JP4868361B2 - Method for producing printed matter having wood grain pattern and printed matter having wood grain pattern - Google Patents

Description

  The present invention relates to a method for producing a printed matter having a wood grain pattern and a printed matter having a wood grain pattern, and in particular, a printed matter having a wood grain pattern that can be suitably used as a surface material for automobile interior parts, furniture, building materials, home appliances, and the like. And a printed matter having a wood grain pattern obtained thereby.

  Conventionally, decorative sheets and decorative boards made of printed materials with a wood grain pattern (wood grain pattern layer) are widely used as surface materials for various products and articles such as automobile interior parts, furniture, building materials, and home appliances. Has been. This is because by using a printed material having such a wood grain pattern, the texture and quality of the wood can be obtained easily and at low cost.

  On the other hand, among the above products, for example, high-quality furniture and interior parts of high-class automobiles are actually manufactured using high-grade wood, and wooden products whose surfaces are covered with a transparent resin layer are used. Has been. In furniture and automobile interior parts made of such woodwork products, the pattern of the wood grain moves and the shadow changes due to the light reflectivity, so that the glitter appears slightly or disappears due to the difference in the light reflection angle. Thus, the feature that the three-dimensional effect is exhibited is exhibited, and thereby, a more distinctive high-class feeling can be obtained.

  By the way, a printed matter having a wood grain pattern is generally manufactured by printing the wood grain pattern on the front and back surfaces of a printing medium made of a transparent resin sheet or resin plate by a gravure printing technique. In such printed matter, various techniques for expressing a wood grain pattern with a more realistic three-dimensional effect have been conventionally proposed (for example, see Patent Documents 1 and 2 below).

  However, the printed matter having a conventional wood grain pattern cannot give the characteristic that the light reflectivity changes due to the difference in the reflection angle of the light, and is therefore applied to high-quality furniture and interior parts of high-end automobiles. It was not possible to express a high-quality wood grain pattern.

  In order to achieve light reflectivity in printed matter with a wood grain pattern, it is possible to use opaque color ink mixed with a light reflecting material (bright material) such as metal powder or pearl powder (pearl pigment). Print the pattern, or use light-reflective ink (brightness ink) containing light-reflecting material in transparent ink, and make the light-reflective layer into a wood grain pattern consisting of an ink layer using opaque color ink It is easily considered to form a laminate. However, the present inventors actually used a non-transparent color ink mixed with a light reflecting material to print a wood grain pattern, or a printed material formed by laminating a light reflecting layer and a wood grain pattern. Produced by gravure printing method, regardless of the light reflection angle, the light reflectivity is always exhibited regardless of the light reflection angle. It turned out that it is impossible to express a grain pattern that changes its nature. This is because the ink layer printed and formed by gravure printing is extremely thin, so that the light reflecting material is parallel to the surface of the substrate in the ink layer or light reflecting layer forming the wood grain pattern. This is thought to be caused to exist in the state of being laid down.

JP-A-5-64952 Japanese Patent Laid-Open No. 9-123484

  Here, the present invention has been made in the background of the circumstances as described above, and the problem to be solved is a grain with a feature that light reflectivity changes depending on a difference in light reflection angle. The object is to provide a method capable of advantageously producing a printed matter having a pattern and a printed matter having such a wood grain pattern.

  In the present invention, in order to solve the problems relating to the method for producing a printed matter having the above-described wood pattern, (a) from the original image data having the wood pattern, the color tone of the wood pattern is used as a reference. A step of creating a plurality of color separation data, and (b) a step of creating a plurality of pattern forming color separations having a grain pattern different from each other based on each of the plurality of color separation data, (C) Based on one color separation data arbitrarily selected from the plurality of color separation data, the density range is the same as one of the pattern forming color separations created based on the color separation data. A step of producing a light reflection layer forming plate having a wood grain pattern, and (d) using the plurality of pattern forming plate plates in order from the one having the highest density range of the wood grain pattern, A similar color to the back side of the transparent substrate A plurality of types of color inks having different color tones are printed in order from a darker one by a screen printing method, and a plurality of types of wood patterns composed of ink layers having different color tones are formed on the back surface of the substrate. (E) immediately before performing screen printing using the pattern forming plate having a wood grain pattern in the same density region as the light reflecting layer forming plate, Screen printing using a reflective layer-forming plate and a light-reflective ink containing a light-reflecting material having an average particle diameter of 30 μm or more and having a content of 4% by weight or less, Forming a light reflecting layer so as to be laminated on the surface of the printed material side of the wood grain pattern formed by screen printing using the pattern forming plate. Printed The gist of the manufacturing method is as follows.

  According to one of the preferred embodiments of the method for producing a printed matter having a wood grain pattern according to the present invention, an opaque ink that is opaque and has a lighter color tone than any of the plurality of types of color ink is used. The method further includes a step of forming a base layer by applying the opaque ink on the plurality of types of wood grain patterns laminated on the back surface over the entire back surface of the substrate by screen printing. It will be.

  And in this invention, in order to solve the problem concerning the printed matter having the above-mentioned wood grain pattern, it has a wood grain pattern manufactured according to the method for producing a printed matter having the above wood grain pattern. The printed matter is also the gist.

  That is, in the method for producing a printed matter having a wood grain pattern according to the present invention, a plurality of types of wood grain patterns having different color tones are formed on the back surface of a sheet-like or plate-like transparent printed material with a high color tone. By forming the layers in order, the wood grain pattern with deeper and three-dimensional feeling can be obtained.

  Further, according to the method of the present invention, the light reflection layer forming plate having a wood grain pattern having the same concentration range as one wood grain pattern selected from a plurality of types of wood grain patterns, and the content of the light reflecting material is predetermined. The light reflecting layer is printed and formed so as to be laminated on the surface to be printed in the selected single grain pattern using the light reflecting ink limited to the value below. It is possible to limit the amount of light reflected by the entire light reflecting layer by moderately reducing the amount of light reflecting material contained in the light reflecting layer, thereby reflecting only one of the multiple types of wood grain patterns. It is possible to advantageously provide realistic light reflectivity in which a slight rise is caused.

  Moreover, in the present method, the light reflecting layer is printed by screen printing using a light reflecting ink containing a light reflecting material having an average particle size of a specific size or more, so that general printing is performed. Without adding any complicated operations that are not included in the technique, the thickness of the light reflecting layer can be increased more advantageously than that of a light reflecting layer printed and formed by gravure printing, for example. And in such a thick light reflecting layer, it becomes possible for all of the light reflecting material to be present in a properly standing state without being laid down along the surface of the substrate, and as a result The light reflectivity can be changed according to the difference in the light reflection angle.

  Therefore, according to the method for producing a printed matter having a wood grain pattern according to the present invention as described above, the three-dimensional effect has a deeper depth, and the radiance slightly appears or disappears due to the difference in the reflection angle of light. As described above, it has a feature that light reflectivity changes in real, and therefore, a printed material having a wood grain pattern that can express a more distinctive high-class feeling that cannot be obtained with a printed material having a conventional wood grain pattern is extremely simple. In addition, it can be produced industrially advantageously.

  Further, according to one of the preferred embodiments of the method for producing a printed matter having a wood grain pattern according to the present invention, the base layer can be advantageously functioned as a backing layer that prevents light transmission as much as possible. Thereby, the texture of the wood grain pattern can be enhanced more effectively.

  Further, even in the printed matter having a wood grain pattern according to the present invention, since it is produced according to the characteristic production method as described above, the operations and effects exhibited by the method for producing the printed matter having the wood grain pattern are substantially the same. The same actions and effects can be enjoyed effectively.

  Hereinafter, in order to clarify the present invention more specifically, the configuration of the present invention will be described in detail with reference to the drawings.

  First, FIG. 1 schematically shows a screen printed material manufactured according to the method for manufacturing a printed material having a wood grain pattern according to the present invention in its cross-sectional form. As apparent from FIG. 1, the screen printed material 10 includes a transparent printing sheet 12 as a printing medium. On the back surface of the printing sheet 12 (in FIG. 1, the lower surface of the printing sheet 12), first to third wood grain pattern layers 14, 16, and 18 made of an ink layer are formed by screen printing. Are laminated. The first to third wood grain pattern layers 14, 16, and 18 have a brownish similar color, and the closer to the printing sheet 12, the darker the color tone.

  Further, in the screen printed product 10, the light reflecting layer 20 is printed and formed by screen printing so as to be sandwiched between the first wood pattern layer 14 and the second wood pattern layer 16. The light reflection layer 20 contains a large number of metal reflectors such as brass and aluminum, and a light reflector 22 (bright material) such as pearl powder (pearl pigment). That is, the light reflecting layer 20 is configured by an ink layer formed using light reflecting ink (bright ink). Although not clearly shown in the figure, the light reflecting layer 20 has the same grain pattern as the second grain pattern layer 16 laminated on the side opposite to the printed sheet 12 side. ing.

  Further, the base layer 24 covers the entire back surface of the printing sheet 12 while covering the entire surface of the first to third wood grain pattern layers 14 to 18 and the light reflection layer 20 on the back surface of the screen printed product 10. In addition, it is formed by screen printing. The base layer 24 has a lighter color, for example, beige, than the third wood grain pattern layer 18 having the lightest light brown color among the first to third wood grain pattern layers 14 to 18. Yes.

  By the way, the screen printed material 10 having the structure as described above is manufactured, for example, according to the following procedure.

  That is, first, as the printing sheet 12, for example, a transparent thin flat plate made of a resin material such as polycarbonate or acrylic resin or a glass material is prepared. In addition, as for this to-be-printed sheet 12, it is desirable that the back surface is made into the smooth surface so that the screen printing operation mentioned later can be performed smoothly without any trouble.

  Next, a base layer forming printing plate used for forming the base layer 24 on the back surface of the printing sheet 12 by screen printing is prepared. Separately, a pattern forming plate and a light reflecting layer forming plate used for forming the first to third wood grain pattern layers 14 to 16 and the light reflecting layer 20 by screen printing, respectively. Are prepared and prepared using a plate making system as shown in FIG. 2, for example.

  As is clear from FIG. 2, the plate making system used here has a known structure including an image data creation device 26 and a plate making device 28. That is, among these devices, the image data device 26 performs predetermined data processing on the image data, and is composed of a CPU or the like that creates pattern formation color separation data and light reflection layer formation color separation data, which will be described later. In addition to the data processing device 30, an input device 32 including a scanner for inputting image data, image data input from the input device 32, An output device 34 composed of a display, a printer, or the like that outputs color separation data created by the data processing device 30, their image data and color separation data, and a data processing program executed by the data processing device 30. And a storage device 36 including a memory and a hard disk for storage.

  On the other hand, the plate making device 28 includes a color separation film creating device 38 for creating a color separation film based on the color separation data created by the data processing device 30 of the image data creation device 26, and the color separation film creating device 38. And a color separation creating apparatus 40 that creates a color separation used by a screen printing machine (not shown) from the color separation film produced in this manner.

  In order to create a pattern forming plate and a light reflecting layer forming plate using such a plate making system, first, it should be expressed or reproduced in the finally obtained screen print 10. Original image data having a wood grain pattern is input by the input device 32.

  At this time, as the original image data, for example, a photograph taken with a film camera or a digital camera and printed, or digital image data stored in a recording medium such as a digital camera or a CD-ROM is used. The When the original image data is a photograph, a scanner or the like is used as the input device 32. On the other hand, when the original image data is digital image data, it is built in the digital camera itself or the data processing device 30. The data reading device is used as the input device 32.

  Although the resolution at the time of inputting the original image data is not particularly limited, the input resolution is 200 dpi or more in order to reproduce the original image more faithfully in the screen print 10 finally obtained. It is desirable that Further, the input original image data is stored in the storage device 36.

  When the original image data is input, the data processing device 30 creates a plurality (three types here) of color separation data from the original image data on the basis of the tone of the color tone of the wood grain pattern it has. The Such a process of creating a plurality of color separation data is performed according to a known method including a method described in Japanese Patent Laid-Open No. 2000-118120.

  That is, in brief description, for example, the entire original image data is first converted to gray scale with an arbitrary gradation. Then, the image data converted to gray scale is created as all-density distribution data 42 having a grain pattern of 0 to 100% density range, that is, the whole grain pattern of the original image as shown in FIG. Is done. Next, from this total density separation data 42, for example, image data of a wood grain pattern portion of a medium / high density region of 50 to 100% is extracted. As shown in FIG. Among them, medium and high density separations having both patterns of wood grain pattern part with dark color tone (high density area of 80% or higher) and wood grain pattern part of intermediate color tone (density area of 50-80%) Data 44 is created. Thereafter, from this medium / high density separation data 44, image data of a wood grain pattern portion of a high density region of, for example, 80 to 100% is further extracted. As shown in FIG. Among the wood grain patterns, high density separation data 46 having a pattern of a wood grain pattern portion having a dark color tone (high density region of 80% or more) is created. The first to third color separation data 44 to 48 created in this way are stored in the storage device 36.

  Next, the three types of color separation data 42 to 46 created as described above are transmitted from the image data creation device 26 to the plate making device 28. Then, by the separation film creating device 38 of the plate making apparatus 28, one high-concentration separation film and one full-concentration separation film are respectively provided on the basis of the high-concentration separation data 46 and the total-concentration separation data 42. At the same time, two middle / high density separation films are created based on the middle / high density separation data 46.

  In addition, the screening system employ | adopted at the time of these color separation film preparations is not limited at all, For example, both FM screening system and AM screening system can be employ | adopted. Further, although no special value is set for the output resolution at the time of creating the color separation film, the original image is reproduced more realistically in the finally obtained screen print 10 as in the case of inputting the original image data. In addition, it is desirable that the output resolution is 2000 dpi or more.

  After that, the high density separation film created based on the high density separation data 46 is used by the plate making apparatus 40 of the plate making apparatus 28, and has, for example, a screen pattern having a wood pattern of a high density region of 80% or more. While the first pattern forming color separation used for printing is created, the medium / high density separation film created based on the medium / high density separation data 44 is used. A second pattern forming color separation used for screen printing having a medium and high density wood grain pattern is created, and a total density separation film created based on the total density separation data 42 is used. Thus, a third pattern forming color separation used for screen printing having a wood grain pattern in the entire density range of 0 to 100% is created.

  In addition, at the same time as or before and after the creation of the first to third pattern forming plates, the plate is created by the plate making device 40 of the plate making apparatus 28 based on the medium / high density plate data 44. In addition, light used for screen printing having the same density range (50 to 100%) as the second pattern-forming color separation, using the remaining one of the medium / high density color separation film A reflection layer forming plate is prepared.

  When the first to third pattern forming separation plates and the light reflection layer separation plate are thus prepared, the first pattern forming separation plate is used as shown in FIG. 6 (a). The screen ink of “dark brown” color is screen-printed on the back surface of the printing sheet 12 by a known method. Thereby, on the back surface of the printing sheet 12, the first wood grain pattern layer 14 having a wood grain pattern pattern with a dark color tone (high density region of 80% or more) in the whole wood grain pattern of the original image is “ It is formed to exhibit a “dark brown” color.

  Thereafter, using a color separation layer for light reflection layer, as shown in FIG. 6B, the light reflective ink is applied to the printed sheet of the first wood grain pattern layer 14 on the back surface of the sheet to be printed 12. Screen printing is performed on the side opposite to the 12 side by a known method. As a result, on the first wood grain pattern layer 14, among the whole wood grain pattern of the original image, a dark color tone (high density region of 80% or higher) wood grain pattern portion and an intermediate color tone (50 to 80%) A light reflecting layer 20 having both patterns of a wood grain pattern portion having a medium density region) is formed by lamination. Thus, although the light reflecting layer 20 having such a pattern exhibits light reflectivity, the portion having the pattern of the wood grain pattern portion of the high concentration region in the light reflecting layer 20 is the first. Since it is laminated on the opposite side to the printed sheet 12 side in one wood grain pattern layer 14, substantially only in the portion having the pattern of the wood grain pattern portion of the medium density region in the light reflection layer 20, Brightness comes to be demonstrated.

  In this case, in particular, as the light-reflecting ink used to print and form the light-reflecting layer 20, the light-reflecting material 22 to be put in a transparent screen ink has an average particle diameter of 30 μm or more. And what is contained in the ratio of 4 weight% or less is used. That is, the light reflecting material 22 having an average particle diameter of 30 μm or more is included in the light reflecting layer 20 at a small ratio of 4% by weight or less.

  This is because the light reflecting layer 20 is printed and formed by a screen printing method, and is sufficiently thick as compared with a case where it is printed and formed by a gravure printing method, for example. Then, when the average particle diameter of the light reflecting material 22 included in the thick light reflecting layer 20 is set to 30 μm or more, such a relatively large light reflecting material 22 becomes light reflective. The light reflection layer 20 has an effect in the light reflection layer 20 that exists in a moderately standing state inside the layer 20, and thereby changes its appearance such that the glitter appears or disappears depending on the difference in the light reflection angle. It is because it can come to be demonstrated. In other words, when the average particle diameter of the light reflecting material 22 included in the light reflecting layer 20 is less than 30 μm, the light reflecting property of the light reflecting layer 20 changes depending on the light reflection angle. It will disappear.

  The upper limit value of the average particle diameter of the light reflecting ink or the light reflecting material 22 included in the light reflecting layer 20 is not particularly limited, but is used, for example, during screen printing of the light reflecting ink. In the range smaller than the size of the screen mesh, the thickness is appropriately determined according to the thickness of the light reflecting layer 22 and the like.

  Further, when the amount of the light reflecting material 22 contained in the light reflecting ink exceeds 4% by weight, the content of the light reflecting material 22 in the reflecting layer 20 is excessively increased, and the light reflecting layer 20 The light reflectivity becomes more prominent. And in that case, depending on the reflection angle of light and the amount of light irradiated, the actual wood grain pattern whose surface is covered with a transparent resin layer that exhibits a slight light reflectivity, It becomes difficult to express realistically. That is, here, in order to more realistically represent the actual wood grain pattern whose surface is covered with a transparent resin plate, the content of the light reflecting material 22 in the light reflecting ink is 4% by weight or less. The value must be within the range of. If the light reflecting material 22 is contained in the light reflecting ink, the lower limit of the content thereof is not limited in any way. % Or more is desirable.

  In the light-reflective ink, the type of transparent ink that becomes the matrix of the light-reflecting material is not limited at all.

  After the light reflecting layer 20 is formed, the second pattern forming color separation is used, and as shown in FIG. 6C, the screen ink used for forming the first wood grain pattern layer 14 is used. Although the color is the same color as the above, the “brown” screen ink with a light color tone is laminated on the back surface of the printing sheet 12 with the first wood grain pattern layer 14 in the light reflecting layer 20 (printing sheet 12 side). On the opposite side to (), screen printing is performed by a known method.

  Thereby, on the light reflection layer 20, among the whole wood grain pattern of the original image, the wood grain pattern portion having a dark color tone (high density region of 80% or more) and the middle color tone (50 to 80% medium density region). The second wood grain pattern layer 16 having both patterns of the wood grain pattern portion having) is laminated and formed in a state of being colored “brown”, but the portion having the pattern of the wood grain pattern portion of the high concentration region Is laminated on the first wood grain pattern layer 14 through a part of the light reflecting layer 20. Therefore, the second wood grain pattern layer 16 can be visually recognized only from the surface side of the sheet to be printed 12 with the pattern of the wood grain part of the medium density region. Thus, in this step, the second wood grain pattern layer 16 is apparently formed on the light reflecting layer 20 and has a pattern of a wood grain pattern portion of a medium density region exhibiting a “brown” color. Will be formed. Then, the light reflecting layer 20 substantially imparts the characteristic light reflectivity as described above to the wood grain pattern portion of the medium density region in the second wood grain pattern layer 16. .

  Next, as shown in FIG. 6 (d), the third pattern forming color separation is used, and the same color as the screen ink used for forming the first and second wood grain pattern layers 14 and 16 is used. However, the “light brown” screen ink having a lighter color tone than the second wood grain pattern layer 16 is laminated on the light reflecting layer 20 of the second wood grain pattern layer 16 (printed sheet 12 side). Is printed on the opposite side by a known method.

  As a result, the entire grain pattern of the original image is laminated on the second grain pattern layer 16 in a state of being colored “light brown”. The wood grain pattern portion is laminated on the first wood grain pattern layer 14 and the second wood grain pattern layer 16. Therefore, in the third wood grain pattern layer 16, only the part having the pattern of the wood grain part of the low density region of 50% or less can be visually recognized from the surface side of the printing sheet 12. Thus, in this step, the third wood grain pattern layer 18 has a pattern of a low density region wood grain pattern portion showing a “light brown” color on the second wood grain pattern layer 16 in appearance. Thus, the layers are formed.

  Further, subsequently, a base layer forming printing plate is used, and an opaque color having a lighter tone than any of the screen inks used for forming the first to third woodgrain layers 14 to 18, for example, beige The color screen ink is solidly applied by a known screen printing method on the side opposite to the side of the third wood grain pattern layer 18 where the second wood grain pattern layer 16 is laminated (printed sheet 12 side). As a result, the beige base layer 24 is laminated on the third wood grain pattern layer 18 over the entire back surface of the printing sheet 12. Thus, the light passes through the first to third wood pattern layers 14 to 18 without hindering the difference in color tone of the first to third wood pattern layers 14 to 18 that are visible from the surface of the printing sheet 12. Transmission is prevented as much as possible. Note that a plurality of the base layers 24 may be formed as necessary. In that case, the color tone becomes thinner as the base layer 24 is farther from the back surface of the printing sheet 12.

  Thus, the first to third wood grain pattern layers 14 to 18, the light reflection layer 20, and the base layer 24 are laminated on the back surface of the printing sheet 12 by a known screen printing method, and are shown in FIG. The intended screen print 10 having such a structure is obtained. And such a screen printed matter 10 comes to be used as a surface material of various products and articles such as automobile interior parts, furniture, building materials, and home appliances. In that case, the surface of the base layer 24 opposite to the printed sheet 10 side is attached to the surface of various articles or products using an adhesive or the like, and attached. The surface (the surface opposite to the back surface on which each ink layer is formed) is exposed to the outside and is used.

  The thicknesses of the first to third wood grain pattern layers 14 to 18, the light reflection layer 20, and the base layer 24 in the screen print 10 obtained as described above are not particularly limited. Although the thickness is about the same as that of a general ink layer formed by a printing method, the light reflecting layer 20 has a light reflecting material 22 having an average particle diameter of 30 μm or more properly standing inside. In order to make it exist in such a state, it is desirable that the thickness be 15 μm or more.

  In addition, the hardness of the squeegee used at the time of screen printing should be about 70 to 80 degrees as measured by a type A durometer in accordance with the “durometer hardness test” defined in JIS-K-6253-1997. Is preferred. This is because when the hardness of the squeegee used is less than 70 degrees, there is a problem that the thickness of each printed layer becomes too thick, and the hardness of the squeegee used is 80 degrees. This is because if it exceeds, the thickness of each printed layer becomes excessively thin.

  As described above, in the present embodiment, the first to third grain pattern layers 14 to 16 having colors different from each other on the back surface of the printing sheet 12 such as “dark brown”, “tea”, and “light brown”. However, the wood grain pattern having a deeper depth and a three-dimensional feeling can be advantageously expressed by being laminated in order from the darkest one.

  In the present embodiment, in particular, the light reflecting layer 20 having the same grain pattern as the second grain pattern layer 16 is provided between the first grain pattern layer 14 and the second grain pattern layer 16 on the screen. The actual wood grain whose surface is covered with a transparent resin plate, that is, the light reflectivity that changes so that the glitter appears slightly or disappears depending on the difference in the light reflection angle Although it is exhibited in the pattern, the light reflectivity can be effectively exhibited in the wood grain pattern having an intermediate color tone. A wood grain pattern that can express a feeling can be obtained very easily and industrially advantageously.

  Further, in the present embodiment, the base layer 24 that prevents transmission of light through the first to third wood pattern layers 14 to 16 as much as possible is printed on the entire back surface of the printing sheet 12 by screen printing. By being formed, the whole wood grain pattern exhibiting the above excellent characteristics can be expressed with higher texture.

  In the present embodiment, on the back surface of the printing sheet 12, the first wood grain layer 14 to 18 that is screen-printed is printed immediately before the second wood grain pattern layer 16 is printed. The light reflection layer 20 was screen-printed after the printing of the one wood grain pattern layer 14 and before the printing of the second wood grain pattern layer 16, but the light reflection layer 20 imparts light reflectivity. Immediately before the printing of the wood grain pattern layer to be performed, screen printing using the light reflecting layer forming plate having the wood grain pattern layer pattern of the same density range as the wood grain pattern layer and the light reflecting ink is performed. Is formed. Therefore, for example, when light reflectivity is imparted to the first wood grain pattern layer 14, the light reflection layer 20 is printed and formed immediately before the first wood grain pattern layer 14 is printed. When light reflectivity is imparted to the third wood pattern layer 18, the light reflection layer 20 is printed and formed immediately before the third wood pattern layer 18 is printed.

  Further, the number and color of the wood grain pattern layer or the number and color of the base layer are not particularly limited to those shown in the embodiment.

  Furthermore, there is a method for creating as many types of separation data as necessary from the original image data, and a method for creating pattern separations and light reflection layer formation separations based on those separation data. Needless to say, the present invention is not limited to the examples.

  In addition, the present invention can be implemented in various forms, and any of various embodiments relating to various changes, modifications, and improvements of the present invention adopted based on the knowledge of those skilled in the art. It should be understood that the present invention belongs to the category of the present invention without departing from the spirit of the present invention.

  Hereinafter, representative examples of the present invention will be shown to further clarify the features of the present invention, but the present invention is not limited by the description of such examples. Needless to say.

<Example 1>
First, using a wood grain pattern photograph taken with a digital camera and a plate making system having a structure as shown in FIG. 2, the photograph is read at an input resolution of 200 to 300 dpi by a scanner provided in the plate making system. After the original image data having the wood grain pattern is created, the total density distribution data having the wood grain pattern of 0 to 100% density range and the wood grain pattern having the density range of 50 to 80% are obtained from the original image data. High-density separation data and high-concentration separation data having a wood grain pattern in a concentration range of 80 to 100% were created by a known method.

  Next, based on the three types of plate separation data, the plate making apparatus of the plate making system creates first, second, and third three types of pattern forming plate having different color tones by a known method. At the same time, based on the medium / high density separation data used for the preparation of the second pattern forming plate, the light reflection layer forming plate was prepared by a known method using a plate making apparatus of the plate making system. Each of these separations was created with an output resolution of 2438 dpi. In addition, a 300-355 mesh screen was used for each pattern forming plate, and a 270-300 mesh screen was used for the light reflecting layer forming plate.

  Separately from these separations, a base layer-forming printing plate is prepared using a 250-270 mesh screen. Further, the printing plate is made of polycarbonate, and the front and back surfaces are smooth. A transparent flat plate having a thickness of 0.5 mm was prepared.

  Then, using the first pattern forming plate, a dark brown screen ink [trade name: Noriphan HTR (manufactured by Mino Group)] is printed on the back surface of the printing sheet by a known screen printing method. Then, the first wood grain pattern layer having the pattern of the wood grain pattern portion having a dark color tone (high density region of 80% or more) in the whole wood grain pattern of the original image is dark brown with a thickness of 10 to 15 μm. It was formed to exhibit.

  Next, using the light reflecting layer forming separation plate, a light reflecting ink [trade name: Noriphan MCF series H is formed on the back side of the printed sheet on the side opposite to the printed sheet 12 side of the first wood grain pattern layer. Type (manufactured by Mino Group Co., Ltd.)] was printed by a known screen printing method to form a light reflecting layer with a thickness of 15 μm or more. Here, as the light reflecting ink, a light reflecting material (H type) having an average particle diameter of 30 μm contained at a ratio of 3% by weight was used.

  Then, using the second pattern-forming color separation, a brown screen ink [trade name: Noriphan HTR (stock) on the opposite side of the light reflecting layer on the back surface of the printed sheet from the first grain pattern layer side. (Mino Group Co., Ltd.)] is printed by a known screen printing method, and the pattern of the wood grain pattern portion having an intermediate color tone (medium / high density range of 50 to 80%) in the whole wood grain pattern of the original image The provided second wood grain pattern layer was formed so as to exhibit a brown color with a thickness of 10 to 15 μm.

  Subsequently, a light brown screen ink [trade name: NORIFAN HTR (trade name) is formed on the reverse side of the second wood grain pattern layer on the back surface of the printing sheet using the third pattern forming plate. Mino Group Co., Ltd.)] is printed by a known screen printing method, and the pattern of the wood grain pattern portion having a light color tone (0-50% middle / high density area) in the whole wood grain pattern of the original image A third grain pattern layer having a thickness of 10 to 15 μm was formed so as to exhibit a light brown color.

  Thereafter, using a base layer forming plate, a beige screen ink [trade name: Noriphan HTR (manufactured by Mino Group)] is applied to the entire back surface of the printing sheet using a known screen printing technique. The beige base layer was formed in a thickness of 10 to 15 μm so as to cover all of the first to third wood grain pattern layers and the light reflection layer.

  Thus, a target screen printed matter having a structure as shown in FIG. 1, in which the first to third wood grain pattern layers, the light reflecting layer, and the base layer are laminated on the back surface of the sheet to be printed. Obtained. In addition, when forming the 1st thru | or 3rd grain pattern layer, the light reflection layer, and the base layer by screen printing, the squeegee whose hardness measured by the type A durometer is 70 degree | times was used.

  And when this obtained screen printed matter was visually observed from the surface, a deep three-dimensional wood grain pattern was recognized. Further, when the screen printed material was observed while changing the angle at which the screen printed material was visually recognized from the surface, it was found that the light reflectivity changed so that the glitter appeared slightly or disappeared.

<Comparative Example 1>
For comparison, the light reflecting material having a value of 10 μm, which is smaller than the range specified in the present invention, is contained at a ratio of 10% by weight, which is a value larger than the range specified in the present invention. The first to third wood grain pattern layers, the light reflection layer, and the base layer are laminated and formed on the back surface of the printed sheet using the same conditions and method as in Example 1 except that the light reflective ink is used. Thus, an intended screen printed matter having a structure as shown in FIG. 1 was obtained.

  And when the obtained screen printed material was visually observed from the surface, a deep three-dimensional wood grain pattern was recognized, but no matter what angle the screen printed material was viewed from, the glitter was generated. Therefore, the feature that the light reflectivity changes depending on the difference in the reflection angle of light was not recognized.

It is a partial section expanded explanatory view showing an example of a screen printed matter manufactured according to the method of the present invention. FIG. 2 is a block explanatory diagram schematically showing a configuration of a plate making system used for manufacturing the screen printed matter shown in FIG. 1. It is explanatory drawing which shows the total density distribution data used for manufacture of the screen printed matter shown by FIG. It is explanatory drawing which shows medium density distribution data used for manufacture of the screen printed matter shown by FIG. It is explanatory drawing which shows the high concentration distribution data used for manufacture of the screen printed matter shown by FIG. It is explanatory drawing which shows an example of the manufacturing process of the screen printed matter shown by FIG. 1, Comprising: (a) shows the state which printed and formed the 1st wood grain pattern layer on the back surface of the to-be-printed sheet 12, ( b) shows a state in which a light reflection layer is printed on the first wood pattern layer, and (c) shows a state in which a second wood pattern layer is printed on the light reflection layer. , (D) shows a state in which a third wood pattern layer is printed on the second wood pattern layer.

Explanation of symbols

DESCRIPTION OF SYMBOLS 10 Screen printed matter 12 Sheet to be printed 14 1st grain pattern layer 16 2nd grain pattern layer 18 3rd grain pattern layer 20 Light reflection layer 22 Light reflection material 24 Base layer 26 Image data creation apparatus 28 Plate making apparatus 42 Total density Separation data 44 Medium / high concentration separation data 46 High concentration separation data

Claims (3)

A step of creating a plurality of color separation data from the original image data having a wood grain pattern on the basis of the color tone of the wood grain pattern;
Based on each of the plurality of color separation data, creating a plurality of pattern forming color separations having a grain pattern different from each other;
Based on one color separation data arbitrarily selected from the plurality of color separation data, a grain pattern having the same density range as one of the pattern forming color separations created based on the color separation data A step of creating a light reflection layer forming plate having:
The plurality of pattern forming separation plates are used in descending order of the density range of the wood grain pattern, and although the colors are similar to each other with respect to the back surface of the sheet-like or plate-like transparent printing medium, Multiple different types of color inks are printed by screen printing in order from dark tones, and multiple types of wood grain patterns composed of ink layers with different color tones are printed on the back side of the printed material. A step of sequentially forming layers,
Immediately before screen printing using the pattern forming plate having a wood grain pattern in the same concentration range as the light reflecting layer forming plate, the light reflecting layer forming plate and an average particle size of 30 μm or more are used. A screen using the light-reflective layer comprising the light-reflective ink containing the light-reflective material and having a content of 4% by weight or less. Forming the wood grain pattern formed by printing so as to be laminated on the surface of the printing material;
A method for producing a printed matter having a wood grain pattern, comprising:   Using an opaque ink that is opaque and has a lighter color tone than any of the plurality of types of color inks, on the plurality of types of wood grain pattern laminated on the back surface of the substrate, the entire back surface of the substrate The method for producing a printed matter having a wood grain pattern according to claim 1, further comprising a step of solidly applying the opaque ink by a screen printing method to form a base layer. A printed matter having a wood grain pattern, which is produced according to the method for producing a printed matter having a wood grain pattern according to claim 1 or 2.