JP3491986B2 - Agricultural sheet - Google Patents

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an agricultural sheet having excellent mechanical properties, dimensional stability, water absorption, light shielding properties, and air permeability, and more specifically, it is composed of biodegradable short fibers and is gentle to the natural world. The present invention relates to an agricultural sheet that is biodegradable by burying treatment.

[0002]

2. Description of the Related Art Conventionally, a spunbond non-woven sheet made of synthetic long fibers, a film sheet made of polyester, polyvinyl or the like has been used as an agricultural sheet stretched in a tunnel shape in greenhouse cultivation or the like. .
These sheets are excellent in terms of uniformity of basis weight and strength. However, spunbonded non-woven sheets have excellent light-shielding properties, but have problems such as lack of breathability, and film sheets also lack breathability. Further, both the spunbond nonwoven sheet and the film sheet have a problem that the atmospheric temperature inside the sheet rises as the temperature rises, and as a result, the water in the soil in which the seedlings are planted evaporates to cause dew condensation.

[0003]

The present invention is intended to solve such problems and is excellent in mechanical properties such as tear strength, dimensional stability, light-shielding property, air permeability, water absorption, flexibility, and biodegradability. The purpose of the present invention is to provide an environmentally friendly agricultural sheet that can be decomposed in the natural world by being composed of short staple fibers.

[0004]

In order to solve this problem, the present invention comprises a short-fiber nonwoven web containing short fibers obtained from a thermoplastic polymer having a biodegradability of at least 50% by weight. It is an agricultural sheet, in which the fibers constituting the short fiber non-woven web have a three-dimensional entanglement, and 50 to 50% of the total area of the agricultural sheet in the widthwise central part.
The gist of the present invention is an agricultural sheet in which a light-shielding portion having a dense structure is formed in a range of 90%, and ventilation portions are formed on both sides of the light-shielding portion. Further, the present invention is
A shape-retaining portion having a dense structure is formed adjacent to the ventilation portion at the end in the width direction, and the ventilation portion is formed with an area ratio of 5 to 40% occupying the entire sheet. The gist is an agricultural sheet formed in the range of 5 to 10% of the entire area of the sheet.

Further, the present invention will be described in detail. The area ratio of the widthwise center of the agricultural sheet is 50-9.
The 0% portion is a non-woven web made of short fibers which is placed on a net of 50 mesh or more and subjected to high pressure liquid flow treatment to form a light-shielding portion having a dense structure. The area of 5-40% of the
It is placed on a net below mesh and subjected to high-pressure liquid flow treatment to form voids (holes) in the non-woven web, and has a breathable structure. The portion having an area ratio of 5 to 10% is a shape-retaining portion having a dense structure, which is placed on a net of 50 mesh or more and subjected to high-pressure liquid flow treatment similarly to the light-shielding portion.

In the present invention, the portion having a dense structure which becomes the light-shielding portion in the center portion in the width direction of the agricultural sheet is in the range of 50 to 90% in area ratio of the entire agricultural sheet. When the area of this light-shielded portion is less than 50%, the seedlings planted inside the tunnel-shaped agricultural sheet are exposed to strong direct sunlight when used in the summer when the sunshine duration is long,
It is not preferable because the soil in the agricultural sheet is dried. On the other hand, if it exceeds 90%, the air permeability is impaired and the temperature inside the tunnel-shaped stretched agricultural sheet is increased, which is not preferable. For the above reasons, the light-shielding portion having a dense structure in the entire agricultural sheet is in the range of 50 to 90%, more preferably 60 to 80%.

The ventilation parts on both sides of the light-shielding part are
The area ratio of the entire agricultural sheet is in the range of 5 to 40%. When the area ratio of the ventilation parts is less than 5%, the ratio of the ventilation parts on both sides of the agricultural sheet stretched in a tunnel shape becomes small, and the temperature inside the seat rises when used in summer. Air is trapped inside the sheet, and as a result the temperature inside the sheet rises, causing moisture in the soil to volatilize.
It is not preferable because it inhibits the growth of germinated plants. In addition, when the area ratio of the aerated portion exceeds 40%, although sufficient air permeability is obtained, morning and evening cold air easily enters the inside of the stretched sheet, and as a result, the growth of plants is impaired, which is not preferable.

The shape-retaining portion arranged adjacent to the ventilation portion is a portion having the same structure as the light-shielding portion and a dense structure, and the total area ratio 5 of the agricultural sheet in the shape-retaining portion is 5
It is formed in the range of 10%. This shape retention part is 5%
When it is less than the above range, the width of the shape-retaining portion occupying the outermost portion of the agricultural sheet becomes small, and the agricultural sheet stretched and used is deformed from the end portion, which is not preferable. Also, 10%
If it exceeds, the dense structure part occupying the side surface of the agricultural sheet will increase, and due to this increase in the dense structure part, the area of the ventilation part formed on the side surface will decrease, and sufficient air permeability can be secured. Not desirable. For the above reasons, the shape-retaining portion has a ratio of 5 to 5 of the total area of the agricultural sheet.
It is formed in the range of 10%.

Next, the agricultural sheet of the present invention will be described in detail with reference to the drawings. FIG. 1 is a perspective view of an agricultural sheet of the present invention. In FIG. 1, reference numeral 1 is a three-dimensionally formed non-woven web made of biodegradable synthetic fibers, recycled fibers such as cotton and rayon by high pressure liquid flow treatment. A light-shielding portion having a dense structure in the widthwise center of the entangled agricultural sheet, 2 is a ventilation portion formed on both sides of the light-shielding portion 1 of the agricultural sheet, and 3 is a widthwise direction of the agricultural sheet. It is a shape-retaining portion having a dense structure formed adjacent to the ventilation portion 2 at the end portion.

The first feature of the agricultural sheet of the present invention is that the synthetic staple fiber obtained from a biodegradable thermoplastic polymer is contained in the agricultural sheet in an amount of 50% by weight or more as a fiber constituting the short fiber nonwoven fabric. There is a point. By including 50% by weight or more of the biodegradable synthetic short fiber with respect to the agricultural sheet, the decomposition rate of the agricultural sheet due to the burying treatment in the natural world is accelerated. That is, when the agricultural sheet is buried in the soil, the biodegradable synthetic short fibers having a three-dimensional entanglement are biodegraded to separate the fibers constituting the agricultural sheet into individual fibers. And the rate of biodegradation is accelerated. If the amount of this biodegradable synthetic short fiber is less than 50% by weight, the remaining short fiber having a slow decomposition rate becomes a fiber mainly forming the three-dimensional entanglement of the non-woven fabric, and the shape of the non-woven fabric when embedding in soil is performed. Is retained for a long time, the fibers constituting the nonwoven fabric are not easily separated from each other, and the decomposition rate of the entire agricultural sheet is impaired, which is not preferable. In addition, in combination with the synthetic short fibers, natural fibers typified by cotton that are biodegradable in nature or regenerated fibers such as rayon can be used.

The biodegradable thermoplastic synthetic staple fiber used in the present invention means a staple fiber obtained by a conventional spinning method using the polymer described below. The polymer is a biodegradable thermoplastic aliphatic polyester polymer, for example, a polymer composed of polyglycolic acid or polylactic acid such as poly (α-hydroxy acid) or a copolymer thereof. And also poly (ε-caprolactone), poly (ω-hydroxyalkanoates) such as poly (β-propiolactone), poly-3-hydroxypropionate, poly-3-hydroxybutyrate, poly −
3-hydroxycaprolate, poly-3-hydroxyheptanoate, poly-3-hydroxyoctanoate, and poly-3-hydroxyvalerate and poly-
Poly (β, such as copolymerization with 4-hydroxybutyrate
-Hydroxyalkanoate). In addition, as a polycondensation polymer of glycol and dicarboxylic acid, for example, polyethylene oxalate, polyethylene succinate, polyethylene adipate, polyethylene azelate, polybutylene oxalate, polybutylene succinate, polybutylene adipate, polybutylene sebacate. , Polyhexamethylene sebacate, polyneopentyl oxalate or copolymers thereof. Further, the aliphatic polyester and polycapramide (nylon 6), polytetramethylene adipamide (nylon 46), polyhexamethylene adipamide (nylon 66), polyundecanamide (nylon 11), polylaurolactamide (nylon 12). And an aliphatic polyester amide type copolymer which is a copolymer with an aliphatic polyamide. In the present invention, any biodegradable one can be used.

The short fiber made of the biodegradable thermoplastic polymer of the present invention can be efficiently produced by the following steps. That is, melt-spinning is performed with a spinning die using a biodegradable polymer, the spun yarn is cooled, and then undrawn yarn is drawn at a speed of 800 to 1200 m / min.

A plurality of the obtained undrawn yarns are combined to form an undrawn yarn bundle, which is subjected to a drawing treatment using a two-stage drawing machine. During the drawing treatment, the breaking elongation of the undrawn yarn is 70 to
A target draw ratio in the range of 95% is set. At the time of stretching, in the first stage stretching treatment, the target stretching ratio of 70
The target stretching ratio is achieved by performing stretching of 85% and then performing the second stage stretching treatment. The drawn yarn is heat-set by a heat roll, crimped by an indenting crimper, and an oil agent for spinning is applied, followed by a drying treatment to obtain a single yarn of the yarn. It is cut into a predetermined fiber length according to the fineness. The number of crimps applied by the indentation crimper is preferably 12 to 25 threads / 25 mm. The crimped fiber bundle is applied with a spinning oil, dried and then cut into a predetermined fiber length according to the fineness of the single yarn of the fiber bundle.

As the cotton used in the present invention, in addition to the unbleached combed yarn and the bleached cotton, cotton wool, knitted fabric, and fluff can be used. The fluff includes bleached and dyed ones.

The anti-hairing machine which can effectively use the anti-hairing in the present invention is a rag machine, a knot breaker, a garnet machine, a slicing machine and the like. The type and combination of anti-fluffing machines used depend on the shape of the fabric to be fluffed, the thickness of the yarns and the strength of the twist, but several same anti-fluffing machines can be connected in series or two types can be used. It is effective to use a combination of the above anti-fluffing machines. Here, the defibration rate by the fluffing machine is preferably in the range of 30 to 95%. When the defibration rate is less than 30%, the high-pressure liquid stream does not penetrate the web when the web is entangled with the high-pressure liquid stream, which is not preferable. Further, if it exceeds 95%, sufficient surface abrasion strength cannot be obtained, which is not preferable. The defibration rate of the fluff is obtained by the formula shown below. Disentanglement rate (%) = (weight of fluff-weight of filamentous material) × 100 / weight of fluff

As the regenerated fiber used in the present invention, viscose rayon, cellulose acetate fiber, and other solution-spun rayon such as lyocell are used.

The fibers constituting the nonwoven web made of the short fibers of the present invention have a fineness of 1.0 to 5.0 denier and a fiber length of 1
It is advisable to adopt one having a size of 0 to 100 mm. When the fineness is less than 1.0 denier, the number of fibers constituting the non-woven web increases, making it difficult to impart a mesh pattern, and when it exceeds 5.0 denier, the number of fibers constituting the non-woven web decreases. Therefore, sufficient light-shielding properties cannot be obtained, which is not preferable.

The nonwoven web of the present invention preferably has a basis weight of 30 to 150 g / m ² . When the basis weight is less than 30 g / m ² , not only the shape retention of the obtained non-woven web is not improved, but also sufficient light-shielding property is not retained, which is not preferable.

On the other hand, when the basis weight exceeds 150 g / m ² , the processing energy of the high-pressure liquid flow becomes large, and under extreme processing conditions, the entanglement of short fibers cannot be maintained in the inner layer of the nonwoven web, resulting in practical use. It is not preferable because excellent mechanical properties cannot be obtained. Also, the basis weight is 150
If it exceeds g / m ² , the thickness of the nonwoven web increases,
The mesh pattern applied to the non-woven web becomes unclear, resulting in a non-woven web having no holes, which is not preferable because good air permeability cannot be obtained.

For the above reasons, the basis weight of the nonwoven web is 30 to
It is in the range of 150 g / m ² , preferably 50-100.
It is in the range of g / m ² . In the present invention, the non-woven web is a card machine which is subjected to opening, and as the card machine to be used, a parallel card machine, a random card machine, a semi-automatic machine depending on the performance required for the non-woven web. One of the random card machines is selected. Also, it may be a parallel card machine with a cross layer,
Further, a non-woven cloth that has been cross-laid may be prepared by using a drafter and changing the vertical / horizontal arrangement of the webs.

The second characteristic of the agricultural sheet of the present invention is a so-called spunlaced nonwoven fabric having three-dimensional entanglement,
The entangled portion of the nonwoven fabric surface is composed of a portion having a dense surface structure and a portion having a hole shape.

That is, when processed into an agricultural sheet, a light-shielding portion having a dense structure is formed in the widthwise central portion of the sheet, and breathable portions having holes are formed on both sides of the light-shielding portion. Further, a shape-retaining portion having a dense structure is formed adjacent to the breathable portion at the widthwise end portion of the sheet.

The agricultural sheet having three-dimensional entanglement of the present invention is produced by the following method. In the present invention, the three-dimensional entanglement means that the fibers forming the short fiber non-woven web are entangled not only in the lateral direction but also in the thickness direction and have a densely integrated structure. Means Further, the densely integrated structure means that the short fibers are predominantly entangled with each other, and the bulk density is higher than that of the carded short fiber web.

As a method for producing a nonwoven web having three-dimensional entanglement according to the present invention, a needle punch method or a spunlace method can be mentioned. In the present invention, a nonwoven fabric by the spunlace method is effectively applied. it can.

Next, the step of producing a nonwoven fabric by the spunlace method in the present invention will be described in detail. The high pressure liquid flow treatment of the short fiber non-woven web in the present invention has a pore size of 0.05 to 1.5.
mm of injection holes are arranged in a row or a plurality of rows with an injection hole interval of 0.5 to 5 mm. This is a process of colliding the fibers constituting the short fiber non-woven web with each other so as to be closely entangled with each other so as to be integrated with each other.

From the viewpoint of economy, it is preferable to use water at normal temperature or hot water as the fluid used for the entanglement treatment. When the high-pressure liquid stream is made to collide with the short fiber non-woven web, the orifice head having the injection holes is formed at a right angle with respect to the traveling direction of the short fiber non-woven web placed on the net. It is advisable to eject the high-pressure liquid flow and make it collide uniformly while vibrating the orifice head in the same direction as the ejection hole interval.

As the net on which the short fiber non-woven web is placed when the high pressure liquid flow is jetted, as long as the high pressure liquid flow can pass through the short fiber non-woven web on the net, it is made of metal. It may be made of polyester, or any other material.

In the present invention, the net used for forming the light-shielding portion and the shape-retaining portion on the short fiber web has a mesh of 50 to 150 mesh. 5
If the net is less than 0 mesh, holes are formed in the short fiber non-woven web subjected to the entanglement treatment, and as a result, sufficient light shielding properties and shape retention properties cannot be maintained, which is not preferable. Also, 1
If it exceeds 50 meshes, sufficient light-shielding property and shape-retaining property can be maintained, but the energy required for the entanglement treatment becomes large, which is not preferable.

The entanglement treatment with the high-pressure liquid flow is preferably performed at least twice. That is, in the first high pressure liquid flow treatment, the short fiber nonwoven web is pre-entangled with the high pressure liquid flow having a liquid pressure of 40 kg / cm ² G or less. The water pressure when performing the first treatment is 4
Above 0 kg / cm ² G, turbulence of the short fiber nonwoven web occurs due to the accompanying air flow generated by the high pressure liquid flow,
It is not preferable from the standpoint of maintaining the quality of the non-woven fabric due to unevenness of weight.

The short-fiber nonwoven web preliminarily entangled is continuously subjected to a water pressure of 50 kg / second as the second and subsequent entanglement treatments.
This is a so-called spunlaced nonwoven fabric in which short fibers are three-dimensionally and densely integrated by being treated with a high-pressure liquid flow of cm ² G or more.

Further, the short fiber non-woven web obtained by the above method is further inverted and subjected to the entanglement treatment by the hydraulic pressure applied in the second time as the third entanglement treatment, whereby the front and back sides are entangled in a minute manner. It can be a spunlaced non-woven fabric.

In the agricultural sheet of the present invention, a method for forming air-permeable portions on both sides of the light-shielding portion will be described. In the above process, a nonwoven web that has been subjected to a high-pressure liquid flow treatment using a net of 50 mesh or more is
Guide it onto a net of 5 mesh or less, and apply the high pressure liquid flow again to both sides of the light shielding part of the short fiber non-woven web that has been subjected to the high pressure liquid flow treatment using the net of 50 mesh or more,
The net shape of 25 mesh or less is given to the short fiber non-woven web to form a breathable portion.

Next, the method for producing the short fiber nonwoven web having the holes will be described in more detail. That is, 5
A non-woven fabric which is entangled with a net of 0 mesh or more is a non-woven fabric partially having pores of a net of 25 mesh or less. That is, the non-woven web obtained by the above method is placed on a net having a mesh structure of 25 mesh or less, and a hole diameter of 0.0
A plurality of orifice heads having 5 to 1.5 mm injection holes arranged at intervals of 0.5 to 5 mm and movable and rotatable in a width of 10 to 30 cm are arranged, and the arrangement angle and the arrangement place of the orifice heads are adjusted. This determines the regulation of the width and position of the hole shape.

The non-woven web obtained by this method has a dense non-woven fabric surface with a net of 50 mesh or more in the portion subjected to the entanglement treatment, and has a breathable function in which the other portion is provided with holes. It is a thing.

The liquid pressure required for jetting the high-pressure liquid flow in this step may be any liquid pressure which does not aim at the formation of entanglement but can give a hole shape, and is usually in the range of 40 to 60 kg / cm ² G. .

Excess water of the short fiber non-woven web obtained as described above is removed by using a known water removing device such as mangle, and further dried by using a suction band hot air circulating dryer. It is possible to obtain a non-woven fabric which has a three-dimensional entanglement and is partially provided with pores.

The sheet of the present invention has
If necessary, post-processing such as printing or dyeing, or by imparting a resin to one or both surfaces of the short fiber non-woven web, shape retention and water repellency can be imparted.

[0038]

EXAMPLES Examples of the present invention will be described below. The measurement of the examples in the present invention was performed by the following method. (1) Tensile strength of non-woven fabric (kg / 5cm width); constant speed extension type tensile tester (Tensilon UTM manufactured by Toyo Baldwin Co., Ltd.
4-1-100) was used and measured according to the strip method described in JIS L-1096. That is, 10 pieces of a sample having a sample width of 5 cm and a sample length of 15 cm are prepared,
For each sample, the maximum tensile strength (kg) was obtained by measuring at a gripping interval of 10 cm and a tensile speed of 10 cm / min, and the average value of the obtained tensile strength values was the tensile strength of the nonwoven fabric (kg / 5 cm width).
And

(2) Compression stiffness (g); sample length is 10c
A total of 5 sample pieces each having m and a sample width of 5 cm were prepared, and each sample piece was bent in the lateral direction to form a cylindrical object, and its end portions were joined to each other to obtain a sample for measuring compression stiffness. Then, a constant speed extension type tensile tester (Tensilon UTM-4-1-manufactured by Toyo Baldwin Co., Ltd.) is used for each measurement sample in the axial direction.
100) was used for compression at a compression rate of 5 cm / min, and the average value of the maximum load values (g) obtained was taken as the compression stiffness (g).

(3) Breathability (m / sec): Five 30 cm square samples were prepared, and a wind generator with a wind speed of 10 m / sec and a wind speed measuring instrument model 6621 manufactured by Japan Canomax Co., Ltd. were used as a measuring instrument. It was measured using. That is, the sample is blown by 7 m
The sample was placed vertically at a wind speed of / sec, the wind speed passing through the sample was measured for each sample at a position 1 cm immediately after the sample, and the average value was taken as the air permeability (m / sec).

(4) Light-shielding property (look): Five 30 cm square samples were prepared, and white light of 200 W was used as a light source.
Illuminance meter ANA-3 manufactured by Tokyo Kodensha Co., Ltd.
00 was used for measurement. That is, the distance between the light source and the measuring device is set to 2000 lux, the sample is placed 10 cm above the measuring device horizontally, the amount of light passing through the sample is measured for each sample, and the average value is taken as the light-shielding property (lux). did.

(5) Water absorption (cm / 10 minutes); JIS L
By the Bayrec method described in -1096, width 2.5c
5 samples of m and 20 cm in length are prepared, and 20 pieces of each sample piece are prepared.
Hang it with a pin on a horizontal bar supported at a certain height above a tank containing distilled water at ± 2 ° C. Align the lower end of the sample piece in a line and lower the horizontal bar so that 1 cm of the lower end of the sample piece is just submerged in water. Next, the elevated height (mm) of water after standing for 10 minutes was measured, and the average value was taken as water absorption (cm / 10 minutes).

(6) Biodegradability: A 30 cm × 30 cm sample was embedded in soil, taken out 3 weeks later, and the shape of the non-woven fabric was visually evaluated for evaluation. In addition, for those that retain the morphology of the nonwoven fabric, the strength of the nonwoven fabric was measured, and those showing a measured value that was 50% or more lower than the initial strength were judged to have good biodegradability.

Example 1 As the biodegradable synthetic fiber, a short fiber having a fineness of 2 denier and a fiber length of 51 mm obtained from polybutylene succinate was used. Using a random card machine, a short fiber non-woven web having a random basis weight of 60 g / m ² was obtained.

The short fiber non-woven web obtained by the above method is
Placed on a 70 mesh wire mesh that moves at 20 m / min,
At a position 50 mm above the short fiber non-woven web, a hole diameter of 0.1
As the first treatment from the liquid flow injection holes arranged at 2 mm and a hole interval of 0.6 mm, the high-pressure liquid flow treatment was performed with normal temperature water with a water pressure of 40 kg / m ² G, and then as the second treatment. Using the same net and injection holes as described above, high pressure liquid flow treatment was performed four times with a water pressure of 70 kg / m ² G.

The obtained nonwoven web was dried with a drier at a temperature of 100 ° C. after removing excess water with mangle. The resulting nonwoven web has a basis weight of 62
It had a three-dimensional entanglement in which the constituent fibers were densely integrated at g / m ² .

The non-woven web obtained by the above method is further introduced onto a 20-mesh net, and the upper part of the net is 50
An orifice head having a width of 30 mm and having a diameter of the injection holes of 0.1 mm and an injection hole spacing of 0.6 mm is located at a position of 12.5 cm at the center of the orifice head from both ends of the nonwoven web. The individual and non-woven webs were set at an angle of 30 degrees with respect to the traveling direction. The distance between the centers of these two orifice heads was 75 cm.

When imparting the hole shape to the nonwoven web, the high-pressure liquid flow treatment at a water pressure of 70 kg / m ² G was performed three times. The obtained non-woven web was formed with shape-holding portions that were densely entangled with a 70-mesh net and had a width of 5 cm from both ends, and voids each having a hole shape with a width of 15 cm inside. Was a non-woven web having a dense structure with the same mesh as the shape-retaining part with a width of 75 cm in the central part.

After removing excess water of the obtained nonwoven web by mangle or the like, it was dried by a suction band type dryer at a temperature of 90 ° C. The performance of the obtained non-woven web is that the tensile strength of the central portion having the light-shielding property in the entangled portion of 70 mesh is 5.2 kg.
The width was / 5 cm. In addition, the tensile strength of the perforated part of 20 mesh is 4.6 because it has air permeability.
The width was kg / 5 cm, and the tensile strength of the widthwise end portion having shape retention was 5.7 kg / 5 cm width.

In addition, the perforated portion of 20 mesh has air permeability by showing clear voids on the surface of the non-woven web, and the 70 mesh portion has a dense structure and has a proper light-shielding property and shape-retaining property. It was something that had.

This non-woven fabric was cut into a size of 30 cm × 30 cm, embedded in soil for 3 weeks, and then taken out. The form of the non-woven fabric was partially impaired. The initial strength is reduced by 75% to 1.3k
The width was g / 5 cm, and the nonwoven fabric had good biodegradability.

Example 2 As fibers constituting the non-woven web, biodegradable synthetic fibers, 2 denier fibers obtained by polybutylene succinate, short fibers having a fiber length of 51 mm, and cotton fibers have an average fineness of 1.8. Bleached cotton with a denier and average fiber length of 22 mm was used. A nonwoven web was obtained under the same conditions as in Example 1 except that the compounding ratio (weight ratio) was biodegradable synthetic fiber: cotton bleached cotton = 60:40.

With regard to the performance of the obtained nonwoven web, the tensile strength of the central light-shielding portion of the 70 mesh entangled portion was 6.5 kg / 5 cm width. In addition, the tensile strength of the portion where holes are provided by 20 mesh for maintaining air permeability is 5.6 kg / 5 cm width, and the tensile strength of the portion having shape retention at the width direction end is 6.9 kg.
The width was / 5 cm.

Further, the perforated portion of 20 mesh has breathability by showing clear voids on the surface of the non-woven web, and the 70 mesh portion is of a dense structure and has a proper light-shielding property and shape retention property. It was something that had.

This non-woven fabric was cut into a size of 30 cm × 30 cm, embedded in soil for 3 weeks, and then taken out. As a result, the form of the non-woven fabric was partially impaired. The initial strength is 57% lower than 2.97.
The width was kg / 5 cm, and the nonwoven fabric had good biodegradability.

Comparative Example 1 A non-woven fabric was obtained under the same conditions as in Example 2 except that the compounding ratio (weight ratio) in Example 2 was changed to biodegradable synthetic fiber: cotton exposed cotton = 30:70.

The obtained non-woven fabric was a non-woven fabric in which a light-shielding portion having a dense entangled portion subjected to an entanglement treatment with a 70-mesh net, a shape-retaining portion, and voids (pores) formed with a 20-mesh net. But this nonwoven fabric 3
When cut into a size of 0 cm × 30 cm, embedded in soil for 3 weeks, and taken out, the shape of the non-woven fabric is retained, and the measured value of the non-woven fabric tenacity is 7.85 kg /
The nonwoven fabric was 5.1 kg / 5 cm wide, which was 35% lower than the width of 5 cm, and the biodegradation rate was slow.

The results obtained by measuring the tensile strength, compression stiffness and softness, light-shielding property, air-blocking property, and water absorption of the nonwoven fabrics in the above-mentioned Examples and Comparative Examples are shown in Table 1, and the biodegradability evaluation results are shown in Table 2. Shown in.

[0059]

[Table 1]

[0060]

[Table 2]

[0061]

As described above, according to the present invention, mechanical properties such as tensile strength, dimensional stability, light-shielding property, breathability,
It is possible to provide a material which is excellent in water absorption and which is suitable as an agricultural sheet that is biodegradable and can be composted. In particular,
According to the present invention, a light-shielding portion having a dense structure is formed in the center in the width direction, and ventilation portions are formed on both sides of the light-shielding portion to exert an excellent effect as an agricultural sheet. Since the shape-retaining portion having a dense structure is formed adjacent to the portion, the shape of the entire sheet is stable, and the extensibility is excellent in combination with the flexibility obtained by the three-dimensional entanglement.

[Brief description of drawings]

FIG. 1 is a perspective view of an agricultural sheet of the present invention.

[Explanation of symbols]

1 shaded area 2 ventilation part 3 Shape retention part

Continuation of front page (56) Reference JP-A-6-200457 (JP, A) JP-A-6-212548 (JP, A) JP-A-6-233632 (JP, A) JP-A-5-336846 (JP , A) JP-A-3-130019 (JP, A) JP-A-1-202223 (JP, A) Actual opening 1-15-1549 (JP, U) Actual opening Sho-58-96763 (JP, U) (58) Fields surveyed (Int.Cl. ⁷ , DB name) A01G 13/02 ZAB

Claims (2)

(57) [Claims] 1. An agricultural sheet comprising a short fiber non-woven web containing short fibers obtained from a thermoplastic polymer having a biodegradability of at least 50% by weight, and a fiber constituting the short fiber non-woven web. Each has a three-dimensional entanglement, and is 50 to 50% of the total area of the agricultural sheet in the widthwise central part.
An agricultural sheet characterized in that a light-shielding portion having a dense structure is formed in a range of 90%, and ventilation portions are formed on both sides of the light-shielding portion. 2. A shape-retaining portion having a dense structure is formed adjacent to the ventilation portion at the end in the width direction, and the ventilation portion is formed with an area ratio of 5 to 40% in the entire sheet. The agricultural sheet according to claim 1, wherein the holding portion is formed in a range of 5 to 10% of the entire area of the agricultural sheet.