JP5278628B1 - 金属面貼付用粘着シート - Google Patents
金属面貼付用粘着シート Download PDFInfo
- Publication number
- JP5278628B1 JP5278628B1 JP2012554546A JP2012554546A JP5278628B1 JP 5278628 B1 JP5278628 B1 JP 5278628B1 JP 2012554546 A JP2012554546 A JP 2012554546A JP 2012554546 A JP2012554546 A JP 2012554546A JP 5278628 B1 JP5278628 B1 JP 5278628B1
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- mass
- adhesive sheet
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
本発明の(メタ)アクリル酸エステル共重合体を構成する(メタ)アクリル酸アルコキシアルキルエステル単量体(A)としては、具体的には、アクリル酸2−メトキシエチル、アクリル酸2−エトキシエチル、アクリル酸2メトキシトリエチレングリコール、アクリル酸3−メトキシプロピル、アクリル酸3−エトキシプロピル、アクリル酸4−メトキシブチル、アクリル酸4−エトキシブチルなどが挙げられる。その中でも、特に、アクリル酸2−メトキシエチル、アクリル酸2−エトキシエチルが好ましい。上記単量体を使用することで、粘着剤層に金属膜を固定するために必要な凝集力を付与できる。
(GPCの測定条件)
・サンプル濃度:0.5質量%(テトラヒドロフラン溶液)
・サンプル注入量:100μL
・溶離液:テトラヒドロフラン(THF)
・流速:1.0mL/min
・カラム温度(測定温度):40℃
・カラム:東ソー株式会社製「TSKgel GMHHR−H」
・検出器:示差屈折
本発明の金属面貼付用粘着シートの粘着剤層を形成する粘着剤組成物は、上記(メタ)アクリル酸エステル共重合体を含有する粘着剤組成物であり、当該組成物中には、上記共重合体以外の成分として、粘着剤層の凝集力を上げるために、架橋剤を含有することが好ましい。
本発明の金属面貼付用粘着シートは、粘着剤層として、上記粘着剤組成物からなる粘着剤層を有することで、高温高湿条件下での粘着剤層の白濁と金属の腐食を抑制できる。
ゲル分率(質量%)=[(粘着剤層のトルエン浸漬後質量)/(粘着剤層のトルエン浸漬前質量)]×100
本発明の金属面貼付用粘着シートは、金属面を腐食させず、良好な耐白化性を有することから、ガラスやフィルムの表面に酸化インジウムスズ(ITO)が設けられたITOガラスやITOフィルム、あるいは、ガラスやフィルムの表面に銀や銅の配線が設けられた金属配線フィルム等の金属面表面を有する部材を固定する際に好適に使用できる。中でも、高い透明性が求められ、かつ、安定した導電性が求められる金属面表面を有する部材の固定に好適に使用できる。また、本発明の金属面貼付用粘着シートは、良好な段差追従性を実現できることから、固定する部材が表面凹凸形状を有する部材、例えば印刷段差が設けられた部材であっても好適に適用できる。
<アクリル共重合体(1)>
アクリル共重合体の調製攪拌機、寒流冷却器、温度計、滴下漏斗及び窒素ガス導入口を備えた反応容器に、アクリル酸2−メトキシエチル75質量%、アクリル酸n−ブチル24質量%、アクリル酸ヒドロキシエチル1質量%と重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100質量%に溶解し、窒素置換後、80℃で8時間重合して重量平均分子量70万のアクリル酸エステル共重合体(1)を得た。
アクリル酸2−メトキシエチルを85質量%、アクリル酸n−ブチルを14質量%とする以外は、アクリル酸エステル共重合体(1)と同様にして、重量平均分子量70万のアクリル酸エステル共重合体(2)を得た。
アクリル共重合体の調製攪拌機、寒流冷却器、温度計、滴下漏斗及び窒素ガス導入口を備えた反応容器に、アクリル酸2−メトキシエチル70質量%、アクリル酸2エチルヘキシル29質量%、アクリル酸ヒドロキシエチル1質量%と重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100質量%に溶解し、窒素置換後、80℃で8時間重合して重量平均分子量100万のアクリル酸エステル共重合体(3)を得た。
アクリル酸2−メトキシエチルを50質量%、アクリル酸n−ブチルを49質量%とする以外は、アクリル酸エステル共重合体(1)と同様にして、重量平均分子量100万のアクリル酸エステル共重合体(4)を得た。
アクリル共重合体の調製攪拌機、寒流冷却器、温度計、滴下漏斗及び窒素ガス導入口を備えた反応容器にアクリル酸n−ブチル80質量%、メタクリル酸メチル19質量%、アクリル酸ヒドロキシエチル1質量%と重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100質量%に溶解し、窒素置換後、80℃で8時間重合して重量平均分子量80万のアクリル酸エステル共重合体(5)を得た。
アクリル共重合体の調製攪拌機、寒流冷却器、温度計、滴下漏斗及び窒素ガス導入口を備えた反応容器にアクリル酸n−ブチル80質量%、アクリル酸19質量%、アクリル酸ヒドロキシエチル1質量%と重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100質量%に溶解し、窒素置換後、80℃で8時間重合して重量平均分子量70万のアクリル酸エステル共重合体(6)を得た。
アクリル共重合体の調製攪拌機、寒流冷却器、温度計、滴下漏斗及び窒素ガス導入口を備えた反応容器に、アクリル酸2−メトキシエチル75質量%、アクリル酸n−ブチル16質量%、メタクリル酸メチル8質量%、アクリル酸ヒドロキシエチル1質量%と重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100質量%に溶解し、窒素置換後、80℃で8時間重合して重量平均分子量70万のアクリル酸エステル共重合体(7)を得た。
アクリル共重合体の調製攪拌機、寒流冷却器、温度計、滴下漏斗及び窒素ガス導入口を備えた反応容器に、アクリル酸2−メトキシエチル75質量%、アクリル酸n−ブチル24質量、アクリル酸4−ヒドロキシブチル1質量%と重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100質量%に溶解し、窒素置換後、80℃で8時間重合して重量平均分子量70万のアクリル酸エステル共重合体(8)を得た。
アクリル酸n−ブチルを22質量%、アクリル酸ヒドロキシエチル3質量%とする以外は、アクリル酸エステル共重合体(1)と同様にして、重量平均分子量70万のアクリル酸エステル共重合体(9)を得た。
アクリル共重合体の調製攪拌機、寒流冷却器、温度計、滴下漏斗及び窒素ガス導入口を備えた反応容器に、アクリル酸2−メトキシエチル40質量%、アクリル酸n−ブチル24質量%、アクリル酸2エチルヘキシル35質量%、アクリル酸ヒドロキシエチル1質量%と重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100質量%に溶解し、窒素置換後、80℃で8時間重合して重量平均分子量70万のアクリル酸エステル共重合体(10)を得た。
アクリル共重合体の調製攪拌機、寒流冷却器、温度計、滴下漏斗及び窒素ガス導入口を備えた反応容器に、アクリル酸2−メトキシエチル70質量%、アクリル酸n−ブチル24質量%、アクリル酸ヒドロキシエチル1質量%、アクリル酸5質量%と重合開始剤として2,2’−アゾビスイソブチルニトリル0.2部とを酢酸エチル100質量%に溶解し、窒素置換後、80℃で8時間重合して重量平均分子量70万のアクリル酸エステル共重合体(11)を得た。
上記アクリル酸エステル共重合体(1)を酢酸エチルで希釈し、樹脂固形分30質量%の粘着剤組成物(a)を得た。
上記アクリル酸エステル共重合体(2)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(b)を得た。
上記アクリル酸エステル共重合体(3)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(c)を得た。
上記アクリル酸エステル共重合体(4)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤(d)を得た。
上記アクリル酸エステル共重合体(5)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(e)を得た。
上記アクリル酸エステル共重合体(6)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(f)を得た。
上記アクリル酸エステル共重合体(7)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(g)を得た。
上記アクリル酸エステル共重合体(8)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(h)を得た。
上記アクリル酸エステル共重合体(9)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(i)を得た。
上記アクリル酸エステル共重合体(10)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(j)を得た。
上記アクリル酸エステル共重合体(11)を酢酸エチルで希釈し樹脂固形分30質量%の粘着剤組成物(k)を得た。
上記粘着剤組成物(a)100質量部にイソシアネート系架橋剤(日本ポリウレタン社製コロネートHX、固形分75%)を0.1質量部添加し15分攪拌後、シリコーン化合物で片面を剥離処理した厚さ50μmのポリエステルフィルム(以下#75剥離フィルム)上に乾燥後の厚さが50μmになるように塗工して、75℃で5分間乾燥した。得られた粘着シートと、シリコーン化合物で片面を剥離処理した厚さ38μmのポリエステルフィルム(以下#38剥離フィルム)を貼り合わせた。その後23℃で7日間熟成し厚さ50μmの、ゲル分率50%の基材レス粘着シートを得た。
イソシアネート系架橋剤を0.08質量部にする以外は、実施例1と同様にして、ゲル分率40%の粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(b)100質量部にする以外は、実施例1と同様にして、ゲル分率50%の粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(b)100質量部、イソシアネート系架橋剤を0.08質量部にする以外は、実施例1と同様にして、ゲル分率40%の粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(g)100質量部にする以外は、実施例1と同様にして、ゲル分率50%の粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(h)100質量部にする以外は、実施例1と同様にして、ゲル分率50%の粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(i)100質量部にする以外は、実施例1と同様にして、ゲル分率55%の粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(c)100質量部にする以外は、実施例1と同様にして、ゲル分率60%の粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(d)100質量部にする以外は、実施例1と同様にして、ゲル分率60%の粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(e)100質量部にする以外は、実施例1と同様にして、ゲル分率60%の粘着シートを得た。
上記粘着剤組成物(f)100質量部にイソシアネート系架橋剤(日本ポリウレタン社製コロネートL−45、固形分45%)を0.1質量部添加し15分攪拌後、シリコーン化合物で片面を剥離処理した厚さ50μmのポリエステルフィルム(以下#75剥離フィルム)上に乾燥後の厚さが50μmになるように塗工して、75℃で5分間乾燥した。得られた粘着シートと、シリコーン化合物で片面を剥離処理した厚さ38μmのポリエステルフィルム(以下#38剥離フィルム)を貼り合わせた。その後23℃で7日間熟成し厚さ50μmの、ゲル分率70%の基材レス粘着シートを得た。
粘着剤組成物(a)100質量部を粘着剤組成物(j)100質量部、イソシアネート系架橋剤を0.3質量部にする以外は、実施例1と同様にして、ゲル分率80%の粘着シートを得た。
粘着剤組成物(f)100質量部を粘着剤組成物(k)100質量部、イソシアネート系架橋剤を0.12質量部にする以外は、比較例4と同様にして、ゲル分率80%の粘着シートを得た。
粘着シートをポリエチレンテレフタレートフィルム、ガラスの順で貼り合わせて調整した試験サンプルを、60℃90%RH条件下に250時間放置し、試験サンプルを上記条件下から取り出した直後のヘイズを、(株)村上色彩技術研究所製「HR−100型」を使用し、測定した。
○:ヘイズ1.0%以下
△:ヘイズ1.0%〜3.0%
×:ヘイズ3.0%以上
粘着シートの片面にポリエチレンテレフタレートフィルム(100μm)に貼り合せた後、50mm×50mmに裁断して、100mm×100mmの酸化インジウムスズ蒸着ポリエチレンテレフタレートフィルムの酸化インジウムスズ膜面に貼り合わせを行う。貼り合せた粘着シートの両端に電気抵抗値測定機 三菱化学(株)製「ロレスターGP」を使用し、初期の電気抵抗値(R1)を測定。粘着シートを貼り合わせた酸化インジウムスズ蒸着ポリエチレンテレフタレートフィルムを60℃、90%RH条件下に250時間放置し、23℃、50%RH条件下に1時間放置した後、初期と同じ箇所での電気抵抗値(R2)を測定した。酸化インジウムスズ(ITO)膜の電気抵抗値変化率は下記の式で算出した。
ITO膜の電気抵抗値変化率(%)=((R2−R1)/R1)×100
○:電気抵抗値変化率90〜110%
×:電気抵抗値変化率90%未満もしくは110%以上
作成した粘着シートの片側の剥離フィルムを剥がし、厚み15μm、幅5mmの印刷層が額縁状に装飾された厚み100μm、長さ50mm、幅40mmのポリエチレンテレフタレートフィルムに貼り合わせた。得られた試験片の残る片側の剥離フィルムを剥がし、厚み1mm、長さ50mm、幅40mmガラス板に貼り合わせ、5気圧、70℃、20分の条件で加熱加圧処理を行った。加熱加圧処理後に23℃下に1日放置し、印刷した装飾部近傍全体をマイクロスコープ(倍率300倍)で観察し、気泡の混入等があるか確認した。気泡混入の評価基準は、以下の通りとした。
○:直径5μm以上の気泡なし
△:直径30μm以上の気泡なし
×:直径30μm以上の気泡あり又は剥がれ
MEA:アクリル酸メトキシエチル
BA:アクリル酸ブチル
2EHA:アクリル酸2エチルへキシル
HEA:アクリル酸ヒドロキシエチル
MA:メタクリル酸メチル
AA:アクリル酸
得られた粘着シートの残る片側の剥離フィルムを剥がし、印刷層が額縁状に装飾された厚み1mm、長さ50mm、幅40mmガラス板に貼り合わせ、5気圧、70℃、20分の条件で加熱加圧処理を行った。加熱加圧処理直後に、印刷した装飾部近傍全体をマイクロスコープ(倍率300倍)で観察し、気泡の混入等があるか確認した。気泡混入の評価基準は、以下の通りとした。
○:直径5μm以上の気泡なし
△:直径30μm以上の気泡なし
×:直径30μm以上の気泡あり又は剥がれ
2,12,22 表面保護パネル
3,13,23 印刷段差
4,4’ ITOフィルム
4a,4a’ 透明樹脂フィルム
4b,4b’ ITO
5,17,27 筐体
6,18,28 画像表示モジュール
7,19,29 接着部材
14 ITO
15,25 粘着剤層
16,26 ハードコートフィルム
24 ITOガラス
25a 透明ガラス
25b,25c ITO
Claims (4)
- 金属面に貼り合わせる粘着シートであって、
前記粘着シートが、(メタ)アクリル酸エステル共重合体を使用したアクリル系粘着剤からなる粘着剤層を有し、
前記(メタ)アクリル酸エステル共重合体が、(メタ)アクリル酸アルコキシアルキルエステル単量体(A)及び炭素数が1〜4のアルキル基を有する(メタ)アクリル酸アルキルエステル(B)を単量体成分として含有し、
(メタ)アクリル酸エステル共重合体を構成する単量体成分中の前記(メタ)アクリル酸アルコキシアルキルエステル単量体(A)の含有量が50質量%以上、前記炭素原子数が1〜4のアルキル基を有する(メタ)アクリル酸アルキルエステル(B)の含有量が5〜45質量%であり、
(メタ)アクリル酸エステル共重合体を構成する単量体成分中のカルボキシル基含有単量体の含有量が1%以下であり、
前記(メタ)アクリル酸エステル共重合体の重量平均分子量が、40万〜160万であることを特徴とする金属面貼付用粘着シート。 - 前記炭素原子数が1〜4のアルキル基を有する(メタ)アクリル酸アルキルエステル(B)が、アクリル酸n−ブチルである請求項1に記載の金属面貼付用粘着シート。
- 前記粘着剤層のみからなる粘着シートである請求項1又は2に記載の金属面貼付用粘着シート。
- 前記粘着剤層が、トルエン中に24時間浸漬した際の下記式で表されるゲル分率が30〜80質量%である請求項1〜3のいずれかに記載の金属面貼付用粘着シート。
ゲル分率(質量%)=[(粘着剤層のトルエン浸漬後質量)/(粘着剤層のトルエン浸漬前質量)]×100