and the solid electrolyte 70. ing. For the solid electrolyte 70, citrate is used, and for the negative electrode 40, a magnesium alloy material containing 0.01% or less of an aluminum component and 0.5 to 1.3% of a manganese component in magnesium is used. Thus, it is possible to suppress the magnesium hydroxide generated by the electrochemical reaction from being deposited on the surface of the negative electrode, and it is possible to maintain a stable discharge for a long time. Moreover, by forming it into the same cylindrical shape as a commercially available single to single type dry battery, it can be easily manufactured at low cost, can be used for various lighting fixtures and electronic devices, and is convenient to carry. A water battery can be provided.

  FIG. 4 schematically shows the configuration of a water battery 100A according to the second embodiment of the present invention. FIG. 5 shows the configuration of the battery cell of the water battery 100A. As shown in FIGS. 4 and 5, the water battery 100A includes a housing 10A, a positive electrode 20A, a positive electrode extraction electrode 30A, a negative electrode 40A, a negative electrode extraction electrode 50A, a sheet material 60A, a solid electrolyte 70, a conductive material. 80A. Here, the positive electrode 20A, the positive electrode extraction electrode 30A, the negative electrode 40A, the negative electrode extraction electrode 50A, and the sheet material 60A constitute a stacked battery cell. The solid electrolyte 70 uses the same material as the water battery 100.

  The housing 10A includes, for example, a box body 10c whose upper surface is opened from a plastic material, and a lid 10d that closes the upper surface. A slit into which the positive electrode 20A and the negative electrode 40A can be fitted is provided inside the box body 10c. The lid body 10d is provided with at least one water injection port 11A. A positive terminal 12A and a negative terminal 13A are provided on the upper surface of the lid 10d.

  The positive electrode 20A is provided in close contact with a rectangular positive electrode plate 21A made of a material having a relatively high conductivity and less ionization tendency than magnesium, for example, high-purity aluminum or high-purity copper, and one surface of the positive electrode plate 20A. The conductive nonwoven fabric 22A containing copper and nickel, and the insulating sheet 23A made of a porous resin disposed on both sides of a laminate of the positive electrode plate 20A and the conductive nonwoven fabric 22A. In the present embodiment, the positive electrode plate 20A is a copper plate.

  The positive electrode lead electrode 30A is formed in a plate shape from a conductive metal material such as copper, and is provided on both upper surfaces of the positive electrode 20A.

  The negative electrode 40A is formed in a rectangular plate shape from a material having a higher ionization tendency than the positive electrode 20A, for example, a high-purity magnesium alloy material similar to that in the first embodiment. The negative electrode 40A is formed to have substantially the same area as the positive electrode 20A.

  The negative electrode extraction electrode 50A is formed in a plate shape from a conductive metal material such as copper, and is provided on both upper surfaces of the negative electrode 40A.

  The sheet material 60A is made of a porous resin and a nonwoven fabric having water absorption and water retention. The sheet material 60A is provided in close contact between the positive electrode 20A and the negative electrode 40A.

  The conductive layer 80A is provided in close contact between the upper part of the positive electrode 20A and the sheet material 60A and between the upper part of the negative electrode 40A and the sheet material 60A.

  As described above, the water battery 100A of the present embodiment includes the housing 10A, the positive electrode 20A, the positive electrode extraction electrode 30A, the negative electrode 40A, the negative electrode extraction electrode 50A, the sheet material 60A, the solid electrolyte 70, the conductive material. 80A. The solid electrolyte 70 is made of citrate, and the negative electrode 40A is made of magnesium alloy material containing 0.01% or less of an aluminum component and 0.5 to 1.3% of a manganese component in magnesium. Furthermore, by using the stacked battery cell, it is possible to suppress the magnesium hydroxide generated by the electrochemical reaction from being deposited on the surface of the negative electrode and to maintain a stable discharge for a long time. .

  The water battery 100A is composed of one battery cell, but the present invention is not limited to this. You may make it comprise using a several laminated battery cell. FIG. 6 shows an example of a battery cell unit made up of a plurality of stacked battery cells. FIG. 6A shows a battery cell unit made up of one negative electrode 40A and two positive electrodes 20A, and FIG. It is a battery cell unit comprising one negative electrode 40A and two positive electrodes 20A.

  FIG. 7 schematically shows the configuration of a water battery 100B according to the third embodiment of the present invention, where FIG. 7A is a view seen from above, FIG. 7B is a sectional view, and FIG. ) Is a side view. As shown in FIG. 7, the water battery 100B includes a housing 10B, a positive electrode 20B, a positive electrode extraction electrode 30B, a negative electrode 40B, a negative electrode extraction electrode 50B, a sheet material 60B, a solid electrolyte 70, and an insulating plate 80B. It has. Here, the positive electrode 20B, the positive electrode extraction electrode 30B, the negative electrode 40B, the negative electrode extraction electrode 50B, and the sheet material 60B constitute a battery cell integrated at the top by resin molding. The solid electrolyte 70 uses the same material as that of the water battery 100 of the first embodiment.

  The housing 10B includes, for example, a box body 10c whose upper surface is opened from a plastic material, and a lid 10d that closes the upper surface. The lid 10d is provided with at least one (for example, two) water inlet 11B. Moreover, the opening part which inserts a battery cell is provided in the upper surface of the cover body 10d.

  The positive electrode 20B is made of a material having a relatively high conductivity and a smaller ionization tendency than magnesium, for example, high-purity aluminum or high-purity copper. In this embodiment, a copper plate is used.

  The positive electrode extraction electrode 30B is formed in a plate shape from a conductive metal material such as copper, and is fixed to both upper surfaces of the positive electrode 20B.

  The negative electrode 40B is formed in a rectangular plate shape from a material having a higher ionization tendency than the positive electrode 20B, for example, a high-purity magnesium alloy material similar to the case of the first embodiment. The negative electrode 40B is formed to have substantially the same area as the positive electrode 20B.

  The negative electrode lead electrode 50B is formed in a plate shape from a conductive metal material such as copper, and is fixed to both upper surfaces of the negative electrode 40B.

  The sheet material 60B is composed of a film having water absorption and water retention properties made of a porous resin. The sheet material 60B is provided by being thermally fused to the surface of the positive electrode 20B.

  The insulating plate 80B is made of, for example, a resin material, and is disposed between the positive electrode 20B and the negative electrode 40B, and between the positive electrode 20B and the negative electrode 40B.

  FIG. 8 shows a manufacturing process of the battery cell of the water battery 100B. In the battery cell manufacturing process of the water battery 100B, as shown in FIG. 8, a conductive heat-sealing resin is applied to a predetermined range above the copper plate of the positive electrode plate 21B. Next, the positive electrode lead electrode 30B is fixed on the applied conductive heat-sealing resin by thermocompression bonding. Next, the sheet material 60B is heat-sealed so as to cover the surface of the positive electrode plate 21B, thereby forming the positive electrode 20B (positive electrode assembly). On the other hand, a conductive heat sealing resin is applied to a predetermined range above the magnesium alloy plate of the negative electrode 40B. Next, the negative electrode lead electrode 50B is fixed on the applied conductive heat-sealing resin by thermocompression bonding to constitute a negative electrode assembly. Next, the insulating plate 80B is disposed and laminated between the obtained positive electrode assembly and negative electrode assembly. Next, the upper part of the positive electrode assembly and the negative electrode assembly is fixed and integrated by resin molding. Finally, the resin molded portion 90B is insulated and waterproofed to complete the battery cell.

  As described above, in the water battery 100B of the present embodiment, the positive electrode 20B, the positive electrode extraction electrode 30B, the negative electrode 40B, the negative electrode extraction electrode 50B, and the sheet material 60B are integrated at the top by resin molding. By constituting the cell, it is possible to suppress the magnesium hydroxide produced by the electrochemical reaction from being deposited on the surface of the negative electrode, and it is possible to maintain a stable discharge for a long time. Further, the battery cell can be easily replaced. Since the other effect of this embodiment is the same as that of the case of 1st Embodiment, description is abbreviate | omitted.

  In addition, although the water battery 100B of this embodiment consists of one battery cell, this invention is not limited to this. You may make it comprise using the battery cell unit which consists of a some battery cell. 9 shows a water battery 100C having a battery cell unit composed of three positive electrodes 20B and two negative electrodes 40B. The battery capacity is increased by using a battery cell unit including a plurality of battery cells.

  FIG. 10 shows the difference in electromotive current in various battery cell configurations. In the figure, “SK” is a battery cell composed of one positive electrode and one negative electrode, “DK” is a battery cell composed of one positive electrode and two negative electrodes, and “TK” is two positive electrodes and three negative electrodes. “DATK” is a battery cell composed of two positive electrodes and three negative electrodes whose electrode terminals are connected in parallel, and “cylindrical” is a battery cell of a cylindrical dry battery. As shown in the figure, the electromotive current of the “DATK” type battery cell composed of two positive electrodes and three negative electrodes having electrode terminals connected in parallel is the largest.

  FIG. 11 shows the difference in the estimated electromotive current in the concentration of the electrolyte base. As shown in the figure, the electromotive current increases as the concentration of the electrolyte base increases. FIG. 12 shows the relationship between the concentration of the electrolyte base and the electromotive voltage. As shown in the figure, the electromotive voltage decreases as the concentration of the electrolyte base increases. The results shown in FIG. 11 and FIG. 12 are obtained using “DK” type battery cells.

  FIG. 13 shows the difference in the estimated electromotive current at the pH value of the electrolyte. As shown in the figure, when the pH value is 12, the electromotive current is the largest. When the pH value is 7, the electromotive current is the smallest. FIG. 14 shows the relationship between the pH value of the electrolyte and the electromotive voltage. As shown in the figure, when the pH value is 7, the electromotive voltage is the largest. The results shown in FIGS. 13 and 14 are obtained by using “DK” type battery cells.

FIG. 15 shows the transition of the electromotive current of the unit area of the water battery of the present invention and the conventional water battery. As shown in the figure, in the case of the conventional water battery (old negative electrode), it dropped to 9 mA / cm ² or less in 50 hours. On the other hand, in the case of the water battery (new negative electrode) of the present invention, it can be maintained at 14 mA / cm ² or more even for 300 hours or more. Further, if the surface of the electrode is cleaned, a longer time can be maintained.

  FIG. 16 shows the difference in electromotive voltage between various electrolytes. As shown in the figure, in the case of citrate, an electromotive voltage higher than that of sodium chloride and potassium chloride can be obtained. FIG. 17 shows the difference in electromotive current of unit areas in various electrolytes. As shown in the figure, in the case of citrate, an electromotive current having a unit area higher than that of sodium chloride and potassium chloride can be obtained.

  In the water battery 100B of the third embodiment described above, as shown in FIG. 18, the battery cell may be formed integrally with the lid 10d of the housing 10B. In this case, since the battery cell is integrally formed with the lid body 10d of the housing 10B, the mounting operation of the battery cell to the lid body 10d and the waterproofing treatment of the mounting portion are not required, and the sealing performance can be improved. .

  Further, in the water batteries 100, 100A, 100B, and 100C of the above-described embodiment, the anticorrosion treatment may be performed on the surface of the negative electrode plate. Thereby, it can suppress that the magnesium hydroxide produced | generated by the electrochemical reaction precipitates on the surface of a negative electrode, and can maintain the stable discharge over a long time.

  The water battery 100A according to the second embodiment described above may further include a fixing member that presses and fixes the stacked body of the positive electrode 20A, the sheet material 60A, and the negative electrode 40A. For example, the laminate of the positive electrode 20A, the sheet material 60A, and the negative electrode 40A is pressure-bonded and fixed to each other using a tape or a heat shrinkable tube as the fixing member.

  In the water battery 100 of the first embodiment described above, a conductive nonwoven fabric may be provided in close contact with the inner surface of the positive electrode 20. In this case, the current collection effect can be improved.

  The present invention is not limited to the above-described embodiment, but includes variously modified forms within the technical scope without departing from the gist of the invention described in the claims.

  INDUSTRIAL APPLICABILITY The present invention can be used for the purpose of easily producing a water battery that can generate electricity simply by injecting a liquid such as water in an emergency such as a disaster at low cost and improving the convenience of use and carrying.

10, 10A, 10B Housing 10a Tube portion 10b, 10d Lid 10c Box body 11, 11A Water inlet 12A Positive electrode terminal 13A Negative electrode terminal 20, 20A, 20B Positive electrode 21A Positive electrode plate 30, 30A, 30B Positive electrode lead electrode 40, 40A, 40B Negative electrode 41 Hole 50, 50A, 50B Negative electrode extraction electrode 51 Disc portion 52 Column portion 53 Negative electrode conductive layer 60, 60A, 60B Sheet material 70 Solid electrolyte 80A Conductive layer 80B Insulating plate 100, 100A, 100B, 100C Water battery P Insulating paper F Exterior coating layer

Claims (6)

A water battery comprising a housing and a battery cell provided in the housing and operating by pouring water into the housing at the time of use,
The battery cell includes a positive electrode made of a metal material having a lower ionization tendency than magnesium, a positive electrode lead electrode electrically connected to the positive electrode, a negative electrode made of a magnesium alloy material, and an electric electrode electrically connected to the negative electrode A connected negative electrode lead electrode, a surface of the positive electrode or a sheet material having water absorption and water retention provided between the positive electrode and the negative electrode, and a water-soluble solid electrolyte filled in the housing. Prepared,
The solid electrolyte is composed of one or more citrates ,
The negative electrode magnesium alloy material contains 0.01% or less of an aluminum component and 0.5 to 1.3% of a manganese component in magnesium . The housing is composed of a lid and a bottomed cylindrical portion provided with at least one water inlet on a side surface,
The positive electrode is formed in a cylindrical shape that can be inserted into the housing from a metal plate,
The negative electrode has a hole for inserting the negative electrode lead electrode at one end, and is formed in a column shape that can be inserted into the positive electrode.
The sheet material is disposed between the positive electrode and the negative electrode,
The water battery according to claim 1, wherein the solid electrolyte is filled in a bottom portion of the housing. The housing is composed of a lid provided with at least one water inlet, and a box body ,
Before SL negative electrode is composed of a plate of the magnesium alloy,
3. The water battery according to claim 1, wherein the sheet material is a porous resin sheet, and is stacked between the positive electrode and the negative electrode. The housing is composed of a lid provided with at least one water inlet, and a box body,
The positive electrode is composed of a flat metal plate,
The negative electrode is composed of the magnesium alloy plate,
The sheet material is a porous resin sheet, and is laminated on both sides of the positive electrode,
3. The water battery according to claim 1, wherein the positive electrode and the negative electrode constitute a battery cell integrated at an upper portion by resin molding. 4. A water battery comprising a housing and a battery cell unit comprising a plurality of battery cells provided in the housing, and operating by pouring water into the housing during use;
The water battery according to claim 3 or 4 , wherein the plurality of battery cells are electrically connected in series or in parallel. The water battery according to claim 5 , wherein a common positive electrode or negative electrode is provided between two battery cells adjacent to each other among the plurality of battery cells.

Images