JP5487853B2 - Incombustible decorative board - Google Patents

Incombustible decorative board Download PDF

Info

Publication number
JP5487853B2
JP5487853B2 JP2009222295A JP2009222295A JP5487853B2 JP 5487853 B2 JP5487853 B2 JP 5487853B2 JP 2009222295 A JP2009222295 A JP 2009222295A JP 2009222295 A JP2009222295 A JP 2009222295A JP 5487853 B2 JP5487853 B2 JP 5487853B2
Authority
JP
Japan
Prior art keywords
resin
layer
decorative board
nonflammable
aluminum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2009222295A
Other languages
Japanese (ja)
Other versions
JP2011068066A (en
Inventor
裕茂 中川
敏則 木福
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Bakelite Co Ltd
Original Assignee
Sumitomo Bakelite Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Bakelite Co Ltd filed Critical Sumitomo Bakelite Co Ltd
Priority to JP2009222295A priority Critical patent/JP5487853B2/en
Publication of JP2011068066A publication Critical patent/JP2011068066A/en
Application granted granted Critical
Publication of JP5487853B2 publication Critical patent/JP5487853B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、不燃性化粧板に関するものである。     The present invention relates to a non-combustible decorative board.

近年では、様々な箇所で不燃性又は難燃性等の耐熱性を要する材料の設置が要求されるに至っている。このような不燃性又は難燃性等を有する耐熱性材料としては、端的には、金属性材料を挙げることができる。
その中でも、特に、アルミニウムは、比較的軽量で加工も容易であることから、耐熱性に関しては材料として適切であるといえる。しかし、アルミニウムをそのまま使用すると、コストが高騰し、その結果、使用量にも限界が生じる問題があった。
In recent years, installation of materials requiring heat resistance such as incombustibility or flame retardance has been required at various locations. As a heat-resistant material having such incombustibility or flame retardancy, a metallic material can be mentioned as an example.
Among them, in particular, aluminum can be said to be suitable as a material with respect to heat resistance because it is relatively light and easy to process. However, when aluminum is used as it is, the cost increases, and as a result, there is a problem that the amount of use is limited.

このため、アルミニウムの代替材として、熱硬化性樹脂系の化粧板において、メラミン樹脂等に水酸化アルミニウム等の無機充填材を添加して、耐熱性を向上させることも提案されている(例えば、特許文献1、2参照)。
しかし、熱硬化性樹脂中への水酸化アルミニウムの分散混合や、得られた樹脂ワニスを塗布ないしは塗工することが必ずしも容易ではなく、その結果、主に、不織布や紙等の基材に樹脂を含浸させたプリプレグを積層して形成される化粧板として適用するには、高度な生産技術を要していた。
このため、現状では、化粧板として装飾的な外観を有しつつ、同時に充分な耐熱性をも併せ持つ板材は殆ど提供されていないのが実情である。
For this reason, as a substitute material for aluminum, in a thermosetting resin-based decorative board, an inorganic filler such as aluminum hydroxide is added to a melamine resin or the like to improve heat resistance (for example, (See Patent Documents 1 and 2).
However, it is not always easy to disperse and mix aluminum hydroxide in a thermosetting resin or to apply or apply the obtained resin varnish. As a result, the resin is mainly applied to substrates such as nonwoven fabric and paper. In order to apply it as a decorative board formed by laminating prepregs impregnated with bismuth, advanced production techniques are required.
For this reason, the present condition is that the board material which has a decorative external appearance as a decorative board, and also has sufficient heat resistance simultaneously is hardly provided.

加えて、この耐熱性については、2000年に建築基準法が改正され、その第2条第9号に定める不燃材料に該当するための、政令で定める技術的基準に適合するか否かの判断基準となる不燃材料試験が、表面燃焼試験、基材燃焼試験から、コーンカロリーメーター発熱性試験やガス有害性試験に変更され、不燃性材料として使用するためには、発熱量を抑制することが要求されるに至っている。このため、上記のような従来の樹脂系の耐熱性化粧板では、発熱量の抑制が難しく、改正後の建築基準法第2条第9号に定める「不燃材料」の認定を取得することが困難となっている。   In addition, regarding this heat resistance, the Building Standards Act was revised in 2000, and it is judged whether or not it conforms to the technical standards stipulated by the Cabinet Order for falling under the non-combustible material specified in Article 2, Item 9 The standard incombustible material test has been changed from the surface combustion test and the base material combustion test to the corn calorimeter exothermic test and gas hazard test. It has been requested. For this reason, with the conventional resin-based heat-resistant decorative board as described above, it is difficult to suppress the amount of heat generation, and it is possible to obtain the “non-combustible material” certification stipulated in the revised Building Standard Law Article 2-9 It has become difficult.

また、メラミン樹脂化粧板は硬度が高く、かつ、優れた耐水性を有するため、建材や家具用途などの分野で使用されてきたが、硬度が高い反面割れやすい性質を有するため、曲げ加工性が要求される分野においては使われなかった。
近年、意匠性に優れたメラミン樹脂化粧板として加熱曲げ加工が可能なポストフォームタイプの化粧板が開発され、扉等にも使用されてきたが、加熱曲げの加工性は4Rが限界であった。
曲げ加工に際しては、裏面を削る所謂Vカット、Uカット加工を行うことにより曲げ加工性は向上するが、薄くなると脆く割れやすくなるためメラミン樹脂化粧板ではあまり適さない。
一方、アルミニウムなどの金属箔にペンキによる塗装を行った場合では曲げ加工性は良好だが、剛性が不足し傷がつきやすく、また意匠性においても乏しいという問題があった。
In addition, melamine resin decorative board has high hardness and excellent water resistance, so it has been used in fields such as building materials and furniture applications. It was not used in the required fields.
In recent years, post-form decorative panels that can be heated and bent as melamine resin decorative sheets with excellent design have been developed and used for doors, etc., but 4R is the limit for heat bending processability. .
In bending, so-called V-cut and U-cut processing for cutting the back surface improves bending workability. However, when it is thinned, it becomes brittle and easily broken, so it is not suitable for a melamine resin decorative board.
On the other hand, when paint is applied to a metal foil such as aluminum, the bending workability is good, but there is a problem that the rigidity is insufficient and scratches are easily formed, and the design is poor.

特開平1−56539号公報JP-A-1-56539 特開平1−56540号公報JP-A-1-56540

本発明は、樹脂系の素材を使用しつつ、発熱量をも抑制して充分な耐熱性、耐燃性を備え、また、曲げ加工性の良好な不燃性化粧板を提供するものである。   The present invention provides a non-combustible decorative board having sufficient heat resistance and flame resistance by using a resin-based material, suppressing heat generation, and having good bending workability.

このような目的は、下記(1)〜(4)に記載の本発明により達成される。
(1) 表面層材料と不燃性芯材層材料とが積層されてなり、表面層と不燃性芯材層とを有する不燃性化粧板であって、
上記表面層材料は、表面層基材の意匠面である第一の面側にはメラミン樹脂を含有する樹脂が担持され、意匠面と反対側である第二の面側にはウレタンアクリル樹脂を含有する樹脂が担持されてなり、
上記不燃性芯材層材料は、第一のアルミニウム層と、水酸化アルミニウム、水酸化マグネシウム、又は、二酸化珪素とアルミナの混合物から選ばれる無機充填材と熱硬化性樹脂とを含む不燃性コア層材料と、第二のアルミニウム層とがこの順に積層されてなり、
上記表面層材料の第二の面側に上記不燃性芯材層材料が積層されてなることを特徴とする不燃性化粧板。
(2) 上記ウレタンアクリル樹脂は、ウレタンアクリル樹脂のエマルジョンを含有する水性クリヤーである上記(1)に記載の不燃性化粧板。
(3) 上記アルミニウム層は、上記表面層材料に積層される側の表面に、エポキシ樹脂によるプライマー処理が施されているものである上記(1)又は(2)に記載の不燃性化粧板。
(4) 上記アルミニウム層の厚みは、0.1〜0.3mmである上記(1)ないし(3)のいずれかに記載の不燃性化粧板。
Such an object is achieved by the present invention described in the following (1) to (4).
(1) A nonflammable decorative board comprising a surface layer material and a nonflammable core layer material laminated, and having a surface layer and a nonflammable core layer,
In the surface layer material, a resin containing a melamine resin is supported on the first surface side which is the design surface of the surface layer base material, and urethane acrylic resin is applied on the second surface side opposite to the design surface. Resin containing is carried,
The noncombustible core layer material includes a first aluminum layer, an inorganic filler selected from aluminum hydroxide, magnesium hydroxide, or a mixture of silicon dioxide and alumina, and a thermosetting resin. The material and the second aluminum layer are laminated in this order,
A nonflammable decorative board, wherein the nonflammable core material layer material is laminated on the second surface side of the surface layer material.
(2) The non-flammable decorative board according to (1), wherein the urethane acrylic resin is an aqueous clear containing an emulsion of urethane acrylic resin.
(3) The nonflammable decorative board according to (1) or (2), wherein the aluminum layer is subjected to primer treatment with an epoxy resin on the surface laminated on the surface layer material.
(4) The nonflammable decorative board according to any one of (1) to (3), wherein the aluminum layer has a thickness of 0.1 to 0.3 mm.

本発明によれば、樹脂系の素材を使用しつつ、発熱量をも抑制して充分な耐熱性、耐燃性を備え、また、曲げ加工性の良好な不燃性化粧板を提供することができる。   According to the present invention, it is possible to provide a non-combustible decorative board having sufficient heat resistance and flame resistance by using a resin-based material, suppressing heat generation, and having good bending workability. .

本発明の一実施の形態を表す不燃性化粧板の概念図である。It is a conceptual diagram of the nonflammable decorative board showing one embodiment of this invention. 本発明の一実施の形態を表す不燃性化粧板の概念図である。It is a conceptual diagram of the nonflammable decorative board showing one embodiment of this invention.

以下、本発明の不燃性化粧板について詳細に説明する。
図1は、本発明の一実施の形態の不燃性化粧板101を示し、この不燃性化粧板101は、図1に示すように、不燃性芯材層12と、この不燃性芯材層12の表面に積層された表面層14とから成っている。
Hereinafter, the nonflammable decorative board of the present invention will be described in detail.
FIG. 1 shows a nonflammable decorative board 101 according to an embodiment of the present invention. As shown in FIG. 1, the nonflammable decorative board 101 includes a nonflammable core layer 12 and a nonflammable core layer 12. And a surface layer 14 laminated on the surface of the substrate.

表面層14は、図1の実施の形態では、化粧層14Aであり、この化粧層14Aは、不燃性芯材層12の意匠面側に配置される。図1の実施の形態では、不燃性芯材層12の片面に、表面層14である化粧層14Aが積層されているのが示されているが、装飾が必要な意匠面を両面に設定する場合には、図2に示したように、両面側に、化粧層14Aを積層した化粧板102の形態とすることもできる。   In the embodiment of FIG. 1, the surface layer 14 is a decorative layer 14 </ b> A, and the decorative layer 14 </ b> A is disposed on the design surface side of the nonflammable core material layer 12. In the embodiment of FIG. 1, it is shown that a decorative layer 14 </ b> A that is a surface layer 14 is laminated on one side of a nonflammable core material layer 12, but a design surface that requires decoration is set on both sides. In this case, as shown in FIG. 2, the decorative plate 102 may be formed by laminating a decorative layer 14 </ b> A on both sides.

また、図1において、表面層(化粧層)を片面のみに設ける場合には、この表面層とは反対側の面に、更に、図示しない別の芯材層を積層することもできる。
本発明の不燃性化粧板101、102は、表面層14の材料である表面層材料と、不燃性芯材層12の材料である不燃性芯材層材料とを重ね合わせて、これを加熱加圧成形して積層することにより製造することができる。
Moreover, in FIG. 1, when providing a surface layer (decorative layer) only on one side, another core material layer which is not shown in figure can also be laminated | stacked on the surface on the opposite side to this surface layer.
The non-combustible decorative plates 101 and 102 of the present invention are obtained by superposing a surface layer material, which is a material of the surface layer 14, and a non-combustible core material, which is a material of the non-combustible core layer 12, and heating them. It can be manufactured by pressure forming and laminating.

以下に、本発明の不燃性化粧板について詳細に説明する。
本発明の不燃性化粧板は、
表面層材料と不燃性芯材層材料とが積層されてなり、表面層と不燃性芯材層とを有する不燃性化粧板であって、
上記表面層材料は、表面層基材の意匠面である第一の面側にはメラミン樹脂を含有する樹脂が担持され、意匠面と反対側である第二の面側にはウレタンアクリル樹脂を含有する樹脂が担持されてなり、
上記不燃性芯材層材料は、第一のアルミニウム層と、水酸化アルミニウム、水酸化マグネシウム、又は、二酸化珪素とアルミナの混合物から選ばれる無機充填材と熱硬化性樹脂とを含む不燃性コア層材料と、第二のアルミニウム層とがこの順に積層されてなり、
上記表面層材料の第二の面側に前記不燃性芯材層材料が積層されてなることを特徴とする。
Below, the incombustible decorative board of this invention is demonstrated in detail.
The incombustible decorative board of the present invention is
A non-combustible decorative board comprising a surface layer material and a non-combustible core layer material laminated, and having a surface layer and a non-combustible core layer,
In the surface layer material, a resin containing a melamine resin is supported on the first surface side which is the design surface of the surface layer base material, and urethane acrylic resin is applied on the second surface side opposite to the design surface. Resin containing is carried,
The noncombustible core layer material includes a first aluminum layer, an inorganic filler selected from aluminum hydroxide, magnesium hydroxide, or a mixture of silicon dioxide and alumina, and a thermosetting resin. The material and the second aluminum layer are laminated in this order,
The nonflammable core material layer material is laminated on the second surface side of the surface layer material.

<1.表面層材料>
まず、本発明の不燃性化粧板を構成する表面層材料について説明する。
本発明の不燃性化粧板で用いられる表面層材料は、表面層基材の意匠面である第一の面側にはメラミン樹脂を含有する樹脂が担持され、意匠面と反対側である第二の面側にはウレタンアクリル樹脂を含有する樹脂が担持されてなるものである。
<1. Surface layer material>
First, the surface layer material which comprises the nonflammable decorative board of this invention is demonstrated.
The surface layer material used in the non-combustible decorative board of the present invention is a second surface which is opposite to the design surface, with a resin containing a melamine resin supported on the first surface side which is the design surface of the surface layer base material. On the surface side, a resin containing urethane acrylic resin is supported.

上記表面層材料で用いられる表面層基材としては、第一の面側に意匠面が形成されたシート状の基材であり、その材質は特に限定されないが、好ましくは、パルプ、リンター、合成繊維、ガラス繊維などを用いることができ、必要に応じて、酸化チタンなどの顔料を含有する酸化チタン含有化粧紙などを用いることができる。
表面層基材の坪量としては特に限定されないが、坪量40〜150g/mのものを好適に用いることができる。
The surface layer substrate used in the surface layer material is a sheet-like substrate having a design surface formed on the first surface side, and the material is not particularly limited, but is preferably pulp, linter, synthetic Fibers, glass fibers, and the like can be used. If necessary, titanium oxide-containing decorative paper containing a pigment such as titanium oxide can be used.
Although it does not specifically limit as a basic weight of a surface layer base material, A thing with a basic weight of 40-150 g / m < 2 > can be used conveniently.

上記表面層材料は、表面層基材の第一の面側にはメラミン樹脂を含有する樹脂が担持されてなる。これにより、不燃性化粧板表面に好適な表面硬度を付与することができる。
ここで用いられるメラミン樹脂としては、通常、メラミンに対するホルムアルデヒドの反応モル比(ホルムアルデヒド/メラミン:以下、単に反応モル比ということがある)を1.0〜4.0、好ましくは1.0〜2.0として反応させて得られたものを好適に用いることができる。
また、上記メラミン樹脂とともに、ウレタンアクリル樹脂を用いることもできる。これにより、不燃性化粧板の表面硬度を有しながら、曲げ加工性を向上させることができる。
The surface layer material is formed by supporting a resin containing a melamine resin on the first surface side of the surface layer base material. Thereby, suitable surface hardness can be provided to the nonflammable decorative board surface.
As the melamine resin used here, the reaction molar ratio of formaldehyde to melamine (formaldehyde / melamine: hereinafter sometimes simply referred to as reaction molar ratio) is 1.0 to 4.0, preferably 1.0 to 2. Those obtained by reacting as 0.0 can be preferably used.
Moreover, a urethane acrylic resin can also be used with the said melamine resin. Thereby, bending workability can be improved, having the surface hardness of a nonflammable decorative board.

上記表面層材料は、表面層基材の意匠面の反対側である第二の面側には、ウレタンアクリル樹脂を含有する樹脂が担持されてなる。これにより、表面層と、不燃性芯材層で用いられるアルミニウム層との接着強度を向上させることができるとともに、不燃性化粧板の曲げ加工性を向上させることができる。
ここで用いられるウレタンアクリル樹脂を含有する樹脂としては、ウレタンアクリル樹脂のエマルジョンを含有する水性クリヤーであることが好ましい。ウレタン樹脂とアクリル樹脂とは、各々がアルミニウム層との接着強度が高く、また、微粒子状のエマルジョンとすることで微粒子中にウレタンアクリル樹脂が微細な複合樹脂として存在できるため、アルミニウム層との良好な接着強度を発現することができる。そして、水性クリヤータイプ(透明なもの)とすることにより、表面層が有する意匠面の色調に及ぼす影響を抑制することができる。
The surface layer material is formed by carrying a resin containing a urethane acrylic resin on the second surface side opposite to the design surface of the surface layer base material. Thereby, while being able to improve the adhesive strength of a surface layer and the aluminum layer used with a nonflammable core material layer, the bending workability of a nonflammable decorative board can be improved.
The resin containing a urethane acrylic resin used here is preferably an aqueous clear containing an emulsion of a urethane acrylic resin. Urethane resin and acrylic resin each have high adhesive strength with the aluminum layer, and since the urethane acrylic resin can exist as fine composite resin in the fine particles by making fine particle emulsion, it is good with aluminum layer Can exhibit high adhesive strength. And by setting it as an aqueous clear type (transparent thing), the influence which it has on the color tone of the design surface which a surface layer has can be suppressed.

上記表面層材料を製造する方法としては、表面層基材の第一の面側と第二の面側に、上記樹脂をそれぞれ塗工などの手段により担持させることができる。
上記塗工手段としては例えば、スプレー装置、シャワー装置、キスコーター、コンマコーターなどの手法を適用することができ、その後、50〜60℃程度で加熱乾燥して溶剤の大半を除去することにより、本発明の表面層材料を得ることができる。
As a method for producing the surface layer material, the resin can be supported on the first surface side and the second surface side of the surface layer base material by means such as coating.
As the coating means, for example, a spray device, a shower device, a kiss coater, a comma coater, or the like can be applied, and then the main solvent is removed by heating and drying at about 50 to 60 ° C. The surface layer material of the invention can be obtained.

<2.不燃性芯材層材料>
<2.1 アルミニウム層>
次に、本発明の不燃性化粧板を構成する不燃性芯材層材料について説明する。
上記不燃性芯材層材料は、第一のアルミニウム層と、不燃性コア層材料と、第二のアルミニウム層から構成される。
まず、上記第一及び第二のアルミニウム層について説明する。
ここで用いられるアルミニウム層は、アルミニウム箔又はアルミニウム板を適用することができ、不燃性化粧板に、耐熱性、不燃性、剛性などを付与することができる。
<2. Nonflammable Core Material>
<2.1 Aluminum layer>
Next, the noncombustible core material constituting the noncombustible decorative board of the present invention will be described.
The nonflammable core material is composed of a first aluminum layer, a nonflammable core layer material, and a second aluminum layer.
First, the first and second aluminum layers will be described.
An aluminum foil or an aluminum plate can be applied to the aluminum layer used here, and heat resistance, nonflammability, rigidity, and the like can be imparted to the nonflammable decorative board.

このアルミニウム層の厚みとしては、0.1mm以上とすることが好ましい。これにより、不燃性化粧板に充分な耐熱性、不燃性を付与することができる。また、厚みの上限については、特に限定されないが、厚みが大きいほど耐熱性、不燃性は向上するが、メラミン化粧板の厚みと重量が増大すると共に、コストも嵩むため、最終的な製品における設計上、許容される範囲で設定することが好ましく、0.3mm以下にすることが好ましい。   The thickness of the aluminum layer is preferably 0.1 mm or more. Thereby, sufficient heat resistance and nonflammability can be provided to a nonflammable decorative board. The upper limit of the thickness is not particularly limited, but the heat resistance and incombustibility increase as the thickness increases, but the thickness and weight of the decorative melamine board increase and the cost increases, so the design in the final product In addition, it is preferably set within an allowable range, and is preferably set to 0.3 mm or less.

上記アルミニウム層は、上記表面層材料に積層される側の表面に、エポキシ樹脂によるプライマー処理が施されているものであることが好ましい。これにより、表面層材料とアルミニウム層との接着強度をさらに向上させることができる。   The aluminum layer is preferably such that a primer treatment with an epoxy resin is performed on the surface to be laminated on the surface layer material. Thereby, the adhesive strength between the surface layer material and the aluminum layer can be further improved.

<2.2 不燃性コア層材料>
次に、不燃性コア層材料について説明する。
本発明の不燃性化粧板において、不燃性コア層は、水酸化アルミニウム、水酸化マグネシウム、または二酸化珪素とアルミナの混合物から選ばれる無機充填材と熱硬化性樹脂とを含むものである。
具体的には、水酸化アルミニウム、水酸化マグネシウム、または二酸化珪素とアルミナの混合物から選ばれる無機充填材と、メラミン樹脂、フェノール樹脂などの熱硬化性樹脂とを含む配合物を調製し、この配合物を板状に固形化したもの、あるいは、この配合物をガラス繊維不織布に含浸させたシート形状のプリプレグを用いることができる。
<2.2 Nonflammable core layer material>
Next, the nonflammable core layer material will be described.
In the nonflammable decorative board of the present invention, the nonflammable core layer contains an inorganic filler selected from aluminum hydroxide, magnesium hydroxide, or a mixture of silicon dioxide and alumina, and a thermosetting resin.
Specifically, a compound containing an inorganic filler selected from aluminum hydroxide, magnesium hydroxide, or a mixture of silicon dioxide and alumina, and a thermosetting resin such as a melamine resin or a phenol resin is prepared. A product obtained by solidifying a product into a plate shape, or a sheet-shaped prepreg obtained by impregnating a glass fiber nonwoven fabric with this compound can be used.

上記配合物を板状に固形化したものを用いる場合、無機充填材としては二酸化珪素とアルミナの混合物を使用し、熱硬化性樹脂としてはフェノール樹脂を用いることが好ましい。
不燃性コア層をこの形態で用いる場合、上記配合物中における無機充填材と熱硬化性樹脂との配合比率は、両者の合計全体に対して、固形分換算で、二酸化珪素とアルミナの混合物は90〜95重量%、フェノール樹脂は10〜5重量%とすることが好ましい。これにより、不燃性と機械的強度との特性バランスを効果的に発現することができる。
二酸化珪素とアルミナは、平均粒径が10〜30μmのものを好ましく使用することができる。なお、粒子径の大きいものと小さいものを混合使用し、最密充填してもよい。
不燃性コア層としてこの形態のものを用いる場合、形成される不燃性コア層の厚みとしては特に限定されないが、2〜3mmとすることが好ましい。
In the case of using a solidified plate-like composition, it is preferable to use a mixture of silicon dioxide and alumina as the inorganic filler and a phenol resin as the thermosetting resin.
When the nonflammable core layer is used in this form, the blending ratio of the inorganic filler and the thermosetting resin in the blend is calculated in terms of solid content with respect to the total of both, and the mixture of silicon dioxide and alumina is 90 to 95% by weight, and phenol resin is preferably 10 to 5% by weight. Thereby, the characteristic balance of nonflammability and mechanical strength can be expressed effectively.
As silicon dioxide and alumina, those having an average particle diameter of 10 to 30 μm can be preferably used. In addition, you may mix and use what has a large particle diameter and a small thing, and may close-pack.
When using this form as a nonflammable core layer, it is although it does not specifically limit as thickness of the nonflammable core layer formed, It is preferable to set it as 2-3 mm.

また、上記配合物をガラス繊維不織布に含浸させたシート形状のプリプレグに用いる場合、坪量が30〜150g/cmのガラス繊維不織布を使用することが望ましい。坪量が30g/cm未満のガラス繊維不織布では、強度や自己保形性が充分ではないため、基材であるガラス繊維不織布に、無機充填材と熱硬化性樹脂とを含む配合物を塗工する際、また、積層による成形時等における取扱いが困難となる場合がある一方、坪量が150
g/cm超のガラス繊維不織布では、積層による成形時に各層間の密着性が不十分となることがある。
Moreover, when using the said mixture for the sheet-shaped prepreg which impregnated the glass fiber nonwoven fabric, it is desirable to use the glass fiber nonwoven fabric whose basic weight is 30-150 g / cm < 2 >. A glass fiber nonwoven fabric having a basis weight of less than 30 g / cm 2 is insufficient in strength and self-retaining properties. Therefore, a glass fiber nonwoven fabric as a substrate is coated with a compound containing an inorganic filler and a thermosetting resin. When working, it may be difficult to handle at the time of molding by lamination, etc., while the basis weight is 150
When the glass fiber nonwoven fabric exceeds g / cm 2, the adhesion between the layers may be insufficient during molding by lamination.

ガラス繊維不織布に含浸させる場合、無機充填材としては水酸化アルミニウム及び/又は水酸化マグネシウムが、熱硬化性樹脂としてはメラミン樹脂を用いることが好ましい。   When the glass fiber nonwoven fabric is impregnated, it is preferable to use aluminum hydroxide and / or magnesium hydroxide as the inorganic filler and melamine resin as the thermosetting resin.

ガラス繊維不織布に含浸させる場合、水酸化アルミニウム及び/又は水酸化マグネシウムとメラミン樹脂との配合比率は、水酸化アルミニウム及び/又は水酸化マグネシウムとメラミン樹脂との合計(固形分換算)に対して、水酸化アルミニウム及び/又は水酸化マグネシウム90〜70重量%、メラミン樹脂10〜30重量%の割合で配合することが好ましい。
この場合、水酸化アルミニウム及び/又は水酸化マグネシウムの配合率の方を高く設定するのは、充分な不燃性を確保するためであり、メラミン樹脂は、無機充填材の結合剤(バインダ)としての役割を有する。
When impregnating the glass fiber nonwoven fabric, the mixing ratio of aluminum hydroxide and / or magnesium hydroxide and melamine resin is based on the total of aluminum hydroxide and / or magnesium hydroxide and melamine resin (in terms of solid content). It is preferable to mix | blend aluminum hydroxide and / or magnesium hydroxide 90 to 70 weight% and the ratio of melamine resin 10 to 30 weight%.
In this case, the higher mixing ratio of aluminum hydroxide and / or magnesium hydroxide is set to ensure sufficient nonflammability, and melamine resin is used as a binder (binder) for inorganic fillers. Have a role.

これは、メラミン樹脂を上記下限値未満とすると、メラミン樹脂が結合剤としての機能を充分に発揮できず、不燃性コア層材料の取扱い時に結合力不足のために、取扱いが困難となる場合があり、その結果、成形後の不燃性化粧板において層間接着強度が不十分となることがあるからである。また、配合物の粘度上昇やままこ状態になることを防ぐため高価で特殊な混合装置を使用するか、又は溶剤や水により低粘度化する必要があり、さらに塗布工程でも、高い粘度の樹脂液を塗布する技術が必要となるか、あるいは、多量の溶剤や水で低粘度化した場合は、溶剤燃焼による炭酸ガス増加等の環境負荷増大や乾燥するためのエネルギーや工程が多大となるなど生産性の低下やコストの増大となることがある。一方、メラミン樹脂が上記上限値を越えると、不燃性付与効果が低下することがある。   This is because if the melamine resin is less than the above lower limit, the melamine resin cannot sufficiently function as a binder, and it may be difficult to handle due to insufficient binding force when handling the nonflammable core layer material. As a result, the interlaminar bond strength may be insufficient in the non-combustible decorative board after molding. In addition, it is necessary to use an expensive and special mixing device to prevent the composition from increasing in viscosity or remaining in a stagnation state, or it is necessary to reduce the viscosity with a solvent or water. If the technology to apply is applied, or if the viscosity is lowered with a large amount of solvent or water, the production will increase the environmental load such as carbon dioxide increase due to solvent combustion, and the energy and process for drying will increase. May decrease the cost and increase the cost. On the other hand, if the melamine resin exceeds the upper limit, the non-flammability imparting effect may be reduced.

なお、ガラス繊維不織布に含浸させる水酸化アルミニウム及び/又は水酸化マグネシウムとメラミン樹脂との配合に際しては、水酸化アルミニウムや水酸化マグネシウムの他にカーボン等の無機フィラーも添加すると水酸化アルミニウムや水酸化マグネシウムの分散性が向上するため好ましい。また、メラミン樹脂や、水酸化アルミニウム及び/又は水酸化マグネシウムは、本発明の目的、効果を損なわない範囲において、その一部を、他の樹脂や無機充填材に置き換えてもよく、この場合も本発明の範囲に含まれるものである。   In addition, when blending aluminum hydroxide and / or magnesium hydroxide and melamine resin impregnated into the glass fiber nonwoven fabric, addition of an inorganic filler such as carbon in addition to aluminum hydroxide or magnesium hydroxide will result in aluminum hydroxide or hydroxide. This is preferable because the dispersibility of magnesium is improved. In addition, a part of the melamine resin, aluminum hydroxide and / or magnesium hydroxide may be replaced with another resin or an inorganic filler as long as the object and effect of the present invention are not impaired. It is included in the scope of the present invention.

この水酸化アルミニウム及び/又は水酸化マグネシウムとメラミン樹脂とを含む配合物は、そのままの状態、もしくは水、アルコール等の溶剤にて希釈して使用する。
この配合物において、固形分に対する水、アルコール等の溶剤(もともと樹脂に含有されているものも含む)の割合を希釈率とすると、希釈率は、配合物中の樹脂の割合にもよるが、通常0.05〜0.5程度、好ましくは0.1〜0.3程度である。この範囲より小さいと配合物の粘度が高く塗工が行いにくい場合があり、一方、この範囲より大きいと粘度が低くなり塗工された配合物がガラス繊維不織布上に保持されにくいことがある。
The compound containing aluminum hydroxide and / or magnesium hydroxide and melamine resin is used as it is or diluted with a solvent such as water or alcohol.
In this blend, when the ratio of water, alcohol and other solvents (including those originally contained in the resin) is the dilution ratio, the dilution ratio depends on the ratio of the resin in the blend. Usually, it is about 0.05 to 0.5, preferably about 0.1 to 0.3. If it is smaller than this range, the viscosity of the blend may be high and coating may be difficult. On the other hand, if it is larger than this range, the viscosity may be low and the coated blend may be difficult to hold on the glass fiber nonwoven fabric.

必要により希釈された水酸化アルミニウム及び/又は水酸化マグネシウムとメラミン樹脂とを含む配合物をガラス繊維不織布に塗工することにより、基材であるガラス繊維不織布に含浸されて不燃性コア層材料が形成される。この場合、例えば、コンマコーターやダイコーター等の各種の通常のコーター装置により塗工することにより、あるいは、スプレーやノズル等の噴霧装置により吹き付けることにより、無機充填材に剪断力を負荷することなく、基材に含浸させることができる。   The non-combustible core layer material is impregnated into the glass fiber nonwoven fabric as a base material by coating a glass fiber nonwoven fabric with a composition containing aluminum hydroxide and / or magnesium hydroxide and melamine resin diluted as necessary. It is formed. In this case, for example, without applying a shearing force to the inorganic filler by coating with various normal coater devices such as a comma coater or a die coater, or by spraying with a spray device such as a spray or nozzle. The substrate can be impregnated.

この場合、塗工時のガラス繊維不織布に対する水酸化アルミニウム及び/又は水酸化マグネシウムとメラミン樹脂とを含む配合物(固形分)の割合を含浸率とすると、含浸率は、ガラス繊維不織布の坪量にもよるが、重量比で通常5〜100倍程度、好ましくは10
〜60倍程度とする。上記下限値未満では、必要厚さを維持しにくくなり、表面平滑性も充分でないことがあるためである。更に、耐燃性の低下、コスト上昇となる。一方、上記上限値を越えると、耐燃性はよいが、積層前の材料の取扱い時に崩れやすい等の欠点を生じることがある。
In this case, the impregnation ratio is the basis weight of the glass fiber nonwoven fabric when the ratio of the mixture (solid content) containing aluminum hydroxide and / or magnesium hydroxide and melamine resin to the glass fiber nonwoven fabric at the time of coating is defined as the impregnation ratio. Depending on the weight ratio, it is usually about 5 to 100 times, preferably 10 times by weight.
About 60 times. This is because if it is less than the above lower limit value, it becomes difficult to maintain the required thickness, and the surface smoothness may not be sufficient. Furthermore, the flame resistance decreases and the cost increases. On the other hand, when the above upper limit is exceeded, the flame resistance is good, but there may be a drawback that the material tends to collapse during handling of the material before lamination.

なお、熱硬化性樹脂として好適であるメラミン樹脂は、通常メラミンに対するホルムアルデヒドの反応モル比(ホルムアルデヒド/メラミン)が1.0〜4.0のものが使用されるが、必ずしも、この範囲に限定されるものではない。但し、樹脂ワニスとしての保存性等の点からは、1.0〜2.0の範囲とすることが好ましく、また、酸性の硬化剤を適宜配合することができる。   As the melamine resin suitable as a thermosetting resin, one having a reaction molar ratio of formaldehyde to melamine (formaldehyde / melamine) of 1.0 to 4.0 is usually used, but is not necessarily limited to this range. It is not something. However, from the viewpoint of storage stability as a resin varnish, it is preferably in the range of 1.0 to 2.0, and an acidic curing agent can be appropriately blended.

一方、無機充填材としての水酸化アルミニウム及び/又は水酸化マグネシウムも、特に限定はないが、平均粒径が1〜100μmのものを好ましく使用することができる。なお、粒子径の大きいものと小さいものを混合使用し、最密充填してもよい。   On the other hand, aluminum hydroxide and / or magnesium hydroxide as the inorganic filler is not particularly limited, but those having an average particle diameter of 1 to 100 μm can be preferably used. In addition, you may mix and use what has a large particle diameter and a small thing, and may close-pack.

不燃性コア層は、好ましくはこのようにして形成された水酸化アルミニウム及び/又は水酸化マグネシウムとメラミン樹脂とを含む配合物が含浸されたガラス繊維不織布、または、二酸化珪素とアルミナの混合物とフェノール樹脂とを含む配合物を板状に固めたものを、図1又は図2に示すように、一枚あるいは複数枚積層して形成される。
ガラス繊維不織布に含浸させたシート形状のプリプレグを用いた場合は、これを薄く形成することができ、基材である各ガラス繊維不織布に無機充填材と樹脂とを充分に含浸させることが容易となると共に、1枚の厚い基材に含浸させた場合と異なり、無機充填材が内部まで充分に含浸した複数のプリプレグによって、不燃性コア層のほぼ全ての断面において、万遍なく充分に無機充填材を分散させることができるため、不燃性効果を高めることができる。
なお、この不燃性コア層18は、少なくとも、以上に説明した形態のものを有すれば、他に補強層等を備えていてもよい。
The non-combustible core layer is preferably a glass fiber nonwoven fabric impregnated with a composition comprising aluminum hydroxide and / or magnesium hydroxide and melamine resin thus formed, or a mixture of silicon dioxide and alumina and phenol As shown in FIG. 1 or FIG. 2, one or a plurality of laminates obtained by solidifying a compound containing resin are formed.
When a sheet-shaped prepreg impregnated in a glass fiber nonwoven fabric is used, it can be formed thin, and it is easy to sufficiently impregnate each glass fiber nonwoven fabric as a base material with an inorganic filler and a resin. Unlike the case of impregnating a single thick substrate, multiple prepregs that have been sufficiently impregnated with inorganic fillers can be used to uniformly and thoroughly fill almost all cross-sections of the noncombustible core layer. Since the material can be dispersed, the nonflammability effect can be enhanced.
In addition, as long as this nonflammable core layer 18 has the thing of the form demonstrated above, you may be equipped with the reinforcement layer etc. in addition.

<3.不燃性化粧板>
次に、本発明の不燃性化粧板について説明する。
本発明の不燃性化粧板は、以上に説明した表面層材料と不燃性芯材層材料とが積層されてなり、表面層と不燃性芯材層とを有するものである。
この表面層材料は、不燃性芯材層材料の表面に積層され一体化されるが、表面層は不燃性芯材層の両面側に設けることもできる。これにより、不燃性化粧板の反りを抑制することができる。
<3. Noncombustible decorative board>
Next, the nonflammable decorative board of the present invention will be described.
The non-combustible decorative board of the present invention is formed by laminating the above-described surface layer material and non-combustible core layer material, and has a surface layer and a non-combustible core material layer.
The surface layer material is laminated and integrated on the surface of the noncombustible core material, but the surface layer can also be provided on both sides of the noncombustible core material layer. Thereby, the curvature of a nonflammable decorative board can be suppressed.

本発明の不燃性化粧板には、上記の表面層材料と不燃性芯材層材料のほか、坪量10〜50g/mのシート又は紙に、メラミン樹脂単独、又はメラミン樹脂60〜95重量%、水酸化アルミニウム又は水酸化マグネシウム又はシリカ40〜5重量%からなる配合物を含浸したオーバーレイ含浸シート又は含浸紙を、表面層材料の意匠面側に組合せて積層することもできる。このオーバーレイ含浸シート又は含浸紙のメラミン樹脂又は配合物の含浸率は、通常のシート又は紙に対して50〜80重量%である。 In addition to the surface layer material and the non-combustible core material, the non-combustible decorative board of the present invention has a basis weight of 10 to 50 g / m 2 on a sheet or paper, melamine resin alone, or melamine resin 60 to 95 weight. %, Aluminum hydroxide or magnesium hydroxide or silica, and an impregnated impregnated sheet or impregnated paper impregnated with 40 to 5% by weight of silica can be combined and laminated on the design surface side of the surface layer material. The impregnation ratio of the melamine resin or the blend of this overlay impregnated sheet or paper is 50 to 80% by weight with respect to a normal sheet or paper.

以上に説明した表面層材料と不燃性芯材層材料とを各層を重ね合わせて、通常の高圧樹脂化粧板の場合と同様に加熱加圧成形することにより、不燃性化粧板とすることができる。
具体的には、まず、不燃性芯材層材料として、第一のアルミニウム層と、一枚もしくは複数枚の不燃性コア層材料と、第二のアルミニウム層とをこの順に重ね合わせる。
次に、表面層材料を一枚(不燃性化粧板の片面に表面層を設ける場合)もしくは二枚(不燃性化粧板の両面に表面層を設ける場合)用意し、表面層材料の第二の面側と不燃性芯
材層材料とを重ね合わせる。
本発明の不燃性化粧板は、上記の構成を加熱加圧成形して積層することにより製造することができる。
加熱加圧成形時には、用いた熱硬化性樹脂が硬化する程度の温度で加熱しながら、6〜10Mpa程度で加圧することが好ましい。成形時には鏡面仕上げ板、エンボス板またはエンボスフィルム等を重ね合わせることができ、これにより、ミラー仕上げ、エンボス仕上げ等の表面に仕上げることもできる。
The surface layer material and the nonflammable core layer material described above are superposed on each other and heat-press molded in the same manner as in the case of a normal high-pressure resin decorative board, whereby a nonflammable decorative board can be obtained. .
Specifically, first, as a noncombustible core material, a first aluminum layer, one or a plurality of noncombustible core layer materials, and a second aluminum layer are superposed in this order.
Next, prepare one surface layer material (when the surface layer is provided on one side of the non-combustible decorative plate) or two sheets (when the surface layer is provided on both sides of the non-combustible decorative plate), and prepare a second surface layer material. The surface side and the nonflammable core material are overlapped.
The nonflammable decorative board of the present invention can be produced by heating and press-molding and laminating the above configuration.
At the time of heat and pressure molding, it is preferable to pressurize at about 6 to 10 MPa while heating at a temperature at which the used thermosetting resin is cured. At the time of molding, a mirror-finished plate, an embossed plate, an embossed film, or the like can be superposed, whereby a surface such as a mirror finished or embossed finished can be finished.

次に、本発明の不燃性化粧板を実施例により具体的に説明する。   Next, the nonflammable decorative board of the present invention will be specifically described with reference to examples.

<実施例1>
(1)表面層材料の調製
表面層基材として、米坪80g/mの酸化チタン含有化粧紙を用いた。
上記基材の第一の面側(意匠面側)には、メラミン樹脂(反応モル比1.4、樹脂固形分50重量%)と、ウレタンアクリル樹脂エマルジョンを含有する水性クリヤー(中央理化工業社製「SU−100」)を、固形分比率で90:10(メラミン樹脂:ウレタンアクリル樹脂)で混ぜたものを固形分で50g/m塗工した。
上記基材の第二の面側には、ウレタンアクリル樹脂エマルジョンを含有する水性クリヤー(中央理化工業社製「SU−100」)を固形分で40g/m塗工した。
これにより、表面層材料(a1)を得た
(2)芯材層材料の調製
(2.1)アルミニウム層
表面層材料に積層される側の表面をエポキシ樹脂によるプライマー処理を施した厚み0.3mmのアルミニウム箔を用い、アルミニウム層(b1)とした。
(2.2)不燃性コア層材料
坪量75g/m 、比重0.23g/cm 、有機バインダー量11重量%のガラス繊維不織布に、水酸化マグネシウム(平均粒子径10μm)70重量%と、メラミン樹脂(反応モル比1.5、樹脂固形分50重量%)30重量%(固形分換算)とからなる混合物100重量部に対して、水15重量部及びアルコール15重量部を加えた配合物を塗工し、120℃の条件で加熱乾燥して含浸率20倍の不燃性コア層材料(c1)を得た。(3)不燃性化粧板の製造
上記で得られた各材料を用い、これらを(a1)1枚、(b1)1枚、(c1)4枚、(b1)1枚の順に積層し、140℃、8MPaの条件下で20分間加熱加圧成形して、厚さ4.1mmの不燃性化粧板(1)を得た。
<Example 1>
(1) Preparation of surface layer material Titanium oxide-containing decorative paper having a weight of 80 g / m 2 was used as the surface layer base material.
An aqueous clear (Chuo Rika Kogyo Co., Ltd.) containing a melamine resin (reaction molar ratio 1.4, resin solid content 50% by weight) and a urethane acrylic resin emulsion is provided on the first surface side (design surface side) of the substrate. 50 g / m 2 of a solid content obtained by mixing 90% (melamine resin: urethane acrylic resin) in a solid content ratio was manufactured.
On the second surface side of the substrate, an aqueous clear containing a urethane acrylic resin emulsion (“SU-100” manufactured by Chuo Rika Kogyo Co., Ltd.) was applied at a solid content of 40 g / m 2 .
Thus, the surface layer material (a1) was obtained. (2) Preparation of the core material layer material (2.1) Aluminum layer The thickness of the surface laminated on the surface layer material was subjected to primer treatment with epoxy resin. A 3 mm aluminum foil was used to form an aluminum layer (b1).
(2.2) Nonflammable core layer material A glass fiber nonwoven fabric having a basis weight of 75 g / m 2 , a specific gravity of 0.23 g / cm 3 and an organic binder amount of 11% by weight, and magnesium hydroxide (average particle diameter of 10 μm) of 70% by weight And 15 parts by weight of water and 15 parts by weight of alcohol to 100 parts by weight of a mixture of melamine resin (reaction molar ratio 1.5, resin solid content 50% by weight) 30% by weight (solid content conversion) The product was coated and dried by heating at 120 ° C. to obtain a nonflammable core layer material (c1) having an impregnation rate of 20 times. (3) Manufacture of noncombustible decorative board Using each material obtained above, these are laminated in the order of (a1) 1 sheet, (b1) 1 sheet, (c1) 4 sheets, (b1) 1 sheet, 140 A non-combustible decorative board (1) having a thickness of 4.1 mm was obtained by heating and pressing under the conditions of 8 ° C. and 20 ° C. for 20 minutes.

<実施例2>
(1)表面層材料の調製
表面層基材として、米坪80g/mの酸化チタン含有化粧紙を用いた。
上記基材の第一の面側(意匠面側)には、メラミン樹脂(反応モル比1.4、樹脂固形分50重量%)を固形分で50g/m塗工した。
上記基材の第二の面側には、ウレタンアクリル樹脂エマルジョンを含有する水性クリヤー(中央理化工業社製「SU−100」)を固形分で40g/m塗工した。
これにより、表面層材料(a2)を得た
(2)芯材層材料の調製
(2.1)アルミニウム層
表面層材料に積層される側の表面をエポキシ樹脂によるプライマー処理を施した厚み0.1mmのアルミニウム箔を用い、アルミニウム層(b2)とした。
(2.2)不燃性コア層材料
平均粒子径30μmの二酸化珪素と平均粒子径10μmのアルミナの混合物(二酸化珪
素:アルミナ=100:1 重量比率)94重量%とフェノール樹脂6重量%(固形分換算)とからなる混合物を120℃の条件で固め、厚み3mmの不燃性コア層(c2)を得た。
(3)不燃性化粧板の製造
上記で得られた各材料を用い、これらを(a2)1枚、(b2)1枚、(c2)1枚、(b2)1枚の順に積層し、140℃、8MPaの条件下で20分間加熱加圧成形して、厚さ3.9mmの不燃性化粧板(2)を得た。
<Example 2>
(1) Preparation of surface layer material Titanium oxide-containing decorative paper having a weight of 80 g / m 2 was used as the surface layer base material.
On the first surface side (design surface side) of the base material, a melamine resin (reaction molar ratio: 1.4, resin solid content: 50% by weight) was applied at a solid content of 50 g / m 2 .
On the second surface side of the substrate, an aqueous clear containing a urethane acrylic resin emulsion (“SU-100” manufactured by Chuo Rika Kogyo Co., Ltd.) was applied at a solid content of 40 g / m 2 .
Thus, the surface layer material (a2) was obtained. (2) Preparation of the core material layer material (2.1) Aluminum layer The thickness of the surface laminated on the surface layer material was subjected to primer treatment with epoxy resin. A 1 mm aluminum foil was used to form an aluminum layer (b2).
(2.2) Nonflammable Core Layer Material 94% by weight of a mixture of silicon dioxide having an average particle diameter of 30 μm and alumina having an average particle diameter of 10 μm (silicon dioxide: alumina = 100: 1 weight ratio) and 6% by weight of phenol resin (solid content) The mixture consisting of (conversion) was hardened under the condition of 120 ° C. to obtain a nonflammable core layer (c2) having a thickness of 3 mm.
(3) Production of non-combustible decorative board Using the materials obtained above, these are laminated in the order of (a2) 1 sheet, (b2) 1 sheet, (c2) 1 sheet, (b2) 1 sheet, 140 A non-combustible decorative board (2) having a thickness of 3.9 mm was obtained by heating and pressing under the conditions of 8 ° C. and 20 ° C. for 20 minutes.

<比較例1>
(1)表面層材料の調製
表面層基材として、米坪80g/mの酸化チタン含有化粧紙を用いた。
上記基材の第一と第二の面にメラミン樹脂(反応モル比1.4、樹脂固形分50重量%)を固形分で各55g/mずつ、計110g/m塗工し、表面層材料(a3)を得た。
(2)芯材層材料の調製
(2.1)アルミニウム層
表面層材料に積層される側の表面をエポキシ樹脂によるプライマー処理を施した厚み0.1mmのアルミニウム箔を用い、アルミニウム層(b3)とした。
(2.2)不燃性コア層材料
坪量75g/m 、比重0.23g/cm 、有機バインダー量11重量%のガラス繊維不織布に、水酸化アルミニウム(平均粒子径10μm)70重量%と、メラミン樹脂(反応モル比1.5、樹脂固形分50重量%)30重量%(固形分換算)とからなる混合物100重量部に対して、水15重量部及びアルコール15重量部を加えた配合物を塗工し、120℃の条件で加熱乾燥して含浸率20倍の不燃性コア層材料(c3)を得た。(3)接着層材料の調製
米坪146g/mのクラフト紙を用い、これにレゾール型フェノール樹脂を固形分で110g/m塗工して接着層材料(d3)を得た。
(4)不燃性化粧板の製造
上記で得られた各材料を用い、これらを(a3)1枚、(d3)1枚、(b3)1枚、(c3)4枚、(b3)1枚の順に積層し、140℃、8MPaの条件下で20分間加熱加圧成形して、厚さ4.1mmの化粧板(3)を得た。
<Comparative Example 1>
(1) Preparation of surface layer material Titanium oxide-containing decorative paper having a weight of 80 g / m 2 was used as the surface layer base material.
The first and second surfaces of the substrate were coated with 110 g / m 2 of melamine resin (reaction molar ratio of 1.4, resin solid content of 50% by weight) in a solid content of 55 g / m 2 each, A layer material (a3) was obtained.
(2) Preparation of core material layer material (2.1) Aluminum layer An aluminum layer (b3) using a 0.1 mm thick aluminum foil on which the surface to be laminated with the surface layer material has been subjected to primer treatment with an epoxy resin. It was.
(2.2) Nonflammable core layer material A glass fiber nonwoven fabric having a basis weight of 75 g / m 2 , a specific gravity of 0.23 g / cm 3 and an organic binder amount of 11% by weight, and aluminum hydroxide (average particle diameter of 10 μm) of 70% by weight And 15 parts by weight of water and 15 parts by weight of alcohol to 100 parts by weight of a mixture of melamine resin (reaction molar ratio 1.5, resin solid content 50% by weight) 30% by weight (solid content conversion) The product was coated and dried by heating at 120 ° C. to obtain a nonflammable core layer material (c3) having an impregnation rate of 20 times. (3) Preparation of Adhesive Layer Material Using kraft paper having a weight of 146 g / m 2 , 110 g / m 2 of a resol type phenol resin was applied to this in solid content to obtain an adhesive layer material (d3).
(4) Manufacture of noncombustible decorative board Using each of the materials obtained above, (a3) 1 sheet, (d3) 1 sheet, (b3) 1 sheet, (c3) 4 sheet, (b3) 1 sheet Were laminated in this order, followed by heating and pressing under conditions of 140 ° C. and 8 MPa for 20 minutes to obtain a decorative plate (3) having a thickness of 4.1 mm.

<比較例2>
(1)表面層材料の調製
表面層基材として、米坪80g/mの酸化チタン含有化粧紙を用いた。
上記基材の第一と第二の面にメラミン樹脂(反応モル比1.4、樹脂固形分50重量%)を固形分で各55g/mずつ、計110g/m塗工し、表面層材料(a4)を得た。
(2)芯材層材料の調製
(2.1)アルミニウム層
表面層材料に積層される側の表面をエポキシ樹脂によるプライマー処理を施した厚み0.3mmのアルミニウム箔を用い、アルミニウム層(b4)とした。
(2.2)不燃性コア層材料
坪量75g/m 、比重0.23g/cm 、有機バインダー量11重量%のガラス繊維不織布に、水酸化マグネシウム(平均粒子径10μm)70重量%と、メラミン樹脂(反応モル比1.5、樹脂固形分50重量%)30重量%(固形分換算)とからなる混合物100重量部に対して、水15重量部及びアルコール15重量部を加えた配合物を塗工し、120℃の条件で加熱乾燥して含浸率20倍の不燃性コア層材料(c4)を得た。(3)不燃性化粧板の製造
上記で得られた各材料を用い、これらを(a4)1枚、(b4)1枚、(c4)4枚、
(b4)1枚の順に積層し、140℃、8MPaの条件下で20分間加熱加圧成形して、厚さ4.1mmの化粧板(4)を得た。
<Comparative example 2>
(1) Preparation of surface layer material Titanium oxide-containing decorative paper having a weight of 80 g / m 2 was used as the surface layer base material.
The first and second surfaces of the substrate were coated with 110 g / m 2 of melamine resin (reaction molar ratio of 1.4, resin solid content of 50% by weight) in a solid content of 55 g / m 2 each, A layer material (a4) was obtained.
(2) Preparation of core layer material (2.1) Aluminum layer An aluminum layer (b4) using a 0.3 mm thick aluminum foil on which the surface laminated on the surface layer material was subjected to primer treatment with an epoxy resin. It was.
(2.2) Nonflammable core layer material A glass fiber nonwoven fabric having a basis weight of 75 g / m 2 , a specific gravity of 0.23 g / cm 3 and an organic binder amount of 11% by weight, and magnesium hydroxide (average particle diameter of 10 μm) of 70% by weight And 15 parts by weight of water and 15 parts by weight of alcohol to 100 parts by weight of a mixture of melamine resin (reaction molar ratio 1.5, resin solid content 50% by weight) 30% by weight (solid content conversion) The product was coated and dried by heating at 120 ° C. to obtain a nonflammable core layer material (c4) having an impregnation rate of 20 times. (3) Production of non-combustible decorative board Using each of the materials obtained above, (a4) 1 sheet, (b4) 1 sheet, (c4) 4 sheets,
(B4) One sheet was laminated in order, and heat-press molding was performed at 140 ° C. and 8 MPa for 20 minutes to obtain a decorative board (4) having a thickness of 4.1 mm.

以上の実施例で得られた不燃性化粧板(1)、(2)と、比較例で得られた化粧板(3)、(4)について特性を評価した。その結果を表1に示す。   The characteristics of the nonflammable decorative boards (1) and (2) obtained in the above examples and the decorative boards (3) and (4) obtained in the comparative examples were evaluated. The results are shown in Table 1.

Figure 0005487853
Figure 0005487853

(試験方法)
1.不燃性試験
日本建築総合試験場の業務標準「防耐火性能試験・評価業務方法書」4.10 不燃性能試験・評価方法における、(2)ii)4.10.2 の発熱性試験・評価方法、及び
4.10.3 のガス有害性試験・評価方法、により実施した。
上記業務標準「防耐火性能試験・評価業務方法書」の上記項目には、建築基準法第2条第9号(不燃材料)の規定に基づく認定に係わる性能評価方法について記載されている。2.耐煮沸性試験
JIS K6902の耐煮沸性試験に準拠した方法で処理を行い、沸騰水中に2時間浸漬後の試験片の膨れ、層間はく離の有無を確認した。
3.曲げ成形性試験
各サンプルの表面層と反対側の面を予めUカットにて加工し、最も薄いところで0.5mmとなる様にした。曲げ成形性試験は該サンプルを用いて行った。
JIS K6902の曲げ成形性試験(A法)に準拠し、156℃、3Rにて外曲げ成形を行い、表面層の意匠面の割れの有無を確認した。
4.鉛筆硬度試験
JIS K5600に準拠して評価を行った。
(Test method)
1. Non-combustibility test Operation standard "Fireproof and fireproof performance test / evaluation method" 4.10 Non-combustibility test / evaluation method in (2) ii) 4.10.2 exothermic test / evaluation method, And 4.13 Gas Hazardous Test / Evaluation Method.
The item of the above-mentioned business standard “Fireproofing Performance Test / Evaluation Business Method” describes the performance evaluation method related to the certification based on the provisions of Article 2, Item 9 (non-combustible material) of the Building Standard Law. 2. Boiling resistance test The treatment was carried out by a method based on the boiling resistance test of JIS K6902, and the presence or absence of delamination and delamination of the test piece after being immersed in boiling water for 2 hours was confirmed.
3. Bend formability test The surface opposite to the surface layer of each sample was processed in advance with a U-cut so that the thickness was 0.5 mm at the thinnest point. The bending formability test was performed using the sample.
Based on the bending formability test (Method A) of JIS K6902, external bending was performed at 156 ° C. and 3R, and the presence or absence of cracks in the design surface of the surface layer was confirmed.
4). Pencil hardness test Evaluation was performed in accordance with JIS K5600.

上記表1に示す結果から明らかなように、実施例1、2で得られた化粧板(1)(2)は、不燃性が基準等に適合し、曲げ成形性も良好であった。
これに対して、比較例1で得られた化粧板(3)は、不燃性は良好だが曲げ加工性が低下した。
また、比較例2で得られた化粧板(4)は、不燃性は良好だが、耐煮沸性、曲げ加工性が低下した。
As is clear from the results shown in Table 1 above, the decorative plates (1) and (2) obtained in Examples 1 and 2 had nonflammability conforming to the standards and the like, and had good bend formability.
On the other hand, the decorative board (3) obtained in Comparative Example 1 had good nonflammability but decreased bending workability.
In addition, the decorative board (4) obtained in Comparative Example 2 has good nonflammability, but has low boiling resistance and bending workability.

本発明の不燃性化粧板は、良好な曲げ加工性、不燃性、層間接着力を有したものである。
そして、表面層(化粧層)には、従来の化粧板と同様の表面層基材が使用できるため、豊富な色柄から自由に選択でき、且つ、公共施設等における不燃性を有する材料の規制を受ける壁等の用途に広く適用することができるものである。
The nonflammable decorative board of the present invention has good bending workability, nonflammability, and interlayer adhesion.
And since the surface layer base material similar to the conventional decorative board can be used for the surface layer (decorative layer), it is possible to freely select from abundant color patterns and to regulate nonflammable materials in public facilities etc. It can be widely applied to applications such as receiving walls.

101 化粧板
102 化粧板
12 不燃性芯材層
14 表面層
14A 化粧層
16 アルミニウム層
18 不燃性コア層
DESCRIPTION OF SYMBOLS 101 Decorative board 102 Decorative board 12 Non-combustible core layer 14 Surface layer 14A Decorative layer 16 Aluminum layer 18 Non-combustible core layer

Claims (4)

表面層材料と不燃性芯材層材料とが積層されてなり、表面層と不燃性芯材層とを有する不燃性化粧板であって、
前記表面層材料は、表面層基材の意匠面である第一の面側にはメラミン樹脂を含有する樹脂が担持され、意匠面と反対側である第二の面側にはウレタンアクリル樹脂を含有する樹脂が担持されてなり、
前記不燃性芯材層材料は、第一のアルミニウム層と、水酸化アルミニウム、水酸化マグネシウム、又は、二酸化珪素とアルミナの混合物から選ばれる無機充填材と熱硬化性樹脂とを含む不燃性コア層材料と、第二のアルミニウム層とがこの順に積層されてなり、
前記表面層材料の第二の面側に前記不燃性芯材層材料が積層されてなることを特徴とする不燃性化粧板。
A non-combustible decorative board comprising a surface layer material and a non-combustible core layer material laminated, and having a surface layer and a non-combustible core layer,
In the surface layer material, a resin containing a melamine resin is supported on the first surface side which is the design surface of the surface layer base material, and urethane acrylic resin is applied on the second surface side opposite to the design surface. Resin containing is carried,
The non-combustible core layer material includes a first aluminum layer, an inorganic filler selected from aluminum hydroxide, magnesium hydroxide, or a mixture of silicon dioxide and alumina, and a thermosetting resin. The material and the second aluminum layer are laminated in this order,
A nonflammable decorative board, wherein the nonflammable core material layer material is laminated on the second surface side of the surface layer material.
前記ウレタンアクリル樹脂は、ウレタンアクリル樹脂のエマルジョンを含有する水性クリヤーである請求項1に記載の不燃性化粧板。   The nonflammable decorative board according to claim 1, wherein the urethane acrylic resin is an aqueous clear containing an emulsion of urethane acrylic resin. 前記アルミニウム層は、前記表面層材料に積層される側の表面に、エポキシ樹脂によるプライマー処理が施されているものである請求項1又は2に記載の不燃性化粧板。   The nonflammable decorative board according to claim 1 or 2, wherein the aluminum layer is subjected to primer treatment with an epoxy resin on a surface on which the aluminum layer is laminated. 前記アルミニウム層の厚みは、0.1〜0.3mmである請求項1ないし3のいずれかに記載の不燃性化粧板。   The nonflammable decorative board according to any one of claims 1 to 3, wherein the aluminum layer has a thickness of 0.1 to 0.3 mm.
JP2009222295A 2009-09-28 2009-09-28 Incombustible decorative board Expired - Fee Related JP5487853B2 (en)