JP5241997B2 - Conductive polymer solution and conductive coating film - Google Patents

Conductive polymer solution and conductive coating film Download PDF

Info

Publication number
JP5241997B2
JP5241997B2 JP2005063687A JP2005063687A JP5241997B2 JP 5241997 B2 JP5241997 B2 JP 5241997B2 JP 2005063687 A JP2005063687 A JP 2005063687A JP 2005063687 A JP2005063687 A JP 2005063687A JP 5241997 B2 JP5241997 B2 JP 5241997B2
Authority
JP
Japan
Prior art keywords
acid
group
poly
conductive polymer
sulfonic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2005063687A
Other languages
Japanese (ja)
Other versions
JP2006249128A (en
Inventor
一義 吉田
太陸 寧
利香 阿部
泰 樋口
泰 政広
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shin Etsu Polymer Co Ltd
Original Assignee
Shin Etsu Polymer Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shin Etsu Polymer Co Ltd filed Critical Shin Etsu Polymer Co Ltd
Priority to JP2005063687A priority Critical patent/JP5241997B2/en
Priority to TW95106734A priority patent/TWI322436B/en
Publication of JP2006249128A publication Critical patent/JP2006249128A/en
Application granted granted Critical
Publication of JP5241997B2 publication Critical patent/JP5241997B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To provide a conductive polymer solution which can prevent corrosion of metals, discoloration of contactants and the like from occurring, and a conductive coating film. <P>SOLUTION: The conductive polymer solution, which contains a &pi;-conjugated conductive polymer, a polyanion and a solvent, has a pH of 5-13 at 25&deg;C. The conductive coating film is formed by coating the above conductive polymer solution. <P>COPYRIGHT: (C)2006,JPO&amp;NCIPI

Description

本発明は、π共役系導電性高分子を含む導電性高分子溶液に関する。また、電子部品や包装材等に導電性を付与するための導電性塗膜に関する。   The present invention relates to a conductive polymer solution containing a π-conjugated conductive polymer. The present invention also relates to a conductive coating for imparting conductivity to electronic parts, packaging materials, and the like.

π共役系導電性高分子は、電子部品、汎用帯電防止材、精密な電子機器の帯電防止包装材、転写ベルトなどの電子写真機器部品に使用されている。
このπ共役系導電性高分子はそれ単独では溶媒に溶解せず、また、融点を迎える前に分解するいわゆる不溶不融の性質を有するため、膜形成が困難である。そこで、膜形成を容易にするために、π共役系導電性高分子を可溶化させる成分を添加するなどして、π共役系導電性高分子を溶媒に溶解させる方法が数多く提案されている。
π-conjugated conductive polymers are used in electrophotographic equipment parts such as electronic parts, general-purpose antistatic materials, antistatic packaging materials for precision electronic equipment, and transfer belts.
This π-conjugated conductive polymer alone is not soluble in a solvent, and has a so-called insoluble and infusible property that decomposes before reaching the melting point, so that film formation is difficult. In order to facilitate film formation, many methods have been proposed for dissolving a π-conjugated conductive polymer in a solvent by adding a component that solubilizes the π-conjugated conductive polymer.

例えば、特許文献1では、スルホ基、カルボキシ基等を有するポリアニオンの存在下でアニリンを重合することにより、ポリアニリンを含有する液を得ることが提案されている。このポリアニリン含有液においては、水中にポリアニリンがnmオーダーで分散しているため、見かけ上および性能上、溶液と同様の挙動を示す。そして、このポリアニリン含有液は、水溶性ポリマーの導電性付与材料として好適であるため、水溶性ポリマーを混合することにより、優れた性能を有する帯電防止材料を得ることができる。
特開平7−105718号公報
For example, Patent Document 1 proposes to obtain a liquid containing polyaniline by polymerizing aniline in the presence of a polyanion having a sulfo group, a carboxy group or the like. In this polyaniline-containing liquid, since polyaniline is dispersed in the order of nm, water exhibits the same behavior as the solution in terms of appearance and performance. And since this polyaniline containing liquid is suitable as an electroconductivity provision material of a water-soluble polymer, the antistatic material which has the outstanding performance can be obtained by mixing a water-soluble polymer.
JP-A-7-105718

しかしながら、特許文献1に記載のポリアニリン含有液を、電子部品と接触する用途に使用すると金属腐食を引き起こしたり、導電性高分子溶液に接触する接触物(例えば、食品等)の変色などの不具合を引き起こしたりすることがあった。
本発明は、上記事情に鑑みてなされたものであって、金属腐食や接触物の変色等を防止できる導電性高分子溶液および導電性塗膜を提供することを目的とする。
However, when the polyaniline-containing liquid described in Patent Document 1 is used for an application in contact with an electronic component, problems such as metal corrosion or discoloration of a contact object (for example, food) that comes into contact with a conductive polymer solution are caused. And sometimes caused it.
This invention is made | formed in view of the said situation, Comprising: It aims at providing the conductive polymer solution and conductive film which can prevent metal corrosion, discoloration of a contact material, etc.

本発明者らは、金属腐食や接触物の変色について調べた結果、π共役系導電性高分子を含む溶液のpHが低いことが原因であることを見出し、以下の導電性高分子溶液および導電性塗膜を発明した。
すなわち、本発明の導電性高分子溶液は、π共役系導電性高分子とポリアニオンと窒素含有芳香族性環式化合物と溶媒とを含有する導電性高分子溶液において、π共役系導電性高分子が、ポリピロール、ポリチオフェン、ポリ(N−メチルピロール)、ポリ(3−メチルチオフェン)、ポリ(3−メトキシチオフェン)、ポリ(3,4−エチレンジオキシチオフェン)から選ばれる1種又は2種からなる(共)重合体であり、ポリアニオンが、ポリスチレンスルホン酸、ポリイソプレンスルホン酸、ポリアクリル酸エチルスルホン酸、ポリアクリル酸ブチルスルホン酸から選ばれ、窒素含有芳香族性環式化合物は、一つの窒素原子を含有するピリジン類及びその誘導体、二つの窒素原子を含有するイミダゾール類及びその誘導体、ピリミジン類及びその誘導体、ピラジン類及びその誘導体、三つの窒素原子を含有するトリアジン類及びその誘導体から選ばれ、温度25℃におけるpHが7〜11であることを特徴とする。
本発明の導電性高分子溶液においては、分子内に水酸基、グリシジル基、アミノ基のいずれか1種以上を有する化合物をさらに含有することが好ましい。
本発明の導電性塗膜は、上述した導電性高分子溶液が塗布されて形成されたことを特徴とする。
As a result of investigating metal corrosion and discoloration of contact materials, the present inventors have found that the cause is that the pH of the solution containing the π-conjugated conductive polymer is low. Invented a protective coating.
That is, the conductive polymer solution of the present invention, in the conductive polymer solution containing a solvent [pi-conjugated conductive polymer and polyanion and a nitrogen-containing aromatic cyclic compound, [pi-conjugated conductive polymer Is one or two selected from polypyrrole, polythiophene, poly (N-methylpyrrole), poly (3-methylthiophene), poly (3-methoxythiophene), poly (3,4-ethylenedioxythiophene) A polyanion selected from polystyrene sulfonic acid, polyisoprene sulfonic acid, polyacrylic acid ethyl sulfonic acid, polyacrylic acid butyl sulfonic acid, and the nitrogen-containing aromatic cyclic compound is one Pyridines and derivatives thereof containing nitrogen atom, imidazoles and derivatives thereof containing two nitrogen atoms, pyrimidine And derivatives thereof, pyrazines and derivatives thereof, selected from triazines and derivatives thereof containing three nitrogen atoms, wherein the pH at a temperature 25 ° C. is 7-11.
The conductive polymer solution of the present invention preferably further contains a compound having at least one of a hydroxyl group, a glycidyl group, and an amino group in the molecule.
The conductive coating film of the present invention is formed by applying the above-described conductive polymer solution.

本発明の導電性高分子溶液は、π共役系導電性高分子の溶解性を充分に保っているにもかかわらず、金属腐食や接触物の変色等を防止できる。したがって、機能性コンデンサの陰極材料やトランジスタなどの電子部品、食品包装材などの食品分野に適用できる。
本発明の導電性塗膜は、金属腐食や接触物の変色等を防止できる。
The conductive polymer solution of the present invention can prevent metal corrosion, discoloration of a contact object, and the like even though the solubility of the π-conjugated conductive polymer is sufficiently maintained. Therefore, it can be applied to the field of food such as cathode materials for functional capacitors, electronic parts such as transistors, and food packaging materials.
The conductive coating film of the present invention can prevent metal corrosion, discoloration of contact materials, and the like.

<導電性高分子溶液>
(π共役系導電性高分子)
π共役系導電性高分子は、主鎖がπ共役系で構成されている有機高分子であれば使用できる。例えば、ポリピロール類、ポリチオフェン類、ポリアセチレン類、ポリフェニレン類、ポリフェニレンビニレン類、ポリアニリン類、ポリアセン類、ポリチオフェンビニレン類、及びこれらの共重合体等が挙げられる。重合の容易さ、空気中での安定性の点からは、ポリピロール類、ポリチオフェン類及びポリアニリン類が好ましい。
π共役系導電性高分子は無置換のままでも、充分な導電性を得ることができるが、導電性をより高めるためには、アルキル基、カルボキシ基、スルホ基、アルコキシ基、ヒドロキシ基、シアノ基等の官能基をπ共役系導電性高分子に導入することが好ましい。
<Conductive polymer solution>
(Π-conjugated conductive polymer)
The π-conjugated conductive polymer can be used as long as the main chain is an organic polymer having a π-conjugated system. Examples thereof include polypyrroles, polythiophenes, polyacetylenes, polyphenylenes, polyphenylene vinylenes, polyanilines, polyacenes, polythiophene vinylenes, and copolymers thereof. From the viewpoint of easy polymerization and stability in air, polypyrroles, polythiophenes and polyanilines are preferred.
Even if the π-conjugated conductive polymer remains unsubstituted, sufficient conductivity can be obtained. However, in order to further improve the conductivity, an alkyl group, a carboxy group, a sulfo group, an alkoxy group, a hydroxy group, a cyano group, It is preferable to introduce a functional group such as a group into the π-conjugated conductive polymer.

このようなπ共役系導電性高分子の具体例としては、ポリピロール、ポリ(N−メチルピロール)、ポリ(3−メチルピロール)、ポリ(3−エチルピロール)、ポリ(3−n−プロピルピロール)、ポリ(3−ブチルピロール)、ポリ(3−オクチルピロール)、ポリ(3−デシルピロール)、ポリ(3−ドデシルピロール)、ポリ(3,4−ジメチルピロール)、ポリ(3,4−ジブチルピロール)、ポリ(3−カルボキシピロール)、ポリ(3−メチル−4−カルボキシピロール)、ポリ(3−メチル−4−カルボキシエチルピロール)、ポリ(3−メチル−4−カルボキシブチルピロール)、ポリ(3−ヒドロキシピロール)、ポリ(3−メトキシピロール)、ポリ(3−エトキシピロール)、ポリ(3−ブトキシピロール)、ポリ(3−ヘキシルオキシピロール)、ポリ(3−メチル−4−ヘキシルオキシピロール)、ポリ(3−メチル−4−ヘキシルオキシピロール)、ポリチオフェン、ポリ(3−メチルチオフェン)、ポリ(3−エチルチオフェン)、ポリ(3−プロピルチオフェン)、ポリ(3−ブチルチオフェン)、ポリ(3−ヘキシルチオフェン)、ポリ(3−ヘプチルチオフェン)、ポリ(3−オクチルチオフェン)、ポリ(3−デシルチオフェン)、ポリ(3−ドデシルチオフェン)、ポリ(3−オクタデシルチオフェン)、ポリ(3−ブロモチオフェン)、ポリ(3−クロロチオフェン)、ポリ(3−ヨードチオフェン)、ポリ(3−シアノチオフェン)、ポリ(3−フェニルチオフェン)、ポリ(3,4−ジメチルチオフェン)、ポリ(3,4−ジブチルチオフェン)、ポリ(3−ヒドロキシチオフェン)、ポリ(3−メトキシチオフェン)、ポリ(3−エトキシチオフェン)、ポリ(3−ブトキシチオフェン)、ポリ(3−ヘキシルオキシチオフェン)、ポリ(3−ヘプチルオキシチオフェン)、ポリ(3−オクチルオキシチオフェン)、ポリ(3−デシルオキシチオフェン)、ポリ(3−ドデシルオキシチオフェン)、ポリ(3−オクタデシルオキシチオフェン)、ポリ(3,4−ジヒドロキシチオフェン)、ポリ(3,4−ジメトキシチオフェン)、ポリ(3,4−ジエトキシチオフェン)、ポリ(3,4−ジプロポキシチオフェン)、ポリ(3,4−ジブトキシチオフェン)、ポリ(3,4−ジヘキシルオキシチオフェン)、ポリ(3,4−ジヘプチルオキシチオフェン)、ポリ(3,4−ジオクチルオキシチオフェン)、ポリ(3,4−ジデシルオキシチオフェン)、ポリ(3,4−ジドデシルオキシチオフェン)、ポリ(3,4−エチレンジオキシチオフェン)、ポリ(3,4−プロピレンジオキシチオフェン)、ポリ(3,4−ブテンジオキシチオフェン)、ポリ(3−メチル−4−メトキシチオフェン)、ポリ(3−メチル−4−エトキシチオフェン)、ポリ(3−カルボキシチオフェン)、ポリ(3−メチル−4−カルボキシチオフェン)、ポリ(3−メチル−4−カルボキシエチルチオフェン)、ポリ(3−メチル−4−カルボキシブチルチオフェン)、ポリアニリン、ポリ(2−メチルアニリン)、ポリ(3−イソブチルアニリン)、ポリ(2−アニリンスルホン酸)、ポリ(3−アニリンスルホン酸)等が挙げられる。   Specific examples of such π-conjugated conductive polymers include polypyrrole, poly (N-methylpyrrole), poly (3-methylpyrrole), poly (3-ethylpyrrole), and poly (3-n-propylpyrrole). ), Poly (3-butylpyrrole), poly (3-octylpyrrole), poly (3-decylpyrrole), poly (3-dodecylpyrrole), poly (3,4-dimethylpyrrole), poly (3,4 Dibutylpyrrole), poly (3-carboxypyrrole), poly (3-methyl-4-carboxypyrrole), poly (3-methyl-4-carboxyethylpyrrole), poly (3-methyl-4-carboxybutylpyrrole), Poly (3-hydroxypyrrole), poly (3-methoxypyrrole), poly (3-ethoxypyrrole), poly (3-butoxypyrrole), poly 3-hexyloxypyrrole), poly (3-methyl-4-hexyloxypyrrole), poly (3-methyl-4-hexyloxypyrrole), polythiophene, poly (3-methylthiophene), poly (3-ethylthiophene) , Poly (3-propylthiophene), poly (3-butylthiophene), poly (3-hexylthiophene), poly (3-heptylthiophene), poly (3-octylthiophene), poly (3-decylthiophene), poly (3-dodecylthiophene), poly (3-octadecylthiophene), poly (3-bromothiophene), poly (3-chlorothiophene), poly (3-iodothiophene), poly (3-cyanothiophene), poly (3 -Phenylthiophene), poly (3,4-dimethylthiophene), poly (3,4-dibuty) Ruthiophene), poly (3-hydroxythiophene), poly (3-methoxythiophene), poly (3-ethoxythiophene), poly (3-butoxythiophene), poly (3-hexyloxythiophene), poly (3-heptyl) Oxythiophene), poly (3-octyloxythiophene), poly (3-decyloxythiophene), poly (3-dodecyloxythiophene), poly (3-octadecyloxythiophene), poly (3,4-dihydroxythiophene), Poly (3,4-dimethoxythiophene), poly (3,4-diethoxythiophene), poly (3,4-dipropoxythiophene), poly (3,4-dibutoxythiophene), poly (3,4-dihexyl) Oxythiophene), poly (3,4-diheptyloxythiophene), poly (3 4-dioctyloxythiophene), poly (3,4-didecyloxythiophene), poly (3,4-didodecyloxythiophene), poly (3,4-ethylenedioxythiophene), poly (3,4-propylene) Dioxythiophene), poly (3,4-butenedioxythiophene), poly (3-methyl-4-methoxythiophene), poly (3-methyl-4-ethoxythiophene), poly (3-carboxythiophene), poly (3-methyl-4-carboxythiophene), poly (3-methyl-4-carboxyethylthiophene), poly (3-methyl-4-carboxybutylthiophene), polyaniline, poly (2-methylaniline), poly (3 -Isobutylaniline), poly (2-anilinesulfonic acid), poly (3-anilinesulfonic acid), etc. It is below.

中でも、ポリピロール、ポリチオフェン、ポリ(N−メチルピロール)、ポリ(3−メチルチオフェン)、ポリ(3−メトキシチオフェン)、ポリ(3,4−エチレンジオキシチオフェン)から選ばれる1種又は2種からなる(共)重合体が抵抗値、反応性の点から好適に用いられる。さらには、ポリピロール、ポリ(3,4−エチレンジオキシチオフェン)は、導電性がより高い上に、耐熱性が向上する点から、より好ましい。
また、ポリ(N−メチルピロール)、ポリ(3−メチルチオフェン)のようなアルキル置換化合物は溶媒溶解性や、疎水性樹脂を添加した場合の相溶性および分散性がより向上することからより好ましい。また、アルキル置換化合物のアルキル基の中では、導電性の低下を防ぐことから、メチル基が好ましい。
Among them, from one or two kinds selected from polypyrrole, polythiophene, poly (N-methylpyrrole), poly (3-methylthiophene), poly (3-methoxythiophene), and poly (3,4-ethylenedioxythiophene). The (co) polymer is preferably used from the viewpoints of resistance and reactivity. Furthermore, polypyrrole and poly (3,4-ethylenedioxythiophene) are more preferable because they have higher conductivity and improved heat resistance.
In addition, alkyl-substituted compounds such as poly (N-methylpyrrole) and poly (3-methylthiophene) are more preferable because solvent solubility and compatibility and dispersibility when a hydrophobic resin is added are further improved. . Further, among the alkyl groups of the alkyl-substituted compound, a methyl group is preferable because it prevents a decrease in conductivity.

上記π共役系導電性高分子は、溶媒中、π共役系導電性高分子を形成する前駆体モノマーを、適切な酸化剤と後述のアニオン基を有する高分子の存在下で化学酸化重合することによって容易に製造できる。
前駆体モノマーは、分子内にπ共役系を有し、適切な酸化剤の作用によって高分子化した際にもその主鎖にπ共役系が形成されるものである。例えば、ピロール類及びその誘導体、チオフェン類及びその誘導体、アニリン類及びその誘導体等が挙げられる。
前駆体モノマーの具体例としては、ピロール、N−メチルピロール、3−メチルピロール、3−エチルピロール、3−n−プロピルピロール、3−ブチルピロール、3−オクチルピロール、3−デシルピロール、3−ドデシルピロール、3,4−ジメチルピロール、3,4−ジブチルピロール、3−カルボキシルピロール、3−メチル−4−カルボキシルピロール、3−メチル−4−カルボキシエチルピロール、3−メチル−4−カルボキシブチルピロール、3−ヒドロキシピロール、3−メトキシピロール、3−エトキシピロール、3−ブトキシピロール、3−ヘキシルオキシピロール、3−メチル−4−ヘキシルオキシピロール、3−メチル−4−ヘキシルオキシピロール、チオフェン、3−メチルチオフェン、3−エチルチオフェン、3−プロピルチオフェン、3−ブチルチオフェン、3−ヘキシルチオフェン、3−ヘプチルチオフェン、3−オクチルチオフェン、3−デシルチオフェン、3−ドデシルチオフェン、3−オクタデシルチオフェン、3−ブロモチオフェン、3−クロロチオフェン、3−ヨードチオフェン、3−シアノチオフェン、3−フェニルチオフェン、3,4−ジメチルチオフェン、3,4−ジブチルチオフェン、3−ヒドロキシチオフェン、3−メトキシチオフェン、3−エトキシチオフェン、3−ブトキシチオフェン、3−ヘキシルオキシチオフェン、3−ヘプチルオキシチオフェン、3−オクチルオキシチオフェン、3−デシルオキシチオフェン、3−ドデシルオキシチオフェン、3−オクタデシルオキシチオフェン、3,4−ジヒドロキシチオフェン、3,4−ジメトキシチオフェン、3,4−ジエトキシチオフェン、3,4−ジプロポキシチオフェン、3,4−ジブトキシチオフェン、3,4−ジヘキシルオキシチオフェン、3,4−ジヘプチルオキシチオフェン、3,4−ジオクチルオキシチオフェン、3,4−ジデシルオキシチオフェン、3,4−ジドデシルオキシチオフェン、3,4−エチレンジオキシチオフェン、3,4−プロピレンジオキシチオフェン、3,4−ブテンジオキシチオフェン、3−メチル−4−メトキシチオフェン、3−メチル−4−エトキシチオフェン、3−カルボキシチオフェン、3−メチル−4−カルボキシチオフェン、3−メチル−4−カルボキシエチルチオフェン、3−メチル−4−カルボキシブチルチオフェン、アニリン、2−メチルアニリン、3−イソブチルアニリン、2−アニリンスルホン酸、3−アニリンスルホン酸等が挙げられる。
The π-conjugated conductive polymer is obtained by chemical oxidative polymerization of a precursor monomer that forms a π-conjugated conductive polymer in a solvent in the presence of a suitable oxidizing agent and a polymer having an anionic group described below. Can be easily manufactured.
The precursor monomer has a π-conjugated system in the molecule, and a π-conjugated system is formed in the main chain even when polymerized by the action of an appropriate oxidizing agent. Examples thereof include pyrroles and derivatives thereof, thiophenes and derivatives thereof, anilines and derivatives thereof, and the like.
Specific examples of the precursor monomer include pyrrole, N-methylpyrrole, 3-methylpyrrole, 3-ethylpyrrole, 3-n-propylpyrrole, 3-butylpyrrole, 3-octylpyrrole, 3-decylpyrrole, 3- Dodecylpyrrole, 3,4-dimethylpyrrole, 3,4-dibutylpyrrole, 3-carboxylpyrrole, 3-methyl-4-carboxylpyrrole, 3-methyl-4-carboxyethylpyrrole, 3-methyl-4-carboxybutylpyrrole 3-hydroxypyrrole, 3-methoxypyrrole, 3-ethoxypyrrole, 3-butoxypyrrole, 3-hexyloxypyrrole, 3-methyl-4-hexyloxypyrrole, 3-methyl-4-hexyloxypyrrole, thiophene, 3 -Methylthiophene, 3-ethylthiophene, -Propylthiophene, 3-butylthiophene, 3-hexylthiophene, 3-heptylthiophene, 3-octylthiophene, 3-decylthiophene, 3-dodecylthiophene, 3-octadecylthiophene, 3-bromothiophene, 3-chlorothiophene, 3 -Iodothiophene, 3-cyanothiophene, 3-phenylthiophene, 3,4-dimethylthiophene, 3,4-dibutylthiophene, 3-hydroxythiophene, 3-methoxythiophene, 3-ethoxythiophene, 3-butoxythiophene, 3- Hexyloxythiophene, 3-heptyloxythiophene, 3-octyloxythiophene, 3-decyloxythiophene, 3-dodecyloxythiophene, 3-octadecyloxythiophene, 3,4-dihydroxythiophene 3,4-dimethoxythiophene, 3,4-diethoxythiophene, 3,4-dipropoxythiophene, 3,4-dibutoxythiophene, 3,4-dihexyloxythiophene, 3,4-diheptyloxythiophene, 3,4-dioctyloxythiophene, 3,4-didecyloxythiophene, 3,4-didodecyloxythiophene, 3,4-ethylenedioxythiophene, 3,4-propylenedioxythiophene, 3,4-butene Oxythiophene, 3-methyl-4-methoxythiophene, 3-methyl-4-ethoxythiophene, 3-carboxythiophene, 3-methyl-4-carboxythiophene, 3-methyl-4-carboxyethylthiophene, 3-methyl-4 -Carboxybutylthiophene, aniline, 2-methylaniline, Examples include 3-isobutylaniline, 2-aniline sulfonic acid, and 3-aniline sulfonic acid.

π共役系導電性高分子の製造で使用する溶媒としては特に制限されず、前記前駆体モノマーを溶解又は分散しうる溶媒であり、酸化剤の酸化力を維持させることができるものであればよい。例えば、水、N−メチル−2−ピロリドン、N,N−ジメチルホルムアミド、N,N−ジメチルアセトアミド、ジメチルスルホキシド、ヘキサメチレンホスホルトリアミド、アセトニトリル、ベンゾニトリル等の極性溶媒、クレゾール、フェノール、キシレノール等のフェノール類、メタノール、エタノール、プロパノール、ブタノール等のアルコール類、アセトン、メチルエチルケトン等のケトン類、ヘキサン、ベンゼン、トルエン等の炭化水素類、ギ酸、酢酸等のカルボン酸、エチレンカーボネート、プロピレンカーボネート等のカーボネート化合物、ジオキサン、ジエチルエーテル等のエーテル化合物、エチレングリコールジアルキルエーテル、プロピレングリコールジアルキルエーテル、ポリエチレングリコールジアルキルエーテル、ポリプロピレングリコールジアルキルエーテル等の鎖状エーテル類、3−メチル−2−オキサゾリジノン等の複素環化合物、アセトニトリル、グルタロジニトリル、メトキシアセトニトリル、プロピオニトリル、ベンゾニトリル等のニトリル化合物等が挙げられる。これらの溶媒は、単独で用いてもよいし、2種類以上の混合物としてもよいし、他の有機溶媒との混合物としてもよい。   The solvent used in the production of the π-conjugated conductive polymer is not particularly limited as long as it is a solvent that can dissolve or disperse the precursor monomer and can maintain the oxidizing power of the oxidizing agent. . For example, polar solvents such as water, N-methyl-2-pyrrolidone, N, N-dimethylformamide, N, N-dimethylacetamide, dimethyl sulfoxide, hexamethylene phosphortriamide, acetonitrile, benzonitrile, cresol, phenol, xylenol, etc. Phenols, alcohols such as methanol, ethanol, propanol and butanol, ketones such as acetone and methyl ethyl ketone, hydrocarbons such as hexane, benzene and toluene, carboxylic acids such as formic acid and acetic acid, ethylene carbonate, propylene carbonate, etc. Carbonate compounds, ether compounds such as dioxane, diethyl ether, ethylene glycol dialkyl ether, propylene glycol dialkyl ether, polyethylene glycol dialkyl ether Chain ethers such as polypropylene glycol dialkyl ether, 3-methyl-2-oxazolidinone heterocyclic compounds such as, acetonitrile, glutarodinitrile, methoxy acetonitrile, propionitrile, nitrile compounds such as benzonitrile and the like. These solvents may be used alone, as a mixture of two or more kinds, or as a mixture with other organic solvents.

酸化剤としては、前記前駆体モノマーを酸化させてπ共役系導電性高分子を得ることができるものであればよく、例えば、ぺルオキソ二硫酸アンモニウム、ぺルオキソ二硫酸ナトリウム、ぺルオキソ二硫酸カリウム等のぺルオキソ二硫酸塩、塩化第二鉄、硫酸第二鉄、硝酸第二鉄、塩化第二銅等の遷移金属化合物、三フッ化ホウ素、塩化アルミニウムなどの金属ハロゲン化合物、酸化銀、酸化セシウム等の金属酸化物、過酸化水素、オゾン等の過酸化物、過酸化ベンゾイル等の有機過酸化物、酸素等が挙げられる。   Any oxidizing agent may be used as long as it can oxidize the precursor monomer to obtain a π-conjugated conductive polymer. Examples thereof include ammonium peroxodisulfate, sodium peroxodisulfate, and potassium peroxodisulfate. Peroxodisulfate, ferric chloride, ferric sulfate, ferric nitrate, transition metal compounds such as cupric chloride, metal halides such as boron trifluoride, aluminum chloride, silver oxide, cesium oxide Metal oxides such as hydrogen peroxide and ozone, organic peroxides such as benzoyl peroxide, oxygen and the like.

[ポリアニオン]
ポリアニオンは、置換若しくは未置換のポリアルキレン、置換若しくは未置換のポリアルケニレン、置換若しくは未置換のポリイミド、置換若しくは未置換のポリアミド、置換若しくは未置換のポリエステル及びこれらの共重合体であって、アニオン基を有する構成単位とアニオン基を有さない構成単位とからなるものである。
このポリアニオンのアニオン基は、π共役系導電性高分子に対するドーパントとして機能して、π共役系導電性高分子の導電性と耐熱性を向上させる。
[Polyanion]
The polyanion is a substituted or unsubstituted polyalkylene, a substituted or unsubstituted polyalkenylene, a substituted or unsubstituted polyimide, a substituted or unsubstituted polyamide, a substituted or unsubstituted polyester, and a copolymer thereof. It consists of a structural unit having a group and a structural unit having no anionic group.
The anion group of the polyanion functions as a dopant for the π-conjugated conductive polymer, and improves the conductivity and heat resistance of the π-conjugated conductive polymer.

ポリアルキレンとは、主鎖がメチレンの繰り返しで構成されているポリマーである。ポリアルキレンとしては、例えば、ポリエチレン、ポリプロピレン、ポリブテン、ポリペンテン、ポリヘキセン、ポリビニルアルコール、ポリビニルフェノール、ポリ3,3,3−トリフルオロプロピレン、ポリアクリロニトリル、ポリアクリレート、ポリスチレン等が挙げられる。   A polyalkylene is a polymer whose main chain is composed of repeating methylenes. Examples of the polyalkylene include polyethylene, polypropylene, polybutene, polypentene, polyhexene, polyvinyl alcohol, polyvinylphenol, poly3,3,3-trifluoropropylene, polyacrylonitrile, polyacrylate, polystyrene, and the like.

ポリアルケニレンとは、主鎖に不飽和結合(ビニル基)が1個以上含まれる構成単位からなるポリマーである。ポリアルケニレンの具体例としては、プロペニレン、1−メチルプロペニレン、1−ブチルプロペニレン、1−デシルプロペニレン、1−シアノプロペニレン、1−フェニルプロペニレン、1−ヒドロキシプロペニレン、1−ブテニレン、1−メチル−1−ブテニレン、1−エチル−1−ブテニレン、1−オクチル−1−ブテニレン、1−ペンタデシル−1−ブテニレン、2−メチル−1−ブテニレン、2−エチル−1−ブテニレン、2−ブチル−1−ブテニレン、2−ヘキシル−1−ブテニレン、2−オクチル−1−ブテニレン、2−デシル−1−ブテニレン、2−ドデシル−1−ブテニレン、2−フェニル−1−ブテニレン、2−ブテニレン、1−メチル−2−ブテニレン、1−エチル−2−ブテニレン、1−オクチル−2−ブテニレン、1−ペンタデシル−2−ブテニレン、2−メチル−2−ブテニレン、2−エチル−2−ブテニレン、2−ブチル−2−ブテニレン、2−ヘキシル−2−ブテニレン、2−オクチル−2−ブテニレン、2−デシル−2−ブテニレン、2−ドデシル−2−ブテニレン、2−フェニル−2−ブテニレン、2−プロピレンフェニル−2−ブテニレン、3−メチル−2−ブテニレン、3−エチル−2−ブテニレン、3−ブチル−2−ブテニレン、3−ヘキシル−2−ブテニレン、3−オクチル−2−ブテニレン、3−デシル−2−ブテニレン、3−ドデシル−2−ブテニレン、3−フェニル−2−ブテニレン、3−プロピレンフェニル−2−ブテニレン、2−ペンテニレン、4−プロピル−2−ペンテニレン、4−ブチル−2−ペンテニレン、4−ヘキシル−2−ペンテニレン、4−シアノ−2−ペンテニレン、3−メチル−2−ペンテニレン、4−エチル−2−ペンテニレン、3−フェニル−2−ペンテニレン、4−ヒドロキシ−2−ペンテニレン、ヘキセニレン等から選ばれる1種以上の構成単位を含む重合体が挙げられる。
これらの中でも、不飽和結合とπ共役系導電性高分子との相互作用があること、置換若しくは未置換のブタジエンを出発物質として合成しやすいことから、置換若しくは未置換のブテニレンが好ましい。
Polyalkenylene is a polymer composed of structural units containing one or more unsaturated bonds (vinyl groups) in the main chain. Specific examples of polyalkenylene include propenylene, 1-methylpropenylene, 1-butylpropenylene, 1-decylpropenylene, 1-cyanopropenylene, 1-phenylpropenylene, 1-hydroxypropenylene, 1-butenylene, 1-methyl-1-butenylene, 1-ethyl-1-butenylene, 1-octyl-1-butenylene, 1-pentadecyl-1-butenylene, 2-methyl-1-butenylene, 2-ethyl-1-butenylene, 2- Butyl-1-butenylene, 2-hexyl-1-butenylene, 2-octyl-1-butenylene, 2-decyl-1-butenylene, 2-dodecyl-1-butenylene, 2-phenyl-1-butenylene, 2-butenylene, 1-methyl-2-butenylene, 1-ethyl-2-butenylene, 1-octyl-2-butenylene 1-pentadecyl-2-butenylene, 2-methyl-2-butenylene, 2-ethyl-2-butenylene, 2-butyl-2-butenylene, 2-hexyl-2-butenylene, 2-octyl-2-butenylene, 2- Decyl-2-butenylene, 2-dodecyl-2-butenylene, 2-phenyl-2-butenylene, 2-propylenephenyl-2-butenylene, 3-methyl-2-butenylene, 3-ethyl-2-butenylene, 3-butyl 2-butenylene, 3-hexyl-2-butenylene, 3-octyl-2-butenylene, 3-decyl-2-butenylene, 3-dodecyl-2-butenylene, 3-phenyl-2-butenylene, 3-propylenephenyl- 2-butenylene, 2-pentenylene, 4-propyl-2-pentenylene, 4-butyl-2-pentenylene, 4-he Selected from sil-2-pentenylene, 4-cyano-2-pentenylene, 3-methyl-2-pentenylene, 4-ethyl-2-pentenylene, 3-phenyl-2-pentenylene, 4-hydroxy-2-pentenylene, hexenylene, etc. And a polymer containing one or more structural units.
Among these, substituted or unsubstituted butenylene is preferable because of the interaction between the unsaturated bond and the π-conjugated conductive polymer and the ease of synthesis using substituted or unsubstituted butadiene as a starting material.

ポリイミドとしては、ピロメリット酸二無水物、ビフェニルテトラカルボン酸二無水物、ベンゾフェノンテトラカルボン酸二無水物、2,2,3,3−テトラカルボキシジフェニルエーテル二無水物、2,2−[4,4’−ジ(ジカルボキシフェニルオキシ)フェニル]プロパン二無水物等の無水物とオキシジアニン、パラフェニレンジアミン、メタフェニレンジアミン、ベンゾフェノンジアミン等のジアミンとからのポリイミドが挙げられる。
ポリアミドとしては、ポリアミド6、ポリアミド6,6、ポリアミド6,10等が挙げられる。
ポリエステルとしては、ポリエチレンテレフタレート、ポリブチレンテレフタレート等が挙げられる。
As polyimide, pyromellitic dianhydride, biphenyltetracarboxylic dianhydride, benzophenone tetracarboxylic dianhydride, 2,2,3,3-tetracarboxydiphenyl ether dianhydride, 2,2- [4,4 Examples include polyimides from anhydrides such as' -di (dicarboxyphenyloxy) phenyl] propane dianhydride and diamines such as oxydianine, paraphenylenediamine, metaphenylenediamine, and benzophenonediamine.
Examples of the polyamide include polyamide 6, polyamide 6,6, polyamide 6,10 and the like.
Examples of the polyester include polyethylene terephthalate and polybutylene terephthalate.

ポリアニオンが置換基を有する場合、その置換基としては、アルキル基、ヒドロキシ基、アミノ基、カルボキシ基、シアノ基、フェニル基、フェノール基、エステル基、アルコキシ基等が挙げられる。溶媒への溶解性、耐熱性及び樹脂への相溶性等を考慮すると、アルキル基、ヒドロキシ基、フェノール基、エステル基が好ましい。
アルキル基は、極性溶媒又は非極性溶媒への溶解性及び分散性、樹脂への相溶性及び分散性等を高くすることができ、ヒドロキシ基は、他の水素原子等との水素結合を形成しやすくでき、有機溶媒への溶解性、樹脂への相溶性、分散性、接着性を高くすることができる。また、シアノ基及びヒドロキシフェニル基は、極性樹脂への相溶性、溶解性を高くすることができ、しかも、耐熱性も高くすることができる。
上記置換基の中では、アルキル基、ヒドロキシ基、エステル基、シアノ基が好ましい。
When the polyanion has a substituent, examples of the substituent include an alkyl group, a hydroxy group, an amino group, a carboxy group, a cyano group, a phenyl group, a phenol group, an ester group, and an alkoxy group. In view of solubility in a solvent, heat resistance, compatibility with a resin, and the like, an alkyl group, a hydroxy group, a phenol group, and an ester group are preferable.
Alkyl groups can increase solubility and dispersibility in polar or nonpolar solvents, compatibility and dispersibility in resins, and hydroxy groups form hydrogen bonds with other hydrogen atoms. This makes it easy to increase solubility in organic solvents, compatibility with resins, dispersibility, and adhesion. In addition, the cyano group and the hydroxyphenyl group can increase the compatibility and solubility in the polar resin, and can also increase the heat resistance.
Among the above substituents, an alkyl group, a hydroxy group, an ester group, and a cyano group are preferable.

前記アルキル基としては、メチル、エチル、プロピル、ブチル、イソブチル、t−ブチル、ペンチル、ヘキシル、オクチル、デシル、ドデシル等の鎖状アルキル基、シクロプロピル、シクロペンチル、シクロヘキシル等のシクロアルキル基が挙げられる。有機溶剤への溶解性、樹脂への分散性、立体障害等を考慮すると、炭素数1〜12のアルキル基がより好ましい。
前記ヒドロキシ基としては、ポリアニオンの主鎖に直接結合したヒドロキシ基又は他の官能基を介在して結合したヒドロキシ基が挙げられる。他の官能基としては、炭素数1〜7のアルキル基、炭素数2〜7のアルケニル基、アミド基、イミド基等が挙げられる。ヒドロキシ基はこれらの官能基の末端又は中に置換されている。これらの中では樹脂への相溶及び有機溶剤への溶解性から、主鎖に結合した炭素数1〜6のアルキル基の末端に結合したヒドロキシ基がより好ましい。
前記アミノ基としては、ポリアニオンの主鎖に直接結合したアミノ基又は他の官能基を介在して結合したアミノ基が挙げられる。他の官能基としては、炭素数1〜7のアルキル基、炭素数2〜7のアルケニル基、アミド基、イミド基等が挙げられる。アミノ基はこれらの官能基の末端又は中に置換されている。
前記フェノール基としては、ポリアニオンの主鎖に直接結合したフェノール基又は他の官能基を介在して結合したフェノール基が挙げられる。他の官能基としては、炭素数1〜7のアルキル基、炭素数2〜7のアルケニル基、アミド基、イミド基等が挙げられる。フェノール基はこれらの官能基の末端又は中に置換されている。
前記エステル基としては、ポリアニオンの主鎖に直接結合したアルキル系エステル基、芳香族系エステル基、他の官能基を介在してなるアルキル系エステル基又は芳香族系エステル基が挙げられる。
シアノ基としては、ポリアニオンの主鎖に直接結合したシアノ基、ポリアニオンの主鎖に結合した炭素数1〜7のアルキル基の末端に結合したシアノ基、ポリアニオンの主鎖に結合した炭素数2〜7のアルケニル基の末端に結合したシアノ基等を挙げることができる。
Examples of the alkyl group include chain alkyl groups such as methyl, ethyl, propyl, butyl, isobutyl, t-butyl, pentyl, hexyl, octyl, decyl, and dodecyl, and cycloalkyl groups such as cyclopropyl, cyclopentyl, and cyclohexyl. . In consideration of solubility in an organic solvent, dispersibility in a resin, steric hindrance, and the like, an alkyl group having 1 to 12 carbon atoms is more preferable.
Examples of the hydroxy group include a hydroxy group directly bonded to the main chain of the polyanion or a hydroxy group bonded via another functional group. Examples of other functional groups include an alkyl group having 1 to 7 carbon atoms, an alkenyl group having 2 to 7 carbon atoms, an amide group, and an imide group. The hydroxy group is substituted at the end or in these functional groups. Among these, a hydroxy group bonded to the terminal of an alkyl group having 1 to 6 carbon atoms bonded to the main chain is more preferable from the viewpoint of compatibility with a resin and solubility in an organic solvent.
Examples of the amino group include an amino group directly bonded to the main chain of the polyanion or an amino group bonded via another functional group. Examples of other functional groups include an alkyl group having 1 to 7 carbon atoms, an alkenyl group having 2 to 7 carbon atoms, an amide group, and an imide group. The amino group is substituted at the end or in these functional groups.
Examples of the phenol group include a phenol group directly bonded to the main chain of the polyanion or a phenol group bonded via another functional group. Examples of other functional groups include an alkyl group having 1 to 7 carbon atoms, an alkenyl group having 2 to 7 carbon atoms, an amide group, and an imide group. The phenol group is substituted at the end or in these functional groups.
Examples of the ester group include an alkyl ester group directly bonded to the main chain of the polyanion, an aromatic ester group, and an alkyl ester group or an aromatic ester group having another functional group interposed therebetween.
The cyano group includes a cyano group directly bonded to the main chain of the polyanion, a cyano group bonded to the terminal of the alkyl group having 1 to 7 carbon atoms bonded to the main chain of the polyanion, and 2 to 2 carbon atoms bonded to the main chain of the polyanion. And a cyano group bonded to the terminal of 7 alkenyl group.

ポリアニオンのアニオン基としては、π共役系導電性高分子への化学酸化ドープが起こりうる官能基であればよいが、中でも、製造の容易さ及び安定性の観点からは、一置換硫酸エステル基、一置換リン酸エステル基、リン酸基、カルボキシ基、スルホ基等が好ましい。さらに、官能基のπ共役系導電性高分子へのドープ効果の観点より、スルホ基、一置換硫酸エステル基、カルボキシ基がより好ましい。   The anion group of the polyanion may be a functional group capable of undergoing chemical oxidation doping to the π-conjugated conductive polymer. Among them, from the viewpoint of ease of production and stability, a monosubstituted sulfate group, A monosubstituted phosphate group, a phosphate group, a carboxy group, a sulfo group and the like are preferable. Furthermore, from the viewpoint of the doping effect of the functional group on the π-conjugated conductive polymer, a sulfo group, a monosubstituted sulfate group, and a carboxy group are more preferable.

ポリアニオンの具体例としては、ポリビニルスルホン酸、ポリスチレンスルホン酸、ポリアリルスルホン酸、ポリアクリル酸エチルスルホン酸、ポリアクリル酸ブチルスルホン酸、ポリアクリルスルホン酸、ポリメタクリルスルホン酸、ポリ−2−アクリルアミド−2−メチルプロパンスルホン酸、ポリイソプレンスルホン酸、ポリビニルカルボン酸、ポリスチレンカルボン酸、ポリアリルカルボン酸、ポリアクリルカルボン酸、ポリメタクリルカルボン酸、ポリ−2−アクリルアミド−2−メチルプロパンカルボン酸、ポリイソプレンカルボン酸、ポリアクリル酸等が挙げられる。これらの単独重合体であってもよいし、2種以上の共重合体であってもよい。
これらのうち、ポリスチレンスルホン酸、ポリイソプレンスルホン酸、ポリアクリル酸エチルスルホン酸、ポリアクリル酸ブチルスルホン酸が好ましい。これらのポリアニオンは、π共役系導電性高分子の熱分解を緩和することができる。
Specific examples of polyanions include polyvinyl sulfonic acid, polystyrene sulfonic acid, polyallyl sulfonic acid, polyacrylic acid ethyl sulfonic acid, polyacrylic acid butyl sulfonic acid, polyacryl sulfonic acid, polymethacryl sulfonic acid, poly-2-acrylamide- 2-methylpropanesulfonic acid, polyisoprenesulfonic acid, polyvinyl carboxylic acid, polystyrene carboxylic acid, polyallyl carboxylic acid, polyacryl carboxylic acid, polymethacryl carboxylic acid, poly-2-acrylamido-2-methylpropane carboxylic acid, polyisoprene Examples thereof include carboxylic acid and polyacrylic acid. These homopolymers may be sufficient and 2 or more types of copolymers may be sufficient.
Among these, polystyrene sulfonic acid, polyisoprene sulfonic acid, polyacrylic acid ethyl sulfonic acid, and polyacrylic acid butyl sulfonic acid are preferable. These polyanions can mitigate thermal decomposition of the π-conjugated conductive polymer.

ポリアニオンの重合度は、モノマー単位が10〜100000個の範囲であることが好ましく、溶媒溶解性及び導電性の点からは、50〜10000個の範囲がより好ましい。   The degree of polymerization of the polyanion is preferably in the range of 10 to 100,000 monomer units, and more preferably in the range of 50 to 10,000 from the viewpoint of solvent solubility and conductivity.

ポリアニオンの製造方法としては、例えば、酸を用いてアニオン基を有さないポリマーにアニオン基を直接導入する方法、アニオン基を有さないポリマーをスルホ化剤によりスルホン酸化する方法、アニオン基含有重合性モノマーの重合により製造する方法が挙げられる。
アニオン基含有重合性モノマーの重合により製造する方法は、溶媒中、アニオン基含有重合性モノマーを、酸化剤及び/又は重合触媒の存在下で、酸化重合又はラジカル重合によって製造する方法が挙げられる。具体的には、所定量のアニオン基含有重合性モノマーを溶媒に溶解させ、これを一定温度に保ち、それに予め溶媒に所定量の酸化剤及び/又は重合触媒を溶解した溶液を添加し、所定時間で反応させる。その反応により得られたポリマーは溶媒によって一定の濃度に調整される。この製造方法において、アニオン基含有重合性モノマーにアニオン基を有さない重合性モノマーを共重合させてもよい。
アニオン基含有重合性モノマーの重合に際して使用する酸化剤、溶媒は、π共役系導電性高分子を形成する前駆体モノマーを重合する際に使用するものと同様である。
得られたポリマーがポリアニオン塩である場合には、ポリアニオン酸に変質させることが好ましい。アニオン酸に変質させる方法としては、イオン交換樹脂を用いたイオン交換法、透析法、限外ろ過法等が挙げられ、これらの中でも、作業が容易な点から限外ろ過法が好ましい。
Examples of methods for producing polyanions include a method of directly introducing an anionic group into a polymer having no anionic group using an acid, a method of sulfonating a polymer having no anionic group with a sulfonating agent, and anionic group-containing polymerization. And a method of production by polymerization of a functional monomer.
Examples of the method for producing an anion group-containing polymerizable monomer by polymerization include a method for producing an anion group-containing polymerizable monomer in a solvent by oxidative polymerization or radical polymerization in the presence of an oxidizing agent and / or a polymerization catalyst. Specifically, a predetermined amount of the anionic group-containing polymerizable monomer is dissolved in a solvent, kept at a constant temperature, and a solution in which a predetermined amount of an oxidizing agent and / or a polymerization catalyst is dissolved in the solvent is added to the predetermined amount. React with time. The polymer obtained by the reaction is adjusted to a certain concentration by the solvent. In this production method, an anionic group-containing polymerizable monomer may be copolymerized with a polymerizable monomer having no anionic group.
The oxidizing agent and solvent used in the polymerization of the anionic group-containing polymerizable monomer are the same as those used in the polymerization of the precursor monomer that forms the π-conjugated conductive polymer.
When the obtained polymer is a polyanionic salt, it is preferably transformed into a polyanionic acid. Examples of the method for transforming into an anionic acid include an ion exchange method using an ion exchange resin, a dialysis method, an ultrafiltration method, and the like. Among these, an ultrafiltration method is preferable from the viewpoint of easy work.

アニオン基含有重合性モノマーは、モノマーの一部が一置換硫酸エステル基、カルボキシ基、スルホ基等で置換されたものであり、例えば、置換若しくは未置換のエチレンスルホン酸化合物、置換若しくは未置換のスチレンスルホン酸化合物、置換若しくは未置換のアクリレートスルホン酸化合物、置換若しくは未置換のメタクリレートスルホン酸化合物、置換若しくは未置換のアクリルアミドスルホン酸化合物、置換若しくは未置換のシクロビニレンスルホン酸化合物、置換若しくは未置換のブタジエンスルホン酸化合物、置換若しくは未置換のビニル芳香族スルホン酸化合物が挙げられる。
具体的には、ビニルスルホン酸及びその塩類、アリルスルホン酸及びその塩類、メタリルスルホン酸及びその塩類、スチレンスルホン酸、メタリルオキシベンゼンスルホン酸及びその塩類、アリルオキシベンゼンスルホン酸及びその塩類、α−メチルスチレンスルホン酸及びその塩類、アクリルアミド−t−ブチルスルホン酸及びその塩類、2−アクリルアミド−2−メチルプロパンスルホン酸及びその塩類、シクロブテン−3−スルホン酸及びその塩類、イソプレンスルホン酸及びその塩類、1,3−ブタジエン−1−スルホン酸及びその塩類、1−メチル−1,3−ブタジエン−2−スルホン酸及びその塩類、1−メチル−1,3−ブタジエン−4−スルホン酸及びその塩類、アクリル酸エチルスルホン酸(CHCH-COO-(CH22-SO3H)及びその塩類、アクリル酸プロピルスルホン酸(CHCH-COO-(CH23-SO3H)及びその塩類、アクリル酸−t−ブチルスルホン酸(CHCH-COO-C(CH32CH-SO3H)及びその塩類、アクリル酸−n−ブチルスルホン酸(CHCH-COO-(CH2-SO3H)及びその塩類、アリル酸エチルスルホン酸(CHCHCH-COO-(CH22-SO3H)及びその塩類、アリル酸−t−ブチルスルホン酸(CHCHCH-COO-C(CH32CH-SO3H)及びその塩類、4−ペンテン酸エチルスルホン酸(CHCH(CH22-COO-(CH22-SO3H)及びその塩類、4−ペンテン酸プロピルスルホン酸(CHCH(CH22-COO-(CH23-SO3H)及びその塩類、4−ペンテン酸−n−ブチルスルホン酸(CHCH(CH22-COO-(CH2-SO3H)及びその塩類、4−ペンテン酸−t−ブチルスルホン酸(CHCH(CH22-COO-C(CH32CH-SO3H)及びその塩類、4−ペンテン酸フェニレンスルホン酸(CHCH(CH22-COO-C64-SO3H)及びその塩類、4−ペンテン酸ナフタレンスルホン酸(CHCH(CH22-COO-C108-SO3H)及びその塩類、メタクリル酸エチルスルホン酸(CHC(CH3)-COO-(CH22-SO3H)及びその塩類、メタクリル酸プロピルスルホン酸(CHC(CH3)-COO-(CH23-SO3H)及びその塩類、メタクリル酸−t−ブチルスルホン酸(CHC(CH3)-COO-C(CH32CH-SO3H)及びその塩類、メタクリル酸−n−ブチルスルホン酸(CHC(CH3)-COO-(CH2-SO3H)及びその塩類、メタクリル酸フェニレンスルホン酸(CHC(CH3)-COO-C64-SO3H)及びその塩類、メタクリル酸ナフタレンスルホン酸(CHC(CH3)-COO-C108-SO3H)及びその塩類、ポリビニルカルボン酸、ポリスチレンカルボン酸、ポリアリルカルボン酸、ポリアクリルカルボン酸、ポリメタクリルカルボン酸、ポリ−2−アクリルアミド−2−メチルプロパンカルボン酸、ポリイソプレンカルボン酸、ポリアクリル酸等が挙げられる。また、これらを2種以上含む共重合体であってもよい。
The anionic group-containing polymerizable monomer is one in which a part of the monomer is substituted with a mono-substituted sulfate group, a carboxy group, a sulfo group, etc., for example, a substituted or unsubstituted ethylene sulfonic acid compound, a substituted or unsubstituted Styrene sulfonic acid compound, substituted or unsubstituted acrylate sulfonic acid compound, substituted or unsubstituted methacrylate sulfonic acid compound, substituted or unsubstituted acrylamide sulfonic acid compound, substituted or unsubstituted cyclovinylene sulfonic acid compound, substituted or unsubstituted And a substituted or unsubstituted vinyl aromatic sulfonic acid compound.
Specifically, vinyl sulfonic acid and salts thereof, allyl sulfonic acid and salts thereof, methallyl sulfonic acid and salts thereof, styrene sulfonic acid, methallyloxybenzene sulfonic acid and salts thereof, allyloxybenzene sulfonic acid and salts thereof, α-methylstyrenesulfonic acid and its salts, acrylamide-t-butylsulfonic acid and its salts, 2-acrylamido-2-methylpropanesulfonic acid and its salts, cyclobutene-3-sulfonic acid and its salts, isoprenesulfonic acid and its Salts, 1,3-butadiene-1-sulfonic acid and its salts, 1-methyl-1,3-butadiene-2-sulfonic acid and its salts, 1-methyl-1,3-butadiene-4-sulfonic acid and its salts, ethyl acrylate sulfonic acid (CH 2 CH-COO- (CH 2 2 -SO 3 H) and its salts, acrylic acid propyl sulfonic acid (CH 2 CH-COO- (CH 2) 3 -SO 3 H) and its salts, acrylic acid -t- butyl sulfonic acid (CH 2 CH-COO -C (CH 3) 2 CH 2 -SO 3 H) and its salts, acrylic acid -n- butyl sulfonic acid (CH 2 CH-COO- (CH 2) 4 -SO 3 H) and salts thereof, ethyl allyl acid sulfonic acid (CH 2 CHCH 2 -COO- (CH 2) 2 -SO 3 H) and its salts, allyl acid -t- butyl sulfonic acid (CH 2 CHCH 2 -COO-C (CH 3) 2 CH 2 -SO 3 H) and salts thereof, 4-pentenoic acid ethylsulfonic acid (CH 2 CH (CH 2 ) 2 —COO— (CH 2 ) 2 —SO 3 H) and salts thereof, 4-pentenoic acid propyl sulfonic acid (CH 2 CH (CH 2 ) 2 —COO— (CH 2 ) 3 -SO 3 H) and salts thereof, 4-pentenoic acid-n-butylsulfonic acid (CH 2 CH (CH 2 ) 2 —COO— (CH 2 ) 4 —SO 3 H) and salts thereof, 4-pentene Acid-t-butyl sulfonic acid (CH 2 CH (CH 2 ) 2 —COO—C (CH 3 ) 2 CH 2 —SO 3 H) and its salts, 4-pentenoic acid phenylene sulfonic acid (CH 2 CH (CH 2 2 ) -COO—C 6 H 4 —SO 3 H) and salts thereof, 4-pentenoic acid naphthalenesulfonic acid (CH 2 CH (CH 2 ) 2 —COO—C 10 H 8 —SO 3 H) and salts thereof, Ethyl methacrylate sulfonic acid (CH 2 C (CH 3 ) —COO— (CH 2 ) 2 —SO 3 H) and salts thereof, propyl methacrylate methacrylate (CH 2 C (CH 3 ) —COO— (CH 2 ) 3 -SO 3 H) and its salts, methacrylic acid-t-butylsulfate Acid (CH 2 C (CH 3) -COO-C (CH 3) 2 CH 2 -SO 3 H) and its salts, methacrylic acid -n- butyl sulfonic acid (CH 2 C (CH 3) -COO- ( CH 2 ) 4 —SO 3 H) and salts thereof, phenylene sulfonic acid methacrylate (CH 2 C (CH 3 ) —COO—C 6 H 4 —SO 3 H) and salts thereof, naphthalene sulfonic acid methacrylate (CH 2) C (CH 3 ) —COO—C 10 H 8 —SO 3 H) and salts thereof, polyvinyl carboxylic acid, polystyrene carboxylic acid, polyallyl carboxylic acid, polyacryl carboxylic acid, polymethacryl carboxylic acid, poly-2-acrylamide— Examples include 2-methylpropanecarboxylic acid, polyisoprene carboxylic acid, polyacrylic acid and the like. Moreover, the copolymer containing 2 or more types of these may be sufficient.

アニオン基を有さない重合性モノマーとしては、エチレン、プロぺン、1−ブテン、2−ブテン、1−ペンテン、2−ペンテン、1−ヘキセン、2−ヘキセン、スチレン、p−メチルスチレン、p−エチルスチレン、p−ブチルスチレン、2,4,6−トリメチルスチレン、p−メトキシスチレン、α−メチルスチレン、2−ビニルナフタレン、6−メチル−2−ビニルナフタレン、1−ビニルイミダゾール、ビニルピリジン、ビニルアセテート、アクリルアルデヒド、アクリルニトリル、N−ビニル−2−ピロリドン、N−ビニルアセトアミド、N−ビニルホルムアミド、N−ビニルイミダゾ−ル、アクリルアミド、N,N−ジメチルアクリルアミド、アクリル酸、アクリル酸メチル、アクリル酸エチル、アクリル酸プロピル、アクリル酸n−ブチル、アクリル酸i−ブチル、アクリル酸t−ブチル、アクリル酸i−オクチル、アクリル酸イソノニルブチル、アクリル酸ラウリル、アクリル酸アリル、アクリル酸ステアリル、アクリル酸イソボニル、アクリル酸シクロヘキシル、アクリル酸ベンジル、アクリル酸エチルカルビトール、アクリル酸フェノキシエチル、アクリル酸ヒドロキシエチル、アクリル酸メトキシエチル、アクリル酸エトキシエチル、アクリル酸メトキシブチル、メタクリル酸、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸n−ブチル、メタクリル酸i−ブチル、メタクリル酸t−ブチル、メタクリル酸2−エチルヘキシル、メタクリル酸ラウリル、メタクリル酸トリデシル、メタクリル酸ステアリル、メタクリル酸シクロヘキシル、メタクリル酸ベンジル、メタクリル酸2−ヒドロキシエチル、メタクリル酸2−ヒドロキシプロピル、アクリロイルモルホリン、ビニルアミン、N,N−ジメチルビニルアミン、N,N−ジエチルビニルアミン、N,N−ジブチルビニルアミン、N,N−ジ−t−ブチルビニルアミン、N,N−ジフェニルビニルアミン、N−ビニルカルバゾール、ビニルアルコール、塩化ビニル、フッ化ビニル、メチルビニルエーテル、エチルビニルエーテル、シクロプロペン、シクロブテン、シクロペンテン、シクロヘキセン、シクロヘプテン、シクロオクテン、2−メチルシクロヘキセン、ビニルフェノール、1,3−ブタジエン、1−メチル−1,3−ブタジエン、2−メチル−1,3−ブタジエン、1,4−ジメチル−1,3−ブタジエン、1,2−ジメチル−1,3−ブタジエン、1,3−ジメチル−1,3−ブタジエン、1−オクチル−1,3−ブタジエン、2−オクチル−1,3−ブタジエン、1−フェニル−1,3−ブタジエン、2−フェニル−1,3−ブタジエン、1−ヒドロキシ−1,3−ブタジエン、2−ヒドロキシ−1,3−ブタジエン等が挙げられる。
これらアニオン基を有さない重合性モノマーを共重合することで溶媒溶解性をコントロールすることができる。
Examples of the polymerizable monomer having no anionic group include ethylene, propene, 1-butene, 2-butene, 1-pentene, 2-pentene, 1-hexene, 2-hexene, styrene, p-methylstyrene, p. -Ethylstyrene, p-butylstyrene, 2,4,6-trimethylstyrene, p-methoxystyrene, α-methylstyrene, 2-vinylnaphthalene, 6-methyl-2-vinylnaphthalene, 1-vinylimidazole, vinylpyridine, Vinyl acetate, acrylaldehyde, acrylonitrile, N-vinyl-2-pyrrolidone, N-vinylacetamide, N-vinylformamide, N-vinylimidazole, acrylamide, N, N-dimethylacrylamide, acrylic acid, methyl acrylate, Ethyl acrylate, propyl acrylate, acrylic acid -Butyl, i-butyl acrylate, t-butyl acrylate, i-octyl acrylate, isononyl butyl acrylate, lauryl acrylate, allyl acrylate, stearyl acrylate, isobornyl acrylate, cyclohexyl acrylate, benzyl acrylate , Ethyl carbitol acrylate, phenoxyethyl acrylate, hydroxyethyl acrylate, methoxyethyl acrylate, ethoxyethyl acrylate, methoxybutyl acrylate, methacrylic acid, methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, methacryl I-Butyl acid, t-butyl methacrylate, 2-ethylhexyl methacrylate, lauryl methacrylate, tridecyl methacrylate, stearyl methacrylate, cyclohexyl methacrylate, methacrylic acid Benzyl, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, acryloylmorpholine, vinylamine, N, N-dimethylvinylamine, N, N-diethylvinylamine, N, N-dibutylvinylamine, N, N-di -T-butylvinylamine, N, N-diphenylvinylamine, N-vinylcarbazole, vinyl alcohol, vinyl chloride, vinyl fluoride, methyl vinyl ether, ethyl vinyl ether, cyclopropene, cyclobutene, cyclopentene, cyclohexene, cycloheptene, cyclooctene, 2-methylcyclohexene, vinylphenol, 1,3-butadiene, 1-methyl-1,3-butadiene, 2-methyl-1,3-butadiene, 1,4-dimethyl-1,3-butadiene, 1,2- Dimethyl , 3-butadiene, 1,3-dimethyl-1,3-butadiene, 1-octyl-1,3-butadiene, 2-octyl-1,3-butadiene, 1-phenyl-1,3-butadiene, 2-phenyl -1,3-butadiene, 1-hydroxy-1,3-butadiene, 2-hydroxy-1,3-butadiene and the like.
Solvent solubility can be controlled by copolymerizing these polymerizable monomers having no anionic group.

導電性高分子溶液における上記π共役系導電性高分子とポリアニオンとの割合は、ポリアニオン100質量部に対してπ共役系導電性高分子1〜1000質量部であることが好ましい。π共役系導電性高分子が1質量部未満であると、導電性が不足する傾向にあり、1000質量部を超えると溶媒溶解性が不足する傾向にある。   The ratio of the π-conjugated conductive polymer and the polyanion in the conductive polymer solution is preferably 1 to 1000 parts by mass of the π-conjugated conductive polymer with respect to 100 parts by mass of the polyanion. When the π-conjugated conductive polymer is less than 1 part by mass, the conductivity tends to be insufficient, and when it exceeds 1000 parts by mass, the solvent solubility tends to be insufficient.

(ドーパント)
導電性高分子溶液において、ポリアニオンはπ共役系導電性高分子のドーパントとして機能するが、導電性高分子溶液にはポリアニオン以外のドーパント(以下、他のドーパントという。)が含まれていてもよい。
他のドーパントとしては、π共役系導電性高分子を酸化還元させることができればドナー性のものであってもよく、アクセプタ性のものであってもよい。
(Dopant)
In the conductive polymer solution, the polyanion functions as a dopant for the π-conjugated conductive polymer, but the conductive polymer solution may contain a dopant other than the polyanion (hereinafter referred to as other dopant). .
Other dopants may be donor or acceptor as long as the π-conjugated conductive polymer can be oxidized and reduced.

[ドナー性ドーパント]
ドナー性ドーパントとしては、例えば、ナトリウム、カリウム等のアルカリ金属、カルシウム、マグネシウム等のアルカリ土類金属、テトラメチルアンモニウム、テトラエチルアンモニウム、テトラプロピルアンモニウム、テトラブチルアンモニウム、メチルトリエチルアンモニウム、ジメチルジエチルアンモニウム等の4級アミン化合物等が挙げられる。
[Donor dopant]
Examples of the donor dopant include alkali metals such as sodium and potassium, alkaline earth metals such as calcium and magnesium, tetramethylammonium, tetraethylammonium, tetrapropylammonium, tetrabutylammonium, methyltriethylammonium, dimethyldiethylammonium, and the like. A quaternary amine compound etc. are mentioned.

[アクセプタ性ドーパント]
アクセプタ性ドーパントとしては、例えば、ハロゲン化合物、ルイス酸、プロトン酸、有機シアノ化合物、有機金属化合物、フラーレン、水素化フラーレン、水酸化フラーレン、カルボン酸化フラーレン、スルホン酸化フラーレン等を使用できる。
さらに、ハロゲン化合物としては、例えば、塩素(Cl)、臭素(Br2)、ヨウ素(I)、塩化ヨウ素(ICl)、臭化ヨウ素(IBr)、フッ化ヨウ素(IF)等が挙げられる。
ルイス酸としては、例えば、PF、AsF、SbF、BF、BCl、BBr、SO等が挙げられる。
有機シアノ化合物としては、共役結合に二つ以上のシアノ基を含む化合物が使用できる。例えば、テトラシアノエチレン、テトラシアノエチレンオキサイド、テトラシアノベンゼン、ジクロロジシアノベンゾキノン(DDQ)、テトラシアノキノジメタン、テトラシアノアザナフタレン等が挙げられる。
[Acceptor dopant]
As the acceptor dopant, for example, a halogen compound, Lewis acid, proton acid, organic cyano compound, organometallic compound, fullerene, hydrogenated fullerene, hydroxylated fullerene, carboxylated fullerene, sulfonated fullerene, or the like can be used.
Furthermore, examples of the halogen compound include chlorine (Cl 2 ), bromine (Br 2 ), iodine (I 2 ), iodine chloride (ICl), iodine bromide (IBr), and iodine fluoride (IF). .
Examples of the Lewis acid include PF 5 , AsF 5 , SbF 5 , BF 5 , BCl 5 , BBr 5 , SO 3 and the like.
As the organic cyano compound, a compound containing two or more cyano groups in a conjugated bond can be used. Examples include tetracyanoethylene, tetracyanoethylene oxide, tetracyanobenzene, dichlorodicyanobenzoquinone (DDQ), tetracyanoquinodimethane, and tetracyanoazanaphthalene.

プロトン酸としては、無機酸、有機酸が挙げられる。さらに、無機酸としては、例えば、塩酸、硫酸、硝酸、リン酸、ホウフッ化水素酸、フッ化水素酸、過塩素酸等が挙げられる。また、有機酸としては、有機カルボン酸、フェノール類、有機スルホン酸等が挙げられる。   Examples of the protonic acid include inorganic acids and organic acids. Furthermore, examples of the inorganic acid include hydrochloric acid, sulfuric acid, nitric acid, phosphoric acid, borohydrofluoric acid, hydrofluoric acid, and perchloric acid. Examples of organic acids include organic carboxylic acids, phenols, and organic sulfonic acids.

有機カルボン酸としては、脂肪族、芳香族、環状脂肪族等にカルボキシ基を一つ又は二つ以上を含むものを使用できる。例えば、ギ酸、酢酸、シュウ酸、安息香酸、フタル酸、マレイン酸、フマル酸、マロン酸、酒石酸、クエン酸、乳酸、コハク酸、モノクロロ酢酸、ジクロロ酢酸、トリクロロ酢酸、トリフルオロ酢酸、ニトロ酢酸、トリフェニル酢酸等が挙げられる。   As the organic carboxylic acid, aliphatic, aromatic, cycloaliphatic and the like containing one or more carboxy groups can be used. For example, formic acid, acetic acid, oxalic acid, benzoic acid, phthalic acid, maleic acid, fumaric acid, malonic acid, tartaric acid, citric acid, lactic acid, succinic acid, monochloroacetic acid, dichloroacetic acid, trichloroacetic acid, trifluoroacetic acid, nitroacetic acid, And triphenylacetic acid.

有機スルホン酸としては、脂肪族、芳香族、環状脂肪族等にスルホ基を一つ又は二つ以上含むもの、又は、スルホ基を含む高分子を使用できる。
スルホ基を一つ含むものとして、例えば、メタンスルホン酸、エタンスルホン酸、1−プロパンスルホン酸、1−ブタンスルホン酸、1−ヘキサンスルホン酸、1−ヘプタンスルホン酸、1−オクタンスルホン酸、1−ノナンスルホン酸、1−デカンスルホン酸、1−ドデカンスルホン酸、1−テトラデカンスルホン酸、1−ペンタデカンスルホン酸、2−ブロモエタンスルホン酸、3−クロロ−2−ヒドロキシプロパンスルホン酸、トリフルオロメタンスルホン酸、トリフルオロエタンスルホン酸、コリスチンメタンスルホン酸、2−アクリルアミド−2−メチルプロパンスルホン酸、アミノメタンスルホン酸、1−アミノ−2−ナフトール−4−スルホン酸、2−アミノ−5−ナフトール−7−スルホン酸、3−アミノプロパンスルホン酸、N−シクロヘキシル−3−アミノプロパンスルホン酸、ベンゼンスルホン酸、アルキルベンゼンスルホン酸、p−トルエンスルホン酸、キシレンスルホン酸、エチルベンゼンスルホン酸、プロピルベンゼンスルホン酸、ブチルベンゼンスルホン酸、ペンチルベンゼンスルホン酸、ヘキチルベンゼンスルホン酸、ヘプチルベンゼンスルホン酸、オクチルベンゼンスルホン酸、ノニルベンゼンスルホン酸、デシルベンゼンスルホン酸、ウンデシルベンゼンスルホン酸、ドデシルベンゼンスルホン酸、ペンタデシルベンゼンスルホン酸、ヘキサデシルベンゼンスルホン酸、2,4−ジメチルベンゼンスルホン酸、ジプロピルベンゼンスルホン酸、4−アミノベンゼンスルホン酸、o−アミノベンゼンスルホン酸、m−アミノベンゼンスルホン酸、4−アミノ−2−クロロトルエン−5−スルホン酸、4−アミノ−3−メチルベンゼン−1−スルホン酸、4−アミノ−5−メトキシ−2−メチルベンゼンスルホン酸、2−アミノ−5−メチルベンゼン−1−スルホン酸、4−アミノ−2−メチルベンゼン−1−スルホン酸、5−アミノ−2−メチルベンゼン−1−スルホン酸、4−アミノ−3−メチルベンゼン−1−スルホン酸、4−アセトアミド−3−クロロベンゼンスルホン酸、4−クロロ−3−ニトロベンゼンスルホン酸、p−クロロベンゼンスルホン酸、ナフタレンスルホン酸、メチルナフタレンスルホン酸、プロピルナフタレンスルホン酸、ブチルナフタレンスルホン酸、ペンチルナフタレンスルホン酸、4−アミノ−1−ナフタレンスルホン酸、8−クロロナフタレン−1−スルホン酸、ナフタレンスルホン酸ホルマリン重縮合物、メラミンスルホン酸ホルマリン重縮合物、アントラキノンスルホン酸、ピレンスルホン酸等が挙げられる。また、これらの金属塩も使用できる。
As the organic sulfonic acid, aliphatic, aromatic, cycloaliphatic or the like containing one or more sulfo groups, or a polymer containing sulfo groups can be used.
As one containing one sulfo group, for example, methanesulfonic acid, ethanesulfonic acid, 1-propanesulfonic acid, 1-butanesulfonic acid, 1-hexanesulfonic acid, 1-heptanesulfonic acid, 1-octanesulfonic acid, 1 -Nonanesulfonic acid, 1-decanesulfonic acid, 1-dodecanesulfonic acid, 1-tetradecanesulfonic acid, 1-pentadecanesulfonic acid, 2-bromoethanesulfonic acid, 3-chloro-2-hydroxypropanesulfonic acid, trifluoromethanesulfone Acid, trifluoroethanesulfonic acid, colistin methanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, aminomethanesulfonic acid, 1-amino-2-naphthol-4-sulfonic acid, 2-amino-5-naphthol- 7-sulfonic acid, 3-aminopropanesulfone N-cyclohexyl-3-aminopropanesulfonic acid, benzenesulfonic acid, alkylbenzenesulfonic acid, p-toluenesulfonic acid, xylenesulfonic acid, ethylbenzenesulfonic acid, propylbenzenesulfonic acid, butylbenzenesulfonic acid, pentylbenzenesulfonic acid, hex Tylbenzenesulfonic acid, heptylbenzenesulfonic acid, octylbenzenesulfonic acid, nonylbenzenesulfonic acid, decylbenzenesulfonic acid, undecylbenzenesulfonic acid, dodecylbenzenesulfonic acid, pentadecylbenzenesulfonic acid, hexadecylbenzenesulfonic acid, 2, 4-dimethylbenzenesulfonic acid, dipropylbenzenesulfonic acid, 4-aminobenzenesulfonic acid, o-aminobenzenesulfonic acid, m-aminobenzenesulfonic acid 4-amino-2-chlorotoluene-5-sulfonic acid, 4-amino-3-methylbenzene-1-sulfonic acid, 4-amino-5-methoxy-2-methylbenzenesulfonic acid, 2-amino-5-methyl Benzene-1-sulfonic acid, 4-amino-2-methylbenzene-1-sulfonic acid, 5-amino-2-methylbenzene-1-sulfonic acid, 4-amino-3-methylbenzene-1-sulfonic acid, 4 -Acetamide-3-chlorobenzenesulfonic acid, 4-chloro-3-nitrobenzenesulfonic acid, p-chlorobenzenesulfonic acid, naphthalenesulfonic acid, methylnaphthalenesulfonic acid, propylnaphthalenesulfonic acid, butylnaphthalenesulfonic acid, pentylnaphthalenesulfonic acid, 4 -Amino-1-naphthalenesulfonic acid, 8-chloronaphthalene-1- Examples include sulfonic acid, naphthalene sulfonic acid formalin polycondensate, melamine sulfonic acid formalin polycondensate, anthraquinone sulfonic acid, and pyrene sulfonic acid. These metal salts can also be used.

スルホ基を二つ以上含むものとしては、例えば、エタンジスルホン酸、ブタンジスルホン酸、ペンタンジスルホン酸、デカンジスルホン酸、o−ベンゼンジスルホン酸、m−ベンゼンジスルホン酸、p−ベンゼンジスルホン酸、トルエンジスルホン酸、キシレンジスルホン酸、クロロベンゼンジスルホン酸、フルオロベンゼンジスルホン酸、ジメチルベンゼンジスルホン酸、ジエチルベンゼンジスルホン酸、アニリン−2,4−ジスルホン酸、アニリン−2,5−ジスルホン酸、3,4−ジヒドロキシ−1,3−ベンゼンジスルホン酸、ナフタレンジスルホン酸、メチルナフタレンジスルホン酸、エチルナフタレンジスルホン酸、ペンタデシルナフタレンジスルホン酸、3−アミノ−5−ヒドロキシ−2,7−ナフタレンジスルホン酸、1−アセトアミド−8−ヒドロキシ−3,6−ナフタレンジスルホン酸、2−アミノ−1,4−ベンゼンジスルホン酸、1−アミノ−3,8−ナフタレンジスルホン酸、3−アミノ−1,5−ナフタレンジスルホン酸、8−アミノ−1−ナフトール−3,6−ジスルホン酸、4−アミノ−5−ナフトール−2,7−ジスルホン酸、4−アセトアミド−4’−イソチオ−シアノトスチルベン−2,2’−ジスルホン酸、4−アセトアミド−4’−イソチオシアナトスチルベン−2,2’−ジスルホン酸、4−アセトアミド−4’−マレイミジルスチルベン−2,2’−ジスルホン酸、ナフタレントリスルホン酸、ジナフチルメタンジスルホン酸、アントラキノンジスルホン酸、アントラセンスルホン酸等が挙げられる。また、これらの金属塩も使用できる。   Examples of those containing two or more sulfo groups include ethanedisulfonic acid, butanedisulfonic acid, pentanedisulfonic acid, decanedisulfonic acid, o-benzenedisulfonic acid, m-benzenedisulfonic acid, p-benzenedisulfonic acid, and toluenedisulfonic acid. , Xylene disulfonic acid, chlorobenzene disulfonic acid, fluorobenzene disulfonic acid, dimethylbenzene disulfonic acid, diethylbenzene disulfonic acid, aniline-2,4-disulfonic acid, aniline-2,5-disulfonic acid, 3,4-dihydroxy-1,3 Benzene disulfonic acid, naphthalene disulfonic acid, methyl naphthalene disulfonic acid, ethyl naphthalene disulfonic acid, pentadecyl naphthalene disulfonic acid, 3-amino-5-hydroxy-2,7-naphthalene disulfonic acid, 1- Cetamide-8-hydroxy-3,6-naphthalenedisulfonic acid, 2-amino-1,4-benzenedisulfonic acid, 1-amino-3,8-naphthalenedisulfonic acid, 3-amino-1,5-naphthalenedisulfonic acid, 8-Amino-1-naphthol-3,6-disulfonic acid, 4-amino-5-naphthol-2,7-disulfonic acid, 4-acetamido-4'-isothio-cyanotostilbene-2,2'-disulfonic acid 4-acetamido-4′-isothiocyanatostilbene-2,2′-disulfonic acid, 4-acetamido-4′-maleimidylstilbene-2,2′-disulfonic acid, naphthalenetrisulfonic acid, dinaphthylmethanedisulfone An acid, anthraquinone disulfonic acid, anthracene sulfonic acid, etc. are mentioned. These metal salts can also be used.

(溶媒)
導電性高分子溶液に含まれる溶媒としては、溶解性パラメータ(SP値)が10以上のものが好ましい。SP値が10以上のものしては、水や、メタノール、エタノール、エチレングリコール、ジエチレングリコール等のアルコール類、無水コハク酸、無水マレイン酸等の脂肪酸類、N−メチルホルムアミド、メチルアセトアミド、アセトニトリル等の窒素化合物類、炭酸エチレン、炭酸プロピレンが挙げられる。溶媒は1種であってもよいし、2種以上であってもよい。
また、溶媒としては、ポリアニオンおよび前記前駆体モノマーを溶解する共に、酸化剤を溶解して前駆体モノマーの重合が進行するものが特に好ましい。
(solvent)
As a solvent contained in the conductive polymer solution, a solvent having a solubility parameter (SP value) of 10 or more is preferable. SP values of 10 or more include water, alcohols such as methanol, ethanol, ethylene glycol, and diethylene glycol, fatty acids such as succinic anhydride and maleic anhydride, N-methylformamide, methylacetamide, acetonitrile, and the like. Nitrogen compounds, ethylene carbonate, propylene carbonate are mentioned. 1 type may be sufficient as a solvent, and 2 or more types may be sufficient as it.
The solvent is particularly preferably a solvent that dissolves the polyanion and the precursor monomer and dissolves the oxidizing agent to advance the polymerization of the precursor monomer.

(導電性高分子溶液のpH)
導電性高分子溶液は、25℃におけるpHが5〜13、好ましくは7〜11になるように調整されたものである。pHが5未満であると、金属腐食や接触物の変色を防止できず、13を超えるとポリアニオンが脱ドープして、導電性が不足する。
pHを調整する方法としては、例えば、π共役系導電性高分子とポリアニオンとの複合体の水溶液(以下、複合体水溶液という。)にアルカリを混合して塩を形成させる方法、酸基をエステル化する方法、酸基をアミド化する方法などが挙げられる。
(PH of conductive polymer solution)
The conductive polymer solution is adjusted so that the pH at 25 ° C. is 5 to 13, preferably 7 to 11. If the pH is less than 5, metal corrosion or discoloration of the contact cannot be prevented, and if it exceeds 13, the polyanion is dedoped and the conductivity is insufficient.
Examples of methods for adjusting the pH include a method of forming a salt by mixing an alkali with an aqueous solution of a complex of a π-conjugated conductive polymer and a polyanion (hereinafter referred to as an aqueous complex solution), and an acid group as an ester. And a method of amidating an acid group.

アルカリを混合する場合のアルカリとしては特に限定されず、公知の無機アルカリや有機アルカリを使用できる。無機アルカリとしては、例えば、水酸化ナトリウム、水酸化カリウム、水酸化カルシウム、アンモニアなどが挙げられる。また、有機アルカリとしては、例えば、エチルアミン、ジエチルアミン、メチルエチルアミン、トリエチルアミンのような脂肪族アミン、アニリン、ベンジルアミン、ピロール、イミダゾール、ピリジンのような芳香族アミンもしくはこれらの誘導体、ピロール、ナトリウムメトキシド、ナトリウムエトキシド等のナトリウムアルコキシド、カリウムアルコキシド、カルシウムアルコキシド等の金属アルコキシドなどが挙げられる。
これらの中でも、弱塩基の脂肪族アミン、芳香族アミン、金属アルコキシドが好ましい。
The alkali in the case of mixing the alkali is not particularly limited, and a known inorganic alkali or organic alkali can be used. Examples of the inorganic alkali include sodium hydroxide, potassium hydroxide, calcium hydroxide, ammonia and the like. Examples of the organic alkali include aliphatic amines such as ethylamine, diethylamine, methylethylamine, and triethylamine, aromatic amines such as aniline, benzylamine, pyrrole, imidazole, and pyridine, or derivatives thereof, pyrrole, sodium methoxide, and the like. And metal alkoxides such as sodium alkoxide such as sodium ethoxide, potassium alkoxide and calcium alkoxide.
Among these, weakly basic aliphatic amines, aromatic amines, and metal alkoxides are preferable.

さらに、有機アルカリとして、窒素含有芳香族性環式化合物を好適に用いることができる。窒素含有芳香族性環式化合物は、ポリアニオンの脱ドープを防止できるだけでなく、導電性を向上させることもできる。
ここで、窒素含有芳香族性環式化合物とは、少なくとも1個以上の窒素原子を含む芳香族性環を有し、芳香族性環中の窒素原子が芳香性環中の他の原子と共役関係を持つものである。共役関係となるためには、窒素原子と他の原子とが不飽和結合を形成している。あるいは、窒素原子が直接的に他の原子と不飽和結合を形成していなくても、不飽和結合を形成している他の原子に隣接していればよい。窒素原子上に存在している非共有電子対が、他の原子同士で形成されている不飽和結合と擬似的な共役関係を構成できるからである。
窒素含有芳香族性環式化合物においては、他の原子と共役関係を有する窒素原子と、不飽和結合を形成している他の原子に隣接している窒素原子を共に有することが好ましい。
Furthermore, a nitrogen-containing aromatic cyclic compound can be suitably used as the organic alkali. The nitrogen-containing aromatic cyclic compound can not only prevent de-doping of the polyanion, but can also improve conductivity.
Here, the nitrogen-containing aromatic cyclic compound has an aromatic ring containing at least one nitrogen atom, and the nitrogen atom in the aromatic ring is conjugated with other atoms in the aromatic ring. It has a relationship. In order to become a conjugated relationship, the nitrogen atom and other atoms form an unsaturated bond. Alternatively, even if the nitrogen atom does not directly form an unsaturated bond with another atom, it may be adjacent to the other atom that forms the unsaturated bond. This is because an unshared electron pair existing on a nitrogen atom can form a pseudo conjugate relationship with an unsaturated bond formed between other atoms.
The nitrogen-containing aromatic cyclic compound preferably has both a nitrogen atom having a conjugated relationship with another atom and a nitrogen atom adjacent to the other atom forming the unsaturated bond.

このような窒素含有芳香族性環式化合物としては、例えば、一つの窒素原子を含有するピリジン類及びその誘導体、二つの窒素原子を含有するイミダゾール類及びその誘導体、ピリミジン類及びその誘導体、ピラジン類及びその誘導体、三つの窒素原子を含有するトリアジン類及びその誘導体等が挙げられる。溶媒溶解性等の観点からは、ピリジン類及びその誘導体、イミダゾール類及びその誘導体、ピリミジン類及びその誘導体が好ましい。
また、窒素含有芳香族性環式化合物は、アルキル基、ヒドロキシ基、カルボキシ基、シアノ基、フェニル基、フェノール基、エステル基、アルコキシ基、カルボニル基等の置換基が環に導入されたものでもよいし、導入されていないものでもよい。また、環は多環であってもよい。
Examples of such nitrogen-containing aromatic cyclic compounds include pyridines and derivatives thereof containing one nitrogen atom, imidazoles and derivatives thereof containing two nitrogen atoms, pyrimidines and derivatives thereof, and pyrazines. And derivatives thereof, triazines containing three nitrogen atoms, and derivatives thereof. From the viewpoint of solvent solubility and the like, pyridines and derivatives thereof, imidazoles and derivatives thereof, and pyrimidines and derivatives thereof are preferable.
Further, the nitrogen-containing aromatic cyclic compound may be one in which a substituent such as an alkyl group, a hydroxy group, a carboxy group, a cyano group, a phenyl group, a phenol group, an ester group, an alkoxy group, or a carbonyl group is introduced into the ring. It may be good or not introduced. The ring may be polycyclic.

置換基のうち、アルキル基としては、メチル、エチル、プロピル、ブチル、イソブチル、t−ブチル、ペンチル、ヘキシル、オクチル、デシル、ドデシル等のアルキル基、シクロプロピル、シクロペンチル、シクロヘキシル等のシクロアルキル基が挙げられる。中でも、有機溶剤への溶解性、樹脂への分散性、立体障害等を考慮すると、炭素数1〜12のアルキル基が好ましい。
ヒドロキシ基としては、ヒドロキシ、メチレンヒドロキシ、エチレンヒドロキシ、トリメチレンヒドロキシ、テトラメチレンヒドロキシ、ペンタメチレンヒドロキシ、ヘキサメチレンヒドロキシ、ヘプタメチレンヒドロキシ、プロピレンヒドロキシ、ブチレンヒドロキシ、エチルメチレンヒドロキシ等のアルキレンヒドロキシ基、プロペニレンヒドロキシ、ブテニレンヒドロキシ、ペンテニレンヒドロキシ等のアルケニレンヒドロキシ基が挙げられる。
カルボキシ基としては、カルボキシ、メチレンカルボキシ、エチレンカルボキシ、トリメチレンカルボキシ、プロピレンカルボキシ、テトラメチレンカルボキシ、ペンタメチレンカルボキシ、ヘキサメチレンカルボキシ、ヘプタメチレカルボキシ、エチルメチレンカルボキシ、フェニルエチレンカルボキシ等のアルキレンカルボキシ、イソプレンカルボキシ、プロペニレンカルボキシ、ブテニレンカルボキシ、ペンテニレンカルボキシ等のアルケニレンカルボキシ基が挙げられる。
Among the substituents, the alkyl group includes alkyl groups such as methyl, ethyl, propyl, butyl, isobutyl, t-butyl, pentyl, hexyl, octyl, decyl, and dodecyl, and cycloalkyl groups such as cyclopropyl, cyclopentyl, and cyclohexyl. Can be mentioned. Among these, in view of solubility in an organic solvent, dispersibility in a resin, steric hindrance, and the like, an alkyl group having 1 to 12 carbon atoms is preferable.
Examples of the hydroxy group include hydroxy, methylene hydroxy, ethylene hydroxy, trimethylene hydroxy, tetramethylene hydroxy, pentamethylene hydroxy, hexamethylene hydroxy, heptamethylene hydroxy, propylene hydroxy, butylene hydroxy, ethylmethylene hydroxy and other alkylene hydroxy groups, propenylene Alkenylene hydroxy groups such as hydroxy, butenylene hydroxy, pentenylene hydroxy and the like can be mentioned.
Examples of the carboxy group include carboxy, methylene carboxy, ethylene carboxy, trimethylene carboxy, propylene carboxy, tetramethylene carboxy, pentamethylene carboxy, hexamethylene carboxy, heptamethyl carboxy, ethyl methylene carboxy, phenylethylene carboxy, etc. And alkenylene carboxy groups such as propenylene carboxy, butenylene carboxy, and pentenylene carboxy.

シアノ基としては、シアノ、メチレンシアノ、エチレンシアノ、トリメチレンシアノ、テトラメチレンシアノ、ペンタメチレンシアノ、ヘキサメチレンシアノ、ヘプタメチレンシアノ、プロピレンシアノ、ブチレンシアノ、エチルメチレンシアノ等のアルキレンシアノ基、プロペニレンシアノ、ブテニレンシアノ、ペンテニレンシアノ等のアルケニレンシアノ基が挙げられる。
フェノール基としては、フェノール、メチルフェノール、エチルフェノール、ブチルフェノール等のアルキルフェノール基、メチレンフェノール、エチレンフェノール、トリメチレンフェノール、テトラメチレンフェノール、ペンタメチレンフェノール、ヘキサメチレンフェノール等のアルキレンフェノール基等が挙げられる。
フェニル基としては、フェニル、メチルフェニル、ブチルフェニル、オクチルフェニル、ジメチルフェニル、等のアルキルフェニル基と、メチレンフェニル、エチレンフェニル、トリメチレンフェニル、テトラメチレンフェニル、ペンタメチレンフェニル、ヘキサメチレンフェニル、ヘプタメチレンフェニル等のアルキレンフェニル基と、プロペニレンフェニル、ブテニレンフェニル、ペンテニレンフェニル等のアルケニレンフェニル等が挙げられる。
アルコキシ基としては、メトキシ、エトキシ、ブトキシ、フェノキシ等が挙げられる。
Examples of the cyano group include alkylene cyano groups such as cyano, methylene cyano, ethylene cyano, trimethylene cyano, tetramethylene cyano, pentamethylene cyano, hexamethylene cyano, heptamethylene cyano, propylene cyano, butylene cyano, ethyl methylene cyano, and propenylene. Examples include alkenylene cyano groups such as cyano, butenylene cyano, and pentenylene cyano.
Examples of the phenol group include alkylphenol groups such as phenol, methylphenol, ethylphenol and butylphenol, and alkylenephenol groups such as methylenephenol, ethylenephenol, trimethylenephenol, tetramethylenephenol, pentamethylenephenol and hexamethylenephenol.
Examples of the phenyl group include alkylphenyl groups such as phenyl, methylphenyl, butylphenyl, octylphenyl, and dimethylphenyl, and methylenephenyl, ethylenephenyl, trimethylenephenyl, tetramethylenephenyl, pentamethylenephenyl, hexamethylenephenyl, and heptamethylene. Examples thereof include alkylenephenyl groups such as phenyl, and alkenylenephenyls such as propenylenephenyl, butenylenephenyl, and pentenylenephenyl.
Examples of the alkoxy group include methoxy, ethoxy, butoxy, phenoxy and the like.

ピリジン類及びその誘導体の具体的な例としては、ピリジン、2−メチルピリジン、3−メチルピリジン、4−メチルピリジン、4−エチルピリジン、2,4−ジメチルピリジン、2,4,6−トリメチルピリジン、3−シアノ−5−メチルピリジン、2−ピリジンカルボン酸、6−メチル−2−ピリジンカルボン酸、2,6−ピリジン−ジカルボン酸、4−ピリジンカルボキシアルデヒド、4−アミノピリジン、2,3−ジアミノピリジン、2,6−ジアミノピリジン、2,6−ジアミノ−4−メチルピリジン、4−ヒドロキシピリジン、2,6−ジヒドロキシピリジン、6−ヒドロキシニコチン酸メチル、2−ヒドロキシ−5−ピリジンメタノール、6−ヒドロキシニコチン酸エチル、4−ピリジンメタノール、4−ピリジンエタノール、2−フェニルピリジン、3−メチルキノリン、3−エチルキノリン、キノリノール、2,3−シクロペンテノピリジン、2,3−シクロヘキサノピリジン、1,2−ジ(4−ピリジル)エタン、1,2−ジ(4−ピリジル)プロパン、2−ピリジンカルボキシアルデヒド、2−ピリジンカルボン酸、2−ピリジンカルボニトリル、2,3−ピリジンジカルボン酸、2,4−ピリジンジカルボン酸、2,5−ピリジンジカルボン酸、2,6−ピリジンジカルボン酸、3−ピリジンスルホン酸等が挙げられる。   Specific examples of pyridines and derivatives thereof include pyridine, 2-methylpyridine, 3-methylpyridine, 4-methylpyridine, 4-ethylpyridine, 2,4-dimethylpyridine, 2,4,6-trimethylpyridine. , 3-cyano-5-methylpyridine, 2-pyridinecarboxylic acid, 6-methyl-2-pyridinecarboxylic acid, 2,6-pyridine-dicarboxylic acid, 4-pyridinecarboxaldehyde, 4-aminopyridine, 2,3- Diaminopyridine, 2,6-diaminopyridine, 2,6-diamino-4-methylpyridine, 4-hydroxypyridine, 2,6-dihydroxypyridine, methyl 6-hydroxynicotinate, 2-hydroxy-5-pyridinemethanol, 6 -Ethyl hydroxynicotinate, 4-pyridinemethanol, 4-pyridineethanol, 2-phenylpyridine, 3-methylquinoline, 3-ethylquinoline, quinolinol, 2,3-cyclopentenopyridine, 2,3-cyclohexanopyridine, 1,2-di (4-pyridyl) ethane, 1,2- Di (4-pyridyl) propane, 2-pyridinecarboxaldehyde, 2-pyridinecarboxylic acid, 2-pyridinecarbonitrile, 2,3-pyridinedicarboxylic acid, 2,4-pyridinedicarboxylic acid, 2,5-pyridinedicarboxylic acid, Examples include 2,6-pyridinedicarboxylic acid and 3-pyridinesulfonic acid.

イミダゾール類及びその誘導体の具体的な例としては、イミダゾール、2−メチルイミダゾール、2−プロピルイミダゾール、2−ウンデジルイミダゾール、2−フェニルイミダゾール、N−メチルイミダゾール、1−(2−ヒドロキシエチル)イミダゾール、2−エチル−4−メチルイミダゾール、1,2−ジメチルイミダゾール、1−ベンジル−2−メチルイミダゾール、1−ベンジル−2−フェニルイミダゾール、1−シアノエチル−2−メチルイミダゾール、1−シアノエチル−2−エチル−4−メチルイミダゾール、2−フェニル−4,5−ジヒドロキシメチルイミダゾール、1−アセチルイミダゾール、4,5−イミダゾールジカルボン酸、4,5−イミダゾールジカルボン酸ジメチル、ベンズイミダゾール、2−アミノべンズイミダゾール、2−アミノべンズイミダゾール−2−スルホン酸、2−アミノ−1−メチルべンズイミダゾール、2−ヒドロキシべンズイミダゾール、2−(2−ピリジル)べンズイミダゾール等が挙げられる。   Specific examples of imidazoles and derivatives thereof include imidazole, 2-methylimidazole, 2-propylimidazole, 2-undecylimidazole, 2-phenylimidazole, N-methylimidazole, 1- (2-hydroxyethyl) imidazole. 2-ethyl-4-methylimidazole, 1,2-dimethylimidazole, 1-benzyl-2-methylimidazole, 1-benzyl-2-phenylimidazole, 1-cyanoethyl-2-methylimidazole, 1-cyanoethyl-2- Ethyl-4-methylimidazole, 2-phenyl-4,5-dihydroxymethylimidazole, 1-acetylimidazole, 4,5-imidazole dicarboxylic acid, dimethyl 4,5-imidazole dicarboxylate, benzimidazole, 2-aminobenz Imidazole, 2-amino-base lens imidazole-2-sulfonic acid, 2-amino-1-methyl-base lens imidazole, 2-hydroxy-base lens imidazole, 2- (2-pyridyl) base lens and imidazole.

ピリミジン類及びその誘導体の具体的な例としては、2−アミノ−4−クロロ−6−メチルピリミジン、2−アミノ−6−クロロ−4−メトキシピリミジン、2−アミノ−4,6−ジクロロピリミジン、2−アミノ−4,6−ジヒドロキシピリミジン、2−アミノ−4,6−ジメチルピリミジン、2−アミノ−4,6−ジメトキシピリミジン、2−アミノピリミジン、2−アミノ−4−メチルピリミジン、4,6−ジヒドロキシピリミジン、2,4−ジヒドロキシピリミジン−5−カルボン酸、2,4,6−トリアミノピリミジン、2,4−ジメトキシピリミジン、2,4,5−トリヒドロキシピリミジン、2,4−ピリミジンジオール等が挙げられる。   Specific examples of pyrimidines and derivatives thereof include 2-amino-4-chloro-6-methylpyrimidine, 2-amino-6-chloro-4-methoxypyrimidine, 2-amino-4,6-dichloropyrimidine, 2-amino-4,6-dihydroxypyrimidine, 2-amino-4,6-dimethylpyrimidine, 2-amino-4,6-dimethoxypyrimidine, 2-aminopyrimidine, 2-amino-4-methylpyrimidine, 4,6 -Dihydroxypyrimidine, 2,4-dihydroxypyrimidine-5-carboxylic acid, 2,4,6-triaminopyrimidine, 2,4-dimethoxypyrimidine, 2,4,5-trihydroxypyrimidine, 2,4-pyrimidinediol, etc. Is mentioned.

ピラジン類及びその誘導体の具体的な例としては、ピラジン、2−メチルピラジン、2,5−ジメチルピラジン、ピラジンカルボン酸、2,3−ピラジンジカルボン酸、5−メチルピラジンカルボン酸、ピラジンアミド、5−メチルピラジンアミド、2−シアノピラジン、アミノピラジン、3−アミノピラジン−2−カルボン酸、2−エチル−3−メチルピラジン、2−エチル−3−メチルピラジン、2,3−ジメチルピラジン、2,3−ジエチルピラジン等が挙げられる。   Specific examples of the pyrazines and derivatives thereof include pyrazine, 2-methylpyrazine, 2,5-dimethylpyrazine, pyrazinecarboxylic acid, 2,3-pyrazinedicarboxylic acid, 5-methylpyrazinecarboxylic acid, pyrazineamide, 5 -Methylpyrazineamide, 2-cyanopyrazine, aminopyrazine, 3-aminopyrazine-2-carboxylic acid, 2-ethyl-3-methylpyrazine, 2-ethyl-3-methylpyrazine, 2,3-dimethylpyrazine, 2, Examples include 3-diethylpyrazine.

トリアジン類及びその誘導体の具体的な例としては、1,3,5−トリアジン、2−アミノ−1,3,5−トリアジン、3−アミノ−1,2,4−トリアジン、2,4−ジアミノ−6−フェニル−1,3,5−トリアジン、2,4,6−トリアミノ−1,3,5−トリアジン、2,4,6−トリス(トリフルオロメチル)−1,3,5−トリアジン、2,4,6−トリ−2−ピリジン−1,3,5−トリアジン、3−(2−ピリジン)−5,6−ビス(4−フェニルスルホン酸)−1,2,4―トリアジン二ナトリウム、3−(2−ピリジン)−5,6−ジフェニル−1,2,4−トリアジン、3−(2−ピリジン)−5,6−ジフェニル−1,2,4―トリアジン−ρ,ρ’−ジスルホン酸二ナトリウム、2−ヒドロキシ−4,6−ジクロロ−1,3,5−トリアジン等が挙げられる。   Specific examples of triazines and derivatives thereof include 1,3,5-triazine, 2-amino-1,3,5-triazine, 3-amino-1,2,4-triazine, and 2,4-diamino. -6-phenyl-1,3,5-triazine, 2,4,6-triamino-1,3,5-triazine, 2,4,6-tris (trifluoromethyl) -1,3,5-triazine, 2,4,6-tri-2-pyridine-1,3,5-triazine, 3- (2-pyridine) -5,6-bis (4-phenylsulfonic acid) -1,2,4-triazine disodium 3- (2-pyridine) -5,6-diphenyl-1,2,4-triazine, 3- (2-pyridine) -5,6-diphenyl-1,2,4-triazine-ρ, ρ′- Disodium disulphonate, 2-hydroxy-4,6-dichloro -1,3,5-triazine and the like.

窒素含有芳香族性環式化合物における窒素原子には非共有電子対が存在しているため、窒素原子上には置換基又はプロトンが配位又は結合されやすい。窒素原子上に置換基又はプロトンが配位又は結合された場合には、窒素原子上にカチオン電荷を帯びる傾向がある。ここで、窒素原子と他の原子とは共役関係を有しているため、窒素原子上に置換基又はプロトンが配位又は結合されたことによって生じたカチオン電荷は窒素含有芳香族性環中に拡散されて、安定した形で存在するようになる。
このようなことから、窒素含有芳香族性環式化合物は、窒素原子に置換基が導入されて窒素含有芳香族性環式化合物カチオンを形成していてもよい。さらに、そのカチオンとアニオンとが組み合わされて塩が形成されていてもよい。塩であっても、カチオンでない窒素含有芳香族性環式化合物と同様の効果を発揮する。
Since a non-shared electron pair exists in the nitrogen atom in the nitrogen-containing aromatic cyclic compound, a substituent or a proton is easily coordinated or bonded on the nitrogen atom. When a substituent or proton is coordinated or bonded to a nitrogen atom, it tends to have a cationic charge on the nitrogen atom. Here, since the nitrogen atom and other atoms have a conjugated relationship, the cation charge generated by the coordination or bonding of a substituent or a proton on the nitrogen atom is contained in the nitrogen-containing aromatic ring. Once diffused, it will exist in a stable form.
For this reason, in the nitrogen-containing aromatic cyclic compound, a substituent may be introduced into the nitrogen atom to form a nitrogen-containing aromatic cyclic compound cation. Further, a salt may be formed by combining the cation and the anion. Even if it is a salt, the same effect as a nitrogen-containing aromatic cyclic compound which is not a cation is exhibited.

窒素含有芳香族性環式化合物の窒素原子に導入される置換基としては、水素、アルキル基、ヒドロキシ基、カルボキシ基、シアノ基、フェニル基、フェノール基、エステル基、アルコキシ基、カルボニル基等が挙げられる。
アルキル基としては、メチル、エチル、プロピル、ブチル、イソブチル、t−ブチル、ペンチル、ヘキシル、オクチル、デシル、ドデシル等のアルキル基と、シクロプロピル、シクロペンチル及びシクロヘキシル等のシクロアルキル基が挙げられる。有機溶剤への溶解性、樹脂への分散性、立体障害等を考慮すると、炭素数1〜12のアルキル基がより好ましい。
ヒドロキシ基としては、ヒドロキシ、メチレンヒドロキシ、エチレンヒドロキシ、トリメチレンヒドロキシ、テトラメチレンヒドロキシ、ペンタメチレンヒドロキシ、ヘキサメチレンヒドロキシ、ヘプタメチレンヒドロキシ、プロピレンヒドロキシ、ブチレンヒドロキシ、エチルメチレンヒドロキシ等のアルキレンヒドロキシ基、プロペニレンヒドロキシ、ブテニレンヒドロキシ、ペンテニレンヒドロキシ等のアルケニレンヒドロキシ基が挙げられる。
カルボキシ基としては、カルボキシ、メチレンカルボキシ、エチレンカルボキシ、トリメチレンカルボキシ、プロピレンカルボキシ、テトラメチレンカルボキシ、ペンタメチレンカルボキシ、ヘキサメチレンカルボキシ、ヘプタメチレンカルボキシ、エチルメチレンカルボキシ、フェニルエチレンカルボキシ等のアルキレンカルボキシ基、イソプレンカルボキシ、プロペニレンカルボキシ、ブテニレンカルボキシ、ペンテニレンカルボキシ等のアルケニレンカルボキシ基が挙げられる。
Examples of the substituent introduced into the nitrogen atom of the nitrogen-containing aromatic cyclic compound include hydrogen, alkyl group, hydroxy group, carboxy group, cyano group, phenyl group, phenol group, ester group, alkoxy group, carbonyl group and the like. Can be mentioned.
Examples of the alkyl group include alkyl groups such as methyl, ethyl, propyl, butyl, isobutyl, t-butyl, pentyl, hexyl, octyl, decyl, and dodecyl, and cycloalkyl groups such as cyclopropyl, cyclopentyl, and cyclohexyl. In consideration of solubility in an organic solvent, dispersibility in a resin, steric hindrance, and the like, an alkyl group having 1 to 12 carbon atoms is more preferable.
Examples of the hydroxy group include hydroxy, methylene hydroxy, ethylene hydroxy, trimethylene hydroxy, tetramethylene hydroxy, pentamethylene hydroxy, hexamethylene hydroxy, heptamethylene hydroxy, propylene hydroxy, butylene hydroxy, ethylmethylene hydroxy and other alkylene hydroxy groups, propenylene Alkenylene hydroxy groups such as hydroxy, butenylene hydroxy, pentenylene hydroxy and the like can be mentioned.
Examples of the carboxy group include carboxy, methylene carboxy, ethylene carboxy, trimethylene carboxy, propylene carboxy, tetramethylene carboxy, pentamethylene carboxy, hexamethylene carboxy, heptamethylene carboxy, ethyl methylene carboxy, phenyl ethylene carboxy and the like, isoprene Alkenylene carboxy groups such as carboxy, propenylene carboxy, butenylene carboxy, pentenylene carboxy and the like can be mentioned.

シアノ基としては、シアノ、メチレンシアノ、エチレンシアノ、トリメチレンシアノ、テトラメチレンシアノ、ペンタメチレンシアノ、ヘキサメチレンシアノ、ヘプタメチレンシアノ、プロピレンシアノ、ブチレンシアノ、エチルメチレンシアノ等のアルキレンシアノ基と、プロペニレンシアノ、ブテニレンシアノ、ペンテニレンシアノ等のアルケニレンシアノ基が挙げられる。
フェノール基としては、フェノール、メチルフェノール、エチルフェノール、ブチルフェノール等のアルキルフェノール基と、メチレンフェノール、エチレンフェノール、トリメチレンフェノール、テトラメチレンフェノール、ペンタメチレンフェノール、ヘキサメチレンフェノール等のアルキレンフェノール基等が挙げられる。
フェニル基としては、フェニル、メチルフェニル、ブチルフェニル、オクチルフェニル、ジメチルフェニル等のアルキルフェニル基、メチレンフェニル、エチレンフェニル、トリメチレンフェニル、テトラメチレンフェニル、ペンタメチレンフェニル、ヘキサメチレンフェニル、ヘプタメチレンフェニル等のアルキレンフェニル基、プロペニレンフェニル、ブテニレンフェニル、ペンテニレンフェニル等のアルケニレンフェニル等が挙げられる。
アルコキシ基としては、メトキシ、エトキシ、ブトキシ、フェノキシ等が挙げられる。
Examples of the cyano group include alkylene cyano groups such as cyano, methylene cyano, ethylene cyano, trimethylene cyano, tetramethylene cyano, pentamethylene cyano, hexamethylene cyano, heptamethylene cyano, propylene cyano, butylene cyano, ethyl methylene cyano, and propylene. Alkenylene cyano groups such as nylene cyano, butenylene cyano, pentenylene cyano and the like can be mentioned.
Examples of the phenol group include alkylphenol groups such as phenol, methylphenol, ethylphenol, and butylphenol, and alkylenephenol groups such as methylenephenol, ethylenephenol, trimethylenephenol, tetramethylenephenol, pentamethylenephenol, and hexamethylenephenol. .
Examples of the phenyl group include alkylphenyl groups such as phenyl, methylphenyl, butylphenyl, octylphenyl, dimethylphenyl, methylenephenyl, ethylenephenyl, trimethylenephenyl, tetramethylenephenyl, pentamethylenephenyl, hexamethylenephenyl, heptamethylenephenyl, etc. And alkenylene phenyl such as propenylene phenyl, butenylene phenyl, and pentenylene phenyl.
Examples of the alkoxy group include methoxy, ethoxy, butoxy, phenoxy and the like.

酸基をエステル化またはアミド化する方法としては、複合体水溶液に酸基とエステル結合を形成する官能基を有する化合物(分子内に水酸基を有する化合物、分子内にグリシジル基を有する化合物)またはアミド結合を形成する官能基を有する化合物(分子内にグリシジル基を有する化合物)を添加し、反応させる方法が挙げられる。
分子内に水酸基を有する化合物としては、例えば、メタノール、エタノール、プロパノール、トリクロロエタノール、トリフルオロエタノール、ヒドロキシエチルアクリレート、ヒドロキシエチルアクリルアミド等の脂肪族アルコール類、ベンジルアルコール、フェノール、ヒドロキノン、ピロガロール、レゾルシノール、ピロカテコール等の芳香族アルコール類やフェノール性水酸基含有化合物、エタノールアミン、ジエタノールアミン、トリエタノールアミンなどのアミノアルコール類などが挙げられる。
分子内にグリシジル基を有する化合物としては、例えば、エチルグリシジルエーテル、ブチルグリシジルエーテル、t−ブチルグリシジルエーテル、アリルグリシジルエーテル、ベンジルグリシジルエーテル、グリシジルフェニルエーテル、ビスフェノールA、ジグリシジルエーテル、メタクリル酸グリシジルエーテル等のグリシジル化合物などが挙げられる。
分子内にアミノ基を有する化合物としては、例えば、前記アミノアルコール類、エチルアミン、アニリン、ベンジルアミン等のアミン化合物などが挙げられる。
As a method of esterifying or amidating an acid group, a compound having a functional group that forms an ester bond with an acid group in a complex aqueous solution (a compound having a hydroxyl group in the molecule, a compound having a glycidyl group in the molecule) or an amide Examples include a method in which a compound having a functional group that forms a bond (a compound having a glycidyl group in the molecule) is added and reacted.
Examples of the compound having a hydroxyl group in the molecule include aliphatic alcohols such as methanol, ethanol, propanol, trichloroethanol, trifluoroethanol, hydroxyethyl acrylate, and hydroxyethyl acrylamide, benzyl alcohol, phenol, hydroquinone, pyrogallol, resorcinol, Aromatic alcohols such as pyrocatechol, phenolic hydroxyl group-containing compounds, amino alcohols such as ethanolamine, diethanolamine, and triethanolamine can be used.
Examples of the compound having a glycidyl group in the molecule include ethyl glycidyl ether, butyl glycidyl ether, t-butyl glycidyl ether, allyl glycidyl ether, benzyl glycidyl ether, glycidyl phenyl ether, bisphenol A, diglycidyl ether, and glycidyl methacrylate methacrylate. And the like.
Examples of the compound having an amino group in the molecule include amine compounds such as the aforementioned amino alcohols, ethylamine, aniline, and benzylamine.

これらのうち、π共役系導電性高分子の導電性を向上させることができることから、脂肪族アルコールまたはフェノール性水酸基含有化合物が好ましい。さらに、フェノール性水酸基含有化合物は、酸化防止機能を有するため、耐熱性および長期安定性を向上させることもできるため、特に好ましい。また、ヒドロキシエチルアクリルアミドやヒドロキシエチルアクリレートのようなアクリル基を有する化合物は、光または開始剤を併用することにより、π共役系導電性高分子を架橋させることができ、熱特性、力学特性を向上させることができる点で好ましい。   Among these, an aliphatic alcohol or a phenolic hydroxyl group-containing compound is preferable because the conductivity of the π-conjugated conductive polymer can be improved. Furthermore, a phenolic hydroxyl group-containing compound is particularly preferable because it has an antioxidant function and can improve heat resistance and long-term stability. In addition, compounds with acrylic groups such as hydroxyethyl acrylamide and hydroxyethyl acrylate can crosslink π-conjugated conductive polymers when used in combination with light or initiator, improving thermal and mechanical properties. It is preferable at the point which can be made.

(導電性高分子溶液の製造方法)
導電性高分子溶液の製造方法としては、例えば、まず、ポリアニオンを水または溶媒に溶解し、これにより得られた溶液にπ共役系導電性高分子の前駆体モノマーおよび必要に応じてドーパントを添加し、充分に攪拌混合した後、酸化剤を滴下して前駆体モノマーを重合させる。得られたπ共役系導電性高分子はポリアニオンと複合体を形成して、溶媒溶解性を持ったものとなる。
次いで、重合終了後、酸化剤、残留モノマー、副生成物を除去、精製し、25℃におけるpHが5〜13になるように上記の調整方法により調整して導電性高分子溶液を得る。
(Method for producing conductive polymer solution)
As a method for producing a conductive polymer solution, for example, first, a polyanion is dissolved in water or a solvent, and a precursor monomer of a π-conjugated conductive polymer and, if necessary, a dopant are added to the resulting solution. Then, after sufficiently stirring and mixing, an oxidizing agent is dropped to polymerize the precursor monomer. The obtained π-conjugated conductive polymer forms a complex with the polyanion and has solvent solubility.
Next, after the polymerization is completed, the oxidizing agent, residual monomers, and by-products are removed and purified, and the conductive polymer solution is obtained by adjusting by the above adjusting method so that the pH at 25 ° C. is 5 to 13.

上述した導電性高分子溶液では、pHが5〜13に調整されているため、酸性が弱く、金属と接触した際の腐食を防止し、また、接触物と接触した際の変色を防止できる。また、ポリアニオンはπ共役系導電性高分子に充分にドープしているため、導電性は確保されている。   In the conductive polymer solution described above, since the pH is adjusted to 5 to 13, the acidity is weak, corrosion when contacting with a metal can be prevented, and discoloration when contacting with a contact object can be prevented. Further, since the polyanion is sufficiently doped into the π-conjugated conductive polymer, conductivity is ensured.

<導電性塗膜>
本発明の導電性塗膜は、上述した導電性高分子塗料が塗布されて形成されたものである。導電性高分子塗料の塗布方法としては、例えば、浸漬、コンマコート、スプレーコート、ロールコート、グラビア印刷などが挙げられる。
この導電性塗膜は、具体的には、電子部品、帯電防止コーティング、帯電防止包装材などの帯電防止材、液晶画面やプラズマディスプレイ画面の電磁波シールド材、転写ベルト、現像ロール、帯電ロール、転写ロールなどの電子写真機器部品、CD、DVDなどの光情報記録媒体の表面などに形成される。
特に、酸に弱い電子部品や包装材に形成した場合には、本発明の効果がとりわけ発揮される。すなわち、電子部品上に導電性塗膜を形成しても電子部品を構成する金属や金属化合物の腐食を防止できる。具体的には、アルミニウムやタンタルなどの弁金属からなる陽極と前記弁金属を電解酸化して得られる酸化物からなる誘電体層とを有する機能性コンデンサにおいて、誘電体層上に本発明の導電性塗膜を陰極として形成することにより、誘電体層の腐食を防止できる。したがって、コンデンサの漏れ電流を小さくできる。また、包装プラスチックフィルム上に本発明の導電性塗膜を形成した場合には、それにより包装(接触)されるものの変色を防止できる。
<Conductive coating film>
The conductive coating film of the present invention is formed by applying the above-described conductive polymer paint. Examples of the method for applying the conductive polymer coating include immersion, comma coating, spray coating, roll coating, and gravure printing.
Specifically, this conductive coating film is an antistatic material such as an electronic component, an antistatic coating, an antistatic packaging material, an electromagnetic shielding material for a liquid crystal screen or a plasma display screen, a transfer belt, a developing roll, a charging roll, a transfer It is formed on the surface of an electrophotographic apparatus component such as a roll, an optical information recording medium such as a CD or DVD.
In particular, the effect of the present invention is particularly exerted when formed on an electronic component or packaging material that is weak against acid. That is, even if a conductive coating film is formed on the electronic component, corrosion of the metal or metal compound constituting the electronic component can be prevented. Specifically, in a functional capacitor having an anode made of a valve metal such as aluminum or tantalum and a dielectric layer made of an oxide obtained by electrolytic oxidation of the valve metal, the conductive layer of the present invention is formed on the dielectric layer. By forming the conductive coating film as the cathode, corrosion of the dielectric layer can be prevented. Therefore, the leakage current of the capacitor can be reduced. Moreover, when the electroconductive coating film of this invention is formed on a packaging plastic film, discoloration of what is packaged (contacted) by it can be prevented.

(実施例1)
(1)ポリスチレンスルホン酸溶液の調製
スチレンスルホン酸ナトリウム50gを水500mlに溶解し、重合開始剤として過硫酸アンモニウム0.15gを加え、70℃で5時間重合した。重合終了後、30%硫酸水溶液30gを添加し、さらに水15000mlを添加し、限外ろ過で300mlまで濃縮して、ポリスチレンスルホン酸溶液を得た。
Example 1
(1) Preparation of polystyrene sulfonic acid solution 50 g of sodium styrene sulfonate was dissolved in 500 ml of water, 0.15 g of ammonium persulfate was added as a polymerization initiator, and polymerization was performed at 70 ° C. for 5 hours. After completion of the polymerization, 30 g of a 30% aqueous sulfuric acid solution was added, 15,000 ml of water was further added, and the solution was concentrated to 300 ml by ultrafiltration to obtain a polystyrene sulfonic acid solution.

(2)導電性高分子溶液の調製
(1)で得たポリスチレンスルホン酸溶液100gに、3,4−エチレンジオキシチオフェン30gを添加し、10℃に冷却しながら1時間攪拌した。これにより得られた溶液に、塩化第二鉄250gを水1250mlに溶解した酸化剤溶液を、10℃に保ちながら2時間かけて滴下し、さらに12時間攪拌を続けて、3,4−エチレンジオキシチオフェンを重合した。
重合終了後、得られた反応溶液を限外ろ過して酸化剤残渣と未反応モノマー、オリゴマー成分を除去し、濃度1質量%の溶液とした。そして、この溶液の固形分100質量部に対して100質量部の2−メチルイミダゾールを添加し、1時間攪拌して、導電性高分子溶液を得た。
(2) Preparation of conductive polymer solution To 100 g of the polystyrenesulfonic acid solution obtained in (1), 30 g of 3,4-ethylenedioxythiophene was added and stirred for 1 hour while cooling to 10 ° C. To this solution, an oxidant solution in which 250 g of ferric chloride was dissolved in 1250 ml of water was added dropwise over 2 hours while maintaining the temperature at 10 ° C., and stirring was further continued for 12 hours. Oxythiophene was polymerized.
After the completion of the polymerization, the obtained reaction solution was ultrafiltered to remove the oxidant residue, unreacted monomers and oligomer components, and a solution having a concentration of 1% by mass was obtained. And 100 mass parts 2-methylimidazole was added with respect to 100 mass parts of solid content of this solution, and it stirred for 1 hour, and obtained the conductive polymer solution.

得られた導電性高分子溶液について、下記の方法に従って表面抵抗、pH、金属腐食性を測定し、評価した。評価結果を表1に示す。
(a)表面抵抗
得られた導電性高分子溶液を厚さ100μmのPETフィルムに塗布し、乾燥させて厚さ2μmの導電性塗膜を形成し、この塗膜の表面抵抗をダイアインスツルメンツ製ハイレスタにより測定した。
(b)pH
得られた導電性高分子溶液のpHを、25℃の恒温室中で市販のpHメーター((株)堀場製作所製pHメーターF−22)により測定した。pHメーターの校正は関東化学(株)製、フタル酸pH標準液(pH4.01)、中性リン酸塩pH標準液(pH6.86)、ホウ酸塩pH標準液(pH9.18)を用いて行った。
(c)金属腐食性
純水によって環境が調節された85℃、85%RHの環境試験槽中にて、表面抵抗測定時に形成した導電性塗膜の上に1gの鉄板(厚さ0.5μm)を置き、100時間放置した。そして、100時間後の鉄板の腐食具合を目視で確認した。
About the obtained conductive polymer solution, surface resistance, pH, and metal corrosivity were measured and evaluated according to the following method. The evaluation results are shown in Table 1.
(A) Surface resistance The obtained conductive polymer solution is applied to a PET film having a thickness of 100 μm and dried to form a conductive film having a thickness of 2 μm. It was measured by.
(B) pH
The pH of the obtained conductive polymer solution was measured with a commercially available pH meter (pH meter F-22 manufactured by Horiba, Ltd.) in a constant temperature room at 25 ° C. For calibration of the pH meter, phthalic acid pH standard solution (pH 4.01), neutral phosphate pH standard solution (pH 6.86), borate pH standard solution (pH 9.18) manufactured by Kanto Chemical Co., Ltd. are used. I went.
(C) Metal corrosivity 1 g of iron plate (thickness 0.5 μm) on the conductive coating formed at the time of surface resistance measurement in an environmental test tank of 85 ° C. and 85% RH, the environment of which was adjusted with pure water. ) And left for 100 hours. And the corrosion condition of the iron plate after 100 hours was confirmed visually.

Figure 0005241997
Figure 0005241997

(実施例2)
2−メチルイミダゾールの代わりにイミダゾールを添加したこと以外は実施例1と同様にして導電性高分子溶液を得た。そして、実施例1と同様にして評価した。評価結果を表1に示す。
(Example 2)
A conductive polymer solution was obtained in the same manner as in Example 1 except that imidazole was added instead of 2-methylimidazole. And it evaluated similarly to Example 1. FIG. The evaluation results are shown in Table 1.

(実施例3)
2−メチルイミダゾールの代わりにヒドロキシエチルアクリレートを添加し、その後100℃で1時間還流したこと以外は実施例1と同様にして導電性高分子溶液を得た。そして、実施例1と同様にして評価した。評価結果を表1に示す。
(Example 3)
A conductive polymer solution was obtained in the same manner as in Example 1 except that hydroxyethyl acrylate was added in place of 2-methylimidazole and then refluxed at 100 ° C. for 1 hour. And it evaluated similarly to Example 1. FIG. The evaluation results are shown in Table 1.

(実施例4)
(1)ポリアクリル酸溶液の調製
アクリル酸ナトリウム50gを水500mlに溶解し、重合開始剤として過硫酸アンモニウム0.15gを加え、70℃で5時間重合した。重合終了後、30%硫酸水溶液30gを添加し、さらに水15000mlを添加し、限外ろ過で300mlまで濃縮して、ポリスチレンスルホン酸溶液を得た。
Example 4
(1) Preparation of polyacrylic acid solution 50 g of sodium acrylate was dissolved in 500 ml of water, 0.15 g of ammonium persulfate was added as a polymerization initiator, and polymerization was carried out at 70 ° C. for 5 hours. After completion of the polymerization, 30 g of a 30% aqueous sulfuric acid solution was added, 15,000 ml of water was further added, and the solution was concentrated to 300 ml by ultrafiltration to obtain a polystyrene sulfonic acid solution.

(2)導電性高分子溶液の調製
(1)で得たポリアクリル酸溶液100gに、3,4−エチレンジオキシチオフェン30gを添加し、10℃に冷却しながら1時間攪拌した。これにより得られた溶液に、塩化第二鉄250gを水1250mlに溶解した酸化剤溶液を、10℃に保ちながら2時間かけて滴下し、さらに12時間攪拌を続けて、3,4−エチレンジオキシチオフェンを重合した。
重合終了後、得られた反応溶液を限外ろ過して酸化剤残渣と未反応モノマー、オリゴマー成分を除去し、濃度1質量%の溶液とした。そして、この溶液の固形分100質量部に対して100質量部のピリジンを添加し、100℃で1時間還流して、導電性高分子溶液を得た。
(2) Preparation of conductive polymer solution 30 g of 3,4-ethylenedioxythiophene was added to 100 g of the polyacrylic acid solution obtained in (1) and stirred for 1 hour while cooling to 10 ° C. To this solution, an oxidant solution in which 250 g of ferric chloride was dissolved in 1250 ml of water was added dropwise over 2 hours while maintaining the temperature at 10 ° C., and stirring was further continued for 12 hours. Oxythiophene was polymerized.
After the completion of the polymerization, the obtained reaction solution was ultrafiltered to remove the oxidant residue, unreacted monomers and oligomer components, and a solution having a concentration of 1% by mass was obtained. And 100 mass parts pyridine was added with respect to 100 mass parts of solid content of this solution, and it recirculate | refluxed at 100 degreeC for 1 hour, and obtained the conductive polymer solution.

(実施例5)
2−メチルイミダゾールの代わりにジエチルアミンを添加したこと以外は実施例1と同様にして導電性高分子溶液を得た。そして、実施例1と同様にして評価した。評価結果を表1に示す。
(Example 5)
A conductive polymer solution was obtained in the same manner as in Example 1 except that diethylamine was added instead of 2-methylimidazole. And it evaluated similarly to Example 1. FIG. The evaluation results are shown in Table 1.

(比較例1)
実施例1において、重合終了後、得られた反応溶液を限外ろ過して得た濃度1質量%の溶液を導電性高分子溶液とし、pHを調整しなかった以外は実施例1と同様にして評価した。
(Comparative Example 1)
In Example 1, after completion of polymerization, a solution having a concentration of 1% by mass obtained by ultrafiltration of the obtained reaction solution was used as a conductive polymer solution, and the same procedure as in Example 1 was carried out except that the pH was not adjusted. And evaluated.

pHが5〜13の範囲にあった実施例1〜5の導電性高分子溶液から形成された導電性塗膜は、表面抵抗が損なわれておらず、また金属腐食性に優れていた。
これに対し、pHが5未満であった比較例1の導電性高分子溶液から形成された導電性塗膜は、これに接した鉄板に赤錆を発生させた。
The conductive coating film formed from the conductive polymer solution of Examples 1 to 5 having a pH in the range of 5 to 13 did not have impaired surface resistance and was excellent in metal corrosivity.
In contrast, the conductive coating film formed from the conductive polymer solution of Comparative Example 1 having a pH of less than 5 caused red rust on the iron plate in contact therewith.

Claims (3)

π共役系導電性高分子とポリアニオンと窒素含有芳香族性環式化合物と溶媒とを含有する導電性高分子溶液において、
π共役系導電性高分子が、ポリピロール、ポリチオフェン、ポリ(N−メチルピロール)、ポリ(3−メチルチオフェン)、ポリ(3−メトキシチオフェン)、ポリ(3,4−エチレンジオキシチオフェン)から選ばれる1種又は2種からなる(共)重合体であり、
ポリアニオンが、ポリスチレンスルホン酸、ポリイソプレンスルホン酸、ポリアクリル酸エチルスルホン酸、ポリアクリル酸ブチルスルホン酸から選ばれ、
窒素含有芳香族性環式化合物は、一つの窒素原子を含有するピリジン類及びその誘導体、二つの窒素原子を含有するイミダゾール類及びその誘導体、ピリミジン類及びその誘導体、ピラジン類及びその誘導体、三つの窒素原子を含有するトリアジン類及びその誘導体から選ばれ、
温度25℃におけるpHが7〜11であることを特徴とする導電性高分子溶液。
In a conductive polymer solution containing a π-conjugated conductive polymer, a polyanion, a nitrogen-containing aromatic cyclic compound, and a solvent,
The π-conjugated conductive polymer is selected from polypyrrole, polythiophene, poly (N-methylpyrrole), poly (3-methylthiophene), poly (3-methoxythiophene), and poly (3,4-ethylenedioxythiophene) (Co) polymer consisting of one or two kinds of
The polyanion is selected from polystyrene sulfonic acid, polyisoprene sulfonic acid, polyacrylic acid ethyl sulfonic acid, polybutyl acrylate sulfonic acid,
Nitrogen-containing aromatic cyclic compounds include pyridines and derivatives thereof containing one nitrogen atom, imidazoles and derivatives thereof containing two nitrogen atoms, pyrimidines and derivatives thereof, pyrazines and derivatives thereof, Selected from triazines containing nitrogen atoms and derivatives thereof,
A conductive polymer solution having a pH of 7 to 11 at a temperature of 25 ° C.
分子内に水酸基、グリシジル基、アミノ基のいずれか1種以上を有する化合物をさらに含有することを特徴とする請求項1に記載の導電性高分子溶液。   The conductive polymer solution according to claim 1, further comprising a compound having at least one of a hydroxyl group, a glycidyl group, and an amino group in the molecule. 請求項1または2に記載の導電性高分子溶液が塗布されて形成されたことを特徴とする導電性塗膜。   A conductive coating film formed by applying the conductive polymer solution according to claim 1.
JP2005063687A 2005-03-08 2005-03-08 Conductive polymer solution and conductive coating film Active JP5241997B2 (en)