JP5751651B2 - Adhesive sheet and method for manufacturing semiconductor device - Google Patents

Description

  The present invention relates to an adhesive sheet particularly suitable for use in a process of dicing a semiconductor wafer or the like to obtain a semiconductor chip and die-bonding the semiconductor chip on an organic substrate or a lead frame, and a semiconductor device using the adhesive sheet It relates to the manufacturing method.

  Semiconductor wafers such as silicon and gallium arsenide are manufactured in a large diameter state. After a circuit is formed on the surface of a semiconductor wafer, the semiconductor wafer is ground to a predetermined thickness by backside grinding, and is cut and separated (diced) into element small pieces (semiconductor chips), and then transferred to the next bonding process. At this time, the semiconductor wafer is subjected to dicing, cleaning, drying, expanding, and pick-up processes in a state where the semiconductor wafer is previously adhered to the adhesive sheet, and then transferred to the next bonding process (for example, Patent Document 1). To 4).

  Incidentally, in recent years, there has been a demand for reducing the thickness of a semiconductor chip due to a demand for miniaturization of elements. In order to reduce the size of the element, the wafer is ground thinner by backside grinding. However, as the wafer thickness decreases, the wafer strength decreases, and even a slight impact may damage the wafer. It is considered that the cause of wafer breakage is mainly a “crushed layer” in which grinder cutting marks and oxide films used during back grinding are combined.

  The fractured layer is a fine unevenness on the ground wafer surface, is in a state where silicon polycrystal or silicon is oxidized by a small amount of oxygen, and is considered to include lattice defects. Due to stress due to surface irregularities and composition changes, even a slight impact may cause cracking and damage of the wafer. For this reason, after the back surface grinding is finished, chemical etching or plasma etching is generally performed on the back surface in order to remove the crushed layer. By removing the crushed layer, the strength of the wafer is improved, and good handling is maintained even for a wafer that has been ground to an extremely thin thickness.

  However, there is a concern that the contamination resistance of the obtained wafer and chip to the metal is reduced by removing the crushed layer.

  The semiconductor wafer comes into contact with various members during circuit formation, back surface grinding, and mounting. At this time, a metal such as copper is released from these other members, and the wafer may be subjected to metal contamination. Impurity metals accumulate in the wafer, and may ionize and move within the wafer under heating conditions such as reflow. And the metal ion which reached | attained the circuit surface obstructs the electrical operation | movement of a product, and causes malfunction. In addition, metal ions that reach the circuit surface may generate metal on the circuit surface (these are sometimes called migrations). In particular, when metal is generated on the surface of a semiconductor wafer in which wiring is miniaturized, the circuit is short-circuited, and the yield of products is reduced.

  On the other hand, the crushed layer, as described above, is a fine unevenness, is in a state where silicon polycrystal or silicon is oxidized by a small amount of oxygen, and is considered to include lattice defects, these compositions, Due to the non-uniformity of the structure, it is considered that the above-described impurity metals can be easily captured and the effect of reducing metal contamination can be obtained. Such a function of the crushed layer is also called a gettering function.

  As described above, by removing the crushed layer after finishing the backside grinding of the wafer, the strength of the wafer is improved, but the gettering function is impaired and the product yield is reduced. For this reason, a technique for providing a gettering function by performing various processes on the semiconductor wafer and chip after removing the crushed layer has been proposed (Patent Documents 5 and 6).

JP-A-2-32181 JP-A-8-239636 Japanese Patent Laid-Open No. 10-8001 JP 2000-17246 A JP-A-2005-277116 JP 2007-242713 A

  However, as in Patent Documents 5 and 6, when a process for imparting a gettering function to a semiconductor wafer or chip is performed, the number of steps increases, resulting in a complicated process and an increase in cost.

  The present invention has been made in view of the above circumstances, and a gettering function is provided for a semiconductor device obtained without subjecting a semiconductor wafer or chip to a special process that increases the number of steps and complicates the process. The purpose is to grant.

  As a result of intensive research aimed at solving the above problems, the present inventors have come up with the idea that a gettering site can be introduced into a semiconductor device by blending a gettering agent with an adhesive used for fixing a semiconductor chip. The present invention has been completed.

The present invention includes the following gist.
(1) It consists of a base material and an adhesive layer laminated on the base material in a peelable manner,
The adhesive layer includes an acrylic polymer (A), an epoxy thermosetting resin (B), a thermosetting agent (C), and a gettering agent (D),
Adhesive layer have a concentration gradient of the gettering agent (D) to the thickness direction,
An adhesive sheet in which the adhesive layer has a low concentration of the gettering agent (D) on the substrate surface side and a high concentration of the gettering agent (D) on the surface opposite to the substrate surface .

(2) The adhesive sheet according to (1), wherein the gettering agent (D) is selected from the group consisting of a heavy metal deactivator (D1), an organic chelating agent (D2), and a copper ion-trapping metal compound (D3).

(3) The adhesive sheet according to (1) or (2), wherein the gettering agent (D) defined by the following has a copper ion adsorption capacity of 30% or more:
1 g of gettering agent was put into 50 g of a copper chloride aqueous solution having a copper ion concentration of 3 ppm, and the copper ion concentration of the copper ion aqueous solution after being left at 121 ° C. under 2 atm for 24 hours was measured.
Copper ion adsorption capacity = (3 ppm-residual copper ion concentration (ppm)) x 100/3 ppm.

(4) The adhesive sheet according to any one of (1) to (3), wherein 1 to 30 parts by weight of the gettering agent (D) is contained per 100 parts by weight of the total solid content constituting the adhesive layer.

(5) The adhesive sheet according to any one of (1) to (4), wherein 10 to 30 parts by weight of the gettering agent (D) is contained per 100 parts by weight of the total solid content constituting the adhesive layer.

(6) The surface of the adhesive layer opposite to the base material lamination surface is attached to the substrate to be diced,
Surface of the base material side of the adhesive layer, after removing the base material, according to any one of those which is adhered to the chip mounting portion for placing the diced adherend (1) to (5) Adhesive sheet.

(7) A semiconductor wafer is attached to the adhesive layer of the adhesive sheet according to any one of (1) to (6), the semiconductor wafer is diced into a semiconductor chip, and the adhesive is attached to the back surface of the semiconductor chip. A method of manufacturing a semiconductor device, comprising a step of leaving a layer to remain and peeling from a base material, and placing the semiconductor chip on a die pad portion or another semiconductor chip via the adhesive layer.

(8) The method for manufacturing a semiconductor device according to (7), wherein the semiconductor wafer has a crush layer formed by back grinding after the back grinding is reduced to a thickness of 50 nm or less.

  When fixing the semiconductor chip, by using the adhesive sheet according to the present invention, it is possible to introduce a gettering site into the obtained semiconductor device without subjecting the semiconductor wafer and the chip to special treatment.

  Moreover, in the adhesive sheet of the present invention, since the gettering agent is blended in the adhesive layer in contact with the semiconductor wafer and the chip, the impurity metal is easily trapped in the adhesive layer and exhibits excellent gettering properties. In addition, the adhesive layer has a gettering agent concentration gradient in the thickness direction, and the chip mounting portion side of the adhesive layer has wettability and is lower than the semiconductor wafer side or chip side of the adhesive layer. Since the concentration of the gettering agent that causes a decrease in the adhesive strength is low, it exhibits excellent wettability and adhesion to the adherend. Further, since the gettering agent has the above concentration gradient with respect to the thickness direction of the adhesive layer, the gettering agent on the chip mounting portion side of the adhesive layer causes a decrease in uneven embedding on the adherend surface. Because of its low concentration, it exhibits excellent shape followability, especially for adherends that have a surface with a large difference in unevenness, and the unevenness on the adherend surface can be embedded with an adhesive, contributing to improved adhesion. To do.

  Examples of the adhesive sheet having the same effect as the adhesive sheet of the present invention include an adhesive sheet using a laminated adhesive layer composed of a layer containing a gettering agent and a layer not containing it. Since the adhesive sheet of the present invention does not have an adhesive layer interface, a higher adhesive strength can be obtained as compared to an adhesive sheet using a laminated adhesive layer. In addition, the adhesive sheet of the present invention can be easily produced with a smaller number of steps as compared with an adhesive sheet using a laminated adhesive layer.

  Hereinafter, the present invention will be described more specifically, including its best mode. The adhesive sheet according to the present invention comprises a base material and an adhesive layer that is releasably laminated on the base material, and the adhesive layer comprises an acrylic polymer (A), an epoxy thermosetting resin ( B), a thermosetting agent (C) and a gettering agent (D), and the adhesive layer has a concentration gradient of the gettering agent (D) in the thickness direction. In addition, in order to improve various physical properties further, the adhesive layer may contain other components as necessary. Moreover, an adhesive bond layer is laminated | stacked on a base material so that peeling is possible. That is, the adhesive layer and the substrate can be peeled off. Hereinafter, each component which comprises an adhesive bond layer is demonstrated concretely.

(A) Acrylic polymer An acrylic polymer (A) is used to impart sufficient adhesiveness and film forming property (sheet processability) to the adhesive layer. A conventionally well-known acrylic polymer can be used as an acrylic polymer (A).

  The weight average molecular weight (Mw) of the acrylic polymer (A) is preferably 10,000 to 2,000,000, and more preferably 100,000 to 1,500,000. If the weight average molecular weight of the acrylic polymer (A) is too low, the adhesive force between the adhesive layer and the substrate becomes high, and pickup failure may occur. If it is too high, the adhesive layer follows the irregularities of the chip mounting portion. It may not be possible and may be a cause of voids.

  The glass transition temperature (Tg) of the acrylic polymer (A) is preferably -60 to 50 ° C, more preferably -50 to 40 ° C, and particularly preferably -40 to 30 ° C. If the glass transition temperature of the acrylic polymer (A) is too low, the peeling force between the adhesive layer and the substrate may become large and chip pick-up failure may occur. If it is too high, the adhesive force for fixing the wafer will be low. May be insufficient.

  As a monomer which comprises the said acrylic polymer (A), a (meth) acrylic acid ester monomer or its derivative (s) is mentioned. For example, an alkyl (meth) acrylate having an alkyl group having 1 to 18 carbon atoms, such as methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) (Meth) acrylates having a cyclic skeleton such as cycloalkyl (meth) acrylate, benzyl (meth) acrylate, isobornyl (meth) acrylate, dicyclopentanyl (meth) acrylate, dicyclopentenyl (meth) Acrylate, dicyclopentenyloxyethyl (meth) acrylate, imide (meth) acrylate, and the like; hydroxymethyl (meth) acrylate having a hydroxyl group, 2-hydroxyethyl (meth) acrylate, 2-hydride Kishipuropiru (meth) acrylate and the like; other, such as glycidyl (meth) acrylate having an epoxy group. In these, the acrylic polymer obtained by superposing | polymerizing the monomer which has a hydroxyl group has preferable compatibility with the epoxy-type thermosetting resin (B) mentioned later. The acrylic polymer (A) may be copolymerized with acrylic acid, methacrylic acid, itaconic acid, vinyl acetate, acrylonitrile, styrene, or the like.

(B) Epoxy-type thermosetting resin As an epoxy-type thermosetting resin (B), a conventionally well-known epoxy resin can be used. Specific examples of the epoxy thermosetting resin (B) include polyfunctional epoxy resins, biphenyl compounds, bisphenol A diglycidyl ether and hydrogenated products thereof, orthocresol novolac epoxy resins, dicyclopentadiene type epoxy resins. And biphenyl type epoxy resin, bisphenol A type epoxy resin, bisphenol F type epoxy resin, phenylene skeleton type epoxy resin and the like, and epoxy compounds having two or more functional groups in the molecule. These can be used individually by 1 type or in combination of 2 or more types.

  The adhesive layer preferably contains 1 to 1500 parts by weight, more preferably 3 to 1200 parts by weight of the epoxy thermosetting resin (B) with respect to 100 parts by weight of the acrylic polymer (A). . If the content of the epoxy thermosetting resin (B) is less than 1 part by weight, sufficient adhesiveness may not be obtained. If the content exceeds 1500 parts by weight, the peel strength between the adhesive layer and the substrate is high. And pickup failure may occur.

(C) Thermosetting agent The thermosetting agent (C) functions as a curing agent for the epoxy thermosetting resin (B). Preferred examples of the thermosetting agent (C) include compounds having two or more functional groups capable of reacting with an epoxy group in one molecule. Examples of the functional group include a phenolic hydroxyl group, an alcoholic hydroxyl group, an amino group, a carboxyl group, and an acid anhydride. Of these, phenolic hydroxyl groups, amino groups, acid anhydrides and the like are preferable, and phenolic hydroxyl groups and amino groups are more preferable.

  Specific examples of the phenolic curing agent include polyfunctional phenolic resin, biphenol, novolac type phenolic resin, dicyclopentadiene type phenolic resin, zylock type phenolic resin, and aralkylphenolic resin. A specific example of the amine curing agent is DICY (dicyandiamide). These can be used individually by 1 type or in mixture of 2 or more types.

  It is preferable that content of the thermosetting agent (C) in an adhesive bond layer is 0.1-500 weight part with respect to 100 weight part of epoxy-type thermosetting resins (B), and is 1-200 weight part. More preferably. If the content of the thermosetting agent (C) is small, the adhesiveness may not be obtained due to insufficient curing, and if it is excessive, the moisture absorption rate of the adhesive layer increases and the package reliability may be lowered.

(D) Gettering agent A gettering agent (D) is mix | blended with an adhesive bond layer, and has a density | concentration gradient with respect to the thickness direction of an adhesive bond layer. The concentration of the gettering agent (D) is lowest on the side of the die pad portion on the substrate or lead frame on which the semiconductor chip is mounted, or on the surface side of another semiconductor chip when the chips are stacked. Hereinafter, the die pad or the lower chip surface on which the chip is mounted may be referred to as a “chip mounting portion”. When the adhesive sheet of the present invention is used, on the chip mounting portion side of the adhesive layer, since the concentration of the gettering agent that causes a decrease in the adhesive strength is low, excellent adhesive strength is exhibited.

  The gettering agent (D) is not particularly limited as long as it has an action of capturing metal ions such as copper ions, but is preferably a heavy metal deactivator (D1), an organic chelating agent (D2), and a copper ion-trapping metal compound. At least one selected from the group consisting of (D3) is used. By adding the gettering agent (D) to the adhesive layer, the adhesive layer is provided with a gettering function, and a gettering site is introduced into the semiconductor device.

(D1) Heavy metal deactivator A heavy metal deactivator is an additive blended in a small amount with various plastics in order to prevent the plastic from being deteriorated by a metal such as a catalyst residue. The heavy metal deactivator is considered to capture the metal component to reduce its action and prevent the deterioration of the plastic. As such a heavy metal deactivator, various inorganic or organic deactivators are known. In the present invention, it is preferable to use an organic heavy metal deactivator. The organic heavy metal deactivator is excellent in dispersibility in the adhesive layer.

As such a heavy metal deactivator, a compound having the following structure in a part of the molecule is preferably used.

  In the above formula, R is hydrogen or a hydrocarbon skeleton that may contain a hetero atom, and is particularly preferably a hydrocarbon skeleton containing a nitrogen atom and / or an oxygen atom.

デカメチレンジカルボキシジサリチロイルヒドラジド（ＡＤＥＫＡ社製、ＣＤＡ−６、ＣＡＳ Ｎｏ．６３２４５−３８−５）

Particularly preferred examples of such heavy metal deactivators include the following compounds.
3- (N-salicyloyl) amino-1,2,4-triazole (manufactured by ADEKA, CDA-1, CAS No. 36411-52-6)

Decamethylenedicarboxydisalicyloylhydrazide (ADEKA, CDA-6, CAS No. 63245-38-5)

(D2) Organic Chelating Agent The organic chelating agent (D2) is not particularly limited, but has a polyvalent carboxylic acid as a functional group, and preferably has an acid value of 100 to 600 mg / g, 260 to 330 mg / g. It is more preferable that If the acid value of the organic chelating agent (D2) is smaller than 100 mg / g, the target gettering function is insufficient, and if it is larger than 600 mg / g, it may interact with the base thermosetting agent. is there.

  Moreover, it is preferable that the mass decreasing start temperature by the differential scanning calorimetry (TG / DTA) of an organic chelating agent (D2) is 190 degreeC or more, and 196 degreeC or more is more preferable. When the mass reduction start temperature of the organic chelating agent (D) by differential scanning calorimetry (TG / DTA) is lower than 190 ° C., the IR reflow resistance of the semiconductor package incorporating the semiconductor device may be lowered.

(D3) Copper ion-trapping metal compound
The copper ion capturing metal compound (D3) is a metal compound having an effect of capturing copper ions. Examples thereof include oxides such as antimony, bismuth, magnesium and aluminum, hydroxides, nitrates and carbonates. These are preferable in that the effect can be obtained with a small amount. Examples thereof preferably include antimony oxide, bismuth oxide, and a mixture thereof, and hydrotalcite that is a magnesium-aluminum oxide and a fired product thereof. Al in the hydrotalcite may be substituted with Cr or Fe.

  A gettering agent (D) can be used individually by said 1 type or in mixture of 2 or more types. The blending amount of the gettering agent (D) is preferably 1 to 30 parts by weight, more preferably 10 to 30 parts by weight, particularly preferably 20 with respect to 100 parts by weight of the total solid content constituting the adhesive layer. -30 parts by weight. When the amount of the gettering agent (D) is too small, the target gettering function is insufficient, and when the amount is too large, the adhesion performance may be impaired.

  By incorporating such a gettering agent (D) into the adhesive layer, a gettering site can be introduced into the semiconductor device. For this reason, the impurity metal accumulated in the wafer is captured by the gettering agent (D) in the adhesive layer even if it moves under heating conditions such as reflow, and therefore migrates on the circuit surface. Will never happen.

  The gettering function of the gettering agent (D) can be evaluated by, for example, the following copper ion adsorption ability.

  That is, 1 g of gettering agent was dissolved in 0.81 g of copper chloride (II) dihydrate manufactured by Kanto Chemical Co., Ltd. in 1 liter of ultrapure water, and further diluted 100 times to produce a copper chloride concentration of 3 ppm. The solution was put into 50 g of an aqueous solution, and this aqueous solution was allowed to stand at 121 ° C. and 2 atm for 24 hours. Then, the copper ion concentration (residual copper ion concentration) of the aqueous copper ion solution was measured, and the initial copper ion concentration (3 ppm), From the residual copper ion concentration (ppm), the copper ion adsorption capacity is evaluated by the following formula.

  Copper ion adsorption capacity (%) = (3 ppm−residual copper ion concentration (ppm)) × 100/3 ppm

  The copper ion adsorption capacity indicates the ratio of the amount of copper ions trapped (adsorbed or absorbed) by the gettering agent, and the higher the copper ion adsorption capacity, the higher the gettering function. The copper ion adsorption ability of the gettering agent (D) used in the present invention is preferably 30% or more, more preferably 50% or more, and particularly preferably 95% or more.

  The gettering function can also be evaluated by the amount of copper ions adsorbed per unit weight of the gettering agent (hereinafter referred to as “copper ion adsorption rate”). Specifically, a gettering agent is added to a copper ion aqueous solution in the same manner as described above, and the copper ion adsorption rate is obtained by the following formula.

Copper ion adsorption rate (%) = (3 ppm-residual copper ion concentration (ppm)) × solution amount (g) × 10 ⁻⁶ × 100 / sample weight (g)

  The copper ion adsorption rate of the gettering agent (D) used in the present invention is preferably 0.003% or more, more preferably 0.010% or more, and particularly preferably 0.013% or more.

  In general, the smaller the particle size of the gettering agent (D), the larger the surface area per weight, so that the impurity metal is easily captured and the gettering function is enhanced. In general, the smaller the particle size, the easier the thin adhesive processing. Therefore, the average particle diameter of the gettering agent (D) used in the present invention is preferably in the range of 1 nm to 30 μm, more preferably 5 nm to 10 μm, and particularly preferably 10 nm to 1 μm.

  When the particle size is large in the raw material state, it is pulverized by an appropriate method (ball mill, three rolls, etc.) in advance or when mixed with other components.

  In addition, the average particle diameter of the gettering agent (D) was obtained as an arithmetic average from 100 particles by observation with a scanning electron microscope (SEM). When the particle shape was not spherical, the longest diameter was taken as the particle size.

Other Components The adhesive layer can contain the following components in addition to the above components.

(E) Curing accelerator The curing accelerator (E) is used to adjust the curing rate of the adhesive composition. The curing accelerator (E) is preferably used particularly when the epoxy thermosetting resin (B) and the thermosetting agent (C) are used in combination.

  Preferred curing accelerators include tertiary amines such as triethylenediamine, benzyldimethylamine, triethanolamine, dimethylaminoethanol, tris (dimethylaminomethyl) phenol; 2-methylimidazole, 2-phenylimidazole, 2-phenyl- Imidazoles such as 4-methylimidazole, 2-phenyl-4,5-dihydroxymethylimidazole, 2-phenyl-4-methyl-5-hydroxymethylimidazole; Organic phosphines such as tributylphosphine, diphenylphosphine, triphenylphosphine; And tetraphenylboron salts such as tetraphenylphosphonium tetraphenylborate and triphenylphosphinetetraphenylborate. These can be used individually by 1 type or in mixture of 2 or more types.

  The curing accelerator (E) is preferably 0.01 to 10 parts by weight, more preferably 0.1 to 0.1 parts by weight with respect to a total of 100 parts by weight of the epoxy thermosetting resin (B) and the thermosetting agent (C). It is included in an amount of 1 part by weight. By containing the curing accelerator (E) in an amount within the above range, it has excellent adhesive properties even when exposed to high temperatures and high humidity, and high package reliability even when exposed to severe reflow conditions. Sex can be achieved. If the content of the curing accelerator (E) is small, sufficient adhesive properties cannot be obtained due to insufficient curing, and if it is excessive, the curing accelerator having a high polarity will pass through the adhesive layer under high temperature and high humidity. The reliability of the package is lowered by segregation and segregation.

(F) Energy ray polymerizable compound The energy ray polymerizable compound may be mix | blended with the adhesive bond layer. The energy ray polymerizable compound (F) contains an energy ray polymerizable group and is polymerized and cured when irradiated with energy rays such as ultraviolet rays and electron beams. Specific examples of such energy beam polymerizable compounds (F) include trimethylolpropane triacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, dipentaerythritol monohydroxypentaacrylate, dipentaerythritol hexaacrylate, or 1,4. Examples include acrylate compounds such as butylene glycol diacrylate, 1,6-hexanediol diacrylate, polyethylene glycol diacrylate, oligoester acrylate, urethane acrylate oligomer, epoxy-modified acrylate, polyether acrylate, and itaconic acid oligomer. Such a compound has at least one polymerizable double bond in the molecule, and usually has a weight average molecular weight of about 100 to 30,000, preferably about 300 to 10,000. Although the compounding quantity of an energy-beam polymeric compound (F) is not specifically limited, It is preferable to use in the ratio of about 1-50 weight part with respect to 100 weight part of solid content whole quantity of an adhesive bond layer.

(G) Photopolymerization initiator When the adhesive layer contains the energy ray polymerizable compound (F) described above, the energy ray polymerizable compound is cured by irradiating energy rays such as ultraviolet rays when using the adhesive layer. Let At this time, by including the photopolymerization initiator (G) in the adhesive layer, the polymerization curing time and the light irradiation amount can be reduced.

  Specific examples of such photopolymerization initiator (G) include benzophenone, acetophenone, benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether, benzoin benzoic acid, benzoin methyl benzoate, and benzoin dimethyl ketal. 2,4-diethylthioxanthone, α-hydroxycyclohexyl phenyl ketone, benzyldiphenyl sulfide, tetramethylthiuram monosulfide, azobisisobutyronitrile, benzyl, dibenzyl, diacetyl, 1,2-diphenylmethane, 2-hydroxy- 2-methyl-1- [4- (1-methylvinyl) phenyl] propanone, 2,4,6-trimethylbenzoyldiphenylphosphine oxide and β-alkyl Examples thereof include roll anthraquinone. A photoinitiator (G) can be used individually by 1 type or in combination of 2 or more types.

  The blending ratio of the photopolymerization initiator (G) is preferably 0.1 to 10 parts by weight and more preferably 1 to 5 parts by weight with respect to 100 parts by weight of the energy beam polymerizable compound (F). . If the amount is less than 0.1 parts by weight, a satisfactory pick-up property may not be obtained due to insufficient photopolymerization. If the amount exceeds 10 parts by weight, a residue that does not contribute to photopolymerization is generated, and the curability of the adhesive layer is increased. It may be insufficient.

(H) Coupling agent The coupling agent (H) may be used to improve the adhesion and adhesion of the adhesive layer to the adherend. Moreover, the water resistance can be improved by using a coupling agent (H), without impairing the heat resistance of the hardened | cured material obtained by hardening | curing an adhesive bond layer.

  As the coupling agent (H), a compound having a group that reacts with a functional group of the acrylic polymer (A), the epoxy thermosetting resin (B), or the like is preferably used. As the coupling agent (H), a silane coupling agent is desirable. Such coupling agents include γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropylmethyldiethoxysilane, β- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, γ- (methacryloxypropyl). ) Trimethoxysilane, γ-aminopropyltrimethoxysilane, N-6- (aminoethyl) -γ-aminopropyltrimethoxysilane, N-6- (aminoethyl) -γ-aminopropylmethyldiethoxysilane, N- Phenyl-γ-aminopropyltrimethoxysilane, γ-ureidopropyltriethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-mercaptopropylmethyldimethoxysilane, bis (3-triethoxysilylpropyl) tetrasulfane, methyltrimethoxy Silane, meth Examples include rutriethoxysilane, vinyltrimethoxysilane, vinyltriacetoxysilane, and imidazolesilane. These can be used individually by 1 type or in mixture of 2 or more types.

  The coupling agent (H) is usually 0.1 to 20 parts by weight, preferably 0.2 to 10 parts by weight with respect to 100 parts by weight as a total of the acrylic polymer (A) and the epoxy thermosetting resin (B). Parts, more preferably 0.3 to 5 parts by weight. If the content of the coupling agent (H) is less than 0.1 parts by weight, the above effect may not be obtained, and if it exceeds 20 parts by weight, it may cause outgassing.

(I) Thermoplastic resin Thermoplastic resin (I) may be used for the adhesive layer. Thermoplastic resin (I) is mix | blended in order to maintain the flexibility of the adhesive bond layer after hardening. The thermoplastic resin (I) preferably has a weight average molecular weight of 1,000 to 100,000, more preferably 3,000 to 80,000. By containing the thermoplastic resin (I) in the above range, the delamination between the base material and the adhesive layer in the pick-up process of the semiconductor chip can be easily performed, and the adhesive layer follows the unevenness of the substrate. Generation of voids can be suppressed.

  The glass transition temperature of the thermoplastic resin (I) is preferably -30 to 150 ° C, more preferably -20 to 120 ° C. If the glass transition temperature of the thermoplastic resin (I) is too low, the peeling force between the adhesive layer and the substrate may become large and chip pick-up failure may occur. If it is too high, the adhesive force for fixing the wafer will be low. May be insufficient.

  Examples of the thermoplastic resin (I) include polyester resin, urethane resin, phenoxy resin, polybutene, polybutadiene, and polystyrene. These can be used individually by 1 type or in mixture of 2 or more types.

  The thermoplastic resin (I) is usually 1 to 300 parts by weight, preferably 2 with respect to 100 parts by weight in total of the acrylic polymer (A), the epoxy thermosetting resin (B) and the thermosetting agent (C). It is contained at a ratio of ˜100 parts by weight. When the content of the thermoplastic resin (I) is in this range, the above effect can be obtained.

(J) Inorganic filler By blending the inorganic filler (J) into the adhesive layer, it becomes possible to adjust the thermal expansion coefficient of the adhesive layer, and after curing on a semiconductor chip, metal or organic substrate Package reliability can be improved by optimizing the thermal expansion coefficient of the adhesive layer. Moreover, it becomes possible to reduce the moisture absorption rate after hardening of an adhesive bond layer.

  Preferable inorganic fillers include powders such as silica, talc, calcium carbonate, titanium white, bengara, silicon carbide, boron nitride, spherical beads of these, single crystal fibers, and glass fibers. Among these, silica filler is preferable. The said inorganic filler (J) can be used individually or in mixture of 2 or more types. Content of an inorganic filler (J) can be normally adjusted in the range of 1-80 weight part with respect to 100 weight part of total solids which comprise an adhesive bond layer.

(K) Crosslinking agent A crosslinking agent may be added to adjust the initial adhesive force and cohesive strength of the adhesive layer. Examples of the crosslinking agent (K) include organic polyvalent isocyanate compounds and organic polyvalent imine compounds.

  Examples of the organic polyvalent isocyanate compound include aromatic polyvalent isocyanate compounds, aliphatic polyvalent isocyanate compounds, alicyclic polyvalent isocyanate compounds, trimers of these organic polyvalent isocyanate compounds, and these organic polyvalent isocyanate compounds. And a terminal isocyanate urethane prepolymer obtained by reacting a polyol compound with a polyol compound.

  Examples of organic polyvalent isocyanate compounds include 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 1,3-xylylene diisocyanate, 1,4-xylene diisocyanate, diphenylmethane-4,4′-diisocyanate, diphenylmethane. -2,4'-diisocyanate, 3-methyldiphenylmethane diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, dicyclohexylmethane-4,4'-diisocyanate, dicyclohexylmethane-2,4'-diisocyanate, trimethylolpropane adduct tolylene diisocyanate and lysine Isocyanates.

  Examples of the organic polyvalent imine compound include N, N′-diphenylmethane-4,4′-bis (1-aziridinecarboxamide), trimethylolpropane-tri-β-aziridinylpropionate, tetramethylolmethane-tri -Β-aziridinylpropionate and N, N′-toluene-2,4-bis (1-aziridinecarboxyamide) triethylenemelamine can be exemplified.

  The crosslinking agent (K) is usually 0.01 to 20 parts by weight, preferably 0.1 to 10 parts by weight, more preferably 0.5 to 5 parts by weight, based on 100 parts by weight of the acrylic polymer (A). Used.

(L) General-purpose additive In addition to the above, various additives may be blended in the adhesive layer as necessary. Examples of various additives include plasticizers, antistatic agents, antioxidants, pigments, and dyes.

(Adhesive sheet)
The adhesive layer composed of the above components has pressure-sensitive adhesiveness and heat-curing property, and has a function of temporarily holding various adherends in an uncured state. Finally, a cured product having high impact resistance can be obtained through heat curing, and it has excellent shear strength and can maintain sufficient adhesive properties even under severe high temperature and high humidity conditions.

  In the adhesive sheet of the present invention, the adhesive layer has a concentration gradient of the gettering agent (D) with respect to the thickness direction of the adhesive layer. On the base material, an adhesive layer is laminated so as to be peelable from the base material. In the adhesive layer, the concentration of the gettering agent (D) is low on the substrate surface side, and the concentration of the gettering agent (D) is high on the surface opposite to the substrate surface (surface to be bonded to the wafer). The adhesive layer includes an acrylic polymer (A), an epoxy thermosetting resin (B), a thermosetting agent (C), and a gettering agent (D).

  In the adhesive layer, a method of forming a concentration gradient of the gettering agent with respect to the thickness direction of the adhesive layer is not particularly limited, and examples thereof include the following methods. First, an adhesive composition containing a gettering agent is applied onto a substrate or a release film, which will be described later, and left for a certain period of time, whereby the gettering agent is precipitated in the adhesive layer. Thereafter, by drying, an adhesive layer in which the concentration of the gettering agent has a gradient is obtained. A two-layer die or the like can also be used. First, an adhesive composition containing a gettering agent is applied on a substrate or a release film described later, and an adhesive composition not containing a gettering agent is applied immediately thereafter (before the drying step). By drying after standing for a certain period of time, transfer of the resin or the like occurs between the adhesive compositions, and an adhesive layer in which the concentration of the gettering agent has a gradient is obtained.

  The adhesive sheet which concerns on this invention forms an adhesive bond layer on a base material so that peeling is possible. The shape of the adhesive sheet according to the present invention can be any shape such as a tape shape or a label shape.

  Examples of the base material of the adhesive sheet include polyethylene film, polypropylene film, polybutene film, polybutadiene film, polymethylpentene film, polyvinyl chloride film, vinyl chloride copolymer film, polyethylene terephthalate film, polyethylene naphthalate film, and polybutylene. Terephthalate film, polyurethane film, ethylene vinyl acetate copolymer film, ionomer resin film, ethylene / (meth) acrylic acid copolymer film, ethylene / (meth) acrylic acid ester copolymer film, polystyrene film, polycarbonate film, polyimide A transparent film such as a film or a fluororesin film is used. These crosslinked films are also used. Furthermore, these laminated films may be sufficient. Moreover, the film which colored these, an opaque film, etc. can be used.

  The adhesive sheet according to the present invention is affixed to various adherends, and after subjecting the adherend to required processing, the adhesive layer is peeled off from the substrate while remaining adhered to the adherend. That is, it is used in a process including a step of transferring an adhesive layer from a substrate to an adherend. For this reason, the surface tension of the surface in contact with the adhesive layer of the substrate is preferably 40 mN / m or less, more preferably 37 mN / m or less, and particularly preferably 35 mN / m or less. The lower limit is usually about 25 mN / m. Such a substrate having a low surface tension can be obtained by appropriately selecting the material, and can also be obtained by applying a release agent to the surface of the substrate and performing a release treatment.

  As the release agent used for the substrate release treatment, alkyd, silicone, fluorine, unsaturated polyester, polyolefin, wax, and the like are used. In particular, alkyd, silicone, and fluorine release agents are used. Is preferable because it has heat resistance.

  In order to release the surface of the substrate using the above release agent, the release agent can be applied as it is without solvent, or after solvent dilution or emulsification, using a gravure coater, Mayer bar coater, air knife coater, roll coater, etc. Then, the laminate may be formed by room temperature or heating or electron beam curing, wet lamination, dry lamination, hot melt lamination, melt extrusion lamination, coextrusion processing, or the like.

  The thickness of the substrate is usually about 10 to 500 μm, preferably about 15 to 300 μm, and particularly preferably about 20 to 250 μm. Moreover, the thickness of an adhesive bond layer is 1-500 micrometers normally, Preferably it is 5-300 micrometers, Most preferably, it is about 10-150 micrometers.

  The method for producing the adhesive sheet is not particularly limited, and the adhesive sheet may be produced by applying and drying a composition constituting the adhesive layer on the substrate, and the adhesive layer is provided on the release film. You may manufacture by transferring to the said base material. The adhesive composition for forming the adhesive layer is obtained by mixing the above-mentioned components at an appropriate ratio. In mixing, each component may be diluted with a solvent in advance, or a solvent may be added during mixing.

  In addition, in order to protect an adhesive bond layer before using an adhesive sheet, you may laminate | stack a peeling film on the upper surface (namely, semiconductor wafer sticking plan surface) of an adhesive bond layer. As the release film, one in which a release agent such as a silicone resin is applied to a plastic material such as a polyethylene terephthalate film or a polypropylene film is used. Further, a pressure-sensitive adhesive layer or a pressure-sensitive adhesive tape may be separately provided on the outer peripheral portion of the surface of the adhesive layer in order to fix another jig such as a ring frame.

  Next, a method of using the adhesive sheet according to the present invention will be described taking as an example the case where the adhesive sheet is applied to the manufacture of a semiconductor device.

(Method for manufacturing semiconductor device)
In the method for manufacturing a semiconductor device according to the present invention, a semiconductor wafer is attached to the adhesive layer of the adhesive sheet, the semiconductor wafer is diced into a semiconductor chip, and the adhesive layer is fixedly left on the back surface of the semiconductor chip. And peeling the substrate from the base material and placing the semiconductor chip on the die pad portion of the organic substrate or the lead frame, or on another semiconductor chip when the chips are stacked, through the adhesive layer.

Hereinafter, a method for manufacturing a semiconductor device according to the present invention will be described in detail.
In the method for manufacturing a semiconductor device according to the present invention, first, a semiconductor wafer having a circuit formed on the front surface and a ground back surface is prepared.

  The semiconductor wafer may be a silicon wafer or a compound semiconductor wafer such as gallium / arsenic. Formation of a circuit on the wafer surface can be performed by various methods including conventionally used methods such as an etching method and a lift-off method. Next, the opposite surface (back surface) of the circuit surface of the semiconductor wafer is ground. The grinding method is not particularly limited, and grinding may be performed by a known means using a grinder or the like. At the time of back surface grinding, an adhesive sheet called a surface protection sheet is attached to the circuit surface in order to protect the circuit on the surface. In the back surface grinding, the circuit surface side (that is, the surface protection sheet side) of the wafer is fixed by a chuck table or the like, and the back surface side on which no circuit is formed is ground by a grinder. The thickness of the wafer after grinding is not particularly limited, but is usually about 20 to 500 μm.

  Thereafter, if necessary, the crushed layer generated during back grinding is removed. The crushed layer is removed by chemical etching, plasma etching, or the like. Although the gettering function of the wafer is reduced due to the removal of the crushing layer, an adhesive layer containing a gettering agent is introduced into the obtained semiconductor device by using the adhesive sheet of the present invention. The gettering function is given to the semiconductor device itself. Therefore, the method for manufacturing a semiconductor device of the present invention can be suitably applied particularly to a semiconductor wafer from which a crushed layer has been removed. That is, the method for manufacturing a semiconductor device of the present invention can be suitably applied to a semiconductor wafer in which the thickness of the crushed layer is 50 nm or less, further 30 nm or less, and particularly 10 nm or less.

  Next, the back side of the ring frame and the semiconductor wafer is placed on the adhesive layer of the adhesive sheet according to the present invention, and lightly pressed to fix the semiconductor wafer. At this time, it is preferable to place the gettering agent (D) high concentration side of the adhesive layer in the adhesive sheet in contact with the semiconductor wafer. Next, when the energy ray polymerizable compound (F) is blended in the adhesive layer, the energy ray polymerizable compound (F) is cured by irradiating the adhesive layer with energy rays from the substrate side. The cohesive force of the agent layer is increased, and the adhesive force between the adhesive layer and the substrate is lowered. Examples of the energy rays to be irradiated include ultraviolet rays (UV) and electron beams (EB), and preferably ultraviolet rays are used. Next, the semiconductor wafer is cut using a cutting means such as a dicing saw to obtain a semiconductor chip. The cutting depth at this time is a depth that takes into account the sum of the thickness of the semiconductor wafer and the adhesive layer and the wear of the dicing saw, and the adhesive layer is also cut to the same size as the chip. The energy beam irradiation may be performed at any stage after the semiconductor wafer is pasted and before the semiconductor chip is peeled off (pickup). For example, it may be performed after dicing, or after the following expanding step. Good. Further, the energy beam irradiation may be performed in a plurality of times.

  Then, if necessary, when the adhesive sheet is expanded, the interval between the semiconductor chips is expanded, and the semiconductor chips can be picked up more easily. At this time, a deviation occurs between the adhesive layer and the base material, the adhesive force between the adhesive layer and the base material is reduced, and the pick-up property of the semiconductor chip is improved. When the semiconductor chip is picked up in this manner, the cut adhesive layer can be fixedly left on the back surface of the semiconductor chip and peeled off from the substrate.

  Next, the semiconductor chip is placed on the die pad of the lead frame which is the chip mounting portion or on the surface of another semiconductor chip (lower chip) through the adhesive layer. The chip mounting portion is heated before or after the semiconductor chip is placed. The heating temperature is usually 80 to 200 ° C., preferably 100 to 180 ° C., and the heating time is usually 0.1 seconds to 5 minutes, preferably 0.5 seconds to 3 minutes. The pressure is usually 1 kPa to 200 MPa.

  After placing the semiconductor chip on the chip mounting portion, further heating may be performed as necessary. The heating conditions at this time are in the above heating temperature range, and the heating time is usually 1 to 180 minutes, preferably 10 to 120 minutes.

  Alternatively, the adhesive layer may be cured by using heat in resin sealing that is normally performed in package manufacturing, without temporarily performing the heat treatment after placement. Through such a process, the adhesive layer is cured, and the semiconductor chip and the chip mounting portion can be firmly bonded. Since the adhesive layer is fluidized under die-bonding conditions, the adhesive layer is sufficiently embedded in the unevenness of the chip mounting portion, and generation of voids can be prevented and the reliability of the package is improved.

  The adhesive composition and adhesive sheet of the present invention can be used for bonding semiconductor compounds, glass, ceramics, metals, etc., in addition to the above-described methods of use.

  EXAMPLES Hereinafter, although an Example demonstrates this invention, this invention is not limited to these Examples. In the following examples and comparative examples, <copper ion adsorption ability and copper ion adsorption rate>, <gettering performance>, <wetting and embedding performance>, <surface mountability>, and <shear strength measurement> evaluation Went as follows.

<Copper ion adsorption capacity and copper ion adsorption rate>
Copper ion prepared by dissolving 0.805 g of copper (II) chloride dihydrate manufactured by Kanto Chemical Co., Ltd. in 1 liter of ultrapure water and further diluting 100 times with 1 g of gettering agent prepared in Examples and Comparative Examples The solution was poured into 50 g of a copper chloride aqueous solution having a concentration of 3 ppm and allowed to stand at 121 ° C. under 2 atm for 24 hours. Then, it filtered using the 0.10 micrometer pore diameter membrane filter. The residual copper ion concentration of the aqueous copper ion solution in the filtrate was measured by atomic absorption spectrometry (measuring device: manufactured by Hitachi, Ltd., atomic absorption photometer Z5310, flame method), and the initial copper ion concentration (3 ppm) and residual From the copper ion concentration (ppm), the copper ion adsorption capacity and the copper ion adsorption rate are evaluated by the following formula.

  Copper ion adsorption capacity (%) = (3 ppm−residual copper ion concentration (ppm)) × 100/3 ppm

Copper ion adsorption rate (%) = (3 ppm-residual copper ion concentration (ppm)) × solution amount (g) × 10 ⁻⁶ × 100 / sample weight (g)

<Evaluation of gettering performance>
The back surface of the silicon wafer was dry-polished using a DGP 8760 manufactured by Disco Corporation (200 mm diameter, 75 μm thick, 10 nm thick crush layer). 1 g of copper chloride powder (manufactured by Kanto Chemical Co., Ltd., product name: copper chloride (II) dihydrate) is uniformly sprayed on the dry-polished surface of the silicon wafer (wafer back surface), and simulated reflow conditions (300 C., 30 minutes), and copper ions were diffused into the silicon wafer. Thereafter, a weak adhesive tape (Adwill D-675 manufactured by Lintec after UV curing) was repeatedly applied to and peeled from the back surface of the wafer, and the copper (II) chloride powder was removed from the back surface of the wafer.

The adhesive sheets prepared in Examples and Comparative Examples were attached to the back surface of the silicon wafer contaminated with copper ions at 40 ° C. 30 minutes later, ultraviolet irradiation (230 mW / cm ² , 120 mJ / cm ² ) was performed from the substrate surface using an ultraviolet irradiation device (Adwill RAD-2000 m / 12, manufactured by Lintec Corporation), and the substrate was peeled off. Thereafter, thermosetting (140 ° C., 1 hour) was performed, and then put into pseudo reflow conditions (300 ° C., 30 minutes).

  The wafer surface (mirror surface, adhesive sheet non-adhered surface) was pre-cleaned with hydrofluoric acid to remove contamination and natural oxide film (about 10 nm) adhering to the surface. Thereafter, the wafer outer periphery 10 mm was masked by being sandwiched by a Teflon (registered trademark) jig, and 5 μm from the wafer surface was etched with a nitric acid / hydrofluoric acid mixture (ratio 3: 1). The entire amount of the obtained etching solution was collected in an evaporating dish. After the collected etching solution was heated and evaporated to dryness, the residue was dissolved with a certain amount of nitric acid / hydrofluoric acid mixed solution to prepare a sample for measuring copper ion concentration. Sample preparation was performed in a clean draft (class 10) installed in a clean room (class 100).

The concentration of copper ions in the silicon wafer was quantitatively measured by ICP-MS measurement.
Device: ELAN6100DRC Plus manufactured by PerkinElmer
Conditions: Plasma power 1500W. The lower limit of copper ion quantification is 3.0 × 10 ¹² atoms / cm ³ (number of atoms per unit volume).

The gettering performance of the adhesive sheet was evaluated by measuring the concentration of copper ions eluted in the etching solution. It shows that the smaller the amount of copper ions eluted in the etching solution, the greater the amount of copper ions captured by the adhesive sheet, and the higher the gettering performance. A copper ion detection amount of 50 × 10 ¹² atoms / cm ³ or less was regarded as good, and a copper ion detection amount exceeding 50 × 10 ¹² atoms / cm ³ was regarded as defective.

  In addition, you may perform the quantitative analysis method of copper ion concentration by methods, such as atomic absorption analysis, ICP-OES, and TOF-SIMS.

<Wettability and embedding performance>
(1) Manufacture of test chip Using a tape mounter (Adwill RAD-2500 m / 8, manufactured by Lintec Co., Ltd.) on a circular glass plate (150 mm diameter, 150 μm thick), the temperature of the table for fixing the glass is set to 40 ° C. The adhesive sheets of Examples or Comparative Examples were affixed and simultaneously fixed to the ring frame. Then, ultraviolet rays from the substrate surface using ultraviolet irradiation apparatus (manufactured by LINTEC Corporation Adwill RAD-2000 m / 12) (230mW / cm 2, 120mJ / cm 2) was. Next, dicing was performed to a size of 8 mm × 8 mm using a dicing apparatus (manufactured by Disco Corporation, DFD651) to produce a glass chip having an adhesive layer. About the cutting amount in the case of dicing, it cut | disconnected the base material 20 micrometers. Subsequently, the glass chip having this adhesive layer was picked up from the adhesive sheet side with a needle and picked up.

(2) A circuit pattern is formed on the copper foil of a copper foil-clad laminate (Mitsubishi Gas Chemical Co., Ltd., CCL-HL830) as a test chip mounting board with a maximum unevenness height of 10 μm, and a solder resist with a thickness of 40 μm on the pattern A substrate (manufactured by Chino Giken Co., Ltd.) having (manufactured by Taiyo Ink Manufacturing Co., Ltd., PSR4000 AUS5) was used. A glass chip having the above-mentioned adhesive layer was pressure-bonded onto this substrate under the conditions of 120 ° C., 1 N, and 1 second via the adhesive layer.

(3) Evaluation of wettability and embedding performance Observe with a microscope from the upper surface (glass surface side) of the glass chip adhered to the substrate, and confirm the presence or absence of bubbles present in the adhesive layer located between the substrate and the glass did. The case where the area of bubbles was 30% or less of the total area was judged as “good”, and the case where it exceeded 30% was judged as “bad”.

<Surface mountability evaluation>
(1) Manufacture of semiconductor chip # 2000 Polished silicon wafer (150 mm diameter, 150 μm thickness) using tape mounter (Adwill RAD-2500 m / 8, manufactured by Lintec Corporation), and the temperature of the table for fixing the silicon wafer The adhesive sheet of the example or the comparative example was attached at 40 ° C., and simultaneously fixed to the ring frame. Thereafter, ultraviolet irradiation apparatus (manufactured by LINTEC Corporation, Adwill RAD-2000 m / 12 ) was irradiated with ultraviolet rays from the substrate surface using the ^{(230mW / cm 2, 120mJ /} cm 2). Next, dicing was performed to a size of 8 mm × 8 mm using a dicing apparatus (DFD651, manufactured by Disco Corporation), and a silicon chip having an adhesive layer was produced. About the cutting amount in the case of dicing, it cut | disconnected the base material 20 micrometers. Subsequently, the silicon chip having this adhesive layer was picked up from the adhesive sheet side with a needle and picked up.

(2) As a semiconductor package manufacturing substrate, a circuit pattern is formed on the copper foil of a copper foil-clad laminate (manufactured by Mitsubishi Gas Chemical Co., Ltd., CCL-HL830), and a 40 μm thick solder resist (manufactured by Taiyo Ink Manufacturing Co., Ltd.) is formed on the pattern. , PSR4000 AUS5) (Chino Giken Co., Ltd.) was used. A silicon chip having the above-mentioned adhesive layer is pressure-bonded onto this substrate under the conditions of 120 ° C., 1 N, and 1 second through the adhesive layer, and then heated in an oven at 140 ° C. for 1 hour. The adhesive layer was heat cured. Thereafter, it is sealed with a molding device (manufactured by Kyocera Chemical Co., KE-1100AS3) using a sealing device (manufactured by Apic Yamada Co., MPC-06M Trial Press) so as to have a sealing thickness of 400 μm, and is taken at 175 ° C. for 5 hours. The mold resin was cured. Next, the sealed substrate is attached to a dicing tape (manufactured by Lintec, Adwill D-510T), and reliability evaluation is performed by dicing to 12 mm × 12 mm size using a dicing apparatus (manufactured by Disco, DFD651). The semiconductor package for was obtained.

(3) Evaluation of surface mountability of semiconductor package After the obtained semiconductor package was left to absorb moisture for 168 hours at 85 ° C. and 60% RH, it was subjected to IR reflow conditions at a maximum temperature of 260 ° C. and a heating time of 1 minute. Heating was performed three times (reflow furnace: WL-15-20DNX type, manufactured by Sagami Riko Co., Ltd.). Thereafter, the presence or absence of package cracks was evaluated by cross-sectional observation and a scanning ultrasonic flaw detector (Hy-Focus manufactured by Hitachi Construction Machinery Finetech Co., Ltd.).

  The number of package cracks when 25 packages were put into the test was counted. The case where the package crack did not occur was determined as “good”, and if one of the 25 package cracks occurred, it was determined as “defective”.

<Measurement of shear strength>
(1) Manufacture of test chip A tape mounter (manufactured by Lintec, Adwill RAD-2500 m / 8) is applied to a surface of a silicon wafer having a thickness of 350 μm (hereinafter also referred to as “CMP surface”) that has been subjected to chemical mechanical polishing (CMP). The adhesive sheets prepared in the examples and comparative examples were affixed and simultaneously fixed to the ring frame. Thereafter, ultraviolet irradiation apparatus (manufactured by LINTEC Corporation, Adwill RAD-2000 m / 12 ) was irradiated with ultraviolet rays from the substrate surface using the ^{(230mW / cm 2, 120mJ /} cm 2). Next, the silicon wafer was diced into a size of 5 mm × 5 mm using a dicing apparatus (DFD 651, manufactured by Disco Corporation) to produce a chip having an adhesive layer. About the cutting amount in the case of dicing, it cut | disconnected the base material 20 micrometers.

(2) As a test chip mounting substrate, a circuit pattern is formed on the copper foil of a copper foil-clad laminate (manufactured by Mitsubishi Gas Chemical Company, CCL-HL830), and a 40 μm thick solder resist (manufactured by Taiyo Ink Manufacturing Co., Ltd.) is formed on the pattern. A substrate (manufactured by Chino Giken Co., Ltd.) having PSR4000 AUS5) was used. A silicon chip having the above-mentioned adhesive layer is pressure-bonded onto this substrate under the conditions of 120 ° C., 1 N, and 1 second through the adhesive layer, and then heated in an oven at 140 ° C. for 1 hour. The adhesive layer was heat cured.

(3) Measurement of shear strength Each of the mounted test chips was left for 48 hours under conditions of 85 ° C. and 85% RH, and then IR reflow (reflow oven: Sagami Riko Co., Ltd.) with a maximum temperature of 260 ° C. and a heating time of 1 minute. WL-15-20DNX type), and a test piece was obtained.

  About each test piece, it left on the measurement stage set to 250 degreeC of the bond tester (Dage company make, Bond tester Series 4000) for 30 second, and measured the adhesive strength of the shear direction of a 5 mm x 5 mm size chip | tip. Stress (N) was measured when stress was applied in the shearing direction at a speed of 200 μm / s and the adhesive state between the adhesive layer and the resist surface of the substrate was broken. Moreover, it calculated | required by calculating the average value of 6 samples as a measured value of 1 level. In addition, when measuring the adhesive strength, fracture observation was performed, and “A” was defined as the interface peeling observed from the interface between the adhesive layer and the substrate, and “B” was observed where the cohesive fracture of the adhesive layer was observed. "

（Ｄ１−２）デカメチレンジカルボキシジサリチロイルヒドラジド（ADEKA社製、CDA-6、CAS No.63245-38-5） （銅イオン吸着能９５％、銅イオン吸着率０．０１４％、粒径０．５μｍ）

（Ｄ２）有機キレート剤：多価カルボン酸を官能基として有する有機キレート剤（ナガセケムテックス社製：テークランＤＯ、酸価２６０〜３３０ｍｇ／ｇ、質量減少開始温度２００℃） （銅イオン吸着能９５．７％、銅イオン吸着率０．０１４％、粒径１μｍ）
（Ｄ３）協和化学工業社製KW-2200（マグネシウムとアルミニウムの酸化物からなるハイドロタルサイト） （銅イオン吸着能９９．８％、銅イオン吸着率０．０１５％、粒径１μｍ）
（Ｅ）硬化促進剤：イミダゾール（四国化成工業社製、キュアゾール２ＰＨＺ）
（Ｆ）エネルギー線重合性化合物：多官能アクリレートオリゴマー（新中村化学社製、ＮＫエステルＡ−ＤＣＰ）
（Ｇ）光重合開始剤：１−ヒドロキシ−シクロヘキシル−フェニルケトン（チバ・スペシャリティ・ケミカルズ社製：イルガキュア１８４）
（Ｈ）カップリング剤：シランカップリング剤（信越化学社製：ＫＢＥ−４０３）
（Ｊ）無機充填材：シリカフィラー（アドマテックス社製：アドマファインＳＣ２０５０） <Adhesive composition>
Each component which comprises an adhesive composition is shown below.
(A) Acrylic polymer: copolymer comprising 55 parts by weight of n-butyl acrylate, 10 parts by weight of methyl acrylate, 20 parts by weight of glycidyl methacrylate, and 15 parts by weight of 2-hydroxyethyl acrylate (weight average molecular weight: 900,000, glass (Transition temperature: -28 ° C)
(B) Epoxy thermosetting resin:
(B1) Bisphenol A type epoxy resin (Japan Epoxy Resin Co., Ltd .: jER828, epoxy equivalent 235 g / eq)
(B2) Novolac type epoxy resin (manufactured by Nippon Kayaku Co., Ltd .: EOCN-104S, epoxy equivalent 218 g / eq)
(C) Thermosetting agent: Novolac type phenol resin (manufactured by DIC: TD-2131, phenolic hydroxyl group equivalent 103 g / eq)
(D) Gettering agent:
(D1-1) 3- (N-salicyloyl) amino-1,2,4-triazole (made by ADEKA, CDA-1, CAS No. 36411-52-6) (copper ion adsorption capacity 99.7%, copper (Ion adsorption rate 0.015%, particle size 1μm)

(D1-2) decamethylene dicarboxy disalicyloyl hydrazide (made by ADEKA, CDA-6, CAS No. 63245-38-5) (copper ion adsorption capacity 95%, copper ion adsorption rate 0.014%, grains (Diameter 0.5μm)

(D2) Organic chelating agent: organic chelating agent having a polyvalent carboxylic acid as a functional group (manufactured by Nagase ChemteX Corporation: Teclan DO, acid value of 260 to 330 mg / g, mass reduction starting temperature of 200 ° C.) (copper ion adsorption capacity 95 0.7%, copper ion adsorption rate 0.014%, particle size 1 μm)
(D3) KW-2200 manufactured by Kyowa Chemical Industry Co., Ltd. (hydrotalcite comprising oxides of magnesium and aluminum) (copper ion adsorption capacity 99.8%, copper ion adsorption rate 0.015%, particle size 1 μm)
(E) Curing accelerator: Imidazole (manufactured by Shikoku Kasei Kogyo Co., Ltd., Curesol 2PHZ)
(F) Energy ray polymerizable compound: polyfunctional acrylate oligomer (manufactured by Shin-Nakamura Chemical Co., Ltd., NK ester A-DCP)
(G) Photopolymerization initiator: 1-hydroxy-cyclohexyl-phenylketone (manufactured by Ciba Specialty Chemicals: Irgacure 184)
(H) Coupling agent: Silane coupling agent (Shin-Etsu Chemical Co., Ltd .: KBE-403)
(J) Inorganic filler: Silica filler (manufactured by Admatechs: Admafine SC2050)

(Examples 1-8)
(Adhesive layer)
The above-mentioned respective components were blended in the amounts shown in Table 1 to obtain adhesive layer compositions 1 to 9 containing a gettering agent and an adhesive layer composition 10 not containing a gettering agent. Methyl ethyl ketone solution (solid concentration 61% by weight) of the obtained adhesive layer composition was used, using a two-layer die coater, including a gettering agent composition and a gettering agent from the release-treated surface side The same amount of adhesive layer so as to have a thickness of 20 μm after drying on the release-treated surface of a release film (SP-PET 381031 manufactured by Lintec Co., Ltd.) that has been release-treated with silicone so that there is no composition for adhesive layer The composition for coating was applied and dried (drying conditions: 100 ° C. for 1 minute in an oven), and then bonded to a base material (polyethylene film, thickness 100 μm, surface tension 33 mN / m) to form an adhesive layer as a base material The adhesive sheet was obtained by transferring it to the top. The adhesive layer had a concentration gradient of the gettering agent (D) such that the release film side had a high concentration with respect to the thickness direction of the adhesive layer.

（各実施例で使用した接着剤層用組成物）
実施例１：接着剤層用組成物１・接着剤層用組成物１０
実施例２：接着剤層用組成物２・接着剤層用組成物１０
実施例３：接着剤層用組成物３・接着剤層用組成物１０
実施例４：接着剤層用組成物４・接着剤層用組成物１０
実施例５：接着剤層用組成物５・接着剤層用組成物１０
実施例６：接着剤層用組成物６・接着剤層用組成物１０
実施例７：接着剤層用組成物７・接着剤層用組成物１０
実施例８：接着剤層用組成物８・接着剤層用組成物１０

(Composition for adhesive layer used in each example)
Example 1: Composition 1 for adhesive layer / Composition 10 for adhesive layer
Example 2: Adhesive layer composition 2 Adhesive layer composition 10
Example 3: Adhesive layer composition 3 Adhesive layer composition 10
Example 4: Adhesive layer composition 4 Adhesive layer composition 10
Example 5: Adhesive layer composition 5 Adhesive layer composition 10
Example 6: Adhesive layer composition 6 Adhesive layer composition 10
Example 7: Adhesive layer composition 7 Adhesive layer composition 10
Example 8: Adhesive layer composition 8 Adhesive layer composition 10

  Using the obtained adhesive sheet, <gettering performance>, <wetting and embedding performance>, <surface mountability> and <shear strength measurement> were evaluated. The results are shown in Tables 2 and 3.

(Comparative Example 1)
The same operation as in Example 1 was performed except that the adhesive layer composition 10 was applied to a thickness of 20 μm after drying and an adhesive sheet was obtained without using the gettering agent (D). The results are shown in Tables 2 and 3.

(Comparative Example 2)
The adhesive layer composition 9 was applied to a thickness of 20 μm after drying, and an adhesive sheet was formed using an adhesive layer having no concentration gradient of the gettering agent (D) with respect to the thickness direction of the adhesive layer. The same operation as in Example 1 was carried out except that it was obtained. The results are shown in Tables 2 and 3.

  In addition, the gettering performance of the wafer (Reference Example 1) in which the copper ion-contaminated wafer and the wafer in which the copper ion-contaminated wafer was not attached (Reference Example 2) was measured.

Claims (8)

A base material and an adhesive layer laminated on the base material in a peelable manner,
The adhesive layer includes an acrylic polymer (A), an epoxy thermosetting resin (B), a thermosetting agent (C), and a gettering agent (D),
The adhesive layer has a concentration gradient of the gettering agent (D) in the thickness direction;
An adhesive sheet in which the adhesive layer has a low concentration of the gettering agent (D) on the substrate surface side and a high concentration of the gettering agent (D) on the surface opposite to the substrate surface.   The adhesive sheet according to claim 1, wherein the gettering agent (D) is selected from the group consisting of a heavy metal deactivator (D1), an organic chelating agent (D2), and a copper ion-trapping metal compound (D3). The adhesive sheet according to claim 1 or 2, wherein the gettering agent (D) defined by the following has a copper ion adsorption capacity of 30% or more.
1 g of gettering agent was put into 50 g of a copper chloride aqueous solution having a copper ion concentration of 3 ppm, and the copper ion concentration of the copper ion aqueous solution after being left at 121 ° C. under 2 atm for 24 hours was measured.
Copper ion adsorption capacity = (3 ppm-residual copper ion concentration (ppm)) x 100/3 ppm.   The adhesive sheet according to any one of claims 1 to 3, comprising 1 to 30 parts by weight of a gettering agent (D) per 100 parts by weight of the total solid content constituting the adhesive layer.   The adhesive sheet according to any one of claims 1 to 4, comprising 10 to 30 parts by weight of a gettering agent (D) per 100 parts by weight of the total solid content constituting the adhesive layer. The surface of the adhesive layer opposite to the base material lamination surface is attached to the substrate to be diced,
Surface of the base material side of the adhesive layer, the adhesive according to after peeling the substrate, any one of claims 1 to 5, intended to be bonded to the chip mounting portion for placing the diced adherend Sheet.   A semiconductor wafer is attached to the adhesive layer of the adhesive sheet according to claim 1, the semiconductor wafer is diced into a semiconductor chip, and the adhesive layer is fixedly left on the back surface of the semiconductor chip. A method for manufacturing a semiconductor device, comprising a step of peeling from a base material and placing the semiconductor chip on a die pad part or another semiconductor chip via the adhesive layer.   The method of manufacturing a semiconductor device according to claim 7, wherein the semiconductor wafer is obtained by reducing a crush layer generated by back surface grinding to 50 nm or less after back surface grinding.