JP4414069B2 - Method for producing polymer compound for photoresist and method for producing photoresist composition - Google Patents

Method for producing polymer compound for photoresist and method for producing photoresist composition Download PDF

Info

Publication number
JP4414069B2
JP4414069B2 JP2000209287A JP2000209287A JP4414069B2 JP 4414069 B2 JP4414069 B2 JP 4414069B2 JP 2000209287 A JP2000209287 A JP 2000209287A JP 2000209287 A JP2000209287 A JP 2000209287A JP 4414069 B2 JP4414069 B2 JP 4414069B2
Authority
JP
Japan
Prior art keywords
group
meth
photoresist
polymer
groups
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2000209287A
Other languages
Japanese (ja)
Other versions
JP2002020424A (en
Inventor
隆 新井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Daicel Corp
Original Assignee
Daicel Chemical Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Daicel Chemical Industries Ltd filed Critical Daicel Chemical Industries Ltd
Priority to JP2000209287A priority Critical patent/JP4414069B2/en
Publication of JP2002020424A publication Critical patent/JP2002020424A/en
Application granted granted Critical
Publication of JP4414069B2 publication Critical patent/JP4414069B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【0001】
【発明の属する技術分野】
本発明は半導体の微細加工などを行う際に用いるフォトレジスト用高分子化合物とフォトレジスト組成物、並びに該フォトレジスト組成物を用いた半導体の製造方法に関する。
【0002】
【従来技術】
半導体製造工程で用いられるレジストは、光照射により照射部がアルカリ可溶性に変化する性質、シリコンウエハーへの密着性、プラズマエッチング耐性、用いる光に対する透明性等の特性を兼ね備えていなくてはならない。該レジストは、一般に、主剤であるポリマーと、光酸発生剤と、上記特性を調整するための数種の添加剤を含む溶液として用いられるが、用途に応じたレジストを調整するには、主剤であるポリマーが上記の各特性をバランス良く備えていることが極めて重要である。
【0003】
近年、半導体集積回路は集積化が進みLSIやVLSIが実用化されており、これに伴って最小パターンはサブミクロン領域に及び、さらに微細化する傾向にある。微細パターンの形成には、薄膜を形成した被処理基板上をレジストで被覆し、選択露光を行った後に現像してレジストパターンを作製し、これをマスクとしてドライエッチングを行い、その後前記レジストを除去することにより所望のパターンを得るリソグラフィ技術の使用が必須である。そしてこれに使用する露光光源として、当初は紫外線が使用されていたが、パターンの微細化に伴い波長の短い遠紫外線や電子線、X線等が使用されるようになってきた。
【0004】
そのため、特にエキシマレーザー(波長248nmのKrFレーザー、波長193nmのArFレーザー)を用いたリソグラフィ技術に対応して、高解像性、高感度、優れた耐ドライエッチング性を有するレジスト材料が要求されている。従来のレジストはフェノール樹脂又はノボラック樹脂をベースとするものが多いが、これらの材料は芳香族環を含んでおり、耐ドライエッチング性には優れているものの、KrFレーザー波長に対しては透明性が低く、ArFレーザー波長に至っては不透明である。このため、従来の樹脂を用いては微細パターンを得ることはできなかった。
【0005】
一方、最近、酸触媒と化学増幅効果を利用した高感度レジストについて、各種の提案がなされている。より具体的には、(1)活性光線(紫外線、遠紫外線、真空紫外光、電子線、X線、各種レーザー光など)の照射により酸を発生する光酸発生剤と、(2)酸に対して不安定な反復的に存在する枝分かれした基を有する重合体との組み合わせからなるレジスト組成物が注目されている。このレジスト組成物から形成されたレジスト膜に活性光線を照射すると、被照射部分において、光酸発生剤から酸が生成し、この酸の作用を受けて、重合体中の酸に対して不安定な反復的に存在する基が分解されて極性基が生成する。これによって、レジスト膜の露光領域及び未露光領域の溶解度特性に大きな変化が生じる。すなわち、露光領域の重合体は極性基が形成されてアルカリ可溶となるため、アルカリ水溶液や極性溶媒で現像することにより露光領域が選択的に除去される。一方、未露光領域の重合体は無極性であるため、無極性溶媒で現像すると未露光領域が選択的に除去される。したがって、現像液を選択することにより、ポジ型、ネガ型の何れにも使用可能となる。多くの場合、現像液としてアルカリ水溶液を用いることにより露光領域を除去している。なお、重合体中の酸に対して不安定な反復的に存在する枝分かれした基は保護されたアルカリ水溶性基であって、酸により重合体から脱離可能な基であることから、保護基と称されている。光酸発生剤から生成した酸の作用によりこの保護基の脱離反応(開裂反応)が生じるが、この反応に伴って、新たに酸が再生されるため、このレジスト組成物は化学増幅型となり、高感度である。
【0006】
最近、エキシマ光に対して透明なレジストとして、メタクリル酸t−ブチル重合体が提案されているが、このレジストは耐ドライエッチング性に欠ける。この耐ドライエッチング性を備え、さらにKrFレーザー、ArFレーザーの波長に対して透明性を持つものとして、脂環式基を有する重合体を用いた化学増幅型レジストが報告されている(特開平4−39665号公報、特開平5−257284号公報、特開平5−265212号公報、特開平7−234511号公報、特開平9−73173号公報など)。前記脂環式基に対応する脂環式炭化水素環として、ノルボルネン、パーヒドロアントラセン、シクロヘキサン、トリシクロデカン、アダマンタンなどが望ましい。
【0007】
しかしながら、上記の脂環式基を有する重合体を用いた化学増幅型レジストにおいては、耐ドライエッチング性を付与する脂環式基が、その組成比の増加につれて重合体の疎水性を高めるとともに剛直性をも増大させる。このため、フェノール樹脂又はノボラック樹脂をベースにしたレジスト並のドライエッチング耐性が得られる組成比、例えば脂環式基を有する構造単位が50モル%以上の領域では、高い疎水性に加え、その硬さのために触媒であるプロトン酸の拡散が妨げられ、増幅率が低下し、結果として生成するカルボン酸量が減少し、現像液であるアルカリ水溶液に対する溶解性が低下するという問題があった。
【0008】
また、これらのレジストは密着性に乏しく、脂環式基の導入によりレジスト膜が硬くなるため、レジスト膜にかかる歪みが大きくなって剥がれやすくなる。このため安定したパターン特性を得ることができないという問題もあった。
【0009】
【発明が解決しようとする課題】
従って、本発明の目的は、アルカリ可溶性や基板密着性等のレジスト特性、特に基板密着性に優れたフォトレジスト用高分子化合物と、この高分子化合物を含むフォトレジスト組成物を提供することにある。
本発明の他の目的は、安定したパターン特性を得ることができるフォトレジスト組成物、及び半導体の製造方法を提供することにある。
【0010】
【課題を解決するための手段】
本発明者らは、上記の目的を達成するため鋭意検討した結果、特定構造の重合開始剤を用いて得られるビニル重合体をフォトレジスト用樹脂として用いると、アルカリ可溶性や基板密着性等のレジスト特性、特に基板密着性が劇的に改善できることを見出し、本発明を完成するに至った。
【0011】
すなわち、本発明は、2〜4環の非芳香族性環式基を分子内に有する(メタ)アクリル酸エステルを全単量体成分に対して30〜90モル%含む単量体混合物を、下記式(1)〜(11)
【化1】

Figure 0004414069
【化2】
Figure 0004414069
(式中、m、n、xは自然数を示す)
から選択された分子内に酸素原子含有基又は置換若しくは無置換アミノ基を有する重合開始剤の存在下、アルコール類(但し、イソプロピルアルコールを除く)からなる重合溶媒中で重合反応に付すことを特徴とするビニル重合体からなるフォトレジスト用高分子化合物の製造方法を提供する。
【0012】
本発明は、また、上記の製造方法によりフォトレジスト用高分子化合物を製造し、得られたフォトレジスト用高分子化合物に光酸発生剤を配合することを特徴とするフォトレジスト組成物の製造方法を提供する。
本発明は、さらに、上記の製造方法によりフォトレジスト組成物を製造し、得られたフォトレジスト組成物を基材又は基板上に塗布してレジスト塗膜を形成し、露光及び現像を経てパターンを形成する工程を含む半導体の製造方法を提供する。
なお、本明細書では、上記発明のほか、分子内に酸素原子含有基又は置換若しくは無置換アミノ基を有する重合開始剤を用いた重合反応により得られるビニル重合体からなるフォトレジスト用高分子化合物についても説明する。
なお、本明細書では、「アクリル」と「メタクリル」とを「(メタ)アクリル」、「アクリロイル」と「メタクリロイル」とを「(メタ)アクリロイル」と総称する場合がある。
【0013】
【発明の実施の形態】
本発明のフォトレジスト用高分子化合物は、分子内に酸素原子含有基又は置換若しくは無置換アミノ基を有する重合開始剤を用いた重合反応により得られるビニル重合体からなる。このビニル重合体は単独重合体又は共重合体(ランダム重合体、交互重合体、ブロック重合体等)の何れであってもよい。また、前記フォトレジスト用高分子化合物は、前記ビニル重合体の1種又は2種以上で構成されていてもよく、前記ビニル重合体の1種又は2種以上と他の重合体とで構成されていてもよい。
【0014】
前記重合開始剤における酸素原子含有基としては、例えば、ヒドロキシル基、カルボキシル基、置換オキシ基、置換オキシカルボニル基、アシル基、置換又は無置換カルバモイル基、ヒドロキシイミノ基、置換オキシイミノ基、ニトロ基などが挙げられる。
【0015】
前記置換オキシ基には、例えば、メトキシ基、エトキシ基、プロポキシ基、t−ブチルオキシ基等のアルコキシ基(特に、C1-4アルコキシ基);フェノキシ基、ナフチルオキシ基等のアリールオキシ基;ベンジルオキシ基などのアラルキルオキシ基;アセトキシ基、プロピオニルオキシ基、ベンゾイルオキシ基等のアシルオキシ基(特に、C1-5脂肪族アシルオキシ基、芳香族アシルオキシ基);メトキシカルボニルオキシ基、エトキシカルボニルオキシ基等のアルコキシカルボニルオキシ基(特に、C1-4アルコキシ−カルボニルオキシ基);フェノキシカルボニルオキシ基等のアリールオキシカルボニルオキシ基;ベンジルオキシカルボニルオキシ基等のアラルキルオキシカルボニルオキシ基などが含まれる。前記置換オキシカルボニル基には、例えば、メトキシカルボニル基、エトキシカルボニル基、t−ブチルオキシカルボニル基等のアルコキシカルボニル基(特に、C1-4アルコキシ−カルボニル基);フェノキシカルボニル基等のアリールオキシカルボニル基;ベンジルオキシカルボニル基等のアラルキルオキシカルボニル基などが含まれる。
【0016】
前記アシル基としては、ホルミル基、アセチル基、プロピオニル基、ヘキサノイル基等の脂肪族アシル基(特に、C1-6脂肪族アシル基);ベンゾイル基等の芳香族アシル基;シクロヘキサンカルボニル基等の脂環式アシル基;ピリジンカルボニル基等の複素環式アシル基などが挙げられる。
【0017】
置換又は無置換カルバモイル基としては、例えば、カルバモイル基;メチルカルバモイル基、エチルカルバモイル基、ジメチルカルバモイル基、ジエチルカルバモイル基等のモノ又はジアルキルカルバモイル基(特に、モノ又はジC1-4アルキルカルバモイル基);1−ピロリジニルカルボニル基、ピペリジノカルボニル基、モルフォリノカルボニル基等の環状アミノカルボニル基などが挙げられる。前記置換オキシイミノ基には、例えば、メトキシイミノ基、エトキシイミノ基等のアルコキシイミノ基(特に、C1-4アルコキシイミノ基);フェノキシイミノ基等のアリールオキシイミノ基;ベンジルオキシイミノ基等のアラルキルオキシイミノ基などが含まれる。
【0018】
前記置換若しくは無置換アミノ基としては、例えば、アミノ基;メチルアミノ基、エチルアミノ基、ジメチルアミノ基、ジエチルアミノ基等のモノ又はジアルキルアミノ基(特に、モノ又はジC1-4アルキルアミノ基);1−ピロリジニル基、ピペリジノ基、モルフォリノ基等の環状アミノ基などが挙げられる。
【0019】
上記の酸素原子含有基及び置換若しくは無置換アミノ基の中でも、酸素原子含有基、特にヒドロキシル基又はカルボキシル基が好ましい。重合開始剤の種類としては、分子内に(特に、末端に)酸素原子含有基又は置換若しくは無置換アミノ基を有する開始剤であれば特に限定されないが、その代表的な例はアゾ系ラジカル重合開始剤である。
【0020】
前記アゾ系ラジカル重合開始剤の具体的な例として、例えば、下記式(1)で表される2,2′−アゾビス{2−メチル−N−[1,1−ビス(ヒドロキシメチル)−2−ヒドロキシエチル]プロピオンアミド}[例えば、和光純薬(株)製、商品名「VA−080」]、式(2)で表される2,2′−アゾビス{2−メチル−N−[2−(ヒドロキシブチル)]プロピオンアミド}[例えば、和光純薬(株)製、商品名「VA−085」]、式(3)で表される2,2′−アゾビス[2−メチル−N−(2−ヒドロキシエチル)プロピオンアミド][例えば、和光純薬(株)製、商品名「VA−086」]、式(4)で表される2,2′−アゾビス{2−[1−(2−ヒドロキシエチル)−2−イミダゾリン−2−イル]プロパン}ジヒドロクロリド、式(5)で表される2,2′−アゾビス[N−(2−カルボキシエチル)−2−メチルプロピオンアミジン]、式(6)で表される2,2′−アゾビス(2−メチルプロピオンアミドオキシム)、式(7)で表される4,4′−アゾビス(4−シアノ吉草酸)[例えば、大塚化学(株)製、商品名「ACVA」]、式(8)で表されるジメチル2,2′−アゾビス(2−メチルプロピオネート)、式(9)で表される1,1′−アゾビス(1−アセトキシ−1−フェニルエタン)などが挙げられる。なお、式(5)中、mは自然数を示す。
【0021】
【化1】
Figure 0004414069
【0022】
【化2】
Figure 0004414069
【0023】
【化3】
Figure 0004414069
【0024】
【化4】
Figure 0004414069
【0025】
【化5】
Figure 0004414069
【0026】
【化6】
Figure 0004414069
【0027】
【化7】
Figure 0004414069
【0028】
【化8】
Figure 0004414069
【0029】
【化9】
Figure 0004414069
【0030】
これらの開始剤うち、式(1)、(2)、(3)及び(4)で表される化合物は分子内にヒドロキシル基を有し[式(1)、(2)、(3)の化合物は、さらに置換カルバモイル基を有する]、式(5)及び(7)で表される化合物は分子内にカルボキシル基を有し[式(5)の化合物は、さらに、置換アミノ基及びヒドロキシイミノ基を有する]、式(6)で表される化合物は分子内にアミノ基(及びヒドロキシイミノ基)を有し、式(8)で表される化合物は分子内に置換オキシカルボニル基(アルコキシカルボニル基)を有し、式(9)で表される化合物は分子内に置換オキシ基(アシルオキシ基)を有している。
【0031】
また、分子内にオキシカルボニル基(−COO−)を有する高分子開始剤(例えば、アゾ系高分子開始剤)も本発明における重合開始剤に含まれる。このような高分子開始剤として、例えば、下記式(10)で表される化合物[例えば、和光純薬(株)製、商品名「VPE−0201」]、式(11)で表される化合物[例えば、和光純薬(株)製、商品名「VPE−0601」]などが挙げられる。なお、式(10)、(11)中、n及びxは自然数を示す。
【0032】
【化10】
Figure 0004414069
【0033】
【化11】
Figure 0004414069
【0034】
本発明において、前記ビニル重合体としては、ビニル重合可能なモノマーの単独又は共重合体であればよいが、特に、(メタ)アクリル系モノマーの単独若しくは共重合体又は(メタ)アクリル系モノマーと他のモノマーとの共重合体が好ましい。中でも、ビニル重合体として、構成単量体の少なくとも一部[例えば、10モル%以上(10〜95モル%程度)、好ましくは20モル%以上(20〜90モル%程度)、さらに好ましくは30モル%以上(30〜90モル%程度)]が多環の非芳香族性環式基を分子内に有する単量体、特に、多環の非芳香族性環式基を分子内に有する(メタ)アクリル酸エステルが好ましい。
【0035】
前記多環の非芳香族性環式基としては、アダマンタン環、ビシクロ[2.2.2]オクタン環、トリシクロ[5.2.1.02,6]デカン環、テトラシクロ[4.4.0.12,5.17,10]ドデカン環、ノルボルナン環、ノルボルネン環、イソボルナン環、ピナン環、ノルピナン環、ボルナン環、デカリン環(パーヒドロナフタレン環)、パーヒドロアントラセン環、パーヒドロフェナントレン環、パーヒドロアセナフテン環、パーヒドロフェナレン環、パーヒドロフルオレン環、パーヒドロインデン環等の2〜4環程度の多環脂環式炭化水素環(橋かけ環式炭化水素環)に対応する多環脂環式基;4−オキサトリシクロ[4.3.1.13,8]ウンデカン−5−オン環等の酸素原子等のヘテロ原子を含有する2〜4環程度の多環の複素環に対応する多環複素環式基が挙げられる。なお、前記多環複素環式基は、複数の環のうち少なくとも1つの環にヘテロ原子が含まれていればよい。
【0036】
前記多環の非芳香族性環式基の環には1又は2以上(例えば1〜4個程度)の置換基が結合していてもよい。このような置換基として、例えば、ハロゲン原子(フッ素、塩素、臭素、又はヨウ素原子)、アルキル基(メチル、エチル、イソプロピル基などのC1-6アルキル基、特にC1-4アルキル基など)、シクロアルキル基、アリール基(フェニル基、ナフチル基など)、ヒドロキシル基、ヒドロキシメチル基、アルコキシ基(メトキシ、エトキシ、イソプロポキシ基などのC1-6アルコキシ基、特にC1-4アルコキシ基など)、アシルオキシ基(アセチルオキシ、プロピオニルオキシ基、(メタ)アクリロイルオキシ基などのC2-6脂肪族アシルオキシ基、特にC2-4脂肪族アシルオキシ基など)、カルボキシル基、カルボキシメチル基、アルコキシカルボニル基(メトキシカルボニル、エトキシカルボニル、プロポキシカルボニル、t−ブチルオキシカルボニル基などのC1-6アルコキシ−カルボニル基、特にC1-4アルコキシ−カルボニル基など)、シクロアルキルオキシカルボニル基(シクロヘキシルオキシカルボニル基など)、アリールオキシカルボニル基(フェニルオキシカルボニル基など)、アラルキルオキシカルボニル基(ベンジルオキシカルボニル基など)、2−テトラヒドロピラニルオキシカルボニル基、2−テトラヒドロフラニルオキシカルボニル基、環にC1-4アルキル基等の置換基を有していてもよい2−オキソテトラヒドロフラニルオキシカルボニル基、置換又は無置換カルバモイル基(カルバモイル基;メチルカルバモイル、ジメチルカルバモイル、ジエチルカルバモイル基などのモノ又はジC1-4アルキルカルバモイル基など)、アシル基(アセチル、プロピオニル基などのC2-6脂肪族アシル基、特にC2-4脂肪族アシル基など)、オキソ基、置換又は無置換アミノ基(アミノ基;メチルアミノ、エチルアミノ、プロピルアミノ、ジメチルアミノ、ジエチルアミノ基などのモノ又はジC1-6アルキルアミノ基、特にモノ又はジC1-4アルキルアミノ基など)、シアノ基、ニトロ基などが挙げられる。前記ヒドロキシル基、ヒドロキシメチル基、カルボキシル基、カルボキシメチル基、アミノ基は慣用の保護基により保護されていてもよい。
【0037】
前記多環の非芳香族性環式基を分子内に有する単量体の代表的な例として、アダマンタン環を有する単量体を例にとると、例えば、1−(メタ)アクリロイルオキシアダマンタン、1−(メタ)アクリロイルオキシ−3,5−ジメチルアダマンタン、1−t−ブトキシカルボニル−3−(メタ)アクリロイルオキシアダマンタン、1,3−ビス(t−ブトキシカルボニル)−5−(メタ)アクリロイルオキシアダマンタン、1−t−ブトキシカルボニル−3−ヒドロキシ−5−(メタ)アクリロイルオキシアダマンタン、1−(2−テトラヒドロピラニルオキシカルボニル)−3−(メタ)アクリロイルオキシアダマンタン、1,3−ビス(2−テトラヒドロピラニルオキシカルボニル)−5−(メタ)アクリロイルオキシアダマンタン、1−ヒドロキシ−3−(2−テトラヒドロピラニルオキシカルボニル)−5−(メタ)アクリロイルオキシアダマンタン、1−ヒドロキシ−3−(メタ)アクリロイルオキシアダマンタン、1,3−ジヒドロキシ−5−(メタ)アクリロイルオキシアダマンタン、1−カルボキシ−3−(メタ)アクリロイルオキシアダマンタン、1,3−ジカルボキシ−5−(メタ)アクリロイルオキシアダマンタン、1−カルボキシ−3−ヒドロキシ−5−(メタ)アクリロイルオキシアダマンタン、1−(メタ)アクリロイルオキシ−4−オキソアダマンタン、3−ヒドロキシ−1−(メタ)アクリロイルオキシ−4−オキソアダマンタン、7−ヒドロキシ−1−(メタ)アクリロイルオキシ−4−オキソアダマンタンなどのアダマンタン環の橋頭位に(メタ)アクリロイルオキシ基が結合しているアダマンタン誘導体;2−(メタ)アクリロイルオキシ−2−メチルアダマンタン、1−ヒドロキシ−2−(メタ)アクリロイルオキシ−2−メチルアダマンタン、5−ヒドロキシ−2−(メタ)アクリロイルオキシ−2−メチルアダマンタン、1,3−ジヒドロキシ−2−(メタ)アクリロイルオキシ−2−メチルアダマンタン、1,5−ジヒドロキシ−2−(メタ)アクリロイルオキシ−2−メチルアダマンタン、1,3−ジヒドロキシ−6−(メタ)アクリロイルオキシ−6−メチルアダマンタンなどのアダマンタン環の橋頭位以外の炭素原子に(メタ)アクリロイルオキシ基が結合しているアダマンタン誘導体;1−(1−(メタ)アクリロイルオキシ−1−メチルエチル)アダマンタン、1−ヒドロキシ−3−(1−(メタ)アクリロイルオキシ−1−メチルエチル)アダマンタン、1,3−ジヒドロキシ−5−(1−(メタ)アクリロイルオキシ−1−メチルエチル)アダマンタン、1−(1−エチル−1−(メタ)アクリロイルオキシプロピル)アダマンタン、1−(1−エチル−1−(メタ)アクリロイルオキシプロピル)−3−ヒドロキシアダマンタン、1−(1−(メタ)アクリロイルオキシ−1−メチルプロピル)アダマンタン、1−(1−(メタ)アクリロイルオキシ−1−メチルプロピル)−3−ヒドロキシアダマンタン、1−(1−(メタ)アクリロイルオキシ−1,2−ジメチルプロピル)アダマンタン、1−(1−(メタ)アクリロイルオキシ−1,2−ジメチルプロピル)−3−ヒドロキシアダマンタン、1−(1−エチル−1−(メタ)アクリロイルオキシプロピル)−3,5−ジヒドロキシアダマンタン、1,3−ジヒドロキシ−5−(1−(メタ)アクリロイルオキシ−1−メチルプロピル)アダマンタン、1,3−ジヒドロキシ−5−(1−(メタ)アクリロイルオキシ−1,2−ジメチルプロピル)アダマンタンなどのアダマンタン環の橋頭位に(メタ)アクリロイルオキシアルキル基が結合しているアダマンタン誘導体などが挙げられる。これらのアダマンタン誘導体は、例えば、対応するアダマンタン骨格を有するアルコールと(メタ)アクリル酸又はその反応性誘導体とを慣用のエステル化反応に付すことにより製造することができる。
【0038】
アダマンタン環以外の多環の非芳香族性環式基を分子内に有する単量体の例としては、上記のアダマンタン環を有する単量体に対応する化合物、例えば、多環の非芳香族性環の橋頭位に(メタ)アクリロイルオキシ基が結合している化合物[例えば、1−(メタ)アクリロイルオキシ−4−オキサトリシクロ[4.3.1.13,8]ウンデカン−5−オンなど]、多環の非芳香族性環の橋頭位以外の炭素原子に(メタ)アクリロイルオキシ基が結合している化合物[例えば、8−ヒドロキシメチル−4−(メタ)アクリロイルオキシメチルトリシクロ[5.2.1.02,6]デカン、4−ヒドロキシメチル−8−(メタ)アクリロイルオキシメチルトリシクロ[5.2.1.02,6]デカン、4−(メタ)アクリロイルオキシメチルテトラシクロ[4.4.0.12,5.17,10]ドデカン、2−(メタ)アクリロイルオキシノルボルナン、2−(メタ)アクリロイルオキシイソボルナン、2−(メタ)アクリロイルオキシメチルノルボルナンなど]、多環の非芳香族性環の橋頭位に(メタ)アクリロイルオキシアルキル基が結合している化合物などが挙げられる。
前記ビニル重合体を構成する(メタ)アクリル系モノマーとしては、上記の多環の非芳香族性環式基を分子内に有する(メタ)アクリル酸エステルのほか、例えば、(a)(メタ)アクリル酸t−ブチルなどのt−ブチルオキシカルボニル基を有する単量体、(b)(メタ)アクリル酸2−テトラヒドロピラニルなどの2−テトラヒドロピラニルオキシカルボニル基を有する単量体、(c)(メタ)アクリル酸2−テトラヒドロフラニルなどの2−テトラヒドロフラニルオキシカルボニル基を有する単量体、(d)2−(メタ)アクリロイルオキシ−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−2−メチル−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−4,4−ジメチル−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−2,4,4−トリメチル−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−3,4,4−トリメチル−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−2,3,4,4−テトラメチル−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−3,3,4−トリメチル−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−2,3,3,4−テトラメチル−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−3,3,4,4−テトラメチル−γ−ブチロラクトン、2−(メタ)アクリロイルオキシ−2,3,3,4,4−ペンタメチル−γ−ブチロラクトン、3−(メタ)アクリロイルオキシ−γ−ブチロラクトン、3−(メタ)アクリロイルオキシ−3−メチル−γ−ブチロラクトン、3−(メタ)アクリロイルオキシ−4−メチル−γ−ブチロラクトン、3−(メタ)アクリロイルオキシ−3,4−ジメチル−γ−ブチロラクトン、3−(メタ)アクリロイルオキシ−4,4−ジメチル−γ−ブチロラクトン、3−(メタ)アクリロイルオキシ−3,4,4−トリメチル−γ−ブチロラクトンなどのγ−ブチロラクトン環を有する単量体、(e)(メタ)アクリル酸4−オキソシクロヘキシルなどのシクロヘキサン環などの単環の非芳香族性環式基(脂環式基、複素環式基)を有する単量体、(f)(メタ)アクリル酸などが挙げられる。
【0039】
また、前記(メタ)アクリル系モノマーと共重合可能なコモノマーとして、例えば、(g)スチレン、ビニルトルエン、α−メチルスチレンなどのスチレン系単量体、(h)無水マレイン酸、(i)ノルボルネン、5−ヒドロキシ−2−ノルボルネン、5−t−ブトキシカルボニルノルボルネン、5−(2−テトラヒドロピラニルオキシカルボニル)ノルボルネン、5−(2−テトラヒドロフラニルオキシカルボニル)ノルボルネン、4−オキサトリシクロ[5.2.1.02,6]デカン−8−エン−5−オン、3−オキサトリシクロ[5.2.1.02,6]デカン−8−エン−4−オン、5−オキサトリシクロ[6.2.1.02,7]ウンデカン−9−エン−6−オン、4−オキサトリシクロ[6.2.1.02,7]ウンデカン−9−エン−5−オン、4−オキサペンタシクロ[6.5.1.19,12.02,6.08,13]ペンタデカン−10−エン−5−オン、3−オキサペンタシクロ[6.5.1.19,12.02,6.08,13]ペンタデカン−10−エン−4−オン、5−オキサペンタシクロ[6.6.1.110,13.02,7.09,14]ヘキサデカン−11−エン−6−オン、4−オキサペンタシクロ[6.6.1.110,13.02,7.09,14]ヘキサデカン−11−エン−5−オンなどのノルボルネン誘導体又はその類縁体(ノルボルネン環に1又は2以上の非芳香族性又は芳香族性の炭素環又は複素環が縮合している化合物)などが挙げられる。
【0040】
前記ビニル重合体を得る際の重合方式は溶液重合、塊状重合、乳化重合、懸濁重合等の何れであってもよいが、溶液重合が特に好ましい。溶液重合に使用する溶媒として、例えば、テトラヒドロフラン、ジオキサンなどのエーテル類;ベンゼン、トルエン、キシレンなどの芳香族炭化水素類;アセトン、メチルエチルケトンなどのケトン類;メタノール、エタノールなどのアルコール類;四塩化炭素、クロロホルム、塩化メチレンなどのハロゲン化炭化水素類;ジメチルホルムアミド、ジメチルスルホキシドなどの非プロトン極性溶媒などが挙げられる。これらの有機溶媒は単独で又は2種以上組み合わせて使用できる。
【0041】
重合系内には重合開始剤とともに連鎖移動剤を存在させてもよい。連鎖移動剤としては慣用のものを使用できる。重合開始剤は、単量体と混合して系内に供給してもよく、単量体とは別個に系内に供給してもよい。また、重合開始剤は重合初期に反応系内に一括して添加してもよく、逐次的に添加してもよい。
【0042】
重合は、通常、攪拌下で行われる。攪拌は攪拌翼や攪拌子を回転させることにより行うことができる。回転は一定の速度で行うのが好ましい。
【0043】
重合温度は、重合方式によっても異なるが、例えば40〜150℃、好ましくは50〜100℃程度である。重合時間は、例えば1〜24時間、好ましくは3〜15時間程度である。
【0044】
ビニル重合体の重量平均分子量(Mw)は、好ましくは3,000〜100,000、さらに好ましくは5,000〜80,000程度であり、分散度(Mw/Mn)は、好ましくは7.0以下、さらに好ましくは6.0以下である。重量平均分子量及び分散度が上記範囲内にある場合にはレジスト用溶剤に対する溶解性が良好であり、化学増幅型レジストの基材高分子として有利である。重量平均分子量(Mw)及び分散度(Mw/Mn)が大きすぎると、レジスト膜が白濁したり、あるいは感度や解像度などのレジスト特性が低下する傾向を示す。なお、重量平均分子量(Mw)及び数平均分子量(Mn)は、屈折率(RI)を用いたテトラヒドロフラン溶媒でのゲルパーミションクロマトグラフィー(GPC)により、スチレン換算の値として得ることができる。ビニル重合体の重量平均分子量や分散度は、単量体の種類や組成比、重合開始剤の種類や量、重合温度や重合時間等を適宜選択することにより調整することができる。
【0045】
こうして得られるビニル重合体は、高分子主鎖の少なくとも片末端に、前記重合開始剤に由来する酸素原子含有基又は置換若しくは無置換アミノ基を有する。そのため、このビニル重合体をフォトレジスト用樹脂として用いると、上記酸素原子含有基又は置換若しくは無置換アミノ基により、基板に対する密着性が大幅に増大するとともに、アルカリ可溶性も向上する。
【0046】
本発明のフォトレジスト組成物は、前記本発明のフォトレジスト用高分子化合物(感光性高分子化合物)のほか、光酸発生剤、溶媒、及び必要に応じて各種添加剤を含んでいる。フォトレジスト組成物は酸のクエンチャーとしてアミン類を含んでいてもよい。
【0047】
前記光酸発生剤としては、露光光を照射することにより酸を発生するものであれば特に限定されず、慣用乃至公知の光酸発生剤を使用できる。例えば、光酸発生剤として、ジアゾニウム塩、ヨードニウム塩(例えば、ジフェニルヨードヘキサフルオロホスフェートなど)、スルホニウム塩(例えば、トリフェニルスルホニウムヘキサフルオロアンチモネート、トリフェニルスルホニウムヘキサフルオロホスフェート、トリフェニルスルホニウムメタンスルホネートなど)、スルホン酸エステル[例えば、1−フェニル−1−(4−メチルフェニル)スルホニルオキシ−1−ベンゾイルメタン、1,2,3−トリスルホニルオキシメチルベンゼン、1,3−ジニトロ−2−(4−フェニルスルホニルオキシメチル)ベンゼン、1−フェニル−1−(4−メチルフェニルスルホニルオキシメチル)−1−ヒドロキシ−1−ベンゾイルメタンなど]、オキサチアゾール誘導体、s−トリアジン誘導体、ジスルホン誘導体(ジフェニルジスルホンなど)、イミド化合物、オキシムスルホネート、ジアゾナフトキノン、ベンゾイントシレートなどが挙げられる。光酸発生剤は単独で又は2種以上組み合わせて使用できる。
【0048】
光酸発生剤の使用量は、光照射により生成する酸の強度や前記フォトレジスト用高分子化合物における各モノマー単位の比率などに応じて適宜選択でき、例えば、前記フォトレジスト用高分子化合物100重量部に対して0.1〜30重量部、好ましくは1〜25重量部、さらに好ましくは2〜20重量部程度の範囲から選択できる。
【0049】
前記溶媒としては、例えば、炭化水素類、ハロゲン化炭化水素類、アルコール類、エステル類、アミド類、ケトン類、エーテル類、セロソルブ類、カルビトール類、グリコールエーテルエステル類等の有機溶媒、及びこれらの混合溶媒などが挙げられる。
【0050】
上記フォトレジスト組成物は半導体の製造用に好適に使用できる。すなわち、例えば、前記フォトレジスト組成物を基材又は基板上に塗布し、乾燥した後、所定のマスクを介して、塗膜(レジスト膜)に光線を露光して(又は、さらに露光後ベークを行い)潜像パターンを形成し、次いで現像することにより、微細なパターンを高い精度で形成できる。
【0051】
基材又は基板としては、シリコンウエハ、金属、プラスチック、ガラス、セラミックなどが挙げられる。フォトレジスト組成物の塗布は、例えば、スピンコータ、ディップコータ、ローラコータなどの慣用の塗布手段を用いて行うことができる。塗膜の厚みは、例えば0.1〜20μm、好ましくは0.3〜2μm程度である。
【0052】
露光には、種々の波長の光線、例えば、紫外線、X線などが利用でき、半導体レジスト用では、通常、g線、i線、エキシマレーザー(例えば、XeCl、KrF、KrCl、ArF、ArClなど)などが使用される。露光エネルギーは、例えば1〜1000mJ/cm2、好ましくは10〜500mJ/cm2程度である。
【0053】
光照射により光酸発生剤から酸が生成し、この酸により前記フォトレジスト用高分子化合物のうち酸脱離性基が速やかに脱離して、可溶化に寄与するカルボキシル基等が生成する。本発明のフォトレジスト組成物は、特に基板密着性に優れるため、安定したパターン特性を得ることができる。
【0054】
【発明の効果】
本発明によれば、高分子化合物が特定構造の重合開始剤を用いた重合反応により得られたビニル重合体で構成されているので、レジスト特性、特に基板密着性が著しく改善される。そのため、レジスト膜の剥離が起こらず、高解像度の微細パターンを安定して得ることができる。
【0055】
【実施例】
以下に、実施例に基づいて本発明をより詳細に説明するが、本発明はこれらの実施例により何ら限定されるものではない。なお、物性の測定方法は、次の通りである。
【0056】
(1)重量平均分子量(Mw)及び分散度(Mw/Mn)
重合体の重量平均分子量(Mw)及び数平均分子量(Mn)は、屈折率計(RI)を用いたテトラヒドロフラン溶媒でのゲルパーミションクロマトグラフィー(GPC)により測定したポリスチレン換算の重量平均分子量及び数平均分子量として求めた。カラムとして、昭和電工(株)製のカラム「E−800」を4本直列につないだものを用い、カラム温度40℃、RI温度40℃、テトラヒドロフランの流速0.8ml/分の測定条件で測定した。分散度(Mw/Mn)は、これらの測定値から算出した。
【0057】
(2)基板密着性
スピンコーターを用いてシリコン基板上に形成したレジスト膜の密着性をJIS 5400に規定の碁盤目法試験に従って評価した。この場合、碁盤目状の切り傷として、すきま間隔=2mm、ます目数=25に設定した。また、碁盤目試験の評価点数も同様にJIS 5400/JISD 0202/碁盤目法試験に従った。
評価点数10:切り傷1本ごとが、細くて両側が滑らかで、切り傷の交点と正方形の1目1目にはがれがない。
評価点数8:切り傷の交点にわずかなはがれがあって、正方形の1目1目にはがれがなく、欠損部の面積は全正方形面積の5%以内である。
評価点数6:切り傷の両側と交点とにはがれがあって、欠損部の面積は全正方形面積の5〜15%である。
評価点数4:切り傷によるはがれの幅が広く、欠損部の面積は全正方形面積の15〜35%である。
評価点数2:切り傷によるはがれの幅は4点より広く、欠損部の面積は全正方形面積の35〜65%である。
評価点数0:はがれの面積は、全正方形面積の65%以上である。
【0058】
実施例1
三角フラスコにアダマンタンアクリレート(=1−アクリロイルオキシアダマンタン)2.34g(10.0mmole)、t−ブチルアクリレート1.28g(10.0mmole)、開始剤2,2′−アゾビス{2−メチル−N−[1,1−ビス(ヒドロキシメチル)−2−ヒドロキシエチル]プロピオンアミド}[和光純薬(株)製、商品名「VA−080」]0.35gを入れ、メタノール35.0gに溶解(懸濁)させてモノマー溶液とした。このモノマー溶液を、還流管および3方コックを備えた100mlフラスコに張り込み、温度を60℃に保ち、10時間攪拌した後、反応液を500mlのヘキサンに落とし、生じた沈殿をろ別した。さらにもう一度再沈精製操作を行うことにより目的とする樹脂(共重合体)0.5gを得た。回収したポリマーをGPC分析したところ、Mwが58,000、分散度(Mw/Mn)が4.20であった。得られたポリマーの基板密着性を評価したところ、評価点数8であった。
【0059】
実施例2
三角フラスコにアダマンタンアクリレート(=1−アクリロイルオキシアダマンタン)2.34g(10.0mmole)、t−ブチルアクリレート1.28g(10.0mmole)、開始剤2,2′−アゾビス{2−メチル−N−[2−(1−ヒドロキシブチル)]プロピオンアミド}[和光純薬(株)製、商品名「VA−085」]0.35gを入れ、メタノール35.0gに溶解(懸濁)させてモノマー溶液とした。このモノマー溶液を、還流管および3方コックを備えた100mlフラスコに張り込み、温度を60℃に保ち、10時間攪拌した後、反応液を500mlのヘキサンに落とし、生じた沈殿をろ別した。さらにもう一度再沈精製操作を行うことにより目的とする樹脂(共重合体)1.5gを得た。回収したポリマーをGPC分析したところ、Mwが15,000、分散度(Mw/Mn)が3.30であった。得られたポリマーの基板密着性を評価したところ、評価点数6であった。
【0060】
実施例3
三角フラスコにアダマンタンアクリレート(=1−アクリロイルオキシアダマンタン)2.34g(10.0mmole)、t−ブチルアクリレート1.28g(10.0mmole)、開始剤2,2′−アゾビス[2−メチル−N−(2−ヒドロキシエチル)プロピオンアミド][和光純薬(株)製、商品名「VA−086」]0.35gを入れ、メタノール35.0gに溶解(懸濁)させてモノマー溶液とした。このモノマー溶液を、還流管および3方コックを備えた100mlフラスコに張り込み、温度を60℃に保ち、10時間攪拌した後、反応液を500mlのヘキサンに落とし、生じた沈殿をろ別した。さらにもう一度再沈精製操作を行うことにより目的とする樹脂(共重合体)1.7gを得た。回収したポリマーをGPC分析したところ、Mwが9,000、分散度(Mw/Mn)が2.40であった。得られたポリマーの基板密着性を評価したところ、評価点数6であった。
【0061】
実施例4
三角フラスコにアダマンタンアクリレート(=1−アクリロイルオキシアダマンタン)2.34g(10.0mmole)、t−ブチルアクリレート1.28g(10.0mmole)、開始剤4,4′−アゾビス(4−シアノ吉草酸)[大塚化学(株)製、商品名「ACVA」]0.35gを入れ、メタノール35.0gに溶解(懸濁)させてモノマー溶液とした。このモノマー溶液を、還流管および3方コックを備えた100mlフラスコに張り込み、温度を60℃に保ち、10時間攪拌した後、反応液を500mlのヘキサンに落とし、生じた沈殿をろ別した。さらにもう一度再沈精製操作を行うことにより目的とする樹脂(共重合体)1.8gを得た。回収したポリマーをGPC分析したところ、Mwが12,000、分散度(Mw/Mn)が2.90であった。得られたポリマーの基板密着性を評価したところ、評価点数8であった。
【0062】
比較例1
三角フラスコにアダマンタンアクリレート(=1−アクリロイルオキシアダマンタン)2.34g(10.0mmole)、t−ブチルアクリレート1.28g(10.0mmole)、開始剤2,2′−アゾビス(2−メチルブチロニトリル)[和光純薬(株)製、商品名「V−59」]0.35gを入れ、メタノール35.0gに溶解(懸濁)させてモノマー溶液とした。このモノマー溶液を、還流管および3方コックを備えた100mlフラスコに張り込み、温度を60℃に保ち、10時間攪拌した後、反応液を500mlのヘキサンに落とし、生じた沈殿をろ別した。さらにもう一度再沈精製操作を行うことにより目的とする樹脂(共重合体)2.0gを得た。回収したポリマーをGPC分析したところ、Mwが8000、分散度(Mw/Mn)が2.30であった。得られたポリマーの基板密着性を評価したところ、評価点数0であった。
【0063】
比較例2
三角フラスコにアダマンタンアクリレート(=1−アクリロイルオキシアダマンタン)2.34g(10.0mmole)、t−ブチルアクリレート1.28g(10.0mmole)、開始剤2,2′−アゾビス(2,4−ジメチルバレロニトリル)[和光純薬(株)製、商品名「V−65」]0.35gを入れ、メタノール35.0gに溶解(懸濁)させてモノマー溶液とした。このモノマー溶液を、還流管および3方コックを備えた100mlフラスコに張り込み、温度を60℃に保ち、10時間攪拌した後、反応液を500mlのヘキサンに落とし、生じた沈殿をろ別した。さらにもう一度再沈精製操作を行うことにより目的とする樹脂(共重合体)2.1gを得た。回収したポリマーをGPC分析したところ、Mwが7800、分散度(Mw/Mn)が2.50であった。得られたポリマーの基板密着性を評価したところ、評価点数0であった。
上記の結果を表1にまとめた。
【0064】
【表1】
Figure 0004414069
【0065】
表1より、特定の官能基を有する開始剤を用いた実施例1〜4の樹脂をフォトレジスト用組成物に用いると、基板密着性が飛躍的に向上することが分かる。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a polymer compound for photoresist and a photoresist composition used when performing microfabrication of a semiconductor and the like, and a semiconductor manufacturing method using the photoresist composition.
[0002]
[Prior art]
The resist used in the semiconductor manufacturing process must have properties such as the property that the irradiated portion changes to alkali-soluble by light irradiation, adhesion to a silicon wafer, plasma etching resistance, and transparency to light used. The resist is generally used as a solution containing a polymer as a main ingredient, a photoacid generator, and several kinds of additives for adjusting the above characteristics. It is extremely important that the polymer as described above has the above properties in a well-balanced manner.
[0003]
In recent years, integration of semiconductor integrated circuits has progressed, and LSIs and VLSIs have been put into practical use. With this, the minimum pattern tends to be in the submicron region and further miniaturized. To form a fine pattern, the substrate to be processed on which a thin film is formed is coated with a resist, subjected to selective exposure and developed to produce a resist pattern, which is then used as a mask for dry etching, and then the resist is removed. Therefore, it is essential to use a lithography technique for obtaining a desired pattern. Ultraviolet rays were originally used as an exposure light source for this, but far-ultraviolet rays, electron beams, X-rays and the like having a short wavelength have come to be used with the miniaturization of patterns.
[0004]
For this reason, resist materials having high resolution, high sensitivity, and excellent dry etching resistance are particularly required for lithography techniques using excimer lasers (KrF laser with a wavelength of 248 nm, ArF laser with a wavelength of 193 nm). Yes. Many conventional resists are based on phenolic resins or novolac resins, but these materials contain aromatic rings and are excellent in dry etching resistance, but are transparent to KrF laser wavelengths. Is low and opaque to ArF laser wavelengths. For this reason, a fine pattern could not be obtained using a conventional resin.
[0005]
On the other hand, various proposals have recently been made regarding high-sensitivity resists utilizing an acid catalyst and a chemical amplification effect. More specifically, (1) a photoacid generator that generates acid upon irradiation with actinic rays (ultraviolet rays, far ultraviolet rays, vacuum ultraviolet rays, electron beams, X-rays, various laser beams, etc.), and (2) acid In contrast, a resist composition comprising a combination of a polymer having a branched group which is unstable and presents repeatedly is attracting attention. When a resist film formed from this resist composition is irradiated with actinic rays, an acid is generated from the photoacid generator at the irradiated portion, and the acid acts to cause instability to the acid in the polymer. Such repetitive groups are decomposed to produce polar groups. This causes a large change in the solubility characteristics of the exposed and unexposed areas of the resist film. That is, since the polymer in the exposed region is formed with a polar group and becomes alkali-soluble, the exposed region is selectively removed by development with an aqueous alkali solution or a polar solvent. On the other hand, since the polymer in the unexposed area is nonpolar, when it is developed with a nonpolar solvent, the unexposed area is selectively removed. Therefore, it is possible to use either a positive type or a negative type by selecting a developing solution. In many cases, an exposed area is removed by using an alkaline aqueous solution as a developer. In addition, the branched group which is present in the polymer and is unstable with respect to the acid is a protected alkaline water-soluble group which can be removed from the polymer by an acid. It is called. The action of the acid generated from the photoacid generator causes the elimination reaction (cleavage reaction) of this protecting group, but this resist composition becomes chemically amplified because a new acid is regenerated along with this reaction. High sensitivity.
[0006]
Recently, a t-butyl methacrylate polymer has been proposed as a resist transparent to excimer light, but this resist lacks dry etching resistance. A chemically amplified resist using a polymer having an alicyclic group has been reported as having such dry etching resistance and being transparent to the wavelengths of KrF laser and ArF laser (Japanese Patent Laid-Open No. Hei 4). No. -39665, JP-A-5-257284, JP-A-5-265212, JP-A-7-234511, JP-A-9-73173, etc.). As the alicyclic hydrocarbon ring corresponding to the alicyclic group, norbornene, perhydroanthracene, cyclohexane, tricyclodecane, adamantane and the like are desirable.
[0007]
However, in a chemically amplified resist using a polymer having the above alicyclic group, the alicyclic group imparting dry etching resistance increases the hydrophobicity of the polymer and increases its rigidity as the composition ratio increases. Increases sex. For this reason, in a composition ratio that can provide dry etching resistance comparable to that of a resist based on a phenol resin or novolac resin, for example, in a region where the structural unit having an alicyclic group is 50 mol% or more, in addition to its high hydrophobicity, its hardness is increased. For this reason, diffusion of the protonic acid as a catalyst is hindered, the amplification factor is lowered, the resulting amount of carboxylic acid is reduced, and the solubility in an alkaline aqueous solution as a developer is lowered.
[0008]
In addition, these resists have poor adhesion, and the introduction of the alicyclic group hardens the resist film, so that the strain applied to the resist film is increased and the resist film is easily peeled off. Therefore, there is a problem that stable pattern characteristics cannot be obtained.
[0009]
[Problems to be solved by the invention]
Accordingly, an object of the present invention is to provide a photoresist polymer compound excellent in resist properties such as alkali solubility and substrate adhesion, particularly substrate adhesion, and a photoresist composition containing the polymer compound. .
Another object of the present invention is to provide a photoresist composition capable of obtaining stable pattern characteristics and a method for producing a semiconductor.
[0010]
[Means for Solving the Problems]
As a result of intensive studies to achieve the above object, the present inventors have found that when a vinyl polymer obtained by using a polymerization initiator having a specific structure is used as a resin for a photoresist, a resist such as alkali solubility or substrate adhesion can be obtained. The inventors have found that characteristics, particularly substrate adhesion, can be dramatically improved, and have completed the present invention.
[0011]
  That is, the present inventionA monomer mixture containing 30 to 90 mol% of (meth) acrylic acid ester having 2 to 4 ring non-aromatic cyclic groups in the molecule is represented by the following formula (1) to (11)
[Chemical 1]
Figure 0004414069
[Chemical 2]
Figure 0004414069
(In the formula, m, n, and x represent natural numbers)
Characterized by being subjected to a polymerization reaction in a polymerization solvent comprising an alcohol (excluding isopropyl alcohol) in the presence of a polymerization initiator having an oxygen atom-containing group or a substituted or unsubstituted amino group in the molecule selected from The manufacturing method of the high molecular compound for photoresists which consists of said vinyl polymer is provided.
[0012]
  The present invention also providesA method for producing a photoresist composition is provided, wherein a polymer compound for photoresist is produced by the production method described above, and a photoacid generator is blended with the obtained polymer compound for photoresist.
  The present invention further provides:A semiconductor comprising a step of producing a photoresist composition by the above production method, applying the obtained photoresist composition on a substrate or a substrate to form a resist coating film, and forming a pattern through exposure and development A manufacturing method is provided.
  In the present specification, in addition to the above-described invention, a photoresist polymer compound comprising a vinyl polymer obtained by a polymerization reaction using a polymerization initiator having an oxygen atom-containing group or a substituted or unsubstituted amino group in the molecule. Is also explained.
  In this specification, “acryl” and “methacryl” may be collectively referred to as “(meth) acryl”, and “acryloyl” and “methacryloyl” may be collectively referred to as “(meth) acryloyl”.
[0013]
DETAILED DESCRIPTION OF THE INVENTION
The polymer compound for photoresist of the present invention comprises a vinyl polymer obtained by a polymerization reaction using a polymerization initiator having an oxygen atom-containing group or a substituted or unsubstituted amino group in the molecule. This vinyl polymer may be either a homopolymer or a copolymer (random polymer, alternating polymer, block polymer, etc.). The photoresist polymer compound may be composed of one or more of the vinyl polymers, and is composed of one or more of the vinyl polymers and another polymer. It may be.
[0014]
Examples of the oxygen atom-containing group in the polymerization initiator include a hydroxyl group, a carboxyl group, a substituted oxy group, a substituted oxycarbonyl group, an acyl group, a substituted or unsubstituted carbamoyl group, a hydroxyimino group, a substituted oxyimino group, and a nitro group. Is mentioned.
[0015]
Examples of the substituted oxy group include alkoxy groups such as a methoxy group, an ethoxy group, a propoxy group, and a t-butyloxy group (in particular, C1-4An alkoxy group); an aryloxy group such as a phenoxy group or a naphthyloxy group; an aralkyloxy group such as a benzyloxy group; an acyloxy group such as an acetoxy group, a propionyloxy group or a benzoyloxy group (particularly C1-5Aliphatic acyloxy group, aromatic acyloxy group); alkoxycarbonyloxy group such as methoxycarbonyloxy group, ethoxycarbonyloxy group (especially C1-4Alkoxy-carbonyloxy group); aryloxycarbonyloxy groups such as phenoxycarbonyloxy group; aralkyloxycarbonyloxy groups such as benzyloxycarbonyloxy group and the like. Examples of the substituted oxycarbonyl group include alkoxycarbonyl groups such as a methoxycarbonyl group, an ethoxycarbonyl group, and a t-butyloxycarbonyl group (in particular, C1-4Alkoxy-carbonyl groups); aryloxycarbonyl groups such as phenoxycarbonyl groups; aralkyloxycarbonyl groups such as benzyloxycarbonyl groups and the like.
[0016]
Examples of the acyl group include aliphatic acyl groups such as formyl group, acetyl group, propionyl group, hexanoyl group (especially C1-6An aliphatic acyl group); an aromatic acyl group such as a benzoyl group; an alicyclic acyl group such as a cyclohexanecarbonyl group; a heterocyclic acyl group such as a pyridinecarbonyl group.
[0017]
Examples of the substituted or unsubstituted carbamoyl group include a carbamoyl group; a mono- or dialkylcarbamoyl group such as a methylcarbamoyl group, an ethylcarbamoyl group, a dimethylcarbamoyl group, and a diethylcarbamoyl group (particularly mono- or di-C).1-4Alkylcarbamoyl group); cyclic aminocarbonyl groups such as 1-pyrrolidinylcarbonyl group, piperidinocarbonyl group and morpholinocarbonyl group. Examples of the substituted oxyimino group include alkoxyimino groups such as methoxyimino group and ethoxyimino group (in particular, C1-4Alkoxyoxymino groups); aryloxyimino groups such as phenoxyimino groups; aralkyloxyimino groups such as benzyloxyimino groups and the like.
[0018]
Examples of the substituted or unsubstituted amino group include an amino group; a mono- or dialkylamino group such as a methylamino group, an ethylamino group, a dimethylamino group, and a diethylamino group (in particular, a mono- or di-C).1-4Alkylamino group); cyclic amino groups such as 1-pyrrolidinyl group, piperidino group and morpholino group.
[0019]
Among the above oxygen atom-containing groups and substituted or unsubstituted amino groups, oxygen atom-containing groups, particularly hydroxyl groups or carboxyl groups are preferred. The type of the polymerization initiator is not particularly limited as long as it is an initiator having an oxygen atom-containing group or a substituted or unsubstituted amino group in the molecule (particularly at the terminal), but a representative example thereof is azo radical polymerization. It is an initiator.
[0020]
As a specific example of the azo radical polymerization initiator, for example, 2,2′-azobis {2-methyl-N- [1,1-bis (hydroxymethyl) -2 represented by the following formula (1): -Hydroxyethyl] propionamide} [for example, product name “VA-080” manufactured by Wako Pure Chemical Industries, Ltd.], 2,2′-azobis {2-methyl-N- [2] represented by the formula (2) -(Hydroxybutyl)] propionamide} [for example, trade name “VA-085” manufactured by Wako Pure Chemical Industries, Ltd.], 2,2′-azobis [2-methyl-N— represented by the formula (3) (2-hydroxyethyl) propionamide] [for example, trade name “VA-086” manufactured by Wako Pure Chemical Industries, Ltd.], 2,2′-azobis {2- [1- ( 2-hydroxyethyl) -2-imidazolin-2-yl] propane} dihydride Chloride, 2,2'-azobis [N- (2-carboxyethyl) -2-methylpropionamidine] represented by formula (5), 2,2'-azobis (2- Methylpropionamidooxime), 4,4′-azobis (4-cyanovaleric acid) represented by formula (7) [for example, trade name “ACVA” manufactured by Otsuka Chemical Co., Ltd.], represented by formula (8) Dimethyl 2,2'-azobis (2-methylpropionate), 1,1'-azobis (1-acetoxy-1-phenylethane) represented by the formula (9), and the like. In formula (5), m represents a natural number.
[0021]
[Chemical 1]
Figure 0004414069
[0022]
[Chemical 2]
Figure 0004414069
[0023]
[Chemical Formula 3]
Figure 0004414069
[0024]
[Formula 4]
Figure 0004414069
[0025]
[Chemical formula 5]
Figure 0004414069
[0026]
[Chemical 6]
Figure 0004414069
[0027]
[Chemical 7]
Figure 0004414069
[0028]
[Chemical 8]
Figure 0004414069
[0029]
[Chemical 9]
Figure 0004414069
[0030]
Among these initiators, the compounds represented by the formulas (1), (2), (3) and (4) have a hydroxyl group in the molecule [of the formulas (1), (2) and (3) The compound further has a substituted carbamoyl group], the compounds represented by formulas (5) and (7) have a carboxyl group in the molecule [the compound of formula (5) further has a substituted amino group and a hydroxyimino group. The compound represented by formula (6) has an amino group (and a hydroxyimino group) in the molecule, and the compound represented by formula (8) has a substituted oxycarbonyl group (alkoxycarbonyl) in the molecule. The compound represented by the formula (9) has a substituted oxy group (acyloxy group) in the molecule.
[0031]
In addition, a polymer initiator (for example, an azo polymer initiator) having an oxycarbonyl group (—COO—) in the molecule is also included in the polymerization initiator in the present invention. As such a polymer initiator, for example, a compound represented by the following formula (10) [for example, trade name “VPE-0201” manufactured by Wako Pure Chemical Industries, Ltd.], a compound represented by the formula (11) [For example, trade name “VPE-0601” manufactured by Wako Pure Chemical Industries, Ltd.]. In formulas (10) and (11), n and x represent natural numbers.
[0032]
[Chemical Formula 10]
Figure 0004414069
[0033]
Embedded image
Figure 0004414069
[0034]
In the present invention, the vinyl polymer may be a vinyl-polymerizable monomer alone or a copolymer, and in particular, a (meth) acrylic monomer alone or a copolymer or a (meth) acrylic monomer Copolymers with other monomers are preferred. Among them, as a vinyl polymer, at least a part of constituent monomers [for example, 10 mol% or more (about 10 to 95 mol%), preferably 20 mol% or more (about 20 to 90 mol%), more preferably 30 Mol% or more (approximately 30 to 90 mol%)] has a polycyclic non-aromatic cyclic group in the molecule, particularly a polycyclic non-aromatic cyclic group in the molecule ( (Meth) acrylic acid esters are preferred.
[0035]
Examples of the polycyclic non-aromatic cyclic group include an adamantane ring, a bicyclo [2.2.2] octane ring, and a tricyclo [5.2.1.0].2,6] Decane ring, tetracyclo [4.4.0.1]2,5. 17,10] Dodecane ring, norbornane ring, norbornene ring, isobornane ring, pinane ring, norpinane ring, bornane ring, decalin ring (perhydronaphthalene ring), perhydroanthracene ring, perhydrophenanthrene ring, perhydroacenaphthene ring, perhydrophena A polycyclic alicyclic group corresponding to about 2 to 4 polycyclic alicyclic hydrocarbon rings (bridged hydrocarbon rings) such as a len ring, perhydrofluorene ring, perhydroindene ring; 4-oxa Tricyclo [4.3.1.13,8And a polycyclic heterocyclic group corresponding to a polycyclic heterocyclic ring having about 2 to 4 rings containing a hetero atom such as an oxygen atom such as an undecan-5-one ring. In the polycyclic heterocyclic group, at least one of the plurality of rings may include a hetero atom.
[0036]
One or more (for example, about 1 to 4) substituents may be bonded to the ring of the polycyclic non-aromatic cyclic group. Examples of such substituents include halogen atoms (fluorine, chlorine, bromine, or iodine atoms), alkyl groups (methyl, ethyl, isopropyl groups, etc.1-6Alkyl groups, especially C1-4Alkyl group, etc.), cycloalkyl group, aryl group (phenyl group, naphthyl group, etc.), hydroxyl group, hydroxymethyl group, alkoxy group (methoxy, ethoxy, isopropoxy group, etc.)1-6Alkoxy groups, especially C1-4Alkoxy groups), acyloxy groups (acetyloxy, propionyloxy groups, (meth) acryloyloxy groups, etc.)2-6Aliphatic acyloxy groups, especially C2-4Aliphatic acyloxy groups, etc.), carboxyl groups, carboxymethyl groups, alkoxycarbonyl groups (methoxycarbonyl, ethoxycarbonyl, propoxycarbonyl, t-butyloxycarbonyl groups, etc.)1-6Alkoxy-carbonyl groups, especially C1-4Alkoxy-carbonyl group etc.), cycloalkyloxycarbonyl group (cyclohexyloxycarbonyl group etc.), aryloxycarbonyl group (phenyloxycarbonyl group etc.), aralkyloxycarbonyl group (benzyloxycarbonyl group etc.), 2-tetrahydropyranyloxy Carbonyl group, 2-tetrahydrofuranyloxycarbonyl group, C on ring1-42-oxotetrahydrofuranyloxycarbonyl group which may have a substituent such as alkyl group, substituted or unsubstituted carbamoyl group (carbamoyl group; mono- or di-C such as methylcarbamoyl, dimethylcarbamoyl, diethylcarbamoyl group)1-4Alkylcarbamoyl groups), acyl groups (acetyl, propionyl groups, etc.)2-6Aliphatic acyl groups, especially C2-4Mono- or di-C such as an aliphatic acyl group, an oxo group, a substituted or unsubstituted amino group (amino group; methylamino, ethylamino, propylamino, dimethylamino, diethylamino group, etc.)1-6Alkylamino groups, especially mono- or di-C1-4Alkylamino group), cyano group, nitro group and the like. The hydroxyl group, hydroxymethyl group, carboxyl group, carboxymethyl group and amino group may be protected by a conventional protecting group.
[0037]
As a typical example of the monomer having a polycyclic non-aromatic cyclic group in the molecule, when a monomer having an adamantane ring is taken as an example, for example, 1- (meth) acryloyloxyadamantane, 1- (meth) acryloyloxy-3,5-dimethyladamantane, 1-t-butoxycarbonyl-3- (meth) acryloyloxyadamantane, 1,3-bis (t-butoxycarbonyl) -5- (meth) acryloyloxy Adamantane, 1-t-butoxycarbonyl-3-hydroxy-5- (meth) acryloyloxyadamantane, 1- (2-tetrahydropyranyloxycarbonyl) -3- (meth) acryloyloxyadamantane, 1,3-bis (2 -Tetrahydropyranyloxycarbonyl) -5- (meth) acryloyloxyadamantane, 1 Hydroxy-3- (2-tetrahydropyranyloxycarbonyl) -5- (meth) acryloyloxyadamantane, 1-hydroxy-3- (meth) acryloyloxyadamantane, 1,3-dihydroxy-5- (meth) acryloyloxyadamantane 1-carboxy-3- (meth) acryloyloxyadamantane, 1,3-dicarboxy-5- (meth) acryloyloxyadamantane, 1-carboxy-3-hydroxy-5- (meth) acryloyloxyadamantane, 1- ( Bridge head positions of adamantane rings such as (meth) acryloyloxy-4-oxoadamantane, 3-hydroxy-1- (meth) acryloyloxy-4-oxoadamantane, 7-hydroxy-1- (meth) acryloyloxy-4-oxoadamantane ( A) an adamantane derivative to which an acryloyloxy group is bonded; 2- (meth) acryloyloxy-2-methyladamantane, 1-hydroxy-2- (meth) acryloyloxy-2-methyladamantane, 5-hydroxy-2- ( (Meth) acryloyloxy-2-methyladamantane, 1,3-dihydroxy-2- (meth) acryloyloxy-2-methyladamantane, 1,5-dihydroxy-2- (meth) acryloyloxy-2-methyladamantane, 1, An adamantane derivative in which a (meth) acryloyloxy group is bonded to a carbon atom other than the bridge head position of an adamantane ring such as 3-dihydroxy-6- (meth) acryloyloxy-6-methyladamantane; 1- (1- (meth) Acryloyloxy-1-methylethyl) adamantane, 1- Hydroxy-3- (1- (meth) acryloyloxy-1-methylethyl) adamantane, 1,3-dihydroxy-5- (1- (meth) acryloyloxy-1-methylethyl) adamantane, 1- (1-ethyl) -1- (meth) acryloyloxypropyl) adamantane, 1- (1-ethyl-1- (meth) acryloyloxypropyl) -3-hydroxyadamantane, 1- (1- (meth) acryloyloxy-1-methylpropyl) Adamantane, 1- (1- (meth) acryloyloxy-1-methylpropyl) -3-hydroxyadamantane, 1- (1- (meth) acryloyloxy-1,2-dimethylpropyl) adamantane, 1- (1- ( (Meth) acryloyloxy-1,2-dimethylpropyl) -3-hydroxyadamantane, -(1-ethyl-1- (meth) acryloyloxypropyl) -3,5-dihydroxyadamantane, 1,3-dihydroxy-5- (1- (meth) acryloyloxy-1-methylpropyl) adamantane, 1,3 Examples thereof include adamantane derivatives in which a (meth) acryloyloxyalkyl group is bonded to the bridge head position of an adamantane ring such as -dihydroxy-5- (1- (meth) acryloyloxy-1,2-dimethylpropyl) adamantane. These adamantane derivatives can be produced, for example, by subjecting an alcohol having a corresponding adamantane skeleton and (meth) acrylic acid or a reactive derivative thereof to a conventional esterification reaction.
[0038]
Examples of monomers having a polycyclic non-aromatic cyclic group other than an adamantane ring in the molecule include compounds corresponding to the above-mentioned monomers having an adamantane ring, for example, polycyclic non-aromatic A compound in which a (meth) acryloyloxy group is bonded to the bridge head position of the ring [for example, 1- (meth) acryloyloxy-4-oxatricyclo [4.3.1.13,8] Undecan-5-one etc.], a compound in which a (meth) acryloyloxy group is bonded to a carbon atom other than the bridgehead position of a polycyclic non-aromatic ring [for example, 8-hydroxymethyl-4- (meth) Acryloyloxymethyltricyclo [5.2.1.02,6] Decane, 4-hydroxymethyl-8- (meth) acryloyloxymethyltricyclo [5.2.1.0]2,6] Decane, 4- (meth) acryloyloxymethyltetracyclo [4.4.0.1]2,5. 17,10] Dodecane, 2- (meth) acryloyloxynorbornane, 2- (meth) acryloyloxyisobornane, 2- (meth) acryloyloxymethylnorbornane, etc.], at the bridge head position of a polycyclic non-aromatic ring (meth) And compounds having an acryloyloxyalkyl group bonded thereto.
As the (meth) acrylic monomer constituting the vinyl polymer, in addition to the (meth) acrylic acid ester having a polycyclic non-aromatic cyclic group in the molecule, for example, (a) (meth) A monomer having a t-butyloxycarbonyl group such as t-butyl acrylate; (b) a monomer having a 2-tetrahydropyranyloxycarbonyl group such as 2-tetrahydropyranyl (meth) acrylate; ) Monomers having a 2-tetrahydrofuranyloxycarbonyl group such as (meth) acrylic acid 2-tetrahydrofuranyl, (d) 2- (meth) acryloyloxy-γ-butyrolactone, 2- (meth) acryloyloxy-2- Methyl-γ-butyrolactone, 2- (meth) acryloyloxy-4,4-dimethyl-γ-butyrolactone, 2- (meth) acrylo Ruoxy-2,4,4-trimethyl-γ-butyrolactone, 2- (meth) acryloyloxy-3,4,4-trimethyl-γ-butyrolactone, 2- (meth) acryloyloxy-2,3,4,4- Tetramethyl-γ-butyrolactone, 2- (meth) acryloyloxy-3,3,4-trimethyl-γ-butyrolactone, 2- (meth) acryloyloxy-2,3,4,4-tetramethyl-γ-butyrolactone, 2- (meth) acryloyloxy-3,3,4,4-tetramethyl-γ-butyrolactone, 2- (meth) acryloyloxy-2,3,3,4,4-pentamethyl-γ-butyrolactone, 3- ( (Meth) acryloyloxy-γ-butyrolactone, 3- (meth) acryloyloxy-3-methyl-γ-butyrolactone, 3- (meth) acrylic Royloxy-4-methyl-γ-butyrolactone, 3- (meth) acryloyloxy-3,4-dimethyl-γ-butyrolactone, 3- (meth) acryloyloxy-4,4-dimethyl-γ-butyrolactone, 3- (meta ) Monomer having a γ-butyrolactone ring such as acryloyloxy-3,4,4-trimethyl-γ-butyrolactone, (e) Monocyclic non-aromatic such as cyclohexane ring such as 4-oxocyclohexyl (meth) acrylate And monomers having an aliphatic cyclic group (an alicyclic group or a heterocyclic group), (f) (meth) acrylic acid, and the like.
[0039]
Examples of the comonomer copolymerizable with the (meth) acrylic monomer include (g) styrene monomers such as styrene, vinyltoluene, and α-methylstyrene, (h) maleic anhydride, and (i) norbornene. , 5-hydroxy-2-norbornene, 5-t-butoxycarbonylnorbornene, 5- (2-tetrahydropyranyloxycarbonyl) norbornene, 5- (2-tetrahydrofuranyloxycarbonyl) norbornene, 4-oxatricyclo [5. 2.1.02,6] Decan-8-en-5-one, 3-oxatricyclo [5.2.1.0]2,6] Decan-8-en-4-one, 5-oxatricyclo [6.2.1.0]2,7] Undecan-9-en-6-one, 4-oxatricyclo [6.2.1.0]2,7] Undecan-9-en-5-one, 4-oxapentacyclo [6.5.1.1]9,12. 02,6. 08,13] Pentadecan-10-en-5-one, 3-oxapentacyclo [6.5.1.1]9,12. 02,6. 08,13] Pentadecan-10-en-4-one, 5-oxapentacyclo [6.6.1.1]10,13. 02,7. 09,14] Hexadecan-11-en-6-one, 4-oxapentacyclo [6.6.1.1]10,13. 02,7. 09,14] Norbornene derivatives such as hexadecan-11-en-5-one or analogs thereof (compounds in which one or more non-aromatic or aromatic carbocycles or heterocycles are condensed on the norbornene ring). Can be mentioned.
[0040]
The polymerization method for obtaining the vinyl polymer may be any of solution polymerization, bulk polymerization, emulsion polymerization, suspension polymerization and the like, but solution polymerization is particularly preferable. Solvents used for solution polymerization include, for example, ethers such as tetrahydrofuran and dioxane; aromatic hydrocarbons such as benzene, toluene and xylene; ketones such as acetone and methyl ethyl ketone; alcohols such as methanol and ethanol; carbon tetrachloride Halogenated hydrocarbons such as chloroform, methylene chloride; aprotic polar solvents such as dimethylformamide and dimethyl sulfoxide. These organic solvents can be used alone or in combination of two or more.
[0041]
A chain transfer agent may be present together with the polymerization initiator in the polymerization system. Conventional chain transfer agents can be used. The polymerization initiator may be mixed with the monomer and supplied into the system, or may be supplied into the system separately from the monomer. Further, the polymerization initiator may be added all at once in the reaction system at the initial stage of polymerization, or may be added sequentially.
[0042]
The polymerization is usually carried out with stirring. Stirring can be performed by rotating a stirring blade or a stirring bar. The rotation is preferably performed at a constant speed.
[0043]
Although superposition | polymerization temperature changes also with superposition | polymerization systems, it is 40-150 degreeC, for example, Preferably it is about 50-100 degreeC. The polymerization time is, for example, about 1 to 24 hours, preferably about 3 to 15 hours.
[0044]
The weight average molecular weight (Mw) of the vinyl polymer is preferably about 3,000 to 100,000, more preferably about 5,000 to 80,000, and the dispersity (Mw / Mn) is preferably 7.0. Hereinafter, it is more preferably 6.0 or less. When the weight average molecular weight and the degree of dispersion are within the above ranges, the solubility in a resist solvent is good, which is advantageous as a base polymer for a chemically amplified resist. When the weight average molecular weight (Mw) and the dispersity (Mw / Mn) are too large, the resist film becomes cloudy or resist characteristics such as sensitivity and resolution tend to be lowered. The weight average molecular weight (Mw) and the number average molecular weight (Mn) can be obtained as styrene equivalent values by gel permeation chromatography (GPC) in a tetrahydrofuran solvent using a refractive index (RI). The weight average molecular weight and degree of dispersion of the vinyl polymer can be adjusted by appropriately selecting the type and composition ratio of the monomer, the type and amount of the polymerization initiator, the polymerization temperature and the polymerization time.
[0045]
The vinyl polymer thus obtained has an oxygen atom-containing group or a substituted or unsubstituted amino group derived from the polymerization initiator at at least one end of the polymer main chain. Therefore, when this vinyl polymer is used as a resin for a photoresist, the oxygen atom-containing group or the substituted or unsubstituted amino group greatly increases the adhesion to the substrate and also improves the alkali solubility.
[0046]
The photoresist composition of the present invention contains a photoacid generator, a solvent, and various additives as required, in addition to the polymer compound for photoresist (photosensitive polymer compound) of the present invention. The photoresist composition may contain amines as an acid quencher.
[0047]
The photoacid generator is not particularly limited as long as it generates an acid when irradiated with exposure light, and a conventional or known photoacid generator can be used. For example, as a photoacid generator, a diazonium salt, an iodonium salt (for example, diphenyliodohexafluorophosphate), a sulfonium salt (for example, triphenylsulfonium hexafluoroantimonate, triphenylsulfonium hexafluorophosphate, triphenylsulfonium methanesulfonate, etc.) ), Sulfonic acid esters [for example, 1-phenyl-1- (4-methylphenyl) sulfonyloxy-1-benzoylmethane, 1,2,3-trisulfonyloxymethylbenzene, 1,3-dinitro-2- (4 -Phenylsulfonyloxymethyl) benzene, 1-phenyl-1- (4-methylphenylsulfonyloxymethyl) -1-hydroxy-1-benzoylmethane, etc.], oxathiazole derivatives, s-triazis Derivatives, (such as diphenyl disulfone) disulfone derivatives, imide compound, an oxime sulfonate, a diazonaphthoquinone, and a benzoin tosylate. A photo-acid generator can be used individually or in combination of 2 or more types.
[0048]
The amount of the photoacid generator used can be appropriately selected according to the strength of the acid generated by light irradiation, the ratio of each monomer unit in the photoresist polymer compound, and the like, for example, 100 weight of the photoresist polymer compound. 0.1 to 30 parts by weight, preferably 1 to 25 parts by weight, and more preferably 2 to 20 parts by weight with respect to parts.
[0049]
Examples of the solvent include organic solvents such as hydrocarbons, halogenated hydrocarbons, alcohols, esters, amides, ketones, ethers, cellosolves, carbitols, glycol ether esters, and the like. Or a mixed solvent thereof.
[0050]
The said photoresist composition can be used conveniently for manufacture of a semiconductor. That is, for example, after applying the photoresist composition on a substrate or substrate and drying, the coating film (resist film) is exposed to light through a predetermined mask (or further subjected to post-exposure baking). Perform) A fine pattern can be formed with high accuracy by forming a latent image pattern and then developing it.
[0051]
Examples of the base material or the substrate include a silicon wafer, metal, plastic, glass, and ceramic. Application of the photoresist composition can be performed using a conventional application means such as a spin coater, a dip coater, or a roller coater. The thickness of the coating film is, for example, about 0.1 to 20 μm, preferably about 0.3 to 2 μm.
[0052]
For exposure, light of various wavelengths such as ultraviolet rays and X-rays can be used. For semiconductor resists, g-rays, i-rays, and excimer lasers (eg, XeCl, KrF, KrCl, ArF, ArCl, etc.) are usually used. Etc. are used. The exposure energy is, for example, 1-1000 mJ / cm2, Preferably 10 to 500 mJ / cm2Degree.
[0053]
By irradiation with light, an acid is generated from the photoacid generator, and this acid quickly removes an acid-eliminable group from the polymer compound for photoresist, thereby generating a carboxyl group that contributes to solubilization. Since the photoresist composition of the present invention is particularly excellent in substrate adhesion, stable pattern characteristics can be obtained.
[0054]
【The invention's effect】
According to the present invention, since the polymer compound is composed of a vinyl polymer obtained by a polymerization reaction using a polymerization initiator having a specific structure, resist characteristics, particularly substrate adhesion, are remarkably improved. Therefore, the resist film does not peel off, and a high-resolution fine pattern can be obtained stably.
[0055]
【Example】
Hereinafter, the present invention will be described in more detail based on examples, but the present invention is not limited to these examples. In addition, the measuring method of a physical property is as follows.
[0056]
(1) Weight average molecular weight (Mw) and dispersity (Mw / Mn)
The weight average molecular weight (Mw) and number average molecular weight (Mn) of the polymer are the weight average molecular weight and number average in terms of polystyrene measured by gel permeation chromatography (GPC) in a tetrahydrofuran solvent using a refractometer (RI). Calculated as molecular weight. Measured under the measurement conditions of column temperature 40 ° C, RI temperature 40 ° C, and tetrahydrofuran flow rate 0.8ml / min using four columns "E-800" made by Showa Denko Co., Ltd. connected in series. did. The degree of dispersion (Mw / Mn) was calculated from these measured values.
[0057]
(2) Substrate adhesion
The adhesion of the resist film formed on the silicon substrate using a spin coater was evaluated according to a cross-cut method test specified in JIS 5400. In this case, the clearance interval was set to 2 mm and the number of meshes was set to 25 as a grid-like cut. Moreover, the evaluation score of the cross cut test similarly followed the JIS 5400 / JISD 0202 / cross cut test.
Evaluation score 10: Each cut is thin and smooth on both sides, and there is no peeling between the cut intersection and the square.
Number of evaluation points 8: There is slight peeling at the intersection of the cuts, there is no peeling at a glance of the square, and the area of the missing part is within 5% of the total square area.
Evaluation score 6: There is peeling between both sides of the cut and the intersection, and the area of the missing part is 5 to 15% of the total square area.
Evaluation score 4: The width of the peeling due to the cut is wide, and the area of the missing part is 15 to 35% of the total square area.
Evaluation score 2: The width of the peeling due to the cut is wider than 4 points, and the area of the missing part is 35 to 65% of the total square area.
Evaluation score 0: The area of peeling is 65% or more of the total square area.
[0058]
Example 1
In an Erlenmeyer flask, 2.34 g (10.0 mmole) of adamantane acrylate (= 1-acryloyloxyadamantane), 1.28 g (10.0 mmole) of t-butyl acrylate, initiator 2,2′-azobis {2-methyl-N— [1,1-Bis (hydroxymethyl) -2-hydroxyethyl] propionamide} [trade name “VA-080”, manufactured by Wako Pure Chemical Industries, Ltd.] 0.35 g was added and dissolved in 35.0 g of methanol (suspended) To make a monomer solution. This monomer solution was put into a 100 ml flask equipped with a reflux tube and a three-way cock, and the temperature was kept at 60 ° C., followed by stirring for 10 hours. Then, the reaction solution was dropped into 500 ml of hexane, and the resulting precipitate was filtered off. Further, the reprecipitation purification operation was performed once again to obtain 0.5 g of the target resin (copolymer). When the collected polymer was analyzed by GPC, it was found that Mw was 58,000 and the dispersity (Mw / Mn) was 4.20. When the substrate adhesion of the obtained polymer was evaluated, the evaluation score was 8.
[0059]
Example 2
In an Erlenmeyer flask, 2.34 g (10.0 mmole) of adamantane acrylate (= 1-acryloyloxyadamantane), 1.28 g (10.0 mmole) of t-butyl acrylate, initiator 2,2′-azobis {2-methyl-N— [2- (1-Hydroxybutyl)] propionamide} [trade name “VA-085” manufactured by Wako Pure Chemical Industries, Ltd.] 0.35 g was added and dissolved (suspended) in 35.0 g of methanol to prepare a monomer solution. It was. This monomer solution was put into a 100 ml flask equipped with a reflux tube and a three-way cock, and the temperature was kept at 60 ° C., followed by stirring for 10 hours. Then, the reaction solution was dropped into 500 ml of hexane, and the resulting precipitate was filtered off. Further, reprecipitation purification operation was performed once again to obtain 1.5 g of the target resin (copolymer). When the collected polymer was analyzed by GPC, it was found that Mw was 15,000 and dispersity (Mw / Mn) was 3.30. When the substrate adhesion of the obtained polymer was evaluated, the evaluation score was 6.
[0060]
Example 3
Into an Erlenmeyer flask, 2.34 g (10.0 mmole) of adamantane acrylate (= 1-acryloyloxyadamantane), 1.28 g (10.0 mmole) of t-butyl acrylate, initiator 2,2′-azobis [2-methyl-N— (2-Hydroxyethyl) propionamide] [trade name “VA-086” manufactured by Wako Pure Chemical Industries, Ltd.] 0.35 g was added, and dissolved (suspended) in 35.0 g of methanol to obtain a monomer solution. This monomer solution was put into a 100 ml flask equipped with a reflux tube and a three-way cock, and the temperature was kept at 60 ° C., followed by stirring for 10 hours. Then, the reaction solution was dropped into 500 ml of hexane, and the resulting precipitate was filtered off. Furthermore, 1.7 g of the target resin (copolymer) was obtained by performing the reprecipitation purification operation once more. When the collected polymer was analyzed by GPC, it was found that Mw was 9,000 and the dispersity (Mw / Mn) was 2.40. When the substrate adhesion of the obtained polymer was evaluated, the evaluation score was 6.
[0061]
Example 4
In an Erlenmeyer flask, 2.34 g (10.0 mmole) of adamantane acrylate (= 1-acryloyloxyadamantane), 1.28 g (10.0 mmole) of t-butyl acrylate, initiator 4,4′-azobis (4-cyanovaleric acid) [Product name “ACVA” manufactured by Otsuka Chemical Co., Ltd.] 0.35 g was added and dissolved (suspended) in 35.0 g of methanol to obtain a monomer solution. This monomer solution was put into a 100 ml flask equipped with a reflux tube and a three-way cock, and the temperature was kept at 60 ° C., followed by stirring for 10 hours. Then, the reaction solution was dropped into 500 ml of hexane, and the resulting precipitate was filtered off. Further, reprecipitation purification operation was performed once again to obtain 1.8 g of a target resin (copolymer). When the collected polymer was analyzed by GPC, it was found that Mw was 12,000 and dispersity (Mw / Mn) was 2.90. When the substrate adhesion of the obtained polymer was evaluated, the evaluation score was 8.
[0062]
Comparative Example 1
In an Erlenmeyer flask, 2.34 g (10.0 mmole) of adamantane acrylate (= 1-acryloyloxyadamantane), 1.28 g (10.0 mmole) of t-butyl acrylate, initiator 2,2′-azobis (2-methylbutyronitrile) ) [Trade name “V-59” manufactured by Wako Pure Chemical Industries, Ltd.] 0.35 g was added and dissolved (suspended) in 35.0 g of methanol to obtain a monomer solution. This monomer solution was put into a 100 ml flask equipped with a reflux tube and a three-way cock, and the temperature was kept at 60 ° C., followed by stirring for 10 hours. Then, the reaction solution was dropped into 500 ml of hexane, and the resulting precipitate was filtered off. Furthermore, reprecipitation purification operation was performed once again to obtain 2.0 g of the target resin (copolymer). When the collected polymer was analyzed by GPC, it was found that Mw was 8000 and dispersity (Mw / Mn) was 2.30. When the substrate adhesion of the obtained polymer was evaluated, the evaluation score was 0.
[0063]
Comparative Example 2
In an Erlenmeyer flask, 2.34 g (10.0 mmole) of adamantane acrylate (= 1-acryloyloxyadamantane), 1.28 g (10.0 mmole) of t-butyl acrylate, initiator 2,2′-azobis (2,4-dimethylvalero) Nitrile) [trade name “V-65” manufactured by Wako Pure Chemical Industries, Ltd.] 0.35 g was added and dissolved (suspended) in 35.0 g of methanol to obtain a monomer solution. This monomer solution was put into a 100 ml flask equipped with a reflux tube and a three-way cock, and the temperature was kept at 60 ° C., followed by stirring for 10 hours. Then, the reaction solution was dropped into 500 ml of hexane, and the resulting precipitate was filtered off. Furthermore, reprecipitation purification operation was performed once again to obtain 2.1 g of the target resin (copolymer). When the collected polymer was analyzed by GPC, it was found that Mw was 7800 and dispersity (Mw / Mn) was 2.50. When the substrate adhesion of the obtained polymer was evaluated, the evaluation score was 0.
The results are summarized in Table 1.
[0064]
[Table 1]
Figure 0004414069
[0065]
From Table 1, it can be seen that when the resins of Examples 1 to 4 using an initiator having a specific functional group are used in a photoresist composition, the substrate adhesion is dramatically improved.

Claims (3)

2〜4環の非芳香族性環式基を分子内に有する(メタ)アクリル酸エステルを全単量体成分に対して30〜90モル%含む単量体混合物を、下記式(1)〜(11)A monomer mixture containing 30 to 90 mol% of (meth) acrylic acid ester having 2 to 4 ring non-aromatic cyclic groups in the molecule is represented by the following formula (1) to (11)
Figure 0004414069
Figure 0004414069
Figure 0004414069
Figure 0004414069
(式中、m、n、xは自然数を示す)(In the formula, m, n, and x represent natural numbers)
から選択された分子内に酸素原子含有基又は置換若しくは無置換アミノ基を有する重合開始剤の存在下、アルコール類(但し、イソプロピルアルコールを除く)からなる重合溶媒中で重合反応に付すことを特徴とするビニル重合体からなるフォトレジスト用高分子化合物の製造方法。Characterized by being subjected to a polymerization reaction in a polymerization solvent comprising an alcohol (excluding isopropyl alcohol) in the presence of a polymerization initiator having an oxygen atom-containing group or a substituted or unsubstituted amino group in the molecule selected from A method for producing a polymer compound for photoresist comprising a vinyl polymer.
請求項1記載の製造方法によりフォトレジスト用高分子化合物を製造し、得られたフォトレジスト用高分子化合物に光酸発生剤を配合することを特徴とするフォトレジスト組成物の製造方法。A method for producing a photoresist composition, comprising: producing a photoresist polymer compound by the production method according to claim 1; and blending the obtained photoresist polymer compound with a photoacid generator. 請求項2記載の製造方法によりフォトレジスト組成物を製造し、得られたフォトレジスト組成物を基材又は基板上に塗布してレジスト塗膜を形成し、露光及び現像を経てパターンを形成する工程を含む半導体の製造方法。The process of manufacturing a photoresist composition with the manufacturing method of Claim 2, apply | coating the obtained photoresist composition on a base material or a board | substrate, forming a resist coating film, and forming a pattern through exposure and image development. A method for manufacturing a semiconductor comprising:
JP2000209287A 2000-07-11 2000-07-11 Method for producing polymer compound for photoresist and method for producing photoresist composition Expired - Fee Related JP4414069B2 (en)