JP4867526B2 - Anti-counterfeit magnetic tape transfer sheet and card - Google Patents

Anti-counterfeit magnetic tape transfer sheet and card Download PDF

Info

Publication number
JP4867526B2
JP4867526B2 JP2006230255A JP2006230255A JP4867526B2 JP 4867526 B2 JP4867526 B2 JP 4867526B2 JP 2006230255 A JP2006230255 A JP 2006230255A JP 2006230255 A JP2006230255 A JP 2006230255A JP 4867526 B2 JP4867526 B2 JP 4867526B2
Authority
JP
Japan
Prior art keywords
parts
weight
layer
transfer sheet
magnetic tape
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2006230255A
Other languages
Japanese (ja)
Other versions
JP2008049643A (en
Inventor
一尋 屋鋪
英誉 井出
直彰 新藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Inc
Original Assignee
Toppan Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Inc filed Critical Toppan Inc
Priority to JP2006230255A priority Critical patent/JP4867526B2/en
Publication of JP2008049643A publication Critical patent/JP2008049643A/en
Application granted granted Critical
Publication of JP4867526B2 publication Critical patent/JP4867526B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、偽造防止を必要とする各種情報表示媒体に関し、詳しくはキャッシュカードやクレジットカード等の磁気カードを製造する際の部品となる、偽造防止磁気テープ転写シート、及び該偽造防止磁気テープ転写シートで転写したカードに関するものである。   The present invention relates to various information display media that require anti-counterfeiting, and in particular, a forgery-preventing magnetic tape transfer sheet that is a component when manufacturing a magnetic card such as a cash card or a credit card, and the anti-counterfeit magnetic tape transfer It relates to a card transferred with a sheet.

近年、偽造防止手段として光の干渉を用いて立体画像や特殊な装飾画像を表現し得る、回折構造や回折格子、光学特性の異なる薄膜を重ねることにより、見る角度により色の変化(カラーシフト)を生じる多層薄膜のようなOVD[OVDは、”Optical(ly) Variable Device”の略。尚、OVDの同義語にDOVIDもあり、”Diffractive Optical(ly) Variable Imaging Device”の略である。]が利用されるようになってきている。これらOVDは高度な製造技術を要すること、独特な視覚効果を有し、一瞥で真偽が判定できることから有効な偽造防止手段としてクレジットカード、有価証券、証明書類等の一部にあるいは全面に形成され使用されている。最近では、有価証券以外にもスポーツ用品やコンピュータ部品をはじめとする電気製品ソフトウエアー等に貼り付けられ、その製品の真正さを証明する認証シールや、それら商品のパッケージに貼りつけられる封印シールとしても広く使われるようになってきた。   In recent years, as a means of preventing counterfeiting, light interference can be used to express stereoscopic images and special decorative images. By overlapping thin films with different diffraction structures, diffraction gratings, and optical properties, color changes depending on viewing angle (color shift) OVD [OVD is an abbreviation of “Optical (ly) Variable Device”. Note that DOVID is also a synonym for OVD, and is an abbreviation for “Differential Optical (ly) Variable Imaging Device”. ] Has come to be used. These OVDs require advanced manufacturing technology, have a unique visual effect, and can be judged at a glance as authenticity, so they can be formed on credit cards, securities, certificates, etc. as part of or on the entire surface as an effective counterfeit measure. Is being used. Recently, in addition to securities, it is affixed to sports equipment, computer parts and other electrical product software, etc., as an authentication sticker that proves the authenticity of the product, and as a seal sticker that is affixed to the package of those products Has also become widely used.

一方、キャッシュカード、及びクレジットカード等では、特許文献1のような、磁気層と回折構造を一体化する事で、カードデザイン上有利であり、しかも機械情報処理を行なえる磁気カードが知られており、また、これらカードの製造方法は、主に回折構造入磁気偽造防止磁気テープ転写シートをカード基材へ転写接着させる方法が公知である。   On the other hand, for cash cards, credit cards, and the like, there is known a magnetic card that is advantageous in card design by integrating a magnetic layer and a diffractive structure as in Patent Document 1 and that can perform mechanical information processing. In addition, as a method for producing these cards, a method of mainly transferring and adhering a magnetic tape transfer sheet with diffractive structure-containing magnetic forgery to a card substrate is known.

しかし、これらカードの製造工程では、接着剤塗工工程、磁気テープ転写工程、積層ラミネート工程、等の高熱を使用する加工工程が有り、特に近年では特許文献2のような耐熱性に優れた、ポリカーボネートを含む耐熱ポリマー材料を使用したカードが普及されている。これら耐熱カードの製造工程では、140℃以上の温度による積層ラミネート工程が想定される。   However, in the manufacturing process of these cards, there are processing steps using high heat such as an adhesive coating step, a magnetic tape transfer step, a laminating laminate step, etc., and in recent years, excellent heat resistance as in Patent Document 2, Cards using heat-resistant polymer materials including polycarbonate are widely used. In the manufacturing process of these heat-resistant cards, a lamination laminating process at a temperature of 140 ° C. or higher is assumed.

従来技術は以下の通り。
特開平6−167920号公報 特開平6−167921号公報
The prior art is as follows.
JP-A-6-167920 Japanese Patent Laid-Open No. 6-167721

上述の様に特許文献2の様な場合でも、偽造防止磁気テープ転写シートについても相当の耐熱性が要求される。カード製造時の高温加工工程において、偽造防止磁気テープ転写シートが高温に曝された場合、回折構造形成層に使用されている樹脂が熱により収縮又は膨張し、この収縮・膨張についていくことのできない光学薄膜に細かいひび割れが生じて、その結果、光学薄膜が白化するという問題があった。   As described above, even in the case of Patent Document 2, the anti-counterfeit magnetic tape transfer sheet is required to have considerable heat resistance. In the high-temperature processing process during card manufacturing, when the anti-counterfeit magnetic tape transfer sheet is exposed to a high temperature, the resin used for the diffraction structure forming layer contracts or expands due to heat, and the contraction / expansion cannot be followed. There was a problem that fine cracks were generated in the optical thin film, resulting in whitening of the optical thin film.

本発明は前記従来の技術が抱える問題点に鑑み提案されたものであり、従来技術よりも耐熱性が高く、カード製造時の高温加工による、光学薄膜の白化が少ない事を特徴とする、偽造防止磁気テープ転写シート、及び該偽造防止磁気テープ転写シートで転写したカードを提供する事を目的とする。   The present invention has been proposed in view of the above-mentioned problems of the prior art, has higher heat resistance than the prior art, and is characterized by low whitening of the optical thin film due to high-temperature processing during card manufacturing. An object of the present invention is to provide a magnetic tape transfer sheet for prevention and a card transferred with the magnetic tape transfer sheet forgery prevention.

前記課題を解決するために本発明が提供する手段を次に挙げる。   Means provided by the present invention in order to solve the above-mentioned problems are as follows.

請求項1に記載の発明は、基材として厚み25μのポリエステルフィルムを用い、このフィルムの片面に下記(1)、(2)、(3)、(4)、(5)、(6)の各組成物を用い、保護層(厚さ1.5μm)、回折構造形成層(厚さ1.5μm)、回折効果層(50nm)、耐熱層(1μm)、磁気記録層(15μm)、接着層(3μm)を順次形成したことを特徴とする偽造防止磁気テープ転写シートを提供するものであり、(1)剥離性保護層組成物は、アクリル樹脂(Tg.105℃)・・19.2重量部ポリエチレンパウダー0.8重量部、メチルエチルケトン45.0重量部、トルエン35.0重量部、(2)回折構造形成層組成物は、ウレタン樹脂20.0重量部、メチルエチルケトン50.0重量部、酢酸エチル30.0重量部(3)回折効果層組成物はアルミニウム(4)耐熱層組成物は変性ノルボルネン樹脂(Tg.171℃)20.0重量部、沈降性硫酸バリウム(比重5.5)10.0重量部、メチルエチルケトン40.0重量部、トルエン30.0重量部(5)磁気記録層組成物は、γ−Fe2O3を30重量部、塩酸ビニル酢酸ビニル重合体3重量部、ポリウレタンエラストマー20重量部、トルエン15重量部、メチルエチルケトン15重量部、イソプロピルアルコール16重量部(6)接着層組成物は、塩酸ビニル酢酸ビニル重合体20重量部、アクリル樹脂10重量部、酢酸エチル20重量部、トルエン50重量部からなる。
The invention according to claim 1 uses a polyester film having a thickness of 25 μm as a substrate, and the following (1), (2), (3), (4), (5), (6) are provided on one side of the film. Using each composition, a protective layer (thickness 1.5 μm), a diffraction structure forming layer (thickness 1.5 μm), a diffraction effect layer (50 nm), a heat-resistant layer (1 μm), a magnetic recording layer (15 μm), an adhesive layer (1) The peelable protective layer composition is an acrylic resin (Tg. 105 ° C.) 19.2 weight Part polyethylene powder 0.8 parts by weight, methyl ethyl ketone 45.0 parts by weight, toluene 35.0 parts by weight, (2) diffraction structure forming layer composition is urethane resin 20.0 parts by weight, methyl ethyl ketone 50.0 parts by weight, acetic acid 30.0 parts by weight of ethyl ( ) The diffraction effect layer composition is aluminum. (4) The heat-resistant layer composition is 20.0 parts by weight of modified norbornene resin (Tg. 171 ° C.), 10.0 parts by weight of precipitated barium sulfate (specific gravity 5.5), and 40. methyl ethyl ketone. 0 parts by weight, 30.0 parts by weight of toluene (5) Magnetic recording layer composition is 30 parts by weight of γ-Fe 2 O 3, 3 parts by weight of vinyl acetate vinyl acetate polymer, 20 parts by weight of polyurethane elastomer, 15 parts by weight of toluene, methyl ethyl ketone 15 parts by weight, 16 parts by weight of isopropyl alcohol (6) The adhesive layer composition comprises 20 parts by weight of vinyl chloride vinyl acetate polymer, 10 parts by weight of acrylic resin, 20 parts by weight of ethyl acetate, and 50 parts by weight of toluene.

また、請求項2に記載の発明は、請求項1記載の偽造防止磁気テープ転写シートを貼付したことを特徴とするカードを提供するものである。
According to a second aspect of the present invention, there is provided a card comprising the anti-counterfeit magnetic tape transfer sheet according to the first aspect .

本発明の偽造防止磁気テープ転写シートおよびカードは、回折効果層の回折構造形成層と逆側に耐熱層を設けることにより、耐熱性が高く、カード製造時の光学薄膜の白化が少ない事を特徴とする、偽造防止磁気テープ転写シート、及び該偽造防止磁気テープ転写シートで転写した磁気カードを提供する事が出来る。   The anti-counterfeit magnetic tape transfer sheet and card of the present invention are characterized by high heat resistance by providing a heat-resistant layer on the opposite side of the diffraction structure forming layer of the diffraction effect layer, and less whitening of the optical thin film during card manufacture. The anti-counterfeit magnetic tape transfer sheet and the magnetic card transferred with the anti-counterfeit magnetic tape transfer sheet can be provided.

以下、本発明の偽造防止磁気テープ転写シート、及び偽造防止磁気テープ転写シートで転写したカードの実施例を図面に基づいて詳細に説明する。図1は前記の偽造防止磁気テープ転写シートの断面を示すもので、図2は偽造防止磁気テープ転写シートをカードに転写貼付している図である。   Hereinafter, an example of a forgery-preventing magnetic tape transfer sheet of the present invention and a card transferred with the forgery-preventing magnetic tape transfer sheet will be described in detail with reference to the drawings. FIG. 1 shows a cross section of the forgery-preventing magnetic tape transfer sheet, and FIG. 2 shows the anti-counterfeit magnetic tape transfer sheet being transferred and pasted to a card.

前記偽造防止磁気テープ転写シート(1)の層構成は、保護層は転写する際の転写性能を高める意図で設けられるため必須層ではないが、請求項6、13も併せて説明するために加えた層構成で以下説明する。なお、同様に剥離層、あるいは離型層を必要に応じて適宜加えた層構成も可能である。   The layer structure of the anti-counterfeit magnetic tape transfer sheet (1) is not an indispensable layer because the protective layer is provided for the purpose of improving the transfer performance at the time of transfer, but is also added to explain claims 6 and 13 together. The layer configuration will be described below. Similarly, a layer structure in which a release layer or a release layer is appropriately added as necessary is also possible.

説明する偽造防止磁気テープ転写シート(1)の層構成は、支持体(2)の片面に保護層(3)、回折構造形成層(4)、回折効果層(5)、耐熱層(6)磁気記録層(7)、接着層(8)を順次形成してなるものである。   The layer structure of the anti-counterfeit magnetic tape transfer sheet (1) to be described is that a protective layer (3), a diffraction structure forming layer (4), a diffraction effect layer (5), and a heat-resistant layer (6) are provided on one side of the support (2). A magnetic recording layer (7) and an adhesive layer (8) are sequentially formed.

前記偽造防止磁気テープ転写シートに於ける支持体2としては厚みが安定しており、かつ耐熱性の高いポリエチレンテレフタレート樹脂フィルムを用いるのが一般的であるが、これに限るものではない。その他の材料としては、ポリエチレンナフタレート樹脂フィルム、ポリイミド樹脂フィルム等が耐熱性の高いフィルムとして知られており、同様の目的で使用することが可能である。また、他のフィルム、例えば、ポリエチレン、ポリプロピレン、耐熱塩化ビニル等の材料でも、塗液の塗工条件、さらに言えば乾燥条件が許せば使用可能である。   As the support 2 in the forgery-preventing magnetic tape transfer sheet, a polyethylene terephthalate resin film having a stable thickness and high heat resistance is generally used, but is not limited thereto. As other materials, polyethylene naphthalate resin films, polyimide resin films and the like are known as films having high heat resistance, and can be used for the same purpose. In addition, other films such as polyethylene, polypropylene, heat-resistant vinyl chloride and the like can be used as long as coating conditions for the coating liquid, more specifically, drying conditions permit.

前記偽造防止磁気テープ転写シートに於ける保護層3としてはポリメチルメタクリレート樹脂と他の熱可塑性樹脂、例えば塩化ビニル/酢酸ビニル共重合体もしくはニトロセルロース樹脂との混合物、又はポリメチルメタクリレート樹脂とポリエチレンワックスとの混合物等が挙げられ、又、酢酸セルロース樹脂と熱硬化性樹脂、例えばエポキシ樹脂、フェノール樹脂、熱硬化型アクリル樹脂もしくはメラミン樹脂との混合物が好ましい例として挙げられる。   As the protective layer 3 in the anti-counterfeit magnetic tape transfer sheet, a polymethyl methacrylate resin and another thermoplastic resin such as a mixture of vinyl chloride / vinyl acetate copolymer or nitrocellulose resin, or a polymethyl methacrylate resin and polyethylene are used. A mixture of wax and the like can be mentioned, and a mixture of cellulose acetate resin and thermosetting resin such as epoxy resin, phenol resin, thermosetting acrylic resin or melamine resin can be mentioned as a preferable example.

支持体2と保護層3との関係としては、材質どうしの関係で何もしなくても剥離可能な場合もあるが、一般的には剥離層もしくは離型層と呼ばれる層を中間に設けて剥離可能にするとか、どちらかの層に剥離を容易にする表面処理を行うことが必要に応じて設けられる。   As for the relationship between the support 2 and the protective layer 3, there is a case where it can be peeled without doing anything because of the relationship between materials, but in general, a layer called a peeling layer or a release layer is provided in the middle for peeling. If necessary, surface treatment for facilitating peeling is provided on either layer as necessary.

この中間の層は、一方の層に剥離層もしくは離型層という形で設けられるものでも、剥がした結果、その中間の層自体の中程から剥がれて両層にそれぞれ部分的に残る構成でも構わない。   This intermediate layer may be provided in the form of a release layer or a release layer on one layer, or may be configured to peel off from the middle of the intermediate layer itself and remain partially in both layers as a result of peeling. Absent.

前記偽造防止磁気テープ転写シートに於いて、回折構造形成層4は、その表面に回折格子を構成する凹凸を付与し、この上に、かつ、この凹凸に沿って設けられる回折効果層4に凹凸を付与するものである。そして、回折効果層4の凹凸表面で反射された回折光は互いに干渉して構造色を有するに至る。一般に、この回折現象によって得られる構造色は、観察者の位置によって異なる色彩を有する。   In the forgery-preventing magnetic tape transfer sheet, the diffractive structure forming layer 4 imparts irregularities constituting the diffraction grating on the surface thereof, and the diffractive effect layer 4 provided thereon and along the irregularities has irregularities. Is given. And the diffracted light reflected by the uneven surface of the diffraction effect layer 4 interferes with each other and has a structural color. In general, the structural color obtained by this diffraction phenomenon has different colors depending on the position of the observer.

回折構造形成層4は、その表面にプレス版にて前記凹凸を成形することが可能であるという性能が要求され、その主となる材質は熱可塑性樹脂、熱硬化性樹脂、紫外線あるいは電子線硬化性樹脂のいずれであっても良い。   The diffractive structure forming layer 4 is required to have a performance capable of forming the unevenness on its surface with a press plate, and the main material is thermoplastic resin, thermosetting resin, ultraviolet ray or electron beam curing. Any of the functional resins may be used.

回折構造形成層4に使用可能な材料は、例えば、アクリル系樹脂、エポキシ系樹脂、セルロース系樹脂、ビニル系樹脂等の熱可塑性樹脂や、反応性水酸基を有するアクリルポリオールやポリエステルポリオール等にポリイソシアネートを架橋剤として添加、架橋したウレタン樹脂や、メラミン系樹脂、フェノール系樹脂等の熱硬化樹脂、エポキシ(メタ)アクリル、ウレタン(メタ)アクリレート等の紫外線あるいは電子線硬化樹脂を、単独もしくはこれらを複合して使用できる。また、前記以外のものであっても、前記凹凸を形成可能であれば適宜使用してよい。   Examples of materials that can be used for the diffractive structure forming layer 4 include polyisocyanates such as thermoplastic resins such as acrylic resins, epoxy resins, cellulose resins, and vinyl resins, acrylic polyols and polyester polyols having reactive hydroxyl groups, and the like. As a cross-linking agent, UV resins such as melamine resins and phenol resins, UV or electron beam curable resins such as epoxy (meth) acryl, urethane (meth) acrylate, etc. Can be used in combination. Moreover, even if it is a thing other than the above, as long as the said unevenness | corrugation can be formed, you may use suitably.

一方、微細凹凸形状を構成する回折格子としては、可干渉な二光線を干渉させて得られる干渉縞を感光材料に感光させるホログラフィ技術が利用できる。このホログラフィ技術によって、例えば、上記構造色を制御して、奥行き感のある立体的画像を構成することが可能である。   On the other hand, as the diffraction grating constituting the fine concavo-convex shape, a holographic technique can be used in which an interference fringe obtained by causing interference of two coherent light beams is exposed to a photosensitive material. With this holographic technique, for example, the structural color can be controlled to form a stereoscopic image with a sense of depth.

また、微小な画素毎にホログラフィ技術を適用して回折格子を形成し、これら回折格子を有する画素を多数配列して画面全体を構成することにより、高い輝感とコントラストを有する画像を表現することも可能である。なお、ホログラフィ技術に限らず、電子線により感光材料に回折格子を直接描画することにより、回折格子を有する前記画素を設けることも可能である。   In addition, a holographic technique is applied to each minute pixel to form a diffraction grating, and a large number of pixels having these diffraction gratings are arranged to form the entire screen, thereby expressing an image having high brightness and contrast. Is also possible. The pixel having the diffraction grating can be provided by directly drawing the diffraction grating on the photosensitive material with an electron beam, not limited to the holography technique.

なお、回折格子を有する画素をそれぞれ適当な形状(例えば、星型、等)で形成する手法や、これら画素で肉眼では見えない細かな文字(いわゆるマイクロ文字)を形成する手法、回折格子を使用していながらあたかも写真のように被写体の色彩を忠実に再現する手法、あるいは、回折格子を使用して、見る角度によって全く違う複数の画像を表現する手法等が開発されており、これら手法を利用することもできる。   In addition, a method for forming each pixel having a diffraction grating in an appropriate shape (for example, a star shape, etc.), a method for forming fine characters (so-called micro characters) that cannot be seen with the naked eye, and a diffraction grating are used. In addition, methods have been developed to faithfully reproduce the colors of the subject as if they were photographs, or to express multiple images that differ completely depending on the viewing angle using a diffraction grating. You can also

前記偽造防止磁気テープ転写シートに於いて、回折効果層5の材質としては、Al、Sn、Cr、Ni、Cu、又は、Au、Ag等の金属材料の単体か、若しくは、その化合物等の公知の真空蒸着材料、及びスパッタリング材料が挙げられる。   In the forgery-preventing magnetic tape transfer sheet, the material of the diffraction effect layer 5 is a single metal material such as Al, Sn, Cr, Ni, Cu, Au, Ag, or a compound thereof. The vacuum evaporation material of this, and sputtering material are mentioned.

一方、回折効果層5に高輝性光反射インキを使用する際は、アルミニウム、銀、ニッケル、金、銅、錫、インジウム、コバルト等の微細な金属粉、または金属ナノ粒子等を有機高分子樹脂に分散して得られた高輝性光反射インキを使用することが出来る。この場合には、回折構造形成層のレリーフ形成面を溶剤によりアタックさせない様にする注意が必要であるが、グラビア印刷法・フレキソ印刷法・スクリーン印刷法等の公知印刷手段により形成可能である。この様な印刷方式にて回折効果層を設ける場合には、乾燥後の膜厚が0.1〜10μm程度になるように調整すれば良い。   On the other hand, when the high-brightness light reflecting ink is used for the diffraction effect layer 5, fine metal powder such as aluminum, silver, nickel, gold, copper, tin, indium, cobalt, or metal nanoparticles is used as the organic polymer resin. It is possible to use a high-brightness light-reflecting ink obtained by dispersing in the above. In this case, care must be taken not to attack the relief forming surface of the diffractive structure forming layer with a solvent, but it can be formed by known printing means such as gravure printing, flexographic printing, and screen printing. When the diffraction effect layer is provided by such a printing method, the film thickness after drying may be adjusted to be about 0.1 to 10 μm.

前記偽造防止磁気テープ転写シートに於いて、耐熱層6は、前記回折構造形成層4及び回折効果層5のレリーフ形状を、カード製造工程の熱加工においても、上述した保護層と共にレリーフ形状を維持する役割を果たす。   In the anti-counterfeit magnetic tape transfer sheet, the heat-resistant layer 6 maintains the relief shape of the diffraction structure forming layer 4 and the diffraction effect layer 5 together with the above-described protective layer even in the thermal processing of the card manufacturing process. To play a role.

上記の目的を達成するために、筆者らの鋭意研究の結果、耐熱層の材料には、ガラス転移温度が150℃以上である樹脂成分を60%以上含むことが重要であるとの結論に至った。ガラス転移温度が150℃未満であると、熱がかかった場合に、結晶状態を保つことができずに耐熱層自体が軟化し、レリーフ形状を維持することができない。   In order to achieve the above object, as a result of intensive studies by the authors, it has been concluded that it is important for the material of the heat-resistant layer to contain at least 60% of a resin component having a glass transition temperature of 150 ° C. or higher. It was. When the glass transition temperature is less than 150 ° C., when heated, the crystalline state cannot be maintained, the heat-resistant layer itself is softened, and the relief shape cannot be maintained.

耐熱層には、ガラス転移温度150℃以上の樹脂以外に40%まで、従来既知の各種フィラー、充填剤、着色剤等を混ぜることができる。ここでは、特に材質に関しては限定しない。   In the heat-resistant layer, conventionally known various fillers, fillers, colorants and the like can be mixed up to 40% in addition to a resin having a glass transition temperature of 150 ° C. or higher. Here, the material is not particularly limited.

添加量に関して説明をすると、40%を超えて着色剤等を添加した場合、分散性が悪く塗膜強度が低下するため耐熱性が劣る結果となる。また、印刷適性が悪い(塗液の流動性や版乾き等)、塗液の保存性(沈降、凝集等)が悪いなどの理由が挙げられる。添加量の40%は、単純な重量比のことでは無く、比重を1と換算した場合の比率である。例えば、白色顔料である沈降性硫酸バリウム(比重5.5)を添加する場合には、比重1の樹脂成分60重量部に対して、220重量部まで添加することが可能である。   The amount of addition will be described. When a colorant or the like is added in excess of 40%, the dispersibility is poor and the coating strength is lowered, resulting in poor heat resistance. Further, there are reasons such as poor printability (flowability of coating liquid, plate drying, etc.) and poor storage stability (precipitation, aggregation, etc.) of the coating liquid. 40% of the added amount is not a simple weight ratio but a ratio when the specific gravity is converted to 1. For example, in the case of adding precipitated barium sulfate (specific gravity 5.5), which is a white pigment, it is possible to add up to 220 parts by weight with respect to 60 parts by weight of the resin component having a specific gravity of 1.

次に、ガラス転移温度150℃以上の樹脂としては、汎用溶剤に溶解(若しくは分散:エマルジョン型)可能であり、熱可塑性の樹脂であることが好ましい。ここで、使用可能な樹脂としては、ポリカーボネート樹脂(Tg.140〜150℃)、ポリアリレート樹脂(Tg.193℃)、ポリスルホン樹脂(Tg.190℃)、ポリエーテルスルホン樹脂(Tg.225℃)、ポリエーテルイミド樹脂(Tg.200℃以上)、環状ポリオレフィン共重合体(Tg.171℃)、変性ノルボルネン系樹脂(Tg.171℃)、ポリアミドイミド樹脂(Tg.200℃以上)、ポリイミド樹脂(Tg.250℃以上)等を挙げることができるが、これに限定されるものでは無い。その他、収縮等の問題無き場合には、熱硬化系、湿気硬化系、紫外線硬化系、電子線硬化系樹脂等を使用しても良い。   Next, the resin having a glass transition temperature of 150 ° C. or higher is preferably a thermoplastic resin that can be dissolved (or dispersed in an emulsion type) in a general-purpose solvent. Here, usable resins include polycarbonate resin (Tg. 140 to 150 ° C.), polyarylate resin (Tg. 193 ° C.), polysulfone resin (Tg. 190 ° C.), and polyether sulfone resin (Tg. 225 ° C.). , Polyetherimide resin (Tg. 200 ° C. or higher), cyclic polyolefin copolymer (Tg. 171 ° C.), modified norbornene resin (Tg. 171 ° C.), polyamideimide resin (Tg. 200 ° C. or higher), polyimide resin ( Tg. 250 ° C. or higher), but is not limited thereto. In addition, when there is no problem such as shrinkage, a thermosetting system, a moisture curing system, an ultraviolet curing system, an electron beam curing resin, or the like may be used.

次に、耐熱層6の膜を形成する際には、例えばグラビア印刷法・フレキソ印刷法・スクリーン印刷法等の公知印刷手段により形成可能である。この様な印刷方式にて耐熱層を設ける場合には、乾燥後の膜厚が0.1〜3.0μm程度になるように調整すれば良い。   Next, when the film of the heat-resistant layer 6 is formed, it can be formed by known printing means such as a gravure printing method, a flexographic printing method, and a screen printing method. When the heat-resistant layer is provided by such a printing method, the film thickness after drying may be adjusted to be about 0.1 to 3.0 μm.

耐熱層の膜厚が0.1μm以下になると、塗工時の均一な膜厚管理が困難となり、また、3.0μm以上となると、耐熱層の吸熱により、接着層8とカード基材との密着不良が生じ易くなる。   If the film thickness of the heat-resistant layer is 0.1 μm or less, it is difficult to control the uniform film thickness during coating, and if it is 3.0 μm or more, the heat absorption of the heat-resistant layer causes the adhesion layer 8 and the card substrate to Adhesion failure is likely to occur.

前記偽造防止磁気テープ転写シートに於いて、磁気記録層6は例えば公知の磁気塗料を用いて印刷もしくは塗布方法により形成したものである。磁気塗料としては例えば、ブチラール樹脂、塩化ビニル/酢酸ビニル共重合体、ウレタン樹脂、ポリエステル樹脂、セルロース系樹脂、アクリル樹脂、スチレン/マレイン酸共重合樹脂等の合成樹脂をバインダー樹脂とし、必要に応じ、ニトリルゴム等のゴム系樹脂、ウレタンエラストマーを添加し、磁性体としてはγ−Fe23、Co含有Fe23、Fe34、バリウムフエライト、ストロンチウムフエライト、Co・Ni・Fe・Crの単独もしくは合金、希土類Co磁性体の他、界面活性剤、シランカップリング剤、可塑剤、ワックス、シリコーンオイル、カーボンその他の顔料を必要に応じて添加し、3本ロール、サンドミル、ボールミル等により混練して作成したものを用いることができる。 In the forgery-preventing magnetic tape transfer sheet, the magnetic recording layer 6 is formed by printing or coating using, for example, a known magnetic paint. Examples of magnetic coating materials include butyral resins, vinyl chloride / vinyl acetate copolymers, urethane resins, polyester resins, cellulose resins, acrylic resins, styrene / maleic acid copolymer resins, and other binder resins. , Rubber resin such as nitrile rubber, and urethane elastomer are added, and γ-Fe 2 O 3 , Co-containing Fe 2 O 3 , Fe 3 O 4 , barium ferrite, strontium ferrite, Co · Ni · Fe · In addition to Cr alone or alloy, rare earth Co magnetic substance, surfactant, silane coupling agent, plasticizer, wax, silicone oil, carbon and other pigments are added as necessary, and three rolls, sand mill, ball mill, etc. What knead | mixed and prepared and can be used.

磁気記録層6は上記の塗布型以外にも、近年高密度記録の可能な点で注目されている蒸着、特に斜方蒸着によって形成された金属薄膜型のものでもよい。例えばニッケルやコバルトの単独もしくは合金の斜方蒸着膜がその具体例である。   In addition to the coating type described above, the magnetic recording layer 6 may be of a metal thin film type formed by vapor deposition that has been attracting attention in recent years because it enables high-density recording, particularly oblique deposition. For example, an oblique deposition film of nickel or cobalt alone or an alloy is a specific example.

前記偽造防止磁気テープ転写シートは偽造防止磁気テープ転写シートに於ける接着層7としては、様々なカード基材(例えば、塩ビ、PET−G、ポリカーボネート、ポリ乳酸)に接した状態で熱および圧力を与えられることにより、被転写材に接着する機能を有する公知の感熱樹脂(感熱性接着材料)が使用される。   The anti-counterfeit magnetic tape transfer sheet has heat and pressure in contact with various card base materials (for example, vinyl chloride, PET-G, polycarbonate, polylactic acid) as the adhesive layer 7 in the anti-counterfeit magnetic tape transfer sheet. Thus, a known heat-sensitive resin (heat-sensitive adhesive material) having a function of adhering to a transfer material is used.

以上、一実施例を説明してきたが、意匠性を向上すべく各層を着色することや表面に印刷を施す等、使用の目的により適宜利用可能である。また、各層の接着性を鑑み、各層間に接着アンカー層を設けることも可能である。   Although one embodiment has been described above, it can be appropriately used depending on the purpose of use, such as coloring each layer to improve the design and printing on the surface. In view of the adhesiveness of each layer, an adhesive anchor layer can be provided between the layers.

前記偽造防止磁気テープ転写シートに於いて、保護層3から金属反射層5までの総厚み
は2〜10μであり、好ましくは2〜6μである。上記厚みを2〜10μの範囲にすることにより、機械情報処理に支障なく磁気カードに使用することが出来る。
In the forgery-preventing magnetic tape transfer sheet, the total thickness from the protective layer 3 to the metal reflective layer 5 is 2 to 10 μm, preferably 2 to 6 μm. When the thickness is in the range of 2 to 10 μm, it can be used for a magnetic card without any trouble in mechanical information processing.

上記のように構成される前記偽造防止磁気テープ転写シート1を形成するに当たっては種々の方法があるが、例えば、支持体2片面に保護層3を従来公知の方法で塗布した後、回折構造形成層4を形成する樹脂組成物を塗布し、従来公知の方法で回折構造形成部9を形成する。次に、回折効果層5を真空蒸着法により形成した後、耐熱層6、磁気記録層7、接着層8を順次塗布して偽造防止磁気テープ転写シート1を形成する。   There are various methods for forming the anti-counterfeit magnetic tape transfer sheet 1 configured as described above. For example, after the protective layer 3 is applied to one side of the support 2 by a conventionally known method, a diffraction structure is formed. The resin composition for forming the layer 4 is applied, and the diffraction structure forming portion 9 is formed by a conventionally known method. Next, after forming the diffraction effect layer 5 by vacuum deposition, the heat-resistant layer 6, the magnetic recording layer 7, and the adhesive layer 8 are sequentially applied to form the forgery-preventing magnetic tape transfer sheet 1.

上記の様に構成される偽造防止磁気テープ転写シート1を使用するに際しては、例えば、図2、図3に示す如く、偽造防止磁気テープ転写シート1を所要の大きさ、形状に切断し、カード基材10に例えば加熱融着する等により貼着した後、支持体2を剥離して回折構造形成部9及び磁気記録層7を有するカードを形成することで本発明の磁気カードが得られる。形成された本発明の磁気カードはカードに回折構造形成部9及び磁気記録層7が一体に形成されており、必要に応じてカード表面の占有面積を小さくすることが出来、その結果カードの装飾性を与える部分が大きくなり、装飾性大なるカードが得られる。又、磁気記録層7上面に回折構造形成部9が形成されているため、磁気記録層7の黒色、茶色等の色が隠れて美麗なカードが得られる。   When using the anti-counterfeit magnetic tape transfer sheet 1 configured as described above, the anti-counterfeit magnetic tape transfer sheet 1 is cut into a required size and shape as shown in FIGS. After sticking to the base material 10 by, for example, heat fusion, the support 2 is peeled off to form a card having the diffraction structure forming portion 9 and the magnetic recording layer 7 to obtain the magnetic card of the present invention. In the formed magnetic card of the present invention, the diffractive structure forming portion 9 and the magnetic recording layer 7 are integrally formed on the card, so that the occupied area of the card surface can be reduced if necessary, and as a result, the decoration of the card The part which gives the sex becomes large, and the card with the great decoration is obtained. Further, since the diffraction structure forming portion 9 is formed on the upper surface of the magnetic recording layer 7, a beautiful card can be obtained by hiding the color of the magnetic recording layer 7 such as black or brown.

図4は、前記偽造防止磁気テープ転写シート1の他の実施例を示すもので、保護層3と回折構造形成層4との間に着色層11を設けたものである。着色層11としては、合成樹脂が使用可能であり、樹脂中に顔料を添加して着色した樹脂組成物を塗布して形成してもよく、合成樹脂のフィルム上に印刷を施したものを貼着して形成してもよい。着色層11が形成された偽造防止磁気テープ転写シート1はカード等に使用した際、カラフルなデザインのカードを得ることが出来る。以下具体的実施例を挙げて本発明を更に詳細に説明する。   FIG. 4 shows another embodiment of the anti-counterfeit magnetic tape transfer sheet 1 in which a colored layer 11 is provided between the protective layer 3 and the diffractive structure forming layer 4. As the colored layer 11, a synthetic resin can be used. The colored layer 11 may be formed by applying a colored resin composition by adding a pigment to the resin, or pasting a printed film on a synthetic resin film. You may wear and form. When the anti-counterfeit magnetic tape transfer sheet 1 on which the colored layer 11 is formed is used for a card or the like, a card having a colorful design can be obtained. Hereinafter, the present invention will be described in more detail with reference to specific examples.

基材として厚み25μのポリエステルフィルムを用い、このフィルムの片面に下記(1)、(2)、(3)、(4)、(5)の各組成物を用い、保護層(厚さ1.5μm)、回折構造形成層(厚さ1.5μm)、回折効果層(50nm)、耐熱層(1μm)、磁気記録層(15μm)、接着層(3μm)を順次塗布形成して偽造防止磁気テープ転写シートを作成した。尚、金属反射層は塗布ではなく真空蒸着法を用いて積層した。   A polyester film having a thickness of 25 μm was used as a substrate, and the following compositions (1), (2), (3), (4), and (5) were used on one side of the film, and a protective layer (thickness 1. 5 μm), a diffraction structure forming layer (thickness 1.5 μm), a diffraction effect layer (50 nm), a heat-resistant layer (1 μm), a magnetic recording layer (15 μm), and an adhesive layer (3 μm) are sequentially applied and formed to prevent forgery. A transfer sheet was prepared. The metal reflective layer was laminated using a vacuum deposition method instead of coating.

上記積層した偽造防止磁気テープ転写シートを0.1ミリの透明硬質塩化ビニルフィルムに熱転写し、支持体を取り除いた後、乳白及び透明硬質塩化ビニルフィルムを0.7〜0.8ミリの厚さになるように積層し、加熱,加圧により一枚の板にし、打ち抜きによりカードサイズ(54ミリ×86ミリ)に打ち抜くことにより、回折構造、磁気入りのプラスチックカードを作成した。得られたカードは美麗な外観を呈し、耐熱性が高く、カード製造時の光学薄膜の白化が少ない事を特徴とする、該偽造防止磁気テープ転写シートを貼付した磁気カードとなった。   The laminated anti-counterfeit magnetic tape transfer sheet was thermally transferred to a 0.1 mm transparent hard vinyl chloride film, the support was removed, and the milky white and transparent hard vinyl chloride film were 0.7 to 0.8 mm thick. A plastic card with a diffractive structure and magnetism was produced by stacking to form a single plate by heating and pressing and punching to a card size (54 mm × 86 mm) by punching. The resulting card was a magnetic card with the anti-counterfeit magnetic tape transfer sheet, characterized by having a beautiful appearance, high heat resistance, and less whitening of the optical thin film during card manufacture.

(1)剥離性保護層組成物
アクリル樹脂(Tg.105℃)・・19.2重量部
ポリエチレンパウダー・・・・・・・0.8重量部
メチルエチルケトン・・・・・・・・45.0重量部
トルエン・・・・・・・・・・・・・35.0重量部
(2)回折構造形成層組成物
ウレタン樹脂・・・・・・・・・・・20.0重量部
メチルエチルケトン・・・・・・・・50.0重量部
酢酸エチル・・・・・・・・・・・・30.0重量部
(3)回折効果層組成物
アルミニウム
(4)耐熱層組成物
変性ノルボルネン樹脂(Tg.171℃)・・20.0重量部
沈降性硫酸バリウム(比重5.5)・・・・・10.0重量部
メチルエチルケトン・・・・・・・40.0重量部
トルエン・・・・・・・・・・・・30.0重量部
(5)磁気記録層組成物
γ−Fe23・・・・・・・・・・30重量部
塩酸ビニル酢酸ビニル重合体・・・・・3重量部
ポリウレタンエラストマー・・・・・20重量部
トルエン・・・・・・・・・・・・・15重量部
メチルエチルケトン・・・・・・・・15重量部
イソプロピルアルコール・・・・・・16重量部
(6)接着層組成物
塩酸ビニル酢酸ビニル重合体・・・・20重量部
アクリル樹脂・・・・・・・・・・・10重量部
酢酸エチル・・・・・・・・・・・・20重量部
トルエン・・・・・・・・・・・・・50重量部
(1) Peelable protective layer composition acrylic resin (Tg. 105 ° C) ··· 19.2 parts by weight polyethylene powder ··· 0.8 parts by weight methyl ethyl ketone ··· 45.0 Part by weight Toluene: 35.0 parts by weight (2) Diffraction structure forming layer composition urethane resin: 20.0 parts by weight Methyl ethyl ketone ..... 50.0 parts by weight ethyl acetate ..... 30.0 parts by weight (3) Diffraction effect layer composition aluminum (4) Heat resistant layer composition modified norbornene resin (Tg. 171 ° C.) 20.0 parts by weight Precipitating barium sulfate (specific gravity 5.5) 10.0 parts by weight methyl ethyl ketone 40.0 parts by weight toluene .... 30.0 parts by weight (5) Magnetic recording layer composition γ Fe 2 O 3 .......... 30 parts by weight hydrochloric acid vinyl acetate vinyl polymer ..... 3 parts by weight polyurethane elastomer ----- 20 parts by weight of toluene ........ 15 parts by weight methyl ethyl ketone 15 parts by weight isopropyl alcohol 16 parts by weight (6) Adhesive layer composition Vinyl chloride vinyl acetate polymer 20 parts by weight Part acrylic resin ... 10 parts by weight ethyl acetate ... 20 parts by weight toluene ... 50 parts by weight Part

本発明の磁気カードの実施例に用いられる偽造防止磁気テープ転写シートを示す縦断面図である。It is a longitudinal cross-sectional view which shows the forgery prevention magnetic tape transfer sheet used for the Example of the magnetic card | curd of this invention. 偽造防止磁気テープ転写シートをカード基材に装着し支持体を剥離して本発明の磁気カードを製造している状態を示す縦断面図である。It is a longitudinal cross-sectional view which shows the state which mounts a forgery prevention magnetic tape transfer sheet to a card | curd base material, peels a support body, and manufactures the magnetic card | curd of this invention. 図2の剥離した状態を示す縦断面図である。It is a longitudinal cross-sectional view which shows the state which peeled in FIG. 本発明の磁気カードの他の実施例に用いられる偽造防止磁気テープ転写シートを示す縦断面図である。It is a longitudinal cross-sectional view which shows the forgery prevention magnetic tape transfer sheet used for the other Example of the magnetic card | curd of this invention.

符号の説明Explanation of symbols

1 回折構造入磁気偽造防止磁気テープ転写シート
2 支持体
3 保護層
4 回折構造形成層
5 回折効果層
6 耐熱層
7 磁気記録層
8 接着層
9 回折効果形成部
10 カード基材
11 着色層
DESCRIPTION OF SYMBOLS 1 Magnetic-counterfeit prevention magnetic tape transfer sheet 2 with diffraction structure 2 Support body 3 Protection layer 4 Diffraction structure formation layer 5 Diffraction effect layer 6 Heat-resistant layer 7 Magnetic recording layer 8 Adhesion layer 9 Diffraction effect formation part 10 Card base material 11 Colored layer

Claims (2)

基材として厚み25μのポリエステルフィルムを用い、このフィルムの片面に下記(1)、(2)、(3)、(4)、(5)、(6)の各組成物を用い、保護層(厚さ1.5μm)、回折構造形成層(厚さ1.5μm)、回折効果層(50nm)、耐熱層(1μm)、磁気記録層(15μm)、接着層(3μm)を順次形成したことを特徴とする偽造防止磁気テープ転写シート。A polyester film having a thickness of 25 μm was used as a substrate, and the following compositions (1), (2), (3), (4), (5), and (6) were used on one side of the film, and a protective layer ( A thickness of 1.5 μm), a diffraction structure forming layer (thickness of 1.5 μm), a diffraction effect layer (50 nm), a heat-resistant layer (1 μm), a magnetic recording layer (15 μm), and an adhesive layer (3 μm). Anti-counterfeit magnetic tape transfer sheet.
(1)剥離性保護層組成物  (1) Peelable protective layer composition
アクリル樹脂(Tg.105℃)・・19.2重量部Acrylic resin (Tg. 105 ° C) ... 19.2 parts by weight
ポリエチレンパウダー・・・・・・・0.8重量部Polyethylene powder ... 0.8 parts by weight
メチルエチルケトン・・・・・・・・45.0重量部Methyl ethyl ketone: 45.0 parts by weight
トルエン・・・・・・・・・・・・・35.0重量部Toluene 35.0 parts by weight
(2)回折構造形成層組成物  (2) Diffraction structure forming layer composition
ウレタン樹脂・・・・・・・・・・・20.0重量部Urethane resin ... 20.0 parts by weight
メチルエチルケトン・・・・・・・・50.0重量部Methyl ethyl ketone: 50.0 parts by weight
酢酸エチル・・・・・・・・・・・・30.0重量部Ethyl acetate ... 30.0 parts by weight
(3)回折効果層組成物  (3) Diffraction effect layer composition
アルミニウムaluminum
(4)耐熱層組成物  (4) Heat-resistant layer composition
変性ノルボルネン樹脂(Tg.171℃)・・20.0重量部Modified norbornene resin (Tg. 171 ° C) 20.0 parts by weight
沈降性硫酸バリウム(比重5.5)・・・・・10.0重量部Precipitated barium sulfate (specific gravity 5.5) ... 10.0 parts by weight
メチルエチルケトン・・・・・・・40.0重量部Methyl ethyl ketone ... 40.0 parts by weight
トルエン・・・・・・・・・・・・30.0重量部Toluene 30.0 parts by weight
(5)磁気記録層組成物  (5) Magnetic recording layer composition
γ−Fe2O3・・・・・・・・・・30重量部γ-Fe2O3 ... 30 parts by weight
塩酸ビニル酢酸ビニル重合体・・・・・3重量部Vinyl chloride vinyl acetate polymer 3 parts by weight
ポリウレタンエラストマー・・・・・20重量部Polyurethane elastomer: 20 parts by weight
トルエン・・・・・・・・・・・・・15重量部Toluene: 15 parts by weight
メチルエチルケトン・・・・・・・・15重量部Methyl ethyl ketone: 15 parts by weight
イソプロピルアルコール・・・・・・16重量部Isopropyl alcohol: 16 parts by weight
(6)接着層組成物  (6) Adhesive layer composition
塩酸ビニル酢酸ビニル重合体・・・・20重量部Vinyl chloride vinyl acetate polymer ... 20 parts by weight
アクリル樹脂・・・・・・・・・・・10重量部Acrylic resin ... 10 parts by weight
酢酸エチル・・・・・・・・・・・・20重量部Ethyl acetate ... 20 parts by weight
トルエン・・・・・・・・・・・・・50重量部Toluene: 50 parts by weight
請求項1記載の偽造防止磁気テープ転写シートを貼付したことを特徴とするカード。A card, to which the anti-counterfeit magnetic tape transfer sheet according to claim 1 is attached.
JP2006230255A 2006-08-28 2006-08-28 Anti-counterfeit magnetic tape transfer sheet and card Expired - Fee Related JP4867526B2 (en)